JP2012094460A - Lithium ion secondary battery - Google Patents
Lithium ion secondary battery Download PDFInfo
- Publication number
- JP2012094460A JP2012094460A JP2010242949A JP2010242949A JP2012094460A JP 2012094460 A JP2012094460 A JP 2012094460A JP 2010242949 A JP2010242949 A JP 2010242949A JP 2010242949 A JP2010242949 A JP 2010242949A JP 2012094460 A JP2012094460 A JP 2012094460A
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- additive
- mass
- active material
- electrode active
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、非水リチウムイオン二次電池に関する。 The present invention relates to a non-aqueous lithium ion secondary battery.
リチウムイオン二次電池は、正極及び負極に、リチウムの吸蔵,放出が可逆的に行われる電池である。電池は充電の際、正極に含まれるリチウムイオンが負極に吸蔵されて容量が発現するが、正極からリチウムイオンが放出されるとともに、正極中のリチウム以外の金属イオンも溶出することが知られている。このように溶出した金属イオンは負極で還元され、金属として析出する。このような金属の析出物は電池内部短絡を引き起こすか、負極上で他の物質と化合物を形成し、抵抗成分となり容量劣化及び寿命劣化を引き起こす。 A lithium ion secondary battery is a battery in which lithium is occluded and released reversibly in a positive electrode and a negative electrode. When a battery is charged, lithium ions contained in the positive electrode are occluded in the negative electrode to develop capacity, but it is known that lithium ions are released from the positive electrode and that metal ions other than lithium in the positive electrode are also eluted. Yes. The metal ions eluted in this way are reduced at the negative electrode and deposited as metal. Such metal deposits cause a short circuit inside the battery or form a compound with another substance on the negative electrode, which becomes a resistance component and causes capacity deterioration and life deterioration.
このような問題を解決するために、特開2009−146822号公報(特許文献1)では、セパレータ中にアルミナ及びマグネシアを混入させ、セパレータ中でマンガンを捕捉する方法が挙げられている。 In order to solve such a problem, Japanese Patent Application Laid-Open No. 2009-146822 (Patent Document 1) includes a method in which alumina and magnesia are mixed in a separator and manganese is captured in the separator.
特開2009−277395号公報(特許文献2)では、マンガン溶出を抑制するために、電極活物質材料をスピネル構造の正・負極を使用する方法が挙げられている。 Japanese Patent Application Laid-Open No. 2009-277395 (Patent Document 2) describes a method of using positive and negative electrodes having a spinel structure as an electrode active material material in order to suppress manganese elution.
特表2009−527089号公報(特許文献3)には、マンガン補足剤としてTiO2,TiS2のような導電物質を炭素系負極活物質の粒子表面、あるいは負極合剤中に添加する方法が挙げられている。 JP 2009-527089 A (Patent Document 3) includes a method of adding a conductive material such as TiO 2 or TiS 2 as a manganese scavenger to the particle surface of the carbon-based negative electrode active material or to the negative electrode mixture. It has been.
特許文献1に記載の技術では、セパレータ中でマンガンが捕集されることにより、セパレータ中のマンガン化合物はセパレータの空隙を埋めてしまう恐れがある。これらマンガン化合物は、電池抵抗の増大を引き起こし、最終的には電池の寿命劣化に繋がる。また、セパレータ中でのマンガン化合物の析出がさらに進んだ場合、内部短絡の恐れもある。 In the technique described in Patent Document 1, manganese is collected in the separator, so that the manganese compound in the separator may fill the gap in the separator. These manganese compounds cause an increase in battery resistance and ultimately lead to deterioration of the battery life. Moreover, when precipitation of the manganese compound in the separator further proceeds, there is a risk of internal short circuit.
特許文献2のように電極材料をスピネル構造にしたところで、マンガン溶出が起きないわけではなく、溶出した時の寿命劣化は避けられない。
When the electrode material has a spinel structure as in
特許文献3において、Mn捕捉剤として用いられているTiO2は対極Liで1.4〜2Vの範囲でプラトー領域を持つ負極材として広く知られている。
このため、TiO2をリチウムチタン酸化物負極系の電池に添加物として添加した場合、TiO2はリチウムチタン酸化物の作動電位と重なるため、活物質として働く。このため、マンガンを捕捉する作用は低いと考えられる。TiS2を用いた場合も同様である。
In
Therefore, in the case of adding TiO 2 as an additive to the battery of the lithium titanium oxide negative electrode system, TiO 2 because overlapping with operating potential of the lithium titanium oxide acts as the active material. For this reason, it is thought that the effect | action which capture | acquires manganese is low. The same applies when TiS 2 is used.
本発明の課題は、以上のようなマンガン溶出による問題を解決するものであって、これにより電池の寿命劣化を抑制し得るリチウムイオン二次電池を提供することにある。 An object of the present invention is to solve the above problems caused by elution of manganese, and to provide a lithium ion secondary battery that can suppress the deterioration of the battery life.
上述の課題を解決するための本発明は、正極と、負極と、電解液と、セパレータとを有するリチウムイオン二次電池であって、前記正極は、正極活物質としてマンガンを含むリチウム酸化物を有し、前記負極または前記セパレータは、添加物として電気陰性度が1.5より低い元素を含む化合物を有することを特徴とするリチウムイオン二次電池である。 The present invention for solving the above-mentioned problems is a lithium ion secondary battery having a positive electrode, a negative electrode, an electrolytic solution, and a separator, wherein the positive electrode is made of lithium oxide containing manganese as a positive electrode active material. And the negative electrode or the separator has a compound containing an element having an electronegativity lower than 1.5 as an additive.
前記添加物は、前記負極活物質表面上、または正極合剤中、または、負極集電体上、またはセパレータ表面上に存在することが好ましい。 The additive is preferably present on the surface of the negative electrode active material, in the positive electrode mixture, on the negative electrode current collector, or on the separator surface.
すなわち、以下のようなリチウムイオン二次電池である。 That is, the following lithium ion secondary battery.
正極と、負極と、電解液と、セパレータとを有するリチウムイオン二次電池であって、前記正極は、正極活物質としてマンガンを含むリチウム酸化物を有し、前記リチウムイオン二次電池は、添加物として電気陰性度が1.5より低い元素を含む化合物を有することを特徴とするリチウムイオン二次電池。 A lithium ion secondary battery having a positive electrode, a negative electrode, an electrolytic solution, and a separator, wherein the positive electrode has a lithium oxide containing manganese as a positive electrode active material, and the lithium ion secondary battery is added A lithium ion secondary battery comprising a compound containing an element having an electronegativity lower than 1.5 as an object.
前記添加物は、前記添加物中の前記元素と、電解液中のマンガンイオンとが置換し得る塩であることを特徴とするリチウムイオン二次電池。 The lithium ion secondary battery, wherein the additive is a salt that can replace the element in the additive with manganese ions in the electrolytic solution.
本発明によれば、リチウムイオン二次電池の寿命劣化を抑制し得る。 According to the present invention, it is possible to suppress the life deterioration of the lithium ion secondary battery.
以下、本発明に係る実施形態について、図面を参照しながら説明する。 Hereinafter, embodiments according to the present invention will be described with reference to the drawings.
リチウムイオン二次電池は充電の際、正極からリチウムイオンが放出されるとともに、正極中のリチウム以外の金属イオンも溶出することが知られている。図1の従来例では、マンガンを含む正極からリチウムイオンが放出され、負極に析出する様子を示した。正極から溶出した金属イオンは、負極上で還元され、金属として析出する。あるいは、負極上で他の物質と反応し、化合物として析出する。これら析出物は析出の場所によっては内部短絡を起こす。または、活物質の働きを抑制する抵抗成分となるため、電池の容量劣化,寿命劣化を引き起こすと考えられる。したがって、金属の析出場所をコントロールすることはリチウムイオン二次電池の寿命劣化を抑制する上で重要な課題となっている。 It is known that when a lithium ion secondary battery is charged, lithium ions are released from the positive electrode and metal ions other than lithium in the positive electrode are also eluted. In the conventional example of FIG. 1, lithium ions were released from the positive electrode containing manganese and deposited on the negative electrode. Metal ions eluted from the positive electrode are reduced on the negative electrode and deposited as metal. Alternatively, it reacts with another substance on the negative electrode and precipitates as a compound. These precipitates cause an internal short circuit depending on the deposition location. Or, since it becomes a resistance component that suppresses the function of the active material, it is considered that it causes the battery capacity deterioration and life deterioration. Therefore, controlling the metal deposition site is an important issue in suppressing the deterioration of the life of the lithium ion secondary battery.
この課題を解決するために本発明では、正極から放出された金属イオンを捕捉することのできる添加物をリチウムイオン二次電池内に添加した。図1の本発明ではマンガンを含む正極から放出されたリチウムイオンが負極成分上で析出することなく、添加物上で析出する様子を示した。このように、マンガンは負極成分以外の場所で析出するため、マンガン析出により起こる、上記課題を解決することができると考えられる。 In order to solve this problem, in the present invention, an additive capable of capturing metal ions released from the positive electrode is added to the lithium ion secondary battery. In the present invention shown in FIG. 1, the lithium ions released from the positive electrode containing manganese are not precipitated on the negative electrode component but are deposited on the additive. Thus, since manganese precipitates in places other than a negative electrode component, it is thought that the said subject which arises by manganese precipitation can be solved.
本発明の添加物は、マンガンより電気陰性度の低い元素、特に電気陰性度が1.5以下である元素を含む化合物を添加物として有することを特徴とする。正極から溶出したマンガンイオンは、添加物中のマンガンより電気陰性度が低い元素と置換する。このため、添加物はマンガンイオンを捕集することができる。 The additive of the present invention is characterized by having as an additive a compound containing an element having an electronegativity lower than that of manganese, particularly an element having an electronegativity of 1.5 or less. Manganese ions eluted from the positive electrode are replaced with an element having a lower electronegativity than manganese in the additive. For this reason, the additive can collect manganese ions.
電気陰性度とは、分子内の原子が電子を引き寄せる強さを示しており、マンガンイオンと、マンガンイオンよりも電気陰性度が低い金属を有する化合物が存在するとき、マンガンイオンはその化合物の金属と選択的に入れ替わる特性がある。マンガンの電気陰性度はポーリングが定義した電気陰性度の値で1.55である。正極から溶出したマンガンイオンと効率的に置換を起こすためには、添加物中の置換を起こす元素の電気陰性度は、マンガンに対して、なるべく低いことが望ましく、0.5以上低いことが好ましい。すなわち、添加物中の置換を起こす元素の電気陰性度は1.5以下であることが好ましい。 Electronegativity refers to the strength with which atoms in a molecule attract electrons. When there is a manganese ion and a compound having a metal whose electronegativity is lower than that of the manganese ion, the manganese ion is the metal of the compound. And have the property of selectively switching. The electronegativity of manganese is 1.55 as defined by Pauling. In order to efficiently perform substitution with manganese ions eluted from the positive electrode, the electronegativity of the element causing substitution in the additive is desirably as low as possible with respect to manganese, and is preferably 0.5 or more. . That is, the electronegativity of the element causing substitution in the additive is preferably 1.5 or less.
電気陰性度が1.5より低い元素には、Na,Mg,K,Ca,Sc,Rb,Sr,Y,Zr,Cs,Ba,Hf,Ta,Fr,Raや、原子番号57から71までのランタノイド、原子番号89から103までのアクチノイドがある。これらの元素を含む添加物は如何なる形態であっても構わない。上記に示す元素の化合物には、Na2CO3,Na2CO4,Na2S2O4,Na2SO3,NaHSO3,Na2SO4,NaNO2,NaNO3,MgO,Mg(OH)2,MgSO4,MgCO3,MgClO4,MgH2,MgB2,MgS,Mg3N2,Mg3N2,MgCo3,K2CO3,K2CO4,K2SO4,KOH,K2O,KO2,CaSO4,CaC2,CaCO3,CaO,Ca(OH)2,RbCl,RbBr,RbOH,SrO、Sr(OH)2,SrCrO4,SrCO3,SrSO4,Sr(NO3)2,SrHPO4,Y2O3,Y3Fe5O12,YVO4,YB66,YBa2Cu3O7,ZrSiO4,ZrO2,ZrW2O8,BaO2,BaO,Ba(OH)2,BaTiO3,BaCO3,HfO2,KTaO3,TaC,RaO等、やLa2CuO4,LaB6,La3Ga5SiO14,CeAl3,CeCu6,CeRu2Si2,Pr6O11等のランタノイド類、PaO,PaO2等のアクチノイド類がある。 Elements with an electronegativity lower than 1.5 include Na, Mg, K, Ca, Sc, Rb, Sr, Y, Zr, Cs, Ba, Hf, Ta, Fr, Ra, and atomic numbers 57 to 71. Lanthanoids, actinides with atomic numbers 89 to 103. The additive containing these elements may be in any form. The compound of the element shown above includes Na 2 CO 3 , Na 2 CO 4 , Na 2 S 2 O 4 , Na 2 SO 3 , NaHSO 3 , Na 2 SO 4 , NaNO 2 , NaNO 3 , MgO, Mg (OH ) 2 , MgSO 4 , MgCO 3 , MgClO 4 , MgH 2 , MgB 2 , MgS, Mg 3 N 2 , Mg 3 N 2 , MgCo 3 , K 2 CO 3 , K 2 CO 4 , K 2 SO 4 , KOH, K 2 O, KO 2 , CaSO 4 , CaC 2 , CaCO 3 , CaO, Ca (OH) 2 , RbCl, RbBr, RbOH, SrO, Sr (OH) 2 , SrCrO 4 , SrCO 3 , SrSO 4 , Sr (NO 3 ) 2 , SrHPO 4 , Y 2 O 3 , Y 3 Fe 5 O 12 , YVO 4 , YB 66 , YBa 2 Cu 3 O 7 , ZrSiO 4 , ZrO 2 , ZrW 2 O 8 , BaO 2 , BaO, Ba ( OH) 2, BaTiO 3, BaCO 3, HfO 2, TaO 3, TaC, RaO like, and La 2 CuO 4, LaB 6, La 3 Ga 5 SiO 14, CeAl 3, CeCu 6, CeRu 2 Si 2, Pr 6 O lanthanoid such as 11, PaO, such PaO 2 There are actinoids.
