JP2012233151A - Salt - Google Patents
Salt Download PDFInfo
- Publication number
- JP2012233151A JP2012233151A JP2011280888A JP2011280888A JP2012233151A JP 2012233151 A JP2012233151 A JP 2012233151A JP 2011280888 A JP2011280888 A JP 2011280888A JP 2011280888 A JP2011280888 A JP 2011280888A JP 2012233151 A JP2012233151 A JP 2012233151A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- formula
- salt
- dye
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、染料として有用な塩に関するものである。 The present invention relates to salts useful as dyes.
染料は、例えば、繊維材料、液晶表示装置、インクジェット及び記録材料などの分野で使用されている。
このような染料としては、例えば、下記式(d−1)で表される化合物、式(d−2)で表される化合物及び式(h−1)で表される化合物が知られている(特許文献1、2及び非特許文献1)。
For example, dyes are used in the fields of fiber materials, liquid crystal display devices, ink jets, and recording materials.
As such a dye, for example, a compound represented by the following formula (d-1), a compound represented by the formula (d-2), and a compound represented by the formula (h-1) are known. (Patent Documents 1 and 2 and Non-Patent Document 1).
従来から知られる上記の化合物は、有機溶媒への溶解性が必ずしも十分に満足できない場合があった。 Conventionally known compounds may not always be sufficiently satisfactory in solubility in organic solvents.
本発明は、以下の[1]〜[6]を提供するものである。
[1]2価以上の金属イオンを形成し得る金属原子を含むn価の有機金属アニオンMn−と、該有機金属アニオンと塩形成しうる染料に由来するオニウムカチオンとの塩であり、かつ、該有機金属アニオンが、式(1)
Mn− nZ+ (1)
[式(1)中、Mn−は、上記の有機金属アニオンを表す。Z+は、ヒドロン又はアルカリ金属カチオンを表す。nは1〜3の整数を表す。nが2以上の整数である場合、複数のZ+は互いに同一でも異なっていてもよい。]
で表される化合物にしたときに下記要件Aを満たすことを特徴とする塩。
要件A:式(1)で表される化合物の濃度0.028g/L溶液で測定された吸光度が、400〜900nmに亘って0.05以下である。
The present invention provides the following [1] to [6].
[1] A salt of an n-valent organometallic anion M n− containing a metal atom capable of forming a bivalent or higher-valent metal ion and an onium cation derived from a dye capable of forming a salt with the organometallic anion, The organometallic anion has the formula (1)
M n− nZ + (1)
Wherein (1), M n-represents an organometallic anion above. Z + represents a hydrone or an alkali metal cation. n represents an integer of 1 to 3. When n is an integer greater than or equal to 2, several Z <+> may mutually be same or different. ]
The salt characterized by satisfy | filling the following requirement A when it is set as the compound represented by these.
Requirement A: Absorbance measured with a 0.028 g / L solution of the compound represented by formula (1) is 0.05 or less over 400 to 900 nm.
[2]前記オニウムカチオンが、シアニン染料に由来するカチオン、トリアリールメタン染料に由来するカチオン、キサンテン染料に由来するカチオン又はアントラキノン染料に由来するカチオンである[1]記載の塩。
[3]前記n価の有機金属アニオンMn−が、置換基を有していてもよいサリチル酸、又はアミノ基に結合したカルボキシメチル基を複数有する化合物に由来する構造を有する有機金属アニオンである[1]又は[2]記載の塩。
[4]前記n価の有機金属アニオンMn−に含まれる2価以上の金属イオンを形成し得る金属原子が、Al、Cr又はCoである[1]〜[3]のいずれか記載の塩。
[5][1]〜[4]のいずれか記載の塩を有効成分とする染料。
[6][5]記載の染料を含む着色組成物。
[2] The salt according to [1], wherein the onium cation is a cation derived from a cyanine dye, a cation derived from a triarylmethane dye, a cation derived from a xanthene dye, or a cation derived from an anthraquinone dye.
[3] The n-valent organometallic anion M n− is an organometallic anion having a structure derived from salicylic acid which may have a substituent or a compound having a plurality of carboxymethyl groups bonded to an amino group. The salt according to [1] or [2].
[4] The salt according to any one of [1] to [3], wherein a metal atom capable of forming a divalent or higher metal ion contained in the n-valent organometallic anion M n- is Al, Cr, or Co. .
[5] A dye comprising the salt according to any one of [1] to [4] as an active ingredient.
[6] A coloring composition containing the dye according to [5].
本発明の塩は、有機溶媒への溶解性に優れる。 The salt of the present invention is excellent in solubility in an organic solvent.
本発明の塩は、2価以上の金属イオンを形成し得る金属原子を含むn価の有機金属アニオンMn−と、該有機金属アニオンと塩形成しうる染料に由来するオニウムカチオンとの塩であり、かつ、該有機金属アニオンが、式(1)
Mn− nZ+ (1)
[式(1)中、Mn−は、上記の有機金属アニオンを表す。Z+は、ヒドロン又はアルカリ金属カチオンを表す。nは1〜3の整数を表す。nが2以上の整数である場合、複数のZ+は互いに同一でも異なっていてもよい。]
で表される化合物(以下「化合物(1)」という場合がある)にしたときに下記要件Aを満たすことを特徴とする塩である。
要件A:式(1)で表される化合物の濃度0.028g/L溶液で測定された吸光度が、400〜900nmに亘って0.05以下である。
本発明の塩の−電荷と+電荷とは同一である。
The salt of the present invention is a salt of an n-valent organometallic anion M n− containing a metal atom capable of forming a bivalent or higher-valent metal ion and an onium cation derived from a dye capable of forming a salt with the organometallic anion. And the organometallic anion has the formula (1)
M n− nZ + (1)
Wherein (1), M n-represents an organometallic anion above. Z + represents a hydrone or an alkali metal cation. n represents an integer of 1 to 3. When n is an integer greater than or equal to 2, several Z <+> may mutually be same or different. ]
The salt is characterized by satisfying the following requirement A when it is made into a compound represented by formula (hereinafter sometimes referred to as “compound (1)”).
Requirement A: Absorbance measured with a 0.028 g / L solution of the compound represented by formula (1) is 0.05 or less over 400 to 900 nm.
The -charge and + charge of the salt of the present invention are the same.
該有機金属アニオンと塩形成しうる染料としては、シアニン染料、アントラキノン染料、トリアリールメタン染料、キサンテン染料、フタロシアニン染料、ジアリールメタン染料、アクリジン染料、アジン染料、チアジン染料、オキサジン染料、アザメチン染料及びアゾ染料等が挙げられる。中でも、シアニン染料、トリアリールメタン染料、キサンテン染料及びアントラキノン染料が好ましい。このような本発明の塩は、染料に由来するカチオンから構成されることにより、染料として有用な色性能を示す。 Examples of the dye capable of forming a salt with the organometallic anion include cyanine dye, anthraquinone dye, triarylmethane dye, xanthene dye, phthalocyanine dye, diarylmethane dye, acridine dye, azine dye, thiazine dye, oxazine dye, azamethine dye and azo dye. And dyes. Of these, cyanine dyes, triarylmethane dyes, xanthene dyes and anthraquinone dyes are preferable. Such a salt of the present invention exhibits a color performance useful as a dye by being composed of a cation derived from the dye.
オニウムカチオンとしては、例えば、それぞれ上記染料に由来するアンモニウムカチオン、オキソニウムカチオン、スルホニウムカチオン、ホスホニウムカチオン等が挙げられる。 Examples of the onium cation include an ammonium cation, an oxonium cation, a sulfonium cation, and a phosphonium cation each derived from the above dye.
以下、本発明の塩を構成するカチオンについて、その由来となる染料を挙げて具体的に例示する。 Hereinafter, the cation constituting the salt of the present invention is specifically exemplified with reference to a dye that is derived from the cation.
シアニン染料に由来するカチオンとしては、例えば、式(1−1)〜式(1−42)でそれぞれ表されるシアニン骨格を有するカチオン等が挙げられる。尚、式中「n−Pr」はn−プロピル基を表し、「n−Bu」はn−ブチル基を表し、「s−Bu」はsec−ブチル基を表す。
シアニン染料としては、式(1−1)〜式(1−42)でそれぞれ表されるカチオンと上記の対アニオンとの塩が挙げられる。対アニオンとしては、ハロゲン化物イオン(例えば、Cl−、Br−、I−)、過塩素酸アニオン、塩素酸アニオン、チオシアン酸アニオン、六フッ化リンアニオン、六フッ化アンチモンアニオン、四フッ化ホウ素アニオン、C6H5SO3 −、CH3−C6H4SO3 −、CF3SO3 −等が挙げられる。
Examples of the cation derived from the cyanine dye include a cation having a cyanine skeleton represented by each of the formulas (1-1) to (1-42). In the formula, “n-Pr” represents an n-propyl group, “n-Bu” represents an n-butyl group, and “s-Bu” represents a sec-butyl group.
Examples of the cyanine dye include salts of cations represented by formulas (1-1) to (1-42) and the above counter anions. Counter anions include halide ions (for example, Cl − , Br − , I − ), perchlorate anions, chlorate anions, thiocyanate anions, phosphorus hexafluoride anions, antimony hexafluoride anions, boron tetrafluoride. anionic, C 6 H 5 SO 3 - , CH 3 -C 6 H 4 SO 3 -, CF 3 SO 3 - , and the like.
トリアリールメタン染料に由来するカチオンを導く染料としては、C.I.Basic Red 9、C.I.Basic Violet 1、C.I.Basic Violet 2、C.I.Basic Violet 3、C.I.Basic Violet 4、C.I.Basic Violet 13、C.I.Basic Violet 14、C.I.Basic Violet 23、C.I.Basic Blue 1、C.I.Basic Blue 5、C.I.Basic Blue 7、C.I.Basic Blue 8、C.I.Basic Blue 11、C.I.Basic Blue 15、C.I.Basic Blue 18、C.I.Basic Blue 20、C.I.Basic Blue 21、C.I.Basic Blue 24、C.I.Basic Blue 26、C.I.Basic Green 1、C.I.Basic Green 4等、及び、下式(g−1)〜(g−7)でそれぞれ表される染料等が挙げられる。また、これらの前駆体となり得る染料、例えば、C.I.Solvent Blue 5(C.I.Basic Blue 7の前駆体となり得る)等も挙げられる。
Examples of dyes that lead to cations derived from triarylmethane dyes include C.I. I. Basic Red 9, C.I. I. Basic Violet 1, C.I. I. Basic Violet 2, C.I. I. Basic Violet 3, C.I. I. Basic Violet 4, C.I. I. Basic Violet 13, C.I. I. Basic Violet 14, C.I. I. Basic Violet 23, C.I. I. Basic Blue 1, C.I. I. Basic Blue 5, C.I. I. Basic Blue 7, C.I. I. Basic Blue 8, C.I. I. Basic Blue 11, C.I. I. Basic Blue 15, C.I. I. Basic Blue 18, C.I. I. Basic Blue 20, C.I. I. Basic Blue 21, C.I. I. Basic Blue 24, C.I. I. Basic Blue 26, C.I. I. Basic Green 1, C.I. I. Examples include Basic Green 4 and the like, and dyes represented by the following formulas (g-1) to (g-7). Also, dyes that can be used as precursors thereof, for example, C.I. I. Solvent Blue 5 (can be a precursor of CI Basic Blue 7) and the like.
キサンテン染料に由来するカチオンを導く染料、即ちキサンテン染料とは、分子内にキサンテン骨格を有する染料の総称である。該キサンテン骨格上に置換されていてもよいアミノ基を少なくとも一つ有していることが好ましく、置換されていてもよいアミノ基を二つ有していることがより好ましい。本発明の塩に含有されるカチオンは、置換されていてもよいアミノ基の窒素原子が正電荷を帯びた構造を有するカチオンであることが好ましく、イミニウムカチオンであることがより好ましい。 A dye that leads to a cation derived from a xanthene dye, that is, a xanthene dye, is a general term for dyes having a xanthene skeleton in the molecule. The xanthene skeleton preferably has at least one optionally substituted amino group, and more preferably has two optionally substituted amino groups. The cation contained in the salt of the present invention is preferably a cation having a structure in which the nitrogen atom of the amino group which may be substituted has a positive charge, and more preferably an iminium cation.
かかるキサンテン染料としては、エオシン(Eosin)系染料、フルオレセイン(Fluorescein)系染料、ローダミン(Rhodamine)系染料、ピロニン(Pyronine)系染料、ローザミン(Rosamine)系染料等が挙げられる。また、Synlett, 2010, No. 1, p. 89-92に記載されているような、キサンテン骨格の酸素原子が硫黄原子、セレン原子又はテルル原子に置換されたローダミン(Rhodamine)系染料やローザミン(Rosamine)系染料等も挙げられる。 Examples of such xanthene dyes include eosin dyes, fluorescein dyes, rhodamine dyes, pyronin dyes, and rosamine dyes. Further, as described in Synlett, 2010, No. 1, p. 89-92, rhodamine dyes or rosamin (in which the oxygen atom of the xanthene skeleton is substituted with a sulfur atom, a selenium atom, or a tellurium atom) (Rosamine) dyes and the like.
キサンテン染料は、通常、Cl−又はPF6 −等の無機アニオンを有するか、分子内にカルボキシラート基(−COO−)やスルホナート基(−SO3 −)等の酸性基を有する。前者の場合、キサンテン染料はいわゆる塩基性染料であり、キサンテン染料に由来するカチオンは、通常、キサンテン染料から無機アニオンの一部又は全部(好ましくは全部)を除いたカチオンである。後者の場合、キサンテン染料はいわゆる内部塩であり、キサンテン染料に由来するカチオンは、通常、かかる内部塩が有する酸性基の一部又は全部(好ましくは全部)が中和された構造のカチオンである。ここで、酸性基として、例えば、カルボキシラート基(−COO−)が中和された基はカルボキシ基(−COOH)又はその塩(−COONa等)であり、スルホナート基(−SO3 −)が中和された基はスルホ基(−SO3H)又はその塩(−SO3Na等)である。 Xanthene dyes, typically, Cl - or PF 6 - or with inorganic anions such as, carboxylate group in a molecule having an acidic group such as (-COO - -) or sulfonate group (-SO 3). In the former case, the xanthene dye is a so-called basic dye, and the cation derived from the xanthene dye is usually a cation obtained by removing some or all (preferably all) inorganic anions from the xanthene dye. In the latter case, the xanthene dye is a so-called internal salt, and the cation derived from the xanthene dye is usually a cation having a structure in which part or all (preferably all) of the acidic groups of the internal salt are neutralized. . Here, as the acidic group, for example, a group in which a carboxylate group (—COO − ) is neutralized is a carboxyl group (—COOH) or a salt thereof (—COONa or the like), and a sulfonate group (—SO 3 — ) is present. The neutralized group is a sulfo group (—SO 3 H) or a salt thereof (—SO 3 Na or the like).
キサンテン染料のうち塩基性染料の具体例としては、C.I.Basic Red 1、C.I.Basic Red 2、C.I.Basic Red 3、C.I.Basic Red 4、Basic Red 8、Basic Red 11、C.I.Basic Violet 10、C.I.Basic Violet 11、C.I.Basic Violet 25、及び、下式(h−1)〜(h−82)でそれぞれ表される染料等が挙げられる。 Specific examples of basic dyes among xanthene dyes include C.I. I. Basic Red 1, C.I. I. Basic Red 2, C.I. I. Basic Red 3, C.I. I. Basic Red 4, Basic Red 8, Basic Red 11, C.I. I. Basic Violet 10, C.I. I. Basic Violet 11, C.I. I. Examples thereof include Basic Violet 25 and dyes represented by the following formulas (h-1) to (h-82).
