JP2014237870A - Bearing component and roller bearing - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide bearing components and a roller bearing that are improved in durability.SOLUTION: There are provided bearing components (11, 12, and 13) that are made of steel consisting of 0.95-1.1 mass% carbon, less than 0.3 mass% silicon, less than 0.5 mass% manganese, less than 0.008 mass% sulfur, 1.4-1.6 mass% chromium, and iron and impurities for the rest, and have carbonitrided layers formed at surface layer parts including contact surfaces (11A, 12A, and 13A) as surfaces to come into contact with other components. The surface layer parts have average nitrogen concentrations of 0.3-0.6 mass% and variance of 0.1 mass% or less in nitrogen concentration. The carbonitrided layers are formed by carrying out a carbonitriding process so that ais 0.88-1.27 and α is 0.012-0.020, where Pis undecomposed ammonia partial pressure and Pis hydrogen partial pressure.

Description

  The present invention relates to a bearing component and a rolling bearing, and more particularly to a bearing component with improved durability and a reduced manufacturing cost, and a rolling bearing including the bearing component.

As a measure for improving the durability of bearing parts used for rolling bearings and the like, carbonitriding is known (see, for example, Patent Documents 1 and 2). Carbonitriding treatment, after the steel is heated to a temperature above the A ₁ transformation point of carbon and nitrogen infested diffuse into the steel, a heat treatment for hardening the steel. The carbonitriding process is effective for extending the life under lubrication with foreign matters, which is an important performance of rolling bearings.

JP 2007-277648 A JP 2008-267402 A

  However, in consideration of recent demands for improving the durability of bearing parts, it may be difficult to impart sufficient durability depending on the application in the conventional carbonitriding process. On the other hand, it is also necessary to reduce the manufacturing cost of bearing parts by improving the efficiency of carbonitriding.

  This invention is made | formed in view of the said subject, The objective is to provide a rolling bearing provided with the bearing component which the durability improved, and the manufacturing cost was reduced, and the said bearing component.

The bearing component according to the present invention comprises 0.95 mass% or more and 1.1 mass% or less of carbon, less than 0.3 mass% silicon, less than 0.5 mass% manganese, and 0.008 mass%. Less than sulfur and 1.4% by mass or more and less than 1.6% by mass of chromium, which is made of steel consisting of the remaining iron and impurities, and carburizes the surface layer part including the contact surface that is in contact with other parts This is a bearing component in which a nitride layer is formed. In the bearing component, an average nitrogen concentration in the surface layer portion is 0.3% by mass or more and 0.6% by mass or less, and a variation in nitrogen concentration in the surface layer portion is 0.1% by mass or less. In the above bearing component, the undecomposed ammonia partial pressure _{P N,} the hydrogen partial pressure in an _{P H,} the following equation (1) _a ^{c *} defined by 0.88 or more 1.27 or less, equation ( The carbonitriding layer is formed by performing carbonitriding so that α defined in 2) is 0.012 or more and 0.020 or less.

  The present inventor has intensively studied measures for improving the durability of bearing parts used for rolling bearings and the like and reducing the manufacturing cost. As a result, the following knowledge was obtained and the present invention was conceived.

  In a bearing part, damage such as a crack is likely to occur on a contact surface (for example, a rolling surface of a bearing ring, a rolling surface of a ball and a roller, or the like) that comes into contact with another component and directly below the contact surface. On the other hand, the durability of the bearing component can be improved by subjecting the contact surface to carbonitriding.

  According to the study of the present inventor, when the nitrogen concentration in the surface layer portion including the contact surface is less than 0.2% by mass, the life of the bearing component under the foreign matter mixed lubrication is reduced. Therefore, in order to suppress a decrease in the life of the bearing component, the nitrogen concentration in the surface layer portion needs to be at least 0.2% by mass or more. On the other hand, when the nitrogen concentration in the surface layer portion exceeds 0.7 mass%, the amount of retained austenite becomes excessive, and the hardness of the contact surface decreases. Therefore, in order to suppress the decrease in the hardness of the contact surface, the nitrogen concentration in the surface layer portion needs to be 0.7% by mass or less.

  The bearing component is manufactured by subjecting the formed steel material to a heat treatment such as carbonitriding or tempering, and then finishing the contact surface. The steel material may be deformed by the heat treatment (for example, the raceway may be elliptical and the roundness may be lost), and the grinding allowance during finishing may vary. Therefore, the conventional bearing component has a problem that the variation of the nitrogen concentration becomes large in the surface layer portion.

  On the other hand, in the bearing component according to the present invention, the average nitrogen concentration in the surface layer portion is 0.3% by mass or more and 0.6% by mass or less, and the variation in nitrogen concentration in the surface layer portion is 0.00. It is reduced to 1% by mass or less. For this reason, in the bearing component, the nitrogen concentration in the surface layer portion is 0.2% by mass or more and 0.7% by mass or less, and a decrease in life under lubrication mixed with foreign matter and a decrease in hardness of the contact surface are suppressed. ing. Therefore, according to the bearing component according to the present invention, a bearing component with improved durability can be provided more reliably.

  Further, according to further examination by the present inventor, when the value of α is 0.012 or less, the amount of nitrogen intrusion into the steel within a predetermined time by carbonitriding is almost constant as the value of α increases. However, when the value of α exceeds 0.012, the rate of increase in the nitrogen penetration amount decreases. Therefore, by setting the value of α to 0.012 or more, nitrogen can be efficiently introduced into the steel during carbonitriding. On the other hand, when the value of α exceeds 0.020, the nitrogen penetration amount within a predetermined time is saturated, and sooting (a phenomenon in which soot is generated in the heat treatment furnace and adheres to the object to be processed) is likely to occur. There is a risk that quality defects such as surface carburization may occur in the object to be treated. Therefore, the value of α is preferably 0.012 or more and 0.020 or less, and more preferably 0.013 or more and 0.018 or less.

Furthermore, the value of a _c ^* is preferably 0.88 or more in order to prevent the steel surface layer from decarburizing. On the other hand, if the value of a _c ^* exceeds 1.27, excessive carbide (cementite: Fe ₃ C) is formed in the surface layer portion of the steel, which may adversely affect the properties of the steel. Therefore, the value of a _c ^* is preferably 0.88 or more and 1.27 or less, and more preferably 0.9 or more and 1.1 or less. Furthermore, if the value of a _c ^* is greater than 1.00, sooting may occur and the steel becomes overcarburized. Therefore, from the viewpoint of preventing excessive carburization, the value of a _c ^* is more preferably 1.00 or less. Thus, carbon concentration in the surface layer portion of the bearing component is appropriate by performing carbonitriding in an atmosphere in which α is 0.012 to 0.020 and a _c ^* is 0.88 to 1.27. The carbonitriding process is made more efficient. As a result, it is possible to reduce the manufacturing cost of the bearing component. Therefore, according to the bearing component according to the present invention, it is possible to provide a bearing component with improved durability and reduced manufacturing costs.

  In the bearing component according to the present invention, the “surface layer portion” means a region from the contact surface to a depth of 20 μm in the thickness direction of the bearing component. Further, “average nitrogen concentration in the surface layer portion” and “variation in nitrogen concentration in the surface layer portion” are as defined in the embodiments of the present invention described later.

  Next, the reason why the component composition of the steel constituting the bearing part according to the present invention is set in the above range will be described.

Carbon: 0.95 mass% or more and 1.1 mass% or less Carbon content has a big influence on the hardness of a bearing component and the amount of carbides after quench hardening. When the carbon content of the steel is 0.95% by mass or more, sufficient hardness and carbide content can be achieved without introducing a large amount of carbon into the steel by heat treatment. On the other hand, when the carbon content exceeds 1.1% by mass, a large carbide is formed at the time of manufacturing the steel, which may adversely affect the durability of the bearing component. Therefore, the carbon content is set to 0.95 mass% or more and 1.1 mass% or less.

Silicon: Less than 0.3% by mass Silicon increases the hydrogen storage amount in steel and promotes hydrogen embrittlement. When the silicon content of steel is 0.3% by mass or more, exfoliation due to hydrogen embrittlement is likely to occur in applications where hydrogen easily enters steel. For this reason, in the above bearing component, the silicon content of steel was set to a low value of less than 0.3% by mass.

Manganese: Less than 0.5 mass% Manganese contributes to the hardenability of the steel and the hardness of the steel before quenching. However, when the manganese content is 0.5% by mass or more, the hardness of the material before quenching is increased, and the workability in the cold process is lowered. Therefore, the manganese content is set to less than 0.5% by mass.

Sulfur: Less than 0.008% by mass Sulfur chemically bonds with manganese and forms non-metallic inclusions such as manganese sulfide. This non-metallic inclusion can adversely affect the life of the bearing. Therefore, in the said bearing component, the sulfur content of steel was set low to less than 0.008 mass%.

Chromium: 1.4 mass% or more and less than 1.6 mass% Chromium contributes to the improvement of hardenability of steel. Further, in the bearing component according to the present invention, the hardenability is lowered because the silicon content is low in order to prevent peeling due to hydrogen embrittlement. Therefore, in order to compensate for the decrease in hardenability due to the lowering of the silicon content, the chromium content of the steel is set to be higher than 1.4% by mass and lower than 1.6% by mass in the bearing component.

