JP2008083234A - Photosensitive composition, resin for use in the photosensitive composition, compound for use in synthesis of the resin and pattern forming method using the photosensitive composition - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a photosensitive composition which substantially avoids degradation of resist pattern profile and degradation of line edge roughness performance in liquid immersion exposure as well as in ordinary exposure (dry exposure), and a pattern forming method using the same. <P>SOLUTION: The photosensitive composition contains a compound (C) represented by formula (I): (R)<SB>n</SB>-N-(A-X)<SB>3-n</SB>, wherein R each independently, when there are a plurality of R's, represents H or a monovalent organic group; A each independently, when there are a plurality of A's, represents a divalent linking group having a bond which is broken by an acid; X each independently, when there are a plurality of X's, represents a monovalent organic group having an alicyclic hydrocarbon structure; and n represents an integer of 0-2. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

  The present invention relates to a photosensitive composition used in a semiconductor manufacturing process such as an IC, a circuit board such as a liquid crystal or a thermal head, and further in a lithography process of other photo applications, a resin used in the photosensitive composition, The present invention relates to a compound used for the synthesis of the resin and a pattern forming method using the photosensitive composition. In particular, a photosensitive composition suitable for exposure with an immersion projection exposure apparatus using far ultraviolet light having a wavelength of 300 nm or less as a light source, a resin used in the photosensitive composition, a compound used in the synthesis of the resin, and The present invention relates to a pattern forming method using the photosensitive composition.

With the miniaturization of semiconductor elements, the exposure light source has become shorter in wavelength and the projection lens has a higher numerical aperture (high NA). Currently, an exposure machine with NA 0.84 using an ArF excimer laser having a 193 nm wavelength as a light source has been developed. ing. These can be expressed by the following equations as is generally well known.
(Resolving power) = k ₁ · (λ / NA)
(Depth of focus) = ± k ₂ · λ / NA ²
Where λ is the wavelength of the exposure light source, NA is the numerical aperture of the projection lens, and k ₁ and k ₂ are coefficients related to the process.

An exposure machine using a F ₂ excimer laser having a wavelength of 157 nm as a light source has been studied for higher resolution by further shortening the wavelength. Lens materials and resists used in the exposure apparatus for shorter wavelength have been studied. Because the materials used in the process are very limited, it is very difficult to stabilize the manufacturing cost and quality of the apparatus and materials, and the exposure apparatus and resist that have sufficient performance and stability within the required period are not in time. The possibility is coming out.

As a technique for increasing the resolving power in an optical microscope, a so-called immersion method in which a high refractive index liquid (hereinafter also referred to as “immersion liquid”) is filled between a projection lens and a sample is known.
This “immersion effect” means that when λ ₀ is the wavelength of the exposure light in the air, n is the refractive index of the immersion liquid with respect to air, θ is the convergence angle of the light beam, and NA ₀ = sin θ. The above-described resolving power and depth of focus can be expressed by the following equations.
(Resolving power) = k ₁ · (λ ₀ / n) / NA ₀
(Depth of focus) = ± k ₂ · (λ ₀ / n) / NA ₀ ²
That is, the immersion effect is equivalent to using an exposure wavelength having a wavelength of 1 / n. In other words, in the case of a projection optical system with the same NA, the depth of focus can be increased n times by immersion.
This is effective for all pattern shapes, and can be combined with a super-resolution technique such as a phase shift method and a modified illumination method which are currently being studied.

Examples of apparatuses in which this effect is applied to the transfer of a fine image pattern of a semiconductor element are introduced in Patent Document 1 (Japanese Patent Laid-Open No. 57-153433), Patent Document 2 (Japanese Patent Laid-Open No. 7-220990), and the like. Yes.
Recent progress in immersion exposure technology is described in Non-Patent Document 1 (SPIE Proc 4688, 11 (2002)), Non-Patent Document 2 (J. Vac. Sci. Tecnol. B 17 (1999)), Non-Patent Document 3 (SPIE Proc 3999, 2 (2000)), Patent Document 3 (Japanese Patent Laid-Open No. 10-303114), and the like. In the case of using an ArF excimer laser as a light source, pure water (refractive index of 1.44 at 193 nm) is considered to be most promising as an immersion liquid in terms of handling safety, transmittance at 193 nm, and refractive index.
When an F ₂ excimer laser is used as a light source, a solution containing fluorine has been studied from the balance between transmittance and refractive index at 157 nm. However, a sufficient product has not yet been seen in terms of environmental safety and refractive index. It has not been issued. From the degree of immersion effect and the degree of completeness of the resist, the immersion exposure technique is considered to be installed in the ArF exposure machine earliest.

Since the resist for KrF excimer laser (248 nm), an image forming method called chemical amplification has been used as an image forming method for a resist in order to compensate for sensitivity reduction due to light absorption. Explaining by taking a positive chemical amplification image forming method as an example, the acid generator in the exposed area is decomposed by exposure to generate an acid upon exposure, and the generated acid is reacted as a reaction catalyst by post exposure baking (PEB). Is used to change an alkali-insoluble group to an alkali-soluble group, and an exposed portion is removed by alkali development.
Although the resist for ArF excimer laser (wavelength: 193 nm) using this chemical amplification mechanism is becoming mainstream at present, the resist profile change due to the placement between exposure and PEB is not sufficiently suppressed, and improvement has been desired. .

JP-A-57-153433 JP-A-7-220990 JP-A-10-303114 Proc. SPIE, 2002, Vol. 4688, p. 11 J.Vac.Sci.Tecnol.B 17 (1999) Proc. SPIE, 2000, Vol. 3999, p. 2

  The object of the present invention is to provide a photosensitive composition with little deterioration in resist pattern profile and line edge roughness performance, not only in normal exposure (dry exposure) but also in immersion exposure, a resin used in the photosensitive composition, It is to provide a pattern forming method using the compound used for the synthesis of the resin and the photosensitive composition.

  This invention is the photosensitive composition of the following structure, the compound used for this photosensitive composition, and the pattern formation method using this photosensitive composition, Thereby, the said objective of this invention is achieved.

一般式（Ｉ’）中、
Ｒは、複数ある場合は各々独立して水素原子又は１価の有機基を表す。
Ｚは、複数ある場合は各々独立して２価の有機基を表す。
Ｙは、複数ある場合は各々独立して（単環又は多環の）脂環炭化水素構造を有する１価の有機基を表す。
Ｒ₁、Ｒ₂は、各々独立してアルキル基、シクロアルキル基を表す。いずれか一方がＸと結合して環状構造を形成していてもよい。Ｒ₁やＲ₂が複数ある場合はそれぞれ同一でも異なっていてもよい。
ｎは、０〜２の整数を表す。
（４）
上記（１）〜（３）のいずれかに記載の感光性組成物により、感光性膜を形成し、該感光性膜を露光、現像する工程を含むことを特徴とするパターン形成方法。
（５）
一般式（Ｉ’）で表されることを特徴とする化合物。

一般式（Ｉ’）中、
Ｒは、複数ある場合は各々独立して水素原子又は１価の有機基を表す。
Ｚは、複数ある場合は各々独立して２価の有機基を表す。
Ｙは、複数ある場合は各々独立して脂環炭化水素構造を有する１価の有機基を表す。
Ｒ₁、Ｒ₂は、各々独立してアルキル基、シクロアルキル基を表す。いずれか一方がＸと結合して環状構造を形成していてもよい。Ｒ₁やＲ₂が複数ある場合はそれぞれ同一でも異なっていてもよい。
ｎは、０〜２の整数を表す。 (1)
A photosensitive composition comprising a compound (C) represented by the following general formula (I):
(R) _n -N- (AX) _3-n (I)
In general formula (I),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
A represents a divalent linking group having a bond that is independently cleaved by an acid when there are a plurality of A's.
X represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Xs.
n represents an integer of 0 to 2.
(2)
The photosensitive composition as described in (1) above, wherein, in the general formula (I), A is a divalent linking group containing a tertiary ester moiety.
(3)
The photosensitive composition as described in (1) or (2) above, wherein the compound (C) is a compound represented by the following general formula (I ′).

In general formula (I ′),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
When there are a plurality of Z, each Z independently represents a divalent organic group.
Y represents a monovalent organic group having an alicyclic hydrocarbon structure (monocyclic or polycyclic) independently when there are a plurality of Y.
R ₁ and R ₂ each independently represents an alkyl group or a cycloalkyl group. Any one of them may be bonded to X to form a cyclic structure. When there are a plurality of R ₁ and R _{2 s} , they may be the same or different.
n represents an integer of 0 to 2.
(4)
A pattern forming method comprising: forming a photosensitive film from the photosensitive composition according to any one of (1) to (3) above; and exposing and developing the photosensitive film.
(5)
The compound represented by general formula (I ').

In general formula (I ′),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
When there are a plurality of Z, each Z independently represents a divalent organic group.
Y represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Y's.
R ₁ and R ₂ each independently represents an alkyl group or a cycloalkyl group. Any one of them may be bonded to X to form a cyclic structure. When there are a plurality of R ₁ and R _{2 s} , they may be the same or different.
n represents an integer of 0 to 2.

  Furthermore, the following structures are mentioned as a preferable embodiment of this invention.

(7)
Furthermore, (B) The photosensitive composition in any one of said (1)-(3) characterized by including the compound which generate | occur | produces an acid by irradiation of actinic light or a radiation.

(8)
The photosensitive composition according to (7) above, wherein the compound of component (B) is a fluorinated substituted alkanesulfonic acid, a fluorine-substituted benzenesulfonic acid, or a sulfonium salt of a fluorine-substituted imide acid.

(9)
Further, (A) any one of the above (1) to (3), (7) and (8), which contains a resin that decomposes by the action of an acid and increases the solubility in an alkaline developer. The positive photosensitive composition described in 1.

(10)
The positive photosensitive composition as described in (9) above, wherein the resin of component (A) has a fluorine atom in the main chain or side chain.

(11)
The positive photosensitive composition as described in (9) above, wherein the resin as the component (A) has a hexafluoroisopropanol structure.

(12)
The positive photosensitive composition as described in (9) above, wherein the resin as the component (A) has a hydroxystyrene structural unit.

(13)
The resin of component (A) has at least one repeating unit selected from 2-alkyl-2-adamantyl (meth) acrylate and dialkyl (1-adamantyl) methyl (meth) acrylate (9) The positive photosensitive composition described in 1.

(14)
The positive photosensitive composition as described in (9) above, wherein the resin as the component (A) has a monocyclic or polycyclic alicyclic hydrocarbon structure.

(15)
The component (A) resin is at least one type of repeating unit selected from 2-alkyl-2-adamantyl (meth) acrylate and dialkyl (1-adamantyl) methyl (meth) acrylate, and at least one type of repeating unit having a lactone structure. The positive photosensitive composition as described in (14), which has at least one type of repeating unit having a unit and a hydroxyl group.

(16)
The positive photosensitive composition as described in (15), wherein the resin as the component (A) further has a repeating unit having a carboxyl group.

(17)
The positive photosensitive composition as described in (9) above, wherein the resin as component (A) has a silicon atom in the main chain or side chain.

(18)
The positive photosensitive composition as described in (9) above, wherein the resin as the component (A) has a repeating unit having a lactone structure.

(19)
The positive electrode according to any one of (9) to (18) above, further comprising a dissolution inhibiting compound having a molecular weight of 3000 or less, which decomposes by the action of an acid and increases the solubility in an alkaline developer. Type photosensitive composition.

(20)
(1) to (1) above, further comprising a dissolution inhibiting compound having a molecular weight of 3000 or less, which is decomposed by the action of a resin soluble in an alkali developer and an acid to increase the solubility in the alkali developer. 3) The positive photosensitive composition according to any one of (7) and (8).

(21)
Furthermore, it contains an acid cross-linking agent that crosslinks a resin soluble in an alkaline developer and a resin soluble in the alkaline developer by the action of an acid, (1) to (3), (7) And the negative photosensitive composition in any one of (8).

(22)
The photosensitive composition according to any one of (1) to (4) and (7) to (21) above, further comprising a basic compound and / or fluorine and / or a silicon-based surfactant. object.

(23)
A compound in which the basic compound has a structure selected from an imidazole structure, a diazabicyclo structure, an onium hydroxide structure, an onium carboxylate structure, a trialkylamine structure, an aniline structure and a pyridine structure, an alkylamine derivative having a hydroxyl group and / or an ether bond Or the photosensitive composition as described in (22) which is an aniline derivative which has a hydroxyl group and / or an ether bond.

  According to the present invention, there is provided a photosensitive composition with little deterioration in resist pattern profile and line edge roughness performance, not only in normal exposure (dry exposure) but also in immersion exposure, a pattern forming method using the photosensitive composition, and A compound in the photosensitive composition can be provided. Also provided are a photosensitive composition suitable for immersion exposure, the above-mentioned performance being good also in immersion exposure, a pattern forming method using the photosensitive composition, and a compound in the photosensitive composition. Can do.

Hereinafter, the present invention will be described in detail.
In addition, in the description of the group (atomic group) in this specification, the description which does not describe substitution and non-substitution includes what does not have a substituent and what has a substituent. . For example, the “alkyl group” includes not only an alkyl group having no substituent (unsubstituted alkyl group) but also an alkyl group having a substituent (substituted alkyl group).

