JP2011080296A - Sound absorbing sheet, method for manufacturing the same, and sound insulation method - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To secure sufficient sound insulating performance, even when constituting a sound absorbing sheet reduced in thickness, to reduce the material cost and improve the space performance (space efficiency), and also to simplify the operation and improve the working efficiency in construction of a sound absorbing sheet. <P>SOLUTION: The sound absorbing sheet constituted by use of a foam resin sheet 2 formed of a foam resin material Ru has a two-layer structure by fixing and laminating a rubber sheet 3 formed of a rubber material Rb with a predetermined thickness onto one surface 2r of the foam resin sheet 2. The sound absorbing sheet is suspended inside or outside a sound insulation wall W or instead of the sound insulation wall W in a curtain-like manner to shield a space H from a noise source M, whereby sound insulation is performed. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

  The present invention relates to a sound-absorbing sheet using a foamed resin sheet formed of a foamed resin material, a manufacturing method thereof, and a soundproofing method.

  In general, as a soundproofing measure against a noise source, there are not a few cases where it is blocked by a sound absorbing sheet using a foamed resin sheet formed of a foamed resin material. For example, when constructing a wall such as a house, an interior material and an exterior material In between, the foamed resin sheet formed with the foamed resin material and having high soundproofing performance and heat insulation performance is interposed.

  Conventionally, a soundproof and heat insulating wall disclosed in Patent Document 1 is known as a wall having such a foamed resin sheet interposed therein. In the same document 1, a foamed synthetic resin plate is layered on a pressure-molded paper board. The two wall materials that have been attached are placed in an airtight manner between the columns with the foamed synthetic resin plate inside through a gap at a predetermined interval, and vent holes that communicate with the gap above and below the outer wall material. And a ventilation sheet is attached to the outer opening of the ventilation hole.

JP-A-9-170274

  However, the above-described conventional soundproofing and heat insulating walls (sound absorbing sheet and soundproofing method) have the following problems.

  First, the sound insulation performance is limited to the sound absorption performance based on the material of the foamed synthetic resin. Therefore, in order to ensure sufficient soundproofing performance, it is necessary to increase the thickness of the foamed synthetic resin plate, and as a result, the cost of the material is increased, and the space performance (space efficiency) during installation is reduced. Invite. Moreover, because the thickness is limited depending on the application, such as a wall of a house, the necessary soundproof performance may not be ensured, and the conventional foamed synthetic resin plate (sound absorbing sheet) has a viewpoint of ensuring soundproof performance. There was room for further improvement.

  Secondly, when a foamed synthetic resin plate is to be constructed inside a wall or the like, it is affixed to the interior material side or the exterior material side using an adhesive or the like. Therefore, when performing the construction, an adhesive application work, a pasting work, and the like are required, which leads to an increase in material costs and work man-hours such as an adhesive accompanying the construction. Eventually, the work is complicated and the work efficiency is lowered, and there is room for further improvement from the viewpoint of improving the workability of the sound absorbing sheet.

  The object of the present invention is to provide a sound-absorbing sheet, a method for manufacturing the sound-absorbing sheet, and a sound-proofing method that solve the problems existing in the background art.

  In order to solve the above-described problem, the sound-absorbing sheet 1 according to the present invention has a rubber surface on one surface 2r of the foamed resin sheet 2 when the sound-absorbing sheet using the foamed resin sheet 2 formed of the foamed resin material Ru is formed. The rubber sheet 3 formed to a predetermined thickness by the material Rb is fixed to be laminated in a two-layer structure. In this case, according to a preferred aspect of the invention, urethane foam can be used for the foamed resin material Ru and urethane rubber can be used for the rubber material Rb. In addition, it is desirable that the other surface 2f of the foamed resin sheet 2 has a substantial surface area larger than an apparent surface area by providing a large number of convex portions 2p. Further, one surface 2 r of the rubber sheet 3 and one surface 2 r of the foamed resin sheet 2 can be bonded by the slow-drying urethane rubber 4.

  On the other hand, the manufacturing method of the sound absorbing sheet according to the present invention is a rubber sheet having a predetermined thickness using the quick-drying rubber material Rb when manufacturing the sound absorbing sheet 1 having the foamed resin sheet 2 formed of the foamed resin material Ru. 3 is applied to one side of the rubber sheet 3 and an adhesive Rj using a slow-drying rubber material is applied. Thereafter, one side of the foamed resin sheet 2 is applied to one side of the rubber sheet 3 to which the adhesive Rj is applied. The two-layer structure is formed by fixing the surface 2r.

