JP2013023593A - Thermally-conductive molded article - Google Patents
Thermally-conductive molded article Download PDFInfo
- Publication number
- JP2013023593A JP2013023593A JP2011160116A JP2011160116A JP2013023593A JP 2013023593 A JP2013023593 A JP 2013023593A JP 2011160116 A JP2011160116 A JP 2011160116A JP 2011160116 A JP2011160116 A JP 2011160116A JP 2013023593 A JP2013023593 A JP 2013023593A
- Authority
- JP
- Japan
- Prior art keywords
- dialkyl carbonate
- weight
- viscosity
- thermally conductive
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、発熱する電子部品に貼付してその電子部品の放熱や冷却という熱対策部材として用いる熱伝導性成形体に関する。 The present invention relates to a heat conductive molded body that is attached to a heat generating electronic component and used as a heat countermeasure member for heat dissipation and cooling of the electronic component.
粘度の低い液状ポリマーに多量の熱伝導性充填材を混合して液状混合組成物とし、この液状混合組成物を所定の形状に硬化させることで、熱伝導性の高い熱伝導性成形体が得られることが知られている。
こうした液状ポリマーとして液状シリコーンが好適に用いられていたが、低分子シロキサンによる接点不良を誘発するおそれがあることなどから、非シリコーン系の液状ポリマーに代替することへの市場の要求が強くなっている。こうした要求に対して、特開2006−312708号公報(特許文献1)には、非シリコーン系の液状ポリマーとしてポリ−α−オレフィン系樹脂を用いた例が記載されている。
A large amount of heat conductive filler is mixed with a low viscosity liquid polymer to obtain a liquid mixed composition, and the liquid mixed composition is cured into a predetermined shape, thereby obtaining a heat conductive molded body having high heat conductivity. It is known that
Liquid silicone has been suitably used as such a liquid polymer, but there is a risk of inducing contact failure due to low-molecular-weight siloxane, and the market demand for replacing it with a non-silicone liquid polymer has increased. Yes. In response to such a requirement, Japanese Patent Laid-Open No. 2006-312708 (Patent Document 1) describes an example in which a poly-α-olefin resin is used as a non-silicone liquid polymer.
しかしながら、熱伝導率を高くするためには熱伝導性充填材を多量に含有させる必要があるが、熱伝導性充填材を高充填した液状ポリマーは粘度が高くなって製造が困難になる。一方、粘度を下げるために可塑剤を多量に添加するとオイルブリードが起こるという課題があった。また、低粘度の可塑剤を選択すると引火点が低く熱伝導性成形体とした場合に難燃性が低下するという課題もあった。 However, in order to increase the thermal conductivity, it is necessary to contain a large amount of a thermally conductive filler, but a liquid polymer highly filled with a thermally conductive filler has a high viscosity and is difficult to produce. On the other hand, there is a problem that oil bleeding occurs when a large amount of plasticizer is added to lower the viscosity. In addition, when a plasticizer having a low viscosity is selected, there is a problem in that flame retardancy is lowered when a flash point is low and a heat conductive molded body is obtained.
そこで本発明は、熱伝導性成形体の原料となる、液状ポリマーに熱伝導性充填材を含有させた液状混合組成物の粘度を低く抑えることができ、且つオイルブリードを抑制した熱伝導性成形体を提供することを目的とする。また、難燃性に優れた熱伝導性成形体を提供することを目的とする。 Therefore, the present invention can reduce the viscosity of a liquid mixed composition containing a heat conductive filler in a liquid polymer, which is a raw material of a heat conductive molded body, and can suppress oil bleed. The purpose is to provide a body. Moreover, it aims at providing the heat conductive molded object excellent in the flame retardance.
上記目的を達成すべく本発明は以下のように構成される。
高分子マトリクスと、可塑剤と、熱伝導性充填材とを含む熱伝導性成形体について、高分子マトリクスが、オレフィン系液状樹脂の硬化体でなり、可塑剤が、炭酸ジアルキルと引火点250℃以上の非シリコーン系オイルとを含んでなり、炭酸ジアルキルと非シリコーン系オイルの合計に対する炭酸ジアルキルの重量比率が0.05以上0.85未満であり、且つ炭酸ジアルキルの含有量が前記高分子マトリクス100重量部に対して100重量部未満であることを特徴とする熱伝導性成形体である。
In order to achieve the above object, the present invention is configured as follows.
About the heat conductive molded object containing a polymer matrix, a plasticizer, and a heat conductive filler, a polymer matrix consists of a hardening body of an olefin liquid resin, and a plasticizer is dialkyl carbonate and
可塑剤に炭酸ジアルキルと引火点が250℃以上の非シリコーン系オイルとを含み、炭酸ジアルキルと引火点250℃以上の非シリコーン系オイルとの合計に対する炭酸ジアルキルの重量比率を0.05以上0.85未満としたため、難燃性に優れ、オイルブリードが少なく熱伝導性充填材を高充填させることが可能な熱伝導性成形体とすることができる。 The plasticizer contains a dialkyl carbonate and a non-silicone oil having a flash point of 250 ° C. or higher, and the weight ratio of the dialkyl carbonate to the total of the dialkyl carbonate and the non-silicone oil having a flash point of 250 ° C. or higher is 0.05 or more and 0.0. Since it was less than 85, it can be set as the heat conductive molded object which is excellent in a flame retardance, has few oil bleeds, and can be highly filled with a heat conductive filler.
炭酸ジアルキルを混合することで可塑剤の含有量を少なくしても液状混合組成物の粘度を低くすることができる。よって、オイルブリードを抑制することができる程度に可塑剤の含有量を少なくすることができる。また熱伝導性成形体を製造する時に気泡を除去し易く、高品質の熱伝導性成形体を容易に製造することができる。換言すれば、液状混合組成物の粘度を製造可能な範囲で最大に設定した場合に、引火点250℃以上の非シリコーン系オイルのみを可塑剤として用いた場合よりも熱伝導性充填材を高充填することができるということであり、熱伝導性成形体の熱伝導率を高めることができる。 By mixing dialkyl carbonate, the viscosity of the liquid mixture composition can be lowered even if the plasticizer content is reduced. Therefore, the plasticizer content can be reduced to such an extent that oil bleed can be suppressed. Moreover, when producing a heat conductive molded body, it is easy to remove bubbles, and a high quality heat conductive molded body can be easily manufactured. In other words, when the viscosity of the liquid mixture composition is set to the maximum within the manufacturable range, the heat conductive filler is higher than when only non-silicone oil having a flash point of 250 ° C. or higher is used as the plasticizer. That is, the thermal conductivity of the thermally conductive molded body can be increased.
