JP2015143179A - Zirconia sintered compact and use thereof - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a zirconia sintered compact which has two or more different color hues, has sensuousness that shows an image of high-quality, and is high in intensity enough to be used as a member.SOLUTION: A zirconia sintered compact comprises a first zirconia sintered compact and a second zirconia sintered compact, wherein the first zirconia sintered compact is the one containing aluminum oxide, the second zirconia sintered compact is the one containing a spinel oxide, a grain boundary is formed between the first zirconia sintered compact and the second zirconia sintered compact, and no gap is formed or color bleeding does not occur on the grain boundary.

Description

  The present invention relates to a zirconia sintered body in which zirconia having different colors are joined by sintering. More specifically, the present invention relates to a zirconia sintered body in which zirconia having different colors are joined by sintering, and one zirconia forms a pattern on the other zirconia.

  In addition to having high toughness and high strength, and having a glossy feeling, the zirconia sintered body can be a member that exhibits a high-class feeling. Therefore, the zirconia sintered body is used as various members such as high-quality watch parts and ornaments. Despite being a high-quality member, the zirconia sintered body has a single color tone. Further, zirconia having different color tones usually have different sintering behaviors. Therefore, when zirconia having different colors was sintered at the same time, cracks, cracks, strains, etc. occurred, and it was impossible to obtain a zirconia sintered body having no defects. Therefore, it was not possible to obtain a zirconia sintered body having two or more different color tones and a member made of the same.

  In order to make a member having two or more different color tones using a zirconia sintered body, a combination of a zirconia sintered body and a material other than the zirconia sintered body and having a color tone different from that of the zirconia sintered body In other words, for example, Patent Documents 1 to 3 have been studied. However, these members are greatly different in texture between materials. For this reason, the obtained member exhibits a design property different from the design property of a member made only of ceramics, and particularly impairs the high-class feeling peculiar to a zirconia sintered body.

  In addition, a ceramic joined body in which two or more ceramics are joined via an intermediate layer such as an adhesive is conventionally known. However, the ceramic joined body is likely to break starting from the intermediate layer. Therefore, in a zirconia sintered body characterized by high toughness and high strength, it is not preferable to form a bonded body through an intermediate layer.

  On the other hand, Patent Document 4 reports a zirconia sintered body obtained by sintering two zirconia molded bodies having different color tones. Patent Document 4 discloses a zirconia sintered body obtained by sintering a zirconia powder compact containing FeCrNi spinel and a zirconia powder compact containing CoAl.

JP 2011-191321 A Japanese Patent Laid-Open No. 08-081255 Japanese Patent No. 4370361 Japanese Patent Laid-Open No. 08-081255

  The sintered body disclosed in Patent Document 4 is made of a zirconia sintered body, and there is no difference in texture between members. However, the sintered body has a “color transition zone” that can be visually observed between zirconia sintered bodies having different color tones. Such a color transition band is visually recognized as “color blur”. The boundary between zirconia sintered bodies becomes unclear due to color bleeding. As a result, the portion where the zirconia sintered body and the zirconia sintered body are in contact, particularly the pattern formed by one of the zirconia sintered bodies, is unclear. Such an unclear pattern gives an impression that further impairs the high-class feeling of the zirconia sintered body.

  Patent Document 4 also discloses a zirconia sintered body having no color transition zone. However, the zirconia sintered body has a gap at the boundary between the zirconia sintered bodies because sintering does not proceed sufficiently. That is, in the zirconia sintered body having no color transition zone in Patent Document 4, the color is not shifted due to the gap. The said clearance gap is visually recognized as a color tone different from any zirconia sintered compact, and reduces the aesthetics as a member. In addition to this, a gap existing at the boundary between the zirconia sintered bodies becomes a starting point of the fracture. Therefore, such a zirconia sintered body has remarkably low mechanical strength and is easily broken as a member.

  Furthermore, since the sintered body disclosed in Patent Document 4 needs to be enlarged to such an extent that color bleeding and gaps do not affect the aesthetics of the member, it cannot be a sintered body having a fine pattern. .

  The present invention solves these problems, is a zirconia sintered body having two or more different color tones, has a high-quality aesthetic, and has sufficient strength to be used as a member It aims at providing a sintered compact. In particular, the present invention is a multi-colored zirconia sintered body composed of a zirconia sintered body exhibiting white color and a zirconia sintered body exhibiting black or other dark color, and has an aesthetic property exhibiting a high-class feeling, and Another object is to provide a zirconia sintered body having sufficient strength for use as a member.

  The present inventors are a zirconia sintered body having two or more different color tones, particularly a zirconia sintered body having two or more different color tones, wherein one zirconia is formed as a pattern on the surface of the other zirconia. A zirconia sintered body was examined.

  As a result, it was found that a zirconia sintered body having two or more different colors can be obtained by simultaneously sintering a zirconia molded body containing spinel oxide and a zirconia molded body containing other than spinel oxide. . Furthermore, such a zirconia sintered body is found that the zirconia sintered body and the zirconia sintered body form a grain boundary as a joint surface thereof, and that the interface does not have color bleeding and gaps, The present invention has been completed.

  That is, the present invention is a zirconia sintered body including a first zirconia sintered body and a second zirconia sintered body, and the first zirconia sintered body is a zirconia sintered body containing aluminum oxide. The second zirconia sintered body is a zirconia sintered body containing a spinel oxide, the first zirconia sintered body and the second zirconia sintered body form a grain boundary, and the grain A zirconia sintered body characterized in that the boundary does not have gaps and color bleeding.

  Hereinafter, the zirconia sintered body of the present invention will be described.

  The zirconia sintered body of the present invention is a zirconia sintered body including a first zirconia sintered body and a second zirconia sintered body (hereinafter also referred to as “multicolor zirconia sintered body”). The first zirconia sintered body (hereinafter also referred to as “light-colored sintered body”) and the second zirconia sintered body (hereinafter also referred to as “dark-colored sintered body”) have different color tones. It is a sintered body. The multicolored zirconia sintered body of the present invention includes a dark-colored sintered body containing spinel oxide as a colorant and a light-colored sintered body containing other than spinel oxide as a colorant, preferably substantially. By being composed of the dark color sintered body and the light color sintered body, it is possible to obtain a member having only a zirconia sintered body for the first time and having a high-quality feeling.

  In the multicolor zirconia sintered body of the present invention, the light-colored sintered body and the dark-colored sintered body form a grain boundary, whereby both the sintered bodies are joined. Furthermore, the light-colored sintered body and the dark-colored sintered body have grain boundaries (hereinafter also referred to as “interfaces”) formed by sintering. Since the interface is sintered, the interface becomes a joint surface having no defects such as cracks and strains. As a result, the interface does not become the starting point of fracture. Therefore, the multicolor zirconia sintered body of the present invention can also be used as a member that requires the original strength of the zirconia sintered body.

  By sintering the light-colored sintered body and the dark-colored sintered body, they become one continuous zirconia sintered body. Therefore, the multicolor zirconia sintered body of the present invention has a light-colored sintered body in addition to a structure in which the crystal particles of the light-colored sintered body are sintered and a structure in which the crystal particles of the dark-colored sintered body are sintered together. And a grain structure having a crystal grain structure in which the crystal grains of the dark-colored sintered body are sintered.

  Therefore, the multicolor zirconia sintered body of the present invention is different from a zirconia composite or zirconia joined body which does not have such a particle structure. A zirconia composite body or a zirconia joined body has only a structure in which light-colored sintered body crystal particles are sintered and a structure in which dark-colored sintered body crystal particles are sintered. Examples of the zirconia composite include a zirconia composite obtained by separately sintering a light-colored sintered body and a dark-colored sintered body and then combining them. Examples of the zirconia joined body include a zirconia joined body in which a light-colored sintered body and a dark-colored sintered body are integrated through an adhesive layer and other intermediate layers.

  The interface in the present invention can be confirmed from an electron image obtained by observation with an electron microscope such as a scanning electron microscope (hereinafter referred to as “SEM”) or observation with an optical microscope. That is, the light color sintered body and the dark color sintered body have different color tones. Therefore, in the optical microscope observation, the interface can be confirmed with the portion where the color tone is changed. Further, the light color sintered body and the dark color sintered body contain different coloring components. Since the electronic image exhibits a different color tone due to the difference in the coloring components, the interface can be confirmed with a portion where the color tone is changed in the electronic image.

  FIG. 1 is an optical micrograph showing an example of the multicolor zirconia sintered body of the present invention. In FIG. 1, the area (1) is a light-colored sintered body, and the area (2) is a dark-colored sintered body. From FIG. 1, the interface (3) which is the boundary part of the area | region of (1) and (2) can be confirmed from the difference in the color tone in an optical micrograph (for example, the broken-line circle part in FIG. 1).

  Moreover, FIG. 2 is a figure which shows an example of the secondary electron image obtained by SEM observation of the multicolor zirconia sintered compact of this invention. In FIG. 2, the area (1) is a light-colored sintered body, and the area (2) is a dark-colored sintered body. From FIG. 2, the interface (3), which is the boundary between the areas (1) and (2), can be confirmed from the color tone difference in the reflected electron image (for example, the arrow in FIG. 2).

  In the multicolor zirconia sintered body of the present invention, the light-colored sintered body and the dark-colored sintered body are joined by sintering. Furthermore, in either the light-colored sintered body or the dark-colored sintered body, one zirconia sintered body has a concave portion, and the other zirconia sintered body has a convex portion, and the concave portion and the convex portion are combined. As described above, the light-colored sintered body and the dark-colored sintered body are preferably laminated and joined. Such a combination of zirconia sintered bodies can form a pattern on the surface of the multicolor zirconia sintered body of the present invention as a pattern without steps or gaps.

