JP2006241336A - Cellulose acylate film-manufacturing method, polarizing plate and liquid crystal display device - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To manufacture a cellulose acylate film that attains a high retardation value without causing a planar failure resulting from a retardation-increasing agent. <P>SOLUTION: The manufacturing method of the cellulose acylate film containing a retardation-increasing agent is provided. The cellulose acylate film having a front retardation value Re within the range of 50-100 nm and a retardation value Rth in the film thickness direction within the range of 160-300 nm is obtained by using as the retardation-increasing agent a powder satisfying the following powder properties: (1) an angle of repose of at most 55°; (2) a compression degree of at most 30%; (3) a spatula angle of at most 75°; and (4) an agglomeration degree of at most 30%. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  The present invention relates to a method for producing a cellulose acylate film that exhibits retardation required for an optical compensation film, a polarizing plate using the cellulose acylate film obtained by the production method, and a liquid crystal display device including the polarizing plate. .

  Among the cellulose films, the cellulose acetate film is characterized by high optical isotropy (low retardation value) compared to other polymer films. Therefore, it is common to use a cellulose acetate film for an application requiring optical isotropy, for example, a polarizing plate. On the other hand, an optical anisotropy (high retardation value) is required for an optical compensation film such as a liquid crystal display device. Therefore, it is common to use a synthetic polymer film having a high retardation value such as a polycarbonate film or a polysulfone film as the optical compensation film.

  Recently, however, cellulose acetate films having a high retardation value that can be used for applications requiring optical anisotropy have been proposed (for example, Patent Document 1 and Patent Document 2). Further, the use of an optical biaxial cellulose acylate film has been proposed as an optical compensation film for a VA (Vertically Aligned) mode liquid crystal display device.

  In order to produce a highly retardation cellulose acylate film, it is useful to use an additive comprising a rod-like or discotic compound as a retardation developer. However, since the cellulose acylate solution used for forming the cellulose acylate film has a high viscosity, when a powder additive is directly added, a dissolution residue is generated, causing streak-like or bumpy surface failure.

Then, adding the said additive to the cellulose acylate solution in the form of the addition liquid which melt | dissolved in the solvent is performed. However, since the additive powder easily aggregates, the aggregate of the powder settles in the additive solution, resulting in a non-uniform solution, and there is also a problem that a streak-like or bumpy surface failure occurs. .
European Patent Publication EP0911656A2 JP 2003-344655 A

  An object of the present invention is to produce a cellulose acylate film that exhibits high retardation without causing a planar failure caused by the retardation enhancer.