  The positive photosensitive composition of the present invention, more preferably the positive resist composition, is decomposed by the action of the compound (C) that generates the organic acid represented by the general formula (I) and the acid, in an alkaline developer. Containing a resin (A) that increases the solubility in water, and further, if necessary, the compound (B) that generates an acid upon irradiation with actinic rays or radiation, and the solubility in an alkali developer by decomposition by the action of the acid. Decomposes by the action of compound (C) which generates an organic acid represented by the general formula (I), an alkali developer, and an acid which contains an increasing dissolution inhibiting compound having a molecular weight of 3000 or less And a dissolution inhibiting compound having a molecular weight of 3000 or less that increases the solubility in an alkaline developer, and further contains a compound (B) that generates an acid upon irradiation with actinic rays or radiation as necessary.

  The negative photosensitive composition of the present invention, more preferably the negative resist composition, comprises a compound (C) that generates an organic acid represented by the general formula (I), a resin soluble in an alkaline developer, and an acid. It contains an acid crosslinking agent that crosslinks with a resin soluble in the alkali developer by action, and further contains a compound (B) that generates an acid upon irradiation with actinic rays or radiation as necessary.

(A) Resin whose solubility in an alkaline developer is increased by the action of an acid The resin used in the photosensitive composition of the present invention is a resin that is decomposed by the action of an acid and increases its solubility in an alkaline developer. Resin having a group (hereinafter also referred to as “acid-decomposable group”) that decomposes by the action of an acid to generate an alkali-soluble group (hereinafter also referred to as “acid-decomposable group”) on the main chain or side chain, or both of the main chain and side chain Resin "," acid-decomposable resin (A) "or" resin (A) ").
Alkali-soluble groups include phenolic hydroxyl groups, carboxylic acid groups, fluorinated alcohol groups, sulfonic acid groups, sulfonamido groups, sulfonylimide groups, (alkylsulfonyl) (alkylcarbonyl) methylene groups, (alkylsulfonyl) (alkylcarbonyl) Imido group, bis (alkylcarbonyl) methylene group, bis (alkylcarbonyl) imide group, bis (alkylsulfonyl) methylene group, bis (alkylsulfonyl) imide group, tris (alkylcarbonyl) methylene group, tris (alkylsulfonyl) methylene group A group having
Preferred alkali-soluble groups include carboxylic acid groups, fluorinated alcohol groups (preferably hexafluoroisopropanol), and sulfonic acid groups.
A preferred group as an acid-decomposable group (acid-decomposable group) is a group obtained by substituting the hydrogen atom of these alkali-soluble groups with a group capable of leaving with an acid.
Examples of the group leaving with an acid include -C (R ₃₆ ) (R ₃₇ ) (R ₃₈ ), -C (R ₃₆ ) (R ₃₇ ) (OR ₃₉ ), -C (R ₀₁ ) (R ₀₂ ). ) (OR ₃₉ ) and the like.
In the formula, R _{36 to} R ₃₉ each independently represents an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, or an alkenyl group. R ₃₆ and R ₃₇ may be bonded to each other to form a ring.
R _{01 and} R ₀₂ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkenyl group.
The acid-decomposable group is preferably a cumyl ester group, an enol ester group, an acetal ester group, a tertiary alkyl ester group or the like. More preferably, it is a tertiary alkyl ester group.

  When the photosensitive composition of the present invention is irradiated with ArF excimer laser light, the acid-decomposable resin is decomposed by the action of an acid having a monocyclic or polycyclic alicyclic hydrocarbon structure, and is applied to an alkaline developer. A resin whose solubility is increased is preferable.

  As a resin that has a monocyclic or polycyclic alicyclic hydrocarbon structure, decomposes by the action of an acid, and increases its solubility in an alkaline developer (hereinafter also referred to as “alicyclic hydrocarbon-based acid-decomposable resin”) , At least selected from the group consisting of repeating units having a partial structure containing an alicyclic hydrocarbon represented by the following general formula (pI) to general formula (pV) and repeating units represented by the following general formula (II-AB) It is preferable that it is resin containing 1 type.

In general formulas (pI) to (pV),
R ₁₁ represents a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group or a sec-butyl group, and Z is an atom necessary for forming a cycloalkyl group together with a carbon atom. Represents a group.
R _{12 to} R ₁₆ each independently represents a linear or branched alkyl group or cycloalkyl group having 1 to 4 carbon atoms. However, at least one of R _{12 to} R ₁₄ , or any of R ₁₅ and R ₁₆ represents a cycloalkyl group.
R _{17 to} R ₂₁ each independently represents a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, or a cycloalkyl group. However, at least one of R _{17 to} R ₂₁ represents a cycloalkyl group. Further, either R ₁₉ or R ₂₁ represents a linear or branched alkyl group or cycloalkyl group having 1 to 4 carbon atoms.
R _{22 to} R ₂₅ each independently represents a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, or a cycloalkyl group. However, at least one of R _{22 to} R ₂₅ represents a cycloalkyl group. R ₂₃ and R ₂₄ may be bonded to each other to form a ring.

In general formula (II-AB),
R ₁₁ ′ and R ₁₂ ′ each independently represents a hydrogen atom, a cyano group, a halogen atom or an alkyl group.
Z ′ represents an atomic group for forming an alicyclic structure containing two bonded carbon atoms (C—C).

  The general formula (II-AB) is more preferably the following general formula (II-AB1) or general formula (II-AB2).

In the formulas (II-AB1) and (II-AB2),
R ₁₃ ′ to R ₁₆ ′ each independently represents a hydrogen atom, a halogen atom, a cyano group, —COOH, —COOR ₅ , a group that decomposes by the action of an acid, —C (═O) —XA′—R. ₁₇ ′ represents an alkyl group or a cycloalkyl group. At least two of R ₁₃ ′ to R ₁₆ ′ may combine to form a ring.
Here, R ₅ represents an alkyl group, a cycloalkyl group, or a group having a lactone structure.
X represents an oxygen atom, a sulfur atom, -NH -, - NHSO ₂ - or an -NHSO ₂ NH-.
A ′ represents a single bond or a divalent linking group.
R ₁₇ ′ represents —COOH, —COOR ₅ , —CN, a hydroxyl group, an alkoxy group, —CO—NH—R ₆ , —CO—NH—SO ₂ —R ₆ or a group having a lactone structure.
R ₆ represents an alkyl group or a cycloalkyl group.
n represents 0 or 1.

In the general formulas (pI) to (pV), the alkyl group in R _{12 to} R ₂₅ represents a linear or branched alkyl group having 1 to 4 carbon atoms.

The cycloalkyl group in R _{11 to} R ₂₅ or the cycloalkyl group formed by Z and the carbon atom may be monocyclic or polycyclic. Specific examples include groups having a monocyclo, bicyclo, tricyclo, tetracyclo structure or the like having 5 or more carbon atoms. The carbon number is preferably 6-30, and particularly preferably 7-25. These cycloalkyl groups may have a substituent.

  Preferred cycloalkyl groups include adamantyl group, noradamantyl group, decalin residue, tricyclodecanyl group, tetracyclododecanyl group, norbornyl group, cedrol group, cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group, A cyclodecanyl group and a cyclododecanyl group can be mentioned. More preferable examples include an adamantyl group, norbornyl group, cyclohexyl group, cyclopentyl group, tetracyclododecanyl group, and tricyclodecanyl group.

  As further substituents of these alkyl groups and cycloalkyl groups, alkyl groups (1 to 4 carbon atoms), halogen atoms, hydroxyl groups, alkoxy groups (1 to 4 carbon atoms), carboxyl groups, alkoxycarbonyl groups (carbon numbers) 2-6). Examples of the substituent that the alkyl group, alkoxy group, alkoxycarbonyl group and the like may further have include a hydroxyl group, a halogen atom, and an alkoxy group.

  The structures represented by the general formulas (pI) to (pV) in the resin can be used for protecting alkali-soluble groups. Examples of the alkali-soluble group include various groups known in this technical field.

  Specific examples include a structure in which a hydrogen atom of a carboxylic acid group, a sulfonic acid group, a phenol group, or a thiol group is substituted with a structure represented by the general formulas (pI) to (pV), preferably a carboxylic acid Group, a hydrogen atom of a sulfonic acid group is substituted with a structure represented by general formulas (pI) to (pV).

  As the repeating unit having an alkali-soluble group protected by the structure represented by the general formulas (pI) to (pV), a repeating unit represented by the following general formula (pA) is preferable.

Here, R represents a hydrogen atom, a halogen atom, or a linear or branched alkyl group having 1 to 4 carbon atoms. A plurality of R may be the same or different.
A represents a single bond, an alkylene group, an ether group, a thioether group, a carbonyl group, an ester group, an amide group, a sulfonamide group, a urethane group, or a urea group, or a combination of two or more groups. Represents. A single bond is preferable.
Rp ₁ represents any group of the above formulas (pI) to (pV).

  The repeating unit represented by the general formula (pA) is particularly preferably a repeating unit composed of 2-alkyl-2-adamantyl (meth) acrylate and dialkyl (1-adamantyl) methyl (meth) acrylate.

  Hereinafter, although the specific example of the repeating unit shown by general formula (pA) is shown, this invention is not limited to this.

Examples of the halogen atom in the general formula (II-AB), R ₁₁ ′, and R ₁₂ ′ include a chlorine atom, a bromine atom, a fluorine atom, and an iodine atom.

Examples of the alkyl group in R ₁₁ ′ and R ₁₂ ′ include a linear or branched alkyl group having 1 to 10 carbon atoms.

  The atomic group for forming the alicyclic structure of Z ′ is an atomic group that forms a repeating unit of an alicyclic hydrocarbon which may have a substituent in a resin, and among them, a bridged type alicyclic group. An atomic group for forming a bridged alicyclic structure forming a cyclic hydrocarbon repeating unit is preferred.

Examples of the skeleton of the alicyclic hydrocarbon formed include those similar to the alicyclic hydrocarbon groups of R _{12 to} R _{25 in} the general formulas (pI) to (pVI).

The alicyclic hydrocarbon skeleton may have a substituent. Examples of such a substituent include R ₁₃ ′ to R ₁₆ ′ in the general formula (II-AB1) or (II-AB2).

  In the alicyclic hydrocarbon-based acid-decomposable resin according to the present invention, the group decomposed by the action of an acid has a partial structure containing the alicyclic hydrocarbon represented by the general formula (pI) to the general formula (pV). It can be contained in at least one kind of repeating unit among the repeating unit having, the repeating unit represented by formula (II-AB), and the repeating unit of the copolymerization component described later.

Various substituents of R ₁₃ ′ to R ₁₆ ′ in the general formula (II-AB1) or the general formula (II-AB2) are atomic groups for forming an alicyclic structure in the general formula (II-AB). It can also be a substituent of the atomic group Z for forming a bridged alicyclic structure.

  Specific examples of the repeating unit represented by the general formula (II-AB1) or (II-AB2) include the following specific examples, but the present invention is not limited to these specific examples.

  The resin A of the present invention preferably has a lactone group. As the lactone group, any group can be used as long as it contains a lactone structure, but preferably a group containing a 5- to 7-membered ring lactone structure, and a bicyclo structure in the 5- to 7-membered ring lactone structure, Those in which other ring structures are condensed to form a spiro structure are preferred. It is more preferable to have a repeating unit having a group having a lactone structure represented by any of the following general formulas (LC1-1) to (LC1-16). Further, a group having a lactone structure may be directly bonded to the main chain. Preferred lactone structures are groups represented by general formulas (LC1-1), (LC1-4), (LC1-5), (LC1-6), (LC1-13), (LC1-14), By using a specific lactone structure, line edge roughness and development defects are improved.

The lactone structure moiety may or may not have a substituent (Rb ₂ ). Preferred substituents (Rb ₂ ) include an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 4 to 7 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkoxycarbonyl group having 1 to 8 carbon atoms, and a carboxyl group. , Halogen atom, hydroxyl group, cyano group, acid-decomposable group and the like. n2 represents an integer of 0 to 4. When n2 is 2 or more, a plurality of Rb ₂ may be the same or different, and a plurality of Rb ₂ may be bonded to form a ring.

As the repeating unit having a group having a lactone structure represented by any of the general formulas (LC1-1) to (LC1-16), R _{13 in the} above general formula (II-AB1) or (II-AB2) may be used. Wherein at least one of 'to R ₁₆ ' has a group represented by the general formulas (LC1-1) to (LC1-16) (for example, R _{5 of} -COOR ₅ is represented by the general formulas (LC1-1) to (LC1) -16) or a repeating unit represented by the following general formula (AI).

In general formula (AI),
Rb ₀ represents a hydrogen atom, a halogen atom, or an alkyl group having 1 to 4 carbon atoms.
Preferred substituents that the alkyl group represented by Rb ₀ may have include a hydroxyl group and a halogen atom.
Examples of the halogen atom for Rb ₀ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
Rb ₀ is preferably a hydrogen atom or a methyl group.
Ab represents a single bond, an alkylene group, a divalent linking group having a monocyclic or polycyclic alicyclic hydrocarbon structure, an ether group, an ester group, a carbonyl group, a carboxyl group, or a divalent group obtained by combining these. To express. A linking group represented by a single bond or —Ab ₁ —CO ₂ — is preferable.
Ab ₁ is a linear, branched alkylene group, monocyclic or polycyclic cycloalkylene group, preferably a methylene group, an ethylene group, a cyclohexylene group, an adamantylene group or a norbornylene group.
V represents a group represented by any one of the general formulas (LC1-1) to (LC1-16).

  The repeating unit having a lactone structure usually has an optical isomer, but any optical isomer may be used. One optical isomer may be used alone, or a plurality of optical isomers may be mixed and used. When one kind of optical isomer is mainly used, the optical purity (ee) thereof is preferably 90 or more, more preferably 95 or more.

  Specific examples of the repeating unit having a group having a lactone structure are given below, but the present invention is not limited thereto.