キサンテン染料のうち内部塩の具体例としては、C.I.Mordant Red 27、及び、下式(h−100)〜(h−118)でそれぞれ表される染料等が挙げられる。 Specific examples of the internal salt among the xanthene dyes include C.I. I. Examples include Modern Red 27 and dyes represented by the following formulas (h-100) to (h-118).
アントラキノン染料に由来するカチオンを導く染料としては、C.I.Basic Blue 22、C.I.Basic Blue 35、C.I.Basic Blue 45、C.I.Basic Blue 47等が挙げられる。 Examples of dyes that lead to cations derived from anthraquinone dyes include C.I. I. Basic Blue 22, C.I. I. Basic Blue 35, C.I. I. Basic Blue 45, C.I. I. Basic Blue 47 etc. are mentioned.
本発明の塩のアニオンを導く化合物(1)は、下記要件Aを満たす。
要件A:化合物(1)の濃度0.028g/L溶液で測定された吸光度が、400〜900nmに亘って0.05以下である。
化合物(1)を、乳酸エチル、クロロホルム、N,N−ジメチルホルミアミド、イオン交換水、メタノール、エタノール及びトルエンのうちのいずれかに溶解させて、吸光度を測定するための溶液を作製する。
この溶液について400〜900nmの吸光度を測定する。該吸光度は、400〜900nm全域に亘って0.05以下であり、好ましくは0.035以下であり、さらに好ましくは0.005以下である。
化合物(1)が要件Aを満たすことにより、本発明の塩は、カチオンとする染料の色性能を保持し、かつ有機溶媒への溶解性に優れる傾向がある。
The compound (1) leading to the anion of the salt of the present invention satisfies the following requirement A.
Requirement A: Absorbance measured with a 0.028 g / L solution of compound (1) is 0.05 or less over 400 to 900 nm.
Compound (1) is dissolved in any of ethyl lactate, chloroform, N, N-dimethylformamide, ion-exchanged water, methanol, ethanol and toluene to prepare a solution for measuring absorbance.
The absorbance at 400 to 900 nm is measured for this solution. The absorbance is 0.05 or less, preferably 0.035 or less, more preferably 0.005 or less over the entire range of 400 to 900 nm.
When the compound (1) satisfies the requirement A, the salt of the present invention tends to maintain the color performance of a cation dye and be excellent in solubility in an organic solvent.
式(1)
Mn− nZ+ (1)
[式(1)中、Mn−は、2価以上の金属原子を含むn価の有機金属アニオンを表す。Z+は、ヒドロン又はアルカリ金属カチオンを表す。nは1〜3の整数を表す。nが2以上の整数である場合、複数のZ+は互いに同一でも異なっていてもよい。]
で表される化合物におけるアルカリ金属としては、ナトリウム及びカリウム等が挙げられる。
Formula (1)
M n− nZ + (1)
[In formula (1), M n− represents an n-valent organometallic anion containing a divalent or higher-valent metal atom. Z + represents a hydrone or an alkali metal cation. n represents an integer of 1 to 3. When n is an integer greater than or equal to 2, several Z <+> may mutually be same or different. ]
Examples of the alkali metal in the compound represented by the formula include sodium and potassium.
前記の有機金属アニオンは、2価以上の金属イオンを形成し得る金属原子と有機化合物とが、イオン結合又は配位結合により結合した構造を有する。
前記の有機化合物としては、置換基を有していてもよいサリチル酸、アミノ基に結合したカルボキシメチル基を複数有する化合物、置換基を有していてもよいベンジル酸、置換基を有していてもよいマンデル酸及び置換基を有していてもよいピコリン酸等が挙げられる。有機金属アニオンMn−としては、置換基を有していてもよいサリチル酸、又はアミノ基に結合したカルボキシメチル基を複数有する化合物をに由来する構造を有する有機金属アニオンであることが好ましい。
The organometallic anion has a structure in which a metal atom capable of forming a divalent or higher valent metal ion and an organic compound are bonded by an ionic bond or a coordinate bond.
Examples of the organic compound include a salicylic acid which may have a substituent, a compound having a plurality of carboxymethyl groups bonded to an amino group, a benzylic acid which may have a substituent, and a substituent. Examples thereof include mandelic acid, which may be substituted, and picolinic acid which may have a substituent. The organometallic anion M n- is preferably an organometallic anion having a structure derived from salicylic acid which may have a substituent or a compound having a plurality of carboxymethyl groups bonded to an amino group.
前記の置換基を有していてもよいサリチル酸としては、例えば、サリチル酸、3−メチルサリチル酸、3−tert−ブチルサリチル酸、3−アミノサリチル酸、3−クロロサリチル酸、4−ブロモサリチル酸、3−メトキシサリチル酸、2−ヒドロキシサリチル酸、3−ニトロサリチル酸、4−トリフルオロメチルサリチル酸、3,5−ジ−tert−ブチルサリチル酸、3,5−ジブロモサリチル酸、3,5−ジクロロサリチル酸、3,5,6−トリクロロサリチル酸、4−ヒドロキシサリチル酸、5−ヒドロキシサリチル酸等が挙げられる。 Examples of the salicylic acid optionally having the above substituent include salicylic acid, 3-methylsalicylic acid, 3-tert-butylsalicylic acid, 3-aminosalicylic acid, 3-chlorosalicylic acid, 4-bromosalicylic acid, and 3-methoxysalicylic acid. 2-hydroxysalicylic acid, 3-nitrosalicylic acid, 4-trifluoromethylsalicylic acid, 3,5-di-tert-butylsalicylic acid, 3,5-dibromosalicylic acid, 3,5-dichlorosalicylic acid, 3,5,6-trichloro Salicylic acid, 4-hydroxysalicylic acid, 5-hydroxysalicylic acid and the like can be mentioned.
前記のアミノ基に結合したカルボキシメチル基を複数有する化合物としては、例えば、
等が挙げられる。
Examples of the compound having a plurality of carboxymethyl groups bonded to the amino group include:
Etc.
前記の置換基を有していてもよいベンジル酸としては、例えば、
等が挙げられる。
Examples of the benzylic acid that may have the above-described substituent include, for example,
Etc.
前記の置換基を有していてもよいマンデル酸としては、例えば、
等が挙げられる。
Examples of the mandelic acid optionally having the above substituent include, for example:
Etc.
前記の置換基を有していてもよいピコリン酸としては、例えば、
等が挙げられる。
Examples of the picolinic acid optionally having the above-described substituent include, for example,
Etc.
2価以上の金属イオンを形成し得る金属原子としては、Al、Cr、Co、Fe、Cu、Ni、Co、Zn、Mg、Ca及びBa等が挙げられる。
中でも、Al、Cr及びCoが好ましい。
Examples of metal atoms that can form a divalent or higher metal ion include Al, Cr, Co, Fe, Cu, Ni, Co, Zn, Mg, Ca, and Ba.
Of these, Al, Cr and Co are preferable.
化合物(1)を構成するアニオンMn−としては、例えば、アニオン(c−1)〜アニオン(c−72)等が挙げられる。 Examples of the anion M n− constituting the compound (1) include anion (c-1) to anion (c-72).
中でも、アニオンMn−としては、アニオン(c−2)、アニオン(c−6)〜アニオン(c−9)、アニオン(c−14)〜アニオン(c−17)、アニオン(c−21)、アニオン(c−22)、アニオン(c−24)〜アニオン(c−26)、アニオン(c−28)、アニオン(c−32)〜アニオン(c−35)、アニオン(c−40)〜アニオン(c−43)、アニオン(c−47)、アニオン(c−48)、アニオン(c−50)〜アニオン(c−62)、アニオン(c−65)及びアニオン(c−66)が好ましく、アニオン(c−2)、アニオン(c−21)、アニオン(c−22)、アニオン(c−26)、アニオン(c−28)、アニオン(c−47)、アニオン(c−48)及びアニオン(c−52)がより好ましく、アニオン(c−28)がさらに好ましい。これらのアニオンであると、本発明の塩は有機溶剤への溶解性に優れる傾向がある。 Especially, as anion Mn- , anion (c-2), anion (c-6)-anion (c-9), anion (c-14)-anion (c-17), anion (c-21) , Anion (c-22), anion (c-24) to anion (c-26), anion (c-28), anion (c-32) to anion (c-35), anion (c-40) to Preferred are anions (c-43), anions (c-47), anions (c-48), anions (c-50) to anions (c-62), anions (c-65) and anions (c-66). , Anion (c-2), anion (c-21), anion (c-22), anion (c-26), anion (c-28), anion (c-47), anion (c-48) and An anion (c-52) is more preferable And an anion (c-28) is more preferable. With these anions, the salt of the present invention tends to be excellent in solubility in an organic solvent.
本発明の塩としては、例えば、塩(I−1)〜塩(I−62)等が挙げられる。 Examples of the salt of the present invention include salt (I-1) to salt (I-62).
本発明の塩は、染料と、化合物(1)とを、溶媒中で混合することで製造することができる。 The salt of the present invention can be produced by mixing the dye and compound (1) in a solvent.
混合時に用いる溶媒としては、N,N−ジメチルホルミアミド、N,N−ジメチルアセトアミド、N−メチルピロリドン、ジメチルスルホキシド、アセトニトリル、酢酸エチル、トルエン、メタノール、エタノール、イソプロパノール、アセトン、テトラヒドロフラン、ジオキサン、水及びクロロホルム等が挙げられる。
中でも、N,N−ジメチルホルミアミド、N,N−ジメチルアセトアミド、N−メチルピロリドン、ジメチルスルホキシド、メタノール、エタノール、イソプロパノール及び水が好ましい。これらの溶媒であると、染料及び化合物(1)の溶解度が高い傾向にある。
溶媒が水である場合、染料及び化合物(1)を溶媒へ溶解させるため、酢酸や塩酸等の酸を加えてもよい。
染料と化合物(1)との混合は、両者を上記の溶媒に溶解させて行ってもよいし、溶解させずに行ってもよい。しかしながら、両者が溶解する溶媒を用いて、かつ溶解させて行うことにより、高い収率で本発明の塩を得ることができる。
As a solvent used at the time of mixing, N, N-dimethylformamide, N, N-dimethylacetamide, N-methylpyrrolidone, dimethyl sulfoxide, acetonitrile, ethyl acetate, toluene, methanol, ethanol, isopropanol, acetone, tetrahydrofuran, dioxane, Examples include water and chloroform.
Among these, N, N-dimethylformamide, N, N-dimethylacetamide, N-methylpyrrolidone, dimethyl sulfoxide, methanol, ethanol, isopropanol and water are preferable. When these solvents are used, the solubility of the dye and the compound (1) tends to be high.
When the solvent is water, an acid such as acetic acid or hydrochloric acid may be added to dissolve the dye and compound (1) in the solvent.
Mixing of the dye and the compound (1) may be performed by dissolving both of them in the above solvent or without dissolving them. However, the salt of the present invention can be obtained in a high yield by carrying out using a solvent in which both are dissolved.
染料と化合物(1)との混合温度は、好ましくは0℃〜150℃、より好ましくは10℃〜120℃、さらに好ましくは20℃〜100℃である。
また、混合時間は、好ましくは1時間〜72時間、より好ましくは2時間〜24時間、さらに好ましくは3時間〜12時間である。
The mixing temperature of the dye and the compound (1) is preferably 0 ° C to 150 ° C, more preferably 10 ° C to 120 ° C, and further preferably 20 ° C to 100 ° C.
The mixing time is preferably 1 hour to 72 hours, more preferably 2 hours to 24 hours, and further preferably 3 hours to 12 hours.
混合に用いた溶媒が水と相溶する溶媒である場合は、該溶液にイオン交換水を加え、さらに1〜3時間攪拌する。その後、析出物を濾過により取得すれば、本発明の塩を得ることができる。必要に応じて、イオン交換水で洗浄してもよい。
混合に用いた溶媒が水と相溶しない溶媒である場合は、該溶液にイオン交換水を加え、さらに1〜3時間攪拌する。その後、有機層を分液により取得すれば、本発明の塩を含む溶液を得ることができる。必要に応じて、イオン交換水で洗浄してもよい。本発明の塩を含む溶液から溶媒を除去することにより、本発明の塩を得ることができる。
When the solvent used for mixing is a solvent compatible with water, ion-exchanged water is added to the solution, and the mixture is further stirred for 1 to 3 hours. Then, if the precipitate is obtained by filtration, the salt of the present invention can be obtained. You may wash | clean with ion-exchange water as needed.
When the solvent used for mixing is a solvent that is incompatible with water, ion-exchanged water is added to the solution, and the mixture is further stirred for 1 to 3 hours. Thereafter, if the organic layer is obtained by liquid separation, a solution containing the salt of the present invention can be obtained. You may wash | clean with ion-exchange water as needed. The salt of the present invention can be obtained by removing the solvent from the solution containing the salt of the present invention.
さらに、本発明の塩をアセトニトリル、酢酸エチル、トルエン、メタノール、エタノール、イソプロパノール、アセトン、クロロホルム等の溶媒に溶解させて、再結晶により精製してもよい。 Furthermore, the salt of the present invention may be dissolved in a solvent such as acetonitrile, ethyl acetate, toluene, methanol, ethanol, isopropanol, acetone, chloroform, and purified by recrystallization.
染料は、市販のものを用いてもよいし、例えば、細田豊著「理論製造 染料化学」、技報堂、396〜402、357〜366、369〜377及び235〜241ページ、松居正樹監修「機能性色素の合成と応用技術」,シーエムシー出版,89〜96頁、Synlett, 2010, No. 1, p. 89-92、J. Organic Chemistry, 2008, Vol. 73, 8711-8718等に記載の公知の方法で製造したものを用いてもよい。 A commercially available dye may be used. For example, Hosoda Yutaka "Theoretical Manufacturing Dye Chemistry", Gihodo, 396-402, 357-366, 369-377 and pages 235-241, supervised by Masaki Matsui "Synthesis of dyes and applied technology", CMC Publishing, 89-96, Synlett, 2010, No. 1, p. 89-92, J. Organic Chemistry, 2008, Vol. 73, 8711-8718, etc. You may use what was manufactured by the method of.
化合物(1)は、市販のものを用いてもよいし、例えば、特公平8−10360や特開2002−258537及び実験化学講座5版22巻312−313ページ等に記載されるように、配位子となる化合物と、金属の硫酸塩や塩化物とを反応させることにより製造できる。 Compound (1) may be a commercially available compound, for example, as described in Japanese Patent Publication No. 8-10360, Japanese Patent Application Laid-Open No. 2002-258537, and Experimental Chemistry Course 5th edition, Volume 22, pages 312-313. It can be produced by reacting a ligand compound with a metal sulfate or chloride.
かくして得られた本発明の塩は、染料として有用である。また、本発明の塩は、有機溶媒への溶解性が高いことから、特に、液晶表示装置などの表示装置のカラーフィルターに用いられる染料として有用である。 The salt of the present invention thus obtained is useful as a dye. Moreover, since the salt of this invention has the high solubility to an organic solvent, it is especially useful as a dye used for the color filter of display apparatuses, such as a liquid crystal display device.
