JP2007165455A - Display apparatus - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a display apparatus having a superior characteristic such as high precision in durability by using an insulating base of a tape-carrier semiconductor package which has high elasticity and mechanical strength, and which does not cause distortion and connection defect due to thermal history. <P>SOLUTION: In the display apparatus using a display element such as a liquid crystal display element or an EL display element receiving a driving signal through the tape-carrier semiconductor package, the insulating base of the tape-carrier semiconductor package is a film having a curl degree of 10% or below at 300°C, especially a polyimide film which is mainly composed of polyimide benzo oxazole obtained by reacting aromatic diamines having a benzo oxazole construction and aromatic tetrapod carboxylic anhydrides, and whose coefficient of linear expansion is 2 to 15 ppm/°C. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

The present invention relates to a display device, and more particularly to a display device that can be preferably applied to a thin display device having a diagonal of 3 inches or more.
More specifically, flat-screen televisions, wall-mounted televisions, hand-held televisions, stationary personal computer display units, mobile personal computers, portable display devices, acoustic device display units, portable music player display units , Display units for in-vehicle amusement devices, displays for portable communication devices, such as mobile phones, mobile vehicles such as automobiles, display devices in cockpits such as ships and aircraft, display units for car navigation systems, guidance displays in public transportation , Advertisement, public relations media, wristwatch, head mounted display, video camera, digital still camera, etc., electronic dictionary, PDA, electronic notebook, GPS, portable game machine, portable karaoke machine, toy display, digital and silver salt Camera display and status / control display Computer displays and a display unit of the state display and control unit of the TV monitor, watch, those that are using the electronic display equipment in the watch other than watch. Remote control display for various home appliances, refrigerator, washing machine, microwave oven, electric kettle, jar pot, dishwasher, electric refrigerator, cooking heater, ventilation fan, electric water heater, natural refrigerant heat pump water heater, household electric well Household appliances such as pumps, air purifiers, electric washing machines, washing machines (fully automatic / two-tank type), washing / drying machines, vacuum cleaners, hot water washing toilet seats, electric razors, household garbage processing machines, coolers, etc. Display unit, display unit of electric lighting equipment, video recorder, DVD recorder, HD recorder, stereo, home theater system, display unit of AV equipment such as radio, display unit of office equipment such as copier, printer, FAX, telephone, Printer, CD drive, FD drive, MO drive, DVD drive, hard disk, IC card, magnetic card Display of credit cards, memory card readers / writers, modems, routers, hubs and other computer peripherals, and computer display units, doorphones, fire alarm systems, gas detection, security systems and other housing and building equipment displays Health promotion equipment display such as department, health meter, blood pressure measuring instrument, electric massage instrument, etc., civil engineering machinery, mining machinery, chemical machinery and storage tank, pulp / paper making machinery, plastic processing machinery, pump, compressor and blower , Hydraulic machinery and pneumatic equipment, power transmission equipment, agricultural machinery and wood processing machinery, metal machine tools, metal processing machinery and casting equipment, food processing machinery, packaging machinery and packing machinery, sewing and textile machinery, refrigerators and Refrigerator application products, vending machines, automatic ticket gates, automatic Production equipment in all industries such as field machines, rotating electrical machines, stationary electrical machinery, switching control equipment, semiconductors, home appliances, automobiles, display units for machine tools, electronic switches, digital transmission equipment, displays in communication equipment The present invention relates to a display device used in a terminal, a terminal device such as an automatic teller machine (including a payment machine), an electric measuring instrument, an electronic application device, a measuring device, and the like.

Thin display devices include liquid crystal display devices, electroluminescence display devices, plasma displays, electrophoretic display devices, field emission display devices, electrochromic display devices, rotating sphere display devices, rotating cylindrical display devices, electronic jet fluids For example, display devices using dry powder movement are known. Such a display device includes a display panel that embodies the display principle itself, and a driving circuit for generating and transmitting a driving signal as its constituent members.
Generation and transmission of such drive signals are performed by an integrated circuit called a driver IC, and are connected to the display panel via an extremely thin circuit board called a tape substrate.
With the recent increase in definition of display panels, the number of drive signal lines led from driver ICs has increased to a very large number, and the pitch of wiring has become very small. For this reason, expansion and contraction of the wiring pitch due to changes in temperature and humidity, warping of the tape substrate, twisting and deformation of the wiring due to deformation have an increasing effect on the product yield.

As these conventional display devices, for example, as a light-receiving display device that is easy to adjust to eyes like printed matter and does not cause eye fatigue due to external light, a spherical, ellipsoidal or columnar display element, and a display element A display unit (see Patent Document 1) in which one or more of these are enclosed in a transparent hollow cylinder, and a plurality of microcapsules whose optical reflection characteristics change by application of an electric field are reliably installed at a desired position. As a result, a display panel capable of high-definition and high-quality multi-color and color display (see Patent Document 2), an array side substrate on which pixel electrodes and an electrochromic layer are formed, a counter electrode and an electrochromic layer are formed. In an electrochromic display device comprising a color filter side substrate and an electrolytic layer injected between the array side substrate and the color filter side substrate, the pixel electrode and In addition, a high-definition electrochromic display device that prevents a short circuit between pixel electrodes and a short circuit between electrochromic layers between adjacent pixels by providing a partition around the electrochromic layer (Patent Document 3) And other liquid crystal display elements (TN liquid crystal, STN liquid crystal, ferroelectric liquid crystal, guest-host liquid crystal, cholesteric liquid crystal, etc.), EL display element, electrophoretic display element, electrochromic Also known are type display elements, oxidation-reduction type display elements, rotary sphere type or rotary cylindrical type display elements, display type display elements by movement of dry powder, and the like.
JP 2002-202536 A JP 2002-365668 A JP 2005-049770 A

Many of these various display elements as described above are known, and many display apparatuses including other elements to be included as a display apparatus such as a semiconductor that bears a drive unit that operates integrally with these display elements are also proposed. Has been.
For example, in an active matrix semiconductor display device in which a pixel TFT and a drive circuit TFT are integrally formed on the same substrate, a gap holding material (polyimide is used as the gap holding material) disposed between the pixel region and the drive circuit region. Resin is an example), the cell gap can be controlled, and a uniform cell thickness can be obtained over the entire semiconductor display device, and the conventional grain spacer is not used. Therefore, when bonding the active matrix substrate and the counter substrate, An active matrix semiconductor display device (see Patent Document 4) that can prevent damage to the drive circuit TFT in which no stress is generated in the drive circuit TFT, or a liquid crystal sealed between a pair of substrates, On the substrate in a matrix form in an intersecting state vertically and horizontally via an interlayer insulating film (polyimide resin etc. is exemplified) A gate wiring and a source wiring are formed, and a thin film transistor is formed by being electrically connected to the gate wiring and the source wiring, and the thin film transistor is electrically connected to a region partitioned by the gate wiring and the source wiring. A pixel electrode is formed by connection, and a liquid crystal display device in which the dielectric constant of the gate insulating film interposed between the gate electrode forming the thin film transistor and the semiconductor active layer is larger than the dielectric constant of the interlayer insulating film (patent The organic insulating tape having a device hole for mounting a semiconductor integrated circuit element with improved reliability by preventing lead disconnection due to the thickness difference of the base film, and affixed to the organic insulating tape Arrangement of inner leads for semiconductor integrated circuit element bonding and output and input outer leads A semiconductor integrated circuit having an aspect ratio of about 4 or more, which is arranged and connected to a metal foil layer on which a pattern is formed and the inner lead so that the longitudinal direction is parallel to the width direction of the organic insulating tape Many types of polyimide resins and films have been proposed for liquid crystal driver tape carrier packages having circuit elements (see Patent Document 6) and insulating substrates for various elements of these display devices.

