JP2008023797A - Steel plate with coating paper and its manufacturing method - Google Patents

Steel plate with coating paper and its manufacturing method Download PDF

Info

Publication number
JP2008023797A
JP2008023797A JP2006197314A JP2006197314A JP2008023797A JP 2008023797 A JP2008023797 A JP 2008023797A JP 2006197314 A JP2006197314 A JP 2006197314A JP 2006197314 A JP2006197314 A JP 2006197314A JP 2008023797 A JP2008023797 A JP 2008023797A
Authority
JP
Japan
Prior art keywords
paper
paint
rust
steel sheet
thickness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2006197314A
Other languages
Japanese (ja)
Inventor
Fujio Nagumo
富士雄 南雲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TOONETSU KK
Original Assignee
TOONETSU KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TOONETSU KK filed Critical TOONETSU KK
Priority to JP2006197314A priority Critical patent/JP2008023797A/en
Publication of JP2008023797A publication Critical patent/JP2008023797A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a steel plate with coating paper which is strong to wind and rain, has good effects against dew condensation and is less prone to deterioration. <P>SOLUTION: The steel plate consists of a steel plate material 1 of an appropriate thickness, a rust-preventive primer coating 2 applied to one surface of the steel plate material, paper 3 superimposed on the rust-preventive primer coating 2 and impregnated with the coating in a part of the thickness and a top coat 4 applied to the exposed side surface of the paper 3. The rust-preventive primer coating 2 soaks into the paper 3 to about a half or smaller of the thickness. The steel plate is formed into a coil as a product. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、風雨に対して強く、しかも結露に対して良好な効果を奏し、劣化しにくい塗料ペーパー付き鋼板及びその製造法に関する。   The present invention relates to a steel sheet with paint paper which is strong against wind and rain, has a good effect on condensation, and hardly deteriorates, and a method for producing the same.

従来の折板屋根において、金属板の裏面には接着剤によって断熱材が接着されている。該断熱材は一般に４ｍｍと５ｍｍがあり結露防止の役割をなしている。     In the conventional folded-plate roof, the heat insulating material is adhere | attached with the adhesive agent on the back surface of the metal plate. The heat insulating material generally has a thickness of 4 mm and 5 mm, and plays a role in preventing condensation.

また、折板屋根としての金属板の裏面に接着された断熱材は外部に露出していなければ紫外線による劣化はないものと思われるが、実際には、例えば駅のホームの屋根や配送センターの庇屋根などでは、トラックのコンテナの照り返しによって紫外線の影響を受けている。これによって断熱材が劣化し接着部から剥がれて断熱材は落下するなどの事故も発生している。   In addition, the heat insulating material bonded to the back surface of the metal plate as a folded plate roof is considered not to be deteriorated by ultraviolet rays unless it is exposed to the outside, but in reality, for example, the roof of the station platform or the distribution center On thatched roofs, the impact of ultraviolet rays is due to the reflection of truck containers. As a result, the heat insulating material is deteriorated and peeled off from the bonded portion, and the heat insulating material is dropped and accidents have occurred.

また、特許文献１は、鋼板と塗料とペーパーハニカムとを具備しているが、屋根材などに用いるものではなく、デスク又は家具などの天板に関するものであり、目的も相違し、さらにペーパー構成も著しく相違している。また、近年、アスベストが含有しているスレート屋根が公害の元凶となっており、その代替品開発が緊急に求められている。
特開２０００−２７９２３４ Moreover, although patent document 1 is equipped with the steel plate, the coating material, and the paper honeycomb, it is not used for a roofing material etc., but is related to top plates, such as a desk or furniture, The objective is also different, Furthermore, paper structure Is also significantly different. In recent years, slate roofs containing asbestos have become the source of pollution, and there is an urgent need to develop alternatives.
JP 2000-279234 A

このようなことから、断熱材を落下させることなく、結露防止の役割をなす部材が求められている。このため、結露防止をなし、風雨に対して強く、しかも劣化しにくい構成の鋼板を開発するとともに、アスベスト入りのスレート屋根の代替品として開発することを目的としたものである。   For this reason, there is a demand for a member that plays a role in preventing condensation without dropping the heat insulating material. For this reason, it aims at developing a steel plate having a structure that prevents condensation, is strong against wind and rain, and is not easily deteriorated, and as an alternative to a slate roof containing asbestos.