本発明の染料は、本発明の塩を有効成分とする染料である。
本発明の着色組成物は、着色剤(以下「着色剤(A)」という場合がある)として本発明の染料を含み、さらに樹脂(B)を含むことが好ましい。本発明の着色組成物は、さらに重合性化合物(C)、重合開始剤(D及び溶剤(E))を含むことがより好ましい。
The dye of the present invention is a dye containing the salt of the present invention as an active ingredient.
The colored composition of the present invention preferably contains the dye of the present invention as a colorant (hereinafter sometimes referred to as “colorant (A)”) and further contains a resin (B). The colored composition of the present invention further preferably contains a polymerizable compound (C) and a polymerization initiator (D and solvent (E)).
着色剤(A)は、本発明の染料のほかに、さらに顔料及び/又は本発明の染料とは異なる染料を含んでいてもよい。
本発明の染料とは異なる染料としては、カラーインデックス(Colour Index)(The Society of Dyers and Colourists 出版)で、ソルベント(Solvent)、アシッド(Acid)、ベーシック(Basic)、リアクティブ(reactive)、ダイレクト(Direct)、ディスパース(Disperse)、又はバット(Vat)に分類されている染料等が挙げられる。より具体的には、以下のようなカラーインデックス(C.I.)番号の染料が挙げられるが、これらに限定されるわけではない。
C.I.ソルベントイエロー25,79,81,82、83,89;
C.I.アシッドイエロー7,23,25,42,65,76;
C.I.リアクティブイエロー2,76,116;
C.I.ダイレクトイエロー4,28,44,86,132;
C.I.ディスパースイエロー54,76;
C.I.ソルベントオレンジ41,54,56,99;
C.I.アシッドオレンジ56,74,95,108,149,162;
C.I.リアクティブオレンジ16;
C.I.ダイレクトオレンジ26;
C.I.ソルベントレッド24,49,90,91,118,119,122,124,125,127,130,132,160,218;
C.I.アシッドレッド73,91,92,97,138,151,211,274,289;
C.I.アシッドバイオレット102;
C.I.ソルベントグリーン1,5;
C.I.アシッドグリーン3,5,9,25,28;
C.I.ベーシックグリーン1;
C.I.バットグリーン1等。
In addition to the dye of the present invention, the colorant (A) may further contain a pigment and / or a dye different from the dye of the present invention.
As dyes different from the dyes of the present invention, the Color Index (published by The Society of Dyers and Colorists), Solvent, Acid, Basic, reactive, direct And dyes classified as (Direct), Disperse, or Vat. More specifically, dyes having the following color index (CI) numbers can be mentioned, but the dye is not limited thereto.
C. I. Solvent Yellow 25, 79, 81, 82, 83, 89;
C. I. Acid Yellow 7, 23, 25, 42, 65, 76;
C. I. Reactive Yellow 2, 76, 116;
C. I. Direct yellow 4, 28, 44, 86, 132;
C. I. Disperse Yellow 54,76;
C. I. Solvent orange 41, 54, 56, 99;
C. I. Acid Orange 56, 74, 95, 108, 149, 162;
C. I. Reactive Orange 16;
C. I. Direct orange 26;
C. I. Solvent Red 24, 49, 90, 91, 118, 119, 122, 124, 125, 127, 130, 132, 160, 218;
C. I. Acid Red 73, 91, 92, 97, 138, 151, 211, 274, 289;
C. I. Acid Violet 102;
C. I. Solvent Green 1,5;
C. I. Acid Green 3, 5, 9, 25, 28;
C. I. Basic Green 1;
C. I. Bat Green 1 etc.
顔料としては、顔料分散レジストに通常用いられる有機顔料又は無機顔料が挙げられる。無機顔料としては、金属酸化物や金属錯塩のような金属化合物が挙げられ、具体的には、鉄、コバルト、アルミニウム、カドミウム、鉛、銅、チタン、マグネシウム、クロム、亜鉛、アンチモン等の金属の酸化物又は複合金属酸化物が挙げられる。また有機顔料及び無機顔料として具体的には、カラーインデックス(Colour Index)(The Society of Dyers and Colourists 出版)で、ピグメント(Pigment)に分類されている化合物が挙げられる。より具体的には、以下のようなカラーインデックス(C.I.)番号の顔料が挙げられるが、これらに限定されるわけではない。 Examples of the pigment include organic pigments and inorganic pigments usually used for pigment dispersion resists. Examples of inorganic pigments include metal compounds such as metal oxides and metal complex salts. Specifically, iron, cobalt, aluminum, cadmium, lead, copper, titanium, magnesium, chromium, zinc, antimony and other metal compounds. Oxides or mixed metal oxides may be mentioned. Specific examples of organic pigments and inorganic pigments include compounds classified as Pigment under the Color Index (published by The Society of Dyers and Colorists). More specifically, pigments having the following color index (CI) numbers can be mentioned, but the invention is not limited to these.
C.I.ピグメントイエロー20、24、31、53、83、86、93、94、109、110、117、125、137、138、139、147、148、150、153、154、166、173及び180;
C.I.ピグメントオレンジ13、31、36、38、40、42、43、51、55、59、61、64、65及び71;
C.I.ピグメントレッド9、97、105、122、123、144、149、166、168、176、177、180、192、215、216、224、242、254、255及び、264;
C.I.ピグメントバイオレット14、19、23、29、32、33、36、37及び38;
C.I.ピグメントグリーン7、10、15、25、36、47及び58等。
C. I. Pigment yellow 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 137, 138, 139, 147, 148, 150, 153, 154, 166, 173 and 180;
C. I. Pigment orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65 and 71;
C. I. Pigment Red 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 215, 216, 224, 242, 254, 255 and 264;
C. I. Pigment violet 14, 19, 23, 29, 32, 33, 36, 37 and 38;
C. I. Pigment Green 7, 10, 15, 25, 36, 47 and 58 etc.
着色剤(A)の含有量は、着色組成物中の固形分に対して、好ましくは5〜60質量%である。ここで、固形分とは、着色組成物中の、溶剤を除く成分の合計をいう。
着色剤(A)中に含まれる本発明の染料の含有量は、好ましくは3〜100質量%である。
本発明の染料とは異なる染料、及び顔料は、それぞれ単独でも2種以上を組み合わせて本発明の染料と共に用いてもよい。
The content of the colorant (A) is preferably 5 to 60% by mass with respect to the solid content in the colored composition. Here, solid content means the sum total of the component except a solvent in a coloring composition.
The content of the dye of the present invention contained in the colorant (A) is preferably 3 to 100% by mass.
Dyes and pigments different from the dye of the present invention may be used alone or in combination of two or more with the dye of the present invention.
樹脂(B)としては、特に限定されるものではなく、どのような樹脂を用いてもよい。樹脂(B)は、アルカリ可溶性樹脂であることが好ましく、(メタ)アクリル酸から導かれる構造単位を含む樹脂であることがより好ましい。ここで、(メタ)アクリル酸は、アクリル酸及び/又はメタクリル酸を表す。 The resin (B) is not particularly limited, and any resin may be used. The resin (B) is preferably an alkali-soluble resin, and more preferably a resin containing a structural unit derived from (meth) acrylic acid. Here, (meth) acrylic acid represents acrylic acid and / or methacrylic acid.
樹脂(B)としては、具体的には、メタクリル酸/ベンジルメタクリレート共重合体、メタクリル酸/ベンジルメタクリレート/スチレン共重合体、メタクリル酸/ベンジルメタクリレート/イソボルニルメタクリレート共重合体、メタクリル酸/スチレン/ベンジルメタクリレート/N−フェニルマレイミド共重合体、メタクリル酸/スチレン/グリシジルメタクリレート共重合体等が挙げられる。 Specific examples of the resin (B) include methacrylic acid / benzyl methacrylate copolymer, methacrylic acid / benzyl methacrylate / styrene copolymer, methacrylic acid / benzyl methacrylate / isobornyl methacrylate copolymer, methacrylic acid / styrene. / Benzyl methacrylate / N-phenylmaleimide copolymer, methacrylic acid / styrene / glycidyl methacrylate copolymer, and the like.
樹脂(B)のポリスチレン換算重量平均分子量は、5,000〜35,000が好ましく、より好ましくは6,000〜30,000である。
樹脂(B)の酸価は、50〜150mg−KOH/gが好ましく、より好ましくは60〜135mg−KOH/gである。
樹脂(B)の含有量は、着色組成物の固形分に対して、好ましくは7〜65質量%であり、より好ましくは13〜60質量%である。
The weight average molecular weight in terms of polystyrene of the resin (B) is preferably 5,000 to 35,000, and more preferably 6,000 to 30,000.
The acid value of the resin (B) is preferably 50 to 150 mg-KOH / g, more preferably 60 to 135 mg-KOH / g.
Content of resin (B) becomes like this. Preferably it is 7-65 mass% with respect to solid content of a coloring composition, More preferably, it is 13-60 mass%.
重合性化合物(C)は、重合開始剤(D)から発生した活性ラジカル、酸等によって重合しうる化合物であれば、特に限定されるものではない。例えば、重合性のエチレン性不飽和結合を有する化合物等が挙げられる。 The polymerizable compound (C) is not particularly limited as long as it is a compound that can be polymerized by an active radical, an acid, or the like generated from the polymerization initiator (D). For example, the compound etc. which have a polymerizable ethylenically unsaturated bond are mentioned.
前記の重合性化合物(C)としては、重合性基を3個以上有する重合性化合物であることが好ましい。重合性基を3以上有する重合性化合物としては、例えば、ペンタエリスリトールテトラアクリレート、ペンタエリスリトールテトラメタクリレート、ジペンタエリスリトールペンタアクリレート、ジペンタエリスリトールペンタメタクリレート、ジペンタエリスリトールヘキサアクリレート、ジペンタエリスリトールヘキサメタクリレート等が挙げられる。前記の重合性化合物(C)は、単独でも2種以上を組み合わせて用いてもよい。
重合性化合物(C)の含有量は、着色組成物の固形分に対して、5〜65質量%であることが好ましく、より好ましくは10〜60質量%である。
The polymerizable compound (C) is preferably a polymerizable compound having three or more polymerizable groups. Examples of the polymerizable compound having 3 or more polymerizable groups include pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, dipentaerythritol pentaacrylate, dipentaerythritol pentamethacrylate, dipentaerythritol hexaacrylate, dipentaerythritol hexamethacrylate, and the like. Can be mentioned. The polymerizable compound (C) may be used alone or in combination of two or more.
It is preferable that content of a polymeric compound (C) is 5-65 mass% with respect to solid content of a coloring composition, More preferably, it is 10-60 mass%.
前記の重合開始剤(D)としては、活性ラジカル発生剤、酸発生剤等が挙げられる。活性ラジカル発生剤は熱又は光の作用によって活性ラジカルを発生する。前記の活性ラジカル発生剤としては、アルキルフェノン化合物、チオキサントン化合物、トリアジン化合物、オキシム化合物等が挙げられる。
前記のアルキルフェノン化合物としては、例えば、2−メチル−2−モルホリノ−1−(4−メチルスルファニルフェニル)プロパン−1−オン、2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン、ベンジルジメチルケタール、2−ヒドロキシ−2−メチル−1−〔4−(2−ヒドロキシエトキシ)フェニル〕プロパン−1−オン、1−ヒドロキシシクロヘキシルフェニルケトン等が挙げられる。
As said polymerization initiator (D), an active radical generator, an acid generator, etc. are mentioned. Active radical generators generate active radicals by the action of heat or light. Examples of the active radical generator include alkylphenone compounds, thioxanthone compounds, triazine compounds, and oxime compounds.
Examples of the alkylphenone compound include 2-methyl-2-morpholino-1- (4-methylsulfanylphenyl) propan-1-one, 2-hydroxy-2-methyl-1-phenylpropan-1-one, Examples include benzyldimethyl ketal, 2-hydroxy-2-methyl-1- [4- (2-hydroxyethoxy) phenyl] propan-1-one, 1-hydroxycyclohexyl phenyl ketone, and the like.
前記のチオキサントン化合物としては、例えば、2−イソプロピルチオキサントン、4−イソプロピルチオキサントン、2,4−ジエチルチオキサントン、2,4−ジクロロチオキサントン、1−クロロ−4−プロポキシチオキサントン等が挙げられる。 Examples of the thioxanthone compound include 2-isopropylthioxanthone, 4-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 1-chloro-4-propoxythioxanthone, and the like.
前記のトリアジン化合物としては、例えば、2,4−ビス(トリクロロメチル)−6−(4−メトキシフェニル)−1,3,5−トリアジン、2,4−ビス(トリクロロメチル)−6−(4−メトキシナフチル)−1,3,5−トリアジン、2,4−ビス(トリクロロメチル)−6−(4−メトキシスチリル)−1,3,5−トリアジン、2,4−ビス(トリクロロメチル)−6−〔2−(5−メチルフラン−2−イル)エテニル〕−1,3,5−トリアジン、2,4−ビス(トリクロロメチル)−6−〔2−(フラン−2−イル)エテニル〕−1,3,5−トリアジン、2,4−ビス(トリクロロメチル)−6−〔2−(4−ジエチルアミノ−2−メチルフェニル)エテニル〕−1,3,5−トリアジン、2,4−ビス(トリクロロメチル)−6−〔2−(3,4−ジメトキシフェニル)エテニル〕−1,3,5−トリアジン等が挙げられる。 Examples of the triazine compound include 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4 -Methoxynaphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxystyryl) -1,3,5-triazine, 2,4-bis (trichloromethyl)- 6- [2- (5-Methylfuran-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (furan-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (4-diethylamino-2-methylphenyl) ethenyl] -1,3,5-triazine, 2,4-bis (Trichloromethyl 6- [2- (3,4-dimethoxyphenyl) ethenyl] -1,3,5-triazine.
前記のオキシム化合物としては、例えば、O−アシルオキシム系化合物が挙げられ、その具体例としては、N−ベンゾイルオキシ−1−(4−フェニルスルファニルフェニル)ブタン−1−オン−2−イミン、N−ベンゾイルオキシ−1−(4−フェニルスルファニルフェニル)オクタン−1−オン−2−イミン、N−アセトキシ−1−[9−エチル−6−(2−メチルベンゾイル)−9H−カルバゾール−3−イル]エタン−1−イミン、N−アセトキシ−1−[9−エチル−6−{2−メチル−4−(3,3−ジメチル−2,4−ジオキサシクロペンタニルメチルオキシ)ベンゾイル}−9H−カルバゾール−3−イル]エタン−1−イミン等が挙げられる。 Examples of the oxime compound include O-acyloxime compounds, and specific examples thereof include N-benzoyloxy-1- (4-phenylsulfanylphenyl) butan-1-one-2-imine, N -Benzoyloxy-1- (4-phenylsulfanylphenyl) octane-1-one-2-imine, N-acetoxy-1- [9-ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl ] Ethane-1-imine, N-acetoxy-1- [9-ethyl-6- {2-methyl-4- (3,3-dimethyl-2,4-dioxacyclopentanylmethyloxy) benzoyl} -9H -Carbazol-3-yl] ethane-1-imine and the like.
