JP2008184217A - Flexible container sheet, and flexible container - Google Patents
Flexible container sheet, and flexible container Download PDFInfo
- Publication number
- JP2008184217A JP2008184217A JP2007021590A JP2007021590A JP2008184217A JP 2008184217 A JP2008184217 A JP 2008184217A JP 2007021590 A JP2007021590 A JP 2007021590A JP 2007021590 A JP2007021590 A JP 2007021590A JP 2008184217 A JP2008184217 A JP 2008184217A
- Authority
- JP
- Japan
- Prior art keywords
- flexible container
- fibers
- sheet
- woven fabric
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、コンテナの形状保持性および屈曲疲労性に優れたフレキシブルコンテナ用シートおよびフレキシブルコンテナに関するものである。 TECHNICAL FIELD The present invention relates to a flexible container sheet and a flexible container that are excellent in container shape retention and bending fatigue.
従来、各種樹脂ペレット類、薬剤類、農薬類、肥料類あるいは食品類などの粒状物を輸送するために、繊維基布に熱可塑性樹脂を被覆加工したシートを用いたフレキシブルコンテナが広く使用されている。そして、上記繊維基布としては、ポリエチレンテレフタレート繊維からなる布帛などが用いられている（例えば、特許文献１など）。さらに、上記シートは、フレキシブルコンテナ袋体の本体布や内張布に使用される。しかしながら、従来の上記袋体には、折り畳みなどの繰り返し屈曲を受けたり、粒状内容物の出し入れ時や運搬時の振動により、布帛を構成する繊維の一部分に過度の荷重が掛かり、変形したり、また繰り返し使用により布帛が部分的に破れるといった問題がある。
本発明は、かかる背景技術に鑑みなされたもので、その目的は、形状保持性および屈曲疲労性に優れたフレキシブルコンテナ用シートおよびそれからなるフレキシブルコンテナを提供することにある。 This invention is made | formed in view of this background art, The objective is to provide the sheet | seat for flexible containers excellent in shape maintenance property and bending fatigue | exhaustion property, and a flexible container consisting thereof.
本発明者らが検討した結果、かかる課題は、織物からなるフレキシブルコンテナに用いるシートであって、該織物が、ポリエチレンナフタレート繊維を経糸または緯糸の少なくとも一方に用いてなる織物であることを特徴とするフレキシブルコンテナ用シート、および、該フレキシブルコンテナ用シートで構成されていることを特徴とするフレキシブルコンテナより達成できることを見出した。 As a result of investigations by the present inventors, such a problem is a sheet used for a flexible container made of a woven fabric, wherein the woven fabric is a woven fabric using polyethylene naphthalate fiber as at least one of warp or weft. It has been found that this can be achieved from a flexible container characterized by comprising the flexible container sheet and the flexible container sheet.
本発明によれば、形状保持性および屈曲疲労性に優れたフレキシブルコンテナ用シートおよびフレキシブルコンテナを提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the sheet | seat and flexible container for flexible containers excellent in shape retainability and bending fatigue | exhaustion property can be provided.
本発明のフレキシブルコンテナ用シートは、織物からなるフレキシブルコンテナに用いるシートである。 The sheet | seat for flexible containers of this invention is a sheet | seat used for the flexible container which consists of textiles.
本発明においては、上記織物が、ポリエチレンナフタレート繊維を経糸または緯糸の少なくとも一方に用いてなる織物であることが肝要である。すなわち、従来のポリエチレンテレフタレート繊維などの織物を用いたシートでは、折り畳みなどの繰り返し屈曲を受けたり、粒状内容物の出し入れ時や、運搬時の振動により、布帛を構成する繊維の一部分に過度の荷重が掛かり変形したり、また繰り返し使用により布帛が部分的に破れるという問題がある。かかる問題に対して本発明者らが検討を行い、上記のようにポリエチレンナフタレート繊維からなる織物を用いたところ、シートが変形しにくく、しかもシートの屈曲疲労性が格段に向上することを究明した。 In the present invention, it is important that the woven fabric is a woven fabric using polyethylene naphthalate fiber as at least one of warp or weft. That is, in a sheet using a conventional woven fabric such as polyethylene terephthalate fiber, excessive load is applied to a part of the fibers constituting the fabric due to repeated bending such as folding, vibration during loading and unloading of granular contents, and transportation. There is a problem that the fabric is deformed by being applied, and the fabric is partially broken by repeated use. The present inventors have investigated this problem and found that the use of a woven fabric made of polyethylene naphthalate fibers as described above reveals that the sheet is hardly deformed and the bending fatigue property of the sheet is remarkably improved. did.