  On the other hand, in the soundproofing method according to the present invention, the soundproofing of the foamed resin sheet 2 formed of the foamed resin material Ru is performed when the soundproofing wall W configured by the sound absorbing sheet using the foamed resin sheet 2 formed of the foamed resin material Ru is used. The sound absorbing sheet 1 laminated in a two-layer structure by adhering a rubber sheet 3 formed to a predetermined thickness with the rubber material Rb on one surface 2r is placed inside the soundproof wall W or outside the soundproof wall W, or Instead of the soundproof wall W, the soundproofing is performed by hanging in a curtain shape and blocking the space H with respect to the noise source M. In this case, according to a preferred aspect of the invention, the sound absorbing sheet 1 can be used side by side in a direction in which the plurality of sound absorbing sheets 1.

  According to the sound absorbing sheet, the manufacturing method thereof, and the soundproofing method according to the present invention, the following remarkable effects can be obtained.

  (1) A sound absorbing sheet 1 laminated in a two-layer structure by fixing a rubber sheet 3 formed to a predetermined thickness with a rubber material Rb to one surface 2r of a foamed resin sheet 2 formed with a foamed resin material Ru. Therefore, in addition to the sound absorption performance based on the foamed resin material Ru, the sound absorption performance of the rubber sheet 3 formed to have a predetermined thickness by the rubber material Rb is taken into account, so that the soundproof performance can be ensured synergistically. Thereby, even if it is a case where the thin sound-absorbing sheet | seat 1 is comprised, while being able to ensure sufficient soundproofing performance, it can also contribute to the cost reduction of material, and the improvement of the space property (space efficiency) at the time of installation.

  (2) Since the sound-absorbing sheet 1 is suspended in a curtain shape and sound is prevented by blocking the space H with respect to the noise source M, it is applied to the interior material side or the exterior material side with an adhesive or the like. There is no need. Therefore, it is not necessary to perform an adhesive application work, a sticking work, or the like when constructing the sound-absorbing sheet 1, thereby simplifying the work and improving work efficiency.

  (3) A rubber sheet 3 having a predetermined thickness is manufactured using the quick-drying rubber material Rb, and an adhesive Rj using a slow-drying rubber material is applied to one side of the rubber sheet 3, and then, Since the sound absorbing sheet 1 is manufactured by fixing one surface 2r of the foamed resin sheet 2 to one side of the rubber sheet 3 coated with the adhesive Rj, the sound absorbing sheet 1 laminated in a two-layer structure can be manufactured easily and reliably. can do.

  (4) According to a preferred embodiment, if urethane foam is used for the foamed resin material Ru and urethane rubber is used for the rubber material Rb, the sound absorbing sheet 1 can be optimized, so that the soundproofing performance is improved. Higher performance can be obtained from the viewpoint.

  (5) If a large number of convex portions 2p are provided on the other surface 2f of the foamed resin sheet 2 according to a preferred embodiment, the substantial surface area can be made larger than the apparent surface area. Can be increased.

  (6) According to a preferred embodiment, if one surface 2r of the rubber sheet 3 and one surface 2r of the foamed resin sheet 2 are bonded by the slow-drying urethane rubber 4, the slow-drying urethane rubber 4 is porous in the foamed resin sheet 2 at the time of bonding. By entering the space, the adhesiveness can be further improved. In particular, when urethane rubber is used for the rubber sheet 3, the adhesiveness (adhesion) with the rubber sheet 3 can be increased.

  (7) When the sound-absorbing sheet 1 is suspended in a curtain shape and applied in accordance with a preferred embodiment, two or more sound-absorbing sheets 1 can be suspended in a stacking direction, so that it can be applied easily and reliably. It can contribute to further improvement of soundproofing performance.

Sectional drawing which shows a part of sound-absorbing sheet which concerns on suitable embodiment of this invention, Sectional drawing which shows the example which constructed the sound-absorbing sheet on the wall, Manufacturing process diagram showing an example of a manufacturing method of the sound absorbing sheet, The block diagram which shows the example which used the same sound-absorbing sheet, Noise attenuation level characteristic diagram with respect to frequency in an example using one sound absorbing sheet, The block diagram which shows the example which uses the two sound absorption sheets, Noise attenuation level characteristic diagram with respect to frequency in an example using two sound absorbing sheets,

  Next, preferred embodiments according to the present invention will be given and described in detail with reference to the drawings.

  First, the structure (structure) of the sound-absorbing sheet 1 according to the present embodiment will be described with reference to FIG.

  As shown in FIG. 1, the sound absorbing sheet 1 has, as shown in FIG. 1, a rubber sheet 3 formed with a predetermined thickness by a rubber material Rb on one surface 2r of a foamed resin sheet 2 formed by a foamed resin material Ru. By adhering, a two-layer structure is laminated.