しかし、上記に示す電気陰性度が1.5より低い元素の中において自然界にごく微量にしか存在しておらず希少価値が高いものが多い。そのような貴重な元素を介在させた化合物を電池に混入させるのには、電池のコストの大幅な増大を招く可能性がある。 However, among the elements having an electronegativity lower than 1.5 described above, there are many elements that are present in nature only in a very small amount and have a high rare value. Incorporation of such a valuable element-containing compound into the battery may lead to a significant increase in battery cost.
そのため、上記に示す電気陰性度が1.5より低い元素を含む化合物において、特にK、Ca,Baを含む化合物を負極側の添加物として用いるのが好ましい。Kを含む化合物ではK2SO4が好ましく、Caを含む化合物ではCaCO3、Baを含む化合物ではBaCO3が好ましい。 Therefore, in the compound containing an element having an electronegativity lower than 1.5 as described above, it is particularly preferable to use a compound containing K, Ca, or Ba as an additive on the negative electrode side. Preferably K 2 SO 4 in a compound containing K, preferably BaCO 3 is a compound containing CaCO 3, Ba is a compound containing Ca.
また、添加物は電池の作動電位の範囲で安定であることが好ましい。添加物に含まれる金属の標準電極電位が、正極に含まれる金属の標準電極電位以下であり、負極に含まれる金属の標準電極電位以上である場合、添加物は電気分解する可能性が高い。電気分解した添加物の金属イオンは負極で還元され、金属として析出する。または、添加物そのものが負極活物質として作動し、マンガン捕捉の効果が落ちる。 Moreover, it is preferable that an additive is stable in the range of the operating potential of a battery. When the standard electrode potential of the metal contained in the additive is less than or equal to the standard electrode potential of the metal contained in the positive electrode and greater than or equal to the standard electrode potential of the metal contained in the negative electrode, the additive is likely to be electrolyzed. Electrolyzed additive metal ions are reduced at the negative electrode and deposited as metal. Alternatively, the additive itself operates as a negative electrode active material, and the effect of capturing manganese falls.
本発明における添加物は電気化学分解を利用して、マンガン捕捉するものではない。添加物が負極で還元されないためには、添加物に含まれる金属は負極に使用される金属よりも標準電極電位の低いものを用いることが望ましい。実際の電池内では、対極に用いる金属や電解液、及びその他の添加剤等の影響がある。このため、必ずしも、標準電極電位に対応する理論上の電位において、金属の酸化還元反応が起こるわけではなく、これに近い電位で起こる。よって、実際には負極に使用される金属の標準電極電位に近い電位の金属ではなく、より低い標準電極電位を持つ金属を使用することが望ましい。負極にLTOを用いる場合は、Tiの標準電極電位である−1.63Vという値を目安とし、添加物中の金属の標準電極電位はこの値より低いことが好ましい。 The additive in the present invention does not capture manganese using electrochemical decomposition. In order for the additive not to be reduced at the negative electrode, it is desirable to use a metal having a lower standard electrode potential than the metal used in the negative electrode. In an actual battery, there are influences of a metal used for the counter electrode, an electrolytic solution, and other additives. For this reason, the metal redox reaction does not necessarily occur at a theoretical potential corresponding to the standard electrode potential, but occurs at a potential close to this. Therefore, in practice, it is desirable to use a metal having a lower standard electrode potential rather than a metal having a potential close to the standard electrode potential of the metal used for the negative electrode. When LTO is used for the negative electrode, the value of -1.63 V, which is the standard electrode potential of Ti, is used as a guide, and the standard electrode potential of the metal in the additive is preferably lower than this value.
標準電極電位が−1.63Vよりも低い元素としては、Na,Mg,K,Ca,Sc,Rb,Sr,Y,Zr,Cs,Ba,Hf,Ta,Fr,Raなどがある。この中で電気陰性度が1.5以下の元素はNa,Mg,K,Ca,Rb,Sr,Baである。しかし、添加物の標準電極電位は、添加物を構成する各元素の組み合わせにより決まるため、標準電極電位が−1.63以上であっても、他の元素との組み合わせによってはLTO負極の条件下で安定な添加物となり得る。 Examples of elements whose standard electrode potential is lower than −1.63 V include Na, Mg, K, Ca, Sc, Rb, Sr, Y, Zr, Cs, Ba, Hf, Ta, Fr, and Ra. Among these elements, elements having an electronegativity of 1.5 or less are Na, Mg, K, Ca, Rb, Sr, and Ba. However, since the standard electrode potential of the additive is determined by the combination of each element constituting the additive, even if the standard electrode potential is -1.63 or more, depending on the combination with other elements, the conditions of the LTO negative electrode Can be a stable additive.
また、添加物は、陽イオンと陰イオンとが電荷を中和する形で生じた塩であることがより好ましい。この理由は、置換が起こった後、添加物から溶出したイオンは安定なイオンとして存在することが好ましいからである。 The additive is more preferably a salt formed in such a way that the cation and the anion neutralize the electric charge. This is because after the substitution takes place, the ions eluted from the additive are preferably present as stable ions.
例えば塩であるK2SO4の場合、マンガンイオン(Mn2+)が接近するとK2SO4は一時的に2分子のK+とSO4-となり、Mn2+はSO4-と反応し、Mn2SO4となることでMn2+が捕捉される。仮に置換が起こらなかった場合でもSO4-はイオンとして安定であるため、イオンとして溶液中存在する。これに対し、例えば塩でないK2Oの場合、Mn2+の接近により2K+とO2-となり、置換が起こらなかった場合O2-が気体となり、電池膨張の原因となる可能性が考えられる。 For example, in the case of K 2 SO 4 which is a salt, when manganese ions (Mn 2+ ) approach, K 2 SO 4 temporarily becomes two molecules of K + and SO 4− , and Mn 2+ reacts with SO 4−. , Mn 2+ is captured by becoming Mn 2 SO 4 . Even if no substitution takes place, SO 4− is stable as an ion and therefore exists as an ion in the solution. In contrast, in the case of K 2 O is not a salt, 2K + and O 2- next by the approach of Mn 2+, if did not occur substituted O 2- is a gas, considered can cause cell expansion It is done.
このため、添加物は、解離した後、安定なイオンとなる塩であることが望ましい。 For this reason, it is desirable that the additive is a salt that becomes stable ions after dissociation.
また、本発明では添加物として、上記のような金属化合物の他、多孔質炭素材料も使用することも可能である。多孔質炭素は、難黒鉛化炭素物質をNaOH若しくは、KOH,K2CO3による化学賦活か、CO2,COのガス賦活によって多孔質炭素化したものであれば使用できる。但し、マンガンをうまく吸着し得る細孔を有する炭素が有効である。比表面積が大きいだけの多孔質炭素では、マンガンを吸着し得ても、細孔が大きければ、充放電に伴い脱離する可能性もある。よって、多孔質炭素の中でも、マンガンを捕集し、かつ脱離させにくいような細孔径を有するものが好ましい。窒素吸着法及び二酸化炭素吸着法によって、細孔径0.2mm〜1nmの細孔が全体の細孔の5〜60%、好ましくは10〜40%を有するものが好ましい。また、その多孔質炭素の平均真比重は1.4〜1.7g/ccが好ましく、その中でも、1.45〜1.68g/ccがより好ましい。 In the present invention, a porous carbon material can be used as an additive in addition to the metal compound as described above. The porous carbon can be used as long as the non-graphitizable carbon material is chemically activated with NaOH or KOH, K 2 CO 3 or gasified with CO 2 or CO. However, carbon having pores that can adsorb manganese well is effective. With porous carbon having a large specific surface area, even if manganese can be adsorbed, if the pores are large, there is a possibility of desorption along with charge / discharge. Accordingly, among the porous carbons, those having a pore diameter that makes it difficult to collect and desorb manganese are preferable. According to the nitrogen adsorption method and the carbon dioxide adsorption method, it is preferable that the pores having a pore diameter of 0.2 mm to 1 nm have 5 to 60%, preferably 10 to 40% of the whole pores. The average true specific gravity of the porous carbon is preferably 1.4 to 1.7 g / cc, and more preferably 1.45 to 1.68 g / cc.
ここまで、添加物について記載した。さらに、添加物の添加形態を検討することで、より寿命劣化抑制に効果がある使用形態となる。添加形態としては、添加場所,添加量等が検討項目として挙げられる。 Up to this point, the additives have been described. Furthermore, by examining the additive form of the additive, the form of use is more effective in suppressing the life deterioration. As the addition form, the addition place, the addition amount, and the like are listed as examination items.
添加物の添加場所としては(1)負極合剤中に分散された状態、(2)負極活物質表面にコーティングされた状態、(3)負極表面にコーティングされた状態(4)負極側のセパレータ表面上に存在する状態、とすることができる。 The additive is added to (1) a state in which it is dispersed in the negative electrode mixture, (2) a state in which the negative electrode active material is coated, (3) a state in which the negative electrode is coated, and (4) a separator on the negative electrode side. A state existing on the surface.
添加物の負極合剤に対する添加量は少なすぎると、負極活物質表面におけるマンガン化合物抑制の効果が十分に得られず、また多すぎると、電池の重量当たりの容量が低くなってしまう。多すぎる場合には、通常の電池使用において内部抵抗が増加し、放電終止電圧に達するまでに得られる連続放電時間も短くなる。本発明の添加物は、負極活物質と添加物の合計質量に対して0.01〜45質量%添加することが好ましい。なお、負極中の添加物の存在方法によって、最適な添加量は異なる。 If the amount of the additive added to the negative electrode mixture is too small, the effect of suppressing the manganese compound on the surface of the negative electrode active material cannot be sufficiently obtained, and if it is too large, the capacity per weight of the battery becomes low. When the amount is too large, the internal resistance increases during normal battery use, and the continuous discharge time obtained before reaching the end-of-discharge voltage is also shortened. The additive of the present invention is preferably added in an amount of 0.01 to 45% by mass with respect to the total mass of the negative electrode active material and the additive. The optimum addition amount varies depending on the method of presence of the additive in the negative electrode.
「負極合剤中に分散された状態」を図2(1)に示した。「負極合剤中に分散された状態」は負極活物質粒子間に添加物粒子が混入している状態を示す。存在の状態は、電極をSEM(Scanning Electron Microscope)観察することによって確認することができる。 “The state of being dispersed in the negative electrode mixture” is shown in FIG. The “state dispersed in the negative electrode mixture” indicates a state in which additive particles are mixed between the negative electrode active material particles. The state of existence can be confirmed by observing the electrode with SEM (Scanning Electron Microscope).
添加物を負極合剤中に分散させる方法としては、電極を作製する際に、添加物を負極活物質,導電助剤と共に混合するか、添加物を予め負極活物質に混合させておき、それに導電助剤,バインダを加えて電極とする等が考えられ、投入のタイミングは特に問わない。
混合方法は、乳鉢による混合や、自動で混合させる装置を用いても良く、混合が起これば特に指定はない。
As a method of dispersing the additive in the negative electrode mixture, when preparing the electrode, the additive is mixed with the negative electrode active material and the conductive auxiliary agent, or the additive is previously mixed with the negative electrode active material, It is conceivable to add a conductive additive and a binder to form an electrode, and the timing of charging is not particularly limited.
The mixing method may be mixing with a mortar or an automatic mixing device, and is not particularly specified if mixing occurs.
このような添加物の分散状態において、添加物の添加量は、負極活物質と添加物の合計質量に対して0.01〜45質量%添加することが好ましいが、0.1〜5.7質量%がより好ましい。 In such a dispersed state of the additive, the additive is preferably added in an amount of 0.01 to 45% by mass with respect to the total mass of the negative electrode active material and the additive, but 0.1 to 5.7%. The mass% is more preferable.
