JP2014114406A - Ultraviolet-curable inkjet composition and recorded material - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an ultraviolet-curable inkjet composition excellent in storage stability and dispersion stability of metal powder, which is suitably applicable to formation of a pattern (printed part) excellent in glossiness and abrasion resistance, and to provide a recorded material having a pattern excellent in glossiness and abrasion resistance formed by using the above ultraviolet-curable inkjet composition.SOLUTION: The ultraviolet-curable inkjet composition is ejected by an inkjet system, and comprises a polymerizable compound, metal powder, and an alcohol component having 2 to 4 carbon atoms. The metal powder comprises a powder subjected to a surface treatment with a fluorine-based silane compound and/or a fluorine-based phosphate as a surface treating agent. The content percentage of the alcohol component in the ultraviolet-curable inkjet composition is 0.05 mass% or more and 7.0 mass% or less.

Description

  The present invention relates to an ultraviolet curable ink jet composition and a recorded matter.

Conventionally, metal plating, foil press printing using a metal foil, thermal transfer using a metal foil, and the like have been used as a method for producing a decorative product exhibiting a glossy appearance.
However, these methods have a problem that it is difficult to form a fine pattern or to apply to a curved surface portion. In addition, the foil stamping printing has a problem that it is difficult to cope with multi-product production because it has low on-demand property, and gradation-like metallic printing cannot be performed.

On the other hand, as a recording method on a recording medium using a composition containing a pigment or a dye, a recording method using an inkjet method is used. The ink jet method is excellent in that it can be suitably applied to formation of a fine pattern and recording on a curved surface portion. In recent years, compositions that cure when irradiated with ultraviolet rays (ultraviolet curable inkjet compositions) have been used in the ink jet method in order to achieve particularly excellent abrasion resistance, water resistance, solvent resistance, and the like. (For example, refer to Patent Document 1).
However, in the ultraviolet curable ink jet composition, when a metal powder is applied instead of a pigment or a dye, it is not possible to sufficiently exhibit the properties such as glossiness inherent to the metal. In addition, the composition has poor stability (storage stability) and causes problems such as a decrease in ejection stability due to an increase in viscosity due to gelation.

JP 2009-57548 A

  An object of the present invention is to provide an ultraviolet curable inkjet composition that can be suitably used for forming a pattern (printing portion) having excellent storage stability, dispersion stability of metal powder, glossiness, and abrasion resistance. It is another object of the present invention to provide a recorded matter having a pattern excellent in glossiness and abrasion resistance formed using the ultraviolet ray curable ink jet composition.

Such an object is achieved by the present invention described below.
The ultraviolet curable inkjet composition of the present invention is an ultraviolet curable inkjet composition discharged by an inkjet method,
A polymerizable compound, a metal powder, and an alcohol component having 2 to 4 carbon atoms,
The metal powder includes a surface treated with a fluorinated silane compound and / or a fluorinated phosphate as a surface treating agent,
The content of the alcohol component in the ultraviolet curable inkjet composition is 0.05% by mass or more and 7.0% by mass or less.
As a result, the composition for ultraviolet curable ink jets can be suitably used for the production of recorded matter having a pattern (printing portion) having excellent storage stability, metal powder dispersion stability, glossiness, and abrasion resistance. Things can be provided.

In the ultraviolet curable ink-jet composition of the present invention, the metal powder is a powder whose surface is mainly composed of Al and is surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester. Is preferred.
Al originally exhibits a particularly excellent gloss feeling among various metal materials. However, when a powder composed of Al is applied to an ultraviolet curable inkjet composition, it is used for an ultraviolet curable inkjet. The inventor has found that the storage stability of the composition is particularly low, and problems such as a decrease in ejection stability due to an increase in viscosity due to gelation are particularly prominent. On the other hand, in this invention, even if it is a case where the surface uses the powder comprised by Al, generation | occurrence | production of the above problems can be prevented reliably. That is, the metal powder constituting the ultraviolet curable ink-jet composition is a powder whose surface is mainly composed of Al and is surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester. The effect of the present invention is particularly remarkable.
In the ultraviolet curable inkjet composition of the present invention, the metal powder preferably has a scaly shape.
Thereby, the glossiness, abrasion resistance, etc. of the recorded matter manufactured using the ultraviolet curable inkjet composition can be made particularly excellent.

In the ultraviolet curable inkjet composition of the present invention, it is preferable that the metal powder includes a surface treated with the fluorine-based silane compound having a chemical structure represented by the following formula (1).
R ¹ SiX ¹ _a R ² _(3-a) (1)
(In Formula (1), R ¹ represents a hydrocarbon group in which part or all of the hydrogen atoms are substituted with fluorine atoms, X ¹ represents a hydrolyzable group, an ether group, a chloro group, or a hydroxyl group; ² represents an alkyl group having 1 to 4 carbon atoms, and a is an integer of 1 to 3 inclusive.)
As a result, the storage stability of the ultraviolet curable ink jet composition is particularly excellent, and the glossiness and abrasion resistance of the printed part of the recorded matter produced using the ultraviolet curable ink jet composition are particularly excellent. Can be.

In the ultraviolet curable inkjet composition of the present invention, it is preferable that the metal powder includes a surface treated with the fluorinated phosphate ester having a chemical structure represented by the following formula (2).
POR _n (OH) _3-n (2)
(In the formula (2), R _{is, CF 3 (CF 2) m} -, CF 3 (CF 2) m (CH 2) l -, CF 3 (CF 2) m (CH 2 O) l -, CF 3 (CF ₂ ) _m (CH ₂ CH ₂ O) ₁ —, CF ₃ (CF ₂ ) _m O—, or CF ₃ (CF ₂ ) _m (CH ₂ ) ₁ O—, and n is 1 or more and 3 or less. M is an integer from 5 to 17, and l is an integer from 1 to 12.)
As a result, the storage stability of the ultraviolet curable ink jet composition is particularly excellent, and the glossiness and abrasion resistance of the printed part of the recorded matter produced using the ultraviolet curable ink jet composition are particularly excellent. Can be.

In the ultraviolet curable ink-jet composition of the present invention, CF ₃ (CF ₂ ) ₅ (CH ₂ ) ₂ O (P) (OH) ₂ and / or CF ₃ (CF ₂ ) ₅ (CH ₂ ) is used as the metal powder. It is preferable that the surface treatment is performed with the fluorine-based phosphate ester represented by ₂ O (P) (OH) (OCH ₂ CH ₃ ).
Thereby, surface treatment with few defects can be more suitably applied to the metal powder, and the chemical stability and dispersion stability of the metal powder in the UV curable ink jet composition are particularly excellent. The storage stability of the ink jet composition and the discharge stability over a long period of time can be made particularly excellent. In the recorded matter produced using the ultraviolet curable ink jet composition, the metal powder can be used for the printed part. It can be arranged more suitably in the vicinity of the outer surface, and the properties such as glossiness inherent in the metal material constituting the metal powder can be more effectively exhibited. Further, even when a polymerizable compound having a low surface tension is used as a constituent material of an ultraviolet curable ink jet composition, a metal powder is reliably produced in a recorded matter produced using the ultraviolet curable ink jet composition. Can be suitably arranged in the vicinity of the outer surface of the printing portion, and the properties such as glossiness inherent in the metal material constituting the metal powder can be sufficiently exhibited.

In the ultraviolet curable inkjet composition of the present invention, the average particle size of the metal powder is preferably 500 nm or more and 3.0 μm or less.
Thereby, the glossiness and high-quality feeling of the recorded matter manufactured using the ultraviolet curable inkjet composition can be further improved. Further, the storage stability and ejection stability of the ultraviolet curable ink jet composition can be further improved.

In the ultraviolet curable inkjet composition of the present invention, it is preferable that the polymerizable compound contains a monomer having an alicyclic structure.
As a result, the storage stability of the ultraviolet curable ink jet composition can be made particularly excellent, and the glossiness and abrasion resistance of the printed portion of the recorded matter produced using the ultraviolet curable ink jet composition can be improved. The property can be made particularly excellent.

In the ultraviolet curable inkjet composition of the present invention, the content of the monomer having the alicyclic structure in the ultraviolet curable inkjet composition is preferably 40% by mass or more and 90% by mass or less.
Thereby, the dispersion stability of the metal powder is particularly excellent, and particularly excellent discharge stability is obtained over a long period of time. In particular, even if the ultraviolet curable ink jet composition does not contain a dispersant, the above excellent effects can be obtained.

In the ultraviolet curable inkjet composition of the present invention, it is preferable that a monofunctional monomer containing a hetero atom in the alicyclic structure is included as the monomer having the alicyclic structure.
Thereby, the dispersion stability of the metal powder is particularly excellent, and particularly excellent discharge stability is obtained over a long period of time. In particular, even if the ultraviolet curable ink jet composition does not contain a dispersant, the above excellent effects can be obtained.

In the ultraviolet curable inkjet composition of the present invention, the content of the monofunctional monomer in the ultraviolet curable inkjet composition is preferably 10% by mass or more and 90% by mass or less.
Thereby, it can use suitably for manufacture of the recorded matter provided with the pattern (printing part) which suppressed cure shrinkage, has few scattering, and was more excellent in glossiness.

In the ultraviolet curable ink jet composition of the present invention, the monomer having the alicyclic structure is tris (2-acryloyloxyethyl) isocyanurate, dicyclopentenyloxyethyl acrylate, adamantyl acrylate, γ-butyrolactone acrylate, N-vinyl. Caprolactam, N-vinylpyrrolidone, pentamethylpiperidyl acrylate, tetramethylpiperidyl acrylate, 2-methyl-2-adamantyl acrylate, 2-ethyl-2-adamantyl acrylate, mevalonic acid lactone acrylate, dimethylol tricyclodecane diacrylate, dimethylol Dicyclopentane diacrylate, dicyclopentenyl acrylate, dicyclopentanyl acrylate, isobornyl acrylate, cyclohexyl Acrylate, acryloyl morpholine, and is preferably one containing one or two or more selected from the group consisting of tetrahydrofurfuryl acrylate.
Thereby, the glossiness and high-quality feeling of the recorded matter manufactured using the ultraviolet curable inkjet composition can be further improved. Further, the storage stability and ejection stability of the ultraviolet curable ink jet composition can be further improved.

In the ultraviolet curable ink jet composition of the present invention, as a polymerizable compound other than the monomer having the alicyclic structure, phenoxyethyl acrylate, 2- (2-vinyloxyethoxy) ethyl acrylate, dipropylene glycol diacrylate, triethylene It is preferable to include one or more selected from the group consisting of propylene glycol diacrylate, 2-hydroxy-3-phenoxypropyl acrylate, and 4-hydroxybutyl acrylate.
As a result, the storage stability and ejection stability of the ultraviolet curable inkjet composition are excellent, and the reactivity of the ultraviolet curable inkjet composition after ejection by the inkjet method is particularly excellent. The productivity of the pattern can be made particularly excellent, and the rub resistance of the formed pattern can be made particularly excellent.

これにより、紫外線硬化型インクジェット用組成物の保存安定性、硬化性を特に優れたものとすることができる。また、紫外線硬化型インクジェット用組成物を用いて製造される記録物においては、金属粉末を構成する金属材料が本来有している光沢感・高級感をより効果的に発揮させ、印刷部の光沢感、耐擦性を特に優れたものとし、記録物の耐久性を特に優れたものとすることができる。
本発明の記録物は、本発明の紫外線硬化型インクジェット用組成物を記録媒体上に付与し、その後、紫外線を照射することにより製造されたことを特徴とする。
これにより、光沢感、耐擦性に優れたパターン（印刷部）を有する記録物を提供することができる。 In the ultraviolet curable inkjet composition of the present invention, the ultraviolet curable inkjet composition preferably further includes a substance A having a partial structure represented by the following formula (5).

Thereby, the storage stability and curability of the ultraviolet curable ink jet composition can be made particularly excellent. In addition, in the recorded matter produced using the ultraviolet curable ink jet composition, the glossiness and luxury feeling inherent in the metal material constituting the metal powder is more effectively exhibited, and the gloss of the printed part The feeling and abrasion resistance can be made particularly excellent, and the durability of the recorded matter can be made particularly excellent.
The recorded matter of the present invention is produced by applying the ultraviolet curable inkjet composition of the present invention onto a recording medium and then irradiating with ultraviolet rays.
Thereby, it is possible to provide a recorded matter having a pattern (printing portion) excellent in glossiness and abrasion resistance.

Hereinafter, preferred embodiments of the present invention will be described in detail.
<< UV-curable inkjet composition >>
First, the ultraviolet curable inkjet composition of the present invention will be described.
The ultraviolet curable inkjet composition of the present invention is ejected by an inkjet method and contains a polymerizable compound that is polymerized by irradiation with ultraviolet rays.

By the way, conventionally, metal plating, foil press printing using a metal foil, thermal transfer using a metal foil, and the like have been used as a method for producing a decorative product exhibiting a glossy appearance.
However, these methods have a problem that it is difficult to form a fine pattern or to apply to a curved surface portion. In addition, foil stamp printing has a problem that gradation-like metallic printing cannot be performed.

  On the other hand, as a recording method on a recording medium using a composition containing a pigment or a dye, a recording method using an inkjet method is used. The ink jet method is excellent in that it can be suitably applied to formation of a fine pattern and recording on a curved surface portion. In recent years, compositions that cure when irradiated with ultraviolet rays (ultraviolet curable inkjet compositions) have been used in the ink jet method in order to achieve particularly excellent abrasion resistance, water resistance, solvent resistance, and the like. ing.