なお、本発明においては、ポリエチレンナフタレート繊維が、織物の経糸または緯糸のいずれかに用いるだけでも十分な効果を得ることができるが、より高い形状保持性や屈曲疲労性を実現する上では、織物の経糸および緯糸の両方に用いることが好ましい。 In the present invention, a polyethylene naphthalate fiber can obtain a sufficient effect even if it is used for either a warp or a weft of a woven fabric, but in realizing higher shape retention and bending fatigue, It is preferable to use it for both warp and weft of a woven fabric.
本発明に用いるポリエチレンナフタレート繊維は、エチレン−２，６−ナフタレート単位を主たる構成成分とするポリエステルからなる繊維であり、１０モル％以下の範囲で適当な第３成分を含む共重合体からなる繊維であってもよい。 The polyethylene naphthalate fiber used in the present invention is a fiber made of polyester having ethylene-2,6-naphthalate unit as a main constituent, and is made of a copolymer containing an appropriate third component in the range of 10 mol% or less. It may be a fiber.
上記ポリエチレンナフタレート繊維の総繊度は、５０〜２０００ｄｔｅｘ、単繊維繊度は１〜１０ｄｔｅｘが好ましい。また、上記繊維の横断面形状は、丸断面でも異型断面でもかまわない。 The total fineness of the polyethylene naphthalate fiber is preferably 50 to 2000 dtex, and the single fiber fineness is preferably 1 to 10 dtex. Moreover, the cross-sectional shape of the fiber may be a round cross section or an irregular cross section.
また、上記ポリエチレンナフタレート繊維は、形状保持性や屈曲疲労性の観点から、強度は、６ｃＮ／ｄｔｅｘ以上が好ましく、７ｃＮ／ｄｔｅｘ以上がより好ましく、また、伸度は、５％以上好ましく、８％以上がより好ましい。同様の観点から、固有粘度は、０．６以上が好ましく、０．７以上がより好ましい。 The polyethylene naphthalate fiber preferably has a strength of 6 cN / dtex or more, more preferably 7 cN / dtex or more, and an elongation of 5% or more, from the viewpoint of shape retention and bending fatigue. % Or more is more preferable. From the same viewpoint, the intrinsic viscosity is preferably 0.6 or more, and more preferably 0.7 or more.
織物を構成するポリエチレンナフタレート繊維以外の繊維としては、ポリアミド繊維、ポリエステル系繊維、ポリオレフィン系繊維、アクリル系繊維、塩化ピニリデン系繊維、ポリビニルアルコール系繊維、アラミド系繊維、ポリイミド系繊維、ポリスルホン系繊維、フッ素系繊維などの繊維単体であっても、またそれらの組み合わせたものであっても良いが、物理的特性、化学的特性の点からポリエステル系繊維が好ましい。
なお、前述したポリエチレンナフタレート繊維、および、上記繊維は、長繊維、短繊維の両方を使用できるが、強力の点から長繊維が好ましい。
Examples of fibers other than polyethylene naphthalate fibers constituting the woven fabric include polyamide fibers, polyester fibers, polyolefin fibers, acrylic fibers, vinylidene chloride fibers, polyvinyl alcohol fibers, aramid fibers, polyimide fibers, and polysulfone fibers. These may be single fibers such as fluorine-based fibers or combinations thereof, but polyester fibers are preferred from the viewpoint of physical characteristics and chemical characteristics.
The polyethylene naphthalate fiber and the fiber described above can use both long fibers and short fibers, but long fibers are preferred from the viewpoint of strength.
また、前述したポリエチレンナフタレート繊維、および、上記繊維は、着色剤、耐候剤、難燃剤、充填剤、帯電防止剤、撥水剤、接着剤などが、含有あるいは繊維表面に付着していてかまわない。 The above-mentioned polyethylene naphthalate fiber and the above-mentioned fiber may contain a colorant, a weathering agent, a flame retardant, a filler, an antistatic agent, a water repellent, an adhesive, or the like, or may adhere to the fiber surface. Absent.
