JP2007196432A - Decorative sheet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a decorative sheet the blocking of which is suppressed even when wound once when a decorative layer is formed and in which the decorative layer is good in weatherable adhesion and weatherable discoloration properties. <P>SOLUTION: In the decorative sheet, at least a colored hiding layer and a picture pattern layer are laminated in turn on a base material sheet. (1) The base material sheet, the colored hiding layer, and the picture pattern layer are adjacent in turn to each other, (2) the colored hiding layer contains an ether type urethane resin as a resin component, and (3) the picture pattern layer contains a resin other than the ether type urethane resin as a resin component. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a decorative sheet.

  A decorative sheet is a decorative material for the purpose of surface protection, decoration, etc. of an adherend such as a wooden board. Generally, a base sheet, a colored hiding layer, a pattern layer, an adhesive layer, a transparent resin layer, etc. are laminated. It becomes. The decorative sheet is attached to the surface of an adherend and used as a decorative board. And this decorative board is used for various building materials, furniture, etc.

  In a decorative sheet, conventionally, a colored hiding layer, a pattern layer, an adhesive layer and the like are formed from a solvent-based coating agent containing an aromatic solvent such as toluene and xylene, an aliphatic solvent such as methyl ethyl ketone and ethyl acetate, and the like. It was.

  Aromatic solvents, aliphatic solvents, etc. are organic volatile substances (VOCs). In particular, aromatic solvents such as toluene and xylene are guideline values for designated chemical substances and chemical substances in indoor air in the Chemical Substances Emissions Control Management Act. It is a formulated substance. In addition, it has been pointed out that there are problems in the working environment due to volatilization of VOC contained in the solvent-based coating agent at the time of manufacturing the decorative sheet, and environmental safety problems in which the remaining VOC is diffused into a general living space when using the decorative sheet. . Therefore, a decorative sheet made of an aqueous coating agent with reduced VOC usage has been proposed (Patent Document 1).

  However, a decorative sheet using an aqueous coating agent has the following drawbacks. That is, compared with a decorative sheet using a solvent-based coating agent, the effect of ultraviolet rays emitted by sunlight, fluorescent lamps, etc. is greater. Specifically, among the layers constituting the decorative sheet, the decorative layer (colored hiding layer and pattern layer) is likely to deteriorate and weather resistance fading easily. In addition, the adhesion of the decorative layer is likely to decrease.

Furthermore, once wound up and stored at the stage of the printing original fabric on which the decoration layer is formed on the base sheet, it may adhere to and migrate to the back surface of the sheet on which the decoration layer overlaps, and the winding sheet may be blocked. .
JP 2001-38849 A

  An object of the present invention is to provide a decorative sheet in which blocking is suppressed even when winding is performed once at the stage of forming a decorative layer, and the weather resistant adhesion and weather fading of the decorative layer are good.

  As a result of intensive studies, the inventor has found that the above-mentioned object can be achieved when the decorative layer is composed of a colored hiding layer and a pattern layer and a specific resin is used as the resin component contained in each layer. The present invention has been completed.

  That is, the present invention relates to the following decorative sheet.

1. A decorative sheet formed by sequentially laminating at least a colored hiding layer and a pattern layer on a base sheet,
(1) The base sheet, the colored hiding layer, and the pattern layer are adjacent to each other in that order.
(2) The colored hiding layer contains an ether urethane resin as a resin component,
(3) The pattern layer contains a resin other than the ether urethane resin as a resin component.
A decorative sheet characterized by that.

  2. Item 2. The decorative sheet according to Item 1, wherein the ether-based urethane resin is obtained by reacting a polyisocyanate, a polyfunctional compound having an active hydrogen atom, and a hydrazone or a hydrazone derivative having an active hydrogen atom.

  3. Item 3. The decorative sheet according to Item 1 or 2, wherein the pattern layer contains a carbonate-based urethane resin as a resin component.

  4). Item 4. The decorative sheet according to any one of Items 1 to 3, wherein a transparent resin layer is formed on the pattern layer via an adhesive layer.

  5. Item 5. The decorative sheet according to any one of Items 1 to 4, wherein at least one of the resin-containing layers is formed from an aqueous composition.

6). A decorative board obtained by laminating the decorative sheet according to any one of Items 1 to 5 and an adherend.

Hereinafter, the decorative sheet of the present invention will be described in detail.

The decorative sheet of the present invention is a decorative sheet formed by sequentially laminating at least a colored concealing layer and a pattern layer on a base sheet,
(1) The base sheet, the colored hiding layer, and the pattern layer are adjacent to each other in that order.
(2) The colored hiding layer contains an ether urethane resin as a resin component,
(3) The pattern layer contains a resin other than the ether urethane resin as a resin component.
It is characterized by that.

  In the decorative sheet of the present invention having the above characteristics, the decorative layer is composed of a colored hiding layer (so-called solid ink layer) and a pattern layer, and each layer contains a specific resin component. Good fading. Further, even when the film is temporarily wound and stored at the stage of the printing original fabric on which the decoration layer is formed, blocking of the printing original fabric is suppressed. Such an effect is good even when the decorative layer is formed from an aqueous coating agent (aqueous composition).

  The decorative sheet of the present invention can be applied to either the case where the resin-containing layer is formed with a solvent-based coating agent or the case where it is formed with a water-based coating agent (aqueous composition). In particular, when at least one of the resin-containing layers is formed of an aqueous composition, it is advantageous from the viewpoint of reducing the amount of VOC used in the decorative sheet.

  Hereinafter, the decorative sheet of the present invention will be described separately for each layer.

A decorative layer (colored hiding layer and pattern layer) is sequentially laminated on the front surface of the base sheet.

  As a base material sheet, what was formed with the thermoplastic resin is suitable. Specifically, polyvinyl chloride, polyethylene terephthalate, polybutylene terephthalate, polyamide, polyethylene, polypropylene, polycarbonate, polyethylene naphthalate, ethylene / vinyl acetate copolymer, ethylene / acrylic acid copolymer, ethylene / acrylic acid ester copolymer Polymers, ionomers, acrylic esters, methacrylic esters and the like.

  The base sheet may be colored with a colorant (pigment or dye). Examples of the colorant include inorganic pigments such as titanium dioxide, carbon black and iron oxide, and organic pigments such as phthalocyanine blue, and various dyes. The colorant can be used alone or in combination of two or more. What is necessary is just to set the addition amount of a coloring agent suitably according to a desired hue.

  The base sheet may contain various additives such as fillers, matting agents, foaming agents, flame retardants, lubricants, antistatic agents, antioxidants, ultraviolet absorbers, and light stabilizers as necessary. Good.

  Although the thickness of a base material sheet can be suitably set with the use of a final product, a usage method, etc., generally about 20-300 micrometers is preferable.

  The base sheet may be subjected to corona discharge treatment on the front surface in order to increase the adhesion of the decorative layer. The method and conditions for the corona discharge treatment may be in accordance with ordinary methods. If necessary, the back surface of the base sheet can be subjected to corona discharge treatment.

Decorative layer (colored hiding layer and pattern layer)
A decoration layer is provided with respect to a base material sheet in order of a coloring concealment layer and a pattern layer.

  The colored hiding layer is a so-called solid ink layer, and is formed by applying and drying a coating liquid on the entire surface of the base sheet. In addition to the pattern or pattern of natural materials such as wood grain and joints, the design pattern layer imparts design properties such as characters and figures to the decorative sheet.

  The decorative layer can be formed by gravure printing, flexographic printing, silk screen printing, offset printing, or the like using a printing ink containing a colorant and a resin.

  The colorant is not particularly limited, and a known colorant can be used. For example, inorganic pigments such as titanium white, zinc white, petal, vermilion, ultramarine, cobalt blue, titanium yellow, carbon black; isoindolinone, Hansa Yellow A, quinacridone, permanent red 4R, phthalocyanine blue, indanthrene blue RS, Examples thereof include organic pigments or dyes such as annin phosphorus black; metal pigments such as aluminum and brass; pearlescent pigments made of foil powder such as titanium dioxide-coated mica and basic lead carbonate. These can be used alone or in combination of two or more.