Japanese Patent Laid-Open No. 10-319440 Japanese Patent Laid-Open No. 10-048610 JP 2002-277894 A

A polyimide resin or a polyimide film is used as an insulating substrate for an element in a conventionally known display device, but any polyimide resin or polyimide film can sufficiently satisfy environmental durability, particularly heat resistance, particularly high temperature. No one has been known to maintain durability against deformation in the plane direction.
An object of the present invention is to provide a display device capable of high-definition display and having high production yield and excellent environmental durability.

As a result of intensive studies, the present inventors have achieved high yield and high-definition image display by using a polymer film satisfying specific physical properties as an insulating substrate, particularly in a display device having a wiring pitch of a specific value or less. The present inventors have found that it is satisfactory and have reached the present invention.
That is, this invention consists of the following structures.
1. A display device using a display element that receives a drive signal via a tape carrier type semiconductor package, wherein the insulating substrate of the tape carrier type semiconductor package is a polyimide film having a curl degree of 10% or less at 300 ° C., and A display device having a minimum pitch of wiring of 40 μm or less.
2. 2. The display device according to 1, wherein the display element is a liquid crystal display element (TN liquid crystal, STN liquid crystal, ferroelectric liquid crystal, guest-host liquid crystal, cholesteric liquid crystal, or the like).
3. 2. The display device according to 1 above, wherein the liquid crystal display element is at least one display element selected from TN liquid crystal, STN liquid crystal, ferroelectric liquid crystal, guest-host liquid crystal, and cholesteric liquid crystal.
4). The display element is selected from an EL display element, an electrophoretic display element, an electrochromic display element, an oxidation-reduction display element, a rotating sphere type or rotating cylindrical display element, and a display type display element by movement of dry powder. 2. The display device according to 1 above, which is one or more display elements.
5. Polyimide film having a linear expansion coefficient of 2 to 15 ppm / ° C. mainly composed of polyimide benzoxazole obtained by reacting an aromatic diamine having an benzoxazole structure with an aromatic tetracarboxylic acid anhydride. The display device according to any one of 1 to 4 above.
6). The insulating substrate has a plane orientation coefficient of 0.75 or more, which is mainly composed of polyimide benzoxazole obtained by reacting an aromatic diamine having a benzoxazole structure and an aromatic tetracarboxylic anhydride, The display device according to any one of 1 to 5, which is a polyimide film having an elastic modulus of 5 GPa or more and a tensile breaking strength of 300 MPa or more.

  In the present invention, the film as an insulating base material satisfying the physical properties of the specific structure in the tape carrier type semiconductor package is mechanical in the circuit pattern manufacturing process, particularly in the circuit pattern manufacturing process in which the minimum pitch of the wiring is 40 μm or less. It has sufficient flatness and dimensional stability through thermal and chemical stresses, and has good dimensional accuracy and flatness even after receiving mechanical and thermal stress when mounting a driver IC on a tape substrate. Can be maintained. With such an effect, it is possible to provide an image display device that can mount a driver IC with a high yield even in a display panel that can display an extremely high-definition image and that has high reliability and durability.

The film as the insulating substrate in the present invention is not particularly limited as long as it is a polyimide film having a curl degree of 10% or less at 300 ° C., and an aromatic diamine for obtaining a polyimide film and an aromatic tetra The reaction with the carboxylic acid is obtained by subjecting an aromatic diamine and an aromatic tetracarboxylic acid (anhydride) to a (ring-opening) polyaddition reaction in a solvent to obtain a polyamic acid solution as a polyimide precursor, Next, a precursor film (green film) is formed from this polyamic acid solution, followed by drying, heat treatment, and dehydration condensation (imidization).
Hereinafter, the polyimide film will be described in detail.
Although the polyimide film in this invention is not specifically limited, The combination of the following aromatic diamine and aromatic tetracarboxylic acid (anhydride) is mentioned as a preferable example.
A. A combination of an aromatic diamine having a benzoxazole structure and an aromatic tetracarboxylic acid.
B. A combination of an aromatic diamine having a diaminodiphenyl ether skeleton and an aromatic tetracarboxylic acid having a pyromellitic acid skeleton.
C. A combination of an aromatic diamine having a phenylenediamine skeleton and an aromatic tetracarboxylic acid having a biphenyltetracarboxylic acid skeleton.
D. A combination of one or more of the above ABCs.
Used in a polyimide benzoxazole film mainly composed of polyimide benzoxazole obtained by reacting an aromatic diamine having a benzoxazole structure that can be particularly preferably used in the present invention and an aromatic tetracarboxylic acid anhydride, Examples of aromatic diamines having a benzoxazole structure include the following compounds.

Among these, amino (aminophenyl) benzoxazole isomers are preferable from the viewpoint of ease of synthesis. Here, “each isomer” refers to each isomer in which two amino groups of amino (aminophenyl) benzoxazole are determined according to the coordination position (eg, the above “formula 1” to “formula 4”). Each compound described in the above. These diamines may be used alone or in combination of two or more.
In the present invention, it is preferable to use 70 mol% or more of the aromatic diamine having the benzoxazole structure.

