JP2009029465A - Heat insulating wrapping cloth and carry bag, non-woven fabric laminate body suitable for manufacturing the same, and manufacturing method of the nonwoven fabric laminate - Google Patents
Heat insulating wrapping cloth and carry bag, non-woven fabric laminate body suitable for manufacturing the same, and manufacturing method of the nonwoven fabric laminate Download PDFInfo
- Publication number
- JP2009029465A JP2009029465A JP2007195412A JP2007195412A JP2009029465A JP 2009029465 A JP2009029465 A JP 2009029465A JP 2007195412 A JP2007195412 A JP 2007195412A JP 2007195412 A JP2007195412 A JP 2007195412A JP 2009029465 A JP2009029465 A JP 2009029465A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- aluminum vapor
- roll
- vapor deposition
- fabric sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、不織布積層シート及びその製造方法並びに、当該シートを用いて製造される風呂敷や手提げ袋に関する。 The present invention relates to a nonwoven fabric laminated sheet, a method for producing the same, and a furoshiki or handbag manufactured using the sheet.
従来、食料品を購入して持ち帰る際の鮮度等の低下を防止するために、ポリエステルフィルムにアルミニウム粉末を蒸着したシート素材と、発泡ポリエチレンのシート素材とをラミネート加工により一体にした複合素材を方形及び類似形の所要平面積に裁断した風呂敷の提案（特許文献１）や、アルミ蒸着面に保護プラスチックフィルムを被覆したアルミ蒸着プラスチックフィルムのフィルム面と不織布とを張り合わせた断熱ラミネートシート材によりアルミ蒸着面を外面又は内面とした手提げ袋の提案（特許文献２）がなされている。
特許文献１の保冷・保温機能を備えた風呂敷は、通常の風呂敷の様に隅を縛って持ち手を形成することが困難で使い勝手が悪いという問題がある。特許文献２の手提げ袋は全体に柔軟性がないことから食品等の収納性が悪く、また、別途取り付ける持ち手が必要など、製造コストも上昇するという問題がある。 The furoshiki equipped with the cold and heat retaining function of Patent Document 1 has a problem that it is difficult to form a handle by tying corners like a normal furoshiki and is inconvenient. Since the handbag of Patent Document 2 is not flexible as a whole, there is a problem that the storage capacity for foods and the like is poor, and a manufacturing cost is increased because a handle to be attached separately is required.
そこで、本願は、保冷・保温機能を付加した風呂敷や手提げ袋等の持ち運び用被包材における使い勝手の向上と製造コストの低減を目的とする。 Therefore, the present application aims to improve the usability and reduce the manufacturing cost of portable enveloping materials such as furoshiki and handbags to which cold and heat retaining functions are added.
上記目的を達成するためになされた本発明の断熱性風呂敷は、不織布シートにアルミ蒸着フィルムを接着した不織布積層体で形成され、以下の構成を有することを特徴とする。
（１−１）前記不織布積層体は、不織布シートに対してアルミ蒸着フィルムが縞状に塗布された接着剤を介して部分的に接着されたものであること。
（１−２）前記縞状に塗布された接着剤の線が風呂敷の隣会う辺間を結ぶ様に形成されていること。
（１−３）前記アルミ蒸着フィルムは、風呂敷の一対の対角の方向に伸びる帯状に前記不織布シートに接着されており、他の一対の対角から中心へ向かって所定範囲の三角形部分には接着されていないこと。
The heat insulating furoshiki of this invention made | formed in order to achieve the said objective is formed with the nonwoven fabric laminated body which adhere | attached the aluminum vapor deposition film on the nonwoven fabric sheet, and has the following structures.
(1-1) The said nonwoven fabric laminated body shall be partially adhere | attached through the adhesive agent with which the aluminum vapor deposition film was apply | coated to the nonwoven fabric sheet in stripe form.
(1-2) It is formed so that the line | wire of the adhesive apply | coated to the said stripe form may connect between the sides which meet a furoshiki.
(1-3) The aluminum vapor-deposited film is bonded to the nonwoven fabric sheet in a strip shape extending in a pair of diagonal directions of a furoshiki, and in a triangular portion of a predetermined range from the other pair of diagonals toward the center. It is not glued.