  As the printing ink, a solvent-based ink may be used, but when a water-based ink (aqueous composition) is used, it is preferable from the environmental viewpoint. The aqueous composition may be a composition (including a resin solution or a resin emulsion) in which the resin component is dissolved or dispersed in water or an aqueous solvent. As the aqueous composition, a resin emulsion (aqueous resin emulsion) is suitable.

  The water that is the solvent can be, for example, industrial water of a grade that is used in known aqueous coating agents.

  Further, as the aqueous solvent, a mixed solvent composed of water and an organic solvent can be used. As the organic solvent, for example, water-soluble organic solvents such as glycols and glycol esters can be suitably used in addition to lower alcohols such as ethanol, methanol, isopropyl alcohol, and n-propyl alcohol. The water-soluble organic solvent is used for the purpose of improving the fluidity of the aqueous composition, improving the wettability to the substrate sheet that is the object to be coated, and adjusting the drying property. The type and amount used are determined accordingly. In the case of a mixed solvent, the ratio of water and organic solvent can be appropriately adjusted within the range of water: organic solvent 20:80 to 100: 0 (weight ratio). What is necessary is just to determine suitably the usage-amount of the water or aqueous medium in an aqueous composition from the range in which solid content in an aqueous composition will be 20 to 80 weight%.

  In the present invention, the colored hiding layer (the printing ink for forming) contains an ether urethane resin as a resin component.

  Although it is not limited as an ether type urethane resin, polyisocyanate, a polyfunctional compound having an active hydrogen atom, a hydrazone or a hydrazone derivative having an active hydrogen atom (hereinafter, hydrazone derivatives having an active hydrogen atom are referred to as “hydrazones”. It is preferable to obtain the compound obtained by the reaction of

  Hereinafter, these components will be described.

≪Polyisocyanate≫
Examples of the polyisocyanate include aliphatic polyisocyanate, alicyclic polyisocyanate, and aromatic polyisocyanate.

  Examples of the aliphatic polyisocyanate include hexamethylene diisocyanate (HDI) and lysine diisocyanate (LDI).

Examples of the alicyclic polyisocyanate include isophorone diisocyanate (IPDI), cyclohexane-1,4-diisocyanate, hydrogenated xylylene diisocyanate (H ₆ XDI), hydrogenated diphenylmethane diisocyanate (H ₁₂ MDI), and the like.

  Examples of the aromatic polyisocyanate include tolylene diisocyanate (TDI), 4,4′-diphenylmethane diisocyanate, 3,3′-dimethyl-4,4′-diphenylmethane diisocyanate, etc., diphenylmethane diisocyanate (MDI), 1,3- Phenylene diisocyanate (PDI) such as phenylene diisocyanate, 1,4-phenylene diisocyanate, 1-chloro-2,4-phenylene disissocyanate, 4,4′-diphenyl diisocyanate, 3,3′-dimethyl-4,4′- Diphenyl diisocyanate such as diphenyl diisocyanate, 3,3′-dimethoxy-4,4′-diphenyl diisocyanate, xylylene diisocyanate (XDI), tetramethylxylene diisocyanate (TMXDI) Naphthalene diisocyanates such as 1,5-naphthalene diisocyanate (NDI) and the like.

  Other examples of polyisocyanates include adducts of the above polyisocyanates with polyhydric alcohols (such as trimethylolpropane) or polyamines, burette reaction products, polymeric polyisocyanates having isocyanurate rings, and the like.

  Polyisocyanate can be used individually or in mixture of 2 or more types. The polyisocyanate includes diisocyanate (aliphatic diisocyanate, alicyclic diisocyanate, aromatic diisocyanate). Diisocyanates are preferred as polyisocyanates.

≪Polyfunctional compound≫
Examples of the polyfunctional compound include various compounds having an active hydrogen atom, for example, a compound having at least one functional group selected from active hydrogen atom-containing functional groups such as hydroxyl group and amino group in the molecule. Use. Suitable polyfunctional compounds include polyether polyols having at least one functional group selected from a hydroxyl group and an amino group, polyamines, hydrazine and hydrazines having two or more hydrazino groups.

  The molecular weight of the polyfunctional compound used in the present invention is not particularly limited, and is a high molecular weight (for example, a number average molecular weight of 400 to 100,000, preferably 500 to 50,000, more preferably about 500 to 10,000). It may be a low molecular weight (for example, a molecular weight of 400 or less, preferably about 30 to 400). In the present specification, a low molecular weight polyfunctional compound may be referred to as a chain extender.

  As the polyfunctional compound, among the above, polyether polyols are essential. The polyether polyols can be used alone or in a mixture with other polyols (low molecular weight polyol and / or high molecular weight polyol). In addition to the polyether polyol, polyamines, hydrazines and the like can also be used as the polyfunctional compound.

Examples of polyether polyols include alkylene oxides (for example, ethylene oxide, propylene oxide, C _2-4 alkylene oxides such as 1,2-, 1,4- and 2,3-butylene oxide) alone or in combination. Examples include polymers, adducts of these alkylene oxides with at least one compound selected from the diols, polyols, tertiary amino group-containing diols, and polyamines described below. The said alkylene oxide can be used individually or in combination of 2 or more types.

  Of the alkylene oxides, at least ethylene oxide is often used. In the alkylene oxide copolymer, the addition form of the alkylene oxide may be random or block addition. Examples of polyether polyols include polyethylene glycol, polypropylene glycol, polyoxyethylene polyoxypropylene glycol, and polytetramethylene ether glycol. Of the polyether polyols, polytetramethylene ether glycol is preferred.

Low molecular weight polyols combined with polyether polyols are not limited, but diols (eg, ethylene glycol, diethylene glycol, triethylene glycol, 1,2-propanediol, 1,3-propanediol, dipropylene glycol, tripropylene glycol) C _2-10 alkylene glycol such as 1,3-butanediol, 2,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, neopentyl glycol; 2-Bis (4-hydroxycyclohexyl) propane (hydrogenated bisphenol A), alicyclic glycols such as 1,4-cyclohexanediol and cyclohexanedimethanol, and alkylene oxide adducts of bisphenol A (for example, ethylene Adducts in which about 1 to 5 moles of oxide or propylene oxide are added), hydrogenated dimer diol, etc.), polyol (eg, glycerin, trimethylolpropane, trimethylolethane, pentaerythritol, etc.), tertiary amino group-containing diol (For example, N-methyl-diethanolamine, N-ethyl-diethanolamine, N-methyl-diisopropanolamine, N-ethyl-diisopropanolamine, etc.).

  The high molecular weight polyol combined with the polyether polyol is not limited, and examples thereof include polyester polyols, polycarbonate polyols, and polybutadiene diol. Among these, polyester polyols include, for example, polyester polyols produced by reaction of polyhydric alcohols with polyvalent carboxylic acids or derivatives thereof, and ring-opening polymerization of lactones (ε-caprolactone, butyrolactone, etc.) that are cyclic esters. Examples thereof include polyester polyols to be produced, the low molecular weight polyols, polyether polyols, polyester polyols produced by the reaction of polyester polyols and lactones, and the like.

  Examples of the polyhydric alcohol for forming the polyester polyol include aliphatic diols such as ethylene glycol, propylene glycol, butanediol, pentanediol, hexanediol and neopentylglycol, alicyclic diols such as cyclohexanediol and cyclohexanedimethanol, Examples include adducts of alkylene oxide (such as ethylene oxide) of bisphenol A. Polycarboxylic acids or derivatives thereof include succinic acid, glutaric acid, adipic acid, azelaic acid, sebacic acid, maleic acid, maleic anhydride, fumaric acid, dimer acid, hydrogenated dimer acid and other aliphatic dicarboxylic acids, phthalates Examples thereof include aromatic dicarboxylic acids such as acid, phthalic anhydride, isophthalic acid, terephthalic acid, trimellitic acid, and naphthalenedicarboxylic acid.

