JP2014119744A - Sheet-like article on which hologram is formed, and accessory using sheet-like article on which hologram is formed - Google Patents

Sheet-like article on which hologram is formed, and accessory using sheet-like article on which hologram is formed Download PDF

Info

Publication number
JP2014119744A
JP2014119744A JP2012289373A JP2012289373A JP2014119744A JP 2014119744 A JP2014119744 A JP 2014119744A JP 2012289373 A JP2012289373 A JP 2012289373A JP 2012289373 A JP2012289373 A JP 2012289373A JP 2014119744 A JP2014119744 A JP 2014119744A
Authority
JP
Japan
Prior art keywords
hologram
resin film
synthetic resin
sheet
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2012289373A
Other languages
Japanese (ja)
Inventor
Yasushi Oda
靖史 織田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ORIE CO Ltd
Original Assignee
ORIE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ORIE CO Ltd filed Critical ORIE CO Ltd
Priority to JP2012289373A priority Critical patent/JP2014119744A/en
Publication of JP2014119744A publication Critical patent/JP2014119744A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a sheet-like article in which clear patterns that have a hologram as a back ground and are formed by sublimation transfer are formed on the surface thereof, by subjecting a surface on which a metal deposition layer of a synthetic resin film constituting a hologram layer is not deposited to the sublimation transfer.SOLUTION: A metal deposition layer 2 is deposited and formed on the rear face of a synthetic resin film 1 so as to exhibit a hologram pattern from the outer face of the synthetic resin film 1. On the rear face of the metal deposition layer 2, a fabric 3 is mounted integrally on the metal deposition layer 2 through a hot melt adhesive 4.

Description

本願発明はホログラムを背景にした鮮明な図柄を表現可能なホログラムを施されたシート状物及びホログラムを施されたシート状物を用いた装身物に関する。  The present invention relates to a sheet-like object provided with a hologram capable of expressing a clear design against the background of a hologram, and an accessory using the sheet-like object provided with the hologram.

ホログラム模様を施した物は、ホログラム層を具備するホログラム転写シートを用いて紙等の被転写物に転写し、被転写物にホログラム模様を施すことが一般的であった（例えば、特許文献１、２又は４参照）。このホログラム転写シートを用いる方法であると、離型紙を必要としていた。
又、ホログラム模様を呈する布として、模様を有する布の表面にホログラム形成層を具備する転写シートで転写し、ホログラム形成層の下方から布に施された模様が見えるようにしたリバーシブル布地が提案されている（例えば、特許文献３参照）。
特許文献３に開示の発明は、金属蒸着層を有するホログラム形成層を具備した転写シートを用いて、布の表面にホログラム形成層を転写しようとするものであり、模様は予め最下層に位置する布地表面にプリント等により施しておく必要性がある。そのため、鮮明な図柄が後に付加表現できないという問題点があった。又、布に施した柄がホログラム形成層を介して視認できるようにしているので、図柄がホログラム模様に遮蔽され布に表現した柄がそのまま表出できなず、図柄が不鮮明になるという問題点があった。
熱転写受像シートとしては、裏面層上に基材層を設け、基材層の上にアルミニウム蒸着層を具備するホログラムフィルム層を、その上にウレタン樹脂等からなる中間層を、更に最上層には飽和ポリエステルと塩化ビニルー酢酸ビニル共重合体との混合樹脂等よりなる受容層を順次接着積層し、最下層の裏面層上面に絵柄を施したり、中間層に染料を加えて全体を有彩色にすることが提案されている（例えば、特許文献４参照）。
特許文献４に開示の発明であると、上記特許文献１に開示の発明と同様に、最下層の裏面層に予め表現しておく必要性があり、後に付加することが出来ず、中間層や上層により裏面層に施した柄が遮蔽され、裏面層の柄が鮮明に表出されないという問題点があった。
ホログラム層上に印刷を施し、印刷インクの濃淡によってホログラム面から表出される視覚性を変化させるようにした印刷物が提案されている（例えば、特許文献５参照）。
特許文献５に開示の発明であると、ホログラム面に予め直接的にインクジェット印刷等の印刷により柄を表現し、更に上面に保護フィルムを積層するようにしている。通常、印刷には基材に紙を使用するため、洗濯等に耐久性がなく、又、ホログラム層に直接印刷をするため、例えば雨模様状のホログラム面であると印刷面が雨模様に変化するというように、印刷された絵柄がホログラムの視覚性変化を直接的に影響を受けるという問題点があった。It is common to transfer a hologram pattern onto a transfer object such as paper using a hologram transfer sheet having a hologram layer, and apply the hologram pattern to the transfer object (for example, Patent Document 1). 2 or 4). The method using this hologram transfer sheet requires release paper.
In addition, a reversible fabric has been proposed as a fabric exhibiting a hologram pattern, which is transferred to the surface of the fabric having a pattern by a transfer sheet having a hologram forming layer so that the pattern applied to the fabric can be seen from below the hologram forming layer. (For example, refer to Patent Document 3).
The invention disclosed in Patent Document 3 is intended to transfer a hologram forming layer onto the surface of a cloth using a transfer sheet having a hologram forming layer having a metal vapor-deposited layer, and the pattern is located in the lowermost layer in advance. There is a need to print on the fabric surface. Therefore, there is a problem that a clear symbol cannot be additionally expressed later. In addition, since the pattern applied to the cloth is visible through the hologram forming layer, the pattern is shielded by the hologram pattern, and the pattern expressed on the cloth cannot be displayed as it is, and the pattern becomes unclear. was there.
As the thermal transfer image-receiving sheet, a base material layer is provided on the back surface layer, a hologram film layer having an aluminum vapor deposition layer is provided on the base material layer, an intermediate layer made of urethane resin or the like is provided thereon, and an uppermost layer is provided on the uppermost layer. Adhesive layers consisting of a mixed resin of saturated polyester and vinyl chloride-vinyl acetate copolymer are adhered and laminated in sequence, and a pattern is applied to the upper surface of the lowermost back layer, or a dye is added to the intermediate layer to make the whole chromatic. Has been proposed (see, for example, Patent Document 4).
In the invention disclosed in Patent Document 4, like the invention disclosed in Patent Document 1, it is necessary to express in advance in the lowermost back layer, and cannot be added later. There is a problem that the pattern applied to the back layer is shielded by the upper layer, and the pattern of the back layer is not clearly exposed.
There has been proposed a printed matter in which printing is performed on a hologram layer, and the visibility expressed from the hologram surface is changed by the density of the printing ink (see, for example, Patent Document 5).
In the invention disclosed in Patent Document 5, a pattern is expressed in advance on the hologram surface by printing such as ink jet printing, and a protective film is further laminated on the upper surface. Usually, paper is used as a base material for printing, so it is not durable for washing, etc., and printing is performed directly on the hologram layer. Thus, there is a problem that the printed pattern is directly affected by the change in the visibility of the hologram.