As a result of intensive studies to achieve the above object, the present inventors have used a retardation developer having a predetermined powder physical property, thereby dissolving the retardation developer in the cellulose acylate solution. The present inventors have found that a cellulose acylate film having a high retardation can be obtained without causing a planar failure due to the remainder or aggregation, and the present invention has been completed.
That is, the means for achieving the object of the present invention is as follows.
[1] A method for producing a cellulose acylate film containing a retardation enhancer,
As the retardation developer, the following powder physical properties:
(1) Angle of repose 55 degrees or less (2) Compressibility 30% or less (3) Spatula angle 75 degrees or less (4) Using a powder satisfying an aggregation degree of 30% or less, the front retardation Re is in the range of 50 to 100 nm. And a cellulose acylate film having a retardation Rth in the film thickness direction of 160 to 300 nm is obtained.
[2] The method for producing a cellulose acylate film according to [1], including a stretching step of stretching the cellulose acylate film by 10% or more in the film casting direction or the casting width direction.
[3] The method for producing a cellulose acylate film according to [2], wherein the stretching step is performed by a uniaxial stretching method, a simultaneous biaxial stretching method, or a sequential biaxial stretching method.
[4] The method for producing a cellulose acylate film according to any one of [1] to [3], which is used in the state of an additive solution in which the retardation developer is dissolved in an organic solvent.
[5] The method for producing a cellulose acylate film according to any one of [1] to [4], wherein the retardation developer is a rod-like or discotic compound.
[6] In the cellulose acylate film, the substitution degree of the hydroxyl group at the 2-position of the glucose unit of the cellulose acylate film by DS2 is DS2, the substitution degree by the acyl group of the hydroxyl group at the 3-position is DS3, and the acyl group of the hydroxyl group at the 6-position is When the substitution degree by the group is DS6, the following mathematical formulas (VI-a) and (VI-b) are satisfied, and the thermal expansion coefficients D (MD) and D (TD) of the cellulose acylate film are the following mathematical formulas ( The method for producing a cellulose acylate film according to any one of [1] to [5], which satisfies VI).
Formula (VI-a): 2.0 ≦ DS2 + DS3 + DS6 ≦ 3.0
Formula (VI-b): DS6 / (DS2 + DS3 + DS6) ≧ 0.315
Formula (VI): 1.0 ≦ D (MD) / D (TD) ≦ 3.0
[7] The method for producing a cellulose acylate film according to any one of [1] to [6], wherein the cellulose acylate film contains at least one of a plasticizer, an ultraviolet absorber, and a release accelerator.
[8] A polarizing plate having a polarizing film and a pair of protective films sandwiching the polarizing film,
A polarizing plate, wherein at least one of the protective films is a cellulose acylate film obtained by the production method according to any one of [1 to [7].
[9] A liquid crystal display device having the cellulose acylate film obtained by the production method according to any one of [1] to [7] or the polarizing plate according to claim 8.
[10] A liquid crystal display device having a liquid crystal cell and a pair of polarizing plates disposed on both sides of the liquid crystal cell,
An OCB or VA mode liquid crystal display device, wherein the polarizing plate is the polarizing plate described in [8].
[11] A VA mode liquid crystal display device using the polarizing plate according to [8] on the backlight side.
[12] A retardation developer comprising a powder satisfying the powder physical properties (1) to (4).
[13] A retardation developer for a cellulose acylate film comprising a powder satisfying the powder physical properties (1) to (4).
[14] A method for producing a cellulose acylate film, comprising a step of adding a powder satisfying the powder physical properties (1) to (4) to a cellulose acylate film solution.
[15] A method for producing a cellulose acylate film, comprising mixing a solution in which powder satisfying the powder physical properties (1) to (4) is dissolved and a cellulose acylate film solution.

  According to the present invention, it is possible to provide a cellulose acylate film having both a good surface shape and high retardation.

  Hereinafter, the present invention will be described in detail. The description of the constituent elements described below may be made based on typical embodiments of the present invention, but the present invention is not limited to such embodiments. In the present specification, a numerical range represented by using “to” means a range including numerical values described before and after “to” as a lower limit value and an upper limit value.

In the present invention, Re (λ) and Rth (λ) respectively represent the front retardation and the retardation in the film thickness direction at the wavelength λ. Re (λ) is measured in KOBRA 21ADH (manufactured by Oji Scientific Instruments) by making light having a wavelength of λ nm incident in the normal direction of the film. Rth (λ) is light having a wavelength of λ nm from the direction inclined by + 40 ° with respect to the normal direction of the film, with Re (λ) and the in-plane slow axis (determined by KOBRA 21ADH) as the tilt axis (rotation axis). And a retardation value measured by making light of wavelength λ nm incident from a direction inclined by −40 ° with respect to the film normal direction with the in-plane slow axis as the tilt axis (rotation axis). KOBRA 21ADH calculates based on the retardation value measured in three directions, the assumed value of the average refractive index, and the input film thickness value. Here, as the assumed value of the average refractive index, the values in the polymer handbook (JOHN WILEY & SONS, INC) and catalogs of various optical films can be used. Those whose average refractive index is not known can be measured with an Abbe refractometer. The average refractive index values of main optical films are exemplified below: cellulose acylate (1.48), cycloolefin polymer (1.52), polycarbonate (1.59), polymethyl methacrylate (1.49), Polystyrene (1.59).
In the present invention, the average refractive index of 1.48 was used for the cellulose acylate film.

The retardation developer used in the present invention has the following powder physical properties:
(1) Angle of repose 55 degrees or less (2) Compressibility 30% or less (3) Spatula angle 75 degrees or less (4) Aggregation degree A powder satisfying 30% or less. In the present invention, by using a retardation developer composed of a powder having the above specific powder physical properties, there is no occurrence of planar failure due to undissolved powder or aggregation in the cellulose acylate solution. A cellulose acylate film having a high retardation can be obtained.
Hereafter, each said physical property is demonstrated.

  The angle of repose is the maximum inclination angle of the slope on which the powder can be formed, and increases as the fine particle powder increases and the water content increases. The angle of repose of the retardation enhancer used in the present invention is 55 degrees or less, preferably 5 to 45 degrees, more preferably 10 to 35 degrees.