  As the polyester polyol, a polyester diol is preferable. Therefore, a diol (eg, an aliphatic diol) is often used as the polyhydric alcohol, and a dicarboxylic acid (eg, an aliphatic dicarboxylic acid) is often used as the polyvalent carboxylic acid or derivative thereof.

Examples of polyamines include ethylene diamine, propylene diamine, trimethylene diamine, tetramethylene diamine, pentamethylene diamine, hexamethylene diamine, heptamethylene diamine, octamethylene diamine and other non-aliphatic polyamines (particularly diamine), 1,4-diamino. Fragrances such as cyclohexane, isophoronediamine (IPDA), hydrogenated xylylenediamine (H ₆ XDA), hydrogenated diphenylmethanediamine (H ₁₂ MDA) and other alicyclic polyamines (particularly diamines), xylylenediamine (XDA), and phenylenediamine And polyamines such as group diamine, diethylenetriamine, triethylenetetramine, and tetraethylenepentamine. These polyamines can be used alone or in admixture of two or more. As polyamines, diamines such as aliphatic diamines and alicyclic diamines are often used.

Examples of hydrazine and hydrazines include hydrazine, mono-substituted hydrazine [for example, alkyl-substituted hydrazine (C _1-6 alkyl hydrazine such as methyl hydrazine and ethyl hydrazine), hydroxyalkyl-substituted hydrazine (2-hydroxyethyl hydrazine, 2-hydroxy hydrazine, etc. Hydroxy C _1-6 alkyl hydrazine such as hydroxypropyl hydrazine, 3-hydroxypropyl hydrazine, etc.)], the following formula (1a)
_{H 2 NHN-R-NHNH 2} (1a)
(Wherein R represents an alkylene group, a cycloalkylene group or an arylene group), dihydrazines represented by the following formula (1b)
_{H 2 NHNOC-R-CONHNH 2} (1b)
(Wherein R is the same as above), dihydrazides represented by the following formula (1c)
_{H 2 NHN-CONH-R-} NHCO-NHNH 2 (1c)
(Wherein R is the same as above) and the corresponding dithiosemicarbazides.

Examples of the alkylene dihydrazines (1a) include C _1-10 alkylene dihydrazines (eg, C _1-6 alkylene dihydrazines) such as methylene dihydrazine, ethylene dihydrazine, propylene dihydrazine, butylene dihydrazine, and the like. Is included.

Examples of the dihydrazides (1b) include polyhydrazides formed by the reaction of a polyvalent carboxylic acid or a derivative thereof ( _C1-4 lower alkyl ester, acid halide or acid anhydride) with hydrazine or the alkylene dihydrazines, for example, Schulic acid dihydrazide, malonic acid dihydrazide, succinic acid dihydrazide, glutaric acid dihydrazide, adipic acid dihydrazide, sebacic acid dihydrazide, dodecanedioic acid dihydrazide, etc. aliphatic C _2-18 dicarboxylic acid dihydrazide, maleic acid dihydrazide, fumaric acid dihydrazide Examples include unsaturated aliphatic dicarboxylic acid dihydrazides such as dihydrazide, aromatic dicarboxylic acid dihydrazides such as phthalic acid dihydrazide, isophthalic acid dihydrazide, and terephthalic acid dihydrazide. Dihydrazides also include carbodihydrazide produced by the reaction of carbonic acid and hydrazine.

The disemicarbazides (1c) and dithiosemicarbazides include compounds produced by the reaction of the polyisocyanate component or polyisothiocyanate component (particularly the diisocyanate component) with hydrazine. As the hydrazine and hydrazines, the hydrazine, alkylene dihydrazines (for example, C _1-6 alkylene dihydrazines), dicarboxylic acid dihydrazide (for example, C _1-12 dicarboxylic acid dihydrazide) are often used.

  The polyfunctional compound may be used in combination with a chain extender. Examples of chain extenders include bifunctional low molecular weight compounds such as low molecular weight polyols (particularly low molecular weight diols), polyamines (particularly diamines), hydrazines and hydrazines (particularly mono-substituted hydrazines), dihydrazides, and the like. , Water and the like.

In order to impart water-solubility or water-dispersibility, it is useful to use a polyfunctional compound having an ionic group or a nonionic group and introduce an ionic group and / or a nonionic group into an ether-based urethane resin. It is. The ionic group has an anionic group (carboxylate group —COO ⁻ , sulfonate group —SO ₃ ⁻ ) generated by neutralizing an acidic group such as a carboxyl group and a sulfonic acid group with a base, and a substituent. In addition, a cationic group that is generated by neutralizing a basic group such as an amino group with an acid may be included. Examples of the nonionic group include polyoxyethylene units having 2 or more repeating oxyethylene units. The anionic group, the cationic group, and the nonionic group of the polyoxyethylene unit can be used alone or in combination of two or more.

  Examples of the polyfunctional compound for imparting water solubility or water dispersibility to the ether-based urethane resin by an anionic group include 2,2-dimethylolpropionic acid, 2,2-dimethylolbutanoic acid, 2, Carboxyl group-containing diols such as 2-dimethylolvaleric acid; carboxyl- or sulfonic acid group-containing diamines such as lysine, arginine, ornithine, aspartic acid, glutamic acid, diaminopropionic acid, diaminobenzoic acid, diaminobenzenesulfonic acid, and dihydroxyethyl phosphate A carboxyl group or sulfonic acid group-containing diol such as acid or dimethylolphosphinic acid; a polyether diol containing a carboxyl group formed by addition ring-opening polymerization of the carboxyl group-containing diol and a lactone; the diol and three or more carboxyl groups A polyvalent carboxylic acid or derivative thereof (for example, trimellitic acid, trimellitic anhydride, methylcyclohexentricarboxylic acid anhydride, vilromellitic acid, etc.) and, if necessary, an aliphatic or aromatic dicarboxylic acid or derivative thereof Examples thereof include a carboxyl group-containing polyether diol produced by a reaction; a polyether diol containing a sulfoisophthalic acid unit using sulfoisophthalic acid as a polyvalent carboxylic acid component.

  Polyfunctional compounds for imparting water-solubility or water-dispersibility to an ether-based urethane resin by an anionic group include tertiary amino group-containing diols, for example, amino group-containing diols such as the N-methyldiethanolamine Tertiary amino group-containing polyether polyols produced by reaction with alkylene oxide are included. Examples of the polyfunctional compound having a nonionic group include polyoxyalkylene glycols having an oxyethylene unit (for example, polyoxyethylene glycol having a molecular weight of 300 or more), polyhydric alcohols (particularly diols), polyamines (particularly diamines), and alkylene oxides. And adducts.

  Preferred polyfunctional compounds for imparting water solubility or water dispersibility include carboxyl group-containing diols, sulfonic acid group-containing diols, and polyoxyethylene unit-containing diols regardless of the molecular weight. The polyfunctional compound having an ionic group or a nonionic group can be used as at least one component of a high molecular weight diol and a chain extender (for example, a low molecular weight diol) depending on the molecular weight and the type of the reactive group. .

  The amount of the polyfunctional compound having an ionic group or nonionic group can be selected within a range that can impart water solubility or water dispersibility to the ether-based urethane resin and does not impair the properties of the resin. The used amount of the carboxyl group-containing diol and the sulfonic acid group-containing diol is, for example, an acid value of the ether urethane resin of 5 to 100 KOHmg / g, preferably 10 to 80 KOHmg / g (for example, 15 to 60 KOHmg / g). Amount. The amount of the tertiary amino group-containing diol used is, for example, an amount such that the ether value of the ether urethane resin is 5 to 50, preferably about 10 to 50. Furthermore, the usage-amount of the diol which has an oxyethylene unit can be selected from the range of about 5 to 50 weight% with respect to the whole ether type urethane resin, Preferably it is about 10 to 50 weight%.