また、活性ラジカル発生剤としては、例えば、2,4,6−トリメチルベンゾイルジフェニルホスフィンオキサイド、2,2’−ビス(o−クロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、10−ブチル−2−クロロアクリドン、2−エチルアントラキノン、ベンジル、9,10−フェナンスレンキノン、カンファーキノン、フェニルグリオキシル酸メチル、チタノセン化合物等を用いてもよい。 Examples of the active radical generator include 2,4,6-trimethylbenzoyldiphenylphosphine oxide, 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetraphenyl-1, 2'-biimidazole, 10-butyl-2-chloroacridone, 2-ethylanthraquinone, benzyl, 9,10-phenanthrenequinone, camphorquinone, methyl phenylglyoxylate, titanocene compound and the like may be used.
前記の酸発生剤としては、例えば、4−ヒドロキシフェニルジメチルスルホニウムp−トルエンスルホナート、4−ヒドロキシフェニルジメチルスルホニウムヘキサフルオロアンチモネート、4−アセトキシフェニルジメチルスルホニウムp−トルエンスルホナート、4−アセトキシフェニル・メチル・ベンジルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムp−トルエンスルホナート、トリフェニルスルホニウムヘキサフルオロアンチモネート、ジフェニルヨードニウムp−トルエンスルホナート、ジフェニルヨードニウムヘキサフルオロアンチモネート等のオニウム塩類や、ニトロベンジルトシレート類、ベンゾイントシレート類等を挙げることができる。
前記の重合開始剤は、単独でも2種以上を組み合わせて用いてもよい。
Examples of the acid generator include 4-hydroxyphenyldimethylsulfonium p-toluenesulfonate, 4-hydroxyphenyldimethylsulfonium hexafluoroantimonate, 4-acetoxyphenyldimethylsulfonium p-toluenesulfonate, 4-acetoxyphenyl, Onium salts such as methyl benzylsulfonium hexafluoroantimonate, triphenylsulfonium p-toluenesulfonate, triphenylsulfonium hexafluoroantimonate, diphenyliodonium p-toluenesulfonate, diphenyliodonium hexafluoroantimonate, and nitrobenzyl tosylate And benzoin tosylate.
The above polymerization initiators may be used alone or in combination of two or more.
重合開始剤(D)の含有量は、樹脂(B)及び重合性化合物(C)の合計量100質量部に対して、好ましくは0.1〜30質量部であり、より好ましくは1〜20質量部である。重合開始剤の含有量が、前記の範囲にあると、高感度化して露光時間が短縮され生産性が向上することから好ましい。 The content of the polymerization initiator (D) is preferably 0.1 to 30 parts by mass, more preferably 1 to 20 parts per 100 parts by mass of the total amount of the resin (B) and the polymerizable compound (C). Part by mass. When the content of the polymerization initiator is within the above range, it is preferable because the sensitivity is increased, the exposure time is shortened, and the productivity is improved.
溶剤(E)としては、例えば、エーテル類、芳香族炭化水素類、ケトン類、アルコール類、エステル類、アミド類等が挙げられる。 Examples of the solvent (E) include ethers, aromatic hydrocarbons, ketones, alcohols, esters, amides, and the like.
前記のエーテル類としては、例えば、テトラヒドロフラン、テトラヒドロピラン、1,4−ジオキサン、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールジプロピルエーテル、ジエチレングリコールジブチルエーテル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノブチルエーテルアセテート等が挙げられる。 Examples of the ethers include tetrahydrofuran, tetrahydropyran, 1,4-dioxane, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether. , Diethylene glycol monobutyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol methyl ethyl ether, diethylene glycol dipropyl ether, diethylene glycol dibutyl ether, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, Propylene glycol monopropyl ether acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate and the like.
前記の芳香族炭化水素類としては、例えば、ベンゼン、トルエン、キシレン、メシチレン等が挙げられる。
前記のケトン類としては、例えば、アセトン、2−ブタノン、2−ヘプタノン、3−ヘプタノン、4−ヘプタノン、4−メチル−2−ペンタノン、4−ヒドロキシ−4−メチル−2−ペンタノン、シクロペンタノン、シクロヘキサノン等が挙げられる。
前記のアルコール類としては、例えば、メタノール、エタノール、プロパノール、ブタノール、ヘキサノール、シクロヘキサノール、エチレングリコール、グリセリン等が挙げられる。
Examples of the aromatic hydrocarbons include benzene, toluene, xylene, mesitylene and the like.
Examples of the ketones include acetone, 2-butanone, 2-heptanone, 3-heptanone, 4-heptanone, 4-methyl-2-pentanone, 4-hydroxy-4-methyl-2-pentanone, and cyclopentanone. And cyclohexanone.
Examples of the alcohols include methanol, ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol, and glycerin.
前記のエステル類としては、例えば、酢酸エチル、酢酸n−ブチル、酢酸イソブチル、ギ酸アミル、酢酸イソアミル、酢酸イソブチル、プロピオン酸ブチル、酪酸イソプロピル、酪酸エチル、酪酸ブチル、アルキルエステル類、乳酸メチル、乳酸エチル、乳酸ブチル、メトキシ酢酸メチル、メトキシ酢酸エチル、メトキシ酢酸ブチル、エトキシ酢酸メチル、エトキシ酢酸エチル、3−メトキシプロピオン酸メチル、3−メトキシプロピオン酸エチル、3−エトキシプロピオン酸メチル、3−エトキシプロピオン酸エチル、2−メトキシプロピオン酸メチル、2−メトキシプロピオン酸エチル、2−メトキシプロピオン酸プロピル、2−エトキシプロピオン酸メチル、2−エトキシプロピオン酸エチル、2−メトキシ−2−メチルプロピオン酸メチル、2−エトキシ−2−メチルプロピオン酸エチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、アセト酢酸メチル、アセト酢酸エチル、3−メトキシブチルアセテート、3−メチル−3−メトキシブチルアセテート、γ−ブチロラクトン等が挙げられる。 Examples of the esters include ethyl acetate, n-butyl acetate, isobutyl acetate, amyl formate, isoamyl acetate, isobutyl acetate, butyl propionate, isopropyl butyrate, ethyl butyrate, butyl butyrate, alkyl esters, methyl lactate, and lactic acid. Ethyl, butyl lactate, methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate, ethyl ethoxyacetate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, 3-ethoxypropion Ethyl acetate, methyl 2-methoxypropionate, ethyl 2-methoxypropionate, propyl 2-methoxypropionate, methyl 2-ethoxypropionate, ethyl 2-ethoxypropionate, 2-methoxy-2-methylpropionic acid Chill, ethyl 2-ethoxy-2-methylpropionate, methyl pyruvate, ethyl pyruvate, propyl pyruvate, methyl acetoacetate, ethyl acetoacetate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, γ -Butyrolactone etc. are mentioned.
前記のアミド類としては、例えば、N,N−ジメチルホルムアミド、N,N−ジメチルアセトアミド、N−メチルピロリドン等が挙げられる。
これらの溶剤は、単独でも2種類以上を組み合わせて用いてもよい。
Examples of the amides include N, N-dimethylformamide, N, N-dimethylacetamide, N-methylpyrrolidone and the like.
These solvents may be used alone or in combination of two or more.
着色組成物における溶剤(E)の含有量は、着色組成物に対して、好ましくは70〜95質量%であり、より好ましくは75〜90質量%である。 Content of the solvent (E) in a coloring composition becomes like this. Preferably it is 70-95 mass% with respect to a coloring composition, More preferably, it is 75-90 mass%.
本発明の着色組成物は、必要に応じて、界面活性剤、充填剤、他の高分子化合物、密着促進剤、酸化防止剤、紫外線吸収剤、光安定剤、連鎖移動剤等の種々の添加剤を含んでもよい。 The coloring composition of the present invention may be added as necessary, such as surfactants, fillers, other polymer compounds, adhesion promoters, antioxidants, ultraviolet absorbers, light stabilizers, chain transfer agents, etc. An agent may be included.
本発明の塩は、染料として有用である。モル吸光係数が高く、かつ有機溶媒への高い溶解性を示すことから、特に、液晶表示装置等の表示装置のカラーフィルタに用いられる染料として有用である。
また、本発明の塩を含む着色組成物は、カラーフィルタをその構成部品の一部として備える表示装置(例えば、公知の液晶表示装置、有機EL装置等)、固体撮像素子等の種々の着色画像に関連する機器に、公知の態様で利用することができる。
The salt of the present invention is useful as a dye. Since it has a high molar extinction coefficient and high solubility in an organic solvent, it is particularly useful as a dye used in a color filter of a display device such as a liquid crystal display device.
In addition, the colored composition containing the salt of the present invention has various colored images such as a display device (for example, a known liquid crystal display device or an organic EL device) having a color filter as a part of its constituent parts, a solid-state imaging device, or the like. It can be used in a known manner for devices related to the above.
以下、実施例によって本発明の着色感光性樹脂組成物についてより詳細に説明する。例中の「%」及び「部」は、特記ない限り、質量%及び質量部である。 Hereinafter, the colored photosensitive resin composition of the present invention will be described in more detail with reference to examples. Unless otherwise specified, “%” and “parts” in the examples are% by mass and parts by mass.
以下の実施例において、化合物は元素分析(VARIO-EL;(エレメンタール(株)製))により同定した。 In the following examples, compounds were identified by elemental analysis (VARIO-EL; (Elemental Co., Ltd.)).
実施例1
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)0.85部をN,N−ジメチルホルミアミド50部に溶解させた溶液(s1)を作成した。別途、式(d−1)で表される化合物(CasOrganic社製)1.02部をN,N−ジメチルホルミアミド10部に溶解させた溶液(t1)を作製した。25℃にて、(s1)に(t1)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、イオン交換水500部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部で洗浄し、式(I−1)で表される塩を1.18部得た。
Example 1
A solution in which 0.85 part of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 50 parts of N, N-dimethylformamide ( s1) was created. Separately, a solution (t1) was prepared by dissolving 1.02 part of the compound represented by the formula (d-1) (manufactured by Cas Organic) in 10 parts of N, N-dimethylformamide. The solution of (t1) was added to (s1) at 25 ° C., and then the temperature was raised to 80 ° C. and stirred for 8 hours. After the mixture was cooled to room temperature, 500 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion-exchanged water to obtain 1.18 parts of a salt represented by the formula (I-1).
式(I−1)で表される塩の同定;
(元素分析)C:77.7 H:8.0 N:2.6
Identification of a salt represented by formula (I-1);
(Elemental analysis) C: 77.7 H: 8.0 N: 2.6
尚、原料として用いた式(f−1)で表される化合物0.35gをクロロホルムに溶解して体積を250cm3とし、そのうちの2cm3をクロロホルムで希釈して100cm3として、濃度0.028g/Lの溶液を調整した。該溶液について、紫外可視分光光度計(V−650DS;日本分光(株)製)(石英セル、光路長;1cm)を用いて400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は425nmであり、吸光度は0.0019であった。 In addition, 0.35 g of the compound represented by the formula (f-1) used as a raw material was dissolved in chloroform to a volume of 250 cm 3 , 2 cm 3 of which was diluted with chloroform to 100 cm 3 and a concentration of 0.028 g. A solution of / L was prepared. About this solution, the absorbance at 400 to 900 nm and the absorbance at the maximum absorption wavelength were measured using an ultraviolet-visible spectrophotometer (V-650DS; manufactured by JASCO Corporation) (quartz cell, optical path length: 1 cm). However, the maximum absorption wavelength was 425 nm, and the absorbance was 0.0019.
実施例2
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)1.0部をN,N−ジメチルホルミアミド70部に溶解させた溶液(s2)を作成した。別途、下記式(d−2)で表される化合物(ビクトリアピュアブルーBO、アルドリッチ社製)3.92部をN,N−ジメチルホルミアミド90部に溶解させた溶液(t2)を作成した。25℃にて、(s2)に(t2)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水100部、次いでイオン交換水1000部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部とヘキサン100部で洗浄し、式(I−3)で表される塩を1.70部得た。
Example 2
A solution in which 1.0 part of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 70 parts of N, N-dimethylformamide ( s2) was created. Separately, a solution (t2) was prepared by dissolving 3.92 parts of a compound represented by the following formula (d-2) (Victoria Pure Blue BO, manufactured by Aldrich) in 90 parts of N, N-dimethylformamide. . The solution of (t2) was added to (s2) at 25 ° C, and then the temperature was raised to 80 ° C and stirred for 8 hours. After the mixture was cooled to room temperature, 100 parts of saturated brine and then 1000 parts of ion-exchanged water were added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 100 parts of ion-exchanged water and 100 parts of hexane to obtain 1.70 parts of a salt represented by the formula (I-3).
式(I−3)で表される塩の同定;
(元素分析)C:75.6 H:7.9 N:4.2
Identification of a salt represented by formula (I-3);
(Elemental analysis) C: 75.6 H: 7.9 N: 4.2
実施例3
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)2.0部をN,N−ジメチルホルミアミド120部に溶解させた溶液(s3)を作成した。別途、ORIENT(登録商標)Oil BLUE 613(C.I.Solvent Blue 5と樹脂との混合物、オリヱント化学工業(株)製)1.96部をN,N−ジメチルホルミアミド24部に溶解させた溶液(t3)を作成した。25℃にて、(s3)に(t3)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、イオン交換水700部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部で洗浄し、式(I−3)で表される塩を含む混合物を2.27部得た。
Example 3
A solution in which 2.0 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 120 parts of N, N-dimethylformamide ( s3) was created. Separately, 1.96 parts of ORIENT (registered trademark) Oil BLUE 613 (mixture of CI Solvent Blue 5 and resin, manufactured by Orient Chemical Co., Ltd.) was dissolved in 24 parts of N, N-dimethylformamide. Solution (t3) was prepared. The solution of (t3) was added to (s3) at 25 ° C., and then the temperature was raised to 80 ° C. and stirred for 8 hours. After the mixture was cooled to room temperature, 700 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion exchange water to obtain 2.27 parts of a mixture containing a salt represented by the formula (I-3).
化合物(1)の合成例1
3,5,6−トリクロロサリチル酸5.00部に水250部を加え、60度で撹拌し溶解し、さらに水酸化ナトリウムを加え、pHを7に調整した。さらに、硫酸クロム水和物2.03部を水200部に溶解させた溶液を添加し、90度で5時間攪拌した。該混合液を室温まで冷却した後、未反応の3,5,6−トリクロロサリチル酸を濾別し、濾液に飽和食塩水500部を添加し、1時間撹拌した。析出物を吸引濾過で取得し、飽和食塩水で洗浄し、式(f−2)で表される化合物を、Z+がヒドロンである化合物とナトリウムイオンである化合物との混合物として2.02部得た。
Synthesis Example 1 of Compound (1)
250 parts of water was added to 5.00 parts of 3,5,6-trichlorosalicylic acid, and the mixture was stirred and dissolved at 60 ° C. Sodium hydroxide was further added to adjust the pH to 7. Further, a solution prepared by dissolving 2.03 parts of chromium sulfate hydrate in 200 parts of water was added and stirred at 90 degrees for 5 hours. After cooling the mixture to room temperature, unreacted 3,5,6-trichlorosalicylic acid was filtered off, 500 parts of saturated brine was added to the filtrate, and the mixture was stirred for 1 hour. The precipitate is obtained by suction filtration, washed with saturated brine, and 2.02 parts of the compound represented by formula (f-2) as a mixture of a compound in which Z + is hydrone and a compound in which sodium ion is used. Obtained.
