JP2008062585A - Manufacturing method of mold for lens substrate forming, mold for lens substrate forming, lens substrate, transmission type screen and rear type projection tv - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a mold for lens substrate forming which can form a lens substrate excellent in utilization efficiency of light and viewing angle characteristics, a manufacturing method which can manufactures the mold for lens substrate forming efficiently, a lens substrate excellent in utilization efficiency of light, a transmission type screen and a rear type projection TV. <P>SOLUTION: The manufacturing method of a mold for lens substrate forming comprises: a process which prepares a member 6 with recesses having a large number of recesses 61 of a spherical surface configuration; a process which uses the member with recesses as a mold and forms a member with spherical surface projections having a large number of spherical surface projections of a spherical surface configuration corresponding to the configuration of the recesses 61 of the member with recesses; a process which eliminates a part of a spherical surface projection thereby forms an aspheric surface projection of an aspheric surface configuration and forms a member with an aspheric surface projection; and a process which uses a member with an aspheric surface projection as a mold and obtains a mold for lens substrate forming having a recess of a configuration corresponding to an aspheric surface projection. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

  The present invention relates to a method for manufacturing a lens substrate forming mold, a lens substrate forming mold, a lens substrate, a transmissive screen, and a rear projection TV.

A display device that projects an image on a screen is known. As such a display device, there is known a rear projection TV applied to a home theater monitor, a large-screen television, and the like, and the demand thereof is increasing in recent years.
In recent years, the demand for rear projection TVs is increasing as a display suitable for home theater monitors, large-screen televisions, and the like.

A lens substrate (lens sheet) having a lens portion such as a lenticular lens is generally used for a transmission screen used in a rear projection TV.
In a transmissive screen used for a rear projection TV, a light shielding portion (black matrix) may be provided in a portion other than a light collecting portion by a lens portion of a lens substrate for the purpose of improving the contrast of a display image.

  As a method for forming such a light shielding portion, for example, a step of forming a first layer made of a photosensitive curable resin layer containing a colorant on a flat surface of a lens sheet, and a colorant on the first layer The second layer made of a photosensitive curable resin layer having a lower content than the first layer, and the step of forming the translucent substrate in this order, and exposure from the lens unit side, thereby collecting by the lens unit. A step of curing at least the first layer at a location corresponding to the light portion in a pattern, and a step of curing the entire surface of the second layer in the vicinity of the interface with the translucent substrate by exposing the entire surface from the translucent substrate side. And, from the lens sheet, by peeling off the translucent substrate on which the first layer cured in a pattern shape is a portion corresponding to the light condensing part by the second layer and the lens part, on the flat surface of the lens sheet, Item that corresponds to the condensing part by the lens part The first layer is removed to form a light transmission part (opening part), the first layer is left at a position corresponding to the non-light condensing part by the lens part, and the light shielding part is made of a photosensitive curable resin layer containing a colorant. There is known a method having a step of forming (see, for example, Patent Document 1).

When the black matrix is formed by using such lens condensing, it is necessary to match the focal position of the lens with the position of the black matrix.
By the way, such a lens substrate is generally manufactured using a substrate with concave portions having a large number of concave portions. As a method for manufacturing the substrate with recesses, there is known a method of manufacturing by etching using a mask having a predetermined pattern of openings (see, for example, Patent Document 2).

  However, the concave substrate obtained by such a method can form only a hemispherical lens, and a lens having a small radius of curvature such as a microlens has a large spherical aberration and a condensing position is clear. Therefore, it is difficult to match the focal position of the lens with the position of the black matrix. In addition, when it is adjusted to a position where it seems to be condensed, an opening is formed, but due to the above aberration, there is light that has not been condensed or light that has already been condensed and diffused, This light cannot go out from the opening, and there is a problem that characteristics such as light use efficiency and viewing angle characteristics are deteriorated.

JP 2002-258410 A JP-A-9-101401

  An object of the present invention is to provide a lens substrate forming mold capable of forming a lens substrate excellent in light utilization efficiency and viewing angle characteristics, and to efficiently manufacture the lens substrate forming mold. It is an object of the present invention to provide a manufacturing method and to provide a lens substrate, a transmissive screen, and a rear projection TV that are excellent in light use efficiency.

Such an object is achieved by the present invention described below.
The method for producing a lens substrate forming mold of the present invention is a method for producing a lens substrate forming mold used for forming a lens substrate having a large number of convex lenses,
A member-with-recess preparing step for preparing a member with a recessed portion having a number of spherically-shaped recessed portions;
A member having a spherical convex portion is formed using the member with concave portion as a mold, and forming a member having a spherical convex portion having a plurality of spherical convex portions corresponding to the shape of the concave portion of the member having the concave portion,
By removing a part of the spherical convex part, an aspherical aspherical convex part is formed, and an aspherical convex part-equipped member forming step for forming an aspherical convex parted member;
And a lens substrate forming mold forming step of obtaining a lens substrate forming mold having a concave portion having a shape corresponding to the convex lens, using the aspherical convex member as a mold.
Thereby, it is possible to provide a lens substrate forming mold capable of forming a lens substrate excellent in light utilization efficiency and viewing angle characteristics.

In the manufacturing method of the lens substrate forming mold of the present invention, it is preferable that a part of the convex portion is removed by laser beam irradiation in the step of forming the aspherical convex member.
This makes it possible to easily form a member with an aspherical convex part having an aspherical convex part, and by using this member with an aspherical convex part as a mold, a lens substrate forming mold having an aspherical concave part Can be easily formed.

In the manufacturing method of the lens substrate forming mold of the present invention, it is preferable that a part of the convex portion is removed by ion beam irradiation in the member forming step with the aspherical convex portion.
This makes it possible to easily form a member with an aspherical convex part having an aspherical convex part, and by using this member with an aspherical convex part as a mold, a lens substrate forming mold having an aspherical concave part Can be easily formed.

これにより、球面収差を小さいものとすることができ、最終的に得られるレンズ基板は、視野角特性および光の利用効率に優れたものとなる。 In the method for manufacturing a lens substrate forming mold of the present invention, the aspherical convex portion satisfies a relationship of A ≧ 0.1 and at least A ₁ ≠ 0 when the cross-sectional shape is expressed by the following formula (I). It is preferable to do.

Thereby, spherical aberration can be made small, and the lens substrate finally obtained has excellent viewing angle characteristics and light utilization efficiency.

The mold for forming a lens substrate of the present invention is manufactured using the method of the present invention.
Thereby, it is possible to easily obtain a lens substrate forming mold capable of forming a lens substrate having excellent light utilization efficiency and viewing angle characteristics.
The lens substrate of the present invention is a lens substrate having a substrate body having a large number of convex lenses and a light-shielding film made of a light-shielding material and having an opening,
The substrate body is formed using the lens substrate forming mold of the present invention.
Thereby, it is possible to provide a lens substrate that is excellent in light utilization efficiency and excellent in viewing angle characteristics.

The lens substrate of the present invention is preferably a microlens substrate provided with a microlens as the convex lens.
As a result, the light utilization efficiency is excellent, and the viewing angle characteristics are particularly excellent.
The transmission screen of the present invention is characterized by including the lens substrate of the present invention.
As a result, it is possible to provide a transmissive screen having excellent light utilization efficiency and viewing angle characteristics.

The transmissive screen of the present invention, a Fresnel lens portion in which a Fresnel lens is formed on the light emission side,
And a lens substrate of the present invention disposed on the light emission side of the Fresnel lens portion.
As a result, it is possible to provide a transmissive screen having excellent light utilization efficiency and viewing angle characteristics.
A rear projection TV according to the present invention includes the transmission screen according to the present invention.
Accordingly, it is possible to provide a rear projection TV that is excellent in light utilization efficiency and viewing angle characteristics.

Hereinafter, a method for manufacturing a lens substrate forming mold, a lens substrate forming mold, a lens substrate, a transmission screen, and a rear projection TV according to the present invention will be described in detail based on preferred embodiments shown in the accompanying drawings.
In the present invention, the “substrate” refers to a concept that is substantially inflexible and includes a relatively large thickness, a sheet-like material, a film-like material, and the like. .
The use of the lens substrate of the present invention is not particularly limited, but in the following description, the lens substrate will be described as being mainly used as a member constituting a transmissive screen and a rear projection TV.

<Lens substrate and transmissive screen>
First, prior to the description of the method for manufacturing the lens substrate forming mold of the present invention and the lens substrate forming mold, the configurations of the lens substrate (convex lens substrate) and the transmissive screen of the present invention will be described.
1 is a schematic longitudinal sectional view showing a preferred embodiment of a lens substrate (microlens substrate) of the present invention, FIG. 2 is a plan view of the lens substrate (microlens substrate) shown in FIG. 1, and FIG. FIG. 2 is a schematic longitudinal sectional view showing a preferred embodiment of the transmission screen of the present invention including the lens substrate (microlens substrate) shown in FIG. 1. In the following description, the left side in FIGS. 1 and 3 is referred to as “(light) incident side”, and the right side is referred to as “(light) emission side”. In the present invention, unless otherwise specified, the “(light) incident side” and the “(light) output side” are the “incident side” of light for obtaining image light (video light), respectively. ”And“ outgoing side ”, not“ incident side ”or“ outgoing side ”of external light or the like.

A microlens substrate (lens substrate) 1 is a member constituting a transmission screen 10 to be described later, and includes a plurality of microlenses (convex lenses) 21 arranged in a predetermined pattern as shown in FIG. A main body 2 and a black matrix (light-shielding film) 3 made of a light-shielding material are provided.
The substrate body 2 is manufactured using a lens substrate forming mold of the present invention, which will be described later, and is usually made of a material having transparency.
The constituent material of the substrate body 2 is not particularly limited, but is mainly composed of a resin material and is composed of a transparent material having a predetermined refractive index.

