JP2010082940A - Armour case and electronic equipment - Google Patents

Armour case and electronic equipment Download PDF

Info

Publication number
JP2010082940A
JP2010082940A JP2008253446A JP2008253446A JP2010082940A JP 2010082940 A JP2010082940 A JP 2010082940A JP 2008253446 A JP2008253446 A JP 2008253446A JP 2008253446 A JP2008253446 A JP 2008253446A JP 2010082940 A JP2010082940 A JP 2010082940A
Authority
JP
Japan
Prior art keywords
layer
thin film
resin layer
deposited thin
film layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2008253446A
Other languages
Japanese (ja)
Other versions
JP5294312B2 (en
Inventor
Yosuke Miyazaki
陽介 宮崎
Masaki Uesugi
雅樹 上杉
Masaru Umehara
賢 梅原
Motoyuki Tanaka
基之 田中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Casio Hitachi Mobile Communications Co Ltd
Original Assignee
Casio Hitachi Mobile Communications Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Casio Hitachi Mobile Communications Co Ltd filed Critical Casio Hitachi Mobile Communications Co Ltd
Priority to JP2008253446A priority Critical patent/JP5294312B2/en
Publication of JP2010082940A publication Critical patent/JP2010082940A/en
Application granted granted Critical
Publication of JP5294312B2 publication Critical patent/JP5294312B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To easily manufacture an amour case, and to enhance a decorative effect and durability. <P>SOLUTION: This amour case 7 is formed integrally with a transparent resin layer 9 in an upper side of an opaque resin layer 8, and a vapor-deposited thin film layer 11 is formed on an upper side of the transparent resin layer 9. The vapor-deposited thin film layer 11 is formed by discontinuous vapor deposition. The opaque resin layer 8 is cut out in its one part (referring to a cut-out hole 8a). An under coat layer 10 is also formed between the transparent resin layer 9 and the vapor-deposited thin film layer 11. A middle coat layer 12 is formed in an upper side of the vapor-deposited thin film layer 11, and further a top coat layer 13 is formed in an upper side of the middle coat layer 12. The top coat layer 13 is formed by applying an ultraviolet ray curing type paint. <P>COPYRIGHT: (C)2010,JPO&amp;INPIT

Description

本発明は、二色成形による外装ケースと、その外装ケースを備える電子機器に関する。   The present invention relates to an outer case formed by two-color molding and an electronic device including the outer case.

例えば携帯電話機や携帯ゲーム機において、白色のＡＢＳ系樹脂製の外装部品の表面に、希土類酸化物超微粒子（Ｈｏ2Ｏ2（酸化ホルミューム）やＮｄ２Ｏ2（酸化ネオジューム）等の微粒子が混入されたアクリル系樹脂塗料をスプレー塗装して可逆的変色性（演色性）を有する塗膜層を形成し、その上に紫外線硬化型塗料をスプレー塗装して透明塗膜層を形成したものがある（特許文献１参照）。   For example, in mobile phones and portable game machines, acrylic resin paint in which fine particles such as rare earth oxide ultrafine particles (Ho2O2 (formum oxide) and Nd2O2 (neodymium oxide)) are mixed on the surface of a white ABS resin exterior component A coating layer having reversible discoloration (color rendering) is formed by spray coating, and a transparent coating layer is formed by spraying an ultraviolet curable coating on the coating layer (see Patent Document 1). .

また、フレーク状や粒子状の光輝性顔料が混入されたアクリル系樹脂塗料をスプレー塗装してベース塗膜層を形成し、その上に、紫外線硬化型クリヤー塗料をスプレー塗装してトップクリヤー塗膜層を形成したものがある（特許文献２参照）。
特開２００１−２０５１８１号公報 特開２００４−１６０７１８号公報 Also, spray coating acrylic resin paint mixed with flaky or particulate glitter pigment to form a base paint film layer, and then spraying UV-curable clear paint on top paint film Some have formed a layer (see Patent Document 2).
Japanese Patent Laid-Open No. 2001-205181 JP 2004-160718 A