  In the water-soluble or water-dispersible ether urethane resin, the ionic group is neutralized. Examples of bases for neutralizing anionic groups (carboxyl groups and sulfonic acid groups) include inorganic bases (alkali metal hydroxides such as ammonia, sodium hydroxide, and potassium hydroxide), and organic bases (dimethylamine). , Aliphatic amines such as trimethylamine, diethylamine, triethylamine, triisopropylamine, monoethanolamine, dimethylethanolamine, ethylethanolamine, diethylethanolamine, diisopropylethanolamine, diethanolamine, methyldiethanolamine, ethyldiethanolamine, isopropyldiethanolamine, triethanolamine , Alkanolamines such as triisopropanolamine, and cyclic amines such as morpholine). Among these bases, it is advantageous to use a volatile base (for example, an organic base such as ammonia, trimethylamine, or triethylamine) in order to increase the water resistance of the coating.

  Examples of acids for neutralizing cationic groups (such as tertiary amino groups) include inorganic acids (hydrochloric acid, sulfuric acid, etc.), organic acids (formic acid, acetic acid, propionic acid, lactic acid, malic acid, methanesulfone). Acid, ethanesulfonic acid, benzenesulfonic acid, p-toluenesulfonic acid, etc.) can be used.

≪Hydrazones or hydrazones≫
Hydrazone or a hydrazone derivative having an active hydrogen atom is represented by the following formula (2) generated by reaction of a hydrazino group —NHNH ₂ with a carbonyl compound.
—NH—N═CR ¹ R ² (2)
(Wherein, R ¹ and R ² are the same or different and each represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, or a heterocyclic group). Examples of the carbonyl compound include ketones and aldehydes. Examples of ketones include acetone, methyl ethyl ketone, diethyl ketone, methyl propyl ketone, methyl isopropyl ketone, dipropyl ketone (butyrone), diisopropyl ketone, and methyl butyl ketone. , methyl isobutyl ketone, methyl t- butyl ketone, saturated or unsaturated C _1-6 alkyl -C _1-6 alkyl ketones such as methyl vinyl ketone, acetophenone, propiophenone, butyrophenone, valerophenone, benzophenone, aromatic such as benzylidene acetophenone Aromatic ketones, aralkyl aldehydes such as benzylacetophenone and dibenzylketone, and heterocyclic ketones such as acetothienone and 2-acetofurone are included. Aldehydes include, for example, saturated or unsaturated aliphatic C _1-12 aldehydes such as formaldehyde, acetaldehyde, propionaldehyde, butyraldehyde, isobutyraldehyde, capronaldehyde, octaaldehyde, acrolein, crotonaldehyde, propiolaldehyde, benzaldehyde, Aromatic aldehydes such as aminobenzaldehyde, benzaldehyde sulfonic acid, tolualdehyde, cinnamaldehyde, salicylaldehyde, anisaldehyde and vanillin, and heterocyclic aldehydes such as thiophene aldehyde and furfural are included. The hydrazone or a derivative thereof may be either an aldehyde hydrazone produced by reaction with aldehydes or a ketone hydrazone produced by reaction with ketones, but ketone hydrazone is often used.

Examples of the alkyl group represented by R ¹ and R ² include 1 to 10 carbon atoms such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, s-butyl, t-butyl, pentyl, hexyl, heptyl, octyl and the like. The cycloalkyl group includes, for example, C _3-10 cycloalkyl groups such as cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, and cyclooctyl groups. Examples of the aryl group include phenyl and naphthyl groups, and examples of the aralkyl group include benzyl, phenethyl and benzhumanyl groups. The heterocyclic group includes, for example, a heterocyclic group containing an oxygen atom as a hetero atom (for example, a 5-membered ring group such as furan or oxazole, a 6-membered ring group such as pyran, a condensed ring such as benzofuran, xanthene, chromane, or isochroman. Group), a heterocyclic group containing a sulfur atom as a hetero atom (eg, a 5-membered ring group such as thiophene, thiazole, isothiazole, thiadiazole, etc.), a heterocyclic group containing a nitrogen atom as a hetero atom (eg, pyrroline, pyrrolidine, 5-membered ring groups such as imidazoline, pyrrole, pyrazole, imidazole, 6-membered ring groups such as piperidine, piperazine, morpholine, pyridine, pyridazine, pyrimidine, pyrazine, indole, indolene, isoindole, indazole, indoline, isoindoline, quinoline, Isoquinoline, phthalazine, Emissions, carbazole, acridine, phenanthridine rosin, fused ring groups such as phenanthroline) and the like. The active hydrogen atom of the hydrazone derivative can be composed of, for example, a hydroxyl group or an amino group. Preferred hydrazone derivatives having an active hydrogen atom include, for example, hydrazine, mono-substituted hydrazines and alkylenedihydrazines and a carbonyl compound, and hydrazono group, mono-substituted hydrazono group = N—NHR ³ as active hydrogen atoms. (R ³ : alkyl group, hydroxyalkyl group) or a hydrazone compound having a hydrazino group (2a) (2b) (2c), produced by a reaction of hydrazides with a carbonyl compound, and a hydrazide group —CONHNH ₂ as an active hydrogen atom And a hydrazone compound (2e) produced by a reaction of a semicarbazide and a carbonyl compound and having a semicarbazide group —NHCO—NHNH ₂ as an active hydrogen atom.

H ₂ NH═CR ¹ R ² (2a)
^{R 3 -HN-N = CR 1} R 2 (2b)
^{_{H 2 NHN-R-NHN =}} CR 1 R 2 (2c)
^{_{H 2 NHNCO-R-CONHN =}} CR 1 R 2 (2d)
_{H 2 NHN-COHN-R-} NHCO-NHN = CR 1 R 2 (2e)
(Wherein R, R ¹ , R ² and R ³ are the same as above)
The alkyl group represented by R ³ includes the same C _1-10 alkyl group as the alkyl group represented by R ¹ and R ² , and is often a C _1-6 alkyl group. Examples of the hydroxyalkyl group include hydroxy C _1-10 alkyl groups such as 2-hydroxyethyl, 2-hydroxypropyl, 3-hydroxypropyl, 4-humanoxybutyl, 3-hydroxybutyl, and 5-hydroxypentyl groups. In many cases, it is a hydroxy C _1-6 alkyl group.

More specifically, the hydrazone compounds (2a), (2b) and (2c) having a hydrazino group —NHNH ₂ as an active hydrogen atom include C _3-8 aliphatic ketones such as acetone hydrazone, methyl ethyl ketone hydrazone, methyl isobutyl ketone hydrazone. Aromatic ketone hydrazone such as hydrazone, acetophenone hydrazone, benzophenone hydrazone, C _2-6 aliphatic aldehyde-hydrazone such as formaldehyde hydrazone, acetaldehyde hydrazone, aldehyde hydrazone such as hydraldehyde, benzaldehyde hydrazone, C _1-6 alkyl hydrazine, hydroxyalkyl hydrazine (2-hydroxyethyl hydrazine, 2-hydroxypropyl hydrazine, hydroxy _{C 1-6,} such as 3-hydroxypropyl hydrazine Arukiruhi Etc. Rajin), C _1-6 alkylenedioxy hydrazines and the ketone (acetone, methyl ethyl ketone, C _3-8 aliphatic ketones such as methyl isobutyl ketone, acetophenone, and aromatic ketones such as benzophenone), or aldehyde (formaldehyde, acetaldehyde, etc. And monohydrazones produced by reaction with an aromatic aldehyde such as benzaldehyde.