添加物を負極合剤中に分散させるこのような添加形態は他の添加形態と比べ作製に手間がかからないという利点がある。 Such an addition form in which the additive is dispersed in the negative electrode mixture has an advantage that it is less time-consuming to produce than other addition forms.
「負極活物質表面にコーティングされた状態」を図2(2)に示す。「負極活物質表面にコーティングされた状態」とは、添加物が負極活物質粒子表面に存在した状態であることを示す。 “A state where the surface of the negative electrode active material is coated” is shown in FIG. “The state coated on the surface of the negative electrode active material” indicates that the additive is present on the surface of the negative electrode active material particles.
存在の状態はSEM(Scanning Electron Microscope)、若しくはTEM(Transmission Electron Microscope)によって確認することができる。 The presence state can be confirmed by SEM (Scanning Electron Microscope) or TEM (Transmission Electron Microscope).
負極活物質表面にコーティングする場合、負極活物質粒子を完全に覆ってしまった状態では、リチウムを吸蔵放出できず、容量が発現しない。したがって、添加物により、負極活物質粒子を完全にコーティングするのではなく、部分的に存在させた状態が好ましい。
一方、コーティング量が少なすぎると、溶出したマンガンの捕捉効果が十分に得られない可能性がある。このため、負極活物質への添加物のコーティングは負極活物質と添加物の合計質量に対して0.01〜34質量%が好ましく、より好ましくは1〜5.7質量%である。
When coating the surface of the negative electrode active material, lithium cannot be occluded and released in a state where the negative electrode active material particles are completely covered, and the capacity is not developed. Therefore, it is preferable that the negative electrode active material particles are not completely coated with the additive but are partially present.
On the other hand, if the coating amount is too small, there is a possibility that the trapping effect of eluted manganese cannot be obtained sufficiently. For this reason, 0.01-34 mass% is preferable with respect to the total mass of a negative electrode active material and an additive, and, as for the coating of the additive to a negative electrode active material, More preferably, it is 1-5.7 mass%.
このように添加剤を負極活物質表面にコーティングする添加形態は添加量の調節が他の添加形態よりも厳密で、調整方法も難しいが、溶出したマンガンとの接触表面積が大きくなるため、より少量の添加物でマンガン捕捉効果が得られると考えられる。 In this way, the additive form in which the additive is coated on the surface of the negative electrode active material is more difficult to adjust the addition amount than the other additive forms, and the adjustment method is difficult, but the contact surface area with the eluted manganese is increased, so the amount is smaller. It is considered that a manganese scavenging effect can be obtained with this additive.
負極活物質へのコーティング手法としては、湿式法及び乾式法などが考えられる。しかし、コーティングが起こる方法であれば、如何なる方法でも問わない。乾式ではメカノケミカル手法によって、せん断力を用いて表面に添加物をすりつけてコーティングする方法や、ボールミル,ビーズミルを用いて表面にコーティングする方法等がある。また、湿式法では、有機若しくは無機溶媒を用いて、それに添加物を溶かした溶液を作製し、その中に負極活物質を投入、混合,乾燥させて添加物でコーティングした負極活物質を入手することができる。混合する際、熱を掛けてもかけなくても構わない。 As a method for coating the negative electrode active material, a wet method, a dry method, or the like can be considered. However, any method may be used as long as the coating occurs. In the dry process, there are a mechanochemical method in which an additive is rubbed on the surface using a shearing force, and a surface is coated using a ball mill or a bead mill. In the wet method, an organic or inorganic solvent is used to prepare a solution in which an additive is dissolved, and the negative electrode active material is placed therein, mixed and dried to obtain a negative electrode active material coated with the additive. be able to. When mixing, it does not matter whether heat is applied or not.
「負極表面にコーティングされた状態」を図2(3)に示す。「負極表面にコーティングされた状態」とは、負極表面に添加物を含む層が存在している状態を示す。このような層は、負極電極上に添加物を含むコーティング剤を塗布し、乾燥させる等の方法により形成させることができる。添加物を含むコーティング剤の作製は、有機溶媒にコーティング剤を分散させる方法によって得られる。溶媒は、負極上に塗布した後に揮発するようなものが好ましい。 “The state coated on the negative electrode surface” is shown in FIG. The “state coated on the negative electrode surface” indicates a state in which a layer containing an additive is present on the negative electrode surface. Such a layer can be formed by applying a coating agent containing an additive on the negative electrode and drying it. The preparation of the coating agent containing the additive is obtained by a method of dispersing the coating agent in an organic solvent. The solvent is preferably one that volatilizes after coating on the negative electrode.
コーティング剤を負極上に塗布する方法としては、負極の一部にコーティング剤をたらし、ブレードコータ−を用いて塗布する手法や、印刷法により添加物を負極上に介在させる手法,コーティング剤をスプレーとして負極表面に吹き付ける手法等が考えられる。この中ではコーティング剤をスプレーとして負極表面に吹き付ける手法が最も簡便である。 As a method of applying the coating agent on the negative electrode, a method of applying the coating agent to a part of the negative electrode and applying it using a blade coater, a method of interposing an additive on the negative electrode by a printing method, a coating agent, A method of spraying the negative electrode surface as a spray is conceivable. Among these, the method of spraying the coating agent on the negative electrode surface as a spray is the simplest.
添加物の添加量は、多すぎる場合、問題があり、少なすぎても効果が得られない。このため、添加物の添加量は適切な量である必要がある。添加物は、負極活物質と添加物の合計質量に対して20〜100質量%であると、電解液の負極への浸透性が悪くなり、リチウムの吸蔵放出がスムーズに行われず、抵抗上昇,急速充放電特性の悪化を招く可能性がある。逆に、コーティング率が0.55質量%未満であると、十分な効果が得られない。
そのため、コーティング率は0.55%〜11.2%が望ましい。
If the amount of additive is too large, there is a problem, and if it is too small, the effect cannot be obtained. For this reason, the addition amount of an additive needs to be an appropriate amount. When the additive is 20 to 100% by mass with respect to the total mass of the negative electrode active material and the additive, the permeability of the electrolytic solution to the negative electrode is deteriorated, lithium is not smoothly absorbed and released, and the resistance is increased. There is a possibility of deteriorating rapid charge / discharge characteristics. Conversely, if the coating rate is less than 0.55% by mass, sufficient effects cannot be obtained.
Therefore, the coating rate is desirably 0.55% to 11.2%.
添加物を負極表面にコーティングするこのような添加形態では、溶出したマンガンが負極活物質に到達する前に添加物に接触することが期待されるため、負極活物質へのマンガン析出による容量低下が効果的に抑えられると考えられる。 In such an addition form in which the additive is coated on the negative electrode surface, the eluted manganese is expected to come into contact with the additive before reaching the negative electrode active material. It is thought that it can be effectively suppressed.
「セパレータ表面上に存在する状態」を図2(4)に示す。「セパレータ表面上に存在する状態」とは、負極面に接するセパレータ表面上に添加物を含む層が存在する状態である。このような層は、負極面に接するセパレータ表面上に添加物を含むコーティング剤を塗布し、乾燥させる等の方法により形成させることができる。添加物を含むコーティング剤の作製は、有機溶媒にコーティング剤を分散させる方法によって得られる。溶媒は、負極上に塗布した後に揮発するようなものが好ましい。セパレータは高熱により収縮するため、コーティング剤を乾燥させる際は10℃〜60℃の低温で行う。このため、セパレータは、この様な低温で乾燥できる溶媒を選択することが好ましい。 The “state existing on the separator surface” is shown in FIG. The “state existing on the separator surface” is a state in which a layer containing an additive is present on the separator surface in contact with the negative electrode surface. Such a layer can be formed by a method such as applying a coating agent containing an additive on the separator surface in contact with the negative electrode surface and drying the coating agent. The preparation of the coating agent containing the additive is obtained by a method of dispersing the coating agent in an organic solvent. The solvent is preferably one that volatilizes after coating on the negative electrode. Since the separator shrinks due to high heat, the coating agent is dried at a low temperature of 10 to 60 ° C. For this reason, it is preferable to select a solvent that can be dried at such a low temperature as the separator.
コーティング剤をセパレータ上に塗布する方法としては、セパレータの一部にコーティング剤をたらし、ブレードコータ−を用いて塗布する手法や、印刷法により添加物をセパレータ上に介在させる手法,コーティング剤をスプレーとして負極表面に吹き付ける手法等が考えられる。この中ではコーティング剤をスプレーとしてセパレータ表面に吹き付ける手法が最も簡便である。 As a method of applying the coating agent on the separator, a method of applying the coating agent to a part of the separator and applying it using a blade coater, a method of interposing an additive on the separator by a printing method, a coating agent, etc. A method of spraying the negative electrode surface as a spray is conceivable. Among these, the method of spraying the coating agent on the separator surface as a spray is the simplest.
添加物の添加量は、多すぎる場合、問題があり、少なすぎても効果が得られない。このため、添加物の添加量は適切な量である必要がある。セパレータ上への添加物の添加量は、負極活物質と添加物の合計質量に対して20%〜100%であると、電解液の負極への浸透性が悪くなり、リチウムの吸蔵放出がスムーズに行われず、抵抗上昇,急速充放電特性の悪化を招く可能性がある。逆に、コーティング率が0.5質量%以下であると、十分な効果が得られない。そのため、コーティング率は0.55〜11.2質量%が望ましい。 If the amount of additive is too large, there is a problem, and if it is too small, the effect cannot be obtained. For this reason, the addition amount of an additive needs to be an appropriate amount. When the additive amount on the separator is 20% to 100% with respect to the total mass of the negative electrode active material and the additive, the permeability of the electrolytic solution to the negative electrode is deteriorated and the insertion and release of lithium is smooth. However, there is a possibility that resistance rises and rapid charge / discharge characteristics deteriorate. Conversely, if the coating rate is 0.5% by mass or less, sufficient effects cannot be obtained. Therefore, the coating rate is preferably from 0.55 to 11.2% by mass.
添加物をセパレータ表面上にコーティングするこのような添加形態では、他の添加形態と比べ、より早い段階で溶出したマンガンが添加物に接触するため、活物質への影響を最小限に抑えた上で、マンガン捕捉効果が得られると考えられる。また、特許文献1記載のセパレータ内部でマンガンを捕捉する方法と比べ、マンガンの析出は表面付近で起こるため、セパレータ内部短絡の恐れが低くなると考えられる。反面、前述の通りセパレータ材料は一般的に熱に弱く、コーティング後の乾燥温度,時間の管理が難しいというデメリットがある。 In such an additive form in which the additive is coated on the separator surface, manganese eluted at an earlier stage comes into contact with the additive compared to other additive forms, so that the influence on the active material is minimized. Thus, it is considered that a manganese capturing effect can be obtained. Further, compared with the method of capturing manganese inside the separator described in Patent Document 1, since precipitation of manganese occurs in the vicinity of the surface, it is considered that the risk of a short circuit inside the separator is reduced. On the other hand, as described above, the separator material is generally vulnerable to heat, and has a demerit that it is difficult to control the drying temperature and time after coating.
次に、負極活物質と正極活物質ついて記載する。 Next, the negative electrode active material and the positive electrode active material will be described.
本発明の効果を得るために、負極活物質の限定は特になく、一般的な負極活物質でよい。一般的な材料としては、チタン酸リチウム,リチウム金属,リチウム−アルミニウム,リチウム−鉛,リチウム−スズ,リチウム−アルミニウム−スズ,リチウム−ガリウム、およびウッド合金などのリチウム含有合金、さらに、以下のような炭素材料が挙げられる。例えば、天然黒鉛,人造黒鉛,無定形炭素,繊維状炭素,粉末状炭素,石油ピッチ系炭素,石炭コークス系炭素がある。これら炭素材料は、直径あるいは繊維長さが0.01〜30μmの粒子、あるいは繊維が好ましい。高容量,高出力が得られるという点においては、0.01〜10μmが好ましい。 In order to acquire the effect of this invention, there is no limitation in particular of a negative electrode active material, A common negative electrode active material may be sufficient. Typical materials include lithium titanate, lithium metal, lithium-aluminum, lithium-lead, lithium-tin, lithium-aluminum-tin, lithium-gallium, and lithium-containing alloys such as wood alloys. Carbon materials. Examples include natural graphite, artificial graphite, amorphous carbon, fibrous carbon, powdered carbon, petroleum pitch-based carbon, and coal coke-based carbon. These carbon materials are preferably particles or fibers having a diameter or fiber length of 0.01 to 30 μm. In terms of obtaining high capacity and high output, 0.01 to 10 μm is preferable.
マンガンの析出を、より抑えるためには、負極活物質として、作動電位が1.5〜2.0V程の高い物質を用いることが好ましい。作動電位が高い負極活物質としては、Li4Ti5O12のようなチタン酸リチウムがあり、特にスピネル型のLi4Ti5O12がより望ましい。このようなチタン酸リチウムは作動電位が1.5Vと高く、このような条件下では、マンガンは析出しにくい。また、チタン酸リチウムは、Liデンドライドの析出が起きにくい高安全材料であるという実用の観点からも望ましい。 In order to further suppress the precipitation of manganese, it is preferable to use a material having an operating potential as high as 1.5 to 2.0 V as the negative electrode active material. As a negative electrode active material having a high operating potential, there is lithium titanate such as Li4Ti5O12, and spinel-type Li4Ti5O12 is particularly desirable. Such a lithium titanate has a high operating potential of 1.5 V, and manganese is hardly deposited under such conditions. Lithium titanate is also desirable from the practical point of view that it is a highly safe material in which precipitation of Li dendride hardly occurs.