また、炭酸ジアルキルの含有量を高分子マトリクス100重量部に対し100重量部未満としたため、難燃性に優れた熱伝導性成形体とすることができる。炭酸ジアルキルの含有量が100重量部を超えると、熱伝導性成形体の難燃性が低下するおそれがあるためである。 Moreover, since the content of dialkyl carbonate is less than 100 parts by weight with respect to 100 parts by weight of the polymer matrix, a thermally conductive molded article having excellent flame retardancy can be obtained. This is because if the content of dialkyl carbonate exceeds 100 parts by weight, the flame retardancy of the thermally conductive molded article may be reduced.
炭酸ジアルキルと非シリコーン系オイルの合計の含有量が高分子マトリクス100重量部に対して121重量部〜257重量部とすることができる。121重量部より少ないと、熱伝導性充填材を高充填することができず、熱伝導性成形体の熱伝導率を十分に高めることができない。一方、257重量部を超えるとオイルブリードが発生するおそれがある。 The total content of the dialkyl carbonate and the non-silicone oil can be 121 parts by weight to 257 parts by weight with respect to 100 parts by weight of the polymer matrix. When the amount is less than 121 parts by weight, the heat conductive filler cannot be highly filled, and the heat conductivity of the heat conductive molded body cannot be sufficiently increased. On the other hand, if it exceeds 257 parts by weight, oil bleed may occur.
熱伝導性充填材には金属水酸化物を含むものとすることができる。換言すれば、熱伝導性充填材の一部に金属水酸化物を含むものとすることができ、また、熱伝導性充填材の全てを金属水酸化物とすることができる。熱伝導性充填材に金属水酸化物を用いることで、熱伝導性成形体の難燃性を高めることができ、また、熱伝導性成形体に占める熱伝導性充填材の量を相対的に高めることができる。 The thermally conductive filler may include a metal hydroxide. In other words, a part of the thermally conductive filler can include a metal hydroxide, and all of the thermally conductive filler can be a metal hydroxide. By using a metal hydroxide for the thermally conductive filler, the flame retardancy of the thermally conductive molded body can be increased, and the amount of thermally conductive filler in the thermally conductive molded body is relatively Can be increased.
また、高分子マトリクスはポリイソブチレンを主成分とすることが好適である。ポリイソブチレンは、オレフィン系液状樹脂の中でも比較的耐熱性が高く、機械的強度が高いからである。そのため、高温での使用や、長期の使用に好適な熱伝導性成形体とすることができる。 The polymer matrix preferably contains polyisobutylene as a main component. This is because polyisobutylene has relatively high heat resistance and high mechanical strength among olefin liquid resins. Therefore, it can be set as the heat conductive molded object suitable for use at high temperature or long-term use.
また、引火点が250℃以上の非シリコーン系オイルをパラフィンオイルとすることができる。パラフィンオイルと炭酸ジアルキルを組合せた可塑剤は、それぞれの単独の粘度の平均値よりも低粘度になるという相乗効果があるため、難燃性の低下を抑えながら、効果的に低粘度化することができるためである。
そして、こうした組合せを採用することで、熱伝導性をより高めた配合において、作業性の良い液状混合組成物を得ることでき、製造が容易で、可塑剤のオイルブリードを抑制した難燃性の高い熱伝導性成形体を得ることができる。
Non-silicone oil having a flash point of 250 ° C. or higher can be used as paraffin oil. Plasticizers that combine paraffin oil and dialkyl carbonate have a synergistic effect of lowering the average viscosity of each individual component, so the viscosity can be effectively reduced while suppressing the reduction in flame retardancy. It is because it can do.
And by adopting such a combination, a liquid mixed composition with good workability can be obtained in a formulation with higher thermal conductivity, easy to manufacture, and flame-retardant with suppressed plasticizer oil bleeding. A high heat conductive molded body can be obtained.
本発明の熱伝導性成形体によれば、熱伝導性充填材を高充填しても作業性の良い液状混合組成物を得ることでき、製造が容易で、オイルブリードが抑制された熱伝導性成形体である。また、難燃性に優れた熱伝導性成形体である。 According to the thermally conductive molded body of the present invention, it is possible to obtain a liquid mixed composition having good workability even when highly filled with a thermally conductive filler, easy manufacture, and thermal conductivity with suppressed oil bleed. It is a molded body. Moreover, it is a heat conductive molded body excellent in flame retardancy.
本発明の熱伝導性成形体は、オレフィン系液状樹脂でなる高分子マトリクスと、炭酸ジアルキルと引火点250℃以上の非シリコーン系オイルとを所定割合で含む可塑剤と、熱伝導性充填材とでなる液状混合組成物を硬化した硬化体である。以下これらの成分について説明する。 The thermally conductive molded article of the present invention includes a polymer matrix made of an olefinic liquid resin, a plasticizer containing a dialkyl carbonate and a non-silicone oil having a flash point of 250 ° C. or higher in a predetermined ratio, and a thermally conductive filler. It is the hardening body which hardened the liquid mixed composition consisting of. Hereinafter, these components will be described.
高分子マトリクス: 高分子マトリクスにはオレフィン系液状樹脂が用いられる。オレフィン系液状樹脂は非シリコーン系高分子であることから、低分子シロキサンに起因する接点障害などが発生するおそれがない。また、オレフィン系液状樹脂は、非シリコーン系高分子の中でも熱伝導性充填材を混合する製造段階で脱泡性が良く、ポットライフが比較的長い硬化系を調整することができる。また、熱伝導性成形体として必要な耐熱性を有することができる。
分子内に反応性の官能基を有する液状樹脂を用いたことで、液状混合組成物を硬化して熱伝導性成形体を形成することができる。具体的には、アリル基、ビニル基などを有するオレフィン系液状樹脂を用いることができ、反応性とポットライフのバランスからアリル末端の液状樹脂とすることが好ましい。
Polymer matrix : An olefin liquid resin is used for the polymer matrix. Since the olefin-based liquid resin is a non-silicone polymer, there is no risk of contact failure due to low-molecular siloxane. In addition, the olefin-based liquid resin has a good defoaming property in a production stage where a heat conductive filler is mixed among non-silicone polymers, and can adjust a curing system having a relatively long pot life. Moreover, it can have heat resistance required as a heat conductive molded object.
By using a liquid resin having a reactive functional group in the molecule, the liquid mixed composition can be cured to form a thermally conductive molded body. Specifically, an olefin-based liquid resin having an allyl group, a vinyl group, or the like can be used, and an allyl-terminated liquid resin is preferable from the balance between reactivity and pot life.
液状樹脂の数平均分子量は、好ましくは1000〜20000の範囲であり、より好ましくは5000〜7000の範囲である。数平均分子量が1000未満では、硬化後に充分な架橋構造をとることができず、熱伝導性成形体の機械的強度が低下して、脆くなるおそれがある。一方、数平均分子量が20000を越えると、粘度が高くなり、熱伝導性充填材を高充填し難くなる。
こうしたオレフィン系液状樹脂としては、ポリイソブチレン、エチレン−プロピレン系ポリマーを挙げることができる。
The number average molecular weight of the liquid resin is preferably in the range of 1000 to 20000, and more preferably in the range of 5000 to 7000. If the number average molecular weight is less than 1000, a sufficient cross-linked structure cannot be obtained after curing, and the mechanical strength of the thermally conductive molded body may be reduced, which may make it brittle. On the other hand, when the number average molecular weight exceeds 20000, the viscosity becomes high and it becomes difficult to highly fill the heat conductive filler.
