JP2007216505A - Method and apparatus for manufacturing resin sheet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method and an apparatus for manufacturing a resin sheet which can obtain a desired cross-sectional shape without a defect when a resin sheet with a large thickness dispersion in the width direction during molding is manufactured and particularly suitable to be used in light guide plates arranged on backs of various displays and in various optical elements. <P>SOLUTION: In the method for manufacturing the resin sheet, a sheet-shaped resin material 14 extruded from a die 12 and a backup sheet 20 supplied on one surface of the resin material 14 are pressed between a mold roller 16 and a nip roller 18 arranged opposite the mold roller 16 so that the resin material is arranged on the side of the mold roller 16 and the backup sheet is arranged on the side of the nip roller 18 in order to transfer the uneven shape of the surface of the mold roller 16 to the resin material. The laminate of the resin material after the transfer and the backup sheet is wound to a peeling roller 24 arranged opposite to the mold roller 16 to be peeled from the mold roller 16. A discharge opening of the die 12 is formed on the side of the mold roller 16 in relation to the common tangent of the mold roller 16 and the nip roller 18 to reduce defects. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a resin sheet manufacturing method and apparatus, and more particularly to a resin sheet manufacturing method and apparatus suitable for use in a light guide plate and various optical elements disposed on the back surface of various display devices.

  As resin sheets used for various optical elements, Fresnel lenses, lenticular lenses, and the like are used in various fields. A regular uneven shape is formed on the surface of such a resin sheet, and this uneven shape exhibits optical performance as a Fresnel lens or a lenticular lens.

  As a method for producing such a resin sheet, various proposals have been made so far (see Patent Documents 1 to 4). In these proposals, the roller molding method is adopted from the viewpoint of improving productivity.

  For example, Patent Document 1 attempts to improve transferability by devising the cooling means until the resin sheet is peeled from the roller. Patent Document 2 discloses a method of manufacturing a Fresnel lens by winding a die around a roller.

  In Patent Document 3, a heat buffer member is arranged inside the forming roller to improve productivity and transferability. Patent Document 4 uses a corona discharge treatment to improve transferability and reduce defects.

  A typical roller forming method of these prior arts is configured as shown in FIG. This apparatus configuration includes a sheet die 2 for shaping a resin material 1 melted by an extruder (not shown) into a sheet shape, a stamper roller 3 having an uneven surface formed thereon, and a stamper roller 3. And a mirror roller 4 for peeling, which is disposed opposite to the mirror roller 4 while facing the stamper roller 3.

Then, the sheet-like resin material 1 extruded from the die 2 is pressed between the stamper roller 3 and the mirror roller 4, and the uneven shape on the surface of the stamper roller 3 is transferred to the resin material 1, and the resin material 1 is peeled off by the mirror roller for peeling. 5 is peeled off from the stamper roller 3 by being wound around.
JP-A-8-31025 JP-A-7-314567 JP 2003-53834 A JP-A-8-287530

  However, any of the above conventional proposals relates to a method for producing a relatively thin resin sheet, and is not suitable for producing a relatively thick resin sheet. In particular, when a resin sheet having a large thickness distribution in the width direction during molding is produced, it is very difficult to obtain a desired cross-sectional shape.

  For example, when PMMA (polymethylmethacrylate resin) is extruded and then subjected to roller molding, when the thickness distribution is given in the width direction and the difference in thickness between the thickest part and the thinnest part is 1 mm or more, the surface or There are various problems such as unevenness on the back surface (shrinkage due to shrinkage when the resin is cured, distribution of elastic recovery amount), overall surface shape transfer rate is reduced, and sharp edge shape cannot be transferred.

  Further, in the conventional proposal, air is often mixed between the resin material 1 and the mirror roller 4 in the configuration shown in FIG. 8 described above. For this reason, bubbles are formed on the back surface of the molded resin sheet. There is a problem that defects in the shape are likely to occur.

  The present invention has been made in view of such circumstances, and when a resin sheet having a large thickness distribution in the width direction at the time of molding can be produced, a desired cross-sectional shape can be obtained without defects, in particular, various displays. It aims at providing the manufacturing method and apparatus of a resin sheet suitable for using for the light-guide plate and various optical elements which are distribute | arranged to the back surface of an apparatus.

  In order to achieve the above object, the present invention provides a sheet-like resin material extruded from a die and a backup sheet supplied to one side of the resin material on the mold roller side, and the backup sheet is a nip roller. The mold roller and the nip roller disposed opposite to the mold roller so as to be on the side, the uneven shape on the surface of the mold roller is transferred to the resin material, and the resin material after transfer and the backup A method for producing a resin sheet that is peeled off from a mold roller by winding a laminate with a sheet on a peeling roller disposed opposite to the mold roller, the discharge port of the die being connected to the mold roller and the nip roller. A method for producing a resin sheet is provided, which is provided on the mold roller side with respect to the common tangent line.

  To this end, the present invention provides a mold roller having a concavo-convex shape formed on the peripheral surface, a nip roller disposed opposite to one side of the mold roller, and a peeling roller disposed opposite to the other side of the mold roller. A die that pushes out a sheet-shaped resin material from a discharge port, the die having the discharge port disposed on the mold roller side with respect to a common tangent line of the mold roller and the nip roller, and a belt-like shape Backup sheet supply means for supplying a flexible backup sheet, wherein the mold roller and the mold roller are arranged such that the resin material extruded from the die is on the mold roller side and the backup sheet is on the nip roller side. The concavo-convex shape on the surface of the mold roller is transferred to the resin material, and a laminated body of the resin material and the backup sheet after the transfer is Providing an apparatus for manufacturing a resin sheet, characterized in that it is peeled off from the wound around in mold roller away rollers.

  According to the present invention, the discharge port of the die is provided on the mold roller side with respect to the common tangent line of the mold roller and the nip roller, and the sheet-like resin material is supplied between the mold roller and the nip roller. The laminate is pressed between the mold roller and the nip roller, the uneven shape is transferred to a resin material, and is peeled off from the mold roller by being wound around the peeling roller.

  As described above, by providing the die discharge port on the mold roller side, air is greatly reduced from being mixed between the resin material and the backup sheet, and the back surface defects of the molded resin sheet are greatly reduced. . In addition, by supporting the back surface of the resin material with a backup sheet, even if the resin sheet has a large thickness distribution in the width direction at the time of molding, the back surface unevenness that occurs immediately after molding is unlikely to occur, and it is early in the state immediately after molding. It is possible to obtain a desired cross-sectional shape by suppressing the deformation on the downstream side by cooling and fixing to the bottom.

