JP2017008472A - Production method of cellulose nanofiber and production apparatus of cellulose nanofiber - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a production method of cellulose nanofibers, with which the cellulose nanofibers can be produced with energy saving by reducing the number of times of mechanical micronization treatment, and to provide a production apparatus of the cellulose nanofibers.SOLUTION: A production method of cellulose nanofibers includes: a step to pretreat pulp fibers in slurry; and a step to micronize the pretreated pulp fibers in the slurry with mechanical treatment, in which the pretreatment step includes: a step to subject the pulp fibers to chemical treatment consisting of oxidation treatment, hydrolysis treatment, or combination thereof; and a step to roughly fibrillate the pulp fibers with a refiner. In the pretreatment step, the chemical treatment step and the rough fibrillation step are preferably performed in this order. In the micronization step, the mechanical treatment is preferably performed with a high-pressure homogenizer.SELECTED DRAWING: Figure 1

Description

  The present invention relates to a method for producing cellulose nanofibers and an apparatus for producing cellulose nanofibers.

  In recent years, nanotechnology that aims to refine materials to the nanometer level and obtain new physical properties that are different from conventional properties of materials has attracted attention. Cellulose nanofibers manufactured from cellulose-based raw materials such as pulp fibers are excellent in strength, elasticity, thermal stability, etc., so they are filled in filter media, filter aids, ion exchanger substrates, and chromatographic analyzers. It is used for industrial use as a filler for blending materials, resins and rubbers, and for use as a blending agent for cosmetics such as lipsticks, powder cosmetics and emulsified cosmetics. Cellulose nanofibers are excellent in water-based dispersibility, so they have viscosity retention agents for foods, cosmetics, paints, etc., food material dough strengtheners, moisture retention agents, food stabilizers, low calorie additives, emulsification It is expected to be used in many applications such as stabilizing aids.

  Cellulose nanofibers can be obtained by defibrating pulp fibers by mechanical treatment. However, when cellulose nanofibers are produced only by mechanical treatment, a large number of mechanical treatments are required, resulting in a very large energy consumption. Therefore, various methods for performing pretreatment such as oxidation treatment and esterification treatment before mechanical treatment have been studied. Among these pretreatments, a method of oxidizing pulp using 2,2,6,6-tetramethyl-1-piperidine-N-oxy radical (TEMPO) and sodium hypochlorite (JP 2008-1728 A). And Japanese Patent Application Laid-Open No. 2010-235679) can effectively reduce the post-process mechanical treatment. However, even with this method, the number of mechanical treatments is not sufficiently reduced, and TEMPO is expensive. For commercialization, it is possible to reduce the number of mechanical treatments while suppressing an increase in cost. A manufacturing method is required.

JP 2008-1728 A JP 2010-235679 A

  The present invention has been made based on the circumstances as described above, and the object thereof is to reduce the number of mechanical miniaturization treatments, and to produce cellulose nanofibers that can produce cellulose nanofibers with energy saving, and cellulose It is to provide a nanofiber manufacturing apparatus.

  The inventors have used a chemical treatment and a specific mechanical treatment in combination as a pretreatment step for mechanically refining the pulp fiber, and beaten the pulp fiber as the specific mechanical treatment. It has been found that the use of a refiner can reduce the number of fine processing steps in the subsequent process, and the present invention has been completed.

  That is, the invention made in order to solve the above problems includes a step of pretreating the pulp fibers in the slurry, and a step of refining the pulp fibers in the slurry that have been pretreated by mechanical treatment. It is a manufacturing method of the cellulose nanofiber provided, Comprising: The said pre-processing process performs the chemical process which consists of an oxidation process, a hydrolysis process, or these combination with respect to the said pulp fiber, and the said pulp fiber by refiner It comprises a step of rough defibration.

