JP2014078350A - Negative electrode active material for sodium ion battery and sodium ion battery - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a negative electrode active material for a sodium ion battery capable of improving charge/discharge efficiency.SOLUTION: A negative electrode active material for a sodium ion battery is provided which has NaTiOcrystalline phase and in which the crystallite size of NaTiOcrystalline phase is within a range of 190Å to 520Å.

Description

  The present invention relates to a negative electrode active material for sodium ion batteries capable of improving charge / discharge efficiency, and a sodium ion battery using the same.

  A sodium ion battery is a battery in which Na ions move between a positive electrode and a negative electrode. Since Na is abundant compared to Li, the sodium ion battery has an advantage that it is easy to reduce the cost compared to the lithium ion battery. In general, a sodium ion battery includes a positive electrode active material layer containing a positive electrode active material, a negative electrode active material layer containing a negative electrode active material, and an electrolyte layer formed between the positive electrode active material layer and the negative electrode active material layer. And have.

Na ₂ Ti ₆ O ₁₃ is known as a negative electrode active material used for sodium ion batteries. For example, Non-Patent Document 1 discloses a sodium ion battery using Na ₂ Ti ₆ O ₁₃ as a negative electrode active material. Although not a sodium ion battery, Non-Patent Document 2 discloses a lithium ion battery using Na ₂ Ti ₆ O ₁₃ as a negative electrode active material. The same description is also described in the prior art of Patent Document 1. Patent Document 2 discloses a sodium ion battery using lithium titanate (Li ₄ Ti ₅ O ₁₂ ) as a negative electrode active material. Patent Document 3 discloses that an active material and a carbon material are combined by a ball mill.

JP 2009-117259 A JP 2011-049126 A JP 2007-048682 A

N. D. Trinh et al., “Synthesis, Characterization and Electrochemical Studies of Active Materials for Sodium Ion Batteries”, ECS Transactions, 35 (32) 91-98 (2011) J. C. Perez-Flores et al., “On the Mechanism of Lithium Insertion into A2Ti6O13 (A = Na, Li)”, ECS Transactions, 41 (41) 195-206 (2012)

Non-Patent Document 1 discloses a sodium ion battery using Na ₂ Ti ₆ O ₁₃ as a negative electrode active material. However, this battery has a problem that the initial charge and discharge efficiency is as low as about 27%, as shown in FIG.

  This invention is made | formed in view of the said situation, and it aims at providing the negative electrode active material for sodium ion batteries which can aim at the improvement of charging / discharging efficiency.

In order to achieve the above object, in the present invention, it has a Na ₂ Ti ₆ O ₁₃ crystal phase, and the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is in the range of 190 to 520%. Provided is a negative electrode active material for a sodium ion battery.

According to the present invention, by the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is within a predetermined range may be a negative active material for a sodium ion batteries can be improved charge and discharge efficiency.

  In the present invention, a positive electrode active material layer containing a positive electrode active material, a negative electrode active material layer containing a negative electrode active material, and an electrolyte layer formed between the positive electrode active material layer and the negative electrode active material layer A sodium ion battery, wherein the negative electrode active material is the above-described negative electrode active material for a sodium ion battery.

  According to this invention, it can be set as a sodium ion battery with high charging / discharging efficiency by using the negative electrode active material for sodium ion batteries mentioned above.

  In the above invention, the negative electrode active material layer contains a conductive material composed of a carbon material, and the carbon material has an interlayer distance d002 of 3.50 mm or less, or is obtained by Raman spectroscopic measurement. The G ratio is preferably 0.80 or less. This is because the charge / discharge efficiency can be further increased.

  The negative electrode active material for a sodium ion battery of the present invention has an effect that charge / discharge efficiency can be improved.

It is a schematic sectional drawing which shows an example of the sodium ion battery of this invention. 4 is a result of XRD measurement on the active material obtained in Example 3. FIG. It is a result of the charging / discharging test of the battery for evaluation obtained in Examples 1-5. 6 is a result of a charge / discharge test of an evaluation battery obtained in Example 6. FIG. It is a result of SEM observation of the active material obtained in Examples 3 and 8. 3 is a result of a charge / discharge test of evaluation batteries obtained in Examples 3 and 8. FIG. It is a result of the charging / discharging test (Na desorption capacity with respect to charging / discharging electric current value) of the battery for evaluation obtained in Example 3, 8. FIG. 4 is a result of SEM observation of an active material obtained in Example 9. 3 is a result of a charge / discharge test of evaluation batteries obtained in Examples 3 and 9. FIG.

