JP2007141418A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2007141418A5 JP2007141418A5 JP2005337814A JP2005337814A JP2007141418A5 JP 2007141418 A5 JP2007141418 A5 JP 2007141418A5 JP 2005337814 A JP2005337814 A JP 2005337814A JP 2005337814 A JP2005337814 A JP 2005337814A JP 2007141418 A5 JP2007141418 A5 JP 2007141418A5
- Authority
- JP
- Japan
- Prior art keywords
- film
- optical recording
- recording medium
- target
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
この発明は、光記録媒体の製造方法ならびにそれに用いられるターゲットおよびその製造方法に関する。詳しくは、無機記録膜を有する光記録媒体の製造方法に関する。 The present invention relates to a method for manufacturing an optical recording medium, a target used therefor, and a method for manufacturing the target. Specifically, the present invention relates to a method for manufacturing an optical recording medium having an inorganic recording film.
近年、情報信号の高密度記録可能な光記録媒体が望まれている。例えば、この要求に応えるために、ブルーレイディスク(Blu-ray Disc(登録商標)、以下BD)の規格が策定され、ハイビジョン画像を光記録媒体に録画、保存することが可能となっている。 In recent years, optical recording media capable of recording information signals at high density have been desired. For example, in order to meet this requirement, a Blu-ray Disc (registered trademark) (hereinafter referred to as BD) standard has been established, and high-definition images can be recorded and stored on an optical recording medium.
このBDに代表される高記録密度の光記録媒体には、再生専用型光記録媒体、書き換え型光記録媒体、追記型光記録媒体の規格があるが、これらのうち、追記型光記録媒体は特に安価であることが望まれる。また、高密度記録の追記型光記録媒体の記録膜を有機材料で作製することは困難であるため、特性面で有利な無機材料を用いて記録膜を作製することが望まれている(例えば特許文献1参照)。 High recording density optical recording media represented by this BD include standards for read-only optical recording media, rewritable optical recording media, and write-once optical recording media. Among these, write-once optical recording media are In particular, it is desired to be inexpensive. Further, since it is difficult to produce a recording film of a write-once optical recording medium for high-density recording with an organic material, it is desired to produce a recording film using an inorganic material advantageous in terms of characteristics (for example, Patent Document 1).
これらの2つの要求に応えるためには、記録膜材料として無機材料を用いた追記型光記録媒体を安価に製造することが必要になるが、そのためには、記録膜の膜総数を少なくし、且つ、総膜厚を薄くすることが好ましい。これは、膜総数が少なければスパッタ室を少なくして設備投資費用を抑えることができ、また、総膜厚が薄ければ材料費を安く抑えることができるためである。 In order to meet these two requirements, it is necessary to inexpensively manufacture a write-once optical recording medium using an inorganic material as a recording film material. For this purpose, the total number of recording films is reduced, In addition, it is preferable to reduce the total film thickness. This is because if the total number of films is small, the number of sputtering chambers can be reduced to reduce the capital investment cost, and if the total film thickness is thin, the material cost can be reduced.
本発明者らは、上述の要求に応える光記録媒体として、Ge酸化物膜と、金属膜とを隣接させた構成を有するものを検討している。この光記録媒体の記録原理は、400〜410nmの光を入射すると、光触媒効果によりGe酸化物膜の酸素が分離し、金属膜側の酸素濃度が高くなり、光学定数が大きく変化する。これにより、変調度の大きな再生信号が得られ、安定して良好な記録特性の得られる光記録媒体を実現できる。この光記録媒体は、例えば、チタン合金膜、Ge酸化物膜、および保護膜としての誘電体膜のみ基板に積層するだけの簡単な構成を有するので、膜層数、総膜厚を書き換え型記録媒体よりもはるかに少なくし、媒体をより安価に製造できる。 The present inventors are examining an optical recording medium that meets the above-described requirements, which has a configuration in which a Ge oxide film and a metal film are adjacent to each other. The recording principle of this optical recording medium is that when light of 400 to 410 nm is incident, oxygen in the Ge oxide film is separated by the photocatalytic effect, the oxygen concentration on the metal film side becomes high, and the optical constant changes greatly. As a result, it is possible to realize an optical recording medium in which a reproduction signal having a large modulation degree is obtained and stable recording characteristics can be obtained. This optical recording medium has a simple configuration in which, for example, only a titanium alloy film, a Ge oxide film, and a dielectric film as a protective film are stacked on the substrate, so that the number of film layers and the total film thickness can be rewritten. It is much less than the medium, and the medium can be manufactured cheaper.
Ge酸化物膜の成膜は、Arガスなどのプロセスガス中に酸素ガスを混合させながら、リアクティブスパッタ法により、一般に入手できるGeターゲットをスパッタリングして成膜することができる。しかし、本発明者らの知見によれば、この成膜方法には、Geターゲット表面の酸化状態によって成膜されるGe酸化物膜の膜特性が変化しやすく、成膜前にプリスパッタしなければ安定しないという問題がある。すなわち、実験レベルでは安定な特性が得られるが、量産レベルでは安定な特性が得られないという問題がある。 The Ge oxide film can be formed by sputtering a commonly available Ge target by reactive sputtering while mixing oxygen gas in a process gas such as Ar gas. However, according to the knowledge of the present inventors, in this film formation method, the film characteristics of the Ge oxide film formed easily change depending on the oxidation state of the Ge target surface, and pre-sputtering must be performed before the film formation. There is a problem that it is not stable. In other words, stable characteristics can be obtained at the experimental level, but stable characteristics cannot be obtained at the mass production level.
また、本発明者らの知見によれば、広いパワーマージンを得るためには、金属膜を窒化することが有効である。この金属膜の成膜も、Arガスなどのプロセスガス中に窒素を混合させながら、一般に入手できる金属ターゲットをスパッタリングして成膜することができる。しかし、本発明者らが検討している光記録媒体は、窒素流量依存性が大きく、量産時の変動に対して十分な製造マージンを有しない。 Further, according to the knowledge of the present inventors, it is effective to nitride a metal film in order to obtain a wide power margin. This metal film can also be formed by sputtering a generally available metal target while mixing nitrogen in a process gas such as Ar gas. However, the optical recording medium studied by the present inventors is highly dependent on the nitrogen flow rate and does not have a sufficient manufacturing margin against fluctuations during mass production.
したがって、この発明の目的は、無機記録膜を有する光記録媒体を、より簡易に特性の劣化を招くことなく量産することができる光記録媒体の製造方法ならびターゲットおよびその製造方法を提供することにある。 Accordingly, an object of the present invention is to provide an optical recording medium manufacturing method, a target, and a manufacturing method thereof, which can easily mass-produce an optical recording medium having an inorganic recording film without causing deterioration of characteristics. is there.
上述の課題を解決するために、第1の発明は、無機記録膜を有する光記録媒体の製造方法であって、
金属からなる隣接膜を成膜する工程と、
Geの酸化物からなる酸化物膜を成膜する工程と
を備え、
酸化物膜および隣接膜の成膜工程では、酸化物膜と隣接膜とは隣接するように成膜され、
酸化物膜の成膜工程では、GeおよびGe酸化物の混合物ターゲットをスパッタリングすることにより酸化物膜を成膜し、
酸化物膜の吸収係数kが、0.15≦k≦0.90であることを特徴とする光記録媒体の製造方法である。
In order to solve the above-mentioned problem, a first invention is a method for manufacturing an optical recording medium having an inorganic recording film,
Forming an adjacent film made of metal;
Forming an oxide film made of Ge oxide,
In the step of forming the oxide film and the adjacent film, the oxide film and the adjacent film are formed so as to be adjacent to each other,
In the oxide film forming step, an oxide film is formed by sputtering a mixture target of Ge and Ge oxide,
The method of manufacturing an optical recording medium is characterized in that an absorption coefficient k of the oxide film is 0.15 ≦ k ≦ 0.90.
第2の発明は、半導体の非飽和酸化物からなるスパッタリングターゲットであって、
少なくともGe粉末およびGe酸化物粉末とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタリングターゲットである。
A second invention is a sputtering target made of a semiconductor unsaturated oxide,
A sputtering target obtained by mixing at least a Ge powder and a Ge oxide powder and firing the mixture under pressure.
第3の発明は、半導体の非飽和酸化物からなるスパッタリングターゲットの製造方法であって、
少なくともGe粉末およびGe酸素物粉末とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタリングターゲットの製造方法である。
A third invention is a method of manufacturing a sputtering target comprising a semiconductor unsaturated oxide,
A method for producing a sputtering target, comprising mixing at least a Ge powder and a Ge oxygen powder, and pressurizing and firing the mixture.
第4の発明は、Tiの非飽和窒化物からなるスパッタリングターゲットであって、
少なくともTi金属粉末とTi窒化物粉末とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタリングターゲットである。
A fourth invention is a sputtering target made of unsaturated nitride of Ti,
A sputtering target comprising: mixing at least Ti metal powder and Ti nitride powder, and pressurizing and firing the mixture.
第5の発明は、Tiの非飽和窒化物からなるスパッタリングターゲットの製造方法であって、
少なくともTi金属粉末とTi窒化物粉末とを混合し、該混合物を加圧焼成することを特徴とするスパッタリングターゲットの製造方法である。
A fifth invention is a method of manufacturing a sputtering target made of an unsaturated nitride of Ti,
A sputtering target manufacturing method comprising mixing at least a Ti metal powder and a Ti nitride powder, and firing the mixture under pressure.
第6の発明は、Tiの非飽和窒化物からなるスパッタターゲットであて、
少なくともTi粉末と、Si粉末と、Ti窒化物粉末およびSi窒化物粉末のうち少なくとも一方とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタターゲットである。
A sixth invention is a sputter target made of unsaturated nitride of Ti,
A sputter target obtained by mixing at least Ti powder, Si powder, and at least one of Ti nitride powder and Si nitride powder, and firing the mixture under pressure.
第7の発明は、Tiの非飽和窒化物からなるスパッタリングターゲットの製造方法であって、
少なくともTi粉末と、Si粉末と、Ti窒化物粉末およびSi窒化物粉末のうち少なくとも一方の粉末とを混合し、該混合物を加圧焼成することを特徴とするスパッタリングターゲットの製造方法である。
A seventh invention is a method of manufacturing a sputtering target made of an unsaturated nitride of Ti,
A sputtering target manufacturing method comprising mixing at least a Ti powder, a Si powder, and at least one of a Ti nitride powder and a Si nitride powder, and firing the mixture under pressure.
第8の発明は、少なくともSiおよびTiを含有するターゲットであって、
Siの含有量が、8原子%以上32原子%以下であることを特徴とするスパッタリングターゲットである。
The eighth invention is a target containing at least Si and Ti,
The sputtering target is characterized in that the Si content is 8 atomic% or more and 32 atomic% or less.
以上説明したように、この発明によれば、無機記録膜を有する光記録媒体を、より簡易に特性の劣化を招くことなく量産することができる。 As described above, according to the present invention, an optical recording medium having an inorganic recording film can be mass-produced more easily without causing deterioration of characteristics.
以下、この発明の実施形態について図面を参照しながら説明する。なお、以下の実施形態の全図においては、同一または対応する部分には同一の符号を付す。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. In all the drawings of the following embodiments, the same or corresponding parts are denoted by the same reference numerals.