  In the production method, before the finer fiber, that is, fibrillation by mechanical (physical) treatment for pulp fibers, chemical prep treatment such as oxidation treatment and hydrolysis treatment and rough defibration using a refiner are performed. Two types of pre-processing such as mechanical pre-processing are performed. The combination of these two types of pretreatments makes the pulp fibers flexible and efficiently produces preliminary defibration. Specifically, the chemical pretreatment can swell part of the chemical bond in the pulp fiber and swell the pulp fiber. The pretreatment using the refiner can shear the pulp fiber. Is effectively applied, fluffing occurs in the pulp fiber, the pulp fiber becomes soft, and preliminary defibration occurs. As a result, it is possible to reduce the number of times of the subsequent miniaturization process and to manufacture cellulose nanofibers with energy saving. In addition, the frequency | count of a refinement | miniaturization process (miniaturization process) means the frequency | count that the slurry containing the pulp fiber processed passes the machine which performs refinement | miniaturization processes, such as a high pressure homogenizer.

  The pretreatment step is preferably performed in the order of the chemical treatment step and the rough defibrating step. By performing the pretreatment in this order, the shearing force is efficiently applied by the refiner to the pulp fibers swollen by the chemical pretreatment, so that the efficiency of preliminary defibration can be improved. it can.

  It is preferable to perform the mechanical treatment in the above-mentioned miniaturization step with a high-pressure homogenizer. By passing through two kinds of pretreatment steps, the pulp fibers are in a sufficiently softened state. By treating such pulp fibers with a high-pressure homogenizer, collisions between the pulp fibers can act. And defibration occurs effectively. Thereby, the processing frequency of a refinement | miniaturization process can be reduced more and the productivity of a cellulose nanofiber can be improved more.

  It is preferable that the high-pressure homogenizer is an opposing collision type high-pressure homogenizer, and the slurry is allowed to collide in a straight line in the miniaturization step. By doing in this way, the energy given from a high pressure homogenizer can be converted into collision energy to the maximum, and more efficient pulp fiber defibration occurs.

  Another invention made in order to solve the above problems is a chemical treatment means for subjecting pulp fibers in a slurry to chemical treatment comprising oxidation treatment, hydrolysis treatment, or a combination thereof, and pulp in the slurry. It is an apparatus for producing cellulose nanofibers comprising a refiner for coarsely defibrating fibers and a high-pressure homogenizer for refining pulp fibers in the slurry. According to the manufacturing apparatus, the pulp fibers can be effectively pretreated by the chemical pretreatment means and the refiner, and the number of times of the micronization process using the high-pressure homogenizer can be reduced. . Therefore, according to the said manufacturing method, a cellulose nanofiber can be manufactured efficiently by energy saving.

  The “cellulose nanofiber” refers to a fine cellulose fiber obtained by defibrating pulp fibers, and generally refers to a cellulose fiber including cellulose fine fibers having a fiber width of nanosize (1 nm to 1000 nm). .

  According to the method for producing cellulose nanofibers and the apparatus for producing cellulose nanofibers of the present invention, the number of mechanical refining treatments can be reduced and cellulose nanofibers can be produced with energy saving.

It is a flowchart of the manufacturing method of the cellulose nanofiber which concerns on one Embodiment of this invention. It is a partial schematic diagram of the opposing collision type high pressure homogenizer used for the manufacturing method of the cellulose nanofiber of FIG.

  Hereinafter, a cellulose nanofiber manufacturing method and a cellulose nanofiber manufacturing apparatus according to an embodiment of the present invention will be described in detail with reference to the drawings as appropriate.

<Method for producing cellulose nanofiber>
As shown in FIG. 1, the manufacturing method of the cellulose nanofiber which concerns on one Embodiment of this invention is equipped with the pre-processing process (s1) and the refinement | miniaturization process (s2), and the said pre-processing process (s1) is a chemical process. A process (s1a) and a rough defibrating process (s1b) are provided. The order of the chemical treatment step (s1a) and the rough defibrating step (s1b) is not particularly limited, and any step may be performed first. According to the production method, the combination of the two types of pretreatments of the chemical treatment step (s1a) and the rough defibration step (s1b) makes the pulp fiber flexible and efficiently produces preliminary defibration. In addition, it is possible to shorten the subsequent miniaturization process, that is, to reduce the number of processes. Hereinafter, each process is explained in detail.

