JP2007050440A - Method and apparatus for manufacturing copper wire - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method and an apparatus for manufacturing a copper wire in which a copper-oxide coating film formed on the surface of a bar-shaped base stock is removed by a simple constitution of the apparatus and also, even in the case where the copper oxide generated in a casting stage or the like is pressed into the interior (the vicinity of the outer layer) of the bar-shaped base stock, a high-quality copper wire can be produced by removing the copper oxide pressed into the interior. <P>SOLUTION: The method for manufacturing the copper wire has a continuously casting stage where a bar-shaped ingot 21 is continuously produced and a continuously rolling stage where a bar-shaped base stock 22 is obtained by rolling the bar-shaped ingot 21 with a plurality of rolling rolls 40, 50 which are arranged in multistage and the copper wire 23 is produced by furthermore rolling the bar-shaped base stock 22. The continuous rolling stage has a finish rolling stage where the surface of the copper wire is formed with finishing rolls 34 and a rolling/polishing stage where the bar-shaped base stock is polished while rolling it with rolling/polishing rolls 35. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a copper wire manufacturing method and a manufacturing apparatus for continuously manufacturing a copper wire by consistently performing from casting to rolling.

Conventionally, as a method for producing the copper wire, a production method using a belt caster type continuous casting machine and a continuous rolling device is widely known (see Patent Document 1 and Patent Document 2).
The belt caster type continuous casting machine used in this manufacturing method has a cast wheel having a groove formed on the outer peripheral surface, and an endless belt that is circulated so as to contact a part of the outer periphery of the cast wheel. The molten metal continuously supplied from a large melting furnace such as a shaft furnace is injected into the space formed between the groove and the endless belt to be cooled and solidified to continuously cast a bar-shaped ingot. Is.

  A continuous rolling device is connected to the belt caster type continuous casting machine, and a copper wire having a predetermined outer diameter is produced by rolling the continuously produced bar-shaped ingot with the continuous rolling device. Can do. As described above, in the method for producing a copper wire using a belt caster type continuous casting machine, a copper wire can be produced at a high speed in a series of production lines by continuously casting and continuously rolling a molten copper from a melting furnace. It is possible to produce a large amount of copper wire at a low cost.

In the manufacturing method, since the high-temperature bar-shaped ingot as cast is rolled as it is, a copper oxide film is easily formed on the surface of the rolled bar-shaped material, and this copper oxide film is formed inside the bar-shaped material during rolling. There was a risk of being pushed into (near the surface layer). The copper wire obtained by rolling the rod-shaped material with the copper oxide film being pushed in has copper oxide inside, but is difficult to distinguish in appearance. When this copper wire is further processed, there is a possibility that troubles such as disconnection of the copper wire or damage to the copper wire may occur.
Moreover, the copper oxide film formed on the surface of the rod-shaped material may peel off in the rolling process and adhere to the surface of the rolling roll. There was a problem that the copper oxide adhering to the rolling roll was pushed into the rod-shaped material and mixed into the copper wire.

In order to prevent the copper oxide film from being generated on the surface of the rod-shaped material, Patent Document 3 proposes a method for producing a copper wire in which the rolling process is performed in a low oxygen partial pressure atmosphere.
In this copper wire manufacturing method, the process of rolling a rod-shaped material is performed in a low oxygen partial pressure atmosphere filled with an inert gas such as nitrogen gas, and a copper oxide film is formed on the surface of the rod-shaped material. This can prevent the above-described trouble caused by the indentation of copper oxide.
JP-A-55-126353 Japanese Patent Publication No.59-6736 JP 2002-103003 A

  By the way, in the manufacturing method of the copper wire described in patent document 3, it is necessary to accommodate several rolling rolls in the space controlled to the inert gas atmosphere (low oxygen partial pressure atmosphere), and the equipment structure becomes complicated. There was a problem that the manufacturing cost of the copper wire manufacturing apparatus would be high. Moreover, since it is necessary to control the oxygen partial pressure in the space low, there is a problem that the manufacturing cost of the copper wire is increased.