The hydrazone compound (2d) having a hydrazide group -CONHNH ₂ as an active hydrogen atom includes the dihydrazides (for example, unsaturated aliphatic dicarboxylic acids such as aliphatic C _2-18 dicarboxylic acid dihydrazide, maleic acid dihydrazide, and fumaric acid dihydrazide). Dihydrazide, phthalic acid dihydrazide, isophthalic acid dihydrazide, aromatic dicarboxylic acid dihydrazide such as terephthalic acid dihydrazide, carbodihydrazide and the like) and monohydrazones produced by the reaction of the ketone or aldehyde. The hydrazone compound having a semicarbazide group -NHCO-NHNH ₂ as the active hydrogen atom (2e), said Jisemikarubajido compound or dithiocarbamate semicarbazide compounds, and the like Monohidorazon acids formed by the reaction of the ketone or aldehyde.

Preferred hydrazones or derivatives thereof include hydrazones (eg, aliphatic ketone hydrazones, especially C _1-4 alkyl-C _1-4 alkyl ketone-hydrazones and aromatic ketone hydrazones), aliphatic dicarboxylic acid dihydrazides and aliphatic ketones ( C _1-4 alkyl-C _1-4 alkyl-ketone etc.) and hydrazones produced by reaction with aromatic ketones (especially aliphatic ketones).

Hydrazone or a hydrazone derivative can be produced by a conventional method. For example, hydrazine or hydrazine, hydrazide, salt or hydrate thereof is 0.6 to 5 mol (preferably with respect to 1 mol of the ketone or aldehyde). Can be obtained by reacting 0.8 to 3 mol, particularly about 1 mol). The reaction can be performed in water or an inert solvent (for example, alcohols, hydrocarbons, ethers, etc.) at room temperature or under heating as necessary. In the formation reaction of hydrazone or hydrazone derivatives, depending on the reaction conditions, a by-product may be generated in which all hydrazino groups —NHNH _{2 of} hydrazine or hydrazines have reacted with ketones or aldehydes. In order to suppress such by-products of by-products, hydrazine or hydrazines are excessive (for example, 1.3 to 20 mol, preferably 1.5 to 10 mol, more preferably 1 mol of ketone or aldehyde). It is advantageous to carry out the reaction using about 2 to 5 mol). The target compound produced by this method can be used after being separated by a separation method such as distillation, rectification, extraction or adsorption. Excess unreacted compounds (hydrazine or hydrazines) may be subjected to the reaction as a chain extender without being removed from the reaction product. In the hydrazone or hydrazone derivative having an active hydrogen atom, the hydrazone derivative having two or more active hydrogens in the molecule is often used as a chain extender, and the hydrazone or hydrazone having one active hydrogen in the molecule. Derivatives can be used as reaction terminators. A hydrazone or hydrazone derivative has one —NHNH ₂ at the terminal and is often used as a reaction terminator.

  The ratio of the compound having a hydrazono group (hydrazone or hydrazone derivative) to the ether-based urethane resin can be selected within a range that does not impair adhesion and blocking resistance. For example, 0.03 to 2 as hydrazono groups per 1 g of polyurethane resin. 0.0 milliequivalent, preferably 0.05 to 1 milliequivalent, more preferably about 0.1 to 0.5 milliequivalent.

≪Other ingredients≫
In addition to the above components, the ether-based urethane resin may be further reacted with another reaction terminator as necessary. As the reaction terminator, monofunctional compounds, for example, alcohols such as methanol, ethanol, propanol, isopropanol, butanol, cyclohexanol, ethylamine, n-propylamine, n-butylamine, dimethylamine, diethylamine, diisopropylamine, etc. Examples include amines and alkanolamines such as N, N-dimethylaminoethanol. If a compound having an ionic dissociable group such as a carboxyl group is used as a reaction terminator, the water solubility or water dispersibility of the polyurethane resin can be increased, and if a compound having a hydrazino group is used, the adhesion to the substrate is increased. May be improved.

  The molecular weight of the ether-based urethane resin of the present invention is, for example, about 2000 to 500,000, preferably 10,000 to 200,000, and more preferably about 20,000 to 150,000.

≪Method for producing ether-based urethane resin≫
The ether-based urethane resin can be obtained by reacting polyisocyanate, the polyfunctional compound, and hydrazone or a hydrazone derivative having an active hydrogen atom. In the reaction, each component may be mixed and reacted at the same time in the reaction system, but in order to obtain a polyurethane resin with good reproducibility and to carry out the reaction smoothly, the reaction between polyisocyanate and the polyfunctional compound is performed. It is advantageous to prepare an isocyanate group-containing prepolymer and react a hydrazone or a hydrazone derivative having an active hydrogen atom with the isocyanate group-containing prepolymer. In the reaction with the prepolymer, a chain extender (diol, hydrazine, hydrazine, dihydrazide, diamine, water, etc.) may be used in combination with hydrazone or a hydrazone derivative. The water-soluble or water-dispersible polyurethane resin can be prepared by using a polyfunctional compound (preferably diol or diamine) having the ionic group and / or nonionic group as a component of the chain extender. The usage-amount of the polyfunctional compound which has the said ionic group and / or nonionic group is as above-mentioned.

In the preparation of the isocyanate group-containing prepolymer, the ratio of the polyisocyanate and the polyfunctional compound is such that the equivalent ratio of the isocyanate group and the functional group containing active hydrogen (hydroxyl group, amino group, etc.) of the polyfunctional compound is 1. 1 / 1-3 / 1, preferably 1.15 / 1-2.0 / 1, more preferably about 1.25 / 1-1.8 / 1. The ratio of polyisocyanate (especially isocyanate group-containing prepolymer) to hydrazone or hydrazone derivative is 0.01 to 1 functional group containing active hydrogen of hydrazone or hydrazone derivative (-NHNH ₂ group, etc.) relative to 1 equivalent of isocyanate group. 1 equivalent (for example, 0.05 to 0.7 equivalent), 0.1 to 0.5 equivalent, preferably about 0.1 to 0.3 equivalent.

  The reaction can be performed, for example, at a temperature of about 0 to 100 ° C. in the presence or absence of a solvent. In addition, reaction with isocyanate and polyether polyol is often performed at about 25-100 degreeC, for example.

  In order to carry out the reaction uniformly, it is advantageous to use a solvent inert to the reaction. Examples of the solvent inert to the reaction include aromatic hydrocarbons such as benzene, toluene and xylene, esters such as methyl acetate, ethyl acetate and butyl acetate, ethers such as diethyl ether and tetrahydrofuran, and N-methylpyrrolidone. Aprotic polar solvents such as acetonitrile, dimethyl sulfoxide, and mixed solvents thereof can be used. For the reaction, a conventional catalyst such as a tertiary amine such as triethylamine, a tin compound such as dibutyltin dilaurate, a titanium compound such as tetrabutoxytitanium, or the like may be used.

  The ether-based urethane resin produced by the above reaction is made aqueous by a conventional method and dissolved or dispersed in an aqueous medium. For example, an ether urethane resin having an anionic group (carboxyl group or sulfonic acid group) can be made aqueous by neutralization with the base, and an ether urethane resin having a cationic group (amino group etc.) It can be made aqueous by neutralization with the acid. The ether-based urethane resin having a nonionic group introduced can be dissolved or dispersed in an aqueous medium as it is. In a preferred ether-based urethane resin, a carboxyl group or an amino group, particularly a carboxyl group is neutralized. In addition, you may dissolve or disperse | distribute the ether-type urethane resin which does not have the said ionic group or nonionic group in an aqueous medium by using surfactant. Further, when an organic solvent, particularly a solvent immiscible with water is used in the reaction system, the immiscible solvent may be removed before being dissolved or dispersed in the aqueous medium, or dissolved or dispersed in the aqueous medium. Then, it may be removed by distillation or replaced with an aqueous solvent such as water.

  In this invention, the printing ink which forms a pattern pattern layer contains resin other than ether type urethane resin as a resin component. That is, the relationship with the printing ink forming the colored hiding layer varies depending on whether or not it contains an ether urethane resin.