本発明に用いる織物は、特に限定されないが、経糸密度および緯糸密度としては、１０〜３０本／インチを採用することができる。また、上記織物は、公知の方法により製織することができる。
本発明においては、上記織物の少なくとも少なくとも片面が、熱可塑性樹脂で被覆されていてもよい。
Although the woven fabric used in the present invention is not particularly limited, 10 to 30 yarns / inch can be adopted as the warp density and the weft density. Moreover, the said textile fabric can be woven by a well-known method.
In the present invention, at least one surface of the woven fabric may be coated with a thermoplastic resin.
上記の熱可塑性樹脂とは、塩化ビニル系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ポリウレタン系樹脂、ポリアクリル系樹脂、ポリフッ化ピニリデンなどのフッ素系樹脂、シリコン系樹脂などであり、これらの少なくとも一種を使用する。なかでも、塩化ビニル系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂が柔軟性、コストなどから好ましく使用される。本発明で使用する塩化ビニル系樹脂は塩化ビニル重合体、塩化ビニル−酢酸ビニル共重合体、塩化ビニル−アクリル酸エステル共重合体、塩化ビニル−塩化ビニリデン共重合体などであり、これらを単独、あるいは２種以上を混合したものに可塑剤、安定剤、耐候剤、架橋剤、抗菌剤、充填剤、防炎剤、着色剤、帯電防止剤などの添加剤を混合したものである。塩化ビニル系樹脂の重合度は６００〜３５００であり、好ましくは８００〜２０００のものを使用する。 The thermoplastic resin is a vinyl resin, a polyolefin resin, a polyester resin, a polyamide resin, a polyurethane resin, a polyacrylic resin, a fluorine resin such as polyvinylidene fluoride, a silicon resin, etc. Use at least one of these. Of these, vinyl chloride resins, polyolefin resins, and polyester resins are preferably used because of their flexibility and cost. The vinyl chloride resin used in the present invention is a vinyl chloride polymer, vinyl chloride-vinyl acetate copolymer, vinyl chloride-acrylic ester copolymer, vinyl chloride-vinylidene chloride copolymer, etc. Alternatively, a mixture of two or more types may be mixed with additives such as plasticizers, stabilizers, weathering agents, crosslinking agents, antibacterial agents, fillers, flameproofing agents, coloring agents, antistatic agents and the like. The degree of polymerization of the vinyl chloride resin is 600-3500, preferably 800-2000.
本発明で使用するオレフィン系樹脂とは、ポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸アルキル共重合体、エチレン−αオレフィン共重合体、高分子鎖中にゴム弾性を持つゴム成分（ソフトセグメント）と常温付近で塑性変形を防止する結晶ないしガラス状成分（ハードセグメント）との互いに相溶しない両成分を有するオレフィンエラストマーなどであり、これらを単独あるいは２種以上を混合したものに可塑剤、安定剤、耐候剤、架橋剤、抗菌剤、充填剤、防炎剤、着色剤、帯電防止剤などの添加剤を混合したものである。 The olefin resin used in the present invention is polyethylene, polypropylene, ethylene-vinyl acetate copolymer, ethylene-alkyl acrylate copolymer, ethylene-α olefin copolymer, rubber having rubber elasticity in a polymer chain. Olefin elastomer having both components (soft segment) and crystal or glassy component (hard segment) that are not compatible with each other at room temperature, which are incompatible with each other, or a mixture of two or more of these And additives such as plasticizers, stabilizers, weathering agents, crosslinking agents, antibacterial agents, fillers, flameproofing agents, colorants, antistatic agents and the like.
