JP2015231464A

JP2015231464A - Footwear for fishing

Info

Publication number: JP2015231464A
Application number: JP2014119349A
Authority: JP
Inventors: 宏森田; Hiroshi Morita; 細見　康雄; Yasuo Hosomi; 康雄細見; 優三石; Yu Mitsuishi
Original assignee: Shimano Inc
Current assignee: Shimano Inc
Priority date: 2014-06-10
Filing date: 2014-06-10
Publication date: 2015-12-24
Anticipated expiration: 2034-06-10
Also published as: JP6452964B2

Abstract

PROBLEM TO BE SOLVED: To provide footwear for fishing, excellent in durability and capable of being produced at low cost.SOLUTION: Footwear for fishing 10 comprises: an upper 12; a midsole 16; a sheet material 20; and an outsole 18. The upper 12 and the midsole 16 are integrally formed. The sheet material 20 is disposed between the midsole 16 and the outsole 18. The sheet material 20 and the midsole 16 are jointed by mechanical means. The outsole 18 is bonded to the sheet material 20 with an adhesive agent. The sheet material 20 is formed of a resin composition having transition resistance. The sheet material 20 does not bleed a plasticizer, and inhibits transition of the plasticizer to the adhesive agent. On the footwear 10, deterioration in adhesive strength due to transition of the plasticizer does not occur. The footwear 10 can achieve excellent durability without using a special adhesive agent.

Description

本発明は、釣り人に着用される履物に関する。 The present invention relates to footwear worn by anglers.

釣り用の履物は、通常、磯や川辺等の釣り場で使用される。この履物を着用した釣り人は、時に、水の中に踏み込んで、水底の岩の上を移動する。水に濡れた岩の上では、履物との間に水の膜が形成される。水の膜によって、履物と岩との摩擦力が低下する。水に濡れた岩の上は滑りやすい。釣り場の岩には、苔や海藻が付着していることが多い。水を含んだ苔や海藻の上は、さらに滑りやすい。安全上、滑りにくい設計がなされた履物が求められている。 Fishing footwear is usually used at fishing grounds such as carp and riverside. Anglers wearing these footwear sometimes step into the water and move on the rocks at the bottom. On a rock wet with water, a film of water is formed between the footwear. The water film reduces the frictional force between the footwear and the rock. It is slippery on rocks wet with water. Moss and seaweed are often attached to rocks at fishing grounds. The moss and seaweed containing water are more slippery. For safety, footwear designed to be slippery is required.

図３は、従来の釣り用履物２４が示された断面図である。この履物２４は、アッパー２６、ミッドソール２８及びアウトソール３０を備えている。アッパー２６及びミッドソール２８は、樹脂組成物からなる。アウトソール３０は、フェルト又は架橋ゴムからなる。アッパー２６とミッドソール２８とは、射出成形法にて一体に成形される。アウトソール３０は、接着剤によってミッドソール２８に接着される。 FIG. 3 is a cross-sectional view showing a conventional fishing footwear 24. The footwear 24 includes an upper 26, a midsole 28, and an outsole 30. The upper 26 and the midsole 28 are made of a resin composition. The outsole 30 is made of felt or crosslinked rubber. The upper 26 and the midsole 28 are integrally formed by an injection molding method. The outsole 30 is bonded to the midsole 28 with an adhesive.

アッパー２６及びミッドソール２８は、溶融した樹脂組成物が一つの金型に注入されることにより、同時に成形される。この履物の製造コストは、低い。一体成形されたアッパー２６及びミッドソール２８は、比較的低価格帯の履物に採用される。アッパーとミッドソールとが一体成形された釣り用履物が、特開２００９-２４７４３９号公報に開示されている。 The upper 26 and the midsole 28 are simultaneously molded by injecting a molten resin composition into one mold. The cost of manufacturing this footwear is low. The integrally formed upper 26 and midsole 28 are used for footwear in a relatively low price range. Japanese Unexamined Patent Publication No. 2009-247439 discloses a fishing footwear in which an upper and a midsole are integrally formed.

