JP2006327891A - Decorating method for transparent glass plate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a decorating method where decoration for a glass plate can be performed easily and inexpensively by special pretreatment on the glass plate surface. <P>SOLUTION: The glass plate surface 1 is processed by the pretreatment that a transparent organic coating 2 excellent in adhesiveness to glass is coated, baked and dried. The decorating method on the glass plate surface is easily performed by transferring a decoration design pattern printed on a hydraulic transferring film 5 to a coated surface with the transparent organic coating 2. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a decoration processing method in the case where a glass plate is used for a mater portion which is one of external components such as a warm air heater.

  As a processing method in the case where the transparent glass plate 1 that has been decorated is used as a mater of appearance components of this type of hot air heating apparatus main body 9 shown in FIG. 8 of the conventional example, as shown in FIG. In general, a single-color silk-printed surface 10 is processed on one side of the transparent glass plate 1 corresponding to the portion, and then the adhesive-coated surface 11 is protected by a release separator resin film 12 for preventing scattering. The film 8 was processed by being pasted via the adhesive application surface 11 after the release separator resin film 12 portion was peeled off.

Although it differs from the said prior art example, there existed some which used the glass plate as a mather of the external appearance component of a warm air heating apparatus main body as shown in patent document 1. FIG.
JP 2004-198083 A

  However, the conventional method for decorating the transparent glass plate has a limited range of silk printing, and there is a limit to the design of the printing pattern and coloring. Regardless, it was difficult to improve the sense of luxury design.

  In order to solve the above-mentioned conventional problems, the decoration processing method for the transparent glass plate of the present invention is a decoration glass plate of a mater part that constitutes an exterior part of a warm air heating device or the like. As a process of applying a transparent organic paint that adheres well to inorganic glass on one side of a transparent glass plate, baking and drying, and then applying a decorated hydraulic transfer film to the transparent organic paint application surface. .

  According to the above invention, since the glass plate itself is inorganic, it is impossible to decorate and decorate with a conventional hydraulic transfer film, so once the transparent organic paint is applied to one side of the glass plate, baking and drying After that, various patterns and various colors can be processed and transferred by making it possible to decorate the transparent organic paint baking surface with a hydraulic transfer film.

  The method for decorating a transparent glass plate according to the present invention allows various patterns and various colors to be processed and transferred onto an inorganic glass plate.

  1st invention is the transparent organic glass which adheres well to the inorganic glass on one side of the transparent glass plate as the decoration processing method in the decorative glass plate of the mater part which constitutes the exterior part of the hot air heater or the like After applying the paint, baking and drying, the process is a process in which the decorated hydraulic transfer film is transferred onto the transparent organic paint application surface.

  And, in order to decorate and adhere the decorative and printed hydraulic transfer film to the transparent glass plate, by applying a transparent organic paint on one end of the inorganic glass surface that cannot be bonded, baking and drying, In the same way that conventional hydraulic transfer films can be easily transferred and adhered to the surface of resin parts, it is possible to easily transfer and adhere to glass surfaces, so that various patterns of hydraulic transfer films can be freely transferred to transparent glass plates. There is also an effect that the adhesive application can be applied and an effect that the glass plate surface serves as a protection for preventing scratches on the thin film which has been transfer bonded.

  2nd invention made it the process of carrying out the transfer coating of the hydraulic transfer film for decorating, after giving light coloring by mixing an appropriate pigment with the transparent type organic paint which adheres and applies to the single side | surface of a transparent type glass plate. Is.

  And, to make it possible to easily transfer and decorate the decorated hydraulic transfer film to the transparent glass plate, as a pretreatment, by coloring the transparent organic paint previously applied to the transparent glass plate, the same hydraulic transfer Even if a film is used, there is an effect that the color tone of the decorative pattern can be easily changed depending on the degree of coloring.