特公平６−９０５９３号公報Japanese Examined Patent Publication No. 6-90593 特許第４９９８３８４号の特許公報Patent No. 4998384 特開平７−２１６７６４号公報Japanese Patent Laid-Open No. 7-216764 特開２００２−１８７３６９号公報JP 2002-187369 A 実用新案登録第３１３１９４３号の登録実用新案公報Registered Utility Model Gazette No. 3119443

本願発明は上記従来技術の問題点を解決するために布を基材の一部に用いること、及び、ホログラム転写シートを用いることなく、ホログラム層の構成要素の一部である金属蒸着層が被着された合成樹脂製フィルムの外面に直接に昇華転写により図柄を転写して表現することでホログラム模様を背景にし表面に昇華転写による鮮明な図柄を表出した多目的に使用できる用途の広いホログラムを施されたシート状物及びホログラムを施されたシート状物を用いた装身物を提供することを目的とする。  In the present invention, a cloth is used as a part of a base material to solve the problems of the prior art, and a metal vapor deposition layer which is a part of a component of a hologram layer is covered without using a hologram transfer sheet. A versatile hologram that can be used for various purposes, with the hologram pattern in the background and the vivid design by sublimation transfer on the surface by expressing the pattern directly by sublimation transfer on the outer surface of the attached synthetic resin film. It is an object of the present invention to provide an accessory using a sheet-like material that has been applied and a sheet-like material that has been subjected to a hologram.

上記目的を達成するために、本願の請求項１に係る発明は表面に昇華転写による図柄を表現されるホログラムを施されたシート状物であって、合成樹脂製フィルムの裏面に金属蒸着層が被着されてホログラム層が形成され、金属蒸着層の裏面には接着剤を介在させて布が重合接着され、合成樹脂製フィルムの表面に昇華転写により図柄が施されてなることを特徴とする。
請求項２に記載の発明は、表面に昇華転写による図柄を表現されたホログラムを施されたシート状物であって、合成樹脂製フィルムの裏面に金属蒸着層が被着されたホログラム層が形成され、前記金属蒸着層の裏面には接着剤を介在させて裏面側合成樹脂製フィルムを接着積層し、該裏面側合成樹脂製フィルムの裏面には接着剤を用いないで布を重合接着して積層し、前記表面側合成樹脂製フィルムの表面に昇華転写により絵柄が施されてなることを特徴とする。
請求項３に記載の発明は、表面及び裏面の両面に昇華転写による図柄を表現されたホログラムを施されたシート状物であって、合成樹脂製フィルムの内側面に金属蒸着層が被着されてなるホログラム層、接着剤、合成樹脂製フィルム、布、合成樹脂製フィルム、接着剤、合成樹脂製フィルムの内側面に金属蒸着層が被着形成されてなるホログラム層を順次積層して一体的に形成し、前記ホログラム層の合成樹脂製フィルムの外側面に昇華転写により図柄が施されてなることを特徴とする。
請求項４に記載の発明は、表面及び裏面の両面に昇華転写による図柄を表現されたホログラムを施されたシート状物であって、合成樹脂製フィルムの内側面に金属蒸着層が被着されてなるホログラム層と別の合成樹脂製フィルムの内側面に金属蒸着層が被着されてなるホログラム層との間に接着剤を介在させて重合接着し、前記合成樹脂製フィルムの外側面に昇華転写により図柄が施されてなることを特徴とする。
請求項５に記載の発明は、請求項１、２、３又は４の何れかに記載のホログラムを施されたシート状物を構成する合成樹脂製フィルムが、ポリエステル系樹脂製フィルムであることを特徴とする。
請求項６に記載の発明は、請求項１、２、３、４又は５の何れかに記載のホログラムを施されたシート状物の接着剤がホットメルト接着剤であることを特徴とする。
請求項７に記載の発明は、上記請求項１、２、３、４、５又は６の何れかに記載のホログラムを施されたシート状物を用いた装身物であって、シート状物を所望形状に切断し、且つ周縁を縁かがりをし、縫製或は貼着により鞄や衣服に取り付けたことを特徴とする。In order to achieve the above-mentioned object, the invention according to claim 1 of the present application is a sheet-like material on which a hologram expressing a pattern by sublimation transfer is applied on the surface, and a metal vapor deposition layer is formed on the back surface of the synthetic resin film. A hologram layer is formed by being deposited, and a cloth is polymerized and bonded to the back surface of the metal vapor deposition layer with an adhesive interposed therebetween, and a pattern is applied to the surface of the synthetic resin film by sublimation transfer. .
The invention according to claim 2 is a sheet-like material having a hologram on which the hologram is expressed by sublimation transfer, and a hologram layer having a metal vapor deposition layer deposited on the back surface of the synthetic resin film is formed. An adhesive is interposed on the back side of the metal vapor deposition layer, and a back side synthetic resin film is adhered and laminated, and the back side of the back side synthetic resin film is polymerized and bonded without using an adhesive. It is characterized in that it is laminated and a pattern is applied to the surface of the surface side synthetic resin film by sublimation transfer.
The invention according to claim 3 is a sheet-like material in which a hologram expressing a pattern by sublimation transfer is applied to both the front and back surfaces, and a metal vapor deposition layer is deposited on the inner surface of the synthetic resin film. Hologram layer, adhesive, synthetic resin film, cloth, synthetic resin film, adhesive, hologram layer with a metal vapor deposition layer deposited on the inner surface of the synthetic resin film And a pattern is formed on the outer surface of the synthetic resin film of the hologram layer by sublimation transfer.
The invention according to claim 4 is a sheet-like material in which a hologram expressing a pattern by sublimation transfer is applied to both the front and back surfaces, and a metal vapor deposition layer is deposited on the inner surface of the synthetic resin film. An adhesive is interposed between the hologram layer formed and the hologram layer formed by depositing a metal vapor deposition layer on the inner surface of another synthetic resin film, and is sublimated on the outer surface of the synthetic resin film. It is characterized in that a pattern is given by transfer.
According to a fifth aspect of the present invention, the synthetic resin film constituting the sheet-like material to which the hologram according to any one of the first, second, third, and fourth aspects is applied is a polyester resin film. Features.
The invention described in claim 6 is characterized in that the adhesive of the sheet-like material on which the hologram according to any one of claims 1, 2, 3, 4 or 5 is applied is a hot melt adhesive.
The invention according to claim 7 is an article using the sheet-like material to which the hologram according to any one of the above-mentioned claims 1, 2, 3, 4, 5 or 6 is applied, and the sheet-like material. Is cut into a desired shape, the periphery is edged, and it is attached to a bag or clothing by sewing or sticking.