  Resins other than ether-based urethane resins are not limited. In addition to polyester-based urethane resins with hydrophilic treatment, carbonate-based urethane resins, polyesters, polyacrylates, polyvinyl acetate, polybutadiene, polyvinyl chloride, chlorinated polypropylene, polyethylene Polystyrene, polystyrene-acrylate copolymer, rosin derivative, alcohol adduct of styrene-maleic anhydride copolymer, cellulose resin and the like can be used together. More specifically, for example, polyacrylamide resins, poly (meth) acrylic resins, polyethylene oxide resins, poly N-vinyl pyrrolidone resins, water-soluble polyester resins, water-soluble polyamide resins, water-soluble amino acids. Also usable are water-based resins, water-soluble phenolic resins, other water-soluble synthetic resins; water-soluble natural polymers such as polynucleotides, polypeptides, polysaccharides, and the like. Further, for example, natural rubber, synthetic rubber, polyvinyl acetate resin, (meth) acrylic resin, polyvinyl chloride resin, polyurethane-polyacrylic resin modified or mixed resin, and other resins can be used. One or more of the above resins are used. In addition, (meth) acrylic monomers such as acrylic acid esters, methacrylic acid esters, hydroxyethyl acrylate, hydroxyethyl methacrylate; nitrile monomers such as acrylonitrile and methacrylonitrile; amide monomers such as acrylamide and methacrylamide; amides thereof N-alkoxy substituted monomers and N-methylol substituted monomers; styrene monomers such as styrene, vinyl toluene, α-methyl styrene, divinyl benzene; allylic monomers such as diallyl phthalate, allyl glycidyl ether, triallyl isocyanurate; Monomers having a polymerizable double bond such as vinyl acetate and N-vinyl pyrrolidone; one or more of these, and acrylic acid, methacrylic acid, maleic acid, maleic anhydride having a carboxyl group It is acid, fumaric acid, itaconic acid, also possible to use one type or alkali solution-soluble (meth) acrylic copolymer comprising a copolymer of more unsaturated carboxylic acids other like. These can use 1 type (s) or 2 or more types.

  In the present invention, as the resin other than the ether urethane resin, a carbonate urethane resin is preferable among the above. That is, when the colored hiding layer contains an ether-based urethane resin as a resin component and the pattern layer contains a carbonate-based urethane resin as a resin component, the combination of both resins provides good blocking suppression and delamination suppression. Demonstrate the effect.

  Although it does not limit as carbonate type urethane resin, For example, what is obtained by reaction of polyisocyanate and the polyfunctional compound which has an active hydrogen element is preferable. As the polyisocyanate, those described above can be used. Polycarbonate polyols are used as the polyfunctional compound.

  Polycarbonate polyols can be synthesized from, for example, phosgenation of polyols, transesterification with diphenyl carbonate, condensation polymerization of dibasic acids and glycols, and the like.

  Specific examples of polycarbonate polyols include 1,3-propanediol, 1,4-butanediol, 1,6-hexanediol, diethylene glycol, tetraethylene glycol, and the like, and diaryl carbonates (for example, diphenyl carbonate, phosgene, and the like). ) And the product obtained by reacting. Examples of the polycarbonate polyols obtained by the condensation polymerization method of dibasic acid and glycols include products obtained by condensation polymerization of divalent phenols of dibasic acids with cyclic diols of glycols (such as glycol carbonate). .

  The thickness of the decoration layer is not limited, and the thickness of the colored hiding layer is preferably about 0.1 to 20 μm, and more preferably about 1 to 10 μm. The thickness of the pattern layer is preferably about 0.1 to 15 μm, and more preferably about 1 to 10 μm.

  In the case where the colored hiding layer and the pattern layer are formed on the base sheet, the adhesion and decoration between the decorative layer and the base sheet even if winding is performed once at the original printing stage where the decorative layer is formed. The durability of the layer is good, and the occurrence of blocking is suppressed.

Specific configuration of the decorative sheet The specific configuration of the decorative sheet is not limited. For example, a decorative sheet in which a decorative layer, a transparent adhesive layer, and a transparent resin layer are laminated on a base sheet can be mentioned. Moreover, the decorative sheet which further provided the transparent protective layer on the transparent resin layer is also mentioned.

  The method for forming the adhesive layer, the transparent resin layer, and the transparent protective layer is not limited. For example, printing such as gravure printing, flexographic printing, silk screen printing, offset printing, transfer printing; application of spray, roller, brush, etc. Any of laminated products such as sheet-like materials can be employed. What is necessary is just to select combining suitably from these methods according to the characteristic, raw material, etc. of each layer. It is desirable from an environmental viewpoint that at least one of the layers containing the resin is formed by lamination of a molded body or a coating film made of an aqueous composition.

  Hereinafter, a specific configuration will be described by taking as an example a decorative sheet having a decorative layer on a base material sheet and laminating a transparent adhesive layer, a transparent resin layer and a transparent protective layer on the decorative layer. .

≪Transparent adhesive layer≫
In the present invention, a transparent adhesive layer is interposed between the decorative layer and the transparent resin layer. The adhesive used in the adhesive layer can be appropriately selected depending on the components constituting the pattern layer or the transparent resin layer. For example, various adhesives including polyurethane resin, polyacrylic resin, polycarbonate resin, epoxy resin and the like can be used. In addition to the reactive curing type, an adhesive such as a hot melt type, an ionizing radiation curing type, and an ultraviolet curing type may be used.

  In the present invention, an adhesive capable of thermocompression bonding is used, and the pattern layer and the transparent resin layer can be laminated by thermocompression bonding.

  The adhesive layer may be transparent or translucent as long as the pattern layer can be recognized.

  The adhesive layer is desirably formed of an aqueous composition in that the VOC of the decorative sheet can be reduced. As the aqueous composition, a composition containing an aqueous binder can be used. The aqueous binder may be in any form such as an aqueous resin solution or an aqueous resin emulsion. The resin used for these can use the thing similar to the aqueous | water-based binder of the aqueous composition used for formation of the said pattern layer.

  In the present invention, a known easy adhesion treatment such as a corona discharge treatment, a plasma treatment, a degreasing treatment, a surface roughening treatment or the like can be applied to the adhesion surface as necessary.

  The thickness of the adhesive layer varies depending on the transparent protective layer, the type of adhesive used, and the like, but generally may be about 0.1 to 30 μm.

≪Transparent resin layer≫
The transparent resin layer may be colored as long as it is transparent. Moreover, it may be translucent as long as the decorative layer is visible.

  Examples of the resin include polyvinyl chloride, polyethylene terephthalate, polybutylene terephthalate, polyamide, polyethylene, polypropylene, ethylene / vinyl acetate copolymer, ethylene / acrylic acid copolymer, ethylene / acrylic acid ester copolymer, and ionomer. , Polymethylpentene, acrylic acid ester, methacrylic acid ester, polycarbonate, cellulose triacetate and the like. The transparent resin layer is particularly preferably a polyolefin resin such as polypropylene. More preferably, it is a polyolefin resin having stereoregularity. When a polyolefin resin is used, it is desirable to form a transparent resin layer by extruding a molten polyolefin resin.

  For the transparent resin layer, a filler, a matting agent, a foaming agent, a flame retardant, a lubricant, an antistatic agent, an antioxidant, an ultraviolet absorber, a light stabilizer, a radical scavenger, a soft component (as necessary) For example, various additives such as rubber) may be included.

  The thickness of the transparent resin layer is not particularly limited, but is generally about 10 to 200 μm.

≪Transparent protective layer≫
The transparent protective layer may be colored as long as it is transparent. Further, it may be translucent as long as the decoration layer is visible. By forming the transparent protective layer, the surface of the decorative sheet can be easily damaged and the scratch resistance can be improved.

