JP2012173367A - Actinic ray-sensitive or radiation-sensitive resin composition and resist film and pattern forming method using the composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a radiation-sensitive resin composition excellent in all of line edge roughness, pattern features, followability for an immersion liquid and dry etching durability, and to provide a resist film and a pattern forming method using the composition.SOLUTION: The radiation-sensitive resin composition contains: (A) a resin having a repeating unit expressed by general formula (I-1) or (I-2); and (C) a compound, which has a molar absorption coefficient ε, at a wavelength of 193 nm measured in an acetonitrile solvent, of a relative ratio of 0.8 or less with respect to triphenylsulfonium nonafluorobutane sulfonate and which generates an acid by irradiation with radiation. In general formulae (I-1) and (I-2), ARand ARrepresent an aromatic group; Rrepresents an alkyl group, a cycloalkyl group or an aryl group; Aand Aeach independently represent a hydrogen atom, an alkyl group, a halogen atom, a cyano group or an alkyloxycarbonyl group; and Z represents a linking group to form a ring together with C-AR.

Description

  The present invention relates to an actinic ray-sensitive or radiation-sensitive resin composition, a resist film using the composition, and a pattern forming method. More specifically, the present invention relates to an ultra-microlithography process applicable to, for example, a manufacturing process of a VLSI and a high-capacity microchip, a process for producing a mold for nanoimprinting and a manufacturing process of a high-density information recording medium, and other photo processing. The present invention relates to a composition suitably used for a fabrication process, and a resist film and a pattern forming method using the composition. In particular, the present invention relates to a composition suitable for exposure using an immersion projection exposure apparatus using far ultraviolet light having a wavelength of 300 nm or less as a light source, and a resist film and a pattern forming method using the same.

The chemically amplified resist composition generates an acid in the exposed area by irradiation with radiation such as far ultraviolet light, and the acid-catalyzed reaction changes the solubility of the active radiation irradiated area and non-irradiated area in the developer. And a pattern forming material for forming a pattern on the substrate.
When a KrF excimer laser is used as an exposure light source, a resin having a basic skeleton of poly (hydroxystyrene) having a small absorption mainly in the 248 nm region is used as a main component. A pattern is formed, which is a better system than the conventional naphthoquinone diazide / novolak resin system.
On the other hand, when a further short wavelength light source, for example, an ArF excimer laser (193 nm) is used as an exposure light source, the compound having an aromatic group exhibits a large absorption in the 193 nm region. It wasn't.
For this reason, an ArF excimer laser resist containing a resin having an alicyclic hydrocarbon structure has been developed. However, it is extremely difficult to find an appropriate combination of resin, acid generator, additive, solvent, and the like used from the viewpoint of the overall performance as a resist.
Regarding these resists, several resist compositions using acid-decomposable resins obtained by copolymerizing acid-decomposable acrylate monomers having an aromatic ring as an acid-decomposable group have been known so far. For example, the resist compositions disclosed in Patent Documents 1 and 2 can be cited, but the absorption in the 193 nm region is high, and problems remain in the pattern shape.
In addition, ArF excimer laser resists using this chemical amplification mechanism are now becoming mainstream, but when exposure is performed using a scanning immersion exposure machine, the immersion liquid follows the movement of the lens. However, if it does not move, the exposure speed decreases, which may affect the productivity. For example, in the case where the immersion liquid is water, it has been desired that the resist film be hydrophobic so that the immersion liquid has good follow-up characteristics. Currently, there is a demand for a resist composition that forms a resist film that can satisfy both shape and dry edging resistance.

JP 2007-279699 A JP 2008-96951 A

  An object of the present invention is to provide an actinic ray-sensitive or radiation-sensitive resin composition excellent in all of line edge roughness, pattern shape, immersion liquid followability and dry edging resistance, and a resist film and a pattern forming method using the same Is to provide.

As a result of intensive studies to solve the above problems, the present inventors have completed the present invention.
For example, the present invention is as follows.
[1]
(A) A resin containing a repeating unit represented by the following general formula (I-1) or (I-2), and (C) a molar extinction coefficient ε at a wavelength of 193 nm measured in an acetonitrile solvent is triphenylsulfonium. An actinic ray-sensitive or radiation-sensitive resin composition containing a compound that generates an acid upon irradiation with actinic rays or radiation in a relative ratio to nonafluorobutanesulfonate of 0.8 or less.

In the general formulas (I-1) and (I-2),
AR ₁ represents an aromatic group.
AR ₂ represents an aromatic group.
R ₁ represents an alkyl group, a cycloalkyl group, or an aryl group.
A ₁ and A ₂ each independently represents a hydrogen atom, an alkyl group, a halogen atom, a cyano group or an alkyloxycarbonyl group.
Z represents a linking group that forms a ring together with C-AR _{2 in} formula (I-2).
[2]
The actinic ray-sensitive or radiation-sensitive resin composition according to [1], wherein the compound (C) is a compound represented by the following general formula (II-1) or (II-2).

上記一般式中、
Ｒａは各々独立に、アルキル基、シクロアルキル基又はアルケニル基を表す。２個のＲａが互いに結合して環を形成してもよく、該環は芳香族環又は飽和炭化水素環と縮環していてもよい。
Ｒ_２０は、水酸基、ハロゲン原子、カルボキシル基、アルキル基、シクロアルキル基、アルコキシ基、アルコキシカルボニル基、アルキルカルボニル基、アルキルスルホニル基、シクロアルキルスルホニル基、又はシクロアルキル基を有する基を表す。複数のＲ_２０が存在する場合、複数のＲ_２０は同一であっても異なっていてもよい。
Ｘ_２は−ＣＲ_２１＝ＣＲ_２２−、−ＮＲ_２３−、−Ｓ−又は−Ｏ−を表す。
Ｒ_２１及びＲ_２２は、各々独立に、水素原子、フッ素原子、水酸基、アルキル基、シクロアルキル基、アルコキシ基、アルコキシカルボニル基、アルキルカルボニル基、アルキルスルホニル基、シクロアルキルスルホニル基又はシクロアルキル基を有する基を表す。
Ｒ_２３は、水素原子、アルキル基、シクロアルキル基、アリール基又はアシル基を表す。
Ｒ_２４はアリール基を表す。
Ｒ_２５及びＲ_２６は、各々独立に、水素原子、ハロゲン原子、アルキル基、シクロアルキル基、アリール基又はシアノ基を表す。
Ｒ_２７及びＲ_２８は、各々独立に、アルキル基、シクロアルキル基、２−オキソアルキル基、２−オキソシクロアルキル基、アルコキシカルボニルアルキル基、アリル基又はビニル基を表す。
Ｒ_２５とＲ_２６及びＲ_２７とＲ_２８はそれぞれ互いに連結して環を形成していても良い。
ｎ_１は０〜３の整数を表す。
ｑは０〜１０の整数を表す。
Ｚ⁻は非求核性アニオンを表す。
〔３〕
前記一般式（ＩＩ−１）で表される化合物（Ｃ）が、下記一般式（ＺＩ−１）で表されるカチオン構造を有する化合物であり、前記一般式（ＩＩ−２）で表される化合物（Ｃ）が、下記一般式（ＺＩ−３）で表されるカチオン構造を有する化合物である、〔２〕に記載の感活性光線性又は感放射線性樹脂組成物。

In the above general formula,
Each Ra independently represents an alkyl group, a cycloalkyl group or an alkenyl group. Two Ras may be bonded to each other to form a ring, and the ring may be condensed with an aromatic ring or a saturated hydrocarbon ring.
R ₂₀ represents a group having a hydroxyl group, a halogen atom, a carboxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. When a plurality of R ₂₀ are present, the plurality of R ₂₀ may be the same or different.
X ₂ is _{-CR 21 = CR 22 -, -} NR 23 -, - S- or an -O-.
R ₂₁ and R ₂₂ each independently represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group or a cycloalkyl group. Represents a group having
R ₂₃ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group or an acyl group.
R ₂₄ represents an aryl group.
R ₂₅ and R ₂₆ each independently represents a hydrogen atom, a halogen atom, an alkyl group, a cycloalkyl group, an aryl group or a cyano group.
R ₂₇ and R ₂₈ each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
R ₂₅ and R ₂₆ and R ₂₇ and R ₂₈ may be connected to each other to form a ring.
n ₁ represents an integer of 0 to 3.
q represents an integer of 0 to 10.
Z ⁻ represents a non-nucleophilic anion.
[3]
The compound (C) represented by the general formula (II-1) is a compound having a cation structure represented by the following general formula (ZI-1), and represented by the general formula (II-2). The actinic ray-sensitive or radiation-sensitive resin composition according to [2], wherein the compound (C) is a compound having a cation structure represented by the following general formula (ZI-3).

In general formula (ZI-1),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, or a group having a cycloalkyl group.
When there are a plurality of R _{14 s,} each independently represents a group having a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. To express.
R ₁₅ each independently represents an alkyl group or a cycloalkyl group. Two R ₁₅ may be bonded to each other to form a ring, and the ring may be condensed with an aromatic ring or a saturated hydrocarbon ring.
l represents an integer of 0-2.
r represents an integer of 0 to 10.

In general formula (ZI-3),
R _{1c to} R _5c are each independently a hydrogen atom, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group Represents a nitro group, an alkylthio group or an arylthio group.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an aryl group.
R _x and R _y each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
Any two or more of R _{1c to} R _5c , R _5c and R _6c , R _6c and R _7c , R _5c and R _x , and R _x and R _y may be bonded to form a ring structure. The ring structure may contain an oxygen atom, a sulfur atom, an ester bond, or an amide bond.
[4]
The actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [3], wherein all of the repeating units constituting the resin (A) are (meth) acrylate-based repeating units.
[5]
(B) The actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [4], further comprising a hydrophobic resin having at least one of a fluorine atom and a silicon atom.
[6]
The actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [5], wherein the resin (A) further contains a repeating unit having a lactone structure.
[7]
The actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [6], wherein the resin (A) further contains a repeating unit represented by the following general formula (AI).

In general formula (AI),
Xa ₁ represents a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₉ . R ₉ represents a hydroxy group or a monovalent organic group.
T represents a single bond or a divalent linking group.
Rx _{1 to} Rx ₃ each independently represents an alkyl group or a cycloalkyl group.
Two of Rx _{1 to} Rx ₃ may combine to form a cycloalkyl group.
[8]
A resist film formed using the actinic ray-sensitive or radiation-sensitive resin composition according to any one of [1] to [7].
[9]
The pattern formation method including the process of exposing the resist film as described in [8], and the process of developing the exposed resist film.
[10]
The pattern forming method according to [9], wherein the exposure is immersion exposure.

The present invention preferably further has the following configuration.
[11]
Any one of [1] to [7], wherein the molar extinction coefficient ε at a wavelength of 193 nm measured in an acetonitrile solvent of the compound (C) is 0.5 or less relative to triphenylsulfonium nonafluorobutanesulfonate. The actinic ray-sensitive or radiation-sensitive resin composition according to Item.
[12]
The activity group according to any one of [1] to [7] and [11], wherein the linking group Z in the general formula (I-2) is represented by the following general formula (I-2-1): A light-sensitive or radiation-sensitive resin composition.

In the above general formula,
R _a1 represents an alkylene group.
Z ′ represents a single bond, an ether bond, a thioether bond, a carbonyl bond, an ester bond, an amide bond, a urethane bond or a urea bond.
* Represents a bond to the carbon atom bonded adjacent the AR _2, ** represents a bond and AR _2.
[13]
The actinic ray-sensitive property according to any one of [1] to [7], [11] and [12], wherein AR ₁ in the general formula (I-1) is a phenyl group having a substituent. Radiation sensitive resin composition.
[14]
The pattern forming method according to [9] or [10], wherein the exposure is exposure with an ArF excimer laser.

  According to the present invention, the actinic ray-sensitive or radiation-sensitive resin composition having excellent line edge roughness, pattern shape, immersion liquid followability and dry edging resistance, and a resist film and a pattern forming method using the same Can be provided.

Hereinafter, embodiments of the present invention will be described in detail.
In the present specification, groups and atomic groups that do not clearly indicate substitution or non-substitution include both those having no substituent and those having a substituent. For example, an “alkyl group” that does not clearly indicate substitution or unsubstituted is not only an alkyl group that does not have a substituent (unsubstituted alkyl group) but also an alkyl group that has a substituent (substituted alkyl group) Is also included.
In the present specification, “active light” or “radiation” means, for example, an emission line spectrum of a mercury lamp, far ultraviolet rays represented by an excimer laser, extreme ultraviolet (EUV) rays, X rays or electron rays (EB). ing. In the present invention, “light” means actinic rays or radiation.
In this specification, “exposure” means not only light irradiation with a mercury lamp, far ultraviolet rays, X-rays, EUV light, etc., but also drawing with particle beams such as electron beams and ion beams, unless otherwise specified. .

The actinic ray-sensitive or radiation-sensitive resin composition of the present invention is
(A) A resin containing a repeating unit represented by the following general formula (I-1) or (I-2) (hereinafter, also simply referred to as “resin (A)”), and (C) measured in an acetonitrile solvent The compound which generate | occur | produces an acid by irradiation of the actinic ray or radiation whose molar extinction coefficient (epsilon) in wavelength 193nm is 0.8 or less with respect to triphenylsulfonium nonafluorobutanesulfonate is contained.

In the general formulas (I-1) and (I-2),
AR ₁ represents an aromatic group.
AR ₂ represents an aromatic group.
R ₁ represents an alkyl group, a cycloalkyl group, or an aryl group.
A ₁ and A ₂ each independently represents a hydrogen atom, an alkyl group, a halogen atom, a cyano group or an alkyloxycarbonyl group.
Z represents a linking group that forms a ring together with C-AR _{2 in} formula (I-2).

The reason why the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is excellent in all of line edge roughness, pattern shape, immersion liquid followability and dry edging resistance is not clear, but is estimated as follows. The
Resin (A) contains a repeating unit represented by the general formula (I-1) or (I-2), thereby contributing to improvement in dissolution contrast between an exposed portion and an unexposed portion in the resist film. It is estimated to be. Furthermore, when used in combination with the compound (C) having excellent light transmittance, the reason is not clear, but it is presumed that excellent line edge roughness and pattern shape are achieved.
In addition, the actinic ray-sensitive or radiation-sensitive resin composition according to the present invention includes the resin (A) containing a repeating unit represented by the general formula (I-1) or (I-2), It is possible to achieve both dry edging resistance and immersion liquid followability. More specifically, the resin (A) contains the repeating unit represented by the general formula (I-1) or (I-2), thereby reducing the dry etching rate of the resist film and receding contact. The corner can be improved.
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention is, for example, a positive composition, typically a positive resist composition. Hereinafter, each component of this composition is demonstrated.

<Resin (A)>
As described above, the actinic ray-sensitive or radiation-sensitive resin composition according to the present invention comprises the resin (A) containing the repeating unit represented by the general formula (I-1) or (I-2). Contains.
The resin (A) is preferably a resin (acid-decomposable resin) whose solubility in an alkaline developer is increased by the action of an acid.
Hereinafter, each group in the repeating unit represented by formula (I-1) or (I-2) will be described.
The aromatic group of AR _1, preferably an aromatic group having 6 to 14 carbon atoms, a phenyl group, a naphthyl group, an anthryl group, and phenanthryl group and the like, more preferably a phenyl group or a naphthyl group, More preferably, it is a phenyl group.
Specific examples of the aromatic group for AR ₂ include a group obtained by removing one arbitrary hydrogen atom from the above-described specific examples of the aromatic group as AR ₁ .
AR ₁ and AR ₂ may each independently have a substituent, and preferred substituents that AR ₁ and AR ₂ may have are alkyl groups having 1 to 8 carbon atoms, and carbon atoms having 4 to 10 carbon atoms. Cycloalkyl group, a C1-C8 alkoxy group, a C2-C8 alkoxycarbonyl group, a carboxyl group, a halogen atom, a hydroxyl group, a cyano group, etc. are mentioned. More preferably, they are a C1-C4 alkyl group and a C1-C8 alkoxy group. When there are two or more substituents, the plural substituents may be the same or different, and the plural substituents may be bonded to form a ring.
The alkyl group in R ₁ may have a substituent, and may be a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a t-butyl group, a pentyl group, a hexyl group, or an octyl group. Group, a dodecyl group, etc. are mentioned, It is preferable that it is a C1-C20 linear or branched alkyl group.
The cycloalkyl group in R ₁ may have a substituent, and examples thereof include a cyclopentyl group and a cyclohexyl group, and a cycloalkyl group having 3 to 20 carbon atoms is preferable.
Preferred substituents that the alkyl group or cycloalkyl group for R ₁ may have include an alkoxy group, a hydroxyl group, a halogen atom, a nitro group, an acyl group, an acyloxy group, an acylamino group, a sulfonylamino group, an alkylthio group, an arylthio group, Heterocyclic residues such as aralkylthio group, thiophenecarbonyloxy group, thiophenemethylcarbonyloxy group, pyrrolidone residue, etc. are mentioned, among them alkoxy group, hydroxyl group, halogen atom, nitro group, acyl group, acyloxy group, acylamino group, A sulfonylamino group is preferred.
Examples of the aryl group in R ₁ include a phenyl group, a xylyl group, a toluyl group, a cumenyl group, a naphthyl group, and an anthracenyl group, and an aryl group having 6 to 14 carbon atoms is preferable.

The alkyl group in A ₁ and A ₂ is preferably a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a t-butyl group, a pentyl group, a hexyl group, an octyl group, or a dodecyl group. Includes a linear or branched alkyl group having 1 to 20 carbon atoms. These groups may have a substituent, and preferred substituents that may be included include an alkoxy group, a hydroxyl group, a halogen atom, a nitro group, an acyl group, an acyloxy group, an acylamino group, a sulfonylamino group, an alkylthio group, Examples include an arylthio group, an aralkylthio group, a thiophenecarbonyloxy group, a thiophenemethylcarbonyloxy group, a heterocyclic residue such as a pyrrolidone residue, and the alkyl group having such a substituent includes a CF ₃ group, an alkyloxy group A carbonylmethyl group, an alkylcarbonyloxymethyl group, a hydroxymethyl group, an alkoxymethyl group and the like are preferable.
The halogen atom in A ₁ and A _2, a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, a fluorine atom is preferable.
Examples of the alkyl group contained in the alkyloxycarbonyl group in A ₁ and A ₂ include the same alkyl groups as in the above ₁ and A ₂ .
Examples of the linking group for Z include an alkylene group, an ether bond, a thioether bond, a carbonyl group, an ester bond, an amide bond, a urethane bond, and a urea bond, or a group obtained by combining two or more of these. Preferably, it is represented by the following general formula (I-2-1).

In the above general formula,
R _a1 represents an alkylene group. The alkylene group may further have a substituent.
The alkylene group for R _a1 preferably has 1 to 10 carbon atoms, and more preferably has 1 to 5 carbon atoms. Examples of such a chain alkylene group include a methylene group, an ethylene group, and a propylene group.
Examples of the substituent that the alkylene group may have include, for example, halogen atoms such as fluorine atom, chlorine atom and bromine atom; mercapto group; hydroxy group; methoxy group, ethoxy group, isopropoxy group, t-butoxy group and benzyloxy. Alkoxy groups: alkyl groups such as methyl group, ethyl group, propyl group, isopropyl group, butyl group, sec-butyl group, t-butyl group, pentyl group and hexyl group; cyclopropyl group, cyclobutyl group, cyclopentyl group, Cycloalkyl groups such as cyclohexyl group and cycloheptyl group; cyano group; nitro group; sulfonyl group; silyl group; ester group; acyl group; vinyl group;
Z ′ represents a single bond, an ether bond, a thioether bond, a carbonyl bond, an ester bond, an amide bond, a urethane bond or a urea bond. Z ′ is more preferably a single bond, an ether bond, a thioether bond, or a carbonyl bond.
* Represents a bond to the carbon atom bonded adjacent the AR _2, ** represents a bond and AR _2.
In the present invention, from the viewpoint of dry etching resistance and receding contact angle improvement, the resin (A) contains a repeating unit represented by the general formula (I-2) or in the general formula (I-1). It is preferable that AR ₁ contains a repeating unit represented by the general formula (I-1) having the above-described substituent, and the resin (A) has a repeating unit represented by the general formula (I-2). It is more preferable to contain.
The total content of the repeating units represented by the general formula (I-1) or (I-2) is preferably 1 to 50 mol% with respect to all the repeating units in the resin, and 2 to 40 mol. % Is more preferable, and 5-35 mol% is still more preferable.
Although the specific example of the repeating unit represented by the said general formula (I-1) or (I-2) is shown below, it is not limited to these.
In the following specific examples, A represents a hydrogen atom, an alkyl group, a halogen atom, a cyano group, or an alkyloxycarbonyl group.

The resin (A) containing the repeating unit represented by the general formula (I-1) or (I-2) is other than the repeating unit represented by the general formula (I-1) or (I-2). In addition, the main chain or side chain of the resin, or both the main chain and the side chain have a group that decomposes by the action of an acid to generate an alkali-soluble group (hereinafter also referred to as “acid-decomposable group”). It is preferable.
The resin (A) is preferably insoluble or hardly soluble in an alkali developer.

The acid-decomposable group preferably has a structure protected with a group capable of decomposing and leaving an alkali-soluble group by the action of an acid.
Alkali-soluble groups include phenolic hydroxyl groups, carboxyl groups, fluorinated alcohol groups, sulfonic acid groups, sulfonamido groups, sulfonylimide groups, (alkylsulfonyl) (alkylcarbonyl) methylene groups, (alkylsulfonyl) (alkylcarbonyl) imides. Group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) methylene group, etc. Is mentioned.

  Preferred alkali-soluble groups include carboxyl groups, fluorinated alcohol groups (preferably hexafluoroisopropanol groups), and sulfonic acid groups.

A preferable group as the acid-decomposable group is a group obtained by substituting the hydrogen atom of these alkali-soluble groups with a group capable of leaving with an acid.
As the acid eliminable group, there can be, for _{example, -C (R 36) (R} 37) (R 38), - C (R 36) (R 37) (OR 39), - C (R 01) (R 02 ) (OR ₃₉ ) and the like.
In the formula, R _{36 to} R ₃₉ each independently represents an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, or an alkenyl group. R ₃₆ and R ₃₇ may be bonded to each other to form a ring.

R ₀₁ and R ₀₂ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkenyl group.

  The acid-decomposable group is preferably a cumyl ester group, an enol ester group, an acetal ester group, a tertiary alkyl ester group or the like. More preferably, it is a tertiary alkyl ester group.

The repeating unit having an acid-decomposable group that can be contained in the resin (A) is preferably a repeating unit represented by the following general formula (AI).

In general formula (AI),
Xa ₁ represents a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₉ . R ₉ represents a hydroxy group or a monovalent organic group, and examples of the monovalent organic group include an alkyl group having 5 or less carbon atoms and an acyl group having 5 or less carbon atoms, preferably 3 or less carbon atoms. And more preferably a methyl group. Xa ₁ preferably represents a hydrogen atom, a methyl group, a trifluoromethyl group or a hydroxymethyl group.

T represents a single bond or a divalent linking group.
Rx _{1 to} Rx ₃ each independently represents an alkyl group (straight or branched) or a cycloalkyl group (monocyclic or polycyclic).
Two of Rx _{1 to} Rx ₃ may combine to form a cycloalkyl group (monocyclic or polycyclic).

Examples of the divalent linking group for T include an alkylene group, —COO—Rt— group, —O—Rt— group, and the like. In the formula, Rt represents an alkylene group or a cycloalkylene group.
T is preferably a single bond or a —COO—Rt— group. Rt is preferably an alkylene group having 1 to 5 carbon atoms, more preferably a —CH ₂ — group, — (CH ₂ ) ₂ — group, or — (CH ₂ ) ₃ — group.
Examples of the alkyl group rx ₁ to Rx _3, methyl, ethyl, n- propyl group, an isopropyl group, n- butyl group, an isobutyl group, those having 1 to 4 carbon atoms such as t- butyl group.

Examples of the cycloalkyl group represented by Rx _{1 to} Rx ₃ include monocyclic cycloalkyl groups such as cyclopentyl group and cyclohexyl group, polycyclic cycloalkyl groups such as norbornyl group, tetracyclodecanyl group, tetracyclododecanyl group, and adamantyl group. Groups are preferred.
Examples of the cycloalkyl group formed by combining at least two of Rx _{1 to} Rx ₃ include a monocyclic cycloalkyl group such as a cyclopentyl group and a cyclohexyl group, a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, A polycyclic cycloalkyl group such as an adamantyl group is preferred. A monocyclic cycloalkyl group having 5 to 6 carbon atoms is particularly preferable.
An embodiment in which Rx ₁ is a methyl group or an ethyl group, and Rx ₂ and Rx ₃ are bonded to form the above-described cycloalkyl group is preferable.