  Moreover, about the copper oxide film of the bar-shaped ingot formed in the casting process before the rolling process, and the copper oxide film formed in the rolling process performed outside the space, the generation cannot be suppressed, These copper oxide films may be pushed into the inside of the rod-shaped material (near the surface layer) during initial rolling. The copper oxide that has been pushed into the rod-shaped material cannot be removed even if the subsequent rolling process is performed in a low oxygen partial pressure atmosphere, so it may remain inside the copper wire and cause problems such as surface scratches. was there.

  The present invention has been made in view of the above-described circumstances, and can remove the copper oxide film formed on the surface of the rod-shaped material with a simple apparatus configuration, and the copper oxide generated in the casting process or the like is inside the rod-shaped material. To provide a copper wire manufacturing method and a copper wire manufacturing apparatus capable of producing a high-quality copper wire by removing the pressed copper oxide even when pressed into (near the surface layer). With the goal.

  In order to solve the above-described problems, a method for producing a copper wire according to the present invention includes a continuous casting step of continuously producing a bar-shaped ingot, and the bar-shaped ingot by a plurality of rolling rolls arranged in multiple stages. Rolling to obtain a rod-shaped material, and further rolling the rod-shaped material to produce a copper wire, and a copper wire manufacturing method, wherein the continuous rolling step is performed by a finish rolling roll. It has a finish rolling process which shape | molds the surface of a copper wire, and the rolling grinding | polishing process which grind | polishes while rolling the said rod-shaped raw material with a rolling grinding | polishing roll before this finishing rolling process.

According to the copper wire manufacturing method of this configuration, in the rolling polishing step provided before the finish rolling step for forming the surface of the copper wire, the copper oxide film formed on the surface of the rod-shaped material can be removed, and the rod-shaped material The copper oxide pushed into the vicinity of the surface layer can also be removed.
Here, in the continuous rolling process after the continuous casting process, the speed at which the rod-shaped material passes between the rolls and the rotation speed of the rolling rolls do not completely coincide with each other, and thus have a constant speed of a certain width. The surface of the rod-shaped material is polished by the sliding of the surface of the rod-shaped material and the roll surface of the polishing roll.

Moreover, since it has the rolling grinding | polishing process which served as both rolling and grinding | polishing, copper oxide can be removed without providing a grinding | polishing mechanism separately, and an installation structure can be simplified.
Moreover, since the bar-shaped raw material from which the copper oxide has been removed is supplied to the finishing rolling process, a copper wire free from copper oxide can be produced. Furthermore, polishing scratches formed on the surface of the rod-shaped material when polished can be eliminated by the finish rolling step, and the surface of the copper wire can be finished smoothly.

  In addition, as a rolling polishing roll used in the rolling polishing step, by using a blast roll whose surface is subjected to blasting, a rod-shaped material can be rolled by pressing with a rolling roll, and a blasted roll The surface of the rod-shaped material can be polished by the surface.

  Here, it is preferable that the arithmetic average roughness Ra of the roll surface of the roll polishing roll is in the range of 1.0 μm ≦ Ra ≦ 10.0 μm. By making the arithmetic average roughness Ra of the roll surface 1.0 μm or more, the rod-shaped material can be reliably polished, and by setting Ra to 10.0 μm or less, the surface of the rod-shaped material is deeply damaged. Can be prevented.

  Furthermore, by cleaning the surface of the roll by spraying rolling oil at a high pressure on at least one of the rolling rolls arranged before the rolling polishing step, the copper oxide attached to the rolling roll is removed. The copper oxide can be reliably removed and the copper oxide can be prevented from being pushed into the rod-shaped material.