そコーテ、発明者は上記課題を解決すべく鋭意，研究を重ねた結果、請求項１の発明を、適宜の厚さの鋼板材と、該鋼板材の一面に塗布された錆止めプライマー塗料と、該錆止めプライマー塗料に重ねられて塗料を厚みの一部に染みこませたペーパーと、該ペーパーの露出側面に上塗り塗料が塗布されてなることを特徴とする塗料ペーパー付き鋼板としたことにより、前記課題を解決した。   As a result of intensive studies and studies by the inventors to solve the above-mentioned problems, the invention of claim 1 is made of a steel plate material having an appropriate thickness, and a rust-preventing primer coating applied to one surface of the steel plate material, By making a steel sheet with paint paper, wherein the paper coated with the rust-preventing primer paint is impregnated with a part of the thickness, and an overcoating paint is applied to the exposed side surface of the paper. Solved the problem.

請求項２の発明を、前述の構成において、前記ペーパーの厚みの約半分以下に前記錆止めプライマー塗料が浸み込んでなることを特徴とする塗料ペーパー付き鋼板としたことにより、前記課題を解決した。また、請求項３の発明を、前述の構成において、前記ペーパーの厚みの約半分以下に前記上塗り塗料が塗布されてなることを特徴とする塗料ペーパー付き鋼板としたことにより、前記課題を解決した。また、請求項４の発明を、前述の構成において、製品としてコイル状に形成されてなることを特徴とする塗料ペーパー付き鋼板としたことにより、前記課題を解決した。   The invention of claim 2 is the steel sheet with paint paper characterized in that, in the above-mentioned configuration, the rust-preventing primer paint is immersed in about half or less of the thickness of the paper, the problem is solved. . The invention of claim 3 is the steel sheet with paint paper characterized in that, in the above-mentioned configuration, the top coat paint is applied to about half or less of the thickness of the paper. . Moreover, the said subject was solved by making invention of Claim 4 into the steel plate with paint paper characterized by being formed in the coil shape as a product in the above-mentioned structure.

請求項５の発明を、適宜の厚さの鋼板材の一面に錆止めプライマー塗料を塗布し、該錆止めプライマー塗料面にペーパーを重ねつつ該ペーパーの一部に前記錆止めプライマー塗料を染みこませ、次いで前記ペーパーの露出側面に上塗り塗料を塗布してなることを特徴とする塗料ペーパー付き鋼板の製造法としたことにより、前記課題を解決した。     The invention according to claim 5 is a method of applying a rust-preventing primer paint on one surface of a steel sheet having an appropriate thickness, and impregnating the rust-preventing primer paint into a part of the paper while overlapping the paper on the rust-preventing primer paint surface, The above-mentioned problems have been solved by employing a method for producing a steel sheet with paint paper, characterized in that a top coat is applied to the exposed side surface of the paper.

請求項６の発明を、前述の構成において、前記ペーパーの厚みの約半分以下に前記錆止めプライマー塗料を浸み込ませてなることを特徴とする塗料ペーパー付き鋼板の製造法としたことにより、前記課題を解決した。また、請求項７の発明を、前述の構成において、前記ペーパーの厚みの約半分以下に前記上塗り塗料を塗布してなることを特徴とする塗料ペーパー付き鋼板の製造法としたことにより、前記課題を解決した。また、請求項８の発明を、前述の構成において、最終段階にてコイル状に形成したことを特徴とする塗料ペーパー付き鋼板の製造法としたことにより、前記課題を解決したものである。     The invention of claim 6 is a method for producing a steel sheet with paint paper, characterized in that, in the above-mentioned configuration, the rust-preventing primer paint is immersed in about half or less of the thickness of the paper. Solved the problem. The invention of claim 7 is the method for producing a steel sheet with paint paper, characterized in that, in the above-mentioned configuration, the top coat paint is applied to about half or less of the thickness of the paper. Solved. The invention of claim 8 solves the above-mentioned problems by adopting a method for producing a steel sheet with paint paper, which is characterized in that it is formed in a coil shape at the final stage in the above-described configuration.

