JP2010197615A - Active light sensitive or radiation sensitive resin composition, and pattern forming method using the same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an active light sensitive or a radiation sensitive resin composition which provides a fine pattern superior in exposure latitude and a pattern form, and to provide a pattern forming method using the same. <P>SOLUTION: The active light sensitive or the radiation sensitive resin composition contains (A) a resin that has a repeating unit including structure represented by general formula (1) and a repeating unit including structure represented by general formula (I) and increases solubility in an alkali developing solution by the action of an acid, and (B) a compound that produces an acid by active light or radiation irradiation. Wherein, codes in formulas (1) and (I) represent differential meanings. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

  The present invention relates to an actinic ray-sensitive or radiation-sensitive resin composition used in semiconductor manufacturing processes such as IC, circuit boards such as liquid crystals and thermal heads, and other photofabrication processes, and the composition. The present invention relates to a pattern forming method. More specifically, the present invention relates to an actinic ray-sensitive or radiation-sensitive resin composition suitable for the case where far ultraviolet rays of 220 nm or less, an electron beam, or the like is used as an irradiation source, and a pattern forming method using the composition. is there.

  In the present invention, “active light” or “radiation” means, for example, an emission line spectrum of a mercury lamp, far ultraviolet rays represented by excimer laser, extreme ultraviolet rays, X-rays, electron beams, and the like. In the present invention, light means actinic rays or radiation.

  The chemically amplified photosensitive composition generates an acid in the exposed area by irradiation with radiation such as far ultraviolet light, and the acid-catalyzed reaction causes the solubility of the active radiation irradiated area and non-irradiated area in the developer. This is a pattern forming material for changing the pattern to form a pattern on the substrate.

  When a KrF excimer laser is used as an exposure light source, a resin having a basic skeleton of poly (hydroxystyrene) having a small absorption mainly in the 248 nm region is used as a main component. A pattern is formed, which is a better system than the conventional naphthoquinone diazide / novolak resin system.

  On the other hand, when a further short wavelength light source, for example, an ArF excimer laser (193 nm) is used as an exposure light source, the compound having an aromatic group exhibits a large absorption in the 193 nm region. It wasn't.

  For this reason, an ArF excimer laser resist containing a resin having an alicyclic hydrocarbon structure has been developed. For example, Patent Documents 1 and 2 describe compositions containing a resin having a polycyclic acid-decomposing repeating unit and a non-acid-decomposing repeating unit. These resins are chemically amplified resists having acid-labile protecting groups that are dissociated by acid, but these resisting groups are sufficient as resist patterns are required to be further miniaturized. It has become difficult to obtain excellent resist performance. For example, in a resin including a repeating unit having an acid dissociable protecting group, a study of using two or more acid dissociable protecting groups in combination (for example, refer to Patent Document 3), in order to make the pattern resolution and pattern shape rectangular. In addition, a novel acid-acid dissociable protecting group has been studied (for example, see Patent Document 4). However, the conventional resist composition still has insufficient points, and further improvements are required for LWR (Line-Width-Roughness), exposure latitude, and pattern shape.

JP 2003-167347 A Japanese Patent Laid-Open No. 2003-223001 Japanese Patent No. 4090773 JP 2007-316515 A

  In view of the actual situation of the above-mentioned background art, the present invention can provide an actinic ray-sensitive or radiation-sensitive resin composition capable of providing a fine pattern excellent in LWR (Line-Width-Roughness), exposure latitude, and pattern shape. Another object is to provide a pattern forming method using the composition.

As a result of intensive studies to solve the above problems, the present inventors have completed the present invention shown below.
(1) (A) It has a repeating unit containing a structure represented by the following general formula (1) and a repeating unit containing a structure represented by the following general formula (I), and is soluble in an alkali developer by the action of an acid. An actinic ray-sensitive or radiation-sensitive resin composition comprising: a resin having an increase in pH; and (B) a compound that generates an acid upon irradiation with an actinic ray or radiation.

In general formula (1),
L represents a lactone structure.
When there are a plurality of R _{0 s,} each independently represents an alkylene group which may have a substituent, a cyclic alkylene group which may have a substituent, or a combination thereof.
Z is independently an ether bond, an ester bond, an amide bond, a urethane bond or a urea bond when there are a plurality of Z.
n represents the number of repetitions and represents an integer of 0 to 5.

In general formula (I),
R ₁ represents an alkyl group which may have a substituent or a cycloalkyl group which may have a substituent.
R ₂ represents a hydrogen atom, an alkyl group that may have a substituent, or a cycloalkyl group that may have a substituent.
X represents a halogen atom, a hydroxyl group, a cyano group, an acetyl group that may have a substituent, an alkoxy group, or an alkyl group that may have a substituent. When there are a plurality of Xs, the plurality of Xs may be the same or different, and a plurality of Xs may be bonded to form a ring.

  k represents an integer of 0 to 4.

(2) The actinic ray-sensitive or radiation-sensitive resin according to (1), wherein the repeating unit including the structure of the general formula (I) is a repeating unit represented by the following general formula (AI) Composition.

In general formula (AI),
R ₃ represents a hydrogen atom, an alkyl group that may have a substituent, a halogen atom, a cyano group, or an alkyloxycarbonyl group that may have a substituent.
R ₁ , R ₂ , X and k are respectively synonymous with R ₁ , R ₂ , X and k in formula (I).

  (3) The actinic ray-sensitive or radiation-sensitive resin composition according to (1) or (2), further comprising (C) a hydrophobic additive resin.

  (4) A pattern comprising a step of forming a film with the actinic ray-sensitive or radiation-sensitive resin composition according to any one of (1) to (3), and exposing and developing the film. Forming method.

Hereinafter, the best mode for carrying out the present invention will be described.
In addition, in the description of the group (atomic group) in this specification, the description which does not describe substitution and non-substitution includes what does not have a substituent and what has a substituent. . For example, the “alkyl group” includes not only an alkyl group having no substituent (unsubstituted alkyl group) but also an alkyl group having a substituent (substituted alkyl group).

(A) Resin whose solubility in an alkaline developer is increased by the action of an acid The resin (A) in the present invention is a repeating unit containing a structure represented by the general formula (1) and a structure represented by the general formula (I) It is a high molecular compound which has a repeating unit containing as an essential component.

First, the structure represented by the general formula (1) will be described.

In general formula (1),
L represents a lactone structure.
When there are a plurality of R _{0 s,} each independently represents an alkylene group which may have a substituent, a cyclic alkylene group which may have a substituent, or a combination thereof.
When there are a plurality of Z, each independently represents an ether bond, an ester bond, an amide bond,
Represents a urethane bond or a urea bond.
n represents the number of repetitions and represents an integer of 0 to 5.

The group represented by R ₀ is not particularly limited as long as it is a chain alkylene group or a cyclic alkylene group, but a preferable chain alkylene group is preferably a chain alkylene having 1 to 10 carbon atoms, more preferably. Has 1 to 5 carbon atoms, and examples thereof include a methylene group, an ethylene group, and a propylene group. Preferable cyclic alkylene is C1-C20 cyclic alkylene, for example, cyclohexylene, cyclopentylene, norbornylene, adamantylene, etc. are mentioned. In order to exhibit the effect of the present invention, a chain alkylene group is more preferable.

Examples of the preferred substituent that the chain alkyl group or cyclic alkyl group of R ₀ may have include a halogen atom (preferably a chloro atom and a fluorine atom), a methoxy group, a methoxycarbonyl group, and the like. Furthermore, a methyl group, an ethyl group, etc. are mentioned.

As the group represented by L, any group can be used as long as it has a lactone structure, but it is preferably a 5- to 7-membered ring lactone structure, and the bicyclo structure or spiro structure is added to the 5- to 7-membered ring lactone structure. Those in which other ring structures are condensed in a form to form are preferable. It is more preferable to have a repeating unit having a lactone structure represented by any of the following general formulas (LC1-1) to (LC1-16). The lactone structure may be directly bonded to the main chain. Preferred lactone structures are (LC1-1), (LC1-4), (LC1-5), (LC1-6), (LC1-13), and (LC1-14).

The lactone structure moiety may or may not have a substituent (Rb ₂ ). Preferred substituents (Rb ₂ ) include an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 4 to 7 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkoxycarbonyl group having 1 to 8 carbon atoms, and a carboxyl group. , Halogen atom, hydroxyl group, cyano group, acid-decomposable group and the like. More preferably, they are a C1-C4 alkyl group, a cyano group, and an acid-decomposable group. n ₂ represents an integer of 0-4. When n ₂ is 2 or more, a plurality of substituents (Rb ₂ ) may be the same or different, and a plurality of substituents (Rb ₂ ) may be bonded to form a ring. .
Among these, preferred lactone repeating units include the following (1-1).

In general formula (1-1),
R represents a hydrogen atom or an alkyl group which may have a substituent.
A is

Represents.

When there are a plurality of R _{0 s,} each independently represents an alkylene group which may have a substituent, a cyclic alkylene group which may have a substituent, or a combination thereof.
Z is independently an ether bond, an ester bond, an amide bond, a urethane bond or a urea bond when there are a plurality of Z.

L has a lactone structure.
n represents the number of repetitions and represents an integer of 0 to 5.

The alkyl group represented by R is preferably an alkyl group having 1 to 4 carbon atoms, more preferably a methyl group or an ethyl group, and most preferably a methyl group. Examples of the substituent that the alkyl group as R may have include, for example, halogen atoms such as fluorine atom, chlorine atom, bromine atom, mercapto group, hydroxy group, methoxy group, ethoxy group, isopropoxy group, t-butoxy group, Examples include an alkoxy group such as a benzyloxy group, and an acetoxy group such as an acetyl group and a propionyl group.
Preferred examples of R ₀ , L, and Z are the same as described above.
More particularly preferable lactone repeating units include the following (1-2).

In general formula (1),
R, A, R ₀ , and Z are as defined above. Preferably, A and Z are ester bonds (—COO—).

When there are a plurality of R _{1 s} , each independently represents an alkyl group which may have a substituent, a cycloalkyl group which may have a substituent, an ester group which may have a substituent, or a cyano group, two R ₁ are bonded in the presence of two or more, may form a ring. R ₁ is preferably an alkyl group or a cyano group.

X represents an alkylene group, an oxygen atom or a sulfur atom.
n represents the number of repetitions and represents an integer of 0 to 5. n is preferably 0 or 1.
m is the number of substituents and represents an integer of 0 to 5. m is preferably 0 or 1.

  Preferable examples of the alkyl group represented by R include the same groups as R in formula (1-1).

Preferable examples of the chain alkylene group and cyclic alkylene group represented by R ₀ include the same groups as R ₀ in formula (1), and among them, a methylene group is particularly preferable.

The alkyl group of R _1, preferably an alkyl group having 1 to 4 carbon atoms, a methyl group, an ethyl group, are more preferable, most preferably a methyl group. Examples of the cycloalkyl group include cyclopropyl, cyclobutyl, cyclopentyl, and cyclohexyl groups. Examples of the ester group include a methoxycarbonyl group, an ethoxycarbonyl group, an n-butoxycarbonyl group, and a t-butoxycarbonyl group. Examples of the substituent include an alkoxy group such as a hydroxy group, a methoxy group, and an ethoxy group, and a halogen atom such as a cyano group and a fluorine atom.
Preferred substitution positions for R ₁ are as follows.

Examples of the alkylene group for X include a methylene group and an ethylene group.
Specific examples of the repeating unit having a group having a lactone structure represented by the general formula (1) are shown below, but the present invention is not limited thereto.

In the following specific examples, R represents a hydrogen atom, an alkyl group which may have a substituent, or a halogen atom, preferably a hydrogen atom, a methyl group, a hydroxymethyl group or an acetoxymethyl group.

Among these, specific examples of preferred general formula (1) and general formula (1-1) include the following specific examples. In the formula, R and R ₁ represent a hydrogen atom, an alkyl group which may have a substituent, or a halogen atom, preferably a hydrogen atom, a methyl group, a hydroxymethyl group or an acetoxymethyl group.

  As for content of the repeating unit which has a lactone structure represented by General formula (1) or General formula (1-1), 10-60 mol% is preferable with respect to all the repeating units in a polymer, More preferably, 20-50 mol %.

  In order to enhance the effect of the present invention, two or more lactone repeating units selected from general formula (1-2) can be used in combination. When using together, it is preferable to select and use 2 or more types from the lactone repeating unit whose n is 1 among general formula (1-2).

  Moreover, in General formula (1-1), it is also possible to use together 2 or more types of lactone repeating units whose n is 0 and 1.

Next, the structure represented by the general formula (I) will be described.

In general formula (I),
R ₁ represents an alkyl group which may have a substituent or a cycloalkyl group which may have a substituent. R ₂ represents a hydrogen atom, an alkyl group that may have a substituent, or a cycloalkyl group that may have a substituent. X represents a halogen atom, a hydroxyl group, a cyano group, an acetyl group that may have a substituent, an alkoxy group that may have a substituent, or an alkyl group that may have a substituent. When there are a plurality of Xs, the plurality of Xs may be the same or different, and a plurality of Xs may be bonded to form a ring. k represents an integer of 0 to 4.

Examples of the alkyl group and cycloalkyl group represented by R ₁ and R ₂ in the general formula (I) include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a t-butyl group, and pentyl. Group, a cyclopentyl group, a hexyl group, a cyclohexyl group, an octyl group, a dodecyl group, etc., a C1-C20 linear or branched alkyl group, and a cycloalkyl group are mentioned. These groups may have a substituent.

Preferred substituents that the alkyl group and cycloalkyl group of R ₁ and R ₂ may have include an alkyl group, an alkylcarbonyloxy group, a cycloalkyl group, a cycloalkylcarbonyloxy group, an aryl group, an arylcarbonyloxy group, and an aralkyl. Group, aralkylcarbonyloxy group, alkoxy group, cycloalkoxy group, aryloxy group, aralkyloxy group, hydroxyl group, halogen atom, nitro group, acyl group, acyloxy group, acylamino group, sulfonylamino group, alkylthio group, cycloalkylthio group, An arylthio group, an aralkylthio group, a thiophenecarbonyloxy group, a thiophenemethylcarbonyloxy group, a heterocyclic residue such as a pyrrolidone residue, and the like are mentioned, and preferably it has 12 or less carbon atoms.

  Examples of the alkyl group having a substituent include a cyclohexylethyl group, an alkylcarbonyloxymethyl group, an alkylcarbonyloxyethyl group, a cycloalkylcarbonyloxymethyl group, a cycloalkylcarbonyloxyethyl group, an arylcarbonyloxyethyl group, and an aralkylcarbonyloxyethyl group. Group, alkyloxymethyl group, cycloalkyloxymethyl group, aryloxymethyl group, aralkyloxymethyl group, alkyloxyethyl group, cycloalkyloxyethyl group, aryloxyethyl group, aralkyloxyethyl group, alkylthiomethyl group, cycloalkylthio Methyl group, arylthiomethyl group, aralkylthiomethyl group, alkylthioethyl group, cycloalkylthioethyl group, arylthioethyl group, aralkyl Thioethyl group, and the like.

  Examples of the cycloalkyl group having a substituent include a methylcyclohexyl group, a methoxycyclohexyl group, a methoxycarboxycyclohexyl group, a methylcyclopentyl group, a methoxycyclopentyl group, and a methoxycarboxycyclopentyl group.

The alkyl group as X may have a substituent, and is preferably an alkyl group having 1 to 8 carbon atoms. Specifically, a methyl group, an ethyl group, a propyl group, an n-butyl group, sec- A butyl group, a hexyl group, an octyl group, etc. can be mentioned.
The alkoxy group as X may have a substituent, and is preferably an alkoxy group having 1 to 8 carbon atoms. For example, methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, cyclohexyl An oxy group etc. can be mentioned.
The ring formed by a plurality of X is preferably a 5- to 7-membered ring.
The group represented by the general formula (I) is insoluble or hardly soluble in an alkali developer, but is decomposed by the action of an acid to generate a carboxyl group and becomes soluble in an alkali developer.