  In the multicolor zirconia sintered body of the present invention, the light-colored sintered body and the dark-colored sintered body have an interface, and the interface has no gap. Thereby, the multicolored zirconia sintered body of the present invention exhibits aesthetics created only from the zirconia sintered body, and the multicolored zirconia sintered body of the present invention can be used as a member that gives a more luxurious impression. it can. In addition, since there is no gap at the interface, it is difficult for the fracture starting from the interface to occur, so that the original mechanical properties of the zirconia sintered body are not impaired.

  In the present invention, the gap is a gap formed at and near the interface that is a joint surface between the light-colored sintered body and the dark-colored sintered body, and is obtained by optical microscope observation or SEM observation at a magnification of 500 times or less. It can be confirmed by an electronic image of at least one of a secondary electron image and a reflected electron image (hereinafter collectively referred to as “electron image”).

  The multicolored zirconia sintered body of the present invention preferably does not contain fine voids such as voids that can be confirmed by secondary electron images or reflected electron images obtained by SEM observation at a magnification exceeding 500 times. However, when the multicolored zirconia sintered body of the present invention is used as various members, it is observed in an electronic image obtained by SEM observation or transmission electron microscope (hereinafter referred to as “TEM”) observation with a magnification exceeding 500 times. It may have a void. Such fine voids do not practically affect the aesthetics of the member.

  In FIG. 2, the interface (3), which is the boundary between the areas (1) and (2), can be confirmed from the difference in color tone in the secondary electron image (for example, the arrow in FIG. 2). Furthermore, the interface confirmed in FIG. 2 is a continuous interface, and no void is confirmed in the interface. On the other hand, FIG. 3 is a view showing a reflected electron image obtained by SEM observation of a multicolor zirconia sintered body having a gap at the interface at a magnification of 500 times. In FIG. 3, (1) is a light-colored sintered body, and (2) is a dark-colored sintered body. The interface between the two was not a continuously formed interface but a partially formed interface (dotted line circle in FIG. 3). Further, it can be confirmed that a part of the interface is peeled off and a gap is formed (indicated by an arrow in FIG. 3).

  In the multicolor zirconia sintered body of the present invention, the light-colored sintered body and the dark-colored sintered body have an interface, and the interface has no color blur. Thereby, since the boundary between the light-colored sintered body and the dark-colored sintered body becomes clear, the multicolored zirconia sintered body of the present invention can be made into a member having a clear pattern. Furthermore, the pattern formed by one zirconia sintered body can be a fine pattern.

  The color blur is a portion exhibiting a color tone in which the color tone of the light-colored sintered body and the color tone of the dark-colored sintered body are mixed, and is observed visually or with an optical microscope. Furthermore, the color blur at the interface is an area including the color tone of the other zirconia sintered body, which is observed in one of the light-colored sintered body and the dark-colored sintered body, and a region in the vicinity of the interface ( Hereinafter, it is also referred to as “transition region”) and is observed visually or with an optical microscope. In the present invention, it means an interface and a region in the vicinity of the interface including the color tone of the dark-colored sintered body, which are observed in the light-colored sintered body, and are observed visually or with an optical microscope. The presence or absence of color bleeding at the interface can be confirmed by visual observation or, for example, by observing the multicolor zirconia sintered body with an optical microscope having a magnification of 10 to 100 times.

  FIG. 4 is a view showing an optical micrograph of the multicolor zirconia sintered body of the present invention. In FIG. 4, the interface (3), which is the boundary between the areas (1) and (2), is clear from the difference in color tone in the optical electron micrograph, and the multicolor zirconia sintered body of the present invention has color blur. I can confirm that I do not. On the other hand, FIG. 5 is an optical micrograph showing an example of a multicolor zirconia sintered body having color blur. In FIG. 5, the area (1) is a light-colored sintered body, and the area (2) is a dark-colored sintered body. As shown in FIG. 5, the boundary between the regions (1) and (2) is blurred and the vicinity of the interface is unclear (for example, a broken-line square portion in FIG. 5). Such a multicolor zirconia sintered body can be confirmed to have color bleeding near the interface.

  The multicolor zirconia sintered body of the present invention may have a transition region that cannot be observed visually or with an optical microscope. The transition region that cannot be observed visually or with an optical microscope does not substantially affect the aesthetics when the multicolor zirconia sintered body of the present invention is used as various members.

  As a transition region that cannot be observed visually or with an optical microscope, either the light-colored sintered body or the dark-colored sintered body is a region of one of the zirconia sintered bodies, and the other includes a coloring component contained in one of the zirconia sintered bodies. The area | region of zirconia sintered compact of this can be mentioned.

  If the coloring component contained in the transition region is 3% by weight or less, further 2.5% by weight or less, and further 2% by weight or less, color bleeding does not occur. Here, the presence / absence of the transition region and the content of the coloring component are obtained by quantitative point analysis (hereinafter referred to as “EPMA analysis”) of an electron microanalyzer in the region of the light-colored sintered body at a certain distance from the interface. It can confirm from the coloring component with respect to the weight of all the elements, and a weight ratio.

  FIG. 6 is a schematic diagram showing the measurement of the transition region by EPMA analysis. In FIG. 6, (1) is the region of the light-colored sintered body, (2) is the region of the dark-colored sintered body, and (3) is the interface. Further, (4) is a region of a light-colored sintered body at a certain distance from the interface, and (5) is a circle having a diameter of 10 μm formed around the (4) region. In the EPMA analysis, all elements included in (5) are analyzed, and when a coloring component is included, the region becomes a transition region. In the present invention, EPMA analysis is performed for a plurality of regions (regions corresponding to (4) in FIG. 6) at different distances from the interface, and a region containing a colored component corresponding to the maximum distance from the interface is detected in the sample. It was set as the transfer area | region of each coloring component.

  The transition region is a region corresponding to the maximum distance from the interface containing the coloring component, and can include a region within 200 μm from the interface, further a region within 150 μm, and further a region within 100 μm, particularly from the interface. A light-colored sintered body region within 200 μm, a light-colored sintered body region within 150 μm, and a light-colored sintered body region within 100 μm can be exemplified.

  When the transition region is in the above range and the amount of the colorant, there is no color blur imparted to aesthetics when the multicolor zirconia sintered body of the present invention is used as a member.

  Examples of the coloring component contained in the transition region include a metal element constituting the spinel oxide contained in the dark-colored sintered body, and further includes at least one of iron (Fe) and cobalt (Co). it can.

  For example, in the light-colored sintered body included in the multicolor zirconia sintered body of the present invention, the transition region is a region within 100 μm from the interface, and iron is 1% by weight or less, further 0.6% by weight or less in the region. Furthermore, although it is 0.3 wt% or less, it can be mentioned that the region beyond the transition region does not contain iron. In this case, the iron transition region is a region within 100 μm from the interface.

  Further, the light-colored sintered body included in the multicolored zirconia sintered body of the present invention has a cobalt content of not more than 0.5% by weight, more preferably not more than 0.3% by weight in a region within 100 μm from the interface, and further in a region within 50 μm. In addition, it can be mentioned that cobalt is not included in a region exceeding 100 μm from the interface. In this case, the transition region of cobalt is within 50 μm from the interface. However, when cobalt is not substantially contained in a region within 50 μm (0% by weight), the region does not have a cobalt transition region, or at least a region closer to the interface than 50 μm from the interface.

  In the multicolor zirconia sintered body of the present invention, it is preferable that one of the light-colored sintered body and the dark-colored sintered body has a pattern formed on the surface of the other zirconia sintered body. . The multicolor zirconia sintered body of the present invention can form a finer pattern as compared with the conventional one. As a result, not only the design properties are further improved, but also a multicolor zirconia sintered body that is a member used in a wider range of applications can be provided.

  In the present invention, the pattern is a diagram, a figure, or a combination of the other zirconia sintered body formed on a part of one of the light-colored sintered body and the dark-colored sintered body. It is. Specific examples of line diagrams include linear lines such as solid lines, broken lines, and wavy lines, numbers, letters, and the like, and examples of shapes include round shapes and geometric shapes such as polyhedron shapes.

  In the multicolor zirconia sintered body of the present invention, the light-colored sintered body may have a pattern on the surface of the dark-colored sintered body, while the dark-colored sintered body has a pattern on the surface of the light-colored sintered body. It may be formed.

The multicolor zirconia sintered body of the present invention can form a pattern having a size obtained by a conventional multicolor zirconia sintered body. In addition to this, the multicolor zirconia sintered body of the present invention can form a clear pattern even in a finer range than before. The pattern is, for example, an area of 1 cm ² or less, further an area of 1 mm ² or less, further an area of 0.5 mm ² or less, further an area of 0.05 mm ² or less, or even 0.005 mm ² or less. A region can be clearly formed. Furthermore, as a pattern which the multicolor zirconia sintered body of the present invention has, for example, a diagram composed of a line having a thickness of about 150 μm, a diagram or a figure having an interval of about 150 μm, a diameter of 1 mm or less, and a diameter of 0. The figure of 5 mm or less can be mentioned.

  Although the shape of the multicolor zirconia sintered body of the present invention and the pattern it has is arbitrary, for example, examples of the shape and pattern of the multicolor zirconia sintered body of the present invention are shown in FIGS.

  For example, FIG. 7 is a schematic view of a multicolored zirconia sintered body having a shape of a bezel ring for a watch and forming the surface of the bezel ring. The left figure is a front view, the middle figure is a side view, and the right figure is a rear view. In the front view, the bezel ring surface is made of a dark-colored sintered body ((2) in the left figure of FIG. 7), and the pattern of the Arabic numeral shape made of a light-colored sintered body on the surface (in the left figure of FIG. 7 (1) )). The side surface is that the multicolor zirconia sintered body is formed by laminating a dark-colored sintered body having concave portions having the same shape as the Arabic numerals on a light-colored sintered body having convex parts having the Arabic numeral shape. (Shown in FIG. 7). Further, the light-colored sintered body has a ring shape having a hollow portion, and the light-colored sintered body and the dark-colored sintered body are laminated (the right diagram in FIG. 7).