  In the third aspect of the invention, when a transparent organic paint that adheres well to inorganic glass is applied to one side of the transparent glass plate, masking or the like is protected so that the transparent organic paint does not adhere to the end face of the transparent glass plate. After the coating and baking and drying, the decorative transfer film is transferred and coated so that the transfer coating on the end face of the glass plate does not adhere.

  And the decorated hydraulic transfer film takes advantage of the property that it does not adhere to the inorganic glass surface, and the application surface of the transparent organic paint to the transparent glass plate is limited to only one surface of the glass plate surface. By limiting the film adhesion surface at the time of transfer film transfer processing and preventing the film from adhering to the glass end face, there is an effect that the crystal feeling of the end face can be sufficiently secured.

  4th invention apply | coats the transparent type organic coating material which adheres well to inorganic glass on the single side | surface of a transparent type | system | group glass plate, transcribe | transfers and paints the hydraulic transfer film for decorating, and, after that, the protective coloring coating on it This is a coating process.

  And, as a second means of changing the color tone of the decorative pattern, after applying a transparent organic paint to the transparent glass plate separately from the second invention, baking and drying, after the transfer transfer treatment of the hydraulic transfer film as before, In order to protect the film surface and the degree of freedom of the color tone of the decorative pattern, by applying a protective coloring paint and baking and drying from above, the decorative film is scratched from both the glass surface and the protective coloring paint. At the same time as preventing and protecting, it is effective as a new means of changing the color of the decorative pattern.

  5th invention, after apply | coating the surface which does not adhere to the surface where a transparent organic coating material adheres to the application surface of a glass surface using a pattern paper etc., when apply | coating the transparent organic coating material applied to the single side | surface of a transparent glass plate, After baking and drying, the decorated hydraulic transfer film is transferred and coated.

  And, when applying the transparent organic paint to be applied to the glass surface as a pretreatment for the decorative processing of the transparent glass plate, by using a pattern paper, the portion where the transparent organic paint adheres to the glass surface and baked, the pattern paper, etc. By allowing the glass surface to remain uncoated and remain in an inorganic surface state, the decorative film can be transferred and bonded to the glass surface without bonding. This allows the design process to remain, and has the effect of creating a more original design sensation.

  6th invention has the process of sticking the scattering prevention film at the time of a glass plate breakage | attachment on a decorating surface.

  And in order to ensure the safety | security when the glass plate by which the decoration process was carried out by the 1st-5th invention should be damaged, the film for scattering prevention is stuck on the transfer adhesion pasting side. This has the effect of improving safety in the event of an emergency.

  In the seventh invention, by coloring the film for preventing scattering in the sixth invention, the degree of freedom of the color of the decorative pattern same as the application of the protective coloring paint can be increased, and at the same time, preventing scattering when the glass is broken. The double effect that it can also be used is obtained.

  Hereinafter, embodiments of the present invention will be described with reference to the drawings. Note that the present invention is not limited to the embodiment.

(Embodiment 1)
1 (a), (b), (c), (d), and (e) are component cross-sectional views showing the processing steps of the decoration processing method for a transparent glass plate in Embodiment 1 of the present invention. As shown in FIG. 1B, a transparent organic paint 2 that can be applied and bonded to glass is applied to one side of the plate-like transparent glass plate 1 shown in FIG. Thereafter, as shown in FIG. 1 (c), the transparent glass plate 1 was baked and coated on the surface of the transparent transfer plate 5 on the hydraulic transfer film 5 on which the decorative pattern floated on the water surface of the aqueous solution 4 poured into the water tank 3 was printed. The whole is submerged as shown in FIG.