Examples of such olefinic liquid resins include polyisobutylene and ethylene-propylene polymers.
熱伝導性充填材: 熱伝導性充填材としては、高い熱伝導性を有する金属、金属酸化物、金属窒化物、金属炭化物、金属水酸化物、炭素質フィラーなどを用いることができる。具体的には、酸化アルミニウム、酸化マグネシウム、酸化亜鉛、窒化ホウ素、窒化アルミニウム、炭化ケイ素、水酸化アルミニウム、水酸化マグネシウム、炭素繊維、黒鉛などが挙げられる。これらの熱伝導性充填材の中で、電気絶縁性が要求される用途では、金属酸化物、金属窒化物、金属炭化物、金属水酸化物などが好適であり、またこれらの中でも難燃性を高める観点から金属水酸化物を用いることが好ましい。一方、熱伝導性を高める観点からは炭素繊維を用いることが好ましい。炭素繊維はまた、反磁性体であり磁場により任意の方向に均一に配向させやすい。磁場により熱伝導性充填材を配向させる場合には、磁場発生装置として、具体的には、永久磁石や電磁石、超伝導磁石などを用いることができる。
熱伝導性充填材は一の種類を単独で用いてもよいが、複数の種類を混合して用いることで熱伝導性や難燃性をバランスよく高めることができる。また、絶縁性の付与や充填性の向上及び劣化の抑制などのために表面処理を施した熱伝導性充填材を用いてもよい。
Thermally conductive filler : As the thermally conductive filler, metals, metal oxides, metal nitrides, metal carbides, metal hydroxides, carbonaceous fillers, and the like having high thermal conductivity can be used. Specific examples include aluminum oxide, magnesium oxide, zinc oxide, boron nitride, aluminum nitride, silicon carbide, aluminum hydroxide, magnesium hydroxide, carbon fiber, and graphite. Among these thermally conductive fillers, metal oxides, metal nitrides, metal carbides, metal hydroxides, etc. are suitable for applications that require electrical insulation, and among these, flame retardancy is also preferred. It is preferable to use a metal hydroxide from the viewpoint of enhancing. On the other hand, it is preferable to use carbon fiber from the viewpoint of increasing thermal conductivity. Carbon fiber is also a diamagnetic material and is easily oriented uniformly in an arbitrary direction by a magnetic field. When the thermally conductive filler is oriented by a magnetic field, specifically, a permanent magnet, an electromagnet, a superconducting magnet, or the like can be used as the magnetic field generator.
One kind of the heat conductive filler may be used alone, but by using a mixture of a plurality of kinds, the heat conductivity and flame retardancy can be improved in a balanced manner. Moreover, you may use the heat conductive filler which performed the surface treatment for the provision of insulation, improvement of a filling property, suppression of deterioration, etc.
熱伝導性充填材の含有量は、高分子マトリクス100重量部に対して好ましくは150重量部から5400重量部の範囲である。150重量部より少ないと、熱伝導性成形体の熱伝導性を高めることができず、5400重量部より多いと、粘度が増加して成形性が悪化したり、硬度が増して接触熱抵抗が高くなり熱特性が悪くなったりするおそれがある。
形状も特に限定されるものではなく、例えば、片鱗状、針状、粒状等の熱伝導性充填材を用いることができる。これらの形状の中では、高分子マトリクス中に高充填しやすい粒状や、磁場や電場、あるいは流動場や剪断場によって任意の方向に配向させることができる繊維状が好ましい。
The content of the thermally conductive filler is preferably in the range of 150 to 5400 parts by weight with respect to 100 parts by weight of the polymer matrix. If the amount is less than 150 parts by weight, the thermal conductivity of the thermally conductive molded body cannot be increased. If the amount is more than 5400 parts by weight, the viscosity increases and the moldability deteriorates, or the hardness increases and the contact thermal resistance increases. There is a possibility that the thermal characteristics become worse due to the increase.
The shape is not particularly limited, and for example, a heat conductive filler such as a scaly shape, a needle shape, or a granular shape can be used. Among these shapes, granular particles that can be easily filled in the polymer matrix, and fiber shapes that can be oriented in an arbitrary direction by a magnetic field, an electric field, a flow field, or a shear field are preferable.
熱伝導性充填材の粒径は、好ましくは0.1μm〜100μmであり、より好ましくは1μm〜50μmである。0.1μmよりも小さいと、液状混合組成物の粘度が上昇してシート等への成形が困難になる。100μmより大きいと熱伝導性成形体の硬さが硬くなるおそれがある。粒径については、均一な粒径のものを用いても良いが、高充填するため、あるいは熱伝導性成形体の硬さを柔軟にするために、2種類以上の異なる平均粒径を有する熱伝導性充填材を混合することが好ましい。 The particle size of the heat conductive filler is preferably 0.1 μm to 100 μm, more preferably 1 μm to 50 μm. If it is smaller than 0.1 μm, the viscosity of the liquid mixed composition increases, making it difficult to form a sheet or the like. If it is larger than 100 μm, the heat conductive molded body may be hard. As for the particle size, those having a uniform particle size may be used, but heat having two or more different average particle sizes is used for high filling or for softening the hardness of the heat conductive molded body. It is preferable to mix a conductive filler.
可塑剤: 可塑剤は、第1に液状樹脂に熱伝導性充填材を含有した液状混合組成物の粘度を低くするための成分である。そして、第2に熱伝導性成形体の硬さを柔らかくするための成分でもある。こうした可塑剤には、炭酸ジアルキルと引火点250℃以上の非シリコーン系オイルとを含んでいる。
引火点が250℃以上の非シリコーン系オイルの動粘度は、好適には70mm2/s〜400mm2/sの範囲であり、液状混合組成物を低粘度にすることができる。また、熱伝導性成形体の難燃性を悪化させ難く、仮に高分子マトリクス100重量部に非シリコーン系オイル300重量部を添加しても高い難燃性(UL94 V−0)を比較的容易に得ることができる。このような非シリコーン系オイルとしては、パラフィン系プロセスオイル、芳香族系プロセスオイル、ナフテン系プロセスオイル、エチレンとαオレフィンのコオリゴマーやこれらの混合物などが挙げられる。
Plasticizer : A plasticizer is a component for lowering the viscosity of a liquid mixed composition that first contains a thermally conductive filler in a liquid resin. Second, it is also a component for softening the hardness of the thermally conductive molded body. Such plasticizers include dialkyl carbonate and non-silicone oils with a flash point of 250 ° C. or higher.