  Further, for example, FIG. 8 is a schematic view of a multicolor zirconia sintered body having a clock face shape. The left figure is a front view, and the right figure is a rear view. In FIG. 8, it is a sintered body having a disk-like shape, and the surface is a dark-colored sintered body. Light-color sintering of a shape having a diagram corresponding to each time from 1 o'clock to 12 o'clock of an analog timepiece and a pattern of 3, 6, 9 and 12 Arabic numerals on the surface of the sintered body Shows having a body. Further, the light-colored sintered body has a disk shape, and the light-colored sintered body and the dark-colored sintered body are laminated (the right diagram in FIG. 8).

  9 to 12 are schematic views showing multicolor zirconia sintered bodies each having a bracelet shape, a housing shape, a mobile phone cover shape, and a disk shape.

  Since the light-colored sintered body and the dark-colored sintered body are joined by sintering, the multicolor zirconia sintered body of the present invention has a high density. It can be mentioned that the relative density of the multicolor zirconia sintered body of the present invention is 99.5% or more, and further 99.7% or more. When the relative density is 99.5% or more, not only there is no gap at the interface, but also defects at portions other than the interface are reduced. Thereby, the mechanical strength of the multicolor zirconia sintered body of the present invention tends to be higher.

  In addition, a zirconia composite_body | complex and a zirconia joined body combine the different zirconia sintered compacts after sintering. Therefore, even if the relative density of the zirconia sintered bodies constituting these is 99.5% or more, the relative density as a zirconia composite or zirconia joined body is not 99.5% or more.

  In the present invention, the relative density of the multicolor zirconia sintered body can be determined from the following equation (1).

Relative density (%) = Measured density of multicolor zirconia sintered body (g / cm ³ ) / Theoretical density of multicolor zirconia sintered body (g / cm ³ ) × 100 (1)

  The actually measured density (sintered body density) of the multicolor zirconia sintered body can be determined by the Archimedes method.

  Furthermore, the theoretical density of the multicolored zirconia sintered body can be calculated from the following formula according to the density and volume ratio of the light-colored sintered body and the dark-colored sintered body.

                M = (Ma * X + Mb * Y) / (X + Y) (1 ')

In the above formula, M is the theoretical density ^{(g /} cm 3) of a multicolor zirconia sintered body, Ma theoretical density ^{(g /} cm 3) of pale sintered body, Mb is the theoretical density of the Koirosho sintered body (g / Cm ³ ), X is the volume ratio of the light-colored sintered body to the volume of the multicolored zirconia sintered body, and Y is the volume ratio of the dark-colored sintered body to the volume of the multicolored zirconia sintered body.

  In the formula (1 ′), Ma and Mb differ depending on the compositions of the light-colored sintered body and the dark-colored sintered body. Ma and Mb may be obtained from the theoretical density of the compounds constituting each sintered body and the weight ratio of these compounds. Examples of the theoretical density of the compounds constituting each sintered body include the following.

Black zirconia: 6.05 g / cm ³
3 mol% yttria-containing zirconia: 6.09 g / cm ³
Aluminum oxide: 3.98 g / cm ³
Aluminum oxide cobalt spinel: 4.42 g / cm ³
Iron oxide: 5.24 g / cm ³

  In the formula (1 ′), X is a volume ratio obtained by multiplying the weight ratio of the light-colored sintered body to the weight of the multicolored zirconia sintered body by Ma, and Y is a dark color with respect to the weight of the multicolored zirconia sintered body. It is a volume ratio obtained by multiplying the weight ratio of the sintered body by Mb.

  The light-colored sintered body and the dark-colored sintered body are 2 mol% or more and 6 mol% or less, further 2.5 mol% or more and 4 mol% or less, further 2.5 mol% or more and 3.5 mol% or less, and further 2.8 mol. It is preferable to contain a stabilizer in an amount of not less than% and not more than 3.2 mol%. By including the stabilizer in the above range, these zirconia sintered bodies become zirconia sintered bodies having a crystal structure of tetragonal crystals. Thereby, it becomes a sintered compact which has high mechanical strength.

  Examples of the stabilizer include at least one selected from the group consisting of yttria, calcia, magnesia, and scandia, and yttria.

  In the present invention, the light-colored sintered body is a white zirconia sintered body and contains aluminum oxide (alumina). By containing alumina, the alumina particles are dispersed between the zirconia crystal particles. Thereby, the original transparency of zirconia is suppressed, and the light-colored sintered body becomes a zirconia sintered body exhibiting a clear white color. Furthermore, when the light-colored sintered body contains only the stabilizer and alumina, formation of an interface free from gaps and color bleeding during the sintering is facilitated.

  The content of alumina is 0.25 wt% or more and 20 wt% or less, further 1 wt% or more and 15 wt% or less, and further 5 wt% or more and 10 wt% or less as the alumina weight with respect to the light-colored sintered body weight. It is preferable. By containing alumina in this range, the color tone of the light-colored sintered body becomes clearer white. Furthermore, if the content of alumina is within the above range, sintering of zirconia proceeds without being inhibited by alumina particles.

The color of the light-colored sintered body is L *, a *, and b * in the L * a * b * color system (hereinafter also referred to simply as “L *”, “a *”, and “b *”). L * = 85 to 100, a * = − 2 to 2, and b * = − 2 to 3.0, and L * = 85 to 95, a * = − 1 -0.5 or less and b * = 0 or more and 1.5 or less, and further L * = 85 or more and 93 or less, a * =-1 or more and -0.4 or less, and b * = It is preferably 0.5 or more and 1.3 or less. When the lightness L ^* is 85 or more and both a ^* and b ^* are near zero, the light-colored sintered body becomes a white zirconia sintered body exhibiting a clear pure white without coloring. Thereby, it can be set as a member with higher aesthetics by combining with a deep color sintered compact.

  The dark color sintered body included in the multicolor zirconia sintered body of the present invention is a zirconia sintered body containing a spinel oxide. By containing a spinel oxide, it becomes a zirconia sintered body having a darker color tone than the color tone of the light-colored sintered body.

  The color of the dark color sintered body may be a desired color tone. For example, the value of L * is 20 or more lower than that of the light color sintered body. Furthermore, it can be illustrated that L * of the dark color sintered body is less than 55.

  When the dark color sintered body is a black zirconia sintered body, as a preferred spinel oxide contained in the dark color sintered body, a spinel oxide containing iron and cobalt, further at least one of zinc or aluminum, iron, And spinel oxide containing cobalt, and further spinel oxide containing zinc, aluminum, iron and cobalt. As a result, the dark-colored sintered body exhibits a black color.

  Preferred spinel oxides include spinel oxides having the following composition.

^{_{(Co X M 2+ 1-X}} ) (Fe Y M 3+ 1-Y) 2 O 4
(However, M ²⁺ = Zn or Mn, M ³⁺ is Al or Cr, 0.1 <X ≦ 1, and 0.5 <Y ≦ 1)

  Moreover, since it becomes a zirconia sintered compact which exhibits deeper black, it is especially preferable that a spinel oxide has the following compositions.

_{(Co X Zn 1-X)} (Fe Y Al 1-Y) 2 O 4
(However, 0.5 <X ≦ 1 and 0.5 <Y ≦ 1)

  The weight of the spinel oxide with respect to the weight of the dark color sintered body is 0.25% to 13% by weight, more preferably 1% to 10% by weight, and further 3% to 5% by weight. preferable. By containing the spinel oxide in this range, the color tone of the sintered body becomes clearer black.

By including the above spinel oxide, the dark-colored sintered body exhibits a black color. The coloration of the zirconia sintered body is L * = 0 or more and 10 or less, a * = − 1 or more and 1 or less, and b * = − 1 or more and 1 or less in the L * a * b * color system. Is preferred. Black zirconia sintered with a lightness L ^* of 10 or less, and both a ^* and b ^* are near zero, so that the dark-colored sintered body is not reddish or bluish and exhibits a true black color. Become a body. Thereby, it can be set as a higher-grade zirconia sintered compact.

  Next, the manufacturing method of the multicolor zirconia sintered compact of this invention is demonstrated.

  The multicolored zirconia sintered body of the present invention is a primary molding step, a primary molding step in which a zirconia powder containing aluminum oxide or a zirconia powder containing a spinel oxide is molded to obtain a primary compact. Secondary molding step of obtaining the secondary molded body by molding the other zirconia powder on the primary molded body at the molding temperature below, sintering to obtain a pre-sintered body by firing the secondary molded body at 1300 ° C or higher It can be manufactured by a manufacturing method including a process and a HIP processing step in which the pre-sintered body is subjected to hot isostatic pressing at 1250 ° C. or higher and 1650 ° C. or lower and 100 MPa or higher and 250 MPa or lower.

  In the primary molding step, a primary molded body is obtained. The primary molded body is a molded body obtained by molding zirconia powder containing aluminum oxide (hereinafter also referred to as “light colored powder”) (hereinafter also referred to as “light colored molded body”), or zirconia powder containing spinel oxide. (Hereinafter, also referred to as “dark colored powder”).

  The molding method in the primary molding step is arbitrary. Examples of the molding method include one or more molding methods including the group of press molding, cold isostatic pressing, cast molding, sheet molding, and injection molding. In order to easily obtain a molded body having an arbitrary shape, the molding method is preferably at least one of casting molding and injection molding. Furthermore, the molding method is more preferably injection molding because a molded body having a more complicated and fine shape can be easily obtained.

  In the secondary molding step, a molded body obtained by molding the other powder on the primary molded body made of one of the light-colored molded body and the dark-colored molded body is produced. Thereby, the molded object with which the primary molded object and the secondary molded object were joined is obtained.

  The molding temperature in the secondary molding step (hereinafter also referred to as “secondary molding temperature”) is set to be equal to or lower than the molding temperature in the primary molding step (hereinafter also referred to as “primary molding temperature”). When the secondary molding temperature is higher than the primary molding temperature, the shape of the primary molded body is likely to be distorted or collapsed during the secondary molding. In this case, a secondary molded body including a state in which the fine shape of the primary molded body such as a convex portion is distorted is obtained. When such a secondary compact is sintered, the resulting multicolored zirconia sintered body becomes a sintered body having color bleeding due to shape distortion.