  The copper wire manufacturing apparatus according to the present invention includes a continuous casting apparatus for continuously producing a bar-shaped ingot, and rolling the bar-shaped ingot to obtain a bar-shaped material, and further rolling the bar-shaped material. A copper wire manufacturing apparatus having a continuous rolling device for producing the copper wire, wherein the continuous rolling device is provided with a plurality of rolling rolls, and the copper wire among the plurality of rolling rolls. The rolling roll that forms the surface of the rolling roll is a finishing rolling roll, and at least one of the rolling rolls arranged before the finishing rolling roll is a rolling polishing roll that polishes the rod-shaped material while rolling it. It is characterized by that.

  According to the copper wire manufacturing apparatus having this configuration, a finish rolling roll for forming the surface of the copper wire is disposed, and a rolling polishing roll that combines rolling and polishing is disposed in front of the finish rolling roll. Therefore, after polishing the surface of the rod-shaped material to remove the copper oxide film formed on the surface of the rod-shaped material and the copper oxide pushed in the vicinity of the surface, it is rolled with a finishing rolling roll, so that there is no contamination with copper oxide. Quality copper wire can be produced. In addition, a roll polishing roll that serves both as rolling and polishing is disposed, so that it is not necessary to provide a separate polishing apparatus, and copper oxide can be removed with a simple equipment configuration.

Here, by using a blast roll having a roll surface subjected to a blast treatment as the rolling polishing roll, the surface of the rod-shaped material can be reliably polished and rolled.
Further, by setting the arithmetic average roughness Ra of the roll surface of the roll polishing roll within the range of 1.0 μm ≦ Ra ≦ 10.0 μm, the surface of the rod-shaped material is reliably polished without causing a deep scratch. be able to.

  Furthermore, the roll surface is washed with the rolling oil by providing a high pressure jetting mechanism for spraying the rolling oil to the roll surface at a high pressure with respect to at least one of the rolling rolls arranged in front of the rolling polishing roll. Thus, it is possible to remove the copper oxide attached to the roll, prevent the copper oxide attached to the roll surface from being pushed into the rod-shaped material, and easily and reliably remove the copper oxide in the polishing step.

  As described above, according to the present invention, the copper oxide film generated on the surface of the rod-shaped material can be removed with a simple apparatus configuration, and the copper oxide generated in the casting process or the like is pushed into the rod-shaped material (near the surface layer). Even in this case, it is possible to provide a copper wire manufacturing method and a copper wire manufacturing apparatus capable of producing a high-quality copper wire by removing the pressed copper oxide.

Hereinafter, a copper wire manufacturing apparatus and a manufacturing method according to embodiments of the present invention will be described with reference to the accompanying drawings. FIG. 3 shows an outline of a copper wire manufacturing apparatus according to an embodiment of the present invention.
The copper wire manufacturing apparatus 1 includes a melting furnace A, a holding furnace B, a casting rod C, a belt caster continuous casting machine D, a continuous rolling apparatus E, and a coiler F.

In this embodiment, a shaft furnace having a cylindrical furnace body is used as the melting furnace A. A plurality of burners (not shown) are arranged in a multistage shape in the vertical direction at the lower part of the furnace body. And the electrolytic copper which is a raw material is inserted from the upper part of a furnace main body, is melt | dissolved by the combustion of the said burner, and a copper molten metal is made continuously.
The holding furnace B is for temporarily storing the molten copper produced in the melting furnace A while holding it at a predetermined temperature, and sending a certain amount of the molten copper to the casting iron C.
The cast iron C is to transfer the molten copper sent from the holding furnace B to the tundish 11 disposed above the belt caster type continuous casting machine D.

A pouring nozzle 12 is disposed at the end of the tundish 11 in the flow direction of the molten copper, and the molten copper in the tundish 11 is supplied to the belt caster continuous casting machine D through the pouring nozzle 12. .
The belt caster type continuous casting machine D has a cast wheel 13 having a groove formed on the outer peripheral surface thereof, and an endless belt 14 that is circulated so as to contact a part of the outer peripheral surface of the cast wheel 13. The molten copper supplied via the pouring nozzle 12 is poured into the space formed between the groove and the endless belt 14 and cooled to continuously cast the bar-shaped ingot 21.