The present invention is not limited to the above items, and the following aromatic diamines may be used. Preferably, the diamines do not have the benzoxazole structure exemplified below as long as the total aromatic diamine is less than 30 mol%. Is a polyimide film using one or two or more in combination.
Examples of such diamines include 4,4′-bis (3-aminophenoxy) biphenyl, bis [4- (3-aminophenoxy) phenyl] ketone, and bis [4- (3-aminophenoxy) phenyl]. Sulfide, bis [4- (3-aminophenoxy) phenyl] sulfone, 2,2-bis [4- (3-aminophenoxy) phenyl] propane, 2,2-bis [4- (3-aminophenoxy) phenyl] -1,1,1,3,3,3-hexafluoropropane, m-phenylenediamine, o-phenylenediamine, p-phenylenediamine, m-aminobenzylamine, p-aminobenzylamine,

3,3'-diaminodiphenyl ether, 3,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl ether, 3,3'-diaminodiphenyl sulfide, 3,3'-diaminodiphenyl sulfoxide, 3,4'-diaminodiphenyl sulfoxide 4,4'-diaminodiphenyl sulfoxide, 3,3'-diaminodiphenyl sulfone, 3,4'-diaminodiphenyl sulfone, 4,4'-diaminodiphenyl sulfone, 3,3'-diaminobenzophenone, 3,4'- Diaminobenzophenone, 4,4′-diaminobenzophenone, 3,3′-diaminodiphenylmethane, 3,4′-diaminodiphenylmethane, 4,4′-diaminodiphenylmethane, bis [4- (4-aminophenoxy) phenyl] methane, 1 , 1-Bi [4- (4-aminophenoxy) phenyl] ethane, 1,2-bis [4- (4-aminophenoxy) phenyl] ethane, 1,1-bis [4- (4-aminophenoxy) phenyl] propane, 1 , 2-bis [4- (4-aminophenoxy) phenyl] propane, 1,3-bis [4- (4-aminophenoxy) phenyl] propane, 2,2-bis [4- (4-aminophenoxy) phenyl ]propane,

1,1-bis [4- (4-aminophenoxy) phenyl] butane, 1,3-bis [4- (4-aminophenoxy) phenyl] butane, 1,4-bis [4- (4-aminophenoxy) Phenyl] butane, 2,2-bis [4- (4-aminophenoxy) phenyl] butane, 2,3-bis [4- (4-aminophenoxy) phenyl] butane, 2- [4- (4-aminophenoxy) Phenyl] -2- [4- (4-aminophenoxy) -3-methylphenyl] propane, 2,2-bis [4- (4-aminophenoxy) -3-methylphenyl] propane, 2- [4- ( 4-aminophenoxy) phenyl] -2- [4- (4-aminophenoxy) -3,5-dimethylphenyl] propane, 2,2-bis [4- (4-aminophenoxy) -3,5-dimethylphen Le] propane, 2,2-bis [4- (4-aminophenoxy) phenyl] -1,1,1,3,3,3-hexafluoropropane,

1,4-bis (3-aminophenoxy) benzene, 1,3-bis (3-aminophenoxy) benzene, 1,4-bis (4-aminophenoxy) benzene, 4,4′-bis (4-aminophenoxy) ) Biphenyl, bis [4- (4-aminophenoxy) phenyl] ketone, bis [4- (4-aminophenoxy) phenyl] sulfide, bis [4- (4-aminophenoxy) phenyl] sulfoxide, bis [4- ( 4-aminophenoxy) phenyl] sulfone, bis [4- (3-aminophenoxy) phenyl] ether, bis [4- (4-aminophenoxy) phenyl] ether, 1,3-bis [4- (4-aminophenoxy) ) Benzoyl] benzene, 1,3-bis [4- (3-aminophenoxy) benzoyl] benzene, 1,4-bis [4- (3 Aminophenoxy) benzoyl] benzene, 4,4′-bis [(3-aminophenoxy) benzoyl] benzene, 1,1-bis [4- (3-aminophenoxy) phenyl] propane, 1,3-bis [4- (3-aminophenoxy) phenyl] propane, 3,4'-diaminodiphenyl sulfide,

2,2-bis [3- (3-aminophenoxy) phenyl] -1,1,1,3,3,3-hexafluoropropane, bis [4- (3-aminophenoxy) phenyl] methane, 1,1 -Bis [4- (3-aminophenoxy) phenyl] ethane, 1,2-bis [4- (3-aminophenoxy) phenyl] ethane, bis [4- (3-aminophenoxy) phenyl] sulfoxide, 4,4 '-Bis [3- (4-aminophenoxy) benzoyl] diphenyl ether, 4,4'-bis [3- (3-aminophenoxy) benzoyl] diphenyl ether, 4,4'-bis [4- (4-amino-α) , Α-dimethylbenzyl) phenoxy] benzophenone, 4,4′-bis [4- (4-amino-α, α-dimethylbenzyl) phenoxy] diphenylsulfone, bis 4- {4- (4-aminophenoxy) phenoxy} phenyl] sulfone, 1,4-bis [4- (4-aminophenoxy) phenoxy-α, α-dimethylbenzyl] benzene, 1,3-bis [4- (4-aminophenoxy) phenoxy-α, α-dimethylbenzyl] benzene, 1,3-bis [4- (4-amino-6-trifluoromethylphenoxy) -α, α-dimethylbenzyl] benzene, 1,3 -Bis [4- (4-amino-6-fluorophenoxy) -α, α-dimethylbenzyl] benzene, 1,3-bis [4- (4-amino-6-methylphenoxy) -α, α-dimethylbenzyl Benzene, 1,3-bis [4- (4-amino-6-cyanophenoxy) -α, α-dimethylbenzyl] benzene,

3,3′-diamino-4,4′-diphenoxybenzophenone, 4,4′-diamino-5,5′-diphenoxybenzophenone, 3,4′-diamino-4,5′-diphenoxybenzophenone, 3, 3'-diamino-4-phenoxybenzophenone, 4,4'-diamino-5-phenoxybenzophenone, 3,4'-diamino-4-phenoxybenzophenone, 3,4'-diamino-5'-phenoxybenzophenone, 3,3 '-Diamino-4,4'-dibiphenoxybenzophenone, 4,4'-diamino-5,5'-dibiphenoxybenzophenone, 3,4'-diamino-4,5'-dibiphenoxybenzophenone, 3,3'- Diamino-4-biphenoxybenzophenone, 4,4′-diamino-5-biphenoxybenzophenone, 3,4 -Diamino-4-biphenoxybenzophenone, 3,4'-diamino-5'-biphenoxybenzophenone, 1,3-bis (3-amino-4-phenoxybenzoyl) benzene, 1,4-bis (3-amino- 4-phenoxybenzoyl) benzene, 1,3-bis (4-amino-5-phenoxybenzoyl) benzene, 1,4-bis (4-amino-5-phenoxybenzoyl) benzene, 1,3-bis (3-amino) -4-biphenoxybenzoyl) benzene, 1,4-bis (3-amino-4-biphenoxybenzoyl) benzene, 1,3-bis (4-amino-5-biphenoxybenzoyl) benzene, 1,4-bis (4-Amino-5-biphenoxybenzoyl) benzene, 2,6-bis [4- (4-amino-α, α-dimethylbenzyl) pheno Si] benzonitrile and some or all of the hydrogen atoms on the aromatic ring in the aromatic diamine are halogen atoms, alkyl groups having 1 to 3 carbon atoms or alkoxyl groups, cyano groups, or alkyl groups or alkoxyl group hydrogen atoms. Examples thereof include aromatic diamines substituted with a halogenated alkyl group having 1 to 3 carbon atoms, partially or entirely substituted with a halogen atom, or an alkoxyl group.