  In a general molding method having primary molding and secondary molding, in particular, cast molding or injection molding having primary molding and secondary molding, the temperature of the primary molded body is increased by heat during secondary molding. Thereby, the temperature of a secondary shaping | molding process rises. Therefore, when the molding temperature is not controlled in the primary molding and the secondary molding, the secondary molding temperature usually exceeds the primary molding temperature. On the other hand, the secondary molding temperature in the present invention is equal to or lower than the primary molding temperature, and further lower than the primary molding temperature. When the secondary molding temperature is equal to or lower than the primary molding temperature, that is, when the primary molding temperature is equal to or higher than the secondary molding temperature, the flow of the pattern and the color blur caused thereby are not generated. By sintering the secondary molded body thus obtained, a multicolor zirconia sintered body having no gaps and color blurs at the interface can be obtained. The flow of the pattern includes, for example, that the shape of the primary molded body such as a convex portion of the primary molded body is deformed by the molding of the secondary molded body.

  In the secondary molding step, the larger the difference between the primary molding temperature and the secondary molding temperature, the easier it is to obtain a secondary molded body that does not include a distorted shape. The primary molding temperature is 3 ° C. or higher, further 5 ° C. or higher, further 10 ° C. or higher, further 20 ° C. or higher, or further 30 ° C. or higher from the secondary molding temperature. However, in the production method of the present invention, the secondary molding temperature is lower than the primary molding temperature, and the difference is 3 to 30 ° C, further 3 to 20 ° C, further 3 to 10 ° C, or even more. Even if it is as small as 5-10 degreeC, the secondary molded object which does not contain the distorted shape can be obtained with sufficient reproducibility.

  The primary molding temperature and the secondary molding temperature may be controlled by the temperature of the mold of the molded body (hereinafter also referred to as “molding mold”). That is, in the molding step, the temperature of the primary molding die is higher than the temperature of the secondary molding die, further 3 ° C or higher, further 5 ° C or higher, further 10 ° C or higher, and further 20 ° C or higher. Furthermore, the secondary molding temperature can be set to be equal to or lower than the primary molding temperature by setting the temperature to 30 ° C. or higher.

  The molding method in the secondary molding step is any one or more of the group consisting of press molding, cold isostatic pressing, cast molding, sheet molding, and injection molding as long as the primary molding temperature and the secondary molding temperature satisfy the above relationship. Any molding method may be used. In order to easily obtain a molded body having an arbitrary shape, the molding method is preferably at least one of casting molding and injection molding. Furthermore, it is more preferable that the molding in the secondary molding step is injection molding because a molded body having a more complicated and fine shape can be easily obtained with good reproducibility.

  It can be exemplified that the injection pressure in the injection molding is from 50 MPa to 150 MPa, and further from 70 MPa to 130 MPa.

  The light-colored powder used for the primary molding process, the secondary molding process, or both processes (hereinafter also referred to as “molding process”) is a zirconia powder containing alumina, and further a mixed powder of alumina powder and zirconia powder. If it is.

The light-colored powder preferably has a BET specific surface area of 7 to ²⁰ m ² / g, more preferably 7.5 to 15 m ² / g. By setting the BET specific surface area within this range, the light-colored molded product tends to have the same sintering behavior as the dark-colored molded product containing the spinel oxide.

  Examples of the zirconia powder include zirconia powder containing 3 mol% yttria.

  The content of alumina is such that the weight of alumina is 0.25% to 20% by weight, further 1% to 20% by weight, and further 5% to 10% by weight with respect to the weight of the light color powder. If it is. Examples of the alumina powder include alumina powder having a purity of 99% or more, and further a purity of 99.5% or more.

  The mixing method is arbitrary as long as the alumina powder and the zirconia powder are uniformly mixed. As a mixing method, wet mixing, ball mill or bead mill is preferable. A specific mixing method includes mixing alumina powder and zirconia powder in a ball mill for 24 hours or more.

  The dark color powder used for the forming step is a zirconia powder containing a spinel oxide and may be a mixed powder of a spinel oxide powder and a zirconia powder.

The weight of the spinel oxide powder may be 2% by weight to 6% by weight, and more preferably 2% by weight to 4% by weight with respect to the weight of the dark color powder. Moreover, it is mentioned that a dark color powder has a BET specific surface area of 4-10 m < ² > / g.

  Examples of the zirconia powder include zirconia powder containing 3 mol% yttria.

  Spinel oxide powder containing iron and cobalt, further spinel oxide powder containing zinc and / or aluminum, iron and cobalt, or spinel oxidation containing zinc, aluminum, iron and cobalt When the product powder is included, the weight of the spinel oxide powder with respect to the weight of the dark color powder is 0.25% to 13% by weight, further 1% to 10% by weight, and further 3% to 5% by weight. It is preferable that

  Preferred spinel oxide powders include spinel oxide powders having the following composition.

^{_{(Co X M 2+ 1-X}} ) (Fe Y M 3+ 1-Y) 2 O 4

(However, M ²⁺ = Zn or Mn, M ³⁺ is Al or Cr, 0.1 <X ≦ 1, and 0.5 <Y ≦ 1)
Moreover, in order to obtain the zirconia sintered compact which exhibits deeper black, it is especially preferable that spinel oxide powder has the following compositions.

_{(Co X Zn 1-X)} (Fe Y Al 1-Y) 2 O 4
(However, 0.5 <X ≦ 1 and 0.5 <Y ≦ 1)

  The mixing method of the spinel oxide powder and the zirconia powder is arbitrary, but wet mixing, and ball milling is preferable. As a mixing method, mixing for 24 hours or more by a ball mill can be mentioned.

  In the molding step, in order to improve the fluidity of the powder, it is preferable that at least one of the light color powder and the dark color powder contains an organic binder.

  When an organic binder is included, the content of the organic binder in each zirconia powder can be 25 to 65% by volume, and further 35 to 60% by volume.

  Examples of the organic binder include at least one selected from the group consisting of an acrylic resin, a polyolefin resin, a wax, and a plasticizer.

  If the zirconia powder and the organic binder can be mixed uniformly, the mixing method is arbitrary. Examples of the mixing method include heat kneading and wet mixing.

  The light-colored molded product and the dark-colored molded product preferably have the same sintering shrinkage strength. Thereby, the distortion resulting from the difference of shrinkage amount does not arise, but a molded object can be sintered in the state which both joined more firmly. For example, the ratio of the same shrinkage ratio of white zirconia to the shrinkage ratio of the black zirconia sintered body to the black zirconia molded body (hereinafter also referred to as “shrinkage ratio”), when the firing temperature is 1200 ° C. It is mentioned that the value is 0.95 to 1.05.

  In the firing step, the secondary molded body is fired to be pre-sintered to obtain a pre-sintered body.

  In the firing step, the firing temperature is 1300 ° C. or higher, and further 1350 ° C. or higher. When the firing temperature is less than 1300 ° C., the sintered body is not densified in the HIP processing step. The firing temperature does not need to be higher than necessary, and may be 1300 ° C. or higher and 1550 ° C. or lower, 1350 ° C. or higher and 1500 ° C. or lower, and 1350 ° C. or higher and 1450 ° C. or lower.

  The firing atmosphere may be any of air, inert atmosphere or vacuum, and is preferably at least one of air or inert atmosphere, and more preferably air. Arbitrary combinations can be applied to the above firing temperature and firing atmosphere. The firing step is preferably atmospheric pressure sintering, which is a method of sintering by simply heating without applying an external force to the compact.

  Although the firing time varies depending on the firing temperature, it is preferably 1 hour or longer, more preferably 2 hours or longer. When the firing time is 1 hour or longer, the removal of the gap is promoted in the firing step. On the other hand, the firing time may be 5 hours or less, and further 3 hours or less.

  In addition, when a molded object is produced from the zirconia powder containing an organic binder, before performing a baking process, a degreasing process is performed and an organic binder is removed from a molded object.

  The baking temperature in the degreasing process may be 400 ° C. or more and 600 ° C. or less. The degreasing atmosphere may be any atmosphere selected from the group consisting of air, inert gas atmosphere, and oxidizing gas atmosphere.

  In the manufacturing method of the present invention, the pre-sintered body is subjected to HIP treatment. Thereby, while suppressing the color bleeding at the interface, the elimination of the gaps at the interface is promoted, the pre-sintered body is sintered, and the multicolor zirconia sintered body of the present invention is obtained.

  In the HIP treatment, a HIP temperature of 1200 ° C. or higher, 1250 ° C. or higher, 1300 ° C. or higher, or 1350 ° C. or higher can be exemplified. If densification progresses, the HIP temperature does not need to be higher than necessary. Examples of the HIP temperature include 1650 ° C. or lower, and further 1450 ° C. or lower.

  The HIP pressure is 50 MPa or more, further 100 MPa or more, and further 140 MPa or more. In HIP processing using a normal HIP processing apparatus, the HIP pressure is 250 MPa or less, and further 180 MPa or less.

  The atmosphere of the HIP treatment may be an inert atmosphere, and can include at least one of a nitrogen atmosphere or an argon atmosphere, and is preferably an argon atmosphere. The above HIP temperature, HIP pressure and atmosphere, and their upper and lower limit values can be arbitrarily combined.

  By the production method of the present invention, it is possible to obtain a multicolor zirconia sintered body having no color bleeding and no gap at the interface.

  Furthermore, the production method of the present invention includes at least one of a processing step and a polishing step (hereinafter, also referred to as “post-treatment step”) for using the obtained multicolor zirconia sintered body as various members. You may go out.

  In the processing step, the multicolor zirconia sintered body obtained by the HIP process is processed into a desired shape. Any processing method can be used. The processing method may be a general cutting process, and examples thereof include one or more members selected from the group consisting of lathe processing, surface grinding, R grinding, and NC processing (numerical control machining).