特開２００９-２４７４３９号公報JP 2009-247439 A

アッパー２６及びミッドソール２８の樹脂組成物には、物性向上のために、可塑剤が配合されている。可塑剤は、アッパー２６及びミッドソール２８の内部を移動して、その表面に滲出する。この現象は、ブリードと称される。アウトソール３０との接着面にブリードした可塑剤は、接着剤に移行する。接着剤は、可塑剤の移行によって可塑化される。この接着剤による接着強度は低い。接着強度の低下により、アウトソール３０の一部又は全部がミッドソール２８から剥離する。アウトソール３０が剥離した履物２４は、修理が必要である。この履物２４は、比較的短期間で廃棄される。長期間使用できる履物が要望されている。 A plasticizer is blended in the resin compositions of the upper 26 and the midsole 28 in order to improve physical properties. The plasticizer moves through the upper 26 and the midsole 28 and exudes to the surface thereof. This phenomenon is called bleeding. The plasticizer that bleeds on the adhesive surface with the outsole 30 moves to the adhesive. The adhesive is plasticized by the migration of the plasticizer. The adhesive strength by this adhesive is low. A part or all of the outsole 30 is peeled off from the midsole 28 due to a decrease in adhesive strength. The footwear 24 from which the outsole 30 has peeled needs repair. The footwear 24 is discarded in a relatively short time. There is a demand for footwear that can be used for a long time.

耐久性向上のために、可塑剤や接着剤の改質等の検討がなされているが、性能上及びコスト上の観点から、未だ満足できるものは得られていない。アウトソールとミッドソールとが糸等で縫合されることにより、可塑剤の移行を原因とする問題は回避し得る。しかし、縫合によってアウトソールが固定された履物が使用されるとき、アウトソールを縫合している糸が、地面と接する。この糸は、履物の繰り返しの使用によって、摩耗し、最終的には破断する。また、フェルトからなるアウトソールは、履物の使用により変形し、徐々に摩耗する。アウトソールの変形・摩耗によって縫合が緩む。糸が破断した履物や、縫合が緩んだ履物は、修理を要する。この履物の耐久性は、十分ではない。 In order to improve durability, studies such as modification of plasticizers and adhesives have been made, but satisfactory ones have not yet been obtained from the viewpoint of performance and cost. By causing the outsole and the midsole to be sewn together with a thread or the like, problems caused by the migration of the plasticizer can be avoided. However, when footwear having the outsole fixed by stitching is used, the thread stitching the outsole contacts the ground. The yarn wears and eventually breaks with repeated use of footwear. In addition, the felt outsole is deformed by the use of footwear and gradually wears. Sutures loosen due to deformation and wear of the outsole. Footwear with broken threads or footwear with loose sutures requires repair. The durability of this footwear is not sufficient.

本発明の目的は、耐久性に優れ、かつ低コストで容易に製造可能な釣り用履物の提供である。 An object of the present invention is to provide fishing footwear that is excellent in durability and can be easily manufactured at low cost.

本発明に係る釣り用履物は、アッパーと、このアッパーと一体に成形されたミッドソールと、このミッドソールに積層されたアウトソールとを備えている。この履物では、ミッドソールとアウトソールとの間に、耐移行性樹脂組成物からなるシート材が配置されている。シート材とミッドソールとは、機械的手段によって接合されている。アウトソールは、シート材に接着剤で接着されている。 The fishing footwear according to the present invention includes an upper, a midsole formed integrally with the upper, and an outsole laminated on the midsole. In this footwear, a sheet material made of a migration-resistant resin composition is disposed between the midsole and the outsole. The sheet material and the midsole are joined by mechanical means. The outsole is bonded to the sheet material with an adhesive.

好ましくは、耐移行性樹脂組成物の基材樹脂は、エチレン−酢酸ビニル系樹脂である。 Preferably, the base resin of the migration resistant resin composition is an ethylene-vinyl acetate resin.

好ましくは、このシート材は、耐移行性樹脂組成物の発泡体である。 Preferably, the sheet material is a foam of a migration resistant resin composition.