本発明の断熱性風呂敷は、アルミ蒸着フィルムが接着されずに不織布シートのままの三角形部分が一対の対角として形成されているので、この部分を縛ることで、重箱などを包んだときに、一般的な風呂敷を用いるのと同様に緊縛並びに持ち手の形成をなすことができる。即ち、前記所定範囲とは、風呂敷として物を包んで縛るのに必要な程度の範囲をいう。また、不織布シートとアルミ蒸着フィルムは、一方向に縞状に伸びる接着剤で接着されており、全面接着ではないから、不織布シートの柔軟性を保持しており、空気層も形成し得るものとなっている。 The heat insulating furoshiki of the present invention is formed as a pair of diagonal corners of the non-woven sheet without being bonded to the aluminum vapor-deposited film, so by tying this part, The binding and the formation of the handle can be made in the same manner as using a general furoshiki. That is, the predetermined range refers to a range necessary to wrap and bind an object as a furoshiki. In addition, the nonwoven fabric sheet and the aluminum vapor deposition film are bonded with an adhesive that extends in a striped manner in one direction, and because it is not a full-surface adhesion, it retains the flexibility of the nonwoven fabric sheet and can also form an air layer. It has become.
上記目的を達成するためになされた本発明の断熱性手提げ袋は、不織布シートにアルミ蒸着フィルムを接着した不織布積層体で形成され、以下の構成を有することを特徴とする。
（２−１）前記不織布積層体を二つ折りにして底を形成し、左右側面を熱融着させて袋体とすると共に、上部に該不織布積層体の一部を打ち抜いた持ち手穴が形成されていること。
（２−２）前記不織布積層体は、不織布シートに対してアルミ蒸着フィルムが縞状に塗布された接着剤を介して部分的に接着されたものであること。
（２−３）前記縞状に塗布された接着剤の線が手提げ袋の水平方向に形成されていること。
（２−４）前記アルミ蒸着フィルムは、手提げ袋の上部から少なくとも前記持ち手穴よりも下方所定範囲を除く底面側部分にだけ接着されていること。
The heat insulating handbag of the present invention made to achieve the above object is formed of a nonwoven fabric laminate in which an aluminum vapor deposition film is bonded to a nonwoven fabric sheet, and has the following configuration.
(2-1) The nonwoven fabric laminate is folded in two to form a bottom, and the right and left side surfaces are heat-sealed to form a bag, and a handle hole is formed in the upper portion by punching out a part of the nonwoven fabric laminate. is being done.
(2-2) The said nonwoven fabric laminated body shall be partially adhere | attached through the adhesive agent with which the aluminum vapor deposition film was apply | coated to the nonwoven fabric sheet in stripe form.
(2-3) The line of the adhesive applied in the stripe pattern is formed in the horizontal direction of the handbag.
(2-4) The aluminum vapor-deposited film is adhered only to the bottom side portion excluding a predetermined range below the handle hole from the upper part of the handbag.
本発明の断熱性手提げ袋は、アルミ蒸着フィルムが接着されずに不織布シートのままの持ち手部分が、打ち抜き加工によって一体に形成されているので、物品を収納して手に持つときに、不織布のみからなる手提げ袋と同様の手触りを感じさせる。また、不織布シートとアルミ蒸着フィルムは、一方向に縞状に伸びる接着剤で接着されており、全面接着ではないから、不織布シートの柔軟性を保持しており、空気層も形成し得るものとなっている。さらに、この縞の方向が水平方向であるから、収納した物によって押し拡げられ難く、ヒートシールをする際のシール位置も気にすることなく決定することができる。 The heat-insulating handbag of the present invention has a non-woven sheet as the handle portion that is not bonded to the aluminum vapor-deposited film, and is integrally formed by punching. Feel the same feel as a handbag. In addition, the nonwoven fabric sheet and the aluminum vapor deposition film are bonded with an adhesive that extends in a striped manner in one direction, and because it is not a full-surface adhesion, it retains the flexibility of the nonwoven fabric sheet and can also form an air layer. It has become. Furthermore, since the direction of the stripes is horizontal, it is difficult to spread by the stored items, and the sealing position when performing heat sealing can be determined without concern.