However, in the ultraviolet curable ink jet composition, when a metal powder is applied instead of a pigment or a dye, it is not possible to sufficiently exhibit the properties such as glossiness inherent to the metal. In addition, the composition has poor stability (storage stability) and causes problems such as a decrease in ejection stability due to an increase in viscosity due to gelation.
Therefore, the inventor has intensively studied for the purpose of solving the above problems, and as a result, has reached the present invention. That is, the ultraviolet curable ink jet composition of the present invention includes an alcohol component having 2 to 4 carbon atoms in addition to the polymerizable compound and the metal powder, and the metal powder includes a fluorine-based silane compound as a surface treatment agent and The content of the alcohol component (the alcohol component having 2 to 4 carbon atoms) in the ultraviolet curable inkjet composition is 0.05% by mass, including / and containing a surface treated with a fluorine-based phosphate ester. The above is 7.0% by mass or less. As a result, even when the content of the dispersant in the ultraviolet curable inkjet composition is low or when no dispersant is contained, the dispersion stability and chemical properties of the metal powder in the ultraviolet curable inkjet composition are improved. It is excellent in stability, can be preserved in the ultraviolet curable inkjet composition, and can have excellent discharge stability over a long period of time, and is manufactured using the ultraviolet curable inkjet composition. In the recorded matter, the metal powder can be suitably arranged in the vicinity of the outer surface of the printing portion, and the characteristics such as glossiness inherent to the metal material constituting the metal powder can be sufficiently exhibited.

<Metal powder>
As described above, the ultraviolet curable inkjet composition of the present invention includes a metal powder that has been surface-treated with a fluorinated silane compound and / or a fluorinated phosphate as a surface treatment agent.
(Mother particles)
First, mother particles (particles subjected to surface treatment with a surface treatment agent) constituting metal particles will be described.
The mother particles constituting the metal powder need only have at least a region including the vicinity of the surface made of a metal material. For example, the whole may be made of a metal material or a non-metal material. And a base made of a metal material that covers the base.

  Further, as the metal material constituting the mother particle, a single metal, various alloys, or the like can be used. However, the mother particle is preferably composed mainly of Al at least near the surface. Al originally exhibits a particularly excellent gloss feeling among various metal materials. However, when a powder composed of Al is applied to an ultraviolet curable inkjet composition, it is used for an ultraviolet curable inkjet. The inventor has found that the storage stability of the composition is particularly low, and problems such as a decrease in ejection stability due to an increase in viscosity due to gelation are particularly prominent. On the other hand, in this invention, even if it is a case where the surface uses the powder comprised by Al, generation | occurrence | production of the above problems can be prevented reliably. That is, the metal powder constituting the ultraviolet curable ink jet composition is a powder whose surface is mainly composed of Al and is surface-treated with a surface treatment agent (fluorine-based silane compound and / or fluorine-based phosphate ester). Therefore, the effect of the present invention is particularly remarkable.

  Further, the mother particles may be produced by any method, but when they are made of Al, a film made of Al is formed by a vapor deposition method, and then It is preferably obtained by pulverizing the membrane. Thereby, the glossiness etc. which Al originally has in the pattern (printing part) formed using the ultraviolet curable inkjet composition of this invention can be expressed more effectively. Moreover, the dispersion | variation in the characteristic between each particle | grain can be suppressed. Moreover, even if it is a comparatively thin metal powder, it can manufacture suitably by using the said method.

When producing mother particles using such a method, for example, the mother particles can be suitably produced by forming a film made of Al (film formation) on a substrate. As the substrate, for example, a plastic film such as polyethylene terephthalate can be used. Further, the substrate may have a release agent layer on the film forming surface.
Moreover, it is preferable that the said grinding | pulverization is performed by providing an ultrasonic vibration to the said film | membrane in a liquid. As a result, it is possible to easily and surely obtain mother particles having a preferable size, and it is possible to suppress the occurrence of variations in size, shape, and characteristics among the particles.

  When the pulverization is performed by the above method, the liquid includes alcohols such as methanol, ethanol, propanol, and butanol, n-heptane, n-octane, decane, dodecane, tetradecane, toluene, xylene, and cymene. Hydrocarbon compounds such as durene, indene, dipentene, tetrahydronaphthalene, decahydronaphthalene, cyclohexylbenzene, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol methyl ethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol methyl ethyl ether , Diethylene glycol monobutyl ether acetate, diethylene glycol n-butyl ether, triplicate Ether compounds such as pyrene glycol dimethyl ether, triethylene glycol diethyl ether, 1,2-dimethoxyethane, bis (2-methoxyethyl) ether, p-dioxane, propylene carbonate, γ-butyrolactone, N-methyl-2-pyrrolidone , N, N-dimethylformamide (DMF), N, N-dimethylacetamide (DMA), dimethyl sulfoxide, cyclohexanone, acetonitrile and the like can be preferably used. By using such a liquid, the productivity of the mother particles and metal powder is made particularly excellent while preventing unintentional oxidation of the mother particles, and the size, shape, and characteristics between each particle Can be made particularly small.

(Surface treatment agent)
As described above, the metal powder according to the present invention is surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester as a surface treatment agent.
First, among the surface treatment agents, the fluorine-based silane compound will be described in detail.
As the fluorine-based silane compound, a silane compound having at least one fluorine atom in the molecule can be used.

In particular, the fluorinated silane compound as the surface treatment agent preferably has a chemical structure represented by the following formula (1).
R ¹ SiX ¹ _a R ² _(3-a) (1)
(In Formula (1), R ¹ represents a hydrocarbon group in which part or all of the hydrogen atoms are substituted with fluorine atoms, X ¹ represents a hydrolyzable group, an ether group, a chloro group, or a hydroxyl group; ² represents an alkyl group having 1 to 4 carbon atoms, and a is an integer of 1 to 3 inclusive.)

As a result, the storage stability of the ultraviolet curable ink jet composition is particularly excellent, and the glossiness and abrasion resistance of the printed part of the recorded matter produced using the ultraviolet curable ink jet composition are particularly excellent. Can be.
Examples of R ¹ in the formula (1) include an alkyl group, an alkenyl group, an aryl group, an aralkyl group, etc. in which a part or all of hydrogen atoms are substituted with fluorine atoms, and are further included in the molecular structure. At least a part of hydrogen atoms (hydrogen atoms not substituted with fluorine atoms) may be substituted with an amino group, a carboxyl group, a hydroxyl group, a thiol group, etc., and -O-, -S in the carbon chain A hetero atom such as-, -NH-, -N =, or an aromatic ring such as benzene may be sandwiched. Specific examples of R ¹ include, for example, a phenyl group, a benzyl group, a phenethyl group, a hydroxyphenyl group, a chlorophenyl group, an aminophenyl group, a naphthyl group, an anthrenyl group in which part or all of the hydrogen atoms are substituted with fluorine atoms, Pyrenyl group, thienyl group, pyrrolyl group, cyclohexyl group, cyclohexenyl group, cyclopentyl group, cyclopentenyl group, pyridinyl group, methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, sec- Butyl group, tert-butyl group, octadecyl group, n-octyl group, chloromethyl group, methoxyethyl group, hydroxyethyl group, aminoethyl group, cyano group, mercaptopropyl group, vinyl group, allyl group, acryloxyethyl group, Methacryloxyethyl group, glycidoxypropyl Group, acetoxy group and the like.

Specific examples of the fluorine-based silane compound represented by the formula (1) include dimethyldimethoxysilane, diethyldiethoxysilane, 1-propenylmethyldichlorosilane, propyldimethylchlorosilane, propylmethyldichlorosilane, propyltrichlorosilane, and propyltriethoxy. Silane, propyltrimethoxysilane, styrylethyltrimethoxysilane, tetradecyltrichlorosilane, 3-thiocyanatepropyltriethoxysilane, p-tolyldimethylchlorosilane, p-tolylmethyldichlorosilane, p-tolyltrichlorosilane, p-tolyltrimethoxy Silane, p-tolyltriethoxysilane, di-n-propyldi-n-propoxysilane, diisopropyldiisopropoxysilane, di-n-butyldi-n-butyroxysilane Di-sec-butyldi-sec-butyroxysilane, di-t-butyldi-t-butyroxysilane, octadecyltrichlorosilane, octadecylmethyldiethoxysilane, octadecyltriethoxysilane, octadecyltrimethoxysilane, octadecyldimethylchlorosilane, octadecylmethyldichlorosilane, octadecyl Methoxydichlorosilane, 7-octenyldimethylchlorosilane, 7-octenyltrichlorosilane, 7-octenyltrimethoxysilane, octylmethyldichlorosilane, octyldimethylchlorosilane, octyltrichlorosilane, 10-undecenyldimethylchlorosilane, undecyltri Chlorosilane, vinyldimethylchlorosilane, methyldodecyldimethoxysilane, methyldodecyldiethoxysilane , Methyloctadecyldimethoxysilane, methyloctadecyldiethoxysilane, n-octylmethyldimethoxysilane, n-octylmethyldiethoxysilane, triacontyldimethylchlorosilane, triaconyltrichlorosilane, methyltrimethoxysilane, methyltriethoxysilane, methyltri N-propoxysilane, methyltriisopropoxysilane, methyltri-n-butyroxysilane, methyltri-sec-butoxyxysilane, methyltri-t-butoxyxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, ethyltri-n-propoxysilane, ethylisopropoxy Silane, Ethyltri-n-Butyloxysilane, Ethyltri-sec-Butyloxysilane, Ethyltri-t-Butyloxysilane, n-P Propyltrimethoxysilane, isobutyltrimethoxysilane, n-hexyltrimethoxysilane, hexadecyltrimethoxysilane, n-octyltrimethoxysilane, n-dodecyltrimethoxysilane, n-octadecyltrimethoxysilane, n-propyltriethoxy Silane, isobutyltriethoxysilane, n-hexyltriethoxysilane, hexadecyltriethoxysilane, n-octyltriethoxysilane, n-dodecyltriethoxysilane, n-octadecyltriethoxysilane, 2- [2- (trichlorosilyl) Ethyl] pyridine, 4- [2- (trichlorosilyl) ethyl] pyridine, diphenyldimethoxysilane, diphenyldiethoxysilane, 1,3- (trichlorosilylmethyl) heptacosane, dibenzyldimethoxy Run, dibenzyldiethoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, phenylmethyldimethoxysilane, phenyldimethylmethoxysilane, phenyldimethoxysilane, phenyldiethoxysilane, phenylmethyldiethoxysilane, phenyldimethylethoxysilane, benzyltri Ethoxysilane, benzyltrimethoxysilane, benzylmethyldimethoxysilane, benzyldimethylmethoxysilane, benzyldimethoxysilane, benzyldiethoxysilane, benzylmethyldiethoxysilane, benzyldimethylethoxysilane, benzyltriethoxysilane, dibenzyldimethoxysilane, dibenzyl Diethoxysilane, 3-acetoxypropyltrimethoxysilane, 3-acryloxypropyltrimeth Sisilane, allyltrimethoxysilane, allyltriethoxysilane, 4-aminobutyltriethoxysilane, (aminoethylaminomethyl) phenethyltrimethoxysilane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, N- (2-aminoethyl) -3-aminopropyltrimethoxysilane, 6- (aminohexylaminopropyl) trimethoxysilane, p-aminophenyltrimethoxysilane, p-aminophenylethoxysilane, m-aminophenyltrimethoxysilane, m-aminophenylethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, ω-aminoundecyltrimethoxysilane, amyltriethoxysilane, benzoxacilepin dimethyl ester 5- (bicycloheptenyl) triethoxysilane, bis (2-hydroxyethyl) -3-aminopropyltriethoxysilane, 8-bromooctyltrimethoxysilane, bromophenyltrimethoxysilane, 3-bromopropyltrimethoxysilane, n-butyltrimethoxysilane, 2-chloromethyltriethoxysilane, chloromethylmethyldiethoxysilane, chloromethylmethyldiisopropoxysilane, p- (chloromethyl) phenyltrimethoxysilane, chloromethyltriethoxysilane, chlorophenyltriethoxy Silane, 3-chloropropylmethyldimethoxysilane, 3-chloropropyltriethoxysilane, 3-chloropropyltrimethoxysilane, 2- (4-chlorosulfonylphenyl) ethyltrimethoxysilane, -Cyanoethyltriethoxysilane, 2-cyanoethyltrimethoxysilane, cyanomethylphenethyltriethoxysilane, 3-cyanopropyltriethoxysilane, 2- (3-cyclohexenyl) ethyltrimethoxysilane, 2- (3-cyclohexenyl) ethyl Triethoxysilane, 3-cyclohexenyltrichlorosilane, 2- (3-cyclohexenyl) ethyltrichlorosilane, 2- (3-cyclohexenyl) ethyldimethylchlorosilane, 2- (3-cyclohexenyl) ethylmethyldichlorosilane , Cyclohexyldimethylchlorosilane, cyclohexylethyldimethoxysilane, cyclohexylmethyldichlorosilane, cyclohexylmethyldimethoxysilane, (cyclohexylmethyl) trichlorosilane, cyclohexyl Rutrichlorosilane, cyclohexyltrimethoxysilane, cyclooctyltrichlorosilane, (4-cyclooctenyl) trichlorosilane, cyclopentyltrichlorosilane, cyclopentyltrimethoxysilane, 1,1-diethoxy-1-silacyclopent-3-ene, 3- (2 , 4-dinitrophenylamino) propyltriethoxysilane, (dimethylchlorosilyl) methyl-7,7-dimethylnorpinane, (cyclohexylaminomethyl) methyldiethoxysilane, (3-cyclopentadienylpropyl) triethoxysilane, N, N-diethyl-3-aminopropyl) trimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltriethoxysilane, Furfuryloxymethyl) triethoxysilane, 2-hydroxy-4- (3-triethoxypropoxy) diphenyl ketone, 3- (p-methoxyphenyl) propylmethyldichlorosilane, 3- (p-methoxyphenyl) propyltrichlorosilane, p- (methylphenethyl) methyldichlorosilane, p- (methylphenethyl) trichlorosilane, p- (methylphenethyl) dimethylchlorosilane, 3-morpholinopropyltrimethoxysilane, (3-glycidoxypropyl) methyldiethoxysilane, 3-glycidoxypropyltrimethoxysilane, 1,2,3,4,7,7, -hexachloro-6-methyldiethoxysilyl-2-norbornene, 1,2,3,4,7,7, -hexachloro -6-triethoxysilyl-2-norbornene, 3-iodopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, (mercaptomethyl) methyldiethoxysilane, 3-mercaptopropylmethyldimethoxysilane, 3-mercaptopropyldimethoxysilane, 3-mercaptopropyltriethoxysilane, 3- Methacryloxypropylmethyldiethoxysilane, 3-methacryloxypropyltrimethoxysilane, methyl {2- (3-trimethoxysilylpropylamino) ethylamino} -3-propionate, 7-octenyltrimethoxysilane, RN- α-phenethyl-N′-triethoxysilylpropylurea, S—N-α-phenethyl-N′-triethoxysilylpropylurea, phenethyltrimethoxysilane, phenethylmethyldimethoxysilane, phenet Didimethylmethoxysilane, phenethyldimethoxysilane, phenethyldiethoxysilane, phenethylmethyldiethoxysilane, phenethyldimethylethoxysilane, phenethyltriethoxysilane, (3-phenylpropyl) dimethylchlorosilane, (3-phenylpropyl) methyldichlorosilane, N -Phenylaminopropyltrimethoxysilane, N- (triethoxysilylpropyl) dansilamide, N- (3-triethoxysilylpropyl) -4,5-dihydroimidazole, 2- (triethoxysilylethyl) -5- (chloro Acetoxy) bicycloheptane, (S) -N-triethoxysilylpropyl-O-menthcarbamate, 3- (triethoxysilylpropyl) -p-nitrobenzamide, 3- (triethoxysilyl) Lopyruccinic anhydride, N- [5- (trimethoxysilyl) -2-aza-1-oxo-pentyl] caprolactam, 2- (trimethoxysilylethyl) pyridine, N- (trimethoxysilylethyl) benzyl- N, N, N-trimethylammonium chloride, phenylvinyldiethoxysilane, 3-thiocyanatopropyltriethoxysilane, N- {3- (triethoxysilyl) propyl} phthalamic acid, 1-trimethoxysilyl-2- ( Chloromethyl) phenylethane, 2- (trimethoxysilyl) ethylphenylsulfonyl azide, β-trimethoxysilylethyl-2-pyridine, trimethoxysilylpropyldiethylenetriamine, N- (3-trimethoxysilylpropyl) pyrrole, N-tri Methoxysilylpropyl-N N, N-tributylammonium bromide, N-trimethoxysilylpropyl-N, N, N-tributylammonium chloride, N-trimethoxysilylpropyl-N, N, N-trimethylammonium chloride, vinylmethyldiethoxylane, vinyltri Ethoxysilane, vinyltrimethoxysilane, vinylmethyldimethoxysilane, vinyldimethylmethoxysilane, vinyldimethylethoxysilane, vinylmethyldichlorosilane, vinylphenyldichlorosilane, vinylphenyldiethoxysilane, vinylphenyldimethylsilane, vinylphenylmethylchlorosilane, vinyl Triphenoxysilane, vinyltris-t-butoxysilane, adamantylethyltrichlorosilane, allylphenyltrichlorosilane, (aminoethyl Aminomethyl) phenethyltrimethoxysilane, 3-aminophenoxydimethylvinylsilane, phenyltrichlorosilane, phenyldimethylchlorosilane, phenylmethyldichlorosilane, benzyltrichlorosilane, benzyldimethylchlorosilane, benzylmethyldichlorosilane, phenethyldiisopropylchlorosilane, phenethyltrichlorosilane, phenethyl Dimethylchlorosilane, phenethylmethyldichlorosilane, 5- (bicycloheptenyl) trichlorosilane, 5- (bicycloheptenyl) triethoxysilane, 2- (bicycloheptyl) dimethylchlorosilane, 2- (bicycloheptyl) trichlorosilane, 1,4 -Bis (trimethoxysilylethyl) benzene, bromophenyltrichlorosilane, 3-phenoxypro Didimethylchlorosilane, 3-phenoxypropyltrichlorosilane, t-butylphenylchlorosilane, t-butylphenylmethoxysilane, t-butylphenyldichlorosilane, p- (t-butyl) phenethyldimethylchlorosilane, p- (t-butyl) phenethyl Trichlorosilane, 1,3- (chlorodimethylsilylmethyl) heptacosane, ((chloromethyl) phenylethyl) dimethylchlorosilane, ((chloromethyl) phenylethyl) methyldichlorosilane, ((chloromethyl) phenylethyl) trichlorosilane, ( (Chloromethyl) phenylethyl) trimethoxysilane, chlorophenyltrichlorosilane, 2-cyanoethyltrichlorosilane, 2-cyanoethylmethyldichlorosilane, 3-cyanopropylmethyldiethoxy One of hydrogen atoms contained in a silane compound such as silane, 3-cyanopropylmethyldichlorosilane, 3-cyanopropylmethyldichlorosilane, 3-cyanopropyldimethylethoxysilane, 3-cyanopropylmethyldichlorosilane, 3-cyanopropyltrichlorosilane, etc. Examples thereof include compounds having a structure in which part or all are substituted with fluorine atoms.