ホログラム転写シートにより転写した物品に昇華転写をするのではなく、直接、鮮明な昇華転写が可能なポリエステル系樹脂よりなるフィルムに昇華転写をすることで、鮮明な図柄が表現できるという効果がある。
直接、ホログラム層の金属蒸着層とは反対面に昇華転写をするため、離型紙等が不要であり、作業性が向上するという効果がある。
基材に布を使用しているため、好みの形状に切断してバッグや衣服等に直接縫着することが可能で、耐洗濯性に優れ、例えば衣服への装飾部品等、用途が拡大するという効果がある。There is an effect that a clear design can be expressed by performing sublimation transfer directly on a film made of a polyester resin capable of performing clear sublimation transfer, instead of performing sublimation transfer on an article transferred by a hologram transfer sheet.
Since the sublimation transfer is directly performed on the surface of the hologram layer opposite to the metal vapor deposition layer, a release paper or the like is unnecessary, and workability is improved.
Since cloth is used for the base material, it can be cut into a desired shape and sewn directly to a bag or clothes, etc., and it has excellent washing resistance. For example, it can be used for decorative parts on clothes. There is an effect.

ホログラムを施されたシート状物の断面図である。（実施例１）It is sectional drawing of the sheet-like object to which the hologram was given. Example 1 ホログラムを施されたシート状物を用いた装身物を示す平面図である。（実施例１）It is a top view which shows the accessory using the sheet-like object to which the hologram was given. Example 1 ホログラムを施されたシート状物の製造方法において、合成樹脂製フィルムの片面に金属蒸着層が被着された状態を示す説明図である。（実施例１）It is explanatory drawing which shows the state by which the metal vapor deposition layer was adhere | attached on the single side | surface of the synthetic resin film in the manufacturing method of the sheet-like material which gave the hologram. Example 1 ホログラムを施されたシート状物を製造する方法おいて、布の片面に接着剤を塗着した状態を示す説明図である。（実施例１）It is explanatory drawing which shows the state which apply | coated the adhesive agent to the single side | surface of the cloth in the method of manufacturing the sheet-like material which gave the hologram. Example 1 ホログラムを施されたシート状物を製造する方法おいて、接着剤を塗着された布に金属蒸着層が被着された合成樹脂製フィルムを重合する状態を示す説明図である。（実施例１）It is explanatory drawing which shows the state which superposes | polymerizes the synthetic resin film by which the metal vapor deposition layer was adhere | attached on the cloth which apply | coated the adhesive agent in the method of manufacturing the sheet-like material which gave the hologram. Example 1 ホログラムを施されたシート状物を製造する方法おいて、布、接着剤、金属蒸着層及び合成樹脂製フィルムよりなる積層体の合成樹脂製フィルムの上面に昇華転写シートを載置しようとする状態を示す説明図である。（実施例１）In a method for producing a hologram-formed sheet, a state in which a sublimation transfer sheet is to be placed on the upper surface of a synthetic resin film of a laminate comprising a cloth, an adhesive, a metal vapor deposition layer, and a synthetic resin film It is explanatory drawing which shows. Example 1 昇華転写シートを合成樹脂製フィルムから剥離する状態を示す説明図である。（実施例１）It is explanatory drawing which shows the state which peels a sublimation transfer sheet from a synthetic resin film. Example 1 ホログラムを施されたシート状物の断面図である。（実施例２）It is sectional drawing of the sheet-like object to which the hologram was given. (Example 2) ホログラムを施されたシート状物を製造する方法おいて、合成樹脂製フィルム、金属蒸着層、接着剤、合成樹脂製フィルムを積層した状態を示す説明図である。（実施例２）It is explanatory drawing which shows the state which laminated | stacked the synthetic resin film, the metal vapor deposition layer, the adhesive agent, and the synthetic resin film in the method of manufacturing the sheet-like material which gave the hologram. (Example 2) ホログラムを施されたシート状物を製造する方法おいて、合成樹脂製フィルム、金属蒸着層、接着剤、合成樹脂製フィルムからなる積層体を布に重合する状態を示す説明図である。（実施例２）It is explanatory drawing which shows the state which superposes | stacks the laminated body which consists of a synthetic resin film, a metal vapor deposition layer, an adhesive agent, and a synthetic resin film on the cloth in the method of manufacturing the sheet-like material which gave the hologram. (Example 2) ホログラムを施されたシート状物を製造する方法おいて、合成樹脂製フィルム、金属蒸着層、接着剤、合成樹脂製フィルム、布からなる積層体の合成樹脂製フィルムの上面に昇華転写シートを載置しようとする状態を示す説明図である。（実施例２）In a method for producing a hologram-formed sheet, a sublimation transfer sheet is placed on the upper surface of a synthetic resin film, a metal vapor-deposited layer, an adhesive, a synthetic resin film, or a synthetic resin film of a laminate made of cloth. It is explanatory drawing which shows the state which is going to put. (Example 2) 昇華転写シートを合成樹脂製フィルムの上面から剥離する状態を示す説明図である。（実施例２）It is explanatory drawing which shows the state which peels a sublimation transfer sheet from the upper surface of a synthetic resin film. (Example 2) ホログラムを施されたシート状物の断面図である。（実施例３）It is sectional drawing of the sheet-like object to which the hologram was given. (Example 3) 積層体間に布を介在させて積層体を層状に重合接着する状態を示す説明図である。（実施例３）It is explanatory drawing which shows the state which superpose | polymerizes and bonds a laminated body in a layer form by interposing a cloth between laminated bodies. (Example 3) ホログラムを施されたシート状物の断面図である。（実施例４）It is sectional drawing of the sheet-like object to which the hologram was given. Example 4 ホログラムを施されたシート状物を製造する方法を示す説明図である。（実施例４）It is explanatory drawing which shows the method of manufacturing the sheet-like object which gave the hologram. Example 4