  The aromatic tetracarboxylic acids used in the present invention are, for example, aromatic tetracarboxylic anhydrides. Specific examples of the aromatic tetracarboxylic acid anhydrides include the following.

These tetracarboxylic dianhydrides may be used alone or in combination of two or more.
In the present invention, one or two or more non-aromatic tetracarboxylic dianhydrides exemplified below may be used in combination as long as they are less than 30 mol% of the total tetracarboxylic dianhydrides. Examples of such tetracarboxylic acid anhydrides include butane-1,2,3,4-tetracarboxylic dianhydride, pentane-1,2,4,5-tetracarboxylic dianhydride, and cyclobutanetetracarboxylic acid. Acid dianhydride, cyclopentane-1,2,3,4-tetracarboxylic dianhydride, cyclohexane-1,2,4,5-tetracarboxylic dianhydride, cyclohex-1-ene-2,3 5,6-tetracarboxylic dianhydride, 3-ethylcyclohex-1-ene-3- (1,2), 5,6-tetracarboxylic dianhydride, 1-methyl-3-ethylcyclohexane-3 -(1,2), 5,6-tetracarboxylic dianhydride, 1-methyl-3-ethylcyclohex-1-ene-3- (1,2), 5,6-tetracarboxylic dianhydride 1-ethylcyclohexane -(1,2), 3,4-tetracarboxylic dianhydride, 1-propylcyclohexane-1- (2,3), 3,4-tetracarboxylic dianhydride, 1,3-dipropylcyclohexane- 1- (2,3), 3- (2,3) -tetracarboxylic dianhydride, dicyclohexyl-3,4,3 ′, 4′-tetracarboxylic dianhydride,

Bicyclo [2.2.1] heptane-2,3,5,6-tetracarboxylic dianhydride, 1-propylcyclohexane-1- (2,3), 3,4-tetracarboxylic dianhydride, 1 , 3-Dipropylcyclohexane-1- (2,3), 3- (2,3) -tetracarboxylic dianhydride, dicyclohexyl-3,4,3 ′, 4′-tetracarboxylic dianhydride, bicyclo [2.2.1] Heptane-2,3,5,6-tetracarboxylic dianhydride, bicyclo [2.2.2] octane-2,3,5,6-tetracarboxylic dianhydride, bicyclo [2.2.2] Oct-7-ene-2,3,5,6-tetracarboxylic dianhydride and the like. These tetracarboxylic dianhydrides may be used alone or in combination of two or more.

  The solvent used when polyamic acid is obtained by polycondensation (polymerization) of the aromatic diamine and aromatic tetracarboxylic acid (anhydride) dissolves both the raw material monomer and the resulting polyamic acid. Although it will not specifically limit if it carries out, A polar organic solvent is preferable, for example, N-methyl-2-pyrrolidone, N-acetyl-2-pyrrolidone, N, N-dimethylformamide, N, N-diethylformamide, N, Examples thereof include N-dimethylacetamide, dimethyl sulfoxide, hexamethylphosphoric amide, ethyl cellosolve acetate, diethylene glycol dimethyl ether, sulfolane, and halogenated phenols. These solvents can be used alone or in combination. The amount of the solvent used may be an amount sufficient to dissolve the monomer as a raw material. As a specific amount used, the mass of the monomer in the solution in which the monomer is dissolved is usually 5 to 40% by mass, The amount is preferably 10 to 30% by mass.

Conventionally known conditions may be applied for the polymerization reaction for obtaining the polyamic acid (hereinafter also simply referred to as “polymerization reaction”). As a specific example, in a temperature range of 0 to 80 ° C., 10 Stirring and / or mixing continuously for 30 minutes. If necessary, the polymerization reaction may be divided or the temperature may be increased or decreased. In this case, the order of adding both monomers is not particularly limited, but it is preferable to add aromatic tetracarboxylic acid anhydrides to the solution of aromatic diamines. The mass of the polyamic acid in the polyamic acid solution obtained by the polymerization reaction is preferably 5 to 40% by mass, more preferably 10 to 30% by mass, and the viscosity of the solution is measured with a Brookfield viscometer (25 ° C.). From the viewpoint of the stability of liquid feeding, it is preferably 10 to 2000 Pa · s, and more preferably 100 to 1000 Pa · s.
The reduced viscosity (ηsp / C) of the polyamic acid in the present invention is not particularly limited, but is preferably 3.0 dl / g or more, more preferably 4.0 dl / g or more. By setting these reduced viscosities, It becomes easy to control the linear expansion coefficient of the obtained polyimide benzoxazole from -10 to +16 (ppm / ° C.).

  Vacuum defoaming during the polymerization reaction is effective for producing a high-quality polyamic acid organic solvent solution. Moreover, you may perform superposition | polymerization by adding a small amount of terminal blockers to aromatic diamines before a polymerization reaction. Examples of the end capping agent include compounds having a carbon-carbon double bond such as maleic anhydride. The amount of maleic anhydride used is preferably 0.001 to 1.0 mol per mol of aromatic diamine.

  As an imidization method by high-temperature treatment, a conventionally known imidation reaction can be appropriately used. For example, using a polyamic acid solution that does not contain a ring-closing catalyst or a dehydrating agent, the imidization reaction proceeds by subjecting it to a heat treatment (so-called thermal ring-closing method), or a polycyclic acid solution containing a ring-closing catalyst and a dehydrating agent In particular, a chemical ring closing method in which an imidization reaction is performed by the action of the above ring closing catalyst and a dehydrating agent can be given.

  100-500 degreeC is illustrated as a heating maximum temperature of a thermal ring closure method, Preferably it is 200-480 degreeC. When the maximum heating temperature is lower than this range, it is difficult to close the ring sufficiently, and when it is higher than this range, the deterioration proceeds and the composite tends to become brittle. A more preferable embodiment includes a two-stage heat treatment in which treatment is performed at 150 to 250 ° C. for 3 to 20 minutes and then treatment at 350 to 500 ° C. for 3 to 20 minutes.

In the chemical ring closure method, imidization reaction of a polyamic acid solution is partially advanced to form a precursor complex having self-supporting property, and then imidization can be performed completely by heating.
In this case, the condition for partially proceeding with the imidization reaction is preferably a heat treatment for 3 to 20 minutes at 100 to 200 ° C., and the condition for allowing the imidization reaction to be completely performed is preferably 200 to 400 ° C. For 3 to 20 minutes.