本発明に係る釣り用履物では、ミッドソールとアウトソールとの間に、耐移行性樹脂組成物からなるシート材を備えている。このシート材は、可塑剤をブリードしない。このシート材は、ミッドソールからブリードした可塑剤の移行を阻止する。この履物では、可塑剤の移行による接着強度の低下が生じない。この履物では、特殊な接着剤等を使用することなく、優れた耐久性が達成される。この履物の製造コストは低い。 The fishing footwear according to the present invention includes a sheet material made of a migration-resistant resin composition between the midsole and the outsole. This sheet material does not bleed the plasticizer. This sheet material prevents migration of the plasticizer bleed from the midsole. In this footwear, the adhesive strength does not decrease due to the migration of the plasticizer. In this footwear, excellent durability is achieved without using a special adhesive or the like. The cost of manufacturing this footwear is low.

図１は、本発明の一実施形態に係る釣り用履物が示された断面図である。FIG. 1 is a cross-sectional view illustrating a fishing footwear according to an embodiment of the present invention. 図２は、図１のII−II線に沿った断面図である。FIG. 2 is a cross-sectional view taken along line II-II in FIG. 図３は、従来の釣り用履物が示された断面図である。FIG. 3 is a cross-sectional view showing a conventional fishing footwear.

以下、適宜図面が参照されつつ、好ましい実施形態に基づいて本発明が詳細に説明される。この実施形態に基づいて本発明が限定的に解釈されるべきではない。 Hereinafter, the present invention will be described in detail based on preferred embodiments with appropriate reference to the drawings. The present invention should not be construed in a limited manner based on this embodiment.

図１は、本発明の一実施形態に係る釣り用履物１０の鉛直方向の断面図である。この履物１０は、アッパー１２、インソール１４、ミッドソール１６、シート材２０及びアウトソール１８を備えている。図示されていないが、アッパー１２の内面には、裏地が積層されている。インソール１４は、アッパー１２に収容され、ミッドソール１６に載置されている。インソール１４は、合成樹脂又はゴムからなる発泡体である。この実施形態では、アウトソール１８が複数のスパイク２２を備えている。アウトソール１８がスパイク２２を備えなくてもよい。 FIG. 1 is a vertical sectional view of a fishing footwear 10 according to an embodiment of the present invention. The footwear 10 includes an upper 12, an insole 14, a midsole 16, a sheet material 20, and an outsole 18. Although not shown, a lining is laminated on the inner surface of the upper 12. The insole 14 is accommodated in the upper 12 and placed on the midsole 16. The insole 14 is a foam made of synthetic resin or rubber. In this embodiment, the outsole 18 includes a plurality of spikes 22. The outsole 18 may not include the spike 22.

本発明に係る釣り用履物１０では、アッパー１２とミッドソール１６とが一体に成形されている。アッパー１２及びミッドソール１６の成形には、射出成形法、圧縮成形法等既知の方法が採用される。アッパー１２及びミッドソール１６の形状は、機能性、デザイン性等の観点から適宜設計される。 In the fishing footwear 10 according to the present invention, the upper 12 and the midsole 16 are integrally formed. For the molding of the upper 12 and the midsole 16, known methods such as an injection molding method and a compression molding method are employed. The shapes of the upper 12 and the midsole 16 are appropriately designed from the viewpoints of functionality, design and the like.

アッパー１２及びミッドソール１６は、樹脂組成物からなる。好ましい基材樹脂は、熱可塑性樹脂である。熱可塑性樹脂として、例えば、塩化ビニル系樹脂、アクリル酸エステル系樹脂、ウレタン系エラストマー、オレフィン系エラストマー等が挙げられる。柔軟性及び耐水性に優れた塩化ビニル系樹脂が好適に用いられる。塩化ビニル系樹脂の例として、ポリ塩化ビニル（ＰＶＣ）、エチレン−塩化ビニル共重合体、塩化ビニル−酢酸ビニル共重合体、塩化ビニリデン、塩化ビニル−アクリル酸メチル共重合体等が挙げられる。アッパー１２及びミッドソール１６が、既知のゴム組成物の架橋体から成形されてもよい。２種以上の樹脂がブレンドされて配合されてもよい。この実施形態において、アッパー１２及びミッドソール１６の樹脂組成物には、基材樹脂としてＰＶＣが配合されている。ＰＶＣは、成形加工が容易でかつ安価である。 The upper 12 and the midsole 16 are made of a resin composition. A preferred base resin is a thermoplastic resin. Examples of the thermoplastic resin include a vinyl chloride resin, an acrylic ester resin, a urethane elastomer, and an olefin elastomer. A vinyl chloride resin excellent in flexibility and water resistance is preferably used. Examples of the vinyl chloride resin include polyvinyl chloride (PVC), ethylene-vinyl chloride copolymer, vinyl chloride-vinyl acetate copolymer, vinylidene chloride, vinyl chloride-methyl acrylate copolymer, and the like. The upper 12 and the midsole 16 may be formed from a crosslinked body of a known rubber composition. Two or more kinds of resins may be blended and blended. In this embodiment, PVC is blended in the resin composition of the upper 12 and the midsole 16 as a base resin. PVC is easy to mold and inexpensive.