The fluorine-based silane compound (surface treatment agent) preferably has a perfluoroalkyl structure (C _n F _{2n + 1} ). As a result, the storage stability of the UV curable ink jet composition is further improved, and the glossiness and abrasion resistance of the printed portion of the recorded matter produced using the UV curable ink jet composition are further improved. Can be.

The fluorine-based silane compound having a perfluoroalkyl structure _{(C n F 2n + 1)} , for example, those represented by the following formula (3).
_{C n F 2n + 1 (CH} 2) m SiX 1 a R 2 (3-a) (3)
(In Formula (3), X ¹ represents a hydrolyzable group, an ether group, a chloro group or a hydroxyl group, R ² represents an alkyl group having 1 to 4 carbon atoms, and n is an integer of 1 to 14) M is an integer of 2 to 6, and a is an integer of 1 to 3.

Specific examples of the compound having such a structure include CF ₃ —CH ₂ CH ₂ —Si (OCH ₃ ) ₃ , CF ₃ (CF ₂ ) ₃ —CH ₂ CH ₂ —Si (OCH ₃ ) ₃ , CF _3. (CF ₂ ) ₅ —CH ₂ CH ₂ —Si (OCH ₃ ) ₃ , CF ₃ (CF ₂ ) ₅ —CH ₂ CH ₂ —Si (OC ₂ H ₅ ) ₃ , CF ₃ (CF ₂ ) ₇ —CH _{2 CH 2 -Si (OCH 3) 3} , CF 3 (CF 2) 11 -CH 2 CH 2 -Si (OC 2 H 5) 3, CF 3 (CF 2) 3 -CH 2 CH 2 -Si (CH 3) _{(OCH 3) 2, CF 3} (CF 2) 7 -CH 2 CH 2 -Si (CH 3) (OCH 3) 2, CF 3 (CF 2) 8 -CH 2 CH 2 -Si (CH 3) (OC _{2 H 5) 2, CF 3} (CF 2) _{8 -CH 2 CH 2 -Si (C} 2 H 5) (OC 2 H 5) 2 and the like.
Further, as the fluorine-based silane compound may be used those having a perfluoroalkyl ether structure _{(C n F 2n + 1 O} ) in place of the above-mentioned perfluoroalkyl structure _{(C n F 2n + 1)} .

The fluorine-based silane compound having a perfluoroalkyl ether structure _{(C n F 2n + 1 O} ), for example, those represented by the following formula (4).
_{C p F 2p + 1 O (} C p F 2p O) r (CH 2) m SiX 1 a R 2 (3-a) (4)
(In Formula (4), X ¹ represents a hydrolyzable group, an ether group, a chloro group, or a hydroxyl group, R ² represents an alkyl group having 1 to 4 carbon atoms, and p is an integer of 1 to 4 inclusive. Yes, r is an integer from 1 to 10, m is an integer from 2 to 6, and a is an integer from 1 to 3.

Specific examples of the compound having such a structure include CF ₃ O (CF ₂ O) ₆ —CH ₂ CH ₂ —Si (OC ₂ H ₅ ) ₃ , CF ₃ O (C ₃ F ₆ O) ₄ —CH. ₂ CH ₂ —Si (OCH ₃ ) ₃ , CF ₃ O (C ₃ F ₆ O) ₂ (CF ₂ O) ₃ —CH ₂ CH ₂ —Si (OCH ₃ ) ₃ , CF ₃ O (C ₃ F ₆ O _{) 8 -CH 2 CH 2 -Si (} OCH 3) 3, CF 3 O (C 4 F 9 O) 5 -CH 2 CH 2 -Si (OCH 3) 3, CF 3 O (C 4 F 9 O) 5 _{-CH 2 CH 2 -Si (CH 3} ) (OC 2 H 5) 2, CF 3 O (C 3 F 6 O) 4 -CH 2 CH 2 -Si (C 2 H 5) (OCH 3) 2 and the like Can be mentioned.

Next, among the surface treatment agents, the fluorine-based phosphate ester will be described in detail.
As the fluorine-based phosphate ester, a phosphate ester having at least one fluorine atom in the molecule can be used.
In particular, the ultraviolet curable inkjet composition of the present invention preferably contains a metal powder surface-treated with a fluorine-based phosphate ester having a chemical structure represented by the following formula (2).
POR _n (OH) _3-n (2)
(In the formula (2), R _{is, CF 3 (CF 2) m} -, CF 3 (CF 2) m (CH 2) l -, CF 3 (CF 2) m (CH 2 O) l -, CF 3 (CF ₂ ) _m (CH ₂ CH ₂ O) ₁ —, CF ₃ (CF ₂ ) _m O—, or CF ₃ (CF ₂ ) _m (CH ₂ ) ₁ O—, and n is 1 or more and 3 or less. M is an integer from 5 to 17, and l is an integer from 1 to 12.)

As a result, the storage stability of the ultraviolet curable ink jet composition is particularly excellent, and the glossiness and abrasion resistance of the printed part of the recorded matter produced using the ultraviolet curable ink jet composition are particularly excellent. Can be.
In formula (2), m is preferably an integer of 5 to 17, more preferably an integer of 7 to 12. Thereby, the effects as described above are more remarkably exhibited.
In formula (2), l is preferably an integer of 1 to 12, but more preferably an integer of 1 to 10. Thereby, the effects as described above are more remarkably exhibited.

Further, the ultraviolet ray curable ink composition of the present invention, as a metal _{powder, CF 3 (CF 2) 5} (CH 2) 2 O (P) (OH) 2 and / or _{CF 3 (CF 2) 5 (} CH ₂ ) ₂ O (P) (OH) (OCH ₂ CH ₃ ), which is preferably surface-treated with the above-mentioned fluorine-based phosphate ester.
Thereby, surface treatment with few defects can be more suitably applied to the metal powder, and the chemical stability and dispersion stability of the metal powder in the UV curable ink jet composition are particularly excellent. The storage stability of the ink jet composition and the discharge stability over a long period of time can be made particularly excellent. In the recorded matter produced using the ultraviolet curable ink jet composition, the metal powder can be used for the printed part. It can be arranged more suitably in the vicinity of the outer surface, and the properties such as glossiness inherent in the metal material constituting the metal powder can be more effectively exhibited. Further, even when a polymerizable compound having a low surface tension is used as a constituent material of an ultraviolet curable ink jet composition, a metal powder is reliably produced in a recorded matter produced using the ultraviolet curable ink jet composition. Can be suitably arranged in the vicinity of the outer surface of the printing portion, and the properties such as glossiness inherent in the metal material constituting the metal powder can be sufficiently exhibited.

Further, fluorine-based phosphate ester (surface treatment agent) is preferably one having a perfluoroalkyl structure _{(C n F 2n + 1)} . As a result, the storage stability of the UV curable ink jet composition is further improved, and the glossiness and abrasion resistance of the printed portion of the recorded matter produced using the UV curable ink jet composition are further improved. Can be.

  The surface treatment agent (fluorine-based silane compound, fluorine-based phosphate ester) as described above may be processed directly on the mother particles, but after the acid or base is treated on the mother particles, The mother particles are preferably treated with a surface treatment agent (fluorine silane compound, fluorine phosphate). As a result, the surface of the mother particles can be more reliably modified by chemical bonding with a surface treatment agent (fluorine-based silane compound and / or fluorine-based phosphate ester), and the effects of the present invention as described above can be achieved. It can be exhibited more effectively. Examples of the acid include hydrochloric acid, sulfuric acid, phosphoric acid, nitric acid, acetic acid, carbonic acid, formic acid, benzoic acid, chlorous acid, hypochlorous acid, sulfurous acid, hyposulfite, nitrous acid, hyponitrous acid, phosphorous acid, and the following. Protic acids such as phosphorous acid can be used. Of these, hydrochloric acid, phosphoric acid, and acetic acid are preferable. On the other hand, as the base, for example, sodium hydroxide, potassium hydroxide, calcium hydroxide or the like can be used. Of these, sodium hydroxide and potassium hydroxide are preferred.