(1)第1の実施形態
光記録媒体の構成
図1は、この発明の第1の実施形態による光記録媒体の一構成例を示す概略断面図である。この光記録媒体10は、基板1上に、無機記録膜6、第1の誘電体膜4a、第2の誘電体膜4b、光透過層5が順次積層された構成を有する。
(1) First embodiment
Configuration of Optical Recording Medium FIG. 1 is a schematic sectional view showing a configuration example of an optical recording medium according to the first embodiment of the present invention. This
この第1の実施形態による光記録媒体10では、光透過層5の側からレーザ光を無機記録膜6に照射することにより、情報信号の記録または再生が行われる。例えば、400nm以上410nm以下の範囲の波長を有するレーザ光を、0.84以上0.86以下の範囲の開口数を有する対物レンズにより集光し、光透過層5の側から無機記録膜6に照射することにより、情報信号の記録または再生が行われる。このような光記録媒体10としては、例えば追記型のBDが挙げられる。
以下、光記録媒体10を構成する基板1、無機記録膜6、第1の誘電体膜4a、第2の誘電体膜4bおよび光透過層5について順次説明する。
In the
Hereinafter, the
(基板)
基板1は、中央に開口(以下、センターホールと称する)が形成された円環形状を有する。この基板1の一主面は、凹凸面11となっており、この凹凸面11上に無機記録膜6が成膜される。以下では、基板1の一主面に対して窪んだ凹部をイングルーブ11G、基板1の一主面に対して突出した凸部をオングルーブ11Lと称する。
(substrate)
The
このイングルーブ11Gおよびオングルーブ11Lの形状としては、例えば、スパイラル状、同心円状などの各種形状が挙げられる。また、イングルーブ11Gおよび/またはオングルーブ11Lが、アドレス情報を付加するためのウォブル(蛇行)されている。
Examples of the shapes of the in-
基板1の直径は、例えば120mmに選ばれる。基板1の厚さは、剛性を考慮して選ばれ、好ましくは0.3mm以上1.3mm以下から選ばれ、より好ましくは0.6mm以上1.3mm以下から選ばれ、例えば1.1mmに選ばれる。また、センタホールの径(半径)は、15mmに選ばれる。
The diameter of the
基板1の材料としては、例えばポリカーボネート系樹脂、ポリオレフィン系樹脂若しくはアクリル系樹脂などのプラスチック材料、またはガラスなどを用いることができる。なお、コストを考慮した場合には、基板1の材料として、プラスチック材料を用いることが好ましい。
As the material of the
(無機記録膜)
無機記録膜6は、基板1の凹凸面11上に順次積層された金属膜2および酸化物膜3からなる。金属膜2は、例えばTiまたはTiおよび添加物から構成される。Tiを主たる材料とすれば基本的に良好な記録特性を得ることができる。添加物は、光学特性、耐久性または記録感度などを向上させるためのものであり、このような添加物としては、例えばAl,Ag,Cu,Pd,Ge,Si,Sn,Ni,Fe,Mg,V,C,Ca,B,Cr,Nb,Zr,S,Se,Mn,Ga,Mo,W,Tb,Dy,Gd,Nd,Zn,Ta,Srからなる群より選ばれた1種以上を用いることができ、具体的には例えばTi,Al,TiSi,TiSiNを用いることができる。具体的には例えば、反射率を高めるための添加物としては、Alが好ましい。
(Inorganic recording film)
The
また、金属膜2を構成する材料としては、Tiの酸化物およびTiと添加物との酸化物を用いることもできる。このような酸化物としては、例えばTiSiOを挙げることができる。
Further, as a material constituting the
酸化物膜3は、例えば、ゲルマニウムの酸化物であるGeOからなる。酸化物膜3の吸収係数kは、好ましくは0.15以上0.90以下、より好ましくは0.20以上0.70以下、更により好ましくは0.25以上0.60以下の範囲である。0.15以上0.90以下の範囲を満たすことで、例えば良好な変調度およびキャリア対ノイズ比(以下、C/N比)を得ることができる。0.20以上0.70以下の範囲を満たすことで、例えばより良好な変調度およびC/N比を得ることができる。0.25以上0.60以下の範囲を満たすことで、例えば更により良好な変調度およびC/N比を得ることができる。
The
なお、この明細書における吸収係数は波長410nmにおけるものである。また、その測定には、エリプソメータ(ルドルフ社製、商品名:Auto EL-462P17)を用いた。 The absorption coefficient in this specification is at a wavelength of 410 nm. For the measurement, an ellipsometer (manufactured by Rudolf, trade name: Auto EL-462P17) was used.
また、酸化物膜3の膜厚は、好ましくは10nm以上35nm以下の範囲である。また、酸化物膜3に対して添加物を加えるようにしてもよく、この添加物としては、例えばTe,Pd,Pt,Cu,Zn,Au,Ag,Si,Ti,Fe,Ni,Sn,Sbなどを用いることができる。このような添加物を加えることで、耐久性および/または反応性(記録感度)を向上することができる。なお、耐久性を向上させるためには、特にPd,Pt,Si,Sbが特に好ましい。
The thickness of the
(誘電体膜)
第1の誘電体膜4aおよび第2の誘電体膜4bは、無機記録膜6上に積層されて、無機記録膜6の光学的、機械的保護、すなわち耐久性の向上や、記録時の無機記録膜6の変形、すなわちふくらみの抑制等を行うためのものである。
(Dielectric film)
The first dielectric film 4 a and the second dielectric film 4 b are laminated on the
第1の誘電体膜4aは、例えばZnS−SiO2より構成される。この第1の誘電体膜4aの厚さは、好ましくは10nm以上58nm以下、より好ましくは23nm以上53nm以下の範囲とされる。膜厚を10nm以上にすることで、良好なジッターを得ることができる。例えば光記録媒体10がBD−Rである場合には、膜厚を10nm以上にすることで、BD−Rの規格であるジッター6.5%以下を満足することができる。一方、膜厚を58nm以下にすることで、良好な反射率を得ることができる。例えば光記録媒体10がBD−Rである場合には、膜厚を58nm以下にすることで、BD−Rの規格で要求される反射率12%以下を満足することができる。
また、膜厚を23nm以上にすることで、より良好なジッターを得ることができる。一方、膜厚を53nm以下にすることで、より良好な反射率を得ることができる。
The first dielectric film 4a is made of, for example, ZnS—SiO 2 . The thickness of the first dielectric film 4a is preferably in the range of 10 nm to 58 nm, more preferably in the range of 23 nm to 53 nm. By setting the film thickness to 10 nm or more, good jitter can be obtained. For example, when the
Further, when the film thickness is 23 nm or more, better jitter can be obtained. On the other hand, when the film thickness is 53 nm or less, a better reflectance can be obtained.
第2の誘電体膜4bは、例えばSiNより構成される。この第2の誘電体膜4bの厚さは、好ましくは35nm以下の範囲から選ばれる。膜厚を35nm以下にすることで、良好なジッターを得ることができる。例えば光記録媒体10がBD−Rである場合には、膜厚を35nm以下にすることで、BD−Rの規格であるジッター6.5%以下を満足することができる。また、上述のように、第1の誘電体層4aと第2の誘電体層4bとを積層することで、変調度を大きくでき、且つ、キャリア対ノイズ比(以下、C/N)を高くできる。
The second dielectric film 4b is made of, for example, SiN. The thickness of the second dielectric film 4b is preferably selected from the range of 35 nm or less. By setting the film thickness to 35 nm or less, good jitter can be obtained. For example, when the
(光透過層)
光透過層5は、例えば、円環形状を有する光透過性シート(フィルム)と、この光透過性シートを基板1に対して貼り合わせるための接着層とから構成される。接着層は、例えば紫外線硬化樹脂または感圧性粘着剤(PSA:Pressure Sensitive Adhesive)からなる。光透過層5の厚さは、好ましくは10μm以上177μm以下の範囲内から選ばれ、例えば100μmに選ばれる。このような薄い光透過層5と、例えば0.85程度の高NA(numerical aperture)化された対物レンズとを組み合わせることによって、高密度記録を実現することができる。
(Light transmission layer)
The
光透過性シートは、記録および/または再生に用いられるレーザ光に対して、吸収能が低い材料からなることが好ましく、具体的には透過率90パーセント以上の材料からなることが好ましい。光透過性シートの材料としては、例えばポリカーボネート樹脂材料、ポリオレフィン系樹脂(例えばゼオネックス(登録商標))が挙げられる。 The light-transmitting sheet is preferably made of a material having a low absorption ability with respect to laser light used for recording and / or reproduction, specifically, a material having a transmittance of 90% or more. Examples of the material for the light transmissive sheet include polycarbonate resin materials and polyolefin resins (for example, ZEONEX (registered trademark)).
また、光透過性シートの厚さは、好ましくは0.3mm以下に選ばれ、より好ましくは3以上177μm以下の範囲内から選ばれる。また、光透過層5の内径(直径)は、例えば22.7mmに選ばれる。
Further, the thickness of the light transmissive sheet is preferably selected to be 0.3 mm or less, more preferably from 3 to 177 μm. The inner diameter (diameter) of the
光記録媒体の製造方法
次に、この発明の第1の実施形態による光記録媒体の製造方法について説明する。
(基板の成形工程)
まず、一主面に凹凸面11が形成された基板1を成形する。基板1の成形の方法としては、例えば射出成形(インジェクション)法、フォトポリマー法(2P法:Photo Polymerization)などを用いることができる。
Method for Manufacturing Optical Recording Medium Next, a method for manufacturing an optical recording medium according to the first embodiment of the present invention will be described.
(Substrate molding process)
First, the board |
(金属膜の成膜工程)
次に、基板1を、例えばTi窒化物からなるターゲットが備えられた真空チャンバ内に搬送し、真空チャンバ内を所定の圧力になるまで真空引きする。その後、真空チャンバ内にプロセスガスを導入しながら、ターゲットをスパッタリングして、基板1上に金属膜2を成膜する。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.1〜0.6Pa
投入電力:1〜3kW
ガス種:Arガス
ガス流量:10〜40sccm
(Metal film formation process)
Next, the
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.1-0.6Pa
Input power: 1-3kW
Gas type: Ar gas Gas flow rate: 10-40 sccm
(酸化物膜の成膜工程)
次に、基板1を、例えばGe酸化物からなるターゲットが備えられた真空チャンバ内に搬送し、真空チャンバ内を所定の圧力になるまで真空引きする。その後、真空チャンバ内にプロセスガスを導入しながら、ターゲットをスパッタリングして、基板1上に酸化物膜3を成膜する。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.1〜0.6Pa
投入電力:1〜3kW
ガス種:Arガス
Arガス流量:10〜80sccm
(Oxide film deposition process)
Next, the
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.1-0.6Pa
Input power: 1-3kW
Gas type: Ar gas Ar gas flow rate: 10-80 sccm
(第1の誘電体膜の成膜工程)
次に、基板1を、例えばZnS−SiO2からなるターゲットが備えられた真空チャンバ内に搬送し、真空チャンバ内を所定の圧力になるまで真空引きする。その後、真空チャンバ内にプロセスガスを導入しながら、ターゲットをスパッタリングして、基板1上に第1の誘電体膜4aを成膜する。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.1〜0.6Pa
投入電力:1〜5kW
ガス種:Arガス
Arガス流量:6sccm
(First dielectric film forming step)
Next, the
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.1-0.6Pa
Input power: 1-5kW
Gas type: Ar gas Ar gas flow rate: 6 sccm
(第2の誘電体膜の成膜工程)
次に、基板1を、例えばSiからなるターゲットが備えられた真空チャンバ内に搬送し、真空チャンバ内を所定の圧力になるまで真空引きする。その後、真空チャンバ内にプロセスガスを導入しながら、ターゲットをスパッタリングして、基板1上に第2の誘電体膜4bを成膜する。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.1〜0.6Pa
投入電力:1〜4kW
ガス種:Arガスおよび窒素ガス
Arガス流量:50sccm
窒素ガス流量:37sccm
(Second dielectric film forming step)
Next, the
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.1-0.6Pa
Input power: 1-4kW
Gas type: Ar gas and nitrogen gas Ar gas flow rate: 50 sccm
Nitrogen gas flow rate: 37sccm
(光透過層の形成工程)
次に、円環形状の光透過性シートを、例えば、このシート一主面に予め均一に塗布された感圧性粘着剤(PSA)を用いて、基板1上の凹凸面11側に貼り合わせる。これにより、基板1上に積層された積層膜を覆うように、光透過層5が形成される。
以上の工程により、図1に示す光記録媒体10が得られる。
(Light transmission layer forming process)
Next, an annular light-transmitting sheet is bonded to the uneven surface 11 side on the
Through the above steps, the
ターゲットの構成
以下に、この発明の第1の実施形態によるターゲットの構成について説明する。まず、酸化物膜3を成膜するためのターゲットの構成について説明する。酸化物膜3を成膜するためのターゲットは、半導体粉末であるGe粉末と半導体酸化物粉末であるGe酸化物粉末との混合物を加圧焼成することによりなるものである。このターゲットは、例えば円盤形状を有し、その直径は、例えば200mmに選ばれ、厚さは、例えば6mmに選ばれる。
Target Configuration The following describes the target configuration according to the first embodiment of the present invention. First, the structure of the target for forming the
加圧焼成後の酸素の含有量は45原子%以上60原子%以下の範囲であることが好ましい。45原子%未満であると、吸収係数kが0.9を越えてしまうため、記録特性などが低下してしまう。また、60原子%を越えると、吸収係数が0.15未満になってしまうため、記録特性などが低下してしまう。 The oxygen content after pressure firing is preferably in the range of 45 atomic% to 60 atomic%. If it is less than 45 atomic%, the absorption coefficient k exceeds 0.9, so that the recording characteristics and the like deteriorate. On the other hand, if it exceeds 60 atomic%, the absorption coefficient becomes less than 0.15, so that the recording characteristics and the like deteriorate.