  The degree of compression is the bulkiness obtained from the difference in bulk density between loose filling and dense filling. The degree of compression of the retardation developer is 30% or less, preferably 1 to 25%, more preferably 3 to 15%.

  The spatula angle is the inclination angle of the slope of the powder deposited on the spatula (metal spatula). The spatula angle of the retardation developer is 75 degrees or less, preferably 5 to 60 degrees, and more preferably 10 to 38 degrees.

The agglomeration degree is a value measured as the amount of agglomerated powder remaining after applying a constant vibration to the standard sieve for a predetermined time. The aggregation degree of the retardation enhancer is 30% or less, preferably 10% or less, more preferably 2% or less. Note that the lower limit is 0% on the measurement principle.
Each of the above physical properties can be measured by a powder tester manufactured by Hosokawa Micron Corporation or a multi tester MT-1001 manufactured by Seishin Corporation. In addition, the above powder physical properties are pulverization, classification, sieving, mixing, granulation / coating, as shown in “Introduction to Revision Supplementary Powder Trouble Optics” (published by Industrial Research Institute, Inc.) 266-302. It can be controlled by appropriately using a method such as drying.

  The front retardation Re of the cellulose acylate film obtained by the production method of the present invention is in the range of 50 to 100 nm, preferably 55 to 90 nm, more preferably 60 to 80 nm. The retardation Rth in the film thickness direction is in the range of 160 to 300 nm, preferably 170 to 260 nm, and more preferably 180 to 240 nm. In the present invention, a cellulose acylate film having a retardation in the above range can be obtained by appropriately selecting the type and amount of the retardation enhancer, the draw ratio, and the like.

  The retardation developer may be a rod-like or discotic compound. As the rod-like or discotic compound, a compound having at least two aromatic rings can be used.

  The addition amount of the retardation enhancer composed of the rod-shaped compound is preferably 0.1 to 30 parts by mass, and preferably 0.5 to 20 parts by mass with respect to 100 parts by mass of the polymer component containing cellulose acylate. Further preferred. The disk-shaped retardation developer is preferably used in a range of 0.05 to 20 parts by mass, and in a range of 0.1 to 10 parts by mass with respect to 100 parts by mass of the polymer component containing the cellulose acylate. It is more preferable to use it, it is more preferable to use in the range of 0.2-5 mass parts, and it is most preferable to use in the range of 0.5-2 mass parts. Since the discotic compound is superior to the rod-shaped compound in Rth retardation expression, it is preferably used when a particularly large Rth retardation is required. Two or more types of retardation developing agents may be used in combination. The retardation developer composed of a rod-like or discotic compound preferably has maximum absorption in the wavelength region of 250 to 400 nm, and preferably has substantially no absorption in the visible region.

Next, the discotic compound will be described.
As the discotic compound, a compound having at least two aromatic rings can be used. In the present specification, the “aromatic ring” includes an aromatic hetero ring in addition to an aromatic hydrocarbon ring.
The aromatic hydrocarbon ring is particularly preferably a 6-membered ring (that is, a benzene ring).
The aromatic heterocycle is generally an unsaturated heterocycle. The aromatic heterocycle is preferably a 5-membered ring, 6-membered ring or 7-membered ring, more preferably a 5-membered ring or 6-membered ring. Aromatic heterocycles generally have the most double bonds. As the hetero atom, a nitrogen atom, an oxygen atom and a sulfur atom are preferable, and a nitrogen atom is particularly preferable. Examples of aromatic heterocycles include furan ring, thiophene ring, pyrrole ring, oxazole ring, isoxazole ring, thiazole ring, isothiazole ring, imidazole ring, pyrazole ring, furazane ring, triazole ring, pyran ring, pyridine ring , Pyridazine ring, pyrimidine ring, pyrazine ring and 1,3,5-triazine ring.
As the aromatic ring, benzene ring, furan ring, thiophene ring, pyrrole ring, oxazole ring, thiazole ring, imidazole ring, triazole ring, pyridine ring, pyrimidine ring, pyrazine ring and 1,3,5-triazine ring are preferable, In particular, a 1,3,5-triazine ring is preferably used. Specifically, for example, a compound disclosed in JP 2001-166144 A is preferably used as the discotic compound.