  The metal powder may have any shape such as a spherical shape, a spindle shape, or a needle shape, but preferably has a scaly shape. Thereby, on the recording medium to which the ultraviolet curable ink jet composition is applied, the metal powder can be arranged so that the main surface of the metal powder follows the surface shape of the recording medium, thereby constituting the metal powder. The glossiness inherent in the metal material can be more effectively exhibited in the obtained recorded matter, and the glossiness and luxury feeling of the pattern (printed portion) to be formed are particularly excellent. In addition, the rub resistance of the recorded matter can be made particularly excellent. Moreover, in the structure which has not performed the surface treatment by the fluorine-type silane compound and / or fluorine-type phosphate ester as mentioned above, the preservation | save of the composition for ultraviolet curable inkjets that a metal powder makes a scaly shape. Although the tendency that the stability and the discharge stability are low has been particularly remarkable, in the present invention, even if the metal powder has a scaly shape, the occurrence of such a problem is surely prevented. be able to. That is, when the shape of the metal powder is scaly, the effect of the present invention is more remarkably exhibited.

In the present invention, the scale shape is an area when the area when observed from a predetermined angle (when viewed in plan) is observed from an angle orthogonal to the observation direction, such as a flat plate shape or a curved plate shape. In particular, the area S ₁ [μm ² ] when observed from the direction in which the projected area is maximum (when viewed in plan) and the direction orthogonal to the observation direction are observed. The ratio (S ₁ / S ₀ ) with respect to the area S ₀ [μm ² ] when observed from the direction in which the area of the area becomes maximum is preferably 2 or more, more preferably 5 or more, and still more preferably 8 or more. It is. As this value, for example, it is possible to observe an arbitrary 10 particles and adopt an average value of values calculated for these particles.

  The average particle size of the metal powder is preferably 500 nm or more and 3.0 μm or less, and more preferably 800 nm or more and 1.8 μm or less. Thereby, the glossiness and high-quality feeling of the recorded matter manufactured using the ultraviolet curable inkjet composition can be further improved. Further, the storage stability and ejection stability of the ultraviolet curable ink jet composition can be further improved.

  The content of the metal powder in the ultraviolet curable inkjet composition is preferably 0.5% by mass or more and 10.0% by mass or less, and more preferably 1.0% by mass or more and 5.0% by mass or less. More preferred. In addition, the composition for ultraviolet curable inkjet may contain 2 or more types of powder as a metal powder. In this case, it is preferable that the sum of these contents is a value within the above range.

<Alcohol component>
The ultraviolet curable inkjet composition of the present invention contains a predetermined amount of an alcohol component having 2 to 4 carbon atoms in addition to the metal powder as described above and a polymerizable compound described later.
That is, the ultraviolet curable inkjet composition of the present invention comprises 0.05% by mass of the metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate as a surface treatment agent and a polymerizable compound. The content ratio is 7.0% by mass or less, and an alcohol component having 2 to 4 carbon atoms is included.
Accordingly, the storage stability of the ultraviolet curable ink jet composition is excellent, and the glossiness of the printed part of the recorded matter produced using the ultraviolet curable ink jet composition is excellent. it can.

  The reason why such an excellent effect can be obtained is considered to be as follows. That is, by including a metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester, in the ultraviolet curable inkjet composition applied to the recording medium, the metal powder is formed near the outer surface. In order to arrange them appropriately, even in the finally obtained recorded matter, the metal powder is suitably arranged in the vicinity of the outer surface of the printed portion, and the gloss of the recorded matter (printed portion) is excellent. it can. Further, by containing a predetermined amount of an alcohol component having 2 to 4 carbon atoms, the dispersion of the metal powder surface-treated with the fluorine-based silane compound and / or the fluorine-based phosphate ester in the ultraviolet curable inkjet composition The stability can be improved, and aggregation, sedimentation, and the like of the metal powder in the ultraviolet curable inkjet composition can be suitably prevented over a long period of time. Then, these effects synergistically work together to improve the storage stability of the ultraviolet curable inkjet composition, and print a recorded matter produced using the ultraviolet curable inkjet composition. It is thought that the glossiness of the part can be made excellent. In addition, since the alcohol component having 2 to 4 carbon atoms is generally highly volatile and is easily removed in the production process of the recorded matter, The occurrence of adverse effects due to the remaining alcohol component is reliably prevented.

The excellent effects as described above can be obtained by including a predetermined amount of an alcohol component having 2 to 4 carbon atoms together with a metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester. If one of these requirements is not met, it cannot be obtained.
That is, although it contains a metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester, it does not contain an alcohol component having 2 to 4 carbon atoms, or an alcohol having 2 to 4 carbon atoms. When the content of the component is less than the predetermined value, the metal powder can be suitably arranged near the outer surface of the droplet of the ultraviolet curable inkjet composition, but in the ultraviolet curable inkjet composition Dispersibility of the metal powder in the ink drops significantly, and droplet discharge by the ink jet method becomes extremely unstable. Further, in this case, the discharge stability of the droplets of the ultraviolet curable ink jet composition is remarkably lowered with time, and it becomes difficult or impossible to discharge the droplets in a relatively short period of time.

  In addition, in the case of containing an alcohol component having 2 to 4 carbon atoms but not containing a metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester, the dispersion stability of the metal powder in a short period However, in the ultraviolet curable ink jet composition applied to the recording medium, it is difficult to suitably arrange the metal powder in the vicinity of the outer surface, and the recorded matter finally obtained The glossiness of (printing part) cannot be made sufficiently excellent.

  Further, when the content of the alcohol component having 2 or more and 4 or less carbon atoms in the ultraviolet curable ink jet composition exceeds a predetermined value, bubbles are generated by drying of the highly volatile alcohol component. When the ink in the vicinity of the nozzle hole is concentrated, ink discharge is lost or bent, and the intermittent discharge performance is significantly reduced. Further, the curability (speed) at the time of ultraviolet curing is lowered, and the printing durability of the finally obtained recorded matter is lowered.

In addition, when an alcohol component having 1 carbon atom (for example, methanol) is used instead of an alcohol component having 2 to 4 carbon atoms, the alcohol has a high polarity and the storage stability of the dispersion is almost increased. In addition, since the volatility is very high, the intermittent ejection property of the ink jet composition is deteriorated.
In addition, when an alcohol component having 5 or more carbon atoms (for example, 1-pentanol or the like) is used instead of the alcohol component having 2 to 4 carbon atoms, the remaining alcohol component increases and at the time of ultraviolet curing. In addition, the curability (speed) of the recording material decreases, and the printing durability of the finally obtained recorded material decreases. In addition, the alcohol component having 5 or more carbon atoms has high dispersibility and excellent storage stability of the metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester. Is reduced in the vicinity of the outer surface, and the glossiness of the printed portion of the recorded matter is reduced.

The ultraviolet curable ink jet composition may include two or more alcohol components having 2 to 4 carbon atoms. In this case, the sum total of these content rates should just be a value within the said range.
The content of the alcohol compound (alcohol component having 2 to 4 carbon atoms) in the ultraviolet curable inkjet composition may be 0.05% by mass or more and 7.0% by mass or less. The mass is preferably from 5.0% by mass to 5.0% by mass, and more preferably from 0.5% by mass to 4.0% by mass. Thereby, the effects of the present invention as described above are more remarkably exhibited.

  The molecular weight of the alcohol component having 2 to 4 carbon atoms is preferably 46 or more and 100 or less, more preferably 46 or more and 74 or less, and even more preferably 46 or more and 60 or less. Thereby, the effects as described above are more remarkably exhibited. In addition, since such liquid components are generally highly volatile and can be removed relatively easily in the manufacturing process of the recorded matter, in the recorded matter finally obtained by combining heating processes, etc. In addition, it is possible to more effectively prevent the occurrence of adverse effects due to the liquid component remaining.

The boiling point of the alcohol component having 2 to 4 carbon atoms (boiling point under 1 atm) is preferably 78 ° C. or higher and 117 ° C. or lower, more preferably 78 ° C. or higher and 100 ° C. or lower, and 78 ° C. or higher and 83 ° C. or lower. More preferably, it is not higher than ° C. Thereby, the effects as described above are more remarkably exhibited.
Examples of the alcohol component having 2 to 4 carbon atoms include ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, 2-methyl-1-propanol, 2-methyl-2-propanol, 1 , 2-ethanediol, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 2,3-butanediol, 2- Methyl-1,2-propanediol, 2-methyl-1,3-propanediol, 1,2,3-propanetriol, 1,2,3-butanetriol, 1,2,4-butanetriol, 2-methyl -1,2,3-propanetriol, 2-hydroxymethyl-1,3-propanediol, 1,2,3,4-butanetetraol, At least a portion of the hydrogen atoms of al compounds, halogen atom, compounds substituted with a substituent such as an amino group, and the like. Of these, ethanol and 2-propanol are preferable. When the ultraviolet curable inkjet composition contains ethanol and / or 2-propanol as an alcohol compound, the storage stability of the ultraviolet curable inkjet composition can be made particularly excellent. In addition, the discharge stability of the ultraviolet curable ink jet composition can be made particularly excellent, and the alcohol component is efficiently removed during the production of a recorded matter using the ultraviolet curable ink jet composition. Therefore, the productivity of recorded matter can be made particularly excellent over a long period of time. Moreover, it is possible to more reliably prevent the occurrence of harmful effects caused by the alcohol component remaining in the recorded matter.

<Polymerizable compound>
The polymerizable compound is a component that is polymerized and cured by irradiation with ultraviolet rays. By including such a component, it is possible to improve the abrasion resistance, water resistance, solvent resistance, and the like of the recorded matter produced using the ultraviolet curable ink jet composition.
The polymerizable compound is in a liquid state and preferably functions as a dispersion medium for dispersing the metal powder in the ultraviolet curable ink jet composition. As a result, even when the content of the polymerizable compound is relatively high, the viscosity of the ultraviolet curable inkjet composition can be made lower, and the droplet ejection stability by the inkjet method is particularly excellent. Can be. Moreover, the adhesiveness of the printing part formed using the ultraviolet curable inkjet composition with respect to various recording media (base materials) can be made excellent by including a polymeric compound. That is, by including the polymerizable compound, the ultraviolet curable inkjet composition has excellent media compatibility.

  The polymerizable compound may be any component that can be polymerized by irradiation with ultraviolet rays. For example, various monomers and various oligomers (including dimers and trimers) can be used. The polymerizable compound preferably contains at least a monomer component. Since the monomer is generally a component having a low viscosity as compared with the oligomer component or the like, it is advantageous for further improving the discharge stability of the ultraviolet curable ink jet composition.

  In particular, the ultraviolet ray curable ink composition of the present invention preferably contains a monomer having an alicyclic structure as the polymerizable compound. Thus, by including the monomer having an alicyclic structure together with the metal powder surface-treated with the fluorine-based silane compound and / or fluorine-based phosphate ester as described above, and the alcohol component, for ultraviolet curable inkjet The storage stability of the composition can be made particularly excellent, and the glossiness and abrasion resistance of the printed part of the recorded matter produced using the ultraviolet curable ink jet composition are particularly excellent. be able to.

  The reason why such an excellent effect can be obtained is considered to be as follows. That is, by including a monomer having an alicyclic structure, the dispersion stability of the metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester in an ultraviolet curable inkjet composition is excellent. And agglomeration and sedimentation of the metal powder in the ultraviolet curable ink jet composition can be suitably prevented over a long period of time. And such an effect synergizes with the effect by including a metal powder surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester and an alcohol component having 2 to 4 carbon atoms. As a result, the storage stability of the ultraviolet curable inkjet composition can be made particularly excellent, and the glossiness and abrasion resistance of the printed part of the recorded matter produced using the ultraviolet curable inkjet composition can be improved. It is considered that the property can be made particularly excellent.

  In addition, in this invention, an alicyclic structure means the ring structure which does not have aromaticity ((pi) electron conjugated system), and contains a hetero atom as a constituent atom besides the ring structure comprised only by the carbon atom. It is a concept that includes In addition, the monomer having an alicyclic structure may be any monomer having an alicyclic structure, and in addition, for example, a monomer having an aromatic ring structure (a ring structure having a π electron conjugated system). Also good.

  Examples of the monomer having an alicyclic structure include tris (2- (meth) acryloyloxyethyl) isocyanurate, dicyclopentenyloxyethyl (meth) acrylate, adamantyl (meth) acrylate, γ-butyrolactone (meth) acrylate, N -Vinylcaprolactam, N-vinylpyrrolidone, pentamethylpiperidyl (meth) acrylate, tetramethylpiperidyl (meth) acrylate, 2-methyl-2-adamantyl (meth) acrylate, 2-ethyl-2-adamantyl (meth) acrylate, mevalon Acid lactone (meth) acrylate, dimethylol tricyclodecane di (meth) acrylate, dimethylol dicyclopentane di (meth) acrylate, dicyclopentenyl (meth) acrylate, dicyclope Tanyl (meth) acrylate, isobornyl (meth) acrylate, cyclohexyl (meth) acrylate, (meth) acryloylmorpholine, tetrahydrofurfuryl (meth) acrylate, phenylglycidyl ether (meth) acrylate, EO-modified hydrogenated bisphenol A di (meth) Examples include acrylate, di (meth) acrylated isocyanurate, tri (meth) acrylated isocyanurate, tris (2-acryloyloxyethyl) isocyanurate, dicyclopentenyloxyethyl acrylate, adamantyl acrylate, and γ-butyrolactone acrylate. N-vinylcaprolactam, N-vinylpyrrolidone, pentamethylpiperidyl acrylate, tetramethylpiperidyl acrylate, 2-methyl-2-ada Nethyl acrylate, 2-ethyl-2-adamantyl acrylate, mevalonic acid lactone acrylate, dimethylol tricyclodecane diacrylate, dimethylol dicyclopentane diacrylate, dicyclopentenyl acrylate, dicyclopentanyl acrylate, isobornyl acrylate, cyclohexyl It is preferable to include one or more selected from the group consisting of acrylate, acryloylmorpholine, and tetrahydrofurfuryl acrylate. Thereby, the glossiness and high-quality feeling of the recorded matter manufactured using the ultraviolet curable inkjet composition can be further improved. Further, the storage stability and ejection stability of the ultraviolet curable ink jet composition can be further improved.