  Examples of the resin material constituting the substrate body 2 include polyolefins such as polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer (EVA), cyclic polyolefin, modified polyolefin, polyvinyl chloride, and polychlorinated. Vinylidene, polystyrene, polyamide (eg, nylon 6, nylon 46, nylon 66, nylon 610, nylon 612, nylon 11, nylon 12, nylon 6-12, nylon 6-66), polyimide, polyamideimide, polycarbonate (PC), Poly- (4-methylpentene-1), ionomer, acrylic resin, acrylonitrile-butadiene-styrene copolymer (ABS resin), acrylonitrile-styrene copolymer (AS resin), butadiene-styrene copolymer Polyoxymethylene, polyvinyl alcohol (PVA), ethylene-vinyl alcohol copolymer (EVOH), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyester such as polycyclohexane terephthalate (PCT), polyether, polyether ketone (PEK), polyether ether ketone (PEEK), polyether imide, polyacetal (POM), polyphenylene oxide, modified polyphenylene oxide, polysulfone, polyether sulfone, polyphenylene sulfide, polyarylate, aromatic polyester (liquid crystal polymer), poly Tetrafluoroethylene, polyvinylidene fluoride, other fluororesins, styrene, polyolefin, polyvinyl chloride, polyurea , Polyester, polyamide, polybutadiene, transpolyisoprene, fluororubber, chlorinated polyethylene, and other thermoplastic elastomers, epoxy resins, phenolic resins, urea resins, melamine resins, unsaturated polyesters, silicones Resins, urethane-based resins, etc., or copolymers, blends, polymer alloys, etc. mainly composed of these, and combinations of one or more of these (for example, blend resins, polymer alloys, laminates) As body etc.).

  The constituent material (solidified material) of the substrate body 2 generally has an absolute refractive index greater than various gases (the atmosphere in which the microlens substrate 1 is used), but the specific value of the absolute refractive index is 1.4 to 1.58 is preferable, and 1.5 to 1.56 is more preferable. When the absolute refractive index of the constituent material of the substrate body 2 is a value within the above range, the viewing angle characteristic can be made particularly excellent while making the utilization efficiency of light (incident light) particularly excellent.

The microlens substrate 1 includes a plurality of microlenses 21 as convex lenses having a convex surface on the light incident surface side.
The microlens 21 has an aspheric shape. Since the microlens 21 has an aspherical shape, spherical aberration can be reduced, and the microlens substrate 1 has excellent viewing angle characteristics and light utilization efficiency.

In particular, in the present embodiment, it is preferable that the microlens 21 satisfies a relationship of A ≧ 0.1 and at least A ₁ ≠ 0 when the cross-sectional shape is expressed by the following formula (I).

By satisfying such a relationship, the spherical aberration can be made particularly small, and the viewing angle characteristics and the light utilization efficiency of the microlens substrate 1 can be made particularly excellent.
At this time, attention is paid to the fact that the paraxial radius of curvature R of the microlens 21 is represented by the following formula (II). Most of the spherical aberration correction burden is given to the second order term (second order coefficient A ₁ ), and the radius of curvature R ₀ of the reference sphere and the aspheric coefficient A ₁ are appropriately selected under the conic constant A ≧ 0.1. Thus, the spherical aberration of the microlens 21 can be controlled, and the shape of the microlens 21 can be selected in consideration of the light condensing state.

  In the present embodiment, the microlens (convex lens) 21 has a flat shape (substantially elliptical) in which the vertical width (vertical width) when the microlens substrate 1 is viewed in plan is smaller than the horizontal width (horizontal width). , Substantially bowl-shaped). When the microlens 21 has such a shape, it is possible to make the viewing angle characteristics particularly excellent while effectively preventing the occurrence of inconvenience such as moire. In particular, both the horizontal and vertical viewing angle characteristics can be improved.

When the length in the minor axis direction (longitudinal direction) of the microlens 21 in plan view is L ₁ [μm] and the length in the major axis direction (lateral direction) is L ₂ [μm], 0.10 ≦ The relationship of L ₁ / L ₂ ≦ 0.99 is preferably satisfied, the relationship of 0.50 ≦ L ₁ / L ₂ ≦ 0.95 is more preferable, and 0.60 ≦ L ₁ / L ₂ is satisfied. More preferably, the relationship of ≦ 0.80 is satisfied. By satisfying the relationship as described above, the effects as described above become more remarkable.

  The length of the microlens 21 in the short axis direction (vertical width of the microlens 21) when viewed in plan is preferably 10 to 500 μm, more preferably 30 to 300 μm, and 50 to 100 μm. Is more preferable. When the length of the microlens 21 in the short axis direction is a value within the above range, it is possible to obtain sufficient resolution in the image projected on the screen while effectively preventing the occurrence of inconvenience such as moire. The productivity of the microlens substrate 1 (transmission type screen 10) can be further increased.

  Further, the length of the microlens 21 in the major axis direction (horizontal width of the microlens 21) in plan view is preferably 15 to 750 μm, more preferably 45 to 450 μm, and 75 to 150 μm. Is more preferable. When the length of the microlens 21 in the short axis direction is a value within the above range, it is possible to obtain sufficient resolution in the image projected on the screen while effectively preventing the occurrence of inconvenience such as moire. The productivity of the microlens substrate 1 (transmission type screen 10) can be further increased.

  The radius of curvature near the center of the microlens 21 is preferably 5 to 250 μm, more preferably 15 to 150 μm, and even more preferably 25 to 50 μm. When the radius of curvature near the center of the microlens 21 is within the above range, the viewing angle characteristics can be made particularly excellent. In particular, both the horizontal and vertical viewing angle characteristics can be improved. The microlens 21 may have a different radius of curvature in the minor axis direction and a radius of curvature in the major axis direction. In such a case, the radius of curvature in the major axis direction is a value within the above range. Is preferred.

The height of the microlens 21 is preferably 5 to 250 μm, more preferably 15 to 150 μm, and still more preferably 25 to 100 μm. When the height of the microlens 21 is within the above range, the light utilization efficiency and viewing angle characteristics can be made particularly excellent.
Further, when the height of the microlens 21 is H [μm] and the length of the microlens 21 in the short axis direction is S [μm], the relationship of 0.9 ≦ S / H ≦ 2.5 is satisfied. It is more preferable that the relationship of 1.0 ≦ S / H ≦ 1.8 is satisfied, and it is more preferable that the relationship of 1.2 ≦ S / H ≦ 1.6 is satisfied. By satisfying such a relationship, the viewing angle characteristic can be made particularly excellent while effectively preventing the occurrence of moire due to light interference.

  The plurality of microlenses 21 are arranged in a staggered pattern (in a staggered pattern). By arranging the microlenses 21 in this way, it is possible to effectively prevent inconveniences such as moire. On the other hand, for example, if the microlenses are arranged in a square lattice shape or the like, it may be difficult to sufficiently prevent the occurrence of inconvenience such as moire depending on the size of the microlenses 21 and the like. . Further, when the microlenses are randomly arranged, depending on the size of the microlens 21 or the like, it becomes difficult to sufficiently increase the occupation ratio of the microlenses in the effective region where the microlenses are formed. It is difficult to sufficiently increase the transmittance (light utilization efficiency), and the obtained image may be dark.

As described above, in the present embodiment, the microlenses 21 are arranged in a staggered pattern when the microlens substrate 1 is viewed in plan view. However, the first row includes a plurality of microlenses 21. 25 and the second row 26 adjacent thereto are preferably shifted by a half pitch in the vertical direction (the minor axis direction of the microlens 21). As a result, it is possible to more effectively prevent the occurrence of moire due to light interference and to make the viewing angle characteristics particularly excellent.
The arrangement method of the microlenses 21 is not limited to the one described above. For example, even if the arrangement is a square lattice, the arrangement is optically random (from the main surface side of the microlens substrate 1 in plan view). In this case, the microlenses 21 may be arranged in a random positional relationship with each other.

Further, when the microlens substrate 1 is viewed in plan from the light incident surface side (direction shown in FIG. 2), the occupation ratio of the microlens 21 is 90% or more in the effective region where the microlens 21 is formed. It is preferable that it is 96% or more, and it is more preferable that it is 97-99.5%. When the occupation ratio of the microlens 21 is a value within the above range, the light use efficiency can be further improved, and the brightness and contrast of the projected image can be made particularly excellent. Note that the occupation ratio of the microlens 21 is the center (the center of the top) 212 of the microlens 21 when viewed in plan and the central portion of the portion adjacent to the microlens 21 where the microlens 21 is not formed. In the line segment to be connected, the ratio of the length L ₃ [μm] of the portion where the microlens 21 is formed to the length L ₄ [μm] of the line segment (L ₃ / L ₄ × 100 [%]) (See FIG. 2).

  As described above, by strictly defining the shape and arrangement method of the microlenses, the viewing angle characteristics and the like can be made particularly excellent while effectively preventing the occurrence of moire due to light interference. . In particular, by strictly defining the shape and arrangement method of the microlens as described above, the effect of having the microlens having the shape and arrangement method as described above and the black matrix 3 as described in detail later are provided. The effects of having them act synergistically, and particularly excellent effects (for example, particularly excellent viewing angle characteristics, light utilization efficiency, etc.) can be obtained.