本発明で使用するポリエステル系樹脂とは柔軟性の面からポリエステルエラストマーが好ましく、高融点結晶性重合体セグメントとしてジカルボン酸にテレフタル酸、イソフタル酸、ナフタレン−２，６−ジカルボン酸などを使用して、ジオールとして１，４−ブタンジオール、エチレングリコール、トリメチレングリコールなどを使用し、特にテレフタル酸と１，４−ブタンジオールからなるポリブチレンテレフタレートが好ましい。一方、低融点重合体セグメントはポリ（テトラメチレンオキシド）グリコール、ポリ（プロピレンオキシド）グリコールのエチレンオキシド付加物、ポリ（ε−カプロラクトン）、ポリブチレンアジペートなどのポリエステルブロック共重合体が好ましい。低融点重合体セグメントの含有量は１０〜９０重量％、好ましくは１５〜７５重量％である。さらに、可塑剤、安定剤、耐候剤、架橋剤、抗菌剤、充填剤、防炎剤、着色剤、帯電防止剤などの添加剤を混合してもよい。 The polyester resin used in the present invention is preferably a polyester elastomer from the viewpoint of flexibility, and terephthalic acid, isophthalic acid, naphthalene-2,6-dicarboxylic acid or the like is used as a dicarboxylic acid as a high melting point crystalline polymer segment. 1,4-butanediol, ethylene glycol, trimethylene glycol or the like is used as the diol, and polybutylene terephthalate composed of terephthalic acid and 1,4-butanediol is particularly preferable. On the other hand, the low-melting polymer segment is preferably a polyester block copolymer such as poly (tetramethylene oxide) glycol, an ethylene oxide adduct of poly (propylene oxide) glycol, poly (ε-caprolactone), or polybutylene adipate. The content of the low-melting polymer segment is 10 to 90% by weight, preferably 15 to 75% by weight. Furthermore, additives such as a plasticizer, a stabilizer, a weathering agent, a crosslinking agent, an antibacterial agent, a filler, a flameproofing agent, a coloring agent, and an antistatic agent may be mixed.
本発明の熱可塑性樹脂はカレンダー法、溶融押し出し法、溶液コーティング法など公知の方法で織物に付与することができる。 The thermoplastic resin of the present invention can be applied to a woven fabric by a known method such as a calendar method, a melt extrusion method, or a solution coating method.
以下、実施例により詳しく説明するが、本発明はこれらに限定されるものではない。なお、実施例および比較例に示す性能値は次の方法で測定した。 Hereinafter, although an Example demonstrates in detail, this invention is not limited to these. The performance values shown in the examples and comparative examples were measured by the following method.
（１）形状保持性
製造したフレキシブルコンテナにポリエステルチップ（帝人ファイバー製）を１０００ｋｇ入れ、３０日間倉庫内で保管した後、フレキシブルコンテナ表面の変形程度を次の基準で評価し、△および○を合格とした。○：変形が殆ど無い、△：多少の変形が見られる、×：変形している。
(1) Shape retention After 1000kg of polyester chip (made by Teijin Fibers) is put into the manufactured flexible container and stored in the warehouse for 30 days, the degree of deformation of the flexible container surface is evaluated according to the following criteria, and △ and ○ are passed. It was. ○: Almost no deformation, Δ: Some deformation is observed, ×: Deformation
（２）屈曲疲労性
製造したフレキシブルコンテナにポリエステルチップ（帝人ファイバー製を１０００ｋｇ入れ、１日間倉庫内で保管した後、フレキシブルコンテナ内のポリエステルチップを排出し、折り畳む。この作業を１００回繰り返し、フレキシブルコンテナ表面の繊維の疲労度合いを次の基準で評価し、△および○を合格とした。○：初期の状態と殆ど変わらない、△：フレキシブルコンテナ表面に繊維毛羽が多少発現している、×：フレキシブルコンテナ表面に繊維毛羽が著しく発現している。
(2) Bending fatigue resistance Polyester chips (1000kg made by Teijin Fibers) are put into the manufactured flexible container, stored in the warehouse for one day, then the polyester chips in the flexible container are discharged and folded. The degree of fatigue of the fiber on the container surface was evaluated according to the following criteria, and Δ and ○ were accepted: ○: Almost the same as the initial state, Δ: Fiber fluff was somewhat expressed on the surface of the flexible container, ×: Fiber fluff is remarkably expressed on the surface of the flexible container.