正極活物質としては、スピネル型結晶構造を有するLiMn2O4が好ましいが、この種の電池に使用されるMn系正極であれば如何なるものであっても良い。LiMnPO4,LiMnSO4等のポリアニオン型化合物を用いることができる。更に、CuO,Cu2O,Ag2O,CuS,CuSO4などのI族金属化合物、TiS2,SiO2,SnOなどのIV族金属化合物、V2O5,V6O12,VOx,Nb2O5,Bi2O3,Sb2O3などのV族金属化合物、CrO3,Cr2O3,MoO3,MoS2,WO3,SeO2などのVI族金属化合物、MnO2、Mn2O3などのVII族金属化合物、Fe2O3,FeO,Fe3O4,FePO4,Ni2O3,NiO,CoO3,CoOなどのVIII族金属化合物が添加されていてもよい。さらに、ジスイルフィド,ポリピロール,ポリアニリン,ポリパラフェニレン,ポリアセチレン,ポリアセン系材料などの導電性高分子化合物、偽グラファイト構造炭素質材料等を添加若しくは表面にコーティングした正極を用いてもよい。 As the positive electrode active material, LiMn 2 O 4 having a spinel crystal structure is preferable, but any Mn-based positive electrode used in this type of battery may be used. Polyanionic compounds such as LiMnPO 4 and LiMnSO 4 can be used. Further, Group I metal compounds such as CuO, Cu 2 O, Ag 2 O, CuS, and CuSO 4 , Group IV metal compounds such as TiS 2 , SiO 2 , and SnO, V 2 O 5 , V 6 O 12 , VO x , Group V metal compounds such as Nb 2 O 5 , Bi 2 O 3 and Sb 2 O 3 , Group VI metal compounds such as CrO 3 , Cr 2 O 3 , MoO 3 , MoS 2 , WO 3 and SeO 2 , MnO 2 , Group VII metal compounds such as Mn 2 O 3 and Group VIII metal compounds such as Fe 2 O 3 , FeO, Fe 3 O 4 , FePO 4 , Ni 2 O 3 , NiO, CoO 3 , and CoO may be added. . Furthermore, a positive electrode with a conductive polymer compound such as disulphide, polypyrrole, polyaniline, polyparaphenylene, polyacetylene, or polyacenic material, a pseudographite-structured carbonaceous material, or the like coated on the surface may be used.
また、スピネル構造を有するリチウムマンガン複合酸化物は、B,F,Mg,Al,Ti,Cr,V,Fe,Co,Ni,Cu,Zn,Nb及びZrからなる群から選ばれた1種類または複数種類の元素を含んでいてもよい。特にこれらの中でも、Mg及びAlのうちの少なくとも一方が含まれていることで、より高いサイクル特性及び高温保存特性が得られる。 Further, the lithium manganese composite oxide having a spinel structure is one kind selected from the group consisting of B, F, Mg, Al, Ti, Cr, V, Fe, Co, Ni, Cu, Zn, Nb and Zr, or Multiple kinds of elements may be included. Among these, higher cycle characteristics and high-temperature storage characteristics can be obtained by including at least one of Mg and Al.
また、本願は前述の通り、正極から溶出するマンガンを、負極周辺に添加した添加物により捕捉する。正極活物質が負極活物質や、添加物に対して極端に多い場合は、マンガンの溶出量も増す。この場合、添加物を増やすことにより、マンガンを十分に捕捉することができる。正極活物質に対する負極活物質の比率は、一般的に容量比率で正極:負極=1〜2:1の範囲である。 Further, as described above, in the present application, manganese eluted from the positive electrode is captured by an additive added around the negative electrode. When the amount of the positive electrode active material is extremely large with respect to the negative electrode active material and additives, the amount of manganese eluted also increases. In this case, manganese can be sufficiently captured by increasing the additive. The ratio of the negative electrode active material to the positive electrode active material is generally in the range of positive electrode: negative electrode = 1 to 2: 1 in terms of capacity ratio.
ここまで、添加物と、添加物の添加形態,負極活物質,正極活物質について述べた。次に図3を用いて、一般的なリチウムイオン二次電池の説明をする。 So far, the additive, the additive form, the negative electrode active material, and the positive electrode active material have been described. Next, a general lithium ion secondary battery will be described with reference to FIG.
正極1について、正極集電体の一端部には正極合剤ペーストを塗布していない集電体露出部が設けられ、一部または両端部にタブを溶接し、正極タブ5が形成されている。また、電体露出部を折り返すことにより、集電体の一端または両端に正極リードを設け、集電体の一部又は両極部にタブを溶接して正極タブとしてもよい。 For the positive electrode 1, a current collector exposed portion not coated with the positive electrode mixture paste is provided at one end of the positive electrode current collector, and tabs are welded to a part or both ends to form the positive electrode tab 5. . Alternatively, the positive electrode tab may be formed by folding a positive electrode exposed portion so that a positive electrode lead is provided at one or both ends of the current collector, and a tab is welded to a part or both electrode portions of the current collector.
負極3について、負極集電体の一部には負極合剤ペーストを塗布していない集電体露出部が設けられ、一部または両端部にタブを溶接し、負極タブ6が形成されている。また、集電体露出部を折り返すことにより、集電体の一端または両端に負極リードを設け、集電体の一部または両極部にタブを溶接して負極タブとしても良い。
As for the
電池缶4としては、リチウムイオン二次電池に一般的に使用されているものを使用することができる。例えば、鉄,ステンレススチール,アルミニウム等の金属缶を用いることが可能であるが、重量エネルギー密度の観点から、金属箔と樹脂フィルムの金属樹脂複合剤が好ましい。金属箔の例として、アルミニウム,鉄,ニッケル,銅,SUS,チタン,金,銀等、ピンホールのない箔であれば何れでもかまわないが、好ましくは軽量且つ安価なアルミニウム箔が好ましい。また、樹脂フィルムとしては外面にはポリエチレンテレフタレートフィルム,ナイロンフィルム等の突き刺し強度が優れた樹脂フィルムを、内面にはポリエチレンフィルム,ナイロンフィルム等の熱可塑性であって融着可能なフィルムが好ましい。耐溶剤性の観点からこのような樹脂フィルムの開口部を熱可塑性樹脂で封止することが望ましい。 As the battery can 4, what is generally used for a lithium ion secondary battery can be used. For example, metal cans such as iron, stainless steel, and aluminum can be used. From the viewpoint of weight energy density, a metal resin composite agent of metal foil and resin film is preferable. As an example of the metal foil, any foil such as aluminum, iron, nickel, copper, SUS, titanium, gold, silver, and the like that does not have a pinhole may be used, but a light and inexpensive aluminum foil is preferable. The resin film is preferably a resin film having excellent puncture strength such as a polyethylene terephthalate film or nylon film on the outer surface, and a thermoplastic and fusible film such as a polyethylene film or nylon film on the inner surface. From the viewpoint of solvent resistance, it is desirable to seal the opening of such a resin film with a thermoplastic resin.
前述の正極活物質は、以下の方法により電極として用いる正極と成すことができるが、これに限られたものではない。正極活物質,正極用導電助剤,正極用バインダ等を含む混合物に、溶剤を加えて十分に混練して得た正極合剤ペーストを、正極集電体の片面または両面に塗布し、乾燥した後、その正極合剤層を所定の厚さ及び所定の電極密度に制御し、正極とする。または、正極活物質と導電助剤のみを溶剤に分散し、集電体に蒸着するか、吹き付けるかして正極を作製することもできる。 The positive electrode active material described above can be formed as a positive electrode used as an electrode by the following method, but is not limited thereto. A positive electrode mixture paste obtained by sufficiently kneading and adding a solvent to a mixture containing a positive electrode active material, a positive electrode conductive additive, a positive electrode binder, etc. was applied to one or both sides of the positive electrode current collector and dried. Thereafter, the positive electrode material mixture layer is controlled to have a predetermined thickness and a predetermined electrode density, thereby forming a positive electrode. Alternatively, the positive electrode can also be produced by dispersing only the positive electrode active material and the conductive additive in a solvent and depositing or spraying on the current collector.
導電剤としては、電池性能に悪影響を及ぼさない電子伝導性材料であれば何でもよい。
通常、天然黒鉛(鱗状黒鉛,鱗片状黒鉛,土状黒鉛など),人造黒鉛,カーボンブラック,アセチレンブラック,ケッチェンブラック,カーボンウィスカー,炭素繊維や金属(銅,ニッケル,アルミニウム,銀,金など)粉,金属繊維,導電性セラミックス材料等の導電性材料を1種またはそれらの混合物として含ませることができる。これらの中で、導電性及び塗工性の観点よりアセチレンブラックが望ましい。その添加量は1〜50重量%が好ましく、特に2〜30重量%が好ましい。これらの混合方法は、物理的な混合であり、その理想とするところは均一混合である。そのため、V型混合機,S型混合機,擂かい機,ボールミル,遊星ボールミルといったような粉体混合機を乾式、あるいは湿式で混合することが可能である。
As the conductive agent, any electronic conductive material that does not adversely affect the battery performance may be used.
Usually, natural graphite (scale-like graphite, scale-like graphite, earth-like graphite, etc.), artificial graphite, carbon black, acetylene black, ketjen black, carbon whisker, carbon fiber and metal (copper, nickel, aluminum, silver, gold, etc.) Conductive materials such as powder, metal fibers, and conductive ceramic materials can be included as one type or a mixture thereof. Among these, acetylene black is desirable from the viewpoints of conductivity and coatability. The addition amount is preferably 1 to 50% by weight, particularly preferably 2 to 30% by weight. These mixing methods are physical mixing, and the ideal is uniform mixing. Therefore, powder mixers such as V-type mixers, S-type mixers, scrapers, ball mills, and planetary ball mills can be mixed dry or wet.
上記結着剤としては、リチウムイオン二次電池に一般的に使用されているものを使用することができる。結着剤としては通常、テトラフルオロエチレン,ポリフッ化ビニリデン,ポリエチレン,ポリプロピレン,エチレン−プロピレンジエンターポリマー(EPDM),スルホン化EPDM、スチレンブタジエンゴム(SBR),フッ素ゴム,カルボキシメチルセルロース等といった熱可塑性樹脂,ゴム弾性を有するポリマー,多糖類等を1種または2種以上の混合物として用いることができる。また、多糖類の様にリチウムと反応する官能基を有する結着剤は、例えばメチル化するなどしてその官能基を失活させておくことが望ましい。その添加量としては、1〜50重量%が好ましく、特に2〜30重量%が好ましい。 As said binder, what is generally used for the lithium ion secondary battery can be used. The binder is usually a thermoplastic resin such as tetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, ethylene-propylene diene terpolymer (EPDM), sulfonated EPDM, styrene butadiene rubber (SBR), fluorine rubber, carboxymethyl cellulose, etc. , Polymers having rubber elasticity, polysaccharides and the like can be used as one kind or a mixture of two or more kinds. In addition, it is desirable that a binder having a functional group that reacts with lithium, such as a polysaccharide, be deactivated by, for example, methylation. The addition amount is preferably 1 to 50% by weight, particularly preferably 2 to 30% by weight.
フィラーとして、電池性能に悪影響を及ぼさない材料であれば何でもよい。通常、ポリプロピレン,ポリエチレン等のオレフィン系ポリマー,エアロゲル,ゼオライト,ガラス,炭素等が用いられる。フィラーの添加量は0〜30重量%が好ましい。 Any material that does not adversely affect battery performance may be used as the filler. Usually, olefin polymers such as polypropylene and polyethylene, aerogel, zeolite, glass, carbon and the like are used. The amount of filler added is preferably 0 to 30% by weight.
さらに、高容量化を目的として、硫黄,セレン,テルルなどのカルコゲン元素を添加することも可能である。添加されたカルコゲン元素は電極材料が有するジスルフィド基のS−S結合に付加し、更なる充放電容量を与える。カルコゲン元素の添加量は0〜30重量%が好ましい。 Furthermore, chalcogen elements such as sulfur, selenium and tellurium can be added for the purpose of increasing the capacity. The added chalcogen element is added to the S—S bond of the disulfide group of the electrode material, and gives further charge / discharge capacity. The amount of chalcogen element added is preferably 0 to 30% by weight.