The resin A of the present invention preferably has a repeating unit containing an organic group having a polar group, particularly a repeating unit having an alicyclic hydrocarbon structure substituted with a polar group. This improves the substrate adhesion and developer compatibility. The alicyclic hydrocarbon structure of the alicyclic hydrocarbon structure substituted with a polar group is preferably an adamantyl group, a diamantyl group, or a norbornane group. The polar group is preferably a hydroxyl group or a cyano group.
As the alicyclic hydrocarbon structure substituted with a polar group, partial structures represented by the following general formulas (VIIa) to (VIId) are preferable.

In general formulas (VIIa) to (VIIc),
R _{2c to} R _4c each independently represents a hydrogen atom, a hydroxyl group or a cyano group. However, at least one of R _{2c to} R _4c represents a hydroxyl group or a cyano group. Preferably, one or two of R _{2c to} R _4c are a hydroxyl group and the rest are hydrogen atoms.
In general formula (VIIa), it is more preferable that two members out of R _{2c to} R _4c are a hydroxyl group and the remaining is a hydrogen atom.

As the repeating unit having a group represented by the general formulas (VIIa) to (VIId), at least one of R ₁₃ ′ to R ₁₆ ′ in the general formula (II-AB1) or (II-AB2) is the above. has a group represented by the general formula (VII) (e.g., represents a group R ₅ in -COOR ₅ is a represented by the general formula (VIIa) ~ (VIId)) , or the following general formula (AIIa) ~ ( A repeating unit represented by AId) can be mentioned.

In general formulas (AIIa) to (AIId),
R _1c represents a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.
R _2c to R _4c have the same meanings as R _2c to R _4c in formulas (VIIa) ~ (VIIc).

  Although the specific example of the repeating unit which has a structure represented by general formula (AIIa)-(AIId) is given to the following, this invention is not limited to these.

  The resin A of the present invention may have a repeating unit represented by the following general formula (VIII).

In the above general formula (VIII),
Z ₂ represents —O— or —N (R ₄₁ ) —. R ₄₁ represents a hydrogen atom, a hydroxyl group, an alkyl group, or —OSO ₂ —R ₄₂ . R ₄₂ represents an alkyl group, a cycloalkyl group or a camphor residue. The alkyl group of R ₄₁ and R ₄₂ may be substituted with a halogen atom (preferably a fluorine atom) or the like.

  Examples of the repeating unit represented by the general formula (VIII) include the following specific examples, but the present invention is not limited thereto.

  The resin A of the present invention preferably has a repeating unit having an alkali-soluble group, and more preferably has a repeating unit having a carboxyl group. By containing this, the resolution in contact hole applications increases. The repeating unit having a carboxyl group includes a repeating unit in which a carboxyl group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or a carboxyl group in the main chain of the resin through a linking group. Either a repeating unit that is bonded, or a polymerization initiator or chain transfer agent having an alkali-soluble group is introduced at the end of the polymer chain at the time of polymerization, and the linking group is a monocyclic or polycyclic hydrocarbon. You may have a structure. Particularly preferred are repeating units of acrylic acid or methacrylic acid.

  The resin A of the present invention may further have a repeating unit having 1 to 3 groups represented by the general formula (F1). This improves line edge roughness performance.

In general formula (F1),
R _{50 to} R ₅₅ each independently represents a hydrogen atom, a fluorine atom or an alkyl group. However, at least one of R _{50 to} R ₅₅ represents a fluorine atom or an alkyl group in which at least one hydrogen atom is substituted with a fluorine atom.
Rx represents a hydrogen atom or an organic group (preferably an acid-decomposable protecting group, an alkyl group, a cycloalkyl group, an acyl group, or an alkoxycarbonyl group).

The alkyl group of R _{50 to} R ₅₅ may be substituted with a halogen atom such as a fluorine atom, a cyano group, etc., preferably an alkyl group having 1 to 3 carbon atoms, such as a methyl group or a trifluoromethyl group. be able to.
R _{50 to} R ₅₅ are preferably all fluorine atoms.

  Examples of the organic group represented by Rx include an acid-decomposable protective group and an optionally substituted alkyl group, cycloalkyl group, acyl group, alkylcarbonyl group, alkoxycarbonyl group, alkoxycarbonylmethyl group, alkoxymethyl group. , 1-alkoxyethyl group is preferable.

  The repeating unit having a group represented by the general formula (F1) is preferably a repeating unit represented by the following general formula (F2).

In general formula (F2),
Rx represents a hydrogen atom, a halogen atom, or an alkyl group having 1 to 4 carbon atoms. Preferable substituents that the alkyl group of Rx may have include a hydroxyl group and a halogen atom.
Fa represents a single bond or a linear or branched alkylene group (preferably a single bond).
Fb represents a monocyclic or polycyclic hydrocarbon group.
Fc represents a single bond or a linear or branched alkylene group (preferably a single bond or a methylene group).
F ₁ represents a group represented by the general formula (F1).
P ₁ represents a 1 to 3.
The cyclic hydrocarbon group for Fb is preferably a cyclopentyl group, a cyclohexyl group, or a norbornyl group.

  Specific examples of the repeating unit having a group represented by the general formula (F1) are shown below, but the present invention is not limited thereto.

  The resin A of the present invention may further contain a repeating unit having an alicyclic hydrocarbon structure and not exhibiting acid decomposability. This can reduce the elution of low molecular components from the resist film to the immersion liquid during immersion exposure. Examples of such a repeating unit include 1-adamantyl (meth) acrylate, tricyclodecanyl (meth) acrylate, and cyclohexyl (meth) acrylate.

  In addition to the above repeating structural units, the resin A of the present invention has dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and general necessary properties of resist, such as resolution, heat resistance, and sensitivity. Various repeating structural units can be contained for the purpose of adjustment.

  Examples of such repeating structural units include, but are not limited to, repeating structural units corresponding to the following monomers.

  As a result, performance required for the alicyclic hydrocarbon-based acid-decomposable resin, in particular, (1) solubility in coating solvent, (2) film-forming property (glass transition temperature), (3) alkali developability, (4 Fine adjustments such as () film slippage (selection of hydrophilicity / hydrophobicity, alkali-soluble group), (5) adhesion of unexposed part to substrate, (6) dry etching resistance, etc. are possible.

  As such a monomer, for example, a compound having one addition polymerizable unsaturated bond selected from acrylic acid esters, methacrylic acid esters, acrylamides, methacrylamides, allyl compounds, vinyl ethers, vinyl esters, etc. Etc.

  In addition, any addition-polymerizable unsaturated compound that can be copolymerized with monomers corresponding to the above various repeating structural units may be copolymerized.

  In the resin (A), the molar ratio of each repeating structural unit is the resist dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and the general required performance of the resist, resolving power, heat resistance, sensitivity. It is set appropriately in order to adjust etc.

The following are mentioned as a preferable aspect of resin A of this invention.
(1) What contains the repeating unit which has a partial structure containing the alicyclic hydrocarbon represented by said general formula (pI)-(pV) (side chain type).
Preferably those containing (meth) acrylate repeating units having a structure of (pI) to (pV).
(2) One containing a repeating unit represented by the general formula (II-AB) (main chain type).
However, in (2), for example, the following can be further mentioned.
(3) A repeating unit represented by the general formula (II-AB), a maleic anhydride derivative and a (meth) acrylate structure (hybrid type).

  In the resin (A), the content of the repeating unit having an acid-decomposable group is preferably 10 to 60 mol%, more preferably 20 to 50 mol%, still more preferably 25 to 40 mol% in all repeating structural units. is there.

  In the acid-decomposable resin, the content of the repeating unit having an acid-decomposable group is preferably 10 to 60 mol%, more preferably 20 to 50 mol%, still more preferably 25 to 40 mol% in all repeating structural units. is there.

  In the resin (A), the content of the repeating unit having a partial structure containing an alicyclic hydrocarbon represented by the general formulas (pI) to (pV) is preferably 20 to 70 mol% in all repeating structural units, More preferably, it is 20-50 mol%, More preferably, it is 25-40 mol%.

  In the resin (A), the content of the repeating unit represented by the general formula (II-AB) is preferably 10 to 60 mol%, more preferably 15 to 55 mol%, still more preferably 20 in all repeating structural units. ˜50 mol%.

In the acid-decomposable resin, the content of the repeating unit having a lactone ring is preferably 10 to 70 mol%, more preferably 20 to 60 mol%, still more preferably 25 to 40 mol% in all repeating structural units.
In the acid-decomposable resin, the content of the repeating unit having an organic group having a polar group is preferably 1 to 40 mol%, more preferably 5 to 30 mol%, still more preferably 5 to 20 mol in all repeating structural units. %.

  In addition, the content of the repeating structural unit based on the monomer of the further copolymer component in the resin can also be appropriately set according to the performance of the desired resist. ) To 99 p% with respect to the total number of moles of the repeating structural unit having a partial structure containing an alicyclic hydrocarbon represented by (pV) and the repeating unit represented by the general formula (II-AB). The following is preferable, More preferably, it is 90 mol% or less, More preferably, it is 80 mol% or less.

  When the photosensitive composition of the present invention is for ArF exposure, the resin preferably does not have an aromatic group from the viewpoint of transparency to ArF light.

  The resin A used in the present invention is preferably one in which all repeating units are composed of (meth) acrylate repeating units. In this case, all of the repeating units may be methacrylate repeating units, all of the repeating units may be acrylate repeating units, and all of the repeating units may be any mixture of methacrylate repeating units / acrylate repeating units, It is preferable that the acrylate repeating unit is 50 mol% or less of the entire repeating unit.

  Resin A has at least a (meth) acrylate repeating unit having a lactone ring, a (meth) acrylate repeating unit having an organic group substituted with at least one of a hydroxyl group and a cyano group, and an acid-decomposable group. A copolymer having three types of repeating units of (meth) acrylate-based repeating units is preferred.

  Preferably, 20 to 50 mol% of repeating units having a partial structure containing an alicyclic hydrocarbon represented by general formulas (pI) to (pV), 20 to 50 mol% of repeating units having a lactone structure, substituted with a polar group It is a ternary copolymer containing 5 to 30% of repeating units having an alicyclic hydrocarbon structure, or a quaternary copolymer containing 0 to 20% of other repeating units.

  Particularly preferable resins include 20 to 50 mol% of repeating units having an acid-decomposable group represented by the following general formulas (ARA-1) to (ARA-5), and the following general formulas (ARL-1) to (ARL- 6) 50 to 50 mol% of a repeating unit having a lactone group represented by formula (6), and a repeating unit having an alicyclic hydrocarbon structure substituted with a polar group represented by the following general formulas (ARH-1) to (ARH-3) A ternary copolymer containing 5 to 30 mol% of units, or a carboxyl group, or a repeating unit having a structure represented by the general formula (F1), having an alicyclic hydrocarbon structure and not exhibiting acid decomposability It is a quaternary copolymer containing 5 to 20 mol% of repeating units.

(In the formula, Rxy1 represents a hydrogen atom or a methyl group, and Rxa1 and Rxb1 represent a methyl group or an ethyl group.)

  The resin (A) used in the present invention can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and the polymerization is performed by heating, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable. Examples of the reaction solvent include ethers such as tetrahydrofuran, 1,4-dioxane, diisopropyl ether, ketones such as methyl ethyl ketone and methyl isobutyl ketone, ester solvents such as ethyl acetate, amide solvents such as dimethylformamide and dimethylacetamide, Furthermore, the solvent which melt | dissolves the composition of this invention like the below-mentioned propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, and cyclohexanone is mentioned. More preferably, the polymerization is performed using the same solvent as that used in the resist composition of the present invention. Thereby, generation | occurrence | production of the particle at the time of a preservation | save can be suppressed.

The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred examples of the initiator include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. If desired, an initiator is added or added in portions, and after completion of the reaction, it is put into a solvent and a desired polymer is recovered by a method such as powder or solid recovery. The concentration of the reaction is 5 to 50% by mass, preferably 10 to 30% by mass.
The reaction temperature is usually 10 ° C to 150 ° C, preferably 30 ° C to 120 ° C, more preferably 60-100 ° C.

The weight average molecular weight of the resin according to the present invention is preferably 1,000 to 200,000, more preferably 3,000 to 20,000, and most preferably 5,000 to 15 in terms of polystyrene by GPC method. , 000. By setting the weight average molecular weight to 1,000 to 200,000, deterioration of heat resistance and dry etching resistance can be prevented, developability is deteriorated, and viscosity is increased, resulting in deterioration of film forming property. Can be prevented.
The degree of dispersion (molecular weight distribution) is usually 1 to 5, preferably 1 to 3, more preferably 1.2 to 3.0, particularly preferably 1.2 to 2.0. . The smaller the degree of dispersion, the better the resolution and the resist shape, the smoother the side wall of the resist pattern, and the better the roughness.

In the positive resist composition of the present invention, the blending amount of all the resins according to the present invention in the entire composition is preferably 50 to 99.9% by mass, more preferably 60 to 99.0% by mass in the total solid content. %.
In the present invention, the resins may be used alone or in combination.

  The resin (A) of the present invention preferably contains no fluorine atom or silicon atom.

(B) Compound that generates acid upon irradiation with actinic ray or radiation The photosensitive composition of the present invention is a compound that generates acid upon irradiation with actinic ray or radiation ("photo acid generator" or "component (B)"). Contain).
Examples of such photoacid generators include photoinitiators for photocationic polymerization, photoinitiators for photoradical polymerization, photodecolorants for dyes, photochromic agents, actinic rays used in microresists, etc. Known compounds that generate an acid upon irradiation with radiation and mixtures thereof can be appropriately selected and used.

