JP2006276657A - Positive resist composition and pattern forming method using same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a positive resist composition improved in thickness reduction of a resist film after pattern development and deterioration of a pattern profile in normal exposure, and further improved in elution of a resist component into a immersion solution, pattern collapse or deterioration of a profile after immersion exposure in liquid immersion exposure, and to provide a pattern forming method using the composition. <P>SOLUTION: The positive resist composition contains: (A) a resin the solubility of which with an alkali developing solution is increased by an action of an acid; (B) a compound which generates an acid by irradiation with active rays or radiation; and (F) a surfactant having a basic group. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a positive resist composition used in a semiconductor manufacturing process such as an IC, a circuit board such as a liquid crystal or a thermal head, and also in a lithography process for other photo applications, and a pattern forming method using the same. It is. In particular, the present invention relates to a positive resist composition suitable for exposure with a projection exposure apparatus using far ultraviolet light having a wavelength of 300 nm or less as a light source, and a pattern forming method using the same.

With the miniaturization of semiconductor elements, the exposure light source has become shorter in wavelength and the projection lens has a higher numerical aperture (high NA). Currently, an exposure machine with NA 0.84 using an ArF excimer laser having a 193 nm wavelength as a light source has been developed. ing. These can be expressed by the following equations as is generally well known.
(Resolving power) = k ₁ · (λ / NA)
(Depth of focus) = ± k ₂ · λ / NA ²
Where λ is the wavelength of the exposure light source, NA is the numerical aperture of the projection lens, and k ₁ and k ₂ are coefficients related to the process.

An exposure machine using a F ₂ excimer laser having a wavelength of 157 nm as a light source has been studied for higher resolution by further shortening the wavelength. Lens materials and resists used in the exposure apparatus for shorter wavelength have been studied. Because the materials used in the process are very limited, it is very difficult to stabilize the manufacturing cost and quality of the apparatus and materials, and the exposure apparatus and resist that have sufficient performance and stability within the required period are not in time. The possibility is coming out.

As a technique for increasing the resolving power in an optical microscope, a so-called immersion method in which a high refractive index liquid (hereinafter also referred to as “immersion liquid”) is filled between a projection lens and a sample is known.
This “immersion effect” means that when λ ₀ is the wavelength of the exposure light in the air, n is the refractive index of the immersion liquid with respect to air, θ is the convergence angle of the light beam, and NA ₀ = sin θ. The above-described resolving power and depth of focus can be expressed by the following equations.
(Resolving power) = k ₁ · (λ ₀ / n) / NA ₀
(Depth of focus) = ± k ₂ · (λ ₀ / n) / NA ₀ ²
That is, the immersion effect is equivalent to using an exposure wavelength having a wavelength of 1 / n. In other words, in the case of a projection optical system with the same NA, the depth of focus can be increased n times by immersion.
This is effective for all pattern shapes, and can be combined with a super-resolution technique such as a phase shift method and a modified illumination method which are currently being studied.

Examples of apparatuses in which this effect is applied to transfer of a fine image exposure pattern of a semiconductor element include Patent Document 1 (Japanese Patent Laid-Open No. 57-153433), Patent Document 2 (Japanese Patent Laid-Open No. 7-220990), and Patent Document 3. (Japanese Examined Patent Publication No. 63-49893) and the like, but the resist suitable for the immersion exposure technique is not discussed.
Patent Document 4 (Japanese Patent Laid-Open No. 10-303114) points out that the refractive index control of the immersion liquid is important because the change in the refractive index of the immersion liquid causes deterioration of the projected image due to the wavefront aberration of the exposure machine. Disclosed is a water to which the temperature coefficient of the refractive index of the immersion liquid is controlled within a certain range and, as a suitable immersion liquid, an additive that lowers the surface tension or increases the surface activity is added. Has been. However, the disclosure of additives and the resist suitable for the immersion exposure technique are not discussed.

Recent progress in immersion exposure technology is described in Non-Patent Document 1 (SPIE Proc 4688, 11 (2002)), Non-Patent Document 2
(J. Vac. Sci. Tecnol. B, 17 (1999)). In the case of using an ArF excimer laser as a light source, pure water (refractive index at 193 nm: 1.44) is considered to be most promising as an immersion liquid in terms of handling safety, transmittance at 193 nm, and refractive index. .
When an F ₂ excimer laser is used as a light source, a solution containing fluorine has been studied from the balance between transmittance and refractive index at 157 nm. However, a sufficient product has not yet been seen in terms of environmental safety and refractive index. It has not been issued. From the degree of immersion effect and the degree of completeness of the resist, the immersion exposure technique is considered to be installed in the ArF exposure machine earliest.

Since the resist for KrF excimer laser (248 nm), an image forming method called chemical amplification has been used as an image forming method for a resist in order to compensate for sensitivity reduction due to light absorption. Explaining by taking a positive chemical amplification image forming method as an example, the acid generator in the exposed area is decomposed by exposure to generate an acid upon exposure, and the generated acid is reacted as a reaction catalyst by post exposure baking (PEB). Is used to change an alkali-insoluble group to an alkali-soluble group, and an exposed portion is removed by alkali development.
Although the resist for ArF excimer laser (193 nm) using this chemical amplification mechanism is becoming mainstream at present, further improvement is required from the viewpoint of reduction in resist film thickness after development and fine pattern profile rectangularity. It was.

  In immersion exposure, the resist film and the optical lens are filled with an immersion liquid (also referred to as an immersion liquid) and exposed through a photomask to transfer the photomask pattern to the resist film. It is expected that the penetration into the resist film will affect the chemical reaction (acid-catalyzed deprotection reaction, development reaction) caused in the resist during or after exposure. But I still do n’t know.

  When a chemically amplified resist is applied to the immersion exposure technique, the acid on the resist surface generated during exposure moves to the immersion liquid, and the acid concentration on the exposed portion surface changes. This was a major problem at the beginning of the development of chemically amplified positive resists. The exposure surface area was exposed to a very small amount of basic contamination of several ppb level from the environment during exposure-PEB (PED: Post Exposure time Delay). Although it seems to be very similar to acid deactivation, the influence and mechanism of immersion exposure on the resist has not yet been clarified.

  In immersion exposure, the resist film comes into contact with the immersion liquid during exposure, so that the resist film component elutes into the immersion liquid and contaminates the exposure machine lens, and the immersion liquid penetrates into the resist film and resists the resist. There has been concern about adverse effects on performance, and image performance such as resist pattern collapse and profile degradation, and improvements have been required.

  The resist composition used for immersion exposure is described in, for example, Patent Document 5 (International Publication No. 2004-068242 pamphlet), Patent Document 6 (International Publication No. 2004-074937 pamphlet), and the like. In the resist composition, there is room for improvement in terms of prevention of elution of resist film components into the immersion liquid and lithography characteristics.

JP-A-57-153433 JP-A-7-220990 Japanese Examined Patent Publication No. 63-49893 JP-A-10-303114 International Publication No. 2004-068242 Pamphlet International Publication No. 2004-074937 Pamphlet Proc. SPIE, 2002, Vol. 4688, p. 11 J. Vac. Sci. Tecnol. B, 17 (1999)

  In view of the above problems, an object of the present invention is to improve a resist film thickness reduction after pattern development and to provide a good pattern profile during normal exposure, and to use the positive resist composition A pattern forming method. Also, during immersion exposure, the resist component is not easily dissolved into the immersion liquid and is good, and the resist pattern collapses and the profile deterioration after immersion exposure is improved. Positive type suitable for immersion exposure. It is an object of the present invention to provide a resist composition and a pattern forming method using the same.

  The present invention is a positive resist composition for normal exposure and immersion exposure having the following constitution and a pattern forming method using the same, thereby achieving the object of the present invention.

(1) (A) a resin whose solubility in an alkaline developer is increased by the action of an acid, (B) a compound that generates an acid upon irradiation with actinic rays or radiation, and (C) a surfactant having a basic group. A positive resist composition characterized by the above.
(2) The positive resist composition as described in (1) above, wherein the resin as the component (A) has an alicyclic hydrocarbon structure.

(3) The positive resist composition as described in (1) or (2) above, wherein the surfactant of component (C) has a structure having a structure represented by the following general formula (1): .
(4) The positive resist composition as described in (3) above, further having a structure represented by the general formula (2).

In the general formula (1), R ₁ represents a hydrogen atom or an alkyl group. X ₁ represents a basic group. l represents an integer of 1 to 50.
In the general formula (2), R ₂ represents a hydrogen atom or an alkyl group. R ₃ represents a linking group. Rf represents an alkyl group, a fluoroalkyl group or a fluoroalkylcarbonyl group. m represents an integer of 1 to 50.

(5) The positive resist composition as described in (1) or (2) above, wherein the surfactant of component (C) has a structure represented by the following general formula (3).

In general formula (3),
R ₄ represents a linking group. R ₅ represents a hydrogen atom or an alkyl group. Rf represents an alkyl group, a fluoroalkyl group or a fluoroalkylcarbonyl group. X ₂ and X ₃ each independently represents a hydrogen atom, an alkyl group, an alkylcarbonyl group, a lactone group, or a basic group. n represents an integer of 1 to 50.

(6) A step of forming a resist film from the chemically amplified resist composition for immersion process according to any one of (1) to (5), exposing the resist film, and developing the resist film. Pattern forming method.
(7) including a step of forming a resist film from the chemically amplified resist composition for immersion process according to any one of (1) to (5), exposing the resist film to immersion exposure, and developing the resist film. A characteristic pattern forming method.

INDUSTRIAL APPLICABILITY According to the present invention, it is possible to provide a positive resist composition in which the resist film thickness is reduced and the rectangularity of the fine pattern profile is improved during normal exposure, and a pattern forming method using the same.
Furthermore, the positive resist composition suitable for immersion exposure has less elution of resist components in the immersion liquid during immersion exposure, and the resist pattern collapses after immersion exposure and profile deterioration is improved. An object and a pattern forming method using the same can be provided.

Hereinafter, the present invention will be described in detail.
In addition, in the description of the group (atomic group) in this specification, the description which does not describe substitution and non-substitution includes what does not have a substituent and what has a substituent. . For example, the “alkyl group” includes not only an alkyl group having no substituent (unsubstituted alkyl group) but also an alkyl group having a substituent (substituted alkyl group).

[1] Resin whose solubility in an alkaline developer is increased by the action of an acid The resin contained in the positive resist composition of the present invention is a resin whose solubility in an alkaline developer is increased by the action of an acid (also referred to as an acid-decomposable resin). And a repeating unit having a group (acid-decomposable group) that is decomposed by the action of an acid to generate a group soluble in an alkali developer.
Examples of the group soluble in an alkali developer (alkali-soluble group) include a hydroxyl group, a carboxy group, and a sulfonic acid group.
The acid-decomposable group may be present in the main chain or side chain of the resin, or in both the main chain and side chain.
A preferred group as the acid-decomposable group is a group in which the hydrogen atom of the —COOH group is substituted with a group capable of leaving with an acid.
Examples of the acid-decomposable group include a cumyl ester group, an enol ester group, an acetal ester group, and a tertiary alkyl ester group. More preferable examples include tertiary alkyl ester groups.

Furthermore, as the acid-decomposable group, for example, —O—C (R ₃₆ ) (R ₃₇ ) (R ₃₈ ), —O—C (R ₃₆ ) (R ₃₇ ) (OR ₃₉ ), —O—C (= O) —O—C (R ₃₆ ) (R ₃₇ ) (R ₃₈ ), —O—C (R ₀₁ ) (R ₀₂ ) (OR ₃₉ ), —O—C (R ₀₁ ) (R ₀₂ ) —C (= O) -OC (R ₃₆ ) (R ₃₇ ) (R ₃₈ ) and the like can be mentioned.
In the formula, R _{36 to} R ₃₉ each independently represents an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group, or an alkenyl group. R ₃₆ and R ₃₇ , R ₃₆ and R ₃₉ may be bonded to each other to form a ring.
R _{01 and} R ₀₂ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkenyl group.
Note that —C (R ₃₆ ) (R ₃₇ ) (R ₃₈ ) means a group in which each group represented by R _{36 to} R ₃₈ is bonded to a carbon atom with a single bond.

The acid-decomposable group is preferably a tertiary ester, and preferably has a cyclic aliphatic group such as groups represented by the following general formulas (pI) to (pV).
In the acid-decomposable resin, the content of the repeating unit having an acid-decomposable group is preferably 10 to 60 mol%, more preferably 20 to 50 mol%, still more preferably 25 to 40 mol% in all repeating structural units. is there.

  The acid-decomposable resin preferably has an alicyclic hydrocarbon structure. The alicyclic hydrocarbon structure may be monocyclic or polycyclic.