  In particular, when the composition contains one or more selected from the group consisting of acryloylmorpholine, tetrahydrofurfuryl acrylate, γ-butyrolactone acrylate, N-vinylcaprolactam, and N-vinylpyrrolidone, an ultraviolet curable ink jet composition The dispersion stability of the metal powder in the product can be further improved, and in the recorded matter produced using the ultraviolet curable ink jet composition, the metal powder is more preferably near the outer surface of the printing part. The glossiness of the obtained recorded matter can be further improved.

  Further, from the viewpoint of further improving the curing rate of the ultraviolet ray curable ink jet composition upon irradiation with ultraviolet rays and the productivity of the recorded matter, tris (2-acryloyloxyethyl) isocyanurate, dicyclopentenyloxyethyl are used. Consists of acrylate, γ-butyrolactone acrylate, N-vinyl pyrrolidone, dimethylol tricyclodecane diacrylate, dimethylol dicyclopentane diacrylate, dicyclopentenyl acrylate, dicyclopentanyl acrylate, acryloylmorpholine, and tetrahydrofurfuryl acrylate It is preferable to include one or more selected from the group, and more preferable to include acryloylmorpholine and / or γ-butyrolactone acrylate. More preferably, it contains γ-butyrolactone acrylate.

Moreover, when it contains a cyclohexyl acrylate and / or tetrahydrofurfuryl acrylate, the flexibility of the printing part formed by hardening | curing a ultraviolet curable inkjet composition can be made further excellent.
Further, from the viewpoint of further improving the abrasion resistance of the printed part formed by curing the ultraviolet curable ink jet composition, tris (2-acryloyloxyethyl) isocyanurate, dicyclopentenyloxyethyl acrylate, Adamantyl acrylate, γ-butyrolactone acrylate, N-vinyl caprolactam, N-vinyl pyrrolidone, dimethylol tricyclodecane diacrylate, dimethylol dicyclopentane diacrylate, dicyclopentenyl acrylate, dicyclopentanyl acrylate, isobornyl acrylate, And preferably one or more selected from the group consisting of acryloylmorpholine, including γ-butyrolactone acrylate and / or N-vinylcaprolactam. More preferably.

  In addition, when it contains one or more selected from the group consisting of γ-butyrolactone acrylate, N-vinylcaprolactam, N-vinylpyrrolidone, isobornyl acrylate, and tetrahydrofurfuryl acrylate, an ultraviolet curable ink jet The shrinkage rate at the time of curing of the composition for printing is reduced, and it is more effective to reduce glossiness due to unintentional wrinkles and the like in the printed part formed by curing the ultraviolet curable inkjet composition Can be prevented.

  The content of the monomer having an alicyclic structure in the ultraviolet curable ink jet composition is preferably 40% by mass or more and 90% by mass or less, more preferably 50% by mass or more and 88% by mass or less, and 55 More preferably, it is at least 85% by mass. Thereby, the dispersion stability of the metal powder is particularly excellent, and particularly excellent discharge stability can be obtained over a long period of time. In particular, even if the ultraviolet curable ink jet composition does not contain a dispersant, the above excellent effects can be obtained. On the other hand, when the content of the monomer having an alicyclic structure in the ultraviolet curable ink jet composition is less than the lower limit, the surface treatment was performed with a fluorine-based silane compound and / or a fluorine-based phosphate ester. There is a possibility that the dispersibility of the metal powder is lowered and the stability of droplet ejection by the ink jet method is lowered. Further, in this case, the temporal stability of the droplet ejection of the ultraviolet curable ink jet composition may also decrease. Further, when the content of the monomer having an alicyclic structure in the ultraviolet curable ink-jet composition exceeds the upper limit, the dispersion stability of the metal powder is excessively improved, which is imparted to the recording medium. In the ultraviolet curable ink jet composition, the internal ratio of the metal powder is increased, and it becomes difficult to properly arrange the metal powder near the outer surface of the applied ultraviolet curable ink jet composition. It may be difficult to make the recorded matter (printed part) obtained to have a sufficiently high gloss. In addition, the ultraviolet curable inkjet composition may contain two or more compounds as a monomer having an alicyclic structure. In this case, it is preferable that the sum of these contents is a value within the above range.

The monomer having an alicyclic structure preferably has 5 or more, more preferably 6 or more constituent atoms of a cyclic structure formed by a covalent bond. Thereby, the storage stability of the ultraviolet curable ink jet composition can be made particularly excellent.
The ultraviolet curable ink jet composition preferably contains a monofunctional monomer containing a hetero atom in the alicyclic structure (a monofunctional monomer having a heterocyclic ring not showing aromaticity) as the monomer having an alicyclic structure. . Thereby, the dispersion stability of the metal powder is particularly excellent, and particularly excellent discharge stability is obtained over a long period of time. In particular, even if the ultraviolet curable ink jet composition does not contain a dispersant, the above excellent effects can be obtained. The reason why such a monomer having an alicyclic structure improves the dispersion stability of the metal powder is not clear, but it has an appropriate affinity for the surface of the metal powder in which hetero atoms of the alicyclic structure are modified with fluorine atoms. This is considered to be due to the nature. Examples of such monofunctional monomers include tris (2- (meth) acryloyloxyethyl) isocyanurate, γ-butyrolactone (meth) acrylate, N-vinylcaprolactam, N-vinylpyrrolidone, pentamethylpiperidyl (meth) acrylate. , Tetramethylpiperidyl (meth) acrylate, mevalonic acid lactone (meth) acrylate, (meth) acryloylmorpholine, tetrahydrofurfuryl (meth) acrylate, and the like.

  The content of the monofunctional monomer (monofunctional monomer containing a hetero atom in the alicyclic structure) in the ultraviolet curable inkjet composition is preferably 10% by mass or more and 90% by mass or less, and more preferably 15% by mass or more. More preferably, it is 80 mass% or less. Thereby, it can use suitably for manufacture of the recorded matter provided with the pattern (printing part) which suppressed cure shrinkage, has few scattering, and was more excellent in glossiness. In addition, the composition for ultraviolet curable inkjets may contain 2 or more types of compounds as a monofunctional monomer containing a hetero atom in an alicyclic structure. In this case, it is preferable that the sum of these contents is a value within the above range.

In the present invention, the polymerizable compound constituting the ultraviolet curable inkjet composition may contain a monomer having no alicyclic structure.
Examples of such a monomer (a monomer having no alicyclic structure) include, for example, phenoxyethyl (meth) acrylate, 2- (2-vinyloxyethoxy) ethyl (meth) acrylate, dipropylene glycol di (meth) acrylate. , Tripropylene glycol di (meth) acrylate, 2-hydroxy-3-phenoxypropyl (meth) acrylate, and 4-hydroxybutyl (meth) acrylate, lauryl (meth) acrylate, 2-methoxyethyl (meth) acrylate, isooctyl ( (Meth) acrylate, stearyl (meth) acrylate, 2-ethoxyethyl (meth) acrylate, benzyl (meth) acrylate, 1H, 1H, 5H-octafluoropentyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate 2-hydroxypropyl (meth) acrylate, isobutyl (meth) acrylate, t-butyl (meth) acrylate, ethyl carbitol (meth) acrylate, 2,2,2-trifluoroethyl (meth) acrylate, 2,2 , 3,3-tetrafluoropropyl (meth) acrylate, methoxytriethylene glycol (meth) acrylate, PO-modified nonylphenol (meth) acrylate, EO-modified nonylphenol (meth) acrylate, EO-modified 2-ethylhexyl (meth) acrylate, phenoxydiethylene glycol ( (Meth) acrylate, EO-modified phenol (meth) acrylate, EO-modified cresol (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, dipropylene glycol (medium) ) Acrylate, 2-n-butyl-2-ethyl-1,3-propanediol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, 1.9-nonanediol di (meth) acrylate, 1,4- Butanediol di (meth) acrylate, bisphenol A EO modified di (meth) acrylate, 1.6-hexanediol di (meth) acrylate, polyethylene glycol 200 di (meth) acrylate, polyethylene glycol 300 di (meth) acrylate, neopentyl Glycol hydroxypivalate di (meth) acrylate, 2-ethyl-2-butyl-propanediol di (meth) acrylate, polyethylene glycol 400 di (meth) acrylate, polyethylene glycol 600 di (meth) acrylate Polypropylene glycol di (meth) acrylate, 1.6-hexanediol di (meth) acrylate, PO-modified bisphenol A di (meth) acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, trimethylolpropane EO-modified tri (meth) acrylate, glycerin PO-added tri (meth) acrylate, tris (meth) acryloyloxyethyl phosphate, pentaerythritol tetra (meth) acrylate, pentaerythritol tri (meth) acrylate, 2- (meth) acryloyl Roxyethyl phthalate, 3- (meth) acryloyloxypropyl acrylate, w-carboxy (meth) acryloyloxyethyl phthalate, ditrimethylolpropante Examples include tra (meth) acrylate, dipentaerythritol penta / hexa (meth) acrylate, dipentaerythritol hexa (meth) acrylate, phenoxyethyl acrylate, 2- (2-vinyloxyethoxy) ethyl acrylate, dipropylene It is preferable to include one or more selected from the group consisting of glycol diacrylate, tripropylene glycol diacrylate, 2-hydroxy-3-phenoxypropyl acrylate, and 4-hydroxybutyl acrylate. In addition to the monomer having an alicyclic structure, by including such a monomer that does not have an alicyclic structure, the inkjet storage method and the ejection stability of the ultraviolet curable inkjet composition are excellent, and the inkjet method The reactivity of the UV curable ink jet composition after ejection by the ink is particularly excellent, the productivity of the recorded matter can be particularly excellent, and the rub resistance of the formed pattern is particularly excellent Can be.

Among these, in the case of a recording material produced using an ultraviolet curable ink jet composition when it contains phenoxyethyl acrylate, the metal powder can be more suitably arranged near the outer surface of the printed part, The glossiness can be further improved.
Further, in the case of containing 2- (2-vinyloxyethoxy) ethyl acrylate, the curing rate of the ultraviolet ray curable inkjet composition when irradiated with ultraviolet rays and the productivity of recorded matter may be further improved. it can.

Moreover, when it contains phenoxyethyl acrylate and / or 2-hydroxy 3-phenoxypropyl acrylate, the flexibility of the printed part formed by curing the ultraviolet ray curable ink composition is further improved. be able to.
Further, from the viewpoint of further improving the abrasion resistance of the printed part formed by curing the ultraviolet curable ink jet composition, 2- (2-vinyloxyethoxy) ethyl acrylate, dipropylene glycol diacrylate And one or more selected from the group consisting of tripropylene glycol diacrylate, and more preferably 2- (2-vinyloxyethoxy) ethyl acrylate.
In addition, when it contains phenoxyethyl acrylate, the shrinkage rate at the time of curing of the ultraviolet curable inkjet composition is reduced, and the printing part formed by curing the ultraviolet curable inkjet composition is unintentional. It is possible to more effectively prevent a reduction in glossiness due to the occurrence of the above.

  The content of the monomer other than the monomer having an alicyclic structure in the ultraviolet curable inkjet composition is preferably 5% by mass or more and 50% by mass or less, and more preferably 10% by mass or more and 40% by mass or less. preferable. This further facilitates adjustment of the curing rate, flexibility, shrinkage rate during curing, and the like of the ultraviolet curable inkjet composition. In addition, the ultraviolet curable inkjet composition may contain two or more compounds as a monomer having no alicyclic structure. In this case, it is preferable that the sum of these contents is a value within the above range.

  The ultraviolet curable ink jet composition may contain an oligomer (including dimer, trimer, etc.), a prepolymer, etc. in addition to the monomer as the polymerizable compound. As the oligomer and prepolymer, for example, those having the above-described monomer as a constituent component can be used. The ultraviolet curable ink jet composition preferably contains a polyfunctional oligomer. As a result, the storage stability of the ultraviolet curable ink-jet composition can be made excellent, and the abrasion resistance of the formed pattern can be made particularly excellent. As the oligomer, a urethane oligomer whose repeating structure is urethane, an epoxy oligomer whose repeating structure is epoxy, and the like are preferably used.

  The content of the polymerizable compound in the ultraviolet curable inkjet composition is preferably 70% by mass or more and 99% by mass or less, and more preferably 80% by mass or more and 98% by mass or less. As a result, the storage stability, ejection stability, and curability of the ultraviolet curable inkjet composition can be further improved, and the gloss of the recorded matter produced using the ultraviolet curable inkjet composition can be improved. The feeling, abrasion resistance, etc. can be further improved. The ultraviolet curable inkjet composition may contain two or more compounds as the polymerizable compound. In this case, it is preferable that the total content of these compounds is a value within the above range.

<Polyether solvent>
The ultraviolet curable inkjet composition of the present invention may contain a polyether solvent in addition to the components described above. Thereby, the storage stability of the ultraviolet curable inkjet composition can be further improved, and the glossiness of the printed part of the recorded matter produced using the ultraviolet curable inkjet composition is further improved. It can be excellent.