The number of aromatic rings contained in the discotic compound is preferably 2 to 20, more preferably 2 to 12, further preferably 2 to 8, and most preferably 2 to 6. preferable.
The bond relationship between two aromatic rings can be classified into (a) a condensed ring, (b) a direct bond with a single bond, and (c) a bond through a linking group (for aromatic rings). , Spiro bonds cannot be formed). The connection relationship may be any of (a) to (c).

  Examples of the condensed ring (a condensed ring of two or more aromatic rings) include an indene ring, a naphthalene ring, an azulene ring, a fluorene ring, a phenanthrene ring, an anthracene ring, an acenaphthylene ring, a biphenylene ring, a naphthacene ring, Pyrene ring, indole ring, isoindole ring, benzofuran ring, benzothiophene ring, indolizine ring, benzoxazole ring, benzothiazole ring, benzimidazole ring, benzotriazole ring, purine ring, indazole ring, chromene ring, quinoline ring, isoquinoline Ring, quinolidine ring, quinazoline ring, cinnoline ring, quinoxaline ring, phthalazine ring, pteridine ring, carbazole ring, acridine ring, phenanthridine ring, xanthene ring, phenazine ring, phenothiazine ring, phenoxathiin ring, phenoxazine ring and thiant It includes emissions ring. Naphthalene ring, azulene ring, indole ring, benzoxazole ring, benzothiazole ring, benzimidazole ring, benzotriazole ring and quinoline ring are preferred.

  The single bond (b) is preferably a bond between carbon atoms of two aromatic rings. Two aromatic rings may be bonded with two or more single bonds to form an aliphatic ring or a non-aromatic heterocyclic ring between the two aromatic rings.

The linking group in (c) is also preferably bonded to carbon atoms of two aromatic rings. The linking group is preferably an alkylene group, an alkenylene group, an alkynylene group, —CO—, —O—, —NH—, —S—, or a combination thereof. Examples of linking groups composed of combinations are shown below. In addition, the relationship between the left and right in the following examples of the linking group may be reversed.
c1: -CO-O-
c2: —CO—NH—
c3: -alkylene-O-
c4: —NH—CO—NH—
c5: —NH—CO—O—
c6: —O—CO—O—
c7: -O-alkylene-O-
c8: -CO-alkenylene-
c9: -CO-alkenylene-NH-
c10: -CO-alkenylene-O-
c11: -alkylene-CO-O-alkylene-O-CO-alkylene-
c12: -O-alkylene-CO-O-alkylene-O-CO-alkylene-O-
c13: -O-CO-alkylene-CO-O-
c14: -NH-CO-alkenylene-
c15: -O-CO-alkenylene-

The aromatic ring and the linking group may have a substituent.
Examples of substituents include halogen atoms (F, Cl, Br, I), hydroxyl groups, carboxyl groups, cyano groups, amino groups, nitro groups, sulfo groups, carbamoyl groups, sulfamoyl groups, ureido groups, alkyl groups, alkenyls. Group, alkynyl group, aliphatic acyl group, aliphatic acyloxy group, alkoxy group, alkoxycarbonyl group, alkoxycarbonylamino group, alkylthio group, alkylsulfonyl group, aliphatic amide group, aliphatic sulfonamido group, aliphatic substituted amino group An aliphatic substituted carbamoyl group, an aliphatic substituted sulfamoyl group, an aliphatic substituted ureido group, and a non-aromatic heterocyclic group.

It is preferable that the alkyl group has 1 to 8 carbon atoms. A chain alkyl group is preferable to a cyclic alkyl group, and a linear alkyl group is particularly preferable. The alkyl group may further have a substituent (eg, hydroxy group, carboxy group, alkoxy group, alkyl-substituted amino group). Examples of alkyl groups (including substituted alkyl groups) include methyl, ethyl, n-butyl, n-hexyl, 2-hydroxyethyl, 4-carboxybutyl, 2-methoxyethyl, and 2- A diethylaminoethyl group is included.
The alkenyl group preferably has 2 to 8 carbon atoms. A chain alkenyl group is preferable to a cyclic alkenyl group, and a linear alkenyl group is particularly preferable. The alkenyl group may further have a substituent. Examples of the alkenyl group include a vinyl group, an allyl group, and a 1-hexenyl group.
The alkynyl group preferably has 2 to 8 carbon atoms. A chain alkynyl group is preferable to a cyclic alkynyl group, and a linear alkynyl group is particularly preferable. The alkynyl group may further have a substituent. Examples of the alkynyl group include ethynyl group, 1-butynyl group and 1-hexynyl group.