<Pretreatment step (s1)>
The pretreatment step (s1) is a step of pretreating the pulp fibers in the slurry, and is a step of pretreating the pulp fibers before refining the pulp fibers by mechanical treatment. . Below, the pulp fiber used as the raw material of a cellulose nanofiber is demonstrated.

Examples of the pulp fibers include broadleaf kraft pulp (LKP) such as hardwood bleached kraft pulp (LBKP), hardwood unbleached kraft pulp (LUKP), softwood bleached kraft pulp (NBKP), and softwood such as softwood unbleached kraft pulp (NUKP). Chemical pulp such as kraft pulp (NKP);
Stone Grand Pulp (SGP), Pressurized Stone Grand Pulp (PGW), Refiner Grand Pulp (RGP), Chemi Grand Pulp (CGP), Thermo Grand Pulp (TGP), Grand Pulp (GP), Thermo Mechanical Pulp (TMP), Mechanical pulp such as chemi-thermomechanical pulp (CTMP) and bleached thermomechanical pulp (BTMP);
Waste paper pulp made from tea waste paper, craft envelope waste paper, magazine waste paper, newspaper waste paper, leaflet waste paper, office waste paper, corrugated waste paper, Kami white waste paper, Kent waste paper, imitation waste paper, lottery waste paper, waste paper waste paper, etc .;
Examples include deinked pulp (DIP) obtained by deinking waste paper pulp. These may be used singly or may be used in combination of plural kinds as long as the effects of the present invention are not impaired.

<Chemical treatment step (s1a)>
The chemical treatment step (s1a), which is one of the pretreatment steps (s1), is a step of subjecting the pulp fibers in the slurry to a chemical treatment comprising oxidation treatment, hydrolysis treatment, or a combination thereof. . By performing such chemical treatment, it is possible to swell the pulp fiber while breaking a part of the chemical bond in the pulp fiber.

  As a minimum of the pulp fiber concentration in the pulp slurry used for a chemical treatment process (s1a), 3 mass% is preferred and 5 mass% is more preferred. On the other hand, as this upper limit, it is 30 mass%, for example. By setting the concentration range, an efficient chemical treatment can be performed. When the concentration is less than the above lower limit, the amount of pulp fibers processed in one treatment is small, and the efficiency is low. On the other hand, when the concentration exceeds the above upper limit, sufficient stirring cannot be performed, and the reactivity and the like are lowered.

  As a temperature of the pulp slurry used for a chemical treatment process (s1a), 40 degreeC or more and 90 degrees C or less are preferable, for example. In addition, about 40 degreeC or more and 70 degrees C or less are preferable for the process at the time of using an enzyme.

  Examples of the oxidizing agent used in the oxidation treatment include ozone, hypochlorous acid or a salt thereof, chlorous acid or a salt thereof, perchloric acid or a salt thereof, persulfuric acid or a salt thereof, a perorganic acid, and the like. Among these, persulfuric acids (persulfuric acid and salts thereof) are preferable. When performing the oxidation treatment, an oxidation catalyst such as an N-oxyl compound can be used in combination. Examples of the catalyst used for the hydrolysis treatment include acids and enzymes. Examples of the acid include sulfuric acid, persulfuric acid, hydrochloric acid and the like, and sulfuric acid and persulfuric acid are preferable. When the acid is used, the pH in the reaction vessel is preferably 3 or less, more preferably 0.5 or more and 2 or less. Examples of the enzyme include a cellulase enzyme, a hemicellulase enzyme, and the like, and a cellulase enzyme is preferable. For the oxidation treatment and the hydrolysis treatment, plural kinds of treatment agents may be used, or the oxidation treatment and the hydrolysis treatment may be combined. When an acid that also functions as an oxidizing agent such as persulfuric acid is used, both an oxidation reaction and a hydrolysis reaction occur.