In the present invention, the polyether-based solvent has a plurality of ether groups (ether oxygen) in the molecule, is liquid at a room temperature (25 ° C.), and has no ultraviolet curing property. Say that.
The content of the polyether solvent in the ultraviolet curable inkjet composition is preferably 0.05% by mass or more and 7.0% by mass or less, and is 0.2% by mass or more and 5.0% by mass or less. More preferably, it is 0.5 mass% or more and 4.0 mass% or less. Thereby, the effects as described above are more remarkably exhibited. The ultraviolet curable ink jet composition may contain two or more polyether solvents. In this case, it is preferable that the sum of these contents is a value within the above range.

  The molecular weight of the polyether solvent is preferably 40 or more and 250 or less, more preferably 60 or more and 230 or less, and still more preferably 90 or more and 200. Thereby, the effects as described above are more remarkably exhibited. In addition, such a polyether solvent is generally highly volatile, and can be removed relatively easily in the manufacturing process of recorded matter. Therefore, a recording finally obtained by combining a heating process or the like. Generation | occurrence | production of the bad influence by the said liquid component remaining in a thing can be prevented more effectively.

The ultraviolet curable ink jet composition preferably includes a polyether solvent that is represented by the following formula (10).
^{_{R 1 -O- (CH 2 CH 2}} O) n -R 2 (10)
(In Formula (10), R ¹ and R ² are each independently a linear alkyl group having 1 to 4 carbon atoms or a hydrogen atom, and n is an integer of 1 to 4) Provided that when ^one of R ¹ and R ² is a hydrogen atom, n is an integer of 2 or more and 4 or less, and when both R ¹ and R ² are hydrogen atoms, n Is 3 or 4.)

  As a result, the storage stability of the ultraviolet curable ink jet composition is particularly excellent, and the glossiness of the printed portion of the recorded matter produced using the ultraviolet curable ink jet composition is particularly excellent. Can do. In addition, since such a polyether solvent is generally highly volatile and is easily removed in the production process of the recorded matter, the polyether-based solvent is included in the finally obtained recorded matter. The occurrence of adverse effects due to the remaining solvent can be prevented more reliably.

In Formula (10), R ¹ and R ² may be each independently a linear alkyl group having 1 to 4 carbon atoms, preferably 2 to 4 carbon atoms, More preferably, the number of carbon atoms is 2. Thereby, the effects as described above are more remarkably exhibited.
In the formula (10), n may be an integer of 1 or more and 4 or less, preferably an integer of 2 or more and 4 or less, more preferably 2. Thereby, the effects as described above are more remarkably exhibited.

<Substance A>
Moreover, it is preferable that the ultraviolet curable inkjet composition of this invention contains the substance A which has a partial structure shown by following formula (5).

  The ultraviolet ray curable ink jet composition contains the substance A having such a chemical structure together with the metal particles subjected to the surface treatment as described above and an alcohol component having 2 to 4 carbon atoms, By including it together with a monomer having an alicyclic structure, the storage stability and curability of the ultraviolet curable inkjet composition can be made particularly excellent. In addition, in the recorded matter produced using the ultraviolet curable ink jet composition, the glossiness and luxury feeling inherent in the metal material constituting the metal powder is more effectively exhibited, and the gloss of the printed part The feeling and abrasion resistance can be made particularly excellent, and the durability of the recorded matter can be made particularly excellent.

In the formula (5), R ¹ may be an oxygen atom, a hydrogen atom, a hydrocarbon group or an alkoxyl group (a chain or alicyclic hydrocarbon group bonded to an oxygen atom). An atom, a methyl group, or an octyloxy group is preferred. As a result, the storage stability and ejection stability of the ultraviolet curable inkjet composition can be further improved, and the glossiness and resistance of the printed part formed using the ultraviolet curable inkjet composition can be improved. The rubbing property can be further improved.

In Formula (5), R ^{2 to} R ⁵ may be independently a hydrogen atom or a hydrocarbon group, but are preferably an alkyl group having 1 to 3 carbon atoms, and is a methyl group. Is more preferable. As a result, the storage stability and ejection stability of the ultraviolet curable inkjet composition can be further improved, and the glossiness and resistance of the printed part formed using the ultraviolet curable inkjet composition can be improved. The rubbing property can be further improved.

  The content of the substance A in the ultraviolet curable inkjet composition is preferably 0.1% by mass or more and 5.0% by mass or less, and more preferably 0.5% by mass or more and 3.0% by mass or less. More preferred. As a result, the storage stability, ejection stability, and curability of the ultraviolet curable inkjet composition can be further improved, and the gloss of the recorded matter produced using the ultraviolet curable inkjet composition can be improved. The feeling, abrasion resistance, etc. can be further improved. The ultraviolet curable inkjet composition may contain two or more compounds as the substance A. In this case, it is preferable that the total content of these compounds is a value within the above range.

When the content of the substance A is X _A [mass%] and the content of the metal powder is X _M [mass%], it is preferable that the relationship of 0.01 ≦ X _A / X _M ≦ 0.8 is satisfied. More preferably, the relationship 0.05 ≦ X _A / X _M ≦ 0.4 is satisfied. By satisfying such a relationship, the storage stability and ejection stability of the ultraviolet curable inkjet composition can be further improved, and the ultraviolet curable inkjet composition is formed. The glossiness and abrasion resistance of the printed part can be further improved.

<Dispersant>
The ultraviolet curable ink jet composition of the present invention may contain a metal powder dispersant. Thereby, the storage stability of the ultraviolet curable inkjet composition can be further improved.
In particular, the ultraviolet curable ink jet composition of the present invention includes a metal powder dispersant having a basic polymer structure (hereinafter also referred to as “basic polymer dispersant”). Also good. Thereby, the storage stability of the ultraviolet curable inkjet composition can be further improved.

The basic polymer dispersant is not particularly limited as long as it shows basicity and has a polymer structure.
The polymer structure constituting the basic polymer dispersant is not particularly limited. For example, an acrylic polymer structure (including a copolymer), a methacrylic polymer structure (including a copolymer), and polyurethane. Examples thereof include a polymer structure, a hydroxyl group-containing carboxylic acid ester structure, a polyether polymer structure, and a silicone polymer structure.
The amine value of the basic polymer dispersant is not particularly limited, but is preferably 3 mgKOH / g or more and 80 mgKOH / g or less, more preferably 10 mgKOH / g or more and 70 mgKOH / g or less.

  Specific examples of the basic polymer dispersant that can be used in the present invention include DISPERBYK-116 (manufactured by Big Chemie), DISPERBYK-182 (manufactured by Big Chemie), DISPERBYK-183 (manufactured by Big Chemie), DISPERBYK-184 ( Bicchemy), DISPERBYK-2155 (Bicchemy), DISPERBYK-2164 (Bicchemy), DISPERBYK-108 (Bicchemy), DISPERBYK-112 (Bicchemy), DISPERBYK-198 (Bicchemy), DISPERBYK-2150 (manufactured by Big Chemie), PAA-1112 (manufactured by Nittobo), and the like.

  In the case where the ultraviolet curable inkjet composition contains a dispersant, the content of the dispersant in the ultraviolet curable inkjet composition is preferably 5.0% by mass or less, and 0.01% by mass to 2%. More preferably, it is 0.0 mass% or less. As a result, the storage stability, ejection stability, and curability of the ultraviolet curable inkjet composition are further improved while sufficiently improving the glossiness of the recorded matter produced using the ultraviolet curable inkjet composition. It can be excellent. The ultraviolet curable ink jet composition may contain two or more compounds as a basic polymer dispersant. In this case, it is preferable that the total content of these compounds is a value within the above range. In addition, when the content of the dispersant in the ultraviolet curable inkjet composition is too high, the dispersion stability of the metal powder is excessively improved, and in the ultraviolet curable inkjet composition applied to the recording medium, The internal ratio of the metal powder is increased, making it difficult to properly arrange the metal powder near the outer surface of the applied ultraviolet curable ink jet composition, and the gloss of the finally obtained recorded matter (printed part) It may be difficult to make the feeling sufficiently excellent.

<Other ingredients>
The ultraviolet curable inkjet composition of the present invention may contain components other than those described above (other components). Examples of such components include photopolymerization initiators, slip agents (leveling agents), solvents other than the above-described alcohol components (alcohol components having 2 to 4 carbon atoms), polymerization accelerators, polymerization inhibitors, and penetrations. Accelerators, wetting agents (humectants), colorants, fixing agents, antifungal agents, preservatives, antioxidants, chelating agents, thickeners, sensitizers (sensitizing dyes) and the like can be mentioned.

  The photopolymerization initiator is not particularly limited as long as it generates active species such as radicals and cations by ultraviolet irradiation and initiates the polymerization reaction of the polymerizable compound. As the photopolymerization initiator, a radical photopolymerization initiator or a cationic photopolymerization initiator can be used, but it is preferable to use a radical photopolymerization initiator. When using a photopolymerization initiator, the photopolymerization initiator preferably has an absorption peak in the ultraviolet region.

Examples of the photo radical polymerization initiator include aromatic ketones, acylphosphine oxide compounds, aromatic onium salt compounds, organic peroxides, thio compounds (thioxanthone compounds, thiophenyl group-containing compounds, etc.), hexaarylbiimidazole compounds, Examples thereof include ketoxime ester compounds, borate compounds, azinium compounds, metallocene compounds, active ester compounds, compounds having a carbon halogen bond, and alkylamine compounds.
Among these, at least one selected from an acylphosphine oxide compound and a thioxanthone compound is preferable from the viewpoint of solubility in a polymerizable compound and curability, and it is more preferable to use an acylphosphine oxide compound and a thioxanthone compound in combination.

  Specific examples of the photo radical polymerization initiator include acetophenone, acetophenone benzyl ketal, 1-hydroxycyclohexyl phenyl ketone, 2,2-dimethoxy-2-phenylacetophenone, xanthone, fluorenone, benzaldehyde, fluorene, anthraquinone, triphenylamine. , Carbazole, 3-methylacetophenone, 4-chlorobenzophenone, 4,4′-dimethoxybenzophenone, 4,4′-diaminobenzophenone, Michler's ketone, benzoin propyl ether, benzoin ethyl ether, benzyldimethyl ketal, 1- (4-isopropylphenyl) ) -2-Hydroxy-2-methylpropan-1-one, 2-hydroxy-2-methyl-1-phenylpropan-1-one, thioxanthone, diethyl Oxanthone, 2-isopropylthioxanthone, 2-chlorothioxanthone, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholino-propan-1-one, bis (2,4,6-trimethylbenzoyl) -phenyl Phosphine oxide, 2,4,6-trimethylbenzoyl-diphenyl-phosphine oxide, 2,4-diethylthioxanthone, bis- (2,6-dimethoxybenzoyl) -2,4,4-trimethylpentylphosphine oxide, etc. 1 type or 2 types or more selected from these can be used in combination.

The content of the photopolymerization initiator in the ultraviolet curable inkjet composition is preferably 0.5% by mass or more and 10% by mass or less. When the content of the photopolymerization initiator is within the above range, the ultraviolet curing rate is sufficiently high, and the photopolymerization initiator is hardly dissolved or colored due to the photopolymerization initiator.
When the ultraviolet curable ink jet composition contains a slip agent, the surface of the recorded matter becomes smooth due to the leveling action, and the abrasion resistance is improved.

  The slip agent is not particularly limited. For example, silicone surfactants such as polyester-modified silicone, polyether-modified silicone, and polyacrylate-modified silicone, and polymer surfactants such as polyacrylate and polyester can be used. It is preferable to use polyether-modified polydimethylsiloxane, polyester-modified polydimethylsiloxane, or polyacrylate-modified dimethylsiloxane.

The ultraviolet curable inkjet composition of the present invention may contain a polymerization inhibitor, but even when it contains a polymerization inhibitor, the polymerization inhibitor in the ultraviolet curable inkjet composition. The content of is preferably 0.6% by mass or less, and more preferably 0.3% by mass or less. Accordingly, since the content of the polymerizable compound in the ultraviolet curable inkjet composition can be relatively increased, the abrasion resistance of the printed portion formed using the ultraviolet curable inkjet composition can be increased. The property and the like can be made particularly excellent. In the present invention, even when the content of the polymerization inhibitor is relatively low, the storage stability and ejection stability of the ultraviolet curable ink jet composition may be sufficiently excellent. it can.
The viscosity at room temperature (20 ° C.) of the ultraviolet curable inkjet composition of the present invention is preferably 20 mPa · s or less, and more preferably 3 mPa · s or more and 15 mPa · s or less. Thereby, the droplet discharge by an inkjet method can be performed suitably.

《Recordings》
Next, the recorded matter of the present invention will be described.
The recorded matter of the present invention is produced by applying the ultraviolet curable ink jet composition as described above onto a recording medium and then irradiating with ultraviolet rays. Such a recorded matter has a pattern (printing portion) excellent in glossiness and abrasion resistance.

  As described above, the ultraviolet curable ink jet composition according to the present invention contains a predetermined polymerizable compound and has excellent adhesion to a recording medium. As described above, since the ultraviolet curable ink jet composition of the present invention is excellent in adhesion to a recording medium, the recording medium may be any one, using either absorbing or non-absorbing. For example, paper (plain paper, ink jet dedicated paper, etc.), plastic materials, metals, ceramics, wood, shells, cotton, polyester, wool and other natural fibers / synthetic fibers, non-woven fabrics, etc. can be used.

  The recorded matter of the present invention may be used for any purpose, and may be applied to, for example, a decorative article or other items. Specific examples of the recorded material of the present invention include console interiors for vehicles such as console lids, switch bases, center clusters, interior panels, emblems, center consoles, meter nameplates, operation parts (key switches) of various electronic devices, decorations. Display items such as decorative parts, indicators, logos, etc. that exhibit properties.

