JP2015042191A

JP2015042191A - Dental wax

Info

Publication number: JP2015042191A
Application number: JP2013174042A
Authority: JP
Inventors: 順一田代; Junichi Tashiro
Original assignee: Individual
Current assignee: Individual
Priority date: 2013-08-25
Filing date: 2013-08-25
Publication date: 2015-03-05
Anticipated expiration: 2033-08-25
Also published as: JP6188486B2

Abstract

PROBLEM TO BE SOLVED: To provide a dental wax facilitating a reformation of a margin part and capable of providing sufficient strength of an occlusion part and the like other than the margin part.SOLUTION: The disk-shaped dental wax for forming a prosthetic appliance covering the surface of a tooth by a lost wax process, includes a high-strength wax layer on one surface side and a high-precision wax layer on the other surface side. The high-strength wax includes resin, however, the high-precision wax includes no resin. The thickness of the high-strength wax layer is defined as 70% or more of the thickness of the disk shape, and most of parts other than the margin part are formed of the high-strength wax.

Description

本発明はロストワックス法によって歯の表面を被覆する補綴物を作成するためのディスク形状の歯科用ワックスに関する。 The present invention relates to a disc-shaped dental wax for producing a prosthesis covering a tooth surface by the lost wax method.

v
鋳造冠等の歯の表面を被覆する補綴物を作成する際には、ロストワックス法が広く用いられている。歯の形状に成形したワックスを埋没材に内包させ、加熱によって埋没材を固化させつつワックスを焼却・除去し、ワックスが除去された箇所に鋳造用合金を流し込み、埋没材を型として、鋳造冠等の補綴物を作成するものである。 v
When creating a prosthesis that covers the surface of a tooth such as a cast crown, the lost wax method is widely used. Incorporate the wax molded into the shape of the teeth in the investment material, incinerate and remove the wax while solidifying the investment material by heating. Or the like.

近年、ワックスを歯の形状に成形するためにＣＡＤ／ＣＡＭ技術が用いられることが多くなってきている。職人的な技能を必要とせずに一定の精度で成形できるので、有効である。 In recent years, CAD / CAM technology is increasingly used to form wax into a tooth shape. It is effective because it can be molded with a certain accuracy without requiring craftsmanship.

ワックスの成形において、補綴物と歯又は歯肉との境界であるマージン部には十分な精度が求められる。マージン部の精度が低ければ歯の表面の被覆が不適切となり、使用者の健康を害する恐れがある。
特許文献１には、レーザー光によるマージン部の計測精度を向上させる歯科用ワックス材料が開示されている。ＣＡＤにおけるマージン部の精度を向上させるものである。 In the molding of wax, sufficient accuracy is required for a margin portion that is a boundary between a prosthesis and a tooth or gingiva. If the accuracy of the margin portion is low, the tooth surface coating becomes inadequate, which may harm the health of the user.
Patent Document 1 discloses a dental wax material that improves the measurement accuracy of a margin portion by laser light. This is to improve the accuracy of the margin part in CAD.

一方、現在のＣＡＭ技術によってワックスを成型する場合、ＣＡＭ加工の後、ロストワックス法によって補綴物を鋳造する前に、ワックスのマージン部を成型し直して（操作して）精度を高めることとなる。このためには、マージン部に用いられるワックスが操作容易で高精度のものであることが好ましい。しかし、マージン部以外の部分、例えば咬合部や連結部（連結冠の場合）は、用いられるワックスが高強度であるほうが操作上好ましい。 On the other hand, when the wax is molded by the current CAM technology, after the CAM process and before the prosthesis is cast by the lost wax method, the margin portion of the wax is reshaped (manipulated) to improve the accuracy. . For this purpose, it is preferable that the wax used in the margin portion is easy to operate and highly accurate. However, it is preferable in terms of operation that the wax used has a high strength in parts other than the margin part, for example, the occlusal part and the connecting part (in the case of a connecting crown).

従来、ＣＡＭ技術を用いずに人手作業でワックスを形成する場合においては、支台模型の表面に操作容易で高精度のワックスを塗布し、その上に強度と彫刻性の高いワックスで歯型を形成することもあった。マージン部の形成を容易にするためである。しかし、ＣＡＭ技術では１枚のワックスディスクを使用するため、２種類のワックスを用いることがなかった。 Conventionally, when manually forming wax without using CAM technology, a highly accurate wax is applied to the surface of the abutment model, and a tooth mold is formed on the surface with wax having high strength and engraving. Sometimes formed. This is to facilitate the formation of the margin portion. However, in the CAM technology, since one wax disk is used, two types of waxes are not used.