  As a resin having an alicyclic hydrocarbon structure, decomposed by the action of an acid, and increased in solubility in an alkali developer (hereinafter also referred to as “alicyclic hydrocarbon-based acid-decomposable resin”), the following general formula (pI ) To a resin containing at least one selected from the group consisting of repeating units having a partial structure containing an alicyclic hydrocarbon represented by the general formula (pV) and repeating units represented by the following general formula (II-AB) It is preferable that

In general formulas (pI) to (pV),
R ₁₁ represents a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group or a sec-butyl group, and Z is an atom necessary for forming a cycloalkyl group together with a carbon atom. Represents a group.
R _{12 to} R ₁₆ each independently represents a linear or branched alkyl group or cycloalkyl group having 1 to 4 carbon atoms, provided that at least one of R _{12 to} R ₁₄ , or R ₁₅ , Any of R ₁₆ represents a cycloalkyl group.
R _{17 to} R ₂₁ each independently represents a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, or a cycloalkyl group, provided that at least one of R _{17 to} R ₂₁ is cyclo Represents an alkyl group. Further, either R ₁₉ or R ₂₁ represents a linear or branched alkyl group or cycloalkyl group having 1 to 4 carbon atoms.
R _{22 to} R ₂₅ each independently represents a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, or a cycloalkyl group, provided that at least one of R _{22 to} R ₂₅ is cyclo Represents an alkyl group. R ₂₃ and R ₂₄ may be bonded to each other to form a ring.

In the formula (II-AB),
R ₁₁ ′ and R ₁₂ ′ each independently represents a hydrogen atom, a cyano group, a halogen atom or an alkyl group. Z ′ represents an atomic group for forming an alicyclic structure containing two bonded carbon atoms (C—C).

  The general formula (II-AB) is more preferably the following general formula (II-AB1) or general formula (II-AB2).

In the formulas (II-AB1) and (II-AB2),
R ₁₃ ′ to R ₁₆ ′ each independently represents a hydrogen atom, a halogen atom, a cyano group, —COOH, —COOR ₅ , a group that decomposes by the action of an acid, —C (═O) —XA′—R. ₁₇ ′ represents an alkyl group or a cycloalkyl group.
Here, R ₅ represents an alkyl group, a cycloalkyl group, or a group having a lactone structure.
X represents an oxygen atom, a sulfur atom, -NH -, - NHSO ₂ - or an -NHSO ₂ NH-.

A ′ represents a single bond or a divalent linking group.
Further, at least two of R ₁₃ ′ to R ₁₆ ′ may be bonded to form a ring. n represents 0 or 1.
R ₁₇ ′ represents —COOH, —COOR ₅ (R ₅ is the same as described above), —CN, hydroxyl group, alkoxy group, —CO—NH—R ₆ , —CO—NH—SO ₂ —R ₆ or a lactone structure. Represents a group having
R ₆ represents an alkyl group or a cycloalkyl group.

In the general formulas (pI) to (pV), the alkyl group in R _{12 to} R ₂₅ represents a linear or branched alkyl group having 1 to 4 carbon atoms.

The cycloalkyl group in R _{11 to} R ₂₅ or the cycloalkyl group formed by Z and the carbon atom may be monocyclic or polycyclic. Specific examples include groups having a monocyclo, bicyclo, tricyclo, tetracyclo structure or the like having 5 or more carbon atoms. The carbon number is preferably 6-30, and particularly preferably 7-25. These cycloalkyl groups may have a substituent.

  Preferred cycloalkyl groups include adamantyl group, noradamantyl group, decalin residue, tricyclodecanyl group, tetracyclododecanyl group, norbornyl group, cedrol group, cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group, A cyclodecanyl group and a cyclododecanyl group can be mentioned. More preferable examples include an adamantyl group, norbornyl group, cyclohexyl group, cyclopentyl group, tetracyclododecanyl group, and tricyclodecanyl group.

  As further substituents of these alkyl groups and cycloalkyl groups, alkyl groups (1 to 4 carbon atoms), halogen atoms, hydroxyl groups, alkoxy groups (1 to 4 carbon atoms), carboxyl groups, alkoxycarbonyl groups (carbon numbers) 2-6). Examples of the substituent that the alkyl group, alkoxy group, alkoxycarbonyl group and the like may further have include a hydroxyl group, a halogen atom, and an alkoxy group.

  The structures represented by the general formulas (pI) to (pV) in the resin can be used for protecting alkali-soluble groups. Examples of the alkali-soluble group include various groups known in this technical field.

  Specific examples include a structure in which a hydrogen atom of a carboxylic acid group, a sulfonic acid group, a phenol group, or a thiol group is substituted with a structure represented by the general formulas (pI) to (pV), preferably a carboxylic acid Group, a hydrogen atom of a sulfonic acid group is substituted with a structure represented by general formulas (pI) to (pV).

  As the repeating unit having an alkali-soluble group protected by the structure represented by the general formulas (pI) to (pV), a repeating unit represented by the following general formula (pA) is preferable.

Here, R represents a hydrogen atom, a halogen atom, or a linear or branched alkyl group having 1 to 4 carbon atoms. A plurality of R may be the same or different.
A represents a single bond, an alkylene group, an ether group, a thioether group, a carbonyl group, an ester group, an amide group, a sulfonamide group, a urethane group, or a urea group, or a combination of two or more groups. Represents. A single bond is preferable.
Rp1 represents any group of the above formulas (pI) to (pV).

  The repeating unit represented by the general formula (pA) is most preferably a repeating unit of 2-alkyl-2-adamantyl (meth) acrylate and dialkyl (1-adamantyl) methyl (meth) acrylate.

  Specific examples of the repeating unit represented by the general formula (pA) are shown below.

Examples of the halogen atom in R ₁₁ ′ and R ₁₂ ′ include a chlorine atom, a bromine atom, a fluorine atom, and an iodine atom.

Examples of the alkyl group in R ₁₁ ′ and R ₁₂ ′ include a linear or branched alkyl group having 1 to 10 carbon atoms.

  The atomic group for forming the alicyclic structure of Z ′ is an atomic group that forms a repeating unit of an alicyclic hydrocarbon which may have a substituent in a resin, and among them, a bridged type alicyclic group. An atomic group for forming a bridged alicyclic structure forming a cyclic hydrocarbon repeating unit is preferred.

Examples of the skeleton of the alicyclic hydrocarbon formed include the same alicyclic hydrocarbon groups as R _{11 to} R _{25 in} the general formulas (pI) to (pVI).

The alicyclic hydrocarbon skeleton may have a substituent. Examples of such a substituent include R ₁₃ ′ to R ₁₆ ′ in the general formula (II-AB1) or (II-AB2).

  In the alicyclic hydrocarbon-based acid-decomposable resin according to the present invention, the group decomposed by the action of an acid has a partial structure containing the alicyclic hydrocarbon represented by the general formula (pI) to the general formula (pV). It can be contained in at least one kind of repeating unit among the repeating unit having, the repeating unit represented by formula (II-AB), and the repeating unit of the copolymerization component described later.

Various substituents of R ₁₃ ′ to R ₁₆ ′ in the general formula (II-AB1) or the general formula (II-AB2) are atomic groups for forming an alicyclic structure in the general formula (II-AB). It can also be a substituent of the atomic group Z for forming a bridged alicyclic structure.

  Specific examples of the repeating unit represented by the general formula (II-AB1) or (II-AB2) include the following specific examples, but the present invention is not limited to these specific examples.

The alicyclic hydrocarbon-based acid-decomposable resin of the present invention preferably has a lactone group. As the lactone group, any group can be used as long as it contains a lactone structure, but a group containing a 5- to 7-membered ring lactone structure is preferred, and a bicyclo structure is added to the 5- to 7-membered ring lactone structure, Those in which other ring structures are condensed to form a spiro structure are preferred. It is more preferable to have a repeating unit having a group having a lactone structure represented by any of the following general formulas (LC1-1) to (LC1-15). Further, a group having a lactone structure may be directly bonded to the main chain. Preferred lactone structures are (LC1-1) (LC1-4) (LC1-5) (LC1-6) (LC1-13) (LC1-14). By using a specific lactone structure, line edge roughness, Development defects are improved.

  The lactone structure portion may or may not have a substituent (Rb2). As preferred substituents (Rb2), an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 4 to 7 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkoxycarbonyl group having 1 to 8 carbon atoms, a carboxyl group, Examples thereof include a halogen atom, a hydroxyl group, a cyano group, and an acid-decomposable group. When n2 is 2 or more, a plurality of Rb2s may be the same or different, and a plurality of Rb2s may be bonded to form a ring.

As the repeating unit having a group having a lactone structure represented by any one of the general formulas (LC1-1) to (LC1-13), R _{13 in the} general formula (II-A) or (II-B) is used. Wherein at least one of 'to R ₁₆ ' has a group represented by the general formulas (LC1-1) to (LC1-16) (for example, R _{5 of} -COOR ₅ is represented by the general formulas (LC1-1) to (LC1) -16) or a repeating unit represented by the following general formula (AI).

In general formula (AI), R _b0 represents a hydrogen atom, a halogen atom, or an alkyl group having 1 to 4 carbon atoms. Preferable substituents that the alkyl group for R _b0 may have include a hydroxyl group and a halogen atom.

Examples of the halogen atom for R _b0 include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. R _b0 is preferably a hydrogen atom or a methyl group.

A _b is an alkylene group, a divalent linking group having a monocyclic or polycyclic alicyclic hydrocarbon structure, a single bond, an ether group, an ester group, a carbonyl group, a carboxyl group, or a divalent group obtained by combining these. Represents. Preferably a single bond, -Ab1-CO ₂ - is a linking group represented by.
Ab1 is a linear, branched alkylene group, monocyclic or polycyclic cycloalkylene group, preferably a methylene group, an ethylene group, a cyclohexyl group, an adamantyl group, or a norbornyl group.

  V represents a group represented by any one of the general formulas (LC1-1) to (LC1-16).

The repeating unit having a lactone structure usually has an optical isomer, but any optical isomer may be used. One optical isomer may be used alone, or a plurality of optical isomers may be mixed and used. When one kind of optical isomer is mainly used, the optical purity (ee) thereof is preferably 90 or more, more preferably 95 or more.
Specific examples of the repeating unit having a group having a lactone structure are given below, but the present invention is not limited thereto.

  The alicyclic hydrocarbon-based acid-decomposable resin of the present invention preferably contains a repeating unit having an alicyclic hydrocarbon structure substituted with a polar group. This improves the substrate adhesion and developer compatibility. The polar group is preferably a hydroxyl group or a cyano group.

In general formula (VIIa), R _{2c to} R _4c each independently represents a hydrogen atom, a hydroxyl group or a cyano group. However, at least one of R _{2c to} R _4c represents a hydroxyl group or a cyano group. Preferably, one or two of R _{2c to} R _4c are a hydroxyl group and the remaining is a hydrogen atom, more preferably two of R _{2c to} R _4c are a hydroxyl group and the remaining is a hydrogen atom.

  The group represented by the general formula (VII) is preferably a dihydroxy body or a monohydroxy body, and more preferably a dihydroxy body.

As the repeating unit having a group represented by the general formula (VIIa) or (VIIb), at least one of R ₁₃ ′ to R ₁₆ ′ in the general formula (II-A) or (II-B) is the above. Those having a group represented by the general formula (VII) (for example, R _{5 of} —COOR ₅ represents a group represented by the general formula (VII)), or a repeating unit represented by the following general formula (AII) Can be mentioned.

In the general formulas (AIIa) and (AIIb), R _1c represents a hydrogen atom, a methyl group, a trifluoromethyl group, or a hydroxymethyl group.

  Specific examples of the repeating unit having a structure represented by the general formulas (AIIa) and (AIIb) are given below, but the present invention is not limited thereto.

  The alicyclic hydrocarbon-based acid-decomposable resin may contain a repeating unit represented by the following general formula (VIII).

In the general formula (VIII), Z ₂ represents —O— or —N (R ₄₁ ) —. R ₄₁ represents a hydrogen atom, a hydroxyl group, an alkyl group, or —OSO ₂ —R ₄₂ . R ₄₂ represents an alkyl group, a cycloalkyl group or a camphor residue. The alkyl group of R ₄₁ and R ₄₂ may be substituted with a halogen atom (preferably a fluorine atom) or the like.

  Examples of the repeating unit represented by the general formula (VIII) include the following specific examples, but the present invention is not limited thereto.

  The alicyclic hydrocarbon-based acid-decomposable resin preferably has a repeating unit having an alkali-soluble group, and more preferably has a repeating unit having a carboxyl group. By containing this, the resolution in contact hole applications increases. The repeating unit having a carboxyl group includes a repeating unit in which a carboxyl group is directly bonded to the main chain of the resin, such as a repeating unit of acrylic acid or methacrylic acid, or a carboxyl group in the main chain of the resin through a linking group. Any of the bonded repeating units is preferable, and the linking group may have a monocyclic or polycyclic hydrocarbon structure. Most preferred are acrylic acid and methacrylic acid.

  The alicyclic hydrocarbon-based acid-decomposable resin may further have a repeating unit having 1 to 3 groups represented by the general formula (F1). This improves line edge roughness performance.

In the general formula (Z), R ₅₀ ~R ₅₅ independently represents a hydrogen atom, a fluorine atom or an alkyl group. However, at least one of R _{50 to} R ₅₅ represents a fluorine atom or an alkyl group in which at least one hydrogen atom is substituted with a fluorine atom. Rx represents a hydrogen atom or an organic group (preferably an acid-decomposable protecting group, an alkyl group, a cycloalkyl group, an acyl group, or an alkoxycarbonyl group).

The alkyl group of R _{50 to} R ₅₅ may be substituted with a halogen atom such as a fluorine atom, a cyano group, etc., preferably an alkyl group having 1 to 3 carbon atoms, such as a methyl group or a trifluoromethyl group. be able to. R _{50 to} R ₅₅ are preferably all fluorine atoms.