  In the bearing component, the inclination of the nitrogen concentration in the thickness direction of the bearing component may be −15 (1 / m) or more. The slope of the nitrogen concentration is measured as described in the examples described later. Thereby, the dispersion | variation in the nitrogen concentration in the said surface layer part after finishing a finishing process to the said contact surface can be reduced easily.

  The “nitrogen concentration gradient” may be the gradient of nitrogen concentration before the finishing process such as grinding on the contact surface, or the nitrogen concentration after finishing the contact surface (product state). The slope may be That is, in the bearing component, the slope of the nitrogen concentration may be −15 (1 / m) or more before finishing the contact surface, or the slope of the nitrogen concentration is − after finishing the finish. It may be 15 (1 / m) or more, and the slope of the nitrogen concentration may be -15 (1 / m) or more before and after the finishing.

  In the bearing component, an average retained austenite amount at a position of 0.05 mm from the contact surface is 25% by volume or more and 35% by volume or less, and a residual at a position of 0.05 mm from the contact surface. The variation in the amount of austenite may be 3% by volume or less.

  According to the study by the present inventor, when the amount of retained austenite at a depth of 0.05 mm from the contact surface is 22% by volume or more, the service life is greatly improved. On the other hand, when the amount of retained austenite at the depth position exceeds 38% by volume, the hardness of the contact surface decreases. Accordingly, the average retained austenite amount at the depth position is set to 25% by volume or more and 35% by volume or less, and the variation of the retained austenite amount at the depth position is set to 3% by volume or less, and the retained austenite at the depth position is set to 3% by volume or less. By making the amount 22 volume% or more and 38 volume% or less, it is possible to further suppress a decrease in life and a decrease in the hardness of the contact surface. Further, “the average amount of retained austenite at the depth position” and “the variation in the amount of retained austenite at the position of the depth” are as defined in the embodiment of the present invention described later.

  In the bearing component, the total average retained austenite amount may be 18% by volume or less.

  According to the study of the present inventor, when the average amount of retained austenite of the entire bearing component is 18% by volume or less, the aging dimensional change rate decreases. Therefore, the dimensional stability of the bearing component can be improved by setting the total average retained austenite amount to 18% by volume or less.

In the bearing component, five or more carbonitrides having a diameter of 0.5 μm or less per 100 μm ² may be present in the surface layer portion.

According to the study of the present inventor, when 5 or more carbonitrides having a diameter of 0.5 μm or less are present per 100 μm ^{2 in the} surface layer portion, the static load capacity of the bearing component is increased by precipitation strengthening of the carbonitride. improves. Therefore, by defining the abundance of the carbonitride in the surface layer within the above range, the static load capacity of the bearing component can be further improved. In this case, the carbon concentration in the surface layer portion is 0.9% by mass or more and 1.1% by mass or less.

Here, “the surface layer portion has 5 or more carbonitrides having a diameter of 0.5 μm or less per 100 μm ² ” means that the bearing part is cut in a cross section perpendicular to the contact surface and the surface layer of the obtained cross section When the part is observed with a microscope, 5 or more carbonitrides having a diameter of 0.5 μm or less are confirmed per 100 μm ² . The “carbonitride” refers to iron carbide or a part of carbon of the carbide substituted with nitrogen, and includes Fe—C compounds and Fe—C—N compounds. Moreover, this carbonitride may contain the alloy elements contained in steel, such as chromium.

  In the bearing component, a nitrogen concentration in a non-grinding portion including a non-grinding surface other than the contact surface may be less than 0.7% by mass.

  According to the study of the present inventor, when the nitrogen concentration in the non-ground portion is 0.7% by mass or more, the amount of retained austenite becomes excessive, and as a result, the hardness of the non-ground surface decreases. Therefore, in order to ensure sufficient hardness on the non-ground surface, the nitrogen concentration in the non-ground portion is preferably less than 0.7% by mass. The “non-ground portion” means a region from the non-ground surface to a depth of 20 μm in the thickness direction of the bearing component. In this case, the hardness at a depth of 0.1 mm from the non-ground surface is 700 HV or more.

  In the bearing component, after heat treatment at a heating temperature of 500 ° C. and a holding time of 1 hour, the Vickers hardness at a position of a depth of 0.4 (mm) from the contact surface is the thickness of the bearing component. It may be 80 HV or more higher than the Vickers hardness in the region where the carbonitrided layer is not formed.

  Thereby, it can be assured that the nitrogen concentration at the contact surface is 0.4 mass% or more.

  The rolling bearing according to the present invention includes the bearing component according to the present invention with improved durability. Therefore, according to the rolling bearing according to the present invention, it is possible to provide a rolling bearing with improved durability.

  As is clear from the above description, according to the bearing component and the rolling bearing according to the present invention, it is possible to provide a bearing component and a rolling bearing with improved durability and reduced manufacturing costs.

It is a schematic sectional drawing which shows the structure of the deep groove ball bearing which concerns on this Embodiment. It is a schematic sectional drawing which shows the structure of the tapered roller bearing which concerns on this Embodiment. It is the schematic for demonstrating the measuring method of the nitrogen concentration in the bearing component which concerns on this Embodiment. It is a graph which shows the measurement result of the nitrogen concentration in the bearing component which concerns on this Embodiment. It is a flowchart for demonstrating the manufacturing method of the bearing component which concerns on this Embodiment. It is the schematic for demonstrating the detail of the hardening hardening process (S20) in the manufacturing method of the bearing components which concerns on this Embodiment. It is a schematic diagram for explaining the undecomposed NH ₃ minutes pressure control step included in the atmosphere control step of FIG. It is a diagram for explaining the H ₂ partial pressure control step included in the atmosphere control step of FIG. It is a figure which shows an example of the heating pattern in the heating pattern control process included in the carbonitriding process of FIG. Is a graph showing the relationship between the nitrogen concentration and indentation-originated flaking life of the surface layer portion (L ₁₀ life). It is a graph showing the relationship between the surface layer portion of the nitrogen concentration variation and indentation-originated flaking life (L ₁₀₎ life. It is a graph which shows nitrogen concentration distribution in the surface layer vicinity of an inner ring. Is a graph showing the relationship between the amount of residual austenite and indentation-originated flaking life of the vicinity of the surface layer (L ₁₀ life). It is a graph which shows distribution of the amount of retained austenite in the surface layer vicinity of a test piece. It is a graph which shows the relationship between the amount of average retained austenite, and a secular dimensional change rate. It is a cross-sectional SEM photograph of the test piece of a comparative example. It is a cross-sectional SEM photograph of the test piece of an Example. It is a graph which shows the influence which presence of carbonitride has on indentation depth. It is a graph which shows the relationship between the nitrogen concentration of a non-grinding part, and the amount of retained austenite. It is a graph which shows the relationship between the amount of retained austenite of a non-grinding part, and the cross-sectional hardness of a non-grinding surface vicinity. It is a photograph of a raceway ring in which a scratch has occurred in a non-ground part. It is the schematic for demonstrating the measuring method of the nitrogen concentration in a sample. It is a graph which shows the relationship between tempering temperature and a cross-sectional hardness difference. It is a graph which shows the relationship between nitrogen concentration and a cross-sectional hardness difference. It is a graph which shows the relationship between nitrogen concentration in the range whose nitrogen concentration is 0.1 mass% or less, and cross-sectional hardness difference. It is a graph which shows nitrogen concentration distribution in steel after a carbonitriding process. It is a graph which shows nitrogen concentration distribution in steel after a nitrogen diffusion process. It is a figure which shows carbon concentration and nitrogen concentration distribution in case the value of _ac ^* is 0.8. It is a figure which shows carbon concentration and nitrogen concentration distribution in case the value of _ac ^* is 0.95. It is a figure which shows nitrogen concentration distribution in case the value of (alpha) is 0.027. It is a figure which shows nitrogen concentration distribution in case the value of (alpha) is 0.005.

  Hereinafter, embodiments of the present invention will be described with reference to the drawings. In the following drawings, the same or corresponding parts are denoted by the same reference numerals, and description thereof will not be repeated.

  First, with reference to FIG. 1, the structure of the deep groove ball bearing 1 as a rolling bearing which concerns on this Embodiment is demonstrated. The deep groove ball bearing 1 includes an annular outer ring 11, an annular inner ring 12 disposed inside the outer ring 11, and a rolling element that is disposed between the outer ring 11 and the inner ring 12 and is held by an annular retainer 14. And a plurality of balls 13. An outer ring rolling surface 11 </ b> A is formed on the inner circumferential surface of the outer ring 11, and an inner ring rolling surface 12 </ b> A is formed on the outer circumferential surface of the inner ring 12. The inner ring 12 is disposed inside the outer ring 11 so that the inner ring rolling surface 12A faces the outer ring rolling surface 11A. The plurality of balls 13 are in contact with the outer ring rolling surface 11A and the inner ring rolling surface 12A on the rolling surface 13A, and are arranged at a predetermined pitch in the circumferential direction by the cage 14. Thereby, the plurality of balls 13 are held on the annular raceway of the outer ring 11 and the inner ring 12 so as to be freely rollable. With such a configuration, the outer ring 11 and the inner ring 12 of the deep groove ball bearing 1 are rotatable relative to each other. Moreover, the outer ring | wheel 11, the inner ring | wheel 12, and the ball | bowl 13 are bearing components which concern on this Embodiment mentioned later.

