JP2008214982A - Decorative plate - Google Patents
Decorative plate Download PDFInfo
- Publication number
- JP2008214982A JP2008214982A JP2007054967A JP2007054967A JP2008214982A JP 2008214982 A JP2008214982 A JP 2008214982A JP 2007054967 A JP2007054967 A JP 2007054967A JP 2007054967 A JP2007054967 A JP 2007054967A JP 2008214982 A JP2008214982 A JP 2008214982A
- Authority
- JP
- Japan
- Prior art keywords
- decorative plate
- decorative
- decorative board
- clearance
- umbrella
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、床材、天井、天井などの建築内装用化粧板であって、複数の矩形部材を連接して広い面を施工可能とする化粧板に関する。 The present invention relates to a decorative board for building interior such as a flooring material, a ceiling, and a ceiling, and relates to a decorative board that allows a wide surface to be constructed by connecting a plurality of rectangular members.
従来、上記のような化粧材の構成では、その端面を図2で示すような連結構造として組み合わせていくものが知られている。しかしながらこのような構造である場合、嵌合はずれや水の浸入といった問題が発生していた。 Conventionally, in the configuration of the decorative material as described above, it is known that end surfaces thereof are combined as a connection structure as shown in FIG. However, in such a structure, problems such as disengagement and water intrusion have occurred.
それに対して、化粧板基材の両面下部に凹部を設けて連結部材でこれらを連結する方法も知られている。しかしながら、このような場合であっても、先の場合より顕著ではないものの、嵌合はずれや水の浸入は避けられないものであった。
本発明はこのような問題点を解決するためになされたものであり、その課題とするところは、嵌合はずれや水の浸入の問題のない化粧板を得ることにある。 The present invention has been made to solve such problems, and the object of the present invention is to obtain a decorative board free from problems of disengagement and water intrusion.
本発明はこの課題を解決するものであり、すなわちその請求項1記載の発明は、底板部の両側に上向きの突出部を備えたコ字状の連結部材によって隣り合う化粧板基材が連結される化粧板において、前記突出部が傘状であり、前記突出部により嵌合されるような係止溝が、化粧板基材の両端部の幅方向の裏面に設けてなり、前記化粧板基材の弾性率は1900〜4000MPaであり、前記突出部と前記係止溝の隙間をaとしたときに、化粧板どうしの隙間を2aとなるように設け前記隙間aが0.2〜0.7mmであり、前記突出部の傘状の最大幅をA、最小幅をBとしたときにA−Bが0.05〜0.5mmとなるように設けてなることを特徴とする化粧板である。 The present invention solves this problem. That is, in the invention according to claim 1, adjacent decorative plate base materials are connected by U-shaped connecting members having upward projecting portions on both sides of the bottom plate portion. In the decorative board, the protruding portion is umbrella-shaped, and a locking groove to be fitted by the protruding portion is provided on the back surface in the width direction of both end portions of the decorative plate base. The elastic modulus of the material is 1900 to 4000 MPa, and when the clearance between the protruding portion and the locking groove is a, the clearance between the decorative plates is 2a, and the clearance a is 0.2 to 0. A decorative board characterized in that it is 7 mm and is provided so that A-B is 0.05 to 0.5 mm when the maximum width of the umbrella-shaped protrusion is A and the minimum width is B. is there.
本発明により、嵌合時の破損がなく、嵌合後も嵌合はずれや水の侵入といった問題も発生することがない化粧板を提供することが可能になるという効果を奏する。 According to the present invention, there is an effect that it is possible to provide a decorative board that is not damaged at the time of fitting and that does not cause problems such as disengagement or intrusion of water even after fitting.
以下、本発明を図面に基づき詳細に説明する。図1に本発明の化粧板の一実施例の断面の構造を示す。
化粧板基材1に係止溝2を設けてなり、連結部材3には傘状突起4を有してなる。
Hereinafter, the present invention will be described in detail with reference to the drawings. FIG. 1 shows a cross-sectional structure of one embodiment of the decorative board of the present invention.
The decorative board substrate 1 is provided with a locking groove 2, and the connecting member 3 has an umbrella-shaped protrusion 4.