  Examples of the organic group represented by Rx include an acid-decomposable protective group and an optionally substituted alkyl group, cycloalkyl group, acyl group, alkylcarbonyl group, alkoxycarbonyl group, alkoxycarbonylmethyl group, alkoxymethyl group. , 1-alkoxyethyl group is preferable.

  The repeating unit having the general formula (F1) is preferably a repeating unit represented by the following general formula (F2).

In the formula, Rx represents a hydrogen atom, a halogen atom, or an alkyl group having 1 to 4 carbon atoms. Preferable substituents that the alkyl group of Rx may have include a hydroxyl group and a halogen atom.
Fa represents a single bond or a linear or branched alkylene group (preferably a single bond).
Fb represents a monocyclic or polycyclic hydrocarbon group.
Fc represents a single bond or a linear or branched alkylene group (preferably a single bond or a methylene group).
F ₁ represents a group represented by the general formula (F1).
P1 represents 1-3.
The cyclic hydrocarbon group for Fb is preferably a cyclopentyl group, a cyclohexyl group, or a norbornyl group.

  Specific examples of the repeating unit having the structure of the general formula (F1) are shown.

  In addition to the above repeating structural units, the alicyclic hydrocarbon-based acid-decomposable resin has dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and general required properties of resist, resolving power and heat resistance. In order to adjust sensitivity and the like, various repeating structural units can be contained.

  Examples of such a repeating structural unit include, but are not limited to, repeating structural units corresponding to the following monomers.

Thereby, performance required for the alicyclic hydrocarbon-based acid-decomposable resin, in particular,
(1) Solubility in coating solvent,
(2) Film formability (glass transition point),
(3) Alkali developability,
(4) Membrane slip (hydrophobic, alkali-soluble group selection),
(5) Adhesion of unexposed part to substrate,
(6) Dry etching resistance,
Etc. can be finely adjusted.

  As such a monomer, for example, a compound having one addition polymerizable unsaturated bond selected from acrylic acid esters, methacrylic acid esters, acrylamides, methacrylamides, allyl compounds, vinyl ethers, vinyl esters, etc. Etc.

  In addition, any addition-polymerizable unsaturated compound that can be copolymerized with monomers corresponding to the above various repeating structural units may be copolymerized.

  In alicyclic hydrocarbon-based acid-decomposable resins, the molar ratio of each repeating structural unit is the resist's dry etching resistance, standard developer suitability, substrate adhesion, resist profile, and resolution that is a general required performance of resists. In order to adjust heat resistance, sensitivity, etc., it is set appropriately.

Preferred embodiments of the alicyclic hydrocarbon-based acid-decomposable resin include the following.
(1) What contains the repeating unit which has a partial structure containing the alicyclic hydrocarbon represented by said general formula (pI)-(pV) (side chain type). Preferably those containing (meth) acrylate repeating units having a structure of (pI) to (pV).
(2) Containing repeating units represented by general formula (II-AB) (main chain type)
However, in (2), for example, the following can be further mentioned.
(3) A repeating unit represented by the general formula (II-AB), a maleic anhydride derivative and a (meth) acrylate structure (hybrid type)

  In the alicyclic hydrocarbon-based acid-decomposable resin, the content of the repeating unit having an acid-decomposable group is preferably 10 to 60 mol%, more preferably 20 to 50 mol%, still more preferably 25 in all repeating structural units. -40 mol%.

  In the alicyclic hydrocarbon-based acid-decomposable resin, the content of the repeating unit having a partial structure containing an alicyclic hydrocarbon is generally 10 to 70 mol% in all repeating structural units, more preferably. It is 15 to 65 mol%, more preferably 20 to 60 mol%.

  In the alicyclic hydrocarbon-based acid-decomposable resin, the content of the repeating unit having a partial structure containing the alicyclic hydrocarbon represented by the general formulas (pI) to (pV) is 25 to 70 in all the repeating structural units. The mol% is preferable, more preferably 35 to 65 mol%, and still more preferably 40 to 60 mol%.

  In the alicyclic hydrocarbon-based acid-decomposable resin, the content of the repeating unit represented by the general formula (II-AB) is preferably 10 to 60 mol%, more preferably 15 to 55 mol% in all repeating structural units. More preferably, it is 20-50 mol%.

  In addition, the content of the repeating structural unit based on the monomer of the further copolymer component in the resin can also be appropriately set according to the performance of the desired resist. ) To 99 p% of the total number of moles of the repeating structural unit having a partial structure containing an alicyclic hydrocarbon represented by (pV) and the repeating unit represented by the general formula (II-AB). The following is preferable, More preferably, it is 90 mol% or less, More preferably, it is 80 mol% or less.

When the composition of the present invention is for ArF exposure, the resin preferably has no aromatic group from the viewpoint of transparency to ArF light.
The alicyclic hydrocarbon-based acid-decomposable resin used in the present invention is preferably one in which all of the repeating units are composed of (meth) acrylate repeating units. In this case, all of the repeating units may be methacrylate, all of the repeating units may be acrylate, or a mixture of methacrylate / acrylate, but the acrylate repeating unit is preferably 50 mol% or less of the entire repeating unit. More preferably 25 to 50% of repeating units having a partial structure containing an alicyclic hydrocarbon represented by general formulas (pI) to (pV), 25 to 50% of repeating units containing the lactone structure, and the polar group 5 to 20% of a terpolymer having 5 to 30% of repeating units having an alicyclic hydrocarbon structure substituted with, or 5 to 20 of repeating units containing a carboxyl group or a structure represented by formula (F1). % Quaternary copolymer.

  The alicyclic hydrocarbon-based acid-decomposable resin used in the present invention can be synthesized according to a conventional method (for example, radical polymerization). For example, as a general synthesis method, a monomer polymerization method in which a monomer species and an initiator are dissolved in a solvent and the polymerization is performed by heating, and a solution of the monomer species and the initiator is dropped into the heating solvent over 1 to 10 hours. The dropping polymerization method is added, and the dropping polymerization method is preferable. Examples of the reaction solvent include ethers such as tetrahydrofuran, 1,4-dioxane, diisopropyl ether, ketones such as methyl ethyl ketone and methyl isobutyl ketone, ester solvents such as ethyl acetate, amide solvents such as dimethylformamide and dimethylacetamide, Furthermore, the solvent which melt | dissolves the composition of this invention like the below-mentioned propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, and cyclohexanone is mentioned. More preferably, the polymerization is performed using the same solvent as that used in the resist composition of the present invention. Thereby, generation | occurrence | production of the particle at the time of a preservation | save can be suppressed.

  The polymerization reaction is preferably performed in an inert gas atmosphere such as nitrogen or argon. As a polymerization initiator, a commercially available radical initiator (azo initiator, peroxide, etc.) is used to initiate the polymerization. As the radical initiator, an azo initiator is preferable, and an azo initiator having an ester group, a cyano group, or a carboxyl group is preferable. Preferred initiators include azobisisobutyronitrile, azobisdimethylvaleronitrile, dimethyl 2,2′-azobis (2-methylpropionate) and the like. If desired, an initiator is added or added in portions, and after completion of the reaction, it is put into a solvent and a desired polymer is recovered by a method such as powder or solid recovery. The reaction concentration is generally 5 to 50% by mass, preferably 10 to 30% by mass. The reaction temperature is usually 10 ° C to 150 ° C, preferably 30 ° C to 120 ° C, more preferably 50 to 100 ° C.

[2] (B) Compound that generates acid upon irradiation with actinic ray or radiation Compound that generates acid upon irradiation with actinic ray or radiation (hereinafter referred to as “acid generator”) used in the positive resist composition of the present invention. Will be described below.
The acid generator used in the present invention can be selected from compounds generally used as an acid generator.
That is, it generates an acid upon irradiation with actinic rays or radiation used for photoinitiators of photocationic polymerization, photoinitiators of photoradical polymerization, photodecolorants of dyes, photochromic agents, or microresists. Known compounds and mixtures thereof can be appropriately selected and used.

  Examples thereof include diazonium salts, phosphonium salts, sulfonium salts, iodonium salts, imide sulfonates, oxime sulfonates, diazodisulfones, disulfones, and o-nitrobenzyl sulfonates.

  Further, a group that generates an acid upon irradiation with these actinic rays or radiation, or a compound in which a compound is introduced into the main chain or side chain of the polymer, for example, US Pat. No. 3,849,137, German Patent No. 3914407. JP, 63-26653, JP, 55-164824, JP, 62-69263, JP, 63-146038, JP, 63-163452, JP, 62-153853, The compounds described in JP-A 63-146029 can be used.

  Furthermore, compounds capable of generating an acid by light described in US Pat. No. 3,779,778, European Patent 126,712 and the like can also be used.

  Preferred compounds among the acid generators include compounds represented by the following general formulas (ZI), (ZII), and (ZIII).

In the above general formula (ZI), R ₂₀₁ , R ₂₀₂ and R ₂₀₃ each independently represents an organic group.
X ⁻ represents a non-nucleophilic anion.
The carbon number of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ is generally 1-30, preferably 1-20.
Two of R _{201 to} R ₂₀₃ may be bonded to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group.

The two of the group formed by bonding of the R ₂₀₁ to R _203, there can be mentioned an alkylene group (e.g., butylene, pentylene).

Specific examples of the organic group as R ₂₀₁ , R ₂₀₂ and R ₂₀₃ include corresponding groups in the compounds (Z1-1), (Z1-2) and (Z1-3) described later.

In addition, the compound which has two or more structures represented by general formula (ZI) may be sufficient. For example, the general formula at least one of R ₂₀₁ to R ₂₀₃ of a compound represented by (ZI) is, at least one bond with structure of R ₂₀₁ to R ₂₀₃ of another compound represented by formula (ZI) It may be a compound.

  More preferable examples of the (ZI) component include compounds (Z1-1), (Z1-2), and (Z1-3) described below.

Compound (Z1-1) is at least one of the aryl groups R ₂₀₁ to R ₂₀₃ in formula (ZI), arylsulfonium compound, i.e., a compound having arylsulfonium as a cation.

In the arylsulfonium compound, all of R _{201 to} R ₂₀₃ may be an aryl group, or R ₂₀₁
Some of to R ₂₀₃ is an aryl group with the remaining being an alkyl group or a cycloalkyl group.

  Examples of the arylsulfonium compound include triarylsulfonium compounds, diarylalkylsulfonium compounds, aryldialkylsulfonium compounds, diarylcycloalkylsulfonium compounds, aryldicycloalkylsulfonium compounds, and the like.

  The aryl group of the arylsulfonium compound is preferably a phenyl group or a naphthyl group, and more preferably a phenyl group. When the arylsulfonium compound has two or more aryl groups, the two or more aryl groups may be the same or different.

  The alkyl group that the arylsulfonium compound has as necessary is preferably a linear or branched alkyl group having 1 to 15 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an n-butyl group, sec- Examples thereof include a butyl group and a t-butyl group.

  The cycloalkyl group that the arylsulfonium compound has as necessary is preferably a cycloalkyl group having 3 to 15 carbon atoms, and examples thereof include a cyclopropyl group, a cyclobutyl group, and a cyclohexyl group.

The aryl group, alkyl group, and cycloalkyl group of R _{201 to} R ₂₀₃ are an alkyl group (for example, having 1 to 15 carbon atoms), a cycloalkyl group (for example, having 3 to 15 carbon atoms), an aryl group (for example, having 6 to 6 carbon atoms) 14), an alkoxy group (for example, having 1 to 15 carbon atoms), a halogen atom, a hydroxyl group, a phenylthio group or the like may be used as a substituent. Preferred substituents are linear or branched alkyl groups having 1 to 12 carbon atoms, cycloalkyl groups having 3 to 12 carbon atoms, and alkoxy groups having 1 to 12 carbon atoms, most preferably alkyl having 1 to 4 carbon atoms. Group, an alkoxy group having 1 to 4 carbon atoms. The substituent may be substituted with any one of the three R _{201 to} R ₂₀₃ , or may be substituted with all three. When R _{201 to} R ₂₀₃ are an aryl group, the substituent is preferably substituted at the p-position of the aryl group.

Examples of the non-nucleophilic anion as X ⁻ include a sulfonate anion, a carboxylate anion, a sulfonylimide anion, a bis (alkylsulfonyl) imide anion, and a tris (alkylsulfonyl) methyl anion.

  A non-nucleophilic anion is an anion that has an extremely low ability to cause a nucleophilic reaction, and is an anion that can suppress degradation over time due to an intramolecular nucleophilic reaction. This improves the temporal stability of the resist.

  Examples of the sulfonate anion include an aliphatic sulfonate anion, an aromatic sulfonate anion, and a camphor sulfonate anion.

  Examples of the carboxylate anion include an aliphatic carboxylate anion, an aromatic carboxylate anion, and an aralkylcarboxylate anion.

  Examples of the aliphatic group in the aliphatic sulfonate anion include, for example, an alkyl group having 1 to 30 carbon atoms, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, sec- Butyl, pentyl, neopentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl And an eicosyl group and a cycloalkyl group having 3 to 30 carbon atoms, specifically, a cyclopropyl group, a cyclopentyl group, a cyclohexyl group, an adamantyl group, a norbornyl group, a boronyl group, and the like.

  The aromatic group in the aromatic sulfonate anion is preferably an aryl group having 6 to 14 carbon atoms, such as a phenyl group, a tolyl group, and a naphthyl group.