  The chemical treatment step (s1a) can be performed by storing the slurry in a known reaction tank and adding a treatment agent such as an oxidizing agent. As the reaction tank, a paper tower such as a bleaching tower can be used. The treatment (reaction) time of the chemical treatment step is changed according to the concentration and temperature of the slurry, the amount of treatment agent added, and the like, and can be, for example, 0.5 hours to 12 hours.

  The slurry that has undergone the chemical treatment step (s1a) is subjected to neutralization treatment, washing treatment, and the like, if necessary, and is provided to the next step. In the case of chemical treatment using an enzyme, the reaction can be terminated by raising the slurry temperature by injecting hot water (hot water) into the slurry and inactivating the enzyme.

<Rough defibrating process (s1b)>
The coarse fibrillation treatment step (s1b), which is one of the pretreatment steps (s1), is a step of coarsely defibrating pulp fibers in the slurry with a refiner. Pretreatment using a refiner that beats while applying a load with an extremely small gap effectively imparts shearing force to the pulp fiber, causing fluffing of the pulp fiber, softening the pulp fiber, and preliminary Defibration occurs. A refiner is a device that beats pulp fibers, and known ones can be used. As the refiner, a conical type, a double disc refiner (DDR), and a single disc refiner (SDR) are preferable from the viewpoint that a shear force can be efficiently applied to the pulp fiber and preliminary defibration can be advanced. . In the rough defibrating process, it is preferable to use a refiner from the viewpoint that separation or cleaning after the process is not necessary.

  The lower limit of the pulp fiber concentration of the pulp slurry subjected to the rough defibrating treatment step (s1b) is preferably 1% by mass, and more preferably 2% by mass. On the other hand, as this upper limit, 8 mass% is preferable and 6 mass% is more preferable. By setting the pulp fiber concentration within the above range, the pulp slurry has a suitable viscosity, so that the refined fiber is efficiently coarsely defibrated by the refiner.

  In the rough defibrating treatment step (s1b), for example, a plurality of refiners can be prepared and pulp fibers can be treated continuously. Further, it is possible to circulate the slurry for one refiner for a long time.

<Order of chemical treatment step (s1a) and rough defibration treatment step (s1b)>
Either the chemical treatment step (s1a) or the rough defibration treatment step (s1b) may be performed first, but the chemical treatment step (s1a) is preferably performed first. By performing the chemical treatment step (s1a) and the rough defibration step (s1b) in this order, a shear force is efficiently imparted to the pulp fibers swollen by the chemical pretreatment by the refiner. Can improve the efficiency of defibration and reduce energy consumption.

  In addition, the chemical treatment step (s1a) and the rough defibrating treatment step (s1b) can be performed in an overlapping manner. For example, the chemical treatment and the rough defibrating treatment can be performed simultaneously by subjecting the slurry to which the acid, enzyme, oxidizing agent, etc. are added to the rough defibrating treatment step (s1b).

<Miniaturization step (s2)>
The refinement step (s2) is a step of refining the pulp fibers in the pretreated slurry by mechanical treatment. Cellulose nanofibers can be obtained through this step. According to the method for producing cellulose nanofibers of the present invention, since the above-described two types of pretreatment are performed, the shortening (reduction in the number of treatments) of the present miniaturization step (s2) can be achieved.