請求項１の発明においては、接着剤を使わなくとも、ペーパーを鋼板材に対して良好に接着でき、結露防止の役割をなす部材としての塗料付きペーパーが落下することを防止できる。また、ペーパーの存在にて表面温度を上昇させることができ、結露防止もある程度良好にできるものである。さらに、ペーパーの露出側面が上塗り塗料の存在にて結露水を保有できる。また、本発明品はアスベスト入りのスレート屋根の代替品として、公害を防止しつつ断熱性能の優れたものとして提供できる。請求項２及び３でも請求項１と同等の効果を奏する。   According to the first aspect of the present invention, the paper can be satisfactorily adhered to the steel plate material without using an adhesive, and the coated paper as a member for preventing condensation can be prevented from falling. Further, the surface temperature can be raised by the presence of paper, and condensation can be prevented to some extent. In addition, the exposed side of the paper can retain dew condensation water due to the presence of the top coat. In addition, the product of the present invention can be provided as an alternative to a slate roof containing asbestos with excellent heat insulation performance while preventing pollution. Claims 2 and 3 have the same effects as those of Claim 1.

請求項４の製造法の発明においては、結露防止の役割をなす部材としての塗料付きペーパーを著しく落下しにくくできる。さらに、ペーパーの存在にて表面温度を上昇させることで、結露防止もある程度良好にできる。さらに、ペーパーの露出側面が上塗り塗料の存在にて結露水を保有できる。請求項５及び６でも請求項４と同等の効果を奏する。   In the invention of the manufacturing method according to the fourth aspect, the paper with paint as a member for preventing condensation can be remarkably prevented from dropping. Furthermore, by increasing the surface temperature in the presence of paper, condensation can be prevented to some extent. In addition, the exposed side of the paper can retain dew condensation water due to the presence of the top coat. Claims 5 and 6 have the same effect as that of Claim 4.

本発明の第１実施例であって、図１乃至２に示すように、適宜の厚さの鋼板材１と、該鋼板材１の一面[図１乃至２において、上面であり、通常は、コイル状としたときには、図１（Ａ）に示すように、裏面側となる]に塗布された錆止めプライマー塗料２と、該錆止めプライマー塗料２に重ねられて該錆止めプライマー塗料２を染みこませたペーパー３と、該ペーパー３の露出側面に上塗り塗料４が塗布されて塗料ペーパー付き鋼板として構成されている。該塗料ペーパー付き鋼板は製品としてはコイル状に構成されている。   In the first embodiment of the present invention, as shown in FIGS. 1 and 2, a steel plate material 1 having an appropriate thickness and one surface of the steel plate material 1 [in FIGS. As shown in FIG. 1 (A), when it is coiled, the rust-preventing primer paint 2 applied on the back side] and the rust-preventing primer paint 2 are soaked in the rust-preventing primer paint 2 The top coating material 4 is applied to the paper 3 and the exposed side surface of the paper 3 to form a steel sheet with paint paper. The steel sheet with paint paper is configured in a coil shape as a product.