  The secondary cyclopropyl ester represented by the general formula (I) can be easily obtained by a condensation reaction of secondary cyclopropyl alcohol and carboxylic acid chloride. Cyclopropyl alcohol can be easily synthesized by using an addition reaction of a cyclopropyl Grignard reagent to an aldehyde. For the cyclopropyl Grignard reagent, the following documents can be referred to.

Science of Synthesis (2004), 7, 573-596.
Moreover, among the repeating units including the structure represented by the general formula (I), a preferred example is a repeating unit represented by the following general formula (AI).

In general formula (AI),
R ₃ represents a hydrogen atom, an alkyl group, a halogen atom, a cyano group or an alkyloxycarbonyl group.
R ₁ , R ₂ , X and k have the same meanings as R ₁ , R ₂ , X and k in formula (I).

The alkyl group for R ₃ is preferably an alkyl group having 1 to 5 carbon atoms. Alkyl group of R ₃ include a halogen atom (preferably fluorine atom), an alkyloxycarbonyl group (preferably having from 1 to 5 carbon atoms), an alkylcarbonyloxy group (preferably having from 1 to 5 carbon atoms), a hydroxyl group, an alkoxy group ( Preferably, it may be substituted with 1 to 5 carbon atoms or the like.

The alkyloxycarbonyl group for R ₃ is preferably an alkyloxycarbonyl group having 1 to 5 carbon atoms.
R ₃ is preferably a hydrogen atom, a methyl group or a hydroxymethyl group.
Specific examples of the repeating unit including the structure represented by the general formula (I) and the repeating unit represented by the general formula (AI) are shown below, but the present invention is not limited thereto.

  The content of the repeating unit containing the structure represented by the general formula (I) or the repeating unit represented by the general formula (AI) is preferably 1 to 30 mol%, more preferably based on all repeating units in the polymer. Is 5 to 15 mol%.

  Further, the resin of the component (A) is a main chain of the resin in addition to the repeating unit having the structure represented by the general formula (I) or the general formula (AI) and having increased solubility in an alkali developer by the action of an acid. Alternatively, the side chain, or both the main chain and the side chain may have a group that decomposes by the action of an acid to generate an alkali-soluble group (hereinafter also referred to as “acid-decomposable group”).

  Alkali-soluble groups include phenolic hydroxyl groups, carboxyl groups, fluorinated alcohol groups, sulfonic acid groups, sulfonamido groups, sulfonylimide groups, (alkylsulfonyl) (alkylcarbonyl) methylene groups, (alkylsulfonyl) (alkylcarbonyl) imides. Group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) methylene group, etc. Is mentioned.

Preferred alkali-soluble groups include carboxyl groups, fluorinated alcohol groups (preferably hexafluoroisopropanol), and sulfonic acid groups.
A preferable group as the acid-decomposable group is a group in which the hydrogen atom of these alkali-soluble groups is substituted with a group capable of leaving with an acid.
Examples of the group leaving with an acid include -C (R ₃₆ ) (R ₃₇ ) (R ₃₈ ), -C (R ₃₆ ) (R ₃₇ ) (OR ₃₉ ), -C (R ₀₁ ) (R ₀₂ ). ) (OR ₃₉ ) and the like.

In the formula, R _{36 to} R ₃₉ each independently represents an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, or an alkenyl group. R ₃₆ and R ₃₇ may be bonded to each other to form a ring.
R _{01 and} R ₀₂ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkenyl group.
The acid-decomposable group is preferably a cumyl ester group, an enol ester group, an acetal ester group, a tertiary alkyl ester group or the like. More preferably, it is a tertiary alkyl ester group.
As the tertiary ester, a repeating unit having a partial structure represented by the following general formula can be preferably used.

As preferred repeating units, those represented by the following general formula (A) are preferred.

In general formula (A),
Xa ₁ represents a hydrogen atom, a methyl group, a trifluoromethyl group or a hydroxymethyl group.
T represents a single bond or a divalent linking group.
Rx _{1 to} Rx ₃ each independently represents an alkyl group (straight or branched) or a cycloalkyl group (monocyclic or polycyclic).
At least two of Rx _{1 to} Rx ₃ may combine to form a cycloalkyl group (monocyclic or polycyclic).

Examples of the divalent linking group for T include an alkylene group, —COO—Rt— group, —O—Rt— group, and the like. In the formula, Rt represents an alkylene group or a cycloalkylene group.
T is preferably a single bond or a —COO—Rt— group. Rt is preferably an alkylene group having 1 to 5 carbon atoms, more preferably a —CH ₂ — group or a — (CH ₂ ) ₃ — group.
The alkyl group of Rx _{1 to} Rx ₃ is preferably an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, or a t-butyl group.

Examples of the cycloalkyl group represented by Rx _{1 to} Rx ₃ include monocyclic cycloalkyl groups such as cyclopentyl group and cyclohexyl group, polycyclic cycloalkyl groups such as norbornyl group, tetracyclodecanyl group, tetracyclododecanyl group, and adamantyl group. Groups are preferred.

Examples of the cycloalkyl group formed by combining at least two of Rx _{1 to} Rx ₃ include a monocyclic cycloalkyl group such as a cyclopentyl group and a cyclohexyl group, a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, A polycyclic cycloalkyl group such as an adamantyl group is preferred.

It is preferable to use either the group represented by the following general formula (2-1) or the group represented by the general formula (2-2) as the tertiary ester.

R ₂ each independently represents an alkyl group which may have a substituent or a monocyclic cycloalkyl group which may have a substituent. However, when at least one R ₂ is a monocyclic cycloalkyl group or all are alkyl groups, they are bonded to each other to form a monocyclic cycloalkyl group.

R ₃ each independently represents an alkyl group which may have a substituent or a polycyclic cyclic alkyl group which may have a substituent. However, when at least one R ₃ is a polycyclic cyclic alkyl group or all are alkyl groups, they are bonded to each other to form a polycyclic cyclic alkyl group.

R _{2, R 3} methyl group as an alkyl group, an ethyl group, n- propyl group, an isopropyl group, n- butyl group, an isobutyl group, those having 1 to 4 carbon atoms such as t- butyl group. The monocyclic cycloalkyl group represented by R ₂ is preferably a cycloalkyl group having 5 to 8 carbon atoms such as a cyclopentyl group or a cyclohexyl group, and more preferably a cyclopentyl group or a cyclohexyl group. Examples of the polycyclic alkyl group represented by R ₃ include a norbornyl group, a tetracyclodecanyl group, a tetracyclododecanyl group, and an adamantyl group.

As a preferred example of the group represented by (2-1), one R ₂ is an alkyl group which may have a substituent, and the other two R ₂ are bonded to each other to form a monocyclic cycloalkyl. In some cases, one R ₂ is a methyl group or an ethyl group, and the other two R ₂ are bonded to each other to form a cyclopentyl group, a cyclohexyl group, or a cycloheptyl group. Can be mentioned. Further, as a preferred example of the group represented by (2-2), one R ₃ is a polycyclic cyclic alkyl group which may have a substituent, and the other two R ₃ have a substituent. In particular, one R ₃ is an adamantyl group which may have a substituent, a norbornane group which may have a substituent, A case where two R ₃ form a methyl group or an ethyl group is exemplified.

  In order to enhance the effect of the present invention, it is preferable to use one or more protective groups selected from the above (2-1) or (2-2) in combination, and from (2-1) to one or more, (2 It is particularly preferable to select one or more types from -2) and use them in combination.

As for content of the repeating unit which has an acid-decomposable group, 20-60 mol% is preferable with respect to all the repeating units in a polymer, More preferably, it is 25-55 mol%.
When (2-1) and (2-2) are used in combination, the content is preferably 5 to 55 mol%.
Although the specific example of the repeating unit which has a preferable acid-decomposable group is shown below, this invention is not limited to this.

The resin of component (A) preferably has a repeating unit having a hydroxyl group or a cyano group. This improves the substrate adhesion and developer compatibility. The repeating unit having a hydroxyl group or a cyano group is preferably a repeating unit having an alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group. The alicyclic hydrocarbon structure in the alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group is preferably an adamantyl group, a diamantyl group, or a norbornane group. As the alicyclic hydrocarbon structure substituted with a preferred hydroxyl group or cyano group, partial structures represented by the following general formulas (VIIa) to (VIId) are preferred.

In general formulas (VIIa) to (VIIc),
R ₂ c to R ₄ c each independently represents a hydrogen atom, a hydroxyl group or a cyano group. However, at least one of R ₂ c to R ₄ c represents a hydroxyl group or a cyano group. Preferably, one or two of R ₂ c to R ₄ c are a hydroxyl group and the remaining is a hydrogen atom. In general formula (VIIa), more preferably, _two of R ₂ c to R ₄ c are hydroxyl groups and the remaining are hydrogen atoms.

Examples of the repeating unit having a partial structure represented by the general formulas (VIIa) to (VIId) include the repeating units represented by the following general formulas (AIIa) to (AIId).

In the general formulas (AIIa) to (AIId),
R ₁ c represents a hydrogen atom, a methyl group, a trifluoromethyl group or a hydroxymethyl group.
R ₂ c to R ₄ c are in the general formula (VIIa) ~ (VIIc), same meanings as R ₂ c~R ₄ c.

The content of the repeating unit having an alicyclic hydrocarbon structure substituted with a hydroxyl group or a cyano group is preferably 5 to 40 mol%, more preferably 5 to 30 mol%, still more preferably 10 with respect to all repeating units in the polymer. ˜25 mol%.
Specific examples of the repeating unit having a hydroxyl group or a cyano group are given below, but the present invention is not limited thereto.

  The resin of component (A) preferably has a repeating unit having an alkali-soluble group. Examples of the alkali-soluble group include a carboxyl group, a sulfonamide group, a sulfonylimide group, a bisulsulfonylimide group, and an aliphatic alcohol (for example, hexafluoroisopropanol group) substituted with an electron-attracting group at the α-position. It is more preferable to have a repeating unit. By containing the repeating unit having an alkali-soluble group, the resolution in contact hole applications is increased. The repeating unit having an alkali-soluble group includes a repeating unit in which an alkali-soluble group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or an alkali in the main chain of the resin through a linking group. Either a repeating unit to which a soluble group is bonded, or a polymerization initiator or chain transfer agent having an alkali-soluble group is used at the time of polymerization and introduced at the end of the polymer chain, and the linking group is monocyclic or polycyclic. It may have a cyclic hydrocarbon structure. Particularly preferred are repeating units of acrylic acid or methacrylic acid.

  The content of the repeating unit having an alkali-soluble group is preferably from 0 to 25 mol%, more preferably from 3 to 20 mol%, still more preferably from 5 to 15 mol%, based on all repeating units in the polymer.

Specific examples of the repeating unit having an alkali-soluble group are shown below, but the present invention is not limited thereto. In specific examples, Rx represents H, CH ₃ , CH ₂ OH, or CF ₃ .

  The resin of component (A) may further have a repeating unit that has an alicyclic hydrocarbon structure and does not exhibit acid decomposability. This can reduce the elution of low molecular components from the resist film to the immersion liquid during immersion exposure. Examples of such a repeating unit include 1-adamantyl (meth) acrylate, diamantyl (meth) acrylate, tricyclodecanyl (meth) acrylate, and cyclohexyl (meth) acrylate repeating units.

The resin (A) of the present invention preferably further has a repeating unit that has an alicyclic hydrocarbon structure having no polar group and does not exhibit acid decomposability. This can reduce the elution of low molecular components from the resist film to the immersion liquid during immersion exposure. An example of such a repeating unit is a repeating unit represented by the following general formula (3).

In general formula (3), R ₅ represents a hydrocarbon group having at least one cyclic structure and having neither a hydroxyl group nor a cyano group.
Ra represents a hydrogen atom, an alkyl group, or a —CH ₂ —O—Ra ₂ group. In the formula, Ra ₂ represents a hydrogen atom, an alkyl group or an acyl group. Ra is preferably a hydrogen atom, a methyl group, a hydroxymethyl group or a trifluoromethyl group, particularly preferably a hydrogen atom or a methyl group.

The cyclic structure possessed by R ₅ includes a monocyclic hydrocarbon group and a polycyclic hydrocarbon group. Examples of the monocyclic hydrocarbon group include a cycloalkyl group having 3 to 12 carbon atoms and a cycloalkenyl group having 3 to 12 carbon atoms. A preferable monocyclic hydrocarbon group is a monocyclic hydrocarbon group having 3 to 7 carbon atoms.

  The polycyclic hydrocarbon group includes a ring assembly hydrocarbon group and a bridged cyclic hydrocarbon group. Examples of the bridged cyclic hydrocarbon ring include a bicyclic hydrocarbon ring, a tricyclic hydrocarbon ring, and a tetracyclic hydrocarbon ring. The bridged cyclic hydrocarbon ring also includes a condensed cyclic hydrocarbon ring (for example, a condensed ring in which a plurality of 5- to 8-membered cycloalkane rings are condensed). Preferred examples of the bridged cyclic hydrocarbon ring include a norbornyl group and an adamantyl group.

  These alicyclic hydrocarbon groups may have a substituent, and preferred substituents include a halogen atom, an alkyl group, a hydroxyl group protected with a protecting group, an amino group protected with a protecting group, and the like. It is done. Preferred halogen atoms include bromine, chlorine and fluorine atoms, and preferred alkyl groups include methyl, ethyl, butyl and t-butyl groups. The above alkyl group may further have a substituent, and the substituent that may further have a halogen atom, an alkyl group, a hydroxyl group protected with a protecting group, an amino protected with a protecting group The group can be mentioned.

  Examples of the protecting group include an alkyl group, a cycloalkyl group, an aralkyl group, a substituted methyl group, a substituted ethyl group, an alkoxycarbonyl group, and an aralkyloxycarbonyl group. Preferred alkyl groups include alkyl groups having 1 to 4 carbon atoms, preferred substituted methyl groups include methoxymethyl, methoxythiomethyl, benzyloxymethyl, t-butoxymethyl, 2-methoxyethoxymethyl groups, and preferred substituted ethyl groups. 1-ethoxyethyl, 1-methyl-1-methoxyethyl, preferred acyl groups include formyl, acetyl, propionyl, butyryl, isobutyryl, valeryl, pivaloyl groups, etc., aliphatic acyl groups having 1 to 6 carbon atoms, alkoxycarbonyl Examples of the group include an alkoxycarbonyl group having 1 to 4 carbon atoms.

The content of the repeating unit having an alicyclic hydrocarbon structure having no polar group and not exhibiting acid decomposability is preferably 0 to 40 mol%, more preferably, based on all repeating units in the resin (A). 0 to 20 mol%.
Specific examples of the repeating unit having an alicyclic hydrocarbon structure having no polar group and not exhibiting acid decomposability are shown below, but the present invention is not limited thereto. In the formula, Ra represents H, CH ₃ , CH ₂ OH, or CF ₃ .

  Resin (A) adjusts dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and resolution, heat resistance, sensitivity, etc., which are general required characteristics of resist, in addition to the above repeating structural units. For this purpose, various repeating structural units can be included.

  Examples of such repeating structural units include, but are not limited to, repeating structural units corresponding to the following monomers.

  As a result, the performance required for the resin (A), in particular, (1) solubility in coating solvents, (2) film-forming properties (glass transition point), (3) alkali developability, (4) film slipping (familiarity) Fine adjustments such as (selection of aqueous and alkali-soluble groups), (5) adhesion of unexposed portions to the substrate, and (6) dry etching resistance are possible.

  As such a monomer, for example, a compound having one addition polymerizable unsaturated bond selected from acrylic acid esters, methacrylic acid esters, acrylamides, methacrylamides, allyl compounds, vinyl ethers, vinyl esters, etc. Etc.

  In addition, any addition-polymerizable unsaturated compound that can be copolymerized with monomers corresponding to the above various repeating structural units may be copolymerized.