しかし、特許文献１、２の技術では、ケース本体を形成した後に装飾層を塗装する方法であるため、製造に手間が掛かる。また、塗装の場合、層厚を数百ミクロン程度まで厚くすると、ウエルドや亀裂が生じるので、層厚は数十ミクロン程度までが限界であり、深みのある色を出すことが出来なかった。   However, since the techniques of Patent Documents 1 and 2 are methods in which a decorative layer is applied after the case body is formed, it takes time to manufacture. In the case of coating, if the layer thickness is increased to about several hundred microns, welds and cracks are generated. Therefore, the layer thickness is limited to about several tens of microns, and a deep color cannot be produced.

本発明の課題は、外装ケースを容易に製造でき、また、装飾効果及び耐久性を向上させることである。   An object of the present invention is to easily manufacture an exterior case, and to improve a decorative effect and durability.

以上の課題を解決するため、請求項１に記載の発明は、不透明樹脂層の上方に透明樹脂層を一体成形した外装ケースであって、前記透明樹脂層の上方に蒸着薄膜層を形成したことを特徴とする。   In order to solve the above problems, the invention described in claim 1 is an exterior case in which a transparent resin layer is integrally formed above an opaque resin layer, and a vapor deposition thin film layer is formed above the transparent resin layer. It is characterized by.

請求項２に記載の発明は、請求項１に記載の外装ケースであって、前記蒸着薄膜層は不連続蒸着により形成されることを特徴とする。   A second aspect of the present invention is the exterior case according to the first aspect, wherein the deposited thin film layer is formed by discontinuous deposition.

請求項３に記載の発明は、請求項１に記載の外装ケースであって、前記蒸着薄膜層は光学蒸着により形成されることを特徴とする。   The invention according to claim 3 is the exterior case according to claim 1, wherein the deposited thin film layer is formed by optical deposition.

請求項４に記載の発明は、請求項１から３のいずれか一項に記載の外装ケースであって、前記不透明樹脂層は一部が切り欠かれており、その切り欠き部と対向する位置に設けられ発光する表示部を備え、この表示部の表示を切り欠き部から可視できるようにしたことを特徴とする。   Invention of Claim 4 is an exterior case as described in any one of Claim 1 to 3, Comprising: The said opaque resin layer is notched partially, The position facing the notch part Provided with a display unit that emits light, and the display of this display unit is made visible from the cutout portion.

請求項５に記載の発明は、請求項１から４のいずれか一項に記載の外装ケースであって、前記透明樹脂層と前記蒸着薄膜層との間にアンダーコート層が形成されていることを特徴とする。   Invention of Claim 5 is an exterior case as described in any one of Claim 1 to 4, Comprising: The undercoat layer is formed between the said transparent resin layer and the said vapor deposition thin film layer. It is characterized by.

請求項６に記載の発明は、請求項１から５のいずれか一項に記載の外装ケースであって、前記蒸着薄膜層の上方にミドルコート層が形成されていることを特徴とする。   A sixth aspect of the present invention is the exterior case according to any one of the first to fifth aspects, wherein a middle coat layer is formed above the deposited thin film layer.

請求項７に記載の発明は、請求項６に記載の外装ケースであって、前記ミドルコート層の上方にトップコート層が形成されていることを特徴とする。   The invention according to claim 7 is the exterior case according to claim 6, wherein a top coat layer is formed above the middle coat layer.

請求項８に記載の発明は、請求項７に記載の外装ケースであって、前記トップコート層は紫外線硬化型塗料の塗装により形成されていることを特徴とする。   The invention according to claim 8 is the exterior case according to claim 7, wherein the top coat layer is formed by application of an ultraviolet curable paint.

請求項９に記載の発明は、不透明樹脂層の上方に透明樹脂層を一体成形した外装ケースであって、前記透明樹脂層の上方に形成した蒸着薄膜層と、前記蒸着薄膜層の上方に形成したトップコート層と、を形成したことを特徴とする。   The invention according to claim 9 is an exterior case in which a transparent resin layer is integrally formed above an opaque resin layer, the vapor deposition thin film layer formed above the transparent resin layer, and the vapor deposition thin film layer formed above the vapor deposition thin film layer The top coat layer is formed.