上記目的を達成するためになされた本発明の不織布積層体は、不織布シートにアルミ蒸着フィルムを接着した不織布積層体であって、以下の構成を有することを特徴とする。
（３−１）縞状に塗布された接着剤を介して不織布シートとアルミ蒸着フィルムとが部分的に接着されたロール状のものであること。
（３−２）前記アルミ蒸着フィルムは、前記不織布シートよりも幅が狭く、かつ、不織布シートの幅方向両端を所定幅に渡って露出させた状態となる様に、前記不織布シートの中央に合わせて接着されていること。
The nonwoven fabric laminate of the present invention made to achieve the above object is a nonwoven fabric laminate in which an aluminum vapor-deposited film is bonded to a nonwoven fabric sheet, and has the following configuration.
(3-1) It is a roll-like thing in which the nonwoven fabric sheet and the aluminum vapor deposition film are partially bonded via an adhesive applied in a striped manner.
(3-2) The aluminum vapor deposition film is narrower than the nonwoven fabric sheet, and is aligned with the center of the nonwoven fabric sheet so that both ends of the nonwoven fabric sheet in the width direction are exposed over a predetermined width. Be glued.
本発明の不織布積層体は、幅方向の両端にはアルミ蒸着フィルムが接着されていない部分を備えている。従って、両端を一対の角とする様に正方形に打ち抜けば、本発明の断熱性風呂敷を容易に製造することができる。また、所定長さに切断し、アルミ蒸着フィルムの幅中心で二つ折りにして両端をヒートシールで接合し、不織布のみの部分に持ち手穴を打ち抜けば、本発明の断熱性手提げ袋を容易に製造することができる。 The nonwoven fabric laminated body of this invention is equipped with the part to which the aluminum vapor deposition film is not adhere | attached at the both ends of the width direction. Therefore, if the both ends are formed in a square shape with a pair of corners, the heat insulating furoshiki of the present invention can be easily manufactured. In addition, the heat insulating handbag of the present invention can be easily obtained by cutting it into a predetermined length, folding it in half at the center of the width of the aluminum vapor-deposited film, joining both ends with heat sealing, and punching the handle hole in the non-woven fabric only part. Can be manufactured.
上記目的を達成するためになされた本発明の不織布積層体の製造方法は、不織布シートにアルミ蒸着フィルムを接着した不織布積層体の製造方法であって、以下の構成を有することを特徴とする。
（４−１）所定幅を有する不織布ロールと、該不織布ロールよりも狭い幅のアルミ蒸着フィルムロールとを用意すること。
（４−２）前記不織布ロールと前記アルミ蒸着フィルムロールとを互いの幅方向中心が一致する様に配置し、それぞれから素材を繰り出すこと。
（４−３）前記それぞれから繰り出された素材間に、縞状に接着剤を垂らしつつ、接着用のローラー組の間に挟み込むこと。
（４−４）前記接着用のローラー組から繰り出される積層体を巻き取ってロール状とすること。
The manufacturing method of the nonwoven fabric laminated body of this invention made | formed in order to achieve the said objective is a manufacturing method of the nonwoven fabric laminated body which adhere | attached the aluminum vapor deposition film on the nonwoven fabric sheet, Comprising: It has the following structures.
(4-1) Prepare a nonwoven fabric roll having a predetermined width and an aluminum vapor deposition film roll having a narrower width than the nonwoven fabric roll.
(4-2) The non-woven fabric roll and the aluminum vapor-deposited film roll are arranged so that the centers in the width direction coincide with each other, and the material is fed out from each.
(4-3) The material is drawn between the materials, and the adhesive is suspended in a striped manner, and sandwiched between the bonding roller sets.
(4-4) The laminated body drawn out from the bonding roller set is wound into a roll shape.
本発明の不織布積層体の製造方法によれば、両端を所定範囲に渡って不織布シートのみとし、中央部分にのみアルミ蒸着フィルムが接着された不織布積層体を連続的に製造することができ、本発明の断熱性風呂敷や断熱性手提げ袋を製造するための不織布積層体を安価に製造することができる。 According to the method for producing a nonwoven fabric laminate of the present invention, it is possible to continuously produce a nonwoven fabric laminate in which both ends are made into a nonwoven fabric sheet only over a predetermined range, and an aluminum vapor deposition film is adhered only to the central portion. The nonwoven fabric laminated body for manufacturing the heat insulating furoshiki and the heat insulating handbag of the invention can be manufactured at low cost.