  The belt caster continuous casting machine D is connected to a continuous rolling device E. The continuous rolling device E continuously rolls the bar-shaped ingot 21 produced from the belt caster type continuous casting machine D to produce a copper wire 23 having a predetermined outer diameter. The copper wire 23 produced from the continuous rolling device E is wound around the coiler F via the cleaning / cooling device 15 and the flaw detector 16.

The cleaning cooling device 15 cleans the surface of the copper wire 23 produced from the continuous rolling device E while cleaning the surface with a cleaning agent such as alcohol.
The flaw detector 16 detects flaws in the copper wire 23 sent from the cleaning / cooling device 15. The flaw detector 16 passes through the flaw detector 16 and is shipped as a product.

Next, the continuous rolling apparatus E will be described. FIG. 1 shows a continuous rolling apparatus E used in the copper wire manufacturing apparatus 1 according to this embodiment.
As shown in FIG. 1, the continuous rolling apparatus E includes a plurality of rolling rolls 40 and 50 arranged in tandem inside an outer cover 31. An inlet 32 for inserting the bar-shaped ingot 21 is formed on one end side of the outer cover 31, and an outlet 33 for manufacturing the copper wire 23 is formed on the other end side of the outer cover 31. In the outer cover 31, vertical rolling rolls 40 for rolling the bar-shaped ingot 21 and the bar-shaped material 22 in the vertical direction and horizontal rolling rolls 50 for rolling in the horizontal direction are alternately arranged.

  Five sets of the first vertical rolling roll 41, the second vertical rolling roll 42, the third vertical rolling roll 43, the fourth vertical rolling roll 44, and the fifth vertical rolling roll 45 are arranged as the vertical rolling roll 40 from the loading port 32 side. Has been. Further, as the horizontal rolling roll 50, five sets of the first horizontal rolling roll 51, the second horizontal rolling roll 52, the third horizontal rolling roll 53, the fourth horizontal rolling roll 54, and the fifth horizontal rolling roll 55 from the loading port 32 side. Is arranged.

  Each of the vertical rolling rolls 40 is supported so as to be rotatable in the vertical direction, and is driven to rotate in the arrow direction shown in FIG. 1 by a power source (not shown). The vertical rolling rolls 40 are each paired and rolled by sandwiching the bar-shaped ingot 21 or the bar-shaped material 22 in the vertical direction. Further, the horizontal rolling rolls 50 are respectively supported so as to be rotatable in the horizontal direction, and are driven to rotate in the arrow direction shown in FIG. 1 by a power source (not shown). The horizontal rolling rolls 50 are each paired and rolled by sandwiching the bar-shaped ingot 21 or the bar-shaped material 22 in the horizontal direction.

  Of the vertical rolling roll 40 and the horizontal rolling roll 50 arranged in this way, the fifth vertical rolling roll 45 and the fifth horizontal rolling roll 55 arranged closest to the outlet 33 form the surface of the copper wire 23. It is set as the finishing rolling roll 34 to do. The finish rolling roll 34 is composed of a smooth roll whose roll surface 34A is a smooth surface as shown in FIG. 2, and can smoothly finish the surface of the copper wire 23. Note that shot peening may be applied to the surface 34A of the finish rolling roll 34. In shot peening, countless metal balls are collided at high speed to form micro unevenness on the roll surface. This is preferable because the surface hardness increases and the fatigue strength also increases and the durability of the roll is improved.

  And at least one of the rolling rolls arranged on the loading port 32 side of the finishing rolling roll 34 is a rolling polishing roll 35 constituted by a blast roll whose roll surface has been subjected to blasting. In the embodiment, as shown in FIG. 1, the third vertical rolling roll 43, the third horizontal rolling roll 53, the fourth vertical rolling roll 44, and the fourth horizontal rolling roll 54 are used as the roll polishing roll 35. Blasting is a process in which a granular material made of a hard material is collided at high speed to form macro unevenness on the roll surface.