アッパー１２及びミッドソール１６の樹脂組成物は、可塑剤を含む。可塑剤は、樹脂組成物の成形加工性及び柔軟性を向上する。フタル酸ジオクチル、フタル酸ジブチル、フタル酸ビス（２−エチルヘキシル）、フタル酸ジヘプチル、フタル酸ジイソデシル、フタル酸トリデシル等のフタル酸系可塑剤、リン酸トリフェニル、リン酸トリクレシル等のリン酸系可塑剤、アジピン酸ジオクチル、アジピン酸ジイソノニル等のアジピン酸系可塑剤、トリメリット酸トリオクチル、トリメリット酸トリ２−エチルヘキシル等のトリメリット酸系可塑剤及びポリエステル系可塑剤が例示される。基材樹脂との相溶性が良く、可塑化効率の高いフタル酸系可塑剤が好ましい。複数の可塑剤がブレンドされて配合されてもよい。 The resin composition of the upper 12 and the midsole 16 includes a plasticizer. The plasticizer improves the moldability and flexibility of the resin composition. Phthalic acid plasticizers such as dioctyl phthalate, dibutyl phthalate, bis (2-ethylhexyl) phthalate, diheptyl phthalate, diisodecyl phthalate and tridecyl phthalate, and phosphoric acid plastics such as triphenyl phosphate and tricresyl phosphate And adipic acid plasticizers such as dioctyl adipate and diisononyl adipate, trimellitic plasticizers such as trioctyl trimellitic acid and tri-2-ethylhexyl trimellitic acid, and polyester plasticizers. A phthalic acid plasticizer having good compatibility with the base resin and high plasticization efficiency is preferred. A plurality of plasticizers may be blended and blended.

樹脂組成物に配合される可塑剤の量は、基材樹脂及び可塑剤の種類に応じて、適宜調整される。基材樹脂がＰＶＣの場合に、好ましい可塑剤はフタル酸ジオクチルである。好ましくは、１００質量部のＰＶＣに対して、２０質量部以上５０質量部以下のフタル酸ジオクチルが配合される。 The amount of the plasticizer blended in the resin composition is appropriately adjusted according to the types of the base resin and the plasticizer. When the base resin is PVC, the preferred plasticizer is dioctyl phthalate. Preferably, 20 parts by weight or more and 50 parts by weight or less of dioctyl phthalate is blended with 100 parts by weight of PVC.

アッパー１２及びミッドソール１６の樹脂組成物に、着色剤、安定剤、充填剤、滑剤、難燃剤等の添加剤が配合されてもよい。 Additives such as a colorant, a stabilizer, a filler, a lubricant, and a flame retardant may be blended in the resin composition of the upper 12 and the midsole 16.

図２は、図１のII−II線に沿った断面図である。図２には、履物１０の一部が示されている。図示される通り、シート材２０は、ほぼ均一な厚みを有する板状である。この実施形態では、シート材２０が、糸２３によって、ミッドソール１６に接合されている。図示されていないが、シート材２０とミッドソール１６とは、その外周に沿って、糸２３により縫合されている。シート材２０とミッドソール１６とが、ピン、鋲等の、他の機械的手段によって固定されてもよい。機械的手段による接合と、接着剤による接着とが併用されてもよい。 FIG. 2 is a cross-sectional view taken along line II-II in FIG. A part of the footwear 10 is shown in FIG. As illustrated, the sheet material 20 has a plate shape having a substantially uniform thickness. In this embodiment, the sheet material 20 is joined to the midsole 16 by a thread 23. Although not shown, the sheet material 20 and the midsole 16 are stitched together by the thread 23 along the outer periphery thereof. The sheet material 20 and the midsole 16 may be fixed by other mechanical means such as a pin or a heel. Bonding by mechanical means and bonding by an adhesive may be used in combination.