式(f−1)で表される化合物と同様の方法で、式(f−2)で表される化合物の400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は400nmであり、吸光度は0.0066であった。 When the maximum absorption wavelength at 400 to 900 nm and the absorbance at the maximum absorption wavelength of the compound represented by formula (f-2) were measured in the same manner as the compound represented by formula (f-1), the maximum absorption was obtained. The wavelength was 400 nm and the absorbance was 0.0066.
化合物(1)の合成例2
3,5−ジブロモサリチル酸10.00部に水250部を加え、60度で撹拌し溶解し、さらに水酸化ナトリウムを加え、pHを7に調整した。さらに、硫酸クロム水和物2.90部を水400部に溶解させた溶液を添加し、90度で5時間攪拌した。該混合液を室温まで冷却した後、未反応の3,5−ジブロモサリチル酸を濾別し、濾液に水1000部を添加し、1時間撹拌した。析出物を吸引濾過で取得し、水で洗浄し、式(f−3)で表される化合物を、Z+がヒドロンである化合物とナトリウムイオンである化合物との混合物として4.89部得た。
Synthesis example 2 of compound (1)
250 parts of water was added to 10.00 parts of 3,5-dibromosalicylic acid, dissolved by stirring at 60 ° C., and sodium hydroxide was further added to adjust the pH to 7. Further, a solution prepared by dissolving 2.90 parts of chromium sulfate hydrate in 400 parts of water was added and stirred at 90 degrees for 5 hours. After the mixture was cooled to room temperature, unreacted 3,5-dibromosalicylic acid was filtered off, 1000 parts of water was added to the filtrate, and the mixture was stirred for 1 hour. The precipitate was collected by suction filtration and washed with water to obtain 4.89 parts of the compound represented by formula (f-3) as a mixture of a compound in which Z + is hydrone and a compound in which sodium ion is used. .
式(f−1)で表される化合物と同様の方法で、式(f−3)で表される化合物の400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は400nmであり、吸光度は0.031であった。 When the maximum absorption wavelength at 400 to 900 nm and the absorbance at the maximum absorption wavelength of the compound represented by formula (f-3) were measured in the same manner as the compound represented by formula (f-1), the maximum absorption was obtained. The wavelength was 400 nm and the absorbance was 0.031.
化合物(1)の合成例3
3,5,6−トリクロロサリチル酸10.00部に水150部を加え、60度で撹拌し溶解し、さらに水酸化ナトリウムを加え、pHを7に調整した。さらに、硫酸アルミニウム4.06部を水200部に溶解させた溶液を添加し、90度で5時間攪拌した。該混合液を室温まで冷却した後、未反応の3,5,6−トリクロロサリチル酸を濾別し、飽和食塩水500部を添加し、1時間撹拌した。析出物を吸引濾過で取得し、水で洗浄し、式(f−4)で表される化合物を、Z+がヒドロンである化合物とナトリウムイオンである化合物との混合物として6.02部得た。
Synthesis Example 3 of Compound (1)
150 parts of water was added to 10.00 parts of 3,5,6-trichlorosalicylic acid, and the mixture was stirred and dissolved at 60 ° C. Sodium hydroxide was further added to adjust the pH to 7. Further, a solution prepared by dissolving 4.06 parts of aluminum sulfate in 200 parts of water was added and stirred at 90 degrees for 5 hours. After cooling the mixture to room temperature, unreacted 3,5,6-trichlorosalicylic acid was filtered off, 500 parts of saturated brine was added, and the mixture was stirred for 1 hour. The precipitate was obtained by suction filtration and washed with water to obtain 6.02 parts of the compound represented by formula (f-4) as a mixture of a compound in which Z + is hydrone and a compound in which sodium ion is used. .
式(f−1)で表される化合物と同様の方法で、式(f−4)で表される化合物の400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は400nmであり、吸光度は0.0036であった。 When the maximum absorption wavelength at 400 to 900 nm and the absorbance at the maximum absorption wavelength of the compound represented by formula (f-4) were measured by the same method as that for the compound represented by formula (f-1), the maximum absorption was obtained. The wavelength was 400 nm and the absorbance was 0.0036.
化合物(1)の合成例4
3,5−ジブロモサリチル酸10.00部に水250部を加え、60度で撹拌し溶解し、さらに水酸化ナトリウムを加え、pHを7に調整した。さらに、硫酸アルミニウム2.89部を水200部に溶解させた溶液を添加し、90度で6時間攪拌した。該混合液を室温まで冷却した後、未反応の3,5−ジブロモサリチル酸を濾別し、濾液に水1000部を添加し、1時間撹拌した。析出物を吸引濾過で取得し、水で洗浄し、式(f−5)で表される化合物を、Z+がヒドロンである化合物とナトリウムイオンである化合物との混合物として10.02部得た。
Synthesis Example 4 of Compound (1)
250 parts of water was added to 10.00 parts of 3,5-dibromosalicylic acid, dissolved by stirring at 60 ° C., and sodium hydroxide was further added to adjust the pH to 7. Further, a solution prepared by dissolving 2.89 parts of aluminum sulfate in 200 parts of water was added and stirred at 90 degrees for 6 hours. After the mixture was cooled to room temperature, unreacted 3,5-dibromosalicylic acid was filtered off, 1000 parts of water was added to the filtrate, and the mixture was stirred for 1 hour. The precipitate was obtained by suction filtration, washed with water, and 10.02 parts of the compound represented by the formula (f-5) was obtained as a mixture of a compound in which Z + is hydrone and a compound in which sodium ion is used. .
式(f−1)で表される化合物と同様の方法で、式(f−5)で表される化合物の400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は637nmであり、吸光度は0.0049であった。 When the maximum absorption wavelength at 400 to 900 nm and the absorbance at the maximum absorption wavelength of the compound represented by formula (f-5) were measured by the same method as that for the compound represented by formula (f-1), the maximum absorption was obtained. The wavelength was 637 nm and the absorbance was 0.0049.
化合物(1)の合成例5
2,4−ジヒドロキシ安息香酸10.00部に水250部を加え、60度で撹拌し溶解し、さらに水酸化ナトリウムを加え、pHを7に調整した。さらに、硫酸アルミニウム5.55部を水200部に溶解させた溶液を添加し、90度で6時間攪拌した。該混合液を室温まで冷却した後、未反応の2,4−ジヒドロキシ安息香酸を濾別し、濾液に水1000部を添加し、1時間撹拌した。析出物を吸引濾過で取得し、水で洗浄し、式(f−6)で表される化合物を、Z+がヒドロンである化合物とナトリウムイオンである化合物との混合物として6.51部得た。
Synthesis example 5 of compound (1)
250 parts of water was added to 10.00 parts of 2,4-dihydroxybenzoic acid, dissolved by stirring at 60 degrees, and sodium hydroxide was added to adjust the pH to 7. Further, a solution prepared by dissolving 5.55 parts of aluminum sulfate in 200 parts of water was added and stirred at 90 degrees for 6 hours. After the mixture was cooled to room temperature, unreacted 2,4-dihydroxybenzoic acid was filtered off, 1000 parts of water was added to the filtrate, and the mixture was stirred for 1 hour. The precipitate was obtained by suction filtration and washed with water to obtain 6.51 parts of the compound represented by the formula (f-6) as a mixture of a compound in which Z + is hydrone and a compound in which sodium ion is used. .
式(f−1)で表される化合物と同様の方法で、式(f−6)で表される化合物の400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は400nmであり、吸光度は0.022であった。 When the maximum absorption wavelength at 400 to 900 nm and the absorbance at the maximum absorption wavelength of the compound represented by formula (f-6) were measured by the same method as that for the compound represented by formula (f-1), the maximum absorption was obtained. The wavelength was 400 nm and the absorbance was 0.022.
化合物(1)の合成例6
2,5−ジヒドロキシ安息香酸10.00部に水250部を加え、60度で撹拌し溶解し、さらに水酸化ナトリウムを加え、pHを7に調整した。さらに、硫酸アルミニウム5.55部を水200部に溶解させた溶液を添加し、90度で6時間攪拌した。該混合液を室温まで冷却した後、未反応の2,5−ジヒドロキシ安息香酸を濾別し、濾液に水1000部を添加し、1時間撹拌した。析出物を吸引濾過で取得し、水で洗浄し、式(f−7)で表される化合物を、Z+がヒドロンである化合物とナトリウムイオンである化合物との混合物として10.01部得た。
Synthesis Example 6 of Compound (1)
250 parts of water was added to 10.00 parts of 2,5-dihydroxybenzoic acid, dissolved by stirring at 60 degrees, and sodium hydroxide was further added to adjust the pH to 7. Further, a solution prepared by dissolving 5.55 parts of aluminum sulfate in 200 parts of water was added and stirred at 90 degrees for 6 hours. After the mixture was cooled to room temperature, unreacted 2,5-dihydroxybenzoic acid was filtered off, 1000 parts of water was added to the filtrate, and the mixture was stirred for 1 hour. The precipitate was obtained by suction filtration, washed with water, and 10.1 parts of the compound represented by the formula (f-7) was obtained as a mixture of a compound in which Z + is hydrone and a compound in which sodium ion is used. .
式(f−1)で表される化合物と同様の方法で、式(f−7)で表される化合物の400〜900nmにおける極大吸収波長及び極大吸収波長での吸光度を測定したところ、極大吸収波長は400nmであり、吸光度は0.048であった。 When the maximum absorption wavelength at 400 to 900 nm and the absorbance at the maximum absorption wavelength of the compound represented by formula (f-7) were measured by the same method as that for the compound represented by formula (f-1), the maximum absorption was obtained. The wavelength was 400 nm and the absorbance was 0.048.
実施例4
式(f−8)で表される化合物(BONTRON(登録商標)E−81、オリヱント化学工業(株)製)2.00部をN,N−ジメチルホルミアミド150部に溶解させた溶液(s4)を作成した。別途、ORIENT(登録商標)Oil BLUE 613(C.I.Solvent Blue 5と樹脂との混合物、オリヱント化学工業(株)製)1.80部をN,N−ジメチルホルミアミド25部に溶解させた溶液(t4)を作成した。25℃にて、(s3)に(t3)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、イオン交換水500部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部で洗浄し、式(I−4)で表される塩を含む混合物2.11部得た。
Example 4
A solution in which 2.00 parts of a compound represented by the formula (f-8) (BONTRON (registered trademark) E-81, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 150 parts of N, N-dimethylformamide ( s4) was created. Separately, 1.80 parts of ORIENT (registered trademark) Oil BLUE 613 (mixture of CI Solvent Blue 5 and resin, manufactured by Orient Chemical Co., Ltd.) was dissolved in 25 parts of N, N-dimethylformamide. Solution (t4) was prepared. The solution of (t3) was added to (s3) at 25 ° C., and then the temperature was raised to 80 ° C. and stirred for 8 hours. After the mixture was cooled to room temperature, 500 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion-exchanged water to obtain 2.11 parts of a mixture containing a salt represented by the formula (I-4).
実施例5
式(f−3)で表される化合物2.10部をN,N−ジメチルホルミアミド150部に溶解させた溶液(s5)を作成した。別途、別途、式(d−1)で表される化合物(CasOrganic社製)1.99部をN,N−ジメチルホルミアミド19部に溶解させた溶液(t5)を作成した。25℃にて、(s5)に(t5)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、イオン交換水500部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部で洗浄し、式(I−5)で表される塩を2.50部得た。
Example 5
A solution (s5) was prepared by dissolving 2.10 parts of the compound represented by the formula (f-3) in 150 parts of N, N-dimethylformamide. Separately, a solution (t5) was prepared by dissolving 1.99 parts of the compound represented by the formula (d-1) (manufactured by Cas Organic) in 19 parts of N, N-dimethylformamide. The solution of (t5) was added to (s5) at 25 ° C, and then the temperature was raised to 80 ° C and stirred for 8 hours. After the mixture was cooled to room temperature, 500 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion-exchanged water to obtain 2.50 parts of a salt represented by the formula (I-5).
式(I−5)で表される塩の同定;
(元素分析)C:53.7 H:4.1 N:2.3
Identification of a salt represented by the formula (I-5);
(Elemental analysis) C: 53.7 H: 4.1 N: 2.3
実施例6
式(f−4)で表される化合物2.00部をN,N−ジメチルホルミアミド150部に溶解させた溶液(s6)を作成した。別途、別途、式(d−1)で表される化合物(CasOrganic社製)1.49部をN,N−ジメチルホルミアミド30部に溶解させた溶液(t6)を作成した。25℃にて、(s6)に(t6)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水50部を加え、1時間撹拌し、さらにイオン交換水300部を加え、2時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部で洗浄し、式(I−6)で表される塩を2.53部得た。
Example 6
A solution (s6) was prepared by dissolving 2.00 parts of the compound represented by the formula (f-4) in 150 parts of N, N-dimethylformamide. Separately, a solution (t6) was prepared by dissolving 1.49 parts of the compound represented by formula (d-1) (manufactured by Cas Organic) in 30 parts of N, N-dimethylformamide. The solution of (t6) was added to (s6) at 25 ° C, and then the temperature was raised to 80 ° C and stirred for 8 hours. After cooling the mixture to room temperature, 50 parts of saturated brine was added and stirred for 1 hour, and further 300 parts of ion-exchanged water was added and stirred for 2 hours. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion-exchanged water to obtain 2.53 parts of a salt represented by the formula (I-6).
式(I−6)で表される塩の同定;
(元素分析)C:60.7 H:4.5 N:2.6
Identification of the salt represented by the formula (I-6);
(Elemental analysis) C: 60.7 H: 4.5 N: 2.6
実施例7
式(f−6)で表される化合物1.60部をN,N−ジメチルホルミアミド130部に溶解させた溶液(s7)を作成した。別途、ORIENT(登録商標)Oil BLUE 613(C.I.Solvent Blue 5と樹脂との混合物、オリヱント化学工業(株)製)1.98部をN,N−ジメチルホルミアミド40部に溶解させた溶液(t7)を作成した。25℃にて、(s7)に(t7)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水200部、次いでイオン交換水600部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部で洗浄し、式(I−7)で表される塩を含む混合物1.31部得た。
Example 7
A solution (s7) was prepared by dissolving 1.60 parts of the compound represented by the formula (f-6) in 130 parts of N, N-dimethylformamide. Separately, 1.98 parts of ORIENT (registered trademark) Oil BLUE 613 (mixture of CI Solvent Blue 5 and resin, manufactured by Orient Chemical Co., Ltd.) was dissolved in 40 parts of N, N-dimethylformamide. Solution (t7) was prepared. The solution of (t7) was added to (s7) at 25 ° C, and then the temperature was raised to 80 ° C and stirred for 8 hours. After cooling the mixture to room temperature, 200 parts of saturated brine and then 600 parts of ion-exchanged water were added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion-exchanged water to obtain 1.31 parts of a mixture containing a salt represented by the formula (I-7).