The timing for adding the ring-closing catalyst to the polyamic acid solution is not particularly limited, and may be added in advance before the polymerization reaction for obtaining the polyamic acid. Specific examples of the ring-closing catalyst include aliphatic tertiary amines such as trimethylamine and triethylamine, and heterocyclic tertiary amines such as isoquinoline, pyridine, and betapicoline. Among them, heterocyclic tertiary amines are mentioned. At least one amine selected from is preferred. Although the usage-amount of a ring-closing catalyst with respect to 1 mol of polyamic acids does not have limitation in particular, Preferably it is 0.5-8 mol.
The timing of adding the dehydrating agent to the polyamic acid solution is not particularly limited, and may be added in advance before the polymerization reaction for obtaining the polyamic acid. Specific examples of the dehydrating agent include aliphatic carboxylic acid anhydrides such as acetic anhydride, propionic anhydride, butyric anhydride, and aromatic carboxylic acid anhydrides such as benzoic anhydride. Among them, acetic anhydride, benzoic anhydride, etc. Acids or mixtures thereof are preferred. Moreover, the usage-amount of the dehydrating agent with respect to 1 mol of polyamic acids is not particularly limited, but is preferably 0.1 to 4 mol. When a dehydrating agent is used, a gelation retarder such as acetylacetone may be used in combination.

The film as the insulating base material of the tape carrier type semiconductor package in the present invention is a film having a curl degree at 300 ° C. of 10% or less, and the curl degree of the film at 300 ° C. (hereinafter, the curl degree of the film at 300 ° C. Means a degree of deformation in the thickness direction with respect to the surface direction of the film after performing a predetermined heat treatment. Specifically, as shown in FIG. After 10 minutes of hot air treatment at ° C., the test piece was placed on a flat surface so as to be concave, and the average value of the distances from the four corner planes (h1, h2, h3, h4: unit mm) was the curl amount (mm ) And a value expressed as a percentage (%) of the curl amount with respect to the distance (35.36 mm) from each vertex to the center of the test piece.
Samples were sampled at a total of 10 points, with 2 points in the width direction (1/3 and 2/3 of the length) as the center points of the test piece at a 1/5 length pitch with respect to the total length of the film. The measured value is an average value of 10 points.
However, if there is not enough film to sample 10 points, sample as much as possible.
Specifically, it is calculated by the following formula.
Curling amount (mm) = (h1 + h2 + h3 + h4) / 4
Curling degree (%) = 100 × (curl amount) /35.36

In the present invention, the curl degree of the film at 400 ° C. is measured in the same manner except that the heat treatment at the time of measurement at 300 ° C. is treated with hot air at 400 ° C. for 10 minutes.
The curl degree at 300 ° C. in the present invention is more preferably 8% or less, still more preferably 5% or less, and further a film having a curl degree at 400 ° C. of 10% or less is preferred.
The film in the present invention is preferably a polyimide film, more preferably a polyimide benzoxazole obtained by reacting an aromatic diamine having a benzoxazole structure with an aromatic tetracarboxylic acid anhydride as a main component. A polyimide film having a linear expansion coefficient of 2 to 15 ppm / ° C., and particularly preferably a polyimide benzoxazole obtained by reacting an aromatic diamine having a benzoxazole structure with an aromatic tetracarboxylic anhydride. The polyimide film has a plane orientation coefficient of 0.75 or more, a tensile modulus of 5 GPa or more, and a tensile strength at break of 300 MPa or more. Because the polyimide film has a linear expansion coefficient of 2 to 15 ppm / ° C., the difference between the linear expansion coefficients of the metal thin film layer such as copper and the like formed on the film is small and peeling occurs due to heating and cooling. hard. Further, when the polyimide film has a plane orientation coefficient of 0.75 or more, a tensile modulus of elasticity of 5 GPa or more, and a tensile breaking strength of 300 MPa or more, a further effect of improving heat resistance can be obtained.

Although the thickness of the (polyimide) film of the present invention is not particularly limited, it is usually 1 to 150 μm, preferably 5 to 50 μm in consideration of use for an insulating substrate. This thickness can be easily controlled by the coating amount when a film raw material solution such as a polyamic acid solution is applied to the support and the raw material concentration in the film raw material solution such as a polyamic acid solution.
In the (polyimide) film of the present invention, it is preferable to add a lubricant to the (polyimide) film to give fine irregularities on the film surface to improve the slipping property of the film.
As the lubricant, inorganic or organic fine particles having an average particle diameter of about 0.03 μm to 3 μm can be used. Specific examples include titanium oxide, alumina, silica, calcium carbonate, calcium phosphate, calcium hydrogen phosphate, calcium pyrophosphate, Examples include magnesium oxide, calcium oxide, and clay minerals.
The (polyimide) film of the present invention may be a non-stretched film or a stretched film. Here, the non-stretched film is mechanical in the surface expansion direction of the film by tenter stretching, roll stretching, inflation stretching, or the like. A film that can be obtained without intentionally applying a large external force.

EXAMPLES Hereinafter, although an Example and a comparative example are shown and this invention is demonstrated more concretely, this invention is not limited by a following example. The physical property evaluation methods in the following examples are as follows except for the above.
Abbreviations of compounds used in Examples and the like are described below.
PMDA: pyromellitic dianhydride TMHQ: P-phenylenebis (trimellitic acid monoester anhydride)
ODA: 4,4′-diaminodiphenyl ether P-PDA: paraphenylenediamine BPDA: 3,3 ′, 4,4′-biphenyltetracarboxylic dianhydride DMF: dimethylformamide DMAC: dimethylacetamide AA: acetic anhydride IQ: isoquinoline Abbreviation GF indicates a polyimide precursor film (green film), and abbreviation IF indicates a polyimide film.

1. Reduced viscosity of polyamic acid (ηsp / C)
A solution dissolved in N-methyl-2-pyrrolidone so that the polymer concentration was 0.2 g / dl was measured at 30 ° C. using an Ubbelohde type viscosity tube.
2. The thickness of the polyimide film The thickness was measured using a micrometer (Millitron 1254D manufactured by Fine Reef).
3. Specimen obtained by cutting a polyimide film to be measured into a strip of 100 mm × 10 mm in the flow direction (MD direction) and the width direction (TD direction), respectively. It was. Using a tensile tester (manufactured by Shimadzu Corporation, Autograph (trade name), model name AG-5000A) under the conditions of a tensile speed of 50 mm / min and a distance between chucks of 40 mm, the tensile modulus of elasticity in each of the MD direction and TD direction, Tensile rupture strength and tensile rupture elongation were measured.