  Each of the above groups may have a substituent. Examples of the substituent include an alkyl group (1 to 4 carbon atoms), a halogen atom, a hydroxyl group, an alkoxy group (1 to 4 carbon atoms), a carboxyl group, An alkoxycarbonyl group (C2-C6) etc. are mentioned, C8 or less is preferable.

  The total content of repeating units having an acid-decomposable group is preferably from 20 to 70 mol%, more preferably from 25 to 50 mol%, based on all repeating units in the resin.

  Although the preferable specific example of the repeating unit which has an acid-decomposable group is shown below, this invention is not limited to this.

In specific examples, Rx and Xa ₁ represent a hydrogen atom, CH ₃ , CF ₃ , or CH ₂ OH. Rxa and Rxb each represents an alkyl group having 1 to 4 carbon atoms. Z represents a substituent containing a polar group, and when there are a plurality of Z, the plurality of Z may be the same as or different from each other. p represents 0 or a positive integer. Specific examples and preferred examples of Z are the same as the specific examples and preferred examples of R ₁₀ in formula (II-1) described later.

  The resin (A) is a resin having at least one of the repeating unit represented by the general formula (I) and the repeating unit represented by the general formula (II) as the repeating unit represented by the general formula (AI). More preferably.

In formulas (I) and (II),
R ₁ and R ₃ each independently represent a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₉ . R ₉ represents a hydroxyl group or a monovalent organic group.
R ₂ , R ₄ , R ₅ and R ₆ each independently represents an alkyl group or a cycloalkyl group.
R represents an atomic group necessary for forming an alicyclic structure together with a carbon atom.

R ₁ and R ₃ preferably represent a hydrogen atom, a methyl group, a trifluoromethyl group or a hydroxymethyl group. Specific examples and preferred examples of the monovalent organic group in R ₉ are the same as those described for R ₉ in formula (AI).

The alkyl group in R ₂ may be linear or branched, and may have a substituent.
The cycloalkyl group in R ₂ may be monocyclic or polycyclic and may have a substituent.
R ₂ is preferably an alkyl group, more preferably 1 to 10 carbon atoms, still more preferably 1 to 5 carbon atoms, and examples thereof include a methyl group and an ethyl group.

  R represents an atomic group necessary for forming an alicyclic structure together with a carbon atom. The alicyclic structure formed by R together with the carbon atom is preferably a monocyclic alicyclic structure, and the carbon number thereof is preferably 3 to 7, more preferably 5 or 6.

R ₃ is preferably a hydrogen atom or a methyl group, and more preferably a methyl group.

The alkyl group in R ₄ , R ₅ , and R ₆ may be linear or branched and may have a substituent. As the alkyl group, those having 1 to 4 carbon atoms such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group and t-butyl group are preferable.

The cycloalkyl group in R ₄ , R ₅ and R ₆ may be monocyclic or polycyclic and may have a substituent. The cycloalkyl group is preferably a monocyclic cycloalkyl group such as a cyclopentyl group or a cyclohexyl group, or a polycyclic cycloalkyl group such as a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group or an adamantyl group.

  As a repeating unit represented by general formula (I), the repeating unit represented by the following general formula (1-a) is mentioned, for example.

In the formula, _{R 1} and _{R 2} have the same meanings as those in formula (1).

The repeating unit represented by the general formula (II) is preferably a repeating unit represented by the following general formula (II-1).

In formula (II-1),
R _{3 to} R ₅ are respectively synonymous with those in the general formula (II).

R ₁₀ represents a substituent containing a polar group. When a plurality of R ₁₀ are present, they may be the same as or different from each other. Examples of the substituent containing a polar group include a hydroxyl group, a cyano group, an amino group, an alkylamide group or a sulfonamide group itself, or a linear or branched alkyl group or cycloalkyl group having at least one of them. An alkyl group having a hydroxyl group is preferable. More preferably, it is a branched alkyl group having a hydroxyl group. As the branched alkyl group, an isopropyl group is particularly preferable.

  p represents an integer of 0 to 15. p is preferably 0 to 2, more preferably 0 or 1.

The acid-decomposable resin is a resin containing at least one of the repeating unit represented by the general formula (I) and the repeating unit represented by the general formula (II) as the repeating unit represented by the general formula (AI). More preferably.
The resin (A) preferably contains a repeating unit having a lactone structure represented by the following general formula (III).

In formula (III),
A represents an ester bond (a group represented by —COO—) or an amide bond (a group represented by —CONH—).
R ₀ represents an alkylene group, a cycloalkylene group, or a combination thereof independently when there are a plurality of R ₀ .
Z is independently a single bond, an ether bond, an ester bond, an amide bond, or a urethane bond when there are a plurality of Zs.

Or urea bond

Represents. Here, R represents a hydrogen atom, an alkyl group, a cycloalkyl group, or an aryl group each independently.

R ₈ represents a monovalent organic group having a lactone structure.
n is the repeating number of the structure represented by —R ₀ —Z—, represents an integer of 1 to 5, and is preferably 1.
R ₇ represents a hydrogen atom, a halogen atom or an alkyl group.

The alkylene group and cycloalkylene group represented by R ₀ may have a substituent.
Z is preferably an ether bond or an ester bond, and particularly preferably an ester bond.

The alkyl group for R ₇ is preferably an alkyl group having 1 to 4 carbon atoms, more preferably a methyl group or an ethyl group, and particularly preferably a methyl group. The alkylene group of R ₀ , the cycloalkylene group, and the alkyl group in R ₇ may each be substituted. Examples of the substituent include a halogen atom such as a fluorine atom, a chlorine atom, and a bromine atom, a mercapto group, and a hydroxy group. Groups, methoxy groups, ethoxy groups, isopropoxy groups, t-butoxy groups, alkoxy groups such as benzyloxy groups, and acyloxy groups such as acetyloxy groups and propionyloxy groups. R ₇ is preferably a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.

A preferable chain alkylene group in R ₀ is preferably a chain alkylene group having 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and examples thereof include a methylene group, an ethylene group, and a propylene group. . A preferable cycloalkylene group is a cycloalkylene group having 3 to 20 carbon atoms, and examples thereof include a cyclohexylene group, a cyclopentylene group, a norbornylene group, and an adamantylene group. In order to exhibit the effect of the present invention, a chain alkylene group is more preferable, and a methylene group is particularly preferable.

The monovalent substituent having a lactone structure represented by R ₈ is not limited as long as it has a lactone structure. General formulas (LC1-1) to (LC1-17) described later as specific examples The structure represented by (LC1-4) is especially preferable among these. Further, n ₂ in (LC1-1) to (LC1-17) is more preferably 2 or less.
R ₈ is preferably a monovalent organic group having an unsubstituted lactone structure or a monovalent organic group having a lactone structure having a methyl group, a cyano group or an alkoxycarbonyl group as a substituent. A monovalent organic group having a lactone structure (cyanolactone) as is more preferable.

Specific examples of the repeating unit having a group having a lactone structure represented by the general formula (III) are shown below, but the present invention is not limited thereto.
In the following specific examples, R represents a hydrogen atom, an alkyl group which may have a substituent, or a halogen atom, preferably a hydrogen atom, a methyl group, a hydroxymethyl group or an acetyloxymethyl group.

  The repeating unit having a lactone structure is more preferably a repeating unit represented by the following general formula (III-1).

In general formula (III-1),
R ₇ , A, R ₀ , Z, and n are as defined in the general formula (III).
R ₉ independently represents an alkyl group, a cycloalkyl group, an alkoxycarbonyl group, a cyano group, a hydroxyl group or an alkoxy group when there are a plurality of R _{9 s, and} when there are a plurality of R _{9 s} , May be formed.

X represents an alkylene group, an oxygen atom, or a sulfur atom.
m is the number of substituents and represents an integer of 0 to 5. m is preferably 0 or 1.

The alkyl group for R ₉ is preferably an alkyl group having 1 to 4 carbon atoms, more preferably a methyl group or an ethyl group, and most preferably a methyl group. Examples of the cycloalkyl group include cyclopropyl, cyclobutyl, cyclopentyl, and cyclohexyl groups. Examples of the alkoxycarbonyl group include a methoxycarbonyl group, an ethoxycarbonyl group, an n-butoxycarbonyl group, and a t-butoxycarbonyl group. Examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, an isopropoxy group, and a butoxy group. These groups may have a substituent, and examples of the substituent include an alkoxy group such as a hydroxy group, a methoxy group, and an ethoxy group, and a halogen atom such as a cyano group and a fluorine atom. R ₉ is more preferably a methyl group, a cyano group or an alkoxycarbonyl group, and even more preferably a cyano group.

  Examples of the alkylene group for X include a methylene group and an ethylene group. X is preferably an oxygen atom or a methylene group, and more preferably a methylene group.

When m is 1 or more, at least one R ₉ is preferably substituted at the α-position or β-position of the lactone carbonyl group, particularly preferably at the α-position.

  Specific examples of the repeating unit having a group having a lactone structure represented by formula (III-1) are shown below, but the present invention is not limited thereto. In the following specific examples, R represents a hydrogen atom, an alkyl group which may have a substituent, or a halogen atom, preferably a hydrogen atom, a methyl group, a hydroxymethyl group or an acetyloxymethyl group.

  The content of the repeating unit represented by the general formula (III) is preferably 15 to 60 mol%, more preferably 20 to 60 mol%, and more preferably 20 to 60 mol% with respect to all the repeating units in the resin when a plurality of types are contained. Preferably it is 30-55 mol%.

  The resin (A) may contain a repeating unit having a lactone group in addition to the unit represented by the general formula (III).

  Any lactone group can be used as long as it has a lactone structure, but it is preferably a 5- to 7-membered ring lactone structure, and forms a bicyclo structure or a spiro structure in the 5- to 7-membered ring lactone structure. The other ring structure is preferably condensed. It is more preferable to have a repeating unit having a lactone structure represented by any of the following general formulas (LC1-1) to (LC1-17). The lactone structure may be directly bonded to the main chain. Preferred lactone structures are (LC1-1), (LC1-4), (LC1-5), (LC1-6), (LC1-13), (LC1-14), and (LC1-17). By using this lactone structure, line width roughness (LWR) and development defects are improved.

The lactone structure portion may or may not have a substituent (Rb ₂ ). Preferred substituents (Rb ₂ ) include an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 4 to 7 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkoxycarbonyl group having 2 to 8 carbon atoms, and a carboxyl group. , Halogen atom, hydroxyl group, cyano group, acid-decomposable group and the like. More preferably, they are a C1-C4 alkyl group, a cyano group, and an acid-decomposable group. n ₂ represents an integer of 0-4. When n ₂ is 2 or more, a plurality of substituents (Rb ₂ ) may be the same or different, and a plurality of substituents (Rb ₂ ) may be bonded to form a ring. .

  As the repeating unit having a lactone structure other than the unit represented by the general formula (III), a repeating unit represented by the following general formula (AII ′) is also preferable.

In general formula (AII ′),
Rb ₀ represents a hydrogen atom, a halogen atom or an alkyl group having 1 to 4 carbon atoms. Preferable substituents that the alkyl group of Rb ₀ may have include a hydroxyl group and a halogen atom. Examples of the halogen atom for Rb ₀ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. Preferred are a hydrogen atom, a methyl group, a hydroxymethyl group, and a trifluoromethyl group, and a hydrogen atom and a methyl group are particularly preferred.

V represents a group having a structure represented by any one of the general formulas (LC1-1) to (LC1-17).
Specific examples of the repeating unit having a lactone group other than the unit represented by the general formula (III) are shown below, but the present invention is not limited thereto.

  Particularly preferred repeating units having a lactone group other than the unit represented by formula (III) include the following repeating units. By selecting an optimal lactone group, the pattern profile and the density dependency are improved.

  The repeating unit having a lactone group usually has an optical isomer, but any optical isomer may be used. One optical isomer may be used alone, or a plurality of optical isomers may be mixed and used. When one kind of optical isomer is mainly used, the optical purity (ee) thereof is preferably 90% or more, more preferably 95% or more.

  The content of the repeating unit having a lactone other than the repeating unit represented by the general formula (III) is preferably 15 to 60 mol% in total, more preferably 15 to 60 mol% with respect to all repeating units in the resin when a plurality of types are contained. Is 20 to 50 mol%, more preferably 30 to 50 mol%.

  In order to enhance the effects of the present invention, two or more lactone repeating units selected from general formula (III) can be used in combination. When using together, it is also preferable to select and use 2 or more types from the lactone repeating unit in which n is 1 in general formula (III).

  The resin (A) preferably has a repeating unit having a hydroxyl group or a cyano group other than the general formulas (AI) and (III). This improves the substrate adhesion and developer compatibility. The repeating unit having a hydroxyl group or a cyano group is preferably a repeating unit having an alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group, and preferably has no acid-decomposable group. The alicyclic hydrocarbon structure in the alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group is preferably an adamantyl group, a diamantyl group, or a norbornane group. As the alicyclic hydrocarbon structure substituted with a preferred hydroxyl group or cyano group, partial structures represented by the following general formulas (VIIa) to (VIId) are preferred.

In general formulas (VIIa) to (VIIc),
R ₂ c to R ₄ c each independently represents a hydrogen atom, a hydroxyl group, or a cyano group. However, at least one of R ₂ c to R ₄ c represents a hydroxyl group or a cyano group. Preferably, one or two of R ₂ c to R ₄ c are a hydroxyl group and the rest are hydrogen atoms. In general formula (VIIa), more preferably, _two of R ₂ c to R ₄ c are a hydroxyl group and the rest are hydrogen atoms.

Examples of the repeating unit having a partial structure represented by the general formulas (VIIa) to (VIId) include the repeating units represented by the following general formulas (AIIa) to (AIId).

In the general formulas (AIIa) to (AIId),
R ₁ c represents a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.

R ₂ c to R ₄ c are in the general formula (VIIa) ~ _(VIIc), same meanings as R 2 c~R ₄ c.

  The content of the repeating unit having a hydroxyl group or a cyano group is preferably from 5 to 40 mol%, more preferably from 5 to 30 mol%, still more preferably from 10 to 25 mol%, based on all repeating units in the resin (A).

  Specific examples of the repeating unit having a hydroxyl group or a cyano group are given below, but the present invention is not limited thereto.

  The resin used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention may have a repeating unit having an alkali-soluble group. Examples of the alkali-soluble group include a carboxyl group, a sulfonamide group, a sulfonylimide group, a bissulfonylimide group, and an aliphatic alcohol (for example, hexafluoroisopropanol group) substituted with an electron-withdrawing group at the α-position. It is more preferable to have a repeating unit. By containing the repeating unit having an alkali-soluble group, the resolution in contact hole applications is increased. The repeating unit having an alkali-soluble group includes a repeating unit in which an alkali-soluble group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or an alkali in the main chain of the resin through a linking group. Either a repeating unit to which a soluble group is bonded, or a polymerization initiator or chain transfer agent having an alkali-soluble group is used at the time of polymerization and introduced at the end of the polymer chain. Both are preferable, and the linking group is monocyclic or polycyclic. It may have a cyclic hydrocarbon structure. Particularly preferred are repeating units of acrylic acid or methacrylic acid.

The resin (A) in the present invention may or may not contain a repeating unit having an alkali-soluble group, but when it is contained, the content of the repeating unit having an alkali-soluble group is the resin (A). 1-20 mol% is preferable with respect to all the repeating units in it, More preferably, it is 3-15 mol%, More preferably, it is 5-10 mol%.
Specific examples of the repeating unit having an alkali-soluble group are shown below, but the present invention is not limited thereto.
In specific examples, Rx represents H, CH ₃ , CH ₂ OH, or CF ₃ .

  The resin (A) of the present invention further has an alicyclic hydrocarbon structure that does not have a polar group (for example, the alkali-soluble group, hydroxyl group, cyano group, etc.) and has a repeating unit that does not exhibit acid decomposability. it can. Examples of such a repeating unit include a repeating unit represented by the general formula (IV).

In general formula (IV), R ₅ represents a hydrocarbon group having at least one cyclic structure and having no polar group.
Ra represents a hydrogen atom, an alkyl group, or a —CH ₂ —O—Ra ₂ group. In the formula, Ra ₂ represents a hydrogen atom, an alkyl group, or an acyl group. Ra is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, particularly preferably a hydrogen atom or a methyl group.

The cyclic structure possessed by R ₅ includes a monocyclic hydrocarbon group and a polycyclic hydrocarbon group. Examples of the monocyclic hydrocarbon group include cycloalkenyl having 3 to 12 carbon atoms such as cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group and the like, and cycloalkyl groups having 3 to 12 carbon atoms and cyclohexenyl group. Groups. Preferable monocyclic hydrocarbon groups are monocyclic hydrocarbon groups having 3 to 7 carbon atoms, and more preferable examples include a cyclopentyl group and a cyclohexyl group.

The polycyclic hydrocarbon group includes a ring assembly hydrocarbon group and a bridged cyclic hydrocarbon group, and examples of the ring assembly hydrocarbon group include a bicyclohexyl group and a perhydronaphthalenyl group. As the bridged cyclic hydrocarbon ring, for example, bicyclic such as pinane, bornane, norpinane, norbornane, bicyclooctane ring (bicyclo [2.2.2] octane ring, bicyclo [3.2.1] octane ring, etc.) Hydrocarbon rings and tricyclic hydrocarbon rings such as homobredan, adamantane, tricyclo [5.2.1.0 ^2,6 ] decane, tricyclo [4.3.1.1 ^2,5 ] undecane ring, tetracyclo [ 4.4.0.1 ^2,5 . 1 ^7,10 ] dodecane, and tetracyclic hydrocarbon rings such as perhydro-1,4-methano-5,8-methanonaphthalene ring. The bridged cyclic hydrocarbon ring includes a condensed cyclic hydrocarbon ring such as perhydronaphthalene (decalin), perhydroanthracene, perhydrophenanthrene, perhydroacenaphthene, perhydrofluorene, perhydroindene, perhydroindene. A condensed ring in which a plurality of 5- to 8-membered cycloalkane rings such as a phenalene ring are condensed is also included.

Preferred examples of the bridged cyclic hydrocarbon ring include a norbornyl group, an adamantyl group, a bicyclooctanyl group, a tricyclo [5,2,1,0 ^2,6 ] decanyl group, and the like. More preferable examples of the bridged cyclic hydrocarbon ring include a norbornyl group and an adamantyl group.

  These alicyclic hydrocarbon groups may have a substituent. Preferred examples of the substituent include a halogen atom, an alkyl group, a hydroxyl group substituted with a hydrogen atom, and an amino group substituted with a hydrogen atom. It is done. Preferred halogen atoms include bromine, chlorine and fluorine atoms, and preferred alkyl groups include methyl, ethyl, butyl and t-butyl groups. The alkyl group described above may further have a substituent, and examples of the substituent that may further include a halogen atom, an alkyl group, a hydroxyl group substituted with a hydrogen atom, and an amino group substituted with a hydrogen atom. The group can be mentioned.

  Examples of the substituent for the hydrogen atom include an alkyl group, a cycloalkyl group, an aralkyl group, a substituted methyl group, a substituted ethyl group, an alkoxycarbonyl group, and an aralkyloxycarbonyl group. Preferred alkyl groups include alkyl groups having 1 to 4 carbon atoms, preferred substituted methyl groups include methoxymethyl, methoxythiomethyl, benzyloxymethyl, t-butoxymethyl, 2-methoxyethoxymethyl groups, and preferred substituted ethyl groups. 1-ethoxyethyl, 1-methyl-1-methoxyethyl, preferred acyl groups include formyl, acetyl, propionyl, butyryl, isobutyryl, valeryl, pivaloyl groups, etc., aliphatic acyl groups having 1 to 6 carbon atoms, alkoxycarbonyl Examples of the group include an alkoxycarbonyl group having 1 to 4 carbon atoms.

The resin (A) has an alicyclic hydrocarbon structure having no polar group, and may or may not contain a repeating unit that does not exhibit acid decomposability. The content of is preferably from 1 to 40 mol%, more preferably from 2 to 20 mol%, based on all repeating units in the resin (A).
Specific examples of the repeating unit having an alicyclic hydrocarbon structure having no polar group and not exhibiting acid decomposability are shown below, but the present invention is not limited thereto. In the formula, Ra represents H, CH ₃ , CH ₂ OH, or CF ₃ .

  Resin (A) used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is not limited to the above repeating structural units, but also includes dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and resist resist. Various repeating structural units can be included for the purpose of adjusting resolution, heat resistance, sensitivity, and the like, which are general necessary characteristics.

  Examples of such repeating structural units include, but are not limited to, repeating structural units corresponding to the following monomers.

  Thereby, performance required for the resin used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, in particular, (1) solubility in coating solvent, (2) film-forming property (glass transition point), Fine adjustments such as (3) alkali developability, (4) film slippage (selection of hydrophilicity / hydrophobicity, alkali-soluble group), (5) adhesion of unexposed part to substrate, (6) dry etching resistance, etc. can be made. .

  As such a monomer, for example, a compound having one addition polymerizable unsaturated bond selected from acrylic acid esters, methacrylic acid esters, acrylamides, methacrylamides, allyl compounds, vinyl ethers, vinyl esters, etc. Etc.

  In addition, any addition-polymerizable unsaturated compound that can be copolymerized with monomers corresponding to the above various repeating structural units may be copolymerized.

  In the resin (A) used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, the content molar ratio of each repeating structural unit is the resistance to dry etching of a resist, suitability for standard developer, substrate adhesion, resist profile, Furthermore, it is appropriately set in order to adjust the resolution, heat resistance, sensitivity, and the like, which are general required performances of the resist.

Resin used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention from the viewpoint of transparency to ArF light when the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is for ArF exposure (A) preferably has substantially no aromatic group. More specifically, the repeating unit having an aromatic group is preferably 5% by mole or less, more preferably 3% by mole or less, and more ideally, during the entire repetition of the resin (A). More preferably, it is 0 mol%, that is, it does not have a repeating unit having an aromatic group. The resin (A) preferably has a monocyclic or polycyclic alicyclic hydrocarbon structure.
In addition, it is preferable that resin (A) does not contain a fluorine atom and a silicon atom from a compatible viewpoint with hydrophobic resin (B) mentioned later.

  The resin (A) used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is preferably such that all of the repeating units are composed of (meth) acrylate repeating units. In this case, all of the repeating units are methacrylate repeating units, all of the repeating units are acrylate repeating units, or all of the repeating units are methacrylate repeating units and acrylate repeating units. Although it can be used, the acrylate-based repeating unit is preferably 50 mol% or less of the total repeating units. Moreover, the alicyclic hydrocarbon substituted by the (meth) acrylate type repeating unit 20-50 mol% which has an acid-decomposable group, the (meth) acrylate type repeating unit 20-50 mol% which has a lactone group, and a hydroxyl group or a cyano group. A copolymer containing 5 to 30 mol% of a (meth) acrylate-based repeating unit having a structure and further containing 0 to 20 mol% of another (meth) acrylate-based repeating unit is also preferred.

  When the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is irradiated with KrF excimer laser light, electron beam, X-ray, or high-energy light beam (EUV, etc.) having a wavelength of 50 nm or less, the resin (A) is: Further, it preferably has a hydroxystyrene repeating unit. More preferably, it has a hydroxystyrene-based repeating unit, a hydroxystyrene-based repeating unit protected with an acid-decomposable group, and an acid-decomposable repeating unit such as a (meth) acrylic acid tertiary alkyl ester.

  Examples of the repeating unit having a preferred acid-decomposable group based on hydroxystyrene include, for example, t-butoxycarbonyloxystyrene, 1-alkoxyethoxystyrene, a repeating unit of (meth) acrylic acid tertiary alkyl ester, and the like. More preferred are repeating units of 2-alkyl-2-adamantyl (meth) acrylate and dialkyl (1-adamantyl) methyl (meth) acrylate.

  The resin (A) in the present invention can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and heating is performed, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable. Examples of the reaction solvent include ethers such as tetrahydrofuran, 1,4-dioxane, diisopropyl ether, ketones such as methyl ethyl ketone and methyl isobutyl ketone, ester solvents such as ethyl acetate, amide solvents such as dimethylformamide and dimethylacetamide, Furthermore, the solvent which melt | dissolves the actinic-ray sensitive or radiation sensitive resin composition of this invention like the below-mentioned propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, and cyclohexanone is mentioned. More preferably, the polymerization is performed using the same solvent as the solvent used in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention. Thereby, generation | occurrence | production of the particle at the time of a preservation | save can be suppressed.

  The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred initiators include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. If desired, an initiator is added or added in portions, and after completion of the reaction, it is put into a solvent and a desired polymer is recovered by a method such as powder or solid recovery. The concentration of the reaction is 5 to 50% by mass, preferably 10 to 30% by mass. The reaction temperature is usually from 10 ° C to 150 ° C, preferably from 30 ° C to 120 ° C, more preferably from 60 ° C to 100 ° C.