実施例8
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)3.0部をN,N−ジメチルホルミアミド200部に溶解させた溶液(s8)を作成した。別途、下記式(h−1)で表される化合物3.49部をN,N−ジメチルホルミアミド40部に溶解させた溶液(t8)を作成した。25℃にて、(s8)に(t8)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水50部、次いでイオン交換水300部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部とヘキサン100部で洗浄し、式(I−31)で表される塩を3.15部得た。
Example 8
A solution in which 3.0 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 200 parts of N, N-dimethylformamide ( s8) was created. Separately, a solution (t8) was prepared by dissolving 3.49 parts of the compound represented by the following formula (h-1) in 40 parts of N, N-dimethylformamide. The solution of (t8) was added to (s8) at 25 ° C, and then the temperature was raised to 80 ° C and stirred for 8 hours. After the mixture was cooled to room temperature, 50 parts of saturated brine and then 300 parts of ion-exchanged water were added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion exchange water and 100 parts of hexane to obtain 3.15 parts of a salt represented by the formula (I-31).
式(I−31)で表される塩の同定;
(元素分析)C:69.7 H:7.7 N:2.6
Identification of a salt represented by formula (I-31);
(Elemental analysis) C: 69.7 H: 7.7 N: 2.6
実施例9
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)1.50部をN,N−ジメチルホルミアミド120部に溶解させた溶液(s9)を作成した。別途、下記式(h−2)で表される化合物1.30部をN,N−ジメチルホルミアミド30部に溶解させた溶液(t9)を作成した。25℃にて、(s9)に(t9)の溶液を添加し、その後80℃に昇温し、6.5時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水100部、次いでイオン交換水700部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部とヘキサン100部で洗浄し、式(I−32)で表される塩を1.50部得た。
Example 9
A solution in which 1.50 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 120 parts of N, N-dimethylformamide ( s9) was created. Separately, a solution (t9) was prepared by dissolving 1.30 parts of the compound represented by the following formula (h-2) in 30 parts of N, N-dimethylformamide. The solution of (t9) was added to (s9) at 25 ° C., and then the temperature was raised to 80 ° C. and stirred for 6.5 hours. After the mixture was cooled to room temperature, 100 parts of saturated brine and then 700 parts of ion-exchanged water were added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion-exchanged water and 100 parts of hexane to obtain 1.50 parts of a salt represented by the formula (I-32).
式(I−32)で表される塩の同定;
(元素分析)C:70.7 H:7.6 N:2.6
Identification of a salt represented by formula (I-32);
(Elemental analysis) C: 70.7 H: 7.6 N: 2.6
実施例10
混合中に混合物の温度が30℃以下になるように、98%硫酸50部に2−(4−ジエチルアミノ−2−ヒドロキシベンゾイル)安息香酸(東京化成工業(株)製)7.83部を徐々に加えて混合した。得られた溶液を5℃まで冷却し、そこに3−(イソプロピルアミノ)フェノール(特開平9−169708号公報に記載された方法に準じて製造)5.37部を加えた。その後、この混合物を5℃で65時間撹拌した。反応混合物を氷水250部中に添加し、析出物を吸引濾過で取得した。残渣をクロロホルム180部に溶解し、イオン交換水300部を加え、さらに10%水酸化ナトリウム水溶液で水層をpH10として、1時間撹拌した。クロロホルム層を分取し、イオン交換水200部で洗浄し、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、式(hx−83)で表される化合物を5.50部得た。
Example 10
Gradually 7.83 parts of 2- (4-diethylamino-2-hydroxybenzoyl) benzoic acid (manufactured by Tokyo Chemical Industry Co., Ltd.) in 50 parts of 98% sulfuric acid so that the temperature of the mixture is 30 ° C. or lower during mixing. And mixed. The obtained solution was cooled to 5 ° C., and 5.37 parts of 3- (isopropylamino) phenol (manufactured according to the method described in JP-A-9-169708) was added thereto. The mixture was then stirred at 5 ° C. for 65 hours. The reaction mixture was added to 250 parts of ice water, and the precipitate was obtained by suction filtration. The residue was dissolved in 180 parts of chloroform, 300 parts of ion exchange water was added, and the aqueous layer was adjusted to pH 10 with a 10% aqueous sodium hydroxide solution and stirred for 1 hour. The chloroform layer was separated, washed with 200 parts of ion exchange water and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 5.50 parts of a compound represented by the formula (hx-83).
式(hx−83)で表される化合物3.00部、トリエチレングリコール(東京化成工業(株)製)3.16部、ジメチルアミノピリジン(和光純薬工業(株)製)0.24部、(1S)−(+)−10−カンファースルホン酸(関東化学(株)製)0.18部に脱水クロロホルム30部を加え、室温で1時間攪拌した。30℃を超えないように、1−エチル−3−(3−ジメチルアミノプロピル)カルボジイミド 塩酸塩((株)同仁化学研究所製)1.83部を脱水クロロホルム7.2部に溶解した溶液を滴下し、室温で5時間攪拌した。該クロロホルム溶液を、1N塩酸300部、次いで10%食塩水200部で分液、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、下記式(h−83)で表される化合物を3.59部得た。 3.00 parts of a compound represented by the formula (hx-83), 3.16 parts of triethylene glycol (manufactured by Tokyo Chemical Industry Co., Ltd.), 0.24 part of dimethylaminopyridine (manufactured by Wako Pure Chemical Industries, Ltd.) 30 parts of dehydrated chloroform was added to 0.18 part of (1S)-(+)-10-camphorsulfonic acid (manufactured by Kanto Chemical Co., Inc.) and stirred at room temperature for 1 hour. A solution prepared by dissolving 1.83 parts of 1-ethyl-3- (3-dimethylaminopropyl) carbodiimide hydrochloride (manufactured by Dojin Chemical Laboratory Co., Ltd.) in 7.2 parts of dehydrated chloroform so as not to exceed 30 ° C. The solution was added dropwise and stirred at room temperature for 5 hours. The chloroform solution was separated with 300 parts of 1N hydrochloric acid and then with 200 parts of 10% brine and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 3.59 parts of a compound represented by the following formula (h-83).
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)1.50部をN,N−ジメチルホルミアミド120部に溶解させた溶液(s10)を作成した。別途、式(h−83)で表される化合物1.79部をN,N−ジメチルホルミアミド100部に溶解させた溶液(t10)を作成した。25℃にて、(s10)に(t10)の溶液を添加し、その後80℃に昇温し、6時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水100部、次いでイオン交換水700部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部とヘキサン100部で洗浄し、式(I−49)で表される塩を1.93部得た。 A solution in which 1.50 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 120 parts of N, N-dimethylformamide ( s10) was prepared. Separately, a solution (t10) was prepared by dissolving 1.79 parts of the compound represented by the formula (h-83) in 100 parts of N, N-dimethylformamide. The solution of (t10) was added to (s10) at 25 ° C., and then the temperature was raised to 80 ° C. and stirred for 6 hours. After the mixture was cooled to room temperature, 100 parts of saturated brine and then 700 parts of ion-exchanged water were added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 100 parts of ion-exchanged water and 100 parts of hexane to obtain 1.93 parts of a salt represented by the formula (I-49).
式(I−49)で表される塩の同定;
(元素分析)C:70.1 H:7.7 N:2.5
Identification of a salt represented by formula (I-49);
(Elemental analysis) C: 70.1 H: 7.7 N: 2.5
実施例11
1,1,7,7−テトラメチル−8−ヒドロキシジュロリジン(Orgacic Letters、第10巻第21号、4799−4801頁、2008年.に記載の方法で製造)15.00部、酪酸250部、無水フタル酸(東京化成工業(株)製)4.50部及び9.8%硫酸1.20部を室温で混合し、この混合溶液を140℃まで昇温し、15時間撹拌した。該混合液を室温まで冷却した後、ヘキサン3000部中に注入した。上澄み液を除去して得られたタール状固体をクロロホルム340部に溶解し、クロロホルム溶液をイオン交換水300部で分液、硫酸ナトリウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、式(hx−17)で表される化合物を4.00部得た。
Example 11
1,1,7,7-tetramethyl-8-hydroxyjulolidine (produced by the method described in Organic Letters, Vol. 10, No. 21, 4799-4801, 2008.) 15.00 parts, butyric acid 250 parts 4.50 parts of phthalic anhydride (manufactured by Tokyo Chemical Industry Co., Ltd.) and 1.20 parts of 9.8% sulfuric acid were mixed at room temperature, and this mixed solution was heated to 140 ° C. and stirred for 15 hours. The mixture was cooled to room temperature and poured into 3000 parts of hexane. The tar-like solid obtained by removing the supernatant was dissolved in 340 parts of chloroform, and the chloroform solution was separated with 300 parts of ion-exchanged water and dehydrated with sodium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 4.00 parts of a compound represented by the formula (hx-17).
式(hx−17)で表される化合物3.00部、トリエチレングリコール(東京化成工業(株)製)3.34部、ジメチルアミノピリジン(和光純薬工業(株)製)0.09部、(1S)−(+)−10−カンファースルホン酸(関東化学(株)製)0.14部及び脱水クロロホルム70部を混合し、室温で1時間攪拌した。30℃を超えないように、1−エチル−3−(3−ジメチルアミノプロピル)カルボジイミド塩酸塩((株)同仁化学研究所製)1.38部を脱水クロロホルム30部に溶解した溶液を滴下し、室温で5時間攪拌した。該クロロホルム溶液を、1N塩酸50部、次いで10%食塩水50部で洗浄し、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、下記式(h−17)で表される化合物を2.90部得た。 3.00 parts of a compound represented by the formula (hx-17), 3.34 parts of triethylene glycol (manufactured by Tokyo Chemical Industry Co., Ltd.), 0.09 part of dimethylaminopyridine (manufactured by Wako Pure Chemical Industries, Ltd.) , (1S)-(+)-10-camphorsulfonic acid (manufactured by Kanto Chemical Co., Inc.) 0.14 part and dehydrated chloroform 70 part were mixed and stirred at room temperature for 1 hour. A solution prepared by dissolving 1.38 parts of 1-ethyl-3- (3-dimethylaminopropyl) carbodiimide hydrochloride (manufactured by Dojindo Laboratories) in 30 parts of dehydrated chloroform was added dropwise so as not to exceed 30 ° C. And stirred at room temperature for 5 hours. The chloroform solution was washed with 50 parts of 1N hydrochloric acid and then with 50 parts of 10% brine and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 2.90 parts of a compound represented by the following formula (h-17).
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)1.07部をN,N−ジメチルホルミアミド70部に溶解させた溶液(s11)を作成した。別途、式(h−17)で表される化合物1.50部をN,N−ジメチルホルミアミド70部に溶解させた溶液(t11)を作成した。25℃にて、(s11)に(t11)の溶液を添加し、その後80℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、飽和食塩水50部、次いでイオン交換水300部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水100部とヘキサン100部で洗浄し、式(I−39)で表される塩を1.50部得た。 A solution in which 1.07 part of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 70 parts of N, N-dimethylformamide ( s11) was prepared. Separately, a solution (t11) was prepared by dissolving 1.50 parts of the compound represented by the formula (h-17) in 70 parts of N, N-dimethylformamide. The solution of (t11) was added to (s11) at 25 ° C., and then the temperature was raised to 80 ° C. and stirred for 8 hours. After the mixture was cooled to room temperature, 50 parts of saturated brine and then 300 parts of ion-exchanged water were added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 100 parts of ion exchange water and 100 parts of hexane to obtain 1.50 parts of a salt represented by the formula (I-39).
式(I−39)で表される塩の同定;
(元素分析)C:72.4 H:7.9 N:2.2
Identification of a salt represented by formula (I-39);
(Elemental analysis) C: 72.4 H: 7.9 N: 2.2
実施例12
Basic Violet 10(ローダミンB、東京化成工業(株)製)10.00部、トリエチレングリコールモノメチルエーテル(東京化成工業(株)製)10.28部、ジメチルアミノピリジン(和光純薬工業(株)製)0.77部、(1S)−(+)−10−カンファースルホン酸(関東化学(株)製)0.58部に脱水クロロホルム120部を加え、室温で1時間攪拌した。30℃を超えないように、1−エチル−3−(3−ジメチルアミノプロピル)カルボジイミド 塩酸塩((株)同仁化学研究所製)5.80部を脱水クロロホルム49.3部に溶解した溶液を滴下し、室温で5時間攪拌した。該クロロホルム溶液を、1N塩酸107部、次いで10%食塩水171部で分液、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、下記式(h−82)で表される化合物を11.50部得た。
25℃にて、式(h−82)で表される化合物11.50部をN,N−ジメチルホルミアミド334部に溶解させ、式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)11.12部を添加し、4時間攪拌した。イオン交換水1668部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水334部とヘキサン100部で洗浄し、式(I−48)で表される塩を9.70部得た。
Example 12
Basic Violet 10 (Rhodamine B, manufactured by Tokyo Chemical Industry Co., Ltd.) 100.00 parts, Triethylene glycol monomethyl ether (manufactured by Tokyo Chemical Industry Co., Ltd.) 10.28 parts, Dimethylaminopyridine (Wako Pure Chemical Industries, Ltd.) (Production) 0.77 part, (1S)-(+)-10-camphorsulfonic acid (manufactured by Kanto Chemical Co., Inc.) 0.58 part was added with 120 parts of dehydrated chloroform and stirred at room temperature for 1 hour. A solution prepared by dissolving 5.80 parts of 1-ethyl-3- (3-dimethylaminopropyl) carbodiimide hydrochloride (manufactured by Dojindo Laboratories) in 49.3 parts of dehydrated chloroform so as not to exceed 30 ° C. The solution was added dropwise and stirred at room temperature for 5 hours. The chloroform solution was separated with 107 parts of 1N hydrochloric acid and then with 171 parts of 10% brine and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 11.50 parts of a compound represented by the following formula (h-82).
At 25 ° C., 11.50 parts of the compound represented by the formula (h-82) was dissolved in 334 parts of N, N-dimethylformamide and the compound represented by the formula (f-1) (BONTRON (registered) (Trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd. (11.12 parts) was added and stirred for 4 hours. 1668 parts of ion-exchanged water was added and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 334 parts of ion exchange water and 100 parts of hexane to obtain 9.70 parts of a salt represented by the formula (I-48).
式(I−48)で表される塩の同定;
(元素分析)C:70.2 H:7.7 N:2.6
Identification of a salt represented by the formula (I-48);
(Elemental analysis) C: 70.2 H: 7.7 N: 2.6
実施例13
Basic Violet 10(ローダミンB、東京化成工業(株)製)10.00部、1−ペンタノール(関東化学(株)製)5.89部、ジメチルアミノピリジン(和光純薬工業(株)製)0.77部、(1S)−(+)−10−カンファースルホン酸(関東化学(株)製)0.58部に脱水クロロホルム120部を加え、室温で1時間攪拌した。30℃を超えないように、1−エチル−3−(3−ジメチルアミノプロピル)カルボジイミド 塩酸塩((株)同仁化学研究所製)5.80部を脱水クロロホルム49.3部に溶解した溶液を滴下し、室温で5時間攪拌した。該クロロホルム溶液を、1N塩酸107部、次いで10%食塩水171部で分液、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、下記式(h−86)で表される化合物を10.80部得た。
25℃にて、式(h−86)で表される化合物10.80部をN,N−ジメチルホルミアミド357部に溶解させ、式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)11.89部を添加し、4時間攪拌した。イオン交換水1784部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水357部とヘキサン100部で洗浄し、式(I−51)で表される塩を10.70部得た。
Example 13
Basic Violet 10 (Rhodamine B, manufactured by Tokyo Chemical Industry Co., Ltd.) 10.00 parts, 1-pentanol (manufactured by Kanto Chemical Co., Inc.) 5.89 parts, Dimethylaminopyridine (manufactured by Wako Pure Chemical Industries, Ltd.) 120 parts of dehydrated chloroform was added to 0.77 parts, 0.58 parts of (1S)-(+)-10-camphorsulfonic acid (manufactured by Kanto Chemical Co., Inc.), and the mixture was stirred at room temperature for 1 hour. A solution prepared by dissolving 5.80 parts of 1-ethyl-3- (3-dimethylaminopropyl) carbodiimide hydrochloride (manufactured by Dojindo Laboratories) in 49.3 parts of dehydrated chloroform so as not to exceed 30 ° C. The solution was added dropwise and stirred at room temperature for 5 hours. The chloroform solution was separated with 107 parts of 1N hydrochloric acid and then with 171 parts of 10% brine and dehydrated with magnesium sulfate. Chloroform was distilled off under reduced pressure from the solution obtained by removing magnesium sulfate to obtain 10.80 parts of a compound represented by the following formula (h-86).