As a droplet discharge method (inkjet method), a piezo method, a method of discharging ink by bubbles generated by heating ink, or the like can be used. The piezo method is preferable from the viewpoint of difficulty in alteration.
The ultraviolet curable ink jet composition can be discharged by an ink jet method using a known droplet discharge device.
The ultraviolet ray curable ink jet composition discharged by the ink jet method is cured by irradiation with ultraviolet rays.

As the ultraviolet light source, for example, a mercury lamp, a metal halide lamp, an ultraviolet light emitting diode (UV-LED), an ultraviolet laser diode (UV-LD), or the like can be used. Among these, ultraviolet light emitting diodes (UV-LED) and ultraviolet laser diodes (UV-LD) are preferable from the viewpoints of small size, long life, high efficiency, and low cost.
As mentioned above, although this invention was demonstrated based on suitable embodiment, this invention is not limited to these.

Next, specific examples of the present invention will be described.
[1] Production of inkjet composition (UV-curable inkjet composition) (Example 1)
First, a film made of polyethylene terephthalate having a smooth surface (surface roughness Ra of 0.02 μm or less) was prepared.

Next, silicone oil was applied to the entire one surface of the film.
Next, a film made of Al was formed on the side coated with silicone oil by vapor deposition.
Next, a polyethylene terephthalate film (base material) on which an Al film was formed was placed in a liquid composed of diethylene glycol diethyl ether, and ultrasonic vibration was applied. Thereby, a scale-like Al particle dispersion (particles to be the mother particles) dispersion was obtained.

Next, 1% by mass of CF ₃ (CF ₂ ) ₅ (CH ₂ ) ₂ O (P) (OH) ₂ as a fluorine-based phosphate is added to the Al particle dispersion obtained as described above. Then, the mixture was stirred at 45 ° C. for 120 minutes to perform surface treatment with a fluorine-based phosphate ester to obtain a metal powder dispersion. The metal powder dispersion was filtered and dried to obtain a metal powder.
The average particle diameter of the metal powder thus obtained was 0.8 μm, and the average thickness was 60 nm.

  Next, metal powder, ethanol, γ-butyrolactone acrylate as a monomer (polymerizable compound) having an alicyclic structure, phenoxyethyl acrylate as a monomer (polymerizable compound) having no alicyclic structure, a photopolymerization initiator Irgacure 819 (manufactured by Ciba Japan), Speedcure TPO (manufactured by ACETO) as a photopolymerization initiator, Speedcure DETX (manufactured by Lambson) as a photopolymerization initiator, and the following formula (6) By mixing with the substance A having a chemical structure, an ink jet composition (an ultraviolet curable ink jet composition) was obtained.

(Examples 2 to 19)
The composition of the metal particles (the composition of the mother particles and the type of compound (fluorine compound) used for the surface treatment) is as shown in Tables 1 and 2, and the inkjet composition (ultraviolet curable inkjet composition) was prepared. Inkjet composition (ultraviolet curable inkjet composition) in the same manner as in Example 1 except that the composition shown in Tables 1 and 2 was changed by changing the type and ratio of raw materials used in ) Was manufactured.

(Comparative Example 1)
An ink jet composition (ultraviolet curable ink jet composition) was produced in the same manner as in the above example except that Al particles that were not subjected to surface treatment were used as the metal powder.
(Comparative Example 2)
The inkjet composition (ultraviolet curable inkjet composition) was used in the same manner as in Comparative Example 1 except that a spherical Al powder (non-surface-treated) manufactured using the gas atomization method was used as the metal powder. Product).

(Comparative Example 3)
Instead of CF ₃ (CF ₂ ) ₅ (CH ₂ ) ₂ O (P) (OH) _{2 as} a fluorine-based phosphate ester, NH ₃ — (CH ₂ ) that is neither a fluorine-based silane compound nor a fluorine-based phosphate ester An ink jet composition (ultraviolet curable ink jet composition) was produced in the same manner as in the above example except that the surface treatment was performed using _3- Si (OCH ₃ ) ₃ to obtain a metal powder.

(Comparative Example 4)
By changing the content ratio of the alcohol component having 2 or more and 4 or less carbon atoms to 0.04% by mass and changing the type and ratio of the raw materials used for the preparation of the ink jet composition (ultraviolet curable ink jet composition). An ink jet composition (ultraviolet curable ink jet composition) was produced in the same manner as in the above example, except that the composition shown in Table 2 was obtained.

(Comparative Example 5)
By changing the content ratio of the alcohol component having 2 to 4 carbon atoms to 7.1% by mass and changing the type and ratio of the raw materials used for preparing the ink jet composition (ultraviolet curable ink jet composition). An ink jet composition (ultraviolet curable ink jet composition) was produced in the same manner as in the above example, except that the composition shown in Table 2 was obtained.

(Comparative Examples 6-9)
By changing the kind and ratio of raw materials used for the preparation of the ink jet composition (ultraviolet curable ink jet composition) without using an alcohol component having 2 to 4 carbon atoms, the composition as shown in Table 2 An ink jet composition (ultraviolet curable ink jet composition) was produced in the same manner as in the above example except that it was changed.

Tables 1 and 2 collectively show the composition of the ink jet composition for each of the above Examples and Comparative Examples. In the table, CF ₃ (CF ₂ ) ₅ (CH ₂ ) ₂ O (P) (OH) ₂ is “S1”, CF ₃ (CF ₂ ) ₅ (CH ₂ ) ₂ O (P) (OH) ( OCH ₂ CH ₃₎ the _{"S2", CF 3 (CF 2) 4} (CH 2) 2 O-PO (OH) 2 to _{"S3", CF 3 (CF 2) 5} -CH 2 CH 2 -Si (OC ₂ H ₅ ) ₃ for “S4”, CF ₃ —CH ₂ CH ₂ —Si (OCH ₃ ) ₃ for “S5”, CF ₃ (CF ₂ ) ₇ —CH ₂ CH ₂ —Si (OCH ₃ ) ₃ for “ S6 ”, CF ₃ (CF ₂ ) ₅ (CH ₂ ) ₂ O—PO (OH) (OC ₂ H ₅ ) as“ S7 ”, CF ₃ (CF ₂ ) ₅ —CH ₂ CH ₂ —Si (OCH ₃ ) "S8" the _{3, NH 3 - (CH 2} ) 3 -Si (OCH 3) 3 to "S'1" ethanol " tOH ", 1-propanol" 1-PrOH ", 2-propanol" 2-PrOH ", 1-butanol" 1-BuOH ", 2-butanol" 2-BuOH ", 2-methyl-1-propanol As “i-BuOH”, 2-methyl-2-propanol as “t-BuOH”, methanol as “MeOH”, 1-pentanol as “1-PeOH”, and monomer having an alicyclic structure (polymerizable compound) Γ-butyrolactone acrylate of “BLA”, tetrahydrofurfuryl acrylate as a monomer having an alicyclic structure (polymerizable compound) “THFA”, and N-vinylcaprolactam as a monomer having an alicyclic structure (polymerizable compound) "VC", N-vinylpyrrolidone as a monomer (polymerizable compound) having an alicyclic structure, "VP", alicyclic "AMO" for acryloylmorpholine as a monomer (polymerizable compound) having a structure, "TAOEI" for tris (2-acryloyloxyethyl) isocyanurate as a monomer (polymerizable compound) having an alicyclic structure, and an alicyclic structure Dicyclopentenyloxyethyl acrylate as a monomer (polymerizable compound) having “DCPTeOEA”, adamantyl acrylate having a alicyclic structure (polymerizable compound) as “AA”, and monomer having an alicyclic structure (polymerizable compound) ) Dimethylol tricyclodecane diacrylate as “DMTCDDA”, dimethylol dicyclopentane diacrylate as the monomer having alicyclic structure (polymerizable compound) “DMDCPTA”, monomer having alicyclic structure (polymerizable compound) )age Dicyclopentenyl acrylate of “DCPTeA”, dicyclopentanyl acrylate as a monomer (polymerizable compound) having an alicyclic structure, “DCPTaA”, and isobornyl acrylate as a monomer having an alicyclic structure (polymerizable compound) "IBA", cyclohexyl acrylate as a monomer (polymerizable compound) having an alicyclic structure "CHA", diacrylated isocyanurate as a monomer (polymerizable compound) having an alicyclic structure "DAI", alicyclic structure The triacrylated isocyanurate as a monomer (polymerizable compound) having TAI is “TAI”, γ-butyrolactone methacrylate as a monomer having an alicyclic structure (polymerizable compound) is “BLM”, and a monomer having an alicyclic structure (polymerization) As a functional compound) “THFM”, dicyclopentenyloxyethyl methacrylate as a monomer (polymerizable compound) having an alicyclic structure “DCPTeOEM”, and adamantyl methacrylate as a monomer (polymerizable compound) having an alicyclic structure “AM” , “PMPM” is pentamethylpiperidyl methacrylate as a monomer (polymerizable compound) having an alicyclic structure, “TMPM” is tetramethylpiperidyl methacrylate as a monomer (polymerizable compound) having an alicyclic structure, and has an alicyclic structure. 2-Methyl-2-adamantyl methacrylate as a monomer (polymerizable compound) “MAM”, 2-ethyl-2-adamantyl methacrylate as a monomer (polymerizable compound) having an alicyclic structure “EAM”, alicyclic structure Monomers with -Mevalonic acid lactone as a (polymerizable compound) "MLM" methacrylate, dicyclopentenyl methacrylate as a monomer having an alicyclic structure (polymerizable compound) "DCPTeM", monomer having an alicyclic structure (polymerizable compound) Dicyclopentanyl methacrylate as “DCPTaM”, isobornyl methacrylate as a monomer having an alicyclic structure (polymerizable compound) “IBM”, and cyclohexyl methacrylate as a monomer having a alicyclic structure (polymerizable compound) “CHM”, phenoxyethyl acrylate as a monomer having no alicyclic structure (polymerizable compound) “PEA”, dipropylene glycol diacrylate having no alicyclic structure (polymerizable compound) as “DPGDA” ”, Which has no alicyclic structure Tripropylene glycol diacrylate as a monomer (polymerizable compound) is “TPGDA”, 2-hydroxy-3-phenoxypropyl acrylate is “HPPA” as a monomer having no alicyclic structure (polymerizable compound), and an alicyclic structure is 4-Hydroxybutyl acrylate as a monomer (polymerizable compound) that does not have "HBA", ethyl carbitol acrylate as a monomer (polymerizable compound) that does not have an alicyclic structure as "ECA", has an alicyclic structure Methoxytriethylene glycol acrylate as a monomer (polymerizable compound) that does not have "MTEGA", t-butyl acrylate as a monomer (polymerizable compound) that does not have an alicyclic structure as "TBA", has an alicyclic structure Benzyl acrylate as a monomer (polymerizable compound) “VEEA” is 2- (2-hydroxyethoxy) ethyl acrylate as a monomer (polymerizable compound) having no alicyclic structure, and “benzyl methacrylate” is a monomer (polymerizable compound) having no alicyclic structure. BM ”, urethane acrylate as a monomer having no alicyclic structure (polymerizable compound)“ UA ”, DISPERBYK-182 (by Big Chemie, amine value: 13 mgKOH / g)“ D2 ”, DISPERBYK-2155 (Big Chemie) Manufactured by the company, amine value: 48 mg KOH / g) is “D5”, the compound represented by the above formula (6) (substance A) is “A1”, the compound represented by the following formula (7) (substance A) is “ A2 ”, a compound (substance A) represented by the following formula (8)“ A3 ”, a substance A represented by the following formula (9)“ A4 ”, Irgacure 8 9 (manufactured by Ciba Japan) is “ic819”, Speedcure TPO (manufactured by ACETO) is “scTPO”, Speedcure DETX (manufactured by Lambson) is “scDETX”, and UV-3500 (manufactured by BYK Chemie) is “UV3500”, Hydroquinone monomethyl ether was indicated by “MEHQ”, LHP-96 (manufactured by Enomoto Kasei Co., Ltd.) by “LHP”, and LF-1984 (manufactured by Enomoto Kasei Co., Ltd.) by “LF”. Moreover, about Example 15, the composition of the constituent material of a mother particle showed the content rate of each element with the weight ratio about Example 15. In addition, the observation is performed on each of the 10 arbitrary metal particles contained in each inkjet composition, and the area S ₁ [μm ² ] when observed from the direction in which the projected area is maximized (when viewed in plan), The ratio (S ₁ / S ₀ ) to the area S ₀ [μm ² ] when observed from the direction in which the area when observed is the maximum among the directions orthogonal to the observation direction is determined, and the average value of these is expressed as 1 and Table 2 are also shown. In addition, the viscosity at 20 ° C. of the inkjet compositions (ultraviolet curable inkjet compositions) of each of the above examples measured according to JIS Z8809 using a vibration viscometer is 3 mPa · s or more. The value was within a range of 15 mPa · s or less. D2 and D5 are both basic and have a polymer structure (basic polymer dispersant).

[2] Droplet discharge stability evaluation (discharge stability evaluation)
Using the inkjet compositions of the respective Examples and Comparative Examples, the evaluation by the following tests was performed.
First, a droplet discharge device installed in a chamber (thermal chamber) and the ink-jet compositions of the above examples and comparative examples were prepared, and the driving waveform of the piezo element was optimized, at 25 ° C. and 50% RH. Under the environment, about 2 million droplets (2000000 droplets) were continuously discharged from each nozzle of the droplet discharge head for each inkjet composition. Thereafter, the operation of the droplet discharge device was stopped, and the droplet discharge device was allowed to stand for 360 hours in an environment of 25 ° C. and 50% RH in a state where the flow path of the droplet discharge device was filled with each inkjet composition.