  Examples thereof include diazonium salts, phosphonium salts, sulfonium salts, iodonium salts, imide sulfonates, oxime sulfonates, diazodisulfones, disulfones, and o-nitrobenzyl sulfonates.

  Further, a group that generates an acid upon irradiation with these actinic rays or radiation, or a compound in which a compound is introduced into the main chain or side chain of the polymer, for example, US Pat. No. 3,849,137, German Patent No. 3914407. JP, 63-26653, JP, 55-164824, JP, 62-69263, JP, 63-146038, JP, 63-163452, JP, 62-153853, The compounds described in JP-A 63-146029 can be used.

  Furthermore, compounds capable of generating an acid by light described in US Pat. No. 3,779,778, European Patent 126,712 and the like can also be used.

  Among the compounds that decompose upon irradiation with actinic rays or radiation to generate an acid, compounds represented by the following general formulas (ZI), (ZII), and (ZIII) can be exemplified.

In the above general formula (ZI), R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.
X ⁻ represents a non-nucleophilic anion, preferably sulfonate anion, carboxylate anion, bis (alkylsulfonyl) amide anion, tris (alkylsulfonyl) methide anion, BF ₄ ⁻ , PF ₆ ⁻ , SbF ₆ ^{− and the} like. Preferably, it is an organic anion containing a carbon atom.

  Preferable organic anions include organic anions represented by the following formula.

Where
Rc ₁ represents an organic group.
Examples of the organic group in Rc ₁ include those having 1 to 30 carbon atoms, and preferably an alkyl group, an aryl group, or a plurality thereof, which may be substituted, is a single bond, —O—, —CO ₂ —, — Examples include groups linked by a linking group such as S-, -SO _3- , -SO ₂ N (Rd ₁ )-. Rd ₁ represents a hydrogen atom or an alkyl group.
Rc ₃ , Rc ₄ and Rc ₅ each independently represents an organic group. Preferred examples of the organic group for Rc ₃ , Rc ₄ , and Rc ₅ include the same organic groups as those for Rc _1, and a perfluoroalkyl group having 1 to 4 carbon atoms is most preferred.
Rc ₃ and Rc ₄ may combine to form a ring. Examples of the group formed by combining Rc ₃ and Rc ₄ include an alkylene group and an arylene group. Preferably, it is a C2-C4 perfluoroalkylene group.
The organic group of Rc ₁ and Rc _{3 to} Rc ₅ is particularly preferably an alkyl group substituted at the 1-position with a fluorine atom or a fluoroalkyl group, or a phenyl group substituted with a fluorine atom or a fluoroalkyl group. By having a fluorine atom or a fluoroalkyl group, the acidity of the acid generated by light irradiation is increased and the sensitivity is improved. Further, when Rc ₃ and Rc ₄ are combined to form a ring, the acidity of the acid generated by light irradiation is increased, and the sensitivity is improved.

The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1-30, preferably 1-20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. The two of the group formed by bonding of the R ₂₀₁ to R _203, there can be mentioned an alkylene group (e.g., butylene, pentylene).
Specific examples of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ include corresponding groups in the compounds (ZI-1), (ZI-2) and (ZI-3) described later.

In addition, the compound which has two or more structures represented by general formula (ZI) may be sufficient. For example, the general formula at least one of R ₂₀₁ to R ₂₀₃ of a compound represented by (ZI) is, at least one bond with structure of R ₂₀₁ to R ₂₀₃ of another compound represented by formula (ZI) It may be a compound.

  More preferable (ZI) components include compounds (ZI-1), (ZI-2), and (ZI-3) described below.

The compound (ZI-1) is at least one of the aryl groups R ₂₀₁ to R ₂₀₃ in formula (ZI), arylsulfonium compound, i.e., a compound having arylsulfonium as a cation.
In the arylsulfonium compound, all of R _{201 to} R ₂₀₃ may be an aryl group, or a part of R _{201 to} R ₂₀₃ may be an aryl group, and the rest may be an alkyl group or a cycloalkyl group.
Examples of the arylsulfonium compound include triarylsulfonium compounds, diarylalkylsulfonium compounds, aryldialkylsulfonium compounds, diarylcycloalkylsulfonium compounds, and aryldicycloalkylsulfonium compounds.
The aryl group of the arylsulfonium compound is preferably an aryl group such as a phenyl group or a naphthyl group, or a heteroaryl group such as an indole residue or a pyrrole residue, more preferably a phenyl group or an indole residue. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.
The alkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an n-butyl group, sec- Examples thereof include a butyl group and a t-butyl group.
The cycloalkyl group that the arylsulfonium compound has as necessary is preferably a cycloalkyl group having 3 to 15 carbon atoms, and examples thereof include a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.
Aryl group, alkyl group of R ₂₀₁ to R _203, cycloalkyl group, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (for example, 6 to 14 carbon atoms) , An alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, or a phenylthio group may be substituted. Preferred substituents are linear or branched alkyl groups having 1 to 12 carbon atoms, cycloalkyl groups having 3 to 12 carbon atoms, and linear, branched or cyclic alkoxy groups having 1 to 12 carbon atoms, and particularly preferable. Is an alkyl group having 1 to 4 carbon atoms and an alkoxy group having 1 to 4 carbon atoms. The substituent may be substituted with any one of the three R _{201 to} R ₂₀₃ , or may be substituted with all three. When R _{201 to} R ₂₀₃ are an aryl group, the substituent is preferably substituted at the p-position of the aryl group.

Next, the compound (ZI-2) will be described. Compound (ZI-2) is a compound in the case where R _{201 to} R ₂₀₃ in formula (ZI) each independently represents an organic group containing no aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.
The organic group having no aromatic ring as R ₂₀₁ to R ₂₀₃ generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.
R _{201 to} R ₂₀₃ are each independently preferably an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group, more preferably a linear, branched, cyclic 2-oxoalkyl group, or an alkoxycarbonylmethyl group, particularly preferably Is a linear, branched 2-oxoalkyl group.

The alkyl group as R ₂₀₁ to R ₂₀₃ may be linear, it may be either branched, preferably a straight-chain or branched alkyl group (e.g., methyl group having 1 to 10 carbon atoms, an ethyl group, a propyl Group, butyl group, pentyl group). The alkyl group as R ₂₀₁ to R ₂₀₃ is a straight-chain or branched 2-oxoalkyl group is preferably an alkoxycarbonyl methyl group.
The cycloalkyl group as R ₂₀₁ to R ₂₀₃ is preferably, and a cycloalkyl group having 3 to 10 carbon atoms (e.g., cyclopentyl, cyclohexyl, norbornyl).
The cycloalkyl group as R ₂₀₁ to R ₂₀₃ is preferably a cyclic 2-oxoalkyl group.
Linear as R ₂₀₁ to R _203, branched or cyclic 2-oxoalkyl group may preferably be a group having a 2-position> C = O in the above-described alkyl or cycloalkyl group.
The alkoxy group in the alkoxycarbonylmethyl group as R ₂₀₁ to R _203, preferably may be mentioned alkoxy groups having 1 to 5 carbon atoms (a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentoxy group).
R _{201 to} R ₂₀₃ may be further substituted with a halogen atom, an alkoxy group (for example, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.

  The compound (ZI-3) is a compound represented by the following general formula (ZI-3), and is a compound having a phenacylsulfonium salt structure.

In general formula (ZI-3),
R _{1c to} R _5c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an alkoxy group, or a halogen atom.
R _6c and R _7c each independently represents a hydrogen atom, an alkyl group or a cycloalkyl group.
Rx and Ry each independently represents an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group.
Any two or more of R _1c to R _7c, and R _x and R _y may be bonded to each other to form a ring structure, the ring structure may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond May be included. Examples of the group formed by combining any two or more of R _{1c to} R _7c and R _x and R _y include a butylene group and a pentylene group.
X ⁻ represents a non-nucleophilic anion, and examples thereof include the same non-nucleophilic anion as X ^{− in} formula (ZI).

The alkyl group as R _{1c to} R _7c may be either linear or branched, for example, a linear or branched alkyl group having 1 to 20 carbon atoms, preferably 1 to 12 carbon atoms. Or a linear or branched alkyl group (for example, a methyl group, an ethyl group, a linear or branched propyl group, a linear or branched butyl group, or a linear or branched pentyl group).
The cycloalkyl group as R _{1c to} R _7c is preferably a cycloalkyl group having 3 to 8 carbon atoms (for example, a cyclopentyl group or a cyclohexyl group).
The alkoxy group as R _{1c to} R _{5c may} be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably a linear or branched alkoxy group having 1 to 5 carbon atoms. (For example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), C3-C8 cyclic alkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group) ).
Preferably, any one of R _{1c to} R _5c is a linear or branched alkyl group, a cycloalkyl group, or a linear, branched or cyclic alkoxy group, and more preferably the sum of the carbon number of R _{1c to} R _5c is 2 ~ 15. Thereby, solvent solubility improves more and generation | occurrence | production of a particle is suppressed at the time of a preservation | save.

_Examples of the alkyl group as R _x and R _y include the same alkyl groups as R _{1c to} R _7c . The alkyl group as R _x and R _y is preferably a linear or branched 2-oxoalkyl group or an alkoxycarbonylmethyl group.
The cycloalkyl group as R _x and R _y may be the same as the cycloalkyl group as R _1c to R _7c. The cycloalkyl group as R _x and R _y is preferably a cyclic 2-oxoalkyl group.
Examples of the linear, branched, or cyclic 2-oxoalkyl group include a group having> C═O at the 2-position of the alkyl group or cycloalkyl group as R _{1c to} R _7c .
Examples of the alkoxy group in the alkoxycarbonylmethyl group include the same alkoxy groups as R _{1c to} R _5c .
R _x and R _y are preferably an alkyl group having 4 or more carbon atoms, more preferably 6 or more, and still more preferably 8 or more.

In general formulas (ZII) and (ZIII),
R ₂₀₄ to R ₂₀₇ each independently represents an aryl group, an alkyl group or a cycloalkyl group.
Phenyl group and a naphthyl group are preferred as the aryl group of R ₂₀₄ to R _207, more preferably a phenyl group.
The alkyl group as R ₂₀₄ to R ₂₀₇ may be linear, it may be either branched, preferably a straight-chain or branched alkyl group (e.g., methyl group having 1 to 10 carbon atoms, an ethyl group, a propyl Group, butyl group, pentyl group).
The cycloalkyl group as R ₂₀₄ to R ₂₀₇ is preferably, and a cycloalkyl group having 3 to 10 carbon atoms (e.g., cyclopentyl, cyclohexyl, norbornyl).
R ₂₀₄ to R ₂₀₇ may have a substituent. The R ₂₀₄ to R ₂₀₇ are substituents which may have, for example, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (e.g., 6 carbon atoms 15), alkoxy groups (for example, having 1 to 15 carbon atoms), halogen atoms, hydroxyl groups, phenylthio groups and the like.
X ⁻ represents a non-nucleophilic anion, and examples thereof include the same non-nucleophilic anion as X ^{− in} formula (ZI).

  Among the compounds that generate an acid upon irradiation with actinic rays or radiation, compounds represented by the following general formulas (ZIV), (ZV), and (ZVI) can be further exemplified.

In general formulas (ZIV) to (ZVI),
Ar ₃ and Ar ₄ each independently represents an aryl group.
R ₂₀₆ represents an alkyl group or an aryl group.
_R207 and _R208 each independently represents an alkyl group, an aryl group, or an electron-withdrawing group.
R ₂₀₇ is preferably an aryl group.
R ₂₀₈ is preferably an electron-withdrawing group, more preferably a cyano group or a fluoroalkyl group.
A represents an alkylene group, an alkenylene group or an arylene group.

  As the compound that generates an acid upon irradiation with actinic rays or radiation, compounds represented by general formulas (ZI) to (ZIII) are preferable.

  The compound (B) is preferably a compound that generates an aliphatic sulfonic acid having a fluorine atom or a benzenesulfonic acid having a fluorine atom upon irradiation with actinic rays or radiation.

  The compound (B) preferably has a triphenylsulfonium structure.

  The compound (B) is preferably a triphenylsulfonium salt compound having an alkyl group or a cycloalkyl group not substituted with fluorine in the cation moiety.

  Among the compounds that generate an acid upon irradiation with actinic rays or radiation, examples of particularly preferable compounds are listed below.

A photo-acid generator can be used individually by 1 type or in combination of 2 or more types. When two or more types are used in combination, it is preferable to combine two types of compounds that generate two types of organic acids that differ in the total number of atoms excluding hydrogen atoms by two or more.
The content of the photoacid generator is preferably 0.1 to 20% by mass, more preferably 0.5 to 10% by mass, still more preferably 1 to 7% by mass, based on the total solid content of the photosensitive composition. is there.

(C) Compound represented by the following general formula (I) The photosensitive composition of the present invention contains a compound represented by the following general formula (I) (also referred to as “compound (C)”).
(R) _n -N- (AX) _3-n (I)
In general formula (I),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
A represents a divalent linking group having a bond that is independently cleaved by an acid when there are a plurality of A's.
X represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Xs. The alicyclic hydrocarbon structure may be monocyclic or polycyclic.
n represents an integer of 0 to 2.

In the general formula (I), A represents a divalent organic group having a bond that is cleaved by an acid.
The bond cleaved by the acid can be formed by, for example, an amide bond, an ester bond, an acetal bond, a carbamoyl bond, a carbonate bond, etc. as described below.

  The bond cleaved by the acid is preferably formed by an ester bond, an acetal bond, or a carbonate bond, and more preferably formed by an ester bond or an acetal bond. The ester bond preferably has an oxygen atom bonded to a tertiary carbon atom. In the acetal bond, two oxygen atoms may each be bonded to a carbon atom, and each carbon atom may be bonded directly or via a linking group to form a ring. Furthermore, an ester bond is most preferable.