なお、本発明の不織布積層体としては、１０００ｍｍ幅前後の積層体ロールを製造する場合であれば、不織布シートの幅：アルミ蒸着フィルムの幅＝１０：５〜１０：７の関係になる様にすれば、断熱性風呂敷や断熱性手提げ袋を製造するのにちょうどよいものとなる。また、アルミ蒸着フィルムとしては、２軸延伸フィルムにアルミ蒸着を施したものを用いると縦横の伸びがアンバランスとならず、被包材の機能としてより好ましいものといえる。 In addition, as a nonwoven fabric laminated body of this invention, if it is a case where the laminated body roll around 1000 mm width is manufactured, it will become the relationship of the width | variety of a nonwoven fabric sheet: The width | variety of an aluminum vapor deposition film = 10: 5-10: 7 Then, it will be just right to manufacture an insulating furoshiki and an insulating bag. Moreover, as an aluminum vapor deposition film, when the thing which gave aluminum vapor deposition to the biaxially stretched film is used, it can be said that the vertical and horizontal elongation does not become unbalanced and is more preferable as a function of the encapsulating material.
本発明によれば、保冷・保温機能を付加した風呂敷や手提げ袋等の持ち運び用被包材として使い勝手のよいものを安価に製造することができる。 According to the present invention, an easy-to-use enveloping material such as a furoshiki or a handbag provided with a cold and heat retaining function can be manufactured at low cost.
次に、本発明の実施形態として、まず、不織布積層体の製造方法を、図１を参照しながら説明する。実施形態としての不織布積層体の製造方法では、まず、所定幅を有する不織布ロール１と、不織布ロール１よりも狭い幅のアルミ蒸着フィルムロール２とを用意する。そして、不織布ロール１とアルミ蒸着フィルムロール２とを互いの幅方向中心が一致する様に配置し、それぞれから素材３，４を繰り出す。こうして各ロール１，２から繰り出された素材３，４間に、接着剤滴下装置５から、溶融した接着剤６を縞状に垂らしつつ冷却ローラー組７の間に挟み込んで接着する。そして、冷却ローラー組７から繰り出される積層体８を巻き取って積層体ロール９とする。 Next, as an embodiment of the present invention, first, a method for producing a nonwoven fabric laminate will be described with reference to FIG. In the method for manufacturing a nonwoven fabric laminate as an embodiment, first, a nonwoven fabric roll 1 having a predetermined width and an aluminum vapor deposition film roll 2 having a narrower width than the nonwoven fabric roll 1 are prepared. And the nonwoven fabric roll 1 and the aluminum vapor deposition film roll 2 are arrange | positioned so that a mutual width direction center may correspond, and the raw materials 3 and 4 are paid out from each. In this manner, the molten adhesive 6 is sandwiched between the cooling roller sets 7 while being dropped from the adhesive dropping device 5 between the raw materials 3 and 4 fed from the rolls 1 and 2 and bonded. And the laminated body 8 drawn | fed out from the cooling roller group 7 is wound up, and it is set as the laminated body roll 9. FIG.
こうして製造された不織布積層体８は、図２に示す様に、両端から所定幅Ｂに渡って不織布シート３のみとなり、中央にアルミ蒸着フィルム４が接着されたものとなる。また、この不織布積層体８においては、長手方向に縞状に接着線１０が形成され、不織布シート３とアルミ蒸着フィルム４の重なっている範囲の全部は接着されてはいない。よって、接着線１０同士の間には、通気性のある不織布シート３を介して侵入する空気を受け入れることができる。 As shown in FIG. 2, the nonwoven fabric laminate 8 manufactured in this way is only the nonwoven fabric sheet 3 over a predetermined width B from both ends, and the aluminum vapor deposition film 4 is bonded to the center. Moreover, in this nonwoven fabric laminated body 8, the adhesive line 10 is formed in stripes in the longitudinal direction, and the whole range where the nonwoven fabric sheet 3 and the aluminum vapor deposition film 4 overlap is not adhered. Therefore, the air which penetrate | invades through the breathable nonwoven fabric sheet 3 can be received between the bonding wires 10.