請求項１０に記載の発明は、請求項１から９のいずれか一項に記載の外装ケースを備える電子機器を特徴とする。   A tenth aspect of the present invention is characterized by an electronic device including the exterior case according to any one of the first to ninth aspects.

本発明によれば、外装ケースを容易に製造でき、また、耐久性を向上させ、装飾効果を大幅に向上させることができる。   According to the present invention, an exterior case can be easily manufactured, durability can be improved, and a decorative effect can be greatly improved.

以下、図を参照して本発明を実施するための最良の形態を詳細に説明する。
図１は本発明を適用した電子機器の一実施形態の構成として携帯電話を示すもので、図１（ａ）は携帯電話を開いた状態、図１（ｂ）は折り畳んだ状態を示しており、１は第１の筐体、２は第２の筐体、３はヒンジ部、４は操作部、５はメイン表示部、６はバックライト付のサブ表示部、７は外装ケースである。 Hereinafter, the best mode for carrying out the present invention will be described in detail with reference to the drawings.
FIG. 1 shows a cellular phone as a configuration of an embodiment of an electronic apparatus to which the present invention is applied. FIG. 1 (a) shows a state in which the cellular phone is opened, and FIG. 1 (b) shows a folded state. Reference numeral 1 denotes a first housing, 2 denotes a second housing, 3 denotes a hinge portion, 4 denotes an operation portion, 5 denotes a main display portion, 6 denotes a sub display portion with a backlight, and 7 denotes an exterior case.

図示例では、第１の筐体１と第２の筐体２がヒンジ部３を介して折り畳み（開閉）自在に結合され、第１の筐体１に操作部４が設けられる一方、第２の筐体２にメイン表示部５及びサブ表示部６が設けられており、サブ表示部６は第２の筐体２の外装ケース７に設けられている。   In the illustrated example, the first housing 1 and the second housing 2 are connected to each other via a hinge portion 3 so as to be freely foldable (openable / closable), and the operation portion 4 is provided on the first housing 1, while the second The main display unit 5 and the sub display unit 6 are provided in the casing 2, and the sub display unit 6 is provided in the outer case 7 of the second casing 2.

（実施形態１）
図２は図１の外装ケース７の全体に施された層構成を示すもので、８は不透明樹脂層、９は透明樹脂層、１０はアンダーコート層、１１は蒸着薄膜層、１２はミドルコート層、１３はトップコート層である。 (Embodiment 1)
FIG. 2 shows the layer structure applied to the entire exterior case 7 of FIG. 1, wherein 8 is an opaque resin layer, 9 is a transparent resin layer, 10 is an undercoat layer, 11 is a deposited thin film layer, and 12 is a middle coat. Layer 13 is a topcoat layer.

外装ケース７は、不透明樹脂層８の上に透明樹脂層９を二色成形により一体に形成したもので、不透明樹脂層８は、例えば黒色顔料を混入したＡＢＳ樹脂(アクリロニトリル・ブタジエン・スチレン(Acrylonitrile butadiene styrene))により形成され、透明樹脂層９は、例えば無色透明のＰＭＭＡ樹脂(ポリメタクリル酸メチル樹脂（Polymethyl methacrylate)）により形成されている。この場合、透明樹脂層９が一次成形され、不透明樹脂層８が二次成形される。なお、不透明樹脂層８には、前記サブ表示部６の位置・大きさ・形状に対応する切欠孔８ａが形成されている。   The outer case 7 is formed by integrally forming a transparent resin layer 9 on an opaque resin layer 8 by two-color molding. The transparent resin layer 9 is made of, for example, a colorless and transparent PMMA resin (polymethyl methacrylate resin). In this case, the transparent resin layer 9 is primary-molded and the opaque resin layer 8 is secondary-molded. The opaque resin layer 8 is provided with a notch 8a corresponding to the position, size, and shape of the sub display section 6.