  In the polishing step, the multicolor zirconia sintered body obtained by the HIP process or a processed product thereof is polished. Thereby, gloss can be strengthened more and the high-class feeling of the multicolor zirconia sintered compact of this invention is emphasized more. Although the polishing method is arbitrary, at least one of barrel polishing or R polishing can be exemplified.

  In the production method of the present invention, any combination of the above conditions may be used in the primary molding step, secondary molding step, firing step, HIP treatment step, and post-treatment step.

  According to the present invention, there is provided a zirconia sintered body having two or more different color tones, having a high-quality aesthetic, and having sufficient strength to be used as a member. it can. In addition, according to the present invention, it is possible to provide a zirconia sintered body having two or more different color tones and having no color bleeding or gap between the zirconia sintered bodies.

  Furthermore, according to the present invention, a member having a high-class feeling can be provided.

Optical micrograph of white / black zirconia sintered body of Example 1 Secondary electron image of white / black zirconia sintered body of Example 1 (scale in the figure is 50 μm) Reflected electron image of the white / black zirconia sintered body of Comparative Example 1 (scale in the figure is 50 μm) Optical micrograph of interface of white / black zirconia sintered body of Example 1 (scale in the figure is 50 μm) Optical micrograph of white / black zirconia sintered body of Comparative Example 3 (scale in the figure is 50 μm) Schematic diagram showing measurement of transition region by quantitative point analysis of EPMA The schematic diagram which shows an example of the bezel ring for watches which consists of the multicolor zirconia sintered compact of this invention The schematic diagram which shows an example of the dial for timepieces which consists of a multicolor zirconia sintered compact of this invention The schematic diagram which shows an example of the bracelet which consists of a multicolor zirconia sintered compact of this invention The schematic diagram which shows an example of the housing | casing which consists of a multicolor zirconia sintered compact of this invention. The schematic diagram which shows an example of the cover for mobile phones consisting of the multicolor zirconia sintered compact of this invention The schematic diagram which shows an example of the disk shaped sintered compact which consists of a multicolor zirconia sintered compact of this invention Overview of the bezel ring of Example 1 Optical micrograph of pattern of white / black zirconia sintered body of Example 1 Optical micrograph of interface of white / black zirconia sintered body of Comparative Example 1 (scale in the figure is 10 μm) Optical micrograph of pattern of white / black zirconia sintered body of Comparative Example 4 Optical micrograph of interface of white / black zirconia sintered body of Example 6 (scale is 10 μm in the figure) Secondary electron image of interface of white / black zirconia sintered body of Example 6 (scale in the figure is 50 μm) Overview of white / black zirconia sintered body of Example 8

  Hereinafter, the present invention will be specifically described with reference to Examples and Comparative Examples. However, the present invention is not limited to these.

(Sintered body density and relative density)
The actual density (sintered body density) of the multicolor zirconia sintered body was measured by the Archimedes method. From the obtained measured density and theoretical density, the relative density of the multicolor zirconia sintered body was determined. The theoretical density of the multicolor zirconia sintered body was calculated from the equation (1 ′). The calculated theoretical densities of the multicolor zirconia sintered bodies of Examples and Comparative Examples are shown in Tables 2, 5, and 7, respectively.

(Specific surface area)
The BET specific surface area by nitrogen adsorption was measured and used as the specific surface area of the powder sample. A general specific surface area measuring device (manufactured by QUANTA CHROME) was used for the measurement.

(Optical microscope observation)
The interface of the sintered compact sample was observed using an optical microscope (device name: MM-800, manufactured by Nikon) or a trinocular zoom stereo microscope (device name: AR-372ZH, manufactured by Arm System Co., Ltd.). In the optical microscope observation, the presence or absence of a gap at the interface and the presence or absence of color bleeding were observed.

(SEM observation)
The interface of the sintered compact sample was observed using SEM (device name: JSM-5400, manufactured by JEOL). In SEM observation, the magnification was set to 500 times, and the presence or absence of a gap at the interface was observed.
(Element quantitative analysis by EPMA)
Using a wavelength dispersive electron beam microanalyzer (EPMA) (device name: EPMA1610, manufactured by Shimadzu Corporation), point analysis was performed in the vicinity of the interface of the light-colored sintered body in the sintered body sample. The measurement conditions are as follows.

Acceleration voltage: 15KV
Irradiation current: 100 nA
Analysis range: φ10μm

  Measurement is performed at a distance of 30 μm, 50 μm, 100 μm, 130 μm, 170 μm, and 200 μm from the interface to the light-colored sintered body, and the measurement region at the farthest distance from the interface is transferred. The area.

(L ^* a ^* b ^* Color tone by color system)
Based on JISZ8722, the color tone of the sintered compact sample was measured. A general color difference meter (device name: Color Analyzer TC-1800MK-II, manufactured by Tokyo Denshoku Co., Ltd.) was used for the measurement. The measurement conditions are as follows.

Light source: D65 light source
Viewing angle: 2 °

  The sintered body sample used was a disk-like shape having a thickness of 1 mm and a diameter of 20 mm, both surfaces of which were polished.

(Mechanical strength test)
As the mechanical strength of multicolor zirconia sintered compact samples. The impact strength was measured by a hard sphere drop test according to ISO14368-3. That is, the multicolor zirconia sintered compact sample was arrange | positioned on the board made from SUS. Thereafter, an iron ball having a weight of 16 g from a height of 5 cm is dropped from a multicolor zirconia sintered body sample in the vicinity of the interface between the light color sintered body and the dark color sintered body, and cracks of the multicolor zirconia sintered body are obtained. The presence or absence of cracks, cracks or other destruction was confirmed. Then, the same measurement was performed by increasing the drop start position of the iron ball (hereinafter also referred to as “falling ball position”) at intervals of 5 cm. The impact strength of the sample of the multicolored zirconia sintered body was determined based on the falling ball position (cm) at which the destruction was confirmed in the multicolored zirconia sintered body.

Example 1
A multi-colored zirconia sintered body composed of a white zirconia sintered body and a black zirconia sintered body, and a watch bezel ring (hereinafter also simply referred to as “bezel ring”) composed of the same.
(Preparation of white zirconia raw material)
The BET specific surface area is 8 m ² / g so that the weight of alumina relative to the total weight of yttria and zirconia in the 3 mol% yttria-stabilized zirconia powder (hereinafter also simply referred to as “alumina weight”) is 5 wt%. High purity aluminum oxide (purity: 99.9%) was added to 3 mol% yttria stabilized zirconia powder (trade name: TZ-3YS, manufactured by Tosoh Corporation).

  After the addition, these powders were mixed with a ball mill for 24 hours in an ethanol solvent using zirconia balls having a diameter of 10 mm. The mixed powder was dried to obtain white zirconia powder.

An acrylic binder was mixed with the obtained white zirconia powder to make a white zirconia raw material. The content of white zirconia powder in the white zirconia raw material was 45% by volume.
(Preparation of black zirconia raw material)
Commercially available black zirconia powder (trade name: TZ-Black, manufactured by Tosoh Corporation) was used as the black zirconia powder. The powder is composed of a spinel oxide containing iron and cobalt in which a part of cobalt is substituted with Zn and a part of iron is substituted with Al, and 3 mol% of yttria-containing zirconia having the following composition: It is a powder. The content of the spinel oxide in the black zirconia powder is 3.5% by weight.

(Co _0.7 Zn _0.3 ) (Fe _0.7 Al _0.3 ) ₂ O ₄

An acrylic binder was mixed with the black zirconia powder to make a black zirconia raw material. In addition, content of the black zirconia powder in a black zirconia raw material was 45 volume%.
(Preparation of secondary compact)
The white zirconia raw material was injection-molded to obtain a bezel-ring-shaped white zirconia molded body having convex portions. The injection molding conditions were a mold temperature of 60 ° C. and a pressure of 100 MPa.

  Next, a black zirconia raw material was injection-molded on the obtained white zirconia molded body. Thereby, the secondary molded object which both joined in the shape which the black zirconia molded object laminated | stacked on the white zirconia molded object was obtained. The temperature of the mold for secondary molding was set to 50 ° C., whereby the primary molding temperature was set to 10 ° C. higher than the secondary molding temperature.

The obtained molded body was degreased in the atmosphere at a heating rate of 2.0 ° C./h, a degreasing temperature of 450 ° C., and a degreasing time of 4 hours.
(Baking and HIP treatment)
The secondary molded body after the degreasing treatment was fired in the air at a heating rate of 100 ° C./h, a firing temperature of 1450 ° C., and a sintering time of 2 hours to obtain a primary sintered body.

  After placing the obtained primary sintered body in an alumina container, it was subjected to HIP treatment in an atmosphere of 99.9% purity argon gas at a HIP temperature of 1350 ° C., a HIP pressure of 150 MPa, and a holding time of 1 hour, A HIP-treated product was obtained. The HIP-treated body was the white / black zirconia sintered body of this example. The production conditions of this example are shown in Table 1, and the evaluation results are shown in Table 2.

The white / black zirconia sintered body obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.7%. It was.
(Component processing)
The surface of the white / black zirconia sintered body side of the white / black zirconia sintered body of this example was processed until the convex portion of the white zirconia sintered body was clearly observed. Thereby, the white / black zirconia sintered body of this example was used as a bezel ring having a pattern made of a white zirconia sintered body on the surface of the black zirconia sintered body. By polishing the bezel ring after surface processing, a bezel ring made of the white / black zirconia sintered body of this example and having a strong gloss was obtained. The bezel ring had a ring shape with an outer diameter of 40 mm, an inner diameter of 30 mm, and a width of 5 mm. The thickness of the ring was 2 mm. FIG. 13 shows an overview of a bezel ring made of a white / black zirconia sintered body of this example, FIG. 4 shows an optical microscopic observation diagram of the interface, and FIG. 14 shows an optical microscopic observation diagram in which the pattern is enlarged.