  Hereinafter, the negative electrode active material for sodium ion batteries and the sodium ion battery of the present invention will be described in detail.

A. First, the negative electrode active material for sodium ion batteries of the present invention will be described. Negative active material for a sodium ion battery of the present _invention has a Na ₂ Ti _{6 O 13} crystal phase, wherein the crystallite size of the _Na 2 _Ti 6 _{O 13} crystal phase is in the range of 190Å~520Å It is what.

According to the present invention, by the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is within a predetermined range may be a negative active material for a sodium ion batteries can be improved charge and discharge efficiency. Here, Non-Patent Document 1 describes that the film formation by electrolytic solution decomposition occurs as a side reaction as a reason why the charge / discharge efficiency is low. However, the present inventor considered that the charge / discharge efficiency could not be explained so low only by the side reaction of film formation, and considered that there may be other reasons. As a result of extensive research, it has been found that the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase affects the charge / discharge efficiency, and the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase falls within a predetermined range. It was confirmed that the charging / discharging efficiency can be improved by setting the inside. Furthermore, as described later, it has been found that not only the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase but also the crystallinity of the carbon material used together with the negative electrode active material affects the charge / discharge efficiency. It was confirmed that the charge / discharge efficiency can be improved by defining the crystallinity.

The negative electrode active material for a sodium ion battery of the present invention has a Na ₂ Ti ₆ O ₁₃ crystal phase. The presence of the Na ₂ Ti ₆ O ₁₃ crystal phase can be confirmed by X-ray diffraction (XRD) measurement or the like. For example, CuKα rays can be used for the XRD measurement. The negative electrode active material for sodium ion batteries of the present invention is usually 2θ = 11.8 °, 14.1 °, 24.5 °, 29.8 °, 30.1 °, 30.5 °, 32.2 °. Typical peaks are observed at positions of 33.5 °, 43.3 °, 44.3 ° and 48.6 °. The positions of these peaks are actually measured values obtained in examples described later, and may be back and forth within a range of ± 0.5 °.

Further, the negative electrode active material for sodium ion battery of the present invention preferably has a large proportion of Na ₂ Ti ₆ O ₁₃ crystal phase, and specifically, preferably contains mainly a Na ₂ Ti ₆ O ₁₃ crystal phase. . Here, “mainly composed of the Na ₂ Ti ₆ O ₁₃ crystal phase” means that the ratio of the Na ₂ Ti ₆ O ₁₃ crystal phase is the highest among all the crystal phases contained in the negative electrode active material for a sodium ion battery. It means big. The ratio of the Na ₂ Ti ₆ O ₁₃ crystal phase contained in the negative electrode active material for sodium ion batteries is preferably 50 mol% or more, more preferably 60 mol% or more, and even more preferably 70 mol% or more. . Moreover, the negative electrode active material for sodium ion batteries of the present invention may be composed of only a Na ₂ Ti ₆ O ₁₃ crystal phase (single-phase active material). In addition, the ratio of the Na ₂ Ti ₆ O ₁₃ crystal phase contained in the negative electrode active material for sodium ion batteries is determined by, for example, a quantitative analysis method by X-ray diffraction (for example, a quantitative method by R value, Rietveld method). Can do.

_Further, the peak intensity of 2 [Theta] = 11.8 ° in the Na ₂ Ti _{6 O 13} crystal phase and _{I A,} the peak intensity of 2 [Theta] = 25.2 ° in the titanium oxide when the _{I B,} of _I B / I _A The value is preferably 0.1 or less, and more preferably 0.01 or less. In addition, _{I B} may be 0.

In the present invention, the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is usually 190 mm or more, preferably 240 mm or more, and more preferably 250 kg or more. This is because if the crystallite size is too small, the proportion of unnecessary crystal phases (for example, crystal phases derived from raw materials) may increase. For example, when an active material having a small crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is synthesized by a solid phase method, it is necessary to lower the firing temperature or shorten the firing time. As a result, for example, the proportion of the crystal phase derived from the raw material such as titanium oxide may increase, and the charge / discharge efficiency may not be sufficiently improved.