  Each microlens 21 is formed using a method as described later, and the focal point f is positioned in the vicinity of an opening (non-light-shielding portion) 31 provided in a black matrix (light-shielding film) 3 described later. Designed to be. That is, parallel light La (parallel light La from a Fresnel lens unit 6 described later) incident on the microlens substrate 1 from a substantially perpendicular direction is collected by each microlens 21 of the microlens substrate 1 and is black. A focal point f is formed in the vicinity of the opening 31 of the matrix 3. As described above, the microlens 21 is focused in the vicinity of the opening 31 of the black matrix 3 so that the light utilization efficiency can be made particularly excellent. As a result, the contrast of an image formed by light transmitted through the microlens substrate can be made particularly excellent.

A black matrix 3 is provided on the surface of the substrate body 2 on the light emission side. The black matrix 3 is made of a light-shielding material and is formed in a film shape. By having such a black matrix 3, the black matrix 3 can absorb external light (external light that is not preferable for forming a projection image), and the image projected on the screen has excellent contrast. Can be. In particular, by having the lens surface side light-shielding portion 4 as described above and the black matrix 3, the contrast of the image by the microlens substrate 1 can be made particularly excellent.
Such a black matrix 3 has an opening 31 on the optical path of the light transmitted through each microlens 21. Thereby, the light condensed by each micro lens 21 can be efficiently passed through the opening 31 of the black matrix 3. As a result, the light utilization efficiency of the microlens substrate 1 can be increased.

  The opening 31 sufficiently prevents the light for image formation from being absorbed and reflected by the black matrix 3 while effectively preventing reflection of external light at a portion other than the opening 31 of the black matrix 3. It is provided with a large size. In the present invention, the “opening” refers to a portion through which light can be transmitted in a light-shielding film having light-shielding properties, and is filled with a material that is not substantially colored (a material having light-transmitting properties). It is a concept that includes such parts.

  The opening 31 of the black matrix 3 may have any shape, but it is preferable that the shape when viewed in plan is substantially circular. When the opening 31 is substantially circular, the size of the opening 31 is not particularly limited, but the diameter is preferably 5 to 80 μm, more preferably 15 to 60 μm, and 20 to 50 μm. More preferably. Thereby, the image projected on a screen can be made more excellent in contrast.

  Further, the thickness (average thickness) of the black matrix 3 is preferably 0.3 to 8 μm, more preferably 0.6 to 5 μm, and further preferably 0.8 to 1.5 μm. preferable. When the thickness of the black matrix 3 is a value within the above range, the function as the black matrix 3 (that is, the image contrast is improved) while preventing unintentional peeling and cracking of the black matrix 3 more reliably. For example, in the transmission screen 10 including the microlens substrate 1, the contrast of the projected image can be made particularly excellent.

  Further, the area ratio (opening ratio) of the opening 31 to the black matrix 3 when viewed in plan is preferably 60 to 97%, more preferably 70 to 95%, and 75 to 90%. Is more preferable. If the aperture ratio is a value within the above range, external light (for example, external light incidentally incident from the side opposite to the light incident side) is sufficiently suppressed from reflecting to the output side. In addition to making the light utilization efficiency particularly excellent, it is possible to prevent the reflection and make the contrast of the obtained image particularly excellent, and the viewing angle characteristics of the microlens substrate 1 are particularly excellent. Can be. On the other hand, if the aperture ratio is less than the lower limit, it may be difficult to make the light utilization efficiency and viewing angle characteristics sufficiently excellent. Also, if the aperture ratio exceeds the upper limit, it becomes difficult to keep external light reflection sufficiently low, and it becomes difficult to prevent reflection and make the contrast of the obtained image sufficiently excellent. there is a possibility.

  Since the microlens substrate (lens substrate) of the present invention is manufactured using the lens substrate forming mold of the present invention as described in detail later, it is excellent in light utilization efficiency. The light utilization efficiency of the microlens substrate 1 (ratio of the amount of light emitted from the exit surface to the amount of light incident from the entrance surface of the microlens substrate 1) is preferably 60% or more, and 70 % Is more preferable, and 80 to 95% is more preferable.

Next, the transmission screen 10 including the microlens substrate 1 as described above will be described.
As shown in FIG. 3, the transmission screen 10 includes a Fresnel lens portion 5 and the microlens substrate 1 described above. The Fresnel lens unit 5 is installed on the light (image light) incident side, and the light transmitted through the Fresnel lens unit 5 is incident on the microlens substrate 1.
The Fresnel lens unit 5 has a prism-shaped Fresnel lens 51 formed in a substantially concentric shape on the exit side surface. The Fresnel lens unit 5 refracts image light from a projection lens (not shown) to produce parallel light La parallel to the vertical direction of the main surface of the microlens substrate 1.

  In the transmissive screen 10 configured as described above, the image light from the projection lens is refracted by the Fresnel lens unit 5 and becomes parallel light La. The parallel light La is incident from the side of the microlens substrate 1 on which the microlenses 21 are formed, collected by the microlenses 21, diffused after being focused. The light that has passed through the opening 31 diffuses and is observed as a planar image by the observer.

<< Method for Manufacturing Lens Substrate Forming Mold >>
Next, a method for manufacturing a lens substrate forming mold used for manufacturing the above-described microlens substrate 1 will be described.
4 is a schematic longitudinal sectional view showing a member with a recess used for manufacturing a lens substrate forming mold, FIG. 5 is a schematic diagram showing a process of forming the member with a recess shown in FIG. FIG. 7 is a schematic diagram showing a process for forming an aspherical convex member, FIG. 8 is a schematic diagram showing a process for forming a lens substrate forming mold, and FIG. 9 is a schematic diagram showing a lens substrate forming mold of the present invention. FIG.
In the manufacturing process described below, a large number of concave portions, convex portions, microlenses, and the like are actually formed on the substrate. However, in order to make the description easy to understand, a part thereof is shown in an emphasized manner. It was.

[Recessed member preparation process]
First, prior to the description of the step of preparing the member with recesses used for manufacturing the lens substrate forming mold, the configuration of the member with recesses will be described.
Although the member 6 with a recessed part may be comprised with what kind of material, it is preferable that it is comprised with the material which is hard to produce a bending | flexion and is hard to be damaged. As a constituent material of the member 6 with a recessed part, various glass materials, various resin materials, etc. are mentioned, for example. Examples of the glass material include soda glass, crystalline glass, quartz glass, lead glass, potassium glass, borosilicate glass, and alkali-free glass. Examples of the resin material include polyethylene, polypropylene, and ethylene- Polyolefin such as propylene copolymer, ethylene-vinyl acetate copolymer (EVA), cyclic polyolefin, modified polyolefin, polyvinyl chloride, polyvinylidene chloride, polystyrene, polyamide (eg, nylon 6, nylon 46, nylon 66, nylon 610) , Nylon 612, nylon 11, nylon 12, nylon 6-12, nylon 6-66), polyimide, polyamideimide, polycarbonate (PC), poly- (4-methylpentene-1), ionomer, acrylic resin, acryloni Ryl-butadiene-styrene copolymer (ABS resin), acrylonitrile-styrene copolymer (AS resin), butadiene-styrene copolymer, polyoxymethylene, polyvinyl alcohol (PVA), ethylene-vinyl alcohol copolymer (EVOH) ), Polyesters such as polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycyclohexane terephthalate (PCT), polyether, polyetherketone (PEK), polyetheretherketone (PEEK), polyetherimide, polyacetal (POM) ), Polyphenylene oxide, modified polyphenylene oxide, polysulfone, polyethersulfone, polyphenylene sulfide, polyarylate, aromatic polyester (liquid crystal polymer) Polytetrafluoroethylene, polyvinylidene fluoride, other fluororesins, styrene, polyolefin, polyvinyl chloride, polyurethane, polyester, polyamide, polybutadiene, trans polyisoprene, fluoro rubber, chlorinated polyethylene Various thermoplastic elastomers such as epoxy resins, phenol resins, urea resins, melamine resins, unsaturated polyesters, silicone resins, urethane resins, etc., or copolymers, blends, polymer alloys, etc. mainly comprising these A resin material etc. are mentioned, Among these, it can use combining 1 type (s) or 2 or more types. Among these, as a constituent material of the member 6 with a recessed part, a glass material is preferable and soda glass, crystalline glass (for example, neo-ceram etc.), and an alkali free glass are more preferable. Such a material is generally excellent in shape stability. Further, soda glass, crystalline glass, and non-alkali glass are easy to process, are relatively inexpensive, and are advantageous from the viewpoint of manufacturing cost.

The member 6 with recesses includes a plurality of spherically shaped recesses 61 arranged in a system (transferred positional relationship) corresponding to the array system of the microlenses 21.
More specifically, in the present embodiment, the concave portion 61 has a flat shape (substantially oval) in which the vertical width (width in the vertical direction) when viewed in plan is smaller than the horizontal width (width in the horizontal direction). (Substantially bowl-shaped). Since the concave portion 61 has such a shape, the obtained lens substrate forming mold K1 can effectively prevent the occurrence of inconvenience such as moire and can have a particularly excellent viewing angle characteristic. The lens substrate 1 can be preferably used for manufacturing.

Further, when the length in the minor axis direction (vertical direction) of the concave portion 61 in plan view is L ₁ [μm] and the length in the major axis direction (lateral direction) is L ₂ [μm], 0.10 ≦ L ₁ / L ₂ ≦ 0.99 is preferably satisfied, more preferably 0.50 ≦ L ₁ / L ₂ ≦ 0.95 is satisfied, and 0.60 ≦ L ₁ / L _It is more preferable to satisfy the relationship of ₂ ≦ 0.80. By satisfying the relationship as described above, the effects as described above become more remarkable.