  In the divalent organic group having a bond cleaved by the acid A, the number of bonds cleaved by the acid is preferably 1 to 3, and more preferably 1.

  X represents a monovalent organic group. Examples of the monovalent organic group include an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkenyl group, an alkoxy group, an alkoxycarbonylamino group, and a cyano group. The plurality of organic groups (X) may be the same or different, and may be bonded to form a ring. The explanation of each group is the same as above. X is most preferably a cycloalkyl group having a monocyclic or polycyclic alicyclic hydrocarbon structure. By introducing the ring structure, the stability is improved, and the storage stability of the composition using the ring structure is improved.

Examples of such an organic group (X) include an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkenyl group, an alkoxy group, an alkoxycarbonylamino group, and a cyano group. The plurality of organic groups (R ′) may be the same or different, and may combine to form a ring.
The alkyl group as the organic group (X) may have a substituent, preferably a linear or branched alkyl group having 1 to 30 carbon atoms, and an oxygen atom, sulfur atom, nitrogen atom in the alkyl chain. You may have. Specifically, methyl group, ethyl group, n-propyl group, n-butyl group, n-pentyl group, n-hexyl group, n-octyl group, n-dodecyl group, n-tetradecyl group, n-octadecyl group, etc. And a branched alkyl group such as isopropyl group, isopropyl group, isobutyl group, t-butyl group, neopentyl group, 2-ethylhexyl group.
The cycloalkyl group as the organic group (X) may have a substituent, preferably a cycloalkyl group having 3 to 20 carbon atoms, may be polycyclic, and has an oxygen atom in the ring. May be. Specific examples include a cyclopropyl group, a cyclopentyl group, a cyclohexyl group, a norbornyl group, an adamantyl group, and the like.
The aryl group as the organic group (X) may have a substituent and is preferably an aryl group having 6 to 14 carbon atoms, and examples thereof include a phenyl group and a naphthyl group.
The aralkyl group as the organic group (X) may have a substituent, preferably an aralkyl group having 7 to 20 carbon atoms, such as a benzyl group, a phenethyl group, a naphthylmethyl group, or a naphthylethyl group. Is mentioned.
Examples of the alkenyl group as the organic group (X) include a group having a double bond at an arbitrary position of the alkyl group or cycloalkyl group.
The alkoxy group in the alkoxy group and the alkoxycarbonylamino group as the organic group (X) is preferably an alkoxy group having 1 to 30 carbon atoms, for example, methoxy group, ethoxy group, propoxy group, n-butoxy group, pentyloxy Group, hexyloxy group, heptyloxy group and the like.
Examples of the substituent that each organic group (X) may have include a halogen atom, a hydroxyl group, a nitro group, a cyano group, a carboxy group, a carbonyl group, and a cycloalkyl group (preferably having 3 to 10 carbon atoms), Aryl group (preferably having 6 to 14 carbon atoms), alkoxy group (preferably having 1 to 10 carbon atoms), acyl group (preferably having 2 to 20 carbon atoms), acyloxy group (preferably having 2 to 10 carbon atoms), alkoxycarbonyl A group (preferably having 2 to 20 carbon atoms), an aminoacyl group (preferably having 2 to 10 carbon atoms), and the like. As for the cyclic structure in the aryl group, cycloalkyl group and the like, examples of the further substituent include an alkyl group (preferably having a carbon number of 1 to 10). As for the aminoacyl group, examples of the further substituent include 1 or 2 alkyl groups (preferably having 1 to 10 carbon atoms).

R represents a hydrogen atom or a monovalent organic group. Examples of the monovalent organic group include an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, an alkenyl group, an alkoxy group, an alkoxycarbonylamino group, and a cyano group. The plurality of organic groups (R) may be the same or different, and may combine to form a ring.
The alkyl group as the organic group (R) may have a substituent, preferably a linear or branched alkyl group having 1 to 30 carbon atoms, and an oxygen atom, a sulfur atom, or a nitrogen atom in the alkyl chain. You may have. Specifically, methyl group, ethyl group, n-propyl group, n-butyl group, n-pentyl group, n-hexyl group, n-octyl group, n-dodecyl group, n-tetradecyl group, n-octadecyl group, etc. And a branched alkyl group such as isopropyl group, isopropyl group, isobutyl group, t-butyl group, neopentyl group, 2-ethylhexyl group.
The cycloalkyl group as the organic group (R) may have a substituent, preferably a cycloalkyl group having 3 to 30 carbon atoms, may be polycyclic, and has an oxygen atom in the ring. May be. Specific examples include groups having a monocyclo, bicyclo, tricyclo, tetracyclo structure or the like having 5 or more carbon atoms. The carbon number is preferably 6-30, and particularly preferably 7-25. These cycloalkyl groups may have a substituent. Preferred cycloalkyl groups include adamantyl group, noradamantyl group, decalin residue, tricyclodecanyl group, tetracyclododecanyl group, norbornyl group, cedrol group, cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group, A cyclodecanyl group and a cyclododecanyl group can be mentioned. More preferable examples include an adamantyl group, a norbornyl group, a cyclohexyl group, a cyclopentyl group, a tetracyclododecanyl group, and a tricyclodecanyl group.
The aryl group as the organic group (R) may have a substituent and is preferably an aryl group having 6 to 14 carbon atoms, and examples thereof include a phenyl group and a naphthyl group.
The aralkyl group as the organic group (R) may have a substituent, preferably an aralkyl group having 7 to 20 carbon atoms, such as a benzyl group, a phenethyl group, a naphthylmethyl group, or a naphthylethyl group. Is mentioned.
Examples of the alkenyl group as the organic group (R) include a group having a double bond at an arbitrary position of the alkyl group or cycloalkyl group.
The alkoxy group in the alkoxy group and the alkoxycarbonylamino group as the organic group (R) is preferably an alkoxy group having 1 to 30 carbon atoms, such as methoxy group, ethoxy group, propoxy group, n-butoxy group, pentyloxy. Group, hexyloxy group, heptyloxy group and the like.
Examples of the substituent that each organic group (R) may have include, for example, a halogen atom, a hydroxyl group, a nitro group, a cyano group, a carboxy group, a carbonyl group, and a cycloalkyl group (preferably having 3 to 10 carbon atoms), Aryl group (preferably having 6 to 14 carbon atoms), alkoxy group (preferably having 1 to 10 carbon atoms), acyl group (preferably having 2 to 20 carbon atoms), acyloxy group (preferably having 2 to 10 carbon atoms), alkoxycarbonyl A group (preferably having 2 to 20 carbon atoms), an aminoacyl group (preferably having 2 to 10 carbon atoms), and the like. As for the cyclic structure in the aryl group, cycloalkyl group and the like, examples of the further substituent include an alkyl group (preferably having a carbon number of 1 to 10). As for the aminoacyl group, examples of the further substituent include 1 or 2 alkyl groups (preferably having 1 to 10 carbon atoms).

  The compound (A) is preferably a compound represented by the following general formula (I ′).

In general formula (I ′),
R is the same as in the above formula (I).
When there are a plurality of Z, each Z independently represents a divalent organic group.
Y represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Y's. The alicyclic hydrocarbon structure may be monocyclic or polycyclic. Specifically, the same thing as X in Formula (I) is mention | raise | lifted. It represents a monovalent organic group having a monocyclic or polycyclic alicyclic hydrocarbon structure. As the monocyclic or polycyclic alicyclic hydrocarbon structure, a cycloalkyl group is most preferable. By introducing the ring structure, the stability is improved, and the storage stability of the composition using the ring structure is improved.
R ₁ and R ₂ each independently represents an alkyl group or a cycloalkyl group. When there are a plurality of R ₁ and R _{2 s} , they may be the same or different. Either R ₁ or R ₂ may be bonded to X to form a cyclic structure. By forming the ring structure, the stability is improved, and the storage stability of the composition using the ring structure is improved. The ring to be formed preferably has 4 to 20 carbon atoms, and may be monocyclic or polycyclic. Examples of the alkyl group and cycloalkyl group in R ₁ and R ₂ are the same as the alkyl group and cycloalkyl group of the organic group in the above (R).
n represents an integer of 0 to 2.

  The divalent linking group as Z is preferably a divalent organic group having 1 to 8 carbon atoms, and examples thereof include an alkylene group and an arylene group (preferably a phenylene group). The divalent linking group as A is more preferably an alkylene group, preferably having 1 to 6 carbon atoms, more preferably 1 to 4 carbon atoms, and sensitivity is improved. The alkylene chain may have a linking group such as an oxygen atom or a sulfur atom.

The compound represented by the general formula (I) is a novel compound.
Compound (A) is a nucleophilic substitution reaction in the presence of a base with a readily available ammonia, a primary or secondary amine, and a compound having an acid-decomposable structure into which a leaving group LG (such as a halogen atom) has been introduced. Can be synthesized by Michael addition of a substituted acrylate (Scheme 2).

  Specific examples of the compound (C) are shown below, but the present invention is not limited thereto.

  The content of the compound (C) in the photosensitive composition of the present invention is preferably 0.001 to 2% by mass, more preferably 0.005 to 1% by mass, based on the solid content of the composition.

Solvents Solvents that can be used when preparing the photosensitive composition by dissolving the above components include, for example, alkylene glycol monoalkyl ether carboxylates, alkylene glycol monoalkyl ethers, lactate alkyl esters, and alkoxypropionate alkyls. And organic solvents such as cyclic lactones having 4 to 10 carbon atoms, monoketone compounds having 4 to 10 carbon atoms, which may contain a ring, alkylene carbonate, alkyl alkoxyacetate, and alkyl pyruvate.

Examples of the alkylene glycol monoalkyl ether carboxylate include propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate, propylene glycol monobutyl ether acetate, propylene glycol monomethyl ether propionate, propylene glycol monoethyl Preferred examples include ether propionate, ethylene glycol monomethyl ether acetate, and ethylene glycol monoethyl ether acetate.
Preferred examples of the alkylene glycol monoalkyl ether include propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, ethylene glycol monomethyl ether, and ethylene glycol monoethyl ether.

Preferred examples of the alkyl lactate include methyl lactate, ethyl lactate, propyl lactate and butyl lactate.
Preferable examples of the alkyl alkoxypropionate include ethyl 3-ethoxypropionate, methyl 3-methoxypropionate, methyl 3-ethoxypropionate, and ethyl 3-methoxypropionate.

  Examples of the cyclic lactone having 4 to 10 carbon atoms include β-propiolactone, β-butyrolactone, γ-butyrolactone, α-methyl-γ-butyrolactone, β-methyl-γ-butyrolactone, γ-valerolactone, γ- Caprolactone, γ-octanoic lactone, and α-hydroxy-γ-butyrolactone are preferred.

  Examples of the monoketone compound having 4 to 10 carbon atoms which may contain a ring include 2-butanone, 3-methylbutanone, pinacolone, 2-pentanone, 3-pentanone, 3-methyl-2-pentanone, 4- Methyl-2-pentanone, 2-methyl-3-pentanone, 4,4-dimethyl-2-pentanone, 2,4-dimethyl-3-pentanone, 2,2,4,4-tetramethyl-3-pentanone, 2 -Hexanone, 3-hexanone, 5-methyl-3-hexanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-methyl-3-heptanone, 5-methyl-3-heptanone, 2,6-dimethyl-4 -Heptanone, 2-octanone, 3-octanone, 2-nonanone, 3-nonanone, 5-nonanone, 2-decanone, 3-decanone, 4-decanone, 5- Xen-2-one, 3-penten-2-one, cyclopentanone, 2-methylcyclopentanone, 3-methylcyclopentanone, 2,2-dimethylcyclopentanone, 2,4,4-trimethylcyclopenta Non, cyclohexanone, 3-methylcyclohexanone, 4-methylcyclohexanone, 4-ethylcyclohexanone, 2,2-dimethylcyclohexanone, 2,6-dimethylcyclohexanone, 2,2,6-trimethylcyclohexanone, cycloheptanone, 2-methylcyclo Preferred are heptanone and 3-methylcycloheptanone.

Preferred examples of the alkylene carbonate include propylene carbonate, vinylene carbonate, ethylene carbonate, and butylene carbonate.
Examples of the alkyl alkoxyacetate include 2-methoxyethyl acetate, 2-ethoxyethyl acetate, 2- (2-ethoxyethoxy) ethyl acetate, 3-methoxy-3-methylbutyl acetate, and 1-methoxy-acetate. 2-propyl is preferred.
Preferred examples of the alkyl pyruvate include methyl pyruvate, ethyl pyruvate, and propyl pyruvate.
As a solvent which can be preferably used, a solvent having a boiling point of 130 ° C. or higher under normal temperature and normal pressure can be mentioned. Specifically, cyclopentanone, γ-butyrolactone, cyclohexanone, ethyl lactate, ethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate, ethyl 3-ethoxypropionate, ethyl pyruvate, 2-ethoxyethyl acetate, acetic acid -2- (2-ethoxyethoxy) ethyl and propylene carbonate are mentioned.
In the present invention, the above solvents may be used alone or in combination of two or more.