  The material used for the transparent protective layer is not particularly limited, and the same materials as known decorative sheets can be used. In the present invention, it is desirable to use a two-component curable urethane resin. The two-component curable urethane resin is not particularly limited as long as it has a polyol as a main component and an isocyanate as a crosslinking agent (curing agent), and a commercially available product can also be used. As the polyol and isocyanate, those listed in the adhesive layer can be preferably used.

  In the present invention, it is desirable that the transparent protective layer is formed of an aqueous composition in that the effects such as VOC reduction are further enhanced. As the aqueous composition, a composition containing an aqueous binder can be used. The aqueous binder may be in any form such as an aqueous resin solution or an aqueous resin emulsion. The resin used for these may be the same as the aqueous binder of the aqueous composition used for forming the decorative layer.

  In the present invention, an ionizing radiation curable resin can also be used as the transparent protective layer. When using an ionizing radiation curable resin, the scratch resistance, weather resistance, etc. are particularly good.

  A well-known thing or a commercial item can be used for ionizing radiation curable resin. Specifically, a composition containing at least one of a prepolymer, an oligomer and a monomer having a polymerizable unsaturated bond or an epoxy group in the molecule is used.

  Examples of the prepolymer or oligomer include, for example, methacrylates such as polyester methacrylate, polyether methacrylate, polyol methacrylate, and melamine methacrylate, urethane acrylates, polyester acrylate, polyether acrylate, urethane acrylate, polyol acrylate, There are acrylates such as melamine acrylate.

  Monomers include styrene monomers such as styrene and α-methylstyrene, acrylic acid such as methyl acrylate, 2-ethylhexyl acrylate, methoxyethyl acrylate, butoxyethyl acrylate, butyl acrylate, and phenyl acrylate. Examples include esters, methacrylic acid esters such as methyl methacrylate, ethyl methacrylate, propyl methacrylate, ethoxymethyl methacrylate, phenyl methacrylate, and lauryl methacrylate.

  As substituted amino alcohol esters of unsaturated acids, acrylic acid-2- (N, N-diethylamino) ethyl, methacrylic acid-2- (N, N-diethylamino) ethyl, acrylic acid-2- (N, N- Dibenzylamino) methyl, acrylic acid-2- (N, N-diethylamino) propyl, and the like.

  In addition, unsaturated carboxylic acid amides such as acrylamide and methacrylamide, ethylene glycol diacrylate, propylene glycol diacrylate, neobenzyl glycol diacrylate, 1,6-hexanediol diacrylate, ethyl carbitol acrylate, diethylene glycol diacrylate, A compound such as triethylene glycol diacrylate, a multifunctional product such as dipropylene glycol diacrylate, ethylene glycol acrylate, diethylene glycol dimethacrylate, or polyethylene glycol diacrylate, and / or having two or more thiol groups in the molecule Polythiol compounds such as trimethylolpropane trithioglycolate, trimethylolpropane trithiopropiolate, There are data pentaerythritol tetra thioglycolic like. Examples of the acrylate monomer having three or more functional groups include trimethylolpropane triacrylate, pentaerythritol hexaacrylate, dipentaerythritol hexamethacrylate, and the like.

  Although the formation method of the transparent protective layer by ionizing radiation curable resin is not limited, For example, it can form by irradiating the ionizing radiation to the coating film of the composition (coating material) containing ionizing radiation curable resin. The ionizing radiation may be any ionizing radiation curable resin contained in the paint and any energy that can act on the radical photopolymerization initiator / sensitizer as an additive to initiate a radical polymerization reaction. And electromagnetic waves such as γ rays. Among these, the electron beam is most practical from the viewpoint of the curing ability of the coating film and the simplicity of the irradiation device. In the case of electron beam irradiation, for example, the film may be crosslinked and cured by electron beam irradiation under conditions of 175 keV and 5 Mrad (50 kGy). In the case where the transparent protective layer is formed of an ionizing radiation curable resin, it is desirable to previously provide a primer layer (particularly a primer layer made of a urethane resin) on the transparent resin layer as a base.

  Although the thickness of a transparent protective layer is not limited, Usually, it is desirable to set it as 0.1-50 micrometers, especially 1-20 micrometers.

  The transparent protective layer (the outermost surface of the decorative sheet) may be provided with an uneven pattern by embossing. More preferably, the embossed recess is subjected to a wiping process in which ink is filled, and the surface is coated with a two-component curable urethane resin (overcoat treatment).

  Embossing is performed to give a desired texture such as the surface of a wood board to the decorative sheet. For example, after heating and softening the transparent protective layer on a heating drum, it is further heated to 140 to 170 ° C. with an infrared radiation heater, pressed and shaped with an embossed plate provided with an uneven pattern of a desired shape, and cooled. Fixed and formed. For this, a known single wafer or rotary embossing machine may be used. Examples of the concavo-convex pattern include a wood grain conduit groove, a float pattern (a concavo-convex pattern of a raised annual ring), a hairline, a grain, a satin, and the like, and a desired pattern can be appropriately selected from these.

  The wiping process is a process of filling ink while scratching the surface with a doctor blade in a recess provided by embossing. As the wiping ink, an ink having a two-component curable urethane resin as a binder can be used. In the wiping process, the product value can be increased by expressing the design closer to the actual wood grain, particularly by performing on the wood grain conduit groove unevenness.

  In the present invention, the transparent protective layer may contain other components. For example, additives such as a solvent, an ultraviolet absorber, an antioxidant, a dispersant, a light stabilizer, a gloss adjusting agent, an antiblocking agent, and a lubricant can be blended.

Decorative plate The decorative plate of the present invention is obtained by laminating the decorative sheet of the present invention on a substrate (adhesive material). More specifically, the sheet is laminated on the substrate so that the transparent protective layer of the decorative sheet becomes the outermost surface layer.

≪Base material≫
The base material to which the decorative sheet of the present invention is applied is not limited, and the same substrate as a known decorative sheet can be used. For example, wood materials, metals, ceramics, plastics, glass and the like can be mentioned. In particular, the decorative sheet of the present invention can be suitably used for a wood material. Specifically, wood materials include veneer, wood veneer, wood plywood, particle board, medium density fiberboard (MDF) made from various materials such as cedar, firewood, firewood, pine, lawan, teak, and melapie. ) And the like.

≪Lamination on substrate≫
The lamination of the decorative sheet to the base material can be performed in the same manner as the lamination of a known decorative sheet. For example, it is possible to suitably laminate a decorative sheet on a substrate by using an adhesive.

  As the adhesive that can be used, any type of adhesive such as a thermoplastic resin, a thermosetting resin, and a rubber can be used. As this, a known product or a commercially available product can be used.

  As thermoplastic resin adhesives, polyvinyl acetate resin, polyvinyl alcohol, polyvinyl acetal (polyvinyl formal, polyvinyl butyral, etc.), cyanoacrylate, polyvinyl alkyl ether, polyvinyl chloride, polyamide, polymethyl methacrylate, nitrocellulose, acetic acid Examples include cellulose, thermoplastic epoxy, polystyrene, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, and the like.

  Thermosetting resin adhesives include urea resin, melamine resin, phenol resin, resorcinol resin, furan resin, epoxy resin, unsaturated polyester resin, polyurethane resin, polyimide, polyamideimide, polybenzimidazole, polybenzothiazole, etc. Illustrated.

  Rubber (elastomer) adhesives include natural rubber, recycled rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, chloroprene rubber, butyl rubber, polysulfide rubber, silicone rubber, polyurethane rubber, stereo rubber (synthetic natural rubber), ethylene propylene rubber And block copolymer rubber (SBS, SIS, SEBS, etc.).

  In the decorative sheet of the present invention, the decorative layer is composed of a colored hiding layer (so-called solid ink layer) and a pattern layer, and each of the layers contains a specific resin component, so that the weather resistant adhesion and weather fading of the decorative layer are good. It is. Further, even when the film is temporarily wound and stored at the stage of the printing original fabric on which the decoration layer is formed, blocking of the printing original fabric is suppressed. Such an effect is good even when the decorative layer is formed from an aqueous coating agent (aqueous composition).