On the other hand, the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is usually 520 Å or less, preferably 510 Å or less, and more preferably 500 Å or less. This is because if the crystallite size is too large, the charge / discharge efficiency may decrease. The reason why the charge / discharge efficiency is lowered includes that the Na ion conduction path and the electron conduction path are lengthened, and that the reactive sites are reduced as the specific surface area is reduced. In Non-Patent Document 1, when Na ₂ Ti ₆ O ₁₃ is synthesized, baking is performed at 800 ° C. for 1 day, and then baking is performed at 930 ° C. for 3 days. These firing conditions are higher in firing temperature and longer in firing time than firing conditions in Examples described later. Therefore, the crystallite size of Na ₂ Ti ₆ O ₁₃ obtained in Non-Patent Document 1 is larger than the crystallite size in the present invention.

In addition, the crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase can be calculated from the half width of the peak obtained by XRD measurement. Specifically, the full width at half maximum (FWHM) of the peak at 2θ = 11.8 ° described above can be used to obtain the Scherrer equation.
D = Kλ / (βcosθ)
K: Scherrer constant, λ: wavelength, β: diffraction line broadening depending on crystallite size, θ: diffraction angle 2θ / θ
Although it is difficult to accurately determine the crystallite size of Na ₂ Ti ₆ O ₁₃ from the XRD pattern described in Figure 5 of Non-Patent Document 1, it is a little less than 1 μm because it has a very high peak. It is estimated that it is about.

  In the negative electrode active material for a sodium ion battery of the present invention, the Na insertion potential with respect to metal Na is preferably 1.0 V or less, and more preferably in the range of 0.5 V to 1.0 V. This is because if the Na insertion potential is too low, the precipitation of metal Na may not be sufficiently suppressed, and if the Na insertion potential is too high, the battery voltage may be reduced. In the present invention, the Na insertion potential of the negative electrode active material can be determined by a cyclic voltammetry (CV) method.

  The negative electrode active material for sodium ion batteries of the present invention is preferably combined with a conductive material. This is because rate characteristics can be improved. The conductive material to be combined is not particularly limited as long as it has desired electronic conductivity, and examples thereof include a carbon material and a metal material. Among these, a carbon material is preferable. Specific examples of the carbon material include carbon black such as acetylene black, ketjen black, furnace black, and thermal black; carbon fiber such as VGCF; graphite; hard carbon; coke and the like. Examples of the metal material include Fe, Cu, Ni, and Al. “The negative electrode active material for sodium ion battery and the conductive material are combined” means a state obtained by performing mechanochemical treatment on both. For example, there are a state where both are dispersed so as to be in close contact with each other in nano order, and a state where the other is dispersed so as to be closely attached with each other in nano order on one surface. A chemical bond may exist between the two. The compounding can be confirmed by, for example, SEM observation, TEM observation, TEM-EELS method, X-ray absorption fine structure (XAFS), or the like. Further, examples of the mechanochemical treatment include a treatment capable of imparting mechanical energy, such as a ball mill. Moreover, a commercially available compounding device (for example, Nobilta manufactured by Hosokawa Micron Corporation) or the like can also be used.

  Moreover, when the negative electrode active material for sodium ion batteries is combined with a conductive material, the ratio of the combined conductive material is preferably within a range of, for example, 1% by weight to 30% by weight, and 5% by weight. More preferably, it is in the range of ˜20% by weight. If the ratio of the composite conductive material is too small, the rate characteristics may not be sufficiently improved. If the composite conductive material ratio is too large, the amount of the active material is relatively small. This is because there is a possibility that the capacity decreases. When the composite conductive material is a carbon material, the carbon material preferably has high crystallinity. Specifically, as described later, it is preferable that the carbon material is combined so that the interlayer distance d002 or the D / G ratio becomes a predetermined value.

The shape of the negative electrode active material for sodium ion batteries of the present invention is preferably, for example, particulate. The average particle diameter (D ₅₀ ) is preferably in the range of 1 nm to 100 μm, and more preferably in the range of 10 nm to 30 μm, for example.

  Moreover, the manufacturing method of the negative electrode active material for sodium ion batteries of this invention will not be specifically limited if it is a method which can obtain the active material mentioned above, For example, a solid-phase method can be mentioned. As a specific example of the solid phase method, there is a method of preparing a raw material composition in which a Na source (for example, sodium carbonate) and a Ti source (for example, titanium oxide) are mixed at a predetermined ratio, and firing the raw material composition. it can. The crystallite size can be controlled by adjusting the firing temperature and firing time, for example. When the firing temperature is high and the firing time is long, the crystallite size tends to increase. The firing temperature is preferably in the range of 700 ° C. to 900 ° C., for example, and more preferably in the range of 750 ° C. to 850 ° C. This is because if the firing temperature is too low, solid phase reaction may not occur, and if the firing temperature is too high, an unnecessary crystal phase may be generated. The firing time is preferably in the range of 20 hours to 80 hours, for example, and more preferably in the range of 40 hours to 60 hours. The firing atmosphere is not particularly limited, and may be an atmosphere in which oxygen is present, an inert gas atmosphere, or a reduced pressure (vacuum) atmosphere.