  In order to achieve the above object, the present invention provides a sheet-shaped resin material extruded from a die and a backup sheet supplied to one side of the resin material, the resin material on the mold roller side, and the backup sheet. Is pressed between the mold roller and the nip roller disposed so as to face the mold roller, the uneven shape on the surface of the mold roller is transferred to the resin material, and the resin material after transfer A method for producing a resin sheet which is peeled off from a mold roller by winding a laminate with the backup sheet on a peeling roller disposed opposite to the mold roller, wherein the temperature of the backup sheet is changed to a glass transition of the resin material. Provided is a method for producing a resin sheet, which is heated to a temperature Tg or higher and then brought into contact with the resin material.

  For this purpose, the present invention includes a mold roller having a concavo-convex shape formed around it, a nip roller disposed opposite to one side of the mold roller, and a peeling roller disposed opposite to the other side of the mold roller. A roller array, a die for extruding a sheet-shaped resin material from a discharge port, a backup sheet supply means for supplying a belt-shaped flexible backup sheet, and a temperature of the backup sheet equal to or higher than the glass transition temperature Tg of the resin material Heating means for heating, and the resin material extruded from the die is sandwiched between the mold roller and the nip roller such that the backup sheet is on the nip roller side and the backup sheet is on the nip roller side. The uneven shape of the roller surface is transferred to the resin material, and a laminate of the resin material and the backup sheet after transfer is transferred to the peeling roller. That is peeled from the can hung by mold roller is provided an apparatus for manufacturing a resin sheet according to claim.

  According to the present invention, since the temperature of the backup sheet is heated to the glass transition temperature Tg or higher of the resin material and then brought into contact with the resin material, even if the resin sheet has a large thickness distribution in the width direction during molding, Unevenness on the back surface that occurs immediately after molding is unlikely to occur, and by cooling and fixing at an early stage in the state immediately after molding, deformation on the downstream side can be suppressed and a desired cross-sectional shape can be obtained.

  The glass transition temperature Tg is explained as follows. When a polymer substance is heated, a phenomenon that changes from a glassy hard state to a rubbery state is called a glass transition, and a temperature at which the glass transition occurs is called a glass transition point (temperature). This temperature varies depending on the material and composition of the resin material, and is, for example, in the range of 90 to 110 ° C. for polymethyl methacrylate resin.

  In the present invention, it is preferable to heat the backup sheet by controlling the temperature of the nip roller to be equal to or higher than the glass transition temperature Tg of the resin material. As described above, the temperature of the resin material is appropriately controlled by controlling the temperature of the nip roller to be equal to or higher than the glass transition temperature Tg of the resin material.

  In the present invention, it is preferable that the difference in thickness between the thickest portion and the thinnest portion in the width direction of the resin material is 1 mm or more due to the uneven shape transferred to the resin material. Moreover, in this invention, it is preferable that the thickness of the thinnest part of the said resin material is 5 mm or less. Thus, the effect of the present invention can be exhibited in the molding of a resin material having a cross-sectional shape that has been difficult to mold.

  In the present invention, it is preferable that the backup sheet is peeled off from the resin material after the laminated body of the resin material and the backup sheet after transfer is peeled off from the mold roller or on the mold roller. As described above, if the backup sheet is peeled off from the resin material after the transfer, it becomes easy to handle the resin material as a product.

  Moreover, in this invention, it is preferable to peel the said backup sheet from this resin material simultaneously with peeling the laminated body of the said resin material and the said backup sheet after transcription | transfer from the said peeling roll. Thus, even if the backup sheet is peeled off, it becomes easy to handle the resin material as a product.

  Moreover, in this invention, it is preferable to clean the said backup sheet after peeling from the said resin material. In this way, if the backup sheet after peeling is cleaned, it is convenient when the backup sheet is reused.

  In the present invention, it is preferable that the backup sheet is an endless annular band. As described above, when the backup sheet has an endless belt shape, the backup sheet can be easily conveyed and the length of the backup sheet can be shortened.

  In the present invention, it is preferable to provide sheet feeding means for continuously supplying the backup sheet and sheet winding means for storing the backup sheet. Thus, by providing the sheet feeding means and the sheet winding means, the backup sheet can be handled very easily.

  As described above, according to the present invention, a desired cross-sectional shape can be obtained without defects even in a resin sheet having a large thickness distribution in the width direction during molding.

  Hereinafter, a preferred embodiment (first embodiment) of a resin sheet manufacturing method and apparatus according to the present invention will be described in detail with reference to the accompanying drawings. FIG. 1 is a configuration diagram showing an example of a resin sheet production line to which a resin sheet production method according to the present invention is applied.

  The resin sheet production line 10 includes a sheet die 12 for shaping the resin material 14 melted by the extruder 11 into a sheet shape, a mold roller 16 having a concavo-convex shape formed on the surface, and a mold roller. A nip roller 18 disposed opposite the mold roller 16, a peeling roller 24 disposed opposed to the mold roller 16, a sheet feeding means 26 for continuously supplying the backup sheet 20, and a sheet winding means 28 for storing the backup sheet 20. , And the like, and a plurality of guide rollers 22, 22... Supporting the conveyance of the resin material 14 and the backup sheet 20.

  The slit size of the die 12 is formed so that the width of the molded molten resin material 14 is wider than the width of the mold of the mold roller 16, and the molten resin material 14 extruded from the die 12 is formed with the mold roller 16. It arrange | positions so that it may extrude between the nip rollers 18. FIG. What is particularly important is that the discharge port of the die 12 (center line is indicated by the symbol C) is provided on the mold roller 16 side with respect to the common tangent S of the mold roller 16 and the nip roller 18. By setting it as such arrangement | positioning, mixing of air between the resin material 14 and the backup sheet 20 will reduce significantly, and the back surface defect of the resin sheet after shaping | molding will reduce significantly.

  A regular uneven shape is formed on the surface of the mold roller 16. This regular uneven | corrugated shape can be made into the inversion shape of the resin material 14 after a shaping | molding shown by FIG. 2, for example. FIG. 2 is a perspective view of a state in which the end surface 14A of the resin material 14 after molding is cut out linearly.

  That is, the back surface of the resin material 14 is a flat surface, and a linear uneven pattern parallel to the arrow is formed on the surface of the resin material 14. This arrow indicates the traveling direction of the resin material 14. Therefore, an endless groove having an inverted shape of the end face 14 </ b> A may be formed on the surface of the mold roller 16. The details of the uneven pattern shape on the surface of the resin material 14 will be described later.

