JP2012201172A - Decoration fiber sheet for automobile - Google Patents
Decoration fiber sheet for automobile Download PDFInfo
- Publication number
- JP2012201172A JP2012201172A JP2011066307A JP2011066307A JP2012201172A JP 2012201172 A JP2012201172 A JP 2012201172A JP 2011066307 A JP2011066307 A JP 2011066307A JP 2011066307 A JP2011066307 A JP 2011066307A JP 2012201172 A JP2012201172 A JP 2012201172A
- Authority
- JP
- Japan
- Prior art keywords
- fiber sheet
- nonwoven fabric
- decorative
- automobile
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は自動車用装飾繊維シートに関し、特には、天井、ドアサイド、ピラーガーニッシュ、リヤパッケージなどの内装材の表皮材として好適に使用することのできる自動車用装飾繊維シートに関する。 The present invention relates to an automotive decorative fiber sheet, and more particularly to an automotive decorative fiber sheet that can be suitably used as a skin material for interior materials such as ceilings, door sides, pillar garnishes, and rear packages.
自動車の内装用表皮材として、従来、装飾性に優れる不織布が使用されている。このような不織布として、ニードルパンチ不織布にプリントを施し、次いで、エンボン加工を施したものが開発されているが、成形時にエンボス模様が消失しやすく、しかも耐摩耗性など、表面耐性が充分ではないという欠点があった。そこでエンボス模様が消失しないように、エンボス部を強く加圧すれば良いが、この場合、不織布の風合が硬くなり、成形性が低下し、しかもエンボス部と非エンボス部との境界で切断や破壊が生じることがあった。 Conventionally, non-woven fabrics having excellent decorative properties have been used as automobile interior skin materials. As such a nonwoven fabric, a needle punched nonwoven fabric that has been printed and then embossed has been developed, but the embossed pattern tends to disappear during molding, and the surface resistance such as wear resistance is not sufficient. There was a drawback. Therefore, it is sufficient to press the embossed part strongly so that the embossed pattern does not disappear. Destruction sometimes occurred.
そのため、本願出願人は、「熱接着性複合繊維を５〜２５重量％含む繊維ウェブの片面からニードリングが施されたニードルパンチ不織布のニードリング面とは反対の面に、樹脂が含浸され、プリント加工およびエンボス加工が施されており、かつ通気度が５０〜１２０ｃｃ／ｃｍ２／ｓｅｃであることを特徴とする車輛内装用表皮材。」（特許文献１）を提案した。このような表皮材（不織布）は実用上満足しうる表面耐性を有し、深みがあるため装飾性に優れ、しかもソフトで暖かい風合を具備するものであった。 Therefore, the applicant of the present application stated that "the surface opposite to the needling surface of the needle punched nonwoven fabric subjected to the needling from one side of the fiber web containing 5 to 25% by weight of the heat-adhesive conjugate fiber is impregnated with resin. A skin material for vehicle interior, which is printed and embossed, and has an air permeability of 50 to 120 cc / cm 2 / sec. ”(Patent Document 1). Such a skin material (nonwoven fabric) has a surface resistance that can be satisfied in practice, has a depth, is excellent in decorativeness, and has a soft and warm texture.
ところで、近年、燃費の向上のために自動車の軽量化、小型化が進行し、自動車室内が狭くなる傾向があるが、搭乗者が自動車室内において快適に過ごすことができるように、自動車室内を広く感じることが望まれていた。しかしながら、従来、不織布にプリントを施す場合、柄がはっきりとするように、濃色のプリントを施すのが一般的であったが、このようなプリントを施した表皮材は前記要望、つまり自動車室内を広く感じることができないものであった。 By the way, in recent years, automobiles have become lighter and smaller in size to improve fuel efficiency, and the interior of the automobile tends to be narrow. However, the interior of the automobile is widened so that passengers can spend comfortably in the automobile. I wanted it to feel. However, conventionally, when printing on a non-woven fabric, it has been common to apply a dark color print so that the pattern is clear. I couldn't feel it widely.
本発明はこのような状況下においてなされたものであり、装飾性に優れているのはもちろんのこと、自動車室内を広く感じることができ、圧迫感を和らげることのできる自動車用装飾繊維シートを提供することを目的とする。 The present invention has been made under such circumstances, and provides a decorative fiber sheet for automobiles that is not only excellent in decorativeness but also can feel the interior of the automobile widely and can relieve the feeling of pressure. The purpose is to do.