The number of carbon atoms in the aliphatic acyl group is preferably 1-10. Examples of the aliphatic acyl group include an acetyl group, a propanoyl group, and a butanoyl group.
The number of carbon atoms in the aliphatic acyloxy group is preferably 1-10. Examples of the aliphatic acyloxy group include an acetoxy group.
The number of carbon atoms of the alkoxy group is preferably 1-8. The alkoxy group may further have a substituent (eg, alkoxy group). Examples of the alkoxy group (including a substituted alkoxy group) include a methoxy group, an ethoxy group, a butoxy group, and a methoxyethoxy group.
The number of carbon atoms of the alkoxycarbonyl group is preferably 2-10. Examples of the alkoxycarbonyl group include a methoxycarbonyl group and an ethoxycarbonyl group.
The number of carbon atoms of the alkoxycarbonylamino group is preferably 2-10. Examples of the alkoxycarbonylamino group include a methoxycarbonylamino group and an ethoxycarbonylamino group.

The alkylthio group preferably has 1 to 12 carbon atoms. Examples of the alkylthio group include a methylthio group, an ethylthio group, and an octylthio group.
The alkylsulfonyl group preferably has 1 to 8 carbon atoms. Examples of the alkylsulfonyl group include a methanesulfonyl group and an ethanesulfonyl group.
The number of carbon atoms in the aliphatic amide group is preferably 1-10. Examples of the aliphatic amide group include an acetamide group.
The number of carbon atoms of the aliphatic sulfonamide group is preferably 1-8. Examples of the aliphatic sulfonamido group include a methanesulfonamido group, a butanesulfonamido group, and an n-octanesulfonamido group.
The number of carbon atoms of the aliphatic substituted amino group is preferably 1-10. Examples of the aliphatic substituted amino group include a dimethylamino group, a diethylamino group, and a 2-carboxyethylamino group.
The number of carbon atoms in the aliphatic substituted carbamoyl group is preferably 2-10. Examples of the aliphatic substituted carbamoyl group include a methylcarbamoyl group and a diethylcarbamoyl group.
The number of carbon atoms in the aliphatic substituted sulfamoyl group is preferably 1-8. Examples of the aliphatic substituted sulfamoyl group include a methylsulfamoyl group and a diethylsulfamoyl group.
The number of carbon atoms in the aliphatic substituted ureido group is preferably 2-10. Examples of the aliphatic substituted ureido group include a methylureido group.
Examples of the non-aromatic heterocyclic group include a piperidino group and a morpholino group.
The molecular weight of the retardation developer composed of a discotic compound is preferably 300 to 800.

  In the present invention, in addition to the aforementioned discotic compound, a rod-shaped compound having a linear molecular structure can also be preferably used. The linear molecular structure means that the molecular structure of the rod-like compound is linear in the most thermodynamically stable structure. The most thermodynamically stable structure can be obtained by crystal structure analysis or molecular orbital calculation. For example, molecular orbital calculation can be performed using molecular orbital calculation software (eg, WinMOPAC2000, manufactured by Fujitsu Limited) to determine the molecular structure that minimizes the heat of formation of the compound. The molecular structure being linear means that in the thermodynamically most stable structure obtained by calculation as described above, the angle of the main chain constituting the molecular structure is 140 degrees or more.

As the rod-shaped compound, those having at least two aromatic rings are preferable, and as the rod-shaped compound having at least two aromatic rings, a compound represented by the following general formula (1) is preferable.
Formula (1): Ar ¹ -L ¹ -Ar ²
In the general formula (1), Ar ¹ and Ar ² are each independently an aromatic group.
In the present specification, the aromatic group includes an aryl group (aromatic hydrocarbon group), a substituted aryl group, an aromatic heterocyclic group, and a substituted aromatic heterocyclic group.
An aryl group and a substituted aryl group are more preferable than an aromatic heterocyclic group and a substituted aromatic heterocyclic group. The heterocycle of the aromatic heterocyclic group is generally unsaturated. The aromatic heterocycle is preferably a 5-membered ring, 6-membered ring or 7-membered ring, more preferably a 5-membered ring or 6-membered ring. Aromatic heterocycles generally have the most double bonds. As a hetero atom, a nitrogen atom, an oxygen atom or a sulfur atom is preferable, and a nitrogen atom or a sulfur atom is more preferable.
As the aromatic ring of the aromatic group, a benzene ring, a furan ring, a thiophene ring, a pyrrole ring, an oxazole ring, a thiazole ring, an imidazole ring, a triazole ring, a pyridine ring, a pyrimidine ring and a pyrazine ring are preferable, and a benzene ring is particularly preferable. .