  In this case, the foamed resin material Ru is preferably foamed urethane, in particular, soft foamed urethane having an open cell structure (open cell structure). An exemplary foamed resin sheet 2 using soft foamed urethane has one surface 2r formed as a flat surface and a plurality of conical convex portions 2p provided on the other surface 2f. The dimension (thickness) from the one surface 2r to the tip of the convex portion 2p is selected to be about 6 [cm]. The convex portions 2p... Make the substantial surface area of the other surface 2f larger than the apparent surface area, and can further improve the sound absorption performance.

  Further, a soft urethane rubber is used for the rubber material Rb. The exemplary rubber sheet 3 using the soft urethane rubber has a thickness of about 0.3 to 0.5 [mm], and the sound-absorbing sheet 1 is manufactured using the quick-drying soft urethane rubber as described later. Manufacturing at the same time. Then, one surface 2r of the rubber sheet 3 and one surface 2r of the foamed resin sheet 2 are bonded (fixed) by the slow-drying urethane rubber 4 and laminated in a two-layer structure as shown in FIG.

  As described above, if urethane foam is selected as the foamed resin material Ru and urethane rubber is selected as the rubber material Rb, the sound absorption sheet 1 can be optimized. Higher performance can be obtained from the viewpoint of improving soundproof performance.

  Next, an example of a method for manufacturing the sound absorbing sheet 1 according to the present embodiment will be described with reference to the manufacturing process diagram shown in FIG.

  First, the rubber sheet 3 is manufactured. When the rubber sheet 3 is manufactured, a fast-drying urethane rubber thin film (sheet) is formed on the surface of the flat plate by spraying a quick-drying urethane rubber, which is a quick-drying rubber material Rb, on the flat plate ( Step S1). At this time, since the thin film is formed with a thickness of about 0.3 to 0.5 [mm] as a guide, the amount of spraying is determined in advance from the spraying area and set, and uniform spraying is performed until the set amount of spraying is completed. Good (step S2). Thereby, the rubber sheet 3 having a target thickness (about 0.3 to 0.5 [mm]) can be easily obtained (step S3).

  Next, the slow-drying urethane rubber 4 which is the same material as the material of the rubber sheet 3 and is a slow-drying rubber material is applied on the obtained rubber sheet 3 (step S4). The slow-drying urethane rubber 4 is used as the adhesive Rj, and is uniformly applied to the upper surface of the rubber sheet 3 by a spray device, for example.

  On the other hand, the foamed resin sheet 2 is manufactured in advance or prepared by purchasing a commercial product in advance. This foamed resin sheet 2 is formed of the above-described flexible foamed urethane having the open cell structure, and has a flat surface on one surface 2r and a convex portion 2p on the other surface 2f. It is. Then, one surface (flat surface) 2r of the prepared foamed resin sheet 2 is superposed on the upper surface of the rubber sheet 3 coated with the slow-drying urethane rubber 4 (step S5). If it overlaps, it pressurizes moderately with respect to the foamed resin sheet 2 (step S6). As a result, the slow-drying urethane rubber 4 maintaining fluidity enters the porous space of the foamed resin sheet 2 having the open cell structure (step S7). Thereby, when the slow-drying urethane rubber 4 that has entered the porous space of the foamed resin sheet 2 is solidified (adhered), the adhesiveness can be further improved, and the rubber sheet 3 is made of urethane rubber. The adhesiveness (adhesiveness) to the rubber sheet 3 can also be enhanced by the identity of the material.

  Thereafter, the slow-drying urethane rubber 4 is solidified by natural drying or forced drying (step S8). When the time necessary for solidification has elapsed, the rubber sheet 3 (sound absorbing sheet 1) is peeled off from the flat plate. Then, the target sound-absorbing sheet 1 can be obtained (steps S9 and S10).

  Next, usage examples of the sound absorbing sheet 1 according to the present embodiment will be described with reference to FIGS. 2 and 4 to 7.