  In order to prevent the resin from aggregating after the preparation of the composition, for example, as described in JP-A-2009-037108, the synthesized resin is dissolved in a solvent to form a solution. A step of heating at about 30 ° C. to 90 ° C. for about 30 minutes to 4 hours may be added.

  The weight average molecular weight of the resin (A) of the present invention is preferably 1,000 to 200,000, more preferably 2,000 to 20,000, still more preferably 3, as a polystyrene conversion value by GPC method. 000 to 15,000, particularly preferably 3,000 to 12,000. By setting the weight average molecular weight to 1,000 to 200,000, deterioration of heat resistance and dry etching resistance can be prevented, developability is deteriorated, and viscosity is increased, resulting in deterioration of film forming property. Can be prevented.

  The dispersity (molecular weight distribution) is usually 1.0 to 3.0, preferably 1.0 to 2.6, more preferably 1.0 to 2.0, and particularly preferably 1.4 to 2.0. Those in the range are used. The smaller the molecular weight distribution, the better the resolution and the resist shape, and the smoother the side wall of the resist pattern, the better the roughness.

In the present invention, the content of the resin (A) in the entire composition is preferably from 30 to 99 mass%, more preferably from 60 to 95 mass%, based on the total solid content.
In addition, the resins of the present invention may be used alone or in combination.

<(C) Compound that generates an acid upon irradiation with actinic rays or radiation with a relative extinction coefficient ε at a wavelength of 193 nm measured in acetonitrile solvent of 0.8 or less relative to triphenylsulfonium nonafluorobutanesulfonate>
In the actinic ray-sensitive or radiation-sensitive resin composition according to the present invention, (C) the molar extinction coefficient ε at a wavelength of 193 nm measured in an acetonitrile solvent has a relative ratio to triphenylsulfonium nonafluorobutanesulfonate (hereinafter simply referred to as “ It contains a compound (hereinafter also simply referred to as “compound (C)”) that generates an acid upon irradiation with actinic rays or radiation having a relative molar extinction coefficient of 0.8 or less.
In the present invention, the relative ratio of the molar extinction coefficient ε at a wavelength of 193 nm measured in acetonitrile solvent to triphenylsulfonium nonafluorobutanesulfonate is measured as an anion structure as nonafluorobutanesulfonate from the viewpoint of comparing the characteristics of the cation structure. The relative ratio of the obtained compound (C) to the triphenylsulfonium nonafluorobutanesulfonate of the molar extinction coefficient ε at a wavelength of 193 nm in an acetonitrile solvent.
The molar extinction coefficient ε was calculated according to the Lambert-Beer equation by measuring the UV spectrum of a measurement solution in which the compound (C) was dissolved in an acetonitrile solvent using a 1 cm square cell and measuring the absorbance (A) at 193 nm. It can be calculated from the solution concentration (c: unit mol / L).
The relative molar extinction coefficient at a wavelength of 193 nm with respect to triphenylsulfonium nonafluorobutanesulfonate of the compound (C) is 0.8 or less, preferably 0.1 to 0.8, and preferably 0.2 to 0.6. Is more preferable, and 0.3 to 0.5 is particularly preferable. When the ratio is 0.8 or less, the transmittance of the resist film is increased and the desired performance is obtained. When the ratio is 0.1 or more, the light absorption efficiency is secured and the sensitivity can be maintained.
Since the relative molar extinction coefficient at a wavelength of 193 nm is affected by the aromatic ring, the absorbance can be controlled within the above range by devising the structure of the compound (C) and adjusting the number of aromatic rings, for example. Specific examples thereof include compounds represented by the following general formula (II-1) or (II-2). From the viewpoint of improving LER and the like, the following general formula (II-1) Or it is preferable that it is a compound represented by (II-2).

In the above general formula,
Each Ra independently represents an alkyl group, a cycloalkyl group or an alkenyl group. These groups may have a substituent. Two Ras may be bonded to each other to form a ring, and the ring may be condensed with an aromatic ring or a saturated hydrocarbon ring. The ring (including the condensed ring) may have a substituent.
R ₂₀ represents a group having a hydroxyl group, a halogen atom, a carboxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. When a plurality of R ₂₀ are present, the plurality of R ₂₀ may be the same or different. These groups may have a substituent.
X ₂ is _{-CR 21 = CR 22 -, -} NR 23 -, - S- or an -O-.
R ₂₁ and R ₂₂ each independently represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group or a cycloalkyl group. Represents a group having These groups may have a substituent.
R ₂₃ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group or an acyl group. These groups may have a substituent.
R ₂₄ represents an aryl group.
R ₂₅ and R ₂₆ each independently represents a hydrogen atom, a halogen atom, an alkyl group, a cycloalkyl group, an aryl group or a cyano group.
R ₂₇ and R ₂₈ each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
R ₂₅ and R ₂₆ and R ₂₇ and R ₂₈ may be connected to each other to form a ring.
n ₁ represents an integer of 0 to 3.
q represents an integer of 0 to 10. q is preferably an integer of 0 to 2.
Z ⁻ represents a non-nucleophilic anion.

The alkyl group for R ₂₀ , R ₂₁ , R ₂₂ and Ra is linear or branched and preferably has 1 to 10 carbon atoms, and is preferably a methyl group, an ethyl group, an n-propyl group or an i-propyl group. Group, n-butyl group, 2-methylpropyl group, 1-methylpropyl group, t-butyl group, n-pentyl group, neopentyl group, n-hexyl group, n-heptyl group, n-octyl group, 2-ethylhexyl Group, n-nonyl group, n-decyl group and the like. Of these alkyl groups, a methyl group, an ethyl group, an n-butyl group, a t-butyl group, and the like are preferable.
Examples of the cycloalkyl group represented by R ₂₀ , R ₂₁ , R ₂₂ and Ra include a monocyclic or polycyclic cycloalkyl group (preferably a cycloalkyl group having 3 to 20 carbon atoms). Cyclopropyl, cyclobutyl, cyclopentyl , Cyclohexyl, cycloheptyl, cyclooctyl, cyclododecanyl, cyclopentenyl, cyclohexenyl, cyclooctadienyl, norbornyl, tricyclodecanyl, tetracyclodecanyl, adamantyl, etc., especially cyclopropyl, cyclopentyl, cyclohexyl , Cycloheptyl and cyclooctyl are preferred.
The alkenyl group for Ra is preferably an alkenyl group having 2 to 15 carbon atoms.

The alkoxy group of R ₂₀ , R ₂₁ and R ₂₂ is linear or branched and preferably has 1 to 10 carbon atoms. For example, methoxy group, ethoxy group, n-propoxy group, i-propoxy group Group, n-butoxy group, 2-methylpropoxy group, 1-methylpropoxy group, t-butoxy group, n-pentyloxy group, neopentyloxy group, n-hexyloxy group, n-heptyloxy group, n-octyl An oxy group, 2-ethylhexyloxy group, n-nonyloxy group, n-decyloxy group, etc. can be mentioned. Of these alkoxy groups, a methoxy group, an ethoxy group, an n-propoxy group, an n-butoxy group, and the like are preferable.

The alkoxycarbonyl group for R ₂₀ , R ₂₁ and R ₂₂ is linear or branched and preferably has 2 to 11 carbon atoms, such as a methoxycarbonyl group, an ethoxycarbonyl group, or an n-propoxycarbonyl group. I-propoxycarbonyl group, n-butoxycarbonyl group, 2-methylpropoxycarbonyl group, 1-methylpropoxycarbonyl group, t-butoxycarbonyl group, n-pentyloxycarbonyl group, neopentyloxycarbonyl group, n-hexyloxy A carbonyl group, n-heptyloxycarbonyl group, n-octyloxycarbonyl group, 2-ethylhexyloxycarbonyl group, n-nonyloxycarbonyl group, n-decyloxycarbonyl group, etc. can be mentioned. Of these alkoxycarbonyl groups, a methoxycarbonyl group, an ethoxycarbonyl group, an n-butoxycarbonyl group, and the like are preferable.

Examples of the group having a cycloalkyl group represented by R ₂₀ , R ₂₁ and R ₂₂ include a group having a monocyclic or polycyclic cycloalkyl group (preferably a cycloalkyl group having 3 to 20 carbon atoms). Examples thereof include a monocyclic or polycyclic cycloalkyloxy group and an alkoxy group having a monocyclic or polycyclic cycloalkyl group. These groups may further have a substituent.

The monocyclic or polycyclic cycloalkyloxy group of R ₂₀ , R ₂₁ and R ₂₂ preferably has a total carbon number of 7 or more, more preferably a total carbon number of 7 or more and 15 or less, It preferably has a monocyclic cycloalkyl group. The monocyclic cycloalkyloxy group having 7 or more carbon atoms is cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group, cyclobutyloxy group, cyclooctyloxy group, cyclododecanyloxy group, etc. Optionally substituted with methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, dodecyl, 2-ethylhexyl, isopropyl, sec-butyl, t -Alkyl group such as butyl group, iso-amyl group, hydroxyl group, halogen atom (fluorine, chlorine, bromine, iodine), nitro group, cyano group, amide group, sulfonamido group, methoxy group, ethoxy group, hydroxyethoxy group, Alkoxy groups such as propoxy group, hydroxypropoxy group, butoxy group, Monocyclic cycloalkyloxy having a substituent such as an alkoxycarbonyl group such as a toxylcarbonyl group, an ethoxycarbonyl group, an acyl group such as a formyl group, an acetyl group or a benzoyl group, an acyloxy group such as an acetoxy group or a butyryloxy group, or a carboxy group And a group having a total carbon number of 7 or more in combination with an arbitrary substituent on the cycloalkyl group.
Examples of the polycyclic cycloalkyloxy group having 7 or more total carbon atoms include a norbornyloxy group, a tricyclodecanyloxy group, a tetracyclodecanyloxy group, an adamantyloxy group, and the like.

The alkoxy group having a monocyclic or polycyclic cycloalkyl group of R ₂₀ , R ₂₁ and R ₂₂ preferably has a total carbon number of 7 or more, more preferably a total carbon number of 7 or more and 15 or less. An alkoxy group having a monocyclic cycloalkyl group is preferable. The alkoxy group having a total of 7 or more carbon atoms and having a monocyclic cycloalkyl group is methoxy, ethoxy, propoxy, butoxy, pentyloxy, hexyloxy, heptoxy, octyloxy, dodecyloxy, 2-ethylhexyloxy, isopropoxy, A monocyclic cycloalkyl group which may have the above-mentioned substituent is substituted on an alkoxy group such as sec-butoxy, t-butoxy, iso-amyloxy, etc., and the total carbon number including the substituent is 7 or more. Represents things. Examples thereof include a cyclohexylmethoxy group, a cyclopentylethoxy group, a cyclohexylethoxy group, and the like, and a cyclohexylmethoxy group is preferable.
Examples of the alkoxy group having a polycyclic cycloalkyl group having a total carbon number of 7 or more include a norbornyl methoxy group, a norbornyl ethoxy group, a tricyclodecanyl methoxy group, a tricyclodecanyl ethoxy group, a tetracyclo group. A decanyl methoxy group, a tetracyclodecanyl ethoxy group, an adamantyl methoxy group, an adamantyl ethoxy group, etc. are mentioned, A norbornyl methoxy group, a norbornyl ethoxy group, etc. are preferable.
The alkyl group of the alkyl group of R _{20, R 21} and _{R 22,} include the same specific examples as the alkyl group as _{R 20,} R _{21, R 22} and Ra described above.

The alkylsulfonyl group and cycloalkylsulfonyl group of R ₂₀ , R _21, and R ₂₂ are linear, branched, or cyclic, and preferably those having 1 to 10 carbon atoms. For example, methanesulfonyl group, ethanesulfonyl Group, n-propanesulfonyl group, n-butanesulfonyl group, tert-butanesulfonyl group, n-pentanesulfonyl group, neopentanesulfonyl group, n-hexanesulfonyl group, n-heptanesulfonyl group, n-octanesulfonyl group, 2 -Ethylhexanesulfonyl group n-nonanesulfonyl group, n-decanesulfonyl group, cyclopentanesulfonyl group, cyclohexanesulfonyl group and the like can be mentioned. Of these alkylsulfonyl groups and cycloalkylsulfonyl groups, a methanesulfonyl group, an ethanesulfonyl group, an n-propanesulfonyl group, an n-butanesulfonyl group, a cyclopentanesulfonyl group, a cyclohexanesulfonyl group, and the like are preferable.
The alkyl group for R ₂₃ is preferably a linear or branched alkyl group having 1 to 20 carbon atoms.
The cycloalkyl group of R ₂₃ is preferably a cycloalkyl group having 3 to 20 carbon atoms.
The aryl group for R ₂₃ is preferably an aryl group having 6 to 10 carbon atoms.
The acyl group for R ₂₃ is preferably an acyl group having 2 to 20 carbon atoms.
Examples of the substituent that each group of R ₂₀ , R ₂₁ , R ₂₂ , R ₂₃ and Ra may have include a halogen atom (for example, a fluorine atom), a hydroxyl group, a carboxyl group, a cyano group, and a nitro group. , Alkoxy groups, alkoxyalkyl groups, alkoxycarbonyl groups, alkoxycarbonyloxy groups and the like.

Examples of the alkoxy group include methoxy group, ethoxy group, n-propoxy group, i-propoxy group, n-butoxy group, 2-methylpropoxy group, 1-methylpropoxy group, t-butoxy group, cyclopentyloxy group, Examples thereof include a linear, branched or cyclic alkoxy group having 1 to 20 carbon atoms such as a cyclohexyloxy group.
Examples of the alkoxyalkyl group include straight chain having 2 to 21 carbon atoms such as methoxymethyl group, ethoxymethyl group, 1-methoxyethyl group, 2-methoxyethyl group, 1-ethoxyethyl group, and 2-ethoxyethyl group. Examples thereof include a chain, branched or cyclic alkoxyalkyl group.
Examples of the alkoxycarbonyl group include methoxycarbonyl group, ethoxycarbonyl group, n-propoxycarbonyl group, i-propoxycarbonyl group, n-butoxycarbonyl group, 2-methylpropoxycarbonyl group, 1-methylpropoxycarbonyl group, t Examples thereof include linear, branched or cyclic alkoxycarbonyl groups having 2 to 21 carbon atoms such as butoxycarbonyl group, cyclopentyloxycarbonyl group, cyclohexyloxycarbonyl group and the like.

Examples of the alkoxycarbonyloxy group include methoxycarbonyloxy group, ethoxycarbonyloxy group, n-propoxycarbonyloxy group, i-propoxycarbonyloxy group, n-butoxycarbonyloxy group, t-butoxycarbonyloxy group, and cyclopentyloxy. Examples thereof include straight-chain, branched or cyclic alkoxycarbonyloxy groups having 2 to 21 carbon atoms such as carbonyloxy group and cyclohexyloxycarbonyloxy group.
Each carbon atom in the general formula (II-1) may have a substituent. Examples of such a substituent include an alkyl group (preferably having 1 to 20 carbon atoms), a cycloalkyl group ( Preferably 3 to 20 carbon atoms, an aryl group (preferably 6 to 10 carbon atoms), an alkoxy group (preferably 1 to 20 carbon atoms), an acyl group (preferably 2 to 20 carbon atoms), an acyloxy group (preferably 2-20 carbon atoms, fluorine atom, chlorine atom, bromine atom, iodine atom, hydroxyl group, carboxyl group, nitro group, cyano group, alkoxycarbonyl group, alkylsulfonyl group, arylsulfonyl group, arylcarbonyl group, alkylcarbonyl group, An alkenylcarbonyl group etc. are mentioned.

The aryl group for R ₂₄ may have a substituent, and is preferably an aryl group having 6 to 14 carbon atoms, and examples thereof include a phenyl group and a naphthyl group.
The alkyl group in R _{25 to} R ₂₈ may have a substituent, preferably a linear or branched alkyl group having 1 to 20 carbon atoms, and an oxygen atom, sulfur atom, nitrogen atom in the alkyl chain. You may have.
Examples of the alkyl group having a substituent include groups in which a linear or branched alkyl group is substituted with a cycloalkyl group (for example, an adamantylmethyl group, an adamantylethyl group, a cyclohexylethyl group, a camphor residue, etc.). .
The cycloalkyl group in R _{25 to} R ₂₈ may have a substituent, preferably a cycloalkyl group having 3 to 20 carbon atoms, and may have an oxygen atom in the ring.
The aryl group as R ₂₅ and R ₂₆ preferably has 5 to 15 carbon atoms, and examples thereof include a phenyl group and a naphthyl group.
When R ₂₅ and R ₂₆ combine to form a ring, the group formed by combining R ₂₅ and R ₂₆ is preferably an alkylene group having 2 to 10 carbon atoms, such as an ethylene group or propylene. Group, butylene group, pentylene group, hexylene group and the like. The ring formed by combining R _6c and R _7c may have a hetero atom such as an oxygen atom in the ring.
Examples of the 2-oxoalkyl group and 2-oxocycloalkyl group as R ₂₇ and R ₂₈ include a group having> C═O at the 2-position of the alkyl group and cycloalkyl group as R _{25 to} R _28. .
The alkoxy group in the alkoxycarbonylalkyl group as R ₂₇ and R ₂₈ may be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably 1 to 5 carbon atoms. Linear and branched alkoxy groups (for example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), cyclic alkoxy groups having 3 to 8 carbon atoms (for example, cyclopentyl) Examples of the alkyl group include, for example, an alkyl group having 1 to 12 carbon atoms, preferably a linear alkyl group having 1 to 5 carbon atoms (for example, a methyl group and an ethyl group). Group).

The allyl group as R ₂₇ and R ₂₈ is not particularly limited, but is substituted with an unsubstituted allyl group or a monocyclic or polycyclic cycloalkyl group (preferably a cycloalkyl group having 3 to 10 carbon atoms). It is preferable that it is an allyl group.

The vinyl group as R ₂₇ and R ₂₈ is not particularly limited, but is substituted with an unsubstituted vinyl group or a monocyclic or polycyclic cycloalkyl group (preferably a cycloalkyl group having 3 to 10 carbon atoms). It is preferably a vinyl group.
As the ring structure that R ₂₇ and R ₂₈ may be bonded to each other, divalent R ₂₇ and R ₂₈ (for example, a methylene group, an ethylene group, a propylene group, and the like) are represented by the general formula (II-2). A 5-membered or 6-membered ring formed with a sulfur atom, particularly preferably a 5-membered ring (that is, a tetrahydrothiophene ring).
Each of these groups may further have a substituent. Examples of the substituent that may be included include a halogen atom, a hydroxyl group, a nitro group, a cyano group, a carboxy group, and an alkyl group (preferably having 1 carbon atom). To 20), a cycloalkyl group (preferably 3 to 10 carbon atoms), an aryl group (preferably 5 to 15 carbon atoms), an aryloxy group (preferably 5 to 15 carbon atoms), an alkoxy group (preferably 1 carbon atom). -10), an acyl group (preferably 2 to 20 carbon atoms), an acyloxy group (preferably 2 to 10 carbon atoms), an alkoxycarbonyl group (preferably 2 to 20 carbon atoms), an alkylcarbonyloxy group (preferably a carbon number). 2 to 20), a cycloalkylcarbonyloxy group (preferably 4 to 11 carbon atoms), an alkylthio group (preferably 1 to 20 carbon atoms), an arylthio group (preferably Ku 5-15 carbon atoms), an aminoacyl group (preferably the like 2 to 20 carbon atoms). As for the cyclic structure in the aryl group, cycloalkyl group and the like, and the aminoacyl group, examples of the substituent further include an alkyl group (preferably having 1 to 20 carbon atoms).
As a ring structure that two Ras may be bonded to each other, a 5-membered or 6-membered ring in which two Ras are formed together with a sulfur atom in the general formula (II-1), particularly preferably A 5-membered ring is mentioned, and it may be condensed with one or more aromatic rings or saturated hydrocarbon rings.
Examples of the aromatic ring that may be condensed include a benzene ring and the like, and examples of the saturated hydrocarbon ring include a cyclohexane ring and the like.
The ring (including the condensed ring) that may be formed by bonding these two Ras to each other may have a substituent. Examples of the substituent include the group or atom described above as R _20. And the same groups or atoms, and other examples include a cyano group, a nitro group, and an alkoxycarbonyloxy group.
As the ring structure which may be condensed with an aromatic ring or a saturated hydrocarbon ring, those having 1 sulfur atom and 18 or less carbon atoms are preferable, and more preferably the following general formula (IV-1) ) To (IV-3). In the formula, * represents a bond.

In the above general formula,
Rb ₁ , Rb ₂ , Rb ₃ and Rb ₄ each independently represent an arbitrary substituent, for example, a substituent that the two Ras may form by bonding to each other. The same thing is mentioned.
In the general formulas (IV-1) to (IV-3), when a plurality of Rb ₁ are present, the plurality of Rb ₁ may be the same or different, and when a plurality of Rb ₂ are present, The plurality of Rb ₂ may be the same or different, and when a plurality of Rb ₃ are present, the plurality of Rb ₃ may be the same or different, and when a plurality of Rb ₄ are present, The plurality of Rb ₄ may be the same or different.
nb1, nb3 and nb4 each independently represents an integer of 0 to 4.
nb2 represents an integer of 0 to 5.
mb represents an integer of 0 to 3.

From the viewpoint of improving LER and the like, preferred cation structures in the compound represented by the general formula (II-1) include the following general formulas (ZI-1), (ZI-2), (ZI-4) or ( ZI-5) (hereinafter also referred to as cation structures (ZI-1), (ZI-2), (ZI-4), and (ZI-5)), respectively, A preferable cation structure in the compound represented by (II-2) includes a cation structure represented by the following general formula (ZI-3) (hereinafter also referred to as cation structure (ZI-3)).
The cation structure (ZI-1) is a structure represented by the following general formula (ZI-1).

In general formula (ZI-1),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, or a group having a cycloalkyl group. These groups may have a substituent.
When there are a plurality of R _{14 s,} each independently represents a group having a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. To express. These groups may have a substituent.
R ₁₅ each independently represents an alkyl group or a cycloalkyl group. These groups may have a substituent. Two R ₁₅ may be bonded to each other to form a ring, and the ring may be condensed with an aromatic ring or a saturated hydrocarbon ring. The ring (including the condensed ring) may have a substituent.
l represents an integer of 0-2.
r represents an integer of 0 to 10.
In the general formula (ZI-1), specific examples and preferred examples of the alkyl group and cycloalkyl group of R ₁₃ , R ₁₄ and R ₁₅ include alkyl groups and cycloalkyl groups of R ₂₀ , R ₂₁ , R ₂₂ and Ra. Are similar to those described above.

Specific examples and preferred examples of the alkoxy group and alkoxycarbonyl group of R ₁₃ and R ₁₄ include the same as those described above for the alkoxy group and alkoxycarbonyl group of R ₂₀ , R ₂₁ , and R ₂₂ .
Specific examples and preferred examples of the group having a cycloalkyl group of R ₁₃ and R ₁₄ include the same groups as those described above as the group having a cycloalkyl group of R ₂₀ , R ₂₁ and R ₂₂ .
Specific examples of the alkyl group of the alkylcarbonyl group of R ₁₄ include the same specific examples as the alkyl group as R ₂₀ , R ₂₁ , R ₂₂ and Ra described above.
Specific examples and preferred examples of the alkylsulfonyl group and cycloalkylsulfonyl group of R ₁₄ include the same as those described above for the alkylsulfonyl group and cycloalkylsulfonyl group of R ₂₀ , R ₂₁ and R ₂₂ .
Specific examples and preferred examples of the substituent that each group of R ₁₃ , R ₁₄ , and R ₁₅ may have include groups of R ₂₀ , R ₂₁ , R ₂₂ , R _23, and Ra. Examples of the substituent which may be included are the same as those described above.
The ring structure that two R ₁₅ may be bonded to each other is a 5- or 6-membered structure in which two divalent R ₁₅ are formed together with the sulfur atom in the general formula (ZI-1). Examples thereof include a ring, particularly preferably a 5-membered ring (that is, a tetrahydrothiophene ring), which may be condensed with an aromatic ring or a saturated hydrocarbon ring. This divalent R ₁₅ may have a substituent, and the substituent is the same as those described above as the substituent that the ring which two Ras may be bonded to each other may have. The same thing is mentioned.
R ₁₅ in the general formula (ZI-1) is preferably a methyl group, an ethyl group, a naphthyl group, a divalent group in which two R _15s are bonded to each other to form a tetrahydrothiophene ring structure together with a sulfur atom.
The substituent that R ₁₃ and R ₁₄ may have is preferably a hydroxyl group, an alkoxy group, an alkoxycarbonyl group, or a halogen atom (particularly a fluorine atom).
l is preferably 0 or 1, and more preferably 1.
As r, 0-2 are preferable.
Below, the preferable specific example of the cation structure represented by general formula (ZI-1) is shown.