  Examples of the substituent of the substituted aryl group and the substituted aromatic heterocyclic group include a halogen atom (F, Cl, Br, I), a hydroxyl group, a carboxyl group, a cyano group, an amino group, an alkylamino group (eg, methyl). Amino group, ethylamino group, butylamino group, dimethylamino group), nitro group, sulfo group, carbamoyl group, alkylcarbamoyl group (eg, N-methylcarbamoyl group, N-ethylcarbamoyl group, N, N-dimethylcarbamoyl group) ), Sulfamoyl group, alkylsulfamoyl group (eg, N-methylsulfamoyl group, N-ethylsulfamoyl group, N, N-dimethylsulfamoyl group), ureido group, alkylureido group (eg, N -Methylureido group, N, N-dimethylureido group, N, N, N'-trimethylureido group), alkyl group (eg, Methyl, ethyl, propyl, butyl, pentyl, heptyl, octyl, isopropyl, s-butyl, t-amyl, cyclohexyl, cyclopentyl), alkenyl (eg, vinyl, allyl) Group, hexenyl group), alkynyl group (eg, ethynyl group, butynyl group), acyl group (eg, formyl group, acetyl group, butyryl group, hexanoyl group, lauryl group), acyloxy group (eg, acetoxy group, butyryloxy group, Hexanoyloxy group, lauryloxy group), alkoxy group (eg, methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, heptyloxy group, octyloxy group), aryloxy group (eg, phenoxy group), Alkoxycarbonyl group (eg, methoxycarbonyl group, ethoxycarbonyl group, Ropoxycarbonyl group, butoxycarbonyl group, pentyloxycarbonyl group, heptyloxycarbonyl group), aryloxycarbonyl group (eg, phenoxycarbonyl group), alkoxycarbonylamino group (eg, butoxycarbonylamino group, hexyloxycarbonylamino group) , Alkylthio groups (eg, methylthio group, ethylthio group, propylthio group, butylthio group, pentylthio group, heptylthio group, octylthio group), arylthio groups (eg, phenylthio group), alkylsulfonyl groups (eg, methylsulfonyl group, ethylsulfonyl group) , Propylsulfonyl group, butylsulfonyl group, pentylsulfonyl group, heptylsulfonyl group, octylsulfonyl group), amide group (eg, acetamido group, butyramide group, hexylamide group, Uriruamido group) and a non-aromatic Hajime Tamaki (e.g., morpholyl groups include pyrazinyl group).

Examples of the substituent of the substituted aryl group and the substituted aromatic heterocyclic group include a halogen atom, a cyano group, a carboxyl group, a hydroxyl group, an amino group, an alkyl-substituted amino group, an acyl group, an acyloxy group, an amide group, an alkoxycarbonyl group, Alkoxy groups, alkylthio groups and alkyl groups are preferred.
The alkyl part and the alkyl group of the alkylamino group, alkoxycarbonyl group, alkoxy group and alkylthio group may further have a substituent. Examples of alkyl moieties and substituents of alkyl groups include halogen atom, hydroxyl, carboxyl, cyano, amino, alkylamino group, nitro, sulfo, carbamoyl, alkylcarbamoyl group, sulfamoyl, alkylsulfamoyl group, ureido, alkylureido Group, alkenyl group, alkynyl group, acyl group, acyloxy group, acylamino group, alkoxy group, aryloxy group, alkoxycarbonyl group, aryloxycarbonyl group, alkoxycarbonylamino group, alkylthio group, arylthio group, alkylsulfonyl group, amide group And non-aromatic heterocyclic groups. As the substituent for the alkyl moiety and the alkyl group, a halogen atom, hydroxyl, amino, alkylamino group, acyl group, acyloxy group, acylamino group, alkoxycarbonyl group and alkoxy group are preferable.