4). Linear expansion coefficient (CTE) of polyimide film
For the polyimide film to be measured, the stretch rate in the MD direction and the TD direction is measured under the following conditions, and the stretch rate / temperature at intervals of 30 ° C. to 45 ° C., 45 ° C. to 60 ° C.,. This measurement was performed up to 300 ° C., and the average value of all measured values was calculated as CTE. The meanings of the MD direction and the TD direction are the same as in the measurement of “3.” above.
Device name: TMA4000S manufactured by MAC Science
Sample length; 20mm
Sample width: 2 mm
Temperature rise start temperature: 25 ° C
Temperature rising end temperature: 400 ° C
Temperature increase rate: 5 ° C / min
Atmosphere: Argon

5. Surface orientation coefficient of polyimide film A polyimide film to be measured was mounted on a measurement jig, and X-ray diffraction measurement was performed under the following conditions to obtain a pole figure about a diffraction peak appearing near 2θ = 21.8 °. .
Device name: RINT 2100PC manufactured by Rigaku Co., Ltd., multipurpose sample base Voltage, current value; 40 kV, 40 mA
Measurement method; reflection method and transmission method scanning range; reflection method α; 15 to 90 ° / 2.5 ° interval
β: 0 to 360 ° / 5 ° interval
Reflection method α: 0-15 ° / 2.5 ° interval
β: 0-360 ° / 5 ° interval slit; DS 0.1 mm, SS 7 mm, RS 7 mm,
Vertical divergence limit slit 1.2mm
Scanning speed: Continuous (360 ° / min)
Detector: Scintillation counter FIG. 3 schematically shows this pole figure. In the figure, peak half widths (HMD and HTD) were determined from diffraction intensity profiles at two broken lines, and the average value of HMD and HTD was defined as Ha (unit: °). The peak half-value width was obtained using a Rigaku analysis program. From the thus obtained Ha, the plane orientation coefficient of the polyimide film was calculated by the following equation.
Plane orientation coefficient = (180 ° −Ha) ÷ 180 °

[Polymeric acid solution polymerization example 1]
(Preliminary dispersion of inorganic particles)
1.22 parts by mass of amorphous silica spherical particles Seahoster KE-P10 (manufactured by Nippon Shokubai Co., Ltd.), 420 parts by mass of N-methyl-2-pyrrolidone, the wetted part of the container, and the infusion pipe are austenitic stainless steel The mixture was placed in a container of SUS316L and stirred with a homogenizer T-25 basic (manufactured by IKA Labortechnik) at a rotation speed of 1000 rpm for 1 minute to obtain a preliminary dispersion. The average particle size in the preliminary dispersion was 0.11 μm.
(Preparation of polyamic acid solution)
A nitrogen inlet tube, a thermometer, a liquid contact part of a container equipped with a stirring rod, and a pipe for infusion were substituted with nitrogen in the reaction container made of austenitic stainless steel SUS316L, and then 223 parts by mass of 5-amino-2- ( p-Aminophenyl) benzoxazole was added. Next, 4000 parts by mass of N-methyl-2-pyrrolidone was added and completely dissolved, and then the preliminary dispersion obtained above was added with 420 parts by mass and 217 parts by mass of pyromellitic dianhydride. When the mixture was stirred at ° C. for 24 hours, a brown viscous polyamic acid solution A was obtained. The reduced viscosity (ηsp / C) was 3.8 dl / g.

[Polymeric acid solution polymerization example 2]
Nitrogen introduction tube, thermometer, vessel wetted part equipped with stirring rod, and infusion pipe were replaced with nitrogen in the reaction vessel of austenitic stainless steel SUS316L, and then 5-amino-2- (p-aminophenyl) ) After adding 223 parts by mass of benzoxazole and 4416 parts by mass of N, N-dimethylacetamide and completely dissolving them, Snowtex DMAC-ST30 (manufactured by Nissan Chemical Industries, Ltd.) 40 in which colloidal silica is dispersed in dimethylacetamide .5 parts by mass (including 8.1 parts by mass of silica) and 217 parts by mass of pyromellitic dianhydride are added and stirred at a reaction temperature of 25 ° C. for 24 hours to obtain a brown and viscous polyamide acid solution B. It was. Ηsp / C of this product was 4.0 dl / g.

[Polymeric acid solution polymerization example 3]
(Preliminary dispersion of inorganic particles)
7.6 parts by weight of amorphous silica spherical particle Seahoster KE-P10 (manufactured by Nippon Shokubai Co., Ltd.), 390 parts by weight of N-methyl-2-pyrrolidone, the liquid contact part of the container, and the infusion pipe are austenitic stainless steel SUS316L And stirred for 1 minute at a rotation speed of 1000 rpm with a homogenizer T-25 basic (manufactured by IKA Labortechnik) to obtain a preliminary dispersion.
(Preparation of polyamic acid solution)
The liquid contact part of the vessel equipped with a nitrogen introduction tube, a thermometer, a stirring rod, and the pipe for infusion were substituted with nitrogen in the reaction vessel made of austenitic stainless steel SUS316L, and then 200 parts by mass of diaminodiphenyl ether was added. Next, after 3800 parts by mass of N-methyl-2-pyrrolidone was added and completely dissolved, 390 parts by mass and 217 parts by mass of pyromellitic dianhydride were added to the preliminary dispersion obtained above. When the mixture was stirred at 0 ° C. for 5 hours, a brown viscous polyamic acid solution C was obtained. The reduced viscosity (ηsp / C) was 3.7 dl / g.

[Polymeric acid solution polymerization example 4]
(Preliminary dispersion of inorganic particles)
3.7 parts by mass of amorphous silica spherical particles Seahoster KE-P10 (manufactured by Nippon Shokubai Co., Ltd.), 420 parts by mass of N-methyl-2-pyrrolidone, and the infusion part are austenitic stainless steel SUS316L And stirred for 1 minute at a rotation speed of 1000 rpm with a homogenizer T-25 basic (manufactured by IKA Labortechnik) to obtain a preliminary dispersion.
(Preparation of polyamic acid solution)
The wetted part of the vessel equipped with a nitrogen introduction tube, a thermometer, and a stirring rod, and the infusion piping were substituted with nitrogen in the reaction vessel made of austenitic stainless steel SUS316L, and then 108 parts by mass of phenylenediamine was added. Next, after 3600 parts by mass of N-methyl-2-pyrrolidone was added and completely dissolved, 420 parts by mass and 292.5 parts by mass of diphenyltetracarboxylic dianhydride were added to the preliminary dispersion obtained above. When the mixture was stirred at 25 ° C. for 12 hours, a brown viscous polyamic acid solution D was obtained. The reduced viscosity (ηsp / C) was 4.5 dl / g.