本発明の請求項１にかかる発明は、「着色した繊維シートにプリントが施された自動車用装飾繊維シートであり、前記着色した繊維シートの平均明度（Ｌｂ）と自動車用装飾繊維シートの最小明度（Ｌａｌ）との最小明度差（ΔＬｌ＝Ｌａｌ−Ｌｂ）が０．９以上であることを特徴とする、自動車用装飾繊維シート。」である。 The invention according to claim 1 of the present invention is “a decorative fiber sheet for automobiles in which a colored fiber sheet is printed. The average lightness (Lb) of the colored fiber sheet and the minimum brightness of the decorative fiber sheet for automobiles” A decorative fiber sheet for automobiles, characterized in that the minimum brightness difference (ΔLl = Lal−Lb) with respect to (Lal) is 0.9 or more. ”
本発明の請求項１にかかる発明は、着色した繊維シートにプリントが施された自動車用装飾繊維シートであるため、装飾性に優れている。また、着色した繊維シートの平均明度（Ｌｂ）と自動車用装飾繊維シートの最小明度（Ｌａｌ）との最小明度差（ΔＬｌ＝Ｌａｌ−Ｌｂ）が０．９以上であるということは、着色した繊維シートよりも明度の高いプリントが施されていることを意味し、明度の高いプリントは膨張して見える心理的効果を発揮するため、自動車室内を広く感じることができ、圧迫感を和らげることができる。更に、最小明度差（ΔＬｌ＝Ｌａｌ−Ｌｂ）が０．９以上であることによって、プリント柄を明確に認識することができるため、装飾性に優れている。 Since the invention according to claim 1 of the present invention is a decorative fiber sheet for automobiles in which a printed fiber sheet is printed, the decorative property is excellent. Further, the minimum lightness difference (ΔLl = Lal−Lb) between the average lightness (Lb) of the colored fiber sheet and the minimum lightness (Lal) of the decorative fiber sheet for automobiles is 0.9 or more. This means that prints with a higher brightness than the seat are applied, and the prints with higher brightness show a psychological effect that appears to expand, so you can feel the interior of the car widely and relieve the feeling of pressure. . Furthermore, since the minimum lightness difference (ΔLl = Lal−Lb) is 0.9 or more, the printed pattern can be clearly recognized, so that the decorativeness is excellent.
本発明の自動車用装飾繊維シート（以下、単に「装飾繊維シート」と表記することがある）は着色した繊維シート（以下、単に「着色繊維シート」と表記することがある）にプリントが施された繊維シートであるため、装飾性に優れている。通常、繊維は白色を有するが、プリントする前の繊維シートは白色以外の色に着色した状態にある。この着色繊維シートは、繊維自体が顔料及び／又は染料を含有する原着繊維を用いて繊維シートを形成したものであっても良いし、繊維シートを形成した後に、顔料及び／又は染料で着色したものであっても良いし、或いはこれらを併用したものであっても良い。 The automotive decorative fiber sheet of the present invention (hereinafter sometimes simply referred to as “decorative fiber sheet”) is printed on a colored fiber sheet (hereinafter sometimes simply referred to as “colored fiber sheet”). The fiber sheet is excellent in decorativeness. Normally, the fiber has a white color, but the fiber sheet before printing is in a state colored to a color other than white. The colored fiber sheet may be a fiber sheet formed by using original fibers containing pigment and / or dye, or colored with a pigment and / or dye after forming the fiber sheet. These may be used, or a combination of these may be used.
なお、着色繊維シートの平均明度（Ｌｂ）は特に限定するものではないが、明度の高いプリントを施すことによって、プリントが膨張して見える心理的効果を発揮できるように、７０以下であるのが好ましく、６９以下であるのがより好ましく、６８．５以下であるのが更に好ましい。 In addition, the average lightness (Lb) of the colored fiber sheet is not particularly limited, but it is 70 or less so that a psychological effect in which the print appears to expand can be exhibited by applying a print with high lightness. Preferably, it is 69 or less, more preferably 68.5 or less.
また、着色繊維シートの態様は特に限定するものではないが、例えば、不織布、織物、編物であることができる。これらの中でも不織布が好適である。 Moreover, although the aspect of a colored fiber sheet is not specifically limited, For example, it can be a nonwoven fabric, a woven fabric, and a knitted fabric. Among these, a nonwoven fabric is suitable.