In the general formula (1), L ¹ represents an alkylene group, an alkenylene group, an alkynylene group,-
A divalent linking group selected from the group consisting of O-, -CO-, and combinations thereof.
The alkylene group may have a cyclic structure. As the cyclic alkylene group, cyclohexylene is preferable, and 1,4-cyclohexylene is particularly preferable. As the chain alkylene group, a linear alkylene group is more preferable than a branched alkylene group.
The number of carbon atoms of the alkylene group is preferably 1-20, more preferably 1-15, still more preferably 1-10, still more preferably 1-8, and most preferably 1-6. It is.

The alkenylene group and alkynylene group preferably have a chain structure rather than a cyclic structure, and more preferably have a linear structure rather than a branched chain structure.
The alkenylene group and the alkynylene group preferably have 2 to 10 carbon atoms, more preferably 2 to 8, more preferably 2 to 6, still more preferably 2 to 4, and most preferably 2. (Vinylene or ethynylene).
The arylene group preferably has 6 to 20 carbon atoms, more preferably 6 to 16, and still more preferably 6 to 12.

In the molecular structure of the general formula (1), the angle formed by Ar ¹ and Ar ² across L ¹ is preferably 140 degrees or more.
As the rod-like compound, a compound represented by the following formula (2) is more preferable.
Formula ^{(2): Ar 1 -L 2} -X-L 3 -Ar 2
In the general formula (2), Ar ¹ and Ar ² are each independently an aromatic group. The definition and examples of the aromatic group are the same as those of Ar ¹ and Ar ^{2 in} the general formula (1).

In the general formula (2), L ² and L ³ are each independently a divalent linking group selected from an alkylene group, —O—, —CO—, and a group consisting of a combination thereof.
The alkylene group preferably has a chain structure rather than a cyclic structure, and more preferably has a linear structure rather than a branched chain structure.
The alkylene group preferably has 1 to 10 carbon atoms, more preferably 1 to 8, more preferably 1 to 6, still more preferably 1 to 4, and 1 or 2 (methylene or Most preferred is ethylene).
L ² and L ³ are particularly preferably —O—CO— or —CO—O—.

In the general formula (2), X is 1,4-cyclohexylene, vinylene or ethynylene.
Specific examples of the compound represented by the general formula (1) or (2) are shown below.

  Specific examples (1) to (34), (41), and (42) have two asymmetric carbon atoms at the 1-position and the 4-position of the cyclohexane ring. However, since the specific examples (1), (4) to (34), (41), and (42) have a symmetrical meso type molecular structure, there are no optical isomers (optical activity), and geometric isomers (trans Type and cis type). The trans type (1-trans) and cis type (1-cis) of specific example (1) are shown below.

As described above, the rod-like compound preferably has a linear molecular structure. Therefore, the trans type is preferable to the cis type. Specific examples (2) and (3) have optical isomers (a total of four isomers) in addition to geometric isomers. As for geometric isomers, the trans type is similarly preferable to the cis type. The optical isomer is not particularly superior or inferior, and may be D, L, or a racemate.
In specific examples (43) to (45), the central vinylene bond includes a trans type and a cis type. For the same reason as above, the trans type is preferable to the cis type.

  A compound represented by the following general formula (3) is also preferable.

General formula (3)

(In the formula, R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁹ and R ¹⁰ each independently represent a hydrogen atom or a substituent, and R ¹ , R ² , R ³ , R ⁴ and R ⁵ each represents an electron donating group, wherein R ⁸ represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, or an alkynyl group having 2 to 6 carbon atoms. Group, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 6 to 12 carbon atoms, an alkoxycarbonyl group having 2 to 12 carbon atoms, an acylamino group having 2 to 12 carbon atoms, cyano Represents a group or a halogen atom.)
Specific examples of the compound represented by the general formula (3) are shown. However, the present invention is not limited to the following specific examples.

Two or more rod-shaped compounds having a maximum absorption wavelength (λmax) shorter than 250 nm in the ultraviolet absorption spectrum of the solution may be used in combination.
The rod-like compound can be synthesized by a method described in the literature. References include Mol. Cryst. Liq. Cryst., 53, 229 (1979), 89, 93 (1982), 145, 111 (1987), 170, 43 Page (1989), J. Am. Chem. Soc., 113, 1349 (1991), 118, 5346 (1996), 92, 1582 (1970), J. Org Chem., 40, 420 (1975), Tetrahedron, 48, 16, 3437 (1992).