  The alkyl group, cycloalkyl group, and aryl group in the aliphatic sulfonate anion and aromatic sulfonate anion may have a substituent.

  Examples of such substituents include nitro groups, halogen atoms (fluorine atoms, chlorine atoms, bromine atoms, iodine atoms), carboxyl groups, hydroxyl groups, amino groups, cyano groups, and alkoxy groups (preferably having 1 to 5 carbon atoms). ), A cycloalkyl group (preferably 3 to 15 carbon atoms), an aryl group (preferably 6 to 14 carbon atoms), an alkoxycarbonyl group (preferably 2 to 7 carbon atoms), an acyl group (preferably 2 to 12 carbon atoms). ), An alkoxycarbonyloxy group (preferably having 2 to 7 carbon atoms), an alkylthio group (preferably having 1 to 15 carbon atoms), and the like. About the aryl group and ring structure which each group has, an alkyl group (preferably C1-C15) can further be mentioned as a substituent.

  Examples of the aliphatic group in the aliphatic carboxylate anion include those similar to the aliphatic group in the aliphatic sulfonate anion.

  Examples of the aromatic group in the aromatic carboxylate anion include the same aromatic groups as in the aromatic sulfonate anion.

  The aralkyl group in the aralkyl carboxylate anion is preferably an aralkyl group having 6 to 12 carbon atoms, such as a benzyl group, a phenethyl group, a naphthylmethyl group, a naphthylethyl group, and a naphthylmethyl group.

  The aliphatic group, aromatic group and aralkyl group in the aliphatic carboxylate anion, aromatic carboxylate anion and aralkylcarboxylate anion may have a substituent. Examples of the substituent include aliphatic sulfonic acid The same halogen atom, alkyl group, cycloalkyl group, alkoxy group, alkylthio group and the like as in the anion can be exemplified.

  Examples of the sulfonylimide anion include saccharin anion.

  The alkyl group in the bis (alkylsulfonyl) imide anion and tris (alkylsulfonyl) methyl anion is preferably an alkyl group having 1 to 5 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, An isobutyl group, a sec-butyl group, a pentyl group, a neopentyl group, and the like can be given. These alkyl groups may have a substituent, and examples of the substituent include a halogen atom, an alkyl group substituted with a halogen atom, an alkoxy group, an alkylthio group, and the like, which are substituted with a fluorine atom. Alkyl groups are preferred.

  Examples of other non-nucleophilic anions include fluorinated phosphorus, fluorinated boron, and fluorinated antimony.

Examples of the non-nucleophilic anion of X ⁻ include an aliphatic sulfonate anion in which the α-position of the sulfonic acid is substituted with a fluorine atom, an aromatic sulfonate anion substituted with a fluorine atom or a group having a fluorine atom, and an alkyl group. A bis (alkylsulfonyl) imide anion substituted with a fluorine atom and a tris (alkylsulfonyl) methide anion wherein an alkyl group is substituted with a fluorine atom are preferred. The non-nucleophilic anion is particularly preferably a perfluoroaliphatic sulfonic acid anion having 4 to 8 carbon atoms, an aromatic sulfonic acid anion having a fluorine atom, most preferably a nonafluorobutanesulfonic acid anion, a perfluorooctanesulfonic acid anion, It is a pentafluorobenzenesulfonic acid anion and 3,5-bis (trifluoromethyl) benzenesulfonic acid anion.

Next, the compound (Z1-2) will be described.
The compound (Z1-2) is a compound when R _{201 to} R ₂₀₃ in the general formula (ZI) each independently represents an organic group not containing an aromatic ring. Here, the aromatic ring includes an aromatic ring containing a hetero atom.

The organic group having no aromatic ring as R ₂₀₁ to R ₂₀₃ generally has 1 to 30 carbon atoms, preferably 1 to 20 carbon atoms.

R _{201 to} R ₂₀₃ are each independently preferably an alkyl group, a cycloalkyl group, an allyl group, or a vinyl group, more preferably a linear, branched, cyclic 2-oxoalkyl group, or an alkoxycarbonylmethyl group, most preferably Is a linear, branched 2-oxoalkyl group.

The alkyl group as R _{201 to} R ₂₀₃ may be either linear or branched, and is preferably a linear or branched alkyl group having 1 to 10 carbon atoms, such as a methyl group, an ethyl group, or a propyl group. Butyl group, pentyl group and the like. More preferable examples of the alkyl group include a 2-linear or branched oxoalkyl group and an alkoxycarbonylmethyl group.

The cycloalkyl group as R ₂₀₁ to R ₂₀₃ is preferably a cycloalkyl group having 3 to 10 carbon atoms, e.g., cyclopentyl, cyclohexyl group and a norbornyl group. More preferred examples of the cycloalkyl group include a 2-oxocycloalkyl group.

  The 2-oxoalkyl group may be linear, branched or cyclic, and preferably includes a group having> C═O at the 2-position of the above alkyl group or cycloalkyl group.

  The alkoxy group in the alkoxycarbonylmethyl group is preferably an alkyl group having 1 to 5 carbon atoms (methyl group, ethyl group, propyl group, butyl group, pentyl group).

R _{201 to} R ₂₀₃ may be further substituted with a halogen atom, an alkoxy group (eg, having 1 to 5 carbon atoms), a hydroxyl group, a cyano group, or a nitro group.

Two members out of R _{201 to} R ₂₀₃ may combine to form a ring structure, and the ring may contain an oxygen atom, a sulfur atom, an ester bond, an amide bond, or a carbonyl group. The two of the group formed by bonding of the R ₂₀₁ to R _203, there can be mentioned an alkylene group (e.g., butylene, pentylene).

  The compound (Z1-3) is a compound represented by the following general formula (Z1-3), and is a compound having a phenacylsulfonium salt structure.

R _{1c to} R _5c each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an alkoxy group or a halogen atom.
R _6c and R _7c represent a hydrogen atom, an alkyl group, or a cycloalkyl group.
Rx and Ry each independently represents an alkyl group, a cycloalkyl group, an allyl group or a vinyl group.

Any two or more of R _{1c to} R _5c , and R _x and R _y may be bonded to each other to form a ring structure, and this ring structure includes an oxygen atom, a sulfur atom, an ester bond, and an amide bond. May be included.

Zc ⁻ represents a non-nucleophilic anion, and examples thereof include the same as the non-nucleophilic anion of X ^{− in} formula (ZI).

The alkyl group as R _{1c to} R _7c is preferably a linear or branched alkyl group having 1 to 20 carbon atoms, such as a methyl group, an ethyl group, a linear or branched propyl group, a linear or branched butyl group, A linear or branched pentyl group can be exemplified.

The cycloalkyl group as R _{1c to} R _7c is preferably a cycloalkyl group having 3 to 8 carbon atoms, and examples thereof include a cyclopentyl group and a cyclohexyl group.

The alkoxy group as R _{1c to} R _{5c may} be linear, branched or cyclic, for example, an alkoxy group having 1 to 10 carbon atoms, preferably a linear or branched alkoxy group having 1 to 5 carbon atoms. (For example, methoxy group, ethoxy group, linear or branched propoxy group, linear or branched butoxy group, linear or branched pentoxy group), C3-C8 cyclic alkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group) ).

Preferably, any one of R _{1c to} R _5c is a linear or branched alkyl group, a cycloalkyl group, or a linear, branched or cyclic alkoxy group, and more preferably the sum of the carbon number of R _{1c to} R _5c is 2 ~ 15. Thereby, solvent solubility improves more and generation | occurrence | production of a particle is suppressed at the time of a preservation | save.

_Examples of the alkyl group and cycloalkyl group as R _x and R _y include the same alkyl groups and cycloalkyl groups as R _{1c to} R _{7c, such} as a 2-oxoalkyl group and a 2-oxocycloalkyl group. An alkoxycarbonylmethyl group is more preferable.

Examples of the 2-oxoalkyl group and 2-oxocycloalkyl group include a group having> C═O at the 2-position of the alkyl group or cycloalkyl group as R _{1c to} R _7c .

Examples of the alkoxy group in the alkoxycarbonylmethyl group include the same alkoxy groups as R _{1c to} R _5c .

Examples of the group formed by combining R _x and R _y include a butylene group and a pentylene group.

R _x and R _y are preferably an alkyl group having 4 or more carbon atoms, more preferably 6 or more, and still more preferably 8 or more.

In formula (ZII), (ZIII), R 204 ~R 207 each independently represents an aryl group, an alkyl group or a cycloalkyl group.

Phenyl group and a naphthyl group are preferred as the aryl group of R ₂₀₄ to R _207, more preferably a phenyl group.

The alkyl group as R ₂₀₄ to R ₂₀₇ is preferably a linear or branched alkyl group having 1 to 10 carbon atoms, for example, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group).

The cycloalkyl group as R ₂₀₄ to R ₂₀₇ is preferably a cycloalkyl group having 3 to 10 carbon atoms, e.g., cyclopentyl, cyclohexyl group and a norbornyl group.

The R ₂₀₄ to R ₂₀₇ are substituents which may have, for example, an alkyl group (for example, 1 to 15 carbon atoms), a cycloalkyl group (for example, 3 to 15 carbon atoms), an aryl group (e.g., 6 carbon atoms 15), alkoxy groups (for example, having 1 to 15 carbon atoms), halogen atoms, hydroxyl groups, phenylthio groups and the like.

X ⁻ represents a non-nucleophilic anion, and examples thereof include the same non-nucleophilic anion as X ^{− in} formula (ZI).

  Preferred examples of the acid generator include compounds represented by the following general formulas (ZIV), (ZV), and (ZVI).

In general formulas (ZIV) to (ZVI), Ar ₃ and Ar ₄ each independently represents an aryl group.

R ₂₀₆ , R ₂₀₇ and R ₂₀₈ are an alkyl group, a cycloalkyl group or an aryl group, and these are the same as the alkyl group, cycloalkyl group or aryl group as R _{204 to} R ₂₀₇ .
A represents an alkylene group, an alkenylene group or an arylene group.

  Among the acid generators, compounds represented by the general formulas (ZI) to (ZIII) are more preferable.

  Among the compounds that generate an acid upon irradiation with actinic rays or radiation, examples of particularly preferable compounds are listed below.

An acid generator can be used individually by 1 type or in combination of 2 or more types.
The content of the acid generator in the positive resist composition is preferably 0.1 to 20% by mass, more preferably 0.5 to 10% by mass, and still more preferably 1 based on the total solid content of the resist composition. -7% by mass.

[3] Surfactant having a basic group (C)
The surfactant having a basic group contained in the positive resist composition of the present invention (hereinafter referred to as a basic surfactant) is a surfactant having at least one basic group in one molecule of the surfactant. is there.
The surfactant is a compound having a molecular weight of 500 or more and containing a hydrophobic group and a hydrophilic group in the molecule.
The hydrophobic group is preferably an alkyl group, a fluoroalkyl group, a fluoroalkylcarbonyl group, or a siloxane, and more preferably a fluoroalkyl group.
The hydrophilic group is preferably a hydroxyl group, an amino group, a cyano group, or a polar group having a hetero atom such as a chlorine atom, more preferably an amino group or a hydroxyl group.
0-8 are preferable and, as for the HLB value which is a parameter | index showing the balance of hydrophilicity / hydrophobicity in 1 molecule, 1-6 are more preferable.
The ratio of the hydrophobic group to the hydrophilic group in the basic surfactant can be appropriately adjusted in consideration of solubility in the solvent used.

The basic surfactant preferably contains a repeating unit represented by the following general formula (1), and is further represented by the following general formula (2) together with the repeating unit represented by the following general formula (1). It is preferable to contain a repeating unit.
The basic surfactant preferably contains a repeating unit represented by the general formula (3).

In general formulas (1), (2) and (3),
R ₁ and R ₂ each independently represents a hydrogen atom or an alkyl group. R ₃ and R ₄ each independently represent a linking group. R ₅ represents a hydrogen atom or an alkyl group. Rf represents an alkyl group, a fluoroalkyl group or a fluoroalkylcarbonyl group. X ₁ represents a basic group. X ₂ and X ₃ each independently represent a hydrogen atom, an alkyl group, an alkylcarbonyl group, a lactone group, or a basic group. l, m, and n represent an integer of 1-50.

The alkyl group for R ₁ , R ₂ , R ₅ , X ₂ and X ₃ is preferably a straight chain or branched alkyl group having 1 to 4 carbon atoms, such as a methyl group, an ethyl group, n -Propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, t-butyl group and the like.

As the linking group for R ₃ and R ₄ , a single bond, an alkylene group, an ether group, a thioether group, a carbonyl group, an ester group, an amide group, a sulfonamide group, a urethane group, or a urea group may be used alone or It represents a combination of two or more groups, and preferably has 6 or less carbon atoms.

The alkyl group of Rf is preferably an alkyl group having 1 to 12 carbon atoms, specifically, methyl group, ethyl group, propyl group, isopropyl group, butyl group, t-butyl group, hexyl group, heptyl group, octyl group, Nonyl group, decanyl group, decanyl group, etc. are mentioned.
The fluoroalkyl group represented by Rf is preferably one having 1 to 12 carbon atoms, specifically, a trifluoromethyl group, a pentafluoroethyl group, a heptafluoropropyl group, a hexafluoroisopropyl group, a nonafluorobutyl group, or a nonafluoro-t. -Butyl group, perfluorohexyl group, perfluoroheptyl group, perfluorooctyl group, perfluorononyl group, perfluorodecanyl group, perfluorododecanyl group and the like.