そして、透明樹脂層９の上には、アンダーコート層１０、蒸着薄膜層１１、ミドルコート層１２及びトップコート層１３が積層されている。すなわち、透明樹脂層９の上に、例えば黒色塗料によるアンダーコート層１０を塗装して、そのアンダーコート層１０の上に金属の不連続蒸着による蒸着薄膜層１１を形成する。   And on the transparent resin layer 9, the undercoat layer 10, the vapor deposition thin film layer 11, the middle coat layer 12, and the topcoat layer 13 are laminated | stacked. That is, an undercoat layer 10 made of, for example, black paint is applied on the transparent resin layer 9, and a deposited thin film layer 11 formed by discontinuous metal deposition is formed on the undercoat layer 10.

ここで、不連続蒸着とは、樹脂表面に非導通の金属薄膜を形成するもので、あえて蒸着にむら(しま模様)を作り光沢に深みを持たせる加飾処理である。その蒸着材料としては、アルミニウム、亜鉛、金、銀、プラチナ、ニッケルなどの金属が使用される。   Here, discontinuous vapor deposition is a decorating process in which a non-conductive metal thin film is formed on the surface of the resin, and an unevenness (a striped pattern) is created in the vapor deposition to increase the gloss. As the deposition material, metals such as aluminum, zinc, gold, silver, platinum and nickel are used.

以上の蒸着薄膜層１１の上に適宜色塗料によるミドルコート層１２を塗装して、さらに、そのミドルコート層１２の上に紫外線硬化型塗料による透明なトップコート（ＵＶコート）層１３を塗装する。   A middle coat layer 12 made of a color paint is appropriately applied on the deposited thin film layer 11, and a transparent top coat (UV coat) layer 13 made of an ultraviolet curable paint is further applied on the middle coat layer 12. .

以上、実施形態の外装ケース７によれば、黒色の不透明樹脂層８の上に透明樹脂層９を二色成形により一体に設けることで、耐久性を向上でき、さらに、その透明樹脂層９の上に黒色のアンダーコート層１０を介して不連続蒸着による蒸着薄膜層１１を設けることで、サブ表示部６において、切欠孔８ａと対向する位置の内部には図示しないサブ液晶モジュールが設けられている。そして、サブ液晶モジュールを外観から見えなくしながら、バックライトを点灯させたサブ液晶表示時には文字等を浮かび上がらせることが可能であり文字などの視認も容易となる。なお、文字等を表示するためサブ液晶モジュール以外の表示モジュール、例えばＬＥＤモジュールを用いてもよい。   As described above, according to the exterior case 7 of the embodiment, by providing the transparent resin layer 9 integrally on the black opaque resin layer 8 by two-color molding, durability can be improved. By providing the vapor deposition thin film layer 11 by discontinuous vapor deposition on the black undercoat layer 10 on the top, a sub liquid crystal module (not shown) is provided in the sub display portion 6 in a position facing the notch hole 8a. Yes. In addition, characters and the like can be raised during sub-liquid crystal display with the backlight turned on while the sub-liquid crystal module is not visible from the outside, and the characters can be easily viewed. A display module other than the sub liquid crystal module, such as an LED module, may be used to display characters and the like.

このように、表面にサブ液晶モジュールが見えなくなることで、意匠性がより自由になる。
そして、サブ液晶モジュール等を外観表面から完全に隠すための部品を追加する必要がなくなるので、部品点数の削減が図れる。
従って、外装ケース７を容易に製造できて、耐久性を向上させ、装飾効果を大幅に向上させることができる。 In this way, the sub liquid crystal module becomes invisible on the surface, so that the design is more free.
Further, since it is not necessary to add a part for completely hiding the sub liquid crystal module from the external surface, the number of parts can be reduced.
Therefore, the outer case 7 can be easily manufactured, the durability can be improved, and the decoration effect can be greatly improved.