  Further, the length in the minor axis direction of the recess 61 when viewed in plan is preferably 10 to 500 μm, more preferably 30 to 300 μm, and further preferably 50 to 100 μm. When the length of the concave portion 61 in the minor axis direction is a value within the above range, the viewing angle characteristics of the manufactured microlens substrate 1 and the contrast and brightness of the image projected by the microlens substrate 1 are particularly excellent. However, sufficient resolution can be obtained in the projected image. Further, when the length of the concave portion 61 in the short axis direction is a value within the above range, it is possible to effectively prevent the occurrence of inconvenience such as moire when the manufactured microlens substrate 1 is used.

  Further, the length in the major axis direction of the concave portion 61 when viewed in plan is preferably 15 to 750 μm, more preferably 45 to 450 μm, and further preferably 75 to 150 μm. When the length of the concave portion 61 in the major axis direction is a value within the above range, the viewing angle characteristics of the microlens substrate 1 manufactured using the obtained lens substrate forming mold K1 and the microlens substrate 1 are projected. It is possible to obtain a sufficient resolution in the projected image while making the contrast and luminance of the image to be particularly excellent. Further, when the length of the concave portion 61 in the major axis direction is a value within the above range, inconvenience such as moire occurs when the microlens substrate 1 manufactured by the obtained lens substrate forming mold K1 is used. While being able to prevent effectively, productivity of the microlens board | substrate 1 (member 6 with a recessed part) can further be improved.

  The concave portion 61 has a spherical shape, and the radius of curvature is preferably 5 to 250 μm, more preferably 15 to 150 μm, and further preferably 25 to 50 μm. When the curvature radius of the concave portion 61 is a value within the above range, the viewing angle characteristics of the microlens substrate 1 manufactured using the obtained lens substrate forming mold K1 can be made particularly excellent. In particular, both the horizontal and vertical viewing angle characteristics can be improved. The concave portion 61 may have a different radius of curvature in the minor axis direction and a radius of curvature in the major axis direction. In such a case, the radius of curvature in the major axis direction is a value within the above range. Preferably there is.

Moreover, it is preferable that the depth of the recessed part 61 is 5-250 micrometers, It is more preferable that it is 15-150 micrometers, It is further more preferable that it is 25-100 micrometers. When the depth of the recess 61 is a value within the above range, the viewing angle characteristics of the microlens substrate 1 manufactured using the obtained lens substrate forming mold K1 can be made particularly excellent.
The plurality of recesses 61 are arranged in a staggered pattern (in a staggered pattern). By arranging the recesses 61 in this way, it is possible to effectively prevent the occurrence of inconvenience such as moire when the microlens substrate 1 manufactured using the obtained lens substrate forming mold K1 is used. . On the other hand, for example, if the recesses are arranged in a square lattice shape, it is difficult to sufficiently prevent the occurrence of inconvenience such as moire depending on the size of the recesses. In addition, when the concave portions are randomly arranged, depending on the size of the concave portion or the like, it becomes difficult to sufficiently increase the occupancy ratio of the concave portions in the effective region where the concave portions are formed. It is difficult to sufficiently increase the use efficiency), and the resulting image may be dark.

  Further, as described above, the recesses 61 are arranged in a staggered pattern when the member 6 with recesses is viewed in plan view, but are adjacent to the first row composed of the plurality of recesses 61. It is preferable that the second row is shifted by a half pitch in the vertical direction (the short axis direction of the recess 61). As a result, when the manufactured microlens substrate 1 is used, it is possible to more effectively prevent the occurrence of moiré due to light interference and to make the viewing angle characteristics particularly excellent. it can.

Next, the manufacturing method of a member with a recessed part (member preparation process with a recessed part) is demonstrated, referring FIG. In practice, a large number of concave portions (lens forming concave portions) are formed on the substrate. Here, in order to make the explanation easy to understand, a part thereof is highlighted.
<A1> First, when manufacturing the member 6 with a recess, the substrate 60 is prepared.
As the substrate 60, a substrate having a uniform thickness and free from bending and scratches is preferably used. The substrate 60 preferably has a surface cleaned by cleaning or the like.

<A2> A mask 8 having a large number of initial holes (openings) 81 is formed on the surface of the prepared substrate 60, and the back surface of the substrate 60 (the surface opposite to the surface on which the mask 8 is formed) A protective film 89 is formed (see a masking process, FIGS. 5A and 5B).
In particular, in this embodiment, first, as shown in FIG. 5A, a back surface protective film 89 is formed on the back surface of the prepared substrate 60, and a mask forming film 80 is formed on the surface of the substrate 60 (mask). Then, as shown in FIG. 5B, the mask 8 is obtained by forming the initial hole 81 in the mask forming film 80 (initial hole forming process). The mask forming film 80 and the back surface protective film 89 can be formed simultaneously.

  The mask forming film 80 is preferably capable of forming an initial hole 81 to be described later by laser light irradiation or the like and having resistance to etching in an etching process to be described later. In other words, the mask forming film 80 (mask 8) is preferably configured so that the etching rate is substantially equal to or lower than that of the substrate 60.

From this point of view, the material forming the mask forming film 80 (mask 8) is, for example, a metal such as Br, Au, Ni, Ti, or Pt, an alloy containing two or more selected from these metals, Examples thereof include oxides (metal oxides), silicon, and resins.
Further, the mask forming film 80 (mask 8) may have, for example, a substantially uniform composition, or a laminated body having a plurality of different layers.

  As described above, the configuration of the mask forming film 80 (mask 8) is not particularly limited. However, the mask forming film 80 (mask 8) is a laminate including a layer mainly composed of chromium and a layer mainly composed of chromium oxide. Preferably there is. The mask forming film 80 having such a configuration can easily and surely form an opening having a desired shape by irradiation of laser light as described later. The mask 8 obtained by using the mask forming film 80 has excellent stability with respect to etching solutions having various compositions (the substrate 60 can be more reliably protected in an etching process described later). . Further, when the substrate 60 is made of a glass material and the mask forming film 80 (mask 8) has the above structure, for example, in an etching process described later, one hydrogen as an etchant is used. A liquid containing ammonium difluoride can be suitably used. Since ammonium monohydrogen difluoride is not a poisonous deleterious substance, it is possible to prevent the human body and the environment during work more reliably. Further, the mask forming film 80 (mask 8) having the above-described configuration can relieve the internal stress of the mask efficiently, and is particularly excellent in adhesion with the substrate 60 (particularly, adhesion in the etching process). ing. For this reason, by using the mask forming film 80 (mask 8) having the above-described configuration, it is possible to easily and reliably form the recess 61 having a desired shape.

  A method for forming the mask forming film 80 is not particularly limited, but the mask forming film 80 (mask 8) is made of a metal material (including an alloy) such as chromium (Br) or gold (Au) or a metal oxide (for example, chromium oxide). ), Or a composite material thereof (for example, a laminated body having a metal layer made of a metal material and a metal oxide layer made of a metal oxide, etc.) The film 80 can be suitably formed by, for example, a vapor deposition method or a sputtering method. When the mask forming film 80 (mask 8) is made of silicon, the mask forming film 80 can be suitably formed by, for example, a sputtering method or a BVD method.

  The thickness of the mask forming film 80 (mask 8) varies depending on the material constituting the mask forming film 80 (mask 8), but is preferably about 0.01 to 2.0 μm, preferably 0.01 to 0.3 μm. The degree is more preferable. If the thickness is less than the lower limit, the shape of the initial hole 81 formed in the initial hole forming step (opening forming step) described later may be distorted depending on the constituent material of the mask forming film 80 and the like. There is. In addition, when wet etching is performed in an etching process described later, the masked portion of the substrate 60 may not be sufficiently protected. On the other hand, if the upper limit value is exceeded, depending on the constituent material of the mask forming film 80, it becomes difficult to form the initial hole 81 that penetrates in the initial hole forming step described later, and the mask forming film 80 (mask Due to the internal stress of 8), the mask forming film 80 (mask 8) may be easily peeled off.

  The back surface protective film 89 is for protecting the back surface of the substrate 60 in the subsequent steps. By this back surface protective film 89, erosion, deterioration, etc. of the back surface of the substrate 60 are suitably prevented. This back surface protective film 89 has the same configuration as the mask forming film 80 (mask 8), for example. Therefore, the back surface protective film 89 can be provided in the same manner as the mask forming film 80 simultaneously with the formation of the mask forming film 80.

<A3> Next, as shown in FIG. 5B, a plurality of initial holes (openings) 81 are formed in the mask forming film 80 to obtain a mask 8 (initial hole forming step). The initial hole 81 formed in this step functions as a mask opening in the later-described etching.
A method for forming the initial hole 81 is not particularly limited, but a method using laser light irradiation is preferable. Thereby, the initial holes 81 having a desired shape arranged in a desired pattern can be easily and accurately formed. As a result, the shape, arrangement method, and the like of the recesses 61 can be controlled more reliably. In addition, by forming the initial hole 81 by laser irradiation, a member with a recess can be manufactured with high productivity. In particular, the concave portion can be easily formed even on a large-area substrate. In addition, by forming the initial hole 81 in the mask forming film 80 by laser light irradiation, the opening (e.g., easier and less expensive than the case where the opening is formed in the resist film by a photolithography method as in the prior art. An initial hole 81) can be formed.

When the initial hole 81 is formed by laser light irradiation, the type of laser light to be used is not particularly limited, but a ruby laser, a semiconductor laser, a YAG laser, a femtosecond laser, a glass laser, a YVO ₄ laser, a Ne- Examples include He laser, Ar laser, CO ₂ laser, and excimer laser. Moreover, you may use wavelengths, such as SHG of each laser, THG, and FHG.