本発明における化粧板基材1は、弾性率が1900〜4000MPaのものが用いられる。具体的には、ポリオレフィン系樹脂に木粉その他の充填剤、添加剤を添加して得られる木質系樹脂を異型押出成形にて成形するものが好適に用いられ、その際に意匠的に問題のない範囲でその添加割合を調整すれば良い。具体的には、ホモポリプロピレン80重量部にマレイン酸変成ポモポリプロピレン20重量部を混合したものに平均粒径100μmに粉砕した木粉を100重量部添加してなるものが好適である。 As the decorative board substrate 1 in the present invention, one having an elastic modulus of 1900 to 4000 MPa is used. Specifically, it is suitable to use a wood-based resin obtained by adding wood powder or other fillers and additives to a polyolefin-based resin by profile extrusion molding. What is necessary is just to adjust the addition ratio in the range which is not. Specifically, a mixture of 80 parts by weight of homopolypropylene mixed with 20 parts by weight of maleic acid-modified pomopolypropylene and 100 parts by weight of wood powder ground to an average particle size of 100 μm is preferable.
本発明における係止溝2は、化粧板基材1の成形時に設けるものでもよいし、成形後に切削加工により設けても良い。 The locking groove 2 in the present invention may be provided when the decorative board substrate 1 is molded, or may be provided by cutting after molding.
本発明における連結部材3は、化粧板基材と同様の材料、同様の方法により成形するのが好適であるが、特にこれに限定するものではなく、同様の弾性率と求める範囲の形状のものが得られれば良い。 The connecting member 3 in the present invention is preferably formed by the same material and the same method as the decorative board base material, but is not particularly limited to this, and has the same elastic modulus and the required shape. If it is obtained.
本発明における傘状突起4は、連結部材3の成形時に設けるものでもよいし、成形後に切削加工により設けても良い。 The umbrella-shaped protrusion 4 in the present invention may be provided when the connecting member 3 is formed, or may be provided by cutting after forming.
化粧板基材としてポリプロピレン(サンアロマー(株)製:「PS201A」)100重量部に平均粒径100μmの木粉を100重量部添加したものを材料とし、異型成形にて下図断面形状のサンプルを作成した。
A寸法:3.7mm、B寸法:3.5mm
a寸法:0.3mm
弾性率:2250MPa
上図の嵌合力を汎用ロードセルに荷重をかけ測定した結果、60N/cm2の値を得た。
A sample with the cross-sectional shape shown in the figure below was prepared by atypical molding using 100 parts by weight of polypropylene powder (manufactured by Sun Allomer Co., Ltd .: “PS201A”) as the decorative board base material and 100 parts by weight of wood powder having an average particle size of 100 μm. did.
A dimension: 3.7 mm, B dimension: 3.5 mm
a dimension: 0.3 mm
Elastic modulus: 2250 MPa
As a result of applying the load to the general-purpose load cell and measuring the fitting force in the above figure, a value of 60 N / cm 2 was obtained.
図1に示すように嵌合した。嵌合時に破損等は認められず、嵌合はずれ、荷重試験(50kg/直径100mm)、水の浸入(50ml水を直径100mm円筒に入れ1時間放置した後に嵌合部からの水の浸入を確認する)等の試験でも異常は認められなかった。また、図1の状態で0℃雰囲気下で下台の合板に接着剤(コニシ(株)製「KU928R」)で接着し、2日放置し、その後40℃雰囲気に変更したが、化粧板同士の突き上げ等不具合は確認されなかった。 As shown in FIG. No breakage, etc. was observed at the time of mating, disengagement, load test (50 kg / 100 mm in diameter), water intrusion (50 ml of water in a 100 mm diameter cylinder was allowed to stand for 1 hour, and then water intrusion from the mating part was confirmed. No abnormalities were found even in the test. Also, in the state of FIG. 1, it was bonded to the lower plywood with an adhesive (“KU928R” manufactured by Konishi Co., Ltd.) in an atmosphere of 0 ° C. and left for 2 days, and then changed to a 40 ° C. atmosphere. No problems such as pushing up were confirmed.