合成樹脂製フィルムと布とは熱溶着で重合接着し、金属蒸着層と合成樹脂製フィルムとはホットメルト接着剤層を介在させることで過熱加圧作業で一体的に積層し、ホログラム層のホログラムを表出する合成樹脂製フィルムの表面に図柄を直接昇華転写することでホログラムを背景にした鮮明な図柄の表現を実現した。  The synthetic resin film and the fabric are polymerized and bonded by thermal welding, and the metal vapor deposition layer and the synthetic resin film are laminated together by overheating and pressurizing work by interposing a hot melt adhesive layer. By virtue of direct sublimation transfer on the surface of the synthetic resin film that expresses the image, a vivid design with a hologram background was realized.

図１及び図２に基いてホログラムを施されたシート状物の実施例を説明する。合成樹脂製フィルム１としてポリエチレンテレフタレートフィルム（以下「ＰＥＴフィルム」という）等のポリエステル系合成樹脂製フィルムを用いる。合成樹脂製フィルム１の裏面にはアルミニウム等よりなる金属蒸着層２を被着形成している。合成樹脂製フィルム１の外面からはホログラム模様が呈されている。ホログラム模様は、金属蒸着層２の構造よりレインボー状模様、３ｃｍレンズ状模様、７色レンズ状模様、１０ｃｍレンズ状模様、クリスタル模様、ハイパー模様、ダスト状模様、筋状（雨状）模様、モザイク模様等の如何なる模様を呈するものであってもよい。金属蒸着層２の裏面には布３が、接着剤４を介して金属蒸着層２に一体的に取り付けられている。布３はポリエステル繊維等の合成繊維よりなる不織布を用いることが好適であるが、綿、麻、レーヨンやキュプラ等の再生繊維、合成繊維と天然繊維との混紡、或は獣毛繊維の何れであってもよく、又、織物であってもよい。接着剤４はホットメルト接着剤であり、具体的にはポリアミド系接着剤を用いることが好適である。ポリエステル系樹脂製フィルム１の表面には昇華転写により絵柄が施されている。  An embodiment of a sheet-like material on which a hologram is applied will be described with reference to FIGS. As the synthetic resin film 1, a polyester synthetic resin film such as a polyethylene terephthalate film (hereinafter referred to as "PET film") is used. A metal vapor deposition layer 2 made of aluminum or the like is deposited on the back surface of the synthetic resin film 1. A hologram pattern is presented from the outer surface of the synthetic resin film 1. The hologram pattern is a rainbow pattern, 3 cm lens pattern, 7 color lens pattern, 10 cm lens pattern, crystal pattern, hyper pattern, dust pattern, stripe pattern (rain pattern), mosaic from the structure of the metal deposition layer 2. It may be any pattern such as a pattern. A cloth 3 is integrally attached to the metal vapor deposition layer 2 via an adhesive 4 on the back surface of the metal vapor deposition layer 2. The cloth 3 is preferably a non-woven fabric made of synthetic fibers such as polyester fibers, but any of recycled fibers such as cotton, hemp, rayon and cupra, a blend of synthetic fibers and natural fibers, or animal hair fibers. It may also be a woven fabric. The adhesive 4 is a hot melt adhesive, and specifically, a polyamide-based adhesive is preferably used. A pattern is given to the surface of the polyester resin film 1 by sublimation transfer.