[Production Examples 1 to 4 of polyimide film]
The polyamic acid solution obtained in Polymerization Examples 1 to 4 was coated on a non-slip material surface of polyethylene terephthalate film A-4100 (manufactured by Toyobo Co., Ltd.) using a comma coater (gap: 650 μm, coating) (Width 1240 mm) and passed through a continuous drying furnace having four drying zones and dried under the following predetermined conditions.
Zone 1 Upper temperature 105 ° C, Lower temperature 110 ° C
Air volume 20 cubic m / min for both top and bottom Zone 2 Upper temperature 110 ° C, Lower temperature 110 ° C
Air volume 30 cubic m / min for both top and bottom Third zone Upper temperature 110 ° C, Lower temperature 110 ° C
Air volume 20 cubic m / min for both top and bottom Zone 4 Upper temperature 110 ° C, Lower temperature 110 ° C
Upper air volume 15 cubic m / min, lower air volume 20 cubic m / min The length of each zone is the same, and the total drying time is 15 minutes.
The air volume is the sum of the air volumes from the outlets for each zone.
The polyamic acid film that became self-supporting after drying was peeled off from the polyester film, and both ends were cut to obtain respective green films having a thickness of 39 μm and a width of 1200 mm.
The obtained green film was passed through a continuous heat treatment furnace purged with nitrogen while holding both ends with a pin tenter. As the second stage, two stages of heating were performed at 400 ° C. for 5 minutes to advance the imidization reaction. Then, it cooled to room temperature in 5 minutes, and the 25-micrometer-thick polyimide film which exhibits brown was obtained. Table 1 shows the characteristics of the obtained film. Shown in

[Production Example 5 of polyimide film]
A stainless steel belt obtained by polishing the polyamic acid solution obtained in Polymerization Example 2 to a thickness of 0.5 mm, a width of 750 mm, and a surface roughness of 0.005 μm was coated with a squeegee / belt gap of 680 μm, and three hot-air drying zones First zone Temperature: 105 ° C, Air volume: 10 cubic m / min Drying time: 4 minutes Second zone Temperature: 115 ° C, Air volume: 20 cubic m / min Drying time: 4 minutes Third zone Temperature: 110 ° C., temperature: 25 cubic m / min Drying time: dried for 4 minutes. The polyamic acid film which became self-supporting after drying was peeled from the stainless steel belt to obtain a green film having a thickness of 39 μm.
The obtained green film was passed through a continuous heat treatment furnace purged with nitrogen, the first stage was heated at 180 ° C. for 3 minutes, and the heating rate was 4 ° C./second, and the second stage was at 460 ° C. for 2 minutes. The imidation reaction was allowed to proceed by applying two stages of heating under the conditions described above. Then, it cooled to room temperature in 5 minutes, and the 25-micrometer-thick polyimide film which exhibits brown was obtained. Table 1 shows the characteristics of the obtained film. Shown in

[Production Examples 6 to 9 of polyimide film]
A stainless steel belt obtained by polishing the polyamic acid solution obtained in Polymerization Examples 1 to 4 to a thickness of 0.5 mm, a width of 750 mm, and a surface roughness of 0.005 μm was coated with a squeegee / belt gap of 680 μm, and three hot-air types First zone Temperature: 110 ° C., Air volume: 10 cubic m / min Drying time: 2 minutes Second zone Temperature: 130 ° C., Air volume: 25 cubic m / min Drying time: 2 minutes 3 zones Temperature: 135 ° C., temperature: 25 cubic m / min Drying time: dried for 2 minutes. The polyamic acid film which became self-supporting after drying was peeled from the stainless steel belt to obtain a green film having a thickness of 36 μm.
The obtained green film was passed through a continuous heat treatment furnace purged with nitrogen, the first stage was heated at 180 ° C. for 3 minutes, and the heating rate was 4 ° C./second, and the second stage was at 460 ° C. for 2 minutes. The imidation reaction was allowed to proceed by applying two stages of heating under the conditions described above. Then, it cooled to room temperature in 5 minutes, and the 25-micrometer-thick polyimide film which exhibits brown was obtained. The properties of the obtained film are shown in Table 1.

「反り」は、カール度測定時の常温（加熱なし）で評価した値である。

“Warpage” is a value evaluated at normal temperature (no heating) at the time of curl degree measurement.

Using the polyimide film obtained in each of the above examples and comparative examples as an insulating substrate, a tape carrier type semiconductor package having a minimum wiring pitch of 40 μm or less was prepared as described below.
A display device using a liquid crystal display panel (element) that receives a drive signal through each tape carrier type semiconductor package thus obtained was prototyped, and the display device using each film was evaluated.
<Production of tape carrier type semiconductor package and connection with display element>
The outline of the production of the tape carrier type semiconductor package and the connection with the display panel (element) will be described below.

Each film was cut into a 50 cm × 200 cm square and fixed by being sandwiched between stainless steel frames having openings. Next, plasma treatment of the film surface was performed. The plasma treatment conditions were a xenon gas, a frequency of 13.56 MHz, an output of 100 W, a gas pressure of 0.8 Pa, a treatment temperature of 25 ° C., and a treatment time of 5 minutes. Next, using a nickel-chromium (3 mass%) alloy target under conditions of a frequency of 13.56 MHz, an output of 400 W, a gas pressure of 0.8 Pa, and a thickness of 10 mm / sec by RF sputtering in an argon atmosphere. An 80-mm nickel-chromium alloy film (underlayer) was formed, and then the temperature of the substrate was raised to 250 ° C., and copper was deposited at a rate of 100 k / sec to form a 0.3 μm thick copper thin film. The obtained copper thin film forming film is fixed to a plastic frame, and a copper sulfate plating bath is used to form a thick copper plating layer (thickening layer) having a thickness of 5 μm, followed by heat treatment at 300 ° C. for 10 minutes. The intended metallized polyimide film was obtained. Using the obtained metallized polyimide film, photoresist: FR-200, manufactured by Shipley Co., Ltd. was applied and dried, then contacted and exposed with a glass photomask, and further developed with a 1.2% by mass aqueous KOH solution. Next, etching is performed with a cupric chloride etching line containing HCl and hydrogen peroxide at 40 ° C. and a spray pressure of ² kgf / cm ² to form a pattern with a minimum wiring pitch of 30 μm, and then to a thickness of 0.5 μm. Electrolytic tin plating was performed, and then an annealing treatment was performed at 125 ° C. for 1 hour to prepare a substrate of each film.