  The cation structure (ZI-2) is a structure represented by the following general formula (ZI-2).

In general formula (ZI-2),
X _I-2 represents an oxygen atom, a sulfur atom, or a —NRa ₁ — group, and Ra ₁ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, or an acyl group.
Ra ₂ and Ra ₃ each independently represents an alkyl group, a cycloalkyl group, or an alkenyl group. Ra ₂ and Ra ₃ may be bonded to each other to form a ring.
When there are a plurality of Ra _{4 s} , each independently represents an organic group.
m represents an integer of 0 to 3.
X _I-2 is preferably the aforementioned —NRa ₁ — group from the viewpoint of improvement of LER or the like.
The alkyl group of Ra _{1 to} Ra ₃ is preferably a linear or branched alkyl group having 1 to 20 carbon atoms.
The cycloalkyl group of Ra _{1 to} Ra ₃ is preferably a cycloalkyl group having 3 to 20 carbon atoms.
The aryl group of Ra _{1 to} Ra ₃ is preferably an aryl group having 6 to 10 carbon atoms.
The acyl group of Ra ₁ is preferably an acyl group having 2 to 20 carbon atoms.
The alkenyl group for Ra ₂ and Ra ₃ is preferably an alkenyl group having 2 to 15 carbon atoms.
As the ring structure which Ra ₂ and Ra ₃ may be bonded to each other, a 5-membered or 6-membered ring formed with a sulfur atom in the general formula (ZI-2), particularly preferably a 5-membered ring (That is, a tetrahydrothiophene ring) is preferable, and examples thereof include the same ring as the ring which may be formed by connecting R ₁₅ in the general formula (ZI-1).
Examples of the organic group for Ra ₄ include the same groups as those exemplified as the substituent that each carbon atom in the general formula (II-1) may have.
The following specific examples are given as a cation structure represented by general formula (ZI-2).

  The cationic structure (ZI-3) is a structure represented by the following general formula (ZI-3).

In general formula (ZI-3),
R _{1c to} R _5c are each independently a hydrogen atom, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group Represents a nitro group, an alkylthio group or an arylthio group.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an aryl group.
R _x and R _y each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
Any two or more of R _{1c to} R _5c , R _5c and R _6c , R _6c and R _7c , R _5c and R _x , and R _x and R _y may be bonded to form a ring structure. The ring structure may contain an oxygen atom, a sulfur atom, an ester bond, or an amide bond.
Examples of the ring structure include an aromatic or non-aromatic hydrocarbon ring, an aromatic or non-aromatic heterocycle, or a polycyclic fused ring formed by combining two or more of these rings. Examples of the ring structure include 3- to 10-membered rings, preferably 4- to 8-membered rings, and more preferably 5- or 6-membered rings.
Examples of the group formed by combining any two or more of R _{1c to} R _5c , R _6c and R _7c , and R _x and R _y include a butylene group and a pentylene group.
The group formed by combining R _5c and R _6c and R _5c and R _x is preferably a single bond or an alkylene group, and examples of the alkylene group include a methylene group and an ethylene group. .
The alkyl group as R _{1c to} R _7c may be either linear or branched, for example, an alkyl group having 1 to 20 carbon atoms, preferably a linear or branched alkyl group having 1 to 12 carbon atoms. Examples of the cycloalkyl group include a cycloalkyl group having 3 to 8 carbon atoms (for example, a cyclopentyl group and a cyclohexyl group).

The aryl group as R _{1c to} R _5c preferably has 5 to 15 carbon atoms, and examples thereof include a phenyl group and a naphthyl group.
The alkoxy group as R _{1c to} R _{5c may} be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably a linear or branched alkoxy group having 1 to 5 carbon atoms. (For example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), C3-C8 cyclic alkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group) ).

Specific examples of the alkyl group in the alkylcarbonyloxy group and alkylthio group as R _1c to R _5c are the same as specific examples of the alkyl group of _R 1c _{to R 5c.}

Specific examples of the cycloalkyl group in the cycloalkyl carbonyl group as R _1c to R _5c are the same as specific examples of the cycloalkyl group of _R 1c _{to R 5c.}

Specific examples of the aryl group in the aryloxy group and arylthio group as R _1c to R _5c are the same as specific examples of the aryl group of _R 1c _{to R 5c.}
Preferably, any one of R _{1c to} R _5c is a linear or branched alkyl group, a cycloalkyl group, or a linear, branched or cyclic alkoxy group, and more preferably the sum of carbon numbers of R _{1c to} R _5c. Is 2-15. Thereby, solvent solubility improves more and generation | occurrence | production of a particle is suppressed at the time of a preservation | save.

The ring structure that any two or more of R _{1c to} R _5c may be bonded to each other is preferably a 5-membered or 6-membered ring, particularly preferably a 6-membered ring (eg, a phenyl ring). It is done.

The ring structure which may be formed by R _5c and R _6c are bonded to each other, bonded R _5c and R _6c are each other a single bond or an alkylene group (methylene group, ethylene group, etc.) by configuring the generally Examples thereof include a carbonyl carbon atom in the formula (I) and a 4-membered ring (particularly preferably a 5- to 6-membered ring) formed together with the carbon atom.

Specific examples and preferred examples of the aryl group as R _6c and R _7c include the same as those described above for the aryl group as R ₂₅ and R ₂₆ .
When R _6c and _{R 7c} are combined to form a _ring, specific examples and preferred examples of the group formed by the bonding of _{R 6c} and _{R 7c may} be bonded with each _{R 25} and _{R 26} form Examples of the group to be mentioned are the same as those described above.

_Examples of the alkyl group and cycloalkyl group as R _x and R _y include the same alkyl group and cycloalkyl group as in R _{1c to} R _7c .
_Examples of the 2-oxoalkyl group and 2-oxocycloalkyl group as R _x and R _y include a group having> C═O at the 2-position of the alkyl group and cycloalkyl group as R _{1c to} R _7c. .
As for the alkoxy group in the alkoxycarbonylalkyl group as R _x and R _y , the same alkoxy groups as those in R _{1c to} R _5c can be exemplified, and the alkyl group includes, for example, an alkyl group having 1 to 12 carbon atoms. Preferably, a C1-C5 linear alkyl group (for example, a methyl group, an ethyl group) can be mentioned.

Specific examples and preferred examples of the allyl group and vinyl group as R _x and R _y include the same as those described above for the allyl group and vinyl group as R ₂₇ and R ₂₈ .

The ring structure which may be formed by R _5c and R _x are bonded to each other, bonded R _5c and R _x each other a single bond or an alkylene group (methylene group, ethylene group, etc.) by configuring the generally Examples thereof include a 5-membered ring (particularly preferably a 5-membered ring) formed together with the sulfur atom and the carbonyl carbon atom in formula (I).

As the ring structure that R _x and R _y may be bonded to each other, divalent R _x and R _y (for example, a methylene group, an ethylene group, a propylene group, and the like) are represented by the general formula (ZI-3). A 5-membered or 6-membered ring formed with a sulfur atom, particularly preferably a 5-membered ring (that is, a tetrahydrothiophene ring).
R _x and R _y are preferably an alkyl group or cycloalkyl group having 4 or more carbon atoms, more preferably 6 or more, and still more preferably 8 or more alkyl groups or cycloalkyl groups.

R _{1c to} R _7c , R _x and R _y may further have a substituent. Examples of such a substituent include a halogen atom (for example, a fluorine atom), a hydroxyl group, a carboxyl group, a cyano group, and a nitro group. Group, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, acyl group, arylcarbonyl group, alkoxyalkyl group, aryloxyalkyl group, alkoxycarbonyl group, aryloxycarbonyl group, alkoxycarbonyloxy group, aryl An oxycarbonyloxy group etc. can be mentioned.

Examples of the alkyl group include a methyl group, an ethyl group, an n-propyl group, an i-propyl group, an n-butyl group, a 2-methylpropyl group, a 1-methylpropyl group, and a t-butyl group. There can be mentioned up to 12 linear or branched alkyl groups.
As said cycloalkyl group, C3-C10 cycloalkyl groups, such as a cyclopentyl group and a cyclohexyl group, can be mentioned, for example.
As said aryl group, C6-C15 aryl groups, such as a phenyl group and a naphthyl group, can be mentioned, for example.

  Examples of the alkoxy group include methoxy group, ethoxy group, n-propoxy group, i-propoxy group, n-butoxy group, 2-methylpropoxy group, 1-methylpropoxy group, t-butoxy group, cyclopentyloxy group, Examples thereof include a linear, branched or cyclic alkoxy group having 1 to 20 carbon atoms such as a cyclohexyloxy group.

  As said aryloxy group, C6-C10 aryloxy groups, such as a phenyloxy group and a naphthyloxy group, etc. can be mentioned, for example.

  Examples of the acyl group include carbon such as acetyl group, propionyl group, n-butanoyl group, i-butanoyl group, n-heptanoyl group, 2-methylbutanoyl group, 1-methylbutanoyl group and t-heptanoyl group. Examples thereof include a linear or branched acyl group having 2 to 12 atoms.

  Examples of the arylcarbonyl group include aryloxy groups having 6 to 10 carbon atoms such as a phenylcarbonyl group and a naphthylcarbonyl group.

  Examples of the alkoxyalkyl group include straight chain having 2 to 21 carbon atoms such as methoxymethyl group, ethoxymethyl group, 1-methoxyethyl group, 2-methoxyethyl group, 1-ethoxyethyl group, and 2-ethoxyethyl group. Examples thereof include a chain, branched or cyclic alkoxyalkyl group.

  Examples of the aryloxyalkyl group include aryloxy groups having 7 to 12 carbon atoms such as a phenyloxymethyl group, a phenyloxyethyl group, a naphthyloxymethyl group, and a naphthyloxyethyl group.

  Examples of the alkoxycarbonyl group include methoxycarbonyl group, ethoxycarbonyl group, n-propoxycarbonyl group, i-propoxycarbonyl group, n-butoxycarbonyl group, 2-methylpropoxycarbonyl group, 1-methylpropoxycarbonyl group, t Examples thereof include linear, branched or cyclic alkoxycarbonyl groups having 2 to 21 carbon atoms such as butoxycarbonyl group, cyclopentyloxycarbonyl group, cyclohexyloxycarbonyl and the like.

  Examples of the aryloxycarbonyl group include aryloxycarbonyl groups having 7 to 11 carbon atoms such as phenyloxycarbonyl group and naphthyloxycarbonyl group.

  Examples of the alkoxycarbonyloxy group include methoxycarbonyloxy group, ethoxycarbonyloxy group, n-propoxycarbonyloxy group, i-propoxycarbonyloxy group, n-butoxycarbonyloxy group, t-butoxycarbonyloxy group, and cyclopentyloxy. Examples thereof include linear, branched or cyclic alkoxycarbonyloxy groups having 2 to 21 carbon atoms such as carbonyloxy group and cyclohexyloxycarbonyloxy.

  Examples of the aryloxycarbonyloxy group include aryloxycarbonyloxy groups having 7 to 11 carbon atoms such as phenyloxycarbonyloxy group and naphthyloxycarbonyloxy group.

In the general formula (ZI-3), R _1c , R _2c , R _4c and R _5c each independently represent a hydrogen atom, and R _3c is a group other than a hydrogen atom, that is, an alkyl group, a cycloalkyl group, More preferably, it represents an aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group, nitro group, alkylthio group or arylthio group.

  Examples of the cation structure represented by the general formula (ZI-3) include the following specific examples.

  The cation structure (ZI-4) is a structure represented by the following general formula (ZI-4).

In General Formula (ZI-4), R _{41 to} R ₄₃ each independently represent a halogen atom, an alkyl group, an alkoxy group, an acetyl group, or a hydroxyl group.
Examples of the halogen atom for R _{41 to} R ₄₃ include a chlorine atom and a fluorine atom.
The alkyl group for R _{41 to} R ₄₃ is preferably a lower alkyl group having 1 to 5 carbon atoms, more preferably a linear or branched alkyl group, and a methyl group, an ethyl group, a propyl group, or n-butyl. And particularly preferably a tert-butyl group.
The alkoxy group for R _{41 to} R ₄₃ is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a linear or branched alkoxy group, and particularly preferably a methoxy group or an ethoxy group.
n1 to n3 are each independently an integer of 0 to 2, preferably 0 or 1 each independently, and more preferably 0.
When any one of n1 to n3 is 2, the plurality of R _{41 to} R ₄₃ may be the same as or different from each other.
Specific examples of preferable cationic structures represented by general formula (ZI-4) are shown below.

  The cationic structure (ZI-5) is a structure represented by the following general formula (ZI-5).

In the general formula (ZI-5), R _{45 to} R ₄₇ each independently represent a halogen atom, an alkyl group, an acetyl group, an alkoxy group, a carboxyl group, a hydroxyl group, or a hydroxyalkyl group.
Examples of the halogen atom, alkyl group, and alkoxy group as R _{45 to} R ₄₇ include the same groups as R _{41 to} R ₄₃ in formula (ZI-4).
The hydroxyalkyl group is preferably a group in which one or more hydrogen atoms of the above alkyl group are substituted with a hydroxy group, and examples thereof include a hydroxymethyl group, a hydroxyethyl group, a hydroxypropyl group, and the like.
n5 is an integer of 0 to 3, preferably 1 or 2, and more preferably 1.
n6 is an integer of 0 to 3, preferably 0 or 1, and more preferably 0.
n7 is an integer of 0 to 2, preferably 0 or 1, and more preferably 1.
Specific examples of preferable cationic structures represented by general formula (ZI-5) are shown below.

  Among the cation structures represented by the general formulas (ZI-1) to (ZI-5), preferred structures are (ZI-1) to (ZI-3), and (ZI-1) or (ZI-3) More preferably.

In the compound represented by the general formula (II-1) or (II-2), the non-nucleophilic anion as Z ⁻ is, for example, a sulfonate anion, a carboxylate anion, a sulfonylimide anion, or a bis (alkylsulfonyl). ) Imide anion, tris (alkylsulfonyl) methide anion, and the like.

  A non-nucleophilic anion is an anion that has an extremely low ability to cause a nucleophilic reaction, and is an anion that can suppress degradation over time due to an intramolecular nucleophilic reaction. Thereby, the temporal stability of the actinic ray-sensitive or radiation-sensitive resin composition is improved.

  Examples of the sulfonate anion include an aliphatic sulfonate anion, an aromatic sulfonate anion, and a camphor sulfonate anion.

  Examples of the carboxylate anion include an aliphatic carboxylate anion, an aromatic carboxylate anion, and an aralkylcarboxylate anion.

  The aliphatic moiety in the aliphatic sulfonate anion may be an alkyl group or a cycloalkyl group, preferably an alkyl group having 1 to 30 carbon atoms and a cycloalkyl group having 3 to 30 carbon atoms such as methyl. Group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, pentyl group, neopentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group , Tridecyl group, tetradecyl group, pentadecyl group, hexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, eicosyl group, cyclopropyl group, cyclopentyl group, cyclohexyl group, adamantyl group, norbornyl group, bornyl group and the like.

  The aromatic group in the aromatic sulfonate anion is preferably an aryl group having 6 to 14 carbon atoms, such as a phenyl group, a tolyl group, and a naphthyl group.

  The alkyl group, cycloalkyl group and aryl group in the aliphatic sulfonate anion and aromatic sulfonate anion may have a substituent. Examples of the substituent of the alkyl group, cycloalkyl group, and aryl group in the aliphatic sulfonate anion and aromatic sulfonate anion include, for example, a nitro group, a halogen atom (fluorine atom, chlorine atom, bromine atom, iodine atom), carboxy group , Hydroxyl group, amino group, cyano group, alkoxy group (preferably having 1 to 15 carbon atoms), cycloalkyl group (preferably having 3 to 15 carbon atoms), aryl group (preferably having 6 to 14 carbon atoms), alkoxycarbonyl group ( Preferably 2 to 7 carbon atoms, acyl group (preferably 2 to 12 carbon atoms), alkoxycarbonyloxy group (preferably 2 to 7 carbon atoms), alkylthio group (preferably 1 to 15 carbon atoms), alkylsulfonyl group (Preferably having 1 to 15 carbon atoms), alkyliminosulfonyl group (preferably having 2 to 15 carbon atoms), aryl An oxysulfonyl group (preferably having 6 to 20 carbon atoms), an alkylaryloxysulfonyl group (preferably having 7 to 20 carbon atoms), a cycloalkylaryloxysulfonyl group (preferably having 10 to 20 carbon atoms), an alkyloxyalkyloxy group ( Preferable examples include 5 to 20 carbon atoms, a cycloalkylalkyloxyalkyloxy group (preferably 8 to 20 carbon atoms), and the like. About the aryl group and ring structure which each group has, an alkyl group (preferably C1-C15) and a cycloalkyl group (preferably C3-C15) can further be mentioned as a substituent.

  Examples of the aliphatic moiety in the aliphatic carboxylate anion include the same alkyl group and cycloalkyl group as in the aliphatic sulfonate anion.

  Examples of the aromatic group in the aromatic carboxylate anion include the same aryl group as in the aromatic sulfonate anion.

  The aralkyl group in the aralkyl carboxylate anion is preferably an aralkyl group having 7 to 12 carbon atoms, such as a benzyl group, a phenethyl group, a naphthylmethyl group, a naphthylethyl group, and a naphthylbutyl group. The alkyl group, cycloalkyl group, aryl group and aralkyl group in the aliphatic carboxylate anion, aromatic carboxylate anion and aralkylcarboxylate anion may have a substituent. Examples of the substituent of the alkyl group, cycloalkyl group, aryl group and aralkyl group in the aliphatic carboxylate anion, aromatic carboxylate anion and aralkylcarboxylate anion include, for example, the same halogen atom and alkyl as in the aromatic sulfonate anion Group, cycloalkyl group, alkoxy group, alkylthio group and the like.

  Examples of the sulfonylimide anion include saccharin anion.

  The alkyl group in the bis (alkylsulfonyl) imide anion and tris (alkylsulfonyl) methide anion is preferably an alkyl group having 1 to 5 carbon atoms, for example, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl. Group, sec-butyl group, pentyl group, neopentyl group and the like. Examples of substituents for these alkyl groups include halogen atoms, alkyl groups substituted with halogen atoms, alkoxy groups, alkylthio groups, alkyloxysulfonyl groups, aryloxysulfonyl groups, cycloalkylaryloxysulfonyl groups, and the like. Alkyl groups substituted with fluorine atoms are preferred. The two alkyl groups in the bis (alkylsulfonyl) imide anion may be the same or different. Similarly, the plurality of alkyl groups in the tris (alkylsulfonyl) methide anion may be the same or different. Also preferred is an embodiment in which two alkyl groups in the bis (alkylsulfonyl) imide anion are bonded to each other to form a cyclic structure. In this case, it is preferable that the formed cyclic structure is a 5- to 7-membered ring.

Examples of other non-nucleophilic anions include fluorinated phosphorus (eg, PF ₆ ⁻ ), fluorinated boron (eg, BF ₄ ⁻ ), and fluorinated antimony (eg, SbF ₆ ⁻ ). .

Examples of the non-nucleophilic anion of Z ⁻ include an aliphatic sulfonate anion in which the α-position of the sulfonic acid is substituted with a fluorine atom, an aromatic sulfonate anion substituted with a fluorine atom or a group having a fluorine atom, and an alkyl group. A bis (alkylsulfonyl) imide anion substituted with a fluorine atom and a tris (alkylsulfonyl) methide anion wherein an alkyl group is substituted with a fluorine atom are preferred. The non-nucleophilic anion is more preferably a perfluoroaliphatic sulfonic acid anion having 4 to 8 carbon atoms, a benzenesulfonic acid anion having a fluorine atom, still more preferably a nonafluorobutanesulfonic acid anion, a perfluorooctanesulfonic acid anion, It is a pentafluorobenzenesulfonic acid anion and 3,5-bis (trifluoromethyl) benzenesulfonic acid anion.
Moreover, it is preferable that the non-nucleophilic anion of Z ⁻ is represented by the following general formula (LD1), for example.

Where
Xf each independently represents a fluorine atom or an alkyl group substituted with at least one fluorine atom.
R ₁ and R ₂ each independently represents a hydrogen atom, a fluorine atom, or an alkyl group.
L each independently represents a divalent linking group.
Cy represents a cyclic organic group.
x represents an integer of 1 to 20.
y represents an integer of 0 to 10.
z represents an integer of 0 to 10.

Xf represents a fluorine atom or an alkyl group substituted with at least one fluorine atom. The alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms. The alkyl group substituted with at least one fluorine atom is preferably a perfluoroalkyl group.
Xf is preferably a fluorine atom or a perfluoroalkyl group having 1 to 4 carbon atoms. More specifically, Xf is a fluorine atom, CF ₃ , C ₂ F ₅ , C ₃ F ₇ , C ₄ F ₉ , C ₅ F ₁₁ , C ₆ F ₁₃ , C ₇ F ₁₅ , C ₈ F ₁₇ , _{CH 2 CF 3, CH 2 CH} 2 CF 3, CH 2 C 2 F 5, CH 2 CH 2 C 2 F 5, CH 2 C 3 F 7, CH 2 CH 2 C 3 F 7, CH 2 C 4 F 9 Or CH ₂ CH ₂ C ₄ F ₉ , and more preferably a fluorine atom or CF ₃ . In particular, it is preferable that both Xf are fluorine atoms.

R ₁ and R ₂ are each independently a hydrogen atom, a fluorine atom, or an alkyl group. This alkyl group may have a substituent (preferably a fluorine atom), and preferably has 1 to 4 carbon atoms. More preferably, it is a C1-C4 perfluoroalkyl group. Specific examples of the alkyl group having a substituent for R ₁ and R ₂ include, for example, CF ₃ , C ₂ F ₅ , C ₃ F ₇ , C ₄ F ₉ , C ₅ F ₁₁ , C ₆ F ₁₃ , and C _{7. F 15, C 8 F 17,} CH 2 CF 3, CH 2 CH 2 CF 3, CH 2 C 2 F 5, CH 2 CH 2 C 2 F 5, CH 2 C 3 F 7, CH 2 CH 2 C 3 F ₇ , CH ₂ C ₄ F ₉ , and CH ₂ CH ₂ C ₄ F ₉ , among which CF ₃ is preferable.

L represents a divalent linking group. Examples of the divalent linking group include —COO—, —OCO—, —CONH—, —CO—, —O—, —S—, —SO—, —SO ₂ —, an alkylene group, and a cycloalkylene group. , An alkenylene group or a divalent linking group obtained by combining a plurality of these groups. Among them, -COO -, - OCO -, - CONH -, - CO -, - O -, - SO 2 -, - COO- alkylene group -, - OCO- alkylene group - or -CONH- alkylene group - is preferably, -COO -, - OCO -, - CONH -, - SO 2 -, - COO- alkylene group - or -OCO- alkylene group - is more preferable.

  Cy represents a cyclic organic group. Examples of the cyclic organic group include an alicyclic group, an aryl group, and a heterocyclic group.

  The alicyclic group may be monocyclic or polycyclic. Examples of the monocyclic alicyclic group include monocyclic cycloalkyl groups such as a cyclopentyl group, a cyclohexyl group, and a cyclooctyl group. Examples of the polycyclic alicyclic group include polycyclic cycloalkyl groups such as a norbornyl group, a tricyclodecanyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, and an adamantyl group. Among these, an alicyclic group having a bulky structure having 7 or more carbon atoms, such as a norbornyl group, a tricyclodecanyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, and an adamantyl group, is a PEB (heating after exposure) step. From the viewpoints of suppressing diffusibility in the film and improving MEEF (Mask Error Enhancement Factor).

  The aryl group may be monocyclic or polycyclic. Examples of the aryl group include a phenyl group, a naphthyl group, a phenanthryl group, and an anthryl group. Among these, a naphthyl group having a relatively low light absorbance at 193 nm is preferable.

  The heterocyclic group may be monocyclic or polycyclic, but the polycyclic group can suppress acid diffusion more. Moreover, the heterocyclic group may have aromaticity or may not have aromaticity. Examples of the heterocyclic ring having aromaticity include a furan ring, a thiophene ring, a benzofuran ring, a benzothiophene ring, a dibenzofuran ring, a dibenzothiophene ring, and a pyridine ring. Examples of the heterocyclic ring not having aromaticity include a tetrahydropyran ring, a lactone ring, and a decahydroisoquinoline ring. As the heterocyclic ring in the heterocyclic group, a furan ring, a thiophene ring, a pyridine ring, or a decahydroisoquinoline ring is particularly preferable. Examples of the lactone ring include the lactone structure exemplified in the aforementioned resin (A).