また、この不織布積層体８から、図３に示す様に、積層体の両端を一対の角とする様に正方形に打ち抜けば、断熱性風呂敷２０を製造することができる。同様に、図４に示す様に、不織布積層体８を所定長さのカットシート３１に切断し（Ａ）、このカットシート３１をアルミ蒸着フィルム４の幅中心で二つ折りにして両端をヒートシールで接合し（Ｂ）、不織布のみの部分に持ち手穴３２を打ち抜けば（Ｃ）、断熱性手提げ袋３０を製造することができる（Ｄ）。 In addition, as shown in FIG. 3, the nonwoven fabric laminate 8 can be manufactured by punching into a square shape so that both ends of the laminate have a pair of corners. Similarly, as shown in FIG. 4, the nonwoven fabric laminate 8 is cut into a cut sheet 31 having a predetermined length (A), the cut sheet 31 is folded in half at the center of the width of the aluminum vapor-deposited film 4, and both ends are heat sealed. (B) and punch through the handle hole 32 only in the non-woven fabric (C), the heat-insulating handbag 30 can be manufactured (D).
次に、実施例を説明する。実施例として、片面にグラビア印刷を施したポリプロピレン不織布（スパンボンド、２５ｇ／ｍ２ 、幅１０００ｍｍ）に対して、アルミ蒸着フィルム（３０μｍの２軸延伸ポリエチレンフィルムの片面にアルミ蒸着、幅５００ｍｍ）を、ポリプロピレン不織布の非印刷面に対してアルミ蒸着面が重なり、かつ、アルミ蒸着フィルムがポリプロピレン不織布の幅中央に位置する様にスジ状ポリエチレンラミネート共押出法で貼り合わせて図２に例示した様な構成の不織布積層体を製造し、図３に示す様に正方形に打ち抜いて断熱性風呂敷を製造した。 Next, examples will be described. As an example, an aluminum vapor-deposited film (aluminum vapor-deposited on one side of a 30 μm biaxially stretched polyethylene film, width 500 mm) is applied to a polypropylene nonwoven fabric (spunbond, 25 g / m 2 , width 1000 mm) subjected to gravure printing on one side. As shown in FIG. 2, the aluminum vapor deposition surface overlaps the non-printing surface of the polypropylene nonwoven fabric, and the aluminum vapor deposition film is laminated by a stripe polyethylene laminate coextrusion method so as to be positioned at the center of the width of the polypropylene nonwoven fabric. A non-woven fabric laminate having the structure was manufactured and punched into a square as shown in FIG. 3 to manufacture a heat insulating furoshiki.
一方、比較例として、アルミ蒸着フィルムを積層しないポリプロピレン不織布（スパンボンド、２５ｇ／ｍ２ 、幅１０００ｍｍ）そのものを正方形に打ち抜いた不織布風呂敷を製造した。 On the other hand, as a comparative example, a nonwoven fabric furoshiki was manufactured by punching a polypropylene nonwoven fabric (spunbond, 25 g / m 2 , width 1000 mm) itself without laminating an aluminum vapor deposition film into a square.
そして、これら実施例及び比較例の風呂敷を用いて、紙コップ（低発泡ポリスチレン製、直径９５ｍｍ×深さ６５ｍｍに八分目（１００ｃｃ）の氷水を入れたものを包んだ場合の水温変化を計測した。なお、実験に当たり、この氷水入りの紙コップを、１８０ｍｍ×２６０ｍｍ×１３０ｍｍ×のポリプロピレン製のカゴの中央に置き、各風呂敷で包んだ。また、水温は、デジタル温度計（熱電対Ｋタイプ；（株）佐藤計量器製作所製の商品番号「ＳＫ−１１０」）で計測した（比較例Ａ、実施例Ｂ）。また、もう一つの比較例として、風呂敷で包まないままの紙コップ内の氷水の温度変化もブランクとして計測した。その結果を、表１及び図５に示す。 Then, using the furoshikis of these examples and comparative examples, a change in water temperature was measured when a paper cup (made of low foam polystyrene, diameter 95 mm × depth 65 mm with ice water of the eighth minute (100 cc) put therein was wrapped. In the experiment, the iced water-containing paper cup was placed in the center of a polypropylene basket of 180 mm × 260 mm × 130 mm × and wrapped with a furoshiki.The water temperature was measured with a digital thermometer (thermocouple K type; (Comparative Example A, Example B) measured by a product number “SK-110” manufactured by Sato Keiki Seisakusho Co., Ltd. As another comparative example, ice water in a paper cup not wrapped in a furoshiki The temperature change was also measured as a blank, and the results are shown in Table 1 and FIG.