In this invention, you may use the mixed solvent which mixed the solvent which contains a hydroxyl group in a structure, and the solvent which does not contain a hydroxyl group as an organic solvent.
Examples of the solvent containing a hydroxyl group include ethylene glycol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol, propylene glycol monomethyl ether, propylene glycol monoethyl ether, ethyl lactate, and the like. Particularly preferred are propylene glycol monomethyl ether and ethyl lactate.
Examples of the solvent not containing a hydroxyl group include propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, butyl acetate, N-methylpyrrolidone, N, N-dimethylacetamide, dimethyl sulfoxide and the like. Among these, propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, and butyl acetate are particularly preferred, and propylene glycol monomethyl ether acetate, ethyl ethoxypropionate. 2-heptanone is most preferred.
The mixing ratio (mass) of the solvent containing a hydroxyl group and the solvent not containing a hydroxyl group is 1/99 to 99/1, preferably 10/90 to 90/10, more preferably 20/80 to 60/40. . A mixed solvent containing 50% by mass or more of a solvent not containing a hydroxyl group is particularly preferred from the viewpoint of coating uniformity.

  The solvent is preferably a mixed solvent of two or more containing propylene glycol monomethyl ether acetate.

Basic Compound The photosensitive composition of the present invention preferably contains a basic compound in order to reduce the change in performance over time from exposure to heating.
Preferred examples of the basic compound include compounds having structures represented by the following formulas (A) to (E).

In general formulas (A) to (E),
R ²⁰⁰ , R ²⁰¹ and R ²⁰² may be the same or different, and are a hydrogen atom, an alkyl group (preferably having 1 to 20 carbon atoms), a cycloalkyl group (preferably having 3 to 20 carbon atoms) or an aryl group (having a carbon number). 6-20), wherein R ²⁰¹ and R ²⁰² may combine with each other to form a ring.

About the said alkyl group, as an alkyl group which has a substituent, a C1-C20 aminoalkyl group, a C1-C20 hydroxyalkyl group, or a C1-C20 cyanoalkyl group is preferable.
R ²⁰³ , R ²⁰⁴ , R ²⁰⁵ and R ²⁰⁶ may be the same or different and each represents an alkyl group having 1 to 20 carbon atoms.
The alkyl groups in these general formulas (A) to (E) are more preferably unsubstituted.

  Preferred compounds include guanidine, aminopyrrolidine, pyrazole, pyrazoline, piperazine, aminomorpholine, aminoalkylmorpholine, piperidine and the like, and more preferred compounds include imidazole structure, diazabicyclo structure, onium hydroxide structure, onium carboxylate Examples thereof include a compound having a structure, a trialkylamine structure, an aniline structure or a pyridine structure, an alkylamine derivative having a hydroxyl group and / or an ether bond, and an aniline derivative having a hydroxyl group and / or an ether bond.

Examples of the compound having an imidazole structure include imidazole, 2,4,5-triphenylimidazole, and benzimidazole. Examples of the compound having a diazabicyclo structure include 1,4-diazabicyclo [2,2,2] octane, 1,5-diazabicyclo [4,3,0] non-5-ene, and 1,8-diazabicyclo [5,4,0. ] Undecar 7-ene etc. are mentioned. Examples of the compound having an onium hydroxide structure include triarylsulfonium hydroxide, phenacylsulfonium hydroxide, sulfonium hydroxide having a 2-oxoalkyl group, specifically triphenylsulfonium hydroxide, tris (t-butylphenyl) sulfonium. Examples thereof include hydroxide, bis (t-butylphenyl) iodonium hydroxide, phenacylthiophenium hydroxide, and 2-oxopropylthiophenium hydroxide. As the compound having an onium carboxylate structure, an anion portion of the compound having an onium hydroxide structure is converted to a carboxylate, and examples thereof include acetate, adamantane-1-carboxylate, and perfluoroalkylcarboxylate. Examples of the compound having a trialkylamine structure include tri (n-butyl) amine and tri (n-octyl) amine. Examples of the aniline compound include 2,6-diisopropylaniline, N, N-dimethylaniline, N, N-dibutylaniline, N, N-dihexylaniline and the like. Examples of the alkylamine derivative having a hydroxyl group and / or an ether bond include ethanolamine, diethanolamine, triethanolamine, and tris (methoxyethoxyethyl) amine. Examples of aniline derivatives having a hydroxyl group and / or an ether bond include N, N-bis (hydroxyethyl) aniline.
These basic compounds are used alone or in combination of two or more.

  The usage-amount of a basic compound is 0.001-10 mass% normally on the basis of solid content of a photosensitive composition, Preferably it is 0.01-5 mass%.

  The use ratio of the acid generator and the basic compound in the composition is preferably acid generator / basic compound (molar ratio) = 2.5 to 300. In other words, the molar ratio is preferably 2.5 or more from the viewpoint of sensitivity and resolution, and is preferably 300 or less from the viewpoint of suppressing the reduction in resolution due to the thickening of the resist pattern over time until post-exposure heat treatment. The acid generator / basic compound (molar ratio) is more preferably 5.0 to 200, still more preferably 7.0 to 150.

Surfactant The photosensitive composition of the present invention preferably further contains a surfactant, and is a fluorine-based and / or silicon-based surfactant (fluorine-based surfactant, silicon-based surfactant, fluorine atom and silicon). It is more preferable to contain any one or two or more of surfactants having both atoms.

When the photosensitive composition of the present invention contains the above-mentioned surfactant, it provides a resist pattern with less sensitivity and development defects with good sensitivity and resolution when using an exposure light source of 250 nm or less, particularly 220 nm or less. Is possible.
Examples of the fluorine-based and / or silicon-based surfactant include, for example, JP-A No. 62-36663, JP-A No. 61-226746, JP-A No. 61-226745, JP-A No. 62-170950, JP 63-34540 A, JP 7-230165 A, JP 8-62834 A, JP 9-54432 A, JP 9-5988 A, JP 2002-277862 A, US Patent Nos. 5,405,720, 5,360,692, 5,529,881, 5,296,330, 5,436,098, 5,576,143, 5,294,511, 5,824,451 Surfactant can be mentioned, The following commercially available surfactant can also be used as it is.
Examples of commercially available surfactants that can be used include EFTOP EF301 and EF303 (manufactured by Shin-Akita Kasei Co., Ltd.), Florard FC430, 431 and 4430 (manufactured by Sumitomo 3M Co., Ltd.), MegaFuck F171, F173, F176 and F189. , F113, F110, F177, F120, R08 (manufactured by Dainippon Ink & Chemicals, Inc.), Surflon S-382, SC101, 102, 103, 104, 105, 106 (manufactured by Asahi Glass Co., Ltd.), Troisol S-366 (Manufactured by Troy Chemical Co., Ltd.), GF-300, GF-150 (manufactured by Toa Gosei Chemical Co., Ltd.), Surflon S-393 (manufactured by Seimi Chemical Co., Ltd.), F-top EF121, EF122A, EF122B, RF122C, EF125M , EF135M, EF351, 352, EF801, EF802, EF 01 (manufactured by Gemco), PF636, PF656, PF6320, PF6520 (manufactured by OMNOVA), FTX-204D, 208G, 218G, 230G, 204D, 208D, 212D, 218, 222D (manufactured by Neos) Fluorine type surfactant or silicon type surfactant can be mentioned. Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) can also be used as a silicon-based surfactant.

In addition to the known surfactants described above, the surfactant is derived from a fluoroaliphatic compound produced by a telomerization method (also called telomer method) or an oligomerization method (also called oligomer method). A surfactant using a polymer having a fluoroaliphatic group can be used. The fluoroaliphatic compound can be synthesized by the method described in JP-A-2002-90991.
As the polymer having a fluoroaliphatic group, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate and / or (poly (oxyalkylene)) methacrylate is preferable and distributed irregularly. Or may be block copolymerized. Examples of the poly (oxyalkylene) group include a poly (oxyethylene) group, a poly (oxypropylene) group, a poly (oxybutylene) group, and the like, and a poly (oxyethylene, oxypropylene, and oxyethylene group). A unit having different chain lengths in the same chain length, such as a block link) or poly (block link of oxyethylene and oxypropylene) may be used. Furthermore, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate (or methacrylate) is not only a binary copolymer but also a monomer having two or more different fluoroaliphatic groups, Further, it may be a ternary or higher copolymer obtained by simultaneously copolymerizing two or more different (poly (oxyalkylene)) acrylates (or methacrylates).

Examples of commercially available surfactants include Megafac F178, F-470, F-473, F-475, F-476, and F-472 (Dainippon Ink Chemical Co., Ltd.). Further, a copolymer of an acrylate (or methacrylate) having a C ₆ F ₁₃ group and (poly (oxyalkylene)) acrylate (or methacrylate), an acrylate (or methacrylate) having a C ₃ F ₇ group and (poly (oxy) And a copolymer of (ethylene)) acrylate (or methacrylate) and (poly (oxypropylene)) acrylate (or methacrylate).

  In the present invention, other surfactants other than fluorine-based and / or silicon-based surfactants can also be used. Specifically, polyoxyethylene lauryl ether, polyoxyethylene stearyl ether, polyoxyethylene cetyl ether, polyoxyethylene alkyl ethers such as polyoxyethylene oleyl ether, polyoxyethylene octylphenol ether, polyoxyethylene nonylphenol ether, etc. Sorbitans such as polyoxyethylene alkyl allyl ethers, polyoxyethylene / polyoxypropylene block copolymers, sorbitan monolaurate, sorbitan monopalmitate, sorbitan monostearate, sorbitan monooleate, sorbitan trioleate, sorbitan tristearate Fatty acid esters, polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monopal Te - DOO, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan trioleate, may be mentioned polyoxyethylene sorbitan tristearate nonionic surfactants of polyoxyethylene sorbitan fatty acid esters such as such.

  These surfactants may be used alone or in several combinations.

  The amount of the surfactant used is preferably 0.01 to 10% by mass, more preferably 0.1 to 5% by mass, based on the total amount of the photosensitive composition (excluding the solvent).

Carboxylic acid onium salt The photosensitive composition in this invention may contain carboxylic acid onium salt. Examples of the carboxylic acid onium salt include a carboxylic acid sulfonium salt, a carboxylic acid iodonium salt, and a carboxylic acid ammonium salt. In particular, as the carboxylic acid onium salt, an iodonium salt and a sulfonium salt are preferable. Furthermore, it is preferable that the carboxylate residue of the (H) carboxylic acid onium salt of the present invention does not contain an aromatic group or a carbon-carbon double bond. As a particularly preferable anion moiety, a linear, branched, monocyclic or polycyclic alkylcarboxylic acid anion having 1 to 30 carbon atoms is preferable. More preferably, an anion of a carboxylic acid in which some or all of these alkyl groups are fluorine-substituted is preferable. The alkyl chain may contain an oxygen atom. This ensures transparency with respect to light of 220 nm or less, improves sensitivity and resolution, and improves density dependency and exposure margin.

  Fluoro-substituted carboxylic acid anions include fluoroacetic acid, difluoroacetic acid, trifluoroacetic acid, pentafluoropropionic acid, heptafluorobutyric acid, nonafluoropentanoic acid, perfluorododecanoic acid, perfluorotridecanoic acid, perfluorocyclohexanecarboxylic acid, 2 , 2-bistrifluoromethylpropionic acid anion and the like.

  These carboxylic acid onium salts can be synthesized by reacting sulfonium hydroxide, iodonium hydroxide, ammonium hydroxide and carboxylic acid with silver oxide in a suitable solvent.

  The content of the carboxylic acid onium salt in the composition is generally 0.1 to 20% by mass, preferably 0.5 to 10% by mass, more preferably 1 to 7% by mass, based on the total solid content of the composition. %.

Dissolution-inhibiting compound having a molecular weight of 3000 or less (hereinafter also referred to as “dissolution-inhibiting compound”) that is decomposed by the action of an acid to increase the solubility in an alkaline developer.
As a dissolution inhibiting compound having a molecular weight of 3000 or less, which decomposes by the action of an acid and increases its solubility in an alkaline developer, it does not decrease the permeability of 220 nm or less, and is described in ProceedingofSPIE, 2724,355 (1996). An alicyclic or aliphatic compound containing an acid-decomposable group such as a cholic acid derivative containing an acid-decomposable group is preferred. Examples of the acid-decomposable group and alicyclic structure are the same as those described above for the alicyclic hydrocarbon-based acid-decomposable resin.

  When exposing the photosensitive composition of this invention with a KrF excimer laser, or irradiating with an electron beam, what contains the structure which substituted the phenolic hydroxyl group of the phenol compound by the acid-decomposable group is preferable. As a phenol compound, what contains 1-9 phenol frame | skeleton is preferable, More preferably, it contains 2-6 pieces.

  The molecular weight of the dissolution inhibiting compound in the present invention is 3000 or less, preferably 300 to 3000, and more preferably 500 to 2500.

  The addition amount of the dissolution inhibiting compound is preferably 3 to 50% by mass, more preferably 5 to 40% by mass, based on the solid content of the photosensitive composition.

  Specific examples of the dissolution inhibiting compound are shown below, but the present invention is not limited thereto.

Resin soluble in alkali developer (hereinafter also referred to as “alkali-soluble resin”)
The alkali dissolution rate of the alkali-soluble resin is preferably 20 kg / sec or more as measured with 0.261N tetramethylammonium hydroxide (TMAH) (23 ° C.). Particularly preferably, it is 200 Å / second or more.

  Examples of the alkali-soluble resin used in the present invention include novolak resin, hydrogenated novolak resin, acetone-pyrogalol resin, o-polyhydroxystyrene, m-polyhydroxystyrene, p-polyhydroxystyrene, hydrogenated polyhydroxystyrene, and halogen. Alternatively, alkyl-substituted polyhydroxystyrene, hydroxystyrene-N-substituted maleimide copolymer, o / p- and m / p-hydroxystyrene copolymer, partially O-alkylated product of hydroxyl group of polyhydroxystyrene (for example, 5- 30 mol% O-methylated product, O- (1-methoxy) ethylated product, O- (1-ethoxy) ethylated product, O-2-tetrahydropyranylated product, O- (t-butoxycarbonyl) methylated product, etc.) Or O-acylated product (for example, 5 to 30 mol) O-acetylated product, O- (t-butoxy) carbonylated product, etc.), styrene-maleic anhydride copolymer, styrene-hydroxystyrene copolymer, α-methylstyrene-hydroxystyrene copolymer, carboxyl group-containing methacrylic acid Examples thereof include, but are not limited to, resins and derivatives thereof, and polyvinyl alcohol derivatives.