  The cyclic organic group may have a substituent. Examples of the substituent include an alkyl group (which may be linear or branched, preferably 1 to 12 carbon atoms), and a cycloalkyl group (monocyclic, polycyclic or spirocyclic). Well, preferably 3 to 20 carbon atoms), aryl group (preferably 6 to 14 carbon atoms), hydroxy group, alkoxy group, ester group, amide group, urethane group, ureido group, thioether group, sulfonamide group, and sulfone An acid ester group is mentioned. The carbon constituting the cyclic organic group (carbon contributing to ring formation) may be a carbonyl carbon.

  x is preferably 1 to 8, more preferably 1 to 4, and particularly preferably 1. y is preferably 0 to 4, and more preferably 0. z is preferably 0 to 8, particularly preferably 0 to 4.

Moreover, it is also preferable that the non-nucleophilic anion of Z ⁻ is represented by the following general formula (LD2), for example.

In General Formula (LD2), Xf, R ₁ , R ₂ , L, Cy, x, y, and z have the same meanings as in General Formula (LD1). Rf is a group containing a fluorine atom.
Examples of the group containing a fluorine atom represented by Rf include an alkyl group having at least one fluorine atom, a cycloalkyl group having at least one fluorine atom, and an aryl group having at least one fluorine atom. .
These alkyl group, cycloalkyl group and aryl group may be substituted with a fluorine atom, or may be substituted with another substituent containing a fluorine atom. When Rf is a cycloalkyl group having at least one fluorine atom or an aryl group having at least one fluorine atom, other substituents containing a fluorine atom include, for example, alkyl substituted with at least one fluorine atom. Groups.
Further, these alkyl group, cycloalkyl group and aryl group may be further substituted with a substituent not containing a fluorine atom. As this substituent, the thing which does not contain a fluorine atom among what was demonstrated about Cy previously can be mentioned, for example.
Examples of the alkyl group having at least one fluorine atom represented by Rf include those described above as the alkyl group substituted with at least one fluorine atom represented by Xf. Examples of the cycloalkyl group having at least one fluorine atom represented by Rf include a perfluorocyclopentyl group and a perfluorocyclohexyl group. Examples of the aryl group having at least one fluorine atom represented by Rf include a perfluorophenyl group.
Specific examples of the compound (C) of the present invention are shown below, but are not limited thereto.
In the following specific examples, the relative molar extinction coefficient is a value obtained by measuring the anion structure as nonafluorobutanesulfonate from the viewpoint of comparing the characteristics of the cation structure.

In this invention, a compound (C) can be used individually by 1 type or in combination of 2 or more types.
The content of the compound (C) in the actinic ray-sensitive or radiation-sensitive resin composition is preferably 0.1 to 30% by mass based on the total solid content of the actinic ray-sensitive or radiation-sensitive resin composition. More preferably, it is 5-30 mass%, More preferably, it is 8-25 mass%.
Further, the compound (C) in the present invention may be used in combination with an acid generator other than the compound (C) (hereinafter also referred to as a combined acid generator).
Although it does not specifically limit as a combined acid generator, Preferably, the compound represented by the following general formula (ZI '), (ZII'), (ZIII ') can be mentioned.

In the general formula (ZI ′), R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.
The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1 to 30, preferably 1 to 20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. Examples of the group formed by combining two of R _{201 to} R ₂₀₃ include an alkylene group (eg, butylene group, pentylene group).
Z ⁻ represents a non-nucleophilic anion (an anion having an extremely low ability to cause a nucleophilic reaction).
Z ^- is a non-nucleophilic anion Z in the compound (C) ^- it has the same meaning as, Z ^- Specific examples and preferred examples of the non-nucleophilic anion Z in the compound (C) ^- specific examples and described above for The thing similar to a preferable example is mentioned.

Examples of the organic group represented by R ₂₀₁ , R ₂₀₂ and R ₂₀₃ include corresponding groups in the compounds (ZI′-1) and (ZI′-2) described later.

In addition, the compound which has two or more structures represented by general formula (ZI ') may be sufficient. For example, at least one of R _{201 to} R ₂₀₃ of the compound represented by the general formula (ZI ′) is different from at least one of R _{201 to} R ₂₀₃ of the other compound represented by the general formula (ZI ′). It may be a compound having a structure bonded through a bond or a linking group.

  More preferred (ZI ′) components include compounds (ZI′-1) and (ZI′-2) described below.

The compound (ZI′-1) is an arylsulfonium compound in which at least one of R _{201 to} R _{203 in} the general formula (ZI ′) is an aryl group, that is, a compound having arylsulfonium as a cation.

Arylsulfonium _compound, all of R 201 _{to R 203} may be an aryl group _{or a} part of R 201 _{to R 203} is an aryl group, but the remainder is an alkyl group or a cycloalkyl _group, the R 201 _{to R 203} All are preferably aryl groups.

  Examples of the arylsulfonium compound include a triarylsulfonium compound, a diarylalkylsulfonium compound, an aryldialkylsulfonium compound, a diarylcycloalkylsulfonium compound, and an aryldicycloalkylsulfonium compound, and a triarylsulfonium compound is preferable. .

  The aryl group of the arylsulfonium compound is preferably a phenyl group or a naphthyl group, and more preferably a phenyl group. The aryl group may be an aryl group having a heterocyclic structure having an oxygen atom, a nitrogen atom, a sulfur atom or the like. Examples of the heterocyclic structure include a pyrrole residue, a furan residue, a thiophene residue, an indole residue, a benzofuran residue, and a benzothiophene residue. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.

  The alkyl group or cycloalkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms and a cycloalkyl group having 3 to 15 carbon atoms, such as a methyl group, Examples thereof include an ethyl group, a propyl group, an n-butyl group, a sec-butyl group, a t-butyl group, a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.

The aryl group, alkyl group and cycloalkyl group of R _{201 to} R ₂₀₃ are an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (for example, 6 to 14 carbon atoms). , An alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, or a phenylthio group may be substituted. Preferred substituents are linear or branched alkyl groups having 1 to 12 carbon atoms, cycloalkyl groups having 3 to 12 carbon atoms, and linear, branched or cyclic alkoxy groups having 1 to 12 carbon atoms, more preferably carbon. These are an alkyl group having 1 to 4 carbon atoms and an alkoxy group having 1 to 4 carbon atoms. The substituent may be substituted with any one of three R _{201 to} R ₂₀₃ , or may be substituted with all three. When R _{201 to} R ₂₀₃ are an aryl group, the substituent is preferably substituted at the p-position of the aryl group.

Next, the compound (ZI′-2) will be described.
Compound (ZI′-2) is a compound in which R _{201 to} R ₂₀₃ in formula (ZI ′) each independently represents an organic group having no aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.

The organic group not containing an aromatic ring as R _{201 to} R ₂₀₃ generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.

R _{201 to} R ₂₀₃ are each independently preferably an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group, more preferably a linear or branched 2-oxoalkyl group, 2-oxocycloalkyl group, alkoxy group. A carbonylmethyl group, particularly preferably a linear or branched 2-oxoalkyl group.

As the alkyl group and cycloalkyl group of R _{201 to} R ₂₀₃ , a linear or branched alkyl group having 1 to 10 carbon atoms (for example, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group). More preferred examples of the alkyl group include a 2-oxoalkyl group and an alkoxycarbonylmethyl group. More preferred examples of the cycloalkyl group include a 2-oxocycloalkyl group.

The 2-oxoalkyl group may be either linear or branched, and a group having> C = O at the 2-position of the above alkyl group is preferable.
The 2-oxocycloalkyl group is preferably a group having> C═O at the 2-position of the cycloalkyl group.

  The alkoxy group in the alkoxycarbonylmethyl group is preferably an alkoxy group having 1 to 5 carbon atoms (methoxy group, ethoxy group, propoxy group, butoxy group, pentoxy group).

R _{201 to} R ₂₀₃ may be further substituted with a halogen atom, an alkoxy group (eg, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.

Next, general formulas (ZII ′) and (ZIII ′) will be described.
In general formulas (ZII ′) and (ZIII ′),
R ₂₀₄ to R ₂₀₇ each independently represents an aryl group, an alkyl group or a cycloalkyl group.
The aryl group, alkyl group, and cycloalkyl group of R _{204 to} R ₂₀₇ are the same as the aryl group described as the aryl group, alkyl group, and cycloalkyl group of R _{201 to} R ₂₀₃ in the aforementioned compound (ZI′-1). It is.
The aryl group, alkyl group, and cycloalkyl group of R _{204 to} R ₂₀₇ may have a substituent. Also as this substituent, what the aryl group, alkyl group, and cycloalkyl group of R _{201 to} R ₂₀₃ in the above-mentioned compound (ZI′-1) may have may be mentioned.
Z ⁻ represents a non-nucleophilic anion, and examples thereof include the same as the non-nucleophilic anion of Z ^{− in} the general formula (ZI ′).
Examples of the combined acid generator that can be used in combination with the compound (C) in the present invention further include compounds represented by the following general formulas (ZIV ′), (ZV ′), and (ZVI ′).

In general formulas (ZIV ′) to (ZVI ′),
Ar ₃ and Ar ₄ each independently represents an aryl group.
R ₂₀₈ , R ₂₀₉ and R ₂₁₀ each independently represents an alkyl group, a cycloalkyl group or an aryl group.
A represents an alkylene group, an alkenylene group or an arylene group.
Specific examples of the aryl group represented by Ar ₃ , Ar ₄ , R ₂₀₈ , R ₂₀₉ and R ₂₁₀ are the same as the specific examples of the aryl group represented by R ₂₀₁ , R ₂₀₂ and R ₂₀₃ in the general formula (ZI′-1). Can be mentioned.
Specific examples of the alkyl group and the cycloalkyl group represented by R ₂₀₈ , R _209, and R ₂₁₀ include an alkyl group and a cycloalkyl group represented by R ₂₀₁ , R _202, and R ₂₀₃ in the general formula (ZI′-2), respectively. The thing similar to a specific example can be mentioned.
The alkylene group of A is alkylene having 1 to 12 carbon atoms (for example, methylene group, ethylene group, propylene group, isopropylene group, butylene group, isobutylene group, etc.), and the alkenylene group of A is 2 to 2 carbon atoms. 12 alkenylene groups (for example, ethenylene group, propenylene group, butenylene group, etc.), and as the arylene group for A, arylene groups having 6 to 10 carbon atoms (for example, phenylene group, tolylene group, naphthylene group, etc.) Can be mentioned.
Among the combined acid generators that can be used in combination with the compound (C) in the present invention, particularly preferred examples are given below.

  When the compound (C) and a combination acid generator other than the compound (C) are used in combination, the acid generator is used in a molar ratio (compound (C) / combination acid generator) and usually 99/1 to 1 20/80, preferably 99/1 to 40/60, more preferably 99/1 to 50/50.

<(B) Hydrophobic resin having at least one of fluorine atom and silicon atom (hereinafter also referred to as hydrophobic resin (B))>
The hydrophobic resin (B) has at least one of a fluorine atom and a silicon atom.
At least one of the fluorine atom and the silicon atom in the hydrophobic resin (B) may be contained in the main chain of the resin, or may be contained in the side chain.

When the hydrophobic resin (B) contains a fluorine atom, the partial structure having a fluorine atom is a resin having an alkyl group having a fluorine atom, a cycloalkyl group having a fluorine atom, or an aryl group having a fluorine atom. Preferably there is.
The alkyl group having a fluorine atom is a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom, preferably 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms, You may have the substituent of.
The cycloalkyl group having a fluorine atom is a monocyclic or polycyclic cycloalkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and may further have another substituent.
Examples of the aryl group having a fluorine atom include those in which at least one hydrogen atom of an aryl group such as a phenyl group or a naphthyl group is substituted with a fluorine atom, and the aryl group may further have another substituent.

  As the alkyl group having a fluorine atom, the cycloalkyl group having a fluorine atom, or the aryl group having a fluorine atom, a group represented by any one of the following general formulas (F2) to (F4) is preferable. However, the present invention is not limited to this.

In general formulas (F2) to (F4),
R _{57 to} R ₆₈ each independently represent a hydrogen atom, a fluorine atom, or an alkyl group (straight or branched). Provided that at least one of R _{57 to} R ₆₁ , at least one of R _{62 to} R ₆₄ and at least one of R _{65 to} R ₆₈ are a fluorine atom or an alkyl group in which at least one hydrogen atom is substituted with a fluorine atom. (Preferably having 1 to 4 carbon atoms).
R _{57 to} R ₆₁ and R _{65 to} R ₆₇ are preferably all fluorine atoms. R ₆₂ , R ₆₃ and R ₆₈ are preferably a fluoroalkyl group (preferably having 1 to 4 carbon atoms), and more preferably a perfluoroalkyl group having 1 to 4 carbon atoms. When R ₆₂ and _{R 63} is a perfluoroalkyl _group, it is preferred that _{R 64} is a hydrogen atom. R ₆₂ and R ₆₃ may be connected to each other to form a ring.

Specific examples of the group represented by the general formula (F2) include a p-fluorophenyl group, a pentafluorophenyl group, and a 3,5-di (trifluoromethyl) phenyl group.
Specific examples of the group represented by the general formula (F3) include trifluoromethyl group, pentafluoropropyl group, pentafluoroethyl group, heptafluorobutyl group, hexafluoroisopropyl group, heptafluoroisopropyl group, hexafluoro (2 -Methyl) isopropyl group, nonafluorobutyl group, octafluoroisobutyl group, nonafluorohexyl group, nonafluoro-t-butyl group, perfluoroisopentyl group, perfluorooctyl group, perfluoro (trimethyl) hexyl group, 2,2 , 3,3-tetrafluorocyclobutyl group, perfluorocyclohexyl group and the like. Hexafluoroisopropyl group, heptafluoroisopropyl group, hexafluoro (2-methyl) isopropyl group, octafluoroisobutyl group, nonafluoro-t-butyl group and perfluoroisopentyl group are preferable, and hexafluoroisopropyl group and heptafluoroisopropyl group are preferable. Further preferred.

Specific examples of the group represented by the general formula (F4) include, for example, —C (CF ₃ ) ₂ OH, —C (C ₂ F ₅ ) ₂ OH, —C (CF ₃ ) (CH ₃ ) OH, -CH _(CF 3) OH and the like, -C _{(CF 3)} 2 OH is preferred.
The partial structure containing a fluorine atom may be directly bonded to the main chain, and further from the group consisting of an alkylene group, a phenylene group, an ether bond, a thioether bond, a carbonyl group, an ester bond, an amide bond, a urethane bond and a ureylene bond. You may couple | bond with the principal chain through the group selected or the group which combined these 2 or more.

  Suitable examples of the repeating unit having a fluorine atom include those shown below.

In the formula, R ₁₀ and R ₁₁ each independently represent a hydrogen atom, a fluorine atom or an alkyl group. The alkyl group is preferably a linear or branched alkyl group having 1 to 4 carbon atoms, which may have a substituent, and examples of the alkyl group having a substituent include a fluorinated alkyl group. it can.

W _{3 to} W ₆ each independently represents an organic group containing at least one fluorine atom. Specific examples include the atomic groups (F2) to (F4).

  In addition to these, the resin (B) may have a unit as shown below as a repeating unit having a fluorine atom.

In the formula, R _{4 to} R ₇ each independently represents a hydrogen atom, a fluorine atom, or an alkyl group. The alkyl group is preferably a linear or branched alkyl group having 1 to 4 carbon atoms, which may have a substituent, and examples of the alkyl group having a substituent include a fluorinated alkyl group. it can.
However, at least one of R _{4 to} R ₇ represents a fluorine atom. R ₄ and R ₅ or R ₆ and R ₇ may form a ring.
W ₂ represents an organic group containing at least one fluorine atom. Specific examples include the atomic groups (F2) to (F4).
L ₂ represents a single bond or a divalent linking group. Examples of the divalent linking group include a substituted or unsubstituted arylene group, a substituted or unsubstituted alkylene group, a substituted or unsubstituted cycloalkylene group, —O—, —SO ₂ —, —CO—, —N (R )-(Wherein R represents a hydrogen atom or alkyl), —NHSO ₂ — or a divalent linking group in which a plurality of these are combined.
Q represents an alicyclic structure. The alicyclic structure may have a substituent, may be monocyclic, may be polycyclic, and may be bridged in the case of polycyclic. As the monocyclic type, a cycloalkyl group having 3 to 8 carbon atoms is preferable, and examples thereof include a cyclopentyl group, a cyclohexyl group, a cyclobutyl group, and a cyclooctyl group. Examples of the polycyclic type include groups having a bicyclo, tricyclo or tetracyclo structure having 5 or more carbon atoms, and a cycloalkyl group having 6 to 20 carbon atoms is preferable, for example, an adamantyl group, norbornyl group, dicyclopentyl group. , Tricyclodecanyl group, tetocyclododecyl group and the like. A part of carbon atoms in the cycloalkyl group may be substituted with a hetero atom such as an oxygen atom. Particularly preferred examples of Q include a norbornyl group, a tricyclodecanyl group, a tetocyclododecyl group, and the like.

The hydrophobic resin (B) may contain a silicon atom.
The partial structure having a silicon atom preferably has an alkylsilyl structure (preferably a trialkylsilyl group) or a cyclic siloxane structure.
Specific examples of the alkylsilyl structure or the cyclic siloxane structure include groups represented by the following general formulas (CS-1) to (CS-3).

In general formulas (CS-1) to (CS-3),
R _{12 to} R ₂₆ each independently represent a linear or branched alkyl group (preferably having 1 to 20 carbon atoms) or a cycloalkyl group (preferably having 3 to 20 carbon atoms).
L < ₃ > -L < ₅ > represents a single bond or a bivalent coupling group. The divalent linking group includes an alkylene group, a phenylene group, an ether bond, a thioether bond, a carbonyl group, an ester bond, an amide bond, a urethane bond, or a group of two or more groups selected from the group consisting of a ureylene bond. A combination is mentioned.
n represents an integer of 1 to 5. n is preferably an integer of 2 to 4.

  The repeating unit having at least either a fluorine atom or a silicon atom is preferably a (meth) acrylate-based repeating unit.

Hereinafter, although the specific example of the repeating unit which has at least any one of a fluorine atom and a silicon atom is given, this invention is not limited to this. In specific examples, X ₁ represents a hydrogen atom, —CH ₃ , —F or —CF ₃ , and X ₂ represents —F or —CF ₃ .

The hydrophobic resin (B) preferably has a repeating unit (b) having at least one group selected from the group consisting of the following (x) to (z).
(X) Alkali-soluble group (y) A group that decomposes by the action of an alkali developer and increases the solubility in an alkali developer (hereinafter also referred to as a polar conversion group).
(Z) A group that is decomposed by the action of an acid to increase the solubility in an alkali developer.

Examples of the repeating unit (b) include the following types.
A repeating unit (b ′) having at least one of a fluorine atom and a silicon atom and at least one group selected from the group consisting of the above (x) to (z) on one side chain
A repeating unit (b *) having at least one group selected from the group consisting of (x) to (z) and having no fluorine atom and no silicon atom
A fluorine atom and silicon on one side chain having at least one group selected from the group consisting of (x) to (z) above and on a side chain different from the side chain in the same repeating unit Repeating unit (b ″) having at least one of atoms

The hydrophobic resin (B) preferably has a repeating unit (b ′) as the repeating unit (b). That is, it is more preferable that the repeating unit (b) having at least one group selected from the group consisting of the above (x) to (z) has at least one of a fluorine atom and a silicon atom.
In addition, when hydrophobic resin (B) has a repeating unit (b *), it is different from the repeating unit which has at least any one of a fluorine atom and a silicon atom (the said repeating unit (b '), (b'')). A side chain having at least one group selected from the group consisting of the following (x) to (z) in the repeating unit (b ″), a fluorine atom and a silicon atom. The side chain having at least one of them is preferably bonded to the same carbon atom in the main chain, that is, in a positional relationship as shown in the following formula (K1).
In the formula, B1 represents a partial structure having at least one group selected from the group consisting of the above (x) to (z), and B2 represents a partial structure having at least one of a fluorine atom and a silicon atom.

The group selected from the group consisting of the above (x) to (z) is preferably (x) an alkali-soluble group or (y) a polar conversion group, and more preferably (y) a polar conversion group.
Examples of the alkali-soluble group (x) include phenolic hydroxyl group, carboxylic acid group, fluorinated alcohol group, sulfonic acid group, sulfonamide group, sulfonylimide group, (alkylsulfonyl) (alkylcarbonyl) methylene group, (alkylsulfonyl) ( Alkylcarbonyl) imide group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) ) And a methylene group.
Preferred alkali-soluble groups include fluorinated alcohol groups (preferably hexafluoroisopropanol), sulfonimide groups, and bis (carbonyl) methylene groups.

  As the repeating unit (bx) having an alkali-soluble group (x), a repeating unit in which an alkali-soluble group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or a linking group is used. Examples include a repeating unit in which an alkali-soluble group is bonded to the main chain of the resin. Furthermore, a polymerization initiator or a chain transfer agent having an alkali-soluble group can be used at the time of polymerization to be introduced at the end of the polymer chain, Either case is preferred.

  In the case where the repeating unit (bx) is a repeating unit having at least one of a fluorine atom and a silicon atom (that is, corresponding to the repeating unit (b ′) or (b ″)), the repeating unit (bx) Examples of the partial structure having a fluorine atom include the same ones as mentioned in the repeating unit having at least one of the fluorine atom and the silicon atom, and preferably represented by the general formulas (F2) to (F4). In this case, the partial structure having a silicon atom in the repeating unit (bx) is the same as that described in the repeating unit having at least one of the fluorine atom and the silicon atom. Preferably, groups represented by the general formulas (CS-1) to (CS-3) can be exemplified.

The content of the repeating unit (bx) having an alkali-soluble group (x) is preferably 1 to 50 mol%, more preferably 3 to 35 mol%, still more preferably 5 to 5 mol% with respect to all repeating units in the resin (B). 20 mol%.
Specific examples of the repeating unit (bx) having an alkali-soluble group (x) are shown below, but the present invention is not limited thereto. In specific examples, X ₁ represents a hydrogen atom, —CH ₃ , —F or —CF ₃ .

Examples of the polar conversion group (y) include a lactone group, a carboxylic acid ester group (—COO—), an acid anhydride group (—C (O) OC (O) —), an acid imide group (—NHCONH—), A carboxylic acid thioester group (—COS—), a carbonic acid ester group (—OC (O) O—), a sulfate ester group (—OSO ₂ O—), a sulfonic acid ester group (—SO ₂ O—), and the like. A lactone group is preferred.
The polarity converting group (y) is, for example, introduced into the side chain of the resin by being included in a repeating unit of acrylic acid ester or methacrylic acid ester, or a polymerization initiator or chain having the polarity converting group (y). Any form in which a transfer agent is introduced at the end of the polymer chain using the polymerization is preferred.

Specific examples of the repeating unit (by) having a polar conversion group (y) include a repeating unit having a lactone structure represented by formulas (KA-1-1) to (KA-1-17) described later. Can do.
Further, the repeating unit (by) having the polarity converting group (y) is a repeating unit having at least one of a fluorine atom and a silicon atom (that is, the repeating unit (b ′), (b ″) corresponds to the repeating unit (b ′)). The resin having the repeating unit (by) is hydrophobic, but is particularly preferable from the viewpoint of reducing development defects.

  As the repeating unit (by), for example, a repeating unit represented by the formula (K0) can be given.

In the formula, R _k1 represents a hydrogen atom, a halogen atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an aryl group, or a group containing a polarity converting group.
R _k2 represents an alkyl group, a cycloalkyl group, an aryl group, or a group containing a polarity converting group.
However, at least one of R _k1 and R _k2 represents a group containing a polarity converting group.

  The polarity converting group represents a group that decomposes by the action of an alkali developer and increases the solubility in the alkali developer as described above. The polar conversion group is preferably a group represented by X in the partial structure represented by the general formula (KA-1) or (KB-1).

X in the general formula (KA-1) or (KB-1) is a carboxylic acid ester group: —COO—, an acid anhydride group: —C (O) OC (O) —, an acid imide group: —NHCONH—, Carboxylic acid thioester group: —COS—, carbonate ester group: —OC (O) O—, sulfate ester group: —OSO ₂ O—, sulfonate ester group: —SO ₂ O—.
Y ¹ and Y ² may be the same or different and each represents an electron-withdrawing group.
The repeating unit (by) has a group that increases the solubility in a preferable alkali developer by having a group having a partial structure represented by the general formula (KA-1) or (KB-1). Are bonded to each other as in the case of the partial structure represented by the general formula (KA-1) and the partial structure represented by (KB-1) when Y ¹ and Y ² are monovalent When it does not have a hand, the group having the partial structure is a group having a monovalent or higher group obtained by removing at least one arbitrary hydrogen atom in the partial structure.
The partial structure represented by the general formula (KA-1) or (KB-1) is linked to the main chain of the resin (B) via a substituent at an arbitrary position.