Examples of the basic group of X ₁ , X ₂ and X ₃ include primary, secondary and tertiary aliphatic amines, aromatic amines and heterocyclic amines. Specifically, methylamine, ethylamine, n-propylamine, isopropylamine, n-butylamine, isobutylamine, sec-butylamine, t-butylamine, ethylenediamine, N, N-dimethylmethylenediamine, trimethylamine, triethylamine, tri-n -Aliphatic amines such as propylamine, triisopropylamine, N, N, N ', N'-tetramethylethylenediamine, methylethylpropylamine, benzylamine, phenethylamine, benzyldimethylamine, aniline derivatives, pyrrole derivatives, oxazole derivatives, Thiazole derivatives, imidazole derivatives, pyrazole derivatives, furazane derivatives, pyrroline derivatives, pyrrolidine derivatives, imidazoline derivatives, imidazolidine derivatives, pyridine derivatives, pyrida Emissions derivatives, pyrimidine derivatives, pyrazine derivatives, pyrazoline derivatives, pyrazolidine derivatives, piperidine derivatives, piperazine derivatives, morpholine derivatives, indole derivatives, 1H-indazole derivatives, aromatic amines such as indoline derivatives, heterocyclic amines, and the like. Among these, more preferred are primary, secondary and tertiary aliphatic amines having 1 to 5 carbon atoms, pyridine derivatives and aniline derivatives.

The basic surfactant preferably contains 1 to 60 mol% of the repeating unit represented by the general formula (1) with respect to all repeating units constituting the basic surfactant, and 1 to 40 mol%. It is more preferable to contain.
Furthermore, it is preferable to contain the repeating unit represented by General formula (2) with the repeating unit represented by General formula (1).
In this case, the repeating unit represented by the general formula (2) is preferably 1 to 90 mol% and more preferably 1 to 70 mol% with respect to all repeating units constituting the basic surfactant.

  The basic surfactant preferably contains 1 to 100 mol% of the repeating unit represented by the general formula (3), and more preferably contains 20 to 100 mol%.

  Although the specific example of the repeating unit represented by General formula (1) below is given, it is not limited to these.

In addition to the above repeating structural units, the basic surfactant can contain various repeating structural units for the purpose of adjusting solvent solubility, suitability for standard developer, resist profile, heat resistance and the like.
In addition, it is also preferable that the basic surfactant containing the repeating unit represented by the general formula (1) contains a repeating structural unit represented by the following general formula (4).

In general formula (4), R ₆ represents a hydrogen atom or an alkyl group. R ₇ represents a linking group. R ₈ represents a hydroxyl group or an alkyl group.
Examples of the alkyl group as R ₆ and R ₈ include the same alkyl groups as R _{1 to} R ₂ in the general formulas (1) to (3).
Examples of the linking group as R ₇ include the same linking groups as R ₃ and R _{4 in} the general formulas (1) to (3).

  The synthesis of the basic surfactant containing the repeating unit represented by the general formula (1) or (3) is performed by, for example, radical weight as described for the synthesis of the above-described alicyclic hydrocarbon-based acid-decomposable resin. It can be done legally. If a chain transfer agent having a perfluoroalkyl group substituted at the end is used, a basic interface having a perfluoroalkyl group at the end of the repeating unit as in specific examples (Fa-13) and (Fa-15) described later. Activators can be synthesized.

  The molecular weight of the basic surfactant is preferably 500 to 10000, more preferably 1000 to 6000. The dispersity (Mw / Mn) is preferably 1 to 3, more preferably 1 to 2.

  Although the specific example of a basic surfactant is given to the following, it is not limited to these.

  The amount of the basic surfactant used is preferably 0.01 to 5% by mass, more preferably 0.1 to 2% by mass, based on the total amount of the positive resist composition (excluding the solvent).

[4] Other surfactants In the present invention, other surfactants can be used in combination with the basic surfactant. Examples of other surfactants used in combination include fluorine-based and / or silicon-based surfactants (fluorine-based surfactants, silicon-based surfactants, surfactants having both fluorine and silicon atoms). it can.

When using an exposure light source of 250 nm or less, particularly 220 nm or less, the fluorine-based and / or silicon-based surfactant improves the sensitivity, resolution, adhesion, and development defects.
Examples of the fluorine-based and / or silicon-based surfactant include, for example, JP-A No. 62-36663, JP-A No. 61-226746, JP-A No. 61-226745, JP-A No. 62-170950, JP 63-34540 A, JP 7-230165 A, JP 8-62834 A, JP 9-54432 A, JP 9-5988 A, JP 2002-277862 A, US Patent Nos. 5,405,720, 5,360,692, 5,529,881, 5,296,330, 5,436,098, 5,576,143, 5,294,511, 5,824,451 Surfactant can be mentioned, The following commercially available surfactant can also be used as it is.

  Examples of commercially available surfactants include F-top EF301 and EF303 (manufactured by Shin-Akita Kasei Co., Ltd.), Florard FC430 and 431 (manufactured by Sumitomo 3M Co., Ltd.), MegaFuck F171, F173, F176, F189 and R08 (large) Nippon Ink Chemical Co., Ltd.), Surflon S-382, SC101, 102, 103, 104, 105, 106 (Asahi Glass Co., Ltd.), Troisol S-366 (Troy Chemical Co., Ltd.), PF636, PF6320 Fluorosurfactant such as PF656, PF6520 (manufactured by OMNOVA) or silicon surfactant. Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.) can also be used as a silicon-based surfactant.

  In addition to the known surfactants described above, the surfactant is derived from a fluoroaliphatic compound produced by a telomerization method (also called telomer method) or an oligomerization method (also called oligomer method). A surfactant using a polymer having a fluoroaliphatic group can be used. The fluoroaliphatic compound can be synthesized by the method described in JP-A-2002-90991.

  As the polymer having a fluoroaliphatic group, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate and / or (poly (oxyalkylene)) methacrylate is preferable and distributed irregularly. Or may be block copolymerized. Examples of the poly (oxyalkylene) group include a poly (oxyethylene) group, a poly (oxypropylene) group, a poly (oxybutylene) group, and the like, and a poly (oxyethylene, oxypropylene, and oxyethylene group). A unit having different chain lengths in the same chain length, such as a block link) or poly (block link of oxyethylene and oxypropylene) may be used. Furthermore, a copolymer of a monomer having a fluoroaliphatic group and (poly (oxyalkylene)) acrylate (or methacrylate) is not only a binary copolymer but also a monomer having two or more different fluoroaliphatic groups, Further, it may be a ternary or higher copolymer obtained by simultaneously copolymerizing two or more different (poly (oxyalkylene)) acrylates (or methacrylates).

Examples of commercially available surfactants include Megafac F178, F-470, F-473, F-475, F-476, and F-472 (Dainippon Ink Chemical Co., Ltd.). Further, a copolymer of an acrylate (or methacrylate) having a C ₆ F ₁₃ group and (poly (oxyalkylene)) acrylate (or methacrylate), an acrylate (or methacrylate) having a C ₆ F ₁₃ group and (poly (oxy) (Ethylene)) acrylate (or methacrylate) and (poly (oxypropylene)) acrylate (or methacrylate) copolymer, acrylate (or methacrylate) and (poly (oxyalkylene)) acrylate having C ₈ F ₁₇ groups (or Copolymer of acrylate (or methacrylate), (poly (oxyethylene)) acrylate (or methacrylate), and (poly (oxypropylene)) acrylate (or methacrylate) having a C ₈ F ₁₇ group List union It can be.

  In the present invention, other surfactants other than fluorine-based and / or silicon-based surfactants can also be used. Specifically, polyoxyethylene lauryl ether, polyoxyethylene stearyl ether, polyoxyethylene cetyl ether, polyoxyethylene alkyl ethers such as polyoxyethylene oleyl ether, polyoxyethylene octylphenol ether, polyoxyethylene nonylphenol ether, etc. Sorbitans such as polyoxyethylene alkyl allyl ethers, polyoxyethylene / polyoxypropylene block copolymers, sorbitan monolaurate, sorbitan monopalmitate, sorbitan monostearate, sorbitan monooleate, sorbitan trioleate, sorbitan tristearate Fatty acid esters, polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monopal Te - DOO, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan trioleate, may be mentioned polyoxyethylene sorbitan tristearate nonionic surfactants of polyoxyethylene sorbitan fatty acid esters such as such.

  The amount of other surfactants other than the basic surfactant is preferably 0.01 to 5% by mass, more preferably 0.1 to 0.1% by mass with respect to the total amount of the positive resist composition (excluding the solvent). 2% by mass.

[5] Alkali-soluble resin The positive resist composition of the present invention can further contain a resin that is soluble in an alkaline developer, thereby improving the sensitivity.
In the present invention, a novolak resin having a molecular weight of about 1000 to 20000 and a polyhydroxystyrene derivative having a molecular weight of about 3000 to 50000 can be used as such a resin, since these have a large absorption with respect to light of 250 nm or less. It is preferable to use a partly hydrogenated amount or 30% by mass or less of the total resin amount.
A resin having a carboxyl group as an alkali-soluble group can also be used. The resin having a carboxyl group preferably has a monocyclic or polycyclic alicyclic hydrocarbon group in order to improve dry etching resistance. Specifically, a methacrylic acid ester and (meth) acrylic acid copolymer having an alicyclic hydrocarbon structure that does not exhibit acid decomposability, or a (meth) acrylic acid ester having an alicyclic hydrocarbon group having a carboxyl group at the terminal And the like.
The addition amount of such an alkali-soluble resin is usually 30% by mass or less based on the total amount of the resin including the acid-decomposable resin.

[6] Basic compound The positive resist composition of the present invention preferably further contains a basic compound. As the basic compound, for example, a nitrogen-containing basic compound, a basic ammonium salt, a basic sulfonium salt, a basic iodonium salt, or the like may be used as long as it does not deteriorate sublimation or resist performance.

  The basic compound is a component having an action of controlling a diffusion phenomenon in a resist film of an acid generated from an acid generator by exposure and suppressing an undesirable chemical reaction in a non-exposed region. By blending such a basic compound, the storage stability of the resist composition that can control the diffusion phenomenon of the acid generated from the acid generator upon exposure in the resist film is improved, and the resolution as a resist is further improved. While improving, the change of the line width of a resist pattern by the fluctuation | variation of the leaving time (PED) from exposure to development processing can be suppressed, and the composition excellent in process stability is obtained.

  Examples of the nitrogen-containing basic compound include primary, secondary and tertiary aliphatic amines, aromatic amines, heterocyclic amines, nitrogen-containing compounds having a carboxy group, and compounds having a sulfonyl group. Examples thereof include nitrogen compounds, nitrogen-containing compounds having a hydroxyl group, nitrogen-containing compounds having a hydroxyphenyl group, alcoholic nitrogen-containing compounds, amide derivatives, imide derivatives, and nitrogen-containing compounds having a cyano group.

  As aliphatic amines, methylamine, ethylamine, n-propylamine, isopropylamine, n-butylamine, isobutylamine, sec-butylamine, tert-butylamine, pentylamine, tert-amylamine, cyclopentylamine, hexylamine, cyclohexylamine, Heptylamine, octylamine, nonylamine, decylamine, dodecylamine, cetylamine, methylenediamine, ethylenediamine, tetraethylenepentamine, dimethylamine, diethylamine, di-n-propylamine, diisopropylamine, di-n-butylamine, diisobutylamine, di -Sec-butylamine, dipentylamine, dicyclopentylamine, dihexylamine, dicyclohexylamine, diheptylamine , Dioctylamine, dinonylamine, didecylamine, didodecylamine, dicetylamine, N, N-dimethylmethylenediamine, N, N-dimethylethylenediamine, N, N-dimethyltetraethylenepentamine, trimethylamine, triethylamine, tri-n-propylamine , Triisopropylamine, tri-n-butylamine, triisobutylamine, tri-sec-butylamine, tripentylamine, tricyclopentylamine, trihexylamine, tricyclohexylamine, triheptylamine, trioctylamine, trinonylamine, trinonylamine Decylamine, tridodecylamine, tricetylamine, N, N, N ′, N′-tetramethylmethylenediamine, N, N, N ′, N′-tetramethylethylenediamine, N, N N ', N'-tetramethyl-tetraethylenepentamine, dimethylethylamine, methylethylpropylamine, benzylamine, phenethylamine, benzyldimethylamine, and the like.