<比較例1>
実施例1のポリプロピレン(サンアロマー(株)製:「PS201A」)100重量部のかわりに、弾性率の異なる材料(試験体1:ゼオン化成(株)製「AH4204」、試験体2:ゼオン化成(株)製「WAH7100」)を用い、それ以外は実施例1と同様の製法で作成した。
A寸法:3.7mm、B寸法:3.5mm
a寸法:0.3mm
弾性率:試験体1 1500MPa
試験体2 4200MPa
試験体1は嵌合パーツが曲がり嵌合させる事が不可能であった。
試験体2は嵌合パーツが破損し、嵌合させる事が不可能であった。
<Comparative Example 1>
Instead of 100 parts by weight of the polypropylene of Example 1 (manufactured by Sun Allomer Co., Ltd .: “PS201A”), materials having different elastic moduli (Test Sample 1: “AH4204” manufactured by Zeon Kasei Co., Ltd.), Test Sample 2: Zeon Kasei ( (WAH7100) manufactured by Co., Ltd.) was used, and the other manufacturing methods were the same as in Example 1.
A dimension: 3.7 mm, B dimension: 3.5 mm
a dimension: 0.3 mm
Elastic modulus: Specimen 1 1500 MPa
Specimen 2 4200 MPa
In the test body 1, it was impossible to bend and fit the fitting parts.
It was impossible to fit the test body 2 because the fitting parts were damaged.
<比較例2>
下記のように寸法を変えた以外は実施例1と同様の製法で作成した。
A寸法:3.7mm、B寸法:2.7mm
a寸法:0.3mm
弾性率:2250MPa
嵌合パーツ及び化粧版とも嵌合時に破損した。
<Comparative example 2>
The same production method as in Example 1 was used except that the dimensions were changed as follows.
A dimension: 3.7 mm, B dimension: 2.7 mm
a dimension: 0.3 mm
Elastic modulus: 2250 MPa
Both the fitting parts and the decorative plate were damaged during fitting.
<比較例3>
下記のように寸法を変えた以外は実施例1と同様の製法で作成した。
A寸法:3.7mm、B寸法:3.68mm
a寸法:0.3mm
弾性率:2250MPa
この嵌合力を汎用ロードセルに荷重をかけ測定した結果5N/cm2の値を得た。
嵌合時に破損等は認められなかったが、嵌合はずれ(荷重試験50kg/直径100mm)、水の浸入(50ml水を直径100mm円筒に入れ1時間放置した後に嵌合部からの水の浸入を確認する)等の試験で異常が確認された。また、この状態で0℃雰囲気下で下板合板に接着剤(コニシ(株)製「KU928R」)で接着し、2日放置し、その後40℃雰囲気に変更したが化粧版同士の突き上げ等不具合は確認されなかった。
<Comparative Example 3>
The same production method as in Example 1 was used except that the dimensions were changed as follows.
A dimension: 3.7 mm, B dimension: 3.68 mm
a dimension: 0.3 mm
Elastic modulus: 2250 MPa
This fitting force was measured by applying a load to a general-purpose load cell, and a value of 5 N / cm 2 was obtained.
No breakage or the like was found at the time of mating, but the mating was lost (load test 50 kg / diameter 100 mm) and water entered (50 ml of water was put into a cylinder with a diameter of 100 mm and left for 1 hour, and then water entered from the mating part. An abnormality was confirmed in a test. Also, in this state, it was bonded to the lower plywood with an adhesive (“KU928R” manufactured by Konishi Co., Ltd.) in an atmosphere of 0 ° C., left for 2 days, and then changed to an atmosphere of 40 ° C. Was not confirmed.
<比較例4>
下記のように寸法を変えた以外は実施例1と同様の製法で作成した。
A寸法:3.7mm、B寸法:3.5mm
a寸法:0.1mm
弾性率:2250MPa
この嵌合力を汎用ロードセルに荷重をかけ測定した結果60N/cm2の値を得た。
嵌合時に破損等は認められず、嵌合はずれ、荷重試験(50kg/直径100mm)、水の浸入(50ml水を直径100mm円筒に入れ1時間放置した後に嵌合部からの水の浸入を確認する)等の試験でも異常は認められなかった。しかし、この状態で0℃雰囲気下で下板合板に接着剤(コニシ(株)製「KU928R」)で接着し、2日放置し、その後40℃雰囲気に変更した際、化粧版同士の突き上げの不具合が確認された。
<Comparative Example 4>
The same production method as in Example 1 was used except that the dimensions were changed as follows.