At 25 ° C., 10.80 parts of the compound represented by the formula (h-86) was dissolved in 357 parts of N, N-dimethylformamide, and the compound represented by the formula (f-1) (BONTRON (registered) (Trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) 11.89 parts was added and stirred for 4 hours. 1784 parts of ion-exchanged water was added and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 357 parts of ion-exchanged water and 100 parts of hexane to obtain 10.70 parts of a salt represented by the formula (I-51).
式(I−51)で表される塩の同定;
(元素分析)C:72.9 H:7.9 N:2.7
Identification of a salt represented by formula (I-51);
(Elemental analysis) C: 72.9 H: 7.9 N: 2.7
実施例14
25℃にて、C.I.Basic Violet 11(Aizen Cathilon Brilliant Pink CD−BH、保土谷化学工業(株)製)2.00部をN,N−ジメチルホルミアミド66部に溶解させ、式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)2.21部を添加し、4時間攪拌した。イオン交換水332部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水66部とヘキサン100部で洗浄し、式(I−8)で表される塩を1.90部得た。
Example 14
C. at 25 ° C. I. 2.00 parts of Basic Violet 11 (Aizen Catiron Brilliant Pink CD-BH, manufactured by Hodogaya Chemical Co., Ltd.) is dissolved in 66 parts of N, N-dimethylformamide and represented by the formula (f-1). 2.21 parts of a compound (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) was added and stirred for 4 hours. 332 parts of ion exchange water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 66 parts of ion-exchanged water and 100 parts of hexane to obtain 1.90 parts of a salt represented by the formula (I-8).
式(I−8)で表される塩の同定;
(元素分析)C:72.4 H:7.6 N:2.8
Identification of the salt represented by the formula (I-8);
(Elemental analysis) C: 72.4 H: 7.6 N: 2.8
実施例15
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)2.29部をN,N−ジメチルホルミアミド92部に溶解させた溶液(s15)を作成した。別途、Basic Violet 10(ローダミンB、東京化成工業(株)製)8.00部をN,N−ジメチルホルミアミド280部に溶解させた溶液(t15)を作成した。25℃にて、(s15)に(t15)の溶液を添加し、その後40℃に昇温し、8時間攪拌した。該混合液を室温まで冷却した後、イオン交換水744部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水372部とヘキサン100部で洗浄し、式(I−7)で表される塩を4.95部得た。
Example 15
A solution in which 2.29 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 92 parts of N, N-dimethylformamide ( s15) was created. Separately, a solution (t15) was prepared by dissolving 8.00 parts of Basic Violet 10 (Rhodamine B, manufactured by Tokyo Chemical Industry Co., Ltd.) in 280 parts of N, N-dimethylformamide. The solution of (t15) was added to (s15) at 25 ° C., and then the temperature was raised to 40 ° C. and stirred for 8 hours. After the mixture was cooled to room temperature, 744 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 372 parts of ion-exchanged water and 100 parts of hexane to obtain 4.95 parts of a salt represented by the formula (I-7).
式(I−7)で表される塩の同定;
(元素分析)C:72.0 H:7.4 N:2.8
Identification of a salt represented by the formula (I-7);
(Elemental analysis) C: 72.0 H: 7.4 N: 2.8
実施例16
式(h−105)で表される化合物(ローダミン101内部塩、ACROS ORGANICS社製)2.00部を6N塩酸70部に溶解させた溶液(t16)を作成した。別途、式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)2.14部をN,N−ジメチルホルミアミド70部に溶解させた溶液(s16)を作成した。25℃にて、(s16)に(t16)の溶液を添加し、室温で6.5時間攪拌した。該混合液をクロロホルム225部で2回分液抽出し、該クロロホルム溶液を硫酸マグネシウムで脱水し、硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去した。得られたオイル状物質をヘキサン20部で洗浄し、式(I−52)で表される塩を3.82部得た。
Example 16
A solution (t16) was prepared by dissolving 2.00 parts of the compound represented by the formula (h-105) (rhodamine 101 internal salt, manufactured by ACROS ORGANICS) in 70 parts of 6N hydrochloric acid. Separately, 2.14 parts of a compound represented by formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Co., Ltd.) was dissolved in 70 parts of N, N-dimethylformamide. A solution (s16) was prepared. The solution of (t16) was added to (s16) at 25 ° C. and stirred at room temperature for 6.5 hours. The mixture was subjected to liquid separation extraction with 225 parts of chloroform twice, the chloroform solution was dehydrated with magnesium sulfate, and the magnesium was removed from the solution obtained by removing the magnesium sulfate under reduced pressure. The obtained oily substance was washed with 20 parts of hexane to obtain 3.82 parts of a salt represented by the formula (I-52).
式(I−52)で表される塩の同定;
(元素分析)C:73.2 H:7.3 N:2.7
Identification of a salt represented by formula (I-52);
(Elemental analysis) C: 73.2 H: 7.3 N: 2.7
実施例17
氷浴下で、Basic Violet 10(ローダミンB、東京化成工業(株)製)10.00部に、脱水クロロホルム50部、N,N−ジメチルホルミアミド3.05部を加え、氷浴下で1時間攪拌した。氷浴下で塩化チオニル(和光純薬工業(株)製)5.46部を滴下し、その後40℃に昇温し、3時間攪拌した。室温まで冷却した後、氷浴下で、ピロリジン(和光純薬工業(株)製)5.94部を滴下し、その後40℃に昇温し、2時間攪拌した。該混合液を室温まで冷却した後、イオン交換水100部とクロロホルム150部を加え、分液してクロロホルム層を分け取った。水層にクロロホルム150部を加え、分液してクロロホルム層を分け取った。2つのクロロホルム層を合わせ、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、得られた固体を酢酸エチル142部で洗浄し、下記式(h−65)で表される化合物を10.76部得た。
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)9.86部に、N,N−ジメチルホルミアミド394部を加え、80℃に昇温し、溶解させた溶液(s17)を作成した。別途、式(h−65)で表される化合物10.00部をN,N−ジメチルホルミアミド350部に溶解させた溶液(t17)を作成した。80℃にて、(s17)に(t17)の溶液を添加し、80℃にて、6.5時間攪拌した。該混合液を室温まで冷却した後、イオン交換水1488部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水744部とヘキサン383部で洗浄し、式(I−41)で表される塩を9.08部得た。
Example 17
In an ice bath, 50 parts of dehydrated chloroform and 3.05 parts of N, N-dimethylformamide were added to 10.00 parts of Basic Violet 10 (Rhodamine B, manufactured by Tokyo Chemical Industry Co., Ltd.). Stir for 1 hour. Under an ice bath, 5.46 parts of thionyl chloride (manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise, and then the temperature was raised to 40 ° C. and stirred for 3 hours. After cooling to room temperature, 5.94 parts of pyrrolidine (manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise in an ice bath, and then the temperature was raised to 40 ° C. and stirred for 2 hours. After cooling the mixture to room temperature, 100 parts of ion-exchanged water and 150 parts of chloroform were added and separated to separate the chloroform layer. To the aqueous layer was added 150 parts of chloroform, and the mixture was separated to separate the chloroform layer. The two chloroform layers were combined and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure, and the obtained solid was washed with 142 parts of ethyl acetate to obtain 10.76 parts of a compound represented by the following formula (h-65). It was.
9.4 parts of N, N-dimethylformamide is added to 9.86 parts of a compound represented by formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) at 80 ° C. The solution (s17) was prepared by heating to Separately, a solution (t17) was prepared by dissolving 10.00 parts of the compound represented by the formula (h-65) in 350 parts of N, N-dimethylformamide. The solution of (t17) was added to (s17) at 80 ° C., and the mixture was stirred at 80 ° C. for 6.5 hours. After the mixture was cooled to room temperature, 1488 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 744 parts of ion exchange water and 383 parts of hexane to obtain 9.08 parts of a salt represented by the formula (I-41).
式(I−41)で表される塩の同定;
(元素分析)C:73.0 H:7.7 N:4.1
Identification of a salt represented by the formula (I-41);
(Elemental analysis) C: 73.0 H: 7.7 N: 4.1
実施例18
氷浴下で、Basic Violet 10(ローダミンB、東京化成工業(株)製)10.00部に、脱水クロロホルム50部、N,N−ジメチルホルミアミド3.05部を加え、氷浴下で1時間攪拌した。氷浴下で塩化チオニル(和光純薬工業(株)製)5.46部を滴下し、その後40℃に昇温し、5.5時間攪拌した。室温まで冷却した後、氷浴下で、ピペリジン(和光純薬工業(株)製)7.11部を滴下し、その後40℃に昇温し、2時間攪拌した。該混合液を室温まで冷却した後、イオン交換水100部とクロロホルム150部を加え、分液してクロロホルム層を分け取った。水層にクロロホルム150部を加え、分液してクロロホルム層を分け取った。2つのクロロホルム層を合わせ、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、下記式(h−66)で表される化合物を11.93部得た。
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)2.88部に、N,N−ジメチルホルミアミド115部を加え、80℃に昇温し、溶解させた溶液(s18)を作成した。別途、式(h−66)で表される化合物3.00部をN,N−ジメチルホルミアミド105部に溶解させた溶液(t18)を作成した。80℃にて、(s18)に(t18)の溶液を添加し、80℃にて、6.5時間攪拌した。該混合液を室温まで冷却した後、イオン交換水440部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水220部とヘキサン114部で洗浄し、式(I−42)で表される塩を3.15部得た。
Example 18
In an ice bath, 50 parts of dehydrated chloroform and 3.05 parts of N, N-dimethylformamide were added to 10.00 parts of Basic Violet 10 (Rhodamine B, manufactured by Tokyo Chemical Industry Co., Ltd.). Stir for 1 hour. Under an ice bath, 5.46 parts of thionyl chloride (manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise, and then the temperature was raised to 40 ° C. and stirred for 5.5 hours. After cooling to room temperature, 7.11 parts of piperidine (manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise in an ice bath, and then the temperature was raised to 40 ° C. and stirred for 2 hours. After cooling the mixture to room temperature, 100 parts of ion-exchanged water and 150 parts of chloroform were added and separated to separate the chloroform layer. To the aqueous layer was added 150 parts of chloroform, and the mixture was separated to separate the chloroform layer. The two chloroform layers were combined and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 11.93 parts of a compound represented by the following formula (h-66).
115 parts of N, N-dimethylformamide is added to 2.88 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) The solution (s18) was dissolved by heating to Separately, a solution (t18) was prepared by dissolving 3.00 parts of the compound represented by the formula (h-66) in 105 parts of N, N-dimethylformamide. The solution of (t18) was added to (s18) at 80 ° C., and the mixture was stirred at 80 ° C. for 6.5 hours. After the mixture was cooled to room temperature, 440 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration, and washed with 220 parts of ion-exchanged water and 114 parts of hexane to obtain 3.15 parts of a salt represented by the formula (I-42).
式(I−42)で表される塩の同定;
(元素分析)C:73.1 H:7.7 N:4.1
Identification of a salt represented by formula (I-42);
(Elemental analysis) C: 73.1 H: 7.7 N: 4.1
実施例19
氷浴下で、Basic Violet 10(ローダミンB、東京化成工業(株)製)10.00部に、脱水クロロホルム200部、N,N−ジメチルホルミアミド3.05部を加え、氷浴下で1時間攪拌した。氷浴下で塩化チオニル(和光純薬工業(株)製)7.45部を滴下し、その後40℃に昇温し、5時間攪拌した。室温まで冷却した後、氷浴下で、ヘキサメチルイミン(和光純薬工業(株)製)10.35部を滴下し、その後40℃に昇温し、2時間攪拌した。該混合液を室温まで冷却した後、イオン交換水200部、クロロホルム300部、飽和食塩水100部を加え、分液してクロロホルム層を分け取り、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、得られた固体を酢酸エチル132部で洗浄し、下記式(h−67)で表される化合物を12.37部得た。
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)9.36部に、N,N−ジメチルホルミアミド375部を加え、80℃に昇温し、溶解させた溶液(s19)を作成した。別途、式(h−67)で表される化合物10.00部をN,N−ジメチルホルミアミド350部に溶解させた溶液(t19)を作成した。80℃にて、(s19)に(t19)の溶液を添加し、80℃にて、6.5時間攪拌した。該混合液を室温まで冷却した後、イオン交換水1450部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水725部とヘキサン374部で洗浄し、式(I−43)で表される塩を9.90部得た。
Example 19
Under ice bath, 200 parts of dehydrated chloroform and 3.05 parts of N, N-dimethylformamide were added to 10.00 parts of Basic Violet 10 (Rhodamine B, manufactured by Tokyo Chemical Industry Co., Ltd.). Stir for 1 hour. 7.45 parts of thionyl chloride (manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise in an ice bath, and then the temperature was raised to 40 ° C. and stirred for 5 hours. After cooling to room temperature, 10.35 parts of hexamethylimine (manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise in an ice bath, and then the temperature was raised to 40 ° C. and stirred for 2 hours. After cooling the mixture to room temperature, 200 parts of ion-exchanged water, 300 parts of chloroform, and 100 parts of saturated brine were added, and the phases were separated and the chloroform layer was separated and dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure, and the obtained solid was washed with 132 parts of ethyl acetate to obtain 12.37 parts of a compound represented by the following formula (h-67). It was.
To 9.36 parts of the compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.), 375 parts of N, N-dimethylformamide is added, and The solution (s19) was prepared by heating to Separately, a solution (t19) was prepared by dissolving 10.00 parts of the compound represented by the formula (h-67) in 350 parts of N, N-dimethylformamide. The solution of (t19) was added to (s19) at 80 ° C., and the mixture was stirred at 80 ° C. for 6.5 hours. After the mixture was cooled to room temperature, 1450 parts of ion-exchanged water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 725 parts of ion-exchanged water and 374 parts of hexane to obtain 9.90 parts of a salt represented by the formula (I-43).