  Aromatic amines and heterocyclic amines include aniline derivatives such as aniline, N-methylaniline, N-ethylaniline, N-propylaniline, N, N-dimethylaniline, 2-methylaniline, 3-methylaniline, 4-methylaniline, ethylaniline, propylaniline, trimethylaniline, 2-nitroaniline, 3-nitroaniline, 4-nitroaniline, 2,4-dinitroaniline, 2,6-dinitroaniline, 3,5-dinitroaniline, N, N-dimethyltoluidine, etc.), diphenyl (p-tolyl) amine, methyldiphenylamine, triphenylamine, phenylenediamine, naphthylamine, diaminonaphthalene, pyrrole derivatives (eg pyrrole, 2H-pyrrole, 1-methylpyrrole, 2,4 -Dimethylpyro , 2,5-dimethylpyrrole, N-methylpyrrole, etc.), oxazole derivatives (eg oxazole, isoxazole etc.), thiazole derivatives (eg thiazole, isothiazole etc.), imidazole derivatives (eg imidazole, 4-methylimidazole, 4 -Methyl-2-phenylimidazole, etc.), pyrazole derivatives, furazane derivatives, pyrroline derivatives (eg pyrroline, 2-methyl-1-pyrroline etc.), pyrrolidine derivatives (eg pyrrolidine, N-methylpyrrolidine, pyrrolidinone, N-methylpyrrolidone etc.) ), Imidazoline derivatives, imidazolidine derivatives, pyridine derivatives (eg pyridine, methylpyridine, ethylpyridine, propylpyridine, butylpyridine, 4- (1-butylpentyl) pyridine, dimethylpyridine) Trimethylpyridine, triethylpyridine, phenylpyridine, 3-methyl-2-phenylpyridine, 4-tert-butylpyridine, diphenylpyridine, benzylpyridine, methoxypyridine, butoxypyridine, dimethoxypyridine, 1-methyl-2-pyridone, 4- Pyrrolidinopyridine, 1-methyl-4-phenylpyridine, 2- (1-ethylpropyl) pyridine, aminopyridine, dimethylaminopyridine, etc.), pyridazine derivatives, pyrimidine derivatives, pyrazine derivatives, pyrazoline derivatives, pyrazolidine derivatives, piperidine derivatives, Piperazine derivatives, morpholine derivatives, indole derivatives, isoindole derivatives, 1H-indazole derivatives, indoline derivatives, quinoline derivatives (eg quinoline, 3-quinolinecarbonitrile) Etc.), isoquinoline derivatives, cinnoline derivatives, quinazoline derivatives, quinoxaline derivatives, phthalazine derivatives, purine derivatives, pteridine derivatives, carbazole derivatives, phenanthridine derivatives, acridine derivatives, phenazine derivatives, 1,10-phenanthroline derivatives, adenine derivatives, adenosine derivatives Guanine derivatives, guanosine derivatives, uracil derivatives, uridine derivatives and the like.

  Examples of the nitrogen-containing compound having a carboxy group include aminobenzoic acid, indolecarboxylic acid, amino acid derivatives (for example, nicotinic acid, alanine, arginine, aspartic acid, glutamic acid, glycine, histidine, isoleucine, glycylleucine, leucine, methionine, phenylalanine. , Threonine, lysine, 3-aminopyrazine-2-carboxylic acid, methoxyalanine) and the like.

  Examples of the nitrogen-containing compound having a sulfonyl group include 3-pyridinesulfonic acid and pyridinium p-toluenesulfonate.

Examples of the nitrogen-containing compound having a hydroxyl group include 2-hydroxypyridine, aminocresol, 2,4-quinolinediol, 3-indolemethanol hydrate, monoethanolamine, diethanolamine, triethanolamine, N-ethyldiethanolamine, N, N- Diethylethanolamine, triisopropanolamine, 2,2′-iminodiethanol, 2-aminoethanol, 3-amino-1-propanol, 4-amino-1-butanol, 4- (2-hydroxyethyl) morpholine, 2- ( 2-hydroxyethyl) pyridine, 1- (2-hydroxyethyl) piperazine, 1- [2- (2-hydroxyethoxy) ethyl] piperazine, piperidineethanol, 1- (2-hydroxyethyl) pyrrolidine, 1- (2- Hydroxyethyl ) -2-pyrrolidinone, 3-piperidino-1,2-propanediol, 3-pyrrolidino-1,2-propanediol, 8-hydroxyeurolidine, 3-quinuclidinol, 3-tropanol, 1-methyl-2 -Pyrrolidine ethanol, 1-aziridine ethanol, N- (2-hydroxyethyl) phthalimide, N- (2-hydroxyethyl) isonicotinamide and the like are exemplified.

  Examples of amide derivatives include formamide, N-methylformamide, N, N-dimethylformamide, acetamide, N-methylacetamide, N, N-dimethylacetamide, propionamide, benzamide and the like.

  Examples of imide derivatives include phthalimide, succinimide, maleimide and the like.

  Specific examples of the nitrogen-containing compound having a cyano group include 3- (diethylamino) propiononitrile, N, N-bis (2-hydroxyethyl) -3-aminopropiononitrile, N, N-bis (2- Acetoxyethyl) -3-aminopropiononitrile, N, N-bis (2-formyloxyethyl) -3-aminopropiononitrile, N, N-bis (2-methoxyethyl) -3-aminopropiononitrile, N, N-bis [2- (methoxymethoxy) ethyl] -3-aminopropiononitrile, methyl N- (2-cyanoethyl) -N- (2-methoxyethyl) -3-aminopropionate, N- (2 -Cyanoethyl) -N- (2-hydroxyethyl) -3-aminopropionic acid methyl, N- (2-acetoxyethyl) -N- (2-cyanoethyl) Methyl 3-aminopropionate, N- (2-cyanoethyl) -N-ethyl-3-aminopropiononitrile, N- (2-cyanoethyl) -N- (2-hydroxyethyl) -3-aminopropiononitrile, N- (2-acetoxyethyl) -N- (2-cyanoethyl) -3-aminopropiononitrile, N- (2-cyanoethyl) -N- (2-formyloxyethyl) -3-aminopropiononitrile, N -(2-cyanoethyl) -N- (2-methoxyethyl) -3-aminopropiononitrile, N (2-cyanoethyl) -N- [2- (methoxymethoxy) ethyl] -3-aminopropiononitrile, N -(2-cyanoethyl) -N- (3-hydroxy-1-propyl) -3-aminopropiononitrile, N- (3-acetoxy-1-propionitrile ) -N- (2-cyanoethyl) -3-aminopropiononitrile, N- (2-cyanoethyl) -N- (3-formyloxy-1-propyl) -3-aminopropiononitrile, N- (2- Cyanoethyl) -N-tetrahydrofurfuryl-3-aminopropiononitrile, N, N-bis (2-cyanoethyl) -3-aminopropiononitrile, diethylaminoacetonitrile, N, N-bis (2-hydroxyethyl) aminoacetonitrile N, N-bis (2-acetoxyethyl) aminoacetonitrile, N, N-bis (2-formyloxyethyl) aminoacetonitrile, N, N-bis (2-methoxyethyl) aminoacetonitrile, N, N-bis [ 2- (methoxymethoxy) ethyl] aminoacetonitrile, N-cyanomethyl-N- (2- Methoxyethyl) -3-aminopropionate methyl, N-cyanomethyl-N- (2-hydroxyethyl) -3-aminopropionate methyl, N- (2-acetoxyethyl) -N-cyanomethyl-3-aminopropionate methyl N-cyanomethyl-N- (2-hydroxyethyl) aminoacetonitrile, N- (2-acetoxyethyl) -N- (cyanomethyl) aminoacetonitrile, N-cyanomethyl-N- (2-formyloxyethyl) aminoacetonitrile, N -Cyanomethyl-N- (2-methoxyethyl) aminoacetonitrile, N-cyanomethyl-N- [2- (methoxymethoxy) ethyl] aminoacetonitrile, N- (cyanomethyl) -N- (3-hydroxy-1-propyl) amino Acetonitrile, N- (3-acetoxy-1- (Lopyl) -N- (cyanomethyl) aminoacetonitrile, N-cyanomethyl-N- (3-formyloxy-1-propyl) aminoacetonitrile, N, N-bis (cyanomethyl) aminoacetonitrile, 1-pyrrolidinepropiononitrile, 1- Piperidine propiononitrile, 4-morpholine propiononitrile, 1-pyrrolidine acetonitrile, 1-piperidine acetonitrile, 4-morpholine acetonitrile, cyanomethyl 3-diethylaminopropionate, N, N-bis (2-hydroxyethyl) -3-aminopropion Cyanomethyl acid, cyanomethyl N, N-bis (2-acetoxyethyl) -3-aminopropionate, cyanomethyl N, N-bis (2-formyloxyethyl) -3-aminopropionate, N, N-bis (2- Me Xylethyl) -3-aminopropionate cyanomethyl, N, N-bis [2- (methoxymethoxy) ethyl] -3-aminopropionate cyanomethyl, 3-diethylaminopropionic acid (2-cyanoethyl), N, N-bis (2 -Hydroxyethyl) -3-aminopropionic acid (2-cyanoethyl), N, N-bis (2-acetoxyethyl) -3-aminopropionic acid (2-cyanoethyl), N, N-bis (2-formyloxyethyl) ) -3-Aminopropionic acid (2-cyanoethyl), N, N-bis (2-methoxyethyl) -3-aminopropionic acid (2-cyanoethyl), N, N-bis [2- (methoxymethoxy) ethyl] -3-aminopropionic acid (2-cyanoethyl), cyanomethyl 1-pyrrolidinepropionate, 1-piperidine pro Examples include cyanomethyl pionate, cyanomethyl 4-morpholine propionate, 1-pyrrolidinepropionic acid (2-cyanoethyl), 1-piperidinepropionic acid (2-cyanoethyl), 4-morpholine propionic acid (2-cyanoethyl).

As the nitrogen-containing basic compound, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5.4.0] -7-undecene, 1,4-diazabicyclo [ 2.2.2] Octane, 4-dimethylaminopyridine, 1-naphthylamine, piperidines, hexamethylenetetramine, imidazoles, hydroxypyridines, pyridines, anilines, hydroxyalkylanilines, 4,4′-diaminodiphenyl ether , Pyridinium p-toluenesulfonate, 2,4,6-trimethylpyridinium p-toluenesulfonate, tetramethylammonium p-toluenesulfonate, tetrabutylammonium lactate, triethylamine, tributylamine, tripentylamine, tri-n-octylami , Tri-i-octylamine, tris (ethylhexyl) amine, tridecylamine, tridodecylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine, Tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decylamine, cyclohexyldimethylamine, methyldicyclohexylamine, ethylenediamine, N, N, N ′, N′-tetramethylethylenediamine, Tetramethylenediamine, hexamethylenediamine, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenyl ether, 4,4'-diaminobenzophenone, 4,4'-diaminodiphenylamine, 2,2-bis (4-aminophenyl) ) Propane, 2- (3- Aminophenyl) -2- (4-aminophenyl) propane, 2- (4-aminophenyl) -2- (3-hydroxyphenyl) propane, 2- (4-aminophenyl) -2- (4-hydroxyphenyl) Propane, 1,4-bis [1- (4-aminophenyl) -1-methylethyl] benzene, 1,3-bis [1- (4-aminophenyl) -1-methylethyl] benzene, bis (2- Tri (cyclo) alkylamines such as dimethylaminoethyl) ether, bis (2-diethylaminoethyl) ether, N, N, N ′, N′-tetrakis (2-hydroxypropyl) ethylenediamine, tricyclohexylamine, aniline, N -Methylaniline, N, N-dimethylaniline, 2-methylaniline, 3-methylaniline, 4-methylaniline, 4-ni Roaniline, diphenylamine, triphenylamine, naphthylamine, aromatic amines such as 2,6-diisopropylaniline, polyethyleneimine, polyallylamine, 2-dimethylaminoethylacrylamide polymer, Nt-butoxycarbonyldi-n-octyl Amine, Nt-butoxycarbonyldi-n-nonylamine, Nt-butoxycarbonyldi-n-decylamine, Nt-butoxycarbonyldicyclohexylamine, Nt-butoxycarbonyl-1-adamantylamine, Nt -Butoxycarbonyl-N-methyl-1-adamantylamine, N, N-di-t-butoxycarbonyl-1-adamantylamine, N, N-di-t-butoxycarbonyl-N-methyl-1-adamantylamine, N -T-Butoxyca Bonyl-4,4′-diaminodiphenylmethane, N, N′-di-t-butoxycarbonylhexamethylenediamine, N, N, N′N′-tetra-t-butoxycarbonylhexamethylenediamine, N, N′-di -T-butoxycarbonyl-1,7-diaminoheptane, N, N'-di-t-butoxycarbonyl-1,8-diaminooctane, N, N'-di-t-butoxycarbonyl-1,9-diaminononane, N, N′-di-t-butoxycarbonyl-1,10-diaminodecane, N, N′-di-t-butoxycarbonyl-1,12-diaminododecane, N, N′-di-t-butoxycarbonyl- 4,4′-diaminodiphenylmethane, Nt-butoxycarbonylbenzimidazole, Nt-butoxycarbonyl-2-methylbenzimidazole, Nt Butoxycarbonyl-2-phenylbenzimidazole, formamide, N-methylformamide, N, N-dimethylformamide, acetamide, N-methylacetamide, N, N-dimethylacetamide, propionamide, benzamide, pyrrolidone, N-methylpyrrolidone, urea Methylurea, 1,1-dimethylurea, 1,3-dimethylurea, 1,1,3,3-tetramethylurea, 1,3-diphenylurea, tri-n-butylthiourea, imidazole, 4-methylimidazole, Imidazoles such as 4-methyl-2-phenylimidazole, benzimidazole, 2-phenylbenzimidazole, pyridine, 2-methylpyridine, 4-methylpyridine, 2-ethylpyridine, 4-ethylpyridine, 2-phenylpyridine , 4-phenylpyridine, 2-methyl-4-phenylpyridine, nicotine, nicotinic acid, nicotinamide, quinoline, 4-hydroxyquinoline, 8-oxyquinoline, acridine and other pyridines, piperazine, 1- (2- Piperazines such as hydroxyethyl) piperazine, pyrazine, pyrazole, pyridazine, quinosaline, purine, pyrrolidine, piperidine, 3-piperidino-1,2-propanediol, morpholine, 4-methylmorpholine, 1,4-dimethylpiperazine, etc. be able to.