  Next, the structure of the tapered roller bearing 2 as another rolling bearing according to the present embodiment will be described with reference to FIG. The tapered roller bearing 2 includes an annular outer ring 21 and an inner ring 22, a plurality of rollers 23 that are rolling elements, and an annular cage 24. An outer ring rolling surface 21 </ b> A is formed on the inner circumferential surface of the outer ring 21, and an inner ring rolling surface 22 </ b> A is formed on the outer circumferential surface of the inner ring 22. The inner ring 22 is arranged inside the outer ring 21 so that the inner ring rolling surface 22A faces the outer ring rolling surface 21A.

  The rollers 23 are in contact with the outer ring rolling surface 21A and the inner ring rolling surface 22A on the rolling surface 23A, and are arranged at a predetermined pitch in the circumferential direction by the cage 24. As a result, the roller 23 is held on the annular raceway of the outer ring 21 and the inner ring 22 so as to roll freely. Further, in the tapered roller bearing 2, the apex of the cone including the outer ring rolling surface 21A, the cone including the inner ring rolling surface 22A, and the cone including the locus of the rotating shaft when the roller 23 rolls is the center of the bearing. It is configured to intersect at one point on the line. With such a configuration, the outer ring 21 and the inner ring 22 of the tapered roller bearing 2 are rotatable relative to each other. The outer ring 21, the inner ring 22, and the rollers 23 are bearing parts according to the present embodiment, similarly to the outer ring 11, the inner ring 12, and the balls 13.

  Next, the structure of the bearing components (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23) according to the present embodiment will be described. The bearing component comprises 0.95 mass% or more and 1.1 mass% or less of carbon, less than 0.3 mass% silicon, less than 0.5 mass% manganese, less than 0.008 mass% sulfur, And 1.4% by mass or more and less than 1.6% by mass of chromium, and is made of steel consisting of the remaining iron and impurities. The bearing component has contact surfaces (outer ring rolling surfaces 11A, 21A, inner ring rolling surfaces 12A, 22A, rolling surfaces 13A, 23A) that come into contact with other components, and a surface layer portion including the contact surfaces. A carbonitriding layer is formed on the surface.

In the bearing component, the average nitrogen concentration in the surface layer portion is 0.3 mass% or more and 0.6 mass% or less, and the variation in nitrogen concentration in the surface layer portion is 0.1 mass% or less. . Thereby, in the said bearing component, the lifetime under foreign material mixing lubrication improves, and the fall of the hardness of the said contact surface is suppressed. Further, in the above-described bearing component, when the undecomposed ammonia partial pressure is P _N and the hydrogen partial pressure is P _H as described later, a _c ^* defined by the above formula (1) is 0.88 or more and 1 The carbonitriding layer is formed by performing carbonitriding so that α defined by the above formula (2) is 0.012 or more and 0.020 or less. For this reason, the manufacturing cost of the bearing component is further reduced. Therefore, the deep groove ball bearing 1 and the tapered roller bearing 2 provided with the bearing parts have improved durability and reduced manufacturing costs.

  In the bearing component, “average nitrogen concentration in the surface layer portion” and “variation in nitrogen concentration in the surface layer portion” are measured as follows. Here, the case where the inner rings 12 and 22 are measured will be described as an example.

  Referring to FIG. 3, first, measurement point S <b> 1 is set at an arbitrary location on the contact surface (inner ring rolling surfaces 12 </ b> A, 22 </ b> A) of inner rings 12, 22. Next, the measurement point S2 shifted by θ (30 °) in the circumferential direction as viewed from the measurement point S1, the measurement point S3 shifted by θ (30 °) in the circumferential direction as viewed from the measurement point S2, and the measurement point S3 Measurement point S4 shifted by θ (30 °) in the circumferential direction when viewed from the side, measurement point S5 shifted by θ (30 °) in the circumferential direction when viewed from the measurement point S4, and circumferential direction when viewed from measurement point S5 And a measurement point S6 shifted by θ (30 °). In this way, a plurality of measurement points S1 to S6 are set on the contact surfaces of the inner rings 12 and 22 and shifted by 30 ° along the circumferential direction. Note that the measurement points S1 to S6 are set in the central portion in the axial direction on the contact surfaces of the inner rings 12 and 22.

  The races such as the inner rings 12 and 22 may be deformed into an oval shape by heat treatment and the roundness may be lost, which may cause variations in the nitrogen concentration in the surface layer after grinding. On the other hand, when the measurement points S1 to S6 that are shifted by 30 ° along the circumferential direction are set, the measurement points are distributed and arranged in a substantially half-circumferential region in the circumferential direction. The measurement points S1 to S6 can include a maximum value and a minimum value of the nitrogen concentration. Therefore, by performing the evaluation based on the measurement values at the measurement points S1 to S6, the “average nitrogen concentration in the surface layer portion” and “the variation in the nitrogen concentration in the surface layer portion” can be more accurately evaluated.

  FIG. 4 shows the nitrogen concentration (vertical axis) of the surface layer measured at the measurement points S1 to S6 (horizontal axis). The average value of each nitrogen concentration shown on the vertical axis in FIG. 4 can be defined as “average nitrogen concentration in the surface layer portion”. The largest value among the differences between the “average nitrogen concentration in the surface layer portion” and the measurement values at the measurement points S1 to S6 can be defined as “the variation in the nitrogen concentration in the surface layer portion”.

  Further, in the bearing parts (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23), the contact surfaces (outer ring rolling surfaces 11A, 21A, inner ring rolling surfaces 12A, 22A, rolling surfaces 13A, 23A). ), The slope of the nitrogen concentration in the thickness direction may be −15 (1 / m) or more. Thereby, after finishing the contact surface, variation in the nitrogen concentration in the surface layer portion can be reduced to 0.1 mass% or less. In the bearing component, even after finishing the contact surface, the slope of the nitrogen concentration in the thickness direction may be −15 (1 / m) or more.

  Further, in the bearing parts (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23), the contact surfaces (outer ring rolling surfaces 11A, 21A, inner ring rolling surfaces 12A, 22A, rolling surfaces 13A, 23A). The average retained austenite amount at a depth of 0.05 mm is not less than 25% by volume and not more than 35% by volume, and the variation in the retained austenite amount at the depth is not more than 3% by volume. Good. Thereby, the fall of the lifetime under foreign material mixing lubrication and the hardness of the said contact surface can further be suppressed. Further, “the average amount of retained austenite at the position of the depth” and “the variation in the amount of retained austenite at the position of the depth” are the “average nitrogen concentration in the surface layer portion” described with reference to FIGS. It can be measured in the same manner as in the case of “variation of nitrogen concentration in the surface layer”.

  In the bearing parts (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23), the average retained austenite amount of the entire bearing parts may be 18% by volume or less. Thereby, since the aging dimensional change rate falls, the dimensional stability of a bearing component can be improved.

Further, in the bearing parts (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23), 5 or more carbonitrides having a diameter of 0.5 μm or less are present per 100 μm ^{2 in the} surface layer portion. Also good. Thereby, the static load capacity of the bearing component can be further improved.

  Further, in the bearing parts (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23), the contact surfaces (outer ring rolling surfaces 11A, 21A, inner ring rolling surfaces 12A, 22A, rolling surfaces 13A, 23A). The nitrogen concentration in the non-grinding portion including the non-grinding surfaces 11B, 12B, and 22B that is a surface other than) may be less than 0.7% by mass. Thereby, sufficient hardness (700HV or more) in the non-ground surfaces 11B, 12B, and 22B can be ensured.

  Further, the bearing parts (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23) are subjected to heat treatment with a heating temperature of 500 ° C. and a holding time of 1 hour, and then the contact surfaces (outer ring rolling). Vickers hardness at a depth of 0.4 (mm) from the running surfaces 11A and 21A, the inner ring rolling surfaces 12A and 22A, and the rolling surfaces 13A and 23A) forms a carbonitriding layer in the thickness direction of the bearing component. It may be higher by 80 HV or more than the Vickers hardness in the untreated region. Thereby, it can be assured that the nitrogen concentration at the contact surface is 0.4 mass% or more.

  Next, a method for manufacturing a bearing component according to the present embodiment will be described. In the bearing component manufacturing method according to the present embodiment, the bearing components (outer rings 11, 21, inner rings 12, 22, balls 13 and rollers 23) according to the present embodiment can be manufactured.

  With reference to FIG. 5, first, as a step (S10), a steel material preparation step is performed. In this step (S10), first, carbon of 0.95 mass% to 1.1 mass%, silicon of less than 0.3 mass%, manganese of less than 0.5 mass%, and 0.008 mass% The steel material which contains less iron and 1.4 mass% or more and less than 1.6 mass% chromium, and consists of remainder iron and impurities is prepared. And the said steel material is shape | molded by the schematic shape of a bearing component. For example, by using a steel bar, a steel wire or the like as a raw material, and processing such as cutting, forging, turning, etc. on the steel bar, the steel wire, etc., outer rings 11 and 21, inner rings 12, 22 as bearing parts, or Steel materials formed into a schematic shape such as balls 13 and rollers 23 are prepared.

Next, a quench hardening process is implemented as process (S20). In this step (S20), after the carbonitriding treatment and the nitrogen diffusion treatment are sequentially performed on the steel material prepared in the step (S10), the temperature of the steel material is equal to or lower than the M _s point (martensitic transformation start point). Cooled to. This step (S20) will be described in detail later.