  In the resin (A), the molar ratio of each repeating structural unit is the resist dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and the general required performance of the resist, resolving power, heat resistance, sensitivity. It is set appropriately in order to adjust etc.

  In the resin of component (A), the molar ratio of each repeating structural unit is the resist dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and general resist performance required for resolving power and heat resistance. In order to adjust sensitivity and the like, it is set appropriately.

When the composition of the present invention is for ArF exposure, the resin of component (A) preferably has no aromatic group from the viewpoint of transparency to ArF light.
Moreover, it is preferable that resin (A) does not contain a fluorine atom and a silicon atom from a compatible viewpoint with hydrophobic resin (HR) mentioned later.

  The resin of component (A) can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and the polymerization is performed by heating, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable. Examples of the reaction solvent include ethers such as tetrahydrofuran, 1,4-dioxane, diisopropyl ether, ketones such as methyl ethyl ketone and methyl isobutyl ketone, ester solvents such as ethyl acetate, amide solvents such as dimethylformamide and dimethylacetamide, Furthermore, the solvent which melt | dissolves the composition of this invention like the below-mentioned propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, and cyclohexanone is mentioned. More preferably, the polymerization is performed using the same solvent as the solvent used in the positive photosensitive composition of the present invention. Thereby, generation | occurrence | production of the particle at the time of a preservation | save can be suppressed.

  The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred initiators include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. If desired, an initiator is added or added in portions, and after completion of the reaction, it is put into a solvent and a desired polymer is recovered by a method such as powder or solid recovery. The concentration of the reaction is 5 to 50% by mass, preferably 10 to 30% by mass. The reaction temperature is usually 10 ° C to 150 ° C, preferably 30 ° C to 120 ° C, more preferably 60-100 ° C.

  The weight average molecular weight of the component (A) resin is preferably 1,000 to 200,000, more preferably 2,000 to 20,000, and still more preferably 3,000 as a polystyrene-converted value by the GPC method. ˜15,000, particularly preferably 3,000 to 10,000. By setting the weight average molecular weight to 1,000 to 200,000, deterioration of heat resistance and dry etching resistance can be prevented, developability is deteriorated, and viscosity is increased, resulting in deterioration of film forming property. Can be prevented.

  The degree of dispersion (molecular weight distribution) is usually 1 to 3, preferably 1 to 2.6, more preferably 1 to 2, and particularly preferably 1.4 to 1.7. The smaller the molecular weight distribution, the better the resolution and the resist shape, and the smoother the side wall of the resist pattern, the better the roughness.

In the composition of the present invention, the blending amount of the resin of the component (A) in the entire composition is preferably 50 to 99.90% by mass, more preferably 60 to 99.0% by mass in the total solid content. .
In the present invention, the resin of component (A) may be used alone or in combination.

(B) Compound that generates acid upon irradiation with actinic ray or radiation The composition of the present invention contains a compound that generates acid upon irradiation with actinic ray or radiation (hereinafter also referred to as “acid generator”).
As an acid generator, photo-initiator of photocation polymerization, photo-initiator of photo-radical polymerization, photo-decoloring agent of dyes, photo-discoloring agent, or irradiation with actinic ray or radiation used for micro-resist etc. Known compounds that generate acids and mixtures thereof can be appropriately selected and used.

  Examples thereof include diazonium salts, phosphonium salts, sulfonium salts, iodonium salts, imide sulfonates, oxime sulfonates, diazodisulfones, disulfones, and o-nitrobenzyl sulfonates.

Further, a group that generates an acid upon irradiation with these actinic rays or radiation, or a compound in which a compound is introduced into the main chain or side chain of the polymer, such as US Pat. No. 3,849,137, German Patent No. No. 3914407, JP-A 63-26653, JP-A 55-164824, JP-A 62-69263, JP-A 63-146038, JP-A 63-163452, The compounds described in JP-A-62-153853 and JP-A-63-146029 can be used.

Furthermore, compounds capable of generating an acid by light described in US Pat. No. 3,779,778, European Patent 126,712, etc. can also be used.
Preferred compounds among the acid generators include compounds represented by the following general formulas (ZI), (ZII), and (ZIII).

In the general formula (ZI),
R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.
The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1 to 30, preferably 1
~ 20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. The two of the group formed by bonding of the R ₂₀₁ to R _203, there can be mentioned an alkylene group (e.g., butylene, pentylene).
Z ⁻ represents a non-nucleophilic anion.

Examples of the non-nucleophilic anion as Z ⁻ include a sulfonate anion, a carboxylate anion, a sulfonylimide anion, a bis (alkylsulfonyl) imide anion, and a tris (alkylsulfonyl) methyl anion.

  A non-nucleophilic anion is an anion that has an extremely low ability to cause a nucleophilic reaction, and is an anion that can suppress degradation over time due to an intramolecular nucleophilic reaction. This improves the temporal stability of the resist.

  Examples of the sulfonate anion include an aliphatic sulfonate anion, an aromatic sulfonate anion, and a camphor sulfonate anion.

  Examples of the carboxylate anion include an aliphatic carboxylate anion, an aromatic carboxylate anion, and an aralkylcarboxylate anion.

  The aliphatic moiety in the aliphatic sulfonate anion may be an alkyl group or a cycloalkyl group, preferably an alkyl group having 1 to 30 carbon atoms and a cycloalkyl group having 3 to 30 carbon atoms such as methyl. Group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, pentyl group, neopentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group , Tridecyl group, tetradecyl group, pentadecyl group, hexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, eicosyl group, cyclopropyl group, cyclopentyl group, cyclohexyl group, adamantyl group, norbornyl group, bornyl group and the like.

  The aromatic group in the aromatic sulfonate anion is preferably an aryl group having 6 to 14 carbon atoms, such as a phenyl group, a tolyl group, and a naphthyl group.

  The alkyl group, cycloalkyl group and aryl group in the aliphatic sulfonate anion and aromatic sulfonate anion may have a substituent. Examples of the substituent of the alkyl group, cycloalkyl group, and aryl group in the aliphatic sulfonate anion and aromatic sulfonate anion include, for example, a nitro group, a halogen atom (fluorine atom, chlorine atom, bromine atom, iodine atom), carboxyl group , Hydroxyl group, amino group, cyano group, alkoxy group (preferably having 1 to 15 carbon atoms), cycloalkyl group (preferably having 3 to 15 carbon atoms), aryl group (preferably having 6 to 14 carbon atoms), alkoxycarbonyl group ( Preferably 2 to 7 carbon atoms, acyl group (preferably 2 to 12 carbon atoms), alkoxycarbonyloxy group (preferably 2 to 7 carbon atoms), alkylthio group (preferably 1 to 15 carbon atoms), alkylsulfonyl group (Preferably having 1 to 15 carbon atoms), alkyliminosulfonyl group (preferably having 2 to 15 carbon atoms), aryl Ruoxysulfonyl group (preferably having 6 to 20 carbon atoms), alkylaryloxysulfonyl group (preferably having 7 to 20 carbon atoms), cycloalkylaryloxysulfonyl group (preferably having 10 to 20 carbon atoms), alkyloxyalkyloxy group (Preferably having 5 to 20 carbon atoms), a cycloalkylalkyloxyalkyloxy group (preferably having 8 to 20 carbon atoms), and the like. About the aryl group and ring structure which each group has, an alkyl group (preferably C1-C15) can further be mentioned as a substituent.

Examples of the aliphatic moiety in the aliphatic carboxylate anion include the same alkyl group and cycloalkyl group as in the aliphatic sulfonate anion.
Examples of the aromatic group in the aromatic carboxylate anion include the same aryl group as in the aromatic sulfonate anion.

  The aralkyl group in the aralkyl carboxylate anion is preferably an aralkyl group having 6 to 12 carbon atoms, such as benzyl group, phenethyl group, naphthylmethyl group, naphthylethyl group, naphthylbutyl group, and the like.

The alkyl group, cycloalkyl group, aryl group and aralkyl group in the aliphatic carboxylate anion, aromatic carboxylate anion and aralkylcarboxylate anion may have a substituent. Examples of the substituent of the alkyl group, cycloalkyl group, aryl group and aralkyl group in the aliphatic carboxylate anion, aromatic carboxylate anion and aralkylcarboxylate anion include, for example, the same halogen atom and alkyl as in the aromatic sulfonate anion Group, cycloalkyl group, alkoxy group, alkylthio group and the like.
Examples of the sulfonylimide anion include saccharin anion.

  The alkyl group in the bis (alkylsulfonyl) imide anion and tris (alkylsulfonyl) methyl anion is preferably an alkyl group having 1 to 5 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, An isobutyl group, a sec-butyl group, a pentyl group, a neopentyl group, and the like can be given. Examples of substituents for these alkyl groups include halogen atoms, alkyl groups substituted with halogen atoms, alkoxy groups, alkylthio groups, alkyloxysulfonyl groups, aryloxysulfonyl groups, cycloalkylaryloxysulfonyl groups, and the like. Alkyl groups substituted with fluorine atoms are preferred.

  Examples of other non-nucleophilic anions include fluorinated phosphorus, fluorinated boron, and fluorinated antimony.

Examples of the non-nucleophilic anion of Z ⁻ include an aliphatic sulfonate anion in which the α-position of the sulfonic acid is substituted with a fluorine atom, an aromatic sulfonate anion substituted with a fluorine atom or a group having a fluorine atom, and an alkyl group. A bis (alkylsulfonyl) imide anion substituted with a fluorine atom and a tris (alkylsulfonyl) methide anion wherein an alkyl group is substituted with a fluorine atom are preferred. The non-nucleophilic anion is more preferably a perfluoroaliphatic sulfonic acid anion having 4 to 8 carbon atoms, a benzenesulfonic acid anion having a fluorine atom, still more preferably a nonafluorobutanesulfonic acid anion, a perfluorooctanesulfonic acid anion, It is a pentafluorobenzenesulfonic acid anion and 3,5-bis (trifluoromethyl) benzenesulfonic acid anion.

Examples of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ include the corresponding groups in the compounds (ZI-1), (ZI-2) and (ZI-3) described later.

In addition, the compound which has two or more structures represented by general formula (ZI) may be sufficient. For example, the general formula at least one of R ₂₀₁ to R ₂₀₃ of a compound represented by (ZI), the structures attached to at least one of R ₂₀₁ to R ₂₀₃ of another compound represented by formula (ZI) It may be a compound.

  More preferred (ZI) components include compounds (ZI-1), (ZI-2), (ZI-3) and (ZI-4) described below.

The compound (ZI-1) is at least one of the aryl groups R ₂₀₁ to R ₂₀₃ in formula (ZI), arylsulfonium compounds, namely, compounds containing an arylsulfonium as a cation.

In the arylsulfonium compound, all of R _{201 to} R ₂₀₃ may be an aryl group, or a part of R _{201 to} R ₂₀₃ may be an aryl group with the remaining being an alkyl group or a cycloalkyl group.

  Examples of the arylsulfonium compound include triarylsulfonium compounds, diarylalkylsulfonium compounds, aryldialkylsulfonium compounds, diarylcycloalkylsulfonium compounds, and aryldicycloalkylsulfonium compounds.

  The aryl group of the arylsulfonium compound is preferably a phenyl group or a naphthyl group, and more preferably a phenyl group. The aryl group may be an aryl group having a heterocyclic structure having an oxygen atom, a nitrogen atom, a sulfur atom or the like. Examples of the aryl group having a heterocyclic structure include a pyrrole residue (a group formed by losing one hydrogen atom from pyrrole) and a furan residue (a group formed by losing one hydrogen atom from furan). Groups), thiophene residues (groups formed by the loss of one hydrogen atom from thiophene), indole residues (groups formed by the loss of one hydrogen atom from indole), benzofuran residues ( A group formed by losing one hydrogen atom from benzofuran), a benzothiophene residue (a group formed by losing one hydrogen atom from benzothiophene), and the like. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.

  The alkyl group or cycloalkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms and a cycloalkyl group having 3 to 15 carbon atoms, such as a methyl group, Examples thereof include an ethyl group, a propyl group, an n-butyl group, a sec-butyl group, a t-butyl group, a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.

Aryl group, alkyl group of R ₂₀₁ to R _203, cycloalkyl group, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (for example, 6 to 14 carbon atoms) , An alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, or a phenylthio group may be substituted. Preferred substituents are linear or branched alkyl groups having 1 to 12 carbon atoms, cycloalkyl groups having 3 to 12 carbon atoms, and linear, branched or cyclic alkoxy groups having 1 to 12 carbon atoms, more preferably carbon. These are an alkyl group having 1 to 4 carbon atoms and an alkoxy group having 1 to 4 carbon atoms. The substituent may be substituted with any one of the three R _{201 to} R ₂₀₃ , or may be substituted with all three. When R _{201 to} R ₂₀₃ are an aryl group, the substituent is preferably substituted at the p-position of the aryl group.

Next, the compound (ZI-2) will be described.
Compound (ZI-2) is a compound in which R _{201 to} R ₂₀₃ in formula (ZI) each independently represents an organic group having no aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.

The organic group having no aromatic ring as R ₂₀₁ to R ₂₀₃ generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.

R _{201 to} R ₂₀₃ are each independently preferably an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group, more preferably a linear or branched 2-oxoalkyl group, 2-oxocycloalkyl group, alkoxy group. A carbonylmethyl group, particularly preferably a linear or branched 2-oxoalkyl group.

The alkyl group and cycloalkyl group of R ₂₀₁ to R _203, preferably a linear or branched alkyl group having 1 to 10 carbon atoms (e.g., methyl group, ethyl group, propyl group, butyl group, pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group). More preferred examples of the alkyl group include a 2-oxoalkyl group and an alkoxycarbonylmethyl group. More preferred examples of the cycloalkyl group include a 2-oxocycloalkyl group.

  The 2-oxoalkyl group may be either linear or branched, and a group having> C = O at the 2-position of the above alkyl group is preferable.

  The 2-oxocycloalkyl group is preferably a group having> C═O at the 2-position of the cycloalkyl group.

  The alkoxy group in the alkoxycarbonylmethyl group is preferably an alkoxy group having 1 to 5 carbon atoms (methoxy group, ethoxy group, propoxy group, butoxy group, pentoxy group).

R _{201 to} R ₂₀₃ may be further substituted with a halogen atom, an alkoxy group (for example, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.

The compound (ZI-3) is a compound represented by the following general formula (ZI-3), and is a compound having a phenacylsulfonium salt structure.

In general formula (ZI-3),
R _1c to R _5c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an alkoxy group or a halogen atom.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group or a cycloalkyl group.
R _x and R _y independently represents an alkyl group, a cycloalkyl group, an allyl group or a vinyl group.

Any two or more of R _{1c to} R _5c , R _6c and R _7c , and R _x and R _y may be bonded to each other to form a ring structure, and this ring structure includes an oxygen atom and a sulfur atom. , An ester bond and an amide bond may be included. Examples of the group formed by combining any two or more of R _{1c to} R _5c , R _6c and R _7c , and R _x and R _y include a butylene group and a pentylene group.

Zc ⁻ represents a non-nucleophilic anion, and examples thereof include the same non-nucleophilic anion as Z ^{− in} formula (ZI).

The alkyl group as R _1c to R _7c may be linear or branched may be any of, for example, alkyl group having 1 to 20 carbon atoms, preferably 1 to 12 linear or branched alkyl group having a carbon number ( Examples thereof include a methyl group, an ethyl group, a linear or branched propyl group, a linear or branched butyl group, and a linear or branched pentyl group. Examples of the cycloalkyl group include cyclohexane having 3 to 8 carbon atoms. An alkyl group (for example, a cyclopentyl group, a cyclohexyl group) can be mentioned.

The alkoxy group as R _{1c to} R _{5c may} be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably a linear or branched alkoxy group having 1 to 5 carbon atoms. (For example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), C3-C8 cyclic alkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group) ).

