JP2008176036A - Radiation-sensitive resin composition and spacer for liquid crystal display element - Google Patents
Radiation-sensitive resin composition and spacer for liquid crystal display element Download PDFInfo
- Publication number
- JP2008176036A JP2008176036A JP2007009144A JP2007009144A JP2008176036A JP 2008176036 A JP2008176036 A JP 2008176036A JP 2007009144 A JP2007009144 A JP 2007009144A JP 2007009144 A JP2007009144 A JP 2007009144A JP 2008176036 A JP2008176036 A JP 2008176036A
- Authority
- JP
- Japan
- Prior art keywords
- group
- carbon atoms
- atoms
- monovalent
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、側鎖不飽和ブロック重合体を含有する感放射線性樹脂組成物、スペーサーとその形成方法および液晶表示素子に関する。 The present invention relates to a radiation-sensitive resin composition containing a side chain unsaturated block polymer, a spacer, a method for forming the spacer, and a liquid crystal display device.
液晶表示素子には、従来から、2枚の基板間の間隔(セルギャップ)を一定に保つため、所定の粒径を有するガラスビーズ、プラスチックビーズ等のスペーサーが使用されているが、これらのスペーサーは、ガラス基板などの透明基板上にランダムに散布されるため、画素形成領域にスペーサーが存在すると、スペーサーの写り込み現象を生じたり、入射光が散乱を受け、液晶表示素子としてのコントラストが低下するという問題があった。
そこで、このような問題を解決するために、スペーサーをフォトリソグラフィーにより形成する方法が採用されるようになってきた。この方法は、感放射線性樹脂組成物を基板上に塗布し、所定のマスクを介して例えば紫外線を露光したのち現像して、ドット状やストライプ状のスペーサーを形成するものであり、画素形成領域以外の所定の場所にのみスペーサーを形成することができるため、前述したような問題は基本的に解決される。
Conventionally, spacers such as glass beads and plastic beads having a predetermined particle diameter have been used for liquid crystal display elements in order to keep the distance (cell gap) between two substrates constant. Is randomly distributed on a transparent substrate such as a glass substrate, so if there is a spacer in the pixel formation area, the spacer will be reflected, or the incident light will be scattered and the contrast of the liquid crystal display element will be reduced. There was a problem to do.
Therefore, in order to solve such a problem, a method of forming a spacer by photolithography has been adopted. In this method, a radiation-sensitive resin composition is applied onto a substrate, exposed to, for example, ultraviolet rays through a predetermined mask, and then developed to form a dot-like or stripe-like spacer. Since the spacer can be formed only at a predetermined place other than the above, the above-described problem is basically solved.
また近年、液晶表示素子の大面積化や生産性の向上等の観点から、マザーガラス基板の大型化(例えば、1,500×1,800mm程度)が進んでいる。しかし、従来の基板サイズ(680×880mm程度)では、マスクサイズよりも基板サイズが小さいため、一括露光方式で対応が可能であったが、大型基板では、この基板サイズと同程度のマスクサイズを作製することはほぼ不可能であり、一括露光方式では対応が困難である。
そこで、大型基板に対応可能な露光方式として、ステップ露光方式が提唱されている。しかし、ステップ露光方式では、一枚の基板に数回露光され、各露光毎に、位置合せやステップ移動に時間を要するため、一括露光方式に比較して、スループットの低減が問題視されている。
In recent years, the mother glass substrate has been increased in size (for example, about 1,500 × 1,800 mm) from the viewpoint of increasing the area of the liquid crystal display element and improving productivity. However, since the conventional substrate size (about 680 × 880 mm) is smaller than the mask size, it was possible to cope with the batch exposure method. However, in the case of a large substrate, the mask size is about the same as this substrate size. It is almost impossible to manufacture, and it is difficult to cope with the batch exposure method.
Therefore, a step exposure method has been proposed as an exposure method that can be applied to a large substrate. However, in the step exposure method, a single substrate is exposed several times, and each exposure requires time for alignment and step movement. Therefore, a reduction in throughput is regarded as a problem compared to the batch exposure method. .
また、一括露光方式では、3,000J/m2程度の露光量が可能であるが、ステップ露光方式では各回の露光量をより低くすることが必要であり、スペーサーの形成に使用される従来の感放射線性樹脂組成物では、1,000J/m2以下の露光量で十分なスペーサー形状および膜厚を達成することが困難であった。
一方、液晶表示素子を作製する工程でのスループットを向上させる観点から、ガラス基板を張り合わせる前に、液晶材料をガラス基板の表面にたらしておく工程技術”ODF(One Drop Fill)法"が導入されており、この方法により、液晶表示素子の作製に要する時間を大幅に短縮することができる。例えば30インチの液晶表示素子の場合、液晶材料を充填するのに、従来の方法では約5日間を要するが、ODF法では2時間程度で十分であり、スループットの大幅な向上が可能となる。
Further, in the batch exposure method, an exposure amount of about 3,000 J / m 2 is possible, but in the step exposure method, it is necessary to lower the exposure amount at each time, which is a conventional method used for forming a spacer. In the radiation sensitive resin composition, it was difficult to achieve a sufficient spacer shape and film thickness with an exposure amount of 1,000 J / m 2 or less.
On the other hand, from the viewpoint of improving the throughput in the process of manufacturing a liquid crystal display element, there is a process technique “ODF (One Drop Fill) method” in which a liquid crystal material is applied to the surface of a glass substrate before the glass substrates are bonded together. The time required for manufacturing the liquid crystal display element can be greatly shortened by this method. For example, in the case of a 30-inch liquid crystal display element, it takes about 5 days to fill the liquid crystal material with the conventional method, but about 2 hours is sufficient with the ODF method, and the throughput can be significantly improved.
従来の張り合わせ方式では、TFTアレイとカラーフィルターを張り合わせる時、荷重をかけるため、その荷重によりスペーサーが均等に押され、スペーサーの高さ均一性が保たれていた。しかし、ODF法では、最初は基板の重さによる荷重と大気圧だけで張り合わせるため、従来法に比較して、初期の張り合わせ荷重が小さい。したがって、小さい荷重でスペーサーが押されても、均等に押されことで高さ均一性を発現することが重要とされている。そのためには、スペーサーの柔軟性が必要とされている。スペーサーの高さが不均一になるとセルギャップの均一性が保てなくなり、セル内に隙間が発生し表示ムラの原因となる。そこで、圧縮荷重による柔軟性と高い回復率を併せ持つスペーサー材が必要となる。
特許文献1では、感光性樹脂組成物中に、水酸基を有する共重合性樹脂に、(メタ)アクリロイルオキシアルキルイソシアネート化合物を反応させて得られた光重合性官能基を構成単位として有する共重合性樹脂を用いることで高感度化、高回復率化等のスペーサーとしての性能向上を達成できることが開示されている。しかし、柔軟性に関しては考慮されていない。
以上のように、従来の感放射線性樹脂組成物では、光重合性官能基を構成単位として有する共重合性樹脂を用いることで、高感度化と高回復率化は可能であるが、高感度化と高回復率化に加え、さらに柔軟性を併せ持つスペーサーを与える材料とはいえない。
In Patent Document 1, a photopolymerizable functional group obtained by reacting a (meth) acryloyloxyalkyl isocyanate compound with a copolymer resin having a hydroxyl group in a photosensitive resin composition as a constituent unit. It is disclosed that the use of a resin can achieve improved performance as a spacer, such as higher sensitivity and higher recovery rate. However, no consideration is given to flexibility.
As described above, the conventional radiation-sensitive resin composition can achieve high sensitivity and high recovery rate by using a copolymerizable resin having a photopolymerizable functional group as a structural unit. In addition to increasing the recovery rate and increasing the recovery rate, it cannot be said that it is a material that gives a spacer having more flexibility.
そこで、本発明の課題は、高感度かつ高解像度で、1,000J/m2以下の露光量でも十分なスペーサー形状が得られ、柔軟性、弾性回復性、ラビング耐性、透明基板との密着性、耐熱性等に優れた液晶表示素子用スペーサーを形成することができる感放射線性樹脂組成物、当該感放射線性樹脂組成物の樹脂成分から形成されたスペーサーとその形成法ならびに当該スペーサーを具備する液晶表示素子に関する。 Therefore, the object of the present invention is to obtain a sufficient spacer shape with high sensitivity and high resolution even at an exposure amount of 1,000 J / m 2 or less, flexibility, elastic recovery, rubbing resistance, and adhesion to a transparent substrate. A radiation-sensitive resin composition capable of forming a spacer for a liquid crystal display device having excellent heat resistance, a spacer formed from a resin component of the radiation-sensitive resin composition, a method for forming the spacer, and the spacer The present invention relates to a liquid crystal display element.
本発明によると、前記課題は、第一に、
[A]リビングラジカル重合で得られた、光重合性不飽和基を有する共重合体、[B]重合性不飽和化合物、および[C]感放射線性重合開始剤を含有することを特徴とする感放射線性樹脂組成物によって達成される。
According to the present invention, the problem is firstly
[A] It contains a copolymer having a photopolymerizable unsaturated group obtained by living radical polymerization, [B] a polymerizable unsaturated compound, and [C] a radiation-sensitive polymerization initiator. This is achieved by the radiation sensitive resin composition.
本発明によると、前記課題は、第二に、
[A]上記光重合性不飽和基を有する共重合体が、2つ以上のブロックセグメントを有し、そのうち少なくとも1つのブロックセグメントに、光重合性不飽和基を含有していることを特徴とする本発明の感放射線性樹脂組成物によって達成される。
According to the present invention, the problem is secondly,
[A] The copolymer having a photopolymerizable unsaturated group has two or more block segments, of which at least one block segment contains a photopolymerizable unsaturated group. This is achieved by the radiation-sensitive resin composition of the present invention.
本発明によると、前記課題は、第三に、
[A]光重合性不飽和基を有する共重合体が(a1)アルカリ可溶性重合性不飽和化合物および/または不飽和カルボン酸無水物、あるいはそれらカルボン酸の保護化物に由来する重合単位を少なくとも1つ含有していることを特徴とする本発明の感放射線性樹脂組成物によって達成される。
According to the present invention, the problem is thirdly,
[A] The copolymer having a photopolymerizable unsaturated group is at least one polymer unit derived from (a1) an alkali-soluble polymerizable unsaturated compound and / or an unsaturated carboxylic acid anhydride, or a protected product thereof. Is achieved by the radiation-sensitive resin composition of the present invention.
本発明の上記目的および利点は、第四に、
下記式(1)、(2)あるいは(3)のそれぞれで表されるチオカルボニルチオ化合物を分子量制御剤として用いる重合を経て製造されたものである上記感放射線性樹脂組成物によって好ましく達成される。
The above objects and advantages of the present invention are fourthly.
It is preferably achieved by the radiation-sensitive resin composition produced by polymerization using a thiocarbonylthio compound represented by the following formula (1), (2) or (3) as a molecular weight control agent. .
〔式(1)において、Z1は水素原子、塩素原子、カルボキシル基、シアノ基、炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、−OX、−SX、−N(X)2、−OC(=O)X、−C(=O)OX、−C(=O)N(X)2、−P(=O)(OX)2、−P(=O)(X)2、または重合体鎖を有する1価の基を示し、各Xは相互に独立に炭素数1〜18のアルキル基、炭素数2〜18のアルケニル基、炭素数6〜18の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜18の1価の複素環式基を示し、上記炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、合計原子数3〜20の1価の複素環式基およびXはそれぞれ置換されていてもよく、pは1以上の整数であり、R1は、p=1のとき、炭素数1〜20のアルキル基、炭素数3〜20の1価の脂環族炭化水素基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、−OX、−SX、−N(X)2または重合体鎖を有する1価の基を示し、各Xの定義は上記に同じであり、p≧2のとき、炭素数1〜20のアルカンに由来するp価の基、炭素数6〜20の芳香族炭化水素に由来するp価の基、炭素原子と異項原子との合計原子数3〜20の複素環式化合物に由来するp価の基または重合体鎖を有するp価の基を示し、そして上記炭素数1〜20のアルキル基、炭素数3〜20の1価の脂環族炭化水素基、炭素数6〜20の1価の芳香族炭化水素基、合計原子数3〜20の1価の複素環式基、X、炭素数1〜20のアルカンに由来するp価の基、炭素数6〜20の芳香族炭化水素に由来するp価の基および合計原子数3〜20の複素環式化合物に由来するp価の基はそれぞれ置換されていてもよい。〕 [In Formula (1), Z 1 is different from a hydrogen atom, a chlorine atom, a carboxyl group, a cyano group, an alkyl group having 1 to 20 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, or a carbon atom. Monovalent heterocyclic group having 3 to 20 atoms in total with the term atom, -OX, -SX, -N (X) 2 , -OC (= O) X, -C (= O) OX, -C (═O) N (X) 2 , —P (═O) (OX) 2 , —P (═O) (X) 2 , or a monovalent group having a polymer chain, wherein each X is mutually Independently an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, or a total of 3 to 18 atoms of carbon atoms and hetero atoms 1 represents a monovalent heterocyclic group, the above alkyl group having 1 to 20 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, and a monovalent heterocyclic group having 3 to 20 atoms in total. And X may be each substituted, p is an integer of 1 or more, R 1 is when p = 1, an alkyl group having 1 to 20 carbon atoms, a monovalent alicyclic of 3 to 20 carbon atoms Group hydrocarbon group, monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, monovalent heterocyclic group having 3 to 20 total atoms of carbon atoms and hetero atoms, -OX, -SX,- Each represents a monovalent group having N (X) 2 or a polymer chain, and the definition of each X is the same as above, and when p ≧ 2, a p-valent group derived from an alkane having 1 to 20 carbon atoms, It has a p-valent group derived from an aromatic hydrocarbon having 6 to 20 carbon atoms, a p-valent group derived from a heterocyclic compound having 3 to 20 total atoms of carbon atoms and hetero atoms, or a polymer chain. a p-valent group, and the above-mentioned alkyl group having 1 to 20 carbon atoms, a monovalent alicyclic hydrocarbon group having 3 to 20 carbon atoms, 1 having 6 to 20 carbon atoms, An aromatic hydrocarbon group, a monovalent heterocyclic group having 3 to 20 atoms in total, X, a p-valent group derived from an alkane having 1 to 20 carbon atoms, and an aromatic hydrocarbon having 6 to 20 carbon atoms The derived p-valent group and the p-valent group derived from the heterocyclic compound having a total of 3 to 20 atoms may each be substituted. ]
〔式(2)において、Z2は炭素数1〜20のアルカンに由来するm価の基、炭素数6〜20の芳香族炭化水素に由来するm価の基、炭素原子と異項原子との合計原子数3〜20の複素環式化合物に由来するm価の基または重合体鎖を有するm価の基を示し、上記炭素数1〜20のアルカンに由来するm価の基、炭素数6〜20の芳香族炭化水素に由来するm価の基および合計原子数3〜20の複素環式化合物に由来するm価の基はそれぞれ置換されていてもよく、R2は炭素数1〜20のアルキル基、炭素数3〜20の1価の脂環族炭化水素基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、−OX、−SX、−N(X)2または重合体鎖を有する1価の基を示し、各Xは相互に独立に炭素数1〜18のアルキル基、炭素数2〜18のアルケニル基、炭素数6〜18の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜18の1価の複素環式基を示し、上記炭素数1〜20のアルキル基、炭素数3〜20の1価の脂環族炭化水素基、炭素数6〜20の1価の芳香族炭化水素基、合計原子数3〜20の1価の複素環式基およびXはそれぞれ置換されていてもよく、mは1以上の整数である。〕 [In the formula (2), Z 2 represents an m-valent group derived from an alkane having 1 to 20 carbon atoms, an m-valent group derived from an aromatic hydrocarbon having 6 to 20 carbon atoms, a carbon atom and a hetero atom. M-valent group derived from a heterocyclic compound having 3 to 20 atoms in total or m-valent group having a polymer chain, m-valent group derived from an alkane having 1 to 20 carbon atoms, carbon number The m-valent group derived from an aromatic hydrocarbon having 6 to 20 and the m-valent group derived from a heterocyclic compound having 3 to 20 atoms in total may be substituted, and R 2 may have 1 to 1 carbon atoms. 20 alkyl groups, monovalent alicyclic hydrocarbon groups having 3 to 20 carbon atoms, monovalent aromatic hydrocarbon groups having 6 to 20 carbon atoms, and 3 to 20 total atoms of carbon atoms and hetero atoms A monovalent heterocyclic group, —OX, —SX, —N (X) 2 or a monovalent group having a polymer chain, wherein each X is a phase Independently of each other, an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, or a total number of 3 atoms of carbon atoms and hetero atoms 18 represents a monovalent heterocyclic group, the above alkyl group having 1 to 20 carbon atoms, a monovalent alicyclic hydrocarbon group having 3 to 20 carbon atoms, and a monovalent aromatic carbon group having 6 to 20 carbon atoms. A hydrogen group, a monovalent heterocyclic group having 3 to 20 atoms in total, and X may each be substituted, and m is an integer of 1 or more. ]
〔式(3)において、Z3およびZ4は相互に独立に水素原子、塩素原子、カルボキシル基、シアノ基、炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、
−OX1、−SX1、−OC(=O)X1、−N(X1)(X2)、−C(=O)OX1、
−C(=O)N(X1)(X2)、−P(=O)(OX1)2、−P(=O)(X1)2または重合体鎖を有する1価の基を示し、X1およびX2は相互に独立に炭素数1〜18のアルキル基、炭素数2〜18のアルケニル基、炭素数6〜18の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜18の1価の複素環式基を示し、前記炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、X1およびX2はそれぞれ置換されていてもよい。〕
[In Formula (3), Z 3 and Z 4 are each independently a hydrogen atom, a chlorine atom, a carboxyl group, a cyano group, an alkyl group having 1 to 20 carbon atoms, or a monovalent aromatic carbon atom having 6 to 20 carbon atoms. A hydrogen group, a monovalent heterocyclic group having 3 to 20 total atoms of carbon atoms and hetero atoms,
-OX 1, -SX 1, -OC ( = O) X 1, -N (X 1) (X 2), - C (= O) OX 1,
-C (= O) N (X 1) (X 2), - a P (= O) (OX 1 ) 2, -P (= O) (X 1) 1 monovalent group having 2 or polymer chain X 1 and X 2 are independently of each other an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, or a carbon atom. A monovalent heterocyclic group having 3 to 18 atoms in total with the atom, the alkyl group having 1 to 20 carbon atoms, the monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, and a carbon atom and a different group The monovalent heterocyclic group having 3 to 20 atoms in total, X 1 and X 2 may be substituted. ]
本発明によると、前記課題は、第五に、
前記感放射線性樹脂組成物からなる、液晶表示素子用スペーサーの形成に用いられる感放射線性樹脂組成物(以下、「液晶表示素子用スペーサー用感放射線性樹脂組成物」という。)によって達成される。
According to the present invention, fifthly, the problem is as follows:
This is achieved by a radiation-sensitive resin composition (hereinafter referred to as “a radiation-sensitive resin composition for spacers for liquid crystal display elements”) used for forming a spacer for liquid crystal display elements, comprising the radiation-sensitive resin composition. .
本発明によると、前記課題は、第六に、
液晶表示素子用スペーサー用感放射線性樹脂組成物から形成されてなる液晶表示素子用スペーサーによって達成される。
According to the present invention, sixthly, the problem is as follows:
This is achieved by a liquid crystal display element spacer formed from a radiation-sensitive resin composition for a liquid crystal display element spacer.
本発明によると、前記課題は、第七に、
少なくとも以下の工程を以下に記載の順序で含むことを特徴とする液晶表示素子用スペーサーの形成方法によって達成される。
(イ)液晶表示素子用スペーサー用感放射線性樹脂組成物の塗膜を基板上に形成する工程、
(ロ)該塗膜の少なくとも一部に露光する工程、
(ハ)露光後の該塗膜を現像する工程、および
(ニ)現像後の該塗膜を加熱する工程。
According to the present invention, seventhly, the problem is as follows:
This is achieved by a method for forming a spacer for a liquid crystal display element, comprising at least the following steps in the order described below.
(A) forming a coating film of a radiation sensitive resin composition for spacers for liquid crystal display elements on a substrate;
(B) a step of exposing at least a part of the coating film;
(C) a step of developing the coated film after exposure, and (d) a step of heating the coated film after development.
本発明によると、前記課題は、第八に、
前記液晶表示素子用スペーサーを具備する液晶表示素子によって達成される。
According to the present invention, eighthly, the problem is as follows:
This is achieved by a liquid crystal display element comprising the liquid crystal display element spacer.
本発明の感放射線性樹脂組成物は高感度かつ高解像度で1,000J/m2以下の露光量でも十分なスペーサー形状を形成することができ、また柔軟性、弾性回復性、ラビング耐性、透明基板との密着性、耐熱性等に優れた液晶表示素子用スペーサーを形成することができる。 The radiation-sensitive resin composition of the present invention can form a sufficient spacer shape with high sensitivity and high resolution even at an exposure amount of 1,000 J / m 2 or less, and is flexible, elastic recoverable, rubbing resistant, transparent A spacer for a liquid crystal display element having excellent adhesion to a substrate, heat resistance and the like can be formed.
感放射線性樹脂組成物
以下、本発明の感放射線性樹脂組成物の各成分について詳述する。
Radiation sensitive resin composition Hereinafter, each component of the radiation sensitive resin composition of this invention is explained in full detail.
(A)ブロック共重合体
本発明の感放射線性樹脂組成物における(A)光重合性不飽和基を有する共重合体とは、化学構造が異なる重合性不飽和化合物で構成されたセグメントを少なくとも2つ以上含み、かつ光重合性不飽和基を含むブロックセグメントを有する共重合体を意味するものとする。ブロックセグメントは重合性不飽和化合物の単一種重合体または複数種の重合体から成ることができる。光重合性不飽和基を有する共重合体はその重合方法や組成に指定は無いが、例えば、カルボキシル基、酸無水物、水酸基等の官能基を有するブロック共重合体に、少なくとも1個のエチレン性不飽和基と、エポキシ基、イソシアネート基等の1個の官能基を有する化合物を付加反応させて得られる。この時、ブロックセグメントはランダム共重合体であってもよい。(A)光重合性不飽和基を有する共重合体はそれぞれがランダム共重合体からなる2つのブロックセグメントを含んでいてもよい。一次重合で生成されるブロックセグメントと二次重合で一次ブロックセグメントに付与される二次ブロックセグメントの2つ以上のセグメントを有し、そのうち少なくとも1つのセグメントに、光重合性不飽和基を含有していることが好ましい。例えば、(A)光重合性不飽和基を有する共重合体は、化合物(a1)ラジカル重合性を有する不飽和カルボン酸および/または不飽和カルボン酸無水物、あるいはそれらカルボン酸の保護化物、および化合物(a3)(a1)(a2)以外のラジカル重合性化合物を含有する重合性混合物を溶媒中、重合開始剤の存在下でリビングラジカル重合し、更に化合物(a2)水酸基等の官能基を有する化合物または、化合物(a1)、(a2)、(a3)を含有する重合性混合物を追添して重合を継続してえられる共重合体(以下、「共重合体[α]」という。)に、(a4)少なくとも1個のエチレン性不飽和基と、エポキシ基、イソシアネート基等の1個の官能基を有する化合物を付加反応することによって製造することができる。また、必要に応じて、さらに重合性混合物を追添して、ブロックセグメントを追加することができる。このようにして得られた(A)光重合性不飽和基を有する共重合体が有するアルカリ可溶性部位は化合物(a1)に由来する。
次に、(A)共重合体を製造するリビングラジカル重合について説明する。
(A) Block copolymer (A) The copolymer having a photopolymerizable unsaturated group in the radiation-sensitive resin composition of the present invention includes at least a segment composed of a polymerizable unsaturated compound having a different chemical structure. A copolymer having a block segment containing two or more and containing a photopolymerizable unsaturated group is meant. The block segment can consist of a single polymer or a plurality of polymers of polymerizable unsaturated compounds. The copolymer having a photopolymerizable unsaturated group is not specified in its polymerization method or composition. For example, at least one ethylene is added to a block copolymer having a functional group such as a carboxyl group, an acid anhydride, or a hydroxyl group. It is obtained by addition reaction of a compound having a functional unsaturated group and one functional group such as an epoxy group or an isocyanate group. At this time, the block segment may be a random copolymer. (A) The copolymer having a photopolymerizable unsaturated group may contain two block segments each made of a random copolymer. It has two or more segments of a block segment generated by primary polymerization and a secondary block segment given to the primary block segment by secondary polymerization, and at least one of them contains a photopolymerizable unsaturated group. It is preferable. For example, (A) a copolymer having a photopolymerizable unsaturated group is compound (a1) an unsaturated carboxylic acid and / or unsaturated carboxylic acid anhydride having radical polymerizability, or a protected product of these carboxylic acids, and A polymerizable mixture containing a radically polymerizable compound other than the compounds (a3), (a1), and (a2) is subjected to living radical polymerization in the presence of a polymerization initiator in a solvent, and the compound (a2) further has a functional group such as a hydroxyl group. A compound or a copolymer obtained by adding a polymerizable mixture containing the compounds (a1), (a2) and (a3) and continuing the polymerization (hereinafter referred to as “copolymer [α]”). (A4) It can be produced by addition reaction of a compound having at least one ethylenically unsaturated group and one functional group such as an epoxy group or an isocyanate group. If necessary, a block segment can be added by further adding a polymerizable mixture. The alkali-soluble part of the copolymer (A) having a photopolymerizable unsaturated group thus obtained is derived from the compound (a1).
Next, (A) Living radical polymerization for producing a copolymer will be described.
上記重合性不飽和化合物を、好ましくは他の共重合可能な不飽和化合物と共に、溶媒中、リビングラジカルを生成するラジカル重合開始剤系の存在下でリビングラジカル重合することにより第一ブロックセグメントを作製し、さらには上記重合性不飽和化合物を必要に応じて複数回追添することにより(A)共重合体を製造することができる。
リビングラジカル重合に際しては、重合性不飽和化合物としてカルボキシル基などの活性ラジカルを失活させるおそれがある官能基を有する化合物を用いる場合、成長末端が失活しないようにするため、必要に応じて、重合性不飽和化合物中の該官能基を、例えばエステル化などにより保護して重合したのち、脱保護することにより、(A)共重合体を得ることもできる。
A first block segment is produced by living radical polymerization of the above polymerizable unsaturated compound, preferably together with other copolymerizable unsaturated compounds, in a solvent in the presence of a radical polymerization initiator system that generates a living radical. Furthermore, the copolymer (A) can be produced by adding the polymerizable unsaturated compound a plurality of times as necessary.
In living radical polymerization, when using a compound having a functional group that may deactivate an active radical such as a carboxyl group as a polymerizable unsaturated compound, in order to prevent the growth terminal from being deactivated, The functional group in the polymerizable unsaturated compound can be protected and polymerized by, for example, esterification, and then deprotected to obtain the copolymer (A).
重合性不飽和化合物をリビングラジカル重合するラジカル重合開始剤系については種々提案されており、例えば、Georgesらにより提案されているTEMPO系(例えば、非特許文献1参照)、Matyjaszewskiらにより提案されている臭化銅と臭素含有エステル化合物の組み合わせからなる系(例えば、非特許文献2参照。)、Hamasakiらにより提案されている四塩化炭素とルテニウム(II)錯体の組み合わせからなる系(例えば、非特許文献3参照)や、特許文献2、特許文献3および特許文献4に開示されているような、0.1より大きな連鎖移動定数をもつチオカルボニル化合物とラジカル開始剤の組み合わせからなる系などを挙げることができる。 Various radical polymerization initiator systems for living radical polymerization of polymerizable unsaturated compounds have been proposed. For example, the TEMPO system proposed by Georges et al. (See, for example, Non-Patent Document 1), and proposed by Matyjazewski et al. A system composed of a combination of copper bromide and a bromine-containing ester compound (for example, see Non-patent Document 2), a system composed of a combination of carbon tetrachloride and a ruthenium (II) complex proposed by Hamasaki et al. And a system comprising a combination of a thiocarbonyl compound having a chain transfer constant greater than 0.1 and a radical initiator, as disclosed in Patent Document 3, Patent Document 2, Patent Document 3, and Patent Document 4, etc. Can be mentioned.
リビングラジカル重合に使用される好適なラジカル重合開始剤系としては、使用される重合性不飽和化合物の種類に応じて、成長末端である活性ラジカルが失活しない系が適宜選択されるが、重合効率やメタルフリー系などを考慮すると、分子量制御剤であるチオカルボニルチオ化合物とラジカル開始剤との組み合わせが好ましい。
上記チオカルボニルチオ化合物とラジカル開始剤との組み合わせに関しては、特許文献2、特許文献3および特許文献4のほか、特許文献5〜9に詳しく記載されている。
As a suitable radical polymerization initiator system used for living radical polymerization, a system in which the active radical at the growth end is not deactivated is appropriately selected depending on the type of the polymerizable unsaturated compound used. In consideration of efficiency and metal-free system, a combination of a thiocarbonylthio compound that is a molecular weight control agent and a radical initiator is preferable.
The combination of the thiocarbonylthio compound and the radical initiator is described in detail in Patent Documents 5 to 9 in addition to Patent Document 2, Patent Document 3 and Patent Document 4.
特許文献2〜特許文献5に記載されているように、チオカルボニルチオ化合物およびラジカル開始剤の存在下に不飽和化合物をリビングラジカル重合することにより、分子量分布の狭いランダム共重合体もしくはブロック共重合体を得ることができる。また、得られるランダム共重合体およびブロック共重合体には官能基を導入することができるため、該共重合体を水性ゲル(特許文献6参照)、フォトレジスト(特許文献7参照)、界面活性剤(特許文献8参照)などの用途にも使用することができることが明らかにされている。
本発明における好ましい上記チオカルボニルチオ化合物としては、例えば、上記式(1)、上記式(2)、または上記式(3)で表される化合物などを挙げることができる。
As described in Patent Documents 2 to 5, a random copolymer or block copolymer having a narrow molecular weight distribution is obtained by living radical polymerization of an unsaturated compound in the presence of a thiocarbonylthio compound and a radical initiator. Coalescence can be obtained. Moreover, since a functional group can be introduced into the obtained random copolymer and block copolymer, the copolymer is converted into an aqueous gel (see Patent Document 6), a photoresist (see Patent Document 7), and a surface activity. It has been clarified that it can also be used for applications such as an agent (see Patent Document 8).
Preferred examples of the thiocarbonylthio compound in the present invention include compounds represented by the above formula (1), the above formula (2), or the above formula (3).