電気化学的活性物質の集電体としては、構成された電池において悪影響を及ぼさない電子伝導体であれば何でもよい。例えば、正極用集電体としては、アルミニウム,チタン,ステンレス鋼,ニッケル,焼成炭素,導電性高分子,導電性ガラス等の他に、接着性,導電性,耐酸化性向上の目的で、アルミニウムや銅等の表面をカーボン,ニッケル,チタンや銀等で処理した物を用いることができる。負極用集電体としては、銅,ニッケル,鉄,ステンレス鋼,チタン,アルミニウム,焼成炭素,導電性高分子,導電性ガラス,Al−Cd合金等の他に、接着性,導電性,耐酸化性向上の目的で、銅等の表面をカーボン,ニッケル,チタンや銀等で処理した物を用いることができる。これらの材料については表面を酸化処理することも可能である。これらの形状については、フォイル状の他、フィルム状,シート状,ネット状,パンチ又はエキスパンドされた物,ラス体,多孔質体,発泡体,繊維群の形成体等が用いられる。厚みは特に限定はないが、1〜500μmのものが用いられる。これらの集電体の中で、正極には耐酸化性に優れているアルミニウム箔が、負極には還元場において安定であり、且つ電導性に優れ、安価な銅箔,ニッケル箔,鉄箔、およびそれらの一部を含む合金箔が好ましい。さらに、電気化学的活性物質層と集電体との密着性が優れている粗面表面粗さが0.2μmRa以上の箔であることが望ましい。このような粗面を得る目的で電解箔は優れている。 The current collector of the electrochemically active substance may be any electronic conductor that does not adversely affect the battery constructed. For example, as a current collector for positive electrode, aluminum, titanium, stainless steel, nickel, baked carbon, conductive polymer, conductive glass, etc., in addition to aluminum for the purpose of improving adhesiveness, conductivity, and oxidation resistance. A material obtained by treating the surface of copper or copper with carbon, nickel, titanium, silver or the like can be used. In addition to copper, nickel, iron, stainless steel, titanium, aluminum, calcined carbon, conductive polymer, conductive glass, Al-Cd alloy, etc., the negative electrode current collector is adhesive, conductive, and oxidation resistant. For the purpose of improving the properties, a material obtained by treating the surface of copper or the like with carbon, nickel, titanium, silver or the like can be used. The surface of these materials can be oxidized. As for these shapes, in addition to the foil shape, a film shape, a sheet shape, a net shape, a punched or expanded material, a lath body, a porous body, a foamed body, a formed body of a fiber group, and the like are used. The thickness is not particularly limited, but a thickness of 1 to 500 μm is used. Among these current collectors, an aluminum foil having excellent oxidation resistance is used for the positive electrode, and a copper foil, nickel foil, iron foil, which is stable in a reduction field and has excellent conductivity, and is inexpensive for the negative electrode. And the alloy foil containing those parts is preferable. Furthermore, it is desirable that the surface of the rough surface having excellent adhesion between the electrochemically active material layer and the current collector has a surface roughness of 0.2 μmRa or more. The electrolytic foil is excellent for the purpose of obtaining such a rough surface.
セパレータ2としては、リチウムイオン二次電池に一般的に使用されているものを使用することができる。セパレータ2としては例えば、ポリオレフィン系,ポリエステル系,ポリアクリロニトリル系,ポリフェニレンサルファイド系,ポリイミド系、及びフッ素樹脂系の微孔膜や不織布を用いることが可能である。それらの中で、濡れ性の悪い微孔膜には界面活性剤等の処理を施すことが必要となる。
As the
上記セパレータの空孔率は強度の観点から98体積%以下が好ましい。また、充放電特性の観点から空孔率は20体積%以上が好ましい。 The porosity of the separator is preferably 98% by volume or less from the viewpoint of strength. Further, the porosity is preferably 20% by volume or more from the viewpoint of charge / discharge characteristics.
本発明に係る非水電解質電池に用いる非水電解質は、特に限定されるものではない。非水電解質の溶媒としては例えば、エチレンカーボネート,プロピレンカーボネート,ブチレンカーボネート,クロロエチレンカーボネート,ビニレンカーボネートなどの環状炭酸エステル;γ−ブチロラクトン,γ−バレロラクトンなどの環状エステル;ジメチルカーボネート,エチルメチルカーボネート,ジエチルカーボネートなどの鎖状炭酸エステル;酢酸メチル,酪酸メチルなどの鎖状エステル;テトラヒドロフランまたはその誘導体、1,3−ジオキサン、1,2−ジメトキシエタン、メチルジグライムなどのエーテル類;アセトニトリル,ベンゾニトリルなどのニトリル類;ジオキサランまたはその誘導体;スルホラン,スルトンまたはその誘導体を用いることができる。これらは単独または2種類以上の混合溶媒でも構わない。また、これら溶媒に塩として、LiClO4,LiBF4,LiAsF6,LiPF6,LiCF3SO3,LiC,F3CO2,LiSCN,LiBr,LiI,Li2SO4,Li2B10Cl10などのLi塩、NaClO4,NaI,NaSCN,NaBrなどのNa塩、KClO4,KSCNなどのK塩、LiN(CF3SO2)2,LiN(C2F5SO2)2,(CH3)4NBF4,(CH3)4NBr,(C2H5)4NClO4,(C2H5)4NI,(C3H7)4NBr,(n−C4H9)4NClO4,(n−C4H9)4NI,(C2H5)4N−maleate,(C2H5)4N−benzoate,(C2H5)4N−phthalateなどの四級アンモニウム塩,ステアリルスルホン酸リチウム,オクチルスルホン酸リチウム,ドデシルベンゼンスルホン酸リチウムなどの有機イオン塩等を用いることができる。これら塩は1種又は2種以上混合したもの等を用いることができる。 The nonaqueous electrolyte used for the nonaqueous electrolyte battery according to the present invention is not particularly limited. Examples of the nonaqueous electrolyte solvent include cyclic carbonates such as ethylene carbonate, propylene carbonate, butylene carbonate, chloroethylene carbonate, and vinylene carbonate; cyclic esters such as γ-butyrolactone and γ-valerolactone; dimethyl carbonate, ethyl methyl carbonate, Chain carbonate esters such as diethyl carbonate; chain esters such as methyl acetate and methyl butyrate; ethers such as tetrahydrofuran or derivatives thereof, 1,3-dioxane, 1,2-dimethoxyethane, methyl diglyme; acetonitrile, benzonitrile Nitriles such as: dioxalane or derivatives thereof; sulfolane, sultone or derivatives thereof can be used. These may be used alone or in combination of two or more. Moreover, as a salt in these solvents, LiClO 4 , LiBF 4 , LiAsF 6 , LiPF 6 , LiCF 3 SO 3 , LiC, F 3 CO 2 , LiSCN, LiBr, LiI, Li 2 SO 4 , Li 2 B 10 Cl 10, etc. Li salt, Na salt such as NaClO 4 , NaI, NaSCN, NaBr, K salt such as KClO 4 , KSCN, LiN (CF 3 SO 2 ) 2 , LiN (C 2 F 5 SO 2 ) 2 , (CH 3 ) 4 NBF 4 , (CH 3 ) 4 NBr, (C 2 H 5 ) 4 NClO 4 , (C 2 H 5 ) 4 NI, (C 3 H 7 ) 4 NBr, (n-C 4 H 9 ) 4 NClO 4 , (n-C 4 H 9 ) 4 NI, (C 2 H 5) 4 n-maleate, (C 2 H 5) 4 n-benzoate, quaternary ammonium salts such as (C 2 H 5) 4 n -phthalate , Lithium stearyl sulfonate, lithium octyl sulfonate, lithium dodecylbenzene sulfonate, etc. A machine ion salt or the like can be used. These salts can be used singly or as a mixture of two or more.
上記の非水電解質は、セパレータを挟み込み積層したり、巻き込んだりした後に電極間に注液することが可能である。注液法としては、常圧で注液することも可能であるが真空含浸方法や加圧含浸方法も可能である。 The non-aqueous electrolyte can be injected between the electrodes after the separator is sandwiched and stacked or wound. As an injection method, it is possible to inject at normal pressure, but a vacuum impregnation method and a pressure impregnation method are also possible.
非水電解質として、イオン液体やリチウム伝導性の固体電解質(−20〜60℃にあって固体あるいは固形状である)を用いることもできる。この固体電解質は上記有機イオン塩等を含む高分子で構成される。これらを含む高分子電解質としては、該リチウム塩を溶解させたポリエチレンオキサイド誘導体か少なくとも該誘導体を含むポリマー,ポリプロピレンオキサイド誘導体か少なくとも該誘導体を含むポリマー,ポリフォスファゼンや該誘導体,イオン解離基を含むポリマー,リン酸エステルポリマー誘導体、さらにポリビニルピリジン誘導体,ビスフェノールA誘導体,ポリアクリロニトリル,ポリビニリデンフルオライド,フッ素ゴム等に非水電解液を含有させた高分子マトリックス材料(ゲル電解質)及び無機固体電解質等のイオン伝導性化合物からなるものが用いられる。 As the non-aqueous electrolyte, an ionic liquid or a lithium conductive solid electrolyte (at 20 to 60 ° C., which is solid or solid) can be used. This solid electrolyte is composed of a polymer containing the organic ion salt or the like. The polyelectrolyte containing these includes a polyethylene oxide derivative in which the lithium salt is dissolved or a polymer containing at least the derivative, a polypropylene oxide derivative or a polymer containing at least the derivative, polyphosphazene or the derivative, and an ion dissociation group Polymer matrix materials (gel electrolytes) and inorganic solid electrolytes containing non-aqueous electrolytes in polymers, phosphate ester polymer derivatives, polyvinyl pyridine derivatives, bisphenol A derivatives, polyacrylonitrile, polyvinylidene fluoride, fluororubber, etc. Those composed of an ion conductive compound are used.
以下、実施例および比較例を用いて本発明をより詳細に説明するが、本発明の技術的範囲はこれにより限定されるものではない。 EXAMPLES Hereinafter, although this invention is demonstrated in detail using an Example and a comparative example, the technical scope of this invention is not limited by this.
〔実施例1〕
二酸化マンガン(MnO2),水酸化リチウム(LiOH)及び酸化アルミニウム(Al2O3)を混合し、空気中にて700℃で10hr加熱して、正極活物質Li1.1Mn1.8Al0.1O4を得た。この正極活物質92質量%と導電材としてのアセチレンブラック3質量%とPVDF(結着剤)のNMP溶液(固形分比12質量%)5質量%とを混合して正極合剤を作製した。この正極合剤を厚み20μmのアルミニウム箔に塗布した後、80℃で乾燥した。その後150℃で真空乾燥した後、合剤層の多孔質度が35%となるようにプレスし、φ16に打ち抜き、正極とした。
[Example 1]
Manganese dioxide (MnO 2 ), lithium hydroxide (LiOH) and aluminum oxide (Al 2 O 3 ) are mixed and heated in air at 700 ° C. for 10 hours to obtain positive electrode active material Li 1.1 Mn 1.8 Al 0.1 O 4 . Obtained. 92% by mass of this positive electrode active material, 3% by mass of acetylene black as a conductive material, and 5% by mass of an NMP solution (solid content ratio 12% by mass) of PVDF (binder) were mixed to prepare a positive electrode mixture. This positive electrode mixture was applied to an aluminum foil having a thickness of 20 μm, and then dried at 80 ° C. After vacuum drying at 150 ° C., the mixture layer was pressed so that the porosity of the mixture layer was 35%, punched out to φ16, and used as a positive electrode.
二酸化チタン(TiO2)と水酸化リチウム(LiOH)とを混合した後、空気中にて600℃で15hr加熱して、負極活物質Li4Ti5O12を得た。 Titanium dioxide (TiO 2 ) and lithium hydroxide (LiOH) were mixed and then heated in air at 600 ° C. for 15 hours to obtain a negative electrode active material Li 4 Ti 5 O 12 .
この負極活物質86.991質量%と金属化合物添加物としてK2SO4を0.009%、導電材としてのアセチレンブラック5質量%とPVDF(結着剤)のNMP溶液(固形分比13質量%)8質量%とを混合して負極合剤を作製した。この負極合剤を厚み10μmの銅箔に塗布した後、80℃で乾燥した。その後150℃で真空乾燥した後、合剤層の多孔度が35%となるようにプレス後、φ16に打ち抜き、負極とした。 The anode active material 86.991 wt% 0.009% to K 2 SO 4 as the metal compound additives, NMP solution (solid content ratio 13 mass 5 wt% of acetylene black as a conductive material and PVDF (binder) %) 8% by mass was mixed to prepare a negative electrode mixture. This negative electrode mixture was applied to a copper foil having a thickness of 10 μm, and then dried at 80 ° C. After vacuum drying at 150 ° C., the mixture layer was pressed so that the porosity of the mixture layer was 35%, and then punched out to φ16 to obtain a negative electrode.
つぎに、LiPF6をエチレンカーボネート(EC)とジエチルカーボネート(DEC)の体積比3:7混合溶媒に溶解した非水処理液を作製し、電解液とした。ここで、添加物として2.5−ジメチル−1.5−ヘキサジエンをLiPF6及び溶媒の5重量%投入し、撹拌した後、電解液とした。 Next, a non-aqueous treatment solution in which LiPF 6 was dissolved in a mixed solvent of ethylene carbonate (EC) and diethyl carbonate (DEC) in a volume ratio of 3: 7 was prepared and used as an electrolytic solution. Here, as an additive, 2.5-dimethyl-1.5-hexadiene was added in 5% by weight of LiPF 6 and a solvent, and the mixture was stirred and used as an electrolytic solution.