  Particularly preferred alkali-soluble resins are novolak resins and o-polyhydroxystyrene, m-polyhydroxystyrene, p-polyhydroxystyrene and copolymers thereof, alkyl-substituted polyhydroxystyrenes, partially O-alkylated polyhydroxystyrenes, Alternatively, O-acylated product, styrene-hydroxystyrene copolymer, and α-methylstyrene-hydroxystyrene copolymer.

  The novolak resin is obtained by subjecting a predetermined monomer as a main component to addition condensation with an aldehyde in the presence of an acidic catalyst.

  Moreover, the weight average molecular weight of alkali-soluble resin is 2000 or more, Preferably it is 5000-200000, More preferably, it is 5000-100000.

  Here, the weight average molecular weight is defined as a polystyrene equivalent value of gel permeation chromatography.

  These alkali-soluble resins in the present invention may be used in combination of two or more.

  The usage-amount of alkali-soluble resin is 40-97 mass% with respect to solid content of the whole composition of a photosensitive composition, Preferably it is 60-90 mass%.

An acid crosslinking agent that crosslinks with the alkali-soluble resin by the action of an acid (hereinafter also referred to as “crosslinking agent”).
A crosslinking agent is used in the negative photosensitive composition of the present invention.

Any crosslinking agent can be used as long as it is a compound that crosslinks a resin soluble in an alkaline developer by the action of an acid, but the following (1) to (3) are preferred.
(1) Hydroxymethyl, alkoxymethyl, and acyloxymethyl forms of phenol derivatives.
(2) A compound having an N-hydroxymethyl group, an N-alkoxymethyl group, or an N-acyloxymethyl group.
(3) A compound having an epoxy group.

  The alkoxymethyl group preferably has 6 or less carbon atoms, and the acyloxymethyl group preferably has 6 or less carbon atoms.

  Of these cross-linking agents, particularly preferred are listed below.

In the formula, L ^{1 to} L ⁸ may be the same or different and each represents a hydrogen atom, a hydroxymethyl group, a methoxymethyl group, an ethoxymethyl group, or an alkyl group having 1 to 6 carbon atoms.
The crosslinking agent is generally used in an amount of 3 to 70% by mass, preferably 5 to 50% by mass, in the solid content of the photosensitive composition.

Other Additives In the photosensitive composition of the present invention, a dye, a plasticizer, a photosensitizer, a light absorber, and a compound that promotes solubility in a developer (for example, a molecular weight of 1000 or less) are included in the photosensitive composition of the present invention. A phenol compound, an alicyclic compound having a carboxyl group, or an aliphatic compound).

Such phenolic compounds having a molecular weight of 1000 or less can be obtained by referring to, for example, the methods described in JP-A-4-1222938, JP-A-2-28531, US Pat. No. 4,916,210, European Patent 219294, etc. It can be easily synthesized by those skilled in the art.
Specific examples of alicyclic or aliphatic compounds having a carboxyl group include carboxylic acid derivatives having a steroid structure such as cholic acid, deoxycholic acid, lithocholic acid, adamantane carboxylic acid derivatives, adamantane dicarboxylic acid, cyclohexane carboxylic acid, cyclohexane Examples thereof include, but are not limited to, dicarboxylic acids.

Pattern Forming Method The photosensitive composition of the present invention is preferably used at a film thickness of 30 to 250 nm, more preferably at a film thickness of 30 to 200 nm, from the viewpoint of improving resolution. Such a film thickness can be obtained by setting the solid content concentration in the photosensitive composition to an appropriate range to give an appropriate viscosity and improving the coating property and film forming property.
The total solid content concentration in the photosensitive composition is generally 1 to 10% by mass, more preferably 1 to 8.0% by mass, and still more preferably 1.0 to 6.0% by mass.

  The photosensitive composition of the present invention is used by dissolving the above components in a predetermined organic solvent, preferably the above mixed solvent, filtering the solution, and then applying the solution on a predetermined support as follows. The filter used for filter filtration is preferably made of polytetrafluoroethylene, polyethylene, or nylon of 0.1 microns or less, more preferably 0.05 microns or less, and still more preferably 0.03 microns or less.

For example, the photosensitive composition is applied onto a substrate (eg, silicon / silicon dioxide coating) used for the manufacture of precision integrated circuit elements by an appropriate coating method such as a spinner or a coater, and dried to form a photosensitive film. Form. In addition, you may coat a well-known antireflection film beforehand.
The photosensitive film is irradiated with actinic rays or radiation through a predetermined mask, preferably baked (heated), developed and rinsed. Thereby, a good pattern can be obtained.

Examples of the actinic ray or radiation include infrared light, visible light, ultraviolet light, far ultraviolet light, X-ray, electron beam, etc., preferably 250 nm or less, more preferably 220 nm or less, particularly preferably 1 to 1. Far ultraviolet light having a wavelength of 200 nm, specifically, KrF excimer laser (248 nm), ArF excimer laser (193 nm), F ₂ excimer laser (157 nm), X-ray, electron beam, etc. ArF excimer laser, F ₂ Excimer laser, EUV (13 nm), and electron beam are preferable.

Before forming the resist film, an antireflection film may be coated on the substrate in advance.
As the antireflection film, any of an inorganic film type such as titanium, titanium dioxide, titanium nitride, chromium oxide, carbon, and amorphous silicon, and an organic film type made of a light absorber and a polymer material can be used. In addition, as the organic antireflection film, commercially available organic antireflection films such as DUV30 series, DUV-40 series manufactured by Brewer Science, AR-2, AR-3, AR-5 manufactured by Shipley, etc. may be used. it can.

In the development step, an alkaline developer is used as follows. As an alkaline developer of the resist composition, inorganic hydroxides such as sodium hydroxide, potassium hydroxide, sodium carbonate, sodium silicate, sodium metasilicate, and aqueous ammonia, primary amines such as ethylamine and n-propylamine, Secondary amines such as diethylamine and di-n-butylamine, tertiary amines such as triethylamine and methyldiethylamine, alcohol amines such as dimethylethanolamine and triethanolamine, tetramethylammonium hydroxide, tetraethylammonium hydroxide and the like Alkaline aqueous solutions such as quaternary ammonium salts, cyclic amines such as pyrrole and pihelidine can be used.
Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline developer.
The alkali concentration of the alkali developer is usually from 0.1 to 20% by mass.
The pH of the alkali developer is usually from 10.0 to 15.0.
Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline aqueous solution.
As the rinsing liquid, pure water can be used, and an appropriate amount of a surfactant can be added.
Further, after the development process or the rinsing process, a process of removing the developer or the rinsing liquid adhering to the pattern with a supercritical fluid can be performed.

  Exposure (immersion exposure) may be performed by filling a liquid (immersion medium) having a higher refractive index than air between the resist film and the lens during irradiation with actinic rays or radiation. Thereby, resolution can be improved. As the immersion medium to be used, any liquid can be used as long as it has a higher refractive index than air, but pure water is preferred. Further, an overcoat layer may be further provided on the photosensitive film so that the immersion medium and the photosensitive film do not come into direct contact with each other during the immersion exposure. Thereby, the elution of the composition from the photosensitive film to the immersion medium is suppressed, and development defects are reduced.

The immersion liquid used for the immersion exposure will be described below.
The immersion liquid is preferably a liquid that is transparent to the exposure wavelength and has a refractive index temperature coefficient as small as possible so as to minimize distortion of the optical image projected onto the resist. In the case of an ArF excimer laser (wavelength: 193 nm), it is preferable to use water from the viewpoints of availability and ease of handling in addition to the above-described viewpoints.
Further, a medium having a refractive index of 1.5 or more can be used in that the refractive index can be further improved. This medium may be an aqueous solution or an organic solvent.

  When water is used as the immersion liquid, the surface tension of the water is reduced and the surface activity is increased, so that the resist layer on the wafer is not dissolved and the influence on the optical coating on the lower surface of the lens element can be ignored. An additive (liquid) may be added in a small proportion. The additive is preferably an aliphatic alcohol having a refractive index substantially equal to that of water, and specifically includes methyl alcohol, ethyl alcohol, isopropyl alcohol and the like. By adding an alcohol having a refractive index substantially equal to that of water, even if the alcohol component in water evaporates and the content concentration changes, an advantage that the change in the refractive index of the entire liquid can be made extremely small can be obtained. On the other hand, when an opaque material or impurities whose refractive index is significantly different from that of water are mixed with 193 nm light, the optical image projected on the resist is distorted, so that distilled water is preferable as the water to be used. Further, pure water filtered through an ion exchange filter or the like may be used.

The electrical resistance of water is desirably 18.3 MQcm or more, the TOC (organic substance concentration) is desirably 20 ppb or less, and deaeration treatment is desirably performed.
Moreover, it is possible to improve lithography performance by increasing the refractive index of the immersion liquid. From such a viewpoint, an additive for increasing the refractive index may be added to water, or heavy water (D ₂ O) may be used instead of water.

  When the photosensitive composition of the present invention is used as a resist film, the receding contact angle of water with respect to the resist film is preferably 70 ° or more. Here, the receding contact angle is at normal temperature and pressure. The receding contact angle is the receding contact angle when the droplet starts to drop when the resist film is tilted.

In order to prevent the resist film from coming into direct contact with the immersion liquid between the resist film of the photosensitive composition of the present invention and the immersion liquid, an immersion liquid hardly soluble film (hereinafter also referred to as “topcoat”). May be provided. The necessary functions for the top coat are suitability for application to the upper layer of the resist, radiation, especially transparency to 193 nm, and poor immersion liquid solubility. It is preferable that the top coat is not mixed with the resist and can be uniformly applied to the resist upper layer.
From the viewpoint of 193 nm transparency, the topcoat is preferably a polymer that does not contain an aromatic, and specifically, a hydrocarbon polymer, an acrylate polymer, a polymethacrylic acid, a polyacrylic acid, a polyvinyl ether, a silicon-containing polymer, And fluorine-containing polymers. From the viewpoint of contaminating the optical lens when impurities are eluted from the top coat into the immersion liquid, it is preferable that the residual monomer component of the polymer contained in the top coat is small.

When peeling the top coat, a developer may be used, or a separate release agent may be used. As the release agent, a solvent having a small penetration into the resist is preferable. It is preferable that the peeling process can be performed with an alkali developer in that the peeling process can be performed simultaneously with the resist development process. The top coat is preferably acidic from the viewpoint of peeling with an alkali developer, but may be neutral or alkaline from the viewpoint of non-intermixability with the resist.
The resolution is improved when there is no difference in refractive index between the top coat and the immersion liquid. In the case of using water as the immersion liquid in an ArF excimer laser (wavelength: 193 nm), the top coat for ArF immersion exposure is preferably close to the refractive index of the immersion liquid. From the viewpoint of making the refractive index close to the immersion liquid, it is preferable to have fluorine atoms in the topcoat. A thin film is more preferable from the viewpoint of transparency and refractive index.

  It is preferable that the top coat is not mixed with the resist and further not mixed with the immersion liquid. From this viewpoint, when the immersion liquid is water, the topcoat solvent is preferably a resist solvent hardly soluble and water-insoluble medium. Furthermore, when the immersion liquid is an organic solvent, the topcoat may be water-soluble or water-insoluble.

  EXAMPLES Hereinafter, although an Example demonstrates this invention still in detail, the content of this invention is not limited by this.

Synthesis Example 1 (Synthesis of Resin (1))
Under a nitrogen stream, 8.6 g of cyclohexanone was placed in a three-necked flask and heated to 80 ° C. To this, 9.8 g of 2-adamantyl isopropyl methacrylate, 4.4 g of dihydroxyadamantyl methacrylate, 8.9 g of norbornane lactone methacrylate, and 8 mol% of a polymerization initiator V-601 (manufactured by Wako Pure Chemical Industries) were dissolved in 79 g of cyclohexanone. The solution was added dropwise over 6 hours. After completion of dropping, the reaction was further carried out at 80 ° C. for 2 hours. The reaction solution was allowed to cool and then added dropwise over 20 minutes to a mixture of 800 m of hexane / 200 ml of ethyl acetate, and the precipitated powder was collected by filtration and dried to obtain 19 g of Resin (1). The weight average molecular weight of the obtained resin was 8800 in terms of standard polystyrene, and the dispersity (Mw / Mn) was 1.9.

  The structure of the acid-decomposable resin (A) used in the examples is shown below. Tables 1 to 3 below show the molar ratio of repeating units in each resin (in order from the left in the structural formula), the weight average molecular weight, and the degree of dispersion.