  The decorative sheet of the present invention can be applied to either the case where the resin-containing layer is formed with a solvent-based coating agent or the case where it is formed with a water-based coating agent (aqueous composition). In particular, when at least one of the resin-containing layers is formed of an aqueous composition, it is advantageous from the viewpoint of reducing the amount of VOC used in the decorative sheet.

  Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. However, the present invention is not limited to the examples.

Examples 1-2 and Comparative Examples 1-3
A colored concealing layer (3 μm) and a pattern pattern layer (1 μm) were sequentially formed on a base sheet (60 μm thick colored polypropylene resin layer) subjected to corona discharge treatment by a gravure printing method.

  The colored hiding layer was formed with a white printing ink containing 30 parts by weight of a titanium oxide white pigment with respect to 15 parts by weight of the aqueous polyurethane resin shown in Table 1 below. The pattern layer was formed with a yellow printing ink containing 5 parts by weight of a yellow pigment (PY213) with respect to 15 parts by weight of the aqueous polyurethane resin shown in Table 1 below.

  Table 1 below shows resin components contained in the colored hiding layer and the pattern layer.

  The preparation method of each resin described in Table 1 is as follows.

≪Ether urethane resin≫
500 parts by weight of hydrogenated xylylene diisocyanate (H ₆ XDI) was added to a mixed solution of 1000 parts by weight of polytetramethylene ether glycol (number average molecular weight: Mn = 1000), 113 parts by weight of dimethylolpropionic acid and 403 parts by weight of ethyl acetate. added. The temperature of the mixture was gradually raised and reacted at 70 ° C.

  After the amine equivalent of the reaction product reached the theoretical value (1373), it was cooled to 60 ° C. 1000 parts by weight of the reaction mixture was added to the mixed solution of 1876.6 parts by weight of water, 79.9 parts by weight of triisopropanolamine and 70.5 parts by weight of the methyl ethyl ketone hydrazone composition while stirring to react. Next, 605 parts by weight of water was added, ethyl acetate and water were combined under heating, and 605 parts by weight were distilled out of the system to obtain an aqueous ether urethane resin.

  The methyl ethyl ketone hydrazone composition was prepared by gradually adding 72 parts by weight of methyl ethyl ketone with stirring to a mixed solution of 258 parts by weight of water and 100 parts by weight of hydrazine hydrate (methyl ethyl ketone hydrazone content 20% by weight). ).

≪Carbonate urethane resin≫
A carbonate urethane resin was prepared in the same manner as the ether urethane resin preparation except that polytetramethylene ether glycol was changed to polyhexamethylene carbonate diol.

≪Ester-based urethane resin≫
Prepare an ester urethane resin in the same way as the ether urethane resin preparation method except that polytetramethylene ether glycol is changed to polyester diol using neopentyl glycol, 1,6-hexanediol and adipic acid. did.

Test example 1
The blocking property of the sheet (original fabric) in a state where a decorative layer (colored hiding layer and pattern pattern layer) was formed on the base sheet was examined. In addition, the weather resistance adhesion of the original decorative layer was examined. Each test method was as follows.

≪Blocking resistance≫
Two original fabric test pieces prepared in each Example and Comparative Example were prepared, and the other back surface was superimposed on one front surface. After standing for 24 hours under conditions of a temperature of 50 ° C., a humidity of 80% RH, and a pressure of 5 kg / cm ² , the overlapped portion was peeled off, and the degree of transition of the decorative layer and the peel response were confirmed.

  The evaluation criteria for the test results are shown below.

○: No ink transfer. Adhesion between raw materials is not recognized (no peeling response)
Δ: No ink transfer. Adhesion of raw fabrics is recognized (with peeling response)
X: There is ink transfer. Remarkably close contact between the raw materials (with peeling response)
≪Weather resistant adhesion≫
A transparent polypropylene film (thickness: 80 μm) was laminated as a transparent resin layer on the front surface of the original fabric prepared in each example and comparative example so that water did not directly contact the decorative layer.

Using a super accelerated weathering tester (“I Super UV Tester”, manufactured by Iwasaki Electric Co., Ltd.) (hereinafter referred to as “S-UV”), each sample laminated with a transparent polypropylene film was temperature 63 ° C., humidity The situation was 50% RH. Under the circumstances, a super accelerated weathering test was performed by repeating a cycle of irradiating the sample with light having an illuminance of 60 mW / cm ² (365 nm) for 20 hours and then allowing the sample to condense for 4 hours for 200 hours. During the test, the sample was directly showered with pure water for 30 seconds when switching between irradiation and condensation.

  After the test, 100 squares of 2-mm square grid-shaped cutter scratches were applied to the surface of the original fabric from which the transparent polypropylene film was removed, and sample tape (registered trademark) (manufactured by Nichiban Co., Ltd .: 24 mm) was used as a sample. It was attached to the surface and peeled off vertically. The weather resistance adhesion was evaluated based on the degree of peeling of the decorative layer, specifically, the degree of ink removal from the decorative layer. For reference, the cycle was added after 200 hours, and the evaluation was also made after 50 hours and after 100 hours.

  The ink removal of the decorative layer was evaluated as follows in more detail, with 100/100 being taken as 0% and 0/100 being taken as 100%.

○: Ink removal of 10 squares or less was recognized at each evaluation Δ: Ink removal of 50 squares or less was recognized at each evaluation ×: Ink removal of 50 squares or more was recognized at one evaluation ≪Weather resistance fading≫
100 parts by weight of an aqueous urethane resin-containing adhesive (byronal MD1480 manufactured by Toyobo Co., Ltd.) and an isocyanate crosslinking agent (manufactured by Nikka Chemical Co., Ltd. NK) Assist IS-100N) A water-based coating agent obtained by mixing 10 parts by weight of water and 10 parts by weight of water was applied and dried by a gravure printing method to form a transparent adhesive layer (3 μm).

  A transparent polypropylene film having a thickness of 80 μm was laminated on the transparent adhesive layer by a dry lamination method to form a transparent resin layer, and a decorative sheet was produced.

  The weather resistance fading property of the produced decorative sheet was examined. The test method was as follows.

  The test was conducted using S-UV under the same conditions as the weather resistance adhesion test. The color difference (ΔE) of the decorative sheet was measured using “X-RAITE 938” manufactured by Nippon Flat Plate Equipment Co., Ltd.

  The weather fading resistance was evaluated by the color difference. The evaluation criteria are as follows.

○: ΔE is 2 or less (grayscale grade 4 or more)
Δ: ΔE is greater than 2 and less than or equal to 6 (grayscale grade 4 to 2)
X: ΔE exceeds 6 (grayscale grade 2 or less)
The test results are shown in Table 2 below.

Claims (6)

A decorative sheet formed by sequentially laminating at least a colored hiding layer and a pattern layer on a base sheet,
(1) The base sheet, the colored hiding layer, and the pattern layer are adjacent to each other in that order.
(2) The colored hiding layer contains an ether urethane resin as a resin component,
(3) The pattern layer contains a resin other than the ether urethane resin as a resin component.
A decorative sheet characterized by that.   The decorative urethane sheet according to claim 1, wherein the ether-based urethane resin is obtained by a reaction of polyisocyanate, a polyfunctional compound having an active hydrogen atom, and hydrazone or a hydrazone derivative having an active hydrogen atom.   The decorative sheet according to claim 1 or 2, wherein the pattern layer contains a carbonate-based urethane resin as a resin component.   The decorative sheet according to any one of claims 1 to 3, wherein a transparent resin layer is formed on the design pattern layer via an adhesive layer.   The decorative sheet according to any one of claims 1 to 4, wherein at least one of the resin-containing layers is formed from an aqueous composition.   A decorative board formed by laminating the decorative sheet according to any one of claims 1 to 5 and an adherend.