As apparent from FIG. 13, the bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface. Further, as apparent from FIG. 4, it was confirmed that the interface white color was not blurred and the interface had no color blur. Further, from FIG. 14, it was confirmed that a line diagram having a thickness of 0.15 mm was formed as a clear pattern because there was no color blur (dashed line square portion in FIG. 14).
(Evaluation)
Optical microscope observation of the interface of the bezel ring was performed. The results are shown in FIG. It was found that white zirconia and black zirconia were sintered to form an interface, and that the interface did not have a gap (for example, a dotted circle in FIG. 1).

  Further, a secondary electron image at the interface of the bezel ring is shown in FIG. The interface could be confirmed also in the secondary electron image (arrow part in FIG. 2). Further, it was confirmed that no gap was formed at the interface and that there was no bonding layer.

  From these results, it was confirmed that the bezel ring made of the white / black zirconia sintered body of this example and the white / black zirconia sintered body of this example had no gap at the interface.

  Further, EPMA analysis was performed on the interface of the bezel ring and in the vicinity of the interface. The results are shown in Table 3. In the white zirconia sintered body, an iron element as a coloring component of the black zirconia sintered body was confirmed in a region within 100 μm from the interface. On the other hand, the cobalt element which is a coloring component of the black zirconia sintered body was not confirmed even in a region within 30 μm from the interface. From this, it was confirmed that the white / black zirconia sintered body of this example had an iron transition region within 100 μm from the interface and no cobalt transition region.

  In the white / black zirconia sintered body of the present example, it was confirmed that although the trace amount of Fe was contained in the white zirconia sintered body, there was no interfacial color blur and no gap.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. Even if the iron ball was dropped from a height of 85 cm, no cracks or cracks occurred. From this, it was confirmed that the white / black zirconia sintered body of this example had a high strength with an impact strength of 85 cm or more.

Example 2
In the same manner as in Example 1 except that the alumina weight was 10% by weight and high-purity aluminum oxide was added, the firing temperature was 1500 ° C, and the HIP treatment temperature was 1450 ° C. The white / black zirconia sintered body of this example was obtained by firing and HIP treatment. The production conditions of this example are shown in Table 1, and the evaluation results are shown in Table 2.

  The obtained white / black zirconia sintered body had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.6%. It was.

  Next, the obtained white / black zirconia sintered body is processed and polished in the same manner as in Example 1, and is made of the white / black zirconia sintered body of this example and has a strong gloss feeling. Got.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Further, the interface of the bezel ring was observed with an optical microscope and SEM observation. As a result, white zirconia and black zirconia are sintered to form an interface, and there is no gap at the interface even though the interface has a curvature, and there is no gap at the interface. It was confirmed that there was no bonding layer.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. Even if the iron ball was dropped from a height of 85 cm, no cracks or cracks occurred. From this, it was confirmed that the white / black zirconia sintered body of this example had a high strength with an impact strength of 85 cm or more.

Example 3
As 3 mol% yttria stabilized zirconia powder, 3 mol% yttria stabilized zirconia powder (trade name: TZ-3Y, manufactured by Tosoh Corporation) having a BET specific surface area of 15 m ² / g was used, and the alumina weight was 10 wt%. In the same manner as in Example 1, except that high-purity aluminum oxide was added, the firing temperature was 1500 ° C., and the HIP treatment temperature was 1450 ° C., this was subjected to molding, firing and HIP treatment. The white / black zirconia sintered body of the example was obtained. The production conditions of this example are shown in Table 1, and the evaluation results are shown in Table 2.

  The obtained white / black zirconia sintered body had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.6%. It was.

  Next, the obtained white / black zirconia sintered body is processed and polished in the same manner as in Example 1, and is made of the white / black zirconia sintered body of this example and has a strong gloss feeling. Got.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Further, the interface of the bezel ring was observed with an optical microscope and SEM observation. As a result, white zirconia and black zirconia are sintered to form an interface, and there is no gap at the interface even though the interface has a curvature, and there is no gap at the interface. It was confirmed that there was no bonding layer.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. Even if the iron ball was dropped from a height of 85 cm, no cracks or cracks occurred. From this, it was confirmed that the white / black zirconia sintered body of this example had a high strength with an impact strength of 85 cm or more.

Example 4
As 3 mol% yttria stabilized zirconia powder, 3 mol% yttria stabilized zirconia powder having a BET specific surface area of 15 m ² / g (trade name: TZ-3Y, manufactured by Tosoh Corporation) was used, and the firing temperature was 1400. The white / black zirconia sintered body of this example was obtained by molding, firing, and HIP treatment in the same manner as in Example 1 except that the temperature was set to ° C. The production conditions of this example are shown in Table 1, and the evaluation results are shown in Table 2.

  The white / black zirconia sintered body obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.7%. It was.

  Next, the obtained white / black zirconia sintered body is processed and polished in the same manner as in Example 1, and is made of the white / black zirconia sintered body of this example and has a strong gloss feeling. Got.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Further, the interface of the bezel ring was observed with an optical microscope and SEM observation. As a result, white zirconia and black zirconia are sintered to form an interface, and there is no gap at the interface even though the interface has a curvature, and there is no gap at the interface. It was confirmed that there was no bonding layer.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. Even if the iron ball was dropped from a height of 85 cm, no cracks or cracks occurred. From this, it was confirmed that the white / black zirconia sintered body of this example had a high strength with an impact strength of 85 cm or more.

Example 5
The same method as in Example 1 except that a 3 mol% yttria-stabilized zirconia powder having a BET specific surface area of 15 m ² / g was used as the 3 mol% yttria-stabilized zirconia powder, and the firing temperature was 1350 ° C. The white / black zirconia sintered body of this example was obtained by molding, firing and HIP treatment. The production conditions of this example are shown in Table 1, and the evaluation results are shown in Table 2.

  The white / black zirconia sintered body obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.7%. It was.

  Next, the obtained white / black zirconia sintered body is processed and polished in the same manner as in Example 1, and is made of the white / black zirconia sintered body of this example and has a strong gloss feeling. Got.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Further, the interface of the bezel ring was observed with an optical microscope and SEM observation. As a result, white zirconia and black zirconia are sintered to form an interface, and there is no gap at the interface even though the interface has a curvature, and there is no gap at the interface. It was confirmed that there was no bonding layer.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. . Even if the iron ball was dropped from a height of 85 cm, no cracks or cracks occurred. From this, it was confirmed that the white / black zirconia sintered body of this example had a high strength with an impact strength of 85 cm or more.

Comparative Example 1
The white / black zirconia sintered body of this comparative example was obtained by molding and firing in the same manner as in Example 1 except that the HIP treatment was not performed. The production conditions of this comparative example are shown in Table 1, and the evaluation results are shown in Table 2.

  The white / black zirconia sintered body thus obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 98.8%. It was.

  Next, the obtained white / black zirconia sintered body was processed and polished in the same manner as in Example 1 to obtain a bezel ring made of the white / black zirconia sintered body of this comparative example.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the sintered body was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Optical microscope observation of the interface of the bezel ring was performed. The results are shown in FIG. From FIG. 15, it can be confirmed that the zirconia sintered body of the present comparative example has an interface (the broken line circle in FIG. 15). However, it was confirmed that the interface has a gap (arrow part in FIG. 15).

  Further, FIG. 3 shows a reflected electron image at the interface of the bezel ring. From FIG. 3, it can be confirmed that the zirconia sintered body of this comparative example has an interface (dotted line circle in FIG. 3). However, as indicated by the arrows in FIG. 3, it was confirmed that a gap having a width of about 5 μm was generated in the range of 100 μm or more at the interface (arrow part in FIG. 3).

  From these results, the bezel ring made of the white / black zirconia sintered body of this comparative example and the white / black zirconia sintered body of this comparative example has a gap at the interface, and there is a gap at the interface. Therefore, it was confirmed that no color blur occurred.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. When the iron ball was dropped from a height of 10 cm, the white / black zirconia sintered body of this comparative example was destroyed. From this, it was confirmed that the white / black zirconia sintered body of this comparative example has an impact strength of 10 cm or less and is inferior in mechanical strength.

Comparative Example 2
The use of high-purity silica in place of high-purity aluminum oxide so that the weight of silica relative to the total weight of yttria and zirconia in 3 mol% yttria-stabilized zirconia powder was 5% by weight (trade name) : 1-FX, manufactured by Tatsumori Co., Ltd.) and white / black zirconia sintered in this comparative example by molding and firing in the same manner as in Example 1 except that HIP treatment was not performed. Got the body.

  The obtained white / black zirconia sintered body was visually confirmed. As a result, it was confirmed that the sintered body had cracks starting from the gaps at the interface and many other cracks, and the sintered body was broken. For this reason, the sintered body was not subjected to HIP treatment. The production conditions of this comparative example are shown in Table 1, and the evaluation results are shown in Table 2. Since the white / black zirconia sintered body of this comparative example was broken, the relative density could not be measured.

  Further, a part of the fractured sintered body is collected, and the white / black zirconia sintered body part of the black / white zirconia sintered body side of the comparative example is partially confirmed until the convex portion of the white zirconia sintered body is clearly confirmed. The surface was processed. When the white / black zirconia sintered body of this comparative example after processing was visually confirmed, the color tone of the white zirconia sintered body in the vicinity of the interface was blurred, and the pattern formed by the white zirconia sintered body was blurred It was a thing. Thereby, it was confirmed that the sintered body had color bleeding at the interface.

Comparative Example 3
Using high-purity aluminum oxide and high-purity zinc oxide powder (trade name: special grade zinc oxide, manufactured by Kishida Chemical Co., Ltd.) The weight of zinc oxide relative to the total weight of yttria and zirconia in 3 mol% yttria-stabilized zirconia powder is 1 weight. The white / black zirconia sintered body of this comparative example was molded and fired in the same manner as in Example 1 except that the zinc oxide powder was added and HIP treatment was not performed. Got. The production conditions of this comparative example are shown in Table 1, and the evaluation results are shown in Table 2.

  The white / black zirconia sintered body thus obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 98.8%. It was.