The partial structure represented by the general formula (KA-1) is a structure that forms a ring structure with the group as X.
X in the general formula (KA-1) is preferably a carboxylic acid ester group (that is, when a lactone ring structure is formed as KA-1), an acid anhydride group, or a carbonic acid ester group. More preferably, it is a carboxylic acid ester group.
The ring structure represented by the general formula (KA-1) may have a substituent, for example, may have nka substituents Z _ka1 .
Z _ka1 independently represents a halogen atom, an alkyl group, a cycloalkyl group, an ether group, a hydroxyl group, an amide group, an aryl group, a lactone ring group, or an electron-withdrawing group, when there are a plurality of Z _ka1 .
Z _ka1 may be linked to form a ring. Examples of the ring formed by connecting Z _{ka1 to} each other include a cycloalkyl ring and a hetero ring (a cyclic ether ring, a lactone ring, etc.).
nka represents an integer of 0 to 10. Preferably it is an integer of 0 to 8, more preferably an integer of 0 to 5, more preferably an integer of 1 to 4, and most preferably an integer of 1 to 3.

The electron withdrawing group as Z _{ka1 is the same} as the electron withdrawing group as Y ¹ and Y ² described later. The electron withdrawing group may be substituted with another electron withdrawing group.

Z _ka1 is preferably an alkyl group, a cycloalkyl group, an ether group, a hydroxyl group, or an electron withdrawing group, and more preferably an alkyl group, a cycloalkyl group, or an electron withdrawing group. In addition, as an ether group, the thing substituted by the alkyl group or the cycloalkyl group, ie, the alkyl ether group, etc. are preferable. The electron withdrawing group has the same meaning as described above.
Examples of the halogen atom as Z _ka1 include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferable.
The alkyl group as Z _ka1 may have a substituent and may be linear or branched. As a linear alkyl group, Preferably it is C1-C30, More preferably, it is 1-20, for example, a methyl group, an ethyl group, n-propyl group, n-butyl group, sec-butyl group, t-butyl. Group, n-pentyl group, n-hexyl group, n-heptyl group, n-octyl group, n-nonyl group, n-decanyl group and the like. As a branched alkyl group, Preferably it is C3-C30, More preferably, it is 3-20, for example, i-propyl group, i-butyl group, t-butyl group, i-pentyl group, t-pentyl group, Examples include i-hexyl group, t-hexyl group, i-heptyl group, t-heptyl group, i-octyl group, t-octyl group, i-nonyl group, t-decanoyl group and the like. C1-C4 things, such as a methyl group, an ethyl group, n-propyl group, i-propyl group, n-butyl group, i-butyl group, t-butyl group, are preferable.
The cycloalkyl group as Z _ka1 may have a substituent, and may be monocyclic or polycyclic. In the case of a polycyclic type, the cycloalkyl group may be a bridged type. That is, in this case, the cycloalkyl group may have a bridged structure. The monocyclic type is preferably a cycloalkyl group having 3 to 8 carbon atoms, and examples thereof include a cyclopropyl group, a cyclopentyl group, a cyclohexyl group, a cyclobutyl group, and a cyclooctyl group. Examples of the polycyclic type include groups having a bicyclo, tricyclo, tetracyclo structure or the like having 5 or more carbon atoms, and a cycloalkyl group having 6 to 20 carbon atoms is preferable. For example, an adamantyl group, norbornyl group, isobornyl group, Examples thereof include a camphanyl group, a dicyclopentyl group, an α-pinel group, a tricyclodecanyl group, a tetocyclododecyl group, and an androstanyl group. As the cycloalkyl group, the following structure is also preferable. A part of carbon atoms in the cycloalkyl group may be substituted with a hetero atom such as an oxygen atom.

Preferred examples of the alicyclic moiety include adamantyl group, noradamantyl group, decalin group, tricyclodecanyl group, tetracyclododecanyl group, norbornyl group, cedrol group, cyclohexyl group, cycloheptyl group, cyclooctyl group, cyclodecanyl group. And cyclododecanyl group. More preferred are an adamantyl group, a decalin group, a norbornyl group, a cedrol group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclodecanyl group, a cyclododecanyl group, and a tricyclodecanyl group.
Examples of the substituent of these alicyclic structures include an alkyl group, a halogen atom, a hydroxyl group, an alkoxy group, a carboxyl group, and an alkoxycarbonyl group. The alkyl group is preferably a lower alkyl group such as a methyl group, an ethyl group, a propyl group, an isopropyl group, or a butyl group, and more preferably a methyl group, an ethyl group, a propyl group, or an isopropyl group. Preferred examples of the alkoxy group include those having 1 to 4 carbon atoms such as a methoxy group, an ethoxy group, a propoxy group, and a butoxy group. Examples of the substituent that the alkyl group and the alkoxy group may have include a hydroxyl group, a halogen atom, and an alkoxy group (preferably having 1 to 4 carbon atoms).

  Further, the above group may further have a substituent, and examples of the further substituent include a hydroxyl group, a halogen atom (fluorine, chlorine, bromine, iodine), a nitro group, a cyano group, the above alkyl group, and a methoxy group. , Ethoxy group, hydroxyethoxy group, propoxy group, hydroxypropoxy group, n-butoxy group, isobutoxy group, sec-butoxy group, alkoxy group such as t-butoxy group, alkoxycarbonyl group such as methoxycarbonyl group, ethoxycarbonyl group, Aralkyl group such as benzyl group, phenethyl group, cumyl group, aralkyloxy group, formyl group, acetyl group, butyryl group, benzoyl group, cyanamyl group, acyl group such as valeryl group, acyloxy group such as butyryloxy group, the above alkenyl group , Vinyloxy group, propenyloxy group, allyloxy group, butene Aryloxy alkenyloxy groups such as the above aryl group, an aryloxy group such as phenoxy group, and an aryloxycarbonyl group such as benzoyloxy group.

X in the general formula (KA-1) is a carboxylic acid ester group, and the partial structure represented by the general formula (KA-1) is preferably a lactone ring, and more preferably a 5- to 7-membered lactone ring.
In addition, as in the following (KA-1-1) to (KA-1-17), a 5- to 7-membered lactone ring as a partial structure represented by the general formula (KA-1) has a bicyclo structure, a spiro It is preferred that other ring structures are condensed in a form that forms the structure.
As for the peripheral ring structure to which the ring structure represented by the general formula (KA-1) may be bonded, for example, those in the following (KA-1-1) to (KA-1-17), or The thing according to can be mentioned.

  As a structure containing a lactone ring structure represented by the general formula (KA-1), a structure represented by any one of the following (KA-1-1) to (KA-1-17) is more preferable. The lactone structure may be directly bonded to the main chain. Preferred structures include (KA-1-1), (KA-1-4), (KA-1-5), (KA-1-6), (KA-1-13), (KA-1- 14) and (KA-1-17).

The structure containing the lactone ring structure may or may not have a substituent. Preferable substituents include those similar to the substituent Z _ka1 that the ring structure represented by the general formula (KA-1) may have.

  Preferred examples of X in the general formula (KB-1) include a carboxylic acid ester group (—COO—).

Y ¹ and Y ² in formula (KB-1) each independently represent an electron-withdrawing group.

  The electron withdrawing group is a partial structure represented by the following formula (EW). * In the formula (EW) represents a bond directly connected to (KA-1) or a bond directly connected to X in (KB-1).

In formula (EW),
n _ew is the repeating number of the linking group represented by —C (R _ew1 ) (R _ew2 ) — and represents an integer of 0 or 1. When n _ew is 0, it represents a single bond, indicating that Y _ew1 is directly bonded.
Y _ew1 is a halogen atom, a cyano group, a nitrile group, a nitro group, a halo (cyclo) alkyl group or a haloaryl group represented by —C (R _f1 ) (R _f2 ) —R _f3 , an oxy group, a carbonyl group, a sulfonyl group Examples thereof include a group, a sulfinyl group, and combinations thereof. The electron-withdrawing group may have the following structure, for example. The “halo (cyclo) alkyl group” represents an alkyl group and a cycloalkyl group that are at least partially halogenated, and the “haloaryl group” represents an aryl group that is at least partially halogenated. In the following structural formula, R _ew3 and R _ew4 each independently represent an arbitrary structure. R _ew3 and R _ew4 may have any structure, and the partial structure represented by the formula (EW) may have an electron withdrawing property, and may be linked to, for example, the main chain of the resin. An alkyl group and a fluorinated alkyl group;

When Y _ew1 is a divalent or higher group, the remaining bond forms a bond with an arbitrary atom or substituent. At least one group of Y _ew1 , R _ew1 , and R _ew2 may be connected to the main chain of the resin (C) through a further substituent.
Y _ew1 is preferably a halogen atom, or a halo (cyclo) alkyl group or haloaryl group represented by —C (R _f1 ) (R _f2 ) —R _f3 .
R _ew1 and R _ew2 each independently represent an arbitrary substituent, for example, a hydrogen atom, an alkyl group, a cycloalkyl group, or an aryl group.
At least two of R _ew1 , R _ew2 and Y _ew1 may be connected to each other to form a ring.

Here, R _f1 represents a halogen atom, a perhaloalkyl group, a perhalocycloalkyl group, or a perhaloaryl group, more preferably a fluorine atom, a perfluoroalkyl group, or a perfluorocycloalkyl group, still more preferably a fluorine atom or a trialkyl group. Represents a fluoromethyl group.
R _f2 and R _f3 each independently represent a hydrogen atom, a halogen atom or an organic group, and R _f2 and R _f3 may be linked to form a ring. Examples of the organic group include an alkyl group, a cycloalkyl group, and an alkoxy group. More preferably, R _f2 represents the same group as R _f1 or is linked to R _f3 to form a ring.
R _{f1 to} R _f3 may be linked to form a ring, and examples of the ring formed include a (halo) cycloalkyl ring and a (halo) aryl ring.
Examples of the (halo) alkyl group in R _{f1 to} R _f3 include the alkyl group in Z _ka1 described above and a structure in which this is halogenated.
Examples of the (per) halocycloalkyl group and the (per) haloaryl group in R _{f1 to} R _f3 or in the ring formed by linking R _f2 and R _f3 include, for example, the aforementioned cycloalkyl group in Z _ka1 is a halogen atom. And a perfluoroaryl group represented by -C _(n) F _(n-1) and more preferably a fluorocycloalkyl group represented by -C _(n) F _(2n-2) H Can be mentioned. Although carbon number n is not specifically limited here, the thing of 5-13 is preferable and 6 is more preferable.

The ring that may be formed by linking at least two of R _ew1 , R _ew2 and Y _ew1 preferably includes a cycloalkyl group or a heterocyclic group, and the heterocyclic group is preferably a lactone ring group. Examples of the lactone ring include structures represented by the above formulas (KA-1-1) to (KA-1-17).

In the repeating unit (by), a plurality of partial structures represented by the general formula (KA-1), a plurality of partial structures represented by the general formula (KB-1), or a general formula (KA) It may have both a partial structure represented by -1) and a partial structure represented by the general formula (KB-1).
Note that part or all of the partial structure of the general formula (KA-1) may also serve as an electron withdrawing group as Y ¹ or Y ² in the general formula (KB-1). For example, when X in the general formula (KA-1) is a carboxylic acid ester group, the carboxylic acid ester group functions as an electron withdrawing group as Y ¹ or Y ² in the general formula (KB-1). There is also a possibility.

  In addition, when the repeating unit (by) corresponds to the repeating unit (b *) or the repeating unit (b ″) and has a partial structure represented by the general formula (KA-1), the general formula (KA) As for the partial structure represented by -1), it is more preferable that the polarity conversion group is a partial structure represented by -COO- in the structure represented by the general formula (KA-1).

  The repeating unit (by) can be a repeating unit having a partial structure represented by the general formula (KY-0).

In the general formula (KY-0),
R ₂ represents a chain or cyclic alkylene group, and when there are a plurality of R ₂ groups, they may be the same or different.
R ₃ represents a linear, branched or cyclic hydrocarbon group in which part or all of the hydrogen atoms on the constituent carbons are substituted with fluorine atoms.
R ₄ is a halogen atom, cyano group, hydroxy group, amide group, alkyl group, cycloalkyl group, alkoxy group, phenyl group, acyl group, alkoxycarbonyl group, or R—C (═O) — or R—C ( = O) A group represented by O- (R represents an alkyl group or a cycloalkyl group). If R ₄ is a plurality may be the same or different, and two or more R ₄ are attached, may form a ring.
X represents an alkylene group, an oxygen atom, or a sulfur atom.
Z and Za represent a single bond, an ether bond, an ester bond, an amide bond, a urethane bond or a urea bond, and when there are a plurality of them, they may be the same or different.
* Represents a bond to the main chain or side chain of the resin.
o is the number of substituents and represents an integer of 1 to 7.
m is the number of substituents and represents an integer of 0 to 7.
n represents the number of repetitions and represents an integer of 0 to 5.
The structure represented by —R ₂ —Z— is preferably a structure represented by — (CH ₂ ) ₁ —COO— (l represents an integer of 1 to 5).

The preferred carbon number range and specific examples of the chain or cyclic alkylene group as R ₂ are the same as those described for the chain alkylene group and cyclic alkylene group in Z ₂ of the general formula (bb).
The linear, branched or cyclic hydrocarbon group as R ₃ has preferably 1 to 30 carbon atoms, more preferably 1 to 20 carbon atoms, and preferably 3 carbon atoms when branched. -30, more preferably 3-20, and in the case of a ring, it is 6-20. Specific examples of R ₃ include specific examples of the alkyl group and cycloalkyl group as Z _ka1 described above.
Preferred carbon numbers and specific examples of the alkyl group and cycloalkyl group as R ₄ and R are the same as those described in the alkyl group and cycloalkyl group as Z _ka1 described above.
The acyl group as R ₄ is preferably one having 1 to 6 carbon atoms, and examples thereof include a formyl group, acetyl group, propionyl group, butyryl group, isobutyryl group, valeryl group, and pivaloyl group.
Examples of the alkyl moiety in the alkoxy group and alkoxycarbonyl group as R ₄ include a linear, branched or cyclic alkyl moiety, and the preferred carbon number of the alkyl moiety and specific examples thereof are those described above for Z _ka1. The same as those described in the alkyl group and cycloalkyl group.
Examples of the alkylene group as X include a chain or cyclic alkylene group, and preferred carbon numbers and specific examples thereof are the same as those described for the chain alkylene group and cyclic alkylene group as R ₂ .

  Moreover, the repeating unit which has a partial structure shown below as a specific structure of a repeating unit (by) is mentioned.

In general formulas (rf-1) and (rf-2),
X ′ represents an electron-withdrawing substituent, preferably a carbonyloxy group, an oxycarbonyl group, an alkylene group substituted with a fluorine atom, or a cycloalkylene group substituted with a fluorine atom.
A represents a single bond or a divalent linking group represented by -C (Rx) (Ry)-. Here, Rx and Ry are each independently a hydrogen atom, a fluorine atom, an alkyl group (preferably having 1 to 6 carbon atoms and optionally substituted with a fluorine atom or the like), or a cycloalkyl group (preferably a carbon atom). And may be substituted with a fluorine atom or the like. Rx and Ry are preferably a hydrogen atom, an alkyl group, or an alkyl group substituted with a fluorine atom.
X represents an electron withdrawing group, and specific examples thereof include the above-mentioned electron withdrawing groups as Y ¹ and Y ² , preferably a fluorinated alkyl group or a fluorinated cycloalkyl group. An aryl group substituted with a fluorine or fluorinated alkyl group, an aralkyl group substituted with a fluorine or fluorinated alkyl group, a cyano group, or a nitro group.
* Represents a bond to the main chain or side chain of the resin. That is, it represents a bond that is bonded to the main chain of the resin through a single bond or a linking group.
In addition, when X 'is a carbonyloxy group or an oxycarbonyl group, A is not a single bond.

When the polarity conversion group is decomposed by the action of an alkali developer and converted in polarity, the receding contact angle with water of the resin composition film after alkali development can be lowered. It is preferable from the viewpoint of suppressing development defects that the receding contact angle with water of the film after alkali development is lowered.
The receding contact angle with water of the resin composition film after alkali development is preferably 50 ° or less, more preferably 40 ° or less, and further preferably 35 ° at a temperature of 23 ± 3 ° C. and a humidity of 45 ± 5%. Hereinafter, it is most preferably 30 ° or less.
The receding contact angle is a contact angle measured when the contact line at the droplet-substrate interface recedes, and is useful for simulating the ease of movement of the droplet in a dynamic state. It is generally known. In simple terms, it can be defined as the contact angle when the droplet interface recedes when the droplet discharged from the needle tip is deposited on the substrate and then sucked into the needle again. It can be measured by using a contact angle measuring method generally called an expansion / contraction method.
The receding contact angle of the film after alkali development is a contact angle when the film shown below is measured by the expansion / contraction method described in the examples described later. That is, an organic antireflection film ARC29SR (manufactured by Nissan Chemical Co., Ltd.) is applied on a silicon wafer (8-inch diameter) and baked at 205 ° C. for 60 seconds. The composition is applied and baked at 120 ° C. for 60 seconds to form a film having a thickness of 120 nm. This contact angle is determined by the expansion / contraction method for a film obtained by developing this film with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsing with pure water, and spin drying.
The hydrolysis rate of the hydrophobic resin (B) with respect to the alkaline developer is preferably 0.001 nm / second or more, more preferably 0.01 nm / second or more, and preferably 0.1 nm / second or more. More preferred is 1 nm / second or more.
Here, the hydrolysis rate of the hydrophobic resin (B) with respect to the alkaline developer is 23.degree. C. with respect to TMAH (tetramethylammonium hydroxide aqueous solution) (2.38% by mass), and the resin film is formed only with the resin (B). This is the speed at which the film thickness decreases when the film is formed.

  The repeating unit (by) is more preferably a repeating unit having at least two or more polar conversion groups.

  When the repeating unit (by) has at least two polar conversion groups, the repeating unit (by) preferably has a group having a partial structure having two polar conversion groups represented by the following general formula (KY-1). Note that when the structure represented by the general formula (KY-1) does not have a bond, it is a group having a monovalent or higher valent group in which at least one arbitrary hydrogen atom in the structure is removed.

In general formula (KY-1),
R _ky1 and R _ky4 are each independently a hydrogen atom, halogen atom, alkyl group, cycloalkyl group, carbonyl group, carbonyloxy group, oxycarbonyl group, ether group, hydroxyl group, cyano group, amide group, or aryl group Represents. Alternatively, R _ky1 and R _ky4 may be bonded to the same atom to form a double bond. For example, R _ky1 and R _ky4 are bonded to the same oxygen atom to form a part of a carbonyl group (═O). May be formed.
R _ky2 and R _ky3 are each independently an electron withdrawing group, or R _ky1 and R _ky2 are linked to form a lactone ring and R _ky3 is an electron withdrawing group. As the lactone ring to be formed, the structures (KA-1-1) to (KA-1-17) are preferable. Examples of the electron withdrawing group include the same groups as those described above for Y ₁ and Y ₂ in the formula (KB-1), and preferably a halogen atom or the aforementioned —C (R _f1 ) (R _f2 ) —R _f3. A halo (cyclo) alkyl group or a haloaryl group represented by the formula: Preferably _{R ky3} halogen atom, or the _{-C (R f1)} (R f2) is represented by the halo (cyclo) alkyl groups or haloaryl groups _{-R f3,} lactone _{R ky2} is linked to _{R ky1} An electron withdrawing group that forms a ring or has no halogen atom.
R _ky1 , R _ky2 , and R _ky4 may be connected to each other to form a monocyclic or polycyclic structure.

Specific examples of R _ky1 and R _ky4 include the same groups as Z _ka1 in formula (KA-1).
As the lactone ring formed by linking R _ky1 and R _ky2 , the structures (KA-1-1) to (KA-1-17) are preferable. Examples of the electron withdrawing group include those similar to Y ₁ and Y ₂ in the formula (KB-1).

  The structure represented by the general formula (KY-1) is more preferably a structure represented by the following general formula (KY-2). Note that the structure represented by the general formula (KY-2) is a group having a monovalent or higher group obtained by removing at least one arbitrary hydrogen atom in the structure.

In formula (KY-2),
R _{ky6 to} R _ky10 are each independently a hydrogen atom, halogen atom, alkyl group, cycloalkyl group, carbonyl group, carbonyloxy group, oxycarbonyl group, ether group, hydroxyl group, cyano group, amide group, or aryl. Represents a group.
Two or more of R _{ky6 to} R _ky10 may be connected to each other to form a monocyclic or polycyclic structure.
R _ky5 represents an electron withdrawing group. Electron-withdrawing groups include the same as those in the _Y 1, _{Y 2,} preferably a halogen atom, or the _{-C (R f1)} halo represented by (R f2) _{-R f3} (cyclo ) An alkyl group or a haloaryl group.
Specific examples of R _{ky5 to} R _ky10 include the same groups as Z _ka1 in formula (KA-1).

  The structure represented by the formula (KY-2) is more preferably a partial structure represented by the following general formula (KY-3).

In formula (KY-3), Z _ka1 and nka have the same meanings as those in formula (KA-1). R _ky5 has the same _{meaning as} in formula (KY-2).
L _ky represents an alkylene group, an oxygen atom or a sulfur atom. _Examples of the alkylene group for L _ky include a methylene group and an ethylene group. L _ky is preferably an oxygen atom or a methylene group, and more preferably a methylene group.
The repeating unit (b) is not limited as long as it is a repeating unit obtained by polymerization such as addition polymerization, condensation polymerization or addition condensation, but is a repeating unit obtained by addition polymerization of a carbon-carbon double bond. It is preferable. Examples include acrylate-based repeating units (including those having substituents at the α-position and β-position), styrene-based repeating units (including those having substituents at the α-position and β-position), vinyl ether-based repeating units, norbornene-based Repeating units, repeating units of maleic acid derivatives (maleic anhydride and derivatives thereof, maleimides, etc.), acrylate repeating units, styrene repeating units, vinyl ether repeating units, norbornene repeating units Preferred are acrylate repeat units, vinyl ether repeat units, and norbornene repeat units, with acrylate repeat units being most preferred.

When the repeating unit (by) is a repeating unit having at least one of a fluorine atom and a silicon atom (that is, when the repeating unit (by) corresponds to the repeating unit (b ′) or (b ″)), the repeating unit (by) Examples of the partial structure having a fluorine atom include the same ones as mentioned in the repeating unit having at least one of the fluorine atom and the silicon atom, and preferably represented by the general formulas (F2) to (F4). In this case, the partial structure having a silicon atom in the repeating unit (by) has the same structure as that described in the repeating unit having at least one of the fluorine atom and the silicon atom. Preferably, groups represented by the general formulas (CS-1) to (CS-3) can be exemplified.
The content of the repeating unit (by) in the hydrophobic resin (B) is preferably from 10 to 100 mol%, more preferably from 20 to 99 mol%, still more preferably based on all repeating units in the resin (B). 30 to 97 mol%, most preferably 40 to 95 mol%.

Specific examples of the repeating unit (by) having a group capable of increasing the solubility in an alkali developer are shown below, but are not limited thereto. Moreover, what was mentioned as a specific example of the repeating unit (a3) of the said resin (A) can also be mentioned as a specific example of a repeating unit (by).
Ra represents a hydrogen atom, a fluorine atom, a methyl group or a trifluoromethyl group.

  In the hydrophobic resin (B), examples of the repeating unit (bz) having a group (z) that is decomposed by the action of an acid are the same as the repeating unit having an acid-decomposable group listed for the resin (A). .

  In the case where the repeating unit (bz) is a repeating unit having at least one of a fluorine atom and a silicon atom (that is, corresponding to the repeating unit (b ′) or (b ″)), the repeating unit (bz) Examples of the partial structure having a fluorine atom include the same ones as mentioned in the repeating unit having at least one of the fluorine atom and the silicon atom, and preferably represented by the general formulas (F2) to (F4). In this case, the partial structure having a silicon atom in the repeating unit (by) has the same structure as that described in the repeating unit having at least one of the fluorine atom and the silicon atom. Preferably, groups represented by the general formulas (CS-1) to (CS-3) can be exemplified.

  In the hydrophobic resin (B), the content of the repeating unit (bz) having a group (z) that is decomposed by the action of an acid is 1 to 80 mol% with respect to all the repeating units in the hydrophobic resin (B). Is preferable, more preferably 10 to 80 mol%, still more preferably 20 to 60 mol%.