B. Next, the sodium ion battery of the present invention will be described. The sodium ion battery of the present invention includes a positive electrode active material layer containing a positive electrode active material, a negative electrode active material layer containing a negative electrode active material, and an electrolyte formed between the positive electrode active material layer and the negative electrode active material layer. The negative electrode active material is a sodium ion battery negative electrode active material as described above.

  FIG. 1 is a schematic cross-sectional view showing an example of the sodium ion battery of the present invention. A sodium ion battery 10 shown in FIG. 1 includes a positive electrode active material layer 1, a negative electrode active material layer 2, an electrolyte layer 3 formed between the positive electrode active material layer 1 and the negative electrode active material layer 2, and a positive electrode active material. It has a positive electrode current collector 4 that collects current from the layer 1, a negative electrode current collector 5 that collects current from the negative electrode active material layer 2, and a battery case 6 that houses these members. The sodium ion battery of the present invention is characterized in that the negative electrode active material layer 2 contains the negative electrode active material described in “A. Negative electrode active material for sodium ion battery”.

According to this invention, it can be set as a sodium ion battery with high charging / discharging efficiency by using the negative electrode active material for sodium ion batteries mentioned above.
Hereinafter, the sodium ion battery of the present invention will be described for each configuration.

1. Negative electrode active material layer First, the negative electrode active material layer in the present invention will be described. The negative electrode active material layer in the present invention is a layer containing at least a negative electrode active material. The negative electrode active material layer may contain at least one of a conductive material, a binder, and a solid electrolyte material in addition to the negative electrode active material.

  The negative electrode active material in the present invention is usually the negative electrode active material described in “A. Negative electrode active material for sodium ion battery” above.

  The negative electrode active material layer in the present invention preferably contains a conductive material. The conductive material may be combined with the negative electrode active material, or may be present in a state mixed with the negative electrode active material in the negative electrode active material layer instead of being combined. It may be. The conductive material is not particularly limited as long as it has desired electronic conductivity, and is the same as described in the above-mentioned “A. Negative electrode active material for sodium ion battery”. Especially, it is preferable that a electrically conductive material is a carbon material, and it is especially preferable that the crystallinity of a carbon material is high. This is because if the carbon material has high crystallinity, Na ions are hardly inserted into the carbon material, and the irreversible capacity due to the insertion of Na ions can be reduced. As a result, the charge / discharge efficiency can be further improved. The crystallinity of the carbon material can be defined by, for example, the interlayer distance d002 and the D / G ratio.

  The carbon material preferably has an interlayer distance d002 of, for example, 3.54 mm or less, more preferably 3.50 mm or less, and further preferably 3.40 mm or less. This is because a carbon material with high crystallinity can be obtained. On the other hand, the interlayer distance d002 is usually 3.36 mm or more. The interlayer distance d002 refers to the surface spacing of the (002) plane in the carbon material, and specifically corresponds to the distance between the graphene layers. The interlayer distance d002 can be obtained from a peak obtained by, for example, an X-ray diffraction (XRD) method using CuKα rays.

The carbon material preferably has a D / G ratio determined by Raman spectroscopy of, for example, 0.90 or less, more preferably 0.80 or less, and even more preferably 0.50 or less, It is especially preferable that it is 0.20 or less. This is because a carbon material with high crystallinity can be obtained. The D / G ratio is a D-band derived from a defect structure near 1350 cm ^{−1 with} respect to a peak intensity of G-band derived from a graphite structure near 1590 cm ⁻¹ observed in Raman spectroscopy (wavelength 532 nm). The peak intensity.

  The binder is not particularly limited as long as it is chemically and electrically stable. For example, a fluorine-based binder such as polyvinylidene fluoride (PVDF) and polytetrafluoroethylene (PTFE), Examples thereof include rubber binders such as styrene butadiene rubber, olefin binders such as polypropylene (PP) and polyethylene (PE), and cellulose binders such as carboxymethyl cellulose (CMC). The solid electrolyte material is not particularly limited as long as it has desired ionic conductivity, and examples thereof include an oxide solid electrolyte material and a sulfide solid electrolyte material. The solid electrolyte material will be described in detail in “3. Electrolyte layer” described later.