  The shape and size of the initial hole 81 formed in this step is not particularly limited, but is substantially circular and the diameter is preferably 0.5 to 30 μm, more preferably 1.0 to 10 μm. Preferably, it is 1.5-5 micrometers. When the diameter of the initial hole 81 is a value within the above range, the concave portion 61 having the above-described shape can be reliably formed in the etching process described later. However, when the initial hole 81 has a flat shape such as a substantially elliptical shape, the length in the minor axis direction can be substituted for the value of the diameter. That is, when the initial hole 81 formed in this step has a flat shape, the width of the initial hole 81 (length in the minor axis direction) is not particularly limited, but is preferably 0.8 to 30 μm, More preferably, it is 1.0-10 micrometers, and it is still more preferable that it is 1.5-5 micrometers. When the width of the initial hole 81 is a value within the above range, the concave portion 61 having the above-described shape can be reliably formed in the etching process described later.

  In addition, when the initial hole 81 formed in this step is a flat shape, the length of the initial hole 81 (length in the major axis direction) is preferably 0.5 to 30 μm, and 1.0 to More preferably, it is 15 micrometers, and it is still more preferable that it is 1.5-10 micrometers. When the length of the initial hole 81 is a value within the above range, the concave portion 61 having the above-described shape can be more reliably formed in the etching process described later.

<A4> Next, as shown in FIG. 5C, the substrate 60 is etched using the mask 8 in which the initial holes 81 are formed, and a large number of recesses 61 are formed on the substrate 60 (etching step). .
The etching method is not particularly limited, and examples thereof include wet etching and dry etching. In the following description, a case where wet etching is used will be described as an example.

By performing etching (wet etching) on the substrate 60 covered with the mask 8 in which the initial holes 81 are formed, as shown in FIG. 5C, the substrate 60 has a portion where the mask 8 does not exist ( A large number of recesses 61 are formed on the substrate 60 by etching from a portion corresponding to the initial hole 81 of the mask 8. As described above, since the initial holes 81 formed in the mask 8 are arranged in a staggered pattern (in a staggered pattern), the formed recesses 61 are formed in a staggered pattern (in a staggered pattern) on the surface of the substrate 60. It will be arranged.
Further, when the wet etching method is used, the concave portion 61 can be suitably formed. For example, when an etchant containing ammonium monohydrogen difluoride is used as the etchant, the substrate 60 can be etched more selectively, and the recesses 61 can be suitably formed.

In the case where the mask 8 (mask forming film 80) is mainly composed of chromium or chromium oxide, a liquid containing ammonium monohydrogen difluoride is particularly suitable as the hydrofluoric acid-based etching solution. Since the ammonium hydrogen difluoride solution is not a poisonous and deleterious substance, it can prevent the influence on the human body and the environment during work. When ammonium monohydrogen difluoride is used as the etching solution, the etching solution may contain, for example, hydrogen peroxide and / or sulfuric acid. Thereby, an etching speed can be made faster.
In addition, wet etching can be performed with a simpler apparatus than dry etching, and more substrates can be processed at one time. Thereby, productivity improves and the member 6 with a recessed part can be provided cheaply.

<A5> Next, as shown in FIG. 5D, the mask 8 is removed (mask removal step). At this time, the back surface protective film 89 is also removed together with the removal of the mask 8.
When the mask 8 is a laminated body having a layer mainly composed of chromium and a layer mainly composed of chromium oxide as described above, the removal of the mask 8 is, for example, ceric ammonium nitrate and perchlorine. It can carry out suitably by etching using a mixture containing an acid.

For example, you may perform a mold release process to the surface side in which the recessed part 61 of the member 6 with a recessed part is provided. Thereby, in the manufacturing method of the lens substrate forming mold K1 described in detail later, the concave member 6 is formed while sufficiently preventing defects such as chipping from occurring in the convex portion 41 ′ of the convex member 4 ′. It can be easily removed. As the mold release treatment, for example, formation of a film composed of a material having releasability such as silicone resin such as alkylpolysiloxane, fluorine resin such as polytetrafluoroethylene, hexamethyldisilazane ([(CH _{3) 3 Si]} 2 NH) surface treatment with a silylating agent such as a surface treatment or the like with a fluorine gas.

As described above, as shown in FIG. 4, the concave member 6 in which a large number of concave portions 61 are formed in a staggered pattern on the substrate 60 is obtained.
The method of forming the plurality of recesses 61 arranged in a staggered pattern on the substrate 60 is not particularly limited, but the method as described above (the initial holes 81 in the mask forming film 80 by laser light irradiation). To obtain the mask 8, and then etching using the mask 8 to form the recess 61 on the substrate 60), the following effects are obtained.

That is, by forming the initial hole 81 in the mask forming film 80 by laser light irradiation, the opening (with a predetermined pattern) can be easily and inexpensively compared with the case where the opening is formed by a conventional photolithography method. A mask having initial holes 81) can be obtained. Thereby, productivity improves and the member 6 with a recessed part can be provided cheaply.
Further, according to the method as described above, it is possible to easily perform processing on a large substrate. When manufacturing a large substrate (a member with a recess, a lens substrate), it is not necessary to bond a plurality of substrates as in the prior art, and the seam of the bonding can be eliminated. As a result, a high-quality large-sized substrate (a member with a recess, a lens substrate) can be manufactured at a low cost by a simple method.
Further, when the initial holes 81 are formed by laser irradiation, the shape, size, arrangement, and the like of the formed initial holes 81 can be managed easily and reliably.

[Protruding member forming step]
Next, a step of forming a member with convex portions having a large number of spherical convex portions using the member 6 with concave portions as described above (a member forming step with convex portions) will be described.
The convex member 4 ′ is formed using the concave member 6 described above as a mold (a convex member forming step).
Specifically, the convex member 4 ′ is formed as follows.

<B1> First, as shown in FIG. 6A, the resin material 40 in a fluid state (for example, the softened resin material 40, An unpolymerized (uncured) resin material 40) is applied, and the resin material 40 is pressed by the flat plate 9.
In this way, by using a resin material as a material for forming the member 4 ′ with a recess, a part near the surface of the protrusion 41 ′ can be easily removed in a member forming process with an aspherical protrusion described later. Can do.

As the resin material 40, the same resin material that constitutes the microlens substrate 1 described above can be used.
In addition, the flat plate 9 may be obtained by performing the above-described mold release treatment on the surface on the side where the resin material 40 is pressed. Thereby, in the process mentioned later, flat plate 9 can be efficiently removed from the surface of member 4 'with convex part.

<B2> Next, the resin material 40 is solidified (including curing (polymerization)), and then the member 6 with concave portions and the flat plate 9 are removed (see FIG. 6B). Thereby, the member 4 ′ having a convex portion including the spherical convex portion 41 ′ is obtained.
In the case where the resin material 40 is solidified by curing (polymerization), examples of the method include irradiation with light such as ultraviolet rays, irradiation with electron beams, and heating.

[Aspherical convex member forming process]
Next, the aspherical convex member 4 having an aspherical convex part (aspherical convex part) 41 is obtained by removing a part of the convex part 41 ′ of the convex parted member 4 ′ as described above. Forming (aspherical convex member forming step).
As described above, the present invention is characterized in that an aspherical convex portion (aspherical convex portion) is formed by removing a part of the spherical convex portion formed as described above. Yes. This makes it possible to easily form a member with an aspherical convex part having an aspherical convex part, and by using this member with an aspherical convex part as a mold, a lens substrate forming mold having an aspherical concave part K1 can be easily formed. Then, by manufacturing the lens substrate using the lens substrate forming mold K1 formed in this way, the spherical aberration of the lens of the lens substrate obtained can be reduced, and as a result, the use of light A lens substrate having excellent efficiency and viewing angle characteristics can be provided.
A method for removing a portion near the surface of the convex portion 41 ′ is not particularly limited, but in the present embodiment, a case where removal is performed by laser light irradiation will be described.

<B3> First, as shown in FIG. 7 (c), the convex portion 41 'to, by irradiating a laser beam L _b, protrusion 41' to remove a portion near the surface of the. By removing using the laser beam in this way, the convex portion 41 ′ can be more easily converted into an aspherical convex portion 41 having an aspheric shape. In general, when a part of the convex portion 41 ′ is removed by cutting or the like, a removed portion or an angular portion is generated in the vicinity thereof, but when laser light is used, due to the heat of laser light irradiation, The angular portion is removed, and the surface shape of the aspherical convex portion 41 can be made smooth. As a result, in the finally obtained microlens substrate 1, it is possible to effectively prevent the occurrence of uneven brightness and uneven color. When laser light is used, the aspherical convex portion 41 having a desired shape can be easily formed by appropriately adjusting the power density of the laser light, the irradiation time, the number of times of irradiation (number of shots), and the like.

In particular, when the shape of the microlens 21 as described above is formed, as shown in FIG. 7C, by irradiating a part of the portion excluding the vicinity of the central portion of the convex portion 41 ′ with the laser light Lb. The shape of the microlens 21 as described above can be formed.
When removing a part of the portion excluding the vicinity of the central portion of the convex portion 41 ′ as in the present embodiment, for example, the laser light is applied to the convex portion 41 ′ via a mask having an opening formed in a ring shape. This can be done by irradiation.

The type of laser light to be used is not particularly limited, but ruby laser, semiconductor laser, YAG laser, femtosecond laser, glass laser, YVO ₄ laser, Ne-He laser, Ar laser, CO ₂ laser, excimer laser, etc. Can be mentioned.
As described above, the aspherical convex member 4 having the same surface shape as that of the microlens substrate 1 is obtained (see FIG. 7D).