  The material of the mold roller 16 includes various steel members, stainless steel, copper, zinc, brass, and a metal lining of these metal materials, and a rubber lining on the surface. These metal materials are HCr plated, Cu plated, Ni plated. For example, ceramics and various composite materials can be used.

  The method for forming the concavo-convex pattern on the surface of the mold roller 16 depends on the concavo-convex pattern (pitch, depth, etc.) and the material of the surface of the mold roller 16, but generally a combination of cutting with an NC lathe and finishing buffing. Can be preferably employed. In addition, other known processing methods (grinding processing, ultrasonic processing, electric discharge processing, etc.) can also be employed.

  The surface roughness of the surface of the mold roller 16 is preferably 0.5 μm or less in Ra, and more preferably 0.2 μm or less.

  The mold roller 16 is driven to rotate in a direction indicated by an arrow in FIG. 1 at a predetermined peripheral speed by a driving means (not shown). The mold roller 16 is provided with temperature adjusting means. By providing such a temperature adjusting means, it is possible to control to suppress the temperature rise or sudden temperature drop of the mold roller 16 due to the resin material 14 in a high temperature state.

  As such temperature adjusting means, a configuration in which oil whose temperature is adjusted is circulated inside the roller can be preferably employed. This supply and discharge of oil can be realized by a configuration in which a rotary joint is provided at the end of the roller. In the resin sheet production line 10 of FIG. 1, this temperature adjusting means is employed.

  The nip roller 18 is disposed opposite to the mold roller 16 and presses the resin material 14 and the backup sheet 20 laminated on the back surface with the mold roller 16. The nip roller 18 is flush with the mold roller 16 on the upstream side in the running direction. Is arranged.

  The surface of the nip roller 18 is preferably processed into a mirror surface. By setting it as such a surface, the back surface of the resin material 14 after shaping | molding can be made into a favorable state. The surface roughness of the surface of the nip roller 18 is preferably 0.5 μm or less in Ra, and more preferably 0.2 μm or less.

  The material of the nip roller 18 includes various steel members, stainless steel, copper, zinc, brass, and a metal lining of these metal materials, and a rubber lining on the surface. These metal materials are HCr plated, Cu plated, Ni plated, etc. These materials, ceramics, and various composite materials can be used.

  The nip roller 18 is rotationally driven in a direction indicated by an arrow in FIG. 1 at a predetermined peripheral speed by a driving means (not shown). In addition, although the structure which does not provide a drive means in the nip roller 18 is also possible, it is preferable to provide a drive means from the point which can make the back surface of the resin material 14 a favorable state.

  The nip roller 18 is provided with a pressing means (not shown) so that the resin material 14 between the nip roller 18 and the mold roller 16 can be pressed with a predetermined pressure. The pressurizing means is configured to apply pressure in the normal direction at the contact point between the nip roller 18 and the mold roller 16, and various known means such as a motor driving means, an air cylinder, and a hydraulic cylinder can be employed.

  The nip roller 18 may be configured to be less likely to bend due to the reaction force of the clamping pressure. As such a configuration, a configuration in which a backup roller is provided on the back side of the nip roller 18 (opposite side of the mold roller 16), a configuration in which a crown shape (middle and high shape) is adopted, and a rigidity in the central portion in the axial direction of the roller is large. A configuration of a roller having such an intensity distribution, a configuration combining these, and the like can be employed.

  The nip roller 18 is provided with temperature adjusting means. The roller set temperature of the nip roller 18 includes the material of the resin material 14, the temperature when the resin material 14 is melted (for example, the slit exit of the die 12), the transport speed of the resin material 14, the outer diameter of the mold roller 16, The optimum value should be selected according to the uneven pattern shape.

  As the roller temperature adjusting means of the nip roller 18, a configuration in which oil whose temperature is adjusted is circulated inside the roller can be preferably employed. This supply and discharge of oil can be realized by a configuration in which a rotary joint is provided at the end of the roller. In the resin sheet production line 10 of FIG. 1, this temperature adjusting means is employed.

  As other temperature adjusting means, for example, various known means such as a structure in which a sheath heater is embedded in the roller and a structure in which a dielectric heating means is disposed in the vicinity of the roller can be adopted.

  The temperature adjusting means of the nip roller 18 can also function as a heating means for heating the temperature of the backup sheet 20 to the glass transition temperature Tg or more of the resin material 14.

  As the backup sheet 20, a resin film, metal foil (aluminum web, iron, stainless steel, copper, brass, zinc, etc.), etc. can be used. Resin film materials include polyethylene, polypropylene, polyvinyl chloride, polyvinylidene chloride, polyvinyl acetate, polystyrene, polycarbonate, polyamide, PET (polyethylene terephthalate), biaxially stretched polyethylene terephthalate, polyethylene naphthalate, and polyamideimide. Known materials such as polyimide, aromatic polyamide, cellulose triacetate, cellulose acetate propionate, and cellulose diacetate can be used. Of these, polyethylene terephthalate, polyethylene naphthalate, and polyamide can be preferably used.

Glass transition temperature _{Tg 20} of the backup sheet 20 is preferably above the glass transition temperature _{Tg 14} of the resin material 14 is larger. Thus, if the thermal deformation of the backup sheet 20 is smaller than that of the resin material 14, the deformation of the backup sheet 20 can be prevented.

Moreover, it is preferable that the longitudinal elastic modulus of the backup sheet 20 is 1 × 10 ⁹ N / mm ² or more in the use environment. Thus, if the longitudinal elastic modulus (so-called Young's modulus) of the backup sheet 20 is within an appropriate range, excessive deformation of the resin material 14 can be prevented by the rigidity of the backup sheet 20.

  Moreover, it is preferable that the thickness of the backup sheet 20 is 0.5-100 micrometers. With the backup sheet 20 having such a thickness, moderate flexibility and moderate rigidity can be obtained.

  The width of the backup sheet 20 is preferably substantially the same size as the width of the resin material 14, and the length of the backup sheet 20 is generally 1000 to 100,000 m. However, application of other sizes is not impeded.

  These backup sheets 20 may be previously subjected to corona discharge, plasma treatment, easy adhesion treatment, heat treatment, dust removal treatment and the like. The surface roughness Ra of the backup sheet 20 is preferably 3 to 10 nm at a cutoff value of 0.25 mm.

  In addition, an uneven shape, for example, an embossed shape, a brushing shape, a blasting shape, a peening shape, a prism shape, or the like, can be applied to substantially the entire surface of the backup sheet 20 that contacts the resin material 14. In this way, the reverse surface of the resin material 14 can also have this inverted shape.