Preferably, any of R _{1c to} R _5c is a linear or branched alkyl group, a cycloalkyl group, or a linear, branched or cyclic alkoxy group, and more preferably the sum of the carbon number of R _{1c to} R _5c. Is 2-15. Thereby, solvent solubility improves more and generation | occurrence | production of a particle is suppressed at the time of a preservation | save.

_Examples of the alkyl group and cycloalkyl group as R _x and R _y include the same alkyl group and cycloalkyl group as in R _{1c to} R _7c , such as a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxy group. A carbonylmethyl group is more preferred.

Examples of the 2-oxoalkyl group and 2-oxocycloalkyl group include a group having> C═O at the 2-position of the alkyl group or cycloalkyl group as R _{1c to} R _7c .

Examples of the alkoxy group in the alkoxycarbonylmethyl group include the same alkoxy groups as in R _{1c to} R _5c .

R _x and R _y are preferably an alkyl group or cycloalkyl group having 4 or more carbon atoms, more preferably 6 or more, and still more preferably 8 or more alkyl groups or cycloalkyl groups.

  Next, the compound (ZI-4) will be described.

The compound (ZI-4) is a compound represented by the following general formula (ZI-4).

In general formula (ZI-4),
R ₁₃ represents a hydrogen atom, a fluorine atom, a hydroxyl group, an alkyl group, a cycloalkyl group, an alkoxy group, or an alkoxycarbonyl group.

When a plurality of R ₁₄ are present, each independently represents an alkyl group, a cycloalkyl group, an alkoxy group, an alkylsulfonyl group, or a cycloalkylsulfonyl group.

R ₁₅ each independently represents an alkyl group, a cycloalkyl group, a phenyl group or a naphthyl group. Two R ₁₅ may combine with each other to form a ring.

  l represents an integer of 0-2.

  r represents an integer of 0 to 10.

Z ^- is, Z in formula (ZI) ^- synonymous.

In formula ^(ZI-4), the alkyl group of R ^{13, R 14} and ^{R 15,} may be linear or branched, preferably has 1 to 10 carbon atoms, a methyl group, an ethyl radical, n -Propyl group, i-propyl group, n-butyl group, 2-methylpropyl group, 1-methylpropyl group, t-butyl group, n-pentyl group, neopentyl group, n-hexyl group, n-heptyl group, n -An octyl group, 2-ethylhexyl group, n-nonyl group, n-decyl group etc. can be mentioned. Of these alkyl groups, a methyl group, an ethyl group, an n-butyl group, a t-butyl group, and the like are preferable.

Examples of the cycloalkyl group of R ¹³ , R ¹⁴ and R ¹⁵ include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclododecanyl, cyclobenenyl, cyclohexenyl, cyclooctadienyl and the like. In particular, cyclopropyl, cyclopentyl, cyclohexyl and cyclooctyl are preferred.

The alkoxy group of R ¹³ and R ¹⁴ is linear or branched and preferably has 1 to 10 carbon atoms, such as methoxy group, ethoxy group, n-propoxy group, i-propoxy group, n -Butoxy group, 2-methylpropoxy group, 1-methylpropoxy group, t-butoxy group, n-pentyloxy group, neopentyloxy group, n-hexyloxy group, n-heptyloxy group, n-octyloxy group, 2-ethylhexyloxy group, n-nonyloxy group, n-decyloxy group and the like can be mentioned. Of these alkoxy groups, a methoxy group, an ethoxy group, an n-propoxy group, an n-butoxy group, and the like are preferable.

The alkoxycarbonyl group for R ¹³ is linear or branched and preferably has 2 to 11 carbon atoms, such as a methoxycarbonyl group, an ethoxycarbonyl group, an n-propoxycarbonyl group, or an i-propoxycarbonyl group. N-butoxycarbonyl group, 2-methylpropoxycarbonyl group, 1-methylpropoxycarbonyl group, t-butoxycarbonyl group, n-pentyloxycarbonyl group, neopentyloxycarbonyl group, n-hexyloxycarbonyl group, n-heptyl Examples thereof include an oxycarbonyl group, an n-octyloxycarbonyl group, a 2-ethylhexyloxycarbonyl group, an n-nonyloxycarbonyl group, and an n-decyloxycarbonyl group. Of these alkoxycarbonyl groups, a methoxycarbonyl group, an ethoxycarbonyl group, an n-butoxycarbonyl group, and the like are preferable.

The alkylsulfonyl group and cycloalkylsulfonyl group of R ¹⁴ are linear, branched, or cyclic, and preferably those having 1 to 10 carbon atoms, such as methanesulfonyl group, ethanesulfonyl group, n-propanesulfonyl. Group, n-butanesulfonyl group, tert-butanesulfonyl group, n-pentanesulfonyl group, neopentanesulfonyl group, n-hexanesulfonyl group, n-heptanesulfonyl group, n-octanesulfonyl group, 2-ethylhexanesulfonyl group n -Nonanesulfonyl group, n-decanesulfonyl group, cyclopentanesulfonyl group, cyclohexanesulfonyl group, etc. can be mentioned. Of these alkylsulfonyl groups, a methanesulfonyl group, an ethanesulfonyl group, an n-propanesulfonyl group, an n-butanesulfonyl group, a cyclopentanesulfonyl group, a cyclohexanesulfonyl group, and the like are preferable.
As r, 0-2 are preferable.

In the general formula (ZI-4), the phenyl group represented by R ¹⁵ may be substituted. For example, the phenyl group, o-tolyl group, m-tolyl group, p-tolyl group, 2,3-dimethylphenyl Group, 2,4-dimethylphenyl group, 2,5-dimethylphenyl group, 2,6-dimethylphenyl group, 3,4-dimethylphenyl group, 3,5-dimethylphenyl group, 2,4,6-trimethylphenyl Group, 4-ethylphenyl group, 4-t-butylphenyl group, 4-cyclohexylphenyl group, 4-fluorophenyl group or the like phenyl group or linear, branched or cyclic alkyl group having 1 to 10 carbon atoms A phenyl group substituted with a hydroxyl group, a carboxyl group, a cyano group, a nitro group, an alkoxy group, an alkoxy group. Examples include groups substituted with one or more groups such as an alkyl group, an alkoxycarbonyl group, and an alkoxycarbonyloxy group.

  Among the substituents for the phenyl group and the alkyl-substituted phenyl group, examples of the alkoxy group include a methoxy group, an ethoxy group, an n-propoxy group, an i-propoxy group, an n-butoxy group, a 2-methylpropoxy group, 1- Examples thereof include linear, branched or cyclic alkoxy groups having 1 to 20 carbon atoms such as a methylpropoxy group, a t-butoxy group, a cyclopentyloxy group, and a cyclohexyloxy group.

  Examples of the alkoxyalkyl group include straight chain having 2 to 21 carbon atoms such as methoxymethyl group, ethoxymethyl group, 1-methoxyethyl group, 2-methoxyethyl group, 1-ethoxyethyl group, and 2-ethoxyethyl group. Examples thereof include a chain, branched or cyclic alkoxyalkyl group. Examples of the alkoxycarbonyl group include a methoxycarbonyl group, an ethoxycarbonyl group, an n-propoxycarbonyl group, an i-propoxycarbonyl group, an n-butoxycarbonyl group, a 2-methylpropoxycarbonyl group, and a 1-methylpropoxycarbonyl group. , T-butoxycarbonyl group, cyclopentyloxycarbonyl group, cyclohexyloxycarbonyl and the like, and straight chain, branched or cyclic alkoxycarbonyl groups having 2 to 21 carbon atoms.

Examples of the alkoxycarbonyloxy group include methoxycarbonyloxy group, ethoxycarbonyloxy group, n-propoxycarbonyloxy group, i-propoxycarbonyloxy group, n-butoxycarbonyloxy group, t-butoxycarbonyloxy group, and cyclopentyloxy. Examples thereof include linear, branched or cyclic alkoxycarbonyloxy groups having 2 to 21 carbon atoms such as carbonyl group and cyclohexyloxycarbonyl. Examples of the optionally substituted phenyl group for R ^{15 in} the general formula (ZI-4) include a phenyl group, a 4-cyclohexylphenyl group, a 4-t-butylphenyl group, a 4-methoxyphenyl group, and 4-t-butoxy. A phenyl group and the like are preferable.

Examples of the optionally substituted naphthyl group for R ¹⁵ include 1-naphthyl group, 2-methyl-1-naphthyl group, 3-methyl-1-naphthyl group, 4-methyl-1-naphthyl group, 4- Methyl-1-naphthyl group, 5-methyl-1-naphthyl group, 6-methyl-1-naphthyl group, 7-methyl-1-naphthyl group, 8-methyl-1-naphthyl group, 2,3-dimethyl-1 -Naphthyl group, 2,4-dimethyl-1-naphthyl group, 2,5-dimethyl-1-naphthyl group, 2,6-dimethyl-1-naphthyl group, 2,7-dimethyl-1-naphthyl group, 2, 8-dimethyl-1-naphthyl group, 3,4-dimethyl-1-naphthyl group, 3,5-dimethyl-1-naphthyl group, 3,6-dimethyl-1-naphthyl group, 3,7-dimethyl-1- Naphthyl group, 3,8-dimethyl-1-naphthyl Group, 4,5-dimethyl-1-naphthyl group, 5,8-dimethyl-1-naphthyl group, 4-ethyl-1-naphthyl group, 2-naphthyl group, 1-methyl-2-naphthyl group, 3-methyl- A naphthyl group substituted with a naphthyl group such as a 2-naphthyl group or 4-methyl-2-naphthyl group or a linear, branched or cyclic alkyl group having 1 to 10 carbon atoms; the naphthyl group or the alkyl substitution And a group in which a naphthyl group is substituted with at least one group such as a hydroxyl group, a carboxyl group, a cyano group, a nitro group, an alkoxy group, an alkoxyalkyl group, an alkoxycarbonyl group, and an alkoxycarbonyloxy group. it can.

Examples of the alkoxy group, alkoxyalkyl group, alkoxycarbonyl group, and alkoxycarbonyloxy group as the substituent include the groups exemplified for the phenyl group and the alkyl-substituted phenyl group. Examples of the optionally substituted naphthyl group of R ^{15 in} the general formula (ZI-4) include 1-naphthyl group, 1- (4-methoxynaphthyl) group, 1- (4-ethoxynaphthyl) group, 1- ( 4-n-propoxynaphthyl) group, 1- (4-n-butoxynaphthyl) group, 2- (7-methoxynaphthyl) group, 2- (7-ethoxynaphthyl) group, 2- (7-n-propoxynaphthyl) group ) Group, 2- (7-n-butoxynaphthyl) group and the like are preferable.

As the ring structure that two R ¹⁵ may be bonded to each other, a 5- or 6-membered ring, particularly preferably a 5-membered ring (that is, a 5-membered ring together with the sulfur atom in the general formula (ZI-4) (that is, A group that forms a tetrahydrothiophene ring) is desirable. Examples of the substituent for the divalent group include a hydroxyl group, a carboxyl group, a cyano group, a nitro group, an alkoxy group, an alkoxyalkyl group, an alkoxy group exemplified as the substituent for the phenyl group and the alkyl-substituted phenyl group. Examples thereof include a carbonyl group and an alkoxycarbonyloxy group. As R ¹⁵ in the general formula (6), a methyl group, an ethyl group, a phenyl group, a 4-methoxyphenyl group, a 1-naphthyl group, and two R ¹⁵ are bonded to each other to form a tetrahydrothiophene ring structure together with a sulfur atom. A divalent group is preferred.
Preferred specific examples of the cation in the compound represented by the general formula (ZI-4) are shown below.

Although the compound shown below is mentioned as a compound which generate | occur | produces the sulfonic acid represented by general formula (ZI-4), It is not limited to these.

Next, general formulas (ZII) and (ZIII) will be described.
In general formulas (ZII) and (ZIII),
R ₂₀₄ to R ₂₀₇ each independently represents an aryl group, an alkyl group or a cycloalkyl group.

Phenyl group and a naphthyl group are preferred as the aryl group of R ₂₀₄ to R _207, more preferably a phenyl group. Aryl group R ₂₀₄ to R ₂₀₇ represents an oxygen atom, a nitrogen atom, may be an aryl group having a heterocyclic structure having a sulfur atom and the like. Examples of the aryl group having a heterocyclic structure include a pyrrole residue (a group formed by losing one hydrogen atom from pyrrole) and a furan residue (a group formed by losing one hydrogen atom from furan). Groups), thiophene residues (groups formed by the loss of one hydrogen atom from thiophene), indole residues (groups formed by the loss of one hydrogen atom from indole), benzofuran residues ( A group formed by losing one hydrogen atom from benzofuran), a benzothiophene residue (a group formed by losing one hydrogen atom from benzothiophene), and the like.

The alkyl group and cycloalkyl group in R ₂₀₄ to R _207, preferably a linear or branched alkyl group having 1 to 10 carbon atoms (e.g., methyl group, ethyl group, propyl group, butyl group, pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group).

Aryl group, alkyl group of R ₂₀₄ to R _207, cycloalkyl groups may have a substituent. Aryl group, alkyl group of R ₂₀₄ to R _207, the cycloalkyl group substituent which may be possessed by, for example, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms ), An aryl group (for example, having 6 to 15 carbon atoms), an alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, and a phenylthio group.

Z ⁻ represents a non-nucleophilic anion, and examples thereof include the same as the non-nucleophilic anion of Z ^{− in} formula (ZI).

Examples of the acid generator further include compounds represented by the following general formulas (ZIV), (ZV), and (ZVI).

In general formulas (ZIV) to (ZVI),
Ar ₃ and Ar ₄ each independently represents an aryl group.
R ₂₀₈ , R ₂₀₉ and R ₂₁₀ each independently represents an alkyl group, a cycloalkyl group or an aryl group.
A represents an alkylene group, an alkenylene group or an arylene group.
Among the acid generators, compounds represented by the general formulas (ZI) to (ZIII) are more preferable.

Further, the acid generator is preferably a compound that generates an acid having one sulfonic acid group or imide group, more preferably a compound that generates monovalent perfluoroalkanesulfonic acid, or a monovalent fluorine atom or fluorine atom. A compound that generates an aromatic sulfonic acid substituted with a group containing fluorinated acid, or a compound that generates a monovalent fluorine atom or imide acid substituted with a group containing a fluorine atom, and even more preferably, It is a sulfonium salt of a substituted alkanesulfonic acid, a fluorine-substituted benzenesulfonic acid, a fluorine-substituted imide acid or a fluorine-substituted methide acid. The acid generator that can be used is particularly preferably a fluorinated substituted alkane sulfonic acid, a fluorinated substituted benzene sulfonic acid or a fluorinated substituted imido acid whose pKa of the generated acid is pKa = -1 or less, and the sensitivity is improved. .
Among acid generators, particularly preferred examples are given below.

In order to improve the effect of the present invention, a compound represented by the following general formula (I) can be given as a particularly preferred compound (B).

In the formula, X ⁺ represents an organic counter ion, and R represents a hydrogen atom or a substituent having 1 or more carbon atoms which may have a substituent.
R is preferably an organic group having 1 to 40 carbon atoms, more preferably an organic group having 3 to 40 carbon atoms, and most preferably an organic group represented by the following formula (II).

  In Formula II, Rc is a cyclic ether, a cyclic thioether, a cyclic ketone, a cyclic carbonate, a lactone, a monocyclic or polycyclic organic group having 3 to 30 carbon atoms that may contain a lactam structure, and Y is a hydroxyl group , Halogen atom, cyano group, carboxyl group, hydrocarbon group having 1 to 10 carbon atoms, hydroxyalkyl group having 1 to 10 carbon atoms, alkoxy group having 1 to 10 carbon atoms, acyl group having 1 to 10 carbon atoms, carbon number Represents an alkoxycarbonyl group having 2 to 10 carbon atoms, an acyloxy group having 2 to 10 carbon atoms, an alkoxyalkyl group having 2 to 10 carbon atoms, a halogenated alkyl group having 1 to 8 carbon atoms, m = 0 to 6, and a plurality of Y When present, they may be the same or different from each other, n = 0 to 10, and the total number of carbon atoms constituting the R group is preferably 40 or less.