  The content of the negative electrode active material in the negative electrode active material layer is preferably larger from the viewpoint of capacity, for example, in the range of 60 wt% to 99 wt%, particularly in the range of 70 wt% to 95 wt%. Is preferred. Further, the content of the conductive material is preferably less as long as the desired electronic conductivity can be ensured, for example, in the range of 5 wt% to 80 wt%, particularly in the range of 10 wt% to 40 wt%. It is preferable. If the content of the conductive material is too low, sufficient electronic conductivity may not be obtained. If the content of the conductive material is too high, the amount of the active material is relatively reduced and the capacity is reduced. This is because there is a possibility that it will end up. Further, the content of the binder is preferably less as long as the negative electrode active material and the like can be stably fixed, and is preferably in the range of 1% by weight to 40% by weight, for example. If the binder content is too low, sufficient binding properties may not be obtained. If the binder content is too high, the amount of active material is relatively reduced and the capacity is reduced. This is because there is a possibility that it will end up. Further, the content of the solid electrolyte material is preferably smaller as long as desired ion conductivity can be ensured, and is preferably in the range of 1 wt% to 40 wt%, for example. If the content of the solid electrolyte material is too small, sufficient ion conductivity may not be obtained. If the content of the solid electrolyte material is too large, the amount of the active material is relatively reduced and the capacity is reduced. This is because there is a possibility that it will end up.

  The thickness of the negative electrode active material layer varies greatly depending on the configuration of the battery, but is preferably in the range of 0.1 μm to 1000 μm, for example.

2. Next, the positive electrode active material layer in the present invention will be described. The positive electrode active material layer in the present invention is a layer containing at least a positive electrode active material. The positive electrode active material layer may contain at least one of a conductive material, a binder, and a solid electrolyte material in addition to the positive electrode active material.

Examples of the positive electrode active material include a layered active material, a spinel active material, and an olivine active material. Specific examples of the positive electrode active material include NaFeO ₂ , NaNiO ₂ , NaCoO ₂ , NaMnO ₂ , NaVO ₂ , Na (Ni _X Mn _1-X ) O ₂ (0 <X <1), Na (Fe _X Mn _{1− X 2} ) O ₂ (0 <X <1), NaVPO ₄ F, Na ₂ FePO ₄ F, Na ₃ V ₂ (PO ₄ ) _{3 and the} like.

The shape of the positive electrode active material is preferably particulate. Further, the average particle diameter (D ₅₀ ) of the positive electrode active material is, for example, preferably in the range of 1 nm to 100 μm, and more preferably in the range of 10 nm to 30 μm. The content of the positive electrode active material in the positive electrode active material layer is preferably higher from the viewpoint of capacity, for example, in the range of 60 wt% to 99 wt%, particularly in the range of 70 wt% to 95 wt%. Is preferred. The type and content of the conductive material, binder, and solid electrolyte material used for the positive electrode active material layer are the same as those described for the negative electrode active material layer described above. Omitted. The thickness of the positive electrode active material layer varies greatly depending on the configuration of the battery, but is preferably in the range of 0.1 μm to 1000 μm, for example.

3. Electrolyte Layer Next, the electrolyte layer in the present invention will be described. The electrolyte layer in the present invention is a layer formed between the positive electrode active material layer and the negative electrode active material layer. Ion conduction between the positive electrode active material and the negative electrode active material is performed via the electrolyte contained in the electrolyte layer. The form of the electrolyte layer is not particularly limited, and examples thereof include a liquid electrolyte layer, a gel electrolyte layer, and a solid electrolyte layer.