計測場所・・・出願人会社の会議室内
計測開始時の室温・・・２８．５℃
計測開始時の湿度・・・８０．０％
Humidity at the start of measurement: 80.0%
実験結果から、ブランク及び比較例に比べて、実施例は断熱効果の差が確認できた。また、この実施例の風呂敷は、包装するに当たり、中央にカゴを置き、まず、アルミ蒸着フィルムが積層されている方の角を持ち上げて折り、その後、アルミ蒸着フィルムの積層されていない角を持ち上げて結んだところ、比較例の風呂敷と変わらない使用感であった。従って、実施例では、本発明の目的である使い勝手のよい断熱性風呂敷が製造できたといえる。また、その製造方法は、上述の実施形態の通りであり、低コストで実施できた。 From the experimental result, the Example has confirmed the difference of the heat insulation effect compared with the blank and the comparative example. In addition, the furoshiki of this embodiment, when packaging, put a basket in the center, first lift and fold the corner where the aluminum vapor deposition film is laminated, then lift the corner where the aluminum vapor deposition film is not laminated As a result, it was the same feeling as the comparative example furoshiki. Therefore, in the Examples, it can be said that an easy-to-use heat insulating furoshiki, which is the object of the present invention, was manufactured. Moreover, the manufacturing method is as the above-mentioned embodiment, and could be implemented at low cost.
以上、発明の実施形態並びに実施例を説明したが、本発明は、これに限定されるものではなく、例えば、不織布シートの幅を１２００ｍｍ、アルミ蒸着フィルムの幅を７００ｍｍとしたり、持ち手穴３２だけでなく不織布のみの部分のヒートシール部をも切断してレジ袋の様な形状の手提げ袋とするなど、その要旨を逸脱しない範囲内における種々の変更が可能である。 As mentioned above, although embodiment and the Example of invention were described, this invention is not limited to this, For example, the width | variety of a nonwoven fabric sheet shall be 1200 mm, the width | variety of an aluminum vapor deposition film shall be 700 mm, or the handle hole 32 In addition, various modifications can be made without departing from the gist of the invention, such as cutting a heat-sealed portion of only a non-woven fabric into a handbag having a shape like a plastic bag.
１・・・不織布ロール
２・・・アルミ蒸着フィルムロール
３・・・不織布シート
４・・・アルミ蒸着フィルム
５・・・接着剤滴下装置
６・・・接着剤
７・・・冷却ローラー組
８・・・不織布積層体
９・・・積層体ロール
１０・・・接着線
２０・・・断熱性風呂敷
３０・・・断熱性手提げ袋
３１・・・カットシート
３２・・・持ち手穴
DESCRIPTION OF SYMBOLS 1 ... Nonwoven fabric roll 2 ... Aluminum vapor deposition film roll 3 ... Nonwoven fabric sheet 4 ... Aluminum vapor deposition film 5 ... Adhesive dripping apparatus 6 ... Adhesive 7 ... Cooling roller group 8.・ ・ Nonwoven fabric laminated body 9 ・ ・ ・ Laminated body roll 10 ・ ・ ・ Adhesive wire 20 ・ ・ ・ Heat-insulating furoshiki 30… Heat-insulating handbag 31… Cut sheet 32… Hand hole
Claims (4)
（１−１）前記不織布積層体は、不織布シートに対してアルミ蒸着フィルムが縞状に塗布された接着剤を介して部分的に接着されたものであること。
（１−２）前記縞状に塗布された接着剤の線が風呂敷の隣会う辺間を結ぶ様に形成されていること。
（１−３）前記アルミ蒸着フィルムは、風呂敷の一対の対角の方向に伸びる帯状に前記不織布シートに接着されており、他の一対の対角から中心へ向かって所定範囲の三角形部分には接着されていないこと。 A heat insulating furoshiki, which is formed of a nonwoven fabric laminate in which an aluminum vapor deposition film is bonded to a nonwoven fabric sheet and has the following configuration.