In the compound of the general formula (I), preferred examples include compounds of the general formula Z _SC1 and general formula Z _IC1 .

In the above general formula (Z _SC1 ),
The definition and preferred range of R are the same as the definition in general formula (I).
R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.

The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1-30, preferably 1-20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. The two of the group formed by bonding of the R ₂₀₁ to R _203, there can be mentioned an alkylene group (e.g., butylene, pentylene).

Examples of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ include corresponding groups in the compounds (Z _SC1-1 ), (Z _SC1 -2) and (Z _SC1-3 ) which will be described later.

A compound having a plurality of structures represented by the general formula (Z _SC1 ) may also be used. For example, the general formula at least one of R ₂₀₁ to R ₂₀₃ of a compound represented by (Z _SC1), bound to at least one of R ₂₀₁ to R ₂₀₃ of another compound represented by the general formula (Z _SC1) It may be a compound having a structure.

More preferred (Z _SC1 ) components include the compounds (Z _SC1 -1), (Z _SC1 -2), and (Z _SC1 -3) described below.

The compound (Z _SC1-1 ) is an arylsulfonium compound in which at least one of R _{201 to} R _{203 in} the general formula (Z _SC1 ) is an aryl group, that is, a compound having arylsulfonium as a cation.
The definition and preferred range of R are the same as the definition in general formula (I).

In the arylsulfonium compound, all of R _{201 to} R ₂₀₃ may be an aryl group, or a part of R _{201 to} R ₂₀₃ may be an aryl group with the remaining being an alkyl group or a cycloalkyl group.

  Examples of the arylsulfonium compound include triarylsulfonium compounds, diarylalkylsulfonium compounds, aryldialkylsulfonium compounds, diarylcycloalkylsulfonium compounds, and aryldicycloalkylsulfonium compounds.

  The aryl group of the arylsulfonium compound is preferably a phenyl group or a naphthyl group, and more preferably a phenyl group. The aryl group may be an aryl group having a heterocyclic structure having an oxygen atom, a nitrogen atom, a sulfur atom or the like. Examples of the aryl group having a heterocyclic structure include a pyrrole residue (a group formed by losing one hydrogen atom from pyrrole) and a furan residue (a group formed by losing one hydrogen atom from furan). Groups), thiophene residues (groups formed by the loss of one hydrogen atom from thiophene), indole residues (groups formed by the loss of one hydrogen atom from indole), benzofuran residues ( A group formed by losing one hydrogen atom from benzofuran), a benzothiophene residue (a group formed by losing one hydrogen atom from benzothiophene), and the like. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.

  The alkyl group or cycloalkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms and a cycloalkyl group having 3 to 15 carbon atoms, such as a methyl group, Examples thereof include an ethyl group, a propyl group, an n-butyl group, a sec-butyl group, a t-butyl group, a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.

Aryl group, alkyl group of R ₂₀₁ to R _203, cycloalkyl group, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (for example, 6 to 14 carbon atoms) , An alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, or a phenylthio group may be substituted. Preferred substituents are linear or branched alkyl groups having 1 to 12 carbon atoms, cycloalkyl groups having 3 to 12 carbon atoms, and linear, branched or cyclic alkoxy groups having 1 to 12 carbon atoms, more preferably carbon. These are an alkyl group having 1 to 4 carbon atoms and an alkoxy group having 1 to 4 carbon atoms. The substituent may be substituted with any one of the three R _{201 to} R ₂₀₃ , or may be substituted with all three. When R _{201 to} R ₂₀₃ are an aryl group, the substituent is preferably substituted at the p-position of the aryl group.

Next, the compound (Z _SC1-2 ) will be described.
The definition and preferred range of R are the same as the definition in general formula (I).
The compound (Z _SC1 -2) is a compound in which R _{201 to} R ₂₀₃ in the formula (Z _SC1 ) each independently represents an organic group having no aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.

The organic group having no aromatic ring as R ₂₀₁ to R ₂₀₃ generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.

R _{201 to} R ₂₀₃ are each independently preferably an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group, more preferably a linear or branched 2-oxoalkyl group, 2-oxocycloalkyl group, alkoxy group. A carbonylmethyl group, particularly preferably a linear or branched 2-oxoalkyl group.

The alkyl group and cycloalkyl group of R ₂₀₁ to R _203, preferably a linear or branched alkyl group having 1 to 10 carbon atoms (e.g., methyl group, ethyl group, propyl group, butyl group, pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group). More preferred examples of the alkyl group include a 2-oxoalkyl group and an alkoxycarbonylmethyl group. More preferred examples of the cycloalkyl group include a 2-oxocycloalkyl group.

The 2-oxoalkyl group may be either linear or branched, and a group having> C = O at the 2-position of the above alkyl group is preferable.
The 2-oxocycloalkyl group is preferably a group having> C═O at the 2-position of the cycloalkyl group.

The alkoxy group in the alkoxycarbonylmethyl group is preferably an alkoxy group having 1 to 5 carbon atoms (methoxy group, ethoxy group, propoxy group, butoxy group, pentoxy group).
R _{201 to} R ₂₀₃ may be further substituted with a halogen atom, an alkoxy group (for example, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.
The compound (Z _SC1 -3) is a compound represented by the following general formula (Z _SC1 -3), and is a compound having a phenacylsulfonium salt structure.

In the general formula (Z _SC1 -3),
The definition and preferred range of R are the same as the definition in general formula (I).
R _1c to R _5c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an alkoxy group or a halogen atom.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group or a cycloalkyl group.
R _x and R _y independently represents an alkyl group, a cycloalkyl group, an allyl group or a vinyl group.

Any two or more of R _{1c to} R _5c , R _6c and R _7c , and R _x and R _y may be bonded to each other to form a ring structure, and this ring structure includes an oxygen atom and a sulfur atom. , An ester bond and an amide bond may be included. Examples of the group formed by combining any two or more of R _{1c to} R _5c , R _6c and R _7c , and R _x and R _y include a butylene group and a pentylene group.

The alkyl group as R _1c to R _7c may be linear or branched may be any of, for example, alkyl group having 1 to 20 carbon atoms, preferably 1 to 12 linear or branched alkyl group having a carbon number ( Examples thereof include a methyl group, an ethyl group, a linear or branched propyl group, a linear or branched butyl group, and a linear or branched pentyl group. Examples of the cycloalkyl group include cyclohexane having 3 to 8 carbon atoms. An alkyl group (for example, a cyclopentyl group, a cyclohexyl group) can be mentioned.

The alkoxy group as R _{1c to} R _{5c may} be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably a linear or branched alkoxy group having 1 to 5 carbon atoms. (For example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), C3-C8 cyclic alkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group) ).

Preferably, any of R _{1c to} R _5c is a linear or branched alkyl group, a cycloalkyl group, or a linear, branched or cyclic alkoxy group, and more preferably the sum of the carbon number of R _{1c to} R _5c. Is 2-15. Thereby, solvent solubility improves more and generation | occurrence | production of a particle is suppressed at the time of a preservation | save.

_Examples of the alkyl group and cycloalkyl group as R _x and R _y include the same alkyl group and cycloalkyl group as in R _{1c to} R _7c , such as a 2-oxoalkyl group, a 2-oxocycloalkyl group, an alkoxy group. A carbonylmethyl group is more preferred.

Examples of the 2-oxoalkyl group and 2-oxocycloalkyl group include a group having> C═O at the 2-position of the alkyl group or cycloalkyl group as R _{1c to} R _7c .

Examples of the alkoxy group in the alkoxycarbonylmethyl group include the same alkoxy groups as in R _{1c to} R _5c .

R _x and R _y are preferably an alkyl group or cycloalkyl group having 4 or more carbon atoms, more preferably 6 or more, and still more preferably 8 or more alkyl groups or cycloalkyl groups.

In the general formula (Z _IC1 )
The definition and preferred range of R are the same as the definition in general formula (I).
R ₂₀₄ to R ₂₀₅ each independently represents an aryl group, an alkyl group or a cycloalkyl group.

Phenyl group and a naphthyl group are preferred as the aryl group of R ₂₀₄ to R _205, more preferably a phenyl group. Aryl group R ₂₀₄ to R ₂₀₅ represents an oxygen atom, a nitrogen atom, may be an aryl group having a heterocyclic structure having a sulfur atom and the like. Examples of the aryl group having a heterocyclic structure include a pyrrole residue (a group formed by losing one hydrogen atom from pyrrole) and a furan residue (a group formed by losing one hydrogen atom from furan). Groups), thiophene residues (groups formed by the loss of one hydrogen atom from thiophene), indole residues (groups formed by the loss of one hydrogen atom from indole), benzofuran residues ( A group formed by losing one hydrogen atom from benzofuran), a benzothiophene residue (a group formed by losing one hydrogen atom from benzothiophene), and the like.

The alkyl group and cycloalkyl group in R ₂₀₄ to R _205, preferably a linear or branched alkyl group having 1 to 10 carbon atoms (e.g., methyl group, ethyl group, propyl group, butyl group, pentyl group), carbon Examples thereof include cycloalkyl groups of several 3 to 10 (cyclopentyl group, cyclohexyl group, norbornyl group).

Aryl group, alkyl group of R ₂₀₄ to R _205, cycloalkyl groups may have a substituent. Aryl group, alkyl group of R ₂₀₄ to R _205, the cycloalkyl group substituent which may be possessed by, for example, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms ), An aryl group (for example, having 6 to 15 carbon atoms), an alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, and a phenylthio group.

Specific examples of the compound represented by the general formula (I) include the following compounds.

An acid generator can be used individually by 1 type or in combination of 2 or more types.
The content of the acid generator is preferably 0.1 to 20% by mass, more preferably 0.5 to 10% by mass, and still more preferably based on the total solid content of the actinic ray-sensitive or radiation-sensitive resin composition. Is 1-7 mass%.

  The positive photosensitive composition of the present invention is a pattern by immersion exposure in which exposure is performed by filling a liquid (an immersion medium) having a refractive index higher than air between the resist film and the lens during irradiation with actinic rays or radiation. It can also be suitably used for formation. Thereby, resolution can be improved. As the immersion medium to be used, any liquid can be used as long as it has a higher refractive index than air, but pure water is preferred.

The immersion liquid used for the immersion exposure will be described below.
The immersion liquid is preferably a liquid that is transparent to the exposure wavelength and has a refractive index temperature coefficient as small as possible so as to minimize distortion of the optical image projected onto the resist film. Is an ArF excimer laser (wavelength; 193 nm), it is preferable to use water from the viewpoints of availability and ease of handling in addition to the above-mentioned viewpoints.
Further, a medium having a refractive index of 1.5 or more can be used in that the refractive index can be further improved. This medium may be an aqueous solution or an organic solvent.

  When water is used as the immersion liquid, the surface tension of the water is decreased and the surface activity is increased, so that the resist film on the wafer is not dissolved and the influence on the optical coating on the lower surface of the lens element can be ignored. An additive (liquid) may be added in a small proportion. The additive is preferably an aliphatic alcohol having a refractive index substantially equal to that of water, and specifically includes methyl alcohol, ethyl alcohol, isopropyl alcohol and the like. By adding an alcohol having a refractive index substantially equal to that of water, even if the alcohol component in water evaporates and the content concentration changes, an advantage that the change in the refractive index of the entire liquid can be made extremely small can be obtained. On the other hand, when an opaque material or impurities whose refractive index is significantly different from that of water are mixed with 193 nm light, the optical image projected on the resist film is distorted. . Further, pure water filtered through an ion exchange filter or the like may be used.

The electrical resistance of water is desirably 18.3 MQcm or more, the TOC (organic substance concentration) is desirably 20 ppb or less, and deaeration treatment is desirably performed.
Moreover, it is possible to improve lithography performance by increasing the refractive index of the immersion liquid. From such a viewpoint, an additive for increasing the refractive index may be added to water, or heavy water (D ₂ O) may be used instead of water.

  When the film comprising the actinic ray-sensitive or radiation-sensitive resin composition of the present invention is exposed through an immersion medium, a hydrophobic resin (HR) can be further added as necessary. As a result, when the hydrophobic resin (HR) is unevenly distributed on the surface of the membrane and the immersion medium is water, the receding contact angle of the membrane surface with respect to the water when the membrane is formed can be improved, and the immersion water followability can be improved. it can. As the hydrophobic resin (HR), any resin can be used as long as the receding contact angle of the surface can be improved by addition, but a resin having at least one of fluorine atom and silicon atom is preferable. The receding contact angle of the film is preferably 60 ° to 90 °, more preferably 70 ° or more. The addition amount can be adjusted as appropriate so that the receding contact angle of the film is in the above range, but is preferably 0.1 to 10% by mass based on the total solid content of the composition of the present invention, more Preferably it is 0.1-5 mass%. Hydrophobic resin (HR) is ubiquitous at the interface as described above, but unlike a surfactant, it does not necessarily have a hydrophilic group in the molecule, and polar / nonpolar substances are mixed uniformly. There is no need to contribute.

  The receding contact angle is the contact angle measured when the contact line at the droplet-substrate interface recedes, and is useful for simulating the ease of droplet movement under dynamic conditions. It is generally known. In simple terms, it can be defined as the contact angle when the droplet interface recedes when the droplet discharged from the needle tip is deposited on the substrate and then sucked into the needle again. It can be measured by using a contact angle measuring method generally called an expansion / contraction method.

  In the immersion exposure process, the immersion head needs to move on the wafer following the movement of the exposure head to scan the wafer at high speed to form the exposure pattern. In this case, the contact angle of the immersion liquid with respect to the resist film is important, and the resist is required to follow the high-speed scanning of the exposure head without remaining droplets.

The fluorine atom or silicon atom in the hydrophobic resin (HR) may be contained in the main chain of the resin or may be substituted on the side chain.
The hydrophobic resin (HR) is preferably a resin having an alkyl group having a fluorine atom, a cycloalkyl group having a fluorine atom, or an aryl group having a fluorine atom as a partial structure having a fluorine atom.
The alkyl group having a fluorine atom (preferably having 1 to 10 carbon atoms, more preferably 1 to 4 carbon atoms) is a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom, It may have a substituent.

The cycloalkyl group having a fluorine atom is a monocyclic or polycyclic cycloalkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and may further have another substituent.
Examples of the aryl group having a fluorine atom include those in which at least one hydrogen atom of an aryl group such as a phenyl group or a naphthyl group is substituted with a fluorine atom, and may further have another substituent.

Preferred examples of the alkyl group having a fluorine atom, the cycloalkyl group having a fluorine atom, or the aryl group having a fluorine atom include groups represented by the following general formulas (F2) to (F4). The present invention is not limited to this.

In general formulas (F2) to (F4),
R _{57 to} R ₆₈ each independently represents a hydrogen atom, a fluorine atom or an alkyl group. However, at least one of R _{57 to} R ₆₁ , R _{62 to} R ₆₄ and R _{65 to} R ₆₈ is a fluorine atom or an alkyl group in which at least one hydrogen atom is substituted with a fluorine atom (preferably having a carbon number of 1 ~ 4). R _{57 to} R ₆₁ and R _{65 to} R ₆₇ are preferably all fluorine atoms. R ₆₂ , R ₆₃ and R ₆₈ are preferably an alkyl group (preferably having 1 to 4 carbon atoms) in which at least one hydrogen atom is substituted with a fluorine atom, and preferably a perfluoroalkyl group having 1 to 4 carbon atoms. Further preferred. R ₆₂ and R ₆₃ may be connected to each other to form a ring.