特開２００１−１１２７９０号公報JP 2001-112790 A

解決しようとする課題は、マージン部の再形成を容易にし、かつ、咬合部等のマージン部以外の強度が十分に得られる歯科用ワックスを提供することである。 The problem to be solved is to provide a dental wax that facilitates the re-formation of the margin part and can sufficiently obtain strength other than the margin part such as the occlusal part.

本発明の歯科用ワックスは、ロストワックス法によって歯の表面を被覆する補綴物を作成するためのディスク形状の歯科用ワックスであって、一面側に高強度ワックス層を有し、他面側に高精度ワックス層を有することを特徴とする。 The dental wax of the present invention is a disc-shaped dental wax for producing a prosthesis covering the tooth surface by the lost wax method, and has a high-strength wax layer on one side and the other side. It has a high-precision wax layer.

マージン部を高精度ワックスによって成形することができる。ここで、「高強度ワックス」及び「高精度ワックス」とは、これら２種のワックス間の相対的な性質の相違として、高強度ワックスはより硬度が高く、高精度ワックスはより操作性が高いことを言う。ここで「操作性」とは、人手による操作が容易であることである。 The margin portion can be formed with high-precision wax. Here, “high-strength wax” and “high-precision wax” mean that the high-strength wax has higher hardness and the high-precision wax has higher operability as the difference in relative properties between these two types of waxes. Say that. Here, “operability” means that manual operation is easy.

本発明の歯科用ワックスは、前記高強度ワックス層に、レジンを含有することを特徴とする。 The dental wax of the present invention is characterized in that the high-strength wax layer contains a resin.

「高強度ワックス」には硬度の高いレジンを含有するワックスを用いる。
通常のワックスはレジンを含有しない又は濃度の低いものであり、硬度が低いものが多く、「高精度ワックス」として用いることができ、器具（インスツルメント等）を用いて人手で加工し、マージン部の再形成することが容易である。
鋳造用原型材料として用いられる歯科用ワックス、特にインレーワックス及びレディキャスティングワックスは、レジンを意図的に含有させることをしない限り、「高精度ワックス」として用いることができる。なお、インレーワックスは、パラフィン、カルナウバ蝋、蜜蝋、ダンマル及びセレシンを成分として含む。 For the “high-strength wax”, a wax containing a resin having high hardness is used.
Ordinary wax does not contain a resin or has a low concentration, and many of them have low hardness, and can be used as a “high-precision wax”. It is easy to reform the part.
Dental waxes, particularly inlay waxes and ready casting waxes, which are used as casting prototype materials can be used as “high-precision waxes” unless the resin is intentionally included. The inlay wax contains paraffin, carnauba wax, beeswax, dammar and ceresin as components.

本発明の歯科用ワックスは、前記高強度ワックス層の厚みが前記ディスク形状の厚みの７０％以上であることを特徴とする。 The dental wax of the present invention is characterized in that the thickness of the high-strength wax layer is 70% or more of the thickness of the disk shape.

マージン部は補綴物の上端または下端にのみ位置する。他の部分は高強度ワックスによる成形が望ましく、高強度ワックス層の厚みをディスク形状の厚みの７０％以上として、マージン部以外の多くが高強度ワックスによる成形となるようにする。 The margin part is located only at the upper end or the lower end of the prosthesis. The other portions are desirably molded with high-strength wax, and the thickness of the high-strength wax layer is set to 70% or more of the thickness of the disk shape so that many portions other than the margin portion are molded with high-strength wax.

マージン部の再形成が容易であり、かつ、咬合部等のマージン部以外の強度が十分に得られる歯科用ワックスを提供することができる。 It is possible to provide a dental wax in which the margin portion can be easily re-formed and sufficient strength other than the margin portion such as the occlusal portion can be obtained.

図１は、歯科用ワックスを示す図である。FIG. 1 is a diagram showing dental wax. 図２は、歯科用ワックスの加工形状を示す図である。FIG. 2 is a diagram showing a processed shape of dental wax. 図３は、歯科用ワックスの加工位置を示す図である。FIG. 3 is a diagram showing a processing position of dental wax. 図４は、ロストワックス法を説明する図である。FIG. 4 is a diagram for explaining the lost wax method.

（ワックスの構成）
図１は、歯科用ワックスを示す図である。歯科用ワックス１は、例えば直径９０ｍｍ、厚さ２０ｍｍの円盤状であり、高強度ワックス層１１の厚さが１５ｍｍ、高精度ワックス層１２の厚さが５ｍｍである。
高強度ワックス層１１はレジンを含有する。
高精度ワックス層１２はレジンを含有しない。 (Wax composition)
FIG. 1 is a diagram showing dental wax. The dental wax 1 has, for example, a disk shape with a diameter of 90 mm and a thickness of 20 mm, the high-strength wax layer 11 has a thickness of 15 mm, and the high-precision wax layer 12 has a thickness of 5 mm.
The high-strength wax layer 11 contains a resin.
The high-precision wax layer 12 does not contain a resin.