The liquid electrolyte layer is usually a layer using a non-aqueous electrolyte. The nonaqueous electrolytic solution usually contains a sodium salt and a nonaqueous solvent. Examples of sodium salts include inorganic sodium salts such as NaPF ₆ , NaBF ₄ , NaClO ₄ and NaAsF ₆ ; and NaCF ₃ SO ₃ , NaN (CF ₃ SO ₂ ) ₂ , NaN (C ₂ F ₅ SO ₂ ) ₂ , NaN Examples thereof include organic sodium salts such as (FSO ₂ ) ₂ and NaC (CF ₃ SO ₂ ) ₃ . The nonaqueous solvent is not particularly limited as long as it dissolves a sodium salt. For example, as a high dielectric constant solvent, cyclic ester (cyclic carbonate) such as ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), γ-butyrolactone, sulfolane, N-methylpyrrolidone (NMP), 1, And 3-dimethyl-2-imidazolidinone (DMI). On the other hand, as low-viscosity solvents, chain esters (chain carbonate) such as dimethyl carbonate (DMC), diethyl carbonate (DEC) and ethyl methyl carbonate (EMC), acetates such as methyl acetate and ethyl acetate, 2-methyl Mention may be made of ethers such as tetrahydrofuran. You may use the mixed solvent which mixed the high dielectric constant solvent and the low-viscosity solvent. The concentration of the sodium salt in the nonaqueous electrolytic solution is, for example, in the range of 0.3 mol / L to 5 mol / L, and preferably in the range of 0.8 mol / L to 1.5 mol / L. This is because if the sodium salt concentration is too low, there is a possibility that the capacity will decrease at the high rate, and if the sodium salt concentration is too high, the viscosity will increase and the capacity may decrease at low temperatures. In the present invention, a low volatile liquid such as an ionic liquid may be used as the nonaqueous electrolytic solution.

  The gel electrolyte layer can be obtained, for example, by adding a polymer to the non-aqueous electrolyte and gelling. Specifically, gelation can be performed by adding a polymer such as polyethylene oxide (PEO), polyacrylonitrile (PAN), or polymethyl methacrylate (PMMA) to the nonaqueous electrolytic solution.

The solid electrolyte layer is a layer made of a solid electrolyte material. The solid electrolyte material is not particularly limited as long as it has Na ion conductivity, and examples thereof include oxide solid electrolyte materials and sulfide solid electrolyte materials. Examples of the oxide solid electrolyte material include Na ₃ Zr ₂ Si ₂ PO ₁₂ , β-alumina solid electrolyte (Na ₂ O-11Al ₂ O ₃ etc.) and the like. Examples of the sulfide solid electrolyte material include Na ₂ S—P ₂ S ₅ .

  The solid electrolyte material in the present invention may be amorphous or crystalline. The shape of the solid electrolyte material is preferably particulate. The average particle diameter (D50) of the solid electrolyte material is preferably in the range of 1 nm to 100 μm, for example, and in particular in the range of 10 nm to 30 μm.

  The thickness of the electrolyte layer varies greatly depending on the type of electrolyte and the configuration of the battery. For example, the thickness of the electrolyte layer is preferably in the range of 0.1 μm to 1000 μm, and more preferably in the range of 0.1 μm to 300 μm.

4). Other Configurations The sodium ion battery of the present invention has at least the negative electrode active material layer, the positive electrode active material layer, and the electrolyte layer described above. Furthermore, it usually has a positive electrode current collector for collecting current of the positive electrode active material layer and a negative electrode current collector for collecting current of the negative electrode active material layer. Examples of the material for the positive electrode current collector include SUS, aluminum, nickel, iron, titanium, and carbon. On the other hand, examples of the material for the negative electrode current collector include SUS, copper, nickel, and carbon. Examples of the shapes of the positive electrode current collector and the negative electrode current collector include a foil shape, a mesh shape, and a porous shape.

  The sodium ion battery of the present invention may have a separator between the positive electrode active material layer and the negative electrode active material layer. This is because a battery with higher safety can be obtained. Examples of the material for the separator include porous films such as polyethylene (PE), polypropylene (PP), cellulose, and polyvinylidene fluoride; and nonwoven fabrics such as a resin nonwoven fabric and a glass fiber nonwoven fabric. Further, the separator may have a single layer structure (for example, PE or PP), or may have a laminated structure (for example, PP / PE / PP). Moreover, the battery case of a general battery can be used for the battery case used for this invention. Examples of the battery case include a SUS battery case.

5. Sodium ion battery The sodium ion battery of this invention will not be specifically limited if it has the positive electrode active material layer, negative electrode active material layer, and electrolyte layer which were mentioned above. The sodium ion battery of the present invention may be a battery in which the electrolyte layer is a solid electrolyte layer, a battery in which the electrolyte layer is a liquid electrolyte layer, or a battery in which the electrolyte layer is a gel electrolyte layer. May be. Further, the sodium ion battery of the present invention may be a primary battery or a secondary battery, but among them, a secondary battery is preferable. This is because it can be repeatedly charged and discharged and is useful, for example, as an in-vehicle battery. In addition, examples of the shape of the sodium ion battery of the present invention include a coin type, a laminate type, a cylindrical type, and a square type. Moreover, the manufacturing method of a sodium ion battery is not specifically limited, It is the same as the manufacturing method in a general sodium ion battery.