［実施例１〜４］
経糸または緯糸に、固有粘度が０．７１、強度が８．３ｃＮ／ｄｔｅｘ、伸度が９．４％のポリエチレンナフタレート（ＰＥＮ）繊維（帝人ファイバー株式会社製テオネックス、１１００ｄｔｅｘ／２５０フィラメント）、あるいは、固有粘度が０．７、強度が８．１ｃＮ／ｄｔｅｘ、伸度が１３．５％のポリエチレンテレフタレート（ＰＥＴ）繊維（帝人ファイバー株式会社製テトロン、１１００ｄｔｅｘ／２５０フィラメント）を使用して平織物とし、２４０℃の温度で熱処理を施した。該織物に青色顔料と酸化防止剤を混合したエチレン・酢酸ビニル共重合体（住友化学株式会社製エバテートＣＶ２０９７）を２００ミクロンの厚みでカレンダー成型し、織物の両面に熱圧縮してフレキシブルコンテナ用シートとした。性能評価した結果を表１に示す。
[Examples 1 to 4]
Polyethylene naphthalate (PEN) fiber (Teonex manufactured by Teijin Fibers Limited, 1100 dtex / 250 filament) having an intrinsic viscosity of 0.71, strength of 8.3 cN / dtex, and elongation of 9.4%, or warp or weft A plain woven fabric using polyethylene terephthalate (PET) fiber (Tetoron, 1100 dtex / 250 filament manufactured by Teijin Fibers Limited) with an intrinsic viscosity of 0.7, strength of 8.1 cN / dtex, and elongation of 13.5% Heat treatment was performed at a temperature of 240 ° C. A sheet for flexible containers is formed by calendering an ethylene / vinyl acetate copolymer (Evatate CV2097, manufactured by Sumitomo Chemical Co., Ltd.) with a thickness of 200 microns into the woven fabric and heat-compressing both sides of the woven fabric. It was. The results of performance evaluation are shown in Table 1.
［比較例１〜４］
経糸または緯糸に、実施例１で用いたポリエチレンテレフタレート（ＰＥＴ）繊維（帝人テクノプロダクツ株式会社製テトロン）、あるいはアラミド繊維（帝人トワロン株式会社製トワロン、１１００ｄｔｅｘ／１０００フィラメント）、ナイロン繊維（旭化成せんい株式会社製、９４０ｄｔｅｘ／１４０フィラメント）を使用して平織物とし、２４０℃の温度で熱処理を施した。該織物に青色顔料と酸化防止剤を混合したエチレン・酢酸ビニル共重合体（住友化学株式会社製エバテートＣＶ２０９７）を２００ミクロンの厚みでカレンダー成型し、繊物の両面に熱圧縮してフレキシブルコンテナ用シートとし性能評価した結果を表２に示す。
[Comparative Examples 1-4]
Polyethylene terephthalate (PET) fibers (Tetron manufactured by Teijin Techno Products Co., Ltd.), aramid fibers (Twaron manufactured by Teijin Twaron Co., Ltd., 1100 dtex / 1000 filament), nylon fibers (Asahi Kasei Fibers) Company-made, 940 dtex / 140 filament) was used to make a plain woven fabric and heat treated at a temperature of 240 ° C. For the flexible container, an ethylene / vinyl acetate copolymer (Evatate CV2097 manufactured by Sumitomo Chemical Co., Ltd.) with a blue pigment and antioxidant mixed in the fabric is calendered to a thickness of 200 microns, and heat-compressed on both sides of the fabric. Table 2 shows the results of performance evaluation as a sheet.
本発明のフレキシブルコンテナ用シートによれば、これを用いて、形状保持性および屈曲疲労性に優れたフレキシブルコンテナを得ることができる。また、該フレキシブルコンテナは、上記特性を有し、折り畳みなどの繰り返し屈曲を受けたり、粒状内容物の出し入れ時や、運搬時の振動により、布帛を構成する繊維の一部分に過度の荷重が掛かり変形したり、また繰り返し使用により布帛が部分的に破れるといった問題が少ないという特徴を有している。 According to the flexible container sheet of the present invention, it is possible to obtain a flexible container excellent in shape retention and bending fatigue. In addition, the flexible container has the above-mentioned characteristics, and is subjected to repeated bending such as folding, or excessive deformation is applied to a part of the fibers constituting the fabric due to vibration during loading / unloading of granular contents or transportation. And the problem that the fabric is partially broken by repeated use is small.
Claims (4)