Next, a tempering step is performed as a step (S30). In this step (S30), with respect to quench hardened steel in the step (S20), heat-treated at a temperature of less than ₁ point A is performed. More specifically, after the step (S20) is completed, the steel material is held at a temperature of 180 ° C. or higher and 220 ° C. or lower (for example, 210 ° C.) of A ₁ or less for a predetermined time, thereby tempering the steel material. Is given. Thereafter, the steel material is cooled by air at room temperature (air cooling). Thereby, the toughness etc. of steel materials can be improved.

  Next, a finishing step is performed as a step (S40). In this step (S40), a grinding process is performed on the contact surfaces (outer ring rolling surfaces 11A and 21A, inner ring rolling surfaces 12A and 22A, and rolling surfaces 13A and 23A) of the steel material that has been tempered. As a result, the outer rings 11 and 21, the inner rings 12 and 22, the balls 13, and the rollers 23 (see FIGS. 1 and 2), which are bearing parts according to the present embodiment, are manufactured, and manufacture of the bearing parts according to the present embodiment. The method is complete. The deep groove ball bearing 1 (see FIG. 1) is manufactured by combining the manufactured outer ring 11, inner ring 12 and ball 13, and the tapered ring bearing 2 (see FIG. 1) is combined by combining the outer ring 21, the inner ring 22 and the roller 23. 2) is manufactured.

Next, the quench hardening step (S20) will be described in detail with reference to FIGS. FIG. 6 is a diagram for explaining the quench hardening process (S20) in detail. FIG. 7 is a view for explaining an undecomposed ammonia (NH ₃ ) partial pressure control step included in the atmosphere control step of FIG. FIG. 8 is a diagram for explaining a hydrogen (H ₂ ) partial pressure control step included in the atmosphere control step of FIG. Moreover, FIG. 9 is a figure which shows an example of the heating pattern (temperature history) in the heating pattern control process included in the carbonitriding process of FIG. In FIG. 9, the horizontal direction indicates time, and it indicates that time has passed toward the right.

Referring to FIG. 6, in the quench hardening step (S20), first, a carbonitriding step is performed in which the steel material prepared in the step (S10) is carbonitrided. Next, a nitrogen diffusion step for diffusing nitrogen that has entered the steel in the carbonitriding step is performed. And after a nitrogen diffusion process is completed, the cooling process which cools steel materials to the temperature below _Ms point is implemented. In the carbonitriding step, the steel material is heated in an atmosphere containing ammonia, carbon monoxide, carbon dioxide, and hydrogen.

The carbonitriding process includes an atmosphere control process 30 in which the atmosphere in the heat treatment furnace is controlled, and a heating pattern control process 40 in which the temperature history applied to the steel material that is the object to be processed in the heat treatment furnace is controlled. . The atmosphere control process 30 and the heating pattern control process 40 can be performed independently and in parallel. The atmosphere control step 30 includes an undecomposed NH ₃ partial pressure control step 31 in which the undecomposed ammonia partial pressure in the heat treatment furnace is controlled, and an H ₂ partial pressure control step 32 in which the hydrogen partial pressure in the heat treatment furnace is controlled. And a CO / CO ₂ partial pressure control step 33 in which the partial pressure of at least one of carbon monoxide and carbon dioxide in the heat treatment furnace is controlled.

In the CO / CO ₂ partial pressure control step 33, with reference to the above formula (1), the carbon activity is controlled by controlling the partial pressure of at least one of carbon monoxide and carbon dioxide in the heat treatment furnace. ( _Ac ^* ) is controlled.

In the atmosphere control step 30, a _c ^* defined by the above formula (1) is 0.88 or more and 1.27 or less (preferably 0.9 or more and 1.1 or less), and the above formula ( 2) Undecomposed NH ₃ partial pressure control step 31, H ₂ partial pressure so that the value of α represented by 2) is in the range of 0.012 to 0.020 (preferably 0.013 to 0.018). A control step 32 and a CO / CO ₂ partial pressure control step 33 are performed. In formula (2), P _N (atm) is the partial pressure of undecomposed ammonia, and P _H (atm) is the partial pressure of hydrogen.

Specifically, referring to FIG. 7, in undecomposed NH ₃ partial pressure control step 31, first, an undecomposed NH ₃ partial pressure measuring step (S11) for measuring the undecomposed ammonia partial pressure in the heat treatment furnace is performed. Is done. The measurement of the undecomposed ammonia partial pressure can be performed using, for example, a gas chromatograph or an infrared analyzer. Based on the undecomposed ammonia partial pressure measured in the step (S11), it is determined whether or not the NH ₃ supply amount adjustment step (S13) for increasing or decreasing the supply amount of ammonia gas to the heat treatment furnace is necessary. A decomposition NH ₃ partial pressure determination step (S12) is performed. The determination is made by comparing the target undecomposed ammonia partial pressure, which is determined in advance so that the value of α is in the range of 0.012 to 0.020, and the measured undecomposed ammonia partial pressure. The determination is made by determining whether the undecomposed ammonia partial pressure is the target undecomposed ammonia partial pressure.

  When the undecomposed ammonia partial pressure is not equal to the target undecomposed ammonia partial pressure, after the step (S13) for increasing or decreasing the undecomposed ammonia partial pressure in the heat treatment furnace is performed, the step (S11) is performed. Will be implemented again. The step (S13) includes, for example, a mass flow controller in which the amount of ammonia (amount of ammonia gas) flowing into the heat treatment furnace per unit time from an ammonia gas cylinder connected to the heat treatment furnace via a pipe is attached to the pipe. It can implement by adjusting with the flow control apparatus provided with. That is, when the measured partial pressure of undecomposed ammonia is higher than the target partial pressure of undecomposed ammonia, the step (S13) can be performed by decreasing the flow rate and increasing the flow rate when the partial pressure is low. . In this step (S13), when there is a predetermined difference between the measured undecomposed ammonia partial pressure and the target undecomposed ammonia partial pressure, it was experimentally determined in advance how much the flow rate should be increased or decreased. It can be determined based on the relationship between the increase / decrease in the flow rate of ammonia gas and the increase / decrease in the partial pressure of undecomposed ammonia.

  On the other hand, when the undecomposed ammonia partial pressure is the target undecomposed ammonia partial pressure, the step (S11) is performed again without performing the step (S13).

The H ₂ partial pressure control step 32 is performed in the same manner as the undecomposed NH ₃ partial pressure control step 31 described above. That is, referring to FIG. 8, in the H ₂ partial pressure control step 32, first, an H ₂ partial pressure measurement step (S21) for measuring the hydrogen partial pressure in the heat treatment furnace is performed. The measurement of the hydrogen partial pressure can be performed using, for example, a heat conduction gas analyzer. Then, based on the hydrogen partial pressure measured in the step (S21), it is determined whether or not the H ₂ supply amount adjusting step (S23) for increasing or decreasing the supply amount of hydrogen gas to the heat treatment furnace is necessary. A determination step (S22) is performed. The determination is made by comparing the target hydrogen partial pressure determined in advance so that the value of α is in the range of 0.012 or more and 0.020 or less and the measured hydrogen partial pressure. Is carried out by determining whether or not is at the target hydrogen partial pressure.

  When the hydrogen partial pressure is not the target hydrogen partial pressure, the step (S23) for increasing or decreasing the hydrogen partial pressure in the heat treatment furnace is performed, and then the step (S21) is performed again. The step (S23) includes, for example, a mass flow controller in which the amount of hydrogen (flow rate of hydrogen gas) flowing into the heat treatment furnace per unit time from a hydrogen gas cylinder connected to the heat treatment furnace via a pipe is attached to the pipe It can implement by adjusting with the flow control apparatus provided with. That is, when the measured hydrogen partial pressure is higher than the target hydrogen partial pressure, the step (S23) can be performed by decreasing the flow rate, and when it is low, increasing the flow rate. In this step (S23), when there is a predetermined difference between the measured hydrogen partial pressure and the hydrogen partial pressure, how much the flow rate is increased or decreased is experimentally determined in advance as in the case of ammonia. It can be determined based on the relationship between the increase or decrease of the hydrogen gas flow rate and the increase or decrease of the hydrogen partial pressure.

  On the other hand, when the hydrogen partial pressure is the target hydrogen partial pressure, the step (S21) is performed again without performing the step (S23).

Referring to FIG. 6, in the CO / CO ₂ partial pressure control step 33, the supply amount of propane (C ₃ H ₈ ) gas, butane gas (C ₄ H ₁₀ ) or the like as an enriched gas is adjusted, so that CO 2 is adjusted. The partial pressure of at least one of the partial pressure of CO ₂ and CO ₂ is controlled, and a _c ^* is adjusted. Specifically, for example, the partial pressure P _CO2 partial pressure P _CO and carbon monoxide to carbon dioxide in the atmosphere by using an infrared gas concentration measurement device are measured. And based on the said measured value, propane (C as an enriched gas) so that a _c ^* defined by the above formula (1) becomes a target value within the range of 0.88 or more and 1.27 or less. The supply amount of ₃ H ₈ ) gas, butane gas (C ₄ H ₁₀ ), etc. is adjusted.