  The present invention is not limited to the above embodiment. The above-described embodiment is an exemplification, and the present invention has substantially the same configuration as the technical idea described in the claims of the present invention, and any device that exhibits the same function and effect is the present invention. It is included in the technical scope of the invention.

  Hereinafter, the present invention will be described in more detail with reference to examples.

[Example 1]
(Synthesis of active material)
As starting materials, sodium carbonate (Na ₂ CO ₃ ) and titanium oxide (anatase, TiO ₂ ) were weighed at a molar ratio of Na ₂ CO ₃ : TiO ₂ = 1: 6 and mixed in ethanol. Next, ethanol was removed by drying, molded into pellets, and fired in a muffle furnace at 700 ° C. for 60 hours. This _gave an active material having an Na ₂ Ti _{6 O 13} crystal phase.

(Production of evaluation battery)
An evaluation battery using the obtained active material was produced. First, the obtained active material, a conductive material (acetylene black, interlayer distance d002 = 3.54 mm, D / G ratio = 0.87), and a binder (polyvinylidene fluoride, PVDF) : Conductive material: Binder = Mixing at a weight ratio of 85: 10: 5 and kneading gave a paste. Next, the obtained paste was applied onto a copper foil with a doctor blade, dried, and pressed to obtain a test electrode having a thickness of 20 μm.

Thereafter, a CR2032-type coin cell was used, the test electrode was used as a working electrode, metal Na was used as a counter electrode, and a polyethylene / polypropylene / polyethylene porous separator (thickness 25 μm) was used as a separator. As the electrolytic solution, a solution in which NaPF ₆ was dissolved at a concentration of 1 mol / L in a solvent in which EC (ethylene carbonate) and DEC (diethyl carbonate) were mixed in the same volume was used. Thereby, a battery for evaluation was obtained.

[Example 2]
An active material was obtained in the same manner as in Example 1 except that firing was performed at 800 ° C. for 30 hours. Further, an evaluation battery was obtained in the same manner as in Example 1 except that the obtained active material was used.

[Example 3]
An active material was obtained in the same manner as in Example 1 except that firing was performed at 800 ° C. for 60 hours. Further, an evaluation battery was obtained in the same manner as in Example 1 except that the obtained active material was used.

[Example 4]
An active material was obtained in the same manner as in Example 1 except that firing was performed at 900 ° C. for 30 hours. Further, an evaluation battery was obtained in the same manner as in Example 1 except that the obtained active material was used.

[Example 5]
An active material was obtained in the same manner as in Example 1 except that firing was performed at 900 ° C. for 60 hours. Further, an evaluation battery was obtained in the same manner as in Example 1 except that the obtained active material was used.

[Evaluation 1]
(XRD measurement)
X-ray diffraction (XRD) measurement using CuKα rays was performed on the active materials obtained in Examples 1 to 5. As a typical example, the results of Example 3 are shown in FIG. As shown in FIG. 2, 2θ = 11.8 °, 14.1 °, 24.5 °, 29.8 °, 30.1 °, 30.5 °, 32.2 °, 33.5 °, 43 Typical peaks indicating a Na ₂ Ti ₆ O ₁₃ crystal phase were observed at positions of 3 °, 44.3 °, and 48.6 °. The crystallite size was calculated from the full width at half maximum (FWHM) of the peak at 2θ = 11.8 ° using the Scherrer equation described above. _Further, the peak intensity of 2 [Theta] = 11.8 ° in the Na ₂ Ti _{6 O 13} crystal phase and _{I A,} the peak intensity of 2 [Theta] = 25.2 ° in the titanium oxide when the _{I B,} of _I B / I _A The value was 0.08.

(Charge / discharge test)
A charge / discharge test was performed on the evaluation batteries obtained in Examples 1 to 5. Specifically, the initial charge / discharge efficiency was determined under the conditions of an environmental temperature of 25 ° C., a current value of 6 mA / g, and a voltage range of 0.5 V to 2.5 V. The results are shown in Table 1 and FIG.

  As shown in Table 1 and FIG. 3, it was revealed that the charge / discharge efficiency is improved when the crystallite size is in the range of 190 to 520 mm. In particular, when the crystallite size is in the range of 250 to 500 mm, charge / discharge efficiency exceeding 80% can be realized.