The kinematic viscosity of the non-silicone
炭酸ジアルキルの動粘度は好適には10mm2/s〜40mm2/sであって比較的低粘度であり、少量の添加で液状混合組成物を低粘度にすることができる。10mm2/sよりも低い場合には、低粘度化の効果は優れるものの揮発性が高くなるため、熱伝導性成形体の硬さが経時で硬くなるおそれがある。一方、40mm2/sより高い場合には、低粘度化の効果が低くなる。炭酸ジアルキルとしては、ROCOOR(Rは炭素数が10〜18のアルキル基)が好ましい。炭酸ジアルキルは非シリコーン系オイルよりも効果的に低粘度にすることができ、例えば、高分子マトリクス100重量部に対して炭酸ジアルキルを150重量部添加した液状混合組成物は、前記非シリコーン系オイルを300重量部添加した液状混合組成物よりも低粘度となる。 The kinematic viscosity of the dialkyl carbonate is preferably a relatively low viscosity to a 10mm 2 / s~40mm 2 / s may be a liquid mix composition in a low viscosity with a small amount of addition. If it is lower than 10 mm 2 / s, the effect of lowering the viscosity is excellent, but the volatility increases, so the hardness of the thermally conductive molded body may become harder over time. On the other hand, when it is higher than 40 mm 2 / s, the effect of lowering the viscosity is lowered. As the dialkyl carbonate, ROCOOR (R is an alkyl group having 10 to 18 carbon atoms) is preferable. Dialkyl carbonate can be made to have a viscosity lower than that of non-silicone oil effectively. For example, a liquid mixed composition in which 150 parts by weight of dialkyl carbonate is added to 100 parts by weight of the polymer matrix can be obtained by using the non-silicone oil. Viscosity is lower than that of the liquid mixed composition to which 300 parts by weight of succinic acid is added.
炭酸ジアルキルと引火点250℃以上の非シリコーン系オイルの合計に対する炭酸ジアルキルの重量比率は0.05以上0.85未満である。こうした範囲で配合することで、液状混合組成物を低粘度にしながら、難燃性の低下を抑えた熱伝導性組成物を得ることができる。炭酸ジアルキルの重量比率が0.05未満では、可塑剤がブリードしない含有量に止めながら、液状混合組成物を十分に低粘度化することができない。0.85以上では、難燃性が低下しやすく、好適な粘度と難燃性の両立が困難になる。 The weight ratio of dialkyl carbonate to the sum of dialkyl carbonate and non-silicone oil having a flash point of 250 ° C. or higher is 0.05 or more and less than 0.85. By mix | blending in such a range, the heat conductive composition which suppressed the flame retardance fall can be obtained, making a liquid mixed composition low viscosity. When the weight ratio of dialkyl carbonate is less than 0.05, the viscosity of the liquid mixture composition cannot be sufficiently lowered while the content of the plasticizer is not bleed. If it is 0.85 or more, the flame retardancy tends to be lowered, and it becomes difficult to achieve both suitable viscosity and flame retardancy.
炭酸ジアルキルの含有量は、高分子マトリクス100重量部に対して100重量部未満である。炭酸ジアルキルの含有量が100重量部を超えると、熱伝導性成形体の難燃性が低下するおそれがあるためである。なお、高分子マトリクス100重量部に対して100重量部未満としているが、炭酸ジアルキルは必須の成分であるため、0重量部を超える量は含まれる。 The content of dialkyl carbonate is less than 100 parts by weight with respect to 100 parts by weight of the polymer matrix. This is because if the content of dialkyl carbonate exceeds 100 parts by weight, the flame retardancy of the thermally conductive molded article may be reduced. In addition, although it is set as less than 100 weight part with respect to 100 weight part of polymer matrices, since dialkyl carbonate is an essential component, the quantity exceeding 0 weight part is contained.
炭酸ジアルキルと非シリコーン系オイルの合計の含有量は、高分子マトリクス100重量部に対して121重量部〜257重量部とすることができる。121重量部未満では、熱伝導性充填材を高充填することができず、熱伝導性成形体の熱伝導性を高めることができない。一方、257重量部を超えると、可塑剤のブリードが多くなる。 The total content of the dialkyl carbonate and the non-silicone oil can be 121 to 257 parts by weight with respect to 100 parts by weight of the polymer matrix. If the amount is less than 121 parts by weight, the heat conductive filler cannot be highly filled, and the heat conductivity of the heat conductive molded body cannot be increased. On the other hand, when the amount exceeds 257 parts by weight, the plasticizer bleed increases.
なお、可塑剤としては比較的低粘度の可塑剤が一般的に好適であり、また、硬化後に硬くなり難い非反応性可塑剤が好適である。ところが、低粘度の可塑剤は引火点が低く、高分子マトリクスに混合すると、難燃性を低下させやすいという問題があり、また非反応性可塑剤を多量に添加すると熱伝導性成形体からブリードするおそれがあるという問題がある。特に、熱伝導性を高めるためには、熱伝導性充填材の充填量を多くする必要があり、それに伴い可塑剤の添加量も多くなるのでこうした問題点は解決する必要があった。炭酸ジアルキルも低粘度の可塑剤として難燃性を悪化させるおそれがあるという欠点を有するものの、原理は不明であるが、同程度の粘度の他の可塑剤と比較して少量の添加量で液状混合組成物を低粘度にする効果が特に高かった。そこで、この性質を利用して炭酸ジアルキルと非シリコーン系オイルとを上記所定の割合で組合せることによってこれらの問題点を解決できたのである。 As the plasticizer, a plasticizer having a relatively low viscosity is generally suitable, and a non-reactive plasticizer that is hard to be hardened after curing is suitable. However, low-viscosity plasticizers have a low flash point, and when mixed with a polymer matrix, there is a problem that flame retardancy tends to decrease. There is a problem that there is a risk. In particular, in order to increase the thermal conductivity, it is necessary to increase the filling amount of the thermally conductive filler, and accordingly, the amount of plasticizer added is also increased, so that these problems need to be solved. Although dialkyl carbonate has the disadvantage that flame retardancy may deteriorate as a low-viscosity plasticizer, the principle is unknown, but it is liquid with a small amount of addition compared to other plasticizers of similar viscosity. The effect of making the mixed composition low viscosity was particularly high. Therefore, by utilizing this property, these problems can be solved by combining dialkyl carbonate and non-silicone oil at the predetermined ratio.