In addition, you may perform a mold release process to the surface side in which the aspherical convex part 41 of the member 4 with an aspherical convex part is provided. Accordingly, in the lens substrate forming mold forming step, which will be described in detail later, the aspherical convex member 4 can be easily formed while sufficiently preventing defects such as chipping in the concave portion K11 of the lens substrate forming mold K1. Can be removed. As the mold release treatment, for example, formation of a film composed of a material having releasability such as silicone resin such as alkylpolysiloxane, fluorine resin such as polytetrafluoroethylene, hexamethyldisilazane ([(CH _{3) 3 Si]} 2 NH) surface treatment with a silylating agent such as a surface treatment or the like with a fluorine gas.

  In the above description, the laser beam is used to remove a part of the convex part 41 ′. However, the present invention is not limited to this. For example, the ion beam is irradiated to remove a part of the convex part 41 ′. May be. Even when the ion beam is used, the same effect as that obtained when the laser beam described above is used can be obtained. When an ion beam is used, a heat treatment may be performed on the surface on the convex portion 41 ′ side after removing a part of the convex portion 41 ′. Thereby, the angular part is removed, and the surface shape of the aspherical convex part 41 can be made smoother.

[Lens substrate forming mold forming process]
Next, a process (lens substrate forming mold forming process) of forming the lens substrate forming mold K1 having a large number of aspherical concave portions using the aspherical convex member 4 as described above will be described.
The lens substrate forming mold K1 is formed by using the aspherical convex member 4 as a mold.

Specifically, the lens substrate forming mold K1 can be obtained as follows.
<C1> First, a conductive film (not shown) is formed on the surface of the member 4 with the aspherical convex portion on the side where the aspherical convex portion 41 is formed.
The material constituting the conductive film is not particularly limited as long as it is a conductive material, and examples thereof include nickel, aluminum, copper, iron, zinc, and alloys thereof.
The conductive film can be formed, for example, by vapor deposition methods such as vapor deposition, ion plating, and sputtering, and wet plating methods such as electrolytic plating and electroless plating. In addition, formation of the electrically conductive film by a wet plating method can be performed after making particles, such as palladium, adhere to the surface in the side in which the aspherical convex part 41 was provided previously.

<C2> Next, as shown in FIG. 8A, a metal substrate (electroformed metal) is electrodeposited on the surface of the conductive film by electroforming to form a lens substrate forming mold K1. By using such an electroforming method, the surface shape of the aspherical convex member 4 can be accurately transferred.
Examples of the electroformed metal include nickel, copper, iron, silver, gold, and alloys thereof.

  Thereafter, by removing the member 4 with aspherical convex portions, a lens substrate forming mold K1 (lens substrate forming mold according to the present invention) having a large number of aspherical concave portions K11 is obtained (FIG. 8 (FIG. 8 ( b), see FIG. Since the lens substrate forming mold K1 thus obtained has a shape corresponding to the aspherical convex member 4 as described above, it can be obtained using this lens substrate forming mold K1. The microlens substrate 1 is excellent in characteristics such as light utilization efficiency and viewing angle characteristics.

<Manufacture of microlens substrate>
Next, a method for manufacturing the microlens substrate 1 using the lens substrate forming mold K1 described above will be described.
10 and 11 are schematic longitudinal sectional views showing an example of a method for manufacturing the microlens substrate shown in FIG. In the following description, the lower side in FIGS. 10 and 11 is referred to as “(light) incident side”, and the upper side is referred to as “(light) emission side”.

  <D1> First, as shown in FIG. 10A, a resin material 23 having fluidity (for example, in a softened state) is formed on the surface of the lens substrate forming mold K1 on which the aspherical concave portion K11 is formed. The resin material 23 and the unpolymerized (uncured) resin material 23) are applied, and the resin material 23 is pressed by the flat plate 9 ″. In particular, in this embodiment, the lens substrate forming mold K1 and the flat plate 9 ″ are The resin material 23 is pressed with the spacer 20 interposed therebetween. Thereby, the thickness of the microlens substrate 1 to be formed can be more reliably controlled, and the focal position of the microlens 21 on the finally obtained microlens substrate 1 can be more reliably controlled. And the occurrence of inconvenience such as color unevenness can be more effectively prevented.

  The spacer 20 is made of a material having a refractive index comparable to that of the resin material 23 (solidified resin material 23). By using the spacer 20 made of such a material, the spacer 20 can be obtained even when the spacer 20 is arranged in the portion where the aspherical concave portion K11 of the lens substrate forming mold K1 is formed. An adverse effect on the optical characteristics of the lens substrate 1 can be effectively prevented. As a result, it is possible to dispose a relatively large number of spacers 20 over almost the entire effective area of the main surface (surface side where the recesses are formed) of the lens substrate forming mold K1, and as a result, the lens substrate forming mold K1. It is possible to effectively eliminate the influence of the deflection of the mold K1, the flat plate 9 ″, etc., and to control the thickness of the obtained microlens substrate 1 more reliably.

As described above, the spacer 20 is made of a material having the same refractive index as that of the resin material 23 (the resin material 23 after solidification). More specifically, the absolute refraction of the constituent material of the spacer 20 is used. The absolute value of the difference between the refractive index and the absolute refractive index of the resin material 23 after solidification is preferably 0.20 or less, more preferably 0.10 or less, and further preferably 0.02 or less. Preferably, the solidified resin material 23 and the spacer 20 are most preferably composed of the same material.
The shape of the spacer 20 is not particularly limited, but is preferably substantially spherical or substantially cylindrical. When the spacer 20 has such a shape, the diameter is preferably 10 to 300 μm, more preferably 30 to 200 μm, and still more preferably 30 to 170 μm.

When the spacer 20 is used as described above, the spacer 20 may be provided between the lens substrate forming mold K1 and the flat plate 9 ″ when the resin material 23 is solidified, and the spacer 20 is supplied. The timing is not particularly limited, and for example, a resin material 23 in which spacers 20 are dispersed in advance as a resin to be applied may be used on the surface of the lens substrate forming mold K1 on which the aspherical concave portion K11 is formed. The resin material 23 may be applied in a state where the spacer 20 is arranged on the substrate forming mold K1, or the spacer 20 may be applied after the resin material 23 is supplied.
Further, the flat plate 9 ″ may have a surface on which the resin material 23 is pressed, which has been subjected to the mold release treatment as described above. It can be removed from the surface of the substrate body 2.

<D2> Next, the resin material 23 is solidified (including curing (polymerization)), and then the flat plate 9 ″ is removed (see FIG. 10B). Thereby, the aspherical concave portion K11 is filled. A substrate body 2 having a microlens 21 made of resin (in particular, a microlens 21 that satisfies the above-described conditions such as shape and arrangement) is obtained.
When the resin material 23 is solidified by curing (polymerization), examples of the method include irradiation with light such as ultraviolet rays, irradiation with electron beams, and heating.

<D3> Next, as shown in FIG. 10C, a colored black matrix-forming material (light-shielding film-forming material) is applied to the exit-side surface of the substrate body 2, and the black matrix-forming material is used. The formed film 32 is formed (light shielding film forming material application step).
The method for applying the black matrix forming material to the surface of the substrate body 2 is not particularly limited. For example, dip coating, doctor blade, spin coating, brush coating, spray coating, electrostatic coating, electrodeposition coating, roll coater, etc. Various coating methods, vapor deposition methods, ion plating methods, vapor phase film formation methods such as sputtering methods, wet plating methods such as electrolytic plating and electroless plating, and the like can be applied. In particular, when the black matrix 3 is formed as a laminate having a layer mainly composed of chromium and a layer mainly composed of chromium oxide, the film 32 is preferably formed by a vapor deposition method. Further, when the black matrix 3 is formed as a material composed of a material containing a pigment or dye (particularly, a material composed of a material including a resin material in addition to the pigment or dye), the black matrix 3 is formed by a coating method. Is preferred. Thereby, the film | membrane 32 of uniform thickness can be formed easily.

  When the black matrix 3 is formed of a material including a pigment or a dye, the black matrix forming material includes a resin material and a liquid medium (for example, a solvent, a dispersion medium, in addition to the pigment and the dye). A liquid that functions as a liquid). Thereby, the film 32 having a uniform thickness can be formed easily and reliably, and the adhesion of the formed film 32 (black matrix 3) to the substrate body 2 can be made particularly excellent. . Further, if the black matrix forming material is composed of a material including a resin material and a liquid medium in addition to a pigment and a dye, a predetermined portion of the film 32 is formed in an opening forming step described in detail later. Can be easily and reliably removed, and the black matrix 3 having the openings 31 having a desired shape can be more reliably formed.

In this step, a treatment for removing a part of the components constituting the black matrix forming material may be performed in the subsequent step. For example, when the black matrix forming material is made of a material containing a liquid medium, for example, a process for removing the liquid medium from the film 32 made of the black matrix forming material (for example, heat treatment) , Decompression treatment or the like).
The thickness of the film 32 formed in this step is usually substantially the same as the thickness of the black matrix 3. Therefore, the thickness (average thickness) of the film 32 is preferably 0.3 to 8.0 μm, more preferably 0.8 to 7.0 μm, and 1.4 to 6.0 μm. Is more preferable.

  <D4> Next, as shown in FIG. 11D, the substrate body 2 is removed from the lens substrate forming mold K1. In this manner, by removing the lens substrate forming mold K1 from the substrate body 2, the removed lens substrate forming mold K1 can be repeatedly used for manufacturing the substrate body 2 (microlens substrate 1). This is advantageous in terms of cost and stability of the quality of the manufactured substrate body 2 (microlens substrate 1).

  <D5> Next, as shown in FIG. 11E, the substrate body 2 is irradiated with a laser beam Lb in a direction perpendicular to the incident-side surface. The irradiated laser beam Lb is refracted and collected by entering the microlens 21. And the film | membrane (film | membrane comprised with the light shielding film formation material) 32 of the site | part irradiated with the laser beam which became high energy by condensing is removed, and the opening part 31 is formed (FIG. 11 ( f)). Thereby, the microlens substrate 1 having the black matrix (light shielding film) 3 is obtained.