この履物１０が使用されるとき、糸２３と地面とは直接は接触しない。この履物１０では、地面との接触による糸２３の摩耗・破断は起こらない。このシート材２０の使用による変形・摩耗の程度は、小さい。この履物１０では、シート材２０の変形・摩耗による縫合の緩みは、少ない。 When the footwear 10 is used, the thread 23 and the ground are not in direct contact. In the footwear 10, the thread 23 is not worn or broken by contact with the ground. The degree of deformation and wear due to the use of the sheet material 20 is small. In the footwear 10, looseness of stitching due to deformation and wear of the sheet material 20 is small.

シート材２０は、耐移行性樹脂組成物からなる。この樹脂組成物からなるシート材２０の内部では、可塑剤の移動が抑制される。この樹脂組成物に可塑剤が配合された場合、可塑剤は、シート材２０の内部に保持される。このシート材２０では、可塑剤のブリードが生じない。ミッドソール１６が可塑剤を含む樹脂組成物から成形された場合、ミッドソール１６からブリードした可塑剤は、シート材２０との境界面に留まり、シート材２０へは移行しない。本願明細書において、耐移行性樹脂組成物とは、可塑剤のブリード及び移行を生じない樹脂組成物を意味する。 The sheet material 20 is made of a migration resistant resin composition. The movement of the plasticizer is suppressed inside the sheet material 20 made of this resin composition. When a plasticizer is blended with this resin composition, the plasticizer is held inside the sheet material 20. In this sheet material 20, no plasticizer bleed occurs. When the midsole 16 is molded from a resin composition containing a plasticizer, the plasticizer bleed from the midsole 16 stays at the boundary surface with the sheet material 20 and does not migrate to the sheet material 20. In the present specification, the migration-resistant resin composition means a resin composition that does not cause plasticizer bleeding and migration.

前述した通り、シート材２０とミッドソール１６とは機械的手段によって接合されている。ミッドソール１６に配合された可塑剤がブリードしてシート材２０との接合部分に達したとしても、機械的手段による接合強度は低下しない。この履物１０では、シート材２０とミッドソール１６との接合が、長期間維持されうる。 As described above, the sheet material 20 and the midsole 16 are joined by mechanical means. Even if the plasticizer blended in the midsole 16 bleeds and reaches the joint portion with the sheet material 20, the joint strength by mechanical means does not decrease. In the footwear 10, the bonding between the sheet material 20 and the midsole 16 can be maintained for a long time.

耐移行性樹脂組成物の基材樹脂として、エチレン−酢酸ビニル系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂等が例示される。成形加工が容易であるとの観点から好ましい基材樹脂は、エチレン−酢酸ビニル系樹脂である。典型的なエチレン−酢酸ビニル系樹脂は、エチレンモノマーと、酢酸ビニルモノマーとのラジカル共重合によって合成されるエチレン−酢酸ビニル共重合体である。 Examples of the base resin of the migration resistant resin composition include ethylene-vinyl acetate resins, polyolefin resins, polyester resins and the like. A preferable base resin from the viewpoint of easy molding is an ethylene-vinyl acetate resin. A typical ethylene-vinyl acetate resin is an ethylene-vinyl acetate copolymer synthesized by radical copolymerization of an ethylene monomer and a vinyl acetate monomer.

エチレン−酢酸ビニル共重合体中の酢酸ビニル含量は、５質量％以上５０質量％以下が好ましい。酢酸ビニル含量が５質量％以上５０質量％以下のエチレン−酢酸ビニル共重合体を基材樹脂とする樹脂組成物には、可塑剤の配合を要さない。成形加工性の観点から、より好ましい酢酸ビニル含量は、１０質量％以上である。柔軟性及び弾性に優れるの観点から、より好ましい酢酸ビニル含量は、４０質量％以下である。エチレン−酢酸ビニル共重合体中の酢酸ビニル含量は、ＪＩＳＫ７１９２に準拠した方法にて測定される。 The vinyl acetate content in the ethylene-vinyl acetate copolymer is preferably 5% by mass or more and 50% by mass or less. The resin composition having an ethylene-vinyl acetate copolymer having a vinyl acetate content of 5% by mass or more and 50% by mass or less as a base resin does not require a plasticizer. From the viewpoint of moldability, a more preferable vinyl acetate content is 10% by mass or more. From the viewpoint of excellent flexibility and elasticity, a more preferable vinyl acetate content is 40% by mass or less. The vinyl acetate content in the ethylene-vinyl acetate copolymer is measured by a method based on JIS K7192.