その他の成分: 熱伝導性成形体の難燃性を高めるために、難燃剤を加えることが好ましい。難燃剤としてはリン系難燃剤、窒素系難燃剤、金属水酸化物などを用いることができ、適宜難燃助剤などを併用することができる。また、熱伝導性充填材の分散性を高めるために、分散剤やカップリング剤を混合することができる。さらに、耐候性を高めるために、酸化防止剤や老化防止剤を添加することができる。また、液状混合組成物には、生産性、耐候性、および耐熱性などの向上を目的として、さらに触媒、硬化遅延剤、劣化防止剤等を含んでもよい。こうした以外にも本発明の目的を損なわない範囲で種々の機能向上のための種々の添加剤を含めることができる。 Other components : It is preferable to add a flame retardant in order to increase the flame retardancy of the thermally conductive molded body. As the flame retardant, a phosphorus flame retardant, a nitrogen flame retardant, a metal hydroxide, or the like can be used, and a flame retardant aid or the like can be used in combination as appropriate. Moreover, in order to improve the dispersibility of a heat conductive filler, a dispersing agent and a coupling agent can be mixed. Furthermore, in order to improve weather resistance, antioxidants and antioxidants can be added. In addition, the liquid mixed composition may further contain a catalyst, a curing retarder, a deterioration inhibitor, and the like for the purpose of improving productivity, weather resistance, heat resistance and the like. In addition to these, various additives for improving various functions can be included within a range not impairing the object of the present invention.
熱伝導性成形体の製造方法: 熱伝導性成形体の原料となるオレフィン系液状樹脂、可塑剤、熱伝導性充填材を混合、分散させて液状混合組成物を得る。そして、この液状混合組成物を金型に注入した後、硬化して熱伝導性成形体を形成する方法を用いることができる。また、樹脂フィルムや金属板等の基材上に液状混合組成物を流延させて硬化する方法等が挙げられる。 Method for producing thermally conductive molded body: A liquid mixed composition is obtained by mixing and dispersing an olefinic liquid resin, a plasticizer, and a thermally conductive filler as raw materials of the thermally conductive molded body. And after pouring this liquid mixed composition into a metal mold | die, it can harden | cure and the method of forming a heat conductive molded object can be used. Moreover, the method etc. which cast and cure a liquid mixed composition on base materials, such as a resin film and a metal plate, are mentioned.
試料の作製: 本発明の実施例または比較例として作成した試料1〜試料11について説明する。なお、各試料の説明において重複部分の説明は省略する。試料1〜試料11の組成を表1に示す。
Preparation of
[試料1]
高分子マトリクスとして、末端にアリル基を有するポリイソブチレン(数平均分子量=5000):67重量部に、可塑剤として炭酸ジアルキル(C14H29OCOOC14H29、40℃における動粘度17.6mm2/s、引火点210℃):33重量部と、熱伝導性充填材として平均粒径10μmの水酸化アルミニウム:240重量部と、平均粒径1μmの水酸化アルミニウム:10重量部、さらに平均繊維長100μmのピッチ系炭素繊維:55重量部と、硬化剤(CR300、株式会社カネカ製):2.5重量部と、白金触媒(PT−CS−3.2cS、Ferro社(米国)製):0.2重量部と、難燃剤として赤燐(ノーバレット120UF、燐化学工業株式会社製):10重量部と、を配合し振動攪拌器により混合して液状混合組成物を調製した。熱伝導性充填材にはチタネート系カップリング剤で表面処理済みのものを用いた。また、熱伝導性充填材やその他の添加剤は、高分子マトリクスと可塑剤の合計量に対して一定の添加量とした。
[Sample 1]
Polyisobutylene having an allyl group at the end as a polymer matrix (number average molecular weight = 5000): 67 parts by weight, dialkyl carbonate (C 14 H 29 OCOOC 14 H 29 ) as a plasticizer, kinematic viscosity at 40 ° C. 17.6 mm 2 / S, flash point 210 ° C.): 33 parts by weight, aluminum hydroxide having an average particle diameter of 10 μm as a thermally conductive filler: 240 parts by weight, aluminum hydroxide having an average particle diameter of 1 μm: 10 parts by weight, and an average fiber Pitch-based carbon fiber having a length of 100 μm: 55 parts by weight, curing agent (CR300, manufactured by Kaneka Corporation): 2.5 parts by weight, platinum catalyst (PT-CS-3.2cS, manufactured by Ferro (USA)): 0.2 parts by weight and red phosphorus as a flame retardant (Nobaret 120UF, manufactured by Rin Chemical Industry Co., Ltd.): 10 parts by weight were mixed and mixed with a vibration stirrer. Thus, a liquid mixed composition was prepared. The thermally conductive filler used was a surface treated with a titanate coupling agent. Further, the heat conductive filler and other additives were set to a constant addition amount with respect to the total amount of the polymer matrix and the plasticizer.
この液状混合組成物を真空脱泡後、シート形状のキャビティを有する金型に注入し、磁束密度が8テスラの磁場を印加して、前記炭素繊維を厚み方向に配向させた。その後130℃雰囲気で1時間加熱することにより前記液状混合組成物を硬化させてシート状の熱伝導性成形体を得た。 This liquid mixed composition was vacuum degassed and then poured into a mold having a sheet-shaped cavity, and a magnetic field having a magnetic flux density of 8 Tesla was applied to orient the carbon fibers in the thickness direction. Thereafter, the liquid mixed composition was cured by heating in an atmosphere at 130 ° C. for 1 hour to obtain a sheet-like thermally conductive molded body.
[試料2、試料3]
試料1に対し炭酸ジアルキルの添加量を変えた試料とした。
[Sample 2, Sample 3]
A sample in which the amount of dialkyl carbonate added was changed with respect to
[試料4〜試料8]
可塑剤として、前記炭酸ジアルキルに加え、引火点250℃以上の非シリコーン系オイルとしてパラフィンオイル(PW−90、出光興産株式会社製、40℃における動粘度90mm2/s、引火点272℃)を混合した試料とした。
[Sample 4 to Sample 8]
As a plasticizer, in addition to the dialkyl carbonate, paraffin oil (PW-90, manufactured by Idemitsu Kosan Co., Ltd., dynamic viscosity at 40 ° C., 90 mm 2 / s, flash point 272 ° C.) is used as a non-silicone oil having a flash point of 250 ° C. or higher. A mixed sample was obtained.
[試料9〜試料11]
可塑剤として、非シリコーン系オイルのみを用いた試料とした。
[Sample 9 to Sample 11]
A sample using only non-silicone oil as a plasticizer was used.
試料の評価:
上記試料1〜試料11として作製したそれぞれの熱伝導性成形体、およびその作製過程で得られたそれぞれの液状混合組成物に対して各種の試験を行い評価した。その評価方法を以下に説明するが、評価結果は表1に示す。
Sample evaluation :
Various tests were performed and evaluated for each of the thermally conductive molded bodies prepared as
[液状混合組成物の粘度]
液状混合組成物の粘度を、回転粘度計(ブルックフィールド社製、商品名:DV−E型、スピンドルNo.14)を用い、25℃雰囲気下で、10rpmの回転数で測定した。
[Viscosity of liquid mixed composition]
The viscosity of the liquid mixture composition was measured at a rotational speed of 10 rpm in a 25 ° C. atmosphere using a rotational viscometer (Brookfield, trade name: DV-E type, spindle No. 14).