（ＣＡＭによる加工）
図２は、歯科用ワックスの加工形状を示す図である。歯科用ワックスをＣＡＭシステムによって加工形状２に加工する。 (Processing by CAM)
FIG. 2 is a diagram showing a processed shape of dental wax. The dental wax is processed into the processed shape 2 by the CAM system.

加工形状２は、補綴物と歯又は歯肉との境界に対応するマージン部２２（図において下方の楕円形状実線及び点線の部分）とその他の本体部２１を有する。 The processed shape 2 includes a margin portion 22 (the lower oval solid line and dotted line portions in the figure) corresponding to the boundary between the prosthesis and the teeth or gingiva, and the other main body portion 21.

図３は、歯科用ワックスの加工位置を示す図である。ＣＡＭシステムによる加工において、マージン部２２を高精度ワックス層１２内に配し、本体部２１の大半、少なくとも咬合部分を、高強度ワックス層１１内に配する。 FIG. 3 is a diagram showing a processing position of dental wax. In processing by the CAM system, the margin portion 22 is disposed in the high-precision wax layer 12, and most of the main body portion 21, at least the occlusal portion, is disposed in the high-strength wax layer 11.

以上により、マージン部２２が高精度ワックスであり、咬合部を含む本体部２１の大半が高強度ワックスである歯科用ワックスが切り出される。 Thus, the dental wax in which the margin portion 22 is a high-precision wax and the main body portion 21 including the occlusal portion is a high-strength wax is cut out.

（補綴物の作成）
切り出された歯科用ワックスのマージン部２２について、器具（インスツルメント等）を用いて人手で加工し、サイズを調整する。
マージン部２２は高精度ワックスである。ワックスがレジンを含有しないので、硬度が低く、インスツルメント等の器具を用いた人手による高精度の調整が容易になる。 (Create a prosthesis)
About the margin part 22 of the cut-out dental wax, it processes manually using an instrument (instrument etc.) and adjusts a size.
The margin part 22 is a high-precision wax. Since the wax does not contain a resin, the hardness is low, and high-precision adjustment using a tool such as an instrument is easy.

図４は、ロストワックス法を説明する図である。図は、容器３の断面図である。
容器３に石膏の埋没材３１と加工形状２に加工されたワックス２３を入れる。加工されたワックス２３の下部には穴部３２が設けられている。 FIG. 4 is a diagram for explaining the lost wax method. The figure is a cross-sectional view of the container 3.
The container 3 is filled with a gypsum investment material 31 and a wax 23 processed into a processed shape 2. A hole 32 is provided in the lower part of the processed wax 23.

埋没材３１を固化させ、容器３を加熱してワックスを高温により焼却・気化させる。固化した埋没材にはワックスの形状の空洞が形成される。そこに、鋳造用合金を流し込むことで、金属製の補綴物が作成される。穴部３２は溶解した金属の湯道となる。 The investment material 31 is solidified, and the container 3 is heated to incinerate and vaporize the wax at a high temperature. Wax-shaped cavities are formed in the solidified investment material. A casting prosthesis is produced by pouring a casting alloy therein. The hole 32 becomes a molten metal runner.

マージン部の再形成を容易にし、かつ、咬合部等のマージン部以外の強度が十分に得られる歯科用ワックスである。多くの歯科技工士及び歯科医師による利用が考えられる。 It is a dental wax that facilitates the re-formation of the margin part and provides sufficient strength other than the margin part such as the occlusal part. It can be used by many dental technicians and dentists.

１歯科用ワックス
１１高強度ワックス層
１２高精度ワックス層
２加工形状
２１本体部
２２マージン部
２３加工されたワックス
３容器
３１埋没材
３２穴部 DESCRIPTION OF SYMBOLS 1 Dental wax 11 High-strength wax layer 12 High-precision wax layer 2 Processing shape 21 Body part 22 Margin part 23 Processed wax 3 Container 31 Investment material 32 Hole part

Claims

A disc-shaped dental wax for creating a prosthesis that covers the tooth surface by the lost wax method,
Has a high-strength wax layer on one side,
A dental wax having a high-precision wax layer on the other side.

The high-strength wax layer contains a resin,
The dental wax according to claim 1, wherein the high-precision wax layer does not contain a resin.

The dental wax according to claim 1 or 2, wherein the thickness of the high-strength wax layer is 70% or more of the thickness of the disk shape.