  At that time, the hydraulic transfer film 5 adheres only to the surface of the transparent glass plate 1 on which the transparent organic paint 2 is applied. Again, the excess area of the hydraulic transfer film 5 remains in 4 parts of the aqueous solution, or part of it adheres to the surface of the transparent glass plate 1 not coated with the transparent organic paint 2, but the hydraulic transfer film 5 Since it cannot adhere to the inorganic glass surface, the water pressure transfer film 5 does not remain completely on the surface other than the surface to which the transparent organic paint 2 is applied by washing it with a certain water pressure after taking it out from the aqueous solution 4. Accordingly, as shown in FIG. 1E, the transparent glass plate 1 is transferred and printed with the hydraulic transfer film 5 on which the decorative pattern is printed, through the transparent organic paint 2 baking surface. Then, in this state, it is possible to process the pattern on the transparent glass plate by baking and drying at a certain temperature.

(Embodiment 2)
2 (a) and 2 (b) are component cross-sectional views illustrating a process of decorating a glass plate in the second embodiment of the present invention. FIG. 2 (a) is applied and baked as a transparent colored organic paint 2a in which an appropriate color pigment is mixed with a transparent organic paint 2 applied as a pretreatment on one side of the transparent glass plate 1 shown in FIG. 1 (b). FIG. 2 (b) shows a dried state, and thereafter, using the hydraulic transfer film 5 on which a decorative pattern is printed in the same manner as in the first embodiment, it is baked and dried in the same manner as in FIG. 1 (e). This indicates a state in which the state is secured. In this case, unlike the case of FIG. 1 (e), the pattern transferred by the hydraulic transfer film 5 can be seen from the glass surface through the transparent colored organic paint 2a. It is possible to expand the color range of the decoration.

(Embodiment 3)
FIG. 3 is a component perspective view showing a third embodiment of the present invention. When the transparent organic coating 2 is applied to the surface of the transparent glass plate 1 as a pretreatment process of the transparent glass plate 1, not only the entire surface of the transparent glass plate 1, but also the entire peripheral end surfaces 1a, 1b, 1c, 1d are masked. In order to prevent the transparent organic paint 2 from adhering, and after ensuring the inorganic surface state of the glass material itself, after applying the transparent organic paint only to the back surface, baking and drying, and decorating with the hydraulic transfer film 5, As a processed product, the glass end faces 1a, 1b, 1c, and 1d can easily maintain the transparent crystal luxury feeling possessed by the glass itself.

(Embodiment 4)
FIG. 4 is a component cross-sectional view showing a fourth embodiment of the present invention. As shown in FIG. 4, after completion of FIG. 1 (e) of the first embodiment, as an additional step, the protective coloring paint 6 is applied and added on the surface of the hydraulic transfer film 5. In this case as well, the color tone of the pattern decorated with the hydraulic transfer film 5 can be freely expanded, and at the same time, it can play a role in preventing and protecting the decorative surface from scratches.

(Embodiment 5)
FIGS. 5A, 5B, 5C, 5D, 5E, and 5F are cross-sectional views of parts showing examples of processing steps of the processing method according to the fifth embodiment of the present invention. FIG. 5 (a) is a part diagram showing an example of the pattern paper 7, in which die-cutting patterns 7a, 7b, 7c, 7d, 7e, and 7f are provided. FIG. 5 (b) shows a state in which this pattern 7 is set on one side of the transparent glass plate 1. From this state, when the transparent organic paint 2 is applied, As shown in FIG. 5 (c), the transparent organic paint 2 is applied only to the die cutting patterns 7a, 7b, 7c, 7d, 7e, and 7f of the pattern 7 on the surface. Therefore, after baking and drying in this state, as shown in FIG. 5 (d), a hydraulic transfer printing process is performed on the hydraulic transfer film 5 as shown in FIGS. 1 (c) and 1 (d) of the first embodiment. Only the portion to which the transparent organic paint 2 is applied by the die cutting process is decorated, and the other surfaces show the state of the transparent glass plate surface itself. FIG. 5E shows a reference cross-sectional view. In this case, since a step portion between the glass surface and the organic paint adhering portion is formed, the decorated portion is easily peeled off. Therefore, if possible, as shown in the cross-sectional reference diagram of FIG. As shown by the above, by applying the protective coloring paint 6, the disadvantages are covered, and the contrast with the decorative part becomes clearer, and the width of the design can be expanded.