着色繊維シートを構成する繊維を構成する樹脂は特に限定するものではないが、例えば、ポリエステル、ナイロン、塩化ビニル、アクリル、ポリプロピレンなどを挙げることができる。これらの中でもポリエステルは耐熱性、耐候性、防汚性等に優れているため好適である。また、装飾繊維シートに成形性が必要とされる場合、エンボス加工を施す場合、或いは強度を必要とする場合には、繊維として、融点が異なる２成分以上の樹脂からなり、繊維断面がサイドバイサイド型、芯鞘型、偏心型などの複合繊維を含むのが好ましい。なお、繊維の繊度は特に限定するものではないが、１〜６ｄｔｅｘであるのが好ましく、１．５〜６ｄｔｅｘであるのがより好ましい。また、繊維の繊維長も特に限定するものではないが、３０〜１１０ｍｍであるのが好ましく、５０〜８０ｍｍであるのがより好ましい。本発明の着色繊維シートは、顔料又は染料の色、種類及び／又は量、樹脂成分の種類及び／又は数、繊度、繊維長などの点で相違する２種類以上の原着繊維を含むことができる。また、原着繊維と非原着繊維とを含むこともできる。 The resin constituting the fiber constituting the colored fiber sheet is not particularly limited, and examples thereof include polyester, nylon, vinyl chloride, acrylic, and polypropylene. Among these, polyester is preferable because it is excellent in heat resistance, weather resistance, antifouling property and the like. In addition, when the decorative fiber sheet requires formability, when embossing is performed, or when strength is required, the fiber is made of a resin having two or more components having different melting points, and the fiber cross section is a side-by-side type. It is preferable to include a composite fiber such as a core-sheath type or an eccentric type. In addition, although the fineness of a fiber is not specifically limited, It is preferable that it is 1-6 dtex, and it is more preferable that it is 1.5-6 dtex. Moreover, the fiber length of the fiber is not particularly limited, but is preferably 30 to 110 mm, and more preferably 50 to 80 mm. The colored fiber sheet of the present invention may contain two or more types of primary fibers that differ in terms of color, type and / or amount of pigment or dye, type and / or number of resin components, fineness, fiber length, and the like. it can. Moreover, an original fiber and a non-original fiber can also be included.
着色繊維シートが不織布の態様である場合、例えば、ニードルパンチ不織布、繊維接着不織布、水流絡合不織布、バインダ接着不織布であることができる。なお、ニードルパンチ、繊維接着、水流絡合、及び／又はバインダ接着を適宜組み合わせることもできる。例えば、ニードルパンチ不織布に対してバインダを含浸、コーティング、又はスプレーし、接着することによって、着色不織布表面を平滑とし、プリントの載りを良くすることができる。 When the colored fiber sheet is an embodiment of a nonwoven fabric, it can be, for example, a needle punched nonwoven fabric, a fiber-bonded nonwoven fabric, a hydroentangled nonwoven fabric, or a binder-bonded nonwoven fabric. Needle punching, fiber bonding, hydroentanglement, and / or binder bonding can be combined as appropriate. For example, by impregnating, coating, or spraying a binder onto a needle punched nonwoven fabric and adhering it, the surface of the colored nonwoven fabric can be made smooth and the printing can be improved.
本発明の装飾繊維シートは上述のような着色繊維シートにプリントが施されたものであり、着色繊維シートの平均明度（Ｌｂ）と装飾繊維シートの最小明度（Ｌａｌ）との最小明度差（ΔＬｌ＝Ｌａｌ−Ｌｂ）が０．９以上である。着色繊維シートの平均明度（Ｌｂ）と装飾繊維シートの最小明度（Ｌａｌ）との最小明度差（ΔＬｌ＝Ｌａｌ−Ｌｂ）がプラス、かつ０．９以上というある程度以上の最低限の明度差があるということは、プリント自体が高い明度を有することを意味し、着色繊維シートに対して明度の高いプリントが施されていることによって、明度の高いプリントが膨張して見える心理的効果を発揮し、自動車室内を広く感じることができ、圧迫感を和らげることができる。また、最小明度差が０．９以上であることによって、プリント柄を明確に認識することができるため、装飾性に優れている。この最小明度差が大きければ大きいほど、プリントが膨張して見える心理的効果を発揮でき、しかも装飾性に優れているため、０．９５以上であるのが好ましい。 The decorative fiber sheet of the present invention is obtained by printing the above-described colored fiber sheet, and the minimum lightness difference (ΔLl) between the average lightness (Lb) of the colored fiber sheet and the minimum lightness (Lal) of the decorative fiber sheet. = Lal-Lb) is 0.9 or more. The minimum lightness difference (ΔLl = Lal−Lb) between the average lightness (Lb) of the colored fiber sheet and the minimum lightness (Lal) of the decorative fiber sheet is plus, and there is a minimum lightness difference of a certain level of 0.9 or more. That means that the print itself has a high lightness, and by giving a high lightness print to the colored fiber sheet, it exerts a psychological effect that the high lightness print appears to expand, You can feel the interior of the car widely and relieve the feeling of pressure. Further, since the minimum lightness difference is 0.9 or more, the printed pattern can be clearly recognized, so that the decorativeness is excellent. The greater the minimum brightness difference, the more effective the prints can be when they appear to expand, and the better the decorativeness, the more preferable is 0.95 or more.