  The sheet feeding means 26 continuously supplies the backup sheet 20. The sheet roll 26 </ b> A is wound around the both ends of the support arm 26 </ b> D and the sheet roll 26 </ b> A is being fed and a new (preliminary) original roll. An anti-roll 26B is provided, and by rotating the support arm 26D with the fulcrum 26C as the rotation center, the backup sheet 20 is continuously run while the roll 26A is being fed out and a new (preliminary) original roll. The anti-roll 26B can be exchanged.

  The backup sheet 20 fed from the sheet feeding means 26 is supplied to the back surface of the resin material 14 through the guide roller 22 and is fed between the mold roller 16 and the nip roller 18.

  Below the mold roller 16, there are three auxiliary rollers 19 from the nip roller 18 to the peeling roller 24 (first auxiliary roller 19A, second auxiliary roller 19B, and third auxiliary roller 19C in order from the upstream). Is arranged. The auxiliary roller 19 is provided for the purpose of assisting the pressing of the nip roller 18 and cooling the resin material 14.

  Therefore, the auxiliary roller 19 is provided with temperature adjusting means. The roller setting temperature of the auxiliary roller 19 includes the material of the resin material 14, the temperature when the resin material 14 is melted (for example, the slit exit of the die 12), the conveyance speed of the resin material 14, the outer diameter of the mold roller 16, and the mold roller 16. The optimum value should be selected according to the shape of the concavo-convex pattern.

  The peeling roller 24 is disposed opposite to the mold roller 16, and is a roller for peeling the resin material 14 from the mold roller 16 by winding the laminated body of the resin material 14 and the backup sheet 20. 18 is arranged 180 degrees downstream. In addition, the arrangement | positioning of the peeling roller 24 can also be other aspects.

  The surface of the peeling roller 24 is preferably processed into a mirror surface. By setting it as such a surface, the back surface of the resin material 14 after shaping | molding can be made into a favorable state. The surface roughness of the surface of the peeling roller 24 is preferably 0.5 μm or less in terms of Ra, and more preferably 0.2 μm or less.

  As the material of the peeling roller 24, various steel members, stainless steel, copper, zinc, brass, these metal materials having a metal core and a rubber lining on the surface, these metal materials are HCr plated, Cu plated, Ni plated For example, ceramics and various composite materials can be used.

  The peeling roller 24 is driven to rotate in the direction of the arrow in FIG. 1 by a driving means (not shown) at a predetermined peripheral speed. In addition, although the structure which does not provide a drive means in the peeling roller 24 is also possible, it is preferable to provide a drive means from the point which can make the back surface of the resin material 14 a favorable state.

  The peeling roller 24 is provided with temperature adjusting means. And the uneven | corrugated pattern shape of the surface of the resin material 14 can be made favorable by setting it as appropriate setting temperature.

  It is preferable to provide surface temperature measuring means (not shown) so that the surface temperatures of the respective rollers and the resin material 14 described above can be monitored. As such surface temperature measuring means, various known measuring means such as an infrared thermometer and a radiation thermometer can be employed.

  Examples of measurement points by such surface temperature measuring means include a plurality of points in the width direction of the resin material 14 between the die 12 and the mold roller 16 and a plurality of points in the width direction of the resin material 14 immediately after the peeling roller 24. The surface of a plurality of points in the width direction of the resin material 14 wound around the mold roller 16 and the peeling roller 24 (on the opposite surface side of the roller) can be considered.

  In addition, the monitoring result of the surface temperature measuring means can be fed back to the temperature adjusting means of each roller, the die 12, etc. and reflected in the temperature control of each roller. It is also possible to operate by feedforward control without providing the surface temperature measuring means.

  A tension detecting means for detecting the tension of the resin material 14 or a plate thickness detecting means (thickness sensor) for detecting the thickness of the resin material 14 is provided on the resin sheet production line 10 in FIG. It can also be preferably adopted. Moreover, the detection result by such a detection means can be compared with a set value and fed back to a draw control (second embodiment) described later.

  The slow cooling zone 30 (or annealing zone) is provided to prevent a rapid temperature change of the resin material 14 downstream of the peeling roller 24. When a sudden temperature change occurs in the resin material 14, for example, the inside of the resin material 14 is in a plastic state while the vicinity of the surface of the resin material 14 is in an elastic state. The surface shape of the material 14 deteriorates. In addition, there is a problem that a temperature difference occurs between the front and back surfaces of the resin material 14 and the resin material 14 is warped.

  As the slow cooling zone 30, it is possible to adopt a configuration in which a horizontal tunnel shape is provided, temperature adjusting means is provided inside the tunnel, and the cooling temperature profile of the resin material 14 can be controlled. As the temperature adjusting means, a structure in which air (hot air or cold air) whose temperature is controlled from a plurality of nozzles is ejected toward the resin material 14, and heating means (nichrome wire heater, infrared heater, dielectric heating means, etc.) Various known means such as a structure for heating the front and back surfaces of the material 14 can be employed.

  A peeling portion 32 is formed downstream of the slow cooling zone 30 (or annealing zone). In the peeling portion 32, the resin material 14 is supported by the guide rollers 22, 22,..., And is linearly conveyed to the right, and the backup sheet 20 is supported by the guide rollers 22, 22,. The

  Thus, if the backup sheet 20 is peeled from the resin material 14 at the peeling portion 32, the resin material 14 as a product can be easily handled.

  A cleaning device (cleaning zone), a defect inspection device (inspection zone), a laminating device, a side cutter, a cross cutter, and an accumulating portion are sequentially provided downstream of the peeling portion 32 with respect to the resin material 14 (all illustrated). (Omitted).

  Among these, the laminating apparatus is an apparatus that attaches a protective film (a film such as polyethylene) to the front and back surfaces of the resin material 14, and the side cutter is an apparatus that cuts off both end portions (discarded portions) of the resin material 14 in the width direction. The cross cutter is a device that cuts the resin material 14 to a predetermined length.

  Some of the above devices may be omitted depending on the application.

  A dancer roller 34, a cleaning unit (not shown), a driving roller 36, and a sheet winding unit 28 are sequentially provided on the downstream side of the peeling unit 32 with respect to the backup sheet 20.

  Among them, the dancer roller 34 is for adjusting the tension of the backup sheet 20, and includes a rotation fulcrum 34A, a rotation arm 34B whose one end is supported by the rotation fulcrum 34A, and a rotation arm 34B. And a roller 34C supported by the other end of the roller. And the tension | tensile_strength of the backup sheet 20 can be adjusted now that the rotation arm 34B is urged | biased by the arrow direction of a figure.