(1-1) The said nonwoven fabric laminated body shall be partially adhere | attached through the adhesive agent with which the aluminum vapor deposition film was apply | coated to the nonwoven fabric sheet in stripe form.
(1-2) It is formed so that the line | wire of the adhesive apply | coated to the said stripe form may connect between the sides which meet a furoshiki.
(1-3) The aluminum vapor-deposited film is bonded to the nonwoven fabric sheet in a strip shape extending in a pair of diagonal directions of a furoshiki, and in a triangular portion of a predetermined range from the other pair of diagonals toward the center. It is not glued.
（２−１）前記不織布積層体を二つ折りにして底を形成し、左右側面を熱融着させて袋体とすると共に、上部に該不織布積層体の一部を打ち抜いた持ち手穴が形成されていること。
（２−２）前記不織布積層体は、不織布シートに対してアルミ蒸着フィルムが縞状に塗布された接着剤を介して部分的に接着されたものであること。
（２−３）前記縞状に塗布された接着剤の線が手提げ袋の水平方向に形成されていること。
（２−４）前記アルミ蒸着フィルムは、手提げ袋の上部から少なくとも前記持ち手穴よりも下方所定範囲を除く底面側部分にだけ接着されていること。 A heat insulating handbag formed of a nonwoven fabric laminate in which an aluminum vapor-deposited film is bonded to a nonwoven fabric sheet and having the following configuration.
(2-1) The nonwoven fabric laminate is folded in two to form a bottom, and the right and left side surfaces are heat-sealed to form a bag, and a handle hole is formed in the upper portion by punching out a part of the nonwoven fabric laminate. is being done.
(2-2) The said nonwoven fabric laminated body shall be partially adhere | attached through the adhesive agent with which the aluminum vapor deposition film was apply | coated to the nonwoven fabric sheet in stripe form.
(2-3) The line of the adhesive applied in the stripe pattern is formed in the horizontal direction of the handbag.
(2-4) The aluminum vapor-deposited film is adhered only to the bottom side portion excluding a predetermined range below the handle hole from the upper part of the handbag.
（３−１）縞状に塗布された接着剤を介して不織布シートとアルミ蒸着フィルムとが部分的に接着されたロール状のものであること。
（３−２）前記アルミ蒸着フィルムは、前記不織布シートよりも幅が狭く、かつ、不織布シートの幅方向両端を所定幅に渡って露出させた状態となる様に、前記不織布シートの中央に合わせて接着されていること。 A nonwoven fabric laminate in which an aluminum vapor deposition film is bonded to a nonwoven fabric sheet, the nonwoven fabric laminate having the following configuration.
(3-1) It is a roll-like thing in which the nonwoven fabric sheet and the aluminum vapor deposition film are partially bonded via an adhesive applied in a striped manner.
(3-2) The aluminum vapor deposition film is narrower than the nonwoven fabric sheet, and is aligned with the center of the nonwoven fabric sheet so that both ends of the nonwoven fabric sheet in the width direction are exposed over a predetermined width. Be glued.
（４−１）所定幅を有する不織布ロールと、該不織布ロールよりも狭い幅のアルミ蒸着フィルムロールとを用意すること。
（４−２）前記不織布ロールと前記アルミ蒸着フィルムロールとを互いの幅方向中心が一致する様に配置し、それぞれから素材を繰り出すこと。
（４−３）前記それぞれから繰り出された素材間に、縞状に接着剤を垂らしつつ、接着用のローラー組の間に挟み込むこと。
（４−４）前記接着用のローラー組から繰り出される積層体を巻き取ってロール状とすること。 A method for producing a nonwoven fabric laminate in which an aluminum vapor-deposited film is bonded to a nonwoven fabric sheet, and having the following configuration.
(4-1) Prepare a nonwoven fabric roll having a predetermined width and an aluminum vapor deposition film roll having a narrower width than the nonwoven fabric roll.
(4-2) The non-woven fabric roll and the aluminum vapor-deposited film roll are arranged so that the centers in the width direction coincide with each other, and the material is fed out from each.
(4-3) The material is drawn between the materials, and the adhesive is suspended in a striped manner, and sandwiched between the bonding roller sets.
(4-4) The laminated body drawn out from the bonding roller set is wound into a roll shape.