次に、金属膜2を成膜するためのターゲットの構成について説明する。金属膜2を成膜するためのターゲットは、遷移金属粉末であるTi粉末と遷移金属窒化物粉末であるTi窒化物粉末との混合物を加圧焼成することによりなるものである。このターゲットは、例えば円盤形状を有し、その直径は、例えば200mmに選ばれ、厚さは、例えば6mmに選ばれる。
Next, the structure of the target for forming the
加圧焼成後の窒素の含有量は1原子%以上20原子%以下の範囲であることが好ましく、1原子%以上10原子%以下の範囲であるこがより好ましい。1原子%以上20原子%以下の範囲にすることで、パワーマージンを大きくし、且つ、ジッターの上昇を抑えることができる。5原子%以上15原子%以下の範囲にすることで、パワーマージンをより大きくし、且つ、ジッターの上昇をより抑えることができる。 The nitrogen content after the pressure firing is preferably in the range of 1 atomic% to 20 atomic%, and more preferably in the range of 1 atomic% to 10 atomic%. By setting it in the range of 1 atomic% or more and 20 atomic% or less, the power margin can be increased and the increase in jitter can be suppressed. By setting it in the range of 5 atomic% or more and 15 atomic% or less, the power margin can be further increased and the increase in jitter can be further suppressed.
ここで、金属の非飽和酸化物は、金属のとりうる最大の価数に対応した化学量論組成より酸素含有量が少ない方向にずれた化合物のこと、すなわち金属の非飽和酸化物における酸素の含有量が、上記金属のとりうる最大価数に対応した化学量論組成の酸素含有量より小さい化合物のことである。 Here, the metal unsaturated oxide is a compound shifted in a direction in which the oxygen content is less than the stoichiometric composition corresponding to the maximum valence that the metal can take, that is, the oxygen in the metal unsaturated oxide. It is a compound whose content is smaller than the oxygen content of the stoichiometric composition corresponding to the maximum valence that the metal can take.
なお、非飽和酸化物もしくは非飽和窒化物としては、1種の非飽和酸化物もしくは非飽和窒化物のほかに、第2の元素あるいは更に複数種類の元素を添加したものについても本発明に含めることにする。 As the unsaturated oxide or unsaturated nitride, in addition to one kind of unsaturated oxide or unsaturated nitride, the addition of a second element or a plurality of other elements is also included in the present invention. I will decide.
ターゲットの製造方法
以下、この発明の第1の実施形態によるターゲットの製造方法について説明する。まず、酸化物膜3を成膜するためのターゲットの製造方法について説明する。
Target Manufacturing Method A target manufacturing method according to the first embodiment of the present invention will be described below. First, a method for manufacturing a target for forming the
(秤量・混合)
半導体粉末であるGe粉末と半導体酸化物粉末であるGe酸化物粉末とをそれぞれ所定量秤量した後、例えば混合乾式を行う。ここで、Ge粉末とGe酸化物粉末との混合比は、加圧焼成後の酸素の含有量が45原子%以上60原子%以下となるように調整することが好ましい。
(Weighing and mixing)
A predetermined amount of each of the Ge powder as the semiconductor powder and the Ge oxide powder as the semiconductor oxide powder is weighed, and then, for example, a mixed dry method is performed. Here, the mixing ratio of the Ge powder and the Ge oxide powder is preferably adjusted so that the oxygen content after pressure firing is not less than 45 atomic% and not more than 60 atomic%.
(加圧焼成)
次に、上述のようにして得られた混合粉末をカーボン製の型に投入し、例えばホットプレス装置によって加圧焼成を行って、焼成体を得る。ここでは、ホットプレス装置は一般的に使用されているものでよく、この装置を用いて、一定圧力および一定の焼成温度で、非酸素雰囲気中にて所定時間焼成が行われる。
(Pressurized firing)
Next, the mixed powder obtained as described above is put into a carbon mold and subjected to pressure firing, for example, with a hot press apparatus to obtain a fired body. Here, a hot press apparatus may be generally used, and by using this apparatus, firing is performed for a predetermined time in a non-oxygen atmosphere at a constant pressure and a constant firing temperature.
(仕上げ工程)
上述のようにして得られた焼成体に対して、所定サイズの円盤形状になるように機械加工を施す。以上により、目的とするターゲットを得ることができる。
(Finishing process)
The fired body obtained as described above is machined so as to have a disk shape of a predetermined size. As described above, the target can be obtained.
次に、金属膜2を成膜するためのターゲットの製造方法について説明する。
(秤量・混合)
遷移金属粉末であるTiと遷移金属窒化物粉末であるTi窒化物粉末とをそれぞれ所定量秤量した後、例えば混合乾式を行う。ここで、Ti粉末とTi窒化物粉末との混合比は、加圧焼成後の窒素の含有量が1原子%以上20原子%以下の範囲となるように調整することが好ましく、5原子%以上15原子%以下の範囲となるように調整することがより好ましい。
Next, a method for manufacturing a target for forming the
(Weighing and mixing)
After a predetermined amount of each of the transition metal powder Ti and the transition metal nitride powder Ti nitride powder is weighed, for example, a dry mixing method is performed. Here, the mixing ratio of the Ti powder and the Ti nitride powder is preferably adjusted so that the nitrogen content after pressure firing is in the range of 1 atomic% or more and 20 atomic% or less. It is more preferable to adjust so that it may become 15 atomic% or less.
(加圧焼成)
次に、上述のようにして得られた混合粉末をカーボン製の型に投入し、例えばホットプレス装置によって加圧焼成を行う。ここでは、ホットプレス装置は一般的に使用されているものでよく、この装置を用いて、一定圧力および一定の焼成温度で、非酸素雰囲気中にて所定時間焼成が行われる。
(Pressurized firing)
Next, the mixed powder obtained as described above is put into a carbon mold and subjected to pressure firing, for example, using a hot press apparatus. Here, a hot press apparatus may be generally used, and by using this apparatus, firing is performed for a predetermined time in a non-oxygen atmosphere at a constant pressure and a constant firing temperature.
(仕上げ工程)
上述のようにして得られた焼成体に対して、所定サイズの円盤形状になるように機械加工を施す。以上により、目的とするターゲットを得ることができる。
(Finishing process)
The fired body obtained as described above is machined so as to have a disk shape of a predetermined size. As described above, the target can be obtained.
この発明の第1の実施形態によれば以下の効果を得ることができる。
金属膜2、酸化物膜3、第1の誘電体膜4a、第2の誘電体膜2b、光透過層5を基板1上に順次積層するだけで光記録媒体10を製造できるので、単純な膜構成を有する高記録密度の光記録媒体10を提供することができる。すなわち、低廉な高記録密度の光記録媒体10を提供することができる。
According to the first embodiment of the present invention, the following effects can be obtained.
Since the
また、Ge酸化物からなるターゲットをスパッタリングして酸化物膜3を成膜するので、量産時において、一定の酸素濃度、すなわち一定の吸収係数を有する酸化物膜3を成膜することができる。
Further, since the
また、Ti窒化物からなるターゲットをスパッタリングして金属膜2を成膜するので、少ない流量の窒素ガスを一定に制御する困難な作業をする必用がなくなる。したがって、量産時において金属膜2を安定して成膜することができる。
In addition, since the
(3)第2の実施形態
光記録媒体の構成
この第2の実施形態による光記録媒体10は、上述の第1の実施形態と同様に、基板1上に、無機記録膜6、誘電体膜4、光透過層5が順次積層された構成を有する。基板1およびその上に積層された各層を構成する材料および厚さなどは、上述の第1の実施形態と同様であるので説明を省略する。
(3) Second embodiment
Configuration of Optical Recording Medium In the
図2は、この発明の第2の実施形態による光記録媒体を示す平面図である。図2に示すように、この光記録媒体10の内周部には、リードイン領域12が設けられ、このリードイン領域12の外周側にユーザデータ領域13が設けられている。また、リードイン領域12には、識別情報記録領域であるBCA(Burst Cutting Area)14が設けられている。
FIG. 2 is a plan view showing an optical recording medium according to the second embodiment of the present invention. As shown in FIG. 2, a lead-in
ユーザデータ領域13は、ユーザが所望のデータを記録するための領域である。リードイン領域12は、例えば識別情報(ID)、暗号鍵および複合鍵などの情報を記録するための領域であり、これらの情報は、光記録媒体10の製造時に記録される。BCA14は、光記録媒体10の製造時に識別情報を記録するための領域である。識別情報は、各媒体に固有な情報であり、例えば、不正コピーの防止などを目的とするものである。
The user data area 13 is an area for the user to record desired data. The lead-in
光記録媒体の製造方法
基板の成形工程から光透過層の形成工程までは、上述の第1の実施形態と同様であるので説明を省略し、以下では光透過層の形成工程の次工程である識別情報の記録工程について説明する。
The manufacturing method of the optical recording medium The steps from the substrate forming step to the light transmitting layer forming step are the same as those in the first embodiment described above, so the description thereof will be omitted. The identification information recording process will be described.
まず、図3を参照しながら、識別情報の記録に用いられる記録装置について説明する。図3に示すように、この記録装置は、モータ21、光ピックアップ22および制御回路23を備える。
First, a recording apparatus used for recording identification information will be described with reference to FIG. As shown in FIG. 3, the recording apparatus includes a
光ピックアップ22は、光記録媒体10に対してレーザ光24を照射して識別情報をバーコードとして記録するための光学系である。レーザ光24の波長は、ユーザデータの記録または再生に用いられるレーザ光とほぼ等しい波長とするこことが好ましい。例えば、光記録媒体10が波長405nmなどの青色レーザ光によりユーザデータの記録または再生が行われる光記録媒体10である場合には、光ピックアップ22のレーザ光22の波長を、波長350nm以上450nm以下の範囲に設定すること好ましい。この波長範囲のレーザを用いることで、ユーザデータの記録と同様の原理に基づき、識別情報に対応する記録マークを良好に無機記録膜6に記録することができる。
The
制御回路23は、記録装置全体を制御する。例えば、レーザ光24のフォーカス制御、光ピックアップ22の位置制御、モータ21の回転制御、識別情報の生成などを行う。モータ21は、図示を省略したターンテーブルに載置された光記録媒体10を回転させる。
The
次に、上述の記録装置を用いた識別情報の記録工程について説明する。
まず、光記録媒体10を、その光透過層5の側が光ピックアップ22に対向するようにして、図示を省略したターンテーブルに載置する。次に、モータ21を駆動して光記録媒体10を所定速度で回転させる。
Next, the identification information recording process using the above-described recording apparatus will be described.
First, the
そして、光ピックアップ22を光記録媒体10の内周部に設けられたBCA14まで移動させた後、光ピックアップ22を駆動させて、例えば識別情報に応じてパルス状に変調されたレーザ光を光透過層5側から照射する。これにより、無機記録膜6のうちレーザ光24が照射された部分では、酸化物膜3の酸素が分離して、酸素濃度が高い層が金属膜2の側に形成され、酸素濃度が低い層が誘電体膜4の側に形成される。その結果、識別情報に応じた記録マークが例えばバーコード状に形成され、識別情報がBCAに記録される。なお、この記録マークの形成に用いられるレーザ光の波長は、上述のように350nm〜450nmの範囲にすることが好ましい。以上により、目的とする光記録媒体10が得られる。
Then, after moving the
図4(a)は、BCAに形成された記録マークの一例を示す。図4(b)は、BCAに記録された識別情報を再生したときの再生信号の波形の一例を示す。なお、図4(a)において斜線を付した部分が記録マークを示し、この記録マークは、パルス状に変調されたレーザ光を照射することにより形成される。 FIG. 4A shows an example of a recording mark formed on the BCA. FIG. 4B shows an example of a waveform of a reproduction signal when the identification information recorded in the BCA is reproduced. In FIG. 4A, the hatched portion indicates a recording mark, and this recording mark is formed by irradiating laser light modulated in a pulse shape.
図4(a)に示すように、識別情報は、バーコード状の縞模様としてBCAに記録される。また、記録マークの部分では反射率が低下するために、再生信号は、図4(b)に示すように、パルス状の波形となる。 As shown in FIG. 4A, the identification information is recorded on the BCA as a bar-code striped pattern. In addition, since the reflectance decreases at the recording mark portion, the reproduction signal has a pulse-like waveform as shown in FIG.