  The cleaning means is for removing contamination (contamination) such as dust adhering to the surface of the backup sheet 20, and is a type of pressing a cleaning tape or a cleaning roller against the backup sheet 20, or a clean air (nitrogen) that has been neutralized. Various known means such as a type of spraying gas or the like on the backup sheet 20 can be employed.

  The drive roller 36 is a mechanism for sandwiching (niping) the backup sheet 20 between the rollers 36A and 36B and transporting the backup sheet 20, and at least one of the roller 36A and the roller 36B is rotationally driven. ing.

  The sheet winding means 28 stores the backup sheet 20, and a winding core 28A in which the backup sheet 20 is wound and stored at both ends of the support arm 28D, and a new (reserved) winding core 28B. By replacing the support core 28D with the pivot point 28C as the center of rotation, the backup core 20A is continuously run and the stored core 28A is replaced with a new (preliminary) core 28B. It can be done.

  Next, a method for producing a resin sheet by the resin sheet production line 10 shown in FIG. 1 will be described.

  As the resin material 14 applied to the present invention, a thermoplastic resin can be used. For example, polymethyl methacrylate resin (PMMA), polycarbonate resin, polystyrene resin, MS resin, AS resin, polypropylene resin, polyethylene resin, polyethylene Examples include terephthalate resins, polyvinyl chloride resins (PVC), thermoplastic elastomers, copolymers thereof, and cycloolefin polymers.

  A laminated body of the sheet-like resin material 14 extruded from the die 12 and the backup sheet 20 fed from the sheet feeding means 26 and supplied to the back surface of the resin material 14 is disposed opposite to the mold roller 16 and the mold roller 16. The nip roller 18 is pressed to transfer the concavo-convex shape on the surface of the mold roller 16 to the resin material 14, and the laminate of the resin material 14 and the backup sheet 20 is wound around the peeling roller 24 disposed to face the mold roller 16. To peel from the mold roller 16.

  At this time, since the discharge port of the die 12 (center line is indicated by C) is provided on the mold roller 16 side with respect to the common tangent S of the mold roller 16 and the nip roller 18, the resin material 14 and the backup sheet 20 is greatly reduced, and the rear surface defects of the resin sheet after molding are greatly reduced.

  The resin material 14 (laminated body with the backup sheet 20) peeled off from the mold roller 16 is transported in the horizontal direction and slowly cooled by passing through the slow cooling zone 30, and the peeling portion 32 is removed in a state where the distortion is removed. , The backup sheet 20 is separated, cut into a predetermined length at a downstream product collecting portion, and accommodated as a resin sheet product.

  On the other hand, the backup sheet 20 separated from the resin material 14 at the peeling portion 32 is removed of contamination by the cleaning means, and is wound around the winding core 28A by the sheet winding means 28 and stored. The backup sheet 20 wound around the winding core 28A can be used again.

  In the production of the resin sheet 14, the extrusion speed of the resin material 14 from the die 12 can be 0.1 to 50 m / min, preferably 0.3 to 30 m / min. Therefore, the peripheral speed of the mold roller 16, the peripheral speed of the nip roller 18, and the conveyance speed of the backup sheet 20 are also substantially matched to this.

  It should be noted that the speed unevenness of each roller is preferably controlled to be within 1% of the set value.

  The pressing pressure of the nip roller 18 against the mold roller 16 is 0 to 200 kN / m (0 to 200 kgf / cm) in terms of linear pressure (value converted assuming that the surface contact due to elastic deformation of each nip roller is linear contact). It is preferable to set it to 0 to 100 kN / m (0 to 100 kgf / cm).

  The temperature control of the nip roller 18 and the peeling roller 24 is preferably performed for each individual roller. And it is preferable that the resin material 14 in the location of the peeling roller 24 is the temperature below the softening point Ta of resin. At this time, when a polymethylmethacrylate resin is used as the resin material 14, the set temperature of the peeling roller 24 can be 50 to 110 ° C.

  Next, details of the uneven pattern shape on the surface of the resin material 14 will be described. As described above, FIG. 2 is a perspective view of a state in which the end surface 14A of the resin material 14 after molding is cut out linearly. The back surface of the resin material 14 is a flat surface.

  The uneven pattern shape on the surface of the resin material 14 is a linear uneven pattern in the longitudinal direction (the arrow direction in the figure). In this pattern, the V-groove 50 formed in the thickest part 14B of the resin material 14 and the plate thickness decreases linearly from both edges of the V-groove 50 toward the thinnest part 14C of the resin material 14. The taper portions 52 and 52 are repeatedly shaped. That is, it is a continuous shape in which the V groove 50 and the taper portions 52 and 52 on both sides, which are line targets with respect to the center line of the V groove 50, are one unit (one pitch).

  In FIG. 2, the thickness of the thinnest portion 14C of the resin material 14 is preferably 5 mm or less, and more preferably 2 mm or less. The difference in thickness between the thickest part 14B and the thinnest part 14C of the resin material 14 is preferably 1 mm or more, and more preferably 2.5 mm or more. By setting it as such a dimension, it can be used conveniently for the light-guide plate and various optical elements which are distribute | arranged to the back surface of various display apparatuses.

  When the molded resin material 14 is used for the light guide plate, a cylindrical cold cathode tube is arranged inside the V groove 50, and light irradiated from the cold cathode tube is resin from the surface of the V groove 50. The light enters the inside of the material 14, is reflected by the tapered portions 52 and 52, and is irradiated in a planar shape from the back surface of the resin material 14.

  Thus, when the resin material 14 after molding is used for the light guide plate, the width P of the V groove 50 is preferably 2 mm or more, and the apex angle θ1 of the V groove 50 is 40 to 80 degrees. preferable. The depth Δt of the V groove 50 is preferably 1 mm or more, and more preferably 2.5 mm or more. The inclination angle θ2 of the tapered portions 52, 52 is preferably 3 to 20 degrees. Further, the width P2 of the tapered portions 52, 52 is preferably 5 mm or more, and more preferably 10 mm or more.

  Next, another uneven pattern shape on the surface of the resin material 14 will be described. FIG. 3 is a perspective view of a state in which the end surface 14A of the resin material 14 after molding is cut out linearly. The back surface of the resin material 14 is a flat surface.