  Next, the obtained white / black zirconia sintered body was processed and polished in the same manner as in Example 1 to obtain a bezel ring made of the white / black zirconia sintered body of this comparative example.

  Optical microscope observation and SEM observation of the interface of the bezel ring were performed. As a result, white zirconia and black zirconia were sintered to form an interface, but it was confirmed that the interface had a gap.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was blurred and color blur was generated on the interface. Further, the interface of the bezel ring was observed with an optical microscope. The results are shown in FIG. From FIG. 5, since the vicinity of the interface of the white zirconia sintered body was gradually discolored, it was confirmed that the white zirconia sintered body did not have a clear interface (dashed line square portion in FIG. 5).

  Further, EPMA analysis was performed near the interface of the bezel ring. The results are shown in Table 3. In the white zirconia sintered body, an iron element as a coloring component of the black zirconia sintered body was confirmed in a region within 130 μm from the interface. Furthermore, the cobalt element which is a coloring component of a black zirconia sintered compact was confirmed in the area | region within 50 micrometers from an interface. From this, it was confirmed that the iron transition region of this comparative example was a region within 130 μm from the interface, and the cobalt transition region was a region within 50 μm from the interface.

  Further, the iron element and the cobalt element each had a concentration exceeding 1% by weight in a region within 30 μm from the interface. It is considered that the iron element and the cobalt element in these regions are one of the causes of color bleeding.

Comparative Example 4
Molding and firing in the same manner as in Example 1 except that the temperature of the molding die at the time of injection molding of the white zirconia raw material was 50 ° C. and the molding temperature at the time of injection molding of the black zirconia raw material was not controlled And the white / black zirconia sintered compact of this comparative example was obtained by carrying out HIP processing. The temperature of the mold during the injection molding of the black zirconia raw material was 60 ° C. The production conditions of this comparative example are shown in Table 1, and the evaluation results are shown in Table 2.

  The white / black zirconia sintered body obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.7%. It was.

  Next, the obtained white / black zirconia sintered body was processed and polished in the same manner as in Example 1 to obtain a bezel ring made of the white / black zirconia sintered body of this comparative example.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface of the pattern made of the white zirconia sintered body was blurred and color blurring occurred in the interface. An optical micrograph of the interface of the bezel ring is shown in FIG. From FIG. 16, the pattern formed by the white zirconia sintered body gradually disappears due to color bleeding, and the 0.15 mm thick line pattern formed by the white zirconia sintered body is in the middle. It has been confirmed that it has disappeared (dotted line square portion in FIG. 16).

Example 6
A watch bezel ring made of a white zirconia sintered body and a black zirconia sintered body was produced.
(Preparation of white zirconia raw material)
3 mol% yttria stabilized zirconia powder having a BET specific surface area of 15 m ² / g (trade name: TZ High purity aluminum oxide (purity; 99.9%) was added to -3Y manufactured by Tosoh Corporation.

  After the addition, these powders were mixed with a ball mill for 24 hours in an ethanol solvent using zirconia balls having a diameter of 10 mm. The mixed powder was dried to obtain white zirconia powder.

An acrylic binder was mixed with the obtained white zirconia powder to make a white zirconia raw material. The content of white zirconia powder in the white zirconia raw material was 45% by volume.
(Preparation of black zirconia raw material)
Commercially available black zirconia powder (trade name: TZ-Black, manufactured by Tosoh Corporation) was used as the black zirconia powder. The powder has the following composition: a spinel oxide powder containing iron and cobalt in which a part of cobalt is substituted with Zn and a part of iron is substituted with Al; and 3 mol% yttria-containing zirconia It is a powder. Further, the content of the spinel oxide is 3.5% by weight.

(Co _0.7 Zn _0.3 ) (Fe _0.7 Al _0.3 ) ₂ O ₄

An acrylic binder was mixed with the black zirconia powder to make a black zirconia raw material. In addition, content of the black zirconia powder in a black zirconia raw material was 45 volume%.
(Production of molded body)
The white zirconia raw material was injection-molded to obtain a bezel-ring-shaped white zirconia molded body having convex portions. At this time, the temperature of the mold was 65 ° C., and the pressure of injection molding was 100 MPa.

  Next, a black zirconia raw material was injection-molded on the obtained white zirconia molded body. The pressure of injection molding was 100 MPa, and the temperature of the mold was 15 ° C. lower than the temperature of the white zirconia raw material injection mold. Thereby, the molded object which both joined in the shape which the black zirconia molded object laminated | stacked on the white zirconia molded object was obtained.

The obtained molded body was degreased in the atmosphere at a heating rate of 2.0 ° C./h, a degreasing temperature of 450 ° C., and a degreasing time of 4 hours.
(Baking and HIP treatment)
The pre-sintered body was obtained by firing the molded body after the degreasing treatment in the air at a heating rate of 100 ° C./h, a firing temperature of 1400 ° C., and a sintering time of 2 hours.

  After placing the obtained pre-sintered body in an alumina container, under an atmosphere of argon gas having a purity of 99.9%, HIP treatment was performed at an HIP temperature of 1350 ° C., an HIP pressure of 150 MPa, and a holding time of 1 hour, A HIP-treated product was obtained. The HIP-treated body was the white / black zirconia sintered body of this example. The production conditions of this example are shown in Table 4, and the evaluation results are shown in Table 5.

The white / black zirconia sintered body obtained had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.7%. It was.
(Component processing)
The surface of the white / black zirconia sintered body side of the white / black zirconia sintered body of this example was processed until the convex portion of the white zirconia sintered body was clearly observed. Thereby, the white / black zirconia sintered body of this example was used as a bezel ring having a pattern made of a white zirconia sintered body on the surface of the black zirconia sintered body. By polishing the bezel ring after surface processing, a bezel ring made of the white / black zirconia sintered body of this example and having a strong gloss was obtained.

The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface. Moreover, the interface of the said bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.
(Evaluation)
Optical microscope observation of the interface of the bezel ring was performed. The results are shown in FIG. It was found that white zirconia and black zirconia were sintered to form an interface, and no gap was formed in the interface (dotted line circle in FIG. 17).

  Further, a secondary electron image at the interface of the bezel ring is shown in FIG. The interface could also be confirmed in the reflected electron image (arrow part in FIG. 18). Further, it was confirmed that no gap was formed at the interface and that there was no bonding layer.

  From these results, it was confirmed that the white / black zirconia sintered body of this example did not have a gap at the interface.

  Further, EPMA analysis was performed on the interface of the bezel ring and in the vicinity of the interface. The results are shown in Table 5. Although the iron element could be confirmed in the region within 50 μm from the interface of the white zirconia sintered body, the iron element which is the coloring component of the black zirconia sintered body was not confirmed in the region within 100 μm from the interface. Furthermore, cobalt element was not confirmed even in a region within 30 μm from the interface. From these results, it was confirmed that in the white / black zirconia sintered body of this example, the iron transition region was within 50 μm from the interface, and there was no cobalt transition region. Further, the Fe concentration present in the vicinity of the interface was 0.5% by weight.

  It was confirmed that the white / black zirconia sintered body of this example did not have interfacial color bleeding and gaps even though a small amount of Fe was contained in the white zirconia sintered body.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. Even if the iron ball was dropped from a height of 85 cm, no cracks or cracks occurred. From this, it was confirmed that the white / black zirconia sintered body of this example had a high strength with an impact strength of 85 cm or more.

Example 7
A white / black zirconia sintered body of this example was obtained by molding, firing, and HIP treatment in the same manner as in Example 6 except that the firing temperature was 1350 ° C. The production conditions of this example are shown in Table 4, and the evaluation results are shown in Table 5.

  The obtained white / black zirconia sintered body had a volume ratio of 41:59 between the white zirconia sintered body and the black zirconia sintered body, and the relative density of the white / black zirconia sintered body was 99.6%. It was.

  Next, the obtained white / black zirconia sintered body is processed and polished in the same manner as in Example 6, and is made of the white / black zirconia sintered body of this example, and has a strong gloss feeling. Got.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Further, the interface of the bezel ring was observed with an optical microscope and SEM observation. As a result, white zirconia and black zirconia are sintered to form an interface, and there is no gap at the interface even though the interface has a curvature, and there is no gap at the interface. It was confirmed that there was no bonding layer.

  Further, EPMA composition analysis was performed on the interface of the bezel ring and in the vicinity of the interface. The results are shown in Table 5. Although the iron element could be confirmed in the region within 50 μm from the interface of the white zirconia sintered body, the iron element which is the coloring component of the black zirconia sintered body was not confirmed in the region within 100 μm from the interface. Furthermore, cobalt element was not confirmed even in a region within 30 μm from the interface. From these results, it was confirmed that in the white / black zirconia sintered body of this example, the iron transition region was within 50 μm from the interface, and there was no cobalt transition region. Further, the Fe concentration present in the vicinity of the interface was 0.5% by weight.

Reference Example A green / black zirconia sintered body composed of a green zirconia sintered body and a black zirconia sintered body was produced.

That is, the BET specific surface area is 15 m ² / g and the alumina content is 0.25 wt% so that the weight of nickel oxide is 4 wt% with respect to the total weight of yttria and zirconia in the 3 mol% yttria stabilized zirconia powder. 3 mol% yttria-stabilized zirconia powder (trade name: TZ-3YSE, manufactured by Tosoh Corporation) was added with nickel oxide powder (trade name: nickel oxide, manufactured by High-Purity Chemical), and 3 mol% yttria-stabilized zirconia Silica powder (trade name: 1-FX, manufactured by Tatsumori Co., Ltd.) was added to the zirconia powder so that the weight of silica (SiO ₂ ) with respect to the total weight of yttria and zirconia in the powder was 2% by weight.

  After the addition, these powders were mixed with a ball mill for 24 hours in an ethanol solvent using zirconia balls having a diameter of 10 mm. The mixed powder was dried to obtain green zirconia powder.