Specific examples of the group represented by the general formula (F2) include a p-fluorophenyl group, a pentafluorophenyl group, and a 3,5-di (trifluoromethyl) phenyl group.
Specific examples of the group represented by the general formula (F3) include trifluoromethyl group, pentafluoropropyl group, pentafluoroethyl group, heptafluorobutyl group, hexafluoroisopropyl group, heptafluoroisopropyl group, hexafluoro (2 -Methyl) isopropyl group, nonafluorobutyl group, octafluoroisobutyl group, nonafluorohexyl group, nonafluoro-t-butyl group, perfluoroisopentyl group, perfluorooctyl group, perfluoro (trimethyl) hexyl group, 2,2 1,3,3-tetrafluorocyclobutyl group, perfluorocyclohexyl group and the like. Hexafluoroisopropyl group, heptafluoroisopropyl group, hexafluoro (2-methyl) isopropyl group, octafluoroisobutyl group, nonafluoro-t-butyl group and perfluoroisopentyl group are preferable, and hexafluoroisopropyl group and heptafluoroisopropyl group are preferable. Further preferred.

Specific examples of the group represented by the general formula (F4) include, for example, —C (CF ₃ ) ₂ OH, —C (C ₂ F ₅ ) ₂ OH, —C (CF ₃ ) (CH ₃ ) OH, -CH (CF ₃₎ OH and the like, -C (CF _{3) 2} OH is preferred.

Hereinafter, although the specific example of the repeating unit which has a fluorine atom is shown, this invention is not limited to this.
In specific examples, X ₁ represents a hydrogen atom, —CH ₃ , —F or —CF ₃ .
X ₂ represents —F or —CF ₃ .

The hydrophobic resin (HR) is preferably a resin having an alkylsilyl structure (preferably a trialkylsilyl group) or a cyclic siloxane structure as a partial structure having a silicon atom.
Specific examples of the alkylsilyl structure or the cyclic siloxane structure include groups represented by the following general formulas (CS-1) to (CS-3).

In general formulas (CS-1) to (CS-3),
R _{12 to} R ₂₆ each independently represents a linear or branched alkyl group (preferably having 1 to 20 carbon atoms) or a cycloalkyl group (preferably having 3 to 20 carbon atoms).
L < ₃ > -L < ₅ > represents a single bond or a bivalent coupling group. As the divalent linking group, an alkylene group, a phenylene group, an ether group, a thioether group, a carbonyl group, an ester group, an amide group, a urethane group, or a urea group is used alone or in combination of two or more groups. A combination is mentioned.
n represents an integer of 1 to 5.

Hereinafter, although the specific example of the repeating unit which has group represented by general formula (CS-1)-(CS-3) is given, this invention is not limited to this. In specific examples, X ₁ represents a hydrogen atom, —CH ₃ , —F or —CF ₃ .

  Furthermore, the hydrophobic resin (HR) may have at least one group selected from the following groups (x) to (z).

(X) an alkali-soluble group,
(Y) a group that decomposes by the action of an alkali developer and increases the solubility in the alkali developer;
(Z) A group that decomposes by the action of an acid.

  (X) Alkali-soluble groups include phenolic hydroxyl groups, carboxylic acid groups, fluorinated alcohol groups, sulfonic acid groups, sulfonamido groups, sulfonylimide groups, (alkylsulfonyl) (alkylcarbonyl) methylene groups, (alkylsulfonyl) ( Alkylcarbonyl) imide group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) ) And a methylene group.

  Preferred alkali-soluble groups include fluorinated alcohol groups (preferably hexafluoroisopropanol), sulfonimide groups, and bis (carbonyl) methylene groups.

  Examples of the repeating unit having an alkali-soluble group (x) include a repeating unit in which an alkali-soluble group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or a main group of the resin via a linking group. Examples include repeating units in which an alkali-soluble group is bonded to the chain. Furthermore, a polymerization initiator or a chain transfer agent having an alkali-soluble group can be used at the time of polymerization to be introduced at the end of the polymer chain. Is also preferable.

  The content of the repeating unit having an alkali-soluble group (x) is preferably from 1 to 50 mol%, more preferably from 3 to 35 mol%, still more preferably from 5 to 20 mol%, based on all repeating units in the polymer.

Specific examples of the repeating unit having an alkali-soluble group (x) are shown below, but the present invention is not limited thereto.

(Y) Examples of the group that decomposes by the action of an alkali developer and increases the solubility in the alkali developer include a group having a lactone structure, an acid anhydride group, an acid imide group, and the like, and preferably a lactone A group having a structure.
As the repeating unit having a group (y) that is decomposed by the action of an alkali developer and increases the solubility in the alkali developer, an alkali is added to the main chain of the resin, such as a repeating unit of an acrylate ester or a methacrylate ester. A polymerization initiator having a repeating unit to which a group (y) that decomposes by the action of the developer and increases the solubility in an alkali developer is bonded, or a group (y) that increases the solubility in an alkali developer And a chain transfer agent used at the time of polymerization are preferably introduced at the end of the polymer chain.

  The content of the repeating unit having a group (y) whose solubility in an alkali developer is increased is preferably 1 to 40 mol%, more preferably 3 to 30 mol%, still more preferably based on all repeating units in the polymer. 5 to 15 mol%.

  Specific examples of the repeating unit having a group (y) that increases the solubility in an alkali developer include the same repeating units as those having a lactone structure exemplified for the resin of the component (B).

  In the hydrophobic resin (HR), examples of the repeating unit having a group (z) that is decomposed by the action of an acid are the same as the repeating unit having an acid-decomposable group exemplified in the resin of the component (B). . In the hydrophobic resin (HR), the content of the repeating unit having a group (z) that is decomposed by the action of an acid is preferably 1 to 80 mol%, more preferably 10 to 10%, based on all repeating units in the polymer. 80 mol%, more preferably 20 to 60 mol%.

The hydrophobic resin (HR) may further have a repeating unit represented by the following general formula (III).

In general formula (III):
R ₄ represents a group having an alkyl group, a cycloalkyl group, an alkenyl group, or a cycloalkenyl group.
L ₆ represents a single bond or a divalent linking group.

In general formula (III), the alkyl group represented by R ₄ is preferably a linear or branched alkyl group having 3 to 20 carbon atoms.

The cycloalkyl group is preferably a cycloalkyl group having 3 to 20 carbon atoms.
The alkenyl group is preferably an alkenyl group having 3 to 20 carbon atoms.
The cycloalkenyl group is preferably a cycloalkenyl group having 3 to 20 carbon atoms.
The divalent linking group of L ₆ is preferably an alkylene group (preferably having 1 to 5 carbon atoms) or an oxy group.

  When the hydrophobic resin (HR) has a fluorine atom, the fluorine atom content is preferably 5 to 80% by mass, and 10 to 80% by mass with respect to the molecular weight of the hydrophobic resin (HR). Is more preferable. Moreover, it is preferable that the repeating unit containing a fluorine atom is 10-100 mass% in hydrophobic resin (HR), and it is more preferable that it is 30-100 mass%.

  When the hydrophobic resin (HR) has a silicon atom, the content of the silicon atom is preferably 2 to 50% by mass and preferably 2 to 30% by mass with respect to the molecular weight of the hydrophobic resin (HR). Is more preferable. Moreover, it is preferable that it is 10-100 mass% in hydrophobic resin (HR), and, as for the repeating unit containing a silicon atom, it is more preferable that it is 20-100 mass%.

  The weight average molecular weight of the hydrophobic resin (HR) in terms of standard polystyrene is preferably 1,000 to 100,000, more preferably 1,000 to 50,000, and even more preferably 2,000 to 15,000. is there.

  The hydrophobic resin (HR), like the resin of the component (A), naturally has few impurities such as metals, and the residual monomer and oligomer components are preferably 0 to 10% by mass, more preferably. Is more preferably 0 to 5% by mass and 0 to 1% by mass. Thereby, a resist having no change over time such as foreign matter in liquid or sensitivity can be obtained. The molecular weight distribution (Mw / Mn, also referred to as dispersity) is preferably in the range of 1 to 5, more preferably 1 to 3, and still more preferably from the viewpoints of resolution, resist shape, resist pattern sidewall, roughness, and the like. It is the range of 1-2.

  As the hydrophobic resin (HR), various commercially available products can be used, or they can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and the polymerization is performed by heating, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable. Examples of the reaction solvent include ethers such as tetrahydrofuran, 1,4-dioxane, diisopropyl ether, ketones such as methyl ethyl ketone and methyl isobutyl ketone, ester solvents such as ethyl acetate, amide solvents such as dimethylformamide and dimethylacetamide, Furthermore, the solvent which melt | dissolves the composition of this invention like the below-mentioned propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, and cyclohexanone is mentioned. More preferably, the polymerization is performed using the same solvent as the solvent used in the positive resist composition of the present invention. Thereby, generation | occurrence | production of the particle at the time of a preservation | save can be suppressed.

  The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred examples of the initiator include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. The concentration of the reaction is 5 to 50% by mass, preferably 30 to 50% by mass. The reaction temperature is usually 10 ° C to 150 ° C, preferably 30 ° C to 120 ° C, more preferably 60-100 ° C.

  After completion of the reaction, the mixture is allowed to cool to room temperature and purified. Purification can be accomplished by a liquid-liquid extraction method that removes residual monomers and oligomer components by combining water and an appropriate solvent, and a purification method in a solution state such as ultrafiltration that extracts and removes only those having a specific molecular weight or less. , Reprecipitation method that removes residual monomer by coagulating resin in poor solvent by dripping resin solution into poor solvent and purification in solid state such as washing filtered resin slurry with poor solvent A normal method such as a method can be applied. For example, the resin is precipitated as a solid by contacting a solvent (poor solvent) in which the resin is hardly soluble or insoluble in a volume amount of 10 times or less, preferably 10 to 5 times that of the reaction solution.

  The solvent (precipitation or reprecipitation solvent) used in the precipitation or reprecipitation operation from the polymer solution may be a poor solvent for the polymer, and may be a hydrocarbon, halogenated hydrocarbon, nitro, depending on the type of polymer. A compound, ether, ketone, ester, carbonate, alcohol, carboxylic acid, water, a mixed solvent containing these solvents, and the like can be appropriately selected for use. Among these, as a precipitation or reprecipitation solvent, a solvent containing at least an alcohol (particularly methanol or the like) or water is preferable.

  The amount of the precipitation or reprecipitation solvent used can be appropriately selected in consideration of efficiency, yield, and the like, but generally 100 to 10000 parts by mass, preferably 200 to 2000 parts by mass with respect to 100 parts by mass of the polymer solution, More preferably, it is 300-1000 mass parts.

  The temperature for precipitation or reprecipitation can be appropriately selected in consideration of efficiency and operability, but is usually about 0 to 50 ° C., preferably around room temperature (for example, about 20 to 35 ° C.). The precipitation or reprecipitation operation can be performed by a known method such as a batch method or a continuous method using a conventional mixing vessel such as a stirring tank.

  The precipitated or re-precipitated polymer is usually subjected to conventional solid-liquid separation such as filtration and centrifugation, and dried before use. Filtration is performed using a solvent-resistant filter medium, preferably under pressure. Drying is performed at a temperature of about 30 to 100 ° C., preferably about 30 to 50 ° C. under normal pressure or reduced pressure (preferably under reduced pressure).

  The resin may be once deposited and separated, and then dissolved again in a solvent, and the resin may be brought into contact with a hardly soluble or insoluble solvent. That is, after completion of the radical polymerization reaction, a solvent in which the polymer is hardly soluble or insoluble is brought into contact, the resin is precipitated (step a), the resin is separated from the solution (step b), and dissolved again in the solvent. (Step c), and then contact the resin solution A with a solvent in which the resin is hardly soluble or insoluble in a volume amount less than 10 times that of the resin solution A (preferably 5 times or less volume). This may be a method including precipitating a resin solid (step d) and separating the precipitated resin (step e).

Specific examples of the hydrophobic resin (HR) are shown below. Table 1 below shows the molar ratio of the repeating units in each resin (corresponding to each repeating unit in order from the left), the weight average molecular weight, and the degree of dispersion.

  In order to prevent the film from coming into direct contact with the immersion liquid between the film made of the actinic ray-sensitive or radiation-sensitive resin composition of the present invention and the immersion liquid, the immersion liquid hardly soluble film (hereinafter referred to as “top”). May also be provided). The functions necessary for the top coat are suitability for coating on the upper layer of the film, transparency to radiation, particularly 193 nm, and poor immersion liquid solubility. It is preferable that the top coat is not mixed with the resist and can be uniformly applied to the upper layer of the film.

  From the viewpoint of 193 nm transparency, the top coat is preferably a polymer that does not contain abundant aromatics. Specifically, the polymer contains a hydrocarbon polymer, an acrylate polymer, polymethacrylic acid, polyacrylic acid, polyvinyl ether, and silicon. Examples thereof include a polymer and a fluorine-containing polymer. The aforementioned hydrophobic resin (HR) is also suitable as a top coat. From the viewpoint of contaminating the optical lens when impurities are eluted from the top coat into the immersion liquid, it is preferable that the residual monomer component of the polymer contained in the top coat is small.

  When peeling the top coat, a developer may be used, or a separate release agent may be used. As the release agent, a solvent having a small penetration into the resist film is preferable. In terms of being able to perform the peeling process simultaneously with the film development process, it is preferable that the peeling process can be performed with an alkaline developer. The top coat is preferably acidic from the viewpoint of peeling with an alkali developer, but may be neutral or alkaline from the viewpoint of non-intermixability with the film.

  The resolution is improved when there is no difference in refractive index between the top coat and the immersion liquid. In the case of using water as the immersion liquid in an ArF excimer laser (wavelength: 193 nm), the top coat for ArF immersion exposure is preferably close to the refractive index of the immersion liquid. From the viewpoint of making the refractive index close to the immersion liquid, it is preferable to have fluorine atoms in the topcoat. A thin film is more preferable from the viewpoint of transparency and refractive index.

  The top coat is preferably not mixed with the membrane and further not mixed with the immersion liquid. From this point of view, when the immersion liquid is water, the solvent used for the top coat is a poorly soluble and non-water-soluble medium in the solvent used for the actinic ray-sensitive or radiation-sensitive resin composition. It is preferable that Furthermore, when the immersion liquid is an organic solvent, the topcoat may be water-soluble or water-insoluble.

Solvent Examples of the solvent that can be used in preparing the actinic ray-sensitive or radiation-sensitive resin composition by dissolving the above components include, for example, alkylene glycol monoalkyl ether carboxylate, alkylene glycol monoalkyl ether, lactic acid Alkyl esters, alkyl alkoxypropionates, cyclic lactones (preferably having 4 to 10 carbon atoms), monoketone compounds that may contain rings (preferably having 4 to 10 carbon atoms), alkylene carbonates, alkyl alkoxyacetates, alkyl pyruvates, etc. The organic solvent can be mentioned.

  Examples of the alkylene glycol monoalkyl ether carboxylate include propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate, propylene glycol monobutyl ether acetate, propylene glycol monomethyl ether propionate, propylene glycol monoethyl Preferred examples include ether propionate, ethylene glycol monomethyl ether acetate, and ethylene glycol monoethyl ether acetate.

  Preferred examples of the alkylene glycol monoalkyl ether include propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, ethylene glycol monomethyl ether, and ethylene glycol monoethyl ether.

Preferred examples of the alkyl lactate include methyl lactate, ethyl lactate, propyl lactate and butyl lactate.
Preferable examples of the alkyl alkoxypropionate include ethyl 3-ethoxypropionate, methyl 3-methoxypropionate, methyl 3-ethoxypropionate, and ethyl 3-methoxypropionate.

  Examples of the cyclic lactone include β-propiolactone, β-butyrolactone, γ-butyrolactone, α-methyl-γ-butyrolactone, β-methyl-γ-butyrolactone, γ-valerolactone, γ-caprolactone, and γ-octano. Preferred are iclactone and α-hydroxy-γ-butyrolactone.