  Examples of a method for performing the mechanical treatment in the micronization step (s2) include a grinder method in which pulp fibers are ground between rotating grindstones, a pulverization method, and the like, and a pulverization method is preferable. Examples of the pulverization method include a pulverization method using a pressure homogenizer, a ball mill, and the like. Among these, the method performed by a pressure type homogenizer is preferable. A pressure homogenizer is used as a disperser that discharges slurry and the like from pores at high pressure. As the pressure homogenizer, a high-pressure homogenizer is preferable. The high-pressure homogenizer refers to a homogenizer having the ability to discharge slurry at a pressure of 10 MPa or more, preferably 100 MPa or more. By treating the pulp fibers with a high-pressure homogenizer, collision between the pulp fibers, a pressure difference, microcavitation, and the like act, and defibration occurs effectively. Thereby, the processing frequency of a refinement | miniaturization process can be reduced (shortening) and the manufacturing efficiency of a cellulose nanofiber can be improved more.

  As the high-pressure homogenizer, a counter-collision type high-pressure homogenizer (microfluidizer, wet jet mill) is preferable, and in the miniaturization step, the slurry is preferably collided in a straight line. Specifically, as shown partially in FIG. 2, in the opposed collision type high pressure homogenizer 10, the upstream flow path 11 is formed so that the pressurized slurries S <b> 1 and S <b> 2 collide with each other at the junction X. Has been. Slurries S1 and S2 collide at the junction X, and the collided slurry S3 flows out from the downstream flow path 12. The downstream flow path 12 is provided perpendicular to the upstream flow path 11, and the upstream flow path 11 and the downstream flow path 12 form a T-shaped flow path. By using such an opposing collision type high-pressure homogenizer 10, energy given from the high-pressure homogenizer can be converted to collision energy to the maximum, and more efficient pulp fiber defibration occurs.

  The lower limit of the pulp fiber concentration of the pulp slurry to be subjected to the refinement step (s2) is preferably 0.5% by mass, and more preferably 1% by mass. On the other hand, as this upper limit, 10 mass% is preferable and 5 mass% is more preferable. By setting the pulp fiber concentration within the above range, the pulp slurry has a suitable viscosity, so that the pulp fibers are efficiently coarsely defibrated by mechanical treatment using a high-pressure homogenizer or the like.

  In the miniaturization step (s2), for example, a single high-pressure homogenizer can be subjected to a plurality of miniaturization processes by circulating the slurry. In addition, a plurality of high-pressure homogenizers can be prepared and pulp fibers can be processed continuously.

<Other processes>
Cellulose nanofibers obtained through the micronization step (s2) can be subjected to a modification treatment step or a drying step as necessary.

  Cellulose nanofibers obtained in this way are filter materials, filter aids, ion exchanger substrates, fillers for chromatographic analyzers, fillers for compounding resins and rubbers, cosmetic compounding agents, viscosity maintaining agents. It can be widely used for food raw material dough strengthening agents, moisture retention agents, food stabilizers, low calorie additives, emulsion stabilization aids and the like.

  The obtained cellulose nanofiber is sufficiently refined and has one peak in a pseudo particle size distribution curve measured by a laser diffraction method in an aqueous dispersion state. Further, the particle size (mode) that becomes a peak in the pseudo particle size distribution curve is preferably 5 μm or more and 25 μm or less. When the obtained cellulose nanofiber has such a particle size distribution, it can exhibit good performance that is sufficiently refined. The “pseudo particle size distribution curve” means a curve indicating a volume-based particle size distribution measured using a particle size distribution measuring apparatus (for example, a laser diffraction / scattering type particle size distribution measuring instrument manufactured by Seishin Corporation).

  The method for producing cellulose nanofibers can reduce the number of mechanical refining treatments and obtain cellulose nanofibers with energy savings without using expensive oxidation catalysts such as N-oxyl compounds such as TEMPO. Therefore, the production cost of cellulose nanofiber can be suppressed. Moreover, when TEMPO etc. are not used, since excess oxidation is suppressed, content of the carboxy group of the cellulose nanofiber obtained is included low. When the amount of the carboxy group of the cellulose nanofiber is small, there is an advantage that excessive hydrophilicity and hydrogen bonding are suppressed, and drying property and dispersibility are improved. As content of the carboxy group of the obtained cellulose nanofiber, it is 0.1 mmol / g or less, for example, and can also be 0.05 mmol / g or less.