Hereinabove, the repeating unit (b) having at least one group selected from the group consisting of the above (x) to (z) has been described, but the content of the repeating unit (b) in the resin (B) is as follows: 1-98 mol% is preferable with respect to all the repeating units in hydrophobic resin (B), More preferably, it is 3-98 mol%, More preferably, it is 5-97 mol%, Most preferably, it is 10-95 mol%.
The content of the repeating unit (b ′) is preferably 1 to 100 mol%, more preferably 3 to 99 mol%, still more preferably 5 to 97 mol%, most preferably based on all repeating units in the hydrophobic resin (B). Is 10-95 mol%.
The content of the repeating unit (b *) is preferably 1 to 90 mol%, more preferably 3 to 80 mol%, still more preferably 5 to 70 mol%, most preferably based on all repeating units in the hydrophobic resin (B). Is 10-60 mol%. The content of the repeating unit having at least one of a fluorine atom and a silicon atom used together with the repeating unit (b *) is preferably 10 to 99 mol% with respect to all the repeating units in the hydrophobic resin (B). Preferably it is 20-97 mol%, More preferably, it is 30-95 mol%, Most preferably, it is 40-90 mol%.
The content of the repeating unit (b ″) is preferably 1 to 100 mol%, more preferably 3 to 99 mol%, still more preferably 5 to 97 mol%, and most preferably based on all repeating units in the hydrophobic resin (B). Is 10-95 mol%.

  The hydrophobic resin (B) may further have a repeating unit represented by the following general formula (CIII).

In general formula (CIII):
R _c31 represents a hydrogen atom, an alkyl group (which may be substituted with a fluorine atom or the like), a cyano group, or a —CH ₂ —O—Rac ₂ group. In the formula, Rac ₂ represents a hydrogen atom, an alkyl group or an acyl group. R _c31 is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, particularly preferably a hydrogen atom or a methyl group.
R _c32 represents a group having an alkyl group, a cycloalkyl group, an alkenyl group, a cycloalkenyl group or an aryl group. These groups may be substituted with a fluorine atom, a group containing a silicon atom, or the like.
L _c3 represents a single bond or a divalent linking group.

In general formula (CIII), the alkyl group represented by R _c32 is preferably a linear or branched alkyl group having 3 to 20 carbon atoms.
The cycloalkyl group is preferably a cycloalkyl group having 3 to 20 carbon atoms.
The alkenyl group is preferably an alkenyl group having 3 to 20 carbon atoms.
The cycloalkenyl group is preferably a cycloalkenyl group having 3 to 20 carbon atoms.
The aryl group is preferably a phenyl group or naphthyl group having 6 to 20 carbon atoms, and these may have a substituent.
R _c32 is preferably an unsubstituted alkyl group or an alkyl group substituted with a fluorine atom.
The divalent linking group of L _c3 is preferably an alkylene group (preferably having 1 to 5 carbon atoms), an oxy group, a phenylene group, or an ester bond (a group represented by —COO—).

  It is also preferable that the hydrophobic resin (B) further has a repeating unit represented by the following general formula (BII-AB).

In the formula (BII-AB),
R _c11 ′ and R _c12 ′ each independently represents a hydrogen atom, a cyano group, a halogen atom or an alkyl group.
Zc ′ represents an atomic group for forming an alicyclic structure containing two bonded carbon atoms (C—C).

  When each group in the repeating unit represented by the general formula (III) or (BII-AB) is substituted with a group containing a fluorine atom or a silicon atom, the repeating unit includes at least the fluorine atom and the silicon atom. It corresponds also to the repeating unit which has either.

Specific examples of the repeating unit represented by the general formulas (III) and (BII-AB) are shown below, but the present invention is not limited thereto. In the formula, Ra represents H, CH ₃ , CH ₂ OH, CF ₃ or CN. Note that the repeating unit in the case where Ra is CF ₃ also corresponds to the repeating unit having at least one of the fluorine atom and the silicon atom.

  As with the resin (A), the hydrophobic resin (B) is naturally free from impurities such as metals, and the residual monomer or oligomer component is preferably 0 to 10% by mass, more preferably 0-5 mass% and 0-1 mass% are still more preferable. Thereby, a resist composition having no change over time such as foreign matter in liquid or sensitivity can be obtained. The molecular weight distribution (Mw / Mn, also referred to as dispersity) is preferably in the range of 1 to 3, more preferably 1 to 2, and still more preferably, in terms of resolution, resist shape, resist pattern side walls, roughness, and the like. It is in the range of 1 to 1.8, most preferably 1 to 1.5.

As the hydrophobic resin (B), various commercially available products can be used, and the hydrophobic resin (B) can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and heating is performed, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable.
The reaction solvent, the polymerization initiator, the reaction conditions (temperature, concentration, etc.) and the purification method after the reaction are the same as those described for the resin (A).

  Specific examples of the hydrophobic resin (B) are shown below. The table below shows the molar ratio of repeating units in each resin (corresponding to each repeating unit in order from the left), weight average molecular weight, and degree of dispersion.

  The actinic ray-sensitive or radiation-sensitive resin composition of the present invention contains an actinic ray-sensitive or radiation-sensitive resin by containing a hydrophobic resin (B) containing at least one of a fluorine atom and a silicon atom. When the hydrophobic resin (B) is unevenly distributed in the surface layer of the film formed from the composition and the immersion medium is water, the receding contact angle of the film surface with respect to water is improved, and the immersion liquid followability is improved. Can do.

  After baking the coating film comprising the actinic ray-sensitive or radiation-sensitive resin composition of the present invention and before exposure, the receding contact angle of the film is the temperature at the time of exposure, usually room temperature 23 ± 3 ° C., humidity 45 ± 5%. 60 ° to 90 °, more preferably 65 ° or more, still more preferably 70 ° or more, and particularly preferably 75 ° or more.

The hydrophobic resin (B) is unevenly distributed at the interface as described above. Unlike the surfactant, the hydrophobic resin (B) does not necessarily have a hydrophilic group in the molecule, and the polar / nonpolar substance is mixed uniformly. It does not have to contribute to
In the immersion exposure process, the immersion head needs to move on the wafer following the movement of the exposure head to scan the wafer at high speed to form the exposure pattern. In this case, the contact angle of the immersion liquid with respect to the resist film is important, and the resist is required to follow the high-speed scanning of the exposure head without remaining droplets.
Hydrophobic resin (B) is hydrophobic, so development residue (scum) and BLOB defects are likely to deteriorate after alkali development, but it has a linear type by having three or more polymer chains via at least one branch. Since the alkali dissolution rate is improved as compared with the resin, the development residue (scum) and BLO defect performance are improved.

When the hydrophobic resin (B) has a fluorine atom, the fluorine atom content is preferably 5 to 80% by mass and preferably 10 to 80% by mass with respect to the average molecular weight of the hydrophobic resin (B). It is more preferable. Moreover, it is preferable that the repeating unit containing a fluorine atom is 10-100 mol% with respect to all the repeating units in hydrophobic resin (B), and it is more preferable that it is 30-100 mol%.
When the hydrophobic resin (B) has a silicon atom, the silicon atom content is preferably 2 to 50% by mass and preferably 2 to 30% by mass with respect to the average molecular weight of the hydrophobic resin (B). It is more preferable. Moreover, it is preferable that it is 10-90 mol% with respect to all the repeating units of hydrophobic resin (B), and, as for the repeating unit containing a silicon atom, it is more preferable that it is 20-80 mol%.

  The weight average molecular weight of the hydrophobic resin (B) is preferably 1,000 to 100,000, more preferably 2,000 to 50,000, and still more preferably 3,000 to 35,000. Here, the weight average molecular weight of the resin indicates a molecular weight in terms of polystyrene measured by GPC (carrier: tetrahydrofuran (THF)).

The content of the resin (B) in the actinic ray-sensitive or radiation-sensitive resin composition can be appropriately adjusted and used so that the receding contact angle of the actinic ray- or radiation-sensitive resin film falls within the above range. It is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, and still more preferably 0.1 to 10% by mass based on the total solid content of the light-sensitive or radiation-sensitive resin composition. %, Particularly preferably 0.5 to 8% by mass.
Resin (B) can be used individually by 1 type or in combination of 2 or more types.

<Basic compound>
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention preferably contains a basic compound in order to reduce changes in performance over time from exposure to heating.
Preferred examples of the basic compound include compounds having structures represented by the following formulas (A) to (E).

In general formulas (A) and (E),
R ²⁰⁰ , R ²⁰¹ and R ²⁰² may be the same or different and are a hydrogen atom, an alkyl group (preferably having 1 to 20 carbon atoms), a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (having a carbon number). 6-20), wherein R ²⁰¹ and R ²⁰² may combine with each other to form a ring.
R ²⁰³ , R ²⁰⁴ , R ²⁰⁵ and R ²⁰⁶ may be the same or different and each represents an alkyl group having 1 to 20 carbon atoms.
About the said alkyl group, as an alkyl group which has a substituent, a C1-C20 aminoalkyl group, a C1-C20 hydroxyalkyl group, or a C1-C20 cyanoalkyl group is preferable.
The alkyl groups in the general formulas (A) and (E) are more preferably unsubstituted.

  Preferred compounds include guanidine, aminopyrrolidine, pyrazole, pyrazoline, piperazine, aminomorpholine, aminoalkylmorpholine, piperidine and the like, and more preferred compounds include imidazole structure, diazabicyclo structure, onium hydroxide structure, onium carboxylate Examples thereof include a compound having a structure, a trialkylamine structure, an aniline structure or a pyridine structure, an alkylamine derivative having a hydroxyl group and / or an ether bond, and an aniline derivative having a hydroxyl group and / or an ether bond.

  Examples of the compound having an imidazole structure include imidazole, 2,4,5-triphenylimidazole, benzimidazole, and 2-phenylbenzimidazole. Examples of the compound having a diazabicyclo structure include 1,4-diazabicyclo [2,2,2] octane, 1,5-diazabicyclo [4,3,0] non-5-ene, and 1,8-diazabicyclo [5,4,0. ] Undec-7-ene etc. are mentioned. Examples of the compound having an onium hydroxide structure include tetrabutylammonium hydroxide, triarylsulfonium hydroxide, phenacylsulfonium hydroxide, sulfonium hydroxide having a 2-oxoalkyl group, specifically, triphenylsulfonium hydroxide, tris ( and t-butylphenyl) sulfonium hydroxide, bis (t-butylphenyl) iodonium hydroxide, phenacylthiophenium hydroxide, 2-oxopropylthiophenium hydroxide, and the like. As the compound having an onium carboxylate structure, an anion portion of the compound having an onium hydroxide structure is converted to a carboxylate, and examples thereof include acetate, adamantane-1-carboxylate, and perfluoroalkylcarboxylate. Examples of the compound having a trialkylamine structure include tri (n-butyl) amine and tri (n-octyl) amine. Examples of the aniline compound include 2,6-diisopropylaniline, N, N-dimethylaniline, N, N-dibutylaniline, N, N-dihexylaniline and the like. Examples of the alkylamine derivative having a hydroxyl group and / or an ether bond include ethanolamine, diethanolamine, triethanolamine, N-phenyldiethanolamine, and tris (methoxyethoxyethyl) amine. Examples of aniline derivatives having a hydroxyl group and / or an ether bond include N, N-bis (hydroxyethyl) aniline.

Preferred examples of the basic compound further include an amine compound having a phenoxy group, an ammonium salt compound having a phenoxy group, an amine compound having a sulfonic acid ester group, and an ammonium salt compound having a sulfonic acid ester group.
As the amine compound, a primary, secondary or tertiary amine compound can be used, and an amine compound in which at least one alkyl group is bonded to a nitrogen atom is preferable. The amine compound is more preferably a tertiary amine compound. As long as at least one alkyl group (preferably having 1 to 20 carbon atoms) is bonded to a nitrogen atom, the amine compound has an cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (preferably having 3 to 20 carbon atoms). Preferably C6-C12) may be bonded to a nitrogen atom. The amine compound preferably has an oxygen atom in the alkyl chain and an oxyalkylene group is formed. The number of oxyalkylene groups is 1 or more, preferably 3 to 9, more preferably 4 to 6 in the molecule. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

As the ammonium salt compound, a primary, secondary, tertiary, or quaternary ammonium salt compound can be used, and an ammonium salt compound in which at least one alkyl group is bonded to a nitrogen atom is preferable. As long as at least one alkyl group (preferably having 1 to 20 carbon atoms) is bonded to a nitrogen atom, the ammonium salt compound has a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group in addition to the alkyl group. (Preferably having 6 to 12 carbon atoms) may be bonded to a nitrogen atom. The ammonium salt compound preferably has an oxygen atom in the alkyl chain and an oxyalkylene group is formed. The number of oxyalkylene groups is 1 or more, preferably 3 to 9, more preferably 4 to 6 in the molecule. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.
Examples of the anion of the ammonium salt compound include halogen atoms, sulfonates, borates, and phosphates. Among them, halogen atoms and sulfonates are preferable. As the halogen atom, chloride, bromide, and iodide are particularly preferable. As the sulfonate, an organic sulfonate having 1 to 20 carbon atoms is particularly preferable. Examples of the organic sulfonate include alkyl sulfonates having 1 to 20 carbon atoms and aryl sulfonates. The alkyl group of the alkyl sulfonate may have a substituent, and examples of the substituent include fluorine, chlorine, bromine, alkoxy groups, acyl groups, and aryl groups. Specific examples of the alkyl sulfonate include methane sulfonate, ethane sulfonate, butane sulfonate, hexane sulfonate, octane sulfonate, benzyl sulfonate, trifluoromethane sulfonate, pentafluoroethane sulfonate, and nonafluorobutane sulfonate. Examples of the aryl group of the aryl sulfonate include a benzene ring, a naphthalene ring, and an anthracene ring. The benzene ring, naphthalene ring and anthracene ring may have a substituent, and the substituent is preferably a linear or branched alkyl group having 1 to 6 carbon atoms or a cycloalkyl group having 3 to 6 carbon atoms. Specific examples of the linear or branched alkyl group and cycloalkyl group include methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, t-butyl, n-hexyl, cyclohexyl and the like. Examples of the other substituent include an alkoxy group having 1 to 6 carbon atoms, a halogen atom, cyano, nitro, an acyl group, and an acyloxy group.

The amine compound having a phenoxy group and the ammonium salt compound having a phenoxy group are those having a phenoxy group at the terminal opposite to the nitrogen atom of the alkyl group of the amine compound or ammonium salt compound. The phenoxy group may have a substituent. Examples of the substituent of the phenoxy group include an alkyl group, an alkoxy group, a halogen atom, a cyano group, a nitro group, a carboxyl group, a carboxylic acid ester group, a sulfonic acid ester group, an aryl group, an aralkyl group, an acyloxy group, and an aryloxy group. Etc. The substitution position of the substituent may be any of the 2-6 positions. The number of substituents may be any in the range of 1 to 5.
It is preferable to have at least one oxyalkylene group between the phenoxy group and the nitrogen atom. The number of oxyalkylene groups is 1 or more, preferably 3 to 9, more preferably 4 to 6 in the molecule. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

In the amine compound having a sulfonic acid ester group and the ammonium salt compound having a sulfonic acid ester group, the sulfonic acid ester group may be any of alkyl sulfonic acid ester, cycloalkyl group sulfonic acid ester, and aryl sulfonic acid ester. In the case of an alkyl sulfonate ester, the alkyl group has 1 to 20 carbon atoms, in the case of a cycloalkyl sulfonate ester, the cycloalkyl group has 3 to 20 carbon atoms, and in the case of an aryl sulfonate ester, the aryl group has 6 carbon atoms. ~ 12 are preferred. Alkyl sulfonic acid ester, cycloalkyl sulfonic acid ester, and aryl sulfonic acid ester may have a substituent. Examples of the substituent include a halogen atom, a cyano group, a nitro group, a carboxyl group, a carboxylic acid ester group, and a sulfonic acid. An ester group is preferred.
It is preferable to have at least one oxyalkylene group between the sulfonate group and the nitrogen atom. The number of oxyalkylene groups is 1 or more, preferably 3 to 9, more preferably 4 to 6 in the molecule. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

  The following compounds are also preferable as the basic compound.

These basic compounds are used alone or in combination of two or more.
The composition of the present invention may or may not contain a basic compound, but when it is contained, the content of the basic compound is based on the solid content of the actinic ray-sensitive or radiation-sensitive resin composition. Usually, it is 0.001-10 mass%, Preferably it is 0.01-5 mass%.

  The use ratio of the acid generator (including the combined acid generator) and the basic compound in the composition is preferably acid generator / basic compound (molar ratio) = 2.5 to 300. In other words, the molar ratio is preferably 2.5 or more from the viewpoint of sensitivity and resolution, and is preferably 300 or less from the viewpoint of suppressing the reduction in resolution due to the thickening of the resist pattern over time until post-exposure heat treatment. The acid generator / basic compound (molar ratio) is more preferably 5.0 to 200, still more preferably 7.0 to 150.

These basic compounds are preferably used in a molar ratio with respect to the following low molecular compound (D): low molecular compound (D) / basic compound = 100/0 to 10/90, and 100/0 to 30 / 70 is more preferable, and it is particularly preferable to use 100/0 to 50/50.
In addition, the basic compound here does not include a low molecular compound having a group capable of leaving by the action of an acid (D) when it is also a basic compound.

<Low molecular compound having a group capable of leaving by the action of an acid>
The composition of the present invention may contain a low molecular compound having a group capable of leaving by the action of an acid (hereinafter also referred to as “low molecular compound (D)” or “compound (D)”). The group capable of leaving by the action of an acid is not particularly limited, but is preferably an acetal group, a carbonate group, a carbamate group, a tertiary ester group, a tertiary hydroxyl group, or a hemiaminal ether group, and a carbamate group or a hemiaminal ether group. It is particularly preferred.
The molecular weight range of the low molecular weight compound having a group capable of leaving by the action of an acid is preferably 100 to 1000, more preferably 100 to 700, and particularly preferably 100 to 500.
Examples of the low molecular weight compound (D) that can be suitably used in the present invention include compounds exemplified in paragraph 0175 of JP-A-2009-199021.
<Solvent>
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention preferably contains a solvent.
Solvents that can be used when preparing the actinic ray-sensitive or radiation-sensitive resin composition by dissolving the above components include, for example, alkylene glycol monoalkyl ether carboxylate, alkylene glycol monoalkyl ether, alkyl lactate Esters, alkyl alkoxypropionates, cyclic lactones (preferably having 4 to 10 carbon atoms), monoketone compounds which may contain rings (preferably having 4 to 10 carbon atoms), alkylene carbonates, alkyl alkoxyacetates, alkyl pyruvates, etc. Mention may be made of organic solvents.

Examples of the alkylene glycol monoalkyl ether carboxylate include propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate, propylene glycol monobutyl ether acetate, propylene glycol monomethyl ether propionate, propylene glycol monoethyl Preferred examples include ether propionate, ethylene glycol monomethyl ether acetate, and ethylene glycol monoethyl ether acetate.
Preferred examples of the alkylene glycol monoalkyl ether include propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, ethylene glycol monomethyl ether, and ethylene glycol monoethyl ether.

Preferred examples of the alkyl lactate include methyl lactate, ethyl lactate, propyl lactate and butyl lactate.
Preferable examples of the alkyl alkoxypropionate include ethyl 3-ethoxypropionate, methyl 3-methoxypropionate, methyl 3-ethoxypropionate, and ethyl 3-methoxypropionate.

  Examples of the cyclic lactone include β-propiolactone, β-butyrolactone, γ-butyrolactone, α-methyl-γ-butyrolactone, β-methyl-γ-butyrolactone, γ-valerolactone, γ-caprolactone, and γ-octano. Preferred are iclactone and α-hydroxy-γ-butyrolactone.

  Examples of the monoketone compound which may contain a ring include 2-butanone, 3-methylbutanone, pinacolone, 2-pentanone, 3-pentanone, 3-methyl-2-pentanone, 4-methyl-2-pentanone, 2 -Methyl-3-pentanone, 4,4-dimethyl-2-pentanone, 2,4-dimethyl-3-pentanone, 2,2,4,4-tetramethyl-3-pentanone, 2-hexanone, 3-hexanone, 5-methyl-3-hexanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-methyl-3-heptanone, 5-methyl-3-heptanone, 2,6-dimethyl-4-heptanone, 2-octanone, 3-octanone, 2-nonanone, 3-nonanone, 5-nonanone, 2-decanone, 3-decanone, 4-decanone, 5-hexen-2-one 3-penten-2-one, cyclopentanone, 2-methylcyclopentanone, 3-methylcyclopentanone, 2,2-dimethylcyclopentanone, 2,4,4-trimethylcyclopentanone, cyclohexanone, 3- Methylcyclohexanone, 4-methylcyclohexanone, 4-ethylcyclohexanone, 2,2-dimethylcyclohexanone, 2,6-dimethylcyclohexanone, 2,2,6-trimethylcyclohexanone, cycloheptanone, 2-methylcycloheptanone, 3-methyl Preferred is cycloheptanone.

Preferred examples of the alkylene carbonate include propylene carbonate, vinylene carbonate, ethylene carbonate, and butylene carbonate.
Examples of the alkyl alkoxyacetate include 2-methoxyethyl acetate, 2-ethoxyethyl acetate, 2- (2-ethoxyethoxy) ethyl acetate, 3-methoxy-3-methylbutyl acetate, and 1-methoxy-acetate. 2-propyl is preferred.
Preferred examples of the alkyl pyruvate include methyl pyruvate, ethyl pyruvate, and propyl pyruvate.
As a solvent which can be preferably used, a solvent having a boiling point of 130 ° C. or higher under normal temperature and normal pressure can be mentioned. Specifically, cyclopentanone, γ-butyrolactone, cyclohexanone, ethyl lactate, ethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate, ethyl 3-ethoxypropionate, ethyl pyruvate, 2-ethoxyethyl acetate, acetic acid -2- (2-ethoxyethoxy) ethyl and propylene carbonate are mentioned.
In the present invention, the above solvents may be used alone or in combination of two or more.

In this invention, you may use the mixed solvent which mixed the solvent which contains a hydroxyl group in a structure, and the solvent which does not contain a hydroxyl group as an organic solvent.
As the solvent containing a hydroxyl group and the solvent not containing a hydroxyl group, the above-mentioned exemplary compounds can be selected as appropriate, but as the solvent containing a hydroxyl group, alkylene glycol monoalkyl ether, alkyl lactate, etc. are preferable, propylene glycol monomethyl ether, More preferred is ethyl lactate. Further, as the solvent not containing a hydroxyl group, alkylene glycol monoalkyl ether acetate, alkyl alkoxypropionate, monoketone compound which may contain a ring, cyclic lactone, alkyl acetate and the like are preferable, and among these, propylene glycol monomethyl ether Acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone and butyl acetate are particularly preferred, and propylene glycol monomethyl ether acetate, ethyl ethoxypropionate and 2-heptanone are most preferred.
The mixing ratio (mass) of the solvent containing a hydroxyl group and the solvent not containing a hydroxyl group is 1/99 to 99/1, preferably 10/90 to 90/10, more preferably 20/80 to 60/40. . A mixed solvent containing 50% by mass or more of a solvent not containing a hydroxyl group is particularly preferred from the viewpoint of coating uniformity.

The solvent is preferably a mixed solvent of two or more containing propylene glycol monomethyl ether acetate.
<Surfactant>
The composition of the present invention may or may not further contain a surfactant. When it contains, it contains either fluorine-based and / or silicon-based surfactant (fluorine-based surfactant, silicon-based surfactant, surfactant having both fluorine atom and silicon atom), or two or more kinds It is preferable to do.

When the actinic ray-sensitive or radiation-sensitive resin composition of the present invention contains the above-mentioned surfactant, adhesion and development defects with good sensitivity and resolution when using an exposure light source of 250 nm or less, particularly 220 nm or less. It is possible to provide a resist pattern with less.
Examples of the fluorine-based and / or silicon-based surfactant include surfactants described in [0276] of US Patent Application Publication No. 2008/0248425. For example, F-top EF301, EF303, (Shin-Akita Kasei Co., Ltd.) )), FLORARD FC430, 431, 4430 (manufactured by Sumitomo 3M Co., Ltd.), Megafac F171, F173, F176, F189, F113, F110, F177, F120, R08 (manufactured by Dainippon Ink & Chemicals, Inc.), Surflon S-382, SC101, 102, 103, 104, 105, 106 (manufactured by Asahi Glass Co., Ltd.), Troisol S-366 (manufactured by Troy Chemical Co., Ltd.), GF-300, GF-150 (Toagosei Chemical Co., Ltd.) ), Surflon S-393 (Seimi Chemical Co., Ltd.), F-top EF121, E 122A, EF122B, RF122C, EF125M, EF135M, EF351, EF352, EF801, EF802, EF601 (manufactured by Gemco), PF636, PF656, PF6320, PF6520 (manufactured by OMNOVA), FTX-204G, 230G, 218G, 218G 204D, 208D, 212D, 218D, 222D (manufactured by Neos Co., Ltd.) and the like. Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) can also be used as a silicon-based surfactant.