本発明の目的が達成される限り、エチレン−酢酸ビニル共重合体を構成するアセチル基の一部がけん化されてもよい。エチレン−酢酸ビニル共重合体が、他の不飽和カルボン酸又はその誘導体で変性されたものであってもよい。他の不飽和カルボン酸の例として、アクリル酸、メタクリル酸、マレイン酸等が挙げられる。不飽和カルボン酸誘導体として、アクリル酸エステル、メタクリル酸エステル、マレイン酸エステル、無水マレイン酸等が例示される。 As long as the object of the present invention is achieved, a part of acetyl groups constituting the ethylene-vinyl acetate copolymer may be saponified. The ethylene-vinyl acetate copolymer may be modified with another unsaturated carboxylic acid or a derivative thereof. Examples of other unsaturated carboxylic acids include acrylic acid, methacrylic acid, maleic acid and the like. Examples of the unsaturated carboxylic acid derivative include acrylic acid ester, methacrylic acid ester, maleic acid ester, and maleic anhydride.

エチレン−酢酸ビニル系樹脂の具体例として、三井・デュポンポリケミカルの商品名「エバフレックス」シリーズ、日本合成化学工業の商品名「ソアレックス」シリーズ、日本ポリエチレンの商品名「ノバテックＥＶＡ」シリーズ等が例示される。 Specific examples of ethylene-vinyl acetate resins include Mitsui / DuPont Polychemical product name “Evaflex” series, Nippon Synthetic Chemical product name “Soarex” series, Nippon Polyethylene product name “Novatech EVA” series, etc. Illustrated.

本発明の効果を損なわない範囲で、耐移行性樹脂組成物には、酸化防止剤、着色剤、安定剤、難燃剤、充填剤、耐電防止剤等の添加剤が配合される。この樹脂組成物が、基材樹脂と相溶可能な他の樹脂を含んでもよい。エチレン−酢酸ビニル系樹脂が基材樹脂とされた場合、これと相溶可能な樹脂として、エチレン−（メタ）アクリル酸共重合体、エチレン−（メタ）アクリル酸エステル共重合体、エチレン−ビニルアルコール樹脂等が例示される。 To the extent that the effects of the present invention are not impaired, additives such as an antioxidant, a colorant, a stabilizer, a flame retardant, a filler, and an antistatic agent are blended in the migration resistant resin composition. This resin composition may contain other resins that are compatible with the base resin. When an ethylene-vinyl acetate resin is used as a base resin, as a resin compatible with the base resin, ethylene- (meth) acrylic acid copolymer, ethylene- (meth) acrylic acid ester copolymer, ethylene-vinyl Examples include alcohol resins.

シート材２０が、耐移行性樹脂組成物の発泡体として成形されてもよい。発泡体からなるシート材２０は、軽量である。このシート材２０は、履物１０の衝撃吸収性及び断熱性の向上にも寄与する。 The sheet material 20 may be molded as a foam of the migration resistant resin composition. The sheet material 20 made of foam is lightweight. This sheet material 20 also contributes to an improvement in the shock absorption and heat insulation properties of the footwear 10.

発泡体からなるシート材２０は、既知の方法により製造されうる。例えば、発泡剤が配合された樹脂組成物が金型内で加熱されることによって、発泡体からなるシート材２０が製造される。 The sheet material 20 made of a foam can be manufactured by a known method. For example, a sheet material 20 made of a foam is manufactured by heating a resin composition containing a foaming agent in a mold.