また、装飾繊維シートの平均明度Ｌａは６５以上であるのが好ましい。このように、平均明度Ｌａが６５以上であると、自動車室内が明るく、広く感じることができ、圧迫感を和らげることができるためである。この平均明度Ｌａが高ければ高い程、自動車室内を広く感じることができるため、装飾繊維シートの平均明度Ｌａは６５．５以上であるのがより好ましく、６６．０以上であるのが更に好ましく、６６．５以上であるのが更に好ましい。なお、装飾繊維シートの平均明度Ｌａの上限は特に限定するものではないが、白色の装飾繊維シートの平均明度Ｌａが１００であることから、１００未満である。 The average lightness La of the decorative fiber sheet is preferably 65 or more. Thus, when the average brightness La is 65 or more, the interior of the automobile can be bright and wide, and the feeling of pressure can be relieved. The higher the average brightness La, the wider the interior of the automobile can be felt, so the average brightness La of the decorative fiber sheet is more preferably 65.5 or more, and even more preferably 66.0 or more. More preferably, it is 66.5 or more. In addition, although the upper limit of the average brightness La of a decoration fiber sheet is not specifically limited, Since the average brightness La of a white decoration fiber sheet is 100, it is less than 100.
なお、プリント柄は前述の最小明度差が０．９以上となる限り、特に限定されるものではないが、例えば、連続した線状、不連続の線状、ドット状、格子状、又はこれらの組合せであることができる。なお、各プリントの形状は同じである必要はなく、異なる形状であっても良い。また、プリントの大きさも同じである必要はなく、異なっていても良く、規則的に又は不規則的に変化することもできる。更に、規則的にプリントされていても良いし、不規則的にプリントされていても良いし、極端な場合には一領域に偏在していても良い。 The printed pattern is not particularly limited as long as the above-mentioned minimum brightness difference is 0.9 or more, but for example, a continuous linear shape, a discontinuous linear shape, a dot shape, a lattice shape, or these Can be a combination. Note that the shape of each print need not be the same, and may be different. Also, the size of the prints need not be the same, may be different, and can vary regularly or irregularly. Furthermore, it may be printed regularly, may be printed irregularly, or may be unevenly distributed in one region in an extreme case.
また、プリントは従来から公知の方法により実施することができる。例えば、所望模様に対応する開口を有するシリンダを用意し、顔料を含む樹脂をプリントすることによって実施することができる。なお、樹脂としては、アクリル樹脂、ポリエステル樹脂、ポリウレタン樹脂などを使用することができ、顔料の色、種類及び量は適宜調整することができる。また、プリント方法はシリンダを使用する方法に限定されず、例えば、グラビア印刷、凸版印刷、オフセット印刷、スクリーン印刷などにより実施することができ、特に限定するものではない。 Printing can be performed by a conventionally known method. For example, it can be carried out by preparing a cylinder having an opening corresponding to a desired pattern and printing a resin containing a pigment. As the resin, an acrylic resin, a polyester resin, a polyurethane resin, or the like can be used, and the color, type, and amount of the pigment can be appropriately adjusted. The printing method is not limited to a method using a cylinder, and for example, it can be carried out by gravure printing, letterpress printing, offset printing, screen printing, etc., and is not particularly limited.
本発明における「明度」はＣＩＥ１９７６Ｌ＊ａ＊ｂ＊表色系で表される明度であり、具体的には、積分球分光光度計（エックスライト（株）製、Ｃｏｌｏｒ ｉ５）を用い、反射測定径２５ｍｍの測定範囲で測定して算出することができる。また、「平均明度」は無作為に選んだ１０点における明度の算術平均値を意味し、「最小明度」は無作為に選んだ１０点における明度の中で、最も明度の低い明度をいう。 “Lightness” in the present invention is lightness represented by the CIE 1976 L * a * b * color system, and specifically, reflection measurement using an integrating sphere spectrophotometer (X-Rite Co., Ltd., Color i5). It can be calculated by measuring within a measurement range of 25 mm in diameter. Further, “average brightness” means an arithmetic average value of brightness at 10 points selected at random, and “minimum brightness” means the brightness with the lowest brightness among the brightness at 10 points selected at random.
本発明の装飾繊維シートは上述のように、着色繊維シートにプリントが施されたものであるが、最小明度差が０．９以上である限り、プリントに加えてエンボス加工が施されていても良い。エンボス模様は特に限定するものではないが、例えば、皮しぼ模様、梨地模様、或いは円、四角形などの所定形状のドットを規則的又は不規則に配置した模様であることができる。 As described above, the decorative fiber sheet of the present invention is printed on a colored fiber sheet, but as long as the minimum lightness difference is 0.9 or more, embossing may be performed in addition to the print. good. The embossed pattern is not particularly limited. For example, the embossed pattern may be a leather pattern, a satin pattern, or a pattern in which dots having a predetermined shape such as a circle or a rectangle are regularly or irregularly arranged.