Among these, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5.4.0] -7-undecene, 1,4-diazabicyclo [2.2.2] Octane, 4-dimethylaminopyridine, 1-naphthylamine, piperidine, 4-hydroxypiperidine, 2,2,6,6-tetramethyl-4-hydroxypiperidine, hexamethylenetetramine, imidazoles, hydroxypyridines, pyridines, 4 , 4'-diaminodiphenyl ether, triethylamine, tributylamine, tripentylamine, tri-n-octylamine, tris (ethylhexyl) amine, tridodecylamine, N, N-di-hydroxyethylaniline, N-hydroxyethyl-N- Nitrogen-containing basic compounds such as ethylaniline are particularly preferred. Yes.

The positive resist composition of the present invention can further use a basic ammonium salt as the basic compound. Specific examples of the basic ammonium salt include the following compounds, but are not limited thereto.
Specifically, ammonium hydroxide, ammonium triflate, ammonium pentaflate, ammonium heptaflate, ammonium nonaflate, ammonium undecaflate, ammonium tridecaflate, ammonium pentadecaflate, ammonium methylcarboxylate, ammonium ethylcarboxylate, Ammonium propyl carboxylate, ammonium butyl carboxylate, ammonium heptyl carboxylate, ammonium hexyl carboxylate, ammonium octyl carboxylate, ammonium nonyl carboxylate, ammonium decyl carboxylate, ammonium undecyl carboxylate, ammonium dodecadecyl carboxylate, ammonium salt Decyl carboxylate, ammonium tetradecyl carboxylate, ammonium pentadecyl carboxylate, ammonium hexadecyl carboxylate, ammonium heptadecyl carboxylate, ammonium octadecyl carboxylate and the like.

  Specific examples of ammonium hydroxide include tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, tetrapentylammonium hydroxide, tetrahexylammonium hydroxide, and tetraheptyl. Ammonium hydroxide, methyltrioctylammonium hydroxide, tetraoctylammonium hydroxide, didecyldimethylammonium hydroxide, tetrakisdecylammonium hydroxide, dodecyltrimethylammonium hydroxide, dodecylethyldimethylammonium hydroxide, didodecyldimethylammonium hydroxide, Tridodecylmethylammonium hydro Side, myristylmethylammonium hydroxide, dimethylditetradecylammonium hydroxide, hexadecyltrimethylammonium hydroxide, octadecyltrimethylammonium hydroxide, dimethyldioctadecylammonium hydroxide, tetraoctadecylammonium hydroxide, diallyldimethylammonium hydroxide, (2 -Chloroethyl) -trimethylammonium hydroxide, (2-bromoethyl) trimethylammonium hydroxide, (3-bromopropyl) -trimethylammonium hydroxide, (3-bromopropyl) triethylammonium hydroxide, glycidyltrimethylammonium hydroxide, choline hydroxy (R)-(+)-(3-chloro-2-hydro Cypropyl) trimethylammonium hydroxide, (S)-(−)-(3-chloro-2-hydroxypropyl) -trimethylammonium hydroxide, (3-chloro-2-hydroxypropyl) -trimethylammonium hydroxide, (2- Aminoethyl) -trimethylammonium hydroxide, hexamethonium hydroxide, decamethonium hydroxide, 1-azoniapropellan hydroxide, petronium hydroxide, 2-chloro-1,3-dimethyl-2-imidazolinium hydroxy And 3-ethyl-2-methyl-2-thiazolinium hydroxide.

The basic compound can be used alone or in combination of two or more, and it is more preferable to use two or more.
The usage-amount of a basic compound is 0.001-10 mass% normally on the basis of solid content of a resist composition as a total amount, Preferably it is 0.01-5 mass%.

[7] Dissolution-inhibiting compound having a molecular weight of 3000 or less, which is decomposed by the action of an acid to increase the solubility in an alkaline developer. The positive resist composition of the present invention is decomposed by the action of an acid in an alkaline developer. It is preferable to contain a dissolution inhibiting compound having a molecular weight of 3000 or less (hereinafter also referred to as “dissolution inhibiting compound”).
The dissolution inhibiting compound contains an acid-decomposable group, such as a cholic acid derivative containing an acid-decomposable group described in Proceeding of SPIE, 2724, 355 (1996), so as not to lower the permeability below 220 nm. Preferred are alicyclic or aliphatic compounds. Examples of the acid-decomposable group and alicyclic structure are the same as those described for the resin as the component (A).
The molecular weight of the dissolution inhibiting compound in the present invention is 3000 or less, preferably 300 to 3000, and more preferably 500 to 2500.

  The addition amount of the dissolution inhibiting compound is preferably 1 to 30% by mass, more preferably 2 to 20% by mass, based on the total solid content of the positive resist composition for immersion exposure.

  Specific examples of the dissolution inhibiting compound are shown below, but are not limited thereto.

[8] Onium carboxylate The positive resist composition of the present invention may contain an onium carboxylate.
Examples of carboxylic acid onium salts in the present invention include carboxylic acid sulfonium salts, carboxylic acid iodonium salts, and carboxylic acid ammonium salts. In particular, the (H) carboxylic acid onium salt is preferably an iodonium salt or a sulfonium salt. Furthermore, in the carboxylic acid onium salt of the present invention, it is preferable that the carboxylate residue does not contain an aromatic group or a carbon-carbon double bond. As a particularly preferable anion moiety, a linear, branched, monocyclic or polycyclic alkylcarboxylic acid anion having 1 to 30 carbon atoms is preferable. More preferably, an anion of a carboxylic acid in which some or all of these alkyl groups are fluorine-substituted is preferable. The alkyl chain may contain an oxygen atom. This ensures transparency with respect to light of 220 nm or less, improves sensitivity and resolution, and improves density dependency and exposure margin.

  Fluoro-substituted carboxylic acid anions include fluoroacetic acid, difluoroacetic acid, trifluoroacetic acid, pentafluoropropionic acid, heptafluorobutyric acid, nonafluoropentanoic acid, perfluorododecanoic acid, perfluorotridecanoic acid, perfluorocyclohexanecarboxylic acid, 2 , 2-bistrifluoromethylpropionic acid anion and the like.

  These carboxylic acid onium salts can be synthesized by reacting sulfonium hydroxide, iodonium hydroxide, ammonium hydroxide and carboxylic acid with silver oxide in a suitable solvent.

  The content of the carboxylic acid onium salt in the composition is suitably from 0.1 to 20% by weight, preferably from 0.5 to 10% by weight, more preferably from 1 to 7% by weight, based on the total solid content of the composition. %.

[9] Carboxylic acid onium salt The positive resist composition of the present invention may contain a carboxylic acid onium salt.
Examples of carboxylic acid onium salts in the present invention include carboxylic acid sulfonium salts, carboxylic acid iodonium salts, and carboxylic acid ammonium salts. In particular, as the carboxylic acid onium salt, an iodonium salt and a sulfonium salt are preferable. Furthermore, in the carboxylic acid onium salt of the present invention, it is preferable that the carboxylate residue does not contain an aromatic group or a carbon-carbon double bond. As a particularly preferable anion moiety, a linear, branched, monocyclic or polycyclic alkylcarboxylic acid anion having 1 to 30 carbon atoms is preferable. More preferably, an anion of a carboxylic acid in which some or all of these alkyl groups are fluorine-substituted is preferable. The alkyl chain may contain an oxygen atom. This ensures transparency with respect to light of 220 nm or less, improves sensitivity and resolution, and improves density dependency and exposure margin.

  Fluoro-substituted carboxylic acid anions include fluoroacetic acid, difluoroacetic acid, trifluoroacetic acid, pentafluoropropionic acid, heptafluorobutyric acid, nonafluoropentanoic acid, perfluorododecanoic acid, perfluorotridecanoic acid, perfluorocyclohexanecarboxylic acid, 2 , 2-bistrifluoromethylpropionic acid anion and the like.

  These carboxylic acid onium salts can be synthesized by reacting sulfonium hydroxide, iodonium hydroxide, ammonium hydroxide and carboxylic acid with silver oxide in a suitable solvent.

  The content of the carboxylic acid onium salt in the composition is suitably from 0.1 to 20% by weight, preferably from 0.5 to 10% by weight, more preferably from 1 to 7% by weight, based on the total solid content of the composition. %.

[10] Other additives In the positive resist composition of the present invention, a dye, a plasticizer, a photosensitizer, and a compound that promotes solubility in a developer (for example, a molecular weight of 1000 or less) are added to the positive resist composition of the present invention. A phenol compound, an alicyclic compound having a carboxyl group, or an aliphatic compound).

Such phenol compounds having a molecular weight of 1000 or less can be obtained by referring to, for example, the methods described in JP-A-4-1222938, JP-A-2-28531, US Pat. No. 4,916,210, European Patent 219294, etc. It can be easily synthesized by those skilled in the art.
Specific examples of alicyclic or aliphatic compounds having a carboxyl group include carboxylic acid derivatives having a steroid structure such as cholic acid, deoxycholic acid, lithocholic acid, adamantane carboxylic acid derivatives, adamantane dicarboxylic acid, cyclohexane carboxylic acid, cyclohexane Examples thereof include, but are not limited to, dicarboxylic acids.

[11] Organic solvent The positive resist composition of the present invention is used by dissolving the above components in a predetermined organic solvent.
Examples of the organic solvent that can be used include ethylene dichloride, cyclohexanone, cyclopentanone, 2-heptanone, γ-butyrolactone, methyl ethyl ketone, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, 2-methoxyethyl acetate, ethylene glycol monoethyl. Ether acetate, propylene glycol monomethyl ether, propylene glycol monomethyl ether acetate, toluene, ethyl acetate, methyl lactate, ethyl lactate, methyl methoxypropionate, ethyl ethoxypropionate, methyl pyruvate, ethyl pyruvate, propyl pyruvate, N, N -Dimethylformamide, dimethylsulfoxide, N-methylpyrrolidone, methoxybutanol, tetrahydrofuran, etc. It can be mentioned.

In this invention, you may use the mixed solvent which mixed the solvent which has a hydroxyl group in a structure, and the solvent which does not have a hydroxyl group as an organic solvent.
Examples of the solvent having a hydroxyl group include ethylene glycol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol, propylene glycol monomethyl ether, propylene glycol monoethyl ether, ethyl lactate, and the like. Propylene glycol monomethyl ether and ethyl lactate are preferred.
Examples of the solvent having no hydroxyl group include propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, butyl acetate, N-methylpyrrolidone, N, N-dimethylacetamide, dimethyl sulfoxide. Among these, propylene glycol monomethyl ether acetate, ethyl ethoxypropionate, 2-heptanone, γ-butyrolactone, cyclohexanone, and butyl acetate are preferable, propylene glycol monomethyl ether acetate, ethyl ethoxypropionate 2-heptanone is more preferable.
The mixing ratio (mass) of the solvent having a hydroxyl group and the solvent having no hydroxyl group is preferably 1/99 to 99/1, more preferably 10/90 to 90/10, and even more preferably 20/80 to 60. / 40. A mixed solvent containing 50% by mass or more of a solvent having no hydroxyl group is particularly preferable from the viewpoint of coating uniformity.

[12] Pattern Forming Method The positive resist composition of the present invention is used by dissolving the above components in a predetermined organic solvent, preferably the mixed solvent, and applying the solution on a predetermined support as follows.
That is, a positive resist composition is formed on a substrate (eg, silicon / silicon dioxide coating) used for the manufacture of precision integrated circuit elements by an appropriate coating method such as a spinner or a coater, with an arbitrary thickness (usually 50 to 500 nm).
In addition, it is preferable that the solid content density | concentration in a resist composition is 2.0-6.0 mass%.
After coating, the resist applied by spin or baking is dried to form a resist film, and then exposed through a mask or the like for pattern formation. The exposure amount can be set as appropriate, but is usually 1 to 100 mJ / cm ² . After exposure, preferably spin or / and bake, develop and rinse to obtain a good pattern. The baking temperature is usually 30 to 300 ° C. From the above-mentioned PED point, it is better that the time from the exposure to the baking process is short.
Here, the exposure light is preferably far ultraviolet rays having a wavelength of 250 nm or less, more preferably 220 nm or less. Specific examples include KrF excimer laser (248 nm), ArF excimer laser (193 nm), F ₂ excimer laser (157 nm), X-rays, and the like.