上記式(1)において、Z1の炭素数1〜20のアルキル基としては、例えば、メチル基、エチル基、n−プロピル基、i−プロピル基、n−ブチル基、i−ブチル基、sec−ブチル基、t−ブチル基、n−ペンチル基、1,1−ジメチルプロピル基、ネオペンチル基、n−ヘキシル基、n−ヘプチル基、n−オクチル基、1,1−ジメチル−3,3−ジメチルブチル基、n−ノニル基、n−デシル基、n−ドデシル基、n−テトラデシル基、n−ヘキサデシル基、n−オクタデシル基、n−エイコシル基などを挙げることができる。
また、Z1の炭素数6〜20の1価の芳香族炭化水素基としては、例えば、フェニル基、1−ナフチル基、2−ナフチル基、1−アントラセニル基、9−アントラセニル基、ベンジル基、α−メチルベンジル基、α,α−ジメチルベンジル基、フェネチル基などを挙げることができる。
In the above formula (1), examples of the alkyl group having 1 to 20 carbon atoms of Z 1 include a methyl group, ethyl group, n-propyl group, i-propyl group, n-butyl group, i-butyl group, sec -Butyl group, t-butyl group, n-pentyl group, 1,1-dimethylpropyl group, neopentyl group, n-hexyl group, n-heptyl group, n-octyl group, 1,1-dimethyl-3,3- A dimethylbutyl group, n-nonyl group, n-decyl group, n-dodecyl group, n-tetradecyl group, n-hexadecyl group, n-octadecyl group, n-eicosyl group, etc. can be mentioned.
Examples of the monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms of Z 1 include a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 9-anthracenyl group, a benzyl group, An α-methylbenzyl group, an α, α-dimethylbenzyl group, a phenethyl group, and the like can be given.
また、Z1の炭素原子と異項原子との合計原子数3〜20の1価の複素環式基としては、例えば、オキシラニル基、アジリジニル基、2−フラニル基、3−フラニル基、2−テトラヒドロフラニル基、3−テトラヒドロフラニル基、1−ピロール基、2−ピロール基、3−ピロール基、1−ピロリジニル基、2−ピロリジニル基、3−ピロリジニル基、1−ピラゾール基、2−ピラゾール基、3−ピラゾール基、2−テトラヒドロピラニル基、3−テトラヒドロピラニル基、4−テトラヒドロピラニル基、2−チアニル基、3−チアニル基、4−チアニル基、2−ピリジニル基、3−ピリジニル基、4−ピリジニル基、2−ピペリジニル基、3−ピペリジニル基、4−ピペリジニル基、2−モルホリニル基、3−モルホリニル基などを挙げることができる。 Examples of the monovalent heterocyclic group having 3 to 20 total atoms of carbon atoms and hetero atoms of Z 1 include oxiranyl group, aziridinyl group, 2-furanyl group, 3-furanyl group, 2- Tetrahydrofuranyl group, 3-tetrahydrofuranyl group, 1-pyrrole group, 2-pyrrole group, 3-pyrrole group, 1-pyrrolidinyl group, 2-pyrrolidinyl group, 3-pyrrolidinyl group, 1-pyrazole group, 2-pyrazole group, 3-pyrazole group, 2-tetrahydropyranyl group, 3-tetrahydropyranyl group, 4-tetrahydropyranyl group, 2-thianyl group, 3-thianyl group, 4-thianyl group, 2-pyridinyl group, 3-pyridinyl group 4-pyridinyl group, 2-piperidinyl group, 3-piperidinyl group, 4-piperidinyl group, 2-morpholinyl group, 3-morpholinyl group, etc. be able to.
また、Z1の−OX、−SX、−N(X)2、−OC(=O)X、−C(=O)OX、−C(=O)N(X)2、−P(=O)(OX)2および−P(=O)(X)2におけるXの炭素数1〜18のアルキル基、炭素数6〜18の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜18の1価の複素環式基としては、例えば、Z1について例示した炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜20の1価の複素環式基のうち、炭素数ないし合計原子数が18以下の基を挙げることができる。
また、同Xの炭素数2〜18のアルケニル基としては、例えば、ビニル基、1−プロペニル基、2−プロペニル基、1−ブテニル基、2−ブテニル基、3−ブテニル基、1−ペンテニル基、2−ペンテニル基、3−ペンテニル基、4−ペンテニル基、1−ヘキセニル基、2−ヘキセニル基、3−ヘキセニル基、4−ヘキセニル基、5−ヘキセニル基などを挙げることができる。
Further, the Z 1 -OX, -SX, -N ( X) 2, -OC (= O) X, -C (= O) OX, -C (= O) N (X) 2, -P (= O) (OX) 2 and —P (═O) (X) 2 in which X is an alkyl group having 1 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, or a carbon atom and a hetero atom. As the monovalent heterocyclic group having 3 to 18 atoms in total, for example, an alkyl group having 1 to 20 carbon atoms exemplified for Z 1 , a monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, or Among the monovalent heterocyclic groups having 3 to 20 total atoms of carbon atoms and hetero atoms, there can be mentioned groups having 18 to 18 carbon atoms in total.
Examples of the alkenyl group having 2 to 18 carbon atoms of X include, for example, a vinyl group, 1-propenyl group, 2-propenyl group, 1-butenyl group, 2-butenyl group, 3-butenyl group, and 1-pentenyl group. 2-pentenyl group, 3-pentenyl group, 4-pentenyl group, 1-hexenyl group, 2-hexenyl group, 3-hexenyl group, 4-hexenyl group, 5-hexenyl group and the like.
上記炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基およびXに対する置換基としては、例えば、水酸基、カルボキシル基、カルボン酸塩基、スルホン酸基、スルホン酸塩基、イソシアナート基、シアノ基、ビニル基、エポキシ基、シリル基、ハロゲン原子のほか、Z1について例示した−OX、−SX、−N(X)2、−OC(=O)X、−C(=O)OX、−C(=O)N(X)2、−P(=O)(OX)2あるいは−P(=O)(X)2;Xについて例示した炭素数1〜18のアルキル基、炭素数2〜18のアルケニル基、炭素数6〜18の1価の芳香族炭化水素基あるいは炭素原子と異項原子との合計原子数3〜18の1価の複素環式基と同様の基の中から適宜選択することができる。これらの置換基は置換誘導体中に1個以上あるいは1種以上存在することができる。ただし、置換誘導体中の合計炭素数ないし合計原子数は20を超えないことが好ましい。 For the above alkyl group having 1 to 20 carbon atoms, monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, monovalent heterocyclic group having 3 to 20 total atoms of carbon atoms and hetero atoms, and X Examples of the substituent include, for example, hydroxyl group, carboxyl group, carboxylate group, sulfonate group, sulfonate group, isocyanate group, cyano group, vinyl group, epoxy group, silyl group, halogen atom, and Z 1 . -OX, -SX, -N (X) 2 , -OC (= O) X, -C (= O) OX, -C (= O) N (X) 2 , -P (= O) (OX) 2 or -P (= O) (X) 2 ; an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms exemplified for X, or Same as monovalent heterocyclic group having 3 to 18 total atoms of carbon atom and hetero atom It can be appropriately selected from group. One or more of these substituents may be present in the substituted derivative. However, it is preferable that the total number of carbon atoms or the total number of atoms in the substituted derivative does not exceed 20.
また、Z1の重合体鎖を有する1価の基としては、例えば、エチレン、プロピレンなどのα−オレフィン類;スチレン、α−メチルスチレンなどの芳香族ビニル化合物;ふっ化ビニル、塩化ビニル、塩化ビニリデンなどのハロゲン化ビニル類;ビニルアルコール、アリルアルコールなどの不飽和アルコール類;酢酸ビニル、酢酸アリルなどの不飽和アルコールのエステル類;(メタ)アクリル酸、p−ビニル安息香酸などの不飽和カルボン酸類;(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸n−プロピル、(メタ)アクリル酸i−プロピル、(メタ)アクリル酸n−ブチル、(メタ)アクリル酸t−ブチル、(メタ)アクリル酸n−ヘキシル、(メタ)アクリル酸シクロヘキシルなどの(メタ)アクリル酸エステル類;(メタ)アクルアミド、N,N−ジメチル(メタ)アクルアミドなどの(メタ)アクルアミド類;(メタ)アクリロニトリル、シアン化ビニリデンなどの不飽和ニトリル類;ブタジエン、イソプレンなどの共役ジエン類などの不飽和化合物の1種以上から形成される付加重合系重合体鎖を有する1価の基のほか、末端がエーテル化されていてもよいポリオキシエチレン、末端がエーテル化されていてもよいポリオキシプロピレンなどのポリエーテルや、ポリエステル、ポリアミド、ポリイミドなどの重付加系重合体鎖や重縮合系重合体鎖などを有する1価の基を挙げることができる。これらの重合体鎖を有する1価の基においては、該重合体鎖が直接式(1)中のチオカルボニル基の炭素原子に結合しても、例えば−CH2−COO−、−C(CH3)(CN)CH2CH2−COO−などの連結手を介して式(1)中のチオカルボニル基の炭素原子に結合してもよい。 Examples of the monovalent group having a polymer chain of Z 1 include α-olefins such as ethylene and propylene; aromatic vinyl compounds such as styrene and α-methylstyrene; vinyl fluoride, vinyl chloride, and chloride. Vinyl halides such as vinylidene; unsaturated alcohols such as vinyl alcohol and allyl alcohol; esters of unsaturated alcohols such as vinyl acetate and allyl acetate; unsaturated carboxylic acids such as (meth) acrylic acid and p-vinylbenzoic acid Acids; methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, i-propyl (meth) acrylate, n-butyl (meth) acrylate, t- (meth) acrylic acid (Meth) acrylic acid esters such as butyl, n-hexyl (meth) acrylate, and cyclohexyl (meth) acrylate (Meth) acramide, (meth) acramides such as N, N-dimethyl (meth) acramide; unsaturated nitriles such as (meth) acrylonitrile and vinylidene cyanide; conjugated dienes such as butadiene and isoprene In addition to a monovalent group having an addition polymer chain formed from one or more of unsaturated compounds, polyoxyethylene whose terminal may be etherified, polyoxyethylene whose terminal may be etherified A monovalent group having a polyether such as propylene, a polyaddition polymer chain such as polyester, polyamide or polyimide, a polycondensation polymer chain, or the like can be given. In the monovalent group having these polymer chains, even when the polymer chain is directly bonded to the carbon atom of the thiocarbonyl group in the formula (1), for example, —CH 2 —COO—, —C (CH 3) (CN) CH 2 CH 2 -COO- may be bonded to the carbon atom of the thiocarbonyl group in the formula (1) via a connecting hands like.
式(1)において、複数存在するZ1は相互に同一でも異なってもよい。
式(1)において、R1は、p=1のとき、炭素数1〜20のアルキル基、炭素数3〜20の1価の脂環族炭化水素基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、−OX、−SX、−N(X)2または重合体鎖を有する1価の基を示す。
In the formula (1), a plurality of Z 1 may be the same as or different from each other.
In Formula (1), when p = 1, R 1 is an alkyl group having 1 to 20 carbon atoms, a monovalent alicyclic hydrocarbon group having 3 to 20 carbon atoms, or a monovalent group having 6 to 20 carbon atoms. A monovalent heterocyclic group, a monovalent heterocyclic group having 3 to 20 total atoms of carbon atoms and hetero atoms, -OX, -SX, -N (X) 2 or a monovalent polymer chain Indicates a group.
上記炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、合計原子数3〜20の1価の複素環式基、−OX、−SX、−N(X)2または重合体鎖を有する1価の基やそれらの置換誘導体としては、例えば、上記Z1のそれぞれ対応する基について例示した基と同様のものを挙げることができる。R1(ただし、p=1)の重合体鎖を有する1価の基においては、該重合体鎖が直接式(1)中の硫黄原子に結合しても、例えば−CH2−COO−、−C(CH3)(CN)CH2CH2−COO−などの連結手を介して式(1)中の硫黄原子に結合してもよい。 The alkyl group having 1 to 20 carbon atoms, the monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, the monovalent heterocyclic group having 3 to 20 atoms in total, -OX, -SX, -N (X As the monovalent group having 2 or a polymer chain or a substituted derivative thereof, for example, the same groups as those exemplified for the respective corresponding groups of Z 1 can be mentioned. In a monovalent group having a polymer chain of R 1 (p = 1), even when the polymer chain is directly bonded to the sulfur atom in the formula (1), for example, —CH 2 —COO—, -C (CH 3) (CN) may be through a linking hand, such CH 2 CH 2 -COO- attached to the sulfur atom in the formula (1).
上記炭素数3〜20の1価の脂環族炭化水素基としては、例えば、シクロペンチル基、シクロヘキシル基、シクロペンテニル基、シクロヘキセニル基などを挙げることができる。
上記炭素数3〜20の1価の脂環族炭化水素基に対する置換基としては、例えば、上記Z1の炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基およびXに対する置換基について例示した基と同様のものの中から適宜選択することができ、これらの置換基は置換誘導体中に1個以上あるいは1種以上存在することができる。ただし、置換誘導体中の合計炭素数ないし合計原子数は20を超えないことが好ましい。
Examples of the monovalent alicyclic hydrocarbon group having 3 to 20 carbon atoms include a cyclopentyl group, a cyclohexyl group, a cyclopentenyl group, and a cyclohexenyl group.
Examples of the substituent for the monovalent alicyclic hydrocarbon group having 3 to 20 carbon atoms include, for example, an alkyl group having 1 to 20 carbon atoms in Z 1 and a monovalent aromatic hydrocarbon having 6 to 20 carbon atoms. Group, a monovalent heterocyclic group having 3 to 20 total atoms of carbon atom and hetero atom, and a group similar to those exemplified for the substituent for X can be appropriately selected from these substituents. May be present in the substituted derivative in one or more or one or more. However, it is preferable that the total number of carbon atoms or the total number of atoms in the substituted derivative does not exceed 20.
また、R1は、p≧2のとき、炭素数1〜20のアルカンに由来するp価の基、炭素数6〜20の芳香族炭化水素に由来するp価の基、炭素原子と異項原子との合計原子数3〜20の複素環式化合物に由来するp価の基または重合体鎖を有するp価の基を示す。
上記炭素数1〜20のアルカンとしては、例えば、メタン、エタン、プロパン、n−ブタン、i−ブタン、n−ペンタン、i−ペンタン、ネオペンタン、n−ヘキサン、n−ヘプタン、n−オクタン、n−ノナン、n−デカン、n−ドデカン、n−テトラデカン、n−ヘキサデカン、n−オクタデカン、n−エイコサンなどを挙げることができる。
In addition, when p ≧ 2, R 1 is a p-valent group derived from an alkane having 1 to 20 carbon atoms, a p-valent group derived from an aromatic hydrocarbon having 6 to 20 carbon atoms, or a carbon atom different from R 1. A p-valent group or a p-valent group having a polymer chain derived from a heterocyclic compound having 3 to 20 atoms in total with the atom is shown.
Examples of the alkane having 1 to 20 carbon atoms include methane, ethane, propane, n-butane, i-butane, n-pentane, i-pentane, neopentane, n-hexane, n-heptane, n-octane, and n. -Nonane, n-decane, n-dodecane, n-tetradecane, n-hexadecane, n-octadecane, n-eicosane and the like can be mentioned.
また、上記炭素数6〜20の芳香族炭化水素としては、例えば、ベンゼン、1,4−ジメチルベンゼン(例えば、1,4−位の各メチル基の炭素原子が式(1)中の硫黄原子に結合する。)、1,2,4,5−テトラメチルベンゼン(例えば、1,2,4,5−位の各メチル基の炭素原子が式(1)中の硫黄原子に結合する。)、1,2,3,4,5,6−ヘキサメチルベンゼン(例えば、1,2,3,4,5,6−位の各メチル基の炭素原子が式(1)中の硫黄原子に結合する。)、1,4−ジ−i−プロピルベンゼン(例えば、1,4−位の各i−プロピル基の2−位の炭素原子が式(1)中の硫黄原子に結合する。)、ナフタレン、アントラセン基などを挙げることができる。 Examples of the aromatic hydrocarbon having 6 to 20 carbon atoms include benzene and 1,4-dimethylbenzene (for example, the carbon atom of each methyl group at the 1,4-position is a sulfur atom in the formula (1)). ), 1,2,4,5-tetramethylbenzene (for example, the carbon atom of each methyl group at the 1,2,4,5-position binds to the sulfur atom in formula (1).) 1,2,3,4,5,6-hexamethylbenzene (for example, the carbon atom of each methyl group at the 1,2,3,4,5,6-position binds to the sulfur atom in formula (1)) 1,4-di-i-propylbenzene (for example, the carbon atom at the 2-position of each i-propyl group at the 1,4-position is bonded to the sulfur atom in the formula (1)). Naphthalene, anthracene group and the like can be mentioned.
また、上記合計原子数3〜20の複素環式化合物としては、例えば、オキシラン、アジリジン、フラン、テトラヒドロフラン、ピロール、ピロリジン、ピラゾール、テトラヒドロピラン、チアン、ピリジン、ピペリジン、モルホリンなどを挙げることができる。
上記炭素数1〜20のアルカンに由来するp価の基、炭素数6〜20の芳香族炭化水素に由来するp価の基および合計原子数3〜20の複素環式化合物に由来するp価の基に対する置換基としては、例えば、上記Z1の炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基およびXに対する置換基について例示した基と同様のものの中から適宜選択することができ、これらの置換基は置換誘導体中に1個以上あるいは1種以上存在することができる。ただし、置換誘導体中の合計炭素数ないし合計原子数は20を超えないことが好ましい。
Examples of the heterocyclic compound having 3 to 20 atoms in total include oxirane, aziridine, furan, tetrahydrofuran, pyrrole, pyrrolidine, pyrazole, tetrahydropyran, thiane, pyridine, piperidine, morpholine, and the like.
P-valent group derived from the alkane having 1 to 20 carbon atoms, p-valent group derived from an aromatic hydrocarbon having 6 to 20 carbon atoms, and p-valent group derived from a heterocyclic compound having 3 to 20 atoms in total. Examples of the substituent for the above group include, for example, an alkyl group having 1 to 20 carbon atoms of Z 1, a monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, and a total number of 3 atoms of carbon atoms and hetero atoms. -20 monovalent heterocyclic groups and the same groups as those exemplified for the substituent for X can be selected as appropriate, and these substituents are present in one or more or one or more kinds in the substituted derivative. be able to. However, it is preferable that the total number of carbon atoms or the total number of atoms in the substituted derivative does not exceed 20.
また、R1のp価の基を与える重合体鎖としては、上記Z1の重合体鎖を有する1価の基について例示した付加重合系重合体鎖、重付加系重合体鎖や重縮合系重合体鎖と同様のものを挙げることができる。R1の重合体鎖を有するp価の基においては、該重合体鎖が直接式(1)中の硫黄原子に結合しても、例えば−CH2−COO−、−C(CH3)(CN)CH2CH2−COO−などの連結手を介して式(1)中の硫黄原子に結合してもよい。 Examples of the polymer chain that gives the p-valent group of R 1 include addition polymerization polymer chains, polyaddition polymer chains, and polycondensation systems exemplified for the monovalent group having the polymer chain of Z 1. The thing similar to a polymer chain can be mentioned. In the p-valent group having the polymer chain of R 1 , even when the polymer chain is directly bonded to the sulfur atom in the formula (1), for example, —CH 2 —COO—, —C (CH 3 ) ( CN) via a coupling hand, such as CH 2 CH 2 -COO- may be bonded to the sulfur atom in the formula (1).
次に、式(2)において、Z2のm価の基を与える炭素数1〜20のアルカンとしては、例えば、上記R1のp価の基を与える炭素数1〜20のアルカン類について例示した化合物と同様のものを挙げることができる。
また、Z2のm価の基を与える炭素数6〜20の芳香族炭化水素としては、例えば、上記R1のp価の基を与える炭素数6〜20の芳香族炭化水素について例示した化合物と同様のものを挙げることができる。
また、Z2のm価の基を与える炭素原子と異項原子との合計原子数3〜20の複素環式化合物としては、例えば、上記R1のp価の基を与える炭素原子と異項原子との合計原子数3〜20の複素環式化合物について例示した化合物と同様のものを挙げることができる。
Next, in the formula (2), examples of the alkane having 1 to 20 carbon atoms that gives an m-valent group of Z 2 include, for example, alkanes having 1 to 20 carbon atoms that give a p-valent group of the above R 1 The same compounds as those described above can be mentioned.
In addition, examples of the aromatic hydrocarbon having 6 to 20 carbon atoms that give an m-valent group of Z 2 include, for example, compounds exemplified for the aromatic hydrocarbon having 6 to 20 carbon atoms that give a p-valent group of R 1 above. The same thing can be mentioned.
In addition, examples of the heterocyclic compound having a total of 3 to 20 carbon atoms and a hetero atom including a m 2 valent group of Z 2 include, for example, a carbon atom and a hetero atom that provide the p valent group of R 1 above. The thing similar to the compound illustrated about the heterocyclic compound of 3-20 total atoms with an atom can be mentioned.
Z2の炭素数1〜20のアルカンに由来するm価の基、炭素数6〜20の芳香族炭化水素に由来するm価の基および合計原子数3〜20の複素環式化合物に由来するm価の基に対する置換基としては、例えば、上記Z1の炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基およびXに対する置換基について例示した基と同様のものの中から適宜選択することができ、これらの置換基は置換誘導体中に1個以上あるいは1種以上存在することができる。ただし、置換誘導体中の合計炭素数ないし合計原子数は20を超えないことが好ましい。
また、Z2のm価の基を与える重合体鎖としては、例えば、上記Z1の重合体鎖を有する1価の基について例示した付加重合系重合体鎖、重付加系重合体鎖や重縮合系重合体鎖と同様のものを挙げることができる。Z2の重合体鎖を有するm価の基においては、該重合体鎖が直接式(2)中のチオカルボニル基の炭素原子に結合しても、例えば−CH2−COO−、−C(CH3)(CN)CH2CH2−COO−などの連結手を介して式(2)中のチオカルボニル基の炭素原子に結合してもよい。
Derived from an m-valent group derived from an alkane having 1 to 20 carbon atoms of Z 2 , an m-valent group derived from an aromatic hydrocarbon having 6 to 20 carbon atoms, and a heterocyclic compound having 3 to 20 atoms in total Examples of the substituent for the m-valent group include, for example, an alkyl group having 1 to 20 carbon atoms of Z 1, a monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, and a total atom of carbon atoms and hetero atoms. The monovalent heterocyclic group of 3 to 20 and the same groups as those exemplified for the substituent for X can be selected as appropriate, and these substituents are one or more or one or more kinds in the substituted derivative. Can exist. However, it is preferable that the total number of carbon atoms or the total number of atoms in the substituted derivative does not exceed 20.
Examples of the polymer chain that gives an m-valent group of Z 2 include, for example, an addition polymerization polymer chain, a polyaddition polymer chain, a heavy chain exemplified for the monovalent group having a polymer chain of Z 1 above. The thing similar to a condensation type polymer chain can be mentioned. In the m-valent group having a polymer chain of Z 2 , even when the polymer chain is directly bonded to the carbon atom of the thiocarbonyl group in the formula (2), for example, —CH 2 —COO—, —C ( CH 3) (CN) CH 2 CH 2 -COO- may be bonded to the carbon atom of the thiocarbonyl group in the formula (2) via a connecting hands like.
式(2)において、R2の炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、−OX、−SX、−N(X)2および重合体鎖を有する1価の基やそれらの置換誘導体としては、例えば、上記Z1のそれぞれ対応する基について例示した基と同様のものを挙げることができる。R2の重合体鎖を有する1価の基においては、該重合体鎖が直接式(2)中の硫黄原子に結合しても、例えば−CH2−COO−、−C(CH3)(CN)CH2CH2−COO−などの連結手を介して式(2)中の硫黄原子に結合してもよい。
また、R2の炭素数3〜20の1価の脂環族炭化水素基やその置換誘導体としては、例えば、上記R1ただし、p=1)の炭素数3〜20の1価の脂環族炭化水素基やその置換誘導体について例示した基と同様のものを挙げることができる。
In the formula (2), a C 1-20 alkyl group of R 2 , a C 6-20 monovalent aromatic hydrocarbon group, a monovalent C 3-20 monovalent carbon atom and a hetero atom. As the monovalent group having a heterocyclic group, —OX, —SX, —N (X) 2 and a polymer chain, or substituted derivatives thereof, for example, the groups exemplified for the corresponding groups of Z 1 above The same thing can be mentioned. In the monovalent group having the polymer chain of R 2 , even when the polymer chain is directly bonded to the sulfur atom in the formula (2), for example, —CH 2 —COO—, —C (CH 3 ) ( CN) via a coupling hand, such as CH 2 CH 2 -COO- may be bonded to the sulfur atom in the formula (2).
Examples of the monovalent alicyclic hydrocarbon group having 3 to 20 carbon atoms of R 2 and substituted derivatives thereof include, for example, the monovalent alicyclic ring having 3 to 20 carbon atoms of the above R 1 , p = 1). Examples thereof are the same as those exemplified for the aromatic hydrocarbon group and substituted derivatives thereof.
式(2)において、複数存在するR2は相互に同一でも異なってもよい。
式(2)において、Z2と−C(=S)−S−R2との間の連結部分が脂肪族炭素原子である場合は、Z2中の脂肪族炭素原子が−C(=S)−S−R2と結合し、該連結部分が芳香族炭素原子である場合は、Z2中の芳香族炭素原子が−C(=S)−S−R2と結合し、さらに該連結部分が硫黄原子である場合は、Z2を示す−SR中の硫黄原子が−C(=S)−S−R2と結合している。
In the formula (2), a plurality of R 2 may be the same as or different from each other.
In Formula (2), when the connecting part between Z 2 and —C (═S) —S—R 2 is an aliphatic carbon atom, the aliphatic carbon atom in Z 2 is —C (═S ) When bonded to —S—R 2 and the linking moiety is an aromatic carbon atom, the aromatic carbon atom in Z 2 is bonded to —C (═S) —S—R 2, and When the moiety is a sulfur atom, the sulfur atom in —SR representing Z 2 is bonded to —C (═S) —S—R 2 .
式(3)において、Z3およびZ4は相互に独立に水素原子、塩素原子、カルボキシル基、シアノ基、炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、
−OX1、−SX1、−OC(=O)X1、−N(X1)(X2)、−C(=O)OX1、
−C(=O)N(X1)(X2)、−P(=O)(OX1)2、−P(=O)(X1)2または重合体鎖を有する1価の基を示し、X1およびX2は相互に独立に炭素数1〜18のアルキル基、炭素数2〜18のアルケニル基、炭素数6〜18の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜18の1価の複素環式基を示し、前記炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、X1およびX2はそれぞれ置換されていてもよい。
Z3およびZ4は上記式(1)におけるZ1として上記に例示したものを同様に例示することができる。
Z3およびZ4としてはそれぞれ、炭素数1〜20のアルキル基のほか、重合性不飽和化合物との反応性の面から、特に、式(1)中のチオカルボニル基(C=S)の炭素原子と、Z3およびZ4中の窒素原子や酸素原子等の異項原子とが共有結合している基、より具体的には、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、−OX1、−N(X1)(X2)等が好ましく、特に、メチル基、エチル基、1−ピロール基、1−ピラゾール基、メトキシ基、エトキシ基、ジメチルアミノ基、ジエチルアミノ基等が好ましい。
In Formula (3), Z 3 and Z 4 are each independently a hydrogen atom, a chlorine atom, a carboxyl group, a cyano group, an alkyl group having 1 to 20 carbon atoms, or a monovalent aromatic hydrocarbon having 6 to 20 carbon atoms. A monovalent heterocyclic group having 3 to 20 total atoms of carbon atom and hetero atom,
-OX 1, -SX 1, -OC ( = O) X 1, -N (X 1) (X 2), - C (= O) OX 1,
-C (= O) N (X 1) (X 2), - a P (= O) (OX 1 ) 2, -P (= O) (X 1) 1 monovalent group having 2 or polymer chain X 1 and X 2 are independently of each other an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms, or a carbon atom. A monovalent heterocyclic group having 3 to 18 atoms in total with the atom, the alkyl group having 1 to 20 carbon atoms, the monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, and a carbon atom and a different group The monovalent heterocyclic group having 3 to 20 atoms in total, X 1 and X 2 may be substituted.
As Z 3 and Z 4 , those exemplified above as Z 1 in the above formula (1) can be exemplified.
Z 3 and Z 4 are each an alkyl group having 1 to 20 carbon atoms, and particularly from the viewpoint of reactivity with the polymerizable unsaturated compound, in particular, the thiocarbonyl group (C═S) in formula (1) A group in which a carbon atom and a hetero atom such as a nitrogen atom or an oxygen atom in Z 3 and Z 4 are covalently bonded, more specifically, a total number of atoms of 3 to 20 of the carbon atom and the hetero atom Are preferably a monovalent heterocyclic group, —OX 1 , —N (X 1 ) (X 2 ) and the like, and in particular, a methyl group, an ethyl group, a 1-pyrrole group, a 1-pyrazole group, a methoxy group, and an ethoxy group. , A dimethylamino group, a diethylamino group and the like are preferable.
本発明における特に好ましいチオカルボニルチオ化合物の具体例としては、下記式(4)〜(28)で表される化合物などを挙げることができる。 Specific examples of particularly preferred thiocarbonylthio compounds in the present invention include compounds represented by the following formulas (4) to (28).
これらのチオカルボニルチオ化合物は、単独でまたは2種以上を混合して使用することができる。 These thiocarbonylthio compounds can be used alone or in admixture of two or more.
次に、〔A〕光重合性不飽和基を有する共重合体は、化合物(a1)ラジカル重合性を有する不飽和カルボン酸および/または不飽和カルボン酸無水物、あるいはそれらカルボン酸の保護化物、および化合物(a3) (a1)、(a2)以外のラジカル重合性化合物を含有する重合性混合物を溶媒中、重合開始剤、チオカルボニルチオ化合物(1)−(28)の存在下でリビングラジカル重合し、更に化合物(a2)水酸基等の官能基を有する化合物または、化合物(a1)、(a2)、(a3)を含有する重合性混合物を追添して重合を継続し、(a4)少なくとも1個のエチレン性不飽和基と、イソシアネート基、エポキシ基等の1個の官能基を有する化合物を付加反応することによって製造することができる。また必要に応じて、さらに重合性混合物を追添して、ブロックセグメントを追加することができる。 Next, [A] the copolymer having a photopolymerizable unsaturated group is compound (a1) an unsaturated carboxylic acid and / or unsaturated carboxylic acid anhydride having radical polymerizability, or a protected product of these carboxylic acids, And compound (a3) Living radical polymerization of a polymerizable mixture containing a radically polymerizable compound other than (a1) and (a2) in a solvent in the presence of a polymerization initiator and a thiocarbonylthio compound (1)-(28) Furthermore, polymerization is continued by adding a compound (a2) having a functional group such as a hydroxyl group or a polymerizable mixture containing the compounds (a1), (a2), and (a3), and (a4) at least 1 It can be produced by addition reaction of a compound having one ethylenically unsaturated group and one functional group such as an isocyanate group or an epoxy group. If necessary, a block segment can be added by further adding a polymerizable mixture.