  FIG. 2 shows an example in which the sound absorbing sheet 1 is constructed on a wall W such as a house. In FIG. 2, 21 is an exterior material (exterior panel), 22 is an interior material (interior panel), and the exterior material 21 and the interior material 22 are a support material 23 such as wood interposed between the exterior material 21 and the interior material 22. And fixed to a pillar (not shown). Thus, since the space Wi is usually provided by the support material 23 between the exterior material 21 and the interior material 22, the sound absorbing sheet 1 is accommodated in the space Wi and the sound absorbing sheet 1 is attached when the sound absorbing sheet 1 is attached. As shown in FIG. 2, the sound absorbing sheet 1 is suspended in the space Wi by attaching the upper end of the sound absorbing sheet 1 to the lower surface of the support member 23 using, for example, an L-shaped attachment 31. By attaching the lower end of the sheet 1 to the upper surface of the support member 23 using the same attachment tool 31, it is possible to prevent shaking. In this case, the sound absorbing sheet 1 is fixed to the vertical piece of the L-shaped fixture 31 with bolts and nuts 32 and the like, and the horizontal piece of the L-shaped fixture 31 is fixed to the support member 23 with screws 33 and the like. To do. Therefore, the sound absorbing sheet 1 is not attached to the exterior material 21 side or the interior material 22 side with an adhesive or the like.

  FIG. 4 shows an example in which a wall W is constituted by the sound absorbing sheet 1 itself when a noise source M such as a machine is installed in the room H. In this case, it is desirable to use one sound absorbing sheet 1 and completely partition the room H. Therefore, when installing the sound absorbing sheet 1, the upper end side of the sound absorbing sheet 1 may be attached to the ceiling X and hung like a curtain. When attaching the sound absorbing sheet 1 to the ceiling X, the above-described fixture 31 can be used. That is, if the sound absorbing sheet 1 is fixed to the vertical piece of the L-shaped fixture 31 with bolts and nuts 32 and the like, and the horizontal piece of the L-shaped fixture 31 is fixed to the ceiling X with screws 33 and the like. Good. Thereby, the sound-absorbing sheet 1 becomes the wall W and is partitioned into the first space Hc in which the noise source M is installed and the second space Hs isolated from the noise source M. Of course, the sound absorption sheet 1 can be used in various forms, and may be installed so as to surround only the noise source M.

  FIG. 5 shows the noise attenuation level in the second space Hs with respect to the first space Hc shown in FIG. 4, that is, the noise attenuation level characteristic P1 with respect to the frequency. As is clear from FIG. 5, the attenuation level in the low frequency region near 100 [Hz] is relatively small, but in the frequency region near 1 [kHz], the attenuation level is around −10 [dB]. In the frequency range of 1 to 10 [kHz], a sufficient soundproofing effect is recognized such that the attenuation level is around −20 [dB].

  FIG. 6 shows an example in which two sound absorbing sheets 1 are used. When installing each of the sound absorbing sheets 1, 1, the sound absorbing sheets 1, 1 are mounted side by side on the ceiling X and suspended like a curtain. You can lower it. Therefore, when attaching the sound absorbing sheets 1 and 1 to the ceiling X, the above-described fixture 31 can be used. As described above, since the sound absorbing sheets 1 and 1 can be hung in a curtain shape and can be constructed, unlike the case where they are attached to a wall surface or the like, even two or more sound absorbing sheets 1 are suspended in a stacking direction. Can be lowered. Thereby, it can construct easily and reliably irrespective of the number of sheets, and can contribute to the further improvement in soundproofing performance. In FIG. 6, the same parts as those in FIG. 4 are denoted by the same reference numerals to clarify the configuration, and detailed description thereof is omitted. As a result, the two sound absorbing sheets 1 and 1 become walls W and are divided into a first space Hc in which the noise source M is installed and a second space Hs isolated from the noise source M.

  FIG. 7 shows the noise attenuation level in the second space Hs with respect to the first space Hc shown in FIG. 6, that is, the noise attenuation level characteristic P2 with respect to the frequency. For comparison, one sound absorption shown in FIG. A noise attenuation level characteristic P1 with respect to a frequency when the sheet 1 is used is indicated by a virtual line. As is clear from FIG. 7, even when two sound absorbing sheets 1 and 1 are used, the attenuation level in the low frequency region near 100 [Hz] is small as in the case of one sound absorbing sheet 1, but 1 In the frequency region in the vicinity of [kHz], the attenuation level is around −20 [dB]. Particularly, in the frequency region of several [kHz], the attenuation level can be attenuated to near −40 [dB]. Soundproof effect is recognized.