また、黒色の不透明樹脂層８の上の透明樹脂層９で発現する色に加えて、その上の黒色のアンダーコート層１０を介して設けた不連続蒸着による蒸着薄膜層１１によるむら(しま模様)による光沢に深みを持たせた加飾処理によって、装飾効果を大幅に向上でき、意匠のバリエーションに富んだ高級感のある外装ケース７とすることができる。   Further, in addition to the color developed in the transparent resin layer 9 on the black opaque resin layer 8, unevenness due to the deposited thin film layer 11 by discontinuous vapor deposition provided through the black undercoat layer 10 thereon (stripe pattern) ), The decoration effect can be greatly improved, and a high-grade exterior case 7 rich in design variations can be obtained.

さらに、蒸着薄膜層１１の上に適宜色のミドルコート層１２を介してＵＶコートによる透明なトップコート層１３を設けることで、カラーバリエーションに富むとともに、ＵＶコートによる傷付き防止も図れる。   Furthermore, by providing a transparent topcoat layer 13 by UV coating on the vapor-deposited thin film layer 11 through a middle coat layer 12 of appropriate color, it is rich in color variations and can be prevented from being damaged by UV coating.

そして、アンダーコート層１０、蒸着薄膜層１１、ミドルコート層１２及びトップコート層１３の色や膜厚等を変化させて、切欠孔８ａの内部から液晶表示の透過率を調整することで、外装ケース７の表面に文字等を薄っすらと浮かび上がらせるための明るさを調整することができる。   And by changing the color, film thickness, etc. of the undercoat layer 10, the deposited thin film layer 11, the middle coat layer 12, and the topcoat layer 13, the transmittance of the liquid crystal display is adjusted from the inside of the cutout hole 8a. It is possible to adjust the brightness to make characters or the like slightly appear on the surface of the case 7.

また、各層の色を変更して各種組み合わせることで、多種多様のカラーバリエーションを揃えることが可能である。   Moreover, it is possible to arrange a wide variety of color variations by changing the color of each layer and combining them in various ways.

（実施形態２）
図３は図１の外装ケース７の全体に施された層構成を示すもので、前述した実施形態１と同様、８は不透明樹脂層、９は透明樹脂層、１０はアンダーコート層、１１は蒸着薄膜層、１２はミドルコート層、１３はトップコート層である。 (Embodiment 2)
FIG. 3 shows the layer structure applied to the entire exterior case 7 of FIG. 1. As in the first embodiment, 8 is an opaque resin layer, 9 is a transparent resin layer, 10 is an undercoat layer, 11 is A vapor deposition thin film layer, 12 is a middle coat layer, and 13 is a top coat layer.

実施形態２は、実施形態１で蒸着薄膜層１１を不連続蒸着により形成したのに替えて、蒸着薄膜層１１を不連続でない光学蒸着により形成した点が実施形態１と異なり、他の層形成は実施形態１と同様である。   The second embodiment is different from the first embodiment in that the deposited thin film layer 11 is formed by non-discontinuous optical deposition instead of the deposited thin film layer 11 formed by discontinuous deposition in the first embodiment. Is the same as in the first embodiment.

すなわち、実施形態２においては、透明樹脂層９の上に塗装したアンダーコート層１０の上に光学蒸着による蒸着薄膜層１１を形成する。   That is, in Embodiment 2, the vapor deposition thin film layer 11 by optical vapor deposition is formed on the undercoat layer 10 painted on the transparent resin layer 9.

ここで、光学蒸着は、主にSiO2、TiO2、ZrO2などの酸化物を使用して、不連続ではなく、光学特性を有する薄膜を形成する加飾処理である。   Here, the optical vapor deposition is a decorating process in which an oxide such as SiO2, TiO2, or ZrO2 is mainly used to form a thin film having optical characteristics rather than discontinuities.