前記重合がリビングラジカル重合の形態をとる場合、重合性不飽和化合物としてカルボキシル基等の活性ラジカルを失活させるおそれがある官能基を有する化合物を用いる場合、成長末端が失活しないようにするため、必要に応じて、該不飽和化合物中の官能基を、例えばエステル化などにより保護して重合したのち、脱保護することにより、より分子量分布の狭い共重合体〔A〕を得ることもできる。 When the polymerization takes the form of living radical polymerization, when using a compound having a functional group that may deactivate an active radical such as a carboxyl group as the polymerizable unsaturated compound, in order to prevent the growth terminal from being deactivated. If necessary, a copolymer [A] having a narrower molecular weight distribution can also be obtained by deprotecting the functional group in the unsaturated compound after polymerization by, for example, esterification. .
前記ラジカル重合開始剤としては、使用される重合性不飽和化合物の種類に応じて適宜選択されるが、一般にラジカル重合開始剤として知られているものを使用することができ、例えば、2,2’−アゾビスイソブチロニトリル、2,2’−アゾビス(2,4−ジメチルバレロニトリル)、2,2’−アゾビス(4−メトキシ−2,4−ジメチルバレロニトリル)等のアゾ化合物;ベンゾイルペルオキシド、ラウロイルペルオキシド、1,1’−ビス(t−ブチルペルオキシ)シクロヘキサン、t−ブチルペルオキシピバレート等の有機過酸化物;過酸化水素;これらの過酸化物と還元剤とからなるレドックス系開始剤等を挙げることができる。 The radical polymerization initiator is appropriately selected according to the type of the polymerizable unsaturated compound to be used, and those generally known as radical polymerization initiators can be used. Azo compounds such as' -azobisisobutyronitrile, 2,2'-azobis (2,4-dimethylvaleronitrile), 2,2'-azobis (4-methoxy-2,4-dimethylvaleronitrile); benzoyl Organic peroxides such as peroxide, lauroyl peroxide, 1,1'-bis (t-butylperoxy) cyclohexane, t-butylperoxypivalate; hydrogen peroxide; redox system starting from these peroxides and reducing agents An agent etc. can be mentioned.
これらのラジカル重合開始剤のうち、酸素等による副反応物が生起し難い観点から、特に、2,2’−アゾビスイソブチロニトリル、2,2’−アゾビス(2,4−ジメチルバレロニトリル)等のアゾ化合物が好ましい。前記ラジカル重合開始剤は、単独でまたは2種以上を混合して使用することができる
また、前記重合に際しては、他の分子量制御剤、例えば、α−メチルスチレンダイマー、t−ドデシルメルカプタン等の1種以上を、ジスルフィド化合物(1)と併用することもできる。
Among these radical polymerization initiators, 2,2′-azobisisobutyronitrile, 2,2′-azobis (2,4-dimethylvaleronitrile) are particularly preferable from the viewpoint that side reactions due to oxygen or the like are unlikely to occur. Azo compounds such as) are preferred. The radical polymerization initiators can be used alone or in admixture of two or more kinds. In the polymerization, other molecular weight control agents such as α-methylstyrene dimer, t-dodecyl mercaptan and the like 1 More than one species can be used in combination with the disulfide compound (1).
前記重合に使用される溶媒としては、特に限定されるものでないが、例えば、
プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル等のプロピレングリコールモノアルキルエーテル;
エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、ジプロピレングリコールモノメチルエーテルアセテート、ジプロピレングリコールモノエチルエーテルアセテート等の(ポリ)アルキレングリコールモノアルキルエーテルアセテート;
ジエチレングリコールジメチルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールジエチルエーテル、ジプロピレングリコールジメチルエーテル、ジプロピレングリコールメチルエチルエーテル、ジプロピレングリコールジエチルエーテル等の(ポリ)アルキレングリコールジエーテル;
テトラヒドロフラン等の他のエーテル;
メチルエチルケトン、シクロヘキサノン、2−ヘプタノン、3−ヘプタノン等のケトン;
ジアセトンアルコール(即ち、4−ヒドロキシ−4−メチルペンタン−2−オン)、4−ヒドロキシ−4−メチルヘキサン−2−オン等のケトアルコール;
乳酸メチル、乳酸エチル等の乳酸アルキルエステル;
2−ヒドロキシ−2−メチルプロピオン酸エチル、ヒドロキシ酢酸エチル、2−ヒドロキシ−3−メチルブタン酸メチル、3−メトキシプロピオン酸メチル、3−メトキシプロピオン酸エチル、3−エトキシプロピオン酸メチル、3−エトキシプロピオン酸エチル、エトキシ酢酸エチル、3−メチル−3−メトキシブチルアセテート、3−メチル−3−メトキシブチルプロピオネート、酢酸エチル、酢酸n−プロピル、酢酸i−プロピル、酢酸n−ブチル、酢酸i−ブチル、酢酸4−メトキシブチル、酢酸3−メトキシブチル、酢酸2−メトキシブチル、ぎ酸n−ペンチル、酢酸i−ペンチル、プロピオン酸n−ブチル、酪酸エチル、酪酸n−プロピル、酪酸i−プロピル、酪酸n−ブチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸n−プロピル、アセト酢酸メチル、アセト酢酸エチル、2−オキソブタン酸エチル等の他のエステル;
トルエン、キシレン等の芳香族炭化水素;
N−メチルピロリドン、N,N−ジメチルホルムアミド、N,N−ジメチルアセトアミド等のアミド
等を挙げることができる。
The solvent used for the polymerization is not particularly limited.
Propylene glycol monoalkyl ethers such as propylene glycol monomethyl ether and propylene glycol monoethyl ether;
Ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, dipropylene glycol monomethyl ether acetate, dipropylene glycol monoethyl ether (Poly) alkylene glycol monoalkyl ether acetates such as acetate;
(Poly) alkylene glycol diethers such as diethylene glycol dimethyl ether, diethylene glycol methyl ethyl ether, diethylene glycol diethyl ether, dipropylene glycol dimethyl ether, dipropylene glycol methyl ethyl ether, dipropylene glycol diethyl ether;
Other ethers such as tetrahydrofuran;
Ketones such as methyl ethyl ketone, cyclohexanone, 2-heptanone, 3-heptanone;
Ketoalcohols such as diacetone alcohol (ie 4-hydroxy-4-methylpentan-2-one), 4-hydroxy-4-methylhexan-2-one;
Lactic acid alkyl esters such as methyl lactate and ethyl lactate;
Ethyl 2-hydroxy-2-methylpropionate, ethyl hydroxyacetate, methyl 2-hydroxy-3-methylbutanoate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, 3-ethoxypropion Ethyl acetate, ethyl ethoxy acetate, 3-methyl-3-methoxybutyl acetate, 3-methyl-3-methoxybutyl propionate, ethyl acetate, n-propyl acetate, i-propyl acetate, n-butyl acetate, i-acetate Butyl, 4-methoxybutyl acetate, 3-methoxybutyl acetate, 2-methoxybutyl acetate, n-pentyl formate, i-pentyl acetate, n-butyl propionate, ethyl butyrate, n-propyl butyrate, i-propyl butyrate, N-butyl butyrate, methyl pyruvate, ethyl pyruvate, pyruvin n- propyl, methyl acetoacetate, ethyl acetoacetate, other esters such as ethyl 2-oxobutanoate;
Aromatic hydrocarbons such as toluene and xylene;
Examples thereof include amides such as N-methylpyrrolidone, N, N-dimethylformamide, and N, N-dimethylacetamide.
これらの溶媒のうち、リビングラジカル重合時に活性ラジカルが失活せず、また感放射線性樹脂組成物としたときの各成分の溶解性、塗布性等の観点から、プロピレングリコールモノメチルエーテル、エチレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、ジプロピレングリコールモノメチルエーテルアセテート、ジエチレングリコールジメチルエーテル、ジエチレングリコールメチルエチルエーテル、ジプロピレングリコールジメチルエーテル、シクロヘキサノン、2−ヘプタノン、3−ヘプタノン、3−メトキシプロピオン酸エチル、3−エトキシプロピオン酸メチル、3−エトキシプロピオン酸エチル、3−メチル−3−メトキシブチルプロピオネート、酢酸n−ブチル、酢酸i−ブチル、酢酸3−メトキシブチル、ぎ酸n−ペンチル、酢酸i−ペンチル、プロピオン酸n−ブチル、酪酸エチル、酪酸i−プロピル、酪酸n−ブチル、ピルビン酸エチル等が好ましい。 Among these solvents, active radicals are not deactivated during living radical polymerization, and from the viewpoints of solubility and coating properties of each component when used as a radiation sensitive resin composition, propylene glycol monomethyl ether, ethylene glycol monomethyl Ether acetate, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, dipropylene glycol monomethyl ether acetate, diethylene glycol dimethyl ether, diethylene glycol methyl ethyl ether, dipropylene glycol dimethyl ether, cyclohexanone, 2 -Heptanone, 3-heptanone, 3-methoxypro Ethyl onate, methyl 3-ethoxypropionate, ethyl 3-ethoxypropionate, 3-methyl-3-methoxybutylpropionate, n-butyl acetate, i-butyl acetate, 3-methoxybutyl acetate, n-formic acid Pentyl, i-pentyl acetate, n-butyl propionate, ethyl butyrate, i-propyl butyrate, n-butyl butyrate, ethyl pyruvate and the like are preferable.
前記溶媒は、単独でまたは2種以上を混合して使用することができる。
前記重合において、ラジカル重合開始剤の使用量は、全不飽和化合物100重量部に対して、好ましくは0.1〜50重量部、より好ましくは0.1〜20重量部である。
また、チオカルボニルチオ化合物(1)〜(3)の使用量は、全不飽和化合物100重量部に対して、好ましくは0.1〜50重量部、より好ましくは0.2〜16重量部、特に好ましくは0.4〜8重量部である。この場合、チオカルボニルチオ化合物(1)〜(3)の使用量が0.1重量部未満では、分子量および分子量分布の規制効果が低下する傾向があり、一方50重量部を超えると、低分子量成分が優先的に生成してしまうおそれがある。
The said solvent can be used individually or in mixture of 2 or more types.
In the said polymerization, the usage-amount of a radical polymerization initiator becomes like this. Preferably it is 0.1-50 weight part with respect to 100 weight part of all the unsaturated compounds, More preferably, it is 0.1-20 weight part.
The amount of the thiocarbonylthio compounds (1) to (3) used is preferably 0.1 to 50 parts by weight, more preferably 0.2 to 16 parts by weight, with respect to 100 parts by weight of the total unsaturated compounds. Especially preferably, it is 0.4-8 weight part. In this case, when the amount of the thiocarbonylthio compounds (1) to (3) used is less than 0.1 parts by weight, the regulation effect of the molecular weight and the molecular weight distribution tends to be reduced. There exists a possibility that a component may produce | generate preferentially.
また、他の分子量制御剤の使用量は、全分子量制御剤100重量部に対して、好ましくは200重量部以下、より好ましくは40重量部以下である。他の分子量制御剤の使用量が200重量部を超えると、本発明の所期の効果が損なわれるおそれがある。
また、溶媒の使用量は、全不飽和化合物100重量部に対して、好ましくは50〜1,000重量部、より好ましくは100〜500重量部である。
また、重合温度は、好ましくは0〜150℃、より好ましくは50〜120℃であり、重合時間は、好ましくは10分〜20時間、より好ましくは30分〜6時間である。
Moreover, the usage-amount of another molecular weight control agent becomes like this. Preferably it is 200 weight part or less with respect to 100 weight part of all the molecular weight control agents, More preferably, it is 40 weight part or less. When the usage-amount of another molecular weight control agent exceeds 200 weight part, there exists a possibility that the desired effect of this invention may be impaired.
Moreover, the amount of the solvent used is preferably 50 to 1,000 parts by weight, more preferably 100 to 500 parts by weight with respect to 100 parts by weight of the total unsaturated compounds.
The polymerization temperature is preferably 0 to 150 ° C., more preferably 50 to 120 ° C., and the polymerization time is preferably 10 minutes to 20 hours, more preferably 30 minutes to 6 hours.
化合物(a1)のアルカリ可溶性モノマーは、好ましくはラジカル重合性を有する不飽和カルボン酸および/または不飽和カルボン酸無水物である。ラジカル重合性を有する不飽和カルボン酸および/または不飽和カルボン酸無水物としては、例えばモノカルボン酸、ジカルボン酸、ジカルボン酸の無水物、多価カルボン酸のモノ〔(メタ)アクリロイロキシアルキル〕エステル、両末端のそれぞれにカルボキシル基と水酸基とを有するポリマーのモノ(メタ)アクリレート、カルボキシル基を有する多環式化合物およびその無水物などを挙げることができる。 The alkali-soluble monomer of the compound (a1) is preferably an unsaturated carboxylic acid and / or an unsaturated carboxylic acid anhydride having radical polymerizability. Examples of the unsaturated carboxylic acid and / or unsaturated carboxylic acid anhydride having radical polymerizability include monocarboxylic acid, dicarboxylic acid, dicarboxylic acid anhydride, and poly [carboxylic acid] mono [(meth) acryloyloxyalkyl]. Examples thereof include esters, mono (meth) acrylates of polymers having a carboxyl group and a hydroxyl group at both ends, polycyclic compounds having a carboxyl group, and anhydrides thereof.
これらの具体例としては、モノカルボン酸として、例えばアクリル酸、メタクリル酸、クロトン酸など;
ジカルボン酸として、例えばマレイン酸、フマル酸、シトラコン酸、メサコン酸、イタコン酸など;
ジカルボン酸の無水物として、例えば上記ジカルボン酸として例示した上記化合物の酸無水物など;
多価カルボン酸のモノ〔(メタ)アクリロイロキシアルキル〕エステルとして、例えばコハク酸モノ〔2−(メタ)アクリロイロキシエチル〕、フタル酸モノ〔2−(メタ)アクリロイロキシエチル〕など;
両末端のそれぞれにカルボキシル基と水酸基とを有するポリマーのモノ(メタ)アクリレートとして、例えばω−カルボキシポリカプロラクトンモノ(メタ)アクリレートなど;
カルボキシル基を有する多環式化合物およびその無水物として、例えば5−カルボキシビシクロ[2.2.1]ヘプト−2−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−5−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−5−エチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−6−メチルビシクロ[2.2.1]ヘプト−2−エン、5−カルボキシ−6−エチルビシクロ[2.2.1]ヘプト−2−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘプト−2−エン無水物などがそれぞれ挙げられる。
Specific examples thereof include monocarboxylic acids such as acrylic acid, methacrylic acid, and crotonic acid;
Examples of dicarboxylic acids include maleic acid, fumaric acid, citraconic acid, mesaconic acid, itaconic acid and the like;
Examples of dicarboxylic acid anhydrides include, for example, acid anhydrides of the above compounds exemplified as the dicarboxylic acid;
Examples of mono [(meth) acryloyloxyalkyl] esters of polyvalent carboxylic acids such as succinic acid mono [2- (meth) acryloyloxyethyl] and phthalic acid mono [2- (meth) acryloyloxyethyl];
Examples of mono (meth) acrylate of a polymer having a carboxyl group and a hydroxyl group at each of both ends, such as ω-carboxypolycaprolactone mono (meth) acrylate;
Examples of the polycyclic compound having a carboxyl group and anhydrides thereof include 5-carboxybicyclo [2.2.1] hept-2-ene and 5,6-dicarboxybicyclo [2.2.1] hept-2-ene. Ene, 5-carboxy-5-methylbicyclo [2.2.1] hept-2-ene, 5-carboxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-carboxy-6- Methylbicyclo [2.2.1] hept-2-ene, 5-carboxy-6-ethylbicyclo [2.2.1] hept-2-ene, 5,6-dicarboxybicyclo [2.2.1] And hept-2-ene anhydride.
これらのうち、モノカルボン酸、ジカルボン酸の無水物が好ましく使用され、特にアクリル酸、メタクリル酸、無水マレイン酸が共重合反応性、アルカリ水溶液に対する溶解性および入手が容易である点から好ましく用いられる。これらは、単独であるいは組み合わせて用いられる。 Of these, monocarboxylic acid and dicarboxylic acid anhydrides are preferably used, and acrylic acid, methacrylic acid, and maleic anhydride are particularly preferably used from the viewpoints of copolymerization reactivity, solubility in alkaline aqueous solutions, and availability. . These may be used alone or in combination.
化合物(a1)のカルボキシル基を保護する保護基としては、特に限定されずカルボキシル基の保護基として公知のものが使用できる。例えば、トリアルキルシリル基、1−アルコキシアルキル基、環状1−アルコキシアルキル基などがあげられる。さらに具体的に、例えば、トリメチルシリル、ジメチルブチルシリル、1−エトキシエチル、1−プロポキシエチル、テトラヒドロフラニル、テトラヒドロピラニル、トリフェニルメチルなどが挙げられる。 The protecting group for protecting the carboxyl group of the compound (a1) is not particularly limited, and a known protecting group for the carboxyl group can be used. Examples thereof include a trialkylsilyl group, a 1-alkoxyalkyl group, and a cyclic 1-alkoxyalkyl group. More specifically, for example, trimethylsilyl, dimethylbutylsilyl, 1-ethoxyethyl, 1-propoxyethyl, tetrahydrofuranyl, tetrahydropyranyl, triphenylmethyl and the like can be mentioned.
共重合体[α]において、(a1)不飽和カルボン酸系化合物は、単独または2種以上を混合して使用することができる。
共重合体[α]において、(a1)不飽和カルボン酸系化合物に由来する繰り返し単位の含有率は、共重合体[α]に基づいて好ましくは1〜50重量%、さらに好ましくは5〜40重量%である。(a1)不飽和カルボン酸系化合物に由来する繰り返し単位の含有率が1重量%未満では、(a4)少なくとも1個のエチレン性不飽和基と、エポキシ基等の1個の官能基を有する化合物との反応により得られる重合体のアルカリ現像液に対する溶解性が低下する傾向があり、一方50重量%を超えると、該重合体のアルカリ現像液に対する溶解性が大きくなりすぎるおそれがある。
In the copolymer [α], the (a1) unsaturated carboxylic acid compound can be used alone or in admixture of two or more.
In the copolymer [α], the content of the repeating unit derived from the (a1) unsaturated carboxylic acid compound is preferably 1 to 50% by weight, more preferably 5 to 40 based on the copolymer [α]. % By weight. (A1) When the content of the repeating unit derived from the unsaturated carboxylic acid compound is less than 1% by weight, (a4) a compound having at least one ethylenically unsaturated group and one functional group such as an epoxy group There is a tendency that the solubility of the polymer obtained by the reaction with the alkali developer tends to be reduced, and when it exceeds 50% by weight, the solubility of the polymer in the alkali developer may become too high.
一方、上記(a2)水酸基等の官能基を有する化合物は特に限定はしないが、
(a2)水酸基含有不飽和化合物としては、例えば、
アクリル酸5−ヒドロキシペンチルエステル、アクリル酸6−ヒドロキシヘキシルエステル、アクリル酸7−ヒドロキシヘプチルエステル、アクリル酸8−ヒドロキシオクチルエステル、アクリル酸9−ヒドロキシノニルエステル、アクリル酸10−ヒドロキシデシルエステル、アクリル酸11−ヒドロキシウンデシルエステル、アクリル酸12−ヒドロキシト゛デシルエステルの如きアクリル酸ヒドロキシアルキルエステル;
メタクリル酸5−ヒドロキシペンチルエステル、メタクリル酸6−ヒドロキシヘキシルエステル、メタクリル酸7−ヒドロキシヘプチルエステル、メタクリル酸8−ヒドロキシオクチルエステル、メタクリル酸9−ヒドロキシノニルエステル、メタクリル酸10−ヒドロキシデシルエステル、メタクリル酸11−ヒドロキシウンデシルエステル、メタクリル酸12−ヒドロキシト゛デシルエステルの如きメタクリル酸ヒドロキシアルキルエステル;
アクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル、アクリル酸3−(6−ヒドロキシエチルヘキサノイルオキシ)プロピルエステル、アクリル酸4−(6−ヒドロキシエチルヘキサノイルオキシ)ブチルエステル、アクリル酸5−(6−ヒドロキシエチルヘキサノイルオキシ)ペンチルエステル、アクリル酸6−(6−ヒドロキシエチルヘキサノイルオキシ)へキシルエステルの如きアクリル酸(6−ヒドロキシエチルヘキサノイルオキシ)アルキルエステル;
メタクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル、メタクリル酸3−(6−ヒドロキシエチルヘキサノイルオキシ)プロピルエステル、メタクリル酸4−(6−ヒドロキシエチルヘキサノイルオキシ)ブチルエステル、メタクリル酸5−(6−ヒドロキシエチルヘキサノイルオキシ)ペンチルエステル、メタクリル酸6−(6−ヒドロキシエチルヘキサノイルオキシ)へキシルエステルの如きメタクリル酸(6−ヒドロキシエチルヘキサノイルオキシ)アルキルエステル;
アクリル酸2−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−エチルエステル、アクリル酸3−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−プロピルエステル、アクリル酸4−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−ブチルエステル、アクリル酸5−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−ペンチルエステル、アクリル酸6−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−ヘキシルエステルの如きアクリル酸(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−アルキルエステル;
メタクリル酸2−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−エチルエステル、メタクリル酸3−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−プロピルエステル、メタクリル酸4−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−ブチルエステル、メタクリル酸5−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−ペンチルエステル、メタクリル酸6−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−ヘキシルエステルの如きメタクリル酸(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−アルキルエステル;
アクリル酸4−ヒドロキシ−シクロヘキシルエステル、アクリル酸4−ヒドロキシメチル−シクロヘキシルメチルエステル、アクリル酸4−ヒドロキシエチル−シクロヘキシルエチルエステル、アクリル酸3−ヒドロキシ−ビシクロ[2.2.1]ヘプト−5−エン−2−イルエステル、アクリル酸3−ヒドロキシメチル−ビシクロ[2.2.1]ヘプト−5−エン−2−イルメチルエステル、アクリル酸3−ヒドロキシエチル−ビシクロ[2.2.1]ヘプト−5−エン−2−イルエチルエステル、アクリル酸8−ヒドロキシ−ビシクロ[2.2.1]ヘプト−5−エン−2−イルエステル、アクリル酸2−ヒドロキシ−オクタヒドロ−4,7−メタノ−インデン−5−イルエステル、アクリル酸2−ヒドロキシメチル−オクタヒドロ−4,7−メタノ−インデン−5−イルメチルエステル、アクリル酸2−ヒドロキシエチル−オクタヒドロ−4,7−メタノ−インデン−5−イルエチルエステル、アクリル酸3−ヒドロキシ−アダマンタン−1−イルエステル、アクリル酸3−ヒドロキシメチル−アダマンタン−1−イルメチルエステル、アクリル酸3−ヒドロキシエチル−アダマンタン−1−イルエチルエステルの如き脂環式構造を有するアクリル酸ヒドロキシアルキルエステル;
メタクリル酸4−ヒドロキシ−シクロヘキシルエステル、メタクリル酸4−ヒドロキシメチル−シクロヘキシルメチルエステル、メタクリル酸4−ヒドロキシエチル−シクロヘキシルエチルエステル、メタクリル酸3−ヒドロキシ−ビシクロ[2.2.1]ヘプト−5−エン−2−イルエステル、メタクリル酸3−ヒドロキシメチル−ビシクロ[2.2.1]ヘプト−5−エン−2−イルメチルエステル、メタクリル酸3−ヒドロキシエチル−ビシクロ[2.2.1]ヘプト−5−エン−2−イルエチルエステル、メタクリル酸8−ヒドロキシ−ビシクロ[2.2.1]ヘプト−5−エン−2−イルエステル、メタクリル酸2−ヒドロキシ−オクタヒドロ−4,7−メタノ−インデン−5−イルエステル、メタクリル酸2−ヒドロキシメチル−オクタヒドロ−4,7−メタノ−インデン−5−イルメチルエステル、メタクリル酸2−ヒドロキシエチル−オクタヒドロ−4,7−メタノ−インデン−5−イルエチルエステル、メタクリル酸3−ヒドロキシ−アダマンタン−1−イルエステル、メタクリル酸3−ヒドロキシメチル−アダマンタン−1−イルメチルエステル、メタクリル酸3−ヒドロキシエチル−アダマンタン−1−イルエチルエステルの如き脂環式構造を有するメタクリル酸ヒドロキシアルキルエステル等を挙げることができる。
On the other hand, the compound (a2) having a functional group such as a hydroxyl group is not particularly limited.
Examples of the (a2) hydroxyl group-containing unsaturated compound include:
Acrylic acid 5-hydroxypentyl ester, acrylic acid 6-hydroxyhexyl ester, acrylic acid 7-hydroxyheptyl ester, acrylic acid 8-hydroxyoctyl ester, acrylic acid 9-hydroxynonyl ester, acrylic acid 10-hydroxydecyl ester, acrylic acid Acrylic acid hydroxyalkyl esters such as 11-hydroxyundecyl ester, acrylic acid 12-hydroxydodecyl ester;
Methacrylic acid 5-hydroxypentyl ester, methacrylic acid 6-hydroxyhexyl ester, methacrylic acid 7-hydroxyheptyl ester, methacrylic acid 8-hydroxyoctyl ester, methacrylic acid 9-hydroxynonyl ester, methacrylic acid 10-hydroxydecyl ester, methacrylic acid Methacrylic acid hydroxyalkyl esters such as 11-hydroxyundecyl ester, methacrylic acid 12-hydroxydodecyl ester;
Acrylic acid 2- (6-hydroxyethylhexanoyloxy) ethyl ester, acrylic acid 3- (6-hydroxyethylhexanoyloxy) propyl ester, acrylic acid 4- (6-hydroxyethylhexanoyloxy) butyl ester, acrylic acid Acrylic acid (6-hydroxyethylhexanoyloxy) alkyl ester such as 5- (6-hydroxyethylhexanoyloxy) pentyl ester, acrylic acid 6- (6-hydroxyethylhexanoyloxy) hexyl ester;
Methacrylic acid 2- (6-hydroxyethylhexanoyloxy) ethyl ester, methacrylic acid 3- (6-hydroxyethylhexanoyloxy) propyl ester, methacrylic acid 4- (6-hydroxyethylhexanoyloxy) butyl ester, methacrylic acid Methacrylic acid (6-hydroxyethylhexanoyloxy) alkyl ester such as 5- (6-hydroxyethylhexanoyloxy) pentyl ester, 6- (6-hydroxyethylhexanoyloxy) hexyl methacrylate;
Acrylic acid 2- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -ethyl ester, acrylic acid 3- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -propyl ester, acrylic acid 4- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -butyl ester, acrylic acid 5- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -pentyl ester, acrylic acid 6- (3-hydroxy Acrylic acid (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -alkyl esters such as -2,2-dimethyl-propoxycarbonyloxy) -hexyl ester;
Methacrylic acid 2- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -ethyl ester, methacrylic acid 3- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -propyl ester, methacrylic acid 4- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -butyl ester, methacrylic acid 5- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -pentyl ester, methacrylic acid 6- (3-hydroxy Methacrylic acid (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -alkyl ester such as -2,2-dimethyl-propoxycarbonyloxy) -hexyl ester;
Acrylic acid 4-hydroxy-cyclohexyl ester, Acrylic acid 4-hydroxymethyl-cyclohexyl methyl ester, Acrylic acid 4-hydroxyethyl-cyclohexyl ethyl ester, Acrylic acid 3-hydroxy-bicyclo [2.2.1] hept-5-ene 2-yl ester, acrylic acid 3-hydroxymethyl-bicyclo [2.2.1] hept-5-en-2-ylmethyl ester, acrylic acid 3-hydroxyethyl-bicyclo [2.2.1] hept- 5-En-2-ylethyl ester, acrylic acid 8-hydroxy-bicyclo [2.2.1] hept-5-en-2-yl ester, acrylic acid 2-hydroxy-octahydro-4,7-methano-indene -5-yl ester, 2-hydroxymethyl-octahydro-4,7-metaacrylate -Inden-5-ylmethyl ester, acrylic acid 2-hydroxyethyl-octahydro-4,7-methano-inden-5-ylethyl ester, acrylic acid 3-hydroxy-adamantan-1-yl ester, acrylic acid 3-hydroxy Acrylic acid hydroxyalkyl esters having an alicyclic structure such as methyl-adamantan-1-ylmethyl ester, acrylic acid 3-hydroxyethyl-adamantan-1-ylethyl ester;
Methacrylic acid 4-hydroxy-cyclohexyl ester, Methacrylic acid 4-hydroxymethyl-cyclohexyl methyl ester, Methacrylic acid 4-hydroxyethyl-cyclohexyl ethyl ester, Methacrylic acid 3-hydroxy-bicyclo [2.2.1] Hept-5-ene 2-yl ester, methacrylic acid 3-hydroxymethyl-bicyclo [2.2.1] hept-5-en-2-ylmethyl ester, methacrylic acid 3-hydroxyethyl-bicyclo [2.2.1] hept- 5-En-2-ylethyl ester, methacrylic acid 8-hydroxy-bicyclo [2.2.1] hept-5-en-2-yl ester, methacrylic acid 2-hydroxy-octahydro-4,7-methano-indene -5-yl ester, 2-hydroxymethyl methacrylate-octahi B, 7-Methano-inden-5-ylmethyl ester, 2-hydroxyethyl methacrylate-octahydro-4,7-methano-inden-5-ylethyl ester, 3-hydroxy-adamantan-1-yl methacrylate Mention may be made of methacrylic acid hydroxyalkyl esters having an alicyclic structure such as esters, methacrylic acid 3-hydroxymethyl-adamantan-1-ylmethyl ester, and methacrylic acid 3-hydroxyethyl-adamantan-1-ylethyl ester. .
また、(メタ)アクリル酸(6−ヒドロキシエチルヘキサノイルオキシ)アルキルエステルの市販品としては、商品名で、PLACCEL FM1D、FM2D(ダイセル化学工業(株)製)等を挙げることができる。(メタ)アクリル酸(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−アルキルエステルの市販品としては、商品名で、HEMAC1(ダイセル化学工業(株)製)等を挙げることができる。 Moreover, as a commercial item of (meth) acrylic acid (6-hydroxyethylhexanoyloxy) alkyl ester, PLACEL FM1D, FM2D (made by Daicel Chemical Industries, Ltd.), etc. can be mentioned by a brand name. As a commercial item of (meth) acrylic acid (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -alkyl ester, HEMAC1 (manufactured by Daicel Chemical Industries, Ltd.) and the like can be given as trade names.