[オイルブリード]
熱伝導性成形体でのオイルブリードの程度を評価した。
熱伝導性成形体を100℃の恒温槽内に24時間置き、その後熱伝導性成形体の表面を目視により観察した。表中の“ブリード”欄において、“あり”は試験片がオイルブリードを起こしたことを示し、“なし”は試験片がオイルブリードを起こさなかったことを示す。
[Oil bleed]
The degree of oil bleed in the thermally conductive molded body was evaluated.
The thermally conductive molded body was placed in a thermostat at 100 ° C. for 24 hours, and then the surface of the thermally conductive molded body was visually observed. In the “Bleed” column of the table, “Yes” indicates that the test piece caused oil bleed, and “None” indicates that the test piece did not cause oil bleed.
[難燃性]
熱伝導性成形体の難燃性について、米国アンダー・ライターズ・ラボラトリーズ・インク(Under Writers Laboratories Inc)によって制定された燃焼試験(UL94)によって評価した。
各試料の試験片(長さ127mm×幅12.7mm×厚さ1mm又は0.5mm)を、試験片の長手方向が鉛直方向となるように固定用クランプに保持した状態で、バーナー(口径:10mm、長さ:約10cm)の炎に10秒間接炎した後、炎から離して各試験片の燃焼時間を記録した。さらに、二度目の接炎後における火種の保持時間(グローイング時間)と、試験片の下方に配置されている脱脂綿を発火させる滴下物の有無とを記録した。以上の操作を各試験片について、5回1組として行った。そして、表2に示す判定基準に基づいて、「V−0」(表2では「94V−0」)又は「V−1」(表2では「94V−1」)についての合否を判定した。なお、この難燃性の判定基準は、「V−0」の方が「V−1」よりも難燃性が高いことを示し、「V−1」の判定基準が不合格であった試験片については、難燃性がないと判定し、表中の“難燃性”欄において“×”と記載した。
[Flame retardance]
The flame retardancy of the thermally conductive molded body was evaluated by a combustion test (UL94) established by Under Writers Laboratories Inc., USA.
In a state where the test piece (length 127 mm × width 12.7 mm ×
[熱抵抗]
熱伝導性成形体の熱抵抗を測定した。
図7で示すように、基板(24)上の発熱体(25)及び放熱体(26)(ヒートシンク(株式会社アルファ製FH60−30)と、その上部に取り付けられたファン(風量:0.01kg/sec、風圧:49Pa))で試料1〜試料11の試験片(27)(10mm×10mmの寸法にカットしたもの)を挟持し、放熱体(26)上に重り(28)を載置して一定荷重(40N)を試験片(27)に加えた。そして、発熱体(25)が発熱した状態で10分間放置した後、試験片(27)における発熱体(25)側の外面の温度T1と放熱体(26)側の外面の温度T2とを測定機(29)により測定した。そして、下記式(1)により試験片(27)の熱抵抗値を算出した。発熱体(25)は通常、CPUに代表される電子部品であるが、シートの性能評価の簡素化および迅速化のため、本試験では発熱体(25)として発熱量が25Wであるヒータを用いた。
熱抵抗値(℃/W)=(T1(℃)−T2(℃))/発熱量(W)・・・式(1)
[Thermal resistance]
The thermal resistance of the thermally conductive molded body was measured.
As shown in FIG. 7, a heating element (25) and a radiator (26) (heat sink (FH60-30 manufactured by Alpha Co., Ltd.)) on the substrate (24) and a fan (air volume: 0.01 kg) mounted thereon. / Sec, wind pressure: 49 Pa)), and the specimen (27) (cut to 10 mm × 10 mm) of
Thermal resistance value (° C./W)=(T1 (° C.) − T2 (° C.)) / Heat generation amount (W) (1)
各試験の評価結果の分析:
[液状混合組成物の粘度]
図2には、液状混合組成物の粘度について、横軸に“可塑剤中の炭酸ジアルキルの割合”をとり、縦軸に“可塑剤配合量”をとってプロットしたグラフを示す。
非シリコーン系オイルと炭酸ジアルキルとからなる可塑剤中の炭酸ジアルキルの重量比率が多くなるほど、可塑剤の合計量が少なくても液状混合組成物の粘度を低粘度にすることができることがわかる。これらの粘度の値とともに、実際の作業性から粘度の評価をした。具体的には、液状混合組成物を調製した後の脱泡性が良く、ブレードコーターを用いてシートを作製した時に、シートの厚みが設定した厚みどおりに作製できたものを、表1の「粘度の評価」において“○”とした。また、特に粘度が比較的低いことから、シート成形時にシーティング速度を速くしても所望の厚みの熱伝導性成形体を作製できたものを“◎”とした。一方、脱泡性が悪く極めて脱泡に時間がかかるもの、あるいはブレードコーターでシートを作製するときに、液状混合組成物の流動性が劣ることに起因してシートの厚みを所望の厚みに調製することが困難であったものを“×”とした。
Analysis of evaluation results for each test :
[Viscosity of liquid mixed composition]
FIG. 2 shows a graph of the viscosity of the liquid mixture composition plotted with the “ratio of dialkyl carbonate in plasticizer” on the horizontal axis and “plasticizer blending amount” on the vertical axis.
It can be seen that as the weight ratio of the dialkyl carbonate in the plasticizer composed of the non-silicone oil and the dialkyl carbonate increases, the viscosity of the liquid mixture composition can be lowered even if the total amount of the plasticizer is small. Together with these viscosity values, the viscosity was evaluated from the actual workability. Specifically, the defoaming property after preparing the liquid mixture composition was good, and when the sheet was produced using a blade coater, the ones that were produced according to the thickness set by the sheet were listed in “ In “Evaluation of viscosity”, “◯” was given. In addition, since the viscosity is relatively low, “◎” indicates that a thermally conductive molded body having a desired thickness could be produced even when the sheeting speed was increased during sheet forming. On the other hand, the thickness of the sheet is adjusted to a desired thickness due to the poor defoaming property, which takes a long time to defoam, or when the sheet is produced with a blade coater, due to the poor fluidity of the liquid mixed composition What was difficult to do was designated as “x”.
次に、液状混合組成物の粘度を詳細に分析するために試料1〜試料11の可塑剤の配合量と粘度の関係を図1に示した。
Next, in order to analyze the viscosity of the liquid mixed composition in detail, the relationship between the blending amount of the plasticizers of
図1において、「DAC」は炭酸ジアルキルを意味し、その後の数字は炭酸ジアルキルと非シリコーン系オイルとでなる可塑剤中の炭酸ジアルキルの割合を示す。例えば「DAC1.0」は、炭酸ジアルキルの割合が1.0(炭酸ジアルキルが100%で非シリコーン系オイルを含まない)であることを、「DAC0.5」は炭酸ジアルキルの割合が0.5(炭酸ジアルキルが50%で残りの50%が非シリコーン系オイル)であることを意味する。 In FIG. 1, “DAC” means dialkyl carbonate, and the subsequent numbers indicate the proportion of dialkyl carbonate in the plasticizer composed of dialkyl carbonate and non-silicone oil. For example, “DAC 1.0” indicates that the ratio of dialkyl carbonate is 1.0 (dialkyl carbonate is 100% and does not include non-silicone oil), and “DAC 0.5” indicates that the ratio of dialkyl carbonate is 0.5. (Dialkyl carbonate is 50% and the remaining 50% is non-silicone oil).