A semiconductor chip for driving was mounted face-down on each film substrate. The bump is formed by electrolytic plating by opening an area formed by a photoresist. After formation, the photoresist is removed. This bump is connected to the electrode of the film substrate by gold-tin eutectic bonding. The connection condition in this case is that a load of 13 kg is applied from the semiconductor chip side with a tool of 440 ° C. and held for 2 seconds.
Semiconductor chip mounting methods include not only gold-tin eutectic connection but also gold-gold thermocompression bonding, ultrasonic connection, anisotropic conductive film, NCP, and the like, and the connection method may be appropriately selected and used.
As other mounting parts, chip resistors, capacitors, package ICs, coils, connectors, and the like are connected by soldering or the like to produce each tape carrier type semiconductor package.
Each tape carrier type semiconductor package is mounted on a 14 inch TFT full color liquid crystal display panel. An anisotropic conductive film is attached to the terminal portion of the display panel, aligned with each tape carrier type semiconductor package substrate, and maintained at the normal temperature or a temperature at which the anisotropic conductive film does not cure. After that, by adding the curing temperature condition of the resin of the anisotropic conductive film and the load condition that the connecting particles of the anisotropic conductive film are crushed and contacted, the display panel and each tape carrier type semiconductor package are connected, A display device using a tape carrier type semiconductor package was produced (FIG. 4).
In addition, temporary attachment can also be abbreviate | omitted.

<Evaluation of display devices>
The connection reliability and heat cycle durability of the obtained display panel were evaluated.
Connection reliability: A drive signal was given to each display panel, a test pattern was displayed, and the presence or absence of connection failure was inspected. The result is shown in Table 2 as the connection failure rate.
A non-defective display panel that did not show poor connection in the inspection was subjected to a temperature cycle test of −25 ° C. to + 60 ° C. (30 minutes each) for 100 cycles, and a test pattern was displayed on the display panel after the test. The presence or absence was inspected and the result was The connection failure rate after C is shown in Table 2.

  As described above, the insulating material of the tape carrier type semiconductor package of the present invention is a film having a curl degree of 10% or less at 300 ° C., particularly an aromatic diamine having a benzoxazole structure and an aromatic tetracarboxylic acid anhydride. A display device using a driving unit which is a polyimide film having a linear expansion coefficient of 2 to 15 ppm / ° C. mainly composed of polyimide benzoxazole obtained by reacting with a substance is specifically a thin television or a wall-mounted television. John, handheld television, stationary personal computer display unit, mobile personal computer, portable display device, acoustic device display unit, portable music player display unit, in-vehicle amusement device display unit, portable communication Device display, for example, mobile phones, mobile vehicles such as automobiles, ships, aircraft Display unit in any cockpit, display unit of car navigation system, guidance display in public transportation, advertisement, public relations media, wristwatch, head mounted display, video camera, digital still camera, etc., electronic dictionary, PDA, electronic notebook, GPS, Portable game machine, portable karaoke machine, toy display, digital and silver salt camera display and status display / control display, computer display, TV monitor status display / control display, wristwatch, A watch other than a wristwatch that uses an electronic display device. Remote control display for various home appliances, refrigerator, washing machine, microwave oven, electric kettle, jar pot, dishwasher, electric refrigerator, cooking heater, ventilation fan, electric water heater, natural refrigerant heat pump water heater, household electric well For home appliances such as pumps, air purifiers, electric washing machines, washing machines (fully automatic / two-tank type), washing / drying machines, vacuum cleaners, warm water washing toilet seats, electric razors, household garbage processing machines, coolers, etc. Display unit, display unit of electric lighting equipment, video recorder, DVD recorder, HD recorder, stereo, home theater system, display unit of AV equipment such as radio, display unit of office equipment such as copier, printer, FAX, telephone, printer CD drive, FD drive, MO drive, DVD drive, hard disk, IC card, magnetic card, Display of display units such as credit cards, memory peripherals such as memory card readers / writers, modems, routers, hubs, etc., and display units of computer bodies, doorphones, fire alarm systems, gas detection, security systems, etc. Health promotion equipment display such as department, health meter, blood pressure measuring instrument, electric massage instrument, etc., civil engineering machinery, mining machinery, chemical machinery and storage tank, pulp / paper making machinery, plastic processing machinery, pump, compressor and blower , Hydraulic machinery and pneumatic equipment, power transmission equipment, agricultural machinery and wood processing machinery, metal machine tools, metal processing machinery and casting equipment, food processing machinery, packaging machinery and packing machinery, sewing and textile machinery, refrigerators and Refrigerator application products, vending machines, automatic ticket gates, automatic entrance , Rotating electrical machines, stationary electrical machinery and equipment, switching control equipment, semiconductor-related, home appliances-related, production equipment in various industries such as automobiles, display parts of machine tools, electronic exchanges, digital transmission equipment, display parts in communication equipment, It can be applied with high durability and accuracy to display units and display devices in equipment and facilities used in terminal equipment such as automatic teller machines (including payment machines), electrical measuring instruments and electronic applied equipment, and measuring equipment.

It is the schematic diagram which showed the measuring method of the curl degree of a film. (A) is a top view, (b) is a sectional view indicated by aa in (a) before hot air treatment, and (c) is indicated by aa in (a) after hot air treatment. It is sectional drawing. It is the figure explaining the outline of the manufacturing process of a tape carrier type semiconductor package. The IC chip indicates a semiconductor chip. It is the figure which represented typically the X-ray-diffraction pole figure of the polyimide film. The outline of the connection of a display panel and a tape carrier type semiconductor package is shown.

Explanation of symbols

(References in FIG. 1 below)
1. 1. (Polyimide) film test piece Alumina / Ceramic plate (Reference in Fig. 2)
1. 1. Base film Copper foil Through-hole plated copper 4. 4. Etching resist Solder resist IC chip 7. Sealing material (reference numeral in FIG. 4 below)
1. Liquid crystal display panel 2. Tape base material 3. Anisotropic conductive film 4. Driver IC chip ITO wiring

Claims (6)

  A display device using a direct-view thin display element that receives a drive signal via a tape carrier type semiconductor package, wherein the insulating substrate of the tape carrier type semiconductor package is a polyimide film having a curl degree of 10% or less at 300 ° C. A display device having a minimum wiring pitch of 40 μm or less.   The display device according to claim 1, wherein the display element is a liquid crystal display element.   The display device according to claim 1, wherein the liquid crystal display element is at least one display element selected from TN liquid crystal, STN liquid crystal, ferroelectric liquid crystal, guest-host liquid crystal, and cholesteric liquid crystal.   The display element is selected from an EL display element, an electrophoretic display element, an electrochromic display element, an oxidation-reduction display element, a rotating sphere type or rotating cylindrical display element, and a display type display element by movement of dry powder. The display device according to claim 1, wherein the display device is at least one type of display element.   Polyimide film having a linear expansion coefficient of 2 to 15 ppm / ° C. mainly composed of polyimide benzoxazole obtained by reacting an aromatic diamine having an benzoxazole structure with an aromatic tetracarboxylic acid anhydride. The display device according to claim 1.   The insulating substrate has a plane orientation coefficient of 0.75 or more, which is mainly composed of polyimide benzoxazole obtained by reacting an aromatic diamine having a benzoxazole structure and an aromatic tetracarboxylic anhydride, The display device according to claim 1, which is a polyimide film having an elastic modulus of 5 GPa or more and a tensile breaking strength of 300 MPa or more.