この第2の実施形態では、例えば波長350nm〜450nmのレーザ光を用いて光記録媒体10のBCA14に識別情報を記録するので、ユーザデータの記録と同様の原理により識別情報を無機記録膜6に記録できる。したがって、識別情報の再生信号の乱れを抑制し、所望の再生信号を得ることができる。また、光透過層5の側からレーザ光を照射して基板1上の積層膜を溶融除去して識別情報を記録する場合と比べて、基板1の変形などによって引き起こされる信号の不具合を抑制することができる。また、積層膜の腐食を招く恐れが少ないので、優れた保存安定性を得ることができる。
In the second embodiment, for example, identification information is recorded on the
(4)第3の実施形態
光記録媒体の構成
この第3の実施形態による光記録媒体10はBCA14を有し、このBCA14には識別情報が記録されている。この識別情報は、レーザ光を基板1側から照射することにより、基板1上に積層された積層膜を溶融除去することにより形成される。これ以外の光記録媒体10の構成に関しては上述の第2の実施形態と同様であるので説明を省略する。
(4) Third embodiment
Configuration of Optical Recording Medium The
光記録媒体の製造方法
基板の成形工程から光透過層の形成工程までは、上述の第2の実施形態と同様であるので説明を省略し、以下では光透過層の形成工程の次工程である識別情報の記録工程について説明する。また、識別情報の記録に用いられる記録装置は、光路長補償素子を光ピックアップ22に備える以外のことは上述の第2の実施形態と同様であるので説明を省略する。なお、光ピックアップ22に備えられる光路長補償素子は、上述の第2の実施形態とは異なる基板1側からレーザ光を照射することを考慮して設けたものである。
Since the process from the substrate forming step to the light transmitting layer forming step is the same as in the second embodiment described above, the description thereof will be omitted, and the following step is the next step of the light transmitting layer forming step. The identification information recording process will be described. The recording apparatus used for recording the identification information is the same as that of the second embodiment except that the optical path length compensation element is provided in the
まず、光記録媒体10を、その基板1の側が光ピックアップ22に対向するようにして、図示を省略したターンテーブルに載置する。次に、モータ21を駆動して光記録媒体10を所定速度で回転させる。
First, the
そして、光ピックアップ22を光記録媒体10の内周部に設けられたBCA14まで移動させた後、光ピックアップ22を駆動させて、例えば識別情報に応じてパルス状に変調されたレーザ光を基板1側から照射する。これにより、無機記録膜6のうちレーザ光24が照射された部分では、基板1上に積層された金属膜2、酸化物膜2、誘電体膜5が溶融除去される。その結果、識別情報に応じたマークが例えばバーコード状に形成され、識別情報がBCA14に記録される。
Then, after moving the
なお、レーザ光は、近赤外レーザ光または赤外レーザ光であることが好ましく、例えば波長800nmのレーザ光である。また、レーザ光照射時の光学ヘッドスキャンスピードを5m/s〜9m/s、レーザパワーを3400mW〜4000mWの範囲とすることが好ましい。この範囲とすることで、記録マークエッジ部分における急激な反射率の上昇を抑制することができる。したがって、識別情報の再生信号のノイズを低減することができる。 The laser light is preferably near-infrared laser light or infrared laser light, for example, laser light having a wavelength of 800 nm. Further, it is preferable to set the optical head scanning speed at the time of laser light irradiation in the range of 5 m / s to 9 m / s and the laser power in the range of 3400 mW to 4000 mW. By setting this range, it is possible to suppress an abrupt increase in reflectance at the recording mark edge portion. Therefore, it is possible to reduce noise in the reproduction signal of the identification information.
この第3の実施形態では、ユーザデータの記録再生時とは異なる基板1側からレーザ光をBCA14に照射して識別情報を記録するため、光透過層5の側からレーザ光を照射した場合とは光吸収特性などが異なるので、マークの境界部分に変形が生じることを抑制きる、BCA14の内部に積層膜の一部が残留することを抑制できる、基板1の変形を抑制できるなどの利点を得ることができる。すなわち、再生信号の乱れを抑制し、所望の再生信号を得ることができる。
In the third embodiment, since the identification information is recorded by irradiating the
また、金属膜2に直接レーザ光を照射できるので、基板1上の積層膜を効果的に破壊除去できる。なお、光透過層5側からレーザ光を照射した場合には、酸化物膜3での吸収発熱などの影響で熱が拡散するために、基板1上の積層膜をきれいに破壊除去できないと考えられる。
Further, since the
以下、実施例により本発明を具体的に説明するが、本発明はこれらの実施例のみに限定されるものではない。なお、以下の実施例においては、上述の実施形態と対応する部分には同一の符号を付す。 EXAMPLES Hereinafter, although an Example demonstrates this invention concretely, this invention is not limited only to these Examples. In the following examples, parts corresponding to those in the above-described embodiment are denoted by the same reference numerals.
本発明の実施例として、ブルーレイディスクの光学系に媒体を設計し、成膜したものを示す。ブルーレイディスクの光学系とは、開口数0.85の対物レンズおよび波長400nm〜410nmの青紫色半導体レーザ光源を用いたものである。なお、本発明はこの光学系に適用が限られるものではなく、開口数や波長が多少違っていても同様の効果が期待される。 As an embodiment of the present invention, a medium is designed and formed into a film on an optical system of a Blu-ray disc. The optical system of the Blu-ray disc uses an objective lens having a numerical aperture of 0.85 and a blue-violet semiconductor laser light source having a wavelength of 400 nm to 410 nm. The application of the present invention is not limited to this optical system, and the same effect is expected even if the numerical aperture and wavelength are slightly different.
評価は、パルステック工業株式会社製、ODU−1000(ブルーレイディスク仕様)を用いた。この光源の波長は405nmであり、対物レンズのNAは0.85である。トラックピッチは、0.32μmである。 For evaluation, ODU-1000 (Blu-ray disc specification) manufactured by Pulstec Industrial Co., Ltd. was used. The wavelength of this light source is 405 nm, and the NA of the objective lens is 0.85. The track pitch is 0.32 μm.
実施例について以下の検討の順序で説明する。
(1−1)無機記録膜の構成の検討
(1−2)酸化物膜の成膜方法の検討
(1−3)Ge酸化物ターゲットの製造方法の検討
(1−4)金属膜に対する窒素混入の検討
(1−5)金属膜に対する窒素の混入量の検討
Examples will be described in the following order of examination.
(1-1) Examination of inorganic recording film configuration (1-2) Examination of oxide film deposition method (1-3) Examination of Ge oxide target production method (1-4) Nitrogen mixing in metal film (1-5) Examination of nitrogen content in metal film
(1−1)無機記録膜の構成の検討
実施例1
図5は、この実施例1による光記録媒体の記録膜構成を示す模式的断面図である。なお、図5においては、基板1に設けられたイングルーブ11Gおよびオングルーブ11Lの図示を省略している。この実施例1の光記録媒体10は、TiSi膜2、GeO膜3、SiN膜4、光透過層5を順次基板1上に積層した構成を有する。
(1-1) Examination of composition of inorganic recording film
Example 1
FIG. 5 is a schematic cross-sectional view showing the recording film configuration of the optical recording medium according to the first embodiment. In FIG. 5, the in-
以下、図5を参照しながら、実施例1の光記録媒体10の製造方法について説明する。まず、射出成形法により、一主面にイングルーブ11Gおよびオングルーブ11Lが設けられた基板1を成形した。樹脂材料としては、ポリカーボネート樹脂を用いた。また、トラックピッチを0.32μmとし、イングルーブ11Gの深さを21nmとし、オングルーブ11Lをウォブル(蛇行)させてアドレス情報を付加した。
Hereinafter, a method of manufacturing the
次に、成膜装置(Unaxis社製、商品名:Cube)を用いて、Ti膜2、GeO膜3、SiN膜4を基板1上に順次積膜した。なお、ターゲットサイズは、直径φ200mmとした。以下、成膜装置による各層の成膜工程について順次説明する。
Next, the
まず、真空チャンバ内を真空引きした後、真空チャンバ内にArガスを導入しながら、Tiターゲットを反応性スパッタリングして、膜厚30nmのTi膜2を基板1上に成膜した。なお、成膜時におけるArガス流量を24sccmとし、スパッタパワーを3.0kWとした。
First, after the vacuum chamber was evacuated, a
次に、大気暴露せず別の真空チャンバに搬送し、真空チャンバ内にArガスを導入しながら、Ge酸化物ターゲットをスパッタリングして、膜厚20nmのGeO膜3を成膜した。なお、成膜時におけるArガス流量を30sccm、スパッタパワーを2kWとした。Ge酸化物ターゲットは、GeO膜3の吸収係数kが0.4となる組成とした。
Next, it was transported to another vacuum chamber without being exposed to the atmosphere, and a Ge oxide target was sputtered while introducing Ar gas into the vacuum chamber to form a
次に、大気暴露せず別の真空チャンバに搬送し、真空チャンバ内にArガスとN2ガスとを導入しながら、Siターゲットを反応性スパッタリングして、膜厚60nmのSiN膜4をGeO膜3上に成膜した。なお、成膜時におけるArガス流量を50sccm、N2ガス流量を37sccm、スパッタパワーを4kWとした。また、このSiN膜4の組成を原子比で3:4、屈折率を2.0、吸収係数を0とした。
Next, the Si target is transported to another vacuum chamber without being exposed to the atmosphere, and the Si target is reactively sputtered while introducing Ar gas and N 2 gas into the vacuum chamber. 3 was deposited. The Ar gas flow rate during film formation was 50 sccm, the N 2 gas flow rate was 37 sccm, and the sputtering power was 4 kW. The composition of the
次に、円環形状のポリカーボネートシートを、このシート一主面に予め塗布された感圧性粘着材(PSA)により基板1上に貼り合わせて、厚さ0.1mmの光透過層5を形成した。以上により、目的とする光記録媒体10が得られた。
Next, an annular polycarbonate sheet was bonded onto the
次に、Ge酸化物ターゲットの組成を変えて、酸素組成が異なるGeO膜3をTiSi膜2上に成膜する以外のことは上述の光記録媒体10とすべて同様にして、GeO膜3の酸素組成が互いに異なる複数の光記録媒体10を得た。
Next, the oxygen of the
そして、上述のようにして得られた複数の光記録媒体10に対して上述の記録再生光学系により8Tマークの単一搬送波を記録、再生したときのC/Nおよび変調度を測定した。
この際、記録再生速度は5.28m/sとした。再生パワーは0.35mWとした。チャンネルビット長は80.0nm(直径12cmの光ディスクに23.3GBの記録密度)で行った。 変調方式は17PPであり、最短マークである2Tマークのマーク長は0.16μm、8Tマークのマーク長は0.64μmである。
C/N評価には、スペクトルアナライザ(Takeda Riken製、商品名:TR4171)を用いた。
Then, the C / N and the degree of modulation when a single carrier wave of 8T mark was recorded and reproduced on the plurality of
At this time, the recording / reproducing speed was set to 5.28 m / s. The reproduction power was 0.35 mW. The channel bit length was 80.0 nm (recording density of 23.3 GB on a 12 cm diameter optical disk). The modulation method is 17PP, the mark length of the 2T mark, which is the shortest mark, is 0.16 μm, and the mark length of the 8T mark is 0.64 μm.
For C / N evaluation, a spectrum analyzer (manufactured by Takeda Riken, trade name: TR4171) was used.
次に、上述のようにして得られた複数の光記録媒体10のGeO膜3の酸素組成を調べるために、分析用のサンプルを以下のようにして作製した。
まず、上述の各光記録媒体10のGeO膜3の成膜工程と同様の条件において、2cm×2cmのSiウェーハ上にGeO膜3を100nm程度成膜した。その後、保護膜としてSiN膜を10nm成膜した。以上により、分析用の複数のサンプルを得た。
次に、上述のようにして得られた複数のサンプルの酸素組成をRBS(Rutherford Backscattering)分析法により測定した。なお、測定装置としては、ソニー株式会社内製の装置を用いた。
Next, in order to examine the oxygen composition of the
First, a
Next, the oxygen composition of the plurality of samples obtained as described above was measured by RBS (Rutherford Backscattering) analysis. As a measuring device, an in-house device manufactured by Sony Corporation was used.
次に、上述のようにして得られた複数の光記録媒体10のGeO膜3の吸収係数を調べるために、分析用のサンプルを以下のようにして作製した。
すなわち、上述の各光記録媒体10のGeO膜3の成膜工程と同様の条件において、2cm×2cmのSiウェーハ上にGeO膜を100nm程度成膜して、分析用の複数のサンプルを得た。次に、上述のようにして得られた分析用サンプルの410nmの波長における吸収係数を、エリプソメータにより測定した。なお、エリプソメータとしては、ルドルフ社製のAuto EL-462P17を用いた。
Next, in order to examine the absorption coefficient of the
That is, a GeO film was formed to a thickness of about 100 nm on a 2 cm × 2 cm Si wafer under the same conditions as those for forming the
次に、上述のようにして測定されたC/N、変調度、酸素組成および吸収係数に基づき、図6に示すグラフを作成した。
図6は、酸素組成および吸収係数と、C/Nとの関係を示すグラフである。横軸が酸素組成および吸収係数を示し、縦軸がC/Nを示す。一般に、吸収係数kと酸素組成xの関係は材料や層が同一であれば一意に決定されるものである。酸素組成の定量分析は測定方法によって誤差が大きくでることがあるが、吸収係数は光学パラメータであり比較的安定に測定することができる。
Next, the graph shown in FIG. 6 was created based on the C / N, modulation degree, oxygen composition, and absorption coefficient measured as described above.