図２に示すホログラムを施されたシート状物を用いた装身物は、布３、接着剤４、金属蒸着層２及び合成樹脂製フィルム１が一体的に積層されてなる積層体を所望形状に切断し、周縁を縁かがりの目的でメロー仕上げ５をして形成されている。布３を被取着物である布製バッグや衣服等の表面に当接させ、メロー仕上げ５の部分に沿って縫い目を設けて縫着するか、不織布３の外面に接着剤を塗着して被取着物である皮革製若しくは合成樹脂製バッグや衣服等の表面に接着して取り付けて装飾目的に使用することができる。  As shown in FIG. 2, an article using a hologram-formed sheet-like material has a desired shape of a laminate in which a cloth 3, an adhesive 4, a metal vapor deposition layer 2, and a synthetic resin film 1 are integrally laminated. The outer periphery is formed with a mellow finish 5 for the purpose of edging. The cloth 3 is brought into contact with the surface of a cloth bag or clothes which is an object to be attached, and is sewn with a seam along the mellow finish 5, or an adhesive is applied to the outer surface of the nonwoven fabric 3 It can be attached to the surface of a leather or synthetic resin bag or clothes as an attachment and used for decoration purposes.

次に、図３〜図７を参照にして実施例１のホログラムを施されたシート状物の製造方法について説明する。先ずは、図３に示すように、ＰＥＴフィルムよりなる合成樹脂製フィルム１の裏面に金属蒸着層２を被着形成して２層よりなる積層体を製造する。次に、図４に示すように、ポリエステル繊維製不織布よりなる布３の表面にホットメルト接着剤４を均一に塗着し布３と接着剤４よりなる２層の積層体を製造する。図５に示すように、布３と接着剤４よりなる２層の積層体の表面に裏面に金属蒸着層２を具備する合成樹脂製フィルム１の裏面を重合し熱圧着し、布３、接着剤４、金属蒸着層２及び合成樹脂製フィルム１よりなる４層積層体を得る。図６に示すように、４層積層体のポリエステル系樹脂製フィルム１の表面に昇華転写シート６を重ね合わせ、転写する図柄により加熱温度は異なるが約１８０℃程度の温度で加熱し加圧する。図７に示すように、昇華転写シート６を１の合成樹脂製フィルム１の表面から剥離して、合成樹脂製フィルム１の表面に絵柄を転写してホログラムを施されたシート状物を得る。得られた製品は、合成樹脂製フィルム１の表面に昇華転写により鮮明な図柄が表現でき、裏面に布３が一体的に取り付けられているので、洗濯等の物理的刺激に対し耐久性を有し、製品を所望形状に切断し、周囲にメロー仕上げを施すことで片面にホログラム模様を背景にし、表面には鮮明な図柄が表出しているワッペン等としてバッグや衣服等に直接縫着或は接着剤を用いて貼着できる。最も裏面側に配設される布３に接着剤を介在させて別の不織布を重合接着し、基布の硬度を高めることも本願発明に包含される。
実施例１は、ポリエステル系樹脂製フィルムである合成樹脂製フィルム１、つまり高分子フィルムの表面に直接的に昇華転写を行うため、ホログラム模様を背景にした鮮明な画像が転写されたシート状物を得ることができる。従来のように、ホログラム層を具備する転写シートで布にホログラム層を転写する必要性がないため、作業性が向上する。Next, with reference to FIGS. 3 to 7, a method for manufacturing the sheet-like material on which the hologram of Example 1 is applied will be described. First, as shown in FIG. 3, a metal vapor deposition layer 2 is deposited on the back surface of a synthetic resin film 1 made of a PET film to produce a laminate composed of two layers. Next, as shown in FIG. 4, a hot-melt adhesive 4 is uniformly applied to the surface of a cloth 3 made of a polyester fiber nonwoven fabric to produce a two-layer laminate made of the cloth 3 and the adhesive 4. As shown in FIG. 5, the back surface of the synthetic resin film 1 having the metal vapor deposition layer 2 on the back surface is polymerized and thermocompression bonded to the front surface of the two-layer laminate composed of the fabric 3 and the adhesive 4, and the fabric 3 and the adhesive are bonded. A four-layer laminate comprising the agent 4, the metal vapor deposition layer 2, and the synthetic resin film 1 is obtained. As shown in FIG. 6, a sublimation transfer sheet 6 is superimposed on the surface of a polyester resin film 1 of a four-layer laminate, and is heated and pressurized at a temperature of about 180 ° C. although the heating temperature varies depending on the pattern to be transferred. As shown in FIG. 7, the sublimation transfer sheet 6 is peeled from the surface of the synthetic resin film 1, and the pattern is transferred to the surface of the synthetic resin film 1 to obtain a sheet-like material on which a hologram is applied. The resulting product can express a clear pattern on the surface of the synthetic resin film 1 by sublimation transfer, and the cloth 3 is integrally attached to the back surface, so that it has durability against physical stimuli such as washing. The product is cut into a desired shape, and a mellow finish is applied around it to make a hologram pattern on one side as a background. Can be attached using an adhesive. It is also included in the present invention to increase the hardness of the base fabric by polymerizing and bonding another non-woven fabric by interposing an adhesive on the cloth 3 arranged on the most back side.
Example 1 is a synthetic resin film 1 that is a polyester resin film, that is, a sheet-like material on which a clear image with a hologram pattern as a background is transferred because sublimation transfer is directly performed on the surface of a polymer film. Can be obtained. Since there is no need to transfer the hologram layer to the cloth with the transfer sheet having the hologram layer as in the conventional case, workability is improved.