具体的には、前記鋼板材１は、約０．２５ｍｍ〜約２ｍｍの亜鉛鉄板、アルミメッキ鋼板、塗装したカラー鉄板等である。また、前記錆止めプライマー塗料２は、材質としては、エポキシ、ウレタン、アクリル樹脂などであり、好ましくは、速乾特殊錆止めプライマー塗料２ａが使用される。その塗布量としては、約５０〜約２００ｇ／ｍ２である。さらに好ましくは、前記錆止めプライマー塗料２の塗布量は、約１３０〜約１６０ｇ／ｍ２である。また、錆止めプライマー塗料２は、２液の場合もあるが、１液とするのが好適である。さらに、プライマー塗料のプライマーには、錆止め内容が包含されているとする考え方もあるため、この明細書では、錆止めプライマー塗料２とプライマー塗料とは同一用語とする。 Specifically, the steel plate material 1 is a galvanized iron plate of about 0.25 mm to about 2 mm, an aluminized steel plate, a painted color iron plate, or the like. The rust-preventing primer paint 2 is made of epoxy, urethane, acrylic resin, or the like, and a quick-drying special rust-preventing primer paint 2a is preferably used. The coating amount is about 50 to about 200 g / m 2 . More preferably, the coating amount of the rust-preventing primer coating 2 is about 130 to about 160 g / m 2 . Further, the rust-preventing primer coating 2 may be two liquids, but is preferably one liquid. Furthermore, since there is a concept that the primer of the primer paint includes rust prevention content, in this specification, the rust prevention primer paint 2 and the primer paint are the same terms.

また、前記ペーパー３は、約０．２ｍｍ〜約１．２ｍｍで、パルプ材、フェルトなどの繊維材、不燃材などより形成され、保水性を有する材料を構成している。具体的には、ウェットフェルト材や、バルクファイバー材、或いは天然鉱物ケイ酸マグネシウムからなる無機質原紙などである。また、前記上塗り塗料４は、水性、油性を問わず、水蒸気を通さない膜ができるような塗料を外すものであり、ウレタン、アクリルエマルジョン、アクリル樹脂製などである。好ましくは、水性反応硬化形ウレタン上塗り塗料４ａが使用される。その塗布量としては、約５０〜約１６０ｇ／ｍ２である。さらに好ましくは、前記ペーパー３の塗布量は約１２０〜約１４０ｇ／ｍ２である。 The paper 3 is about 0.2 mm to about 1.2 mm, and is formed of a fiber material such as pulp material or felt, a non-combustible material, or the like, and constitutes a material having water retention. Specifically, it is a wet felt material, a bulk fiber material, or an inorganic base paper made of a natural mineral magnesium silicate. Further, the top coat 4 is a paint that removes a paint that can form a water vapor-impervious film regardless of water or oil, and is made of urethane, acrylic emulsion, acrylic resin, or the like. Preferably, the aqueous reaction curable urethane top coat 4a is used. The coating amount is about 50 to about 160 g / m 2 . More preferably, the coating amount of the paper 3 is about 120 to about 140 g / m 2 .

特に重要な点は、前記鋼板材１の一面に塗布された前記錆止めプライマー塗料２に、乾かない状態の約３０秒〜２分後に、前記ペーパー３が重ねられる。このとき、該ペーパー３の厚みの約半分以下の繊維部分に前記錆止めプライマー塗料２が浸み込んでおり、且つ該錆止めプライマー塗料２が前記ペーパー３の裏面まで露出していないことが必要である。     The particularly important point is that the paper 3 is overlaid on the rust-preventing primer coating 2 applied on one surface of the steel plate material 1 after about 30 seconds to 2 minutes in a dry state. At this time, it is necessary that the rust-preventing primer coating 2 is infiltrated into a fiber portion of about half or less of the thickness of the paper 3 and that the rust-preventing primer coating 2 is not exposed to the back surface of the paper 3. .