本発明の装飾繊維シートは装飾性に優れているばかりでなく、自動車室内において使用すると、広く感じることができ、圧迫感を和らげることのできるシートである。そのため、例えば、天井、ドアサイド、ピラーガーニッシュ、リヤパッケージなどの自動車内装材の表皮材として使用すると、広々とした開放感をもって快適なドライブを楽しむことができる。 The decorative fiber sheet of the present invention is not only excellent in decorativeness, but also can be widely felt when used in an automobile room, and can reduce the feeling of pressure. Therefore, for example, when used as a skin material for automobile interior materials such as a ceiling, door side, pillar garnish, rear package, etc., a comfortable drive can be enjoyed with a spacious feeling of opening.
以下に、本発明の実施例を記載するが、本発明は以下の実施例に限定されるものではない。 Examples of the present invention will be described below, but the present invention is not limited to the following examples.
（第１バインダ接着不織布の準備）
原着ポリエステル繊維（繊度：２．２ｄｔｅｘ、繊維長：５１ｍｍ）を１００％用いて、カード機により開繊して繊維ウエブを形成した後、片面から針密度４００本／ｍ２でニードルパンチ処理を行い、ニードルパンチ不織布（目付：１７０ｇ／ｍ２、厚さ：１．７ｍｍ）を製造した。
(Preparation of first binder-bonded nonwoven fabric)
Using 100% of the original polyester fiber (fineness: 2.2 dtex, fiber length: 51 mm), the fiber web is formed with a card machine, and then the needle punch treatment is performed at a needle density of 400 / m 2 from one side. This was carried out to produce a needle punched nonwoven fabric (weight per unit: 170 g / m 2 , thickness: 1.7 mm).
他方、次の割合で配合した第１バインダ溶液を調製した。
（１）アクリルバインダ［ＤＩＣＮＡＬ（登録商標） ＤＳ−２３、ＤＩＣ社製］・・・１２部
（２）増粘剤［ネオゲン（登録商標）Ｓ−２０Ｄ、第一工業製薬社製］・・・０．１部
（３）界面活性剤（セロゲン（登録商標）ＷＳ−Ｃ、第一工業製薬社製）・・・０．２部
（４）アンモニア水・・・０．１部
（５）水・・・８７．６部
On the other hand, the 1st binder solution mix | blended with the following ratio was prepared.
(1) Acrylic binder [DICNAL (registered trademark) DS-23, manufactured by DIC Corporation] ... 12 parts (2) Thickener [Neogen (registered trademark) S-20D, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.] 0.1 part (3) surfactant (Serogen (registered trademark) WS-C, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) ... 0.2 part (4) Ammonia water ... 0.1 part (5) Water ... 87.6 parts
次いで、前記第１バインダ溶液を泡立てた後、前記ニードルパンチ不織布のニードリング面とは反対の面から塗布し、含浸させた後に、温度１３０℃のキャンドライヤーで乾燥し、外観がグレー色のバインダ接着着色不織布（目付：１８０ｇ／ｍ２、厚さ：１．７ｍｍ）を製造した。 Next, after foaming the first binder solution, the needle punched nonwoven fabric is coated from the surface opposite to the needling surface, impregnated, and then dried with a can dryer having a temperature of 130 ° C. An adhesive-colored nonwoven fabric (weight per unit: 180 g / m 2 , thickness: 1.7 mm) was produced.
（第２バインダ接着不織布の準備）
原着ポリエステル繊維（繊度：２．２ｄｔｅｘ、繊維長：５１ｍｍ）を１００％用いて、カード機により開繊して繊維ウエブを形成した後、片面から針密度４００本／ｍ２でニードルパンチ処理を行い、ニードルパンチ不織布（目付：１５５ｇ／ｍ２、厚さ：１．６ｍｍ）を製造した。
(Preparation of second binder-bonded nonwoven fabric)
Using 100% of the original polyester fiber (fineness: 2.2 dtex, fiber length: 51 mm), the fiber web is formed with a card machine, and then the needle punch treatment is performed at a needle density of 400 / m 2 from one side. This was carried out to produce a needle punched nonwoven fabric (basis weight: 155 g / m 2 , thickness: 1.6 mm).
他方、次の割合で配合した第２バインダ溶液を調製した。
（１）アクリルバインダ［ＤＩＣＮＡＬ（登録商標） Ｅ−２４０Ｎ、ＤＩＣ社製］・・・６部
（２）増粘剤［ネオゲン（登録商標）Ｓ−２０Ｄ、第一工業製薬社製］・・・１．０部
（３）界面活性剤（セロゲン（登録商標）ＷＳ−Ｃ、第一工業製薬社製）・・・０．２部
（４）アンモニア水・・・０．１部
（５）水・・・９２．７部
On the other hand, the 2nd binder solution mix | blended with the following ratio was prepared.