測定結果を基に、可塑剤中の炭酸ジアルキルの割合が一定の場合の可塑剤配合量と粘度の関係を示す近似式、式(2)〜式(5)を見積もった。
y=1.78×104x−0.460 式(2)・炭酸ジアルキルの割合が1.0
y=2.72×104x−0.684 式(3)・炭酸ジアルキルの割合が0.5
y=8.63×104x−0.778 式(4)・炭酸ジアルキルの割合が0.33
y=3.64×104x−0.658 式(5)・炭酸ジアルキルの割合が0
※)ただし、xは液状混合組成物の粘度(mPa・s)を表し、yは高分子マトリクス100重量部に対する可塑剤配合量(重量部)を表す。
但し、炭酸ジアルキルの割合が0.1の試料は1点しかないため、近似式を作成することはできなかった。また、本願において近似式は全て最小二乗法によるものである。
Based on the measurement results, approximate equations (2) to (5) showing the relationship between the plasticizer blending amount and the viscosity when the proportion of dialkyl carbonate in the plasticizer is constant were estimated.
y = 1.78 × 10 4 x− 0.460 Formula (2) The ratio of dialkyl carbonate is 1.0
y = 2.72 × 10 4 x −0.684 Formula (3) The proportion of dialkyl carbonate is 0.5
y = 8.63 × 10 4 x− 0.778 Formula (4) The ratio of dialkyl carbonate is 0.33.
y = 3.64 × 10 4 x −0.658 Formula (5) The ratio of dialkyl carbonate is 0
*) Where x represents the viscosity (mPa · s) of the liquid mixture composition, and y represents the amount of plasticizer blended (parts by weight) relative to 100 parts by weight of the polymer matrix.
However, since there was only one sample with a dialkyl carbonate ratio of 0.1, an approximate expression could not be created. In the present application, all approximate expressions are based on the least square method.
得られた近似式に任意の粘度の値を代入することで、その液状混合組成物の粘度が前記値となる可塑剤配合量を見積もることができる。例えば粘度56000mPa・sを代入することで、各炭酸ジアルキルの割合のときに、粘度が56000mPa・sとなる可塑剤配合量を見積もることができた。 By substituting an arbitrary viscosity value into the obtained approximate expression, it is possible to estimate the plasticizer blending amount at which the viscosity of the liquid mixture composition is the above value. For example, by substituting the viscosity of 56000 mPa · s, it was possible to estimate the amount of the plasticizer blended so that the viscosity becomes 56000 mPa · s at the ratio of each dialkyl carbonate.
さらに図1で求めた各近似式、式(2)〜式(5)から粘度56000mPa・sと粘度42000mPa・sの場合の可塑剤配合量を算出し、横軸に“可塑剤中の炭酸ジアルキルの割合”、縦軸に“可塑剤配合量(重量部)”としたグラフ中にプロットした。そして、図2に示す粘度56000mPa・sの等粘度曲線(曲線1)と粘度42000mPa・sの等粘度曲線(曲線2)を作成した。なお、56000mPa・sは試料4の粘度であり、42000mPa・sは試料5の粘度である。 Furthermore, the plasticizer compounding amount in the case of the viscosity of 56000 mPa · s and the viscosity of 42000 mPa · s is calculated from the approximate expressions obtained in FIG. 1 and the expressions (2) to (5), and the horizontal axis indicates “dialkyl carbonate in the plasticizer”. The ratio was plotted on the vertical axis and the amount of plasticizer blended (parts by weight) on the vertical axis. Then, an isoviscosity curve (curve 1) having a viscosity of 56000 mPa · s and an isoviscosity curve (curve 2) having a viscosity of 42000 mPa · s shown in FIG. 2 were prepared. 56000 mPa · s is the viscosity of sample 4, and 42000 mPa · s is the viscosity of sample 5.
そして、この図2の上に、試料1〜試料11をプロットし、粘度56000mPa・sの等粘度曲線(曲線1)を基準として、この等粘度曲線よりも粘度が低い試料を好ましい粘度の試料とし、この等粘度曲線よりも粘度が高い試料を高粘度の試料と位置づけた図3を作成した。図3を見ると、炭酸ジアルキルとパラフィンオイルを混合した試料の粘度は、それぞれを単独に用いた試料どうしを結ぶ直線よりも低粘度となることがわかる。このことから、炭酸ジアルキルとパラフィンオイルの組合せには、粘度を下げる相乗効果があるものと考えられる。
Then,
[難燃性]
図4では、横軸に“可塑剤中の炭酸ジアルキルの割合”、縦軸に“可塑剤配合量(重量部)”としたグラフ中に試料1〜試料11にプロットした際、難燃性の試験結果から、難燃性を有する試料を「○」とし、難燃性のない試料を「●」と表記した。
炭酸ジアルキルの重量比率が多くなると、急激に難燃性が悪くなる傾向があることがわかる。
難燃性の評価結果については、試料2、試料4、試料8の評価結果を基に閾値を推定した。すなわち、高分子マトリクス100重量部に対する可塑剤中の炭酸ジアルキルが100重量部である試料2および試料8は難燃性がなく、前記炭酸ジアルキルが97重量部である試料5は難燃性がV−0であった。また、パラフィンオイルの影響についても試料5に対してパラフィンオイルが少ない試料2と、パラフィンオイルが多い試料8とで、難燃性の評価結果に差があることから、本発明の範囲ではパラフィンオイルの配合量は難燃性にほとんど影響を及ぼさないものと考えられる。以上のことから、炭酸ジアルキルが100重量部未満であれば難燃性を有することができるものと考えられる。こうした分析に基づき図4には、炭酸ジアルキルが100重量部であることを示す曲線3(難燃性限界値曲線)を示す。
[Flame retardance]
In FIG. 4, when plotted on
It can be seen that as the weight ratio of dialkyl carbonate increases, flame retardancy tends to deteriorate rapidly.
About the evaluation result of flame retardance, the threshold value was estimated based on the evaluation results of Sample 2, Sample 4, and Sample 8. That is, Sample 2 and Sample 8 in which 100 parts by weight of the dialkyl carbonate in the plasticizer with respect to 100 parts by weight of the polymer matrix are not flame retardant, and Sample 5 in which the dialkyl carbonate is 97 parts by weight have a flame resistance of V. -0. In addition, as for the influence of paraffin oil, there is a difference in the evaluation results of flame retardancy between sample 2 with less paraffin oil and sample 8 with more paraffin oil compared to sample 5, and therefore within the scope of the present invention It is considered that the blending amount of has little influence on the flame retardancy. From the above, it is considered that if the dialkyl carbonate is less than 100 parts by weight, it can have flame retardancy. Based on such analysis, FIG. 4 shows a curve 3 (flame retardancy limit curve) indicating that the dialkyl carbonate is 100 parts by weight.