  The uneven pattern shape on the surface of the resin material 14 is a linear uneven pattern in the longitudinal direction (the arrow direction in the figure). The cross-sectionally saw-tooth pattern has a vertical wall 54 that connects the thickest portion 14B and the thinnest portion 14C of the resin material 14 and the upper edge (thickest portion 14B) of the vertical wall 54. The taper portion 56 whose thickness decreases linearly toward the thinnest portion 14C is repeated.

  In FIG. 3, the thickness of the thinnest portion 14C of the resin material 14 is preferably 5 mm or less, and more preferably 2 mm or more. The difference in thickness between the thickest part 14B and the thinnest part 14C of the resin material 14 is preferably 1 mm or more, and more preferably 2.5 mm or more. By setting it as such a dimension, it can be used conveniently for the light-guide plate and various optical elements which are distribute | arranged to the back surface of various display apparatuses.

  When the molded resin material 14 is used for the light guide plate, a cylindrical cold cathode tube is disposed on the side surface of the vertical wall 54, and the light beam irradiated from the cold cathode tube is irradiated on the surface (side surface) of the vertical wall 54. ) Is incident on the inside of the resin material 14, is reflected by the taper portion 56, and is irradiated in a planar shape from the back surface of the resin material 14.

  Thus, when using the resin material 14 after shaping | molding for a light-guide plate, it is preferable that the taper part 56 inclination-angle (theta) 3 shall be 3-20 degree | times.

  In addition, when using the resin material 14 after shaping | molding for a light-guide plate, shapes other than these can also be employ | adopted. For example, the cross-sectional shape of the V-groove 50 of the resin material 14 in FIG. 2 is V-shaped, but other shapes such as a rectangular shape, a trapezoidal shape, an arc shape, a parabolic shape, etc. are also possible. It can be used if it satisfies the required characteristics and formability.

  Further, the uneven shape on the surface of the mold roller 16 does not need to be the inverted shape of the surface of the resin material 14 in FIG. 2 or 3, and the product shape of the resin material 14 is illustrated in consideration of the shrinkage allowance of the resin material 14. It can also be set as the shape offset from this shape so that it may become the shape of 2 or FIG.

  Next, another embodiment (second embodiment) of the method and apparatus for producing a resin sheet according to the present invention will be described in detail. FIG. 4 is a configuration diagram showing a resin sheet production line 10 ′ to which the resin sheet production method according to the present invention is applied. In addition, the same code | symbol is attached | subjected about the member similar to 1st Embodiment shown by FIG. 1, and the description is abbreviate | omitted.

  In the present embodiment, three rollers of a plurality of nip rollers 18 (nip roller 18A, nip roller 18B, and nip roller 18C) are used instead of one roller of the nip roller 18 of the first embodiment.

  In the resin sheet production line 10 ', the nip roller 18A is arranged at the 9 o'clock position in the clockwise direction, the nip roller 18B is arranged at the 7 o'clock position in the clockwise direction, and the nip roller 18C is arranged at the 5 o'clock position in the clockwise direction. Each performs substantially the same function as the nip roller 18 of the first embodiment.

  However, since there are three rollers, it is possible to increase the pinching distance and easily obtain a desired cross-sectional shape. In addition, by driving the nip roller 18A, the nip roller 18B, and the nip roller 18C individually, a so-called draw control operation method is possible.

  When the driving means is provided in the nip roller 18 (18A, 18B, and 18C), a configuration in which each driving speed is variable can be preferably employed. Accordingly, for example, an operation method in which the nip rollers 18A, 18B, and 18C are gradually increased from the peripheral speed of the die roller 16 in the order of the nip rollers 18A, 18B, and 18C (within a range of at most several%) can be employed.

  Each of the nip rollers 18A, 18B, and 18C is provided with a pressing means (not shown) so that the resin material 14 between the nip rollers 18A, 18B, and 18C can be clamped with a predetermined pressure. Each of the pressurizing means is configured to apply pressure in the normal direction at the contact point between the nip rollers 18A, 18B, and 18C and the mold roller 16, and is well-known such as a motor driving means, an air cylinder, a hydraulic cylinder, or the like. Various means can be adopted.

  Further, in the resin sheet production line 10 ′ of FIG. 4, cooling devices 38 and 40 are provided to assist the temperature adjusting means of the nip rollers 18 </ b> A, 18 </ b> B, and 18 </ b> C.

  Each of the cooling devices 38 and 40 is an air nozzle, and the air nozzle of the cooling device 38 is such that air is blown to the laminated body of the resin material 14 and the backup sheet 20 being conveyed from the gap between the nip roller 18B and the nip roller 18C. The air nozzle of the cooling device 40 is arranged so that air is blown to the nip roller 18C. In this way, the temperature of the resin material 14 (laminated body) can be directly controlled, and the temperature of the resin material 14 (laminated body) can be controlled via the nip roller 18C.

  The air temperature and air supply amount (spraying flow rate) of the cooling devices 38 and 40 are the material of the resin material 14, the temperature when the resin material 14 is melted (for example, the slit exit of the die 12), the transport speed of the resin material 14, the mold The optimum value should be selected according to the outer diameter of the roller 16, the uneven pattern shape of the mold roller 16, the set temperature of the nip rollers (nip roller 18A, nip roller 18B, and nip roller 18C), and the like.

  On the other hand, the driving of the nip rollers (nip roller 18A, nip roller 18B, and nip roller 18C) is a so-called draw control operation method in which the nip rollers 18A, 18B, and 18C are gradually increased from the peripheral speed of the mold roller 16 in this order. The draw value between the nip rollers 18A, 18B, and 18C is preferably 0 to 3%, and more preferably 0 to 1%.

  Next, a method for producing a resin sheet using the resin sheet production line 10 'shown in FIG. 4 will be described.

  A laminated body of the sheet-like resin material 14 extruded from the die 12 and the backup sheet 20 fed from the sheet feeding means 26 and supplied to the back surface of the resin material 14 is disposed opposite to the mold roller 16 and the mold roller 16. The nip rollers 18 </ b> A, 18 </ b> B, and 18 </ b> C are sequentially pressed to transfer the uneven shape on the surface of the mold roller 16 to the resin material 14, and the peeling roller in which the laminate of the resin material 14 and the backup sheet 20 is disposed to face the mold roller 16. It is peeled off from the mold roller 16 by being wound around 24.

  In the production of this resin sheet, the extrusion speed of the resin material 14 from the die 12 can be 0.1 to 50 m / min, preferably 0.3 to 30 m / min. Accordingly, the peripheral speed of the mold roller 16 is also substantially matched with this.