水酸基含有不飽和化合物のうち、共重合反応性およびイソシアネート化合物との反応性の点から、アクリル酸6−ヒドロキシヘキシルエステル、メタクリル酸6−ヒドロキシヘキシルエステル、アクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル、メタクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル、アクリル酸2−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−エチルエステル、メタクリル酸2−(3−ヒドロキシ−2,2−ジメチル−プロポキシカルボニルオキシ)−エチルエステル、アクリル酸4−ヒドロキシメチル−シクロヘキシルメチルエステル、メタクリル酸4−ヒドロキシメチル−シクロヘキシルメチルエステル、アクリル酸3−ヒドロキシメチル−アダマンタン−1−イルメチルエステル、メタクリル酸3−ヒドロキシメチル−アダマンタン−1−イルメチルエステル等が好ましい。 Among the hydroxyl group-containing unsaturated compounds, acrylic acid 6-hydroxyhexyl ester, methacrylic acid 6-hydroxyhexyl ester, acrylic acid 2- (6-hydroxyethylhexanoyl) from the viewpoint of copolymerization reactivity and reactivity with isocyanate compounds Oxy) ethyl ester, methacrylic acid 2- (6-hydroxyethylhexanoyloxy) ethyl ester, acrylic acid 2- (3-hydroxy-2,2-dimethyl-propoxycarbonyloxy) -ethyl ester, methacrylic acid 2- (3 -Hydroxy-2,2-dimethyl-propoxycarbonyloxy) -ethyl ester, acrylic acid 4-hydroxymethyl-cyclohexylmethyl ester, methacrylic acid 4-hydroxymethyl-cyclohexylmethyl ester, acrylic acid 3-hydroxymethyl Le - adamantan-1-yl methyl ester, methacrylic acid 3-hydroxymethyl - adamantan-1-yl methyl ester, and the like are preferable.
共重合体[α]において、(a2)の水酸基含有不飽和化合物は、単独でまたは2種以上を混合して使用することができる。
共重合体[α]において、(a2)の水酸基含有不飽和化合物に由来する繰り返し単位の含有率は、共重合体[α]に基づいて、好ましくは1〜50重量%、さらに好ましくは3〜40重量%、特に好ましくは5〜30重量%である。(a2)水酸基含有不飽和化合物に由来する繰り返し単位の含有率が1重量%未満では、(a4)不飽和イソシアネート化合物の重合体への導入率が低下して、感度が低下する傾向があり、一方50重量%を超えると、(a4)不飽和イソシアネート化合物との反応により得られる重合体の保存安定性が低下する傾向がある。
In the copolymer [α], the hydroxyl group-containing unsaturated compound (a2) can be used alone or in admixture of two or more.
In the copolymer [α], the content of the repeating unit derived from the hydroxyl group-containing unsaturated compound (a2) is preferably 1 to 50% by weight, more preferably 3 to 3, based on the copolymer [α]. It is 40% by weight, particularly preferably 5 to 30% by weight. When the content of the repeating unit derived from the (a2) hydroxyl group-containing unsaturated compound is less than 1% by weight, the introduction rate of the unsaturated isocyanate compound into the polymer (a4) tends to decrease, and the sensitivity tends to decrease. On the other hand, when it exceeds 50% by weight, the storage stability of the polymer obtained by the reaction with the (a4) unsaturated isocyanate compound tends to be lowered.
一方、上記(a3) (a1)、(a2)以外のラジカル重合性化合物は特に限定はしないが、
化合物(a3)としては、例えば、
メチルアクリレート、エチルアクリレート、n−プロピルアクリレート、i−プロピルアクリレート、n−ブチルアクリレート、i−ブチルアクリレート、sec−ブチルアクリレート、t−ブチルアクリレートなどのアクリル酸アルキルエステル;メチルメタクリレート、エチルメタクリレート、n−プロピルメタクリレート、i−プロピルメタクリレート、n−ブチルメタクリレート、i−ブチルメタクリレート、sec−ブチルメタクリレート、t−ブチルメタクリレートなどのメタクリル酸アルキルエステル;シクロヘキシルアクリレート、2−メチルシクロヘキシルアクリレート、トリシクロ[5.2.1.02,6]デカン−8−イルアクリレート(以下、「トリシクロ[5.2.1.02,6]デカン−8−イル」を「ジシクロペンタニル」という。)、2−ジシクロペンタニルオキシエチルアクリレート、イソボロニルアクリレート、テトラヒドロフリルアクリレートなどのアクリル酸の脂環族エステル;シクロヘキシルメタクリレート、2−メチルシクロヘキシルメタクリレート、ジシクロペンタニルメタクリレート、2−ジシクロペンタニルオキシエチルメタクリレート、イソボロニルメタクリレート、テトラヒドロフリルメタクリレートなどのメタクリル酸の脂環族エステル;フェニルアクリレート、ベンジルアクリレートなどのアクリル酸アリールエステル;フェニルメタクリレート、ベンジルメタクリレートなどのメタクリル酸アリールエステル;マレイン酸ジエチル、フマル酸ジエチル、イタコン酸ジエチルなどのジカルボン酸ジエステル;2−ヒドロキシエチルアクリレート、2−ヒドロキシプロピルアクリレートなどのアクリル酸ヒドロキシアルキルエステル;2−ヒドロキシエチルメタクリレート、2−ヒドロキシプロピルメタクリレートなどのメタクリル酸ヒドロキシアルキルエステル;スチレン、α−メチルスチレン、m−メチルスチレン、p−メチルスチレン、p−メトキシスチレンなどの芳香族ビニル化合物や、アクリロニトリル、メタクリロニトリル、塩化ビニル、塩化ビニリデン、アクリルアミド、メタクリルアミド、酢酸ビニル、1,3−ブタジエン、イソプレン、2,3−ジメチル−1,3−ブタジエン、N−シクロヘキシルマレイミド、N−フェニルマレイミド、N−ベンジルマレイミド、N−スクシンイミジル−3−マレイミドベンゾエート、N−スクシンイミジル−4−マレイミドブチレート、N−スクシンイミジル−6−マレイミドカプロエート、N−スクシンイミジル−3−マレイミドプロピオネート、N−(9−アクリジニル)マレイミドなどを挙げることができる。
On the other hand, radically polymerizable compounds other than the above (a3) (a1) and (a2) are not particularly limited,
As the compound (a3), for example,
Alkyl acrylates such as methyl acrylate, ethyl acrylate, n-propyl acrylate, i-propyl acrylate, n-butyl acrylate, i-butyl acrylate, sec-butyl acrylate, t-butyl acrylate; methyl methacrylate, ethyl methacrylate, n- Methacrylic acid alkyl esters such as propyl methacrylate, i-propyl methacrylate, n-butyl methacrylate, i-butyl methacrylate, sec-butyl methacrylate, t-butyl methacrylate; cyclohexyl acrylate, 2-methylcyclohexyl acrylate, tricyclo [5.2.1 .0 2,6] decan-8-yl acrylate (hereinafter, the "tricyclo [5.2.1.0 2,6] decan-8-yl,""dicyanamide Clopentanyl ”), alicyclic esters of acrylic acid such as 2-dicyclopentanyloxyethyl acrylate, isobornyl acrylate, tetrahydrofuryl acrylate; cyclohexyl methacrylate, 2-methylcyclohexyl methacrylate, dicyclopentanyl methacrylate, 2 -Alicyclic esters of methacrylic acid such as dicyclopentanyloxyethyl methacrylate, isobornyl methacrylate, and tetrahydrofuryl methacrylate; aryl esters of acrylic acid such as phenyl acrylate and benzyl acrylate; aryl esters of methacrylic acid such as phenyl methacrylate and benzyl methacrylate Dicarboxylic acid diesters such as diethyl maleate, diethyl fumarate and diethyl itaconate; Acrylic acid hydroxyalkyl esters such as loxyethyl acrylate and 2-hydroxypropyl acrylate; Methacrylic acid hydroxyalkyl esters such as 2-hydroxyethyl methacrylate and 2-hydroxypropyl methacrylate; Styrene, α-methylstyrene, m-methylstyrene, p- Aromatic vinyl compounds such as methylstyrene and p-methoxystyrene, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, acrylamide, methacrylamide, vinyl acetate, 1,3-butadiene, isoprene, 2,3-dimethyl-1 , 3-butadiene, N-cyclohexylmaleimide, N-phenylmaleimide, N-benzylmaleimide, N-succinimidyl-3-maleimidobenzoate, N-succinimid Examples thereof include dil-4-maleimidobutyrate, N-succinimidyl-6-maleimidocaproate, N-succinimidyl-3-maleimidopropionate, and N- (9-acridinyl) maleimide.
これらの化合物(a3)のうち、2−メチルシクロヘキシルアクリレート、t−ブチルメタクリレート、ジシクロペンタニルメタクリレート、スチレン、p−メトキシスチレン、1,3−ブタジエンなどが、共重合反応性の点から好ましい。
また化合物(a3)のうち、エポキシ基含有重合性不飽和化合物としては、例えば、アクリル酸グリシジル、アクリル酸2−メチルグリシジル、アクリル酸3,4−エポキシブチル、アクリル酸6,7−エポキシヘプチル、アクリル酸3,4−エポキシシクロヘキシル等のアクリル酸エポキシアルキルエステル;メタクリル酸グリシジル、メタクリル酸2−メチルグリシジル、メタクリル酸3,4−エポキシブチル、メタクリル酸6,7−エポキシヘプチル、メタクリル酸3,4−エポキシシクロヘキシル等のメタクリル酸エポキシアルキルエステル;α−エチルアクリル酸グリシジル、α−n−プロピルアクリル酸グリシジル、α−n−ブチルアクリル酸グリシジル、α−エチルアクリル酸6,7−エポキシヘプチル等のα−アルキルアクリル酸エポキシアルキルエステル;o−ビニルベンジルグリシジルエーテル、m−ビニルベンジルグリシジルエーテル、p−ビニルベンジルグリシジルエーテル等のグリシジルエーテルを挙げることができる。
Of these compounds (a3), 2-methylcyclohexyl acrylate, t-butyl methacrylate, dicyclopentanyl methacrylate, styrene, p-methoxystyrene, 1,3-butadiene and the like are preferable from the viewpoint of copolymerization reactivity.
Moreover, as an epoxy-group-containing polymerizable unsaturated compound among compounds (a3), for example, glycidyl acrylate, 2-methylglycidyl acrylate, 3,4-epoxybutyl acrylate, 6,7-epoxyheptyl acrylate, Acrylic acid epoxy alkyl esters such as 3,4-epoxycyclohexyl acrylate; glycidyl methacrylate, 2-methylglycidyl methacrylate, 3,4-epoxybutyl methacrylate, 6,7-epoxyheptyl methacrylate, 3,4 methacrylate -Epoxycyclohexyl and other methacrylic acid epoxy alkyl esters; α-ethyl acrylate glycidyl, α-n-propyl acrylate glycidyl, α-n-butyl acrylate glycidyl, α-ethyl acrylate 6,7-epoxyheptyl and the like -Alkyl acrylic Examples include acid epoxy alkyl esters; glycidyl ethers such as o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, and p-vinylbenzyl glycidyl ether.
また化合物(a3)のうち、オキセタニル基含有重合性不飽和化合物としては、例えば、3−(メタクリロイルオキシメチル)オキセタン、3−(メタクリロイルオキシメチル)−3−エチルオキセタン、3−(メタクリロイルオキシメチル)−2−メチルオキセタン、3−(メタクリロイルオキシメチル)−2−トリフロロメチルオキセタン、3−(メタクリロイルオキシメチル)−2−ペンタフロロエチルオキセタン、3−(メタクリロイルオキシメチル)−2−フェニルオキセタン、3−(メタクリロイルオキシメチル)−2,2−ジフロロオキセタン、3−(メタクリロイルオキシメチル)−2,2,4−トリフロロオキセタン、3−(メタクリロイルオキシメチル)−2,2,4,4−テトラフロロオキセタン、3−(メタクリロイルオキシエチル)オキセタン、3−(メタクリロイルオキシエチル)−3−エチルオキセタン、2−エチル−3−(メタクリロイルオキシエチル)オキセタン、3−(メタクリロイルオキシエチル)−2−トリフロロメチルオキセタン、3−(メタクリロイルオキシエチル)−2−ペンタフロロエチルオキセタン、3−(メタクリロイルオキシエチル)−2−フェニルオキセタン、2,2−ジフロロ−3−(メタクリロイルオキシエチル)オキセタン、3−(メタクリロイルオキシエチル)−2,2,4−トリフロロオキセタン、3−(メタクリロイルオキシエチル)−2,2,4,4−テトラフロロオキセタン、3−(アクリロイルオキシメチル)オキセタン、3−(アクリロイルオキシメチル)−3−エチルオキセタン、3−(アクリロイルオキシメチル)−2−メチルオキセタン、3−(アクリロイルオキシメチル)−2−トリフロロメチルオキセタン、3−(アクリロイルオキシメチル)−2−ペンタフロロエチルオキセタン、3−(アクリロイルオキシメチル)−2−フェニルオキセタン、3−(アクリロイルオキシメチル)−2,2−ジフロロオキセタン、3−(アクリロイルオキシメチル)−2,2,4−トリフロロオキセタン、3−(アクリロイルオキシメチル)−2,2,4,4−テトラフロロオキセタン、3−(アクリロイルオキシエチル)オキセタン、3−(アクリロイルオキシエチル)−3−エチルオキセタン、2−エチル−3−(アクリロイルオキシエチル)オキセタン、3−(アクリロイルオキシエチル)−2−トリフロロメチルオキセタン、3−(アクリロイルオキシエチル)−2−ペンタフロロエチルオキセタン、3−(アクリロイルオキシエチル)−2−フェニルオキセタン、2,2−ジフロロ−3−(アクリロイルオキシエチル)オキセタン、3−(アクリロイルオキシエチル)−2,2,4−トリフロロオキセタン、3−(アクリロイルオキシエチル)−2,2,4,4−テトラフロロオキセタン、2−(メタクリロイルオキシメチル)オキセタン、2−メチル−2−(メタクリロイルオキシメチル)オキセタン、3−メチル−2−(メタクリロイルオキシメチル)オキセタン、4−メチル−2−(メタクリロイルオキシメチル)オキセタン、2−(メタクリロイルオキシメチル)−2−トリフロロメチルオキセタン、2−(メタクリロイルオキシメチル)−3−トリフロロメチルオキセタン、2−(メタクリロイルオキシメチル)−4−トリフロロメチルオキセタン、2−(メタクリロイルオキシメチル)−2−ペンタフロロエチルオキセタン、2−(メタクリロイルオキシメチル)−3−ペンタフロロエチルオキセタン、2−(メタクリロイルオキシメチル)−4−ペンタフロロエチルオキセタン、2−(メタクリロイルオキシメチル)−2−フェニルオキセタン、2−(メタクリロイルオキシメチル)−3−フェニルオキセタン、2−(メタクリロイルオキシメチル)−4−フェニルオキセタン、2,3−ジフロロ−2−(メタクリロイルオキシメチル)オキセタン、2,4−ジフロロ−2−(メタクリロイルオキシメチル)オキセタン、3,3−ジフロロ−2−(メタクリロイルオキシメチル)オキセタン、3,4−ジフロロ−2−(メタクリロイルオキシメチル)オキセタン、4,4−ジフロロ−2−(メタクリロイルオキシメチル)オキセタン、2−(メタクリロイルオキシメチル)−3,3,4−トリフロロオキセタン、2−(メタクリロイルオキシメチル)−3,4,4−トリフロロオキセタン、2−(メタクリロイルオキシメチル)−3,3,4,4−テトラフロロオキセタン、
2−(メタクリロイルオキシエチル)オキセタン、2−(2−(2−メチルオキセタニル))エチルメタクリレート、2−(2−(3−メチルオキセタニル))エチルメタクリレート、2−(メタクリロイルオキシエチル)−2−メチルオキセタン、2−(メタクリロイルオキシエチル)−4−メチルオキセタン、2−(メタクリロイルオキシエチル)−2−トリフロロメチルオキセタン、2−(メタクリロイルオキシエチル)−3−トリフロロメチルオキセタン、2−(メタクリロイルオキシエチル)−4−トリフロロメチルオキセタン、2−(メタクリロイルオキシエチル)−2−ペンタフロロエチルオキセタン、2−(メタクリロイルオキシエチル)−3−ペンタフロロエチルオキセタン、2−(メタクリロイルオキシエチル)−4−ペンタフロロエチルオキセタン、2−(メタクリロイルオキシエチル)−2−フェニルオキセタン、2−(メタクリロイルオキシエチル)−3−フェニルオキセタン、2−(メタクリロイルオキシエチル)−4−フェニルオキセタン、2,3−ジフロロ−2−(メタクリロイルオキシエチル)オキセタン、2,4−ジフロロ−2−(メタクリロイルオキシエチル)オキセタン、3,3−ジフロロ−2−(メタクリロイルオキシエチル)オキセタン、3,4−ジフロロ−2−(メタクリロイルオキシエチル)オキセタン、4,4−ジフロロ−2−(メタクリロイルオキシエチル)オキセタン、2−(メタクリロイルオキシエチル)−3,3,4−トリフロロオキセタン、2−(メタクリロイルオキシエチル)−3,4,4−トリフロロオキセタン、2−(メタクリロイルオキシエチル)−3,3,4,4−テトラフロロオキセタン、2−(アクリロイルオキシメチル)オキセタン、2−メチル−2−(アクリロイルオキシメチル)オキセタン、3−メチル−2−(アクリロイルオキシメチル)オキセタン、4−メチル−2−(アクリロイルオキシメチル)オキセタン、2−(アクリロイルオキシメチル)−2−トリフロロメチルオキセタン、2−(アクリロイルオキシメチル)−3−トリフロロメチルオキセタン、2−(アクリロイルオキシメチル)−4−トリフロロメチルオキセタン、2−(アクリロイルオキシメチル)−2−ペンタフロロエチルオキセタン、2−(アクリロイルオキシメチル)−3−ペンタフロロエチルオキセタン、2−(アクリロイルオキシメチル)−4−ペンタフロロエチルオキセタン、2−(アクリロイルオキシメチル)−2−フェニルオキセタン、2−(アクリロイルオキシメチル)−3−フェニルオキセタン、2−(アクリロイルオキシメチル)−4−フェニルオキセタン、2,3−ジフロロ−2−(アクリロイルオキシメチル)オキセタン、2,4−ジフロロ−2−(アクリロイルオキシメチル)オキセタン、3,3−ジフロロ−2−(アクリロイルオキシメチル)オキセタン、3,4−ジフロロ−2−(アクリロイルオキシメチル)オキセタン、4,4−ジフロロ−2−(アクリロイルオキシメチル)オキセタン、2−(アクリロイルオキシメチル)−3,3,4−トリフロロオキセタン、2−(アクリロイルオキシメチル)−3,4,4−トリフロロオキセタン、2−(アクリロイルオキシメチル)−3,3,4,4−テトラフロロオキセタン、2−(アクリロイルオキシエチル)オキセタン、2−(2−(2−メチルオキセタニル))エチルメタクリレート、2−(2−(3−メチルオキセタニル))エチルメタクリレート、2−(アクリロイルオキシエチル)−2−メチルオキセタン、2−(アクリロイルオキシエチル)−4−メチルオキセタン、2−(アクリロイルオキシエチル)−2−トリフロロメチルオキセタン、2−(アクリロイルオキシエチル)−3−トリフロロメチルオキセタン、2−(アクリロイルオキシエチル)−4−トリフロロメチルオキセタン、2−(アクリロイルオキシエチル)−2−ペンタフロロエチルオキセタン、2−(アクリロイルオキシエチル)−3−ペンタフロロエチルオキセタン、2−(アクリロイルオキシエチル)−4−ペンタフロロエチルオキセタン、2−(アクリロイルオキシエチル)−2−フェニルオキセタン、2−(アクリロイルオキシエチル)−3−フェニルオキセタン、2−(アクリロイルオキシエチル)−4−フェニルオキセタン、2,3−ジフロロ−2−(アクリロイルオキシエチル)オキセタン、2,4−ジフロロ−2−(アクリロイルオキシエチル)オキセタン、3,3−ジフロロ−2−(アクリロイルオキシエチル)オキセタン、3,4−ジフロロ−2−(アクリロイルオキシエチル)オキセタン、4,4−ジフロロ−2−(アクリロイルオキシエチル)オキセタン、2−(アクリロイルオキシエチル)−3,3,4−トリフロロオキセタン、2−(アクリロイルオキシエチル)−3,4,4−トリフロロオキセタン、2−(アクリロイルオキシエチル)−3,3,4,4−テトラフロロオキセタン等の(メタ)アクリル酸エステルが挙げられる。
Among the compounds (a3), examples of the oxetanyl group-containing polymerizable unsaturated compound include 3- (methacryloyloxymethyl) oxetane, 3- (methacryloyloxymethyl) -3-ethyloxetane, and 3- (methacryloyloxymethyl). 2-methyloxetane, 3- (methacryloyloxymethyl) -2-trifluoromethyloxetane, 3- (methacryloyloxymethyl) -2-pentafluoroethyloxetane, 3- (methacryloyloxymethyl) -2-phenyloxetane, 3 -(Methacryloyloxymethyl) -2,2-difluorooxetane, 3- (methacryloyloxymethyl) -2,2,4-trifluorooxetane, 3- (methacryloyloxymethyl) -2,2,4,4-tetra Fluoroxetane, 3- (methacrylo Ruoxyethyl) oxetane, 3- (methacryloyloxyethyl) -3-ethyloxetane, 2-ethyl-3- (methacryloyloxyethyl) oxetane, 3- (methacryloyloxyethyl) -2-trifluoromethyloxetane, 3- (methacryloyloxy) Ethyl) -2-pentafluoroethyloxetane, 3- (methacryloyloxyethyl) -2-phenyloxetane, 2,2-difluoro-3- (methacryloyloxyethyl) oxetane, 3- (methacryloyloxyethyl) -2,2, 4-trifluorooxetane, 3- (methacryloyloxyethyl) -2,2,4,4-tetrafluorooxetane, 3- (acryloyloxymethyl) oxetane, 3- (acryloyloxymethyl) -3-ethyloxetane, 3- (Acry Yloxymethyl) -2-methyloxetane, 3- (acryloyloxymethyl) -2-trifluoromethyloxetane, 3- (acryloyloxymethyl) -2-pentafluoroethyloxetane, 3- (acryloyloxymethyl) -2- Phenyloxetane, 3- (acryloyloxymethyl) -2,2-difluorooxetane, 3- (acryloyloxymethyl) -2,2,4-trifluorooxetane, 3- (acryloyloxymethyl) -2,2,4 , 4-tetrafluorooxetane, 3- (acryloyloxyethyl) oxetane, 3- (acryloyloxyethyl) -3-ethyloxetane, 2-ethyl-3- (acryloyloxyethyl) oxetane, 3- (acryloyloxyethyl)- 2-trifluoromethyloxetane, 3- ( (Acryloyloxyethyl) -2-pentafluoroethyloxetane, 3- (acryloyloxyethyl) -2-phenyloxetane, 2,2-difluoro-3- (acryloyloxyethyl) oxetane, 3- (acryloyloxyethyl) -2, 2,4-trifluorooxetane, 3- (acryloyloxyethyl) -2,2,4,4-tetrafluorooxetane, 2- (methacryloyloxymethyl) oxetane, 2-methyl-2- (methacryloyloxymethyl) oxetane, 3-methyl-2- (methacryloyloxymethyl) oxetane, 4-methyl-2- (methacryloyloxymethyl) oxetane, 2- (methacryloyloxymethyl) -2-trifluoromethyloxetane, 2- (methacryloyloxymethyl) -3 -Trifluoromethyl Oxetane, 2- (methacryloyloxymethyl) -4-trifluoromethyloxetane, 2- (methacryloyloxymethyl) -2-pentafluoroethyl oxetane, 2- (methacryloyloxymethyl) -3-pentafluoroethyloxetane, 2- ( Methacryloyloxymethyl) -4-pentafluoroethyloxetane, 2- (methacryloyloxymethyl) -2-phenyloxetane, 2- (methacryloyloxymethyl) -3-phenyloxetane, 2- (methacryloyloxymethyl) -4-phenyloxetane 2,3-difluoro-2- (methacryloyloxymethyl) oxetane, 2,4-difluoro-2- (methacryloyloxymethyl) oxetane, 3,3-difluoro-2- (methacryloyloxymethyl) oxetane, 3, 4-difluoro-2- (methacryloyloxymethyl) oxetane, 4,4-difluoro-2- (methacryloyloxymethyl) oxetane, 2- (methacryloyloxymethyl) -3,3,4-trifluorooxetane, 2- (methacryloyl) Oxymethyl) -3,4,4-trifluorooxetane, 2- (methacryloyloxymethyl) -3,3,4,4-tetrafluorooxetane,
2- (methacryloyloxyethyl) oxetane, 2- (2- (2-methyloxetanyl)) ethyl methacrylate, 2- (2- (3-methyloxetanyl)) ethyl methacrylate, 2- (methacryloyloxyethyl) -2-methyl Oxetane, 2- (methacryloyloxyethyl) -4-methyloxetane, 2- (methacryloyloxyethyl) -2-trifluoromethyloxetane, 2- (methacryloyloxyethyl) -3-trifluoromethyloxetane, 2- (methacryloyloxy) Ethyl) -4-trifluoromethyloxetane, 2- (methacryloyloxyethyl) -2-pentafluoroethyloxetane, 2- (methacryloyloxyethyl) -3-pentafluoroethyloxetane, 2- (methacryloyloxyethyl) -4- N-tafluoroethyloxetane, 2- (methacryloyloxyethyl) -2-phenyloxetane, 2- (methacryloyloxyethyl) -3-phenyloxetane, 2- (methacryloyloxyethyl) -4-phenyloxetane, 2,3-difluoro- 2- (methacryloyloxyethyl) oxetane, 2,4-difluoro-2- (methacryloyloxyethyl) oxetane, 3,3-difluoro-2- (methacryloyloxyethyl) oxetane, 3,4-difluoro-2- (methacryloyloxy) Ethyl) oxetane, 4,4-difluoro-2- (methacryloyloxyethyl) oxetane, 2- (methacryloyloxyethyl) -3,3,4-trifluorooxetane, 2- (methacryloyloxyethyl) -3,4,4 -Trifluorooxeta 2- (methacryloyloxyethyl) -3,3,4,4-tetrafluorooxetane, 2- (acryloyloxymethyl) oxetane, 2-methyl-2- (acryloyloxymethyl) oxetane, 3-methyl-2- ( (Acryloyloxymethyl) oxetane, 4-methyl-2- (acryloyloxymethyl) oxetane, 2- (acryloyloxymethyl) -2-trifluoromethyloxetane, 2- (acryloyloxymethyl) -3-trifluoromethyloxetane, 2 -(Acryloyloxymethyl) -4-trifluoromethyloxetane, 2- (acryloyloxymethyl) -2-pentafluoroethyloxetane, 2- (acryloyloxymethyl) -3-pentafluoroethyloxetane, 2- (acryloyloxymethyl) ) -4-Pen Tafluoroethyloxetane, 2- (acryloyloxymethyl) -2-phenyloxetane, 2- (acryloyloxymethyl) -3-phenyloxetane, 2- (acryloyloxymethyl) -4-phenyloxetane, 2,3-difluoro- 2- (acryloyloxymethyl) oxetane, 2,4-difluoro-2- (acryloyloxymethyl) oxetane, 3,3-difluoro-2- (acryloyloxymethyl) oxetane, 3,4-difluoro-2- (acryloyloxy) Methyl) oxetane, 4,4-difluoro-2- (acryloyloxymethyl) oxetane, 2- (acryloyloxymethyl) -3,3,4-trifluorooxetane, 2- (acryloyloxymethyl) -3,4,4 -Trifluorooxetane, 2- (acryloyl Cymethyl) -3,3,4,4-tetrafluorooxetane, 2- (acryloyloxyethyl) oxetane, 2- (2- (2-methyloxetanyl)) ethyl methacrylate, 2- (2- (3-methyloxetanyl) ) Ethyl methacrylate, 2- (acryloyloxyethyl) -2-methyloxetane, 2- (acryloyloxyethyl) -4-methyloxetane, 2- (acryloyloxyethyl) -2-trifluoromethyloxetane, 2- (acryloyloxy) Ethyl) -3-trifluoromethyloxetane, 2- (acryloyloxyethyl) -4-trifluoromethyloxetane, 2- (acryloyloxyethyl) -2-pentafluoroethyloxetane, 2- (acryloyloxyethyl) -3- Pentafluoroethyl oxetane, 2 (Acryloyloxyethyl) -4-pentafluoroethyloxetane, 2- (acryloyloxyethyl) -2-phenyloxetane, 2- (acryloyloxyethyl) -3-phenyloxetane, 2- (acryloyloxyethyl) -4-phenyl Oxetane, 2,3-difluoro-2- (acryloyloxyethyl) oxetane, 2,4-difluoro-2- (acryloyloxyethyl) oxetane, 3,3-difluoro-2- (acryloyloxyethyl) oxetane, 3,4 -Difluoro-2- (acryloyloxyethyl) oxetane, 4,4-difluoro-2- (acryloyloxyethyl) oxetane, 2- (acryloyloxyethyl) -3,3,4-trifluorooxetane, 2- (acryloyloxy) Ethyl) -3,4,4-tri And (meth) acrylic acid esters such as fluorooxetane and 2- (acryloyloxyethyl) -3,3,4,4-tetrafluorooxetane.
これらのうち、3−(メタクリロイルオキシメチル)オキセタン、3−(メタクリロイルオキシメチル)−2−トリフロロメチルオキセタン、3−(メタクリロイルオキシメチル)−2−フェニルオキセタン、2−(メタクリロイルオキシメチル)オキセタン、2−(メタクリロイルオキシメチル)−4−トリフロロメチルオキセタンなどが得られる感光性樹脂組成物のプロセスマージンが広く、かつ、得られるスペーサーの耐薬品性を高める点から好ましく用いられる。
上記化合物(a3)は、単独でまたは2種以上を混合して使用することができる。
Among these, 3- (methacryloyloxymethyl) oxetane, 3- (methacryloyloxymethyl) -2-trifluoromethyloxetane, 3- (methacryloyloxymethyl) -2-phenyloxetane, 2- (methacryloyloxymethyl) oxetane, The photosensitive resin composition from which 2- (methacryloyloxymethyl) -4-trifluoromethyloxetane and the like are obtained has a wide process margin and is preferably used from the viewpoint of enhancing the chemical resistance of the resulting spacer.