  Here, as shown in FIG. 3, the roll surface 35A of the roll polishing roll 35 has irregularities caused by the blast treatment, and the arithmetic average roughness Ra of the surface is 1.0 μm ≦ Ra ≦ 10.0 μm. It is set to be within the range. In the present embodiment, the arithmetic average roughness Ra of the roll surface 35A of the roll polishing roll 35 is set to be in the range of 3.0 μm ≦ Ra ≦ 6.0 μm.

Moreover, the 1st vertical rolling roll 41, the 1st horizontal rolling roll 51, the 2nd vertical rolling roll 42, and the 2nd horizontal rolling roll 52 are comprised by the smooth roll with a smooth roll surface. The surface of these rolling rolls may be shot peened to improve durability.
The first vertical rolling roll 41 and the first horizontal rolling roll 51 are provided with a nozzle 36 for spraying rolling oil onto the roll surface at a high pressure.

Next, a copper wire manufacturing method using the copper wire manufacturing apparatus 1 having the above-described configuration will be described.
First, a copper raw material such as electric copper is charged into the furnace body of the melting furnace A, and the copper raw material is melted by burning a burner to obtain a molten copper. This molten copper is sent to the holding furnace B and is transferred to the tundish 11 through the casting rod C while being kept at a predetermined temperature. Then, it is supplied from the tundish 11 to the space formed between the casting wheel 13 and the endless belt 14 of the belt caster continuous casting machine D through the pouring nozzle 12, cooled and solidified to form a bar-shaped ingot 21. Produced.

  The bar-shaped ingot 21 continuously produced by the belt caster type continuous casting machine D is supplied to the continuous rolling device E. The bar-shaped ingot 21 is charged from the charging port 32 of the continuous rolling apparatus E, and is initially rolled by the first vertical rolling roll 41 and the first horizontal rolling roll 51 to become the bar-shaped material 22. The rod-shaped material 22 is further divided into a second vertical rolling roll 42, a second horizontal rolling roll 52, a third vertical rolling roll 43, a third horizontal rolling roll 53, a fourth vertical rolling roll 44, a fourth horizontal rolling roll 54, and a fifth. The copper wire 23 having a predetermined outer diameter is continuously rolled by the vertical rolling roll 45 and the fifth horizontal rolling roll 55 and produced from the production outlet 33.

  Here, in order to roll the bar-shaped ingot 21 produced from the belt caster type continuous casting machine D at a high temperature in the atmosphere, a copper oxide film is generated on the surface of the bar-shaped material 22. The copper oxide film may be crushed when being rolled and pushed into the vicinity of the surface of the rod-shaped material 22. Moreover, the crushed copper oxide may adhere to the roll surface and be pushed into the rod-shaped material 22 being rolled. Such a phenomenon is likely to occur in the initial rolling stage where the temperature of the rod-shaped material 22 is high, that is, the first vertical rolling roll 41, the first horizontal rolling roll 51, the second vertical rolling roll 42, the second horizontal rolling roll 52, and the like. Is.

  In the present embodiment, the fifth vertical rolling roll 45 and the fifth horizontal rolling roll 55 that are located closest to the outlet 33 are the finishing rolling roll 34 that forms the surface of the copper wire 23, and this finishing rolling roll 34. The third vertical rolling roll 43, the third horizontal rolling roll 53, the fourth vertical rolling roll 44, and the fourth horizontal rolling roll 54 on the side of the loading port 32 are more than a rolling polishing roll 35 constituted by a blast roll. Yes. The rotational speed of these rolling polishing rolls 35 and the passing speed of the rod-shaped material 22 passing between these rolls do not completely coincide with each other and have a relative speed. It is set to be 04 m / sec or more.

  The rotational speed of the third vertical rolling roll 43, the third horizontal rolling roll 53, the fourth vertical rolling roll 44, the fourth horizontal rolling roll 54, and the relative speed between the rod-shaped material 22, which are the rolling polishing rolls 35 in this way. Is set to be 0.04 m / sec or more, so that the surface of the rod-shaped material 22 is polished by sliding with the uneven roll surface 35A of the rolling polishing roll 35 (blast roll), The copper oxide film generated on the surface of the rod-shaped material 22 or the copper oxide pushed into the vicinity of the surface can be removed.