  On the other hand, the driving of the nip rollers (nip roller 18A, nip roller 18B, and nip roller 18C) is a so-called draw control operation method in which the nip rollers 18A, 18B, and 18C are gradually increased from the peripheral speed of the mold roller 16 in this order. The draw value between the nip rollers 18A, 18B, and 18C is preferably 0 to 3%, and more preferably 0 to 1%.

  It should be noted that the speed unevenness of each roller is preferably controlled to be within 1% of the set value.

  The pressing pressure of each nip roller (nip roller 18A, nip roller 18B, and nip roller 18C) against the mold roller 16 is 0 to 0 in terms of linear pressure (value converted assuming that the surface contact due to elastic deformation of each nip roller is a line contact). 200 kN / m (0 to 200 kgf / cm) is preferable, and 0 to 100 kN / m (0 to 100 kgf / cm) is more preferable.

  The temperature control of the nip rollers 18A, 18B, 18C and the peeling roller 24 is preferably performed for each individual roller. And it is preferable that the resin material 14 in the location of the peeling roller 24 is the temperature below the softening point Ta of resin. At this time, when a polymethylmethacrylate resin is used as the resin material 14, the set temperature of the peeling roller 24 can be 50 to 110 ° C.

  The resin material 14 peeled off from the mold roller 16 is transported in the horizontal direction, gradually cooled by passing through the slow cooling zone 30, and cut into a predetermined length in the downstream product removing portion in a state where distortion is removed. And accommodate as a resin sheet product.

  Next, still another embodiment (third embodiment) of the resin sheet manufacturing method and apparatus according to the present invention will be described in detail. FIG. 5 is a configuration diagram showing a resin sheet production line 10 ″ to which the resin sheet production method according to the present invention is applied. In addition, the same code | symbol is attached | subjected about the same and similar member as 1st Embodiment shown in FIG. 1, and 2nd Embodiment shown in FIG. 4, and the description is abbreviate | omitted.

  In the present embodiment, instead of the sheet feeding means 26 and the sheet winding means 28 of the first and second embodiments, a sheet circulation means 26 'is provided. The sheet circulation means 26 'is a means for circulating the backup sheet 20 as an endless belt.

  The sheet circulation means 26 ′ is composed of a sheet driving means 27 and a guide roller 22. The sheet driving means 27 is a mechanism for sandwiching (niping) the backup sheet 20 between the rollers 27A and 27B and transporting the backup sheet 20, so that at least one of the rollers 27A and 27B is rotationally driven. It has become.

  In this sheet circulating means 26 ', the backup sheet 20 is an endless belt, so that the backup sheet 20 can be easily conveyed and the length of the backup sheet 20 can be shortened. Further, the configuration of the sheet circulating means 26 'is simpler than the combined configuration of the sheet feeding means 26, the sheet winding means 28, and the like.

  Also with such a resin sheet production line 10 ″, a good product can be produced depending on the line conditions and the material of the resin material 14.

  According to the manufacturing method and apparatus (first to third embodiments) of the resin sheet according to the present invention described above, even if the resin sheet has a large thickness distribution in the width direction at the time of molding, it is desired without any defects. A cross-sectional shape can be obtained.

  As mentioned above, although embodiment of the manufacturing method and apparatus of the resin sheet which concern on this invention was described, this invention is not limited to the said embodiment, Various aspects can be taken.

  For example, the number and arrangement of the nip rollers may take various aspects other than the present embodiment as long as the same function can be obtained.

  Further, the temperature adjusting means, the cooling device (38 and the like), the slow cooling zone 30 and the like can adopt various aspects other than the present embodiment as long as the same function can be obtained.

  In addition, as a heating means for heating the temperature of the backup sheet 20 to the glass transition temperature Tg or more of the resin material 14, a temperature adjusting means for the nip roller 18 is cited, but other heating means (for example, hot air jetting means) is separately provided. It may be provided in the vicinity of the nip roller 18.

  Examples of the present invention and comparative examples will be described below.

[Example A]
The resin sheet of the Example and the comparative example was manufactured using the manufacturing line 10 of the resin sheet shown by FIG. The cross-sectional shape of the resin sheet was the shape shown in FIG. The repeating unit P was 28 mm, W was 4.2 mm, D was 3.5 mm, t1 was 1 mm, and t2 was 1.64 mm. Further, both ends of the repeating unit P are arcs in contact with the slope, and the radius of curvature R is 15 mm.

  The position of the discharge port of the die 12 in the horizontal direction was changed as follows, and resin sheets of Examples and Comparative Examples were manufactured. The distance in the vertical direction between the nip portion (the portion where the clearance is minimized) between the mold roller 16 and the nip roller 18 and the discharge port of the die 12 was 156 mm.

  Example 1: Discharge port of the die 12 (center line is indicated by C) is provided on the 16 mm type roller 16 side with respect to the common tangent S of the type roller 16 and the nip roller 18.

  Example 2: A discharge port of the die 12 (a center line is indicated by a symbol C) is provided on the 6 mm type roller 16 side with respect to a common tangent S of the mold roller 16 and the nip roller 18.

  Comparative Example 1: A discharge port of the die 12 (a center line is indicated by a symbol C) is provided on the 14 mm nip roller 18 side with respect to a common tangent line S between the mold roller 16 and the nip roller 18.

  Comparative Example 2: Discharge port of the die 12 (center line is indicated by the symbol C) is provided on the side of the 64 mm nip roller 18 with respect to the common tangent S of the mold roller 16 and the nip roller 18.

  Manufacturing conditions common to the examples and the comparative examples were as follows.

Peripheral speed of mold roller 16: 1.3 m / min Composition of resin material 14: PMMA (Mitsubishi Rayon, model number: VH001)
Temperature of the resin material 14 at the discharge port of the die 12: 255 ° C
Evaluation of the resin sheet after molding was performed by visually observing the number of bubble-like defects generated on the back surface of the resin sheet having a width of 500 mm and a length of 900 mm, and the degree of occurrence was 3 in the order of small number: ○, Δ, × Evaluation was performed in stages.

以上の比較結果により本発明の効果が確認できた。 The evaluation results of the molded resin sheet are as shown in Table 1 below.

From the above comparison results, the effect of the present invention was confirmed.

[Example B]
The resin sheet of the Example and the comparative example was manufactured using the manufacturing line 10 of the resin sheet shown by FIG. The cross-sectional shape of the resin sheet was the shape shown in FIG. The repeating unit P was 28 mm, W was 4.2 mm, D was 3.5 mm, t1 was 1 mm, and t2 was 1.64 mm. Further, both ends of the repeating unit P are arcs in contact with the slope, and the radius of curvature R is 15 mm.