The said compound (a3) can be used individually or in mixture of 2 or more types.
共重合体〔α〕において、(a3)他の不飽和化合物に由来する繰り返し単位の含有率は、共重合体〔α〕に基いて、好ましくは20〜80重量%、特に好ましくは30〜70重量%である。(a3)他の不飽和化合物に由来する繰り返し単位の含有率が20重量%未満では、(a4)との反応により得られる重合体の保存安定性が低下する傾向があり、一方80重量%を超えると、該重合体のアルカリ現像液に対する溶解性が低下する傾向がある。また、(メタ)アクリル酸エポキシ(シクロ)アルキルエステル類を使用する時は、含有率10重量%以下が好ましく、10重量%以上では、保存安定性が低下する傾向がある。 In the copolymer [α], the content of repeating units derived from (a3) other unsaturated compounds is preferably 20 to 80% by weight, particularly preferably 30 to 70%, based on the copolymer [α]. % By weight. (A3) If the content of repeating units derived from other unsaturated compounds is less than 20% by weight, the storage stability of the polymer obtained by the reaction with (a4) tends to decrease, while 80% by weight When it exceeds, there exists a tendency for the solubility with respect to the alkali developing solution of this polymer to fall. Further, when (meth) acrylic acid epoxy (cyclo) alkyl esters are used, the content is preferably 10% by weight or less, and if it is 10% by weight or more, the storage stability tends to decrease.
共重合体〔α〕を多段階重合により製造する場合、第1共重合体が占める割合((第1共重合体重量/共重合体〔α〕)×100)は、好ましくは30〜95%、特に好ましくは、50〜90%である。30%より低い場合は、重合反応が十分に進行しない場合があり、また電気特性が低下したり、現像性、強靭性が低下する場合があり好ましくない。また、95%より大きい場合は、追添成分の性能が十分に発揮できず好ましくない。 When the copolymer [α] is produced by multistage polymerization, the proportion of the first copolymer ((weight of the first copolymer / copolymer [α]) × 100) is preferably 30 to 95%. Especially preferably, it is 50 to 90%. If it is lower than 30%, the polymerization reaction may not proceed sufficiently, and electrical characteristics may deteriorate, developability and toughness may decrease, which is not preferable. On the other hand, if it is larger than 95%, the performance of the additional component cannot be sufficiently exhibited, which is not preferable.
本発明で用いられる共重合体〔α〕は、ゲルパーミエーションクロマトグラフィーで測定したポリスチレン換算重量平均分子量(以下、「Mw」という)は、好ましくは、2×103〜1×105、より好ましくは5×103〜5×104である。Mwが2×103未満であると、現像マージンが十分ではなくなる場合があり、得られる被膜の残膜率などが低下したり、また得られるスペーサーのパターン形状、耐熱性などに劣ることがある。一方、Mwが1×105を超えると、感度が低下したりパターン形状に劣ることがある。 The copolymer [α] used in the present invention preferably has a polystyrene-equivalent weight average molecular weight (hereinafter referred to as “Mw”) measured by gel permeation chromatography, preferably 2 × 10 3 to 1 × 10 5 . Preferably it is 5 * 10 < 3 > -5 * 10 < 4 >. If the Mw is less than 2 × 10 3 , the development margin may not be sufficient, and the remaining film ratio of the resulting film may decrease, or the pattern shape of the resulting spacer, heat resistance, etc. may be inferior. . On the other hand, if Mw exceeds 1 × 10 5 , the sensitivity may decrease or the pattern shape may be inferior.
さらに、本発明で用いられる〔A〕光重合性不飽和基を有する共重合体のゲルパーミエーションクロマトグラフィーで測定した残留モノマー量は、好ましくは5.0%未満、より好ましくは3.0%未満、特に好ましくは2.0%未満である。
本発明における〔A〕共重合体は、共重合体〔α〕に、(a4)少なくとも1個のエチレン性不飽和基と、イソシアネート基、エポキシ基等の1個の官能基を有する化合物を反応させることにより得られるものである。
Further, the residual monomer amount measured by gel permeation chromatography of the copolymer having a photopolymerizable unsaturated group [A] used in the present invention is preferably less than 5.0%, more preferably 3.0%. Less than, particularly preferably less than 2.0%.
In the present invention, the copolymer [A] is obtained by reacting the copolymer [α] with (a4) a compound having at least one ethylenically unsaturated group and one functional group such as an isocyanate group or an epoxy group. It is obtained by making it.
(a4)少なくとも1個のエチレン性不飽和基と、イソシアネート基、エポキシ基等の1個の官能基を有する化合物は特に限定はしないが、
イソシアネート基含有不飽和化合物としては、例えば、
2−アクリロイルオキシエチルイソシアネート、3−アクリロイルオキシプロピルイソシアネート、4−アクリロイルオキシブチルイソシアネート、6−アクリロイルオキシヘキシルイソシアネート、8−アクリロイルオキシオクチルイソシアネート、10−アクリロイルオキシデシルイソシアネート、1,1−(ビスアクリロイルオキシメチル)エチルイソシアネートの如きアクリル酸誘導体;
2−メタクリロイルオキシエチルイソシアネート、3−メタクリロイルオキシプロピルイソシアネート、4−メタクリロイルオキシブチルイソシアネート、6−メタクリロイルオキシヘキシルイソシアネート、8−メタクリロイルオキシオクチルイソシアネート、10−メタクリロイルオキシデシルイソシアネート、1,1−(ビスメタクリロイルオキシメチル)エチルイソシアネートの如きメタクリル酸誘導体
を挙げることができる。
(A4) The compound having at least one ethylenically unsaturated group and one functional group such as an isocyanate group or an epoxy group is not particularly limited.
As an isocyanate group-containing unsaturated compound, for example,
2-acryloyloxyethyl isocyanate, 3-acryloyloxypropyl isocyanate, 4-acryloyloxybutyl isocyanate, 6-acryloyloxyhexyl isocyanate, 8-acryloyloxyoctyl isocyanate, 10-acryloyloxydecyl isocyanate, 1,1- (bisacryloyloxy Acrylic acid derivatives such as methyl) ethyl isocyanate;
2-methacryloyloxyethyl isocyanate, 3-methacryloyloxypropyl isocyanate, 4-methacryloyloxybutyl isocyanate, 6-methacryloyloxyhexyl isocyanate, 8-methacryloyloxyoctyl isocyanate, 10-methacryloyloxydecyl isocyanate, 1,1- (bismethacryloyloxy Mention may be made of methacrylic acid derivatives such as methyl) ethyl isocyanate.
また、2−アクリロイルオキシエチルイソシアネートの市販品としては、商品名で、カレンズAOI(昭和電工(株)製)、2−メタクリロイルオキシエチルイソシアネートの市販品としては、商品名で、カレンズMOI(昭和電工(株)製)、1,1−(ビスアクリロイルオキシメチル)エチルイソシアネートの市販品としては、商品名で、カレンズBEI(昭和電工(株)製)を挙げることができる。
これらの不飽和イソシアナート化合物のうち、共重合体〔α〕との反応性の点から、2−アクリロイルオキシエチルイソシアネート、2−メタクリロイルオキシエチルイソシアネート等が好ましい。
Moreover, as a commercial item of 2-acryloyloxyethyl isocyanate, it is a brand name, Karenz AOI (made by Showa Denko KK), and as a commercial item of 2-methacryloyloxyethyl isocyanate, it is a brand name, Karenz MOI (Showa Denko). As a commercially available product of 1,1- (bisacryloyloxymethyl) ethyl isocyanate, Karenz BEI (manufactured by Showa Denko KK) can be mentioned as a commercial name.
Of these unsaturated isocyanate compounds, 2-acryloyloxyethyl isocyanate, 2-methacryloyloxyethyl isocyanate, and the like are preferable from the viewpoint of reactivity with the copolymer [α].
エポキシ基含有重合性不飽和化合物としては、例えば、
アクリル酸グリシジル、アクリル酸2−メチルグリシジル、4−ヒドロキシブチルアクリレートグリシジルエーテル、アクリル酸3,4−エポキシブチル、アクリル酸6,7−エポキシヘプチル、アクリル酸3,4−エポキシシクロヘキシル等のアクリル酸エポキシ(シクロ)アルキルエステル;
メタクリル酸グリシジル、メタクリル酸2−メチルグリシジル、メタクリル酸3,4−エポキシブチル、メタクリル酸6,7−エポキシヘプチル、メタクリル酸3,4−エポキシシクロヘキシル等のメタクリル酸エポキシ(シクロ)アルキルエステル;
α−エチルアクリル酸グリシジル、α−n−プロピルアクリル酸グリシジル、α−n−ブチルアクリル酸グリシジル、α−エチルアクリル酸6,7−エポキシヘプチル、α−エチルアクリル酸3,4−エポキシシクロヘキシル等の他のα−アルキルアクリル酸エポキシ(シクロ)アルキルエステル;
o−ビニルベンジルグリシジルエーテル、m−ビニルベンジルグリシジルエーテル、p−ビニルベンジルグリシジルエーテル等のグリシジルエーテル
等を挙げることができる。
As an epoxy group-containing polymerizable unsaturated compound, for example,
Acrylic acid epoxy such as glycidyl acrylate, 2-methylglycidyl acrylate, 4-hydroxybutyl acrylate glycidyl ether, 3,4-epoxybutyl acrylate, 6,7-epoxyheptyl acrylate, 3,4-epoxycyclohexyl acrylate (Cyclo) alkyl esters;
Methacrylic acid epoxy (cyclo) alkyl esters such as glycidyl methacrylate, 2-methylglycidyl methacrylate, 3,4-epoxybutyl methacrylate, 6,7-epoxyheptyl methacrylate, 3,4-epoxycyclohexyl methacrylate;
α-ethyl acrylate glycidyl, α-n-propyl acrylate glycidyl, α-n-butyl acrylate glycidyl, α-ethyl acrylate 6,7-epoxyheptyl, α-ethyl acrylate 3,4-epoxycyclohexyl, etc. Other α-alkyl acrylic acid epoxy (cyclo) alkyl esters;
Examples thereof include glycidyl ethers such as o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, and p-vinylbenzyl glycidyl ether.
これらのエポキシ基含有不飽和化合物のうち、共重合反応性およびスペーサーの強度の点から、メタクリル酸グリシジル、メタクリル酸2−メチルグリシジル、メタクリル酸6,7−エポキシヘプチル、4−ヒドロキシブチルアクリレートグリシジルエーテル、o−ビニルベンジルグリシジルエーテル、m−ビニルベンジルグリシジルエーテル、p−ビニルベンジルグリシジルエーテル等が好ましい。 Among these epoxy group-containing unsaturated compounds, from the viewpoint of copolymerization reactivity and spacer strength, glycidyl methacrylate, 2-methylglycidyl methacrylate, 6,7-epoxyheptyl methacrylate, 4-hydroxybutyl acrylate glycidyl ether O-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, p-vinylbenzyl glycidyl ether, and the like are preferable.
〔A〕重合体において、(a4)少なくとも1個のエチレン性不飽和基と、イソシアネート基、エポキシ基等の1個の官能基を有する化合物は、単独でまたは2種以上を混合して使用することができる。
本発明において、共重合体〔α〕とイソシアネート基含有不飽和化合物との反応は、例えば、ジラウリン酸ジ−n−ブチルすず(IV)等の触媒やp−メトキシフェノール等の重合禁止剤を含む共重合体〔α〕溶液に、室温または加温下で、攪拌しつつ、イソシアネート基含有不飽和化合物を投入することによって実施することができる。
[A] In the polymer, (a4) the compound having at least one ethylenically unsaturated group and one functional group such as an isocyanate group or an epoxy group is used alone or in admixture of two or more. be able to.
In the present invention, the reaction between the copolymer [α] and the isocyanate group-containing unsaturated compound includes, for example, a catalyst such as di-n-butyltin (IV) dilaurate and a polymerization inhibitor such as p-methoxyphenol. It can be carried out by adding an isocyanate group-containing unsaturated compound to the copolymer [α] solution while stirring at room temperature or under heating.
〔A〕重合体を製造する際のイソシアネート基含有不飽和化合物の使用量は、共重合体〔α〕中の(a2)水酸基含有不飽和化合物に由来する重合単位に対して、好ましくは0.1〜90重量%、さらに好ましくは10〜80重量%、特に好ましくは25〜75重量%である。不飽和イソシアナート化合物の使用量が0.1重量%未満では、感度ならびに弾性特性向上への効果が小さく、一方90重量%を超えると、未反応のイソシアネート基含有不飽和化合物が残存し、得られる重合体溶液や感放射線性樹脂組成物の保存安定性が低下する傾向がある。 [A] The amount of the isocyanate group-containing unsaturated compound used in the production of the polymer is preferably 0.00 relative to the polymer unit derived from the (a2) hydroxyl group-containing unsaturated compound in the copolymer [α]. 1 to 90% by weight, more preferably 10 to 80% by weight, particularly preferably 25 to 75% by weight. When the amount of the unsaturated isocyanate compound used is less than 0.1% by weight, the effect of improving the sensitivity and the elastic properties is small. On the other hand, when the amount exceeds 90% by weight, an unreacted isocyanate group-containing unsaturated compound remains and is obtained. The storage stability of the obtained polymer solution and radiation sensitive resin composition tends to be lowered.
共重合体〔α〕とエポキシ基含有不飽和化合物との反応は、例えば、テトラブチルアンモニウムブロマイド等の触媒やp−メトキシフェノール等の重合禁止剤を含む共重合体〔α〕溶液に、加温下で、攪拌しつつ、エポキシ基含有不飽和化合物を投入することによって実施することができる。 The reaction between the copolymer [α] and the epoxy group-containing unsaturated compound is carried out, for example, by heating the copolymer [α] solution containing a catalyst such as tetrabutylammonium bromide and a polymerization inhibitor such as p-methoxyphenol. Below, it can implement by throwing in an epoxy-group-containing unsaturated compound, stirring.
〔A〕重合体を製造する際のエポキシ基含有不飽和化合物の使用量は、共重合体〔α〕中の(a1)カルボキシル基含有不飽和化合物に由来する重合単位に対して、好ましくは0.1〜90重量%、さらに好ましくは10〜80重量%、特に好ましくは25〜75重量%である。エポキシ基含有不飽和化合物の使用量が0.1重量%未満では、感度ならびに弾性特性向上への効果が小さく、一方90重量%を超えると、未反応のエポキシ基含有不飽和化合物が残存し、得られる重合体溶液や感放射線性樹脂組成物の保存安定性が低下する傾向がある。
上記の共重合体〔A〕を含む感放射線性樹脂組成物は、現像する際に現像残りを生じることなく容易に所定パターン形状を形成することができる。
前記〔A〕光重合性不飽和基を有する共重合体は、単独でまたは2種以上を混合して使用することができる。
また、本発明においては、他のアルカリ可溶性樹脂を1種以上、〔A〕光重合性不飽和基を有する共重合体と併用することもできる。
[A] The amount of the epoxy group-containing unsaturated compound used in the production of the polymer is preferably 0 with respect to the polymer units derived from the (a1) carboxyl group-containing unsaturated compound in the copolymer [α]. 0.1 to 90% by weight, more preferably 10 to 80% by weight, particularly preferably 25 to 75% by weight. If the amount of the epoxy group-containing unsaturated compound used is less than 0.1% by weight, the effect of improving sensitivity and elastic properties is small. On the other hand, if it exceeds 90% by weight, an unreacted epoxy group-containing unsaturated compound remains, The storage stability of the resulting polymer solution and radiation sensitive resin composition tends to decrease.
The radiation-sensitive resin composition containing the copolymer [A] can easily form a predetermined pattern shape without causing a development residue during development.
[A] The copolymer having a photopolymerizable unsaturated group can be used alone or in admixture of two or more.
Moreover, in this invention, 1 or more types of other alkali-soluble resin can also be used together with the copolymer which has [A] photopolymerizable unsaturated group.
〔B〕重合性不飽和化合物
本発明の感放射線性樹脂組成物における〔B〕重合性不飽和化合物としては、2官能以上のアクリレートおよびメタクリレート(以下、「(メタ)アクリレート」という。)が好ましい。
[B] Polymerizable unsaturated compound [B] The polymerizable unsaturated compound in the radiation-sensitive resin composition of the present invention is preferably a bifunctional or higher acrylate and methacrylate (hereinafter referred to as “(meth) acrylate”). .
2官能の(メタ)アクリレートとしては、例えば、エチレングリコールアクリレート、エチレングリコールメタクリレート、1,6−ヘキサンジオールジアクリレート、1,6−ヘキサンジオールジメタクリレート、1,9−ノナンジオールジアクリレート、1,9−ノナンジオールジメタクリレート、テトラエチレングリコールジアクリレート、テトラエチレングリコールジメタクリレート、ポリプロピレングリコールジアクリレート、ポリプロピレングリコールジメタクリレート、ビスフェノキシエタノールフルオレンジアクリレート、ビスフェノキシエタノールフルオレンジメタクリレートなどを挙げることができる。 Examples of the bifunctional (meth) acrylate include ethylene glycol acrylate, ethylene glycol methacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, 1,9-nonanediol diacrylate, 1,9. -Nonanediol dimethacrylate, tetraethylene glycol diacrylate, tetraethylene glycol dimethacrylate, polypropylene glycol diacrylate, polypropylene glycol dimethacrylate, bisphenoxyethanol full orange acrylate, bisphenoxyethanol full orange methacrylate, and the like.
また、2官能の(メタ)アクリレートの市販品としては、例えば、アロニックスM−210、同M−215、同M−220、同M−240、M−260、同M−270、同M−1200、同M−1600、同M−6200(以上、東亞合成(株)製)、KAYARAD HDDA、KAYARAD HX−220、同HX−620、同R−526、同R−167、同R−604、同R−684、同R−551、同R−712、UX−2201、UX−2301、UX−3204、UX−3301、UX−4101、UX−6101、UX−7101、UX−8101、UX−0937、MU−2100、MU−4001(以上、日本化薬(株)製)、アートレジンUN−9000PEP、同UN−9200A、同UN−7600、同UN−333、同UN−1003、同UN−1255、同UN−6060PTM、同UN−6060P(以上、根上工業(株)製)、同SH−500B、ビスコート260、同215、同312、同335HP(以上、大阪有機化学工業(株)製)、ライトアクリレートBEPG−A、同HPP−A、ライトエステルG−201P、エポキシエステル40EM、同70PA、同80MFA、同3002M、同3002A(以上共栄社化学(株)製)、デナコールアクリレートDA−721、同DA−722、DM−201(以上、ナガセケムテックス(株)製)、BMI−70、BMI−80(以上、ケイ・アイ化成(株)製)などを挙げることができる。 Moreover, as a commercial item of bifunctional (meth) acrylate, for example, Aronix M-210, M-215, M-220, M-240, M-260, M-270, M-1200 , M-1600, M-6200 (above, manufactured by Toagosei Co., Ltd.), KAYARAD HDDA, KAYARAD HX-220, HX-620, R-526, R-167, R-604, R-684, R-551, R-712, UX-2201, UX-2301, UX-3204, UX-3301, UX-4101, UX-6101, UX-7101, UX-8101, UX-0937, MU-2100, MU-4001 (manufactured by Nippon Kayaku Co., Ltd.), Art Resin UN-9000PEP, UN-9200A, UN-7600, UN-33 3, UN-1003, UN-1255, UN-6060PTM, UN-6060P (manufactured by Negami Kogyo Co., Ltd.), SH-500B, Biscote 260, 215, 312, 335HP (and above) , Manufactured by Osaka Organic Chemical Industry Co., Ltd.), light acrylate BEPG-A, HPP-A, light ester G-201P, epoxy ester 40EM, 70PA, 80MFA, 3002M, 3002A (Kyoeisha Chemical Co., Ltd.) ), Denacol Acrylate DA-721, DA-722, DM-201 (above, manufactured by Nagase ChemteX Corporation), BMI-70, BMI-80 (above, manufactured by KEI Kasei Co., Ltd.), etc. Can be mentioned.
また、3官能以上の(メタ)アクリレートとしては、例えば、トリメチロールプロパントリアクリレート、トリメチロールプロパントリメタクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールトリメタクリレート、ペンタエリスリトールテトラアクリレート、ペンタエリスリトールテトラメタクリレート、ジペンタエリスリトールペンタアクリレート、ジペンタエリスリトールペンタメタクリレート、ジペンタエリスリトールヘキサアクリレート、ジペンタエリスリトールヘキサメタクリレート、トリ(2−アクリロイロキシエチル)フォスフェート、トリ(2−メタクリロイロキシエチル)フォスフェートや、9官能以上の(メタ)アクリレートとして、直鎖アルキレン基および脂環式構造を有し、かつ2個以上のイソシアネート基を有する化合物と、分子内に1個以上の水酸基を有し、かつ3個、4個あるいは5個のアクリロイロキシ基および/またはメタクリロイロキシ基を有する化合物とを反応させて得られるウレタンアクリレート系化合物などを挙げることができる。 Examples of the tri- or higher functional (meth) acrylate include, for example, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol triacrylate, pentaerythritol trimethacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, dipentaerythritol. Pentaacrylate, dipentaerythritol pentamethacrylate, dipentaerythritol hexaacrylate, dipentaerythritol hexamethacrylate, tri (2-acryloyloxyethyl) phosphate, tri (2-methacryloyloxyethyl) phosphate, (Meth) acrylate has a linear alkylene group and an alicyclic structure, and two or more Urethane acrylate obtained by reacting a compound having an isocyanate group with a compound having one or more hydroxyl groups in the molecule and having 3, 4, or 5 acryloyloxy groups and / or methacryloyloxy groups And the like.
3官能以上の(メタ)アクリレートの市販品としては、例えば、アロニックスM−309、同M−315、同M−350、同M−400、同M−402、同M−405、同M−408、同M−450、同M−1310、同M−1600、同M−1960、同M−7100、同M−8030、同M−8060、同M−8100、同M−8530、同M−8560、同M−9050、アロニックスTO−1450(以上、東亞合成(株)製)、KAYARAD TMPTA、同GPO−303、同DPHA、同DPCA−20、同DPCA−30、同DPCA−60、同DPCA−120、同MAX−3510(以上、日本化薬(株)製)、ビスコート295、同300、同360、同GPT、同3PA、同400(以上、大阪有機化学工業(株)製)や、ウレタンアクリレート系化合物として、ニューフロンティア R−1150、同R−1303、同R−1304、同R−1305、同R−1306、同R−1308(第一工業製薬(株)製)、KAYARAD DPHA−40H、UX−5000(日本化薬(株)製)、UN−9000H(根上工業(株)製)などを挙げることができる。
本発明において、重合性不飽和化合物は、単独でまたは2種以上を混合して使用することができる。
Examples of commercially available trifunctional or higher functional (meth) acrylates include Aronix M-309, M-315, M-350, M-400, M-402, M-405, and M-408. M-450, M-1310, M-1600, M-1960, M-7100, M-8030, M-8060, M-8100, M-8530, M-8530, M-8560 M-9050, Aronix TO-1450 (manufactured by Toagosei Co., Ltd.), KAYARAD TMPTA, GPO-303, DPHA, DPCA-20, DPCA-30, DPCA-60, DPCA- 120, MAX-3510 (above, manufactured by Nippon Kayaku Co., Ltd.), Biscote 295, 300, 360, GPT, 3PA, 400 (above, Osaka Organic Chemical Industries, Ltd.) Manufactured as) and urethane acrylate compounds such as New Frontier R-1150, R-1303, R-1304, R-1305, R-1306, R-1308 (Daiichi Kogyo Seiyaku Co., Ltd.) , KAYARAD DPHA-40H, UX-5000 (manufactured by Nippon Kayaku Co., Ltd.), UN-9000H (manufactured by Negami Kogyo Co., Ltd.), and the like.
In this invention, a polymerizable unsaturated compound can be used individually or in mixture of 2 or more types.
〔C〕感放射線性重合開始剤
〔C〕感放射線性重合開始剤は、放射線に感応して、〔B〕重合性不飽和化合物の重合を開始しうる活性種を生じる成分である。
このような〔C〕感放射線性重合開始剤としては、O−アシルオキシム系化合物、アセトフェノン系化合物、ビイミダゾール系化合物、ベンゾイン系化合物、ベンゾフェノン系化合物、α−ジケトン系化合物、多核キノン系化合物、キサントン系化合物、ホスフィン系化合物、トリアジン系化合物等を挙げることができる。
[C] Radiation-sensitive polymerization initiator [C] The radiation-sensitive polymerization initiator is a component that generates an active species capable of initiating polymerization of the [B] polymerizable unsaturated compound in response to radiation.
Examples of such [C] radiation sensitive polymerization initiators include O-acyloxime compounds, acetophenone compounds, biimidazole compounds, benzoin compounds, benzophenone compounds, α-diketone compounds, polynuclear quinone compounds, Examples include xanthone compounds, phosphine compounds, triazine compounds, and the like.
O−アシルオキシム系化合物としては、9.H.−カルバゾール系のO−アシルオキシム型重合開始剤が好ましい。例えば、1−〔9−エチル−6−ベンゾイル−9.H.−カルバゾール−3−イル〕−ノナン−1,2−ノナン−2−オキシム−O−ベンゾアート、1−〔9−エチル−6−ベンゾイル−9.H.−カルバゾール−3−イル〕−ノナン−1,2−ノナン−2−オキシム−O−アセタート、1−〔9−エチル−6−ベンゾイル−9.H.−カルバゾール−3−イル〕−ペンタン−1,2−ペンタン−2−オキシム−O−アセタート、1−〔9−エチル−6−ベンゾイル−9.H.−カルバゾール−3−イル〕−オクタン−1−オンオキシム−O−アセタート、1−〔9−エチル−6−(2−メチルベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−ベンゾアート、1−〔9−エチル−6−(2−メチルベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−アセタート、1−〔9−エチル−6−(1,3,5−トリメチルベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−ベンゾアート、1−〔9−ブチル−6−(2−エチルベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−ベンゾアート、1−〔9−エチル−6−(2−メチル−4−テトラヒドロピラニルメトキシベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−アセタート、1−〔9−エチル−6−(2−メチル−4−テトラヒドロフラニルメトキシベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−アセタート、エタノン、1−〔9−エチル−6−〔2−メチル−4−(2,2−ジメチル−1,3−ジオキソラニル)メトキシベンゾイル〕−9.H.−カルバゾール−3−イル〕−、1−(O−アセチルオキシム)等を挙げることができる。 As the O-acyloxime compound, 9. H. A carbazole-based O-acyloxime polymerization initiator is preferred. For example, 1- [9-ethyl-6-benzoyl-9. H. -Carbazol-3-yl] -nonane-1,2-nonane-2-oxime-O-benzoate, 1- [9-ethyl-6-benzoyl-9. H. -Carbazol-3-yl] -nonane-1,2-nonane-2-oxime-O-acetate, 1- [9-ethyl-6-benzoyl-9. H. -Carbazol-3-yl] -pentane-1,2-pentane-2-oxime-O-acetate, 1- [9-ethyl-6-benzoyl-9. H. -Carbazol-3-yl] -octane-1-one oxime-O-acetate, 1- [9-ethyl-6- (2-methylbenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-benzoate, 1- [9-ethyl-6- (2-methylbenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-acetate, 1- [9-ethyl-6- (1,3,5-trimethylbenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-benzoate, 1- [9-butyl-6- (2-ethylbenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-benzoate, 1- [9-ethyl-6- (2-methyl-4-tetrahydropyranylmethoxybenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-acetate, 1- [9-ethyl-6- (2-methyl-4-tetrahydrofuranylmethoxybenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-acetate, ethanone, 1- [9-ethyl-6- [2-methyl-4- (2,2-dimethyl-1,3-dioxolanyl) methoxy Benzoyl] -9. H.-Carbazol-3-yl]-, 1- (O-acetyloxime) and the like.
これらのO−アシルオキシム化合物のうち、特に1−〔9−エチル−6−(2−メチルベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−アセタート、
エタノン、1−〔9−エチル−6−〔2−メチル−4−(2,2−ジメチル−1,3−ジオキソラニル)メトキシベンゾイル〕−9.H.−カルバゾール−3−イル〕−、1−(O−アセチルオキシム)が好ましい。
Of these O-acyloxime compounds, 1- [9-ethyl-6- (2-methylbenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-acetate,
Ethanone, 1- [9-ethyl-6- [2-methyl-4- (2,2-dimethyl-1,3-dioxolanyl) methoxybenzoyl] -9. H.-Carbazol-3-yl]-, 1- (O-acetyloxime) is preferred.
前記O−アシルオキシム化合物は、単独でまたは2種以上を混合して使用することができる。本発明において、O−アシルオキシム化合物を用いることにより、1,500J/m2以下の露光量でも十分な感度、密着性を有したスペーサーを得ることを可能にする。
前記アセトフェノン系化合物としては、例えば、α−ヒドロキシケトン系化合物、α−アミノケトン系化合物等を挙げることができる。
The O-acyloxime compounds can be used alone or in admixture of two or more. In the present invention, the use of an O-acyloxime compound makes it possible to obtain a spacer having sufficient sensitivity and adhesion even with an exposure amount of 1,500 J / m 2 or less.
Examples of the acetophenone compound include an α-hydroxyketone compound and an α-aminoketone compound.
前記α−ヒドロキシケトン系化合物としては、例えば、1−フェニル−2−ヒドロキシ−2−メチルプロパン−1−オン、1−(4−i−プロピルフェニル)−2−ヒドロキシ−2−メチルプロパン−1−オン、4−(2−ヒドロキシエトキシ)フェニル−(2−ヒドロキシ−2−プロピル)ケトン、1−ヒドロキシシクロヘキシルフェニルケトン等を挙げることができ、また前記α−アミノケトン系化合物としては、例えば、2−メチル−1−(4−メチルチオフェニル)−2−モルホリノプロパン−1−オン、2−ベンジル−2−ジメチルアミノ−1−(4−モルホリノフェニル)−ブタン−1−オン、2−(4−メチルベンゾイル)−2−(ジメチルアミノ)−1−(4−モルフォリノフェニル)−ブタン−1−オン等を挙げることができる。これら以外の化合物として、例えば、2,2−ジメトキシアセトフェノン、2,2−ジエトキシアセトフェノン、2,2−ジメトキシ−2−フェニルアセトフェノン等を挙げることができる。 Examples of the α-hydroxyketone compound include 1-phenyl-2-hydroxy-2-methylpropan-1-one, 1- (4-i-propylphenyl) -2-hydroxy-2-methylpropane-1 -One, 4- (2-hydroxyethoxy) phenyl- (2-hydroxy-2-propyl) ketone, 1-hydroxycyclohexylphenylketone and the like. Examples of the α-aminoketone compound include 2 -Methyl-1- (4-methylthiophenyl) -2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butan-1-one, 2- (4- And methylbenzoyl) -2- (dimethylamino) -1- (4-morpholinophenyl) -butan-1-one. wear. Examples of compounds other than these include 2,2-dimethoxyacetophenone, 2,2-diethoxyacetophenone, 2,2-dimethoxy-2-phenylacetophenone, and the like.