Here, the value of α is determined by the undecomposed NH ₃ partial pressure control step 31, the H ₂ partial pressure control step 32, and the CO / CO ₂ partial pressure control step 33 with reference to the above equation (2). It can be controlled by changing at least one of cracked ammonia partial pressure, hydrogen partial pressure, and a _c ^* . That is, the value of α is determined by, for example, the H ₂ partial pressure in a state where the undecomposed NH ₃ partial pressure control step 31 and the CO / CO ₂ partial pressure control step 33 keep the undecomposed ammonia partial pressure and a _c ^* constant. The control step 32 may control by changing the hydrogen partial pressure, or the hydrogen partial pressure and a _c ^* value are kept constant by the H ₂ partial pressure control step 32 and the CO / CO ₂ partial pressure control step 33. In this state, the partial pressure of undecomposed ammonia may be changed and controlled by the undecomposed NH ₃ partial pressure control step 31.

Furthermore, with reference to FIG. 6, in the heating pattern control process 40, the heating history provided to steel materials is controlled. Specifically, as shown in FIG. 9, the steel material in an atmosphere which is controlled by an atmosphere control step 30 described above, A ₁ transformation point or more in a 820 ° C. or higher 880 ° C. or less (preferably not more than 870 ° C. 830 ° C. or higher ) At a temperature of 180 minutes to 600 minutes (preferably 240 minutes to 480 minutes). When the holding time elapses, the heating pattern control process 40 ends, and at the same time, the atmosphere control process 30 ends.

Referring to FIG. 6, a nitrogen diffusion process is performed after the carbonitriding process is completed. In this step, the steel material is heated at a temperature equal to or lower than the treatment temperature in the carbonitriding step, and is maintained for 30 minutes to 120 minutes (preferably 45 minutes to 90 minutes). Thereby, the nitrogen which penetrate | invaded in steel can be diffused. In this step, a _c ^* is 0.88 to 1.27 (preferably 0.9 to 1.1), and α is 0.003 to 0.012 (preferably 0). 0.003 or more and 0.008 or less), the atmosphere in the heat treatment furnace is controlled. The control of the a _c ^* value and the α value can be performed in the same manner as in the carbonitriding step.

Referring to FIG. 6, the cooling process is performed after the nitrogen diffusion process is completed. In this step, the steel material is immersed in oil (oil-cooled) to be cooled to a temperature not higher than the _MS point. By performing the above steps (carbonitriding step, nitrogen diffusion step, and cooling step) in order, the surface layer portion of the steel material is carbonitrided and quenched and hardened.

Example 1
First, the influence of the average nitrogen concentration in the surface layer and the variation in nitrogen concentration on the durability of the bearing parts was investigated. Specifically, indentation was formed on the rolling surface of the race (inner ring), and an indentation origin type peeling life test was performed to evaluate the life of the inner ring under lubrication mixed with foreign matter. The experimental procedure is as follows.

  The test was carried out using a deep groove ball bearing of JIS standard 6206 model number (inner diameter 30 mm, outer diameter 62 mm, width 16 mm, 9 rolling elements). First, an inner ring was produced by the same procedure as in the present embodiment (carbonitriding temperature: 850 ° C., tempering temperature: 180 ° C.). In the carbonitriding process, the concentration distribution of nitrogen entering the surface of the inner ring was controlled by adjusting the partial pressure of undecomposed ammonia, hydrogen partial pressure, carbon activity, heat treatment time, and quenching temperature. For comparison, an inner ring that does not perform the nitrogen diffusion step after the carbonitriding step was also produced.

  Next, an indenter for measuring the Rockwell hardness of a conical diamond was pressed with a load of 196 N to the groove bottom center of the rolling surface of the produced inner ring to form an indentation. Thirty indentations were formed per inner ring, and were formed at equal intervals in the circumferential direction (that is, every 12 ° of the central angle).

  Next, a bearing was produced by combining the produced inner ring with the outer ring, rolling elements and retainer. And the lifetime test was done using the produced bearing. A tester having a structure in which a radial load is equally applied to two bearings was used. A test was performed by applying a load of about 3.04 GPa to one bearing and rotating the bearing at a rotational speed of 3000 rpm. Lubrication was performed by continuously flowing a certain amount of oil into the housing in which the test bearings were arranged.

  By the above test, the relationship between the nitrogen concentration in the surface layer portion of the inner ring and the indentation origin type peeling life was investigated. In addition, when the nitrogen concentration in the surface layer portion was constant (0.4% by mass), the relationship between the variation in the nitrogen concentration in the surface layer portion and the indentation origin type peeling life was also investigated. The “variation in the nitrogen concentration in the surface layer portion” was measured by the same method as in the above embodiment (see FIGS. 3 and 4).

The test results are shown in FIGS. Figure 10 is a nitrogen concentration of the inner ring of the surface layer portion (horizontal axis, mass%), shows the relationship between the L ₁₀ life of indentation-originated flaking life (vertical axis, h). Figure 11 is a variation of the nitrogen concentration of the inner ring of the surface layer portion (horizontal axis, mass%) and the indentation-originated flaking life L ₁₀ life (the vertical axis, h) shows the relationship between the.

As shown in FIG. 10, when the nitrogen concentration in the surface layer is less than 0.2% by weight (shown in broken lines in FIG. 10) it was reduced L ₁₀ life. On the other hand, as will be described later in the investigation results, when the nitrogen concentration in the surface layer portion exceeds 0.7 mass%, the amount of retained austenite becomes excessive and the hardness of the contact surface decreases (see FIGS. 19 and 20). ).

Further, as shown in FIG. 11, while the variation of the nitrogen concentration of 0.1% by weight (shown in broken line in FIG. 11) above a certain L ₁₀ life if less is ensured, 0 If more than .1% by weight _{L 10} life was reduced significantly. From these results, in order to suppress the life under the contamination with foreign matter and the decrease in the hardness of the contact surface, the nitrogen concentration of the surface layer portion should be 0.2% by mass or more and 0.7% by mass or less, that is, the surface layer It has been found that it is effective to set the average nitrogen concentration in the part to 0.3 mass% or more and 0.6 mass% or less, and the variation in the nitrogen concentration in the surface layer portion to 0.1 mass% or less.

(Example 2)
Next, the relationship between the variation in the nitrogen concentration in the surface layer and the slope of the nitrogen concentration was investigated. First, steps (S10) to (S30) were performed by the same procedure as in the present embodiment to produce an inner ring (Example). The time for the carbonitriding process was 4 hours, and the time for the nitrogen diffusion process was 1 hour. Moreover, the inner ring | wheel which does not implement a nitrogen diffusion process after a carbonitriding process was also produced for the comparison (comparative example). Then, the nitrogen concentration distribution in the vicinity of the surface layer was investigated for the inner ring produced before the finishing step (S40).

  FIG. 12 shows the nitrogen concentration distribution in the depth direction of the produced inner ring. In FIG. 12, the horizontal axis indicates the depth (mm) of the inner ring, and the vertical axis indicates the nitrogen concentration (mass%). In FIG. 12, (A) shows the measurement result of the example, (A ′) shows an approximate curve for the measurement result of the example, (B) shows the measurement result of the comparative example, (B ′) The approximate curve with respect to the measurement result of a comparative example is shown. For example, when the slope of the nitrogen concentration is calculated between two points at a depth of 0.3% by mass and 0.1% by mass, the relational expression of (0.3−0.1) / distance (m) is obtained. A slope of the nitrogen concentration was obtained, and as a result, the slope of the nitrogen concentration was larger in the example than in the comparative example (−15 (1 / m) or more). Further, when the finishing step (S40) is performed such that the deformation amount of the inner ring by heat treatment is 0.2 mm and the average nitrogen concentration in the surface layer portion is 0.4 mass%, in the comparative example, the variation in the nitrogen concentration in the surface layer portion is 0. It was 0.08 mass% (0.1 mass% or less) in the Example, whereas it was .25 mass%. From this result, it was found that performing the nitrogen diffusion step after the carbonitriding step is effective for reducing variation in the nitrogen concentration in the surface layer portion after finishing.

Example 3
Next, an experiment was conducted to investigate the influence of the average retained austenite amount near the surface layer and the variation in retained austenite amount on the durability of the bearing component. First, an inner ring was produced by the same procedure as in the above embodiment. The carbonitriding step was performed so that the average nitrogen concentration in the surface layer portion was 0.4% by mass. In the tempering step, the amount of retained austenite near the rolling surface of the inner ring was controlled by adjusting the treatment temperature. Next, a bearing was produced by combining the produced inner ring and other bearing parts (outer ring, rolling element, cage, etc.). A life test was performed in the same manner as in Example 1.

13, the amount of retained austenite at a depth position of 0.05mm from the inner ring of the rolling surface (horizontal axis,% by volume) and, L ₁₀ life of indentation-originated flaking life (vertical axis, h) the relationship between Show. As shown in FIG. 13, in with L ₁₀ life of the amount of retained austenite is increased is increased (when the amount of retained austenite exceeds 22% by volume became the 100h than L ₁₀ life). On the other hand, when the amount of retained austenite exceeded 38% by volume, the hardness of the contact surface decreased to 700 HV or less. From this result, in order to suppress the life under the contamination with foreign matter and the decrease in the hardness of the contact surface, the amount of retained austenite at a depth of 0.05 mm from the rolling surface is 22% by volume or more and 38% by volume or less. That is, it is effective to set the average retained austenite amount at the depth position to 25% by volume or more and 35% by volume or less, and to set the variation in the retained austenite amount at the depth position to 3% by volume or less. I understood.