  Manufacturing conditions common to the examples and the comparative examples were as follows.

Peripheral speed of mold roller 16: 1.3 m / min Composition of resin material 14: PMMA (Mitsubishi Rayon, model number: VH001)
Temperature of the resin material 14 at the discharge port of the die 12: 260 ° C
Material of backup sheet 20: SUS304
Evaluation of the resin sheet after molding was performed by visually observing the number of bubble-like defects generated on the back surface of the resin sheet having a width of 500 mm and a length of 900 mm, and the degree of occurrence was 3 in the order of small number: ○, Δ, × Evaluation was performed in stages.

In Examples 1 and 2 and Comparative Examples 1 and 2,
Each set temperature of the mold roller 16 (stamper roller), the nip roller 18, the peeling roller 24, and the cooling roller 19B was set as shown in the table of FIG.

  In Examples 1 and 2, the temperature of the backup sheet 20 is heated to the glass transition temperature Tg or higher of the resin material 14 and then brought into contact with the resin material 14. In Comparative Examples 1 and 2, the backup sheet 20 The temperature of was heated below the glass transition temperature Tg of the resin material 14 and then brought into contact with the resin material 14.

  FIG. 7 is a table showing processing conditions and evaluation results in Example B. From the above comparison results, the effect of the present invention was confirmed.

The block diagram which shows the example of the production line of the resin sheet to which this invention is applied The perspective view of the state which cut off the end face of the resin material after molding in a straight line The perspective view of the state which cut off the end face of the resin material after molding in a straight line The block diagram which shows the other example of the production line of the resin sheet to which this invention is applied The block diagram which shows the further another example of the production line of the resin sheet to which this invention is applied Sectional drawing of the resin sheet in Example A Table showing processing conditions and evaluation results in Example B Configuration diagram showing production line of resin sheet of conventional example

Explanation of symbols

  DESCRIPTION OF SYMBOLS 10, 10 ', 10' '... Resin sheet production line, 12 ... Die, 14 ... Resin material, 16 ... Mold roller, 18 ... Nip roller, 18A, 18B, 18C ... Nip roller, 20 ... Backup sheet, 22 ... Guide roller , 24 ... peeling roller, 26 ... sheet feeding means, 28 ... sheet winding means, 30 ... slow cooling zone, 38 ... cooling device

Claims (12)

A sheet-shaped resin material extruded from a die and a backup sheet supplied to one side of the resin material are arranged such that the resin material is on the mold roller side and the backup sheet is on the nip roller side. Clamping with the nip roller disposed opposite the mold roller,
The uneven shape on the surface of the mold roller is transferred to the resin material,
A method for producing a resin sheet that is peeled off from a mold roller by winding a laminate of the resin material after transfer and the backup sheet on a peeling roller disposed to face the mold roller,
A method for producing a resin sheet, characterized in that a discharge port of the die is provided on the mold roller side with respect to a common tangent line of the mold roller and the nip roller. A sheet-shaped resin material extruded from a die and a backup sheet supplied to one side of the resin material are arranged such that the resin material is on the mold roller side and the backup sheet is on the nip roller side. Clamping with the nip roller disposed opposite the mold roller,
The uneven shape on the surface of the mold roller is transferred to the resin material,
A method for producing a resin sheet that is peeled off from a mold roller by winding a laminate of the resin material after transfer and the backup sheet on a peeling roller disposed to face the mold roller,
A method for producing a resin sheet, comprising: heating a temperature of the backup sheet to a glass transition temperature Tg or higher of the resin material and then bringing the backup material into contact with the resin material.   The method for producing a resin sheet according to claim 1, wherein the backup sheet is heated by controlling the temperature of the nip roller to be equal to or higher than the glass transition temperature Tg of the resin material.   4. The thickness difference between the thickest part and the thinnest part in the width direction of the resin material is 1 mm or more due to the uneven shape transferred to the resin material. 2. A method for producing a resin sheet according to item 1.   The thickness of the thinnest part of the said resin material is 5 mm or less, The manufacturing method of the resin sheet of any one of Claims 1-4 characterized by the above-mentioned.   The said backup sheet is peeled from this resin material, after peeling the laminated body of the said resin material and the said backup sheet after transfer from the said type | mold roller, The any one of Claims 1-5 characterized by the above-mentioned. Manufacturing method of resin sheet.   The said backup sheet is peeled from this resin material simultaneously with peeling the laminated body of the said resin material after transfer and the said backup sheet from the said peeling roll, The any one of Claims 1-5 characterized by the above-mentioned. The manufacturing method of the resin sheet of description.   The method for producing a resin sheet according to claim 6 or 7, wherein the backup sheet after peeling from the resin material is cleaned.   The method for producing a resin sheet according to any one of claims 1 to 8, wherein the backup sheet is an endless annular strip.   The method for producing a resin sheet according to any one of claims 1 to 8, further comprising sheet feeding means for continuously supplying the backup sheet and sheet winding means for storing the backup sheet. A roller row comprising a mold roller having a concavo-convex shape formed on the peripheral surface, a nip roller disposed opposite to one side of the mold roller, and a peeling roller disposed opposite to the other side of the mold roller;
A die for extruding a sheet-shaped resin material from a discharge port, wherein the discharge port is disposed on the mold roller side with respect to a common tangent line of the mold roller and the nip roller;
Backup sheet supply means for supplying a belt-like flexible backup sheet,
The resin material extruded from the die is sandwiched between the mold roller and the nip roller so that the backup sheet is on the nip roller side on the mold roller side,
The uneven shape on the surface of the mold roller is transferred to the resin material,
An apparatus for manufacturing a resin sheet, wherein a laminate of the resin material after transfer and the backup sheet is wound around the peeling roller and peeled off from the mold roller. A roller having a mold roller having a concavo-convex shape formed on the periphery thereof, a nip roller disposed to face one side of the mold roller, and a peeling roller disposed to face the other side of the mold roller;
A die for extruding a sheet-shaped resin material from the discharge port;
Backup sheet supply means for supplying a belt-like flexible backup sheet;
Heating means for heating the temperature of the backup sheet to a glass transition temperature Tg or more of the resin material,
The resin material extruded from the die is sandwiched between the mold roller and the nip roller so that the backup sheet is on the nip roller side on the mold roller side,
The uneven shape on the surface of the mold roller is transferred to the resin material,
An apparatus for producing a resin sheet, wherein a laminate of the resin material after transfer and the backup sheet is wound around the peeling roller and peeled off from the mold roller.