図８に示されるホログラムを施されたシート状物の実施例２を説明する。合成樹脂製フィルム７の裏面に金属蒸着層８が被着されてホログラム層を形成している。合成樹脂製フィルム７には、ポリエステル系樹脂製フィルムを使用する。金属蒸着層８の裏面には、ホットメルト接着剤９を介在してポリエステル系の合成樹脂製フィルム１０が一体的に積層されている。合成樹脂製フィルム１０の裏面にはポリエステル繊維からなる不織布１１が接着剤を用いることなく加熱による溶着で一体的に被着積層されている。つまり、布１１、合成樹脂製フィルム１０、接着剤９、金属蒸着層８及び合成樹脂製フィルム７が下から順に積層された５層積層体に形成され、合成樹脂製フィルム７の外面に昇華転写による図柄が施されている。不織布よりなる布１１には、接着剤を用いて別の不織布よりなる布を接着し、布１１の強度を高めることも本願発明に包含され。合成樹脂製フィルム７の表面には、昇華転写により図柄が施されている。  Example 2 of the sheet-like material provided with the hologram shown in FIG. 8 will be described. A metal vapor deposition layer 8 is deposited on the back surface of the synthetic resin film 7 to form a hologram layer. A polyester resin film is used for the synthetic resin film 7. A polyester-based synthetic resin film 10 is integrally laminated on the back surface of the metal vapor-deposited layer 8 with a hot melt adhesive 9 interposed therebetween. On the back surface of the synthetic resin film 10, a nonwoven fabric 11 made of polyester fibers is integrally laminated by heat welding without using an adhesive. That is, the cloth 11, the synthetic resin film 10, the adhesive 9, the metal vapor deposition layer 8, and the synthetic resin film 7 are formed in a five-layer laminate in order from the bottom, and are sublimated and transferred to the outer surface of the synthetic resin film 7. The design by is given. It is also included in the present invention that the cloth 11 made of non-woven fabric is bonded to another cloth made of non-woven cloth using an adhesive to increase the strength of the cloth 11. The surface of the synthetic resin film 7 is provided with a pattern by sublimation transfer.

図９〜図１２を参照にして実施例２のホログラムを施されたシート状物の製造方法について説明する。先ず、図９に示すように、合成樹脂製フィルム７の裏面に金属蒸着法により金属蒸着層８を被着形成する。金属蒸着層８の裏面にはホットメルト接着剤９を介在させて合成樹脂製フィルム１０を接着している。図１０に示すように、合成樹脂製フィルム１０の裏面にポリエステル繊維よりなる不織布の布１１を重合し、加熱加圧により合成樹脂製フィルム１０の裏面にポリエステル繊維よりなる不織布製の布１１を溶着して、布１１、合成樹脂製フィルム１０、接着剤９、金属蒸着層８、及び合成樹脂製フィルム７よりなる５層の積層体を得る。この５層の積層体の合成樹脂製フィルム７の表面に昇華転写シート６を載置した状態で加熱及び加圧をし、図１２に示すように昇華転写シート６を合成樹脂製フィルム７の表面から剥離する。得られた製品は、合成樹脂製フィルム７の表面に鮮明な図柄が施され、背景にはホログラム模様を有する装飾性の高い製品であった。  With reference to FIGS. 9 to 12, a method for manufacturing the sheet-like material on which the hologram of Example 2 is applied will be described. First, as shown in FIG. 9, a metal vapor deposition layer 8 is deposited on the back surface of the synthetic resin film 7 by a metal vapor deposition method. A synthetic resin film 10 is bonded to the back surface of the metal vapor deposition layer 8 with a hot melt adhesive 9 interposed therebetween. As shown in FIG. 10, a nonwoven fabric cloth 11 made of polyester fibers is polymerized on the back surface of the synthetic resin film 10, and the nonwoven cloth cloth 11 made of polyester fibers is welded to the back surface of the synthetic resin film 10 by heating and pressing. Thus, a five-layer laminate including the cloth 11, the synthetic resin film 10, the adhesive 9, the metal vapor deposition layer 8, and the synthetic resin film 7 is obtained. The sublimation transfer sheet 6 is heated and pressurized in a state where the sublimation transfer sheet 6 is placed on the surface of the five-layer laminate synthetic resin film 7, and the sublimation transfer sheet 6 is then applied to the surface of the synthetic resin film 7 as shown in FIG. Peel from. The obtained product was a highly decorative product having a clear pattern on the surface of the synthetic resin film 7 and a hologram pattern in the background.

図１３に示されるホログラムを施されたシート状物の実施例３を説明する。ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１２、金属蒸着層１３、ホットメルト接着剤１４、ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１５、布１６、ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１７、接着剤１８、金属蒸着層１９、ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２０が順に重合積層されて一体化し９層積層体を形成している。ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１２及びポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２０の外面には夫々昇華転写により鮮明な図柄が表現されている。
このシート状物は所望形状に切断して周囲をメロー仕上げ等の縁かがり加工をすることで、より装飾性が高まる。断面中心部にポリエステル繊維よりなる不織布の布１６が配設されていることで縫製することが可能である。ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１２とポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２０から表出されるホログラム模様を異ならしめることや、昇華転写する図柄を表裏面で異ならしめることで、表裏面からは異なる視覚性を訴えるホログラムを背景とした絵柄が表現でき、リバーシブルのホログラムを施されたシート状物を提供することができる。Example 3 of the sheet-like material provided with the hologram shown in FIG. 13 will be described. Synthetic resin film 12 made of polyester resin film, metal vapor deposition layer 13, hot melt adhesive 14, synthetic resin film 15 made of polyester resin film, cloth 16, synthetic resin made of polyester resin film A film 17, an adhesive 18, a metal vapor deposition layer 19, and a synthetic resin film 20 made of a polyester resin film are sequentially laminated and integrated to form a nine-layer laminate. On the outer surfaces of the synthetic resin film 12 made of a polyester resin film and the synthetic resin film 20 made of a polyester resin film, clear patterns are expressed by sublimation transfer, respectively.
The sheet-like material is cut into a desired shape and the periphery thereof is subjected to edge processing such as mellow finishing, whereby the decorativeness is further enhanced. It is possible to sew by arranging a non-woven cloth 16 made of polyester fiber in the center of the cross section. By making the hologram pattern displayed from the synthetic resin film 12 made of the polyester resin film and the synthetic resin film 20 made of the polyester resin film different, or making the pattern to be sublimated transferred differently on the front and back surfaces, From the front and back surfaces, it is possible to express a picture against a background of a hologram that appeals to different visual properties, and it is possible to provide a sheet-like material with a reversible hologram.