FIG. 6 is a graph showing the relationship between oxygen composition and absorption coefficient and C / N. The horizontal axis represents the oxygen composition and the absorption coefficient, and the vertical axis represents C / N. In general, the relationship between the absorption coefficient k and the oxygen composition x is uniquely determined if the materials and layers are the same. The quantitative analysis of the oxygen composition may have a large error depending on the measurement method, but the absorption coefficient is an optical parameter and can be measured relatively stably.
図6から以下のことが分かる。まず、変調度に着目すると、吸収係数kが0.2未満になると変調度が急激に低下し、吸収係数kが0.9を越える変調度が40%以下となってしまう。次に、2TのC/Nに着目すると、吸収係数kが0.15未満になるとC/Nが低下し、0.9を越えるとC/Nが40dB以下になってしまう。
また、ここでは詳細な説明は省略するが、吸収係数が0.15未満になると、急激に記録感度が悪化し、情報信号の記録を行うことができなくなった。これは、吸収が十分でなかったことと、酸素が多く安定な組成であるためと考えられる。
以上の点を考慮すると、GeO膜3の吸収係数kの範囲は、好ましくは0.15以上0.90以下、より好ましくは0.20以上0.70以下、更により好ましくは0.25以上0.60以下の範囲である。
The following can be seen from FIG. First, focusing on the modulation factor, when the absorption coefficient k is less than 0.2, the modulation factor is drastically reduced, and the modulation factor at which the absorption coefficient k exceeds 0.9 is 40% or less. Next, focusing on C / N of 2T, when the absorption coefficient k is less than 0.15, the C / N decreases, and when it exceeds 0.9, the C / N becomes 40 dB or less.
Although a detailed description is omitted here, when the absorption coefficient is less than 0.15, the recording sensitivity suddenly deteriorates and the information signal cannot be recorded. This is presumably because the absorption was not sufficient and the composition was stable with a lot of oxygen.
Considering the above points, the range of the absorption coefficient k of the
実施例2
図7は、この実施例2による光記録媒体の記録膜構成を示す模式的断面図である。
成膜装置(Unaxis社製、商品名:Sprinter)を用いて、膜厚25nmのTiSiO膜2、膜厚22nmのGeO膜3、膜厚45nmのZnS−SiO24a、膜厚10nmのSiN膜4bを基板1上に順次成膜した。その後、感圧性粘着材(PSA)によりポリカーボネートシートを基板1の凹凸面11側に貼り合せて、SiN膜4b上に光透過層5を形成した。この光透過層5の厚さは、PSAおよびポリカーボネートシートを含めて100μmとした。以上により、目的とする光記録媒体10を得た。
Example 2
FIG. 7 is a schematic cross-sectional view showing the recording film configuration of the optical recording medium according to the second embodiment.
Using a film forming apparatus (trade name: Sprinter, manufactured by Unaxis), a
成膜手順は以下の通りである。
まず、真空チャンバ内を真空引きした後、真空チャンバ内にArガスおよび酸素ガスを導入しながら、TiSiターゲットをスパッタリングして、膜厚25nmのTiSi膜2を基板1上に成膜した。このTiSiターゲット中のSiの組成比を20原子%とし、このTiSiO膜2における酸素組成を21原子%とした。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.2Pa
投入電力:3kW
Arガス流量:30sccm
酸素ガス流量:5sccm
The film forming procedure is as follows.
First, after evacuating the vacuum chamber, a TiSi target was sputtered while introducing Ar gas and oxygen gas into the vacuum chamber, and a
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.2Pa
Input power: 3kW
Ar gas flow rate: 30sccm
Oxygen gas flow rate: 5 sccm
次に、真空チャンバ内を真空引きした後、真空チャンバ内にArガスを導入しながら、Ge酸化物ターゲットをスパッタリングして、膜厚22nmのGeO膜3をTiSi膜2上に成膜した。なお、Ge酸化物ターゲットは、GeO膜3の吸収係数kが0.4となる組成とした。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.2Pa
投入電力:2kW
Arガス流量:30sccm
Next, after evacuating the vacuum chamber, a Ge oxide target was sputtered while introducing Ar gas into the vacuum chamber to form a 22 nm-
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.2Pa
Input power: 2kW
Ar gas flow rate: 30sccm
次に、真空チャンバ内を真空引きした後、真空チャンバ内にプロセスガスを導入しながら、ZnS−SiO2ターゲットをスパッタリングして、膜厚45nmのZnS−SiO2膜4aをGeO膜3上に成膜した。ZnS−SiO2膜4aの組成比(原子比)ZnS:SiO2が80:20となるようにした。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.1Pa
投入電力:1kW
Arガス流量:6sccm
Next, after evacuating the vacuum chamber, a ZnS—SiO 2 target is sputtered while introducing a process gas into the vacuum chamber to form a ZnS—SiO 2 film 4 a having a thickness of 45 nm on the
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.1 Pa
Input power: 1kW
Ar gas flow rate: 6sccm
次に、真空チャンバ内を真空引きした後、真空チャンバ内にArガスおよびN2プロセスガスを導入しながら、Siターゲットをスパッタリングして、膜厚10nmのSi3N4膜4bを基板1上に成膜した。
この成膜工程における成膜条件の一例を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.3Pa
投入電力:4kW
Arガス流量:50sccm
N2ガス流量:37sccm
Next, after evacuating the vacuum chamber, the Si target is sputtered while introducing Ar gas and N 2 process gas into the vacuum chamber, so that the Si 3 N 4 film 4b having a thickness of 10 nm is formed on the
An example of film forming conditions in this film forming process is shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.3 Pa
Input power: 4kW
Ar gas flow rate: 50 sccm
N 2 gas flow rate: 37sccm
上述のようにして得られた複数の光記録媒体10に対して、ランダムデータの記録を行ったときのリーディングジッターおよびトレーリングジッターを測定した。
記録再生条件は、BDの25GB密度とし、2倍速(9.83m/s)で記録、1倍速(4.92m/s)で再生した。再生パワーは0.35mWとし、再生信号はリミットイコライザー(プリイコライザーゲイン7.1dB)を通し、タイムインターバルアナライザー(横河電機株式会社製、TA720)によりジッターを測定した。
記録の線速度は9.83m/s(2倍速記録)、再生時の線速度は4.92m/s(1倍速)、チャンネルビット長は74.50nm(直径12cmの光ディスクに25GBの記録密度)で行った。
変調方式は17PPであり、最短マークである2Tマークのマーク長は0.149μm、8Tマークのマーク長は0.596μmである。
その結果を図8に示す。
Reading jitter and trailing jitter when random data was recorded on the plurality of
The recording / reproducing conditions were
The linear velocity of recording is 9.83 m / s (double speed recording), the linear velocity during reproduction is 4.92 m / s (single speed), and the channel bit length is 74.50 nm (recording density of 25 GB on a 12 cm diameter optical disk). I went there.
The modulation method is 17PP, the mark length of the 2T mark which is the shortest mark is 0.149 μm, and the mark length of the 8T mark is 0.596 μm.
The result is shown in FIG.
図8から以下のことが分かる。すなわち、GeO膜3の酸素濃度および吸収係数には最適範囲が存在することがわかる。例えば、BD−Rのジッター規格値である6.5%以下を満たすためには、吸収係数kを0.15≦k≦0.90の範囲にすることが好ましいことが分かる。したがって、GeO膜3の吸収係数kが0.15≦k≦0.90となるように、GeO膜3の酸素濃度を調整することにより、良好な特性を有する光記録媒体10を得ることができる。
The following can be seen from FIG. That is, it can be seen that there are optimum ranges for the oxygen concentration and the absorption coefficient of the
よって、上述の検討によれば、良好な記録を行うためには、Ge酸化物膜3の吸収係数kを0.15≦k≦0.90の範囲とすることが好ましい。
Therefore, according to the above examination, in order to perform good recording, it is preferable to set the absorption coefficient k of the
比較例1
次に、GeO膜3とTiSi膜2との間に膜厚3nmのSiN膜を成膜する以外のことは、上述の実施例2とすべて同様にして光記録媒体10を得た。
Comparative Example 1
Next, an
そして、上述の実施例2と同様にして、比較例1の光記録媒体10に情報信号の記録を行って、変調度を測定した。その結果、変調度が10%以下に低下し、ほとんど良好な記録が行われなかった。SiN膜の厚さから考えると、光学的にも熱的にも記録には殆ど影響を与えないはずであるが、記録に多大な影響を与えるという結果となった。これは、Ti合金の表面が酸化することにより、光触媒効果が発現し、GeO膜3の酸素が分離することが記録原理となっているためである。このことは、透過型電子顕微鏡(TEM:Transmission Electron Microscope)を用いた断面TEM観察により、記録後GeO膜3が2層に分離し、酸素組成の多い層がTiSi側に、酸素組成の少ない層がその反対側の面に形成されることで明らかにされた。
Then, in the same manner as in Example 2 described above, an information signal was recorded on the
したがって、TiSi膜2にGeO膜3が直接接することが、この光記録媒体10の無機記録膜6にとっては極めて重要な点である。また、その成膜の際にTiSi膜2とGeO膜3の間で大気暴露すると酸化皮膜および不純物が付着することで、記録特性が大幅に劣化するため、大気暴露をせずに連続に成膜することが望ましい。
Therefore, it is very important for the
(1−2)酸化物膜の成膜方法の検討
まず、比較例として、プロセスガスとしてArガスおよび酸素ガスを導入しながら、リアクティブスパッタリング法によりGeターゲットをスパッタリングして、GeO膜3を成膜した場合について説明する。
(1-2) Examination of Oxide Film Formation Method First, as a comparative example, a Ge target is formed by sputtering a Ge target by a reactive sputtering method while introducing Ar gas and oxygen gas as process gases. The case where the film is formed will be described.
比較例2Comparative Example 2
まず、実施例2と同様にして、同一の基板1を複数成形し、これらの基板1上にTiSi膜2を成膜した。次に、プロセスガスとしてArおよび酸素の混合ガスを導入しながら、リアクティブスパッタリング法により、Geターゲットをスパッタリングして、GeO膜3を成膜した。この成膜工程では、Arガスの流量を30sccm一定とし、酸素ガスの流量を記録媒体毎に変化させて、異なる吸収係数を有するGeO膜3をTiSi膜2上に成膜した。これ以外のことは上述の実施例2と同様にして、GeO膜3の酸素組成が互いに異なる複数の光記録媒体10を得た。
First, in the same manner as in Example 2, a plurality of
比較例3
GeO膜の成膜前のプリスパッタ条件を変える以外のことは、上述の比較例2と同様にして、GeO膜3の酸素組成が互いに異なる複数の光記録媒体10を得た。
Comparative Example 3
Except for changing the pre-sputtering conditions before the formation of the GeO film, a plurality of
比較例4
比較例2の光記録媒体10の作製から数週間程度経過後に、比較例2と同一のGeターゲットを用いてGeO膜3を成膜する以外のことは、上述の比較例2と同様にして、GeO膜3の酸素組成が互いに異なる複数の光記録媒体10を得た。
Comparative Example 4
Except for forming the
図9に、上述した比較例2〜4のGeO膜の成膜工程における酸素流量と、GeO膜の吸収係数との関係を示すグラフである。なお、吸収係数は、波長410nmにおけるものであり、その測定にはエリプソメータ(ルドルフ社製、商品名:Auto EL-462P17)を用いた。 FIG. 9 is a graph showing the relationship between the oxygen flow rate and the absorption coefficient of the GeO film in the GeO film forming process of Comparative Examples 2 to 4 described above. The absorption coefficient was measured at a wavelength of 410 nm, and an ellipsometer (manufactured by Rudolf, trade name: Auto EL-462P17) was used for the measurement.
図9から以下のことが分かる。すなわち、酸素ガス流量が約40〜47sccmの範囲で所望の0.15〜0.90の範囲の吸収係数が得られることが分かる。また、詳細な説明は省略するが、この酸素ガス流量の範囲でGeO膜3を成膜して光記録媒体10を作製したところ、この記録媒体10では実施例2とほぼ同等の記録特性が得られた。
The following can be seen from FIG. That is, it can be seen that the desired absorption coefficient in the range of 0.15 to 0.90 can be obtained when the oxygen gas flow rate is in the range of about 40 to 47 sccm. Although detailed description is omitted, when the
また、図9中の丸、三角、四角でプロットしたものは、成膜前のプリスパッタの条件が異なっている光記録媒体10や、成膜の日時が数週間程度異なっている光記録媒体10に関するものであるが、同じ吸収係数を得るために必要な酸素流量が大きく揺らいでいることが分かる。これは、Geターゲット表面の酸化の度合いが比較例2〜4で微妙に異なるため、成膜されるGeO膜3の膜質が変わることを示している。
Also, the plots of circles, triangles, and squares in FIG. 9 are
更に、Ge表面の酸化膜付着状況はいわゆるヒステリシスを有する。つまり、表面が酸化されると酸素流量を下げても酸素組成が高く保たれ、また、酸素を流さずにスパッタし表面をクリーニングした後に成膜すると、同じ酸素流量でも成膜された膜の酸素組成は低く、また、成膜を続けていると徐々にGeターゲット表面が酸化されてきて吸収係数が変化する。したがって、このような状態では安定して生産ができず、量産には向かない。 Furthermore, the oxide film adhesion state on the Ge surface has a so-called hysteresis. In other words, when the surface is oxidized, the oxygen composition is kept high even when the oxygen flow rate is lowered, and when the film is formed after sputtering and cleaning the surface without flowing oxygen, the oxygen of the film formed even at the same oxygen flow rate The composition is low, and when the film formation is continued, the surface of the Ge target is gradually oxidized and the absorption coefficient changes. Therefore, stable production is not possible in such a state, which is not suitable for mass production.