これを模式的な断面図として書くと、図２（Ｂ）に示すように、前記ペーパー３の厚みｔに対してこの約半分と、前記錆止めプライマー塗料２が浸み込んだ厚みｔａとが略等しい状態であり、これ以下となっていることが好ましい。つまり、前記ペーパー３の厚みｔの約半分以下の繊維部分に前記錆止めプライマー塗料２が浸み込んでおり、前記ペーパー３の裏面側の厚みの約半分は、繊維質のみで構成するような状態を保持している[図２（Ａ）]。そして、該ペーパー３の裏面側に前記上塗り塗料４が塗布される。この塗布によって該塗料が、前記ペーパー３の厚みｔの約半分又はこれ以下の裏面側の繊維部分Ｔｂに浸透し、水性反応して保水性を有する働きをなす。     When this is written as a schematic cross-sectional view, as shown in FIG. 2 (B), about half of the thickness t of the paper 3 and the thickness ta into which the rust-preventing primer paint 2 has been immersed are approximately. It is preferable that the state is equal to or less than this. That is, the rust-preventing primer coating 2 is immersed in a fiber portion of about half or less of the thickness t of the paper 3, and about half of the thickness on the back side of the paper 3 is composed of only fiber. [FIG. 2 (A)]. Then, the top coat 4 is applied to the back side of the paper 3. By this application, the paint permeates into the fiber portion Tb on the back surface side which is about half or less than the thickness t of the paper 3 and functions to have water retention through an aqueous reaction.

次に、本発明の製造法について図４（Ａ）及び（Ｂ）にて説明する。まず、適宜の厚さのコイルとして巻かれている鋼板材１がセットされる。この場合のコイル状の鋼板材１の外表面（上面）が本発明の塗料ペーパー付き鋼板の裏面側となるようにして設けられている。該鋼板材１の上面[製品となった場合には裏面：図１（Ａ）参照]に前記錆止めプライマー塗料２を塗布する。この塗布は、具体的には、コーティングロール１０にて塗布する。塗料厚は調整ロール１１、１２間の間隙にて調整する。     Next, the manufacturing method of the present invention will be described with reference to FIGS. First, the steel plate material 1 wound as a coil having an appropriate thickness is set. In this case, the outer surface (upper surface) of the coiled steel sheet material 1 is provided so as to be the back surface side of the steel sheet with paint paper of the present invention. The rust-preventing primer coating 2 is applied to the upper surface of the steel plate 1 [the rear surface when it becomes a product: see FIG. 1 (A)]. Specifically, this coating is performed by the coating roll 10. The coating thickness is adjusted by the gap between the adjustment rolls 11 and 12.

この直後に、コイル状のペーパー３を巻き解きつつ、前記錆止めプライマー塗料２の上面にペーパー３を重ねつつ該ペーパー３の一部に前記錆止めプライマー塗料２を染みこませる。この重ね工程は、上下の押圧ロール１３、１４にて行う。この直後に、その前記錆止めプライマー塗料２を第１乾燥機１５にて約３０秒から約２分乾燥させる。そして、前記ペーパー３の裏面側の厚みの約半分は、繊維質のみで構成するような状態を保持させて、該ペーパー３の上面（塗料ペーパー付き鋼板の裏面側）に、前記上塗り塗料４を塗布する。この塗布は、具体的には、コーティングロール１６にて２回目の塗布をする。塗料厚は上部調整ロール１７、１８間の間隙にて調整する。この直後に、前記上塗り塗料４を第２乾燥機１９にて約２分から約４分乾燥させる。このような作業によって塗料ペーパー付き鋼板を製造する。     Immediately after this, the rust-preventing primer paint 2 is soaked in a part of the paper 3 while unrolling the coiled paper 3 and overlapping the paper 3 on the upper surface of the rust-preventing primer paint 2. This overlapping process is performed by the upper and lower pressing rolls 13 and 14. Immediately after this, the rust-preventing primer coating 2 is dried in the first dryer 15 for about 30 seconds to about 2 minutes. And about half of the thickness of the back surface side of the paper 3 is kept in a state of being composed of only the fiber, and the top coating material 4 is applied to the upper surface of the paper 3 (the back surface side of the steel sheet with paint paper). Apply. Specifically, this coating is performed for the second time by the coating roll 16. The coating thickness is adjusted by the gap between the upper adjustment rolls 17 and 18. Immediately after this, the top coat 4 is dried in the second dryer 19 for about 2 minutes to about 4 minutes. A steel sheet with paint paper is manufactured by such operations.