図１４を参照にして実施例１３のホログラムを施されたシート状物の製造方法について説明する。先ずは、合成樹脂製フィルム１２の片面にアルミニウムの金属蒸着層１３を被着形成する。金属蒸着層１３の合成樹脂製フィルム１２が被着されていない面には接着剤１４を介在して合成樹脂製フィルム１５を接着し、４層の積層体２１を製造する。合成樹脂製フィルム２０の片面には金属蒸着層１９を被着形成する。金属蒸着層１９の合成樹脂製フィルム２０が被着されていない面には接着剤１８を介在して合成樹脂製フィルム１７を接着し４層の積層体２２を製造する。積層体２２と積層体２１との間には不織布よりなる布１６を介在して熱加圧により布１６をポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１５、１７に溶着する。得られた９層の積層体のポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム１２、２０の外面に昇華転写シート（図示省略）を当接し、加熱加圧して両面に昇華転写による図柄が施されたシートを得る。  With reference to FIG. 14, the manufacturing method of the sheet-like object which gave the hologram of Example 13 is demonstrated. First, an aluminum metal deposition layer 13 is deposited on one surface of a synthetic resin film 12. A synthetic resin film 15 is adhered to the surface of the metal vapor deposition layer 13 on which the synthetic resin film 12 is not attached, with an adhesive 14 interposed therebetween, and a four-layer laminate 21 is manufactured. A metal vapor deposition layer 19 is deposited on one side of the synthetic resin film 20. A synthetic resin film 17 is adhered to the surface of the metal vapor deposition layer 19 on which the synthetic resin film 20 is not adhered, with an adhesive 18 interposed therebetween, to produce a four-layer laminate 22. A cloth 16 made of a nonwoven fabric is interposed between the laminated body 22 and the laminated body 21, and the cloth 16 is welded to the synthetic resin films 15 and 17 made of a polyester resin film by heat and pressure. A sublimation transfer sheet (not shown) is brought into contact with the outer surfaces of the synthetic resin films 12 and 20 made of a polyester resin film of the resulting 9-layer laminate, and a pattern by sublimation transfer is applied to both surfaces by heating and pressing. Get a sheet.

図１５に示されるホログラムを施されたシート状物の実施例４を説明する。ポリエステル系樹脂製フィルム２３、アルミニウムの金属蒸着層２４、接着剤２５、アルミニウムの金属蒸着層２６、ポリエステル系樹脂製フィルム２７が順に層状に一体的に重合されている。ポリエステル系樹脂製フィルム２３、２６からはホログラム模様が表出されている。ポリエステル系樹脂製フィルム２３、２６には昇華転写により図柄が施されている。ポリエステル系樹脂製フィルム２３とポリエステル系樹脂製フィルム２６に形成されているホログラム模様を表面と裏面とで異ならしめ、且つ昇華転写された図柄も異ならしめることで表裏面で異なるホログラム模様の背景を具備した図柄を表現できる。  Example 4 of the sheet-like material provided with the hologram shown in FIG. 15 will be described. A polyester resin film 23, an aluminum metal vapor deposition layer 24, an adhesive 25, an aluminum metal vapor deposition layer 26, and a polyester resin film 27 are integrally polymerized in this order. Hologram patterns are exposed from the polyester resin films 23 and 26. The polyester resin films 23 and 26 are given a pattern by sublimation transfer. The hologram pattern formed on the polyester resin film 23 and the polyester resin film 26 is made different between the front and back surfaces, and the background of the different hologram patterns is provided on the front and back surfaces by making the sublimation transferred patterns different. Can be expressed.

図１６を参照にして実施例４のホログラムを施されたシート状物の製造方法について説明する。ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２３の片面にアルミニウムの金属蒸着層２４を被着形成する。ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２７の片面にアルミニウムの金属蒸着層２６を被着形成する。金属蒸着層２６にホットメルト接着剤２５を塗着し、ホットメルト接着剤２５の塗着面に金属蒸着層２４を重合し、加熱加圧接着する。得られたポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２３、金属蒸着層２４、接着剤２５、金属蒸着層２６、ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２７よりなる５層の積層体のポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２３、２７の外面に昇華転写シートを重合した状態で加熱加圧し、ポリエステル系樹脂製フィルムよりなる合成樹脂製フィルム２３、２７の表面からホログラムを背景にした鮮明な図柄が施された模様が呈される。  With reference to FIG. 16, the manufacturing method of the sheet-like object which gave the hologram of Example 4 is demonstrated. An aluminum metal deposition layer 24 is deposited on one side of a synthetic resin film 23 made of a polyester resin film. An aluminum metal deposition layer 26 is deposited on one side of a synthetic resin film 27 made of a polyester resin film. A hot melt adhesive 25 is applied to the metal vapor deposition layer 26, and the metal vapor deposition layer 24 is polymerized on the surface to which the hot melt adhesive 25 is applied, followed by heat and pressure bonding. A synthetic resin film 23 made of a polyester-based resin film, a metal vapor-deposited layer 24, an adhesive 25, a metal vapor-deposited layer 26, and a 5-layer laminate composed of a synthetic resin-made film 27 made of a polyester-based resin film. Heat-pressed in a state where a sublimation transfer sheet is polymerized on the outer surface of the synthetic resin films 23 and 27 made of a polyester resin film, and a hologram from the surface of the synthetic resin films 23 and 27 made of a polyester resin film A pattern with a clear pattern is displayed.