<Manufacturing equipment for cellulose nanofiber>
An apparatus for producing cellulose nanofibers according to an embodiment of the present invention includes chemical treatment means, a refiner, and a high-pressure homogenizer.

  The chemical treatment means performs chemical treatment consisting of oxidation treatment, hydrolysis treatment, or a combination thereof on pulp fibers in the slurry. Examples of the chemical treatment means include a reaction tank having a charging means such as an oxidant, an acid, and an enzyme. As the reaction tank, a papermaking tower such as a bleaching tower can be used as described above. As the refiner and the high-pressure homogenizer, those described in “Method for producing cellulose nanofiber” can be used. The cellulose nanofiber production apparatus may be provided with a dehydrating means such as a filter and a screw press, and a drying means, in addition to a chemical treatment means, a refiner, and a high-pressure homogenizer. The said cellulose nanofiber manufacturing apparatus can be used by the method mentioned above as "the manufacturing method of a cellulose nanofiber." According to the cellulose nanofiber manufacturing apparatus, the mechanical refinement process can be shortened, that is, the number of processes can be reduced, and the cellulose nanofiber can be efficiently produced with energy saving.

  EXAMPLES Hereinafter, although this invention is explained in full detail based on an Example, this invention is not interpreted limitedly based on description of this Example.

[Example 1]
(Chemical treatment process)
A cellulase enzyme was added to a pulp slurry (temperature: 50 ° C.) having a concentration of 20% by mass (pulp type: LBKP) and subjected to chemical treatment. After 5 hours, the enzyme was inactivated by heating to 100 ° C.
(Rough defibrating process)
The pulp slurry subjected to the above chemical treatment was prepared to a pulp concentration of 4% by mass and subjected to rough defibrating treatment with a refiner. The processing time by the refiner was 10 minutes.
(Miniaturization process)
The pulp slurry that had undergone the above rough defibrating step was prepared to a pulp concentration of 2% by mass and subjected to a refinement step by mechanical treatment. This treatment was performed using a counter-impact type wet jet mill (high-pressure homogenizer). This wet jet mill is configured such that the slurry collides with each other in a straight line.

[Example 2]
As a chemical treatment step, an oxidizing agent (ammonium persulfate) was added to a pulp slurry (temperature 80 ° C.) with a concentration of 20% by mass to carry out a chemical treatment. The same operation as in Example 1 was performed to obtain cellulose nanofibers.

[Example 3]
Cellulose nanofibers were obtained in the same manner as in Example 2 except that a polishing machine (“Mascoloider” manufactured by Masuko Sangyo Co., Ltd.) was used as the miniaturization step.

[Example 4]
Cellulose nanofibers were obtained in the same manner as in Example 1, except that a polishing machine (“Mascoloider” manufactured by Masuko Sangyo Co., Ltd.) was used as the miniaturization step.

[Example 5]
As a chemical treatment step, an acid (dilute sulfuric acid) was added to a pulp slurry (temperature 80 ° C.) having a concentration of 20% by mass to perform a chemical treatment, and after 5 hours, it was neutralized with sodium hydroxide. Performed the same operation as Example 1 and obtained the cellulose nanofiber.

[Example 6]
Cellulose nanofibers were obtained by performing the same operation as in Example 5 except that a polishing machine (“Mascoloider” manufactured by Masuko Sangyo Co., Ltd.) was used as the miniaturization step.

[Comparative Example 1]
Cellulose nanofibers were obtained by performing the same operations as in Example 1 except that the chemical treatment step and the rough defibration step were not performed.

[Comparative Example 2]
Cellulose nanofibers were obtained in the same manner as in Example 1 except that the chemical treatment step was not performed.