[オイルブリード]
図5には、各試料のオイルブリードの評価結果を示す。可塑剤の配合量が300重量部と多量である試料8および試料11でオイルブリードが見られ、他の試料はオイルブリードが起こらなかった。本評価結果内では、可塑剤の配合量が同程度の試料において炭酸ジアルキルの重量比率が増すことで、オイルブリードし易くなった試料はなく、少なくとも試料10の257重量部を上限として、それ以下の可塑剤の配合量では、オイルブリードは起こらないものと考えられる。そのためオイルブリード“あり”の試料とオイルブリード“なし”の試料を区切る補助線として、直線4(y=257の直線)(ブリード限界値直線)を示した。
[Oil bleed]
FIG. 5 shows the evaluation result of oil bleed of each sample. Oil bleed was observed in Sample 8 and Sample 11 where the blending amount of the plasticizer was as large as 300 parts by weight, and no oil bleed occurred in the other samples. Within the results of this evaluation, there is no sample that is easy to oil bleed by increasing the weight ratio of dialkyl carbonate in the sample with the same amount of plasticizer, and at least 257 parts by weight of
上記実験例(試料の作製、評価)は本発明の1例であり、例えば、用いる高分子マトリクスや可塑剤の粘度、難燃剤や熱伝導性充填材の配合量により、液状混合組成物の粘度や最適な可塑剤の配合量は異なってくる。しかし、熱伝導性成形体の熱伝導性を高めようとするときに、配合を調整するにしても、成形性、オイルブリードの抑制、難燃性などの観点から自ずと配合の限界があり、そうした限界的な配合に対して、可塑剤を「炭酸ジアルキルと引火点が250℃以上の非シリコーン系オイルとを混合し、且つ炭酸ジアルキルの配合量を高分子マトリクス100重量部に対して100重量部以下とする」ことで、従来のよりも成形し易い液状混合組成物を調製できること、あるいは、従来の限界よりも、より多くの熱伝導性充填材を配合することで熱伝導性を高めながら、可塑剤のオイルブリードを抑制し、難燃性に優れた熱伝導性組成物を得ることができるということが、これらの実験例から導き出される。 The above experimental example (sample preparation and evaluation) is an example of the present invention. For example, the viscosity of the liquid mixed composition depends on the viscosity of the polymer matrix and plasticizer used, and the blending amount of the flame retardant and the heat conductive filler. And the optimum plasticizer content varies. However, even when adjusting the formulation when trying to increase the thermal conductivity of the thermally conductive molded body, there are naturally limitations on the formulation in terms of moldability, suppression of oil bleed, flame retardancy, etc. For limiting compounding, the plasticizer is “dialkyl carbonate and non-silicone oil having a flash point of 250 ° C. or higher, and the compounding amount of dialkyl carbonate is 100 parts by weight with respect to 100 parts by weight of the polymer matrix. By making it `` below '', it is possible to prepare a liquid mixture composition that is easier to mold than the conventional one, or while increasing the thermal conductivity by blending more heat conductive filler than the conventional limit, It can be derived from these experimental examples that the oil bleed of the plasticizer can be suppressed and a heat conductive composition excellent in flame retardancy can be obtained.
このような観点から実験例の評価結果について図6を用いて検討すると、「粘度56000mPa・sを示す曲線1とブリード限界値直線(直線4)の交点」から「粘度56000mPa・sを示す曲線1と難燃性限界値曲線(曲線3)の交点(ただし交点を含まず)」まで、すなわち炭酸ジアルキルの割合が0.05以上0.85未満であることが、上記効果を得るために適した配合である。こうした範囲について、本実験例の材料を用いたときの可塑剤の配合量を見積もると121〜257重量部となる。
From this point of view, the evaluation results of the experimental example are examined with reference to FIG. 6. From “the intersection of
前記炭酸ジアルキルの範囲が、0.21〜0.60の範囲であれば、より熱伝導性を高めようとしたときに、成形性、オイルブリードの抑制、難燃性の特性を満たすことができる。図2について説明すれば、熱伝導性充填材の配合量を多くできる配合とは、液状混合組成物の粘度を低粘度にできる配合であり、ここでは「粘度42000mPa・sを示す曲線2とブリード限界値直線(直線4)の交点」から「粘度42000mPa・sを示す曲線2と難燃性限界値曲線(曲線3)の交点(ただし交点を含まず)」までの範囲、すなわち炭酸ジアルキルの割合を0.21以上0.60未満と規定することができる。こうした範囲について、本実験例の可塑剤の配合量を見積もると、166重量部〜257重量部となる。 When the range of the dialkyl carbonate is in the range of 0.21 to 0.60, it is possible to satisfy the properties of moldability, suppression of oil bleed, and flame retardancy when trying to increase thermal conductivity. . Referring to FIG. 2, the blending that can increase the blending amount of the thermally conductive filler is a blending that can reduce the viscosity of the liquid mixed composition. Here, “curve 2 showing a viscosity of 42000 mPa · s and bleed” Range from “intersection of limit value straight line (straight line 4)” to “intersection of curve 2 showing viscosity 42000 mPa · s and flame retardancy limit value curve (curve 3) (but not including the intersection)”, that is, ratio of dialkyl carbonate Can be defined as 0.21 or more and less than 0.60. About such a range, when the compounding quantity of the plasticizer of this experiment example is estimated, it will be 166 weight part-257 weight part.
なお、上記実施形態は本発明の一例であり、こうした形態に限定されるものではなく、本発明の趣旨に反しない任意の変更形態を含むものである。 In addition, the said embodiment is an example of this invention and is not limited to such a form, The arbitrary modification which does not contradict the meaning of this invention is included.
24 基板
25 発熱体
26 放熱体
27 試験片
28 重り
29 測定機
24
Claims (5)
高分子マトリクスが、オレフィン系液状樹脂の硬化体でなり、
可塑剤が、炭酸ジアルキルと引火点250℃以上の非シリコーン系オイルとを含んでなり、
炭酸ジアルキルと非シリコーン系オイルの合計に対する炭酸ジアルキルの重量比率が0.05以上0.85未満であり、且つ炭酸ジアルキルの含有量が前記高分子マトリクス100重量部に対して100重量部未満であることを特徴とする熱伝導性成形体。 In a thermally conductive molded body including a polymer matrix, a plasticizer, and a thermally conductive filler,
The polymer matrix is a cured product of an olefin liquid resin,
The plasticizer comprises a dialkyl carbonate and a non-silicone oil having a flash point of 250 ° C. or higher;
The weight ratio of dialkyl carbonate to the total of dialkyl carbonate and non-silicone oil is 0.05 or more and less than 0.85, and the content of dialkyl carbonate is less than 100 parts by weight with respect to 100 parts by weight of the polymer matrix. The heat conductive molded object characterized by the above-mentioned.