Further, although the surface of the rod-shaped material 22 is scratched by sliding with the roll surface 35A of the rolling polishing roll 35 (blast roll), the surface of the rod-shaped material 22 is smoothed by removing the surface damage by rolling with the finishing rolling roll 34. A copper wire 23 having a smooth surface can be produced.
Here, in the present embodiment, the arithmetic average roughness Ra of the roll surface 35A of the roll polishing roll 35 is set to be within a range of 3.0 μm ≦ Ra ≦ 6.0 μm. Polishing can be reliably performed without deep scratches on the surface, and the copper wire 23 having no scratches can be produced by rolling with the finish rolling roll 34.

  In the present embodiment, the first vertical rolling roll 41 and the first horizontal rolling roll 51 are provided with a nozzle 36 for spraying the rolling oil onto the roll surface at a high pressure. By spraying the rolling oil at a high pressure, The copper oxide adhered to the roll surface can be removed, the copper oxide can be suppressed from being pushed into the rod-shaped material 22, and the copper oxide can be reliably removed by polishing with the roll polishing roll 35.

  The copper wire 23 thus obtained is cleaned and cooled by the cleaning / cooling device 15, the flaw detector 16 detects the scratch, and the copper wire 23 having no quality problem is wound around the coiler F, Shipped as a product.

  In addition, although this embodiment demonstrated the continuous rolling apparatus provided with 5 sets of the vertical rolling rolls 40 and 5 sets of the horizontal rolling rolls 50, it is not limited to this. The number and arrangement of the rolling rolls may be different, a rolling polishing roll 35 for polishing the surface of the rod-shaped material 22, and a finishing rolling roll 34 for rolling the polished rod-shaped material 22 to form the surface of the copper wire 23. What is necessary is just to have.

  Moreover, although the vertical rolling roll 40 and the horizontal rolling roll 50 were continuously provided in the continuous rolling apparatus, it was not limited to this, For example, the 2nd horizontal rolling roll 50 and the 3rd vertical rolling roll 40 may be provided with an adjusting mechanism for adjusting the tension of the rod-shaped material 22.

Further, for example, by rolling the finish rolling roll 34 in a low oxygen partial pressure atmosphere as disclosed in Patent Document 3, it is ensured that the copper oxide film is generated again on the rod-shaped material 22 from which the copper oxide has been removed. This is preferable because a high quality copper wire 23 can be produced.
Furthermore, although the nozzle 36 which sprays rolling oil with high pressure with respect to the roll surface was demonstrated with what was provided in the 1st vertical rolling roll 41 and the 1st horizontal rolling roll 51, it is not limited to this, Other rolling A nozzle 36 may also be provided on the roll.

Below, the result of the confirmation experiment performed in order to confirm the effectiveness of this invention is demonstrated. The confirmation experiment was performed using the copper wire manufacturing apparatus according to the embodiment described above, changing the arithmetic average roughness Ra of the roll surface of the rolling polishing roll, and the flaw detection result of the produced copper wire and the remaining copper oxide. The state was compared. The relative speed between the rotational speed of the rolling abrasive roll and the rod-shaped material was set to 0.04 m / sec or more, and the rolling oil used was Quake Roll 560-MT manufactured by Nippon Quaker Chemical Co., Ltd., having a concentration of 8%. .
Here, the roll polishing roll is a blast roll that has been blasted on the roll surface. Alumina is used as a shot used for the blast treatment, and the roll surface roughness is adjusted by changing the shot diameter.

  The confirmation experiment results are shown in Table 1.

As shown in Table 1, when the arithmetic average roughness Ra of the roll polishing roll surface is set in the range of 1.0 μm to 10.0 μm, the copper oxide is removed and the surface has no scratches. Copper wire could be obtained.
When the arithmetic average roughness Ra of the roll surface of the roll polishing roll was smaller than 1.0 μm, the copper oxide film on the surface of the copper wire could be removed, but the copper oxide pushed into the copper wire remained. It was confirmed that Moreover, the surface damage resulting from this copper oxide was confirmed.
Further, when the arithmetic average roughness Ra of the roll surface of the roll polishing roll was larger than 10.0 μm, scratches due to polishing marks were confirmed on the surface of the copper wire.