更に、図9中の48sccmでは吸収係数がほぼ0となっているが、47sccmでは吸収係数が0.4である。つまり、所望の吸収係数が0.4程度であると、そのような状態をそもそも安定に作成することが不可能である。 Further, the absorption coefficient is substantially 0 at 48 sccm in FIG. 9, but the absorption coefficient is 0.4 at 47 sccm. That is, when the desired absorption coefficient is about 0.4, it is impossible to create such a state stably in the first place.
次に、Arガスのみを導入しながら、Ge酸化物ターゲットをスパッタリングしてGeO膜を成膜する光記録媒体の製造方法について説明する。この実施例では、成膜ガス雰囲気中に酸素が含まれないため、成膜されたGeO膜3に含まれる酸素はすべてターゲット内に初めから含まれるものである。
Next, a method of manufacturing an optical recording medium in which a GeO film is formed by sputtering a Ge oxide target while introducing only Ar gas will be described. In this embodiment, since oxygen is not contained in the film forming gas atmosphere, all the oxygen contained in the formed
実施例3Example 3
まず、実施例2と同様にして、同一の基板1を複数成形し、これらの基板1上にTiSi膜2を成膜した。次に、プロセスガスとしてArガスを導入しながら、Ge酸化物ターゲットをスパッタリングして、TiSi膜2上にGeO膜3を成膜した。Ge酸化物ターゲットにおけるGeと酸素との組成比(原子比)を1:1とした。すなわち、Ge50O50とした。
First, in the same manner as in Example 2, a plurality of
図10に、ターゲットの使用量(GeO成膜量)と吸収係数との関係を示す。なお、吸収係数は、波長410nmにおけるものであり、その測定にはエリプソメータ(ルドルフ社製、商品名:Auto EL-462P17)を用いた。 FIG. 10 shows the relationship between the target usage (GeO deposition amount) and the absorption coefficient. The absorption coefficient was measured at a wavelength of 410 nm, and an ellipsometer (manufactured by Rudolf, trade name: Auto EL-462P17) was used for the measurement.
図10から以下のことが分かる。すなわち、成膜開始から4kWhまでは吸収係数が安定しない。この原因は、ターゲットの表面が初期状態では平坦であり、エロージョンがある程度大きくなるまでは放電が安定しないことと、スパッタが進むにつれて表面の状態が変わりターゲット上の酸素濃度が変化することとにある。 The following can be understood from FIG. That is, the absorption coefficient is not stable from the start of film formation to 4 kWh. This is because the surface of the target is flat in the initial state, the discharge is not stable until the erosion is increased to some extent, and the state of the surface changes as the sputtering proceeds, and the oxygen concentration on the target changes. .
一方、成膜開始から4kWh以上では吸収係数の変化が落ち着き、一定量の吸収係数、すなわち、酸素濃度となっている。この状態にターゲットがなると、プリスパッタをせずとも常に一定の吸収係数のGeO膜3を安定して得ることができる。さらに、ターゲットの寿命は200kWh以上であるので、成膜開始から4kWhまでをGeO膜3の組成を安定化させるための初期化期間としても、この初期化期間はコスト的には何ら問題のないレベルの長さである。また、このターゲットを用いた場合、十分使用した後の安定状態での吸収係数は0.4であることが分かる。
On the other hand, at 4 kWh or more from the start of film formation, the change in absorption coefficient settles down to a certain amount of absorption coefficient, that is, oxygen concentration. When the target is in this state, the
さらに、Ge50O50以外の酸素組成のGe酸化物ターゲットを用いて光記録媒体10を作製し、ターゲットの使用量(GeO成膜量)と吸収係数との関係を調べた。
その結果、酸素組成がGe55O45の場合、上述の場合と同様に4kWh以上使用後に吸収係数を測定したところ、安定状態での吸収係数は0.9であった。また、酸素組成がGe40O60の場合は、上述の場合と同様に4kWh以上使用後に吸収係数を測定したところ、安定状態での吸収係数は0.15であった。上述の実施例2で示したように、良好な記録特性の得られる吸収係数kの範囲は0.15≦k≦0.90であるため、この吸収係数を有するGeO膜3を安定に成膜できるGe酸化物ターゲットの酸素の組成比は45原子%以上60原子%以下となる。
Furthermore, the
As a result, when the oxygen composition was Ge 55 O 45 , the absorption coefficient was measured after use of 4 kWh or more in the same manner as described above, and the absorption coefficient in a stable state was 0.9. When the oxygen composition was Ge 40 O 60 , the absorption coefficient was measured after use of 4 kWh or more as in the above case, and the absorption coefficient in a stable state was 0.15. As shown in Example 2 above, the range of the absorption coefficient k that provides good recording characteristics is 0.15 ≦ k ≦ 0.90. Therefore, the
(1−3)Ge酸化物ターゲットの製造方法の検討
次に、実施例として、Ge酸化物ターゲットの製造方法について説明する。
実施例4
Geが飽和な酸化物となった場合には、GeO2の組成を有する。従って、Geの場合にも飽和酸化物の場合は、Ge(100-X)OX(X:原子%)という形で記述した場合には、GeO2ではx=66.7となる。
(1-3) Examination of Ge oxide target manufacturing method Next, a Ge oxide target manufacturing method will be described as an example.
Example 4
When Ge becomes a saturated oxide, it has a composition of GeO 2 . Accordingly, in the case of Ge as well, in the case of a saturated oxide, if it is described in the form of Ge (100-X) O x (X: atomic%), x = 66.7 in GeO 2 .
以下に、Ge非飽和酸化物であるGe50O50およびGe60O40からなるターゲットの形成工程を説明する。まず、原材料として、Ge粉末およびGeO2粉末を各々所定量秤量し、乾式混合を行なった後に、得られた混合粉末をカーボン製の型に投入しホットプレス装置によって加圧焼成を行って、焼成体を得た。この加圧焼成は、圧力19.6Mpa、焼成温度1043K〜1173Kの間の一定温度、所定時間、不活性ガス雰囲気の条件で行った。そして、焼成体に対して機械加工を施し、直径32mm、厚さ4mmのターゲットに加工した。 The following describes a Ge 50 O 50 and Ge 60 O of 40 target forming step is Ge desaturation oxide. First, as a raw material, Ge powder and GeO 2 powder are weighed in predetermined amounts, and after dry mixing, the obtained mixed powder is put into a carbon mold and subjected to pressure firing by a hot press apparatus, followed by firing. Got the body. This pressure firing was performed under conditions of a pressure of 19.6 Mpa, a constant temperature between a firing temperature of 1043K and 1173K, a predetermined time, and an inert gas atmosphere. Then, the fired body was processed into a target having a diameter of 32 mm and a thickness of 4 mm.
次に、作製したターゲットについて、理論密度に対する相対密度(%)の測定を行なった。その結果を図11に示す。ここで、相対密度とは、作製したターゲットの直径、厚さ、重量から算出した密度の理論密度に対する割合であり、理論密度とはターゲット組成の各元素について重量を算出し、この重量の総和をターゲット体積で除することにより求めたものである。 Next, the relative density (%) with respect to the theoretical density was measured for the produced target. The result is shown in FIG. Here, the relative density is a ratio of the density calculated from the diameter, thickness, and weight of the produced target to the theoretical density, and the theoretical density is calculated for each element of the target composition, and the sum of the weights is calculated. It is obtained by dividing by the target volume.
図11から以下のことが分かる。すなわち、比較的低い温度において相対密度が100%のターゲットを作製できる。ターゲットの密度が低いと、ターゲット作製上、割れやすく容易に作製することが困難である。また、密度の低いターゲットをスパッタリングに使用するとスパッタレートの低下を招き、ディスク製造上コストアップとなってしまう。相対密度として80%以下である場合にはそのような問題が発生し、成膜の安定性のみならず、記録再生特性にも影響する。したがって、スパッタリングに使用されるターゲットの密度として、スパッタリングレートなどを安定に保つためには、相対密度としておおよそ80%以上が望ましい。
なお、実施例1、2、3、5では、同様の方法で得られた焼成体を直径200mm、厚さ6mmのターゲットに加工したものを用いた。
The following can be seen from FIG. That is, a target having a relative density of 100% can be manufactured at a relatively low temperature. When the density of the target is low, it is difficult to easily produce a target because it is easily broken. In addition, if a target having a low density is used for sputtering, the sputtering rate is lowered, resulting in an increase in disk manufacturing cost. Such a problem occurs when the relative density is 80% or less, which affects not only the stability of the film formation but also the recording / reproducing characteristics. Therefore, the relative density of the target used for sputtering is preferably about 80% or more in order to keep the sputtering rate and the like stable.
In Examples 1, 2, 3, and 5, a fired body obtained by the same method was processed into a target having a diameter of 200 mm and a thickness of 6 mm.
(1−4)金属膜に対する窒素混入の検討
次に、実施例5として、TiSi膜2に窒素を混入した場合について説明する。
上述の実施例2ではジッター値としては良好な特性が得られた。しかし、記録再生をする際にはドライブのばらつきや使用環境により、媒体にとって常に最適な記録パワーで記録されるとは限らない。したがって、市場で広範に問題なく記録再生が行われるためには、記録媒体の記録パワーマージンが広いことが望まれる。
(1-4) Examination of Nitrogen Mixing into Metal Film Next, as Example 5, a case where nitrogen is mixed into the
In Example 2 described above, good characteristics were obtained as the jitter value. However, when recording / reproduction is performed, recording is not always performed with the optimum recording power for the medium due to variations in the drive and usage environment. Therefore, a wide recording power margin of the recording medium is desired so that recording and reproduction can be performed without any problems in the market.
実施例5Example 5
まず、実施例2と同様にして、TiSi膜2に窒素が混入されていない光記録媒体10を作製した。ここでは、膜構成は実施例2とほぼ同じだが、TiSiのSi組成は27原子%とし、成膜雰囲気に酸素は混入せず、膜厚は27nmとした。また、Ge酸化物層の吸収係数は0.4、膜厚は25nmとした。
そして、この光記録媒体10のパワーマージンを測定した。記録再生条件は実施例2と同一である。
なお、パワーマージンの測定では、PwとPs(それぞれピークパワーとスペースパワーを示す。BD規格の定義による。)の比を保ったままパワーを変えてゆき、その他のパワーは固定とした。その測定結果を図12に示す。
First, in the same manner as in Example 2, an
Then, the power margin of the
In the measurement of the power margin, the power was changed while maintaining the ratio of Pw and Ps (representing peak power and space power, respectively, as defined by the BD standard), and other powers were fixed. The measurement results are shown in FIG.
次に、TiSi膜2に窒素ガスを混入させて光記録媒体10を作製した。TiSi膜2の成膜工程において、Arプロセスガス30sccmに対して3sccmの窒素ガスを混合して成膜を行った。これ以外のことは、上述の実施例2と同様にした。そして、作製された光記録媒体10のパワーマージンを測定した。なお、パワーマージンの測定は、上述の光記録媒体10と同様にして測定を行った。その測定結果を図13に示す。
Next, an
図12および図13から以下のことが分かる。すなわち、リミットイコライザーを通したジッター値として8.5%以下となるパワーの範囲を最適パワーで割った値をパワーマージンと定義すると、図12の場合は25%であったのに対して、TiSi中に窒素を含めたものは31%にまで広がっている。 The following can be understood from FIGS. That is, when a value obtained by dividing a power range of 8.5% or less as a jitter value through the limit equalizer by the optimum power is defined as a power margin, in the case of FIG. Those containing nitrogen have spread to 31%.
しかし、窒素ガスを3sccmを流す際には、流量のコントロールは0.5sccm単位であり、この程度の少ない流量では窒素量を安定して混入することは難しい。量産時にはターゲットの使用状況に応じて表面の状態が変化するため、窒素混入量をコントロールせざるをえなくなり、また、流量にてそれを安定におこなうことは困難である。 However, when flowing 3 sccm of nitrogen gas, the flow rate is controlled in units of 0.5 sccm, and it is difficult to stably mix the nitrogen amount with such a small flow rate. During mass production, the state of the surface changes according to the usage conditions of the target, so the amount of nitrogen contamination must be controlled, and it is difficult to stably achieve it with a flow rate.