このように製造した塗料ペーパー付き鋼板では、最大の特長は、そのペーパー３が剥がれない。つまり、前記錆止めプライマー塗料２が、前記ペーパー３と前記鋼板材１とに対して接着剤の役割をなすためである。これによって、風雨などでも容易に剥がれて一部落下する危険を回避できる。水性、油性を問わず、水蒸気を通さない膜ができるような塗料を外すものである。   In the steel sheet with paint paper manufactured in this way, the greatest feature is that the paper 3 is not peeled off. In other words, the rust-preventing primer coating 2 serves as an adhesive for the paper 3 and the steel plate material 1. As a result, it is possible to avoid the risk of being easily peeled off and partly dropped even in wind and rain. Regardless of whether it is water-based or oil-based, it removes the paint that can form a film that does not allow water vapor to pass.

また、前記ペーパー３の存在にて、表面温度を上げることができる。この機能によって結露水がそのペーパー３内に留まり、落下しにくくできる。特に、つまり、ペーパー３箇所で結露水を吸収する役割をなす。これは、前記上塗り塗料４の存在が、前記ペーパー３の保水性を維持するのに役立つものである。前記上塗り塗料４は、水性、油性を問わず、水蒸気を通さない膜ができるような塗料を外すものであり、保水性維持ができる。     Further, the presence of the paper 3 can increase the surface temperature. With this function, the condensed water stays in the paper 3 and can be prevented from falling. In particular, it plays the role of absorbing condensed water at three locations on the paper. This is because the presence of the top coat 4 helps to maintain the water retention of the paper 3. Regardless of whether it is water-based or oil-based, the top coat 4 removes a paint that forms a film that does not allow water vapor to pass through, and can maintain water retention.

また、本発明の塗料ペーパー付き鋼板を、ＪＲなどの駅ホームの折板屋根に応用した場合には、従来でも、関東地区では、雪が降った翌朝に結露水の落下が見られる程度であり、このような場合にも十分な対応ができるものである。さらに、上塗り塗料４なる塗料ゆえに、前記ペーパー３の劣化などを保護する役割もなすとともに、前記ペーパー３の剥がれを阻止できるものである。     In addition, when the steel sheet with paint paper of the present invention is applied to a folded-plate roof of a station platform such as JR, conventionally, in the Kanto area, the fall of condensed water is seen the next morning when it snows, Even in such a case, a sufficient countermeasure can be taken. Furthermore, because of the paint that is the top coat 4, it also serves to protect the paper 3 from deterioration and the like, and can prevent the paper 3 from peeling off.

（Ａ）は本発明の実施形態を示す斜視図、（Ｂ）は（Ａ）の（ア）個所の拡大断面図である。(A) is a perspective view which shows embodiment of this invention, (B) is an expanded sectional view of the (a) location of (A). （Ａ）は本発明の実施形態を示す要部拡大断面図、（Ｂ）は本発明の実施形態の変形例を示す要部拡大断面図である。(A) is a principal part expanded sectional view which shows embodiment of this invention, (B) is a principal part expanded sectional view which shows the modification of embodiment of this invention. （Ａ）乃至（Ｄ）は、本発明の製造法の過程を示す断面図であって、（Ａ）は鋼板の断面図、（Ｂ）は鋼板上に錆止めプライマー塗料を塗布した状態の断面図、（Ｃ）は前記錆止めプライマー塗料上にペーパーを重ねつつ該ペーパーの一部に前記錆止めプライマー塗料を染みこませた状態の断面図、（Ｄ）は前記ペーパーの上面に上塗り塗料を塗布して該塗料を前記ペーパーの一部に染みこませた状態の断面図である。(A) thru | or (D) is sectional drawing which shows the process of the manufacturing method of this invention, Comprising: (A) is sectional drawing of a steel plate, (B) is sectional drawing of the state which apply | coated the rust prevention primer coating material on the steel plate. , (C) is a cross-sectional view of a state in which the rust-preventing primer paint is infiltrated into a part of the paper while the paper is overlaid on the rust-preventing primer paint, It is sectional drawing of the state which soaked this paint in a part of said paper. （Ａ）は本発明の製造工程の概要図、（Ｂ）はコーティングロール個所の状態図である。(A) is the outline figure of the manufacturing process of this invention, (B) is a state figure of a coating roll location.