In addition to the known surfactants described above, the surfactant is derived from a fluoroaliphatic compound produced by a telomerization method (also called telomer method) or an oligomerization method (also called oligomer method). A surfactant using a polymer having a fluoroaliphatic group can be used. The fluoroaliphatic compound can be synthesized by the method described in JP-A-2002-90991.
As the polymer having a fluoroaliphatic group, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate and / or (poly (oxyalkylene)) methacrylate is preferable and distributed irregularly. Or may be block copolymerized. Examples of the poly (oxyalkylene) group include a poly (oxyethylene) group, a poly (oxypropylene) group, a poly (oxybutylene) group, and the like, and a poly (oxyethylene, oxypropylene, and oxyethylene group). A unit having different chain lengths in the same chain length, such as a block link) or poly (block link of oxyethylene and oxypropylene) may be used. Furthermore, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate (or methacrylate) is not only a binary copolymer but also a monomer having two or more different fluoroaliphatic groups, Further, it may be a ternary or higher copolymer obtained by simultaneously copolymerizing two or more different (poly (oxyalkylene)) acrylates (or methacrylates).

For example, as a commercially available surfactant, Megafac F178, F-470, F-473, F-475, F-476, F-472 (manufactured by Dainippon Ink & Chemicals, Inc.), C ₆ F ₁₃ group Copolymer of acrylate (or methacrylate) and (poly (oxyalkylene)) acrylate (or methacrylate), acrylate (or methacrylate) and (poly (oxyethylene)) acrylate (or methacrylate) having a C ₃ F ₇ group And a copolymer of (poly (oxypropylene)) acrylate (or methacrylate).

  In the present invention, surfactants other than the fluorine-based and / or silicon-based surfactants described in [0280] of US Patent Application Publication No. 2008/0248425 may also be used.

These surfactants may be used alone or in several combinations.
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention may or may not contain a surfactant, but when it is contained, the amount of surfactant used is actinic ray-sensitive or Preferably it is 0.0001-2 mass% with respect to the total solid content (total quantity except a solvent) of a radiation sensitive resin composition, More preferably, it is 0.0003-2 mass%, Most preferably, it is 0.0005-1 mass. %.
On the other hand, it is also preferable that the addition amount of the surfactant is 10 ppm or less or not contained. This increases the uneven distribution of the surface of the hydrophobic resin, whereby the resist film surface can be made more hydrophobic, and the water followability during immersion exposure can be improved.
<Carboxylic acid onium salt>
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention may contain an onium carboxylate. As the carboxylic acid onium salt, an iodonium salt and a sulfonium salt are preferable. As the anion moiety, a linear, branched, monocyclic or polycyclic alkylcarboxylic acid anion having 1 to 30 carbon atoms is preferable. More preferably, an anion of a carboxylic acid in which some or all of these alkyl groups are fluorine-substituted is preferable. The alkyl chain may contain an oxygen atom. This ensures transparency with respect to light of 220 nm or less, improves sensitivity and resolution, and improves density dependency and exposure margin.

  Fluorine-substituted carboxylic acid anions include fluoroacetic acid, difluoroacetic acid, trifluoroacetic acid, pentafluoropropionic acid, heptafluorobutyric acid, nonafluoropentanoic acid, perfluorododecanoic acid, perfluorotridecanoic acid, perfluorocyclohexanecarboxylic acid, 2 , 2-bistrifluoromethylpropionic acid anion and the like.

  The content of the carboxylic acid onium salt in the composition is generally 0.1 to 20% by mass, preferably 0.5 to 10% by mass, more preferably 1 to 7% by mass, based on the total solid content of the composition. %.

<Dissolution-inhibiting compound having a molecular weight of 3000 or less, which is decomposed by the action of an acid to increase the solubility in an alkaline developer>
As a dissolution inhibiting compound having a molecular weight of 3000 or less (hereinafter also referred to as “dissolution inhibiting compound”), which is decomposed by the action of an acid to increase the solubility in an alkaline developer, the permeability at 220 nm or less is not lowered. An alicyclic or aliphatic compound containing an acid-decomposable group is preferred, such as a cholic acid derivative containing an acid-decomposable group described in Proceeding of SPIE, 2724, 355 (1996). Examples of the acid-decomposable group and alicyclic structure are the same as those described above for the resin (A).

When the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is exposed with a KrF excimer laser or irradiated with an electron beam, the phenolic hydroxyl group of the phenol compound is an acid-decomposable group as a dissolution inhibiting compound. Those containing a structure substituted with are preferred. The phenol compound preferably contains 1 to 9 phenol skeletons, more preferably 2 to 6 phenol skeletons.
The addition amount of the dissolution inhibiting compound is preferably 3 to 50% by mass, more preferably 5 to 40% by mass, based on the solid content of the positive resist composition.
Specific examples of the dissolution inhibiting compound are shown below, but the present invention is not limited thereto.

<Other additives>
In the actinic ray-sensitive or radiation-sensitive resin composition of the present invention, a compound (for example, molecular weight) that further promotes solubility in dyes, plasticizers, photosensitizers, light absorbers, and developers as necessary. 1000 or less phenolic compounds, alicyclic or aliphatic compounds having a carboxyl group) and the like can be contained.

Such phenol compounds having a molecular weight of 1000 or less are described in, for example, JP-A-4-122938, JP-A-2-28531, US Pat. No. 4,916,210, European Patent 219294, and the like. It can be easily synthesized by those skilled in the art with reference to the above method.
Specific examples of alicyclic or aliphatic compounds having a carboxyl group include carboxylic acid derivatives having a steroid structure such as cholic acid, deoxycholic acid, lithocholic acid, adamantane carboxylic acid derivatives, adamantane dicarboxylic acid, cyclohexane carboxylic acid, cyclohexane Examples thereof include, but are not limited to, dicarboxylic acids.
<Pattern formation method>
The pattern forming method of the present invention includes steps of exposing and developing a resist film.
The resist film is formed from the actinic ray-sensitive or radiation-sensitive resin composition of the present invention described above, and more specifically, is preferably formed on a substrate. In the pattern forming method of the present invention, the step of forming a film of a resist composition on the substrate, the step of exposing the film, and the developing step can be performed by generally known methods.
The actinic ray-sensitive or radiation-sensitive resin composition of the present invention is preferably used at a film thickness of 30 to 250 nm, more preferably at a film thickness of 30 to 200 nm, from the viewpoint of improving resolution. preferable. By setting the solid content concentration in the actinic ray-sensitive or radiation-sensitive resin composition to an appropriate range to have an appropriate viscosity, and improving the coating property and film forming property, such a film thickness is obtained. Can do.
The total solid concentration in the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is generally 1 to 10% by mass, more preferably 1 to 8.0% by mass, and still more preferably 1.0 to 6.0% by mass.

The actinic ray-sensitive or radiation-sensitive resin composition of the present invention is prepared by dissolving the above-described components in a predetermined organic solvent, preferably the mixed solvent, filtered, and applied onto a predetermined support as follows. And use. The pore size of the filter used for filter filtration is preferably 0.1 microns or less, more preferably 0.05 microns or less, and even more preferably 0.03 microns or less made of polytetrafluoroethylene, polyethylene, or nylon.
Note that a plurality of types of filters may be connected in series or in parallel. The composition may be filtered multiple times. Furthermore, you may perform a deaeration process etc. with respect to a composition before and after filter filtration.

For example, the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is appropriately applied to a spinner, coater or the like on a substrate (eg, silicon / silicon dioxide coating) used for manufacturing a precision integrated circuit device. By applying and drying, a resist film can be formed.
The resist film is irradiated with actinic rays or radiation through a predetermined mask, preferably baked (heated), developed and rinsed. Thereby, a good pattern can be obtained.
It is also preferable to include a preheating step (PB; Prebake) after the film formation and before the exposure step.
It is also preferable to include a post-exposure heating step (PEB; Post Exposure Bake) after the exposure step and before the development step.
The heating temperature is preferably 70 to 120 ° C., more preferably 80 to 110 ° C. for both PB and PEB.
The heating time is preferably 30 to 300 seconds, more preferably 30 to 180 seconds, and still more preferably 30 to 90 seconds.
Heating can be performed by means provided in a normal exposure / developing machine, and may be performed using a hot plate or the like.
The reaction of the exposed part is promoted by baking, and the sensitivity and pattern profile are improved.

Examples of the actinic ray or radiation include infrared light, visible light, ultraviolet light, far ultraviolet light, extreme ultraviolet light, X-ray, electron beam, etc., preferably 250 nm or less, more preferably 220 nm or less, particularly Preferably, far ultraviolet light having a wavelength of 1 to 200 nm, specifically, KrF excimer laser (248 nm), ArF excimer laser (193 nm), F ₂ excimer laser (157 nm), X-ray, EUV (13 nm), electron beam, etc. ArF excimer laser, F ₂ excimer laser, EUV (13 nm), and electron beam are preferable.

Before forming the resist film, an antireflection film may be coated on the substrate in advance.
As the antireflection film, any of an inorganic film type such as titanium, titanium dioxide, titanium nitride, chromium oxide, carbon, and amorphous silicon, and an organic film type made of a light absorber and a polymer material can be used. In addition, as the organic antireflection film, commercially available organic antireflection films such as DUV30 series, DUV-40 series manufactured by Brewer Science, AR-2, AR-3, AR-5 manufactured by Shipley, etc. may be used. it can.

As the alkaline developer in the development step, a quaternary ammonium salt typified by tetramethylammonium hydroxide is usually used. In addition, inorganic alkali, primary amine, secondary amine, tertiary amine, alcohol amine are also used. An aqueous alkali solution such as a cyclic amine can also be used.
Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline developer.
The alkali concentration of the alkali developer is usually from 0.1 to 20% by mass.
The pH of the alkali developer is usually from 10.0 to 15.0.
Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline aqueous solution.
As the rinsing liquid, pure water can be used, and an appropriate amount of a surfactant can be added.
As a developing method, for example, a method in which a substrate is immersed in a tank filled with a developer for a certain period of time (dip method), a method in which the developer is raised on the surface of the substrate by surface tension and is left stationary for a certain time (paddle) Method), a method of spraying the developer on the substrate surface (spray method), a method of continuously discharging the developer while scanning the developer discharge nozzle on the substrate rotating at a constant speed (dynamic dispensing method) Etc. can be applied.

In the rinsing step, the developed wafer is cleaned using a rinsing liquid. The cleaning method is not particularly limited. For example, a method of continuing to discharge the rinse liquid onto the substrate rotating at a constant speed (rotary coating method), or immersing the substrate in a tank filled with the rinse liquid for a certain period of time. A method (dip method), a method of spraying a rinsing liquid on the substrate surface (spray method), and the like can be applied. Among them, a cleaning treatment is performed by a spin coating method, and after cleaning, the substrate is rotated at a speed of 2000 rpm to 4000 rpm. It is preferable to rotate and remove the rinse liquid from the substrate. It is also preferable to include a heating step (Post Bake) after the rinsing step. The developing solution and the rinsing solution remaining between the patterns and inside the patterns are removed by baking. The heating step after the rinsing step is usually 40 to 160 ° C., preferably 70 to 95 ° C., and usually 10 seconds to 3 minutes, preferably 30 seconds to 90 seconds.
Moreover, the process which removes the developing solution or rinse liquid adhering on a pattern with a supercritical fluid can be performed after a image development process or a rinse process.

Exposure (immersion exposure) may be performed by filling a liquid (immersion medium) having a higher refractive index than air between the film and the lens during irradiation with actinic rays or radiation. Thereby, resolution can be improved. The immersion medium used is preferably water. Water is also suitable in terms of a small temperature coefficient of refractive index, ease of availability, and ease of handling.
A medium having a refractive index of 1.5 or more can also be used in that the refractive index can be improved. This medium may be an aqueous solution or an organic solvent.

  When water is used as the immersion liquid, an additive for the purpose of improving the refractive index may be added in a small proportion. Examples of additives are detailed in Chapter 12 of CMC Publishing "Processes and Materials for Immersion Lithography". On the other hand, the presence of impurities that are opaque to 193 nm light and impurities whose refractive index is significantly different from that of water causes distortion of the optical image projected on the film, and therefore, distilled water is preferred as the water to be used. Further, pure water purified with an ion exchange filter or the like may be used. The electric resistance of pure water is desirably 18.3 MQcm or more, the TOC (organic concentration) is desirably 20 ppb or less, and it is desirable that deaeration treatment is performed.

The embodiment of the present invention will be described more specifically with reference to examples. However, the scope of the present invention is not limited to the following examples.
[Resin (A)]
<Resin Synthesis Example 1: Synthesis of Resin (A-1)>

Under a nitrogen stream, 10.7 g of cyclohexanone was placed in a three-necked flask and heated to 85 ° C. To this, 4.4 g of monomer 1, 1.2 g of monomer 2, 3.9 g of monomer 3, 0.7 g of monomer 4, and polymerization initiator V-601 (manufactured by Wako Pure Chemical Industries, Ltd.) A solution prepared by dissolving 6.5 mol% in 19.9 g of cyclohexanone was added dropwise over 6 hours. After completion of dropping, the reaction was further continued at 85 ° C. for 2 hours. The reaction solution was allowed to cool and then added dropwise to a mixed solution of 250.2 g of heptane / 107.2 g of ethyl acetate. The precipitated powder was collected by filtration and dried to obtain 8.3 g of Resin (A-1). The polymer composition ratio (molar ratio) determined from NMR was 40/10 / 42.5 / 7.5 (in order from the left in the structural formula). The weight average molecular weight of the obtained resin was 8600 in terms of standard polystyrene, and the dispersity (Mw / Mn) was 1.5.
Similarly, other resins (A-2) to (A-12) shown below were synthesized.
The structure of the acid-decomposable resin (A) used in the examples is shown below. Table 2 below shows the molar ratio of repeating units in each resin (in order from the left in the structural formula), weight average molecular weight (Mw), and dispersity (Mw / Mn).

<Preparation of actinic ray-sensitive or radiation-sensitive resin composition>
The components shown in Table 3 below are dissolved in a solvent, and a solution having a solid content concentration of 4% by mass is prepared for each, and this is filtered through a polyethylene filter having a pore size of 0.05 μm. A composition (positive photosensitive resin composition) was prepared. The prepared positive photosensitive resin composition was evaluated by the following method, and the results are shown in Table 3.
<Image performance test>
[Exposure conditions: ArF immersion exposure]
An organic antireflection film ARC29SR (manufactured by Nissan Chemical Industries, Ltd.) was applied on a silicon wafer (12 inch diameter), and baked at 205 ° C. for 60 seconds to form an antireflection film having a thickness of 98 nm. The positive photosensitive resin composition prepared thereon was applied and baked at 120 ° C. for 60 seconds to form a photosensitive film having a thickness of 100 nm. The obtained wafer was used with an ArF excimer laser immersion scanner (XT1700i, NA1.20, C-Quad, outer sigma 0.981, inner sigma 0.895, XY deflection manufactured by ASML), 1: 1 with a line width of 75 nm. Exposure was through a 6% halftone mask with a line and space pattern. Ultra pure water was used as the immersion liquid. Thereafter, heating was performed at 120 ° C. for 60 seconds, followed by development with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsing with pure water, and spin drying to obtain a resist pattern.
[Line edge roughness (LER)]
The line edge roughness (nm) is measured using a length-measuring scanning electron microscope (SEM) to observe a line-and-space 1/1 pattern with a line width of 75 nm, and the longitudinal edge of the line pattern is in the range of 5 μm. The distance from the reference line that should have an edge was measured at 50 points with a length measurement SEM (Hitachi, Ltd. S-8840) to obtain the standard deviation (σ), and 3σ was calculated. A smaller value indicates better performance [profile shape (pattern shape)]
Observe a line-and-space 1/1 pattern with a line width of 75 nm, ○ if the cross-sectional shape is rectangular, △ if the skirt is generated, △ if the skirt is severe, × if the skirt is too severe Xx indicates that a bridge is generated.
[Etching resistance (dry etching resistance)]
The etching rate of the resist film with respect to CF ₄ gas was measured using a reactive ion etching apparatus (CSE-1110) manufactured by ULVAC. The relative etching rate ratio (etching rate of each example resist / etching rate of the resist of Example 1) when the etching rate of the resist of Example 1 was 1.0 was used as an index of etching resistance. The larger the value, the worse the etching, and the smaller the value, the better the etching.
[Retreating angle (Immersion liquid followability)]
The prepared positive photosensitive resin composition was applied on a silicon wafer (8-inch diameter), and baked at 120 ° C. for 60 seconds to form a resist film having a thickness of 120 nm. The receding contact angle of the water droplet was measured by the expansion / contraction method of a dynamic contact angle meter (manufactured by Kyowa Interface Science Co., Ltd.). An initial droplet size of 35 μL was sucked at a speed of 6 μL / sec for 5 seconds, and a value with a stable dynamic contact angle during suction was defined as a receding contact angle. The measurement environment is 23 ± 3 ° C. and relative humidity 45 ± 5%. The larger the value of the receding contact angle, the more the immersion liquid (water) can follow the higher scanning speed.

The symbols described in Table 3 are as follows.
Resin (A) and hydrophobic resin (B) correspond to those exemplified above.
[Acid generator (compound (C))]

The molar extinction coefficient ε for calculating the relative molar extinction coefficient is calculated according to the Lambert-Beer formula using a 1 cm square cell for a measurement solution in which an acid generator (compound (C)) is dissolved in an acetonitrile solvent. Using this, the UV spectrum was measured and calculated from the absorbance at 193 nm (A) and the measured solution medium concentration (c: unit mol / L). In addition, in order to compare the characteristics of the cation structure, the anion structure is a value calculated in the same manner as nonafluorobutanesulfonate.
The basic compound, surfactant and solvent are as follows.
(Basic compound)
DIA: 2,6-diisopropylaniline TMEA: tris (methoxyethoxyethyl) amine PEA: N-phenyldiethanolamine TOA: trioctylamine PBI: 2-phenylbenzimidazole DHA: N, N-dihexylaniline (surfactant)
W-1: MegaFuck F176 (Dainippon Ink Chemical Co., Ltd .; fluorine-based)
W-2: Megafuck R08 (Dainippon Ink Chemical Co., Ltd .; fluorine and silicon)
W-3: Troisol S-366 (manufactured by Troy Chemical Co .; fluorine type)
W-4: PF656 (manufactured by OMNOVA; fluorine-based)
W-5: PF6320 (manufactured by OMNOVA; fluorine-based)
(solvent)
S1-1: Propylene glycol monomethyl ether acetate (PGMEA)
S1-2: Cyclohexanone S2-1: Propylene glycol monomethyl ether (PGME)
S2-2: Propylene carbonate S2-3: γ-Butyrolactone

As is clear from Table 3, Comparative Example 1 in which the resin does not contain the repeating unit represented by the general formula (I-1) or (I-2) is inferior in LER, etching resistance, and receding contact angle. . It can be seen that Comparative Example 2 in which the acid generator does not satisfy the requirement of compound (C) (relative molar extinction coefficient of 0.8 or less) is inferior in any of LER, profile shape, etching resistance, and receding contact angle.
On the other hand, Examples 1-20 in which resin contains the repeating unit represented by general formula (I-1) or (I-2), and an acid generator satisfy | fills the requirements of compound (C) are LER, profile shape It can be seen that both the etching resistance and the receding contact angle are excellent.
In addition, about the prescription of each Example, although dry exposure was performed on the conditions according to the said liquid immersion exposure, the favorable result was obtained about LER, profile shape, and etching resistance also about these.

Claims (10)

(A) A resin containing a repeating unit represented by the following general formula (I-1) or (I-2), and (C) a molar extinction coefficient ε at a wavelength of 193 nm measured in an acetonitrile solvent is triphenylsulfonium. An actinic ray-sensitive or radiation-sensitive resin composition containing a compound that generates an acid upon irradiation with actinic rays or radiation in a relative ratio to nonafluorobutanesulfonate of 0.8 or less.

In the general formulas (I-1) and (I-2),
AR ₁ represents an aromatic group.
AR ₂ represents an aromatic group.
R ₁ represents an alkyl group, a cycloalkyl group, or an aryl group.
A ₁ and A ₂ each independently represents a hydrogen atom, an alkyl group, a halogen atom, a cyano group or an alkyloxycarbonyl group.
Z represents a linking group that forms a ring together with C-AR _{2 in} formula (I-2). The actinic-ray sensitive or radiation sensitive resin composition of Claim 1 whose said compound (C) is a compound represented by the following general formula (II-1) or (II-2).

In the above general formula,
Each Ra independently represents an alkyl group, a cycloalkyl group or an alkenyl group. Two Ras may be bonded to each other to form a ring, and the ring may be condensed with an aromatic ring or a saturated hydrocarbon ring.
R ₂₀ represents a group having a hydroxyl group, a halogen atom, a carboxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. When a plurality of R ₂₀ are present, the plurality of R ₂₀ may be the same or different.
X ₂ is _{-CR 21 = CR 22 -, -} NR 23 -, - S- or an -O-.
R ₂₁ and R ₂₂ each independently represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group or a cycloalkyl group. Represents a group having
R ₂₃ represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group or an acyl group.
R ₂₄ represents an aryl group.
R ₂₅ and R ₂₆ each independently represents a hydrogen atom, a halogen atom, an alkyl group, a cycloalkyl group, an aryl group or a cyano group.
R ₂₇ and R ₂₈ each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
R ₂₅ and R ₂₆ and R ₂₇ and R ₂₈ may be connected to each other to form a ring.
n ₁ represents an integer of 0 to 3.
q represents an integer of 0 to 10.
Z ⁻ represents a non-nucleophilic anion. The compound (C) represented by the general formula (II-1) is a compound having a cation structure represented by the following general formula (ZI-1), and represented by the general formula (II-2). The actinic-ray-sensitive or radiation-sensitive resin composition of Claim 2 whose compound (C) is a compound which has a cation structure represented by the following general formula (ZI-3).

In general formula (ZI-1),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, or a group having a cycloalkyl group.
When there are a plurality of R _{14 s,} each independently represents a group having a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, an alkoxycarbonyl group, an alkylcarbonyl group, an alkylsulfonyl group, a cycloalkylsulfonyl group, or a cycloalkyl group. To express.
R ₁₅ each independently represents an alkyl group or a cycloalkyl group. Two R ₁₅ may be bonded to each other to form a ring, and the ring may be condensed with an aromatic ring or a saturated hydrocarbon ring.
l represents an integer of 0-2.
r represents an integer of 0 to 10.

In general formula (ZI-3),
R _{1c to} R _5c are each independently a hydrogen atom, alkyl group, cycloalkyl group, aryl group, alkoxy group, aryloxy group, alkoxycarbonyl group, alkylcarbonyloxy group, cycloalkylcarbonyloxy group, halogen atom, hydroxyl group Represents a nitro group, an alkylthio group or an arylthio group.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, a halogen atom, a cyano group or an aryl group.
R _x and R _y each independently represents an alkyl group, a cycloalkyl group, a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxycarbonylalkyl group, an allyl group, or a vinyl group.
Any two or more of R _{1c to} R _5c , R _5c and R _6c , R _6c and R _7c , R _5c and R _x , and R _x and R _y may be bonded to form a ring structure. The ring structure may contain an oxygen atom, a sulfur atom, an ester bond, or an amide bond.   The actinic-ray sensitive or radiation sensitive resin composition of any one of Claims 1-3 whose all the repeating units which comprise the said resin (A) are (meth) acrylate type repeating units.   (B) The actinic ray-sensitive or radiation-sensitive resin composition according to any one of claims 1 to 4, further comprising a hydrophobic resin having at least one of a fluorine atom and a silicon atom.   The actinic ray-sensitive or radiation-sensitive resin composition according to claim 1, wherein the resin (A) further contains a repeating unit having a lactone structure. The actinic-ray sensitive or radiation sensitive resin composition of any one of Claims 1-6 in which the said resin (A) further contains the repeating unit represented by the following general formula (AI).

In general formula (AI),
Xa ₁ represents a hydrogen atom, a methyl group which may have a substituent, or a group represented by —CH ₂ —R ₉ . R ₉ represents a hydroxy group or a monovalent organic group.
T represents a single bond or a divalent linking group.
Rx _{1 to} Rx ₃ each independently represents an alkyl group or a cycloalkyl group.
Two of Rx _{1 to} Rx ₃ may combine to form a cycloalkyl group.   The resist film formed using the actinic-ray-sensitive or radiation-sensitive resin composition of any one of Claims 1-7. The pattern formation method including the process of exposing the resist film of Claim 8, and the process of developing the exposed resist film.   The pattern formation method according to claim 9, wherein the exposure is immersion exposure.