  In the same manner as in Example 1 except that the green zirconia powder was used instead of white zirconia powder and the firing temperature was 1400 ° C., the green / white color of this example was obtained by molding, firing and HIP treatment. A black zirconia sintered body was obtained. The production conditions of this example are shown in Table 6, and the evaluation results are shown in Table 7.

  The green / black zirconia sintered body thus obtained had a volume ratio of 41:59 between the green zirconia sintered body and the black zirconia sintered body, and the relative density of the green / black zirconia sintered body was 99.9%. It was.

  Next, the obtained green / black zirconia sintered body is processed and polished in the same manner as in Example 1, and is made of the green / black zirconia sintered body of this reference example and has a strong gloss feeling. Got.

  The bezel ring had a surface made of a black zirconia sintered body, and had a pattern made of a green zirconia sintered body on the surface.

  The interface of the bezel ring was confirmed visually. As a result, it was confirmed that the green color of the interface was not blurred and the interface had no color blur.

  Further, the interface of the bezel ring was observed with an optical microscope and SEM observation. As a result, green zirconia and black zirconia are sintered to form an interface, and even though the interface has a curvature, there is no gap at the interface, and there is no gap at the interface. It was confirmed that there was no bonding layer.

  Furthermore, the mechanical strength test of the obtained bezel ring was performed. Even when the iron ball was dropped from a height of 85 cm, no cracks or cracks were generated, and it was confirmed that the green / black zirconia sintered body of this reference example had high strength.

  As a result, even if a zirconia sintered body containing silica and a transition metal oxide is used instead of the light-colored sintered body, the zirconia sintered body containing the spinel oxide and the zirconia sintered body containing the spinel oxide are used. It turned out that the multicolor zirconia sintered compact with the dark-colored sintered compact which is a body is obtained.

Example 8
A disc-shaped white / black zirconia sintered body composed of a white zirconia sintered body and a black zirconia sintered body was produced.
(Preparation of raw materials)
White zirconia powder obtained by the same method as in Example 1 was used as a white zirconia raw material, and commercially available black zirconia powder (trade name: TZ-Black, manufactured by Tosoh Corporation) was used as a black zirconia raw material.
(Production of molded body)
A white primary zirconia material was uniaxially press-molded at room temperature to obtain a convex primary molded body. The obtained primary compact was filled with black zirconia powder, and the primary compact and black zirconia powder were simultaneously uniaxially press-molded. A secondary compact was obtained by subjecting the compact after uniaxial pressing to cold isostatic pressing (CIP). The pressure for CIP treatment was 200 MPa, and the CIP temperature was room temperature or lower.
(Baking and HIP treatment)
The white / black zirconia sintered body of this example was obtained by firing and HIP treatment in the same manner as in Example 1 except that the obtained secondary molded body was used.
(Component processing)
The surface of the white / black zirconia sintered body side of the white / black zirconia sintered body of this example was processed until the convex portion of the white zirconia sintered body was clearly observed. As a result, the white / black zirconia sintered body of this example was used as a disc-shaped zirconia sintered body having a pattern made of a white zirconia sintered body on the surface of the black zirconia sintered body. By polishing the disk-shaped zirconia sintered body after the surface processing, a disk-shaped zirconia sintered body made of the white / black zirconia sintered body of this example and having a strong gloss feeling was obtained. An overview of the obtained disk-shaped zirconia sintered body is shown in FIG. The disc-shaped zirconia sintered body had a diameter of 16 mm and a thickness of 2.5 mm, and the pattern width was 3 mm.

  The interface of the disk-shaped zirconia sintered body was visually confirmed. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Furthermore, the interface of the disk-shaped zirconia sintered body was observed with an optical microscope and SEM observation. As a result, white zirconia and black zirconia are sintered to form an interface, and there is no gap at the interface even though the interface has a curvature, and there is no gap at the interface. It was confirmed that there was no bonding layer.

Example 9
As 3 mol% yttria stabilized zirconia powder, 3 mol% yttria stabilized zirconia powder (trade name: TZ-3Y, manufactured by Tosoh Corporation) having a BET specific surface area of 15 m ² / g was used, and the alumina weight was 10 wt%. In the same manner as in Example 8, except that high-purity aluminum oxide was added to the zirconia powder, the firing temperature was 1450 ° C., and the HIP treatment temperature was 1400 ° C., The white / black zirconia sintered body of this example was obtained by firing and HIP treatment. Further, the obtained white / black zirconia sintered body was processed in the same manner as in Example 8, and a disk-shaped zirconia sintered body having a diameter of 16 mm and a thickness of 2.5 mm and a pattern width of 3 mm was obtained. .

  The disk-shaped zirconia sintered body had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the disk-shaped zirconia sintered body was visually confirmed. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Furthermore, the interface of the disk-shaped zirconia sintered body was observed with an optical microscope and SEM observation. As a result, it was confirmed that white zirconia and black zirconia were sintered to form an interface, that no gap was formed at the interface, and that there was no bonding layer.

Example 10
As 3 mol% yttria stabilized zirconia powder, 3 mol% yttria stabilized zirconia powder having a BET specific surface area of 15 m ² / g (trade name: TZ-3Y, manufactured by Tosoh Corporation) was used, and the firing temperature was 1400. The white / black zirconia sintered body of this example was obtained by molding, firing, and HIP treatment in the same manner as in Example 8 except that the temperature was set to ° C. Further, the obtained white / black zirconia sintered body was processed in the same manner as in Example 8, and a disk-shaped zirconia sintered body having a diameter of 16 mm and a thickness of 2.5 mm and a pattern width of 3 mm was obtained. .

  The disk-shaped zirconia sintered body had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the disk-shaped zirconia sintered body was visually confirmed. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Furthermore, the interface of the disk-shaped zirconia sintered body was observed with an optical microscope and SEM observation. As a result, it was confirmed that white zirconia and black zirconia were sintered to form an interface, that no gap was formed at the interface, and that there was no bonding layer.

Example 11
As 3 mol% yttria-stabilized zirconia powder, 3 mol% yttria-stabilized zirconia powder (trade name: TZ-3Y, manufactured by Tosoh Corporation) having a BET specific surface area of 15 m ² / g was used. The white / black zirconia sintered body of this example was obtained by molding, firing, and HIP treatment by various methods. Further, the obtained white / black zirconia sintered body was processed in the same manner as in Example 8, and a disk-shaped zirconia sintered body having a diameter of 16 mm and a thickness of 2.5 mm and a pattern width of 3 mm was obtained. .

  The disk-shaped zirconia sintered body had a surface made of a black zirconia sintered body, and had a pattern made of a white zirconia sintered body on the surface.

  The interface of the disk-shaped zirconia sintered body was visually confirmed. As a result, it was confirmed that the white color of the interface was not blurred and the interface had no color blur.

  Furthermore, the interface of the disk-shaped zirconia sintered body was observed with an optical microscope and SEM observation. As a result, it was confirmed that white zirconia and black zirconia were sintered to form an interface, that no gap was formed at the interface, and that there was no bonding layer.

  The zirconia sintered body of the present invention can be widely used for watch parts, decorative articles, portable device parts, in-vehicle parts, high-grade daily parts, and the like. In particular, the zirconia sintered body of the present invention includes watch parts such as watch bands, bezels, dials, watch cases, decorative parts such as brooches, tie pins, handbag fittings, bracelets, portable electronic device cases, lighter cases, cosmetics. It can be used for exterior parts such as cases, mobile phone cases, and earphone housings, as well as daily necessities such as knives and cooking utensils, and logos of various products.

(1) ... Light-colored sintered body (2) ... Dark-colored sintered body (3) ... Interface (4) ... Region of light-colored sintered body at a certain distance from the interface (5) ..A circle with a diameter of 10 μm formed around a light-colored sintered body at a certain distance from the interface

Claims (9)

  A zirconia sintered body including a first zirconia sintered body and a second zirconia sintered body, wherein the first zirconia sintered body is a zirconia sintered body containing aluminum oxide, The zirconia sintered body is a zirconia sintered body containing a spinel oxide, the first zirconia sintered body and the second zirconia sintered body form a grain boundary, and the grain boundary has a gap and a color. A zirconia sintered body characterized by having no bleeding.   The zirconia sintered body of one of the first zirconia sintered body and the second zirconia sintered body forms a pattern on the surface of the other zirconia sintered body. The zirconia sintered body according to 1.   The zirconia sintered body according to claim 1, wherein the relative density is 99.5% or more.   The zirconia sintered body according to any one of claims 1 to 3, wherein the first zirconia sintered body contains 0.25 wt% or more and 20 wt% or less of aluminum oxide.   The zirconia sintered body according to any one of claims 1 to 4, wherein the spinel oxide contained in the second zirconia sintered body is a spinel oxide containing iron and cobalt. 6. The zirconia sintered body according to claim 1, wherein the spinel oxide contained in the second zirconia sintered body has the following composition.
^{_{(Co X M 2+ 1-X}} ) (Fe Y M 3+ 1-Y) 2 O 4
However, M < ²⁺ > is at least one of Zn or Mn, M < ³⁺ > is at least one of Al or Cr, and 0.1 <X <= 1 and 0.5 <Y <= 1.   A primary molding step in which either a zirconia powder containing aluminum oxide or a zirconia powder containing a spinel oxide is molded to obtain a primary molded body, on the primary molded body at a molding temperature equal to or lower than the primary molding step. A secondary molding step of forming the other zirconia powder to obtain a secondary molded body, a sintering step of firing the secondary molded body at 1300 ° C. or higher to obtain a preliminary sintered body, and 1250 of the preliminary sintered body The manufacturing method of the zirconia sintered compact as described in any one of Claims 1 thru | or 6 including the HIP process process of carrying out hot isostatic pressing at 100 degreeC or more and 1650 degrees C or less and 100 MPa or more and 250 MPa or less.   The manufacturing method according to claim 7, wherein the molding in the secondary molding step is injection molding.   The member containing the zirconia sintered compact as described in any one of Claims 1 thru | or 6.