  Therefore, according to the sound absorbing sheet 1 and the manufacturing method and the soundproofing method according to this embodiment, the rubber material Rb has a predetermined thickness on one surface 2r of the foamed resin sheet 2 formed of the foamed resin material Ru. In addition to the sound absorption performance based on the foamed resin material Ru, in addition to the sound absorption performance based on the foamed resin material Ru, the rubber sheet 3 formed to a predetermined thickness is used. By taking into account the sound absorption performance, it is possible to ensure a soundproof performance that is synergistically enhanced. Thereby, even if it is a case where the thin sound-absorbing sheet | seat 1 is comprised, while being able to ensure sufficient soundproofing performance, it can contribute also to the cost reduction of material, and the improvement of the space property (space efficiency) at the time of installation. In addition, since the sound absorbing sheet 1 is suspended in a curtain shape and sound insulation is performed by blocking the space H with respect to the noise source M, it is necessary to apply it to the interior material side or the exterior material side using an adhesive or the like. There is no. Therefore, when performing the construction, an adhesive application work, a sticking work, and the like are not required, and the work can be simplified and work efficiency can be improved. In addition, a rubber sheet 3 having a predetermined thickness is manufactured using the quick-drying rubber material Rb, and an adhesive Rj using a slow-drying rubber material is applied to one side of the rubber sheet 3, and thereafter Since the sound absorbing sheet 1 is manufactured by fixing one surface 2r of the foamed resin sheet 2 to one side of the rubber sheet 3 coated with the agent Rj, the sound absorbing sheet 1 laminated in a two-layer structure is easily and reliably manufactured. be able to.

  The preferred embodiment (modified embodiment) has been described in detail above, but the present invention is not limited to such an embodiment, and the present invention is not limited to such a configuration, shape, material, quantity, numerical value, and the like. Any change, addition, or deletion can be made without departing from the scope of the above.

  For example, urethane foam is optimal as the foamed resin material Ru, but other foamed resin materials are not excluded. Similarly, urethane rubber is optimal as the rubber material Rb, but other rubber materials are not excluded. In this case, the adhesive Rj between the rubber sheet 3 and the foamed resin sheet 2 is optimally the slow-drying urethane rubber 4, but does not exclude the case where it is fixed (adhered) with another adhesive. On the other hand, although the case where many convex-shaped parts 2p ... was provided in the other surface 2f of the foamed resin sheet 2 was shown, the case where a recessed part is provided or formed flat is not excluded. Moreover, although the case where the sound-absorbing sheet 1 is installed using the fixture 31 is illustrated, various types of fixtures (attachment means and suspension means) can be used when installing the sound-absorbing sheet 1.

  The sound absorbing sheet, the manufacturing method thereof, and the soundproofing method according to the present invention can be used in various fields as a soundproofing measure against various noise sources.

  1: sound absorbing sheet, 2: foamed resin sheet, 2r: one side of the foamed resin sheet, 2f: the other side of the foamed resin sheet, 3: rubber sheet, 2p ...: convex portion, 4: slow-drying urethane rubber, Ru: Foam resin material, Rb: Rubber material, Rj: Adhesive, W: Sound barrier, M: Noise source

Claims (8)

  In a sound-absorbing sheet using a foamed resin sheet formed of a foamed resin material, a rubber sheet formed to a predetermined thickness with a rubber material is bonded to one surface of the foamed resin sheet and laminated in a two-layer structure. A sound-absorbing sheet.   The sound absorbing sheet according to claim 1, wherein urethane foam is used for the foamed resin material.   The sound absorbing sheet according to claim 1 or 2, wherein urethane rubber is used as the rubber material.   4. The sound absorbing sheet according to claim 1, wherein the other surface of the foamed resin sheet has a substantial surface area larger than an apparent surface area by providing a plurality of convex portions. .   The sound-absorbing sheet according to any one of claims 1 to 4, wherein one side of the rubber sheet and one side of the foamed resin sheet are bonded with a slow-drying urethane rubber.   In a method for producing a sound-absorbing sheet having a foamed resin sheet formed of a foamed resin material, a quick-drying rubber material is used to produce a rubber sheet having a predetermined thickness, and a slow-drying rubber material is provided on one side of the rubber sheet. A sound-absorbing sheet characterized in that it is laminated in a two-layer structure by applying the adhesive used, and then adhering one side of the foamed resin sheet to one side of the rubber sheet to which the adhesive has been applied. Manufacturing method.   In a soundproofing method for soundproofing by a soundproof wall constituted by a sound absorbing sheet using a foamed resin sheet formed of a foamed resin material, one surface of the foamed resin sheet formed of the foamed resin material has a predetermined thickness by a rubber material. A sound absorbing sheet laminated in a two-layer structure by fixing the formed rubber sheet is hung in a curtain shape inside the soundproof wall, outside the soundproof wall, or instead of the soundproof wall, and is a space for noise sources The soundproofing method characterized by performing soundproofing by interrupting | blocking.   8. The soundproofing method according to claim 7, wherein the sound absorbing sheets are used side by side in a direction in which a plurality of sound absorbing sheets are stacked.