A dimension: 3.7 mm, B dimension: 3.5 mm
a dimension: 0.1 mm
Elastic modulus: 2250 MPa
The fitting force was measured by applying a load to a general-purpose load cell, and a value of 60 N / cm 2 was obtained.
No breakage, etc. was observed at the time of mating, disengagement, load test (50 kg / 100 mm in diameter), water intrusion (50 ml of water was placed in a 100 mm diameter cylinder and left for 1 hour, and then water intrusion from the mating part was confirmed. No abnormalities were found even in the test. However, in this state, when the adhesive is attached to the lower plywood in an atmosphere of 0 ° C. with an adhesive (“KU928R” manufactured by Konishi Co., Ltd.), left for 2 days, and then changed to an atmosphere of 40 ° C., the decorative plates are pushed up. A bug was confirmed.
<比較例5>
下記のように寸法を変えた以外は実施例1と同様の製法で作成した。
A寸法:3.7mm、B寸法:3.5mm
a寸法:1.0mm
弾性率:2250MPa
この嵌合力を汎用ロードセルに荷重をかけ測定した結果60N/cm2の値を得た。
嵌合時に破損等は認められず、嵌合はずれ、荷重試験(50kg/直径100mm)、水の浸入(50ml水を直径100mm円筒に入れ1時間放置した後に嵌合部からの水の浸入を確認する)等の試験でも異常は認められなかった。また、上図の状態で0℃雰囲気下で下板合板に接着剤(コニシ(株)製「KU928R」)で接着し、2日放置し、その後40℃雰囲気に変更しても化粧版同士の突き上げ等不具合は確認されなかった。しかし、隙間Cが0℃雰囲気下で2a=2mmと大きくなり、外観上好ましくなかった。
<Comparative Example 5>
The same production method as in Example 1 was used except that the dimensions were changed as follows.
A dimension: 3.7 mm, B dimension: 3.5 mm
a dimension: 1.0 mm
Elastic modulus: 2250 MPa
The fitting force was measured by applying a load to a general-purpose load cell, and a value of 60 N / cm 2 was obtained.
No breakage, etc. was observed at the time of mating, disengagement, load test (50 kg / 100 mm in diameter), water intrusion (50 ml of water was placed in a 100 mm diameter cylinder and left for 1 hour, and then water intrusion from the mating part was confirmed. No abnormalities were found even in the test. In the state of the above figure, even if it is bonded to the lower plywood with an adhesive (“KU928R” manufactured by Konishi Co., Ltd.) in an atmosphere of 0 ° C. and left for 2 days, No problems such as pushing up were confirmed. However, the gap C was as large as 2a = 2 mm in an atmosphere at 0 ° C., which was not preferable in appearance.
本発明の化粧板は、特に床材として好適な建築内装用化粧板として利用可能である。 The decorative board of the present invention can be used as a decorative board for building interiors particularly suitable as a flooring material.
1…化粧板基材
2…係止溝
3…連結部材
4…傘状突起
DESCRIPTION OF SYMBOLS 1 ... Decorative plate base material 2 ... Locking groove 3 ... Connecting member 4 ... Umbrella-shaped protrusion
Claims (1)
前記化粧板基材の弾性率は1900〜4000MPaであり、
前記突出部と前記係止溝の隙間をaとしたときに、化粧板どうしの隙間を2aとなるように設け、
前記隙間aが0.2〜0.7mmであり、
前記突出部の傘状の最大幅をA、最小幅をBとしたときにA−Bが0.05〜0.5mmとなるように設けてなることを特徴とする化粧板。
In a decorative board in which adjacent decorative plate base members are connected by a U-shaped connecting member having upward protruding portions on both sides of the bottom plate portion, the protruding portions are umbrella-shaped and are fitted by the protruding portions. Such a locking groove is provided on the back surface in the width direction of both ends of the decorative board substrate,
The elastic modulus of the decorative board substrate is 1900 to 4000 MPa,
When the gap between the protruding portion and the locking groove is a, the gap between the decorative plates is 2a,
The gap a is 0.2 to 0.7 mm,
A decorative board, wherein the protrusion has an umbrella-shaped maximum width A and a minimum width B, and AB is 0.05 to 0.5 mm.