式(I−43)で表される塩の同定;
(元素分析)C:73.2 H:7.9 N:4.0
Identification of a salt represented by formula (I-43);
(Elemental analysis) C: 73.2 H: 7.9 N: 4.0
実施例20
25℃にて、式(h−66)で表される化合物2.73部をN,N−ジメチルホルミアミド96部に溶解させ、式(f−8)で表される化合物(BONTRON(登録商標)E−81、オリヱント化学工業(株)製)2.75部を添加し、16時間攪拌した。イオン交換水383部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水96部とヘキサン96部で洗浄し、式(I−57)で表される塩を3.06部得た。
Example 20
At 25 ° C., 2.73 parts of the compound represented by the formula (h-66) were dissolved in 96 parts of N, N-dimethylformamide, and the compound represented by the formula (f-8) (BONTRON (Registered) 2.75 parts (trademark) E-81, manufactured by Orient Chemical Co., Ltd.) was added and stirred for 16 hours. Ion exchange water 383 parts was added and further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 96 parts of ion exchange water and 96 parts of hexane to obtain 3.06 parts of a salt represented by the formula (I-57).
式(I−57)で表される塩の同定;
(元素分析)C:71.4 H:7.7 N:4.0
Identification of a salt represented by formula (I-57);
(Elemental analysis) C: 71.4 H: 7.7 N: 4.0
実施例21
3−ブロモフルオロベンゼン(東京化成工業(株)製)3.30部、ジエチルアミン6.00部、銅粉末(関東化学(株)製)0.064部、ヨウ化銅(I)0.19部、りん酸三カリウムn水和物(関東化学(株)製)9.20部及び2−(ジメチルアミノ)エタノール(東京化成工業(株)製)20.0部を室温で混合し、80℃に昇温して72時間攪拌した。該混合液を室温まで冷却した後、水200部とクロロホルム150部を加え、分液してクロロホルム層を取得し、硫酸マグネシウムで脱水した。硫酸マグネシウムを除去して得た溶液からクロロホルムを減圧下で留去し、下記式(gx−1)で表される化合物を2.06部得た。
Example 21
3-Bromofluorobenzene (Tokyo Chemical Industry Co., Ltd.) 3.30 parts, diethylamine 6.00 parts, copper powder (Kanto Chemical Co., Ltd.) 0.064 parts, copper iodide (I) 0.19 parts , 9.20 parts of tripotassium phosphate n-hydrate (manufactured by Kanto Chemical Co., Ltd.) and 20.0 parts of 2- (dimethylamino) ethanol (manufactured by Tokyo Chemical Industry Co., Ltd.) are mixed at room temperature, and 80 ° C. The mixture was warmed to 72 and stirred for 72 hours. After cooling the mixed solution to room temperature, 200 parts of water and 150 parts of chloroform were added and separated to obtain a chloroform layer, which was dehydrated with magnesium sulfate. Chloroform was distilled off from the solution obtained by removing magnesium sulfate under reduced pressure to obtain 2.06 parts of a compound represented by the following formula (gx-1).
N,N−ジエチル−3−メチルアニリン(東京化成工業(株)製)16.30部、ジメトキシメタン(東京化成工業(株)製)19.00部及び酢酸100部を混合した。該混合溶液に、酢酸/98%硫酸(1/1)混合物300部を滴下し、室温で10分攪拌した。析出物を吸引濾過で取得し、イオン交換水1000部で洗浄し、下記式(gx−2)で表される化合物を10.04部得た。 16.30 parts of N, N-diethyl-3-methylaniline (manufactured by Tokyo Chemical Industry Co., Ltd.), 19.00 parts of dimethoxymethane (manufactured by Tokyo Chemical Industry Co., Ltd.) and 100 parts of acetic acid were mixed. To the mixed solution, 300 parts of an acetic acid / 98% sulfuric acid (1/1) mixture was added dropwise and stirred at room temperature for 10 minutes. The precipitate was obtained by suction filtration and washed with 1000 parts of ion-exchanged water to obtain 10.04 parts of a compound represented by the following formula (gx-2).
式(gx−2)で表される化合物6.70部、過マンガン酸カリウム(関東化学(株)製)20部、硫酸銅(II)五水和物(関東化学(株)製)20部を混合し、室温で6時間攪拌した。該反応物にクロロホルム200部を加え、クロロホルム抽出溶液を濾別した。クロロホルムを減圧下で留去し、下記式(gx−3)で表される化合物を6.20部得た。 6.70 parts of the compound represented by the formula (gx-2), 20 parts of potassium permanganate (manufactured by Kanto Chemical Co., Ltd.), 20 parts of copper (II) sulfate pentahydrate (manufactured by Kanto Chemical Co., Ltd.) Were mixed and stirred at room temperature for 6 hours. 200 parts of chloroform was added to the reaction product, and the chloroform extract was filtered off. Chloroform was distilled off under reduced pressure to obtain 6.20 parts of a compound represented by the following formula (gx-3).
式(gx−3)で表される化合物14.10部、式(gx−1)で表される化合物34.50部、オキシ塩化りん(関東化学(株)製)50部を室温で混合し、100℃に昇温して3時間攪拌した。該混合液を室温まで冷却した後、酢酸エチル120部/過塩素酸10部の混合溶媒中に加え、1時間攪拌した。析出物を吸引濾過で取得し、酢酸エチル200部で洗浄し、下記式(g−1)で表される塩を8.64部得た。 14.10 parts of the compound represented by the formula (gx-3), 34.50 parts of the compound represented by the formula (gx-1), and 50 parts of phosphorus oxychloride (manufactured by Kanto Chemical Co., Ltd.) were mixed at room temperature. The mixture was heated to 100 ° C. and stirred for 3 hours. The mixture was cooled to room temperature, added to a mixed solvent of 120 parts of ethyl acetate / 10 parts of perchloric acid, and stirred for 1 hour. The precipitate was obtained by suction filtration and washed with 200 parts of ethyl acetate to obtain 8.64 parts of a salt represented by the following formula (g-1).
式(f−1)で表される化合物(BONTRON(登録商標)E−108、オリヱント化学工業(株)製)1.54部をN,N−ジメチルホルミアミド61部に溶解させた溶液(s21)を作成した。別途、式(g−1)で表される塩1.50部をN,N−ジメチルホルミアミド15部に溶解させた溶液(t21)を作成した。25℃にて、(s21)に(t21)の溶液を添加し、2時間攪拌した。該混合液に、イオン交換水382部を加え、さらに1時間攪拌した。その後、析出物を吸引濾過で取得し、イオン交換水127部で洗浄し、式(I−61)で表される塩を1.78部得た。 A solution in which 1.54 parts of a compound represented by the formula (f-1) (BONTRON (registered trademark) E-108, manufactured by Orient Chemical Industry Co., Ltd.) is dissolved in 61 parts of N, N-dimethylformamide ( s21) was created. Separately, a solution (t21) was prepared by dissolving 1.50 parts of the salt represented by the formula (g-1) in 15 parts of N, N-dimethylformamide. The solution of (t21) was added to (s21) at 25 ° C. and stirred for 2 hours. To the mixture, 382 parts of ion exchange water was added, and the mixture was further stirred for 1 hour. Thereafter, the precipitate was obtained by suction filtration and washed with 127 parts of ion-exchanged water to obtain 1.78 parts of a salt represented by the formula (I-61).
式(I−61)で表される塩の同定;
(元素分析)C:73.7 H:8.4 N:4.1
Identification of the salt represented by the formula (I-61);
(Elemental analysis) C: 73.7 H: 8.4 N: 4.1
〔吸光度の測定〕
塩又は塩を含む混合物0.35gを溶媒に溶解して体積を250cm3とし、そのうちの2cm3を溶媒で希釈して100cm3として、濃度0.028g/Lの溶液を調整した。該溶液について、紫外可視分光光度計(V−650DS;日本分光(株)製)(石英セル、光路長;1cm)を用いて極大吸収波長(λmax)及び極大吸収波長(λmax)での吸光度を測定した。用いた溶媒とともに、結果を表12に示す。
(Measurement of absorbance)
A solution having a concentration of 0.028 g / L was prepared by dissolving 0.35 g of a salt or a salt-containing mixture in a solvent to a volume of 250 cm 3 , 2 cm 3 of which was diluted with a solvent to 100 cm 3 . The solution was measured with a UV-visible spectrophotometer (V-650DS; manufactured by JASCO Corporation) (quartz cell, optical path length: 1 cm) at the maximum absorption wavelength (λ max ) and the maximum absorption wavelength (λ max ). Absorbance was measured. The results are shown in Table 12 together with the solvents used.
〔溶解性の評価〕
実施例1〜21でそれぞれ得られた塩又は塩を含む混合物、式(d−1)、式(d−2)、式(h−1)、式(h−2)、式(h−83)、式(h−17)、式(h−82)、式(h−86)、式(h−105)、式(h−65)、式(h−66)及び式(h−67)でそれぞれ表される化合物、Basic Violet 10、Basic Violet 11並びに式(g−1)で表される化合物について、プロピレングリコールモノメチルエーテルアセテート(以下、PGMEAと略す)、プロピレングリコールモノメチルエーテル(以下、PGMEと略す)、乳酸エチル(以下、ELと略す)、N,N−ジメチルホルミアミド(以下、DMFと略す)への溶解度を、以下のようにして求めた。
50mLサンプル管中、下記の割合で化合物と上記溶媒とを混合し、その後、サンプル管を密栓し、30℃で3分間超音波振とう機にて振とうさせた。次いで室温で30分間放置後、濾過し、その残渣を目視で観察した。残渣として不溶物が確認できなかった場合、溶解性は良好であると判断し、不溶物が確認できた場合は、溶解性は不良であると判断した。表13に溶解性は良好であると判断した最大濃度を記した。結果を表13に示す。×は1%で不良であることを意味する。
1% 塩又は混合物0.01g、溶媒1g
3% 塩又は混合物0.03g、溶媒1g
5% 塩又は混合物0.05g、溶媒1g
7% 塩又は混合物0.07g、溶媒1g
10% 塩又は混合物0.10g、溶媒1g
20% 塩又は混合物0.20g、溶媒1g
[Evaluation of solubility]
The salt obtained by Examples 1-21, or the mixture containing a salt, Formula (d-1), Formula (d-2), Formula (h-1), Formula (h-2), Formula (h-83) ), Formula (h-17), formula (h-82), formula (h-86), formula (h-105), formula (h-65), formula (h-66) and formula (h-67) Are represented by the following formulas: Basic Violet 10, Basic Violet 11 and the compound represented by formula (g-1): propylene glycol monomethyl ether acetate (hereinafter abbreviated as PGMEA), propylene glycol monomethyl ether (hereinafter referred to as PGMEA) The solubility in ethyl lactate (hereinafter abbreviated as EL) and N, N-dimethylformamide (hereinafter abbreviated as DMF) was determined as follows.
In a 50 mL sample tube, the compound and the solvent were mixed at the following ratio, and then the sample tube was sealed and shaken at 30 ° C. for 3 minutes with an ultrasonic shaker. Subsequently, after standing at room temperature for 30 minutes, it filtered, and the residue was observed visually. When insoluble matter could not be confirmed as a residue, it was judged that the solubility was good, and when insoluble matter could be confirmed, it was judged that the solubility was poor. Table 13 shows the maximum concentration judged to have good solubility. The results are shown in Table 13. X means 1%, which is poor.
1 g salt or mixture 0.01 g, solvent 1 g
0.03 g of 3% salt or mixture, 1 g of solvent
5% salt or mixture 0.05g, solvent 1g
7% salt or mixture 0.07g, solvent 1g
0.10 g of 10% salt or mixture, 1 g of solvent
20% salt or mixture 0.20g, solvent 1g
実施例22
〔着色組成物の調製〕
(A)着色剤:塩(I−1):実施例1で合成した塩 20部
(B−1)樹脂:メタクリル酸/ベンジルメタクリレート共重合体(モル比;30/70;重量平均分子量10700、酸価70mgKOH/g) 70部
(C−1)重合性化合物:ジペンタエリスリトールヘキサアクリレート(日本化薬社製) 30部
(D−1)光重合開始剤:ベンジルジメチルケタール(イルガキュア651;BASFジャパン社製) 15部
(E−1)溶剤:N,N−ジメチルホルムアミド 680部
を混合して着色組成物を得る。
Example 22
(Preparation of coloring composition)
(A) Colorant: salt (I-1): salt synthesized in Example 1 20 parts (B-1) resin: methacrylic acid / benzyl methacrylate copolymer (molar ratio; 30/70; weight average molecular weight 10700, Acid value 70 mg KOH / g) 70 parts (C-1) polymerizable compound: dipentaerythritol hexaacrylate (manufactured by Nippon Kayaku Co., Ltd.) 30 parts (D-1) photopolymerization initiator: benzyl dimethyl ketal (Irgacure 651; BASF Japan) 15 parts (E-1) Solvent: 680 parts of N, N-dimethylformamide are mixed to obtain a colored composition.
〔カラーフィルタの作製〕
ガラス上に、上記で得た着色組成物をスピンコート法で塗布し、揮発成分を揮発させる。冷却後、パターンを有する石英ガラス製フォトマスク及び露光機を用いて光照射する。光照射後に、水酸化カリウム水溶液で現像し、オーブンで200℃に加熱してカラーフィルタを得る。
[Production of color filters]
On the glass, the colored composition obtained above is applied by spin coating to volatilize volatile components. After cooling, light irradiation is performed using a quartz glass photomask having a pattern and an exposure machine. After light irradiation, development is performed with an aqueous potassium hydroxide solution, and the color filter is obtained by heating to 200 ° C. in an oven.
実施例23
実施例1で合成した化合物(I−1)を、実施例2で合成した化合物(I−3)に代える以外は、実施例3と同様にして、着色組成物及びカラーフィルタを得る。
Example 23
A colored composition and a color filter are obtained in the same manner as in Example 3, except that the compound (I-1) synthesized in Example 1 is replaced with the compound (I-3) synthesized in Example 2.
表2の結果から、実施例の塩は有機溶媒に対して高い溶解度を示すことがわかる。また、当該塩を含む着色組成物は、異物の発生が少なく、高品質なカラーフィルタを作製することが可能である。 From the results in Table 2, it can be seen that the salts of Examples show high solubility in organic solvents. In addition, the coloring composition containing the salt is less likely to generate foreign matters and can produce a high-quality color filter.
本発明の塩は、有機溶媒への溶解性に優れる。 The salt of the present invention is excellent in solubility in an organic solvent.
Claims (6)
かつ、該有機金属アニオンが、式(1)
Mn− nZ+ (1)
[式(1)中、Mn−は、上記の有機金属アニオンを表す。Z+は、ヒドロン又はアルカリ金属カチオンを表す。nは1〜3の整数を表す。nが2以上の整数である場合、複数のZ+は互いに同一でも異なっていてもよい。]
で表される化合物にしたときに下記要件Aを満たすことを特徴とする塩。
要件A:式(1)で表される化合物の濃度0.028g/L溶液で測定される吸光度が、400〜900nmに亘って0.05以下である。 A salt of an n-valent organometallic anion M n− containing a metal atom capable of forming a bivalent or higher-valent metal ion and an onium cation derived from a dye capable of forming a salt with the organometallic anion,
And the organometallic anion is represented by the formula (1)
M n− nZ + (1)
Wherein (1), M n-represents an organometallic anion above. Z + represents a hydrone or an alkali metal cation. n represents an integer of 1 to 3. When n is an integer greater than or equal to 2, several Z <+> may mutually be same or different. ]
The salt characterized by satisfy | filling the following requirement A when it is set as the compound represented by these.
Requirement A: The absorbance measured with a 0.028 g / L solution of the compound represented by formula (1) is 0.05 or less over 400 to 900 nm.