  As described above, in this embodiment, a part of the film made of the light shielding film forming material is removed by the energy of the focused laser beam, and the opening 31 is formed. As described above, by using the light condensed by the microlens (particularly, laser light having a uniform frequency and phase), only a predetermined portion of the film made of the colored light-shielding film forming material is selectively selected. Can be removed. In other words, by using the laser beam condensed by the microlens to form the opening, light having a high energy density can be selectively given only to a specific part, and the opening is formed of a light shielding film forming material. In addition, it is possible to selectively remove the opening portion of the film, and to effectively prevent the other portion from being adversely affected. Moreover, according to this embodiment, the light shielding film which has the opening part of a desired shape in a desired site | part can be reliably formed with a simple method with few processes. As a result, an image obtained by using the microlens substrate can have excellent light utilization efficiency and excellent contrast.

In addition, since the laser light is generally light having a uniform frequency and phase, by selecting the type of laser light according to the film made of the light shielding film forming material and the constituent material of the microlens substrate, It is possible to more reliably prevent the occurrence of adverse effects on the portions of the film composed of the substrate body and the light shielding film forming material that should remain.
The type of laser light used in this step is not particularly limited. For example, ruby laser, semiconductor laser, YAG laser, femtosecond laser, glass laser, YVO ₄ laser, Ne-He laser, Ar laser, CO ₂ laser, excimer A laser etc. are mentioned. Moreover, you may use wavelengths, such as SHG of each laser, THG, and FHG.
Note that the above-described series of processes of applying the light-shielding film forming material and irradiating the laser beam may be repeated. Thereby, the light shielding film (black matrix) can be formed thicker, and the contrast can be further improved.

《Rear projection TV》
Next, a rear projection TV using the transmission screen described above will be described.
FIG. 12 is a diagram schematically showing the configuration of the rear projection TV of the present invention.
As shown in the figure, the rear projection TV 300 has a configuration in which a projection optical unit 310, a light guide mirror 320, and a transmission screen 10 are arranged in a housing 340.

Since the rear projection TV 300 includes the transmission screen 10 as described above, it is possible to display an excellent image with excellent contrast and generation of bright spots. It also has excellent viewing angle characteristics, light utilization efficiency, and the like.
In particular, in the microlens substrate 1 described above, since the elliptical microlenses 21 are arranged in a staggered pattern (in a staggered pattern), the rear projection TV 300 is not particularly susceptible to problems such as moire.

As mentioned above, although this invention was demonstrated based on embodiment of illustration, this invention is not limited to these.
For example, each part of the lens substrate forming mold, the lens substrate (microlens substrate), the transmissive screen, and the rear projection TV can be replaced with one having any configuration that can exhibit the same function. Moreover, you may add arbitrary structures. For example, the lens substrate may have a colored portion colored at a predetermined density near the surface thereof. Thereby, the contrast of the displayed image can be further improved.

Moreover, in the manufacturing method of the lens substrate forming mold and the lens substrate (microlens substrate), an arbitrary step may be added.
In addition, the order of the steps in the lens substrate forming mold and the lens substrate manufacturing method is not limited to that described above, and the order may be changed as necessary.
Moreover, in embodiment mentioned above, although demonstrated as what gives a composition to the surface of the member with a recessed part and a lens substrate formation type | mold, for example, on the surface of a flat plate (or base material film mounted on the flat plate) You may manufacture a member with a convex part and a micro lens substrate by providing a composition and pressing this with a member with a concave part and a lens substrate formation type | mold.

In the above-described embodiment, the lens substrate is described as a microlens substrate including a microlens. However, in the present invention, the lens substrate may be, for example, a lenticular lens substrate.
In the above-described embodiment, the transmission screen is described as including a microlens substrate and a Fresnel lens portion. However, the transmission screen of the present invention does not necessarily include a Fresnel lens portion. Good. For example, the transmission screen of the present invention may be substantially constituted only by the microlens substrate of the present invention.

  In the above-described embodiment, the lens substrate is described as a member constituting the transmission screen and the rear projection TV. However, the use of the lens substrate of the present invention is not limited to the above. Anything can be used. For example, the lens substrate of the present invention includes a diffusion plate, a black matrix screen, a projection display device (front projector) screen (front projection screen), a liquid crystal light valve component of the projection display device (front projector), a laser printer. It may be applied to a condensing element of an LED light source, a constituent member of a backlight requiring a liquid crystal panel, or the like.

(Example 1)
[Recessed member preparation process]
The member with a recessed part provided with the recessed part was manufactured as follows.
First, a soda glass substrate (absolute refractive index n ₂ : 1.50) having a width of 1.2 m × length of 0.7 m and a thickness of 4.8 mm was prepared as a substrate.
This soda glass substrate was immersed in a cleaning solution containing 4 wt% ammonium monohydrogen difluoride and 8 wt% hydrogen peroxide and etched by 6 μm to clean the surface.
Thereafter, cleaning with pure water and drying using N ₂ gas (removal of pure water) were performed.

  Next, a chromium / chromium oxide laminate (a laminate in which chromium oxide was laminated on the outer surface side of chromium) was formed on the soda glass substrate by sputtering. That is, a mask forming film and a back surface protective film made of a chromium / chromium oxide laminate were formed on the surface of a soda glass substrate. The thickness of the chromium layer was 0.03 μm, and the thickness of the chromium oxide layer was 0.01 μm.

Next, laser processing was performed on the mask forming film to form a large number of initial holes in a range of 113 cm × 65 cm in the central portion of the mask forming film, thereby forming a mask.
The laser processing was performed using an excimer laser under the conditions of an energy density of 1.2 J / cm ² , a beam diameter of 2 μm at the processing point, and a scanning speed of 0.1 m / sec.
As a result, substantially circular initial holes were formed in a staggered pattern over the entire range of the mask forming film. The diameter of the initial hole was 2 μm.

Next, wet etching was performed on the soda glass substrate to form concave portions (recesses for forming microlenses) having a flat shape (substantially elliptical shape) when viewed in plan on the soda glass substrate. The formed recess has a spherical surface, and the length (pitch) in the minor axis direction is 75 μm, the length in the major axis direction is 100 μm, the radius of curvature is 50 μm, and the depth is 50 μm. Moreover, the occupation rate of the recessed part in the effective area | region in which the recessed part was formed was 98%.
In the wet etching, an aqueous solution containing 4 wt% ammonium monohydrogen difluoride and 8 wt% hydrogen peroxide was used as an etchant, and the immersion time was 2.0 hours.

Next, the mask and the back surface protective film were removed by etching using a mixture of ceric ammonium nitrate and perchloric acid.
Next, cleaning with pure water and drying using N ₂ gas (removal of pure water) were performed.
Thereafter, a gas phase surface treatment (silylation treatment) with hexamethyldisilazane was performed on the side of the substrate where the concave portions were formed, and a mold release treatment was performed.
Thereby, the member with a recessed part in which many spherical-shaped recessed parts were arranged on the soda glass substrate in zigzag form was obtained.

[Protruding member forming step]
Next, unpolymerized (uncured) acrylic resin (PMMA resin (methacrylic resin)) was applied to the surface of the member with recesses on the side where the recesses were formed.
Next, the acrylic resin was pressed with a flat plate made of soda glass. At this time, air was prevented from entering between the flat plate and the acrylic resin. Moreover, as a flat plate, the surface on which the acrylic resin is pressed is subjected to a gas phase surface treatment (mold release treatment) with hexamethyldisilazane.

Thereafter, the acrylic resin was cured by heating to 120 ° C. to obtain a member with convex portions having a large number of spherical convex portions. The length (pitch) of the convex portion in the minor axis direction was 75 μm, the length in the major axis direction was 100 μm, the radius of curvature was 50 μm, and the height was 50 μm. Moreover, the occupation rate of the convex part in the effective area | region in which the convex part is formed was 98%.
Next, the concave member and the flat plate were removed.

[Aspherical convex member forming process]
Next, by irradiating the convex part of the member with the convex part with laser light, a part of the convex part was removed, and an aspherical convex part was formed. The irradiated laser beam was a ring having an inner diameter of 26 μm and an outer diameter of 70 μm, and was irradiated so that the center of the ring coincided with the center when the convex portion was viewed in plan. The energy density of the laser beam was 1.2 J / cm ² and the number of shots of the laser beam for one convex lens was two.
Thereby, the member with an aspherical convex part which has an aspherical aspherical convex part was obtained.

When the shape of the cross section of the formed aspherical concave portion is expressed by the above-described formula (I), the radius of curvature R ₀ of the reference spherical surface of the convex portion formed on the member with the aspherical convex portion is 50 μm, the cone coefficient A Was 1.0, the aspheric coefficient A ₁ was 0.32, and the aspheric coefficient A ₂ was 0.40.
Thereafter, a gas phase surface treatment (silylation treatment) with hexamethyldisilazane was performed on the surface side where the aspherical convex portion was formed, and a mold release treatment was performed.

[Lens substrate forming mold forming process]
Next, palladium powder was adhered to the surface of the member with the aspherical convex portion on the side where the aspherical convex portion is formed.
Next, a conductive film made of Ni-P was formed on the surface of the member with the aspherical convex portion on the side where the aspherical convex portion was formed by electroless plating.