これらのアセトフェノン系化合物のうち、特に、2−メチル−1−(4−メチルチオフェニル)−2−モルホリノプロパン−1−オン、2−(4−メチルベンゾイル)−2−(ジメチルアミノ)−1−(4−モルフォリノフェニル)−ブタン−1−オンが好ましい。
本発明においては、アセトフェノン系化合物を併用することにより、感度、スペーサー形状や圧縮強度をさらに改善することが可能となる。
Among these acetophenone compounds, 2-methyl-1- (4-methylthiophenyl) -2-morpholinopropan-1-one, 2- (4-methylbenzoyl) -2- (dimethylamino) -1- (4-Morpholinophenyl) -butan-1-one is preferred.
In the present invention, the sensitivity, spacer shape and compressive strength can be further improved by using an acetophenone compound in combination.
また、前記ビイミダゾール系化合物としては、例えば、2,2’−ビス(2−クロロフェニル)−4,4’,5,5’−テトラキス(4−エトキシカルボニルフェニル)−1,2’−ビイミダゾール、2,2’−ビス(2−ブロモフェニル)−4,4’,5,5’−テトラキス(4−エトキシカルボニルフェニル)−1,2’−ビイミダゾール、2,2’−ビス(2−クロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2,4−ジクロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2,4,6−トリクロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2−ブロモフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2,4−ジブロモフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2,4,6−トリブロモフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール等を挙げることができる。 Examples of the biimidazole compound include 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetrakis (4-ethoxycarbonylphenyl) -1,2′-biimidazole. 2,2′-bis (2-bromophenyl) -4,4 ′, 5,5′-tetrakis (4-ethoxycarbonylphenyl) -1,2′-biimidazole, 2,2′-bis (2- Chlorophenyl) -4,4 ′, 5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis (2,4-dichlorophenyl) -4,4 ′, 5,5′-tetraphenyl -1,2'-biimidazole, 2,2'-bis (2,4,6-trichlorophenyl) -4,4 ', 5,5'-tetraphenyl-1,2'-biimidazole, 2,2 '-Bis (2-bromophenyl)- , 4 ′, 5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis (2,4-dibromophenyl) -4,4 ′, 5,5′-tetraphenyl-1, 2'-biimidazole, 2,2'-bis (2,4,6-tribromophenyl) -4,4 ', 5,5'-tetraphenyl-1,2'-biimidazole and the like can be mentioned. .
これらのビイミダゾール系化合物のうち、2,2’−ビス(2−クロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2,4−ジクロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール、2,2’−ビス(2,4,6−トリクロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾール等が好ましく、特に2,2’−ビス(2,4−ジクロロフェニル)−4,4’,5,5’−テトラフェニル−1,2’−ビイミダゾールが好ましい。
本発明においては、ビイミダゾール系化合物を併用することにより、感度、解像度や密着性をさらに改善することが可能となる。
また、ビイミダゾール系化合物を併用する場合、それを増感するため、ジアルキルアミノ基を有する脂肪族系または芳香族系の化合物(以下、「アミノ系増感剤」という。)を添加することができる。
Among these biimidazole compounds, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis (2 , 4-dichlorophenyl) -4,4 ′, 5,5′-tetraphenyl-1,2′-biimidazole, 2,2′-bis (2,4,6-trichlorophenyl) -4,4 ′, 5 , 5′-tetraphenyl-1,2′-biimidazole and the like are preferable, and in particular, 2,2′-bis (2,4-dichlorophenyl) -4,4 ′, 5,5′-tetraphenyl-1,2 ′. -Biimidazole is preferred.
In the present invention, it is possible to further improve sensitivity, resolution and adhesion by using a biimidazole compound in combination.
When a biimidazole compound is used in combination, an aliphatic or aromatic compound having a dialkylamino group (hereinafter referred to as “amino sensitizer”) may be added to sensitize it. it can.
アミノ系増感剤としては、例えば、N−メチルジエタノールアミン、4,4’−ビス(ジメチルアミノ)ベンゾフェノン、4,4’−ビス(ジエチルアミノ)ベンゾフェノン、p−ジメチルアミノ安息香酸エチル、p−ジメチルアミノ安息香酸i−アミル等を挙げることができる。
これらのアミノ系増感剤のうち、特に4,4’−ビス(ジエチルアミノ)ベンゾフェノンが好ましい。
前記アミノ系増感剤は、単独でまたは2種以上を混合して使用することができる。
Examples of amino sensitizers include N-methyldiethanolamine, 4,4′-bis (dimethylamino) benzophenone, 4,4′-bis (diethylamino) benzophenone, ethyl p-dimethylaminobenzoate, p-dimethylamino. Examples include i-amyl benzoate.
Of these amino sensitizers, 4,4′-bis (diethylamino) benzophenone is particularly preferable.
The amino sensitizers can be used alone or in admixture of two or more.
さらに、ビイミダゾール系化合物とアミノ系増感剤とを併用する場合、水素供与化合物として、チオール系化合物を添加することができる。ビイミダゾール系化合物は前記アミノ系増感剤によって増感されて開裂し、イミダゾールラジカルを発生するが、そのままでは高い重合開始能が発現されず、得られるスペーサーが逆テーパ形状のような好ましくない形状となる場合が多い。しかし、ビイミダゾール系化合物とアミノ系増感剤とが共存する系に、チオール系化合物を添加することにより、イミダゾールラジカルにチオール系化合物から水素ラジカルが供与される結果、イミダゾールラジカルが中性のイミダゾールに変換されるとともに、重合開始能の高い硫黄ラジカルを有する成分が発生し、それによりスペーサーの形状をより好ましい順テーパ状にすることができる。 Further, when a biimidazole compound and an amino sensitizer are used in combination, a thiol compound can be added as a hydrogen donor compound. The biimidazole compound is sensitized and cleaved by the amino sensitizer to generate an imidazole radical, but as it is, high polymerization initiating ability is not expressed, and the resulting spacer has an unfavorable shape such as a reverse taper shape. In many cases. However, by adding a thiol compound to a system in which a biimidazole compound and an amino sensitizer coexist, hydrogen radicals are donated from the thiol compound to the imidazole radical, so that the imidazole radical is neutral imidazole. In addition, a component having a sulfur radical having a high polymerization initiating ability is generated, whereby the spacer can have a more preferable forward taper shape.
前記チオール系化合物としては、例えば、2−メルカプトベンゾチアゾール、2−メルカプトベンゾオキサゾール、2−メルカプトベンゾイミダゾール、2−メルカプト−5−メトキシベンゾチアゾール、2−メルカプト−5−メトキシベンゾイミダゾール等の芳香族系化合物;3−メルカプトプロピオン酸、3−メルカプトプロピオン酸メチル、3−メルカプトプロピオン酸エチル、3−メルカプトプロピオン酸オクチル等の脂肪族系モノチオール;3,6−ジオキサ−1,8−オクタンジチオール、ペンタエリストールテトラ(メルカプトアセテート)、ペンタエリストールテトラ(3−メルカプトプロピオネート)等の2官能以上の脂肪族系チオールを挙げることができる。 Examples of the thiol compound include aromatics such as 2-mercaptobenzothiazole, 2-mercaptobenzoxazole, 2-mercaptobenzimidazole, 2-mercapto-5-methoxybenzothiazole, 2-mercapto-5-methoxybenzimidazole. Compounds: aliphatic monothiols such as 3-mercaptopropionic acid, methyl 3-mercaptopropionate, ethyl 3-mercaptopropionate, octyl 3-mercaptopropionate; 3,6-dioxa-1,8-octanedithiol, Bifunctional or higher aliphatic thiols such as pentaerythritol tetra (mercaptoacetate) and pentaerythritol tetra (3-mercaptopropionate) can be exemplified.
これらのチオール系化合物のうち、特に2−メルカプトベンゾチアゾールが好ましい。
また、ビイミダゾール系化合物とアミノ系増感剤とを併用する場合、アミノ系増感剤の添加量は、ビイミダゾール系化合物100重量部に対して、好ましくは0.1〜50重量部、さらに好ましくは1〜20重量部である。アミノ系増感剤の添加量が0.1重量部未満では、感度、解像度や密着性の改善効果が低下する傾向があり、一方50重量部を超えると、得られるスペーサーの形状が損なわれる傾向がある。
また、ビイミダゾール系化合物とアミノ系増感剤とを併用する場合、チオール系化合物の添加量は、ビイミダゾール系化合物100重量部に対して、好ましくは0.1〜50重量部、さらに好ましくは1〜20重量部である。チオール系化合物の添加量が0.1重量部未満では、スペーサーの形状の改善効果が低下したり、膜減りを生じやすくなる傾向があり、一方50重量部を超えると、得られるスペーサーの形状が損なわれる傾向がある。
Of these thiol compounds, 2-mercaptobenzothiazole is particularly preferable.
Further, when the biimidazole compound and the amino sensitizer are used in combination, the addition amount of the amino sensitizer is preferably 0.1 to 50 parts by weight with respect to 100 parts by weight of the biimidazole compound. Preferably it is 1-20 weight part. If the addition amount of the amino sensitizer is less than 0.1 parts by weight, the effect of improving the sensitivity, resolution and adhesion tends to decrease. On the other hand, if it exceeds 50 parts by weight, the shape of the resulting spacer tends to be impaired. There is.
In addition, when a biimidazole compound and an amino sensitizer are used in combination, the addition amount of the thiol compound is preferably 0.1 to 50 parts by weight, more preferably 100 parts by weight of the biimidazole compound. 1 to 20 parts by weight. If the addition amount of the thiol compound is less than 0.1 parts by weight, the effect of improving the spacer shape tends to be reduced or the film tends to be reduced. There is a tendency to be damaged.
さらに、感放射線カチオン重合開始剤としては、オニウム塩として例えばフェニルジアゾニウムテトラフルオロボレート、フェニルジアゾニウムヘキサフルオロホスホネート、フェニルジアゾニウムヘキサフルオロアルセネート、フェニルジアゾニウムトリフルオロメタンスルホナート、フェニルジアゾニウムトリフルオロアセテート、フェニルジアゾニウム−p−トルエンスルホナート、4−メトキシフェニルジアゾニウムテトラフルオロボレート、4−メトキシフェニルジアゾニウムヘキサフルオロホスホネート、4−メトキシフェニルジアゾニウムヘキサフルオロアルセネート、4−メトキシフェニルジアゾニウムトリフルオロメタンスルホナート、4−メトキシフェニルジアゾニウムトリフルオロアセテート、4−メトキシフェニルジアゾニウム−p−トルエンスルホナート、4−ter−ブチルフェニルジアゾニウムテトラフルオロボレート、4−ter−ブチルフェニルジアゾニウムヘキサフルオロホスホネート、4−ter−ブチルフェニルジアゾニウムヘキサフルオロアルセネート、4−ter−ブチルフェニルジアゾニウムトリフルオロメタンスルホナート、4−ter−ブチルフェニルジアゾニウムトリフルオロアセテート、4−ter−ブチルフェニルジアゾニウム−p−トルエンスルホナートなどのジアゾニウム塩; トリフェニルスルホニウムテトラフルオロボレート、トリフェニルスルホニウムヘキサフルオロホスホネート、トリフェニルスルホニウムヘキサフルオロアルセネート、トリフェニルスルホニウムトリフルオロメタンスルホナート、トリフェニルスルホニウムトリフルオロアセテート、トリフェニルスルホニウム−p−トルエンスルホナート、4−メトキシフェニルジフェニルスルホニウムテトラフルオロボレート、4−メトキシフェニルジフェニルスルホニウムヘキサフルオロホスホネート、4−メトキシフェニルジフェニルスルホニウムヘキサフルオロアルセネート、4−メトキシフェニルジフェニルスルホニウムトリフルオロメタンスルホナート、4−メトキシフェニルジフェニルスルホニウムトリフルオロアセテート、4−メトキシフェニルジフェニルスルホニウム−p−トルエンスルホナート、4−フェニルチオフェニルジフェニルテトラフルオロボレート、4−フェニルチオフェニルジフェニルヘキサフルオロホスホネート、4−フェニルチオフェニルジフェニルヘキサフルオロアルセネート、4−フェニルチオフェニルジフェニルトリフルオロメタンスルホナート、4−フェニルチオフェニルジフェニルトリフルオロアセテート、4−フェニルチオフェニルジフェニル−p−トルエンスルホナートなどのスルホニウム塩;
ビス(p−トリル)ヨードニウム テトラキス(ペンタフルオロフェニル)ボレート、(p−トリル)(p−イソプロピルフェニル)ヨードニウム テトラキス(ペンタフルオロフェニル)ボレート等のヨードニウム塩が挙げられる。
Further, as the radiation-sensitive cationic polymerization initiator, onium salts such as phenyldiazonium tetrafluoroborate, phenyldiazonium hexafluorophosphonate, phenyldiazonium hexafluoroarsenate, phenyldiazonium trifluoromethanesulfonate, phenyldiazonium trifluoroacetate, phenyldiazonium- p-toluenesulfonate, 4-methoxyphenyldiazonium tetrafluoroborate, 4-methoxyphenyldiazonium hexafluorophosphonate, 4-methoxyphenyldiazonium hexafluoroarsenate, 4-methoxyphenyldiazonium trifluoromethanesulfonate, 4-methoxyphenyldiazoniumtri Fluoroacetate, 4-methoxyphenyl Azonium-p-toluenesulfonate, 4-ter-butylphenyldiazonium tetrafluoroborate, 4-ter-butylphenyldiazonium hexafluorophosphonate, 4-ter-butylphenyldiazonium hexafluoroarsenate, 4-ter-butylphenyldiazonium trifluoro Diazonium salts such as romethanesulfonate, 4-ter-butylphenyldiazonium trifluoroacetate, 4-ter-butylphenyldiazonium-p-toluenesulfonate; triphenylsulfonium tetrafluoroborate, triphenylsulfonium hexafluorophosphonate, triphenylsulfonium Hexafluoroarsenate, triphenylsulfonium trifluoromethanesulfonate, trif Nylsulfonium trifluoroacetate, triphenylsulfonium-p-toluenesulfonate, 4-methoxyphenyldiphenylsulfonium tetrafluoroborate, 4-methoxyphenyldiphenylsulfonium hexafluorophosphonate, 4-methoxyphenyldiphenylsulfonium hexafluoroarsenate, 4-methoxy Phenyldiphenylsulfonium trifluoromethanesulfonate, 4-methoxyphenyldiphenylsulfonium trifluoroacetate, 4-methoxyphenyldiphenylsulfonium-p-toluenesulfonate, 4-phenylthiophenyldiphenyltetrafluoroborate, 4-phenylthiophenyldiphenylhexafluorophosphonate 4-phenylthiophenyl diphenyl Sa fluoro Arce sulfonate, 4-phenylthiophenyldiphenylsulfonium trifluoromethane sulfonate, 4-phenylthiophenyldiphenylsulfonium trifluoroacetate, sulfonium salts such as 4-phenylthiophenyldiphenylsulfonium -p- toluenesulfonate;
Examples include iodonium salts such as bis (p-tolyl) iodonium tetrakis (pentafluorophenyl) borate and (p-tolyl) (p-isopropylphenyl) iodonium tetrakis (pentafluorophenyl) borate.
また、メタロセン化合物として、(1−6−η−クメン)(η−シクロペンタジエニル)鉄(1+)六フッ化リン酸(1−)等が挙げられる。
これらの感放射線カチオン重合開始剤の市販品としては、例えばジアゾニウム塩であるアデカウルトラセットPP−33(旭電化工業(株)製)、スルホニウム塩であるOPTOMER SP−150、同−170(旭電化工業(株)製)、およびメタロセン化合物であるIrgacure261(チバ・スペシャルティ・ケミカルズ社製)などが挙げられる。
上記の感放射線重合開始剤は、単独で、または2種類以上を混合して使用することができる。
感放射線性樹脂組成物において、他の感放射線重合開始剤の使用割合は、全感放射線重合開始剤100重量部に対して、好ましくは100重量部以下、さらに好ましくは80重量部以下、特に好ましくは60重量部以下である。他の感放射線重合開始剤の使用割合が100重量部を超えると、本発明の所期の効果が損なわれるおそれがある。
Examples of the metallocene compound include (1-6-η-cumene) (η-cyclopentadienyl) iron (1+) hexafluorophosphate (1-).
Commercially available products of these radiation-sensitive cationic polymerization initiators include, for example, Adeka Ultra Set PP-33 (made by Asahi Denka Kogyo Co., Ltd.) which is a diazonium salt, OPTOMER SP-150 and 170 (both Asahi Denka) which are sulfonium salts. Kogyo Co., Ltd.) and Irgacure 261 (Ciba Specialty Chemicals Co., Ltd.), which is a metallocene compound.
Said radiation sensitive polymerization initiator can be used individually or in mixture of 2 or more types.
In the radiation-sensitive resin composition, the use ratio of the other radiation-sensitive polymerization initiator is preferably 100 parts by weight or less, more preferably 80 parts by weight or less, particularly preferably 100 parts by weight of the total radiation-sensitive polymerization initiator. Is 60 parts by weight or less. When the usage-amount of another radiation sensitive polymerization initiator exceeds 100 weight part, there exists a possibility that the desired effect of this invention may be impaired.
任意添加剤
本発明の感放射線性樹脂組成物には、必要に応じて、本発明の効果を損なわない範囲で上記以外の任意添加剤、例えば、接着助剤、界面活性剤、保存安定剤、耐熱性向上剤などを配合することができる。
上記接着助剤は、形成されたスペーサーと基板との接着性を向上させるために使用する成分である。
Optional additives In the radiation-sensitive resin composition of the present invention, if necessary, optional additives other than those described above as long as the effects of the present invention are not impaired, for example, an adhesion assistant, a surfactant, a storage stabilizer, A heat resistance improver can be blended.
The adhesion assistant is a component used for improving the adhesion between the formed spacer and the substrate.
このような接着助剤としては、例えばカルボキシル基、メタクリロイル基、ビニル基、イソシアネート基、エポキシ基などの反応性官能基を有する官能性シランカップリング剤が好ましく、その例としては、トリメトキシシリル安息香酸、γ−メタクリロキシプロピルトリメトキシシラン、ビニルトリアセトキシシラン、ビニルトリメトキシシラン、γ−イソシアナートプロピルトリエトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、β−(3,4−エポキシシクロヘキシル)エチルトリメトキシシランなどを挙げることができる。 As such an adhesion assistant, for example, a functional silane coupling agent having a reactive functional group such as a carboxyl group, a methacryloyl group, a vinyl group, an isocyanate group, and an epoxy group is preferable. Examples thereof include trimethoxysilyl benzoate. Acid, γ-methacryloxypropyltrimethoxysilane, vinyltriacetoxysilane, vinyltrimethoxysilane, γ-isocyanatopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane, β- (3,4-epoxycyclohexyl) Examples thereof include ethyltrimethoxysilane.
これらの接着助剤は、単独でまたは2種以上を混合して使用することができる。
接着助剤の配合量は、〔A〕重合体100重量部に対して、好ましくは20重量部以下、さらに好ましくは15重量部以下である。接着助剤の配合量が20重量部を超えると、現像残りを生じやすくなる傾向がある。
また、上記界面活性剤は、塗布性を向上させるために使用する成分である。
このような界面活性剤としては、例えば、フッ素系界面活性剤、シリコーン系界面活性剤などが好ましい。
These adhesion assistants can be used alone or in admixture of two or more.
The blending amount of the adhesion assistant is preferably 20 parts by weight or less, more preferably 15 parts by weight or less with respect to 100 parts by weight of the [A] polymer. When the blending amount of the adhesion assistant exceeds 20 parts by weight, there is a tendency that development residue is likely to occur.
Moreover, the said surfactant is a component used in order to improve applicability | paintability.
As such a surfactant, for example, a fluorine-based surfactant, a silicone-based surfactant and the like are preferable.
上記フッ素系界面活性剤としては、末端、主鎖および側鎖の少なくともいずれかの部位にフルオロアルキル基および/またはフルオロアルキレン基を有する化合物が好ましく、その例としては、1,1,2,2−テトラフロロ−n−オクチル(1,1,2,2−テトラフロロ−n−プロピル)エーテル、1,1,2,2−テトラフロロ−n−オクチル(n−ヘキシル)エーテル、ヘキサエチレングリコールジ(1,1,2,2,3,3−ヘキサフロロ−n−ペンチル)エーテル、オクタエチレングリコールジ(1,1,2,2−テトラフロロ−n−ブチル)エーテル、ヘキサプロピレングリコールジ(1,1,2,2,3,3−ヘキサフロロ−n−ペンチル)エーテル、オクタプロピレングリコールジ(1,1,2,2−テトラフロロ−n−ブチル)エーテル、パーフロロ−n−ドデカンスルホン酸ナトリウム、1,1,2,2,3,3−ヘキサフロロ−n−デカン、1,1,2,2,8,8,9,9,10,10−デカフロロ−n−ドデカンや、フロロアルキルベンゼンスルホン酸ナトリウム、フロロアルキル燐酸ナトリウム、フロロアルキルカルボン酸ナトリウム、ジグリセリンテトラキス(フロロアルキルポリオキシエチレンエーテル)、フロロアルキルアンモニウムヨージド、フロロアルキルベタイン、他のフロロアルキルポリオキシエチレンエーテル、パーフロロアルキルポリオキシエタノール、パーフロロアルキルアルコキシレート、カルボン酸フロロアルキルエステルなどを挙げることができる。 The fluorine-based surfactant is preferably a compound having a fluoroalkyl group and / or a fluoroalkylene group in at least one of the terminal, main chain and side chain, and examples thereof include 1,1,2,2 -Tetrafluoro-n-octyl (1,1,2,2-tetrafluoro-n-propyl) ether, 1,1,2,2-tetrafluoro-n-octyl (n-hexyl) ether, hexaethylene glycol di (1, 1,2,2,3,3-hexafluoro-n-pentyl) ether, octaethylene glycol di (1,1,2,2-tetrafluoro-n-butyl) ether, hexapropylene glycol di (1,1,2, 2,3,3-hexafluoro-n-pentyl) ether, octapropylene glycol di (1,1,2,2-tetrafluoro-n- Til) ether, sodium perfluoro-n-dodecanesulfonate, 1,1,2,2,3,3-hexafluoro-n-decane, 1,1,2,2,8,8,9,9,10,10 -Decafluoro-n-dodecane, sodium fluoroalkylbenzenesulfonate, sodium fluoroalkylphosphate, sodium fluoroalkylcarboxylate, diglycerin tetrakis (fluoroalkylpolyoxyethylene ether), fluoroalkylammonium iodide, fluoroalkylbetaine, other fluoro Examples thereof include alkyl polyoxyethylene ether, perfluoroalkyl polyoxyethanol, perfluoroalkyl alkoxylate, and carboxylic acid fluoroalkyl ester.
また、フッ素系界面活性剤の市販品としては、例えば、BM−1000、BM−1100(以上、BM CHEMIE社製)、メガファックF142D、同F172、同F173、同F183、同F178、同F191、同F471、同F476(以上、大日本インキ化学工業(株)製)、フロラードFC−170C、同−171、同−430、同−431(以上、住友スリーエム(株)製)、サーフロンS−112、同−113、同−131、同−141、同−145、同−382、サーフロンSC−101、同−102、同−103、同−104、同−105、同−106(以上、旭硝子(株)製)、エフトップEF301、同303、同352(以上、新秋田化成(株)製)、フタージェントFT−100、同−110、同−140A、同−150、同−250、同−251、同−300、同−310、同−400S、フタージェントFTX−218、同−251(以上、(株)ネオス製)などを挙げることができる。 Examples of commercially available fluorosurfactants include BM-1000, BM-1100 (above, manufactured by BM CHEMIE), MegaFuck F142D, F172, F173, F183, F183, F178, F191, F471, F476 (above, Dainippon Ink & Chemicals, Inc.), Florard FC-170C, -171, -430, -431 (above, Sumitomo 3M Limited), Surflon S-112 -113, -131, -141, -145, -382, Surflon SC-101, -102, -103, -104, -105, -106 (above, Asahi Glass ( Co., Ltd.), Ftop EF301, 303, 352 (above, Shin-Akita Kasei Co., Ltd.), Footent FT-100, -110, -140A The -150, the -250, the -251, the -300, the -310, the same -400S, Ftergent FTX-218, the -251 (or more, (Ltd.) NEOS), and the like.
上記シリコーン系界面活性剤としては、例えば、トーレシリコーンDC3PA、同DC7PA、同SH11PA、同SH21PA、同SH28PA、同SH29PA、同SH30PA、同SH−190、同SH−193、同SZ−6032、同SF−8428、同DC−57、同DC−190(以上、東レ・ダウコーニング・シリコーン(株)製)、TSF−4440、TSF−4300、TSF−4445、TSF−4446、TSF−4460、TSF−4452(以上、GE東芝シリコーン(株)製)などの商品名で市販されているものを挙げることができる。 Examples of the silicone-based surfactant include Toray Silicone DC3PA, DC7PA, SH11PA, SH21PA, SH28PA, SH29PA, SH30PA, SH-190, SH-193, SZ-6032, SF -8428, DC-57, DC-190 (above, manufactured by Toray Dow Corning Silicone Co., Ltd.), TSF-4440, TSF-4300, TSF-4445, TSF-4446, TSF-4460, TSF-4442 (The above-mentioned, GE Toshiba Silicone Co., Ltd. product) etc. can be mentioned what is marketed.
また、上記以外の界面活性剤として、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンステアリルエーテル、ポリオキシエチレンオレイルエーテルなどのポリオキシエチレンアルキルエーテル;ポリオキシエチレン−n−オクチルフェニルエーテル、ポリオキシエチレン−n−ノニルフェニルエーテルなどのポリオキシエチレンアリールエーテル;ポリオキシエチレンジラウレート、ポリオキシエチレンジステアレートなどのポリオキシエチレンジアルキルエステルなどのノニオン系界面活性剤や、オルガノシロキサンポリマーKP341(信越化学工業(株)製)、(メタ)アクリル酸系共重合体ポリフローNo.57、同No.95(以上、共栄社化学(株)製)などを挙げることができる。 Moreover, as surfactants other than the above, polyoxyethylene lauryl ether, polyoxyethylene stearyl ether, polyoxyethylene alkyl ethers such as polyoxyethylene oleyl ether; polyoxyethylene-n-octylphenyl ether, polyoxyethylene-n -Polyoxyethylene aryl ethers such as nonylphenyl ether; nonionic surfactants such as polyoxyethylene dialkyl esters such as polyoxyethylene dilaurate and polyoxyethylene distearate; and organosiloxane polymer KP341 (Shin-Etsu Chemical Co., Ltd.) Manufactured), (meth) acrylic acid copolymer polyflow No. 57, no. 95 (above, manufactured by Kyoeisha Chemical Co., Ltd.).
これらの界面活性剤は、単独でまたは2種以上を混合して使用することができる。
界面活性剤の配合量は、〔A〕ブロック共重合体100重量部に対して、好ましくは1.0重量部以下、さらに好ましくは0.5重量部以下である。この場合、界面活性剤の配合量が1.0重量部を超えると、膜ムラを生じやすくなる傾向がある。
上記保存安定剤としては、例えば、硫黄、キノン類、ヒドロキノン類、ポリオキシ化合物、アミン、ニトロニトロソ化合物などを挙げることができ、より具体的には、4−メトキシフェノール、N−ニトロソ−N−フェニルヒドロキシルアミンアルミニウムなどを挙げることができる。
これらの保存安定剤は、単独でまたは2種以上を混合して使用することができる。
保存安定剤の配合量は、〔A〕ブロック共重合体100重量部に対して、好ましくは3.0重量部以下、さらに好ましくは0.5重量部以下である。保存安定剤の配合量が3.0重量部を超えると、感度が低下してパターン形状が劣化するおそれがある。
These surfactants can be used alone or in admixture of two or more.
The compounding amount of the surfactant is preferably 1.0 part by weight or less, more preferably 0.5 part by weight or less, with respect to 100 parts by weight of the [A] block copolymer. In this case, when the compounding amount of the surfactant exceeds 1.0 part by weight, film unevenness tends to occur.
Examples of the storage stabilizer include sulfur, quinones, hydroquinones, polyoxy compounds, amines, nitronitroso compounds, and more specifically, 4-methoxyphenol, N-nitroso-N-phenyl. Examples include hydroxylamine aluminum.
These storage stabilizers can be used alone or in admixture of two or more.
The amount of the storage stabilizer is preferably 3.0 parts by weight or less, more preferably 0.5 parts by weight or less with respect to 100 parts by weight of the [A] block copolymer. When the amount of the storage stabilizer exceeds 3.0 parts by weight, the sensitivity may be lowered and the pattern shape may be deteriorated.
また、上記耐熱性向上剤としては、例えば、N−(アルコキシメチル)グリコールウリル化合物、N−(アルコキシメチル)メラミン化合物、2個以上のエポキシ基を有する化合物などを挙げることができる。
例えば、N−(アルコキシメチル)グリコールウリル化合物、N−(アルコキシメチル)メラミン化合物などを挙げることができる。
Examples of the heat resistance improver include N- (alkoxymethyl) glycoluril compounds, N- (alkoxymethyl) melamine compounds, and compounds having two or more epoxy groups.
Examples thereof include N- (alkoxymethyl) glycoluril compounds and N- (alkoxymethyl) melamine compounds.
上記N−(アルコキシメチル)グリコールウリル化合物としては、例えば、N,N,N’,N’−テトラ(メトキシメチル)グリコールウリル、N,N,N’,N’−テトラ(エトキシメチル)グリコールウリル、N,N,N’,N’−テトラ(n−プロポキシメチル)グリコールウリル、N,N,N’,N’−テトラ(i−プロポキシメチル)グリコールウリル、N,N,N’,N’−テトラ(n−ブトキシメチル)グリコールウリル、N,N,N’,N’−テトラ(t−ブトキシメチル)グリコールウリルなどを挙げることができる。 Examples of the N- (alkoxymethyl) glycoluril compound include N, N, N ′, N′-tetra (methoxymethyl) glycoluril, N, N, N ′, N′-tetra (ethoxymethyl) glycoluril. N, N, N ′, N′-tetra (n-propoxymethyl) glycoluril, N, N, N ′, N′-tetra (i-propoxymethyl) glycoluril, N, N, N ′, N ′ -Tetra (n-butoxymethyl) glycoluril, N, N, N ′, N′-tetra (t-butoxymethyl) glycoluril and the like can be mentioned.