(1) Acrylic binder [DICNAL (registered trademark) E-240N, manufactured by DIC Corporation] ... 6 parts (2) Thickener [Neogen (registered trademark) S-20D, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.] 1.0 part (3) surfactant (Serogen (registered trademark) WS-C, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) ... 0.2 part (4) Ammonia water ... 0.1 part (5) Water ... 92.7 parts
次いで、前記第２バインダ溶液を泡立てた後、前記ニードルパンチ不織布のニードリング面とは反対の面から塗布し、含浸させた後に、温度１３０℃のキャンドライヤーで乾燥し、外観がダークグレー色のバインダ接着着色不織布（目付：１５５ｇ／ｍ２、厚さ：１．６ｍｍ）を製造した。 Next, after bubbling the second binder solution, the needle punched nonwoven fabric is applied from the surface opposite to the needling surface, impregnated, and then dried with a can dryer having a temperature of 130 ° C., and the appearance is a dark gray binder. An adhesive-colored nonwoven fabric (weight per unit area: 155 g / m 2 , thickness: 1.6 mm) was produced.
（第３バインダ接着不織布の準備）
原着ポリエステル繊維（繊度：２．２ｄｔｅｘ、繊維長：５１ｍｍ）を２５％、原着ポリエステル繊維（繊度：３．３ｄｔｅｘ、繊維長：６４ｍｍ）を７５％用いて、カード機により開繊して繊維ウエブを形成した後、片面から針密度４００本／ｍ２でニードルパンチ処理を行い、ニードルパンチ不織布（目付：１４０ｇ／ｍ２、厚さ：１．６ｍｍ）を製造した。
(Preparation of third binder-bonded nonwoven fabric)
The fiber is opened with a card machine using 25% of the original polyester fiber (fineness: 2.2 dtex, fiber length: 51 mm) and 75% of the original polyester fiber (fineness: 3.3 dtex, fiber length: 64 mm). After forming the web, needle punching was performed from one side at a needle density of 400 needles / m 2 to produce a needle punched nonwoven fabric (weight per unit: 140 g / m 2 , thickness: 1.6 mm).
他方、次の割合で配合した第３バインダ溶液を調製した。
（１）アクリルバインダ［ＤＩＣＮＡＬ（登録商標） Ｅ−２４０Ｎ、ＤＩＣ社製］・・・７．８部
（２）アクリルバインダ［ボンコート（登録商標） ＡＮ−１１９０Ｓ、ＤＩＣ社製］・・・２部
（３）増粘剤［ネオゲン（登録商標）Ｓ−２０Ｄ、第一工業製薬社製］・・・１．５部
（４）界面活性剤（セロゲン（登録商標）ＷＳ−Ｃ、第一工業製薬社製）・・・０．２部
（５）アンモニア水・・・０．１部
（６）水・・・８８．４部
On the other hand, the 3rd binder solution mix | blended with the following ratio was prepared.
(1) Acrylic binder [DICNAL (registered trademark) E-240N, manufactured by DIC Corporation] 7.8 parts (2) Acrylic binder [Boncoat (registered trademark) AN-1190S, manufactured by DIC Corporation] ... 2 parts (3) Thickener [Neogen (registered trademark) S-20D, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.] 1.5 parts (4) Surfactant (Serogen (registered trademark) WS-C, Daiichi Kogyo Seiyaku 0.25 (5) Ammonia water ... 0.1 part (6) Water ... 88.4 parts
次いで、前記第３バインダ溶液を泡立てた後、前記ニードルパンチ不織布のニードリング面とは反対の面から塗布し、含浸させた後に、温度１３０℃のキャンドライヤーで乾燥し、外観がライトグレー色のバインダ接着着色不織布（目付：１５０ｇ／ｍ２、厚さ：１．６ｍｍ）を製造した。 Next, after foaming the third binder solution, the needle punched nonwoven fabric was applied from the surface opposite to the needling surface, impregnated, and then dried with a can dryer at a temperature of 130 ° C., and the appearance was light gray. A binder-bonded colored nonwoven fabric (weight per unit area: 150 g / m 2 , thickness: 1.6 mm) was produced.
（第１プリント液の準備）
次の割合で配合した第１プリント液を調製した。
（１）増粘剤［カーボポール９４０、日本ルーブリゾール（株）製］・・・０．３３部
（２）消泡剤［シンエツシリコーンＫＭ−７３、信越化学工業（株）製］・・・０．４部
（３）アクリルバインダ［ボンコート（登録商標）３２１８ＥＦ、ＤＩＣ（株）製］・・・２０部
（４）黒顔料［Ｒ.Ｗ.ＢＬＡＣＫ ＲＣ（Ｖ）、ＤＩＣ（株）製］・・・０．０３部
（５）増粘剤［ニカゾール（登録商標） ＶＴ−２５３、日本カーバイド工業（株）製］・・・０．６部
（６）水・・・７８．６４部
(Preparation of the first printing liquid)
The 1st printing liquid mix | blended with the following ratio was prepared.