そこで、本発明は、窒素をターゲット中に所望の濃度で含ませ、Arのみをプロセスガスとして用いて成膜することにより、より安定して生産ができるようにするものである。
窒素の組成は、X線光電子分析装置(ESCA,ULVAC-PHI ESCA5400MC)により測定した。測定条件は、X線はMgKα、出力は14kV(400W)、分析径は1.1mmφ、真空度1.2×10-5Pa、光電子脱出角度45度である。試料はグルーブの無い鏡面ポリカーボネート基板上にTiSi(N)を30nm成膜し、保護膜としてAgを5nm程度成膜した。測定時はイオンエッチングにて表面を15nm程度けずり、TiSi表面を露出させてから測定を行った。定量分析は、Ti,Si,O,Nを合計したものを100%とし、窒素の組成を原子比で示す。その結果、上記Ar30sccmに対して窒素を3sccm流したものは、窒素組成が7原子%となった。
Therefore, the present invention makes it possible to produce more stably by including nitrogen at a desired concentration in a target and forming a film using only Ar as a process gas.
The composition of nitrogen was measured with an X-ray photoelectron analyzer (ESCA, ULVAC-PHI ESCA5400MC). The measurement conditions are X-ray MgKα,
また、X線光電子分析装置(ESCA,ULVAC-PHI ESCA5400MC)を用いると窒素がTiもしくはSiのどちらに結合しているかも明らかになる。そこで、TiおよびSiのスペクトルのずれを観測したところ、Tiにピークのシフトが観測された一方で、Siはほとんど変化していなかったため、窒素のうち殆どはTiに結合していることが判明した。 In addition, when an X-ray photoelectron analyzer (ESCA, ULVAC-PHI ESCA5400MC) is used, it becomes clear whether nitrogen is bound to Ti or Si. Therefore, when a shift in the spectrum of Ti and Si was observed, a peak shift was observed in Ti, but Si was hardly changed, and thus it was found that most of nitrogen was bonded to Ti. .
そこで、以下に、このような組成がArスパッタのみで成膜できる焼成ターゲットについて説明する。焼成ターゲットの作製に用いる材料は、Ti粉末、Si粉末、そしてTi窒化物(TiN)粉末である。なお、Tiが飽和な窒化物となった場合には、TiNの組成を有する。 Accordingly, a fired target having such a composition that can be formed only by Ar sputtering will be described below. Materials used for the production of the firing target are Ti powder, Si powder, and Ti nitride (TiN) powder. When Ti becomes a saturated nitride, it has a composition of TiN.
まず、Ti非飽和窒化物として、Ti68Si25N7を形成する工程を説明する。原材料として、Ti粉末、Si粉末およびTiN粉末を各々所定量秤量し、乾式混合を行なった後に、得られた混合粉末をカーボン製の型に投入しホットプレス装置によって加圧焼成を行なって焼成体を得た。この加圧焼成は、圧力29.4MPa、焼成温度1073Kから1223Kの間の一定温度、所定時間、真空雰囲気の条件にて行った。そして、この焼成体に対して機械加工を施し、直径200mm、厚さ6mmのターゲットを得た。 First, a process of forming Ti 68 Si 25 N 7 as the Ti unsaturated nitride will be described. As raw materials, Ti powder, Si powder and TiN powder are weighed in predetermined amounts, and after dry mixing, the obtained mixed powder is put into a carbon mold and subjected to pressure firing with a hot press device to obtain a fired body. Got. This pressure firing was performed under conditions of a pressure of 29.4 MPa, a constant temperature between a firing temperature of 1073K to 1223K, a predetermined time, and a vacuum atmosphere. The fired body was machined to obtain a target having a diameter of 200 mm and a thickness of 6 mm.
他の実施例と同様、スパッタリングに使用されるターゲットの密度として、スパッタリングレートなどを安定に保つためには、相対密度としておおよそ80%以上が望ましい。 As in the other examples, the density of the target used for sputtering is preferably about 80% or more as the relative density in order to keep the sputtering rate and the like stable.
(1−5)金属膜に対する窒素の混入量の検討
実施例6
次に、実施例6として、窒素混入量依存性について、窒素ガス流量を0sccmから9sccmまで変えて光記録媒体10を作製し、記録再生を行って各種評価を行った場合について説明する。図14に、窒素ガス流量、最適記録パワー、そのパワーにおけるジッター値が得られるパワーマージン(peak to peak)、およびTi合金膜中の窒素組成を示す。なお、記録再生条件は、記録を1倍速(4.92m/s)とした以外は実施例5と同様である。
(1-5) Examination of nitrogen content in metal film
Example 6
Next, as Example 6, the case where the nitrogen gas flow rate is changed from 0 sccm to 9 sccm, the
以下、実施例6において作製した光記録媒体10について具体的に説明する。
図14に示すように、作製する光記録媒体10毎にTi合金膜の成膜工程における窒素ガス流量を変える以外のことは上述の実施例5とすべて同様にして、Ti合金膜の窒素組成が互いに異なる複数の光記録媒体10を得た。
Hereinafter, the
As shown in FIG. 14, the nitrogen composition of the Ti alloy film is the same as in Example 5 except that the nitrogen gas flow rate in the Ti alloy film forming process is changed for each
図14の記録特性から以下のことが分かる。すなわち、窒素ガス流量を3sccmにして、窒素組成を7原子%含めることにより、窒素を流さない場合に比べるとパワーマージンが20%から24%へ、大幅に向上していることが分かる。この際、ボトムジッターは共に5.5%程度でほぼ同じレベルである。記録感度は0.1mW悪化しているが、この程度の記録感度の悪化は問題ないレベルである。 The following can be understood from the recording characteristics of FIG. That is, it can be seen that by setting the nitrogen gas flow rate to 3 sccm and including 7 atomic% of the nitrogen composition, the power margin is greatly improved from 20% to 24% as compared with the case where no nitrogen is supplied. At this time, the bottom jitter is about 5.5%, which is almost the same level. Although the recording sensitivity has deteriorated by 0.1 mW, this level of deterioration in recording sensitivity is at a level that causes no problem.
さらに、窒素ガス流量を増やして、窒素ガス流量を6sccmとし、窒素組成を15原子%とすると、パワーマージンは22%となり、窒素ガス流量3sccmの場合に比して若干狭まるが、窒素ガス流量0sccmの場合のパワーマージン20%よりは改善されている。一方、ボトムジッターは若干悪化し、記録感度は更に悪化している。 Further, when the nitrogen gas flow rate is increased to 6 sccm and the nitrogen composition is 15 atomic%, the power margin is 22%, which is slightly narrower than the nitrogen gas flow rate of 3 sccm, but the nitrogen gas flow rate is 0 sccm. In this case, the power margin is improved from 20%. On the other hand, the bottom jitter is slightly deteriorated, and the recording sensitivity is further deteriorated.
窒素流量を9sccm、窒素組成を23原子%にすると、ジッターは8%以上となるため、Ti合金膜であるTiSi膜2に窒素を混入させる場合には、窒素組成でおよそ20原子%以下までが好ましい範囲である。
When the nitrogen flow rate is 9 sccm and the nitrogen composition is 23 atomic%, the jitter is 8% or more. Therefore, when nitrogen is mixed into the
実施例5と同様にして窒素組成を1原子%≦x≦20原子%の範囲で含むターゲットを同様に作成することで、図14に示したのと同様の特性を示す光記録媒体10を、窒素を含むターゲットにより実現でき、いずれの媒体でも成膜条件を安定させることができる。
ここでは、Tiと添加物SiとからなるTiSi膜に窒素を混入する場合について説明したが、Si以外の他の添加物を含有するTiSn膜などに窒素を混入するようにしてもよい。この場合にも、TiSi膜に窒素を混入する場合とほぼ同様の効果を得ることができる。また、Ti膜に窒素を添加した場合にも、ほぼ同様の効果を得ることができる。
In the same manner as in Example 5, a target including the nitrogen composition in the range of 1 atomic% ≦ x ≦ 20 atomic% was similarly prepared, whereby an
Here, the case where nitrogen is mixed into a TiSi film made of Ti and additive Si has been described, but nitrogen may be mixed into a TiSn film containing an additive other than Si. Also in this case, substantially the same effect as when nitrogen is mixed into the TiSi film can be obtained. Further, when nitrogen is added to the Ti film, substantially the same effect can be obtained.
次に、第2の実施形態に対応する実施例7〜8について以下の順序で説明する。
(2)青色レーザによるBCAの形成方法の検討
次に、青色レーザによるBCAの形成方法について検討を行った。以下に、この検討内容について説明する。
Next, Examples 7 to 8 corresponding to the second embodiment will be described in the following order.
(2) Examination of BCA Formation Method Using Blue Laser Next, a BCA formation method using a blue laser was examined. The contents of this study will be described below.
実施例7
この実施例7の光記録媒体10は、TiSi膜2、GeO膜3、ZnS−SiO2膜4a、SiN膜4b、光透過層5を基板1上に順次積層した構成を有する。
Example 7
The
以下、実施例7の光記録媒体10の製造方法について説明する。まず、射出成形法により、一主面にイングルーブ11Gおよびオングルーブ11Lが設けられた基板1を成形した。樹脂材料としては、ポリカーボネート樹脂を用いた。また、トラックピッチを0.32μmとし、イングルーブ11Gの深さを21nmとし、オングルーブ11Lをウォブル(蛇行)させてアドレス情報を付加した。
A method for manufacturing the
次に、真空チャンバ内を真空引きした後、真空チャンバ内にArガスを導入しながら、TiSiターゲットをスパッタリングして、膜厚27nmのTiSi膜2を基板1上に成膜した。このTiSi膜2におけるSiの組成比を27原子%とした。
この成膜工程における成膜条件を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.2Pa
投入電力:3kW
Arガス流量:30sccm
Next, after evacuating the vacuum chamber, a TiSi target was sputtered while introducing Ar gas into the vacuum chamber, and a
The film forming conditions in this film forming process are shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.2Pa
Input power: 3kW
Ar gas flow rate: 30sccm
次に、真空チャンバ内を真空引きした後、真空チャンバ内にArガスを導入しながら、Ge酸化物ターゲットをスパッタリングして、膜厚26nmのGeO膜3をTiSi膜2上に成膜した。なお、Ge酸化物ターゲットの酸素組成は、GeO膜3の吸収係数kが0.40となるように調整した。
この成膜工程における成膜条件を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.2Pa
投入電力:2kW
Arガス流量:30sccm
Next, after evacuating the vacuum chamber, a Ge oxide target was sputtered while introducing Ar gas into the vacuum chamber to form a 26 nm-
The film forming conditions in this film forming process are shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.2Pa
Input power: 2kW
Ar gas flow rate: 30sccm
次に、真空チャンバ内を真空引きした後、真空チャンバ内にArガスを導入しながら、ZnS−SiO2ターゲットをスパッタリングして、膜厚45nmのZnS−SiO2膜4aをGeO膜3上に成膜した。
この成膜工程における成膜条件を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.1Pa
投入電力:1kW
Arガス流量:6sccm
Next, after evacuating the vacuum chamber, a ZnS—SiO 2 target is sputtered while introducing Ar gas into the vacuum chamber, and a ZnS—SiO 2 film 4 a having a thickness of 45 nm is formed on the
The film forming conditions in this film forming process are shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.1 Pa
Input power: 1kW
Ar gas flow rate: 6sccm
次に、真空チャンバ内を真空引きした後、真空チャンバ内にArガスおよびN2ガスを導入しながら、Siターゲットをスパッタリングして、膜厚7nmのSiN膜4bを基板1上に成膜した。
この成膜工程における成膜条件を以下に示す。
真空到達度:5.0×10-5Pa
雰囲気:0.3Pa
投入電力:4kW
Arガス流量:50sccm
N2ガス流量:37sccm
Next, after evacuating the inside of the vacuum chamber, a Si target was sputtered while introducing Ar gas and N 2 gas into the vacuum chamber, and a SiN film 4b having a thickness of 7 nm was formed on the
The film forming conditions in this film forming process are shown below.
Degree of vacuum: 5.0 × 10 −5 Pa
Atmosphere: 0.3 Pa
Input power: 4kW
Ar gas flow rate: 50 sccm
N 2 gas flow rate: 37sccm
次に、円環形状のポリカーボネートシートを、このシート一主面に予め塗布された感圧性粘着材(PSA)により基板1上に貼り合わせて、厚さ0.1mmの光透過層5を形成した。
Next, an annular polycarbonate sheet was bonded onto the
次に、波長405nmのレーザ光をパルス状に変調して、光透過層5の側からBCAに照射した。これにより、BCAにバーコード状の記録マークが形成された光記録媒体10を得た。なお、ビーム幅を約5μm、線速度を10m/s、レーザ照射パワーを160mW、1回転あたりのビーム送り量を2μmとした。
Next, a laser beam having a wavelength of 405 nm was modulated in a pulse shape and irradiated to the BCA from the
実施例8
次に、波長800nm帯のレーザ光を照射して記録マークを形成する以外のことは上述の実施例7とすべて同様にして、BCAにバーコードが形成された光記録媒体10を得た。
Example 8
Next, the
次に、上述のようにして得られた実施例7〜8のBCAに記録された信号を再生し、この再生信号を評価した。 Next, the signals recorded in the BCAs of Examples 7 to 8 obtained as described above were reproduced, and the reproduced signals were evaluated.