１、７、１０、１２、１５、１７、２３、２７ 合成樹脂製フィルム
２、８、１３、１９、２４ 金属蒸着層
３、１１、１６ 布
４、９、１４、１８、２５ 接着剤
５ 縁かがり
６ 昇華転写シート1, 7, 10, 12, 15, 17, 23, 27 Synthetic resin film 2, 8, 13, 19, 24 Metallized layer 3, 11, 16 Cloth 4, 9, 14, 18, 25 Adhesive 5 Edge Kagari 6 Sublimation transfer sheet

Claims (7)

合成樹脂製フィルムの表面に昇華転写による図柄が表現されたホログラムを施されたシート状物であって、
前記合成樹脂製フィルムの裏面に金属蒸着層が被着されてホログラム層が形成され、
前記金属蒸着層の裏面には接着剤を介在させて布が重合接着され、
前記合成樹脂製フィルムの表面に昇華転写により図柄が施されてなることを特徴とするホログラムを施されたシート状物。It is a sheet-like material with a hologram on which a pattern by sublimation transfer is expressed on the surface of a synthetic resin film,
A metal vapor deposition layer is deposited on the back surface of the synthetic resin film to form a hologram layer,
A cloth is polymerized and bonded to the back surface of the metal deposition layer with an adhesive interposed therebetween,
A sheet-like article provided with a hologram, wherein a pattern is applied to the surface of the synthetic resin film by sublimation transfer. 表面に昇華転写による図柄を表現されたホログラムを施されたシート状物であって、
合成樹脂製フィルムの裏面に金属蒸着層が被着されたホログラム層が形成され、
前記金属蒸着層の裏面には接着剤を介在させて裏面側合成樹脂製フィルムを接着積層し、
該裏面側合成樹脂製フィルムの裏面には接着剤を用いないで布を重合接着して積層し、
前記表面側合成樹脂製フィルムの表面に昇華転写により絵柄が施されてなることを特徴とするホログラムを施されたシート状物。A sheet-like object with a hologram on which the surface is represented by a sublimation transfer pattern,
A hologram layer with a metal vapor deposition layer deposited on the back side of the synthetic resin film is formed,
The back side of the metal vapor deposition layer is adhesively laminated with a back side synthetic resin film with an adhesive interposed therebetween,
The back side of the back side synthetic resin film is laminated by polymerizing and bonding a cloth without using an adhesive,
A sheet-like article provided with a hologram, wherein a pattern is applied to the surface of the surface-side synthetic resin film by sublimation transfer. 表面及び裏面の両面に昇華転写による図柄を表現されたホログラムを施されたシート状物であって、
合成樹脂製フィルムの内側面に金属蒸着層が被着されてなるホログラム層、接着剤、合成樹脂製フィルム、布、合成樹脂製フィルム、接着剤、合成樹脂製フィルムの内側面に金属蒸着層が被着形成されてなるホログラム層を順次積層して一体的に形成し、
前記ホログラム層の合成樹脂製フィルムの外側面に昇華転写により図柄が施されてなることを特徴とするホログラムを施されたシート状物。A sheet-like material on which a hologram expressing a pattern by sublimation transfer is applied to both the front and back surfaces,
Hologram layer, adhesive, synthetic resin film, cloth, synthetic resin film, adhesive, synthetic resin film on the inner surface of the synthetic resin film. A hologram layer formed by deposition is sequentially laminated and formed integrally.
A sheet-like article provided with a hologram, wherein the outer surface of the synthetic resin film of the hologram layer is provided with a pattern by sublimation transfer. 表面及び裏面の両面に昇華転写による図柄を表現されたホログラムを施されたシート状物であって、
合成樹脂製フィルムの内側面に金属蒸着層が被着されてなるホログラム層と別の合成樹脂製フィルムの内側面に金属蒸着層が被着されてなるホログラム層との間に接着剤を介在させて重合接着し、
前記合成樹脂製フィルムの外側面に昇華転写により図柄が施されてなることを特徴とするホログラムを施されたシート状物。A sheet-like material on which a hologram expressing a pattern by sublimation transfer is applied to both the front and back surfaces,
An adhesive is interposed between the hologram layer formed by depositing a metal vapor-deposited layer on the inner surface of a synthetic resin film and the hologram layer formed by depositing a metal vapor-deposited layer on the inner surface of another synthetic resin film. And polymerized
A sheet-like article provided with a hologram, wherein a pattern is applied to the outer surface of the synthetic resin film by sublimation transfer. 上記合成樹脂製フィルムが、ポリエステル系樹脂製フィルムであることを特徴とする請求項１、２、３又は４の何れかに記載のホログラムを施されたシート状物。  5. The sheet-like material provided with the hologram according to claim 1, wherein the synthetic resin film is a polyester resin film. 上記接着剤がホットメルト接着剤であることを特徴とする請求項１、２、３、４又は５の何れかに記載のホログラムを施されたシート状物。  6. The sheet-like material provided with the hologram according to claim 1, wherein the adhesive is a hot melt adhesive. 上記請求項１、２、３、４、５又は６の何れかに記載のホログラムを施されたシート状物を所望形状に切断し、且つ周縁を縁かがりをし、縫製或は貼着により鞄や衣服に取り付けたことを特徴とするホログラムを施されたシート状物を用いた装身物。  The sheet-like material on which the hologram according to any one of claims 1, 2, 3, 4, 5, or 6 is applied is cut into a desired shape, and the periphery is edged, and the rim is sewn or adhered. Ornament using a sheet-like material with a hologram characterized by being attached to clothes.
JP2012289373A 2012-12-17 2012-12-17 Sheet-like article on which hologram is formed, and accessory using sheet-like article on which hologram is formed Pending JP2014119744A (en)