Synthesis Example 2 (Synthesis of Compound C (A-2, A-3))
A mixture of 2- (1-adamantyl) -2-propyl acrylate 10.0 g (40.26 mmol), 2.0 M-ammonia / MeOH solution 80 mL, and MeOH 60 mL was heated to reflux for 48 hours under a nitrogen stream. Water (200 mL) and ethyl acetate (200 mL) were added, the organic layer was washed successively with water, a saturated aqueous sodium chloride solution, and water, and the organic layer was dried over sodium sulfate. The solvent was concentrated to give the residue was purified by column chromatography _(SiO 2, hexane / ethyl acetate = 10/1) compound to give A-2 (4.6 g) and A-3 (2.3g).
A-2:
¹ H-NMR (400 MHz, CDCl 3) δ 1.45 (s, 3H), 1.64-1.69 (m, 12H), 2.00 (bs, 3H), 2.45 (t, 2H) , 2.76 (t, 2H)
A-3:
¹ H-NMR (400 MHz, CDCl 3) δ 1.45 (s, 3H), 1.64-1.69 (m, 12H), 2.00 (bs, 3H), 2.38 (t, 2H) , 2.87 (t, 2H)
MALDI-TOF m / z [C48H75NO6 + H] ⁺ . calcd 762.5673, found 762.5784

Examples and Comparative Examples <Resist Preparation>
The components shown in Table 4 below were dissolved in a solvent, and a solution with a solid content concentration of 6% by mass was prepared for each, and this was filtered through a 0.1 μm polyethylene filter to prepare a positive resist solution. The prepared positive resist composition was evaluated by the following method, and the results are shown in Table 4 below. In addition, about each component in Table 4, the ratio at the time of using multiple is a mass ratio.

[Image performance test]
(Exposure condition (1))
An organic antireflection film ARC29A (Nissan Chemical Co., Ltd.) was applied on a silicon wafer and baked at 205 ° C. for 60 seconds to form a 78 nm antireflection film. The positive resist composition prepared thereon was applied and baked at 130 ° C. for 60 seconds to form a 250 nm resist film. The obtained wafer was subjected to pattern exposure using an ArF excimer laser scanner (PAS5500 / 1100, NA0.75, σo / σi = 0.85 / 0.55, manufactured by ASML). Thereafter, heating was performed at 130 ° C. for 60 seconds, followed by development with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsing with pure water, and spin drying to obtain a resist pattern.

(Exposure condition (2))
This condition is to form a resist pattern by an immersion exposure method using pure water.
An organic antireflection film ARC29A (Nissan Chemical Co., Ltd.) was applied on a silicon wafer and baked at 205 ° C. for 60 seconds to form a 78 nm antireflection film. The positive resist composition prepared thereon was applied and baked at 130 ° C. for 60 seconds to form a 250 nm resist film. The obtained wafer was subjected to pattern exposure using an ArF excimer laser immersion scanner (NA 0.85). Ultra pure water was used as the immersion liquid. Thereafter, heating was performed at 130 ° C. for 60 seconds, followed by development with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsing with pure water, and spin drying to obtain a resist pattern.

  In (Exposure Condition 1) and (Exposure Condition 2), the line edge roughness performance and pattern profile of the obtained resist pattern were observed using a scanning electron microscope (Hitachi S-4800).

[Line edge roughness (LER)]
For the range of 5 μm edge in the longitudinal direction of the line pattern, measure the distance from the reference line where the edge should be at 50 points with a length measuring SEM (S-8840, manufactured by Hitachi, Ltd.), calculate the standard deviation, and calculate 3σ did. A value of less than 5.0 was rated as ◯, a value of 5.0 to 7.0 as Δ, and a value of 7.0 or more as x. A smaller value indicates better performance.

Symbols in the examples are as follows.
The acid generator and the compound (C) correspond to those exemplified above.
[Basic compounds]
TPI: 2,4,5-triphenylimidazole TPSA: triphenylsulfonium acetate HEP: N-hydroxyethylpiperidine DIA: 2,6-diisopropylaniline DCMA: dicyclohexylmethylamine TPA: tripentylamine HAP: hydroxyantipyrine TBAH: tetrabutyl Ammonium hydroxide TMEA: Tris (methoxyethoxyethyl) amine PEA: N-phenyldiethanolamine TOA: Trioctylamine DBN: 1,5-diazabicyclo [4.3.0] non-5-ene PBI: 2-phenylbenzimidazole
DHA: N, N-dihexylaniline

[Surfactant]
W-1: MegaFuck F176 (Dainippon Ink Chemical Co., Ltd.) (Fluorine)
W-2: Megafuck R08 (Dainippon Ink Chemical Co., Ltd.) (fluorine and silicon)
W-3: Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) (silicon-based)
W-4: Troisol S-366 (manufactured by Troy Chemical Co., Ltd.)
W-5: PF656 (manufactured by OMNOVA, fluorine-based)
W-6: PF6320 (manufactured by OMNOVA, fluorine-based)

〔solvent〕
A1: Propylene glycol monomethyl ether acetate A2: 2-heptanone A3: Cyclohexanone A4: γ-Butyrolactone B1: Propylene glycol monomethyl ether B2: Ethyl lactate B3: Propylene carbonate

  From the results in Table 4, the positive resist composition of the present invention has little deterioration in the resist pattern profile and line edge roughness due to the placement between exposure and PEB, not only in normal exposure but also in immersion exposure. It can be seen that the followability to the immersion liquid is good in immersion exposure.

<Experimental example of multilayer resist>
(1) Formation of lower resist layer FHi-028DD resist (resist for i-line manufactured by Fuji Film Orin) was applied to a 6-inch silicon wafer using a spin coater Mark8 manufactured by Tokyo Electron, and baked at 90 ° C for 90 seconds. A uniform film having a thickness of 0.55 μm was obtained.
This was further heated at 200 ° C. for 3 minutes to form a lower resist layer having a thickness of 0.40 μm.

(2) Formation of upper resist layer The components shown in Table 5 below are dissolved in a solvent to prepare a solution having a solid content concentration of 11% by mass, and precision filtered through a membrane filter having a diameter of 0.1 μm to prepare an upper resist composition. did.
The upper resist composition was similarly applied on the lower resist layer, and heated at 130 ° C. for 90 seconds to form an upper resist layer having a thickness of 0.20 μm.

  Resins (SI-1) to (SI-5) in Table 5 are as follows.

(3) Resist Evaluation The wafer thus obtained was exposed while changing the exposure amount by loading a resolution mask on an ArF excimer stepper 9300 manufactured by ISI.
Next, after heating at 120 ° C. for 90 seconds, the film was developed with a tetrahydroammonium hydroxide developer (2.38 mass%) for 60 seconds, rinsed with distilled water, and dried to form an upper layer pattern. Similarly, the pattern profile and line edge roughness were evaluated.
The results are shown in Table 5.

  From the results in Table 5, it is clear that the photosensitive composition of the present invention is excellent in pattern profile and line edge roughness even when used as a two-layer resist.

<Positive resist for KrF>
<Resist preparation>
The components shown in Table 6 below were dissolved in a solvent and filtered through a 0.1 μm polytetrafluoroethylene filter to prepare a positive resist solution having a solid content concentration of 14% by mass.

<Resist evaluation>
The prepared positive resist solution is uniformly coated on a silicon substrate subjected to hexamethyldisilazane treatment using a spin coater, and is heated and dried on a hot plate at 120 ° C. for 90 seconds to obtain a 0.4 μm resist. A film was formed.
The resist film was subjected to pattern exposure using a line and space mask using a KrF excimer laser stepper (NA = 0.63), and heated on a hot plate at 110 ° C. for 90 seconds immediately after the exposure. Further, the resist film was developed with an aqueous 2.38 mass% tetramethylammonium hydroxide solution at 23 ° C. for 60 seconds, rinsed with pure water for 30 seconds, dried, and a line pattern was formed. Edge roughness was evaluated.
The evaluation results are shown in Table 6.

  Repeat unit molar ratio of resin (R-2), (R-7), (R-8), (R-9), (R-14), and (R-17) used in Table 6 and weight The average molecular weight is shown in the table below.

  From the results of Table 6, it is clear that the photosensitive composition of the present invention is excellent in pattern profile and line edge roughness even as a positive resist composition in KrF excimer laser exposure.

<KrF negative resist>
<Resist preparation>
The components shown in Table 8 below were dissolved in a solvent, and this was filtered through a 0.1 μm polytetrafluoroethylene filter to prepare a negative resist solution having a solid concentration of 14% by mass.
The prepared negative resist solution was evaluated in the same manner as in Example 44, and the results are shown in Table 8.

  The structure, molecular weight and molecular weight distribution, and crosslinking agent of the alkali-soluble resin in Table 8 are shown below.

  From the results of Table 8, it is clear that the photosensitive composition of the present invention is excellent in pattern profile and line edge roughness even as a negative resist composition in KrF excimer laser exposure.

<Positive resist for EB>
<Resist preparation>
The components shown in Table 6 above were dissolved in a solvent, and this was filtered through a 0.1 μm polytetrafluoroethylene filter to prepare a positive resist solution having a solid content concentration of 12% by mass.

<Resist evaluation>
The prepared positive resist solution is uniformly applied on a silicon substrate subjected to hexamethyldisilazane treatment using a spin coater, and is heated and dried on a hot plate at 120 ° C. for 60 seconds to obtain a 0.3 μm resist. A film was formed.
This resist film was irradiated with an electron beam projection lithography apparatus (acceleration voltage 100 keV) manufactured by Nikon Corporation, and immediately after the irradiation, it was heated on a hot plate at 110 ° C. for 90 seconds. Further, development was performed at 23 ° C. for 60 seconds using an aqueous tetramethylammonium hydroxide solution having a concentration of 2.38% by mass, rinsed with pure water for 30 seconds, and then dried to form a line and space pattern. Similarly, the pattern profile and line edge roughness were evaluated.
Table 9 shows the evaluation results.

  From the results of Table 9, it is clear that the photosensitive composition of the present invention is excellent in pattern profile and line edge roughness even as a positive resist composition by electron beam irradiation.

<Negative resist for EB>
<Resist preparation>
The components shown in Table 8 above were dissolved in a solvent, and this was filtered through a 0.1 μm polytetrafluoroethylene filter to prepare a negative resist solution having a solid content concentration of 12% by mass.

<Resist evaluation>
The prepared negative resist solution is uniformly applied on a silicon substrate subjected to hexamethyldisilazane treatment using a spin coater, and is heated and dried on a hot plate at 120 ° C. for 60 seconds to obtain a 0.3 μm resist. A film was formed.
This resist film was irradiated with an electron beam projection lithography apparatus (acceleration voltage 100 keV) manufactured by Nikon Corporation, and immediately after the irradiation, it was heated on a hot plate at 110 ° C. for 90 seconds. Further, development was performed at 23 ° C. for 60 seconds using an aqueous tetramethylammonium hydroxide solution having a concentration of 2.38% by mass, rinsed with pure water for 30 seconds, and then dried to form a line and space pattern. Similarly, the pattern profile and line edge roughness were evaluated.
Table 10 shows the evaluation results.

  From the results in Table 10, it is clear that the photosensitive composition of the present invention is excellent in pattern profile and line edge roughness even as a negative resist composition by electron beam irradiation.

<EUV resist>
The components shown in Table 6 were dissolved in a solvent, and this was filtered through a 0.1 μm polytetrafluoroethylene filter to prepare a positive resist solution with a solid content concentration of 8% by mass, and evaluated as follows. .

<Resist evaluation>
The prepared positive resist solution is uniformly coated on a silicon substrate subjected to hexamethyldisilazane treatment using a spin coater, and is heated and dried on a hot plate at 120 ° C. for 60 seconds to obtain a 0.15 μm resist. A film was formed. The obtained resist film was subjected to surface exposure using EUV light (wavelength 13 nm) while changing the exposure amount by 0.5 mJ in the range of 0 to 10.0 mJ, and further baked at 110 ° C. for 90 seconds. Then, using a 2.38% tetramethylammonium hydroxide (TMAH) aqueous solution, the dissolution rate at each exposure amount was measured to obtain a sensitivity curve. In this sensitivity curve, the exposure amount when the dissolution rate of the resist is saturated was taken as sensitivity, and the dissolution contrast (γ value) was calculated from the gradient of the linear portion of the sensitivity curve. The larger the γ value, the better the dissolution contrast.
The evaluation results are shown in Table 11 below.

  From the results in Table 11, it can be seen that the resist composition of the present invention is superior in sensitivity and high contrast as compared with the composition of the comparative example in the property evaluation by irradiation with EUV light.

Claims (5)

A photosensitive composition comprising a compound (C) represented by the following general formula (I):
(R) _n -N- (AX) _3-n (I)
In general formula (I),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
A represents a divalent linking group having a bond that is independently cleaved by an acid when there are a plurality of A's.
X represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Xs.
n represents an integer of 0 to 2.   The photosensitive composition according to claim 1, wherein in the general formula (I), A is a divalent linking group containing a tertiary ester moiety. The photosensitive composition according to claim 1 or 2, wherein the compound (C) is a compound represented by the following general formula (I ').

In general formula (I ′),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
When there are a plurality of Z, each Z independently represents a divalent organic group.
Y represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Y's.
R ₁ and R ₂ each independently represents an alkyl group or a cycloalkyl group. Any one of them may be bonded to X to form a cyclic structure. When there are a plurality of R ₁ and R _{2 s} , they may be the same or different.
n represents an integer of 0 to 2.   A pattern forming method comprising the steps of: forming a photosensitive film from the photosensitive composition according to claim 1; and exposing and developing the photosensitive film. The compound represented by general formula (I ').

In general formula (I ′),
When there are a plurality of Rs, they each independently represent a hydrogen atom or a monovalent organic group.
When there are a plurality of Z, each Z independently represents a divalent organic group.
Y represents a monovalent organic group having an alicyclic hydrocarbon structure each independently when there are a plurality of Y's.
R ₁ and R ₂ each independently represents an alkyl group or a cycloalkyl group. Any one of them may be bonded to X to form a cyclic structure. When there are a plurality of R ₁ and R _{2 s} , they may be the same or different.
n represents an integer of 0 to 2.