電池は図3に示されるような捲回型電池として作製した。その中に準備した正極及び負極を厚さ25μmのポリエチレンセパレータを挟み相対するように巻き取り、電池缶に挿入し、電解液を注入し電池とした。 The battery was fabricated as a wound battery as shown in FIG. The positive electrode and the negative electrode prepared therein were wound up so as to face each other with a polyethylene separator having a thickness of 25 μm interposed therebetween, inserted into a battery can, and an electrolyte solution was injected to obtain a battery.
<添加物の金属増加率>
上記のように作製した電池は、電流密度0.5mA/cm2の定電流で、充電電圧3V,放電電圧1Vで3サイクル充放電を行い、初期充放電試験電池とした。また、同様の作製方法,測定方法で3000サイクル目放電が終わった電池と、先ほどの充放電試験電池を解体し、負極を取り出して、負極におけるマンガンの存在をICPにて確認、また添加物とした金属化合物の金属の量を初期充放電試験電池の負極と、サイクル試験後の電池とで比較し、その増加率を求めた。
<Metal increase rate of additive>
The battery produced as described above was subjected to charge and discharge for 3 cycles at a constant current of 0.5 mA / cm 2 and a charge voltage of 3 V and a discharge voltage of 1 V, to obtain an initial charge / discharge test battery. Also, the battery after the 3000th cycle discharge by the same production method and measurement method and the previous charge / discharge test battery were disassembled, the negative electrode was taken out, and the presence of manganese in the negative electrode was confirmed by ICP. The amount of the metal of the obtained metal compound was compared between the negative electrode of the initial charge / discharge test battery and the battery after the cycle test, and the increase rate was determined.
<抵抗上昇率>
抵抗を測定する試験を次のように行った。上記で初期充放電試験電池の負極と、3000サイクル試験後の負極において、対極リチウムの条件において、25℃で0.5mA/cm2の定電流で1Vまで充電し、それぞれインピーダンス測定を行った。インピーダンス測定は、0.01〜5000Hzの範囲において振幅10mVで行った。図4におけるコール・コールプロットにおいて、初期充放電試験電池の負極を1Vまで充電した時のインピーダンスプロットの半円のZ′値をR1とし、サイクル試験後のZ′値をR2とし、抵抗上昇率を次のように求めた。
<Rate of increase in resistance>
A test for measuring resistance was performed as follows. The negative electrode of the initial charge / discharge test battery and the negative electrode after the 3000 cycle test were charged to 1 V at a constant current of 0.5 mA / cm 2 at 25 ° C. under the condition of counter lithium, and the impedance was measured. The impedance measurement was performed at an amplitude of 10 mV in the range of 0.01 to 5000 Hz. In the Cole-Cole plot in FIG. 4, the Z ′ value of the semicircle of the impedance plot when the negative electrode of the initial charge / discharge test battery is charged to 1 V is R1, the Z ′ value after the cycle test is R2, and the resistance increase rate Was determined as follows.
抵抗上昇率(%)=R2/R1×100−(1) Resistance increase rate (%) = R2 / R1 × 100− (1)
〔実施例2〕
負極合剤を作製する際、負極合剤の混合比を負極活物質86.98質量%と添加物としてK2SO4を0.02%、導電材としてのアセチレンブラック5質量%とPVDF(結着剤)のNMP溶液(固形分比13質量%)8質量%としたほかは実施例1と同様に作製,測定を行った。
[Example 2]
When preparing the negative electrode mixture, the mixing ratio of the negative electrode mixture was 86.98% by mass of the negative electrode active material, 0.02% of K 2 SO 4 as an additive, 5% by mass of acetylene black as a conductive material, and PVDF (condensation). This was prepared and measured in the same manner as in Example 1 except that the NMP solution (solid content ratio: 13% by mass) was 8% by mass.
〔実施例3〕
負極合剤を作製する際、負極合剤の混合比を負極活物質82質量%と添加物としてK2SO4を5%、導電材としてのアセチレンブラック5質量%とPVDF(結着剤)のNMP溶液(固形分比13質量%)8質量%としたほかは実施例1と同様に作製,測定を行った。
Example 3
When preparing the negative electrode mixture, the mixing ratio of the negative electrode mixture was 82% by mass of the negative electrode active material, 5% of K 2 SO 4 as an additive, 5% by mass of acetylene black as a conductive material, and PVDF (binder). It was produced and measured in the same manner as in Example 1 except that the NMP solution (solid content ratio 13% by mass) was 8% by mass.
〔実施例4〕
負極合剤を作製する際、負極合剤の混合比を負極活物質80質量%と添加物としてK2SO4を7%、導電材としてのアセチレンブラック5質量%とPVDF(結着剤)のNMP溶液(固形分比13質量%)8質量%としたほかは実施例1と同様に作製,測定を行った。
Example 4
When preparing the negative electrode mixture, the mixing ratio of the negative electrode mixture was 80% by mass of the negative electrode active material, 7% of K 2 SO 4 as an additive, 5% by mass of acetylene black as a conductive material, and PVDF (binder). It was produced and measured in the same manner as in Example 1 except that the NMP solution (solid content ratio 13% by mass) was 8% by mass.
〔実施例5〜8〕
負極合剤を作製する際、添加物としてCaCO3を用いたほかは、実施例1〜4と同様に作製,測定を行った。
[Examples 5 to 8]
When preparing the negative electrode mixture, preparation and measurement were performed in the same manner as in Examples 1 to 4 except that CaCO 3 was used as an additive.
〔実施例9〜12〕
負極合剤を作製する際、添加物としてBaCO3を用いたほかは、実施例1〜4と同様に作製,測定を行った。
[Examples 9 to 12]
When producing the negative electrode mixture, production and measurement were performed in the same manner as in Examples 1 to 4 except that BaCO 3 was used as an additive.
〔比較例1〕
負極合剤の作製において、アルミナをセパレータ中に添加物として添加した。
[Comparative Example 1]
In preparation of the negative electrode mixture, alumina was added as an additive in the separator.
セパレータとしてPP繊維からなる厚み30μmの不織布を用い、この中にアルミナを加えた。アルミナは負極活物質とアルミナの合計質量に対して0.5質量%となるように加えた。測定は実施例1と同様に行った。 A 30 μm-thick nonwoven fabric made of PP fibers was used as a separator, and alumina was added thereto. The alumina was added so that it might become 0.5 mass% with respect to the total mass of a negative electrode active material and an alumina. The measurement was performed in the same manner as in Example 1.
〔比較例2〕
負極合剤の作製において、実施例1から添加物を除いた負極合剤を作製し、負極を作製した。
[Comparative Example 2]
In the preparation of the negative electrode mixture, a negative electrode mixture was prepared by removing the additive from Example 1, and a negative electrode was prepared.
また、正極活物質にスピネルLiMn2O4を用いた。その他は実施例1と同様に作製,測定を行った。 Further, spinel LiMn 2 O 4 was used as the positive electrode active material. Others were produced and measured in the same manner as in Example 1.
実施例1〜12いずれの場合においても従来技術である比較例1,2と比べ抵抗上昇率が低い値を示している。添加物量が負極活物質の質量aと、添加物の質量bの合計質量a+bに対して0.01〜8.05質量%のすべての範囲で効果が得られる。これは添加物が電池の抵抗増加を抑えていることを示す。 In any of Examples 1 to 12, the resistance increase rate is lower than those of Comparative Examples 1 and 2 as the prior art. The effect is obtained when the additive amount is in a range of 0.01 to 8.05 mass% with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive. This indicates that the additive suppresses the increase in battery resistance.
また、添加物の金属増加率は添加物の増加に伴い増している。これは添加物がマンガンを捕捉していることを示す。また、抵抗上昇率は添加物の増加に伴い下降し、ある添加物濃度を超えると、上昇に転じることがわかる。これは添加物の割合が多い場合、添加物が電気抵抗として働き、抵抗上昇率の値は大きくなると考えられる。 Moreover, the metal increase rate of an additive is increasing with the increase in an additive. This indicates that the additive has captured manganese. It can also be seen that the rate of increase in resistance decreases with an increase in the additive, and starts to increase when a certain additive concentration is exceeded. This is considered that when the ratio of the additive is large, the additive acts as an electric resistance, and the value of the resistance increase rate is increased.
抵抗上昇率を最も低く抑えられた添加物濃度は、負極活物質と添加物の合計質量に対して添加物K2SO4を5.56質量%で用いた実施例であった。しかし、添加物の金属増加率が最も高かったのは、CaCO3である。このことから、濃度をさらに最適化することによりさらに効果を挙げられる可能性がある。 The additive concentration at which the rate of increase in resistance was minimized was an example in which the additive K 2 SO 4 was used at 5.56% by mass with respect to the total mass of the negative electrode active material and the additive. However, CaCO 3 has the highest metal increase rate of the additive. From this, there is a possibility that further effects can be obtained by further optimizing the concentration.
電気陰性度が1.5よりも高い元素のみからなる化合物を添加物として用い、比較例とした。電気陰性度が1.5よりも高い元素のみからなる化合物としては、Sb2S3,GaNを用いた。 A compound consisting only of an element having an electronegativity higher than 1.5 was used as an additive as a comparative example. Sb 2 S 3 , GaN was used as a compound consisting only of elements having an electronegativity higher than 1.5.
〔比較例3〕
電極を作製する際、電極合剤の混合比を負極活物質82質量%と、添加物としてSb2S3を5%、導電材としてのアセチレンブラック5質量%と、PVDF(結着剤)のNMP溶液(固形分比13質量%)8質量%入れたほかは、実施例1と同様に作製,測定を行った。
[Comparative Example 3]
When preparing the electrode, the mixing ratio of the electrode mixture was 82% by mass of the negative electrode active material, 5% of Sb 2 S 3 as an additive, 5% by mass of acetylene black as a conductive material, and PVDF (binder). Production and measurement were performed in the same manner as in Example 1 except that 8% by mass of NMP solution (solid content ratio: 13% by mass) was added.
〔比較例4〕
負極合剤を作製する際、添加物としてGaNを用いたほかは、比較例3と同様に作製,測定を行った。
[Comparative Example 4]
The negative electrode mixture was prepared and measured in the same manner as in Comparative Example 3 except that GaN was used as an additive.
添加物の添加濃度が等しい比較例3,4と実施例3,7,11を比較した(表2)。実施例3,7,11はいずれも比較例3,4よりも金属増加量が大きく、抵抗上昇率が低く抑えられている。これはK2SO4,CaCO3,BaCO3がマンガンより電気陰性度が低いという性質によりマンガンを捕捉していることを示している。 Comparative Examples 3 and 4 having the same additive concentration were compared with Examples 3, 7 and 11 (Table 2). In Examples 3, 7, and 11, the amount of increase in metal is larger than that in Comparative Examples 3 and 4, and the rate of increase in resistance is kept low. This indicates that K 2 SO 4 , CaCO 3 , and BaCO 3 capture manganese due to the property that it has a lower electronegativity than manganese.
次に添加物の添加様式を「負極活物質粒子表面にコーティングされた状態」とした実施例を示す。 Next, an example in which the additive is added in the “coated state on the negative electrode active material particle surface” will be described.
〔実施例13〕
電極を作製する際、電極合剤の混合比を負極活物質86.95質量%と添加物K2SO4を0.05%とし、添加物はメカノケミカル法により予め負極活物質表面にコーティングしたほかは、実施例1と同様に作製,測定を行った。
Example 13
When producing the electrode, the mixing ratio of the electrode mixture was 86.95% by mass of the negative electrode active material and 0.05% of the additive K 2 SO 4 , and the additive was coated on the surface of the negative electrode active material in advance by a mechanochemical method. Others were produced and measured in the same manner as in Example 1.
〔実施例14〕
電極を作製する際、電極合剤の混合比を負極活物質86質量%と添加物K2SO4を1%としたほかは、実施例13と同様に作製,測定を行った。
Example 14
The electrode was prepared and measured in the same manner as in Example 13 except that the mixing ratio of the electrode mixture was 86% by mass of the negative electrode active material and 1% of the additive K 2 SO 4 .
〔実施例15〕
電極を作製する際、電極合剤の混合比を負極活物質82質量%と添加物K2SO4を5%としたほかは、実施例13と同様に作製,測定を行った。
Example 15
The electrode was prepared and measured in the same manner as in Example 13 except that the mixing ratio of the electrode mixture was 82% by mass of the negative electrode active material and 5% of the additive K 2 SO 4 .
〔実施例16〕
電極を作製する際、電極合剤の混合比を負極活物質80質量%と添加物K2SO4を7%としたほかは、実施例13と同様に作製,測定を行った。
Example 16
The electrode was prepared and measured in the same manner as in Example 13 except that the mixing ratio of the electrode mixture was 80% by mass of the negative electrode active material and 7% of the additive K 2 SO 4 .