Therefore, under the conditions of this confirmation experiment, by setting the arithmetic mean roughness Ra of the roll surface of the roll polishing roll within the range of 1.0 ≦ Ra ≦ 10.0, the copper oxide pushed into the inside is surely obtained. It was confirmed that it was possible to produce a high-quality copper wire with no scratches on the surface.
However, the present invention is not limited to this range, and it is preferable to adjust the arithmetic average roughness Ra of the roll surface according to the relative speed condition, the type of rolling oil, and the like.

It is explanatory drawing of the continuous rolling apparatus used for the manufacturing apparatus of the copper wire which is this embodiment. It is a front view of the finishing rolling roll with which the continuous rolling apparatus of FIG. 1 was equipped. It is a front view of the rolling grinding | polishing roll with which the continuous rolling apparatus of FIG. 1 was equipped. It is the schematic diagram which showed schematically the manufacturing apparatus of the copper wire which is this embodiment.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Copper wire manufacturing apparatus 21 Rod-shaped ingot 22 Rod-shaped raw material 23 Copper wire 34 Finish rolling roll 35 Roll polishing roll 36 Nozzle (spouting mechanism)
D belt caster type continuous casting machine (continuous casting machine)
E Continuous rolling equipment

Claims (8)

A continuous casting process for continuously producing a bar-shaped ingot, and rolling the bar-shaped ingot by a plurality of rolling rolls arranged in multiple stages to obtain a bar-shaped material, and further rolling the bar-shaped material to obtain a copper wire A method of producing a copper wire having a continuous rolling step to produce,
The continuous rolling step includes a finish rolling step of forming the surface of the copper wire with a finish rolling roll, and a rolling polishing step of polishing the rod-shaped material while rolling the rod-shaped material with a roll polishing roll before the finish rolling step; The manufacturing method of the copper wire characterized by having.   The method for producing a copper wire according to claim 1, wherein a blast roll having a roll surface subjected to a blast treatment is used as the rolled polishing roll.   3. The method for producing a copper wire according to claim 1, wherein an arithmetic average roughness Ra of the roll surface of the rolled polishing roll is in a range of 1.0 μm ≦ Ra ≦ 10.0 μm. .   The surface of the roll is washed by spraying rolling oil at a high pressure on at least one of the rolling rolls arranged before the rolling polishing step. The manufacturing method of the copper wire in any one. Copper having a continuous casting apparatus for continuously producing a bar-shaped ingot, and a continuous rolling apparatus for rolling the rod-shaped ingot to obtain a rod-shaped material and further rolling the rod-shaped material to produce the copper wire Wire manufacturing equipment,
In the continuous rolling apparatus, a plurality of rolling rolls are arranged in multiple stages, and the rolling roll that forms the surface of the copper wire among the plurality of rolling rolls is a finishing rolling roll, which is upstream of the finishing rolling roll. At least one of the rolling rolls arranged on the roll is a rolled polishing roll that polishes the rod-shaped material while rolling it.   The said rolling polishing roll is a blast roll by which the blast process was performed to the roll surface which contacts the said rod-shaped raw material, The manufacturing apparatus of the copper wire of Claim 5 characterized by the above-mentioned.   7. The copper wire manufacturing apparatus according to claim 5, wherein an arithmetic average roughness Ra of the roll surface of the rolled polishing roll is in a range of 1.0 μm ≦ Ra ≦ 10.0 μm. .   The continuous rolling device is provided with an ejection mechanism that sprays rolling oil onto the surface of the roll at a high pressure with respect to at least one of the rolling rolls arranged in front of the polishing roll. The manufacturing apparatus of the copper wire in any one of Claims 5-7.