  Thereafter, 4 million droplets (4000000 droplets) were continuously discharged from each nozzle of the droplet discharge head in an environment of 25 ° C. and 50% RH. The average deviation amount d from the center target position of the center position of each of the landed droplets of the 4000000 droplets ejected from a designated nozzle near the center of the droplet ejection head after being left for 360 hours. Values were obtained and evaluated according to the following five-step criteria. It can be said that the smaller the value is, the more effectively the occurrence of flight bending is prevented.

A: The average value of the shift amount d is less than 0.07 μm.
B: The average value of the shift amount d is 0.07 μm or more and less than 0.14 μm.
C: The average value of the shift amount d is 0.14 μm or more and less than 0.17 μm.
D: The average value of the shift amount d is 0.17 μm or more and less than 0.21 μm.
E: The average value of the shift amounts d is 0.21 μm or more.

[3] Frequency characteristics of inkjet composition In the state in which the droplet ejection device installed in the chamber (thermal chamber) and the inkjet compositions of the respective examples and comparative examples are prepared and the drive waveform of the piezoelectric element is optimized, In an environment of 25 ° C. and 50% RH, each ink jet composition was subjected to droplet ejection while changing the frequency (frequency) of the piezo element from all nozzles of the droplet ejection head. The droplet discharge time at each frequency was 20 minutes. The frequency range that can be actually used was evaluated according to the following four-stage criteria, with the number of undischarged nozzles being less than 1% of the total number of nozzles after 20 minutes of discharge being the highest frequency that can be actually used. It can be said that the larger this value, the better the frequency characteristics.
A: 15 kHz or more.
B: 10 kHz or more and less than 15 kHz.
C: 5 kHz or more and less than 10 kHz.
D: Less than 5 kHz.

[4] Storage stability evaluation of inkjet composition (long-term stability evaluation)
[4.1] Dispersibility The inkjet compositions of the above Examples and Comparative Examples were allowed to stand for 60 days in an environment of 40 ° C., and then passed through 1 L with a capsule filter (manufactured by Yamachine Filter) with a filtration accuracy of 3 μm. The concentration before and after liquid passage was measured, and the loss due to filter filtration of coarse particles due to insufficient dispersion was determined by the rate of concentration reduction, and evaluated according to the following criteria.
A: The ink density reduction rate is less than 5%.
B: The ink density reduction rate is 5% or more and less than 10%.
C: The ink density reduction rate is 10% or more and less than 20%.
D: The ink density reduction rate is 20% or more and less than 40%.

[4.2] Increasing rate of viscosity The inkjet compositions of the above Examples and Comparative Examples were measured in accordance with JIS Z8809 using a vibration viscometer after being left in an environment of 40 ° C. for 60 days. The viscosity at 20 ° C. of the inkjet compositions of each of the above examples and comparative examples was measured to determine the rate of increase in viscosity immediately after production, and evaluated according to the following criteria.

A: Increase rate of viscosity is less than 5%.
B: Increase rate of viscosity is 5% or more and less than 10%.
C: Increase rate of viscosity is 10% or more and less than 18%.
D: Increase rate of viscosity is 18% or more and less than 23%.
E: The rate of increase in viscosity is 23% or more, or generation of foreign matter is observed.

[5] Curability About the ink jet compositions of the respective Examples and Comparative Examples, the ink jet printer manufactured by Epson; introduced into PM800C, and using Diafoil G440E (thickness 38 μm) manufactured by Mitsubishi Resin Co., Ltd. as a recording medium, Solid printing was performed at an ink amount of 9 g / m ^2. Immediately after printing, the LED-UV lamp; Foseon's RX firefly (gap 6 mm, peak wavelength 365 nm, 1000 mW / cm ² ) was used to irradiate ultraviolet rays, and inkjet Whether the composition was cured or not was evaluated and evaluated according to the following five-step criteria. Whether it was cured or not was determined by rubbing the surface with a cotton swab and whether or not the uncured ink composition adhered. In addition, whether it corresponds to the irradiation amount of the following AE can be calculated by how many seconds the lamp is irradiated.

A: Cured with an ultraviolet irradiation dose of less than 200 mJ / cm ² .
B: It hardened | cured with the ultraviolet irradiation amount of 200 mJ / cm < ² > or more and less than 300 mJ / cm < ² >.
C: It hardened | cured with the ultraviolet irradiation amount of 300 mJ / cm < ² > or more and less than 500 mJ / cm < ² >.
D: It hardened | cured with the ultraviolet irradiation amount of 500 mJ / cm < ² > or more and less than 1000 mJ / cm < ² >.
E: It hardens | cures by the ultraviolet irradiation amount of 1000 mJ / cm < ² > or more. Or it does not cure at all.

[6] Manufacture of Recorded Items Using the inkjet compositions of the examples and comparative examples, interior panels as recorded products were manufactured as follows.
First, the inkjet composition was put into an inkjet apparatus.
Thereafter, the inkjet composition was ejected in a predetermined pattern onto a base material (recording medium) having a curved surface portion formed using polycarbonate (manufactured by Asahi Glass Co., Ltd., Carboglass polish 2 mm thick).

Then, after heating at 60 ° C. for 5 minutes, ultraviolet rays having a spectrum having maximum values at wavelengths of 365 nm, 380 nm, and 395 nm are irradiated for 10 seconds with an irradiation intensity of 160 mW / cm ² to cure the inkjet composition on the substrate. , Got an interior panel as a record.
Using the method as described above, ten interior panels (recorded matter) were produced using the ink-jet compositions of the examples and comparative examples.

  Moreover, what was shape | molded using polyethylene terephthalate (Diafoil G440E 38micrometer thickness made from Mitsubishi Plastics) as a base material, low density polyethylene (TuX (L-LDPE) HC-E # 80 made from Mitsui Chemicals, Inc. cello). ), Biaxially stretched polypropylene (OP U-1 # 60 made by Mitsui Chemical Tosero Co., Ltd.), hard vinyl chloride (Sunday sheet (transparent) 0.5 mm thickness made by Acrysandy Co.) Ten interior panels (recorded matter) were produced in the same manner as described above except that the ones molded using the same were used, using the inkjet compositions of the examples and comparative examples.

[7] Evaluation of recorded matter Each recorded matter obtained as described above was evaluated as follows.
[7.1] Appearance evaluation of recorded matter Each recorded matter produced in each of the above examples and comparative examples was visually observed and evaluated according to the following seven criteria.

A: It has a glossy feeling rich in luxury and has an extremely excellent appearance.
B: It has a glossy feeling full of luxury and has a very excellent appearance.
C: It has a glossiness with a high-class feeling and has an excellent appearance.
D: Glossy with a high-class feeling and a good appearance.
E: Inferior gloss and appearance is slightly poor.
F: Inferior glossiness and poor appearance.
G: Inferior glossiness and extremely poor appearance.

[7.2] Glossiness About the pattern formation part of each recorded matter manufactured by each said Example and comparative example, using the glossiness meter (MINOLTA MULTI GLOSS 268), the glossiness in the angle of 60 degrees is measured, Evaluation was made according to the following criteria.
A: Glossiness is 400 or more.
B: Glossiness is 300 or more and less than 400.
C: Glossiness is 200 or more and less than 300.
D: Glossiness is less than 200.

[7.3] Abrasion resistance With respect to the recorded matter according to each of the above examples and comparative examples, when 48 hours have elapsed since the production of the recorded matter, a Southerland Lab Tester was used and polyethylene terephthalate was used as a phase paper according to JIS K5701. A rub resistance test using a film made by Mitsubishi Plastics (Diafoil G440E) was performed, and the recorded material after the rub resistance test was also glossy by the same method as described in [7.2] above. The degree of reduction in gloss before and after the abrasion resistance test was determined and evaluated according to the following criteria.

A: The reduction rate of glossiness is less than 5%.
B: The reduction rate of glossiness is 5% or more and less than 13%.
C: The reduction rate of glossiness is 13% or more and less than 23%.
D: The reduction rate of glossiness is 23% or more and less than 27%.
E: Gloss reduction rate is 27% or more, or the surface of the recording medium is exposed due to metal particles falling off.

  These results are shown in Table 3. In Table 3, “M1” is a recorded matter manufactured using a polycarbonate substrate, “M2” is a recorded material manufactured using a polyethylene terephthalate substrate, and a low density polyethylene substrate. “M3” is a recorded matter manufactured using a biaxially oriented polypropylene base material, and “M4” is a recorded matter manufactured using a biaxially oriented polypropylene base material. Indicated by “M5”.

  As is clear from Table 3, the ultraviolet curable inkjet composition of the present invention was excellent in droplet ejection stability, storage stability, and curability. Further, the recorded matter of the present invention had excellent gloss and appearance, and was excellent in the abrasion resistance of the pattern forming portion. In addition, by using the ultraviolet curable inkjet composition of the present invention, stable and excellent results were obtained regardless of the type of recording medium. On the other hand, in the comparative example, a satisfactory result was not obtained.

Claims (15)

An ultraviolet curable ink jet composition discharged by an ink jet method,
A polymerizable compound, a metal powder, and an alcohol component having 2 to 4 carbon atoms,
The metal powder includes a surface treated with a fluorinated silane compound and / or a fluorinated phosphate as a surface treating agent,
The ultraviolet curable inkjet composition, wherein the content of the alcohol component in the ultraviolet curable inkjet composition is 0.05% by mass or more and 7.0% by mass or less.   2. The ultraviolet curable ink jet composition according to claim 1, wherein the metal powder is a powder whose surface is mainly composed of Al and is surface-treated with a fluorine-based silane compound and / or a fluorine-based phosphate ester. .   The ultraviolet curable ink jet composition according to claim 1, wherein the metal powder has a scaly shape. The ultraviolet curable inkjet composition according to any one of claims 1 to 3, wherein the metal powder includes a surface treated with the fluorine-based silane compound having a chemical structure represented by the following formula (1). object.
R ¹ SiX ¹ _a R ² _(3-a) (1)
(In Formula (1), R ¹ represents a hydrocarbon group in which part or all of the hydrogen atoms are substituted with fluorine atoms, X ¹ represents a hydrolyzable group, an ether group, a chloro group, or a hydroxyl group; ² represents an alkyl group having 1 to 4 carbon atoms, and a is an integer of 1 to 3 inclusive.) 5. The ultraviolet curable ink jet according to claim 1, wherein the metal powder includes a surface treated with the fluorine-based phosphate ester having a chemical structure represented by the following formula (2). Composition.
POR _n (OH) _3-n (2)
(In the formula (2), R _{is, CF 3 (CF 2) m} -, CF 3 (CF 2) m (CH 2) l -, CF 3 (CF 2) m (CH 2 O) l -, CF 3 (CF ₂ ) _m (CH ₂ CH ₂ O) ₁ —, CF ₃ (CF ₂ ) _m O—, or CF ₃ (CF ₂ ) _m (CH ₂ ) ₁ O—, and n is 1 or more and 3 or less. M is an integer from 5 to 17, and l is an integer from 1 to 12.) As the metal _{powder, CF 3 (CF 2) 5} (CH 2) 2 O (P) (OH) 2 and / or _{CF 3 (CF 2) 5 (} CH 2) 2 O (P) (OH) (OCH 2 CH ₃₎ an ultraviolet curable ink composition according to any one of claims 1 to 5, including those subjected to surface treatment with the fluorine-based phosphate ester represented.   The ultraviolet curable inkjet composition according to claim 1, wherein the metal powder has an average particle size of 500 nm to 3.0 μm.   The ultraviolet curable inkjet composition according to any one of claims 1 to 7, comprising a monomer having an alicyclic structure as the polymerizable compound.   The ultraviolet curable inkjet composition according to claim 8, wherein the content of the monomer having an alicyclic structure in the ultraviolet curable inkjet composition is 40% by mass or more and 90% by mass or less.   The ultraviolet curable ink jet composition according to claim 8 or 9, comprising a monofunctional monomer containing a hetero atom in the alicyclic structure as the monomer having the alicyclic structure.   The ultraviolet curable inkjet composition according to claim 10, wherein the content of the monofunctional monomer in the ultraviolet curable inkjet composition is 10% by mass or more and 90% by mass or less.   Monomers having the alicyclic structure include tris (2-acryloyloxyethyl) isocyanurate, dicyclopentenyloxyethyl acrylate, adamantyl acrylate, γ-butyrolactone acrylate, N-vinylcaprolactam, N -Vinylpyrrolidone, pentamethylpiperidyl acrylate, tetramethylpiperidyl acrylate, 2-methyl-2-adamantyl acrylate, 2-ethyl-2-adamantyl acrylate, mevalonic acid lactone acrylate, di Methylol tricyclodecane diacrylate, dimethylol dicyclopentane diacrylate, dicyclopentenyl acrylate, dicyclopentanyl acrylate, isobornyl acrylate, cyclohexyl acrylate , Acryloylmorpholine, and Tetrahydrofurfuryl acrylate les - one selected from the group consisting of bets or the claims 8 to include two or more to either ultraviolet ray curable ink composition according to one of 11.   Examples of polymerizable compounds other than the monomer having the alicyclic structure include phenoxyethyl acrylate, 2- (2-vinyloxyethoxy) ethyl acrylate, dipropylene glycol diacrylate, and tripropylene glycol diacrylate. 13. One or more selected from the group consisting of 2-hydroxy-3-phenoxypropyl acrylate and 4-hydroxybutyl acrylate are contained in any one of claims 8 to 12. An ultraviolet curable ink jet composition as described in 1. The ultraviolet curable inkjet composition according to any one of claims 1 to 13, wherein the ultraviolet curable inkjet composition further comprises a substance A having a partial structure represented by the following formula (5).

  15. A recorded matter produced by applying the ultraviolet curable inkjet composition according to any one of claims 1 to 14 onto a recording medium and then irradiating with ultraviolet rays.