[Comparative Example 3]
Cellulose nanofibers were obtained in the same manner as in Example 1 except that the chemical treatment step was not performed and an oblique collision type high-pressure homogenizer was used in the miniaturization step.

[Comparative Example 4]
Cellulose nanofibers were obtained by performing the same operation as in Example 1 except that the rough defibrating step was not performed.

[Comparative Example 5]
Cellulose nanofibers were obtained in the same manner as in Example 1 except that a polishing machine (“Mascolloyer” manufactured by Masuko Sangyo Co., Ltd.) was used as the miniaturization step without performing the chemical treatment step.

  In each of the examples and comparative examples, the volume-based particle size distribution of pulp fibers in the treated slurry was measured for each treatment with a high-pressure homogenizer or polishing machine in the refinement treatment. This measurement was performed using a laser diffraction / scattering particle size distribution measuring instrument manufactured by Seishin Enterprise Co., Ltd. In the measured pseudo particle size distribution curve, the treatment with a high-pressure homogenizer or a grinder was repeated until there was one peak and this peak was in the range of 5 μm to 25 μm. In the pseudo particle size distribution curve, it was judged that cellulose nanofibers were obtained at the stage where there was one peak and this peak was in the range of 5 μm or more and 25 μm or less, and the refinement process was terminated. Table 1 shows the number of times of the miniaturization process performed in each example and comparative example.

  In addition, the numerical value shown in the parentheses in the column of each processing step in Table 1 is a relative value indicating the amount of energy consumed per time of each processing step, where 1 is the energy consumption per time of enzyme treatment. is there. Table 1 shows the energy (relative value) consumed in the production of the cellulose nanofibers of each Example and Comparative Example as an integrated value of energy consumed in each step.

  As shown in Table 1 above, in Examples 1 to 6 in which rough fibrillation treatment using a chemical treatment and a refiner was performed as a pretreatment, the number of treatments in the refinement process was reduced to 3 times or less. I understand that. Moreover, in Examples 1-6, it turns out that the amount of energy consumption can be reduced significantly by being able to reduce the frequency | count of a refinement | miniaturization process with a large amount of energy consumed per time.

  According to the method for producing cellulose nanofibers of the present invention, the number of mechanical refining treatments can be reduced, and cellulose nanofibers can be produced with energy saving.

s1 Pretreatment process s2 Refinement process s1a Chemical treatment process s1b Coarse defibration process 10 Opposing collision type high-pressure homogenizer 11 Upstream flow path 12 Downstream flow path S1, S2, S3 Slurry X Merge section

Claims (5)

A method for producing cellulose nanofibers, comprising: a step of pretreating pulp fibers in a slurry; and a step of refining the pulp fibers in the slurry that have been pretreated by mechanical treatment,
The pretreatment step is
A process for subjecting the pulp fiber to a chemical treatment comprising an oxidation treatment, a hydrolysis treatment or a combination thereof, and a step of coarsely defibrating the pulp fiber with a refiner. Method.   The method for producing cellulose nanofiber according to claim 1, wherein the pretreatment step is performed in the order of the chemical treatment step and the rough defibrating step.   The manufacturing method of the cellulose nanofiber of Claim 1 or Claim 2 which performs the mechanical process in the said refinement | miniaturization process with a high pressure homogenizer.   The method for producing cellulose nanofiber according to claim 3, wherein the high-pressure homogenizer is a counter-collision type high-pressure homogenizer, and the slurry collides in a straight line in the miniaturization step. Chemical treatment means for subjecting pulp fibers in the slurry to chemical treatment comprising oxidation treatment, hydrolysis treatment or a combination thereof;
An apparatus for producing cellulose nanofibers, comprising: a refiner that coarsely defibrates pulp fibers in the slurry; and a high-pressure homogenizer that refines pulp fibers in the slurry.