(1) Thickener [Carbopol 940, manufactured by Nippon Lubrizol Co., Ltd.] ... 0.33 parts (2) Antifoaming agent [Shin-Etsu Silicone KM-73, manufactured by Shin-Etsu Chemical Co., Ltd.] 0.4 parts (3) Acrylic binder [Boncoat (registered trademark) 3218EF, manufactured by DIC Corporation] 20 parts (4) Black pigment [R.W. BLACK RC (V), manufactured by DIC Corporation] ... 0.03 part (5) Thickener [Nicazole (registered trademark) VT-253, manufactured by Nippon Carbide Industries, Ltd.] ... 0.6 part (6) Water ... 78.64 parts
（第２プリント液の準備）
次の割合で配合した第２プリント液を調製した。
（１）増粘剤［カーボポール９４０、日本ルーブリゾール（株）製］・・・０．３３部
（２）消泡剤［シンエツシリコーンＫＭ−７３、信越化学工業（株）製］・・・０．４部
（３）アクリルバインダ［ボンコート（登録商標）３２１８ＥＦ、ＤＩＣ（株）製］・・・２０部
（４）白色顔料［Ｒ.Ｗ ＷＨＩＴＥ ＰＡＳＴＥ ６９、ＤＩＣ（株）製］・・・０．９部
（５）増粘剤［ニカゾール（登録商標）ＶＴ−２５３、日本カーバイド工業（株）製］・・・０．６部
（６）水・・・７７．７７部
(Preparation of second printing liquid)
A second printing liquid blended at the following ratio was prepared.
(1) Thickener [Carbopol 940, manufactured by Nippon Lubrizol Co., Ltd.] ... 0.33 parts (2) Antifoaming agent [Shin-Etsu Silicone KM-73, manufactured by Shin-Etsu Chemical Co., Ltd.] 0.4 parts (3) Acrylic binder [Boncoat (registered trademark) 3218EF, manufactured by DIC Corporation] ... 20 parts (4) White pigment [R.W WHITE PASTE 69, manufactured by DIC Corporation] ... 0.9 parts (5) Thickener [Nicazole (registered trademark) VT-253, manufactured by Nippon Carbide Industries, Ltd.] ... 0.6 parts (6) Water ... 77.77 parts
（実施例１）
準備した外観がグレー色の第１バインダ接着不織布のバインダ付着面（Ｌｂ＝６４．８７）に対して、開口を有するシリンダを用い、第２プリント液をプリントした後、温度１６０℃のドライヤーで乾燥し、自動車用装飾不織布（幅：６５ｃｍ）を製造した。つまり、図１に示すように、格子状模様の印影の部分を「く」の字状に、同じ大きさで、規則的にプリントした（印影部の太さ：１ｍｍ、図１においては黒色で描写）。この自動車用装飾不織布は立体的で装飾性に優れ、また、平均明度Ｌａは６６．７９で、最小明度Ｌａｌは６６．６２で、最小明度差（ΔＬｌ）は１．７５であり、自動車室内を広く感じることができ、圧迫感を和らげることができるものであった。
Example 1
Using a cylinder with an opening on the binder-attached surface (Lb = 64.87) of the first binder-bonded nonwoven fabric with a gray appearance, after printing the second print liquid, dry it with a dryer at a temperature of 160 ° C. Thus, a decorative nonwoven fabric for automobiles (width: 65 cm) was produced. That is, as shown in FIG. 1, the imprinted portion of the lattice-like pattern was regularly printed in the shape of “<” with the same size (thickness of the imprinted portion: 1 mm, black in FIG. 1). Depiction). This decorative nonwoven fabric for automobiles is three-dimensional and excellent in decorativeness, and the average brightness La is 66.79, the minimum brightness Lal is 66.62, and the minimum brightness difference (ΔLl) is 1.75. I could feel it widely and relieve the feeling of pressure.
（比較例１）
準備した外観がグレー色の第１バインダ接着不織布のバインダ付着面（Ｌｂ＝６４．８７）に対して、開口を有するシリンダを用い、第１プリント液をプリントしたこと以外は、実施例１と同様にして、自動車用装飾不織布（幅：６５ｃｍ）を製造した。この自動車用装飾不織布は立体的で装飾性に優れていたが、平均明度Ｌａは６１．７９で、最小明度Ｌａｌは６１．４９で、最小明度差（ΔＬｌ）は−３．０８であり、自動車室内を広く感じることができないものであった。
(Comparative Example 1)
The prepared appearance is the same as in Example 1 except that the first printing liquid is printed using a cylinder having an opening on the binder-attached surface (Lb = 64.87) of the first binder-bonded nonwoven fabric having a gray color. Thus, a decorative nonwoven fabric for automobiles (width: 65 cm) was produced. This decorative nonwoven fabric for automobiles was three-dimensional and excellent in decorativeness, but the average brightness La was 61.79, the minimum brightness Lal was 61.49, and the minimum brightness difference (ΔLl) was −3.08. I couldn't feel the room wide.