  Examples of the monoketone compound which may contain a ring include 2-butanone, 3-methylbutanone, pinacolone, 2-pentanone, 3-pentanone, 3-methyl-2-pentanone, 4-methyl-2-pentanone, 2 -Methyl-3-pentanone, 4,4-dimethyl-2-pentanone, 2,4-dimethyl-3-pentanone, 2,2,4,4-tetramethyl-3-pentanone, 2-hexanone, 3-hexanone, 5-methyl-3-hexanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-methyl-3-heptanone, 5-methyl-3-heptanone, 2,6-dimethyl-4-heptanone, 2-octanone, 3-octanone, 2-nonanone, 3-nonanone, 5-nonanone, 2-decanone, 3-decanone, 4-decanone, 5-hexen-2-one, -Penten-2-one, cyclopentanone, 2-methylcyclopentanone, 3-methylcyclopentanone, 2,2-dimethylcyclopentanone, 2,4,4-trimethylcyclopentanone, cyclohexanone, 3-methyl Cyclohexanone, 4-methylcyclohexanone, 4-ethylcyclohexanone, 2,2-dimethylcyclohexanone, 2,6-dimethylcyclohexanone, 2,2,6-trimethylcyclohexanone, cycloheptanone, 2-methylcycloheptanone, 3-methylcyclo A preferred example is heptanone.

Preferred examples of the alkylene carbonate include propylene carbonate, vinylene carbonate, ethylene carbonate, and butylene carbonate.
Examples of the alkyl alkoxyacetate include 2-methoxyethyl acetate, 2-ethoxyethyl acetate, 2- (2-ethoxyethoxy) ethyl acetate, 3-methoxy-3-methylbutyl acetate, and 1-methoxy-acetate. 2-propyl is preferred.
Preferred examples of the alkyl pyruvate include methyl pyruvate, ethyl pyruvate, and propyl pyruvate.

As a solvent which can be preferably used, a solvent having a boiling point of 130 ° C. or higher under normal temperature and normal pressure can be mentioned. Specifically, cyclopentanone, γ-butyrolactone, cyclohexanone, ethyl lactate, ethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate, ethyl 3-ethoxypropionate, ethyl pyruvate, 2-ethoxyethyl acetate, acetic acid -2- (2-ethoxyethoxy) ethyl and propylene carbonate are mentioned.
In the present invention, the above solvents may be used alone or in combination of two or more.

In this invention, you may use the mixed solvent which mixed the solvent which contains a hydroxyl group in a structure, and the solvent which does not contain a hydroxyl group as an organic solvent.
Examples of the solvent containing a hydroxyl group include ethylene glycol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol, propylene glycol monomethyl ether, propylene glycol monoethyl ether, ethyl lactate, and the like. Particularly preferred are propylene glycol monomethyl ether and ethyl lactate.

  Examples of the solvent not containing a hydroxyl group include propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, butyl acetate, N-methylpyrrolidone, N, N-dimethylacetamide, dimethyl sulfoxide and the like. Among these, propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, and butyl acetate are particularly preferred, and propylene glycol monomethyl ether acetate, ethyl ethoxypropionate. 2-heptanone is most preferred.

  The mixing ratio (mass) of the solvent containing a hydroxyl group and the solvent not containing a hydroxyl group is 1/99 to 99/1, preferably 10/90 to 90/10, more preferably 20/80 to 60/40. . A mixed solvent containing 50% by mass or more of a solvent not containing a hydroxyl group is particularly preferred from the viewpoint of coating uniformity.

  The solvent is preferably a mixed solvent of two or more containing propylene glycol monomethyl ether acetate.

Basic Compound The composition of the present invention preferably contains a basic compound in order to reduce the change in performance over time from exposure to heating.
Preferred examples of the basic compound include compounds having structures represented by the following formulas (A) to (E).

In general formulas (A) to (E),
R ²⁰⁰ , R ²⁰¹ and R ²⁰² may be the same or different, and are a hydrogen atom, an alkyl group (preferably having 1 to 20 carbon atoms), a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (having a carbon number). 6-20), wherein R ²⁰¹ and R ²⁰² may combine with each other to form a ring.

About the said alkyl group, as an alkyl group which has a substituent, a C1-C20 aminoalkyl group, a C1-C20 hydroxyalkyl group, or a C1-C20 cyanoalkyl group is preferable.
R ²⁰³ , R ²⁰⁴ , R ²⁰⁵ and R ²⁰⁶ may be the same or different and each represents an alkyl group having 1 to 20 carbon atoms.
The alkyl groups in these general formulas (A) to (E) are more preferably unsubstituted.

  Preferred compounds include guanidine, aminopyrrolidine, pyrazole, pyrazoline, piperazine, aminomorpholine, aminoalkylmorpholine, piperidine and the like, and more preferred compounds include imidazole structure, diazabicyclo structure, onium hydroxide structure, onium carboxylate Examples thereof include a compound having a structure, a trialkylamine structure, an aniline structure or a pyridine structure, an alkylamine derivative having a hydroxyl group and / or an ether bond, and an aniline derivative having a hydroxyl group and / or an ether bond.

  Examples of the compound having an imidazole structure include imidazole, 2,4,5-triphenylimidazole, benzimidazole, and 2-phenylbenzimidazole. Examples of the compound having a diazabicyclo structure include 1,4-diazabicyclo [2,2,2] octane, 1,5-diazabicyclo [4,3,0] non-5-ene, and 1,8-diazabicyclo [5,4,0. ] Undecar 7-ene etc. are mentioned. Examples of the compound having an onium hydroxide structure include tetrabutylammonium hydroxide, triarylsulfonium hydroxide, phenacylsulfonium hydroxide, sulfonium hydroxide having a 2-oxoalkyl group, specifically, triphenylsulfonium hydroxide, tris ( and t-butylphenyl) sulfonium hydroxide, bis (t-butylphenyl) iodonium hydroxide, phenacylthiophenium hydroxide, 2-oxopropylthiophenium hydroxide, and the like. As the compound having an onium carboxylate structure, an anion portion of the compound having an onium hydroxide structure is converted to a carboxylate, and examples thereof include acetate, adamantane-1-carboxylate, and perfluoroalkylcarboxylate. Examples of the compound having a trialkylamine structure include tri (n-butyl) amine and tri (n-octyl) amine. Examples of the aniline compound include 2,6-diisopropylaniline, N, N-dimethylaniline, N, N-dibutylaniline, N, N-dihexylaniline and the like. Examples of the alkylamine derivative having a hydroxyl group and / or an ether bond include ethanolamine, diethanolamine, triethanolamine, N-phenyldiethanolamine, and tris (methoxyethoxyethyl) amine. Examples of aniline derivatives having a hydroxyl group and / or an ether bond include N, N-bis (hydroxyethyl) aniline.

  Preferred examples of the basic compound further include an amine compound having a phenoxy group, an ammonium salt compound having a phenoxy group, an amine compound having a sulfonic acid ester group, and an ammonium salt compound having a sulfonic acid ester group.

As the amine compound, a primary, secondary or tertiary amine compound can be used, and an amine compound in which at least one alkyl group is bonded to a nitrogen atom is preferable. The amine compound is more preferably a tertiary amine compound. As long as at least one alkyl group (preferably having 1 to 20 carbon atoms) is bonded to a nitrogen atom, the amine compound has an cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (preferably having 3 to 20 carbon atoms). Preferably C6-C12) may be bonded to a nitrogen atom. The amine compound preferably has an oxygen atom in the alkyl chain and an oxyalkylene group is formed. The number of oxyalkylene groups is one or more in the molecule, preferably 3 to 9, and more preferably 4 to 6. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

As the ammonium salt compound, a primary, secondary, tertiary, or quaternary ammonium salt compound can be used, and an ammonium salt compound in which at least one alkyl group is bonded to a nitrogen atom is preferable. As long as at least one alkyl group (preferably having 1 to 20 carbon atoms) is bonded to a nitrogen atom, the ammonium salt compound has a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group in addition to the alkyl group. (Preferably having 6 to 12 carbon atoms) may be bonded to a nitrogen atom. The ammonium salt compound preferably has an oxygen atom in the alkyl chain and an oxyalkylene group is formed. The number of oxyalkylene groups is one or more in the molecule, preferably 3 to 9, and more preferably 4 to 6. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group. Examples of the anion of the ammonium salt compound include halogen atoms, sulfonates, borates, and phosphates. Among them, halogen atoms and sulfonates are preferable. As the halogen atom, chloride, bromide, and iodide are particularly preferable. As the sulfonate, an organic sulfonate having 1 to 20 carbon atoms is particularly preferable. Examples of the organic sulfonate include alkyl sulfonates having 1 to 20 carbon atoms and aryl sulfonates. The alkyl group of the alkyl sulfonate may have a substituent, and examples of the substituent include fluorine, chlorine, bromine, alkoxy groups, acyl groups, and aryl groups. Specific examples of the alkyl sulfonate include methane sulfonate, ethane sulfonate, butane sulfonate, hexane sulfonate, octane sulfonate, benzyl sulfonate, trifluoromethane sulfonate, pentafluoroethane sulfonate, and nonafluorobutane sulfonate. Examples of the aryl group of the aryl sulfonate include a benzene ring, a naphthalene ring, and an anthracene ring. The benzene ring, naphthalene ring and anthracene ring may have a substituent, and the substituent is preferably a linear or branched alkyl group having 1 to 6 carbon atoms or a cycloalkyl group having 3 to 6 carbon atoms. Specific examples of the linear or branched alkyl group and cycloalkyl group include methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, t-butyl, n-hexyl, cyclohexyl and the like. Examples of the other substituent include an alkoxy group having 1 to 6 carbon atoms, a halogen atom, cyano, nitro, an acyl group, and an acyloxy group.

  The amine compound having a phenoxy group and the ammonium salt compound having a phenoxy group are those having a phenoxy group at the terminal opposite to the nitrogen atom of the alkyl group of the amine compound or ammonium salt compound. The phenoxy group may have a substituent. Examples of the substituent of the phenoxy group include an alkyl group, an alkoxy group, a halogen atom, a cyano group, a nitro group, a carboxyl group, a carboxylic acid ester group, a sulfonic acid ester group, an aryl group, an aralkyl group, an acyloxy group, and an aryloxy group. Etc. The substitution position of the substituent may be any of the 2-6 positions. The number of substituents may be any in the range of 1 to 5.

It is preferable to have at least one oxyalkylene group between the phenoxy group and the nitrogen atom. The number of oxyalkylene groups is one or more in the molecule, preferably 3 to 9, and more preferably 4 to 6. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

  In the amine compound having a sulfonic acid ester group and the ammonium salt compound having a sulfonic acid ester group, the sulfonic acid ester group may be any of alkyl sulfonic acid ester, cycloalkyl group sulfonic acid ester, and aryl sulfonic acid ester. In the case of an alkyl sulfonate ester, the alkyl group has 1 to 20 carbon atoms, in the case of a cycloalkyl sulfonate ester, the cycloalkyl group has 3 to 20 carbon atoms, and in the case of an aryl sulfonate ester, the aryl group has 6 carbon atoms. ~ 12 are preferred. Alkyl sulfonic acid ester, cycloalkyl sulfonic acid ester, and aryl sulfonic acid ester may have a substituent. Examples of the substituent include a halogen atom, a cyano group, a nitro group, a carboxyl group, a carboxylic acid ester group, and a sulfonic acid. An ester group is preferred.

It is preferable to have at least one oxyalkylene group between the sulfonate group and the nitrogen atom. The number of oxyalkylene groups is one or more in the molecule, preferably 3 to 9, and more preferably 4 to 6. Among the oxyalkylene groups, an oxyethylene group (—CH ₂ CH ₂ O—) or an oxypropylene group (—CH (CH ₃ ) CH ₂ O— or —CH ₂ CH ₂ CH ₂ O—) is preferable, and more preferably oxy Ethylene group.

These basic compounds are used alone or in combination of two or more.
The usage-amount of a basic compound is 0.001-10 mass% normally on the basis of solid content of actinic-ray-sensitive or radiation-sensitive resin composition, Preferably it is 0.01-5 mass%.

  The use ratio of the acid generator and the basic compound in the composition is preferably acid generator / basic compound (molar ratio) = 2.5 to 300. That is, the molar ratio is preferably 2.5 or more from the viewpoints of sensitivity and resolution, and is preferably 300 or less from the viewpoint of suppressing the reduction in resolution due to pattern thickening over time until post-exposure heat treatment. The acid generator / basic compound (molar ratio) is more preferably 5.0 to 200, still more preferably 7.0 to 150.

Surfactant The actinic ray-sensitive or radiation-sensitive resin composition of the present invention preferably further contains a surfactant, and is a fluorine-based and / or silicon-based surfactant (fluorine-based surfactant, silicon-based interface). It is more preferable to contain any one or two or more of an activator and a surfactant having both fluorine atoms and silicon atoms.

  When the actinic ray-sensitive or radiation-sensitive resin composition of the present invention contains the above-mentioned surfactant, adhesion and development defects can be obtained with good sensitivity and resolution when using an exposure light source of 250 nm or less, particularly 220 nm or less. It is possible to provide a resist pattern with less.

  Examples of the fluorine-based and / or silicon-based surfactant include surfactants described in [0276] of US Patent Application Publication No. 2008/0248425. For example, Ftop EF301, EF303, (Shin-Akita Kasei Co., Ltd.) )), FLORARD FC430, 431, 4430 (manufactured by Sumitomo 3M Co., Ltd.), Megafac F171, F173, F176, F189, F113, F110, F177, F120, R08 (manufactured by Dainippon Ink & Chemicals, Inc.), Surflon S-382, SC101, 102, 103, 104, 105, 106 (manufactured by Asahi Glass Co., Ltd.), Troisol S-366 (manufactured by Troy Chemical Co., Ltd.), GF-300, GF-150 (Toagosei Chemical Co., Ltd.) ), Surflon S-393 (manufactured by Seimi Chemical Co., Ltd.), F-top EF121, EF122A EF122B, RF122C, EF125M, EF135M, EF351, 352, EF801, EF802, EF601 (manufactured by Gemco), PF636, PF656, PF6320, PF6520 (manufactured by OMNOVA), FTX-204G, 208G, 218G, 230G 208D, 212D, 218D, 222D (manufactured by Neos Co., Ltd.) and the like. Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) can also be used as a silicon-based surfactant.

  In addition to the known surfactants described above, the surfactant is derived from a fluoroaliphatic compound produced by a telomerization method (also called telomer method) or an oligomerization method (also called oligomer method). A surfactant using a polymer having a fluoroaliphatic group can be used. The fluoroaliphatic compound can be synthesized by the method described in JP-A-2002-90991.

  As the polymer having a fluoroaliphatic group, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate and / or (poly (oxyalkylene)) methacrylate is preferable and distributed irregularly. Or may be block copolymerized. Examples of the poly (oxyalkylene) group include a poly (oxyethylene) group, a poly (oxypropylene) group, a poly (oxybutylene) group, and the like, and a poly (oxyethylene, oxypropylene, and oxyethylene group). A unit having different chain lengths in the same chain length, such as a block link) or poly (block link of oxyethylene and oxypropylene) may be used. Furthermore, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate (or methacrylate) is not only a binary copolymer but also a monomer having two or more different fluoroaliphatic groups, Further, it may be a ternary or higher copolymer obtained by simultaneously copolymerizing two or more different (poly (oxyalkylene)) acrylates (or methacrylates).

For example, as a commercially available surfactant, Megafac F178, F-470, F-473, F-475, F-476, F-472 (manufactured by Dainippon Ink & Chemicals, Inc.), C ₆ F ₁₃ group Copolymer of acrylate (or methacrylate) and (poly (oxyalkylene)) acrylate (or methacrylate), acrylate (or methacrylate) and (poly (oxyethylene)) acrylate (or methacrylate) having C ₃ F ₇ groups And a copolymer of (poly (oxypropylene)) acrylate (or methacrylate).

  In the present invention, surfactants other than fluorine-based and / or silicon-based surfactants described in [0280] of US Patent Application Publication No. 2008/0248425 can also be used.

  These surfactants may be used alone or in several combinations.

  The amount of the surfactant used is preferably 0.0001 to 2% by mass, more preferably 0.001 to 1% by mass, based on the total amount of the actinic ray-sensitive or radiation-sensitive resin composition (excluding the solvent). is there.