これらのN−(アルコキシメチル)グリコールウリル化合物のうち、N,N,N’,N’−テトラ(メトキシメチル)グリコールウリルが好ましい。
上記N−(アルコキシメチル)メラミン化合物としては、例えば、N,N,N’,N’,N’’,N’’−ヘキサ(メトキシメチル)メラミン、N,N,N’,N’,N’’,N’’−ヘキサ(エトキシメチル)メラミン、N,N,N’,N’,N’’,N’’−ヘキサ(n−プロポキシメチル)メラミン、N,N,N’,N’,N’’,N’’−ヘキサ(i−プロポキシメチル)メラミン、N,N,N’,N’,N’’,N’’−ヘキサ(n−ブトキシメチル)メラミン、N,N,N’,N’,N’’,N’’−ヘキサ(t−ブトキシメチル)メラミンなどを挙げることができる。
これらのN−(アルコキシメチル)メラミン化合物のうち、N,N,N’,N’,N’’,N’’−ヘキサ(メトキシメチル)メラミンが好ましく、その市販品としては、例えば、ニカラックN−2702、同MW−30M(以上 三和ケミカル(株)製)などを挙げることができる。
Of these N- (alkoxymethyl) glycoluril compounds, N, N, N ′, N′-tetra (methoxymethyl) glycoluril is preferred.
Examples of the N- (alkoxymethyl) melamine compound include N, N, N ′, N ′, N ″, N ″ -hexa (methoxymethyl) melamine, N, N, N ′, N ′, N '', N ''-hexa (ethoxymethyl) melamine, N, N, N ′, N ′, N ″, N ″ -hexa (n-propoxymethyl) melamine, N, N, N ′, N ′ , N ″, N ″ -hexa (i-propoxymethyl) melamine, N, N, N ′, N ′, N ″, N ″ -hexa (n-butoxymethyl) melamine, N, N, N Examples include ', N', N ″, N ″ -hexa (t-butoxymethyl) melamine.
Of these N- (alkoxymethyl) melamine compounds, N, N, N ′, N ′, N ″, N ″ -hexa (methoxymethyl) melamine is preferred. -2702, MW-30M (manufactured by Sanwa Chemical Co., Ltd.) and the like.
また、上記2個以上のエポキシ基を有する化合物としては、例えば、エチレングリコールジグリシジルエーテル、ジエチレングリコールジグリシジルエーテル、トリエチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ジプロピレングリコールジグリシジルエーテル、トリプロピレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、1,6−ヘキサンジオールジグリシジルエーテル、グリセリンジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、水添ビスフェノールAジグリシジルエーテル、ビスフェノールAジグリシジルエーテルなどを挙げることができる。 Examples of the compound having two or more epoxy groups include ethylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, triethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, and dipropylene glycol. Diglycidyl ether, tripropylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, glycerin diglycidyl ether, trimethylolpropane triglycidyl ether, hydrogenated bisphenol A Examples include diglycidyl ether and bisphenol A diglycidyl ether. It is possible.
また、2個以上のエポキシ基を有する化合物の市販品としては、例えば、エポライト40E、同100E、同200E、同70P、同200P、同400P、同1500NP、同80MF、同100MF、同1600、同3002、同4000(以上 共栄社化学(株)製)、エピコート152、エピコート154(以上 ジャパンエポキシレジン(株)製)などを挙げることができる。これらは、単独でまたは2種以上を混合して使用することができる。 Examples of commercially available compounds having two or more epoxy groups include Epolite 40E, 100E, 200E, 70P, 200P, 400P, 1500NP, 80MF, 100MF, 1600, 3002, 4000 (manufactured by Kyoeisha Chemical Co., Ltd.), Epicoat 152, Epicoat 154 (manufactured by Japan Epoxy Resin Co., Ltd.), and the like. These can be used individually or in mixture of 2 or more types.
感放射線性樹脂組成物の調製
本発明の感放射線性樹脂組成物は、上記の〔A〕光重合性不飽和基を有する共重合体、〔B〕成分、〔C〕成分および上記の如き任意的に添加するその他の成分を均一に混合することによって調製される。本発明の感放射線性樹脂組成物は、好ましくは適当な溶媒に溶解されて溶液状態で用いられる。例えば〔A〕光重合性不飽和基を有する共重合体、〔B〕成分、〔C〕成分および任意的に添加されるその他の成分を、所定の割合で混合することにより、溶液状態の感放射線性樹脂組成物を調製することができる。
Preparation of Radiation Sensitive Resin Composition The radiation sensitive resin composition of the present invention comprises the above-mentioned [A] copolymer having a photopolymerizable unsaturated group, [B] component, [C] component and any of the above It is prepared by uniformly mixing other components to be added. The radiation-sensitive resin composition of the present invention is preferably used in a solution state after being dissolved in an appropriate solvent. For example, [A] a copolymer having a photopolymerizable unsaturated group, [B] component, [C] component and other components optionally added are mixed at a predetermined ratio to thereby give a solution state sensitivity. A radiation resin composition can be prepared.
本発明の感放射線性樹脂組成物の調製に用いられる溶媒としては、〔A〕光重合性不飽和基を有する共重合体、〔B〕成分、〔C〕成分および任意的に配合されるその他の成分の各成分を均一に溶解し、各成分と反応しないものが用いられる。
このような溶媒としては、上述した〔A〕光重合性不飽和基を有する共重合体を製造するために使用できる溶媒として例示したものと同様のものを挙げることができる。
Solvents used in the preparation of the radiation sensitive resin composition of the present invention include [A] a copolymer having a photopolymerizable unsaturated group, [B] component, [C] component and other optionally blended Those components are dissolved uniformly and do not react with each component.
As such a solvent, the same thing as what was illustrated as a solvent which can be used in order to manufacture the copolymer which has the above-mentioned [A] photopolymerizable unsaturated group can be mentioned.
このような溶媒のうち、各成分の溶解性、各成分との反応性、塗膜形成のし易さなどの点から、例えばアルコール、グリコールエーテル、エチレングリコールアルキルエーテルアセテート、エステルおよびジエチレングリコールが好ましく用いられる。これらのうち、例えばベンジルアルコール、2−フェニルエチルアルコール、3−フェニル−1−プロパノール、エチレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、シクロヘキサノールアセテート、ジエチレングリコールジエチルエーテル、ジエチレングリコールエチルメチルエーテル、ジエチレングリコールジメチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、メトキシプロピオン酸メチル、エトキシプロピオン酸エチルが特に好ましく使用できる。 Of these solvents, alcohols, glycol ethers, ethylene glycol alkyl ether acetates, esters and diethylene glycol are preferably used from the viewpoints of solubility of each component, reactivity with each component, and ease of film formation. It is done. Among these, for example, benzyl alcohol, 2-phenylethyl alcohol, 3-phenyl-1-propanol, ethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, cyclohexanol acetate, diethylene glycol diethyl ether, diethylene glycol ethyl methyl ether, diethylene glycol dimethyl ether, Propylene glycol monomethyl ether, propylene glycol monomethyl ether acetate, methyl methoxypropionate, and ethyl ethoxypropionate can be particularly preferably used.
さらに、上記溶媒とともに膜厚の面内均一性を高めるため、高沸点溶媒を併用することもできる。併用できる高沸点溶媒としては、例えばN−メチルホルムアミド、N,N−ジメチルホルムアミド、N−メチルホルムアニリド、N−メチルアセトアミド、N,N−ジメチルアセトアミド、N−メチルピロリドン、ジメチルスルホキシド、ベンジルエチルエーテル、ジヘキシルエーテル、アセトニルアセトン、イソホロン、カプロン酸、カプリル酸、1−オクタノール、1−ノナノール、酢酸ベンジル、安息香酸エチル、シュウ酸ジエチル、マレイン酸ジエチル、γ−ブチロラクトン、炭酸エチレン、炭酸プロピレン、フェニルセロソルブアセテートなどが挙げられる。これらのうち、N−メチルピロリドン、γ−ブチロラクトン、N,N−ジメチルアセトアミドが好ましい。 Furthermore, in order to improve the in-plane uniformity of the film thickness together with the above solvent, a high boiling point solvent can be used in combination. Examples of the high boiling point solvent that can be used in combination include N-methylformamide, N, N-dimethylformamide, N-methylformanilide, N-methylacetamide, N, N-dimethylacetamide, N-methylpyrrolidone, dimethylsulfoxide, and benzylethyl ether. , Dihexyl ether, acetonyl acetone, isophorone, caproic acid, caprylic acid, 1-octanol, 1-nonanol, benzyl acetate, ethyl benzoate, diethyl oxalate, diethyl maleate, γ-butyrolactone, ethylene carbonate, propylene carbonate, phenyl Examples include cellosolve acetate. Of these, N-methylpyrrolidone, γ-butyrolactone, and N, N-dimethylacetamide are preferable.
本発明の感放射性樹脂組成物の溶媒として、高沸点溶媒を併用する場合、その使用量は、溶媒全量に対して、好ましくは50重量%以下、より好ましくは40重量%以下、さらに好ましくは30重量%以下とすることができる。高沸点溶媒の使用量がこの使用量を超えると、塗膜の膜厚均一性、感度および残膜率が低下する場合がある。
本発明の感放射線性樹脂組成物を溶液状態として調製する場合、溶液中に占める溶媒以外の成分、すなわち〔A〕光重合性不飽和基を有する共重合体、〔B〕成分および〔C〕成分ならびに任意的に添加されるその他の成分の合計量の割合は、使用目的や所望の膜厚の値などに応じて任意に設定することができ、例えば5〜50重量%、好ましくは7〜40重量%、さらに好ましくは10〜35重量%である。
このようにして調製された組成物溶液は、孔径0.5μm程度のミリポアフィルタなどを用いて濾過した後、使用に供することもできる。
When a high boiling point solvent is used in combination as the solvent of the radiation sensitive resin composition of the present invention, the amount used is preferably 50% by weight or less, more preferably 40% by weight or less, still more preferably 30%, based on the total amount of the solvent. It can be made into weight% or less. When the amount of the high-boiling solvent used exceeds this amount, the coating film thickness uniformity, sensitivity, and residual film rate may be reduced.
When preparing the radiation sensitive resin composition of the present invention in a solution state, components other than the solvent in the solution, that is, [A] a copolymer having a photopolymerizable unsaturated group, [B] component and [C] The ratio of the total amount of the components and other components optionally added can be arbitrarily set according to the purpose of use, the value of the desired film thickness, etc., for example, 5 to 50% by weight, preferably 7 to It is 40% by weight, more preferably 10 to 35% by weight.
The composition solution thus prepared can be used after being filtered using a Millipore filter having a pore diameter of about 0.5 μm.
スペーサーの形成方法
次に、本発明の感放射線性樹脂組成物を用いて本発明のスペーサーを形成する方法について説明する。
本発明のスペーサーの形成方法は、以下の工程を以下に記載の順序で実施することを特徴とするものである。
Next, a method for forming the spacer of the present invention using the radiation-sensitive resin composition of the present invention will be described.
The spacer forming method of the present invention is characterized in that the following steps are performed in the order described below.
(1)上記感放射線性樹脂組成物の被膜を基板上に形成する工程、
(2)上記被膜の少なくとも一部に露光する工程、
(3)露光後の被膜を現像する工程、および
(4)現像後の被膜を加熱する工程。
(1) A step of forming a film of the radiation sensitive resin composition on a substrate,
(2) a step of exposing at least a part of the coating;
(3) a step of developing the film after exposure, and (4) a step of heating the film after development.
以下、これらの各工程について順次説明する。 Hereinafter, each of these steps will be described sequentially.
(1)本発明の感放射線性樹脂組成物の被膜を基板上に形成する工程
透明基板の一面に透明導電膜を形成し、該透明導電膜の上に、本発明の感放射線性樹脂組成物の組成物溶液を塗布したのち、塗布面を加熱(プレベーク)することにより、被膜を形成する。
スペーサーの形成に用いられる透明基板としては、例えば、ガラス基板、樹脂基板などを挙げることができ、より具体的には、ソーダライムガラス、無アルカリガラスなどのガラス基板;ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエーテルスルホン、ポリカーボネート、ポリイミドなどのプラスチックからなる樹脂基板を挙げることができる。
(1) Step of forming a coating film of the radiation sensitive resin composition of the present invention on a substrate A transparent conductive film is formed on one surface of a transparent substrate, and the radiation sensitive resin composition of the present invention is formed on the transparent conductive film. After coating the composition solution, the coating surface is heated (prebaked) to form a coating.
Examples of the transparent substrate used for forming the spacer include a glass substrate and a resin substrate. More specifically, glass substrates such as soda lime glass and non-alkali glass; polyethylene terephthalate, polybutylene terephthalate, A resin substrate made of a plastic such as polyethersulfone, polycarbonate, or polyimide can be used.
透明基板の一面に設けられる透明導電膜としては、酸化スズ(SnO2)からなるNESA膜(米国PPG社の登録商標)、酸化インジウム−酸化スズ(In2O3−SnO2)からなるITO膜などを挙げることができる。
組成物溶液の塗布方法としては、特に限定されず、例えば、スプレー法、ロールコート法、回転塗布法(スピンコート法)、スリットダイ塗布法(スピンレス法)、バー塗布法、インクジェット塗布法などの適宜の方法を採用することができ、特にスピンコート法、スリットダイ塗布法が好ましい。
また、プレベークの条件は、各成分の種類、配合割合などによっても異なるが、好ましくは70〜120℃で1〜15分間程度である。
なお、被膜のプレベーク後の膜厚は、特に限定されないが、好ましくは0.5〜10μm、より好ましくは1.0〜7.0μm程度である。
本発明の感光性樹脂組成物の被膜を形成する方法としては、他にドライフィルム法によることができる。
As a transparent conductive film provided on one surface of the transparent substrate, an NESA film (registered trademark of PPG, USA) made of tin oxide (SnO 2 ), an ITO film made of indium oxide-tin oxide (In 2 O 3 -SnO 2 ) And so on.
The coating method of the composition solution is not particularly limited, and examples thereof include a spray method, a roll coating method, a spin coating method (spin coating method), a slit die coating method (spinless method), a bar coating method, and an ink jet coating method. An appropriate method can be adopted, and a spin coating method and a slit die coating method are particularly preferable.
Moreover, although the conditions of prebaking differ also with the kind of each component, a mixture ratio, etc., Preferably it is about 1 to 15 minutes at 70-120 degreeC.
In addition, the film thickness after the pre-baking of the film is not particularly limited, but is preferably about 0.5 to 10 μm, more preferably about 1.0 to 7.0 μm.
As another method for forming a film of the photosensitive resin composition of the present invention, a dry film method can be used.
組成物溶液の塗布法としては、例えば、スプレー法、ロールコート法、回転塗布法(スピンコート法)、スリットダイ塗布法、バー塗布法、インクジェット塗布法などの適宜の方法を採用することができ、特にスピンコート法、スリットダイ塗布法が好ましい。
また、本発明の感光性樹脂組成物の被膜を形成する際に、ドライフィルム法を採用する場合、該ドライフィルムは、ベースフィルム、好ましくは可とう性のベースフィルム上に、本発明の感光性樹脂組成物からなる感光性層を積層してなるもの(以下、「感光性ドライフィルム」という)である。
As a coating method of the composition solution, for example, an appropriate method such as a spray method, a roll coating method, a spin coating method (spin coating method), a slit die coating method, a bar coating method, or an ink jet coating method can be employed. In particular, a spin coating method and a slit die coating method are preferable.
Further, when the dry film method is adopted when forming the coating film of the photosensitive resin composition of the present invention, the dry film is formed on the base film, preferably a flexible base film. It is formed by laminating a photosensitive layer made of a resin composition (hereinafter referred to as “photosensitive dry film”).
上記感光性ドライフィルムは、ベースフィルム上に、本発明の感光性樹脂組成物を好ましくは液状組成物として塗布したのち乾燥することにより、感光性層を積層して形成することができる。感光性ドライフィルムのベースフィルムとしては、例えば、ポリエチレンテレフタレート(PET)、ポリエチレン、ポリプロピレン、ポリカーボネート、ポリ塩化ビニルなどの合成樹脂のフィルムを使用することができる。ベースフィルムの厚さは、15〜125μmの範囲が適当である。得られる感光性層の厚さは、1〜30μmの程度が好ましい。 The photosensitive dry film can be formed by laminating a photosensitive layer on the base film by applying the photosensitive resin composition of the present invention, preferably as a liquid composition, and then drying. As a base film of the photosensitive dry film, for example, a synthetic resin film such as polyethylene terephthalate (PET), polyethylene, polypropylene, polycarbonate, polyvinyl chloride, or the like can be used. The thickness of the base film is suitably in the range of 15 to 125 μm. The thickness of the obtained photosensitive layer is preferably about 1 to 30 μm.
また、感光性ドライフィルムは、未使用時に、その感光性層上にさらにカバーフィルムを積層して保存することもできる。このカバーフィルムは、未使用時には剥がれず、使用時には容易に剥がすことができるように、適度な離型性を有する必要がある。このような条件を満たすカバーフィルムとしては、例えば、PETフィルム、ポリプロピレンフィルム、ポリエチレンフィルム、ポリ塩化ビニルフィルム、ポリウレタンフィルムなどの合成樹脂フィルムの表面にシリコーン系離型剤を塗布または焼き付けフィルムを使用することができる。カバーフィルムの厚さは、通常、5〜30μm程度が好ましい。
これらカバーフィルムは、必要に応じて2層もしくは3層のカバーフィルムを積層することができる。
Moreover, the photosensitive dry film can also be preserve | saved by laminating | stacking a cover film on the photosensitive layer at the time of unused. This cover film needs to have an appropriate releasability so that it does not peel off when not in use and can be easily peeled off when in use. As a cover film satisfying such conditions, for example, a silicone-based release agent is applied or baked onto the surface of a synthetic resin film such as a PET film, a polypropylene film, a polyethylene film, a polyvinyl chloride film, or a polyurethane film. be able to. The thickness of the cover film is usually preferably about 5 to 30 μm.
These cover films can be laminated with a two-layer or three-layer cover film as required.
(2)上記被膜の少なくとも一部に放射線を照射する工程
次いで、形成された被膜の少なくとも一部に放射線を露光する。この場合、被膜の一部に露光する際には、所定のパターンを有するフォトマスクを介して露光する。
露光に使用される放射線としては、例えば可視光線、紫外線、遠紫外線などを使用することができる。波長が190〜450nmの範囲にある放射線が好ましく、特に365nmの紫外線を含む放射線が好ましい。
露光量は、露光される放射線の波長365nmにおける強度を照度計(OAI model 356 、OAI Optical Associates Inc.製)により測定した値として、好ましくは100〜10,000J/m2、より好ましくは1,500〜3,000J/m2である。
(2) Step of irradiating at least a part of the film Next, at least a part of the formed film is exposed to radiation. In this case, when exposing a part of the film, the exposure is performed through a photomask having a predetermined pattern.
As the radiation used for the exposure, for example, visible light, ultraviolet light, far ultraviolet light and the like can be used. Radiation having a wavelength in the range of 190 to 450 nm is preferable, and radiation containing ultraviolet light of 365 nm is particularly preferable.
The exposure amount is preferably 100 to 10,000 J / m 2 , more preferably 1, as a value measured by an illuminometer (OAI model 356, manufactured by OAI Optical Associates Inc.) at a wavelength of 365 nm of the radiation to be exposed. it is a 500~3,000J / m 2.
(3)現像工程
次いで、露光後の被膜を現像することにより、不要な部分を除去して、所定のパターンを形成する。
(3) Development Step Next, the exposed film is developed to remove unnecessary portions and form a predetermined pattern.
現像に使用される現像液としては、例えば、水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム、ケイ酸ナトリウム、メタケイ酸ナトリウム、アンモニアなどの無機アルカリ;エチルアミン、n−プロピルアミンなどの脂肪族1級アミン;ジエチルアミン、ジ−n−プロピルアミンなどの脂肪族2級アミン;トリメチルアミン、メチルジエチルアミン、ジメチルエチルアミン、トリエチルアミンなどの脂肪族3級アミン;ピロール、ピペリジン、N−メチルピペリジン、N−メチルピロリジン、1,8−ジアザビシクロ[5.4.0]−7−ウンデセン、1,5−ジアザビシクロ[4.3.0]−5−ノネンなどの脂環族3級アミン;ピリジン、コリジン、ルチジン、キノリンなどの芳香族3級アミン;ジメチルエタノールアミン、メチルジエタノールアミン、トリエタノールアミンなどのアルカノールアミン;テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシドなどの4級アンモニウム塩などのアルカリ性化合物の水溶液を使用することができる。 Examples of the developer used for development include inorganic alkalis such as sodium hydroxide, potassium hydroxide, sodium carbonate, sodium silicate, sodium metasilicate, and ammonia; aliphatic primary amines such as ethylamine and n-propylamine. Aliphatic secondary amines such as diethylamine and di-n-propylamine; aliphatic tertiary amines such as trimethylamine, methyldiethylamine, dimethylethylamine and triethylamine; pyrrole, piperidine, N-methylpiperidine, N-methylpyrrolidine, 1, Aliphatic tertiary amines such as 8-diazabicyclo [5.4.0] -7-undecene and 1,5-diazabicyclo [4.3.0] -5-nonene; fragrances such as pyridine, collidine, lutidine and quinoline Group tertiary amine; dimethylethanolamine, methyl It can be used an aqueous solution of an alkaline compound such as quaternary ammonium salts such as tetramethylammonium hydroxide, tetraethylammonium hydroxide; ethanolamine, alkanolamines such as triethanolamine.
また、上記アルカリ性化合物の水溶液には、メタノール、エタノールなどの水溶性有機溶媒および/または界面活性剤を適当量添加して使用することもできる。
現像方法としては、液盛り法、ディッピング法、シャワー法などのいずれでもよく、現像時間は、好ましくは常温で10〜180秒間程度である。
現像後、例えば流水洗浄を30〜90秒間行ったのち、例えば圧縮空気や圧縮窒素で風乾させることによって、所望のパターンが形成される。
In addition, an appropriate amount of a water-soluble organic solvent such as methanol or ethanol and / or a surfactant can be added to the aqueous solution of the alkaline compound.
The developing method may be any of a liquid piling method, a dipping method, a shower method, and the like, and the developing time is preferably about 10 to 180 seconds at room temperature.
After development, for example, after washing with running water for 30 to 90 seconds, a desired pattern is formed by, for example, air drying with compressed air or compressed nitrogen.
(4)加熱工程
次いで、得られたパターン(被膜)を、例えばホットプレート、オーブンなどの加熱装置により、所定温度、例えば180〜240℃で、所定時間、例えばホットプレート上では5〜30分間、オーブン中では15〜180分間、加熱(ポストベーク)することにより、所定のスペーサーを得ることができる。
(4) Heating step Next, the obtained pattern (coating film) is heated at a predetermined temperature, for example, 180 to 240 ° C., for a predetermined time, for example, 5-30 minutes on the hot plate, for example, by a heating device such as a hot plate or an oven. A predetermined spacer can be obtained by heating (post-baking) for 15 to 180 minutes in an oven.
液晶表示素子
本発明の液晶表示素子は、以下の方法により作製される。まず、液晶配向能を有する配向膜が形成された基板を2枚作成し、それぞれの配向膜における液晶配向方向が直交または逆平行となるように、2枚の基板を間隙(セルギャップ)を介して対向させ、2枚の基板の周辺部を本発明のスペーサーを介して貼り合わせ、基板の表面およびスペーサーにより区画されたセルギャップ内に液晶を充填し、充填孔を封止して液晶セルを構成する。そして、液晶セルの外表面、すなわち、液晶セルを構成するそれぞれの基板の他面側に、偏光板を、その偏光方向が当該基板の一面に形成された配向膜の液晶配向方向と一致または直交するように貼り合わせることにより、本発明の液晶表示素子を得る。
Liquid crystal display element The liquid crystal display element of this invention is produced with the following method. First, two substrates on which an alignment film having liquid crystal alignment ability is formed are prepared, and the two substrates are placed through a gap (cell gap) so that the liquid crystal alignment directions in each alignment film are orthogonal or antiparallel. The peripheral portions of the two substrates are bonded together via the spacer of the present invention, the liquid crystal is filled in the cell gap defined by the surface of the substrate and the spacer, the filling hole is sealed, and the liquid crystal cell is Constitute. Then, on the outer surface of the liquid crystal cell, that is, on the other surface side of each substrate constituting the liquid crystal cell, a polarizing plate is aligned or orthogonal to the liquid crystal alignment direction of the alignment film formed on one surface of the substrate. Thus, the liquid crystal display element of the present invention is obtained.
上記液晶としては、例えばネマティック型液晶、スメクティック型液晶を挙げることができる。その中でもネマティック型液晶が好ましく、例えばシッフベース系液晶、アゾキシ系液晶、ビフェニル系液晶、フェニルシクロヘキサン系液晶、エステル系液晶、ターフェニル系液晶、ビフェニルシクロヘキサン系液晶、ピリミジン系液晶、ジオキサン系液晶、ビシクロオクタン系液晶、キュバン系液晶などが用いられる。また、これらの液晶に、例えばコレスチルクロライド、コレステリルノナエート、コレステリルカーボネートなどのコレステリック液晶や商品名「C−15」、「CB−15」(メルク社製)として販売されているようなカイラル剤などを添加して使用することもできる。さらに、p−デシロキシベンジリデン−p−アミノ−2−メチルブチルシンナメートなどの強誘電性液晶も使用することができる。
また、液晶セルの外側に使用される偏光板としては、ポリビニルアルコールを延伸配向させながら、ヨウ素を吸収させたH膜と呼ばれる偏光膜を酢酸セルロース保護膜で挟んだ偏光板またはH膜そのものからなる偏光板などを挙げることができる。
Examples of the liquid crystal include a nematic liquid crystal and a smectic liquid crystal. Among them, nematic liquid crystal is preferable, for example, Schiff base liquid crystal, azoxy liquid crystal, biphenyl liquid crystal, phenyl cyclohexane liquid crystal, ester liquid crystal, terphenyl liquid crystal, biphenyl cyclohexane liquid crystal, pyrimidine liquid crystal, dioxane liquid crystal, bicyclooctane. Type liquid crystal, cubane type liquid crystal, etc. are used. Further, for these liquid crystals, for example, cholesteric liquid crystals such as cholestyl chloride, cholesteryl nonate, cholesteryl carbonate, and chiral agents such as those sold under the trade names “C-15” and “CB-15” (manufactured by Merck). Etc. can also be used. Furthermore, a ferroelectric liquid crystal such as p-decyloxybenzylidene-p-amino-2-methylbutylcinnamate can also be used.
Further, the polarizing plate used outside the liquid crystal cell is composed of a polarizing plate or an H film itself in which a polarizing film called an H film that absorbs iodine while sandwiching and stretching polyvinyl alcohol is sandwiched between cellulose acetate protective films. A polarizing plate etc. can be mentioned.
以下に合成例、実施例を示して、本発明をさらに具体的に説明するが、本発明は以下の実施例に限定されるものではない。 The present invention will be described more specifically with reference to synthesis examples and examples. However, the present invention is not limited to the following examples.
<ゲルパーミエーションクロマトグラフィーによる共重合体の分子量の測定>
装置:GPC−101(昭和電工(株)製)
カラム:GPC−KF−801、GPC−KF−802、GPC−KF−803およびGPC−KF−804を結合
移動相:リン酸0.5重量%を含むテトラヒドロフラン
<Measurement of molecular weight of copolymer by gel permeation chromatography>
Apparatus: GPC-101 (made by Showa Denko KK)
Column: GPC-KF-801, GPC-KF-802, GPC-KF-803 and GPC-KF-804 are combined Mobile phase: Tetrahydrofuran containing 0.5% by weight of phosphoric acid
光重合性不飽和基を有する共重合体〔A〕の合成例1〜6および比較合成例1〜2
合成例1
冷却管、撹拌機を備えたフラスコに、ピラゾール−1−ジカルボン酸シアノ(ジメチル)メチルエステル4重量部、酢酸3−メトキシブチル250重量部を仕込み、引き続いてメタクリル酸18重量部、スチレン5重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部、メタクリル酸ベンジル30重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を70℃に上昇させる。70℃に達した段階で2,2’−アゾビス(2,4−ジメチルバレロニトリル)を2重量部添加し、この温度を3時間保持して重合後、メタクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル(商品名PLACCEL FM1D(ダイセル化学工業(株)製)20重量部を添加し、更に3時間保持することにより、固形分濃度31.0重量%の共重合体〔α〕溶液を得た。この〔α〕重合体を、重合体(α−1)とする。
Synthesis examples 1 to 6 and comparative synthesis examples 1 and 2 of a copolymer [A] having a photopolymerizable unsaturated group
Synthesis example 1
A flask equipped with a condenser and a stirrer was charged with 4 parts by weight of pyrazole-1-dicarboxylic acid cyano (dimethyl) methyl ester and 250 parts by weight of 3-methoxybutyl acetate, followed by 18 parts by weight of methacrylic acid and 5 parts by weight of styrene. After charging 30 parts by weight of tricyclo [5.2.1.0 2,6 ] decan-8-yl methacrylate, 17 parts by weight of tetrahydrofuran-2-yl methacrylate, and 30 parts by weight of benzyl methacrylate, and substituting with nitrogen. The temperature of the solution is raised to 70 ° C. while gently stirring. When the temperature reached 70 ° C., 2 parts by weight of 2,2′-azobis (2,4-dimethylvaleronitrile) was added, and this temperature was maintained for 3 hours. After polymerization, 2- (6-hydroxyethylhexamethacrylate) was obtained. Noyloxy) ethyl ester (trade name PLACEL FM1D (manufactured by Daicel Chemical Industries, Ltd.)) 20 parts by weight, and further maintained for 3 hours, a copolymer [α] solution having a solid content concentration of 31.0% by weight This [α] polymer is referred to as polymer (α-1).
得られた共重合体(α−1)について、MwをGPC(ゲルパーミエイションクロマトグラフィー)を用いて測定したところ、7,100であった。
次いで、前記共重合体〔α〕溶液に、2−メタクリロイルオキシエチルイソシアネート(商品名カレンズMOI、昭和電工(株)製)10重量部、4−メトキシフェノール0.08重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度32.6重量%の〔A〕重合体溶液を得た。この〔A〕重合体を、重合体(A−1)とする。
It was 7,100 when Mw was measured using GPC (gel permeation chromatography) about the obtained copolymer ((alpha) -1).