（比較例２）
準備した外観がグレー色の第１バインダ接着不織布を自動車用装飾不織布とした。この自動車用装飾不織布は実施例１の装飾布不織布と比較して単調で、あまり装飾性に優れておらず、また、バインダ付着面における平均明度Ｌａは６４．８７であり、自動車室内を広く感じることができないものであった。
(Comparative Example 2)
The prepared first binder-bonded nonwoven fabric having a gray appearance was used as a decorative nonwoven fabric for automobiles. This decorative nonwoven fabric for automobiles is monotonous compared with the decorative fabric nonwoven fabric of Example 1 and is not very decorative, and the average lightness La on the binder-attached surface is 64.87, which makes the interior of the automobile feel wide. It was something that could not be done.
（実施例２）
準備した外観がダークグレー色の第２バインダ接着不織布のバインダ付着面（Ｌｂ＝６８．１９）に対して、開口を有するシリンダを用い、第２プリント液をプリントした後、温度１６０℃のドライヤーで乾燥し、自動車用装飾不織布（幅：６５ｃｍ）を製造した。つまり、図１に示すように、格子状模様の印影の部分を「く」の字状に、同じ大きさで、規則的にプリントした（印影部の太さ：１ｍｍ、図１においては黒色で描写）。この自動車用装飾不織布は立体的で装飾性に優れ、また、平均明度Ｌａは６９．８１で、最小明度Ｌａｌは６９．１６で、最小明度差（ΔＬｌ）は０．９７であり、自動車室内を広く感じることができ、圧迫感を和らげることができるものであった。
(Example 2)
Using a cylinder with an opening on the binder-attached surface (Lb = 68.19) of the second binder-bonded nonwoven fabric with a dark gray appearance, print the second print liquid and then dry it with a dryer at a temperature of 160 ° C. Thus, a decorative nonwoven fabric for automobiles (width: 65 cm) was produced. That is, as shown in FIG. 1, the imprinted portion of the lattice-like pattern was regularly printed in the shape of “<” with the same size (thickness of the imprinted portion: 1 mm, black in FIG. 1). Depiction). This decorative nonwoven fabric for automobiles is three-dimensional and excellent in decorativeness, and the average brightness La is 69.81, the minimum brightness Lal is 69.16, and the minimum brightness difference (ΔLl) is 0.97. I could feel it widely and relieve the feeling of pressure.
（比較例３）
準備した外観がダークグレー色の第２バインダ接着不織布を自動車用装飾不織布とした。この自動車用装飾不織布のバインダ付着面における平均明度Ｌａは６８．１９であり、自動車室内を広く感じることができたが、実施例２の装飾不織布と比較して単調で、あまり装飾性に優れていなかった。
(Comparative Example 3)
The prepared second binder-bonded nonwoven fabric having a dark gray color was used as a decorative nonwoven fabric for automobiles. The average brightness La on the binder-attached surface of this decorative nonwoven fabric for automobiles was 68.19, and the interior of the automobile could be felt widely, but it was monotonous and excellent in decorativeness compared with the decorative nonwoven fabric of Example 2. There wasn't.
（比較例４）
準備した外観がライトグレー色の第３バインダ接着不織布のバインダ付着面（Ｌｂ＝７０．７８）に対して、開口を有するシリンダを用い、第２プリント液をプリントしたこと以外は、実施例１と同様にして、自動車用装飾不織布（幅：６５ｃｍ）を製造した。この自動車用装飾不織布の平均明度Ｌａは７１．８０で、最小明度Ｌａｌは７１．４７で、最小明度差（ΔＬｌ）は０．６９であり、自動車室内をある程度広く感じることができたが、プリント柄がぼやけてしまい、あまり装飾性に優れていなかった。
(Comparative Example 4)
Example 1 except that the second print liquid was printed using a cylinder having an opening with respect to the binder adhesion surface (Lb = 70.78) of the third binder-bonded nonwoven fabric having a light gray color as the prepared appearance. Similarly, a decorative nonwoven fabric for automobiles (width: 65 cm) was produced. The average brightness La of this automobile decorative nonwoven fabric was 71.80, the minimum brightness Lal was 71.47, and the minimum brightness difference (ΔLl) was 0.69. The pattern was blurred and was not very decorative.
本発明の自動車用装飾繊維シートは装飾性に優れ、しかも自動車室内において使用すると、広く感じることができ、圧迫感を和らげることのできるシートである。そのため、例えば、天井、ドアサイド、ピラーガーニッシュ、リヤパッケージなどの内装材の表皮材として好適に使用することができる。 The decorative fiber sheet for automobiles of the present invention is a sheet that is excellent in decorativeness, and that can be widely felt when used in an automobile interior, and can relieve the feeling of pressure. Therefore, for example, it can be suitably used as a skin material for interior materials such as ceilings, door sides, pillar garnishes, and rear packages.
Claims (1)