以上、実施形態２の外装ケース７によれば、光学蒸着にすることで、光学特性を有する蒸着薄膜層１１によって、実施形態１の通常の蒸着とは違うバリエーション展開が可能になる。   As described above, according to the exterior case 7 of the second embodiment, by using the optical deposition, the variation of the vapor deposition thin film layer 11 having optical characteristics can be developed differently from the normal deposition of the first embodiment.

（実施形態３）
図４は図１の外装ケースの全体に施された層構成を示すもので、前述した実施形態１と同様、８は不透明樹脂層、９は透明樹脂層、１１は蒸着薄膜層、１３はトップコート層である。 (Embodiment 3)
FIG. 4 shows a layer structure applied to the entire exterior case of FIG. 1. As in the first embodiment, 8 is an opaque resin layer, 9 is a transparent resin layer, 11 is a vapor-deposited thin film layer, and 13 is a top. It is a coat layer.

実施形態３は、実施形態１におけるアンダーコート層１０とミドルコート層１２をなくした点が実施形態１と異なり、他の層形成は実施形態１と同様である。   The third embodiment is different from the first embodiment in that the undercoat layer 10 and the middle coat layer 12 in the first embodiment are eliminated, and other layer formation is the same as in the first embodiment.

このように、透明樹脂層９の上に金属の不連続蒸着または光学蒸着による蒸着薄膜層１１を形成して、その上にＵＶコートによる透明なトップコート層１３を形成しても、同様の作用効果が得られる。   As described above, even when the vapor-deposited thin film layer 11 is formed on the transparent resin layer 9 by discontinuous metal deposition or optical vapor deposition, and the transparent top coat layer 13 is formed thereon by UV coating, the same effect is obtained. An effect is obtained.

（変形例）
なお、以上の実施形態においては、携帯電話としたが、本発明はこれに限定されるものではなく、カメラ、ＰＤＡ、ノートパソコン、ウェアラブルパソコン、電卓、電子辞書、その他の修飾されたケースを備える電子機器すべてに用いることができる。
また、実施形態では、不透明樹脂層として黒色顔料を混入したＡＢＳ樹脂としたが、他の色でも良く、材料もＡＢＳ樹脂に限らず任意である。
さらに、蒸着薄膜層として耐久性を向上させる材料（例えば硬い金属）で蒸着することでトップコート層をなくすようにしても良い。
また、他の透明樹脂層や蒸着薄膜層やコート層の材料や厚み等も任意であり、その他、具体的な細部構造等についても適宜に変更可能であることは勿論である。例えばミドルコート層はなくても良い。
また、外装ケースの全体に施さずに、その一部に本発明の層構成を適用するようにしてもよい。 (Modification)
In the above embodiment, the cellular phone is used. However, the present invention is not limited to this, and includes a camera, a PDA, a notebook computer, a wearable computer, a calculator, an electronic dictionary, and other modified cases. Can be used for all electronic devices.
In the embodiment, the opaque resin layer is an ABS resin mixed with a black pigment, but other colors may be used, and the material is not limited to the ABS resin and is arbitrary.
Further, the top coat layer may be eliminated by vapor deposition with a material (for example, hard metal) that improves durability as the vapor deposition thin film layer.
In addition, the material and thickness of other transparent resin layers, vapor-deposited thin film layers, and coat layers are arbitrary, and it is needless to say that specific detailed structures can be appropriately changed. For example, the middle coat layer may not be provided.
Moreover, you may make it apply the layer structure of this invention to the one part, without giving to the whole exterior case.

本発明を適用した電子機器の一実施形態の構成を示すもので、携帯電話を開いた状態を示した正面図（ａ）と、折り畳んだ状態を示した正面図（ｂ）である。BRIEF DESCRIPTION OF THE DRAWINGS The structure of one Embodiment of the electronic device to which this invention is applied is shown, the front view (a) which showed the state which opened the mobile phone, and the front view (b) which showed the folded state. 図１の外装ケースの全体に施された層構成を示すもので、実施形態１を示した断面図である。FIG. 2 is a cross-sectional view showing the first embodiment, showing a layer configuration applied to the entire exterior case of FIG. 1. 図１の外装ケースの全体に施された層構成を示すもので、実施形態２を示した断面図である。FIG. 3 is a cross-sectional view showing a second embodiment, showing a layer configuration applied to the entire exterior case of FIG. 1. 図１の外装ケースの全体に施された層構成を示すもので、実施形態３を示した断面図である。FIG. 7 is a cross-sectional view showing a third embodiment, showing a layer configuration applied to the entire exterior case of FIG. 1.