Example 4
Next, the influence of the average retained austenite amount of the entire bearing part on the dimensional stability of the bearing part was investigated. First, a ring-shaped test piece having an outer diameter (φ) of 60 mm, an inner diameter (φ) of 54 mm, and a width (t) of 15 mm was produced by changing the carbonitriding temperature, the tempering temperature, and the nitrogen concentration of the surface layer portion. And the heat processing which hold | maintains 2500 hours at 120 degreeC with respect to this test piece was implemented, and the secular dimensional change rate was computed by remove | dividing the dimensional difference of the outer diameter before and behind the said heat processing by the outer diameter before the said heat processing.

  FIG. 14 shows the relationship between the depth from the surface of the test piece (horizontal axis, mm) and the amount of retained austenite (vertical axis, volume%). In the legend in FIG. 14, the heat treatment conditions are indicated by the notation “carbonitriding temperature−tempering temperature−nitrogen concentration in the surface layer”. For example, the notation “850 ° C.-180 ° C.-0.1% by mass” indicates that the carbonitriding temperature is 850 ° C., the tempering temperature is 180 ° C., and the nitrogen concentration in the surface layer is 0.1% by mass. Yes. The average retained austenite amount in the test piece was calculated from the distribution of the retained austenite amount in FIG. 14, and the relationship with the aged dimensional change rate of the corresponding test piece calculated previously was investigated. FIG. 15 shows the relationship between the average retained austenite amount (horizontal axis, volume%) of the whole test piece and the aging rate of change (vertical axis).

As shown in FIG. 15, the average retained austenite amount and the aging dimensional change rate were in a proportional relationship. In addition, by setting the average retained austenite amount to 18% by volume or less, it was possible to reduce the aging rate of dimensional change to 60 × 10 ⁻⁵ or less.

(Example 5)
Next, the effect of carbonitrides existing in the surface layer on the static load capacity of bearing parts was investigated. When steel containing chromium (Cr) is infiltrated into the steel by carbonitriding or the like, the chromium concentration in the base material decreases and the austenite single-phase region expands. To rise. As a result, when a high concentration carbonitriding process is performed without taking any special measures, carbonitrides are reduced or eliminated even if decarburization does not occur. Here, from the viewpoint of increasing the strength of the bearing component, it is considered preferable to leave the carbonitride and use the precipitation strengthening function of the carbonitride.

In the present embodiment, the value of carbon activity a _c ^* in the carbonitriding process is set to 0.88 or more and 1.27 or less, and carburization is performed earlier than the increase in the carbon solid solubility limit of the nitrogen-enriched layer. Thus, the disappearance of carbonitride is suppressed. An experiment was conducted to confirm the effect of the remaining carbonitride.

FIG. 16 is a cross-sectional SEM (Scanning Electron Microscope) photograph of the test piece when carbonitriding is performed by the conventional method (magnification 5000 times), and FIG. 17 is carbonitriding by the same procedure as in the present embodiment. It is a cross-sectional SEM photograph of the test piece in the case of (a _c ^* = 1) (magnification 5000 times). In the photograph of FIG. 16, carbonitrides are almost lost, whereas in the photograph of FIG. 17, there are at least 5 or more carbonitrides having a diameter of 0.5 μm or less per 100 μm ² .

Next, in order to confirm the effect of the carbonitride, carbonitriding was performed on the test piece under different conditions, and a sample with a hardness of 750 HV was produced while changing the abundance (number density) of the carbide. An experiment was conducted to measure the depth of indentation formed by pressing a ball made of silicon nitride having a diameter (φ) of 9.525 mm on the surface of the sample. The experimental results are shown in FIG. In FIG. 18, the horizontal axis indicates the pressure (GPa) of pressing a silicon nitride ball, and the vertical axis indicates the depth (μm) of the indentation formed by pressing the ball. In FIG. 18, square marks indicate measurement results of samples in which carbonitride has disappeared (Comparative Example), and diamonds indicate measurement results of samples in which 5 or more carbon nitrides having a diameter of 0.5 μm or less exist per 100 μm ² (Example). Is shown.

As shown in FIG. 18, the depth of the indentation is smaller in the sample in which 5 or more carbonitrides having a diameter of 0.5 μm or less exist per 100 μm ² as compared with the sample in which the carbonitride has disappeared. Was confirmed. From this result, it was found that it is effective for the static load capacity of the bearing parts to be 5 or more carbon nitrides having a diameter of 0.5 μm or less per 100 μm ² in the surface layer portion.

(Example 6)
Next, the influence of the nitrogen concentration of the non-ground part and the amount of retained austenite on the hardness of the non-ground surface was investigated. First, a bearing component was produced by the same procedure as in the present embodiment. At this time, the nitrogen concentration and the amount of retained austenite in non-ground portions such as corners and thin portions were changed. Then, the relationship between the nitrogen concentration and the amount of retained austenite in the non-ground part and the hardness of the non-ground surface was investigated.

  The experimental results are shown in FIG. 19 and FIG. In FIG. 19, the horizontal axis indicates the nitrogen concentration (mass%) in the non-ground part, and the vertical axis indicates the amount of retained austenite (volume%) in the non-ground part. In FIG. 20, the horizontal axis represents the amount of retained austenite (volume%) in the non-ground part, and the vertical axis represents the hardness (HV) at a depth of 0.1 mm from the non-ground surface. As shown in FIG. 19, when the nitrogen concentration in the non-ground part was 0.7% by mass or more, the amount of retained austenite was 35% by volume or more. As shown in FIG. 20, when the amount of retained austenite in the non-ground portion was 35% by volume or more, the cross-sectional hardness at the depth position was lowered to 700 HV or less. From this result, in order to ensure sufficient hardness of the non-grinding portion, it was found effective to make the nitrogen concentration of the non-grinding portion less than 0.7 mass%.

  Generally, 80 to 90% of machine breakdown accidents are caused by fatigue. Moreover, the location which becomes the beginning of those destruction is a shape change part, such as a hole, a notch, a stepped part, a crack, a defect, or a wound. In other words, the stress is concentrated in these shape changing portions and the fatigue strength is lowered, so that the parts are destroyed. When the hardness on the non-ground surface is low, as shown in the photograph of FIG. 21, a scratch A is generated during assembly and transportation, and stress is concentrated on the scratch A, and there is a high possibility that it becomes a starting point of fracture. Therefore, in order to ensure sufficient durability of the product, it is necessary to secure the hardness on the non-ground surface to 700 HV or higher.

(Example 7)
Next, a method for determining a cross-sectional hardness measurement position and a cross-sectional hardness difference reference value for ensuring that the nitrogen concentration at the contact surface of the bearing component is 0.4 mass% or more will be described.

(1) About a test piece and an experimental method (1-1) Introduction First, it is necessary to determine the heating temperature and holding time in the high-temperature tempering having a high correlation with the nitrogen concentration. Here, since transformation by high-temperature tempering is a thermal activation process, increasing the heating temperature and increasing the holding time have the same meaning, and it is not meaningful to make them both variables. It is done. Therefore, in this embodiment, the holding time is fixed (1 hour), and the heating temperature is changed to 300 ° C., 400 ° C., 500 ° C., 600 ° C., and 700 ° C., and the difference in hardness becomes the clearest. The optimum heating temperature was determined by examining the heating temperature.

  In addition, differences in hardenability due to differences in the chemical composition of each material and differences in the cooling rate during quenching affect hardness after quenching, and also affect hardness after high-temperature tempering. It is done. Therefore, in this example, the absolute value of the cross-sectional hardness itself is not used, but the hardness at a deep position (core portion) from the surface layer that is not nitrided (here, the hardness at a depth of 1 mm from the outermost surface after heat treatment, for example) ) And the hardness difference (hardness difference) between the hardness at an arbitrary depth in the nitrided region was adopted as an index. That is, the chemical composition of the material may differ between material lots, and the hardness difference is for offsetting such a difference.

(1-2) Target test pieces Table 1 shows chemical components of the test specimens to be investigated. All the materials were within the above component ranges, and these were subjected to carbonitriding in various heat treatment furnaces and heat treatment atmospheres. The carbonitriding temperature was included in the range of 840 ° C. or higher and 860 ° C. or lower.

  Specifically, for specimen No. 1, the treatment temperature was 850 ° C., the treatment time was 120 minutes (min) (hereinafter referred to as “850 ° C. × 120 min”), and the undecomposed ammonia fraction: 0 The carbonitriding process was performed at 2% by volume and carbon activity: 0.9. For test piece No. 2, carbonitriding was performed at 840 ° C. × 70 min, undecomposed ammonia fraction: 0.1% by volume, and carbon activity: 0.85. For test piece number 3, carbonitriding was performed at 850 ° C. × 120 min, undecomposed ammonia fraction: 0.1% by volume, and carbon activity: 0.9. Further, for specimen No. 4, carbonitriding was performed at 850 ° C. × 90 min, undecomposed ammonia fraction: 0.1 vol%, and carbon activity: 0.9. For test piece No. 5, carbonitriding was performed at 850 ° C. × 90 min, undecomposed ammonia fraction: 0.1% by volume, and carbon activity: 0.9.