符号の説明Explanation of symbols

１…鋼板材、２…錆止めプライマー塗料、３…ペーパー、４…上塗り塗料、
１０、１６…コーティングロール、１３、１４…押圧ロール、１５…第１乾燥機、
１９…第２乾燥機。 1 ... steel plate material, 2 ... anti-rust primer paint, 3 ... paper, 4 ... top coat paint,
10, 16 ... coating roll, 13, 14 ... pressing roll, 15 ... first dryer,
19 ... Second dryer.

Claims (8)

適宜の厚さの鋼板材と、該鋼板材の一面に塗布された錆止めプライマー塗料と、該錆止めプライマー塗料に重ねられて塗料を厚みの一部に染みこませたペーパーと、該ペーパーの露出側面に上塗り塗料が塗布されてなることを特徴とする塗料ペーパー付き鋼板。   Steel sheet material of appropriate thickness, rust-preventing primer coating applied to one surface of the steel sheet material, paper superimposed on the rust-preventing primer coating and soaking the paint into a part of the thickness, and exposed side surface of the paper A steel sheet with paint paper, characterized in that a top coat is applied to the steel sheet. 請求項１において、前記ペーパーの厚みの約半分以下に前記錆止めプライマー塗料が浸み込んでなることを特徴とする塗料ペーパー付き鋼板。   The steel sheet with paint paper according to claim 1, wherein the rust-preventing primer paint is immersed in about half or less of the thickness of the paper. 請求項１又は２において、前記ペーパーの厚みの約半分以下に前記上塗り塗料が塗布されてなることを特徴とする塗料ペーパー付き鋼板。   The steel sheet with paint paper according to claim 1 or 2, wherein the top coating material is applied to about half or less of the thickness of the paper. 請求項１、２又は３において、製品としてコイル状に形成されてなることを特徴とする塗料ペーパー付き鋼板。   The steel sheet with paint paper according to claim 1, 2 or 3, wherein the steel sheet is formed in a coil shape as a product. 適宜の厚さの鋼板材の一面に錆止めプライマー塗料を塗布し、該錆止めプライマー塗料面にペーパーを重ねつつ該ペーパーの一部に前記錆止めプライマー塗料を染みこませ、次いで前記ペーパーの露出側面に上塗り塗料を塗布してなることを特徴とする塗料ペーパー付き鋼板の製造法。   Apply a rust-preventing primer paint on one surface of a steel sheet of appropriate thickness, soak up the rust-preventing primer paint in a part of the paper while layering the paper on the rust-preventing primer paint surface, and then overcoat the exposed side of the paper A method for producing a steel sheet with paint paper, characterized by applying a paint. 請求項５において、前記ペーパーの厚みの約半分以下に前記錆止めプライマー塗料を浸み込ませてなることを特徴とする塗料ペーパー付き鋼板の製造法。   6. The method for producing a steel sheet with paint paper according to claim 5, wherein the rust-preventing primer paint is immersed in about half or less of the thickness of the paper. 請求項５又は６において、前記ペーパーの厚みの約半分以下に前記上塗り塗料を塗布してなることを特徴とする塗料ペーパー付き鋼板の製造法。   The method for producing a steel sheet with paint paper according to claim 5 or 6, wherein the top coat paint is applied to about half or less of the thickness of the paper. 請求項５、６又は７において、最終段階にてコイル状に形成したことを特徴とする塗料ペーパー付き鋼板の製造法。






8. The method of manufacturing a steel sheet with paint paper according to claim 5, 6 or 7, wherein the steel sheet is formed in a coil shape at the final stage.






JP2006197314A 2006-07-19 2006-07-19 Steel plate with coating paper and its manufacturing method Pending JP2008023797A (en)