発泡剤の種類は特に限定されないが、アゾジカルボンアミド、アゾビスイソブチロニトリルのようなアゾ化合物、Ｎ，Ｎ−ジニトロソペンタメチレンテトラミンのようなニトロソ化合物、ベンゼンスルホニルヒドラジド、４，４−オキシビス（ベンゼンスルホニルヒドラジド）のようなヒドラジド化合物、アジド化合物、トリアゾール化合物、重炭酸ナトリウム、重炭酸アンモニウムのような無機化合物等が例示される。シート材２０の樹脂組成物に、架橋剤、架橋助剤、発泡助剤、発泡抑制剤等が適宜配合されてもよい。 The type of blowing agent is not particularly limited, but azo compounds such as azodicarbonamide and azobisisobutyronitrile, nitroso compounds such as N, N-dinitrosopentamethylenetetramine, benzenesulfonylhydrazide, and 4,4-oxybis Examples thereof include hydrazide compounds such as (benzenesulfonylhydrazide), azide compounds, triazole compounds, inorganic compounds such as sodium bicarbonate and ammonium bicarbonate. In the resin composition of the sheet material 20, a crosslinking agent, a crosslinking aid, a foaming aid, a foaming inhibitor, and the like may be appropriately blended.

この履物１０において、シート材２０の厚みは、１．０ｍｍ以上２０ｍｍ以下である。可塑剤の移行が抑制されるとの観点からより好ましい厚みは、２．０ｍｍ以上である。軽量化及びコスト低減の観点から、より好ましい厚みは、１５ｍｍ以下である。 In the footwear 10, the thickness of the sheet material 20 is 1.0 mm or more and 20 mm or less. A more preferable thickness is 2.0 mm or more from the viewpoint that the migration of the plasticizer is suppressed. From the viewpoint of weight reduction and cost reduction, a more preferable thickness is 15 mm or less.

この実施形態では、アウトソール１８はフェルトからなる。フェルトは、ポリオレフィン繊維、ポリエステル繊維、ポリアクリル繊維等が加圧・圧縮されることによって得られる。フェルトは、吸水性に優れ、かつ柔軟である。フェルトからなるアウトソール１８は、凹凸のある地面に追従して変形する。このアウトソール１８では、水に濡れた岩の上でも、履物１０との間に水の膜が形成されない。このアウトソール１８を備えた履物１０は、釣り場での防滑性に優れる。 In this embodiment, the outsole 18 is made of felt. The felt is obtained by pressing and compressing polyolefin fiber, polyester fiber, polyacrylic fiber, or the like. The felt is excellent in water absorption and flexible. The outsole 18 made of felt deforms following the uneven ground. In the outsole 18, no water film is formed between the outsole 18 and the footwear 10 even on a rock wet with water. The footwear 10 provided with the outsole 18 is excellent in slip resistance at a fishing spot.

図示される通り、この実施形態では、アウトソール１８が複数のスパイク２２を備えている。スパイク２２の材質は、金属又は樹脂である。スパイク２２によって、フェルトからなるアウトソール１８の摩耗が低減される。フェルトからなるアウトソール１８がスパイク２２を備えることにより、履物１０の耐久性が向上する。 As shown, in this embodiment, the outsole 18 includes a plurality of spikes 22. The material of the spike 22 is metal or resin. The spike 22 reduces the wear of the felt outsole 18. Since the outsole 18 made of felt includes the spikes 22, the durability of the footwear 10 is improved.

本発明の目的が達成される限り、履物１０が、ゴム又は樹脂からなるアウトソール１８を備えてもよい。アウトソール１８が、ゴム又は樹脂の発泡体として成形されてもよい。 As long as the object of the present invention is achieved, the footwear 10 may include an outsole 18 made of rubber or resin. The outsole 18 may be molded as a foam of rubber or resin.