  For test piece No. 6, carbonitriding was performed at 850 ° C. × 90 min, undecomposed ammonia fraction: 0.13% by volume, and carbon activity: 0.9. For test piece No. 7, carbonitriding was performed at 850 ° C. × 150 min, undecomposed ammonia fraction: 0.1% by volume, and carbon activity: 0.85. Further, for specimen No. 8, carbonitriding was performed at 850 ° C. × 150 min, undecomposed ammonia fraction: 0.25 volume%, and carbon activity: 0.9. For test piece number 9, carbonitriding was performed at 850 ° C. × 180 min, undecomposed ammonia fraction: 0.3 vol%, and carbon activity: 0.95. For test piece number 10, carbonitriding was performed at 850 ° C. × 90 min, undecomposed ammonia fraction: 0.2% by volume, and carbon activity: 0.9.

(1-3) Nitrogen concentration measurement method In order to investigate the correlation between the cross-sectional hardness of the sample after high-temperature tempering and the nitrogen concentration, it is necessary to measure the nitrogen concentration distribution in the sample (steel). EPMA linear analysis was used to measure the nitrogen concentration in the steel after carbonitriding. The quantification was performed by analyzing a calibration test piece having a known nitrogen concentration and using the calibration curve. The schematic diagram of the sample and measurement method used for EPMA analysis (Electron Probe Micro Analysis) is as shown in FIG.

  As shown in FIG. 22, consider a case where the inner ring 12 is used as a sample, for example. About the sample, the nitrogen concentration of the sample after carbonitriding was measured. Specifically, a test piece 12A as shown in FIG. 22 is cut out from the sample, and along the direction from the outer peripheral surface 12B to the inner peripheral surface 12C of the test piece, the central portion of the test piece 12A in the height direction ( EPMA line analysis was performed on the cut end face at a position having a half width.

(1-4) Method for Measuring Cross Section Hardness In the test piece 12A described in (1-3) above, the hardness was measured on the cut end face subjected to EPMA analysis. As a measuring method, Vickers hardness measurement was performed using a micro Vickers hardness meter.

(2) Search for holding temperature of high temperature tempering (2-1) Contents of experiment In order to search for a tempering temperature (heating temperature) having a high correlation with the nitrogen concentration, a heating temperature of 180 ° C. was used for 2 hours after carbonitriding Five types of high-temperature tempering were performed on the test piece 12A subjected to tempering called holding time, with the holding time being 1 hour at each heating temperature of 300 ° C, 400 ° C, 500 ° C, 600 ° C, and 700 ° C. The atmosphere during high temperature tempering was an air atmosphere. And the cross-sectional hardness was measured about the test piece processed by each high temperature tempering conditions. In addition, it measured here about the test piece of the test piece numbers 8 and 9 of the carbonitriding process conditions considered that there is much nitrogen penetration | invasion amount.

(2-2) Experimental results A graph summarizing the experimental results is shown in FIG. In the graph shown in FIG. 23, the tempering temperature (° C.) is taken as the horizontal axis, and the difference in cross-sectional hardness (that is, (maximum value of cross-sectional hardness) − (cross-sectional hardness at a depth of 1 mm from the outermost surface after heat treatment): The result of the experiment is arranged with the vertical axis (also denoted as ΔHV). As can be seen from FIG. 23, the difference ΔHV in the cross-sectional hardness was the largest after high-temperature tempering with the heating temperature set at 500 ° C. and the holding time set at 1 hour. The difference ΔHV in the cross-sectional hardness when the heating temperature was 500 ° C. was a value approximately twice the difference ΔHV in the cross-sectional hardness after high-temperature tempering at a heating temperature of 300 ° C. or 700 ° C. Therefore, the hardness after tempering, which has a relatively high correlation with the nitrogen concentration, is considered to be the hardness after tempering at a heating temperature of about 500 ° C. For this reason, in the following experiment, the cross-sectional hardness was measured on a test piece after high-temperature tempering with a heating temperature of 500 ° C. and a holding time of 1 hour.

(3) Investigation of relationship between nitrogen concentration and difference in cross-sectional hardness (ΔHV) Here, each test piece having the composition shown in Table 1 was subjected to carbonitriding, and further subjected to a high temperature tempering at a heating temperature of 500 ° C. and a holding time After performing the heat treatment for 1 hour, the nitrogen concentration of the test piece 12A was measured by EPMA analysis as described with reference to FIG. The carbonitriding treatment was performed under the conditions that the heating temperature was 850 ° C. and the carbon activity / undecomposed ammonia fraction (γ) value was 4.75. Moreover, about the said test piece 12A, the cross-sectional hardness in the depth direction was measured in the cut-out end surface shown in FIG. Then, the relationship between the cross-sectional hardness at a certain position in the depth direction and the cross-sectional hardness at a depth position of 1 (mm) from the outermost surface after heat treatment (cross-sectional hardness difference (ΔHV)) was investigated. The results are shown in FIGS.

  24 and 25, the horizontal axis represents the nitrogen concentration (mass%), and the vertical axis represents the cross-sectional hardness difference (ΔHV) (the unit is Vickers hardness). Moreover, FIG. 25 extracts the relationship between the nitrogen concentration and the cross-sectional hardness difference in the range where the nitrogen concentration is 0 to 0.1 mass% from FIG. From FIG. 24, in the range where the nitrogen concentration exceeds 0 and 0.1% by mass or less, the correlation between the nitrogen concentration and the difference in cross-sectional hardness is strong, while in the range where the nitrogen concentration exceeds 0.1% by mass, the nitrogen concentration It was found that the correlation with the difference in cross-sectional hardness was relatively weak. This is probably because incomplete quenching may occur in a region where the nitrogen concentration is high, and nitrogen dissolved in the test piece does not necessarily contribute to a decrease in the martensite decomposition rate. Further, when the correlation coefficient between the nitrogen concentration and the cross-sectional hardness difference is calculated in FIG. 25 in the range where the nitrogen concentration exceeds 0 and is 0.1 mass% or less, the correlation coefficient between them is as high as 0.8348. For this reason, it is considered that the nitrogen concentration can be predicted from the cross-sectional hardness difference within the range of 0 to 0.1% by mass. Therefore, in the following experiment, the nitrogen concentration is 0.06% by mass and the cross-sectional hardness difference is a substantially intermediate position in a region (0 to 0.1% by mass) in which the nitrogen concentration and the cross-sectional hardness difference have a positive correlation. We decided to use the relationship with 80ΔHV.

(4) Relationship between carbonitriding time and nitrogen concentration distribution In the case of a rolling bearing component, grinding is performed after quenching and tempering to adjust its shape. Therefore, when carbonitriding is performed under certain processing conditions, the nitrogen concentration on the outermost surface of the product (rolling surface or rolling surface) changes due to the machining allowance. For this reason, in order to keep the nitrogen concentration on the outermost surface of the product at 0.4% by mass or more, it is necessary to change the carbonitriding conditions by one-side grinding allowance.

  In FIG. 26, the treatment time is 4 hours (in the figure (in the figure) under the condition that the heating temperature is 850 ° C. and the carbon activity / undecomposed ammonia fraction (γ) is 4.75. A)), 6 hours ((B) in the figure), 8 hours ((C) in the figure), 10 hours ((D) in the figure) nitrogen concentration distribution (high temperature tempering is performed) The previous). In FIG. 26, the horizontal axis indicates the depth (mm) from the surface, and the vertical axis indicates the nitrogen concentration (mass%). Here, when the carbonitriding process is performed under a condition where the value of γ is greater than 5, the nitrogen penetration amount decreases and the region where the nitrogen concentration is high is biased to the surface side. As a result, it becomes practically difficult to set the nitrogen concentration on the product surface to 0.4 mass% or more, except for a method in which the treatment time is very long. Further, when the carbonitriding temperature is 860 ° C. or higher, it is difficult to keep the value of γ at 5 or lower, and when it is 840 ° C. or lower, the diffusion rate of nitrogen into the steel becomes slow. As a result, the processing time becomes longer. For this reason, a temperature of about 850 ° C. is appropriate for the carbonitriding of the steel. The heating temperature during carbonitriding can be determined by the size of the prior austenite crystal grains after quenching. When the heating temperature is 850 ° C., the size of the prior austenite crystal grains in the above steel Is in the range of No. 9 to No. 11 in the JIS standard.

  26, when the one-side grinding allowance on the outermost surface of the product is 0.125 (mm), the carbonitriding time is 4 hours, and when it is 0.15 (mm), 6 hours, 0.175 ( mm) for 8 hours, and 0.2 (mm) for 10 hours, the nitrogen concentration on the outermost surface of the product may be 0.4% by mass or more. I understood.