Next, Ni was electrodeposited on the conductive film by electroforming to form a lens substrate forming mold.
Thereafter, the aspherical convex member was removed to obtain a lens substrate forming mold having an aspherical aspherical recess. The length (pitch) in the minor axis direction of the formed recess was 75 μm, the length in the major axis direction was 100 μm, the radius of curvature was 50 μm, and the depth was 50 μm. Moreover, the occupation rate of the recessed part in the effective area | region in which the recessed part was formed was 98%. Moreover, the recessed part had the shape corresponding to the aspherical convex part of the said member with an aspherical convex part.

[Microlens substrate formation process]
Next, the aspherical convex member and the flat plate were removed.
Next, unpolymerized (uncured) acrylic resin (PMMA resin (methacrylic resin)) was applied to the surface of the lens substrate forming mold on which the concave portion was formed.
Next, the acrylic resin was pressed with a flat plate made of soda glass. At this time, air was prevented from entering between the flat plate and the acrylic resin. Moreover, as a flat plate, the surface on which the acrylic resin is pressed is subjected to a gas phase surface treatment (mold release treatment) with hexamethyldisilazane.

  Thereafter, the acrylic resin was cured by heating to 120 ° C. to obtain a substrate body provided with a large number of aspherical microlenses. The length (pitch) in the minor axis direction of the microlens was 75 μm, the length in the major axis direction was 100 μm, the radius of curvature was 50 μm, and the height was 50 μm. Moreover, the occupation ratio of the convex part in the effective area | region in which the micro lens was formed was 98%. Further, the microlens had the same shape as the aspherical convex portion of the member having the aspherical convex portion.

Next, the flat plate was removed.
Next, a colored light-shielding film forming material containing a black pigment was applied to the surface of the substrate on the emission side (surface opposite to the surface on which the microlenses are formed) by a roll coater (light-shielding film forming material). Application step). As the light-shielding film forming material, a mixture containing 10 wt% black pigment, 20 wt% damar resin, and 70 wt% xylene (liquid medium) was used.
Thereafter, xylene was removed from the light-shielding film forming material applied to the substrate, thereby forming a film covering the entire emission side of the substrate. The average thickness of the formed film was 5 μm.

Next, the lens substrate forming mold was removed from the substrate body provided with the light shielding film forming material.
Next, a laser beam in the vertical direction was irradiated from the surface of the substrate body on which the microlens was formed to the incident-side surface of the substrate body (opening forming step). As a result, the laser light is condensed by the microlens, and only the vicinity of the condensing portion of the microlens is selectively removed from the film, and the black matrix having a large number of openings is coated on the substrate body. Thus obtained microlens substrate was obtained. The opening had a flat shape (substantially elliptical shape), and the length (diameter) in the minor axis direction was 23 μm and the length in the major axis direction was 30 μm. The formed black matrix had a thickness of 5 μm.
A transmissive screen as shown in FIG. 3 was obtained by assembling the microlens substrate manufactured as described above and the Fresnel lens portion manufactured by extrusion molding.

(Examples 2 to 5)
In the member forming process with aspherical convex portions, the laser light irradiation conditions were changed as shown in Table 1, and thereby the curvature radius, conical coefficient, and aspherical coefficient of the reference spherical surface were set to values as shown in Table 1. A microlens substrate and a transmissive screen were manufactured in the same manner as in Example 1 except for the above.
(Example 6)
A microlens substrate and a transmission screen were manufactured in the same manner as in Example 1 except that in the step of forming the member with aspherical convex portions, an ion beam was irradiated instead of the laser beam. For ion beam irradiation, an ion beam irradiation apparatus is used to apply a laser beam pressure of 5 × 10 ⁻³ Pa and an ion acceleration voltage to the portion irradiated with the laser beam in the first embodiment. The test was performed at 200V.

(Comparative example)
A microlens substrate and a transmissive screen were produced in the same manner as in Example 1 except that the substrate body was produced using the concave member obtained in Example 1 as a lens substrate forming mold.
About each said Example and a comparative example, the irradiation condition of the laser beam in the member formation process with an aspherical convex part, the curvature radius of a reference spherical surface regarding an aspherical convex part, a cone coefficient, an aspherical coefficient, and the manufactured microlens substrate has Table 1 summarizes the radius of curvature, conical coefficient, aspheric coefficient, etc. of the reference spherical surface of the microlens.

[Evaluation of image brightness (light utilization efficiency)]
The luminance of the image (light utilization efficiency) was evaluated for the transmissive screens of the examples and comparative examples.
The evaluation of the luminance (light utilization efficiency) of the image is based on the luminance B of light measured on the light exit surface side of the transmissive screen when white light of A (= 300) [cd / m ² ] is incident. This was performed by determining the ratio (B / A) of [cd / m ² ]. It can be said that the larger the value of B / A, the better the light utilization efficiency.

[Production of rear projection TV]
Rear projection TVs as shown in FIG. 12 were produced using the transmissive screens of the respective examples and comparative examples.
[Evaluation of viewing angle characteristics]
With the sample image displayed on the transmission screen of the rear projection TV of each of the examples and comparative examples, the viewing angle is measured in the vertical direction (up and down direction) and in the horizontal direction (left and right direction), and the α angle (1/2 gain), β angle (1/3 gain), and γ angle (1/10 gain) were obtained.
The viewing angle was measured under the condition of measuring at an interval of 1 degree with a variable angle photometer (goniophotometer).
These results are summarized in Table 2.

  As is clear from Table 2, in the present invention, both the light utilization efficiency and the viewing angle characteristics were excellent. On the other hand, in the comparative example, a satisfactory result was not obtained.

It is a typical longitudinal section showing a suitable embodiment of a micro lens substrate (lens substrate) of the present invention. FIG. 2 is a plan view of the microlens substrate shown in FIG. 1. It is a typical longitudinal cross-sectional view which shows suitable embodiment of the transmission type screen of this invention provided with the micro lens board | substrate (lens board | substrate) shown in FIG. It is a typical longitudinal cross-sectional view which shows the member with a recessed part used for manufacture of the type | mold for lens substrate formation. It is a typical schematic diagram which shows the formation process of the member with a recessed part shown in FIG. It is a schematic diagram which shows the formation process of a member with an aspherical convex part. It is a schematic diagram which shows the formation process of a member with an aspherical convex part. It is a schematic diagram which shows the formation process of the type | mold for lens substrate formation. It is a typical longitudinal cross-sectional view which shows the lens substrate formation type | mold of this invention. It is sectional drawing which showed typically the manufacturing process of the lens board | substrate (microlens board | substrate) of this invention. It is sectional drawing which showed typically the manufacturing process of the lens board | substrate (microlens board | substrate) of this invention. It is a figure which shows typically the structure of the rear type projection TV of this invention.

Explanation of symbols

  DESCRIPTION OF SYMBOLS 1 ... Micro lens board | substrate (lens board | substrate) 2 ... Board | substrate main body 20 ... Spacer 21 ... Micro lens (convex lens) 212 ... Center 23 ... Resin material 25 ... 1st row | line 26 ... 2nd row 3 ... Black matrix (light-shielding film) DESCRIPTION OF SYMBOLS 31 ... Opening part 32 ... Film | membrane (film | membrane comprised with the material for light shielding film formation) 4 ... Member with aspherical convex part 40 ... Resin material 41 ... Aspherical convex part 4 '... Member with convex part 41' ... Convex part ( (Spherical convex part) 5 ... Fresnel lens part 51 ... Fresnel lens 6 ... Member with concave part (member with concave part for microlens formation) 61 ... Concave part 60 ... Substrate 8 ... Mask 81 ... Initial hole (opening part) 89 ... Back surface protective film 80 ... Mask forming film 9, 9 "... Flat plate K1 ... Lens substrate forming mold K11 ... Recess (aspherical recess) 10 ... Transmission screen 300 ... Rear projection TV 310 ... projection optical unit 320 ... light guide mirror 340 ... housing

Claims (10)

A method of manufacturing a lens substrate forming mold used for forming a lens substrate having a large number of convex lenses,
A member-with-recess preparing step for preparing a member with a recessed portion having a number of spherically-shaped recessed portions;
A member having a spherical convex portion is formed using the member with concave portion as a mold, and forming a member having a spherical convex portion having a plurality of spherical convex portions corresponding to the shape of the concave portion of the member having the concave portion,
By removing a part of the spherical convex part, an aspherical aspherical convex part is formed, and an aspherical convex part-equipped member forming step for forming an aspherical convex parted member;
A lens substrate forming mold forming step of obtaining a lens substrate forming mold having a concave portion having a shape corresponding to the convex lens, using the aspherical convex member as a mold. Production method.   The method for manufacturing a lens substrate forming mold according to claim 1, wherein, in the member forming step with the aspherical convex portion, a part of the convex portion is removed by laser light irradiation.   The method for manufacturing a lens substrate forming mold according to claim 1, wherein in the member forming step with the aspherical convex portion, a part of the convex portion is removed by irradiation with an ion beam. 4. The lens according to claim 1, wherein the aspherical convex portion satisfies a relationship of A ≧ 0.1 and at least A ₁ ≠ 0 when the cross-sectional shape is represented by the following formula (I). A method for manufacturing a substrate forming mold.

  A lens substrate forming mold manufactured by using the method according to claim 1. A lens substrate having a substrate body having a large number of convex lenses and a light-shielding film made of a light-shielding material and having an opening,
A lens substrate, wherein the substrate body is formed using the lens substrate forming mold according to claim 5.   The lens substrate according to claim 6, which is a microlens substrate including a microlens as the convex lens.   A transmissive screen comprising the lens substrate according to claim 6. A Fresnel lens part having a Fresnel lens formed on the light exit side;
A transmissive screen comprising the lens substrate according to claim 6, which is disposed on a light emission side of the Fresnel lens portion.   A rear projection TV comprising the transmissive screen according to claim 8.