Next, 10 parts by weight of 2-methacryloyloxyethyl isocyanate (trade name Karenz MOI, manufactured by Showa Denko KK) and 0.08 part by weight of 4-methoxyphenol are added to the copolymer [α] solution, and then 60 parts. By stirring and reacting at 2 ° C. for 2 hours, an [A] polymer solution having a solid content concentration of 32.6% by weight was obtained. Let this [A] polymer be a polymer (A-1).
合成例2
冷却管、撹拌機を備えたフラスコに、ピラゾール−1−ジカルボン酸シアノ(ジメチル)メチルエステル4重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてメタクリル酸18重量部、スチレン5重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部、メタクリル酸ベンジル30重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を70℃に上昇させる。70℃に達した段階で2,2’−アゾビス(2,4−ジメチルバレロニトリル)を2重量部添加し、この温度を3時間保持して重合後、メタクリル酸2−ヒドロキシエチルエステル20重量部を添加し、更に3時間保持することにより、固形分濃度31.1重量%の共重合体〔α〕溶液を得た。この〔α〕重合体を、重合体(α−2)とする。
Synthesis example 2
A flask equipped with a condenser and a stirrer was charged with 4 parts by weight of pyrazole-1-dicarboxylic acid cyano (dimethyl) methyl ester and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 18 parts by weight of methacrylic acid, 5 parts by weight of styrene, After charging 30 parts by weight of tricyclo [5.2.1.0 2,6 ] decan-8-yl methacrylate, 17 parts by weight of tetrahydrofuran-2-yl methacrylate and 30 parts by weight of benzyl methacrylate, and substituting with nitrogen, The temperature of the solution is raised to 70 ° C. with gentle stirring. When the temperature reached 70 ° C., 2 parts by weight of 2,2′-azobis (2,4-dimethylvaleronitrile) was added, and this temperature was maintained for 3 hours. After polymerization, 20 parts by weight of methacrylic acid 2-hydroxyethyl ester Was added and held for 3 hours to obtain a copolymer [α] solution having a solid content concentration of 31.1% by weight. This [α] polymer is referred to as polymer (α-2).
得られた共重合体(α−2)について、MwをGPC(ゲルパーミエイションクロマトグラフィー)を用いて測定したところ、7,200であった。
次いで、前記共重合体〔α〕溶液に、2−メタクリロイルオキシエチルイソシアネート(商品名カレンズMOI、昭和電工(株)製)10重量部、4−メトキシフェノール0.08重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度32.7重量%の〔A〕重合体溶液を得た。この〔A〕重合体を、重合体(A−2)とする。
It was 7,200 when Mw was measured using GPC (gel permeation chromatography) about the obtained copolymer ((alpha) -2).
Next, 10 parts by weight of 2-methacryloyloxyethyl isocyanate (trade name Karenz MOI, manufactured by Showa Denko KK) and 0.08 part by weight of 4-methoxyphenol are added to the copolymer [α] solution, and then 60 parts. By stirring and reacting at 2 ° C. for 2 hours, an [A] polymer solution having a solid content concentration of 32.7% by weight was obtained. Let this [A] polymer be a polymer (A-2).
合成例3
冷却管、撹拌機を備えたフラスコに、ピラゾール−1−ジカルボン酸シアノ(ジメチル)メチルエステル4重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてメタクリル酸10重量部、アクリル酸4重量部、スチレン5重量部、メタクリル酸ブチル41重量部、メタクリル酸ベンジル40重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を70℃に上昇させる。70℃に達した段階で2,2’−アゾビス(2,4−ジメチルバレロニトリル)を2重量部添加し、この温度を3時間保持して重合後、メタクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル(商品名PLACCEL FM1D(ダイセル化学工業(株)製20重量部を添加し、更に3時間保持することにより、固形分濃度31.3重量%の共重合体〔α〕溶液を得た。この〔α〕重合体を、重合体(α−3)とする。
Synthesis example 3
A flask equipped with a condenser and a stirrer was charged with 4 parts by weight of cyano (dimethyl) methyl ester of pyrazole-1-dicarboxylic acid and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 10 parts by weight of methacrylic acid and 4 parts by weight of acrylic acid. Then, 5 parts by weight of styrene, 41 parts by weight of butyl methacrylate, and 40 parts by weight of benzyl methacrylate were charged, and after nitrogen substitution, the temperature of the solution was raised to 70 ° C. while gently stirring. When the temperature reached 70 ° C., 2 parts by weight of 2,2′-azobis (2,4-dimethylvaleronitrile) was added, and this temperature was maintained for 3 hours. After polymerization, 2- (6-hydroxyethylhexamethacrylate) was obtained. Noyloxy) ethyl ester (trade name PLACEL FM1D (Daicel Chemical Industries, Ltd., 20 parts by weight) was added, and the mixture was maintained for 3 hours to obtain a copolymer [α] solution having a solid content concentration of 31.3% by weight. This [α] polymer is referred to as “polymer (α-3)”.
得られた共重合体(α−3)について、MwをGPC(ゲルパーミエイションクロマトグラフィー)を用いて測定したところ、7,300であった。
次いで、前記共重合体〔α〕溶液に、2−アクリロイルオキシエチルイソシアネート(商品名カレンズAOI、昭和電工(株)製)10重量部、4−メトキシフェノール0.08重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度32.8重量%の〔A〕重合体溶液を得た。この〔A〕重合体を、重合体(A−3)とする。
With respect to the obtained copolymer (α-3), Mw was measured using GPC (gel permeation chromatography) to be 7,300.
Next, 10 parts by weight of 2-acryloyloxyethyl isocyanate (trade name Karenz AOI, Showa Denko KK) and 0.08 parts by weight of 4-methoxyphenol are added to the copolymer [α] solution, and then 60 parts. By stirring and reacting at 2 ° C. for 2 hours, a [A] polymer solution having a solid content concentration of 32.8% by weight was obtained. This [A] polymer is referred to as a polymer (A-3).
合成例4
冷却管、撹拌機を備えたフラスコに、ピラゾール−1−ジカルボン酸シアノ(ジメチル)メチルエステル4重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてメタクリル酸18重量部、スチレン5重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部、メタクリル酸グリシジル10重量部、メタクリル酸ベンジル20重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を70℃に上昇させる。70℃に達した段階で2,2’−アゾビス(2,4−ジメチルバレロニトリル)を2重量部添加し、この温度を3時間保持して重合後、メタクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル(商品名PLACCEL FM1D(ダイセル化学工業(株)製)20重量部を添加し、更に3時間保持することにより、固形分濃度31.1重量%の共重合体〔α〕溶液を得た。この〔α〕重合体を、重合体(α−4)とする。
Synthesis example 4
A flask equipped with a condenser and a stirrer was charged with 4 parts by weight of pyrazole-1-dicarboxylic acid cyano (dimethyl) methyl ester and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 18 parts by weight of methacrylic acid, 5 parts by weight of styrene, 30 parts by weight of tricyclo [5.2.1.0 2,6 ] decan-8-yl methacrylate, 17 parts by weight of tetrahydrofuran-2-yl methacrylate, 10 parts by weight of glycidyl methacrylate and 20 parts by weight of benzyl methacrylate are charged. Then, after purging with nitrogen, the temperature of the solution is raised to 70 ° C. while gently stirring. When the temperature reached 70 ° C., 2 parts by weight of 2,2′-azobis (2,4-dimethylvaleronitrile) was added, and this temperature was maintained for 3 hours. After polymerization, 2- (6-hydroxyethylhexamethacrylate) was obtained. Noyloxy) ethyl ester (trade name PLACEL FM1D (manufactured by Daicel Chemical Industries, Ltd.)) 20 parts by weight, and further maintained for 3 hours, a copolymer [α] solution having a solid content concentration of 31.1% by weight This [α] polymer is referred to as “polymer (α-4)”.
得られた共重合体(α−4)について、MwをGPC(ゲルパーミエイションクロマトグラフィー)を用いて測定したところ、7,200であった。
次いで、前記共重合体〔α〕溶液に、2−メタクリロイルオキシエチルイソシアネート(商品名カレンズMOI、昭和電工(株)製)10重量部、4−メトキシフェノール0.08重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度31.6重量%の〔A〕重合体溶液を得た。この〔A〕重合体を、重合体(A−4)とする。
It was 7,200 when Mw was measured using GPC (gel permeation chromatography) about the obtained copolymer ((alpha) -4).
Next, 10 parts by weight of 2-methacryloyloxyethyl isocyanate (trade name Karenz MOI, manufactured by Showa Denko KK) and 0.08 part by weight of 4-methoxyphenol are added to the copolymer [α] solution. By stirring and reacting at 2 ° C. for 2 hours, an [A] polymer solution having a solid content concentration of 31.6% by weight was obtained. This [A] polymer is referred to as a polymer (A-4).
合成例5
冷却管、撹拌機を備えたフラスコに、ピラゾール−1−ジカルボン酸シアノ(ジメチル)メチルエステル4重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてメタクリル酸18重量部、スチレン5重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部、メタクリル酸2−メチルグリシジル10重量部、メタクリル酸ベンジル20重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を70℃に上昇させる。70℃に達した段階で2,2’−アゾビス(2,4−ジメチルバレロニトリル)を2重量部添加し、この温度を3時間保持して重合後、メタクリル酸2−(6−ヒドロキシエチルヘキサノイルオキシ)エチルエステル(商品名PLACCEL FM1D(ダイセル化学工業(株)製)20重量部を添加し、更に3時間保持することにより、固形分濃度31.0重量%の共重合体〔α〕溶液を得た。この〔α〕重合体を、重合体(α−5)とする。
Synthesis example 5
A flask equipped with a condenser and a stirrer was charged with 4 parts by weight of pyrazole-1-dicarboxylic acid cyano (dimethyl) methyl ester and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 18 parts by weight of methacrylic acid, 5 parts by weight of styrene, 30 parts by weight of tricyclo [5.2.1.0 2,6 ] decan-8-yl methacrylate, 17 parts by weight of tetrahydrofuran-2-yl methacrylate, 10 parts by weight of 2-methylglycidyl methacrylate, 20 parts by weight of benzyl methacrylate Then, the temperature of the solution is raised to 70 ° C. while gently stirring. When the temperature reached 70 ° C., 2 parts by weight of 2,2′-azobis (2,4-dimethylvaleronitrile) was added, and this temperature was maintained for 3 hours. After polymerization, 2- (6-hydroxyethylhexamethacrylate) was obtained. Noyloxy) ethyl ester (trade name PLACEL FM1D (manufactured by Daicel Chemical Industries, Ltd.)) 20 parts by weight, and further maintained for 3 hours, a copolymer [α] solution having a solid content concentration of 31.0% by weight This [α] polymer is referred to as “polymer (α-5)”.
得られた共重合体(α−5)について、MwをGPC(ゲルパーミエイションクロマトグラフィー)を用いて測定したところ、7,100であった。
次いで、前記共重合体〔α〕溶液に、4−メトキシフェノール0.08重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度31.5重量%の〔A〕重合体溶液を得た。この〔A〕重合体を、重合体(A−5)とする。
It was 7,100 when Mw was measured using GPC (gel permeation chromatography) about the obtained copolymer ((alpha) -5).
Next, 0.08 part by weight of 4-methoxyphenol was added to the copolymer [α] solution, followed by stirring and reaction at 60 ° C. for 2 hours, whereby a solid content concentration of 31.5% by weight [A A polymer solution was obtained. Let this [A] polymer be a polymer (A-5).
合成例6
冷却管、撹拌機を備えたフラスコに、ピラゾール−1−ジカルボン酸シアノ(ジメチル)メチルエステル4重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてスチレン5重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部、メタクリル酸ベンジル25重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を70℃に上昇させる。70℃に達した段階で2,2’−アゾビス(2,4−ジメチルバレロニトリル)を2重量部添加し、この温度を3時間保持して重合後、メタクリル酸23重量部を添加し、更に3時間保持することにより、重合することにより、固形分濃度27.7重量%の共重合体〔α〕溶液を得た。この〔α〕重合体を、重合体(α−6)とする。
Synthesis Example 6
A flask equipped with a condenser and a stirrer was charged with 4 parts by weight of pyrazole-1-dicarboxylic acid cyano (dimethyl) methyl ester and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 5 parts by weight of styrene and tricyclomethacrylate [5. 2.1.0 2,6 ] 30 parts by weight of decan-8-yl, 17 parts by weight of tetrahydrofuran-2-yl methacrylate, and 25 parts by weight of benzyl methacrylate were substituted with nitrogen, and then gently stirred. The temperature of the solution is raised to 70 ° C. When the temperature reached 70 ° C., 2 parts by weight of 2,2′-azobis (2,4-dimethylvaleronitrile) was added, the temperature was maintained for 3 hours, and after polymerization, 23 parts by weight of methacrylic acid was added. By maintaining for 3 hours, a copolymer [α] solution having a solid content concentration of 27.7 wt% was obtained by polymerization. This [α] polymer is referred to as polymer (α-6).
得られた共重合体(α−6)について、MwをGPC(ゲルパーミエイションクロマトグラフィー)を用いて測定したところ、6,800であった。
次いで、前記共重合体〔α〕溶液に、メタクリル酸グリシジル10重量部、4−メトキシフェノール0.08重量部、テトラブチルアンモニウムブロミド0.07重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度29.4重量%の〔A〕重合体溶液を得た。この〔A〕重合体を、重合体(A−6)とする。
It was 6,800 when Mw was measured using GPC (gel permeation chromatography) about the obtained copolymer ((alpha) -6).
Next, 10 parts by weight of glycidyl methacrylate, 0.08 part by weight of 4-methoxyphenol, and 0.07 part by weight of tetrabutylammonium bromide were added to the copolymer [α] solution, and the mixture was stirred at 60 ° C. for 2 hours. The [A] polymer solution having a solid content concentration of 29.4% by weight was obtained. Let this [A] polymer be a polymer (A-6).
比較合成例1
冷却管、撹拌機を備えたフラスコに、2,2’−アゾビスイソブチロニトリル5重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてメタクリル酸18重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、スチレン5重量部、メタクリル酸2−ヒドロキシエチルエステル25重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を80℃に上昇させ、この温度を4時間保持し、その後100℃に上昇させ、この温度を1時間保持して重合することにより、固形分濃度28.0重量%の共重合体〔β−1〕溶液を得た。
Comparative Synthesis Example 1
A flask equipped with a condenser and a stirrer was charged with 5 parts by weight of 2,2′-azobisisobutyronitrile and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 18 parts by weight of methacrylic acid and tricyclomethacrylate [5. 2.1.0 2,6 ] 30 parts by weight of decan-8-yl, 5 parts by weight of styrene, 25 parts by weight of 2-hydroxyethyl methacrylate and 17 parts by weight of tetrahydrofuran-2-yl methacrylate were charged with nitrogen. Then, while gently stirring, the temperature of the solution is raised to 80 ° C., this temperature is kept for 4 hours, then raised to 100 ° C., and this temperature is kept for 1 hour to polymerize to obtain a solid content concentration. A 28.0 wt% copolymer [β-1] solution was obtained.
得られた共重合体〔β−1〕について、GPCを用いて測定したところ、Mwは15,000であった。
次いで、前記共重合体〔β−1〕溶液に、2−メタクリロイルオキシエチルイソシアネート(商品名カレンズMOI、昭和電工(株)製)14重量部、4−メトキシフェノール0.08重量部を添加したのち、60℃で2時間攪拌して反応させることにより、固形分濃度30.9重量%の重合体(a−1)溶液を得た。
When the obtained copolymer [β-1] was measured using GPC, Mw was 15,000.
Next, 14 parts by weight of 2-methacryloyloxyethyl isocyanate (trade name Karenz MOI, Showa Denko KK) and 0.08 parts by weight of 4-methoxyphenol are added to the copolymer [β-1] solution. By stirring and reacting at 60 ° C. for 2 hours, a polymer (a-1) solution having a solid content concentration of 30.9% by weight was obtained.
比較合成例2
冷却管、撹拌機を備えたフラスコに、2,2’−アゾビスイソブチロニトリル5重量部、ジエチレングリコールメチルエチルエーテル250重量部を仕込み、引き続いてメタクリル酸18重量部、メタクリル酸トリシクロ[5.2.1.02,6]デカン−8−イル30重量部、スチレン5重量部、ブタジエン5重量部、メタクリル酸6−ヒドロキシヘキシルエステル25重量部、メタクリル酸テトラヒドロフラン−2−イル17重量部を仕込んで、窒素置換したのち、緩やかに攪拌しつつ、溶液の温度を80℃に上昇させ、この温度を4時間保持し、その後100℃に上昇させ、この温度を1時間保持して重合することにより、固形分濃度27.5重量%の共重合体(a−2)溶液を得た。
得られた共重合体(a−2)について、MwをGPCを用いて測定したところ、14,000であった。
Comparative Synthesis Example 2
A flask equipped with a condenser and a stirrer was charged with 5 parts by weight of 2,2′-azobisisobutyronitrile and 250 parts by weight of diethylene glycol methyl ethyl ether, followed by 18 parts by weight of methacrylic acid and tricyclomethacrylate [5. 2.1.0 2,6 ] 30 parts by weight of decan-8-yl, 5 parts by weight of styrene, 5 parts by weight of butadiene, 25 parts by weight of 6-hydroxyhexyl methacrylate, 17 parts by weight of tetrahydrofuran-2-yl methacrylate After charging and replacing with nitrogen, the temperature of the solution is raised to 80 ° C. while gently stirring, and this temperature is maintained for 4 hours, then raised to 100 ° C., and this temperature is maintained for 1 hour for polymerization. Thus, a copolymer (a-2) solution having a solid content concentration of 27.5% by weight was obtained.
It was 14,000 when Mw was measured using GPC about the obtained copolymer (a-2).
実施例1〜6および比較例1〜2
(I)感放射線性樹脂組成物の調製
上記合成例重合体〔A〕、〔B〕および〔C〕成分、さらに、接着助剤としてγ−グリシドキシプロピルトリメトキシシラン5重量部、界面活性剤としてFTX−218(商品名、(株)ネオス製)0.5重量部、保存安定剤として4−メトキシフェノール0.5重量部を混合し、固形分濃度が20重量%になるようにプロピレングリコールモノメチルエーテルアセテートに溶解したのち、孔径0.5μmのミリポアフィルタでろ過して、組成物溶液を調製した。各成分の量を表1に示す。
なお、実施例7〜8については下記に示すドライフィルム法を用いて実施した。実施例7〜8については上記調製において固形分濃度50重量%になるよう調製した。
Examples 1-6 and Comparative Examples 1-2
(I) Preparation of Radiation Sensitive Resin Composition Above Synthetic Example Polymer [A], [B] and [C] Components, and further 5 parts by weight of γ-glycidoxypropyltrimethoxysilane as an adhesion aid, surfactant 0.5 parts by weight of FTX-218 (trade name, manufactured by Neos Co., Ltd.) as an agent and 0.5 parts by weight of 4-methoxyphenol as a storage stabilizer are mixed, and propylene is mixed so that the solid content concentration becomes 20% by weight. After dissolving in glycol monomethyl ether acetate, the solution was filtered through a Millipore filter having a pore size of 0.5 μm to prepare a composition solution. The amount of each component is shown in Table 1.
In addition, about Examples 7-8, it implemented using the dry film method shown below. About Examples 7-8, it prepared so that it might become 50 weight% of solid content concentration in the said preparation.
実施例7
スピンナーを用いて塗膜する代わりに、感放射線性樹脂組成物の液状組成物をドライフィルム法で塗膜を作成した以外は、実施例1〜6と同様にして、パターン状薄膜を形成して評価した。各成分を表1に示す。なお、露光工程前にベースフィルムの剥離除去を行った。評価結果を表2に示す。
ドライフィルムの作成および転写は以下のごとく行った。
厚さ38μmのポリエチレンテレフタレート(PET)フィルム上に、アプリケーターを用いて感放射線性樹脂組成物の液状組成物を塗布し、塗膜を100℃で5分間加熱し、厚さ4μmの感放射線性ドライフィルムを作製した。次に、ガラス基板の表面に、感放射線性転写層の表面が当接されるように感放射線性転写ドライフィルムを重ね合わせ、熱圧着法で感放射線性ドライフィルムをガラス基板に転写した。
Example 7
Instead of coating using a spinner, a patterned thin film was formed in the same manner as in Examples 1 to 6, except that a coating film was formed by a dry film method using a liquid composition of a radiation sensitive resin composition. evaluated. Each component is shown in Table 1. The base film was peeled and removed before the exposure process. The evaluation results are shown in Table 2.
Dry film preparation and transfer were performed as follows.
A liquid composition of a radiation-sensitive resin composition is applied onto a polyethylene terephthalate (PET) film having a thickness of 38 μm using an applicator, and the coating film is heated at 100 ° C. for 5 minutes to form a radiation-sensitive dry film having a thickness of 4 μm. A film was prepared. Next, the radiation-sensitive transfer dry film was superposed on the surface of the glass substrate so that the surface of the radiation-sensitive transfer layer was in contact, and the radiation-sensitive dry film was transferred to the glass substrate by a thermocompression bonding method.
実施例8
実施例7と同様にして、感放射線性ドライフィルムを作製後、パターン状薄膜を形成して評価した。各成分を表1に示す。評価結果を表2に示す。
Example 8
In the same manner as in Example 7, after producing a radiation-sensitive dry film, a patterned thin film was formed and evaluated. Each component is shown in Table 1. The evaluation results are shown in Table 2.
(A)成分
合成例に記載
A−1〜A−6
(B)成分
B−1:ジペンタエリスリトールヘキサアクリレート
(C)成分
C−1:1−〔9−エチル−6−(2−メチルベンゾイル)−9.H.−カルバゾール−3−イル〕−エタン−1−オンオキシム−O−アセタート(商品名IRGACURE OXE 02、チバ・スペシャルティー・ケミカルズ社製)
C−2:2−(4−メチルベンゾイル)−2−(ジメチルアミノ)−1−(4−モルフォリノフェニル)−ブタン−1−オン(商品名イルガキュア379、チバ・スペシャルティー・ケミカルズ社製)
(A) component described in synthesis examples A-1 to A-6
(B) component B-1: dipentaerythritol hexaacrylate (C) component C-1: 1- [9-ethyl-6- (2-methylbenzoyl) -9. H. -Carbazol-3-yl] -ethane-1-one oxime-O-acetate (trade name IRGACURE OXE 02, manufactured by Ciba Specialty Chemicals)
C-2: 2- (4-methylbenzoyl) -2- (dimethylamino) -1- (4-morpholinophenyl) -butan-1-one (trade name Irgacure 379, manufactured by Ciba Specialty Chemicals)
評価
上記に示すように調製した組成物の評価を以下のように実施した。評価結果を表2に示す。
Evaluation The composition prepared as described above was evaluated as follows. The evaluation results are shown in Table 2.
(II)スペーサーの形成
無アルカリガラス基板上にスピンナーを用いて、前記組成物溶液を塗布したのち、80℃のホットプレート上で3分間プレベークして、膜厚4.0μmの被膜を形成した。ドライフィルムの場合、実施例7で示した方法により被膜を形成した。
次いで、得られた被膜に、15μm角の残しパターンを有するフォトマスクを介して、365nmにおける強度が250W/m2の紫外線を10秒間露光した。その後、水酸化カリウムの0.05重量%水溶液により、25℃で60秒間現像したのち、純水で1分間洗浄した。その後、オーブン中、230℃で20分間ポストベークすることにより、所定パターンのスペーサーを形成した。
(II) Formation of Spacer The composition solution was applied on an alkali-free glass substrate using a spinner and then pre-baked on an 80 ° C. hot plate for 3 minutes to form a film having a thickness of 4.0 μm. In the case of a dry film, a film was formed by the method shown in Example 7.
Next, the obtained film was exposed to ultraviolet rays having an intensity of 365 W / m 2 at 365 nm for 10 seconds through a photomask having a 15 μm square remaining pattern. Thereafter, development was performed with a 0.05 wt% aqueous solution of potassium hydroxide at 25 ° C. for 60 seconds, followed by washing with pure water for 1 minute. Then, the spacer of the predetermined pattern was formed by post-baking for 20 minutes at 230 degreeC in oven.
(III)感度の評価
露光量を変量とした以外は前記(II)スペーサーの形成と同様にして、スペーサーを形成したとき、現像後の残膜率(現像後の膜厚×100/初期膜厚。以下同様。)が90%以上になる露光量を感度とした。この露光量が1,000J/m2以下のとき、感度が良好といえる。以下の評価項目はそれぞれの実施例における感度でパターン形成した。
(III) Evaluation of sensitivity When the spacer was formed in the same manner as the formation of the spacer (II) except that the exposure amount was changed, the residual film ratio after development (film thickness after development × 100 / initial film thickness) The same applies to the following). When this exposure amount is 1,000 J / m 2 or less, it can be said that the sensitivity is good. The following evaluation items were patterned by the sensitivity in each example.
(IV)現像性の評価
前記(II)で現像時に現像時間を40秒間に短縮した時、パターンが形成されている場合を良好(○)、残渣が生じている場合を不良(×)として評価した。評価結果を表2に示す。
(IV) Evaluation of developability When the development time is shortened to 40 seconds during development in (II), the pattern is formed as good (◯), and the residue is evaluated as bad (×). did. The evaluation results are shown in Table 2.
(V)解像度の評価
前記(II)でパターンを形成したとき、残しパターンが解像できている場合を良好(○)、解像できていない場合を不良(×)として評価した。評価結果を表2に示す。
(V) Evaluation of resolution When the pattern was formed in (II), the case where the remaining pattern was resolved was evaluated as good (◯), and the case where the pattern was not resolved was evaluated as defective (×). The evaluation results are shown in Table 2.
(VI)圧縮変位量の評価
前記(II)で得たパターンについて、微小圧縮試験機(DUH−201、(株)島津製作所製)を用い、直径50μmの平面圧子により、50mNの荷重を加えたときの変形量を、測定温度23℃で測定した。この値が0.5μm以上のとき、圧縮変位量は良好といえる。評価結果を表2に示す。
(VI) Evaluation of Compression Displacement A load of 50 mN was applied to the pattern obtained in (II) using a micro compression tester (DUH-201, manufactured by Shimadzu Corporation) with a flat indenter having a diameter of 50 μm. The amount of deformation was measured at a measurement temperature of 23 ° C. When this value is 0.5 μm or more, it can be said that the amount of compressive displacement is good. The evaluation results are shown in Table 2.
(VII)耐熱性の評価
前記(II)で得たパターンについて、更にオーブン中で230℃で20分放置した後、スペーサーの高さ変化が2%未満であれば良好(○)、2%〜4%未満であればやや良好(△)、4%以上であれば不良(×)として評価した。評価結果を表2に示す
(VII) Evaluation of heat resistance About the pattern obtained in (II) above, after leaving it in an oven at 230 ° C. for 20 minutes, if the height change of the spacer is less than 2%, it is good (◯), 2% to If it was less than 4%, it was evaluated as slightly good (Δ), and if it was 4% or more, it was evaluated as defective (x). The evaluation results are shown in Table 2.
(VIII)ラビング耐性の評価
前記(II)で得たパターンを形成した基板に、液晶配向剤としてAL3046(商品名、JSR(株)製)を液晶配向膜塗布用印刷機に用いて塗布したのち、180℃で1時間乾燥して、乾燥膜厚0.05μmの配向剤の塗膜を形成した。その後、この塗膜に、ポリアミド製の布を巻き付けたロールを有するラビングマシーンを用い、ロールの回転数500rpm、ステージの移動速度1cm/秒として、ラビング処理を行った。このとき、パターンの削れや剥がれの有無を評価した。評価結果を表2に示す。
(VIII) Evaluation of rubbing resistance After applying AL3046 (trade name, manufactured by JSR Co., Ltd.) as a liquid crystal aligning agent to a substrate on which the pattern obtained in (II) is formed, using a printing machine for applying a liquid crystal alignment film. And dried at 180 ° C. for 1 hour to form a coating film of an orientation agent having a dry film thickness of 0.05 μm. Thereafter, a rubbing machine having a roll around which a polyamide cloth was wound was applied to this coating film, and the rubbing treatment was performed at a roll rotation speed of 500 rpm and a stage moving speed of 1 cm / sec. At this time, the presence or absence of pattern scraping or peeling was evaluated. The evaluation results are shown in Table 2.
Claims (8)
−OX1、−SX1、−OC(=O)X1、−N(X1)(X2)、−C(=O)OX1、
−C(=O)N(X1)(X2)、−P(=O)(OX1)2、−P(=O)(X1)2または重合体鎖を有する1価の基を示し、X1およびX2は相互に独立に炭素数1〜18のアルキル基、炭素数2〜18のアルケニル基、炭素数6〜18の1価の芳香族炭化水素基または炭素原子と異項原子との合計原子数3〜18の1価の複素環式基を示し、前記炭素数1〜20のアルキル基、炭素数6〜20の1価の芳香族炭化水素基、炭素原子と異項原子との合計原子数3〜20の1価の複素環式基、X1およびX2はそれぞれ置換されていてもよい。〕 [A] A copolymer having a photopolymerizable unsaturated group was produced by polymerization using a thiocarbonylthio compound represented by the following formula (1), (2) or (3) as a molecular weight control agent. The radiation-sensitive resin composition according to any one of claims 1 to 3.
-OX 1, -SX 1, -OC ( = O) X 1, -N (X 1) (X 2), - C (= O) OX 1,
-C (= O) N (X 1) (X 2), - a P (= O) (OX 1 ) 2, -P (= O) (X 1) 1 monovalent group having 2 or polymer chain X 1 and X 2 are each independently an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, a monovalent aromatic hydrocarbon group having 6 to 18 carbon atoms or a carbon atom. A monovalent heterocyclic group having 3 to 18 atoms in total with the atom, the alkyl group having 1 to 20 carbon atoms, the monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, and a carbon atom and a different group A monovalent heterocyclic group having 3 to 20 atoms in total, X 1 and X 2 may be substituted. ]
(イ)請求項5に記載の感放射線性樹脂組成物の被膜を基板上に形成する工程、
(ロ)該被膜の少なくとも一部に露光する工程、
(ハ)露光後の該被膜を現像する工程、および
(ニ)現像後の該被膜を加熱する工程。 A method for forming a spacer for a liquid crystal display element, comprising at least the following steps in the order described below.
(A) forming a film of the radiation sensitive resin composition according to claim 5 on a substrate;
(B) exposing at least a part of the coating;
(C) a step of developing the coated film after exposure, and (d) a step of heating the coated film after development.