(5) Relationship between Nitrogen Diffusion Treatment and Nitrogen Concentration Distribution It is effective to perform nitrogen diffusion treatment after carbonitriding to prevent the occurrence of incompletely hardened structure and hardness reduction due to excessive amount of retained austenite. . FIG. 27 shows the nitrogen concentration distribution (measured value and calculated value) in the steel after the nitrogen diffusion treatment. In FIG. 27, the horizontal axis indicates the depth (mm) from the surface, and the vertical axis indicates the nitrogen concentration (mass%). In FIG. 27, (A) is a calculated value when the carbonitriding treatment time is 6 hours and the nitrogen diffusion treatment time is 2 hours (the undecomposed NH ₃ concentration is 0.1% by volume). ) Is the calculated value when the carbonitriding treatment time is 6 hours and the nitrogen diffusion treatment time is 1 hour (undecomposed NH ₃ concentration is 0.05% by volume), and (C) is the carbonitriding treatment. Calculated value when the time for nitrogen diffusion treatment is 2 hours (undecomposed NH ₃ concentration is 0.05% by volume), (D) is the time for carbonitriding treatment for 4 hours, nitrogen diffusion The calculated value when the processing time of the processing is 2 hours (the undecomposed NH ₃ concentration is 0.1% by volume) is shown. These calculated values were calculated assuming that the diffusion coefficient of nitrogen was 1.2 × 10 ⁻⁶ (m ² / s). The calculated values shown in (A) to (D) almost coincided with the actually measured values.

Next, FEM analysis was performed by changing the carbonitriding time and the nitrogen diffusion time (carbonitriding time: 4, 5, 6, 7, 8, 9, 10 hours, nitrogen diffusion time: 1, 2 Time), the nitrogen concentration distribution under each treatment condition was calculated. And the regression formula which made the said calculation result the objective variable was computed. Further, nitrogen is diffused into 0.03 mm by the high temperature tempering (heating temperature: 500 ° C., holding time: 1 hour), and grinding allowance (0.1 to 0.2 mm) in finishing after heat treatment In consideration of the above, the following formulas (3) and (4) for determining the measurement position of the cross-sectional hardness difference after the high-temperature tempering were constructed. The following formula (3) shows the measurement position (x ₁ ) of the cross-sectional hardness for ensuring that the nitrogen concentration on the outermost surface of the product is 0.4% by mass or more, and the formula (4) is the outermost surface of the product. The measurement position (x ₂ ) of the cross-sectional hardness for ensuring that the nitrogen concentration is 0.3 mass% or more is shown. In this case, the heating temperature in the nitrogen diffusion treatment was 850 ° C., the undecomposed NH ₃ concentration was 0.06 vol%, and the carbon activity was 0.9.

(6) Quality Assurance Procedure From the examination results of (1) to (5) above, the procedure for assuring that the nitrogen concentration on the outermost surface of the product is 0.4% by mass or more after the heat treatment is as follows. First, calculate the carbonitriding time T _{1 (h),} the measurement position of the cross-sectional hardness after time nitrogen diffusion process T ₂ a _(h) back hot sintering are substituted into the equation ₍₃₎ x ₁ (mm) To do. Next, high temperature tempering is performed at a heating temperature of 500 ° C. and a holding time of 1 hour. Next, a test piece is cut out from the product after high-temperature tempering, the calculated measurement position x ₁ (mm) and the cross-sectional hardness in the non-nitrided inside are measured, and the cross-sectional hardness difference is calculated from the difference between the measured values. To do. And it is discriminate | determined whether the said cross-sectional hardness difference is 80 (DELTA) HV or more. Thereby, if the said cross-sectional hardness difference is 80 (DELTA) HV or more, it can ensure that the nitrogen concentration in the product outermost surface after grinding is 0.4 mass% or more.

When the carbonitriding time T ₁ is 6 hours and the nitrogen diffusion time T ₂ is 2 hours, the difference in cross-sectional hardness at a depth of 0.4 mm is 80 ΔHV or more from the above equation (3). Furthermore, it is guaranteed that the nitrogen concentration on the outermost surface of the product is 0.4% by mass or more. Further, carbonitriding time T ₁ of the treatment is less than 6 hours, also when the time T ₂ of the nitrogen diffusion process is less than 2 hours, similarly evaluated by cross-sectional hardness difference at a depth position of 0.4mm can do.

(Example 8)
Next, the relationship between the atmosphere during carbonitriding and the carbon concentration and nitrogen concentration distribution was investigated. First, the relationship between the atmosphere during carbonitriding and the carbon concentration distribution was investigated. FIG. 28 shows the carbon concentration and nitrogen concentration distribution when carbonitriding is performed for 2.5 hours in an atmosphere where the value of a _c ^* is 0.80 and the value of α is 0.017 (Comparative Example). ). FIG. 29 shows carbon concentration and nitrogen concentration distributions when carbonitriding is performed for 2.5 hours in an atmosphere where the value of a _c ^* is 0.95 and the value of α is 0.017 ( Example). 28 and 29, the horizontal axis indicates the distance (mm) from the surface, and the vertical axis indicates the carbon concentration and nitrogen concentration (mass%). Further, “C” and “N” in FIG. 28 and FIG. 29 indicate the distribution of the carbon concentration and the nitrogen concentration, respectively.

Referring to FIG. 28 and FIG. 29, since the value of α is the same in the example and the comparative example, nitriding was normally performed in each of the example and the comparative example. However, in the comparative example, the carbide near the surface disappeared and the carbon concentration decreased, and further, decarburization was confirmed slightly in the matrix (see FIG. 28), whereas in the example, the carbon near the surface was reduced. The concentration was almost equivalent to the carbon concentration in the parent phase (see FIG. 29). From this result, it was confirmed that by controlling the atmosphere during the carbonitriding process (by setting an appropriate a _c ^* value), it is possible to maintain an appropriate carbon concentration in the steel surface layer. .

Next, the relationship between the atmosphere during the carbonitriding process and the nitrogen concentration distribution was investigated. FIG. 30 shows a nitrogen concentration distribution when carbonitriding is performed for 5 hours in an atmosphere where the value of a _c ^* is 1 and the value of α is 0.017 (Example). FIG. 31 shows a nitrogen concentration distribution when carbonitriding is performed for 5 hours in an atmosphere where the value of a _c ^* is 1 and the value of α is 0.005 (comparative example). Referring to FIGS. 30 and 31, the carbonitriding time was the same in the example and the comparative example, but in the comparative example, the nitrogen penetration amount was smaller than that in the example and the nitrogen concentration was low. From this result, it was confirmed that by appropriately managing the atmosphere during the carbonitriding process (by setting it to an appropriate α value), the penetration rate of nitrogen can be improved and the efficiency of the carbonitriding process can be improved. It was.

  The embodiments and examples disclosed herein are illustrative in all respects and should not be construed as being restrictive. The scope of the present invention is defined by the terms of the claims, rather than the description above, and is intended to include any modifications within the scope and meaning equivalent to the terms of the claims.

  The bearing component and rolling bearing of the present invention can be particularly advantageously applied to bearing components and rolling bearings that require improved durability.

1 deep groove ball bearing, 2 tapered roller bearing, 11, 21 outer ring, 11A, 21A outer ring rolling surface, 11B, 12B, 22B unground surface, 12, 22 inner ring, 12A, 22A inner ring rolling surface, 13 balls, 13A, 23A Rolling surface, 14, 24 Cage, 23 rollers, 30 Atmosphere control process, 31 Undecomposed NH ₃ partial pressure control process, 32 H ₂ partial pressure control process, 33 CO / CO ₂ partial pressure control process, 40 Heating pattern Control process.

Claims (9)

0.95 to 1.1 mass% carbon, less than 0.3 mass% silicon, less than 0.5 mass% manganese, less than 0.008 mass% sulfur, and 1.4 mass% A bearing component that is made of steel consisting of the balance iron and impurities, and containing a carbonitriding layer on the surface layer including the contact surface that is in contact with other components. There,
The average nitrogen concentration in the surface layer part is 0.3% by mass or more and 0.6% by mass or less, and the variation in nitrogen concentration in the surface layer part is 0.1% by mass or less,
The undecomposed ammonia partial pressure _{P N,} the hydrogen partial pressure in an _{P H,} 1.27 or less being defined _a ^{c *} is 0.88 or more by the following equation (1) is defined by equation (2) A bearing component in which the carbonitriding layer is formed by performing carbonitriding so that α is 0.012 or more and 0.020 or less.
  The bearing component according to claim 1, wherein a gradient of nitrogen concentration in a thickness direction of the bearing component is −15 (1 / m) or more.   The average amount of retained austenite at a position 0.05 mm deep from the contact surface is 25% by volume or more and 35% by volume or less, and the amount of residual austenite at a position 0.05 mm deep from the contact surface varies. The bearing component according to claim 1 or 2, which is 3% by volume or less.   The bearing component according to any one of claims 1 to 3, wherein an overall average retained austenite amount is 18% by volume or less. The bearing component according to any one of claims 1 to 4, wherein the surface layer portion includes five or more carbonitrides having a diameter of 0.5 µm or less per 100 µm ² .   The bearing component according to any one of claims 1 to 5, wherein a nitrogen concentration in an unground portion including an unground surface that is a surface other than the contact surface is less than 0.7 mass%.   The bearing component according to claim 6, wherein the hardness at a position of a depth of 0.1 mm from the non-ground surface is 700 HV or more.   After performing a heat treatment with a heating temperature of 500 ° C. and a holding time of 1 hour, the carbonitriding in the thickness direction of the bearing component is Vickers hardness at a depth of 0.4 (mm) from the contact surface. The bearing component according to claim 1, wherein the bearing component is 80 HV or more higher than the Vickers hardness in a region where no layer is formed.   A rolling bearing comprising the bearing component according to claim 1.