[Example 6]
An evaluation battery was obtained in the same manner as in Example 3 except that graphite (interlayer distance d002 = 3.36 mm, D / G ratio = 0.12) was used as the conductive material.

[Example 7]
An evaluation battery was obtained in the same manner as in Example 3 except that VGCF (interlayer distance d002 = 3.37 mm, D / G ratio = 0.07) was used as the conductive material.

[Evaluation 2]
(Charge / discharge test)
A charge / discharge test was performed on the evaluation batteries obtained in Examples 3, 6, and 7. Specifically, the initial charge / discharge efficiency was determined under the conditions of an environmental temperature of 25 ° C., a current value of 6 mA / g, and a voltage range of 0.5 V to 2.5 V. The results are shown in Table 2.

  As shown in Table 2, it became clear that the higher the crystallinity of the conductive material (the smaller the interlayer distance d002 and the smaller the D / G ratio), the better the charge / discharge efficiency. FIG. 4 shows the result of Example 6 in which the charge / discharge efficiency was highest.

[Example 8]
The active material obtained in Example 3 and acetylene black (interlayer distance d002 = 3.54Å, D / G ratio = 0.87) were mixed so that the weight ratio of active material: acetylene black = 90: 10 was obtained. These were weighed, and these mixtures were placed in a ZrO ₂ pot and ball milled (180 rpm × 24 hours). Thereby, an active material in which acetylene black was combined was obtained. An evaluation battery was obtained in the same manner as in Example 3, except that the obtained composite active material was used.

[Evaluation 3]
(SEM observation)
SEM observation of the active material obtained in Examples 3 and 8 was performed. The result is shown in FIG. As shown in FIG. 5A, in Example 8, it was confirmed that the active material and acetylene black were combined.

(Charge / discharge test)
A charge / discharge test was performed on the evaluation batteries obtained in Examples 3 and 8. Specifically, it was performed under the conditions of an environmental temperature of 25 ° C. and a voltage range of 0.5 V to 2.5 V. The current value was changed to 6 mA / g, 30 mA / g, 150 mA / g, and 750 mA / g. The results are shown in FIGS. As shown in FIGS. 6 and 7, it was confirmed that Example 8 was superior to Example 3 in terms of capacity, rate characteristics, and cycle characteristics.

[Example 9]
The active material obtained in Example 3 and graphite (interlayer distance d002 = 3.36 mm, D / G ratio = 0.12) were weighed so that the weight ratio of active material: graphite = 90: 10 was obtained. These mixtures were placed in a ZrO ₂ pot and subjected to ball milling (180 rpm × 24 hours). Thereby, an active material in which graphite was combined was obtained. An evaluation battery was obtained in the same manner as in Example 3, except that the obtained composite active material was used.

[Evaluation 4]
(SEM observation)
SEM observation of the active material obtained in Example 9 was performed. The result is shown in FIG. As shown in FIG. 8, in Example 9, it was confirmed that the active material and graphite were combined.

(Charge / discharge test)
A charge / discharge test was performed on the evaluation batteries obtained in Examples 3 and 9. Specifically, it was performed under conditions of an environmental temperature of 25 ° C. and a voltage range of 10 mV to 2.5 V. The current value was 6 mA / g. The result is shown in FIG. As shown in FIG. 9, it was confirmed that Example 9 was superior to Example 3 in terms of capacity retention rate.

DESCRIPTION OF SYMBOLS 1 ... Positive electrode active material layer 2 ... Negative electrode active material layer 3 ... Electrolyte layer 4 ... Positive electrode collector 5 ... Negative electrode collector 6 ... Battery case 10 ... Sodium ion battery

Claims (3)

Having a Na ₂ Ti ₆ O ₁₃ crystal phase,
A negative electrode active material for a sodium ion battery, wherein a crystallite size of the Na ₂ Ti ₆ O ₁₃ crystal phase is in a range of 190 to 520 Å. A sodium ion battery having a positive electrode active material layer containing a positive electrode active material, a negative electrode active material layer containing a negative electrode active material, and an electrolyte layer formed between the positive electrode active material layer and the negative electrode active material layer There,
A sodium ion battery, wherein the negative electrode active material is the negative electrode active material for sodium ion batteries according to claim 1. The negative electrode active material layer contains a conductive material composed of a carbon material,
3. The sodium ion battery according to claim 2, wherein the carbon material has an interlayer distance d002 of 3.50 mm or less or a D / G ratio obtained by Raman spectroscopy of 0.80 or less.