〔実施例17〜20〕
負極合剤を作製する際、添加物としてCaCO3を用いたほかは、実施例13〜16と同様に作製,測定を行った。
[Examples 17 to 20]
Making the negative electrode mixture, except using CaCO 3 as an additive, manufactured in the same manner as in Example 13 to 16 were measured.
〔実施例21〜24〕
負極合剤を作製する際、添加物としてBaCO3を用いたほかは、実施例17〜20と同様に作製,測定を行った。
[Examples 21 to 24]
When producing the negative electrode mixture, production and measurement were performed in the same manner as in Examples 17 to 20 except that BaCO 3 was used as an additive.
実施例13〜24いずれの場合においても従来技術である比較例3,4と比べ抵抗上昇率が低い値を示している。これは添加物が電池の抵抗増加を抑えていることを示しており、添加物の添加様式は「負極活物質表面にコーティングされた状態」で効果を発揮することを示す。添加物の量は、負極活物質の質量aと、添加物の質量bの合計質量a+bに対して0.06〜8.05質量%の範囲で効果が得られることが分かった。また、添加物の金属増加率は添加物の増加に伴い増している。これは添加物がマンガンを捕捉していることを示す。また、抵抗上昇率は添加物の増加に伴い下降し、ある添加物濃度を超えると、上昇に転じることがわかる。これは添加物の割合が多い場合、添加物が電気抵抗として働き、抵抗上昇率の値は大きくなると考えられる。抵抗上昇率を最も低く抑えられた添加物濃度は負極活物質と添加物の合計質量に対して添加物K2SO4を5.75質量%で用いた実施例であった。 In any of Examples 13 to 24, the resistance increase rate is lower than those of Comparative Examples 3 and 4 which are the prior art. This indicates that the additive suppresses an increase in the resistance of the battery, and the additive addition mode exhibits the effect in the “coated state on the negative electrode active material surface”. The amount of the additive was found to be effective in the range of 0.06 to 8.05% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive. Moreover, the metal increase rate of an additive is increasing with the increase in an additive. This indicates that the additive has captured manganese. It can also be seen that the rate of increase in resistance decreases with an increase in the additive, and starts to increase when a certain additive concentration is exceeded. This is considered that when the ratio of the additive is large, the additive acts as an electric resistance, and the value of the resistance increase rate is increased. The additive concentration at which the rate of increase in resistance was minimized was an example in which the additive K 2 SO 4 was used at 5.75 mass% with respect to the total mass of the negative electrode active material and the additive.
しかし、マンガンを最も効率よく捕捉した添加物はCaCO3である。このことから、濃度をさらに最適化することにより、さらに効果を挙げられる可能性がある。 However, the additive that traps manganese most efficiently is CaCO 3 . For this reason, further optimization can be achieved by further optimizing the concentration.
電気陰性度が1.5よりも高い元素のみからなる化合物を添加物として用い、比較例とした。電気陰性度が1.5よりも高い元素のみからなる化合物としては、Sb2S3,GaNを用いた。 A compound consisting only of an element having an electronegativity higher than 1.5 was used as an additive as a comparative example. Sb 2 S 3 , GaN was used as a compound consisting only of elements having an electronegativity higher than 1.5.
〔比較例5〕
電極を作製する際、添加物としてSb2S3を用い、負極合剤の混合比を負極活物質82質量%と添加物を5%としたほかは、実施例13と同様に作製,測定を行った。
[Comparative Example 5]
When preparing the electrode, Sb 2 S 3 was used as an additive, and the mixing ratio of the negative electrode mixture was changed to 82% by mass of the negative electrode active material and 5% of the additive. went.
〔比較例6〕
負極合剤を作製する際、添加物としてGaNを用いたほかは、比較例5と同様に作製,測定を行った。
[Comparative Example 6]
The negative electrode mixture was prepared and measured in the same manner as in Comparative Example 5, except that GaN was used as an additive.
添加物の添加濃度が等しい比較例5,6と実施例15,19,23を比較した(表4)。実施例15,19,23はいずれも比較例5,6よりも金属増加量が大きく、抵抗上昇率が低く抑えられている。これはK2SO4,CaCO3,BaCO3がマンガンより電気陰性度が低いという性質によりマンガンを捕捉していることを示している。 Comparative Examples 5 and 6 having the same additive concentration were compared with Examples 15, 19, and 23 (Table 4). In Examples 15, 19, and 23, the amount of increase in metal is larger than that in Comparative Examples 5 and 6, and the rate of increase in resistance is kept low. This indicates that K 2 SO 4 , CaCO 3 , and BaCO 3 capture manganese due to the property that it has a lower electronegativity than manganese.
次に添加物の添加様式を「負極表面にコーティングされた状態」とした実施例を示す。 Next, an example in which the additive is added in the “coated state on the negative electrode surface” will be described.
〔実施例25〕
添加物を含まない負極を実施例1と同様の方法により作製した後、エタノールに分散させた添加物K2SO4を負極上にスプレーとして吹き付けた。なお、最終的な材料質量比は負極活物質が86.75質量%、添加物K2SO4が0.25%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 25
A negative electrode containing no additive was produced in the same manner as in Example 1, and then the additive K 2 SO 4 dispersed in ethanol was sprayed on the negative electrode as a spray. The final material mass ratio is 86.75% by mass for the negative electrode active material, 0.25% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% for PVDF (binder). It was prepared by adjusting to be%. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例26〕
添加物を含まない負極を実施例1と同様の方法により作製した後、エタノールに分散させた添加物K2SO4を負極上にスプレーとして吹き付けた。なお、最終的な材料質量比は負極活物質が86.5質量%、添加物K2SO4が0.5%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 26
A negative electrode containing no additive was produced in the same manner as in Example 1, and then the additive K 2 SO 4 dispersed in ethanol was sprayed on the negative electrode as a spray. The final material mass ratio was 86.5% by mass for the negative electrode active material, 0.5% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% for PVDF (binder). It was prepared by adjusting to be%. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例27〕
添加物を含まない負極を実施例1と同様の方法により作製した後、エタノールに分散させた添加物K2SO4を負極上にスプレーとして吹き付けた。なお、最終的な材料質量比は負極活物質が82質量%、添加物K2SO4が5%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 27
A negative electrode containing no additive was produced in the same manner as in Example 1, and then the additive K 2 SO 4 dispersed in ethanol was sprayed on the negative electrode as a spray. The final material mass ratio is 82% by mass for the negative electrode active material, 5% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). It was prepared by adjusting to. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例28〕
添加物を含まない負極を実施例1と同様の方法により作製した後、エタノールに分散させた添加物K2SO4を負極上にスプレーとして吹き付けた。なお、最終的な材料質量比は負極活物質が77質量%、添加物K2SO4が10%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 28
A negative electrode containing no additive was produced in the same manner as in Example 1, and then the additive K 2 SO 4 dispersed in ethanol was sprayed on the negative electrode as a spray. The final material mass ratio is 77% by mass for the negative electrode active material, 10% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). It was prepared by adjusting to. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例29〕
添加物を含まない負極を実施例1と同様の方法により作製した後、エタノールに分散させた添加物K2SO4を負極上にスプレーとして吹き付けた。なお、最終的な材料質量比は負極活物質が75質量%、添加物K2SO4が12%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 29
A negative electrode containing no additive was produced in the same manner as in Example 1, and then the additive K 2 SO 4 dispersed in ethanol was sprayed on the negative electrode as a spray. The final material mass ratio is 75% by mass for the negative electrode active material, 12% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). It was prepared by adjusting to. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例30〜34〕
添加物としてCaCO3を用いたほかは、実施例25〜29と同様に作製,測定を行った。
[Examples 30 to 34]
Except for using CaCO 3 as an additive, preparation and measurement were performed in the same manner as in Examples 25-29.
〔実施例35〜39〕
添加物としてBaCO3を用いたほかは、実施例25〜29と同様に作製,測定を行った。
[Examples 35-39]
Fabrication and measurement were performed in the same manner as in Examples 25 to 29 except that BaCO 3 was used as an additive.
実施例25〜39いずれの場合においても従来技術である比較例1,2と比べ抵抗上昇率が低い値を示している。これは添加物が電池の抵抗増加を抑えていることを示しており、添加物の添加様式は「負極表面にコーティングされた状態」で効果を発揮することを示す。添加物の量は、負極活物質の質量aと、前記添加物の質量bの合計質量a+bに対して0.29〜13.8質量%の範囲で効果が得られることが分かった。 In any of Examples 25 to 39, the resistance increase rate is lower than those of Comparative Examples 1 and 2 which are the prior art. This indicates that the additive suppresses the increase in resistance of the battery, and the additive addition mode exhibits the effect in the “state coated on the negative electrode surface”. The amount of the additive was found to be effective in the range of 0.29 to 13.8% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive.
また、添加物の金属増加率は添加物の増加に伴い増している。これは添加物がマンガンを捕捉していることを示す。また、抵抗上昇率は添加物の増加に伴い下降し、ある添加物濃度を超えると、上昇に転じることがわかる。これは添加物の割合が多い場合、添加物が電気抵抗として働き、抵抗上昇率の値は大きくなると考えられる。抵抗上昇率を最も低く抑えられた添加物濃度は負極活物質と添加物の合計質量に対して添加物K2SO4を5.56質量%で用いた実施例であった。 Moreover, the metal increase rate of an additive is increasing with the increase in an additive. This indicates that the additive has captured manganese. It can also be seen that the rate of increase in resistance decreases with an increase in the additive, and starts to increase when a certain additive concentration is exceeded. This is considered that when the ratio of the additive is large, the additive acts as an electric resistance, and the value of the resistance increase rate is increased. The additive concentration at which the rate of increase in resistance was minimized was an example in which the additive K 2 SO 4 was used at 5.56% by mass with respect to the total mass of the negative electrode active material and the additive.
しかし、マンガンを最も効率よく捕捉した添加物はBaCO3である。このことから、濃度をさらに最適化することによりさらに効果を挙げられる可能性がある。 However, the additive that most efficiently captures manganese is BaCO 3 . From this, there is a possibility that further effects can be obtained by further optimizing the concentration.
電気陰性度が1.5よりも高い元素のみからなる化合物を添加物として用い、比較例とした。電気陰性度が1.5よりも高い元素のみからなる化合物としては、Sb2S3,GaNを用いた。 A compound consisting only of an element having an electronegativity higher than 1.5 was used as an additive as a comparative example. Sb 2 S 3 , GaN was used as a compound consisting only of elements having an electronegativity higher than 1.5.
〔比較例7〕
添加物としてSb2S3を用いたこと以外は実施例25と同様に作製,測定を行った。なお、最終的な材料比は負極活物質が82質量%、添加物Sb2S3が5%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節した。
[Comparative Example 7]
Fabrication and measurement were performed in the same manner as in Example 25 except that Sb 2 S 3 was used as an additive. The final material ratio is 82% by mass for the negative electrode active material, 5% for the additive Sb 2 S 3 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). Adjusted.
〔比較例8〕
添加物としてGaNを用いたほかは、比較例7と同様に作製,測定を行った。
[Comparative Example 8]
Fabrication and measurement were performed in the same manner as in Comparative Example 7, except that GaN was used as an additive.
添加物の添加濃度が等しい比較例7,8と実施例27,32,37を比較した(表6)。実施例27,32,37はいずれも比較例7,8よりも金属増加量が大きく、抵抗上昇率が低く抑えられている。これはK2SO4,CaCO3,BaCO3がマンガンより電気陰性度が低いという性質によりマンガンを捕捉していることを示している。 Comparative Examples 7 and 8 having the same additive concentration were compared with Examples 27, 32 and 37 (Table 6). In Examples 27, 32, and 37, the amount of increase in metal is larger than that in Comparative Examples 7 and 8, and the rate of increase in resistance is kept low. This indicates that K 2 SO 4 , CaCO 3 , and BaCO 3 capture manganese due to the property that it has a lower electronegativity than manganese.
次に添加物の添加様式を「セパレータ表面上に存在する状態」とした実施例を示す。 Next, an example in which the additive is added in a “state existing on the separator surface” will be described.