In the exposure, immersion exposure may be performed via an immersion liquid.
The immersion liquid used for the immersion exposure will be described below.
The immersion liquid is preferably a liquid that is transparent to the exposure wavelength and has a refractive index temperature coefficient as small as possible so as to minimize distortion of the optical image projected onto the resist. In the case of an ArF excimer laser (wavelength: 193 nm), it is preferable to use water from the viewpoints of availability and ease of handling in addition to the above-described viewpoints.
When water is used as the immersion liquid, the surface tension of the water is decreased and the surface activity is increased, so that the resist layer on the wafer is not dissolved and the influence on the optical coating on the lower surface of the lens element can be ignored. An additive (liquid) may be added in a small proportion. The additive is preferably an aliphatic alcohol having a refractive index substantially equal to that of water, and specifically includes methyl alcohol, ethyl alcohol, isopropyl alcohol and the like. By adding an alcohol having a refractive index substantially equal to that of water, even if the alcohol component in water evaporates and the content concentration changes, an advantage that the change in the refractive index of the entire liquid can be extremely small can be obtained. On the other hand, when an opaque substance or impurities whose refractive index is significantly different from that of water are mixed with respect to 193 nm light, the optical image projected on the resist is distorted. Therefore, distilled water is preferable as the water to be used. Further, pure water filtered through an ion exchange filter or the like may be used.
The electrical resistance of water is desirably 18.3 M ohm · cm or more, and the TOC (organic concentration) is desirably 20 ppb or less. Moreover, it is desirable to have deaerated.

In order to prevent the resist film from coming into direct contact with the immersion liquid between the resist film of the positive resist of the present invention and the immersion liquid, an immersion liquid hardly soluble film (hereinafter also referred to as “top coat”) is provided. It may be provided. The necessary functions for the top coat are suitability for application to the upper layer of the resist, radiation, especially transparency to 193 nm, and poor immersion liquid solubility. It is preferable that the top coat is not mixed with the resist and can be uniformly applied to the resist upper layer.
From the viewpoint of 193 nm transparency, the topcoat is preferably a polymer that does not contain an aromatic, and specifically, a hydrocarbon polymer, an acrylate polymer, a polymethacrylic acid, a polyacrylic acid, a polyvinyl ether, a silicon-containing polymer, And fluorine-containing polymers.
When peeling the top coat, a developer may be used, or a separate release agent may be used. As the release agent, a solvent having a small penetration into the resist is preferable. It is preferable that the peeling process can be performed with an alkali developer in that the peeling process can be performed simultaneously with the resist development process. From the viewpoint of peeling with an alkaline developer, the topcoat is preferably acidic, but may be neutral or alkaline from the viewpoint of non-intermixability with the resist.
The resolution is improved when there is no difference in refractive index between the topcoat and the immersion liquid. When the exposure light source is an ArF excimer laser (wavelength: 193 nm), it is preferable to use water as the immersion liquid, so that the top coat for ArF immersion exposure is close to the refractive index of water (1.44). Is preferred. A thin film is more preferable from the viewpoint of transparency and refractive index.

In the development process, a developer is used as follows. As a developer of a positive resist composition for immersion exposure, inorganic hydroxides such as sodium hydroxide, potassium hydroxide, sodium carbonate, sodium silicate, sodium metasilicate, aqueous ammonia, ethylamine, n-propylamine, etc. Primary amines, secondary amines such as diethylamine and di-n-butylamine, tertiary amines such as triethylamine and methyldiethylamine, alcohol amines such as dimethylethanolamine and triethanolamine, tetramethylammonium hydroxide, tetraethyl Alkaline aqueous solutions such as quaternary ammonium salts such as ammonium hydroxide and cyclic amines such as pyrrole and pihelidine can be used.
Furthermore, alcohols and surfactants can be added in appropriate amounts to the alkaline aqueous solution.
As the rinsing liquid, pure water can be used, and an appropriate amount of a surfactant can be added.
The alkali concentration of the alkali developer is usually from 0.1 to 20% by mass.
The pH of the alkali developer is usually from 10.0 to 15.0.

  Further, after the development process or the rinsing process, a process of removing the developer or the rinsing liquid adhering to the pattern with a supercritical fluid can be performed.

  EXAMPLES Hereinafter, although an Example demonstrates this invention still in detail, the content of this invention is not limited by this.

<Synthesis of Resin (1)>
2-adamantyl-2-propyl methacrylate, 3,5-dihydroxy-1-adamantyl methacrylate and norbornane lactone acrylate were charged at a ratio of 40/20/40 (molar ratio), propylene glycol monomethyl ether acetate / propylene glycol monomethyl ether = 60 / 40 was dissolved to prepare 450 g of a solution having a solid content concentration of 22%. 1 mol% of a polymerization initiator V-601 (dimethyl 2,2′-azobis (2-methylpropionate) manufactured by Wako Pure Chemical Industries, Ltd. was added to this solution, and this was added at 100 ° C. over 6 hours in a nitrogen atmosphere. The solution was added dropwise to 50 g of a mixed solution of propylene glycol monomethyl ether acetate / propylene glycol monomethyl ether = 60/40, and the reaction solution was stirred for 2 hours after the completion of the reaction. The white powder which crystallized and broke out in 5 L of a mixed medium of 5/1 of ethyl acetate / ethyl acetate was collected by filtration to recover the target resin (1-A1) Polymer composition from ¹³ CNMR and polymer acid value measurement Ratio (2-adamantyl-2-propyl methacrylate / 3,5-dihydroxy-1-adamantyl methacrylate / norbornane lactone acrylic (A / b / c) was determined to be 39/21/40 (molar ratio), and the weight average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement was 9700, and the degree of dispersion (Mw / Mn) Was 2.01.

  Resins (2) to (12) used in this example were synthesized in the same manner as for resin (1). The structures of the resins (1) to (12) used in the examples are shown below.

<Synthesis Example of (Fa-1)>
N, N-dimethylethyl methacrylate, nonafluoro-n-hexyl methacrylate, and hydroxyethyl methacrylate are charged at a ratio of 20/40/20, and 10 mol% of thioglycerol is added and dissolved in propylene glycol monomethyl ether acetate. 450 g of a 10% strength solution was prepared. To this solution, 5 mol% of a polymerization initiator V-601 manufactured by Wako Pure Chemical Industries, Ltd. was added, and this was added dropwise to 50 g of a propylene glycol monomethyl ether acetate solution heated to 80 ° C. over 4 hours in a nitrogen atmosphere. After completion of dropping, the reaction solution was stirred for 2 hours to obtain a reaction solution (Fa-1). After completion of the reaction, the reaction solution (Fa-1) was cooled to room temperature, crystallized in a mixed solvent of 4.5 times the amount of hexane / ethyl acetate = 90/10, and the precipitated white powder was collected by filtration. Resin (Fa-1) as a product was recovered.
^The polymer composition ratio determined from ¹³ CNMR and acid value titration was 20/40/20. Moreover, the weight average molecular weight of standard polystyrene conversion calculated | required by GPC measurement was 2500, and dispersion degree was 2.3.

<Synthesis Example of (Fb-7)>
PF6320 (made by OMNOVA) 10g and L-alanine 0.4g were melt | dissolved in tetrahydrofuran 150mL, and it stirred at 0 degreeC by nitrogen atmosphere. To this solution, a mixed solution of 0.4 g of thionyl chloride and 50 mL of tetrahydrofuran was added dropwise, followed by stirring at 40 ° C. for 4 hours to obtain a reaction solution (Fb-7). After completion of the reaction, the reaction mixture (Fb-7) was extracted with ethyl acetate, and the oil layer was washed with sodium bicarbonate and aqueous hydrochloric acid solution, dried over sodium sulfate and concentrated. The concentrate was washed with hexane to obtain the target resin (Fb-7).

  (Fa-3), (Fa-5), (Fa-8), (Fa-9) and (Fa-13) were synthesized in the same manner as (Fa-1).

[Examples 1 to 12 and Comparative Examples 1 to 4]
<Resist preparation>
The components shown in Table 1 below were dissolved in a solvent to prepare a solution having a solid concentration of 6.0% by mass, and this was filtered through a 0.1 μm polyethylene filter to prepare a positive resist composition. The prepared positive resist composition was evaluated by the following method, and the results are shown in Table 1. The ratio when using a plurality of components is a mass ratio.

[Image performance test]
(Exposure condition 1: Exposure evaluation for exposure without immersion liquid (normal exposure conditions))
An organic antireflection film ARC29A (Nissan Chemical Co., Ltd.) was applied on a silicon wafer and baked at 205 ° C. for 60 seconds to form a 78 nm antireflection film. The positive resist composition prepared thereon was applied and baked at 120 ° C. for 60 seconds to form a 150 nm resist film. Using the ArF excimer laser scanner (PAS5500 / 1100, NA0.75, σo / σi = 0.85 / 0.55) by ArF excimer laser scanner, the pattern was patterned through a halftone phase shift mask with a transmittance of 6%. Exposed. Thereafter, heating was performed at 120 ° C. for 60 seconds, followed by development with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsing with pure water, and spin drying to obtain a resist pattern.

(Exposure condition 2: Exposure evaluation for exposure through immersion liquid (immersion exposure condition))
An organic antireflection film ARC29A (Nissan Chemical Co., Ltd.) was applied on a silicon wafer and baked at 205 ° C. for 60 seconds to form a 78 nm antireflection film. The positive resist composition prepared thereon was applied and baked at 120 ° C. for 60 seconds to form a 150 nm resist film. The obtained wafer was subjected to pattern exposure using an ArF excimer laser immersion scanner (NA 0.75). Thereafter, heating was performed at 120 ° C. for 60 seconds, followed by development with an aqueous tetramethylammonium hydroxide solution (2.38 mass%) for 30 seconds, rinsing with pure water, and spin drying to obtain a resist pattern.

[Profile Evaluation Conditions]
The resist pattern used for the evaluation is a dense pattern having a 90 nm line and a space ratio of 1: 1. An exposure dose (Eopt) for reproducing the mask size was obtained by a Hitachi measuring SEM (S-9260), and a cross-sectional pattern profile evaluation was performed at Eopt by a Hitachi cross-sectional SEM (S-4300).
The pattern collapse was evaluated as ○ when the 90 nm line and space pattern was formed without falling, Δ when partially collapsed, and × when all were collapsed.
Changes in the resist film thickness after pattern formation are as follows: when the resist film thickness is reduced by 0 to 5% compared to the coating thickness before development, and when the resist film thickness is decreased by 5 to 10%, Δ10 % Indicates that the resist film thickness is decreased.

[Generated acid elution amount]
The prepared resist composition was applied to an 8-inch silicon wafer and baked at 120 ° C. for 60 seconds to form a 150 nm resist film. The resist film was exposed to 50 mJ / cm ² on the entire surface with an exposure machine with a wavelength of 193 nm, and then 5 ml of pure water deionized using an ultrapure water production apparatus (Milli-Q Jr., manufactured by Nihon Millipore) It was dripped in. Water was placed on the resist film for 50 seconds, the water was collected, and the acid elution concentration was quantified by LC-MS.
LC equipment; Waters 2695
MS equipment: esquire 3000plus manufactured by Bruker Daltonics
The detection intensity of ionic species was measured with the LC-MS apparatus, and the amount of acid eluted was calculated.

The symbols in Table 2 are as follows.
The acid generator corresponds to that exemplified above.

N-1: N, N-dibutylaniline N-2: N-cyanoethyl-N-ethylaniline N-3: 2,6-diisopropylaniline N-4: tri-n-octylamine N-5: N, N- Dihydroxyethylaniline N-6: Hydroxyantipyrine N-7: 2,4,5-trisphenylimidazole

W-1: Megafuck F176 (manufactured by Dainippon Ink & Chemicals, Inc.)
(Fluorine)
W-2: Megafuck R08 (Dainippon Ink Chemical Co., Ltd.)
(Fluorine and silicon)
W-3: Polysiloxane polymer KP-341 (manufactured by Shin-Etsu Chemical Co., Ltd.)
(Silicon)
W-4: Troisol S-366 (manufactured by Troy Chemical Co., Ltd.)
W-5: PF656 (manufactured by OMNOVA, fluorine-based)
W-6: PF6320 (manufactured by OMNOVA, fluorine-based)

SL-1: Cyclohexanone SL-2: Propylene glycol monomethyl ether acetate SL-3: Ethyl lactate SL-4: Propylene glycol monomethyl ether SL-5: γ-butyrolactone SL-6: Propylene carbonate

  From Table 2, the positive resist composition of the present invention has a reduced resist film thickness after pattern development and pattern profile deterioration under normal exposure conditions, and an immersion liquid under immersion exposure conditions. It is clear that the dissolution of the resist component into the resist and the collapse of the resist pattern after pattern development are improved.

Claims (6)

  (A) a resin whose solubility in an alkaline developer is increased by the action of an acid, (B) a compound that generates an acid upon irradiation with actinic rays or radiation, and (C) a surfactant having a basic group. A positive resist composition characterized by the above.   The positive resist composition according to claim 1, wherein the resin (A) has an alicyclic hydrocarbon structure. The positive resist composition according to claim 1, wherein the surfactant (C) has a structure represented by the general formula (1).

In the general formula (1), R ₁ represents a hydrogen atom or an alkyl group. X ₁ represents a basic group. l represents an integer of 1 to 50. The positive resist composition according to claim 1, wherein the surfactant (C) has a structure represented by the general formula (3).

In general formula (3),
R ₄ represents a linking group. R ₅ represents a hydrogen atom or an alkyl group. Rf represents an alkyl group, a fluoroalkyl group or a fluoroalkylcarbonyl group. X ₂ and X ₃ each independently represents a hydrogen atom, an alkyl group, an alkylcarbonyl group, a lactone group, or a basic group. n represents an integer of 1 to 50.   A pattern forming method comprising: forming a resist film from the composition according to claim 1; and exposing and developing the resist film.   6. The pattern forming method according to claim 5, wherein the exposure is performed through an immersion liquid.