Carboxylic acid onium salt The positive resist composition in the present invention may contain a carboxylic acid onium salt. Examples of the carboxylic acid onium salt include a carboxylic acid sulfonium salt, a carboxylic acid iodonium salt, and a carboxylic acid ammonium salt. In particular, as the carboxylic acid onium salt, an iodonium salt and a sulfonium salt are preferable. Furthermore, it is preferable that the carboxylate residue of the carboxylic acid onium salt of the present invention does not contain an aromatic group or a carbon-carbon double bond. As a particularly preferable anion moiety, a linear, branched, monocyclic or polycyclic alkylcarboxylic acid anion having 1 to 30 carbon atoms is preferable. More preferably, an anion of a carboxylic acid in which some or all of these alkyl groups are fluorine-substituted is preferable. The alkyl chain may contain an oxygen atom. This ensures transparency with respect to light of 220 nm or less, improves sensitivity and resolution, and improves density dependency and exposure margin.

  Fluoro-substituted carboxylic acid anions include fluoroacetic acid, difluoroacetic acid, trifluoroacetic acid, pentafluoropropionic acid, heptafluorobutyric acid, nonafluoropentanoic acid, perfluorododecanoic acid, perfluorotridecanoic acid, perfluorocyclohexanecarboxylic acid, 2 , 2-bistrifluoromethylpropionic acid anion and the like.

  These carboxylic acid onium salts can be synthesized by reacting sulfonium hydroxide, iodonium hydroxide, ammonium hydroxide and carboxylic acid with silver oxide in a suitable solvent.

  The content of the carboxylic acid onium salt in the composition is generally 0.1 to 20% by mass, preferably 0.5 to 10% by mass, more preferably 1 to 7% by mass, based on the total solid content of the composition. %.

Dissolution-inhibiting compound having a molecular weight of 3000 or less that decomposes by the action of an acid to increase the solubility in an alkali developer. Dissolution-inhibiting compound having a molecular weight of 3000 or less that decomposes by the action of an acid to increase the solubility in an alkali developer. (Hereinafter also referred to as “dissolution inhibitor compound”), in order not to lower the permeability of 220 nm or less, such as a cholic acid derivative containing an acid-decomposable group described in ProceedingofSPIE, 2724,355 (1996), An alicyclic or aliphatic compound containing an acid-decomposable group is preferred. Examples of the acid-decomposable group and alicyclic structure are the same as those described for the component (B) resin.

  When the positive resist composition of the present invention is exposed with a KrF excimer laser or irradiated with an electron beam, it preferably contains a structure in which the phenolic hydroxyl group of the phenol compound is substituted with an acid-decomposable group. As a phenol compound, what contains 1-9 phenol frame | skeleton is preferable, More preferably, it contains 2-6 pieces.

The molecular weight of the dissolution inhibiting compound in the present invention is 3000 or less, preferably 300 to 3000, and more preferably 500 to 2500.
The addition amount of the dissolution inhibiting compound is preferably 3 to 50% by mass, more preferably 5 to 40% by mass, based on the solid content of the positive resist composition.
Specific examples of the dissolution inhibiting compound are shown below, but the present invention is not limited thereto.

Other Additives In the positive resist composition of the present invention, if necessary, a dye, a plasticizer, a photosensitizer, a light absorber, and a compound that promotes solubility in a developer (for example, a molecular weight of 1000 or less) A phenol compound, an alicyclic compound having a carboxyl group, or an aliphatic compound).

  Such phenol compounds having a molecular weight of 1000 or less can be obtained by referring to, for example, the methods described in JP-A-4-1222938, JP-A-2-28531, US Pat. No. 4,916,210, European Patent 219294, etc. It can be easily synthesized by those skilled in the art.

  Specific examples of alicyclic or aliphatic compounds having a carboxyl group include carboxylic acid derivatives having a steroid structure such as cholic acid, deoxycholic acid, lithocholic acid, adamantane carboxylic acid derivatives, adamantane dicarboxylic acid, cyclohexane carboxylic acid, cyclohexane Examples thereof include, but are not limited to, dicarboxylic acids.

Pattern Forming Method The positive resist composition of the present invention is preferably used at a film thickness of 30 to 250 nm, more preferably at a film thickness of 30 to 200 nm, from the viewpoint of improving resolution. Such a film thickness can be obtained by setting the solid content concentration in the positive resist composition to an appropriate range to give an appropriate viscosity and improving the coating property and film forming property.
The total solid content concentration in the positive resist composition is generally 1 to 10% by mass, more preferably 1 to 8.0% by mass, and still more preferably 1.0 to 6.0% by mass.

  The positive resist composition of the present invention is used by dissolving the above components in a predetermined organic solvent, preferably the mixed solvent, filtering the solution, and then applying the solution on a predetermined support as follows. The pore size of the filter used for filter filtration is preferably 0.1 microns or less, more preferably 0.05 microns or less, and still more preferably 0.03 microns or less made of polytetrafluoroethylene, polyethylene, or nylon.

For example, a positive resist composition is coated on a substrate (eg, silicon / silicon dioxide coating) used for manufacturing a precision integrated circuit element by an appropriate coating method such as a spinner or a coater, and dried to form a resist film. Form.
The resist film is irradiated with actinic rays or radiation through a predetermined mask, preferably baked (heated), developed and rinsed. Thereby, a good pattern can be obtained.

Examples of the actinic ray or radiation include infrared light, visible light, ultraviolet light, far ultraviolet light, extreme ultraviolet light, X-ray, electron beam, etc., preferably 250 nm or less, more preferably 220 nm or less, particularly preferably. Is far ultraviolet light having a wavelength of 1 to 200 nm, specifically, KrF excimer laser (248 nm), ArF excimer laser (193 nm), F ₂ excimer laser (157 nm), X-ray, electron beam, etc., ArF excimer laser F ₂ excimer laser, EUV (13 nm), and electron beam are preferable.

Before forming the resist film, an antireflection film may be coated on the substrate in advance.
As the antireflection film, any of an inorganic film type such as titanium, titanium dioxide, titanium nitride, chromium oxide, carbon, and amorphous silicon, and an organic film type made of a light absorber and a polymer material can be used. In addition, as the organic antireflection film, commercially available organic antireflection films such as DUV30 series, DUV-40 series manufactured by Brewer Science, AR-2, AR-3, AR-5 manufactured by Shipley, etc. may be used. it can.

  In the development step, an alkaline developer is used as follows. Examples of the alkali developer for the positive resist composition include inorganic hydroxides such as sodium hydroxide, potassium hydroxide, sodium carbonate, sodium silicate, sodium metasilicate, and aqueous ammonia, and primary amines such as ethylamine and n-propylamine. Secondary amines such as diethylamine and di-n-butylamine, tertiary amines such as triethylamine and methyldiethylamine, alcohol amines such as dimethylethanolamine and triethanolamine, tetramethylammonium hydroxide, tetraethylammonium hydroxide Alkaline aqueous solutions of cyclic amines such as quaternary ammonium salts such as pyrrole and pihelidine can be used.

Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline developer.
The alkali concentration of the alkali developer is usually from 0.1 to 20% by mass.
The pH of the alkali developer is usually from 10.0 to 15.0.
Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline aqueous solution.
As the rinsing liquid, pure water can be used, and an appropriate amount of a surfactant can be added.
In addition, after the developing process or the rinsing process, a process of removing the developing solution or the rinsing liquid adhering to the pattern with a supercritical fluid can be performed.

EXAMPLES Hereinafter, although an Example demonstrates this invention, this invention is not limited to this.
Synthesis Example 1 (Synthesis of Resin (1))
Under a nitrogen stream, 19.98 g of cyclohexanone was placed in a three-necked flask and heated to 80 ° C. To this, 4.88 g, 0.95 g, 2.19 g, 1.92 g, 0.31 g, polymerization initiator V601 (manufactured by Wako Pure Chemicals, 0.553 g, 6.0 mol% with respect to the monomer) are dissolved in 10.76 g of cyclohexanone in order from the left. The solution was added dropwise over 6 hours. After completion of dropping, the reaction was further carried out at 80 ° C. for 2 hours. The reaction solution was allowed to cool and then added dropwise to a mixed solution of 420 g of hexane / 180 g of ethyl acetate over 20 minutes. The precipitated powder was collected by filtration and dried to obtain 9.5 g of polymer (1). The weight average molecular weight of the obtained polymer (1) was 8540 in terms of standard polystyrene, and the dispersity (Mw / Mn) was 1.56.

Moreover, the resin 2-7 of the following this invention and the resin R1 of the comparative example were synthesize | combined by the method similar to the synthesis example 1. FIG.

Comparative Example 2 (Synthesis of polymer (R2))
Acetoxystyrene, styrene, and 1-cyclopropylethyl methacrylate were charged at a ratio (molar ratio) of 60/15/25 and dissolved in tetrahydrofuran to prepare 100 mL of a solution having a solid concentration of 20% by mass. To this solution was added 2 mol% of a polymerization initiator V-65 manufactured by Wako Pure Chemical Industries, Ltd., and this was added dropwise to 10 mL of tetrahydrofuran heated to 60 ° C. over 4 hours in a nitrogen atmosphere. After completion of the dropwise addition, the reaction solution was heated for 4 hours, 1 mol% of V-65 was added again, and the mixture was stirred for 4 hours. After completion of the reaction, the reaction solution was cooled to room temperature, crystallized in 3 L of hexane, and the precipitated white powder was collected by filtration.

The composition ratio of the polymer determined from C ¹³ NMR was 58/16/26 (molar ratio). Moreover, the weight average molecular weight of standard polystyrene conversion calculated | required by GPC measurement was 9,500.

This polymer was dissolved in 100 ml of tetrahydrofuran, 5 ml of tetramethylammonium hydroxide was added and stirred for 1 hour, and distilled water was added to precipitate the polymer. The precipitate was washed with distilled water and then dried under reduced pressure. After the polymer was dissolved in 100 ml of ethyl acetate, hexane was added and the precipitated polymer was powdered by drying under reduced pressure. The weight average molecular weight in terms of standard polystyrene determined by GPC measurement for this powder was 10,000.

<Resist preparation>
The components shown in Table 2 below were dissolved in a solvent, and a solution with a solid content of 4% by mass was prepared for each, and this was filtered through a polyethylene filter having a pore size of 0.05 μm to prepare a positive photosensitive composition. . The prepared positive photosensitive composition was evaluated by the following method, and the results are shown in Table 3. About each component in Table 2, the ratio at the time of using multiple is a mass ratio.
In addition, in 2, when the positive photosensitive composition contains a hydrophobic resin (HR), the addition form was described as “addition”.

  Hereinafter, abbreviations in the table are shown.

[Photoacid generator]

[Basic compounds]
DIA: 2,6-Diisopropylaniline TBAH: Tetrabutylammonium hydroxide TMEA: Tris (methoxyethoxyethyl) amine PEA: N-phenyldiethanolamine [Surfactant]
W-1: MegaFuck F176 (Dainippon Ink Chemical Co., Ltd.) (Fluorine)
W-2: Megafuck R08 (Dainippon Ink Chemical Co., Ltd.) (fluorine and silicon)
W-3: Troisol S-366 (manufactured by Troy Chemical Co., Ltd.)
W-4: PF656 (manufactured by OMNOVA, fluorine-based)
W-5: PF6320 (manufactured by OMNOVA, fluorine-based)
〔solvent〕
A1: Propylene glycol monomethyl ether acetate A3: γ-butyrolactone B1: Propylene glycol monomethyl ether (Exposure conditions 1: Examples 1-3, Comparative Examples 1-2: ArF immersion exposure)
An organic antireflection film ARC29SR (manufactured by Nissan Chemical Industries, Ltd.) was applied on a silicon wafer, and baked at 205 ° C. for 60 seconds to form a 95 nm antireflection film. The positive photosensitive composition prepared thereon was applied and baked at 85 ° C. for 60 seconds to form a 100 nm resist film. Using an ArF excimer laser immersion scanner (XT-1700Fi manufactured by ASML, NA 1.20, σo / σi = 0.94 / 0.74), the obtained wafer was passed through a 6% halftone mask having a 1/1 line and space pattern at 50 nm. Exposed. Ultra pure water was used as the immersion liquid. Then, after heating for 60 seconds at the temperature described in Table 2, the film was developed with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsed with pure water, and then spin-dried to form a resist pattern.

(Exposure condition 2: Examples 4 to 7: ArF / Dry exposure)
An organic antireflection film ARC29A (Nissan Chemical Co., Ltd.) was applied on a silicon wafer and baked at 205 ° C. for 60 seconds to form a 78 nm antireflection film. The positive resist composition prepared thereon was applied and baked at 130 ° C. for 60 seconds to form a 120 nm resist film. The obtained wafer was exposed through a 6% halftone mask having a 75 nm 1: 1 line and space pattern using an ArF excimer laser scanner (PAS5500 / 1100, manufactured by ASML, NA0.75). Then, after heating for 60 seconds at the temperature described in Table 3, the film was developed with a tetramethylammonium hydroxide aqueous solution (2.38 mass%) for 30 seconds, rinsed with pure water, and then spin-dried to obtain a resist pattern. .

(LWR (Line Width Roughness) measurement)
A 50 nm 1/1 (line and space) pattern line was measured at 50 points, and the 3σ value = LWR was calculated.

(Exposure latitude evaluation)
The exposure amount that reproduces the mask pattern of 75 nm line and space is set as the optimal exposure amount. When the exposure amount is changed, an exposure amount width that allows the pattern size to be 75 nm ± 10% is obtained, and this value is divided by the optimal exposure amount. Percentages. The larger the value, the smaller the change in performance due to the change in exposure amount, and the better the exposure latitude.

(Pattern shape evaluation)
The 75 nm 1: 1 line and space pattern formed by the method described in the above exposure conditions was observed using a scanning electron microscope (Hitachi, Ltd. S-4300), and the pattern shape was observed. A rectangular shape is preferred.

Claims (4)

(A) It has a repeating unit containing a structure represented by the following general formula (1) and a repeating unit containing a structure represented by the following general formula (I), and the solubility in an alkali developer is increased by the action of an acid. An actinic ray-sensitive or radiation-sensitive resin composition comprising a resin and (B) a compound that generates an acid upon irradiation with actinic rays or radiation.

In general formula (1),
L represents a lactone structure.
When there are a plurality of R _{0 s,} each independently represents an alkylene group which may have a substituent, a cyclic alkylene group which may have a substituent, or a combination thereof.
Z is independently an ether bond, an ester bond, an amide bond, a urethane bond or a urea bond when there are a plurality of Z.
n represents the number of repetitions and represents an integer of 0 to 5.

In general formula (I),
R ₁ represents an alkyl group which may have a substituent or a cycloalkyl group which may have a substituent.
R ₂ represents a hydrogen atom, an alkyl group that may have a substituent, or a cycloalkyl group that may have a substituent.
X represents a halogen atom, a hydroxyl group, a cyano group, an acetyl group that may have a substituent, an alkoxy group, or an alkyl group that may have a substituent. When there are a plurality of Xs, the plurality of Xs may be the same or different, and a plurality of Xs may be bonded to form a ring.
k represents an integer of 0 to 4. The actinic ray-sensitive or radiation-sensitive resin composition according to claim 1, wherein the repeating unit containing the structure of the general formula (I) is a repeating unit represented by the following general formula (AI).

In general formula (AI),
R ₃ represents a hydrogen atom, an alkyl group that may have a substituent, a halogen atom, a cyano group, or an alkyloxycarbonyl group that may have a substituent.
R ₁ , R ₂ , X and k are respectively synonymous with R ₁ , R ₂ , X and k in formula (I).   The actinic ray-sensitive or radiation-sensitive resin composition according to claim 1, further comprising (C) a hydrophobic additive resin.   A pattern forming method comprising a step of forming a film with the actinic ray-sensitive or radiation-sensitive resin composition according to claim 1, and exposing and developing the film.