(Embodiment 6)
FIG. 6 is a component cross-sectional view showing a sixth embodiment of the present invention. In this case, the transparent organic paint 2 and the hydraulic pressure applied to the transparent glass plate 1 in the first to fifth embodiments. In order to improve the safety when the glass body decorated with the transfer film 5 is broken, the anti-scattering film 8 should be applied to the decorative surface so that it will not scatter as much as possible even if the glass breaks. This improves safety.

(Embodiment 7)
FIG. 7 is a component cross-sectional view showing a seventh embodiment of the present invention. In this case, unlike the sixth embodiment, the scattering prevention film 8 is colored to form a colored scattering prevention film 8a. Thus, there is an effect that the protective coloring paint 6 shown in FIG. 4 in the fourth embodiment and FIG. 5F in the fifth embodiment can be eliminated.

  Since the decorative processing method to the transparent glass plate of the present invention can process and transfer various patterns and various colors to an inorganic glass plate, it can be used for a cooker in addition to being used for a mater constituting an exterior part. It can also be used for members that are used for visual effects, such as glass tops.

(A) (b) (c) (d) (e) Part sectional drawing which shows an example of the decorating process in Embodiment 1 of this invention. (A) (b) Part sectional drawing which shows an example of the decorating method in Embodiment 2 Component perspective view which shows an example of the decoration processing method in Embodiment 3 Component sectional drawing which shows an example of the decoration processing method in Embodiment 4 (A) (b) (c) (d) (e) (f) Part sectional drawing which shows an example of the decorating process in Embodiment 5 Component sectional drawing which shows an example of the decorating method in the Embodiment 6 Component sectional drawing which shows an example of the decoration processing method in Embodiment 7 External view of conventional hot air heater Component cross-sectional view showing an example of conventional decorating method

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Transparent glass plate 2 Transparent organic paint 2a Transparent coloring organic paint 5 Hydraulic transfer film 9 Hot air heating apparatus main body 10 Printing surface 11 Adhesive coating surface

Claims (7)

In the decorative glass plate of the mate section that constitutes the exterior part of the hot air heater, etc., as a decoration processing method, a transparent organic paint that adheres well to inorganic glass is applied to one side of the transparent glass plate, dried by baking Later, a decorative processing method on a transparent glass plate in which a decorated hydraulic transfer film is transferred onto a transparent organic paint coating surface. The transparent according to claim 1, wherein a transparent pigment is mixed with a transparent organic paint to be adhesively applied to one side of a transparent glass plate to give a light color, and then a hydraulic transfer film for decoration is transferred and coated. Decorating method for glass plates. When applying a transparent organic paint that adheres well to inorganic glass on one side of the transparent glass plate, protect it from masking to prevent the transparent organic paint from adhering to the end surface of the transparent glass plate, and after baking and drying The method for decorating a transparent glass plate according to claim 1 or 2, wherein a transfer coating on the end surface of the glass plate is prevented from adhering to the decorative transfer film by transfer coating. Applying a transparent organic paint that adheres well to inorganic glass on one side of a transparent glass plate, baking and drying, then applying a hydraulic transfer film for decorating, and then applying a protective colored coating on top Item 1. A method for decorating transparent glass according to item 1. When applying a transparent organic paint to one side of a transparent glass plate, use a pattern paper or the like to form a surface with or without a transparent organic paint on the glass surface, then bake and dry, then decorate The process for decorating a transparent glass plate according to claim 1, wherein the applied hydraulic transfer film is transferred and coated. The decoration processing method to the transparent glass plate of any one of Claims 1-5 which has the process of affixing the scattering prevention film at the time of a glass plate breakage | damage on a decorating surface. The decoration processing method to the transparent glass plate of Claim 6 using the scattering prevention film which gave the coloring process.