〔実施例40〕
添加物を含まない負極を実施例1と同様の方法により作製した。添加物K2SO4をアセトンに分散させたコーティング剤をセパレータにスプレーし、セパレータを25℃で30分放置後、40℃で3時間真空乾燥させた。なお、材料比は最終的に、負極活物質が86.6質量%、添加物K2SO4が0.4%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 40
A negative electrode containing no additive was produced in the same manner as in Example 1. A coating agent in which the additive K 2 SO 4 was dispersed in acetone was sprayed on the separator, and the separator was left at 25 ° C. for 30 minutes and then vacuum-dried at 40 ° C. for 3 hours. The material ratio was 86.6% by mass for the negative electrode active material, 0.4% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% for PVDF (binder). It was prepared by adjusting to be%. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例41〕
添加物を含まない負極を実施例1と同様の方法により作製した。添加物K2SO4をアセトンに分散させたコーティング剤をセパレータにスプレーし、セパレータを25℃で30分放置後、40℃で3時間真空乾燥させた。なお、材料比は最終的に、負極活物質が86.5質量%、添加物K2SO4が0.5%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 41
A negative electrode containing no additive was produced in the same manner as in Example 1. A coating agent in which the additive K 2 SO 4 was dispersed in acetone was sprayed on the separator, and the separator was left at 25 ° C. for 30 minutes and then vacuum-dried at 40 ° C. for 3 hours. The material ratio was 86.5% by mass for the negative electrode active material, 0.5% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% for PVDF (binder). It was prepared by adjusting to be%. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例42〕
添加物を含まない負極を実施例1と同様の方法により作製した。添加物K2SO4をアセトンに分散させたコーティング剤をセパレータにスプレーし、セパレータを25℃で30分放置後、40℃で3時間真空乾燥させた。なお、材料比は最終的に、負極活物質が77質量%、添加物K2SO4が10%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 42
A negative electrode containing no additive was produced in the same manner as in Example 1. A coating agent in which the additive K 2 SO 4 was dispersed in acetone was sprayed on the separator, and the separator was left at 25 ° C. for 30 minutes and then vacuum-dried at 40 ° C. for 3 hours. The final material ratio is 77% by mass for the negative electrode active material, 10% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). It was prepared by adjusting to. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例43〕
添加物を含まない負極を実施例1と同様の方法により作製した。添加物K2SO4をアセトンに分散させたコーティング剤をセパレータにスプレーし、セパレータを25℃で30分放置後、40℃で3時間真空乾燥させた。なお、材料比は最終的に、負極活物質が67質量%、添加物K2SO4が20%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節して作製した。それ以外は実施例1と同様に作製,測定を行った。
Example 43
A negative electrode containing no additive was produced in the same manner as in Example 1. A coating agent in which the additive K 2 SO 4 was dispersed in acetone was sprayed on the separator, and the separator was left at 25 ° C. for 30 minutes and then vacuum-dried at 40 ° C. for 3 hours. The final material ratio is 67% by mass for the negative electrode active material, 20% for the additive K 2 SO 4 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). It was prepared by adjusting to. Other than that, it produced and measured similarly to Example 1. FIG.
〔実施例44〜47〕
添加物としてCaCO3を用いたほかは、実施例40〜51と同様に作製,測定を行った。
[Examples 44 to 47]
Production and measurement were performed in the same manner as in Examples 40 to 51 except that CaCO 3 was used as an additive.
〔実施例48〜51〕
添加物としてBaCO3を用いたほかは、実施例40〜51と同様に作製,測定を行った。
[Examples 48 to 51]
Production and measurement were performed in the same manner as in Examples 40 to 51 except that BaCO 3 was used as an additive.
実施例40〜51いずれの場合においても従来技術である比較例1,2と比べ抵抗上昇率が低い値を示している。これは添加物が電池の抵抗増加を抑えていることを示しており、添加物の添加様式は「セパレータ表面上に存在する状態」で効果を発揮することを示す。添加物の量は、負極活物質の質量aと、添加物の質量bの合計質量a+bに対して0.46〜23.0質量%の範囲で効果が得られることが分かった。 In any of Examples 40 to 51, the resistance increase rate is lower than that of Comparative Examples 1 and 2 which are the prior art. This indicates that the additive suppresses an increase in the resistance of the battery, and the addition mode of the additive exhibits an effect in the “state existing on the separator surface”. The amount of the additive was found to be effective in the range of 0.46 to 23.0% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive.
また、添加物の金属増加率は添加物の増加に伴い増している。これは添加物がマンガンを捕捉していることを示す。また、抵抗上昇率は添加物の増加に伴い下降し、ある添加物濃度を超えると、上昇に転じることがわかる。これは添加物の割合が多い場合、添加物が電気抵抗として働き、抵抗上昇率の値は大きくなると考えられる。 Moreover, the metal increase rate of an additive is increasing with the increase in an additive. This indicates that the additive has captured manganese. It can also be seen that the rate of increase in resistance decreases with an increase in the additive, and starts to increase when a certain additive concentration is exceeded. This is considered that when the ratio of the additive is large, the additive acts as an electric resistance, and the value of the resistance increase rate is increased.
抵抗上昇率を最も低く抑えられた添加物濃度は負極活物質と添加物の合計質量に対して添加物CaCO3を11.1質量%で用いた実施例であった。しかし、マンガンを最も効率よく捕捉した添加物はBaCO3である。このことから、濃度をさらに最適化することによりさらに効果を挙げられる可能性がある。 The additive concentration at which the rate of increase in resistance was minimized was an example in which the additive CaCO 3 was used at 11.1% by mass relative to the total mass of the negative electrode active material and the additive. However, the additive that most efficiently captures manganese is BaCO 3 . From this, there is a possibility that further effects can be obtained by further optimizing the concentration.
電気陰性度が1.5よりも高い元素のみからなる化合物を添加物として用い、比較例とした。電気陰性度が1.5よりも高い元素のみからなる化合物としては、Sb2S3,GaNを用いた。 A compound consisting only of an element having an electronegativity higher than 1.5 was used as an additive as a comparative example. Sb 2 S 3 , GaN was used as a compound consisting only of elements having an electronegativity higher than 1.5.
〔比較例9〕
添加物としてマンガンよりも電気陰性度の高いSb2S3を用いたこと以外は実施例40と同様に作製,測定を行った。なお、最終的な材料比は負極活物質が82質量%、添加物Sb2S3が5%、導電材としてアセチレンブラックが5質量%、PVDF(結着剤)が8質量%となるように調節した。
[Comparative Example 9]
Production and measurement were carried out in the same manner as in Example 40 except that Sb 2 S 3 having a higher electronegativity than manganese was used as an additive. The final material ratio is 82% by mass for the negative electrode active material, 5% for the additive Sb 2 S 3 , 5% by mass for acetylene black as a conductive material, and 8% by mass for PVDF (binder). Adjusted.
〔比較例10〕
添加物としてマンガンより電気陰性度の高いGaNを用いたほかは、比較例9と同様に作製,測定を行った。
[Comparative Example 10]
Fabrication and measurement were performed in the same manner as in Comparative Example 9 except that GaN having a higher electronegativity than manganese was used as an additive.
比較例9,10と実施例41,45,41を比較した(表8)。添加物添加量は少ないにもかかわらず、実施例41,45,41はいずれも比較例7,8よりも金属増加量が大きく、抵抗上昇率が低く抑えられている。これはK2SO4,CaCO3,BaCO3がマンガンより電気陰性度が低いという性質によりマンガンを捕捉していることを示している。 Comparative Examples 9 and 10 were compared with Examples 41, 45, and 41 (Table 8). Despite the small amount of additive added, all of Examples 41, 45, and 41 have a larger metal increase than Comparative Examples 7 and 8, and the resistance increase rate is kept low. This indicates that K 2 SO 4 , CaCO 3 , and BaCO 3 capture manganese due to the property that it has a lower electronegativity than manganese.
いずれの添加物添加場所においても従来例よりも低い抵抗上昇率が得られた。最も効果的だったのは、K2SO4を、負極活物質の質量aと添加物の質量bの合計質量a+bに対して5.75%の割合で負極合剤中に混ぜた実施例3である。添加物を負極合剤中に分散させた状態で添加する形態は、手法も簡易であるため、有用な添加方法と言える。 A resistance increase rate lower than that of the conventional example was obtained at any additive addition site. Example 3 in which K 2 SO 4 was mixed in the negative electrode mixture in a proportion of 5.75% with respect to the total mass a + b of the negative electrode active material mass a and the additive mass b was most effective. It is. The form in which the additive is added in a state of being dispersed in the negative electrode mixture can be said to be a useful addition method because the technique is simple.
1 正極
2 セパレータ
3 負極
4 電池缶
5 正極タブ
6 負極タブ
7 内蓋
8 内圧開放弁
9 ガスケット
10 PTC素子
11 電池蓋
DESCRIPTION OF SYMBOLS 1
Claims (13)
前記負極または前記セパレータは、添加物として電気陰性度が1.5より低い元素を含む化合物を有することを特徴とするリチウムイオン二次電池。 A lithium ion secondary battery having a positive electrode, a negative electrode, an electrolytic solution, and a separator, wherein the positive electrode has a lithium oxide containing manganese as a positive electrode active material,
The said negative electrode or the said separator has a compound containing the element whose electronegativity is lower than 1.5 as an additive, The lithium ion secondary battery characterized by the above-mentioned.
前記添加物は、前記添加物中の前記元素と、電解液中のマンガンイオンとが置換し得る塩であることを特徴とするリチウムイオン二次電池。 In claim 1,
The lithium ion secondary battery, wherein the additive is a salt that can replace the element in the additive with manganese ions in the electrolytic solution.
前記元素は、K,Ca,Baの少なくともいずれかであることを特徴とするリチウムイオン二次電池。 In claim 1 or claim 2,
The lithium ion secondary battery, wherein the element is at least one of K, Ca, and Ba.
前記負極は、負極集電体と、前記負極集電体表面に設けられた負極合剤の層とを有し、 前記負極合剤は、導電材と、結着材と、負極活物質とを有し、
前記負極活物質の作動電位は1.0〜2.0Vであることを特徴とするリチウムイオン二次電池。 In any one of Claims 1 thru | or 3,
The negative electrode has a negative electrode current collector and a negative electrode mixture layer provided on the surface of the negative electrode current collector. The negative electrode mixture comprises a conductive material, a binder, and a negative electrode active material. Have
The negative electrode active material has an operating potential of 1.0 to 2.0 V, a lithium ion secondary battery.
前記負極活物質はチタン酸リチウムであることを特徴とするリチウムイオン二次電池。 In any one of Claim 1 thru | or 4,
The lithium ion secondary battery, wherein the negative electrode active material is lithium titanate.
前記負極は、負極集電体と、前記負極集電体表面に設けられた負極合剤の層とを有し、 前記負極合剤は、導電材と、結着材と負極活物質とを有し、
前記添加物は前記負極合剤中に分散していることを特徴とするリチウムイオン二次電池。 In any one of Claims 1 thru | or 5,
The negative electrode has a negative electrode current collector and a negative electrode mixture layer provided on the surface of the negative electrode current collector. The negative electrode mixture has a conductive material, a binder, and a negative electrode active material. And
The lithium ion secondary battery, wherein the additive is dispersed in the negative electrode mixture.
前記負極は、負極集電体と、前記負極集電体表面に設けられた負極合剤の層とを有し、 前記負極合剤は、導電材と、結着材と、負極活物質とを有し、
前記負極活物質の粒子の表面には、前記添加物の粒子が付着していることを特徴とするリチウムイオン二次電池。 In any one of Claims 1 thru | or 5,
The negative electrode has a negative electrode current collector and a negative electrode mixture layer provided on the surface of the negative electrode current collector. The negative electrode mixture comprises a conductive material, a binder, and a negative electrode active material. Have
The lithium ion secondary battery, wherein the particles of the additive are attached to the surface of the particles of the negative electrode active material.
前記負極は、負極集電体と、前記負極集電体表面に設けられた負極合剤の層とを有し、 前記添加物は、負極の表面に層状に設けられていることを特徴とするリチウムイオン二次電池。 In any one of Claims 1 thru | or 5,
The negative electrode has a negative electrode current collector and a layer of a negative electrode mixture provided on the surface of the negative electrode current collector, and the additive is provided in layers on the surface of the negative electrode Lithium ion secondary battery.
前記添加物は、前記セパレータの表面に層状に設けられていることを特徴とするリチウムイオン二次電池。 In any one of Claims 1 thru | or 5,
The lithium ion secondary battery, wherein the additive is provided in a layered manner on the surface of the separator.
前記添加物の量は、前記負極活物質の質量aと、前記添加物の質量bの合計質量a+bに対して0.01〜8.05質量%の範囲であることを特徴とするリチウムイオン二次電池。 In claim 6,
The amount of the additive is in the range of 0.01 to 8.05% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive. Next battery.
前記添加物の量は、前記負極活物質の質量aと、前記添加物の質量bの合計質量a+bに対して0.06〜8.05質量%の範囲であることを特徴とするリチウムイオン二次電池。 In claim 7,
The amount of the additive is in the range of 0.06 to 8.05% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive. Next battery.
前記添加物の量は、前記負極活物質の質量aと、前記添加物の質量bの合計質量a+bに対して0.29〜13.8質量%の範囲であることを特徴とするリチウムイオン二次電池。 In claim 8,
The amount of the additive is in the range of 0.29 to 13.8% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive. Next battery.
前記添加物の量は、前記負極活物質の質量aと、前記添加物の質量bの合計質量a+bに対して0.46〜23.0質量%の範囲であることを特徴とするリチウムイオン二次電池。 In claim 9,
The amount of the additive is in the range of 0.46 to 23.0% by mass with respect to the total mass a + b of the mass a of the negative electrode active material and the mass b of the additive. Next battery.