本発明に係る履物１０では、アウトソール１８とシート材２０との間に塗布された接着剤によって、アウトソール１８がシート材２０に固定される。接着剤は、アウトソール１８及びシート材２０の種類に応じて適宜選択される。耐水性及び柔軟性の観点から好ましい接着剤は、ゴム系接着剤、アクリル樹脂系接着剤及びポリウレタン系接着剤である。初期接着強度が高く、安価なゴム系接着剤が特に好ましい。ゴム系接着剤として、クロロプレンゴム系接着剤、ニトリルゴム系接着剤、スチレン・ブタジエンゴム系接着剤及び天然ゴム系接着剤が例示される。フェルトからなるアウトソール１８と、樹脂組成物からなるシート材２０との接着には、クロロプレンゴム系接着剤が好適に用いられる。 In the footwear 10 according to the present invention, the outsole 18 is fixed to the sheet material 20 by an adhesive applied between the outsole 18 and the sheet material 20. The adhesive is appropriately selected according to the types of the outsole 18 and the sheet material 20. Preferred adhesives from the viewpoint of water resistance and flexibility are rubber adhesives, acrylic resin adhesives, and polyurethane adhesives. A rubber adhesive that has a high initial adhesive strength and is inexpensive is particularly preferable. Examples of rubber adhesives include chloroprene rubber adhesives, nitrile rubber adhesives, styrene / butadiene rubber adhesives, and natural rubber adhesives. A chloroprene rubber-based adhesive is suitably used for bonding the outsole 18 made of felt and the sheet material 20 made of a resin composition.

ゴム系接着剤は、通常、可塑剤の移行によって可塑化される。可塑化されたゴム系接着剤による接着強度は低い。本発明に係る履物１０では、接着剤が、耐移行性樹脂組成物からなるシート材２０と、アウトソール１８とに接している。この実施形態では、アウトソール１８はフェルトからなる。耐移行性樹脂組成物からなるシート材２０及びフェルトからなるアウトソール１８は、可塑剤をブリードしない。この履物１０では、耐移行性樹脂組成物からなるシート材２０によって、接着剤が、ミッドソール１６と隔てられている。この履物１０では、シート材２０が、ミッドソール１６に含まれる可塑剤の接着剤への移行を阻止する。本発明に係る履物１０では、ゴム系接着材を使用した場合でも、可塑剤の移行による接着強度の低下が生じない。この履物１０では、特殊な接着剤等を使用することなく、長期間、アウトソール１８とシート材２０との強固な固定が維持される。この履物１０は、耐久性に優れる。 Rubber adhesives are usually plasticized by plasticizer migration. The adhesive strength by the plasticized rubber adhesive is low. In the footwear 10 according to the present invention, the adhesive is in contact with the sheet material 20 made of the migration-resistant resin composition and the outsole 18. In this embodiment, the outsole 18 is made of felt. The sheet material 20 made of the migration-resistant resin composition and the outsole 18 made of felt do not bleed the plasticizer. In the footwear 10, the adhesive is separated from the midsole 16 by a sheet material 20 made of a migration-resistant resin composition. In the footwear 10, the sheet material 20 prevents the plasticizer included in the midsole 16 from shifting to the adhesive. In the footwear 10 according to the present invention, even when a rubber-based adhesive is used, the adhesive strength does not decrease due to the migration of the plasticizer. In the footwear 10, strong fixation between the outsole 18 and the sheet material 20 is maintained for a long time without using a special adhesive or the like. The footwear 10 is excellent in durability.

本発明に係る釣り用の履物は、短靴、長靴、胴長靴等の形状に成形可能であり、釣り場の多様な環境に対応することができる。 The footwear for fishing according to the present invention can be formed into a shape of a short boot, a long boot, a trunk boot, and the like, and can correspond to various environments of a fishing spot.

１０、２４・・・釣り用履物
１２、２６・・・アッパー
１４・・・インソール
１６、２８・・・ミッドソール
１８、３０・・・アウトソール
２０・・・シート材
２２・・・スパイク
２３・・・糸
10, 24 ... Footwear 12, 26 ... Upper 14 ... Insole 16,28 ... Midsole 18,30 ... Outsole 20 ... Seat material 22 ... Spike 23 ··yarn

Claims

It has an upper, a midsole molded integrally with the upper, and an outsole laminated on the midsole.
Between the midsole and the outsole, a sheet material made of a migration-resistant resin composition is disposed,
The sheet material is joined to the midsole by mechanical means;
Fishing footwear wherein the outsole is bonded to the sheet material with an adhesive.

The footwear for fishing according to claim 1, wherein the base resin of the migration-resistant resin composition is an ethylene-vinyl acetate resin.

The fishing footwear according to claim 1 or 2, wherein the sheet material is a foam of a migration-resistant resin composition.