符号の説明Explanation of symbols

２ 筐体
５ メイン表示部
６ サブ表示部
７ 外装ケース
８ 不透明樹脂層
８ａ 切欠孔
９ 透明樹脂層
１０ アンダーコート層
１１ 蒸着薄膜層
１２ ミドルコート層
１３ トップコート層 2 Housing 5 Main display section 6 Sub display section 7 Exterior case 8 Opaque resin layer 8a Notch hole 9 Transparent resin layer 10 Undercoat layer 11 Deposition thin film layer 12 Middle coat layer 13 Topcoat layer

Claims (10)

不透明樹脂層の上方に透明樹脂層を一体成形した外装ケースであって、
前記透明樹脂層の上方に蒸着薄膜層を形成したことを特徴とする外装ケース。 An exterior case integrally formed with a transparent resin layer above the opaque resin layer,
An exterior case, wherein a vapor-deposited thin film layer is formed above the transparent resin layer. 前記蒸着薄膜層は不連続蒸着により形成されることを特徴とする請求項１に記載の外装ケース。   The exterior case according to claim 1, wherein the deposited thin film layer is formed by discontinuous deposition. 前記蒸着薄膜層は光学蒸着により形成されることを特徴とする請求項１に記載の外装ケース。   The exterior case according to claim 1, wherein the deposited thin film layer is formed by optical deposition. 前記不透明樹脂層は一部が切り欠かれており、その切り欠き部と対向する位置に設けられ発光する表示部を備え、この表示部の表示を切り欠き部から可視できるようにしたことを特徴とする請求項１から３のいずれか一項に記載の外装ケース。   A part of the opaque resin layer is cut out, and a display unit that emits light is provided at a position facing the cutout unit, and the display of the display unit is made visible from the cutout unit. The exterior case according to any one of claims 1 to 3. 前記透明樹脂層と前記蒸着薄膜層との間にアンダーコート層が形成されていることを特徴とする請求項１から４のいずれか一項に記載の外装ケース。   The outer case according to any one of claims 1 to 4, wherein an undercoat layer is formed between the transparent resin layer and the vapor-deposited thin film layer. 前記蒸着薄膜層の上方にミドルコート層が形成されていることを特徴とする請求項１から５のいずれか一項に記載の外装ケース。   The outer case according to any one of claims 1 to 5, wherein a middle coat layer is formed above the deposited thin film layer. 前記ミドルコート層の上方にトップコート層が形成されていることを特徴とする請求項６に記載の外装ケース。   The outer case according to claim 6, wherein a top coat layer is formed above the middle coat layer. 前記トップコート層は紫外線硬化型塗料の塗装により形成されていることを特徴とする請求項７に記載の外装ケース。   The outer case according to claim 7, wherein the top coat layer is formed by application of an ultraviolet curable paint. 不透明樹脂層の上方に透明樹脂層を一体成形した外装ケースであって、
前記透明樹脂層の上方に形成した蒸着薄膜層と、
前記蒸着薄膜層の上方に形成したトップコート層と、
を形成したことを特徴とする外装ケース。 An exterior case integrally formed with a transparent resin layer above the opaque resin layer,
A deposited thin film layer formed above the transparent resin layer;
A topcoat layer formed above the deposited thin film layer;
An exterior case characterized by forming 請求項１から９のいずれか一項に記載の外装ケースを備えることを特徴とする電子機器。   An electronic device comprising the exterior case according to claim 1.
JP2008253446A 2008-09-30 2008-09-30 Exterior case and electronic device Expired - Fee Related JP5294312B2 (en)