図15(a)は、BCAに形成される記録マークのイメージを示す。図15(b)は、実施例7の再生信号の波形を示す。図15(c)は、実施例8の再生信号の波形を示す。なお、図15(b)および図15(c)では、実施例7および実施例8の比較を容易にするため微少なノイズの図示は省略している。 FIG. 15A shows an image of a recording mark formed on the BCA. FIG. 15B shows the waveform of the reproduction signal of the seventh embodiment. FIG. 15C shows the waveform of the reproduction signal of Example 8. In FIG. 15B and FIG. 15C, illustration of minute noise is omitted to facilitate comparison between the seventh embodiment and the eighth embodiment.
図15(b)および図15(c)を比較すると以下のことが分かる。すなわち、実施例8では、記録マークの境界部分に急激に反射率が高くなる領域があるのに対して、実施例7では、記録マークの境界部分に急激に反射率が高くなる領域がないことが分かる。これは、800nm帯のレーザでは波長依存性があるため、400nm帯での記録再生に最適化された光記録媒体10ではBCAに対する情報信号の記録が困難であるためと考えられる。また、図示は省略するが、実施例7では、BCA部の全体の信号レベルも比較的均一であった。
Comparison of FIG. 15B and FIG. 15C reveals the following. That is, in Example 8, there is a region where the reflectivity suddenly increases at the boundary portion of the recording mark, whereas in Example 7, there is no region where the reflectivity increases rapidly at the boundary portion of the recording mark. I understand. This is presumably because the 800 nm band laser has wavelength dependence, and thus it is difficult to record information signals on the BCA in the
次に、第3の実施形態に対応する実施例9〜28について以下の順序で説明する。
(3)赤外レーザによるBCAの形成方法の検討
次に、赤外レーザによるBCAの形成方法について検討を行った。以下に、この検討内容について説明する。
Next, Examples 9 to 28 corresponding to the third embodiment will be described in the following order.
(3) Examination of BCA Formation Method Using Infrared Laser Next, a BCA formation method using an infrared laser was examined. The contents of this study will be described below.
実施例9〜13
まず、上述の実施例7とすべて同様にして複数の光記録媒体10を得た。次に、上述のようにして得られた複数の光記録媒体10ごとに光学ヘッドスキャンスピードを3m/s〜11m/sの範囲で変えて、出力パワー4000mW、波長810nmのレーザ光をパルス状に変調して、基板1側からBCAに照射した。これにより、TiSi膜2、GeO膜3、ZnS−SiO2膜4aおよびSiN膜4bを溶融除去され、BCAにバーコード状の記録マークが形成された複数の光記録媒体10を得た。なお、ビーム幅を約30μm、レーザ照射パワーを4000mW、1回転あたりのビーム送り量を2μmとした。
Examples 9-13
First, a plurality of
実施例14〜18
出力パワー3400mWにする以外のことは上述の実施例9〜13とすべて同様にして、BCAにバーコード状の記録マークが形成された複数の光記録媒体10を得た。
Examples 14-18
Except for the output power of 3400 mW, a plurality of
実施例19〜23
光透過層側からBCAにレーザ光を照射する以外のことは実施例9〜13とすべて同様にして、BCAにバーコード状の記録マークが形成された複数の光記録媒体10を得た。
Examples 19-23
Except for irradiating the laser beam to the BCA from the light transmitting layer side, the same procedure as in Examples 9 to 13 was performed to obtain a plurality of
実施例24〜28
光透過層側からBCAにレーザ光を照射する以外のことは実施例14〜18とすべて同様にして、BCAにバーコード状の記録マークが形成された複数の光記録媒体10を得た。
Examples 24-28
Except for irradiating the BCA with laser light from the light transmitting layer side, the same procedure as in Examples 14 to 18 was performed to obtain a plurality of
上述の実施例9〜28では、実用上の観点から、波長810nmの赤外レーザを用いたが、レーザ光の波長は適宜選択できるものであり、赤外レーザは、波長810nmのものに限定されるものではなく、例えば720nm〜2500nmの波長範囲のものを用いることができる。上述の実施例9〜28において波長810nmのレーザ光を用いたのは具体的には以下の理由による。すなわち、基板1上の積層膜を破壊除去することが可能なレーザパワーを、波長810nm以外のレーザでは得ることが困難である。すなわち、650nm帯や400nm帯のレーザではレーザパワーが不足であるため、積層膜を破壊除去することは困難である。
In Examples 9 to 28 described above, an infrared laser with a wavelength of 810 nm was used from a practical viewpoint. However, the wavelength of the laser beam can be appropriately selected, and the infrared laser is limited to one with a wavelength of 810 nm. For example, the thing of the wavelength range of 720 nm-2500 nm can be used. The reason why laser light having a wavelength of 810 nm is used in Examples 9 to 28 is as follows. That is, it is difficult to obtain a laser power capable of destructively removing the laminated film on the
次に、上述のようにして得られた実施例9〜28のBCAに記録された信号を再生し、この再生信号を評価した。 Next, the signals recorded in the BCA of Examples 9 to 28 obtained as described above were reproduced, and the reproduced signals were evaluated.
図16は、実施例9〜13のBCAの再生信号の評価結果を示す。図17は、実施例14〜18のBCAの再生信号の評価結果を示す。図18は、実施例19〜23のBCAの再生信号の評価結果を示す。図19は、実施例24〜28のBCAの再生信号の評価結果を示す。図20は、実施例9〜13の再生信号を示す。図21は、実施例14〜18の再生信号を示す。図22は、実施例19〜23の再生信号を示す。図23は、実施例24〜28の再生信号を示す。なお、図16〜図19の評価結果の欄において、「○」は、BCA部の信号レベルが比較的均一で、且つ、記録マークの境界部分に急激に反射率が高くなる領域がない再生信号を示し、「×」は、BCA部の信号レベルが均一でなく、且つ、記録マークの境界部分に急激に反射率が高くなる領域がある再生信号を示している。また、図20〜図23のA〜Eの各図において、下部に示された信号波形は、上部に示された信号波形の一部を拡大したものである。A〜Eはそれぞれ、スキャンスピード3m/s〜11m/sにてBCAを形成した光記録媒体10の信号波形に対応する。
FIG. 16 shows the evaluation results of the BCA reproduction signals of Examples 9-13. FIG. 17 shows the evaluation results of the BCA reproduction signals of Examples 14-18. FIG. 18 shows the evaluation results of the BCA reproduction signals of Examples 19-23. FIG. 19 shows the evaluation results of the BCA reproduction signals of Examples 24-28. FIG. 20 shows reproduction signals of Examples 9 to 13. FIG. 21 shows reproduced signals of Examples 14-18. FIG. 22 shows reproduced signals of Examples 19-23. FIG. 23 shows reproduction signals of Examples 24-28. In the evaluation result columns of FIGS. 16 to 19, “◯” indicates a reproduction signal in which the signal level of the BCA portion is relatively uniform and there is no region where the reflectivity suddenly increases at the boundary portion of the recording mark. “×” indicates a reproduction signal in which the signal level of the BCA portion is not uniform and there is a region where the reflectance rapidly increases at the boundary portion of the recording mark. Further, in each of FIGS. 20 to 23, the signal waveform shown in the lower part is an enlarged part of the signal waveform shown in the upper part. A to E correspond to signal waveforms of the
図16〜図19から、光透過層5側からレーザ光を照射した場合には、光学ヘッドスキャンスピードおよびレーザパワーに関わらず、BCA部の信号レベルが均一でなく、且つ、記録マークの境界部分に急激に反射率が高くなる領域があることが分かる。
これに対して、基板1側からレーザ光を照射した場合には、光学ヘッドスキャンスピードを5m/s〜9m/s、レーザパワーを3400mW〜4000mWの範囲とすることにより、BCA部の信号レベルが比較的均一で、且つ、記録マークの境界部分に急激に反射率が高くなる領域がないことが分かる。
16 to 19, when the laser beam is irradiated from the
On the other hand, when the laser beam is irradiated from the
以上、この発明の第1〜第3の実施形態について具体的に説明したが、この発明は、上述の一実施形態に限定されるものではなく、この発明の技術的思想に基づく各種の変形が可能である。 The first to third embodiments of the present invention have been specifically described above. However, the present invention is not limited to the above-described embodiment, and various modifications based on the technical idea of the present invention can be made. Is possible.
例えば、上述の第1〜第3の実施形態において挙げた数値はあくまでも例に過ぎず、必要に応じてこれと異なる数値を用いてもよい。 For example, the numerical values given in the first to third embodiments are merely examples, and different numerical values may be used as necessary.
また、上述の第1〜第3の実施形態では、誘電体膜が第1の誘電体膜4aおよび第2の誘電体膜4bからなる積層構造を有する場合を例として説明したが、誘電体膜を単層構造としてもよい。この場合、誘電体膜を構成する材料としては、例えばSiN,ZnS−SiO2,AlN,Al2O3,SiO2,TiO2、SiCなどを用いることができ、記録特性の点からすると、ZnS−SiO2を用いることが好ましい。誘電体膜4の厚さは、例えば10nm以上100nm以下の範囲である。
In the first to third embodiments described above, the case where the dielectric film has a laminated structure including the first dielectric film 4a and the second dielectric film 4b has been described as an example. May have a single-layer structure. In this case, for example, SiN, ZnS—SiO 2 , AlN, Al 2 O 3 , SiO 2 , TiO 2 , SiC, or the like can be used as a material constituting the dielectric film. From the viewpoint of recording characteristics, ZnS It is preferable to use —SiO 2 . The thickness of the
また、上述の第1〜第3の実施形態では、金属膜3をTiから構成する場合について説明したが、Ti以外の光触媒効果を発現する金属材料などから金属膜3を構成しても、上述の第1〜第3の実施形態と同様に情報信号を記録可能な光記録媒体が得られると考えられる。
In the first to third embodiments described above, the case in which the
1 基板
2 金属膜
3 酸化物膜
4 誘電体膜
5 光透過層
6 無機記録膜
10 光記録媒体
DESCRIPTION OF
Claims (11)
金属からなる隣接膜を成膜する工程と、
Geの酸化物からなる酸化物膜を成膜する工程と
を備え、
上記酸化物膜および上記隣接膜の成膜工程では、上記酸化物膜と上記隣接膜とは隣接するように成膜され、
上記酸化物膜の成膜工程では、GeおよびGe酸化物の混合物ターゲットをスパッタリングすることにより上記酸化物膜を成膜し、
上記酸化物膜の吸収係数kが、0.15≦k≦0.90であることを特徴とする光記録媒体の製造方法。 A method for producing an optical recording medium having an inorganic recording film,
Forming an adjacent film made of metal;
Forming an oxide film made of Ge oxide,
In the film formation step of the oxide film and the adjacent film, the oxide film and the adjacent film are formed so as to be adjacent to each other,
In the film formation step of the oxide film, the oxide film is formed by sputtering a mixture target of Ge and Ge oxide,
The method for producing an optical recording medium, wherein an absorption coefficient k of the oxide film is 0.15 ≦ k ≦ 0.90.
少なくともGe粉末およびGe酸化物粉末とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタリングターゲット。 A sputtering target made of a semiconductor unsaturated oxide,
A sputtering target obtained by mixing at least a Ge powder and a Ge oxide powder and firing the mixture under pressure.
少なくともTi金属粉末とTi窒化物粉末とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタリングターゲット。 A sputtering target made of an unsaturated nitride of Ti,
A sputtering target comprising: mixing at least a Ti metal powder and a Ti nitride powder, and pressurizing and firing the mixture.
少なくともTi粉末と、Si粉末と、Ti窒化物粉末およびSi窒化物粉末のうち少なくとも一方とを混合し、該混合物を加圧焼成してなることを特徴とするスパッタターゲット。 A sputtering target made of an unsaturated nitride of Ti,
A sputtering target obtained by mixing at least a Ti powder, a Si powder, and at least one of a Ti nitride powder and a Si nitride powder, and firing the mixture under pressure.
上記Siの含有量が、8原子%以上32原子%以下であることを特徴とするスパッタリングターゲット。 A target containing at least Si and Ti,
A sputtering target, wherein the Si content is 8 atomic% or more and 32 atomic% or less.