[Wavelength dispersion modifier]
In the present invention, it is preferable to add a compound (hereinafter also referred to as a wavelength dispersion adjusting agent) that reduces the wavelength dispersion of the film to the cellulose acylate film.
Hereinafter, the wavelength dispersion adjusting agent will be described.
In the present invention, a compound capable of preventing coloration of the film and controlling the wavelength dispersion of Re (λ) and Rth (λ) of the cellulose acylate film by absorbing in the ultraviolet region of a wavelength of 200 to 400 nm. The difference between Re and Rth at wavelengths of 400 nm and 700 nm, preferably | Re ₍₄₀₀₎ −Re ₍₇₀₀₎ | and | Rth ₍₄₀₀₎ −Rth ₍₇₀₀₎ | can be reduced.

Furthermore, in the present invention, in order to improve the Rth wavelength dispersion of the cellulose acylate film, the Rth wavelength dispersion ΔRth = | Rth ₍₄₀₀₎ −Rth ₍₇₀₀₎ | represented by the following formula (iv) is decreased. It is preferable that at least one compound to be contained is contained in a range satisfying the following formulas (v) and (vi).
(Iv) ΔRth = | Rth ₍₄₀₀₎ −Rth ₍₇₀₀₎ |
(V) (ΔRth (B) −ΔRth (0)) / B ≦ −2.0
(Vi) 0.01 ≦ B ≦ 30
The above formulas (v) and (vi) are: (v) (ΔRth (B) −ΔRth (0)) / B ≦ −3.0
(Vi) 0.05 ≦ B ≦ 25
It is more desirable to be
(V) (ΔRth (B) −ΔRth (0)) / B ≦ −4.0
(Vi) 0.1 ≦ B ≦ 20
It is even more desirable.

  In general, the Re and Rth values of the cellulose acylate film have a wavelength dispersion characteristic that the longer wavelength side is larger than the shorter wavelength side. Therefore, it is required to smooth the chromatic dispersion by increasing Re and Rth on the relatively short wavelength side. On the other hand, a compound having absorption in the ultraviolet region of 200 to 400 nm has a wavelength dispersion characteristic in which the absorbance on the long wavelength side is larger than that on the short wavelength side. If the compound itself is isotropically present inside the cellulose acylate film, it is assumed that the birefringence of the compound itself, and thus the wavelength dispersion of Re and Rth, is large on the short wavelength side as well as the wavelength dispersion of absorbance. .

  Therefore, as described above, by using the compound having absorption in the ultraviolet region of 200 to 400 nm and assuming that the wavelength dispersion of Re and Rth of the compound itself is large on the short wavelength side, the Re and Rth of the cellulose acylate film are used. Chromatic dispersion can be prepared. For this purpose, it is preferable that the compound for adjusting the wavelength dispersion is sufficiently uniformly compatible with the cellulose acylate. The absorption band range in the ultraviolet region of such a compound is preferably 200 to 400 nm, more preferably 220 to 395 nm, and even more preferably 240 to 390 nm.

In recent years, liquid crystal display devices such as televisions, notebook personal computers, and mobile portable terminals have been required to have excellent transmittance of optical members used in liquid crystal display devices in order to increase luminance with less power. In that respect, cellulose acylate containing a compound having absorption in the ultraviolet region of 200 to ₄₀₀ nm and reducing | Re ₍₄₀₀₎ -Re ₍₇₀₀₎ | and | Rth ₍₄₀₀₎ -Rth ₍₇₀₀₎ | The film preferably has a high spectral transmittance. In the cellulose acylate film used in the present invention, the spectral transmittance at a wavelength of 380 nm is preferably 45% to 95%, and the spectral transmittance at a wavelength of 350 nm is preferably 10% or less.

  As described above, the wavelength dispersion adjusting agent preferably used in the present invention preferably has a molecular weight of 250 to 1000 from the viewpoint of volatility. More preferably, it is 260-800, More preferably, it is 270-800, Most preferably, it is 300-800. A specific monomer structure may be used as long as these molecular weights are within the range, and an oligomer structure or a polymer structure in which a plurality of the monomer units are bonded may be used.

  It is preferable that the wavelength dispersion adjusting agent does not volatilize during the dope casting and drying process for producing the cellulose acylate film.

(Compound addition amount)
The added amount of the wavelength dispersion adjusting agent preferably used in the present invention is preferably 0.01 to 30% by mass, more preferably 0.1 to 20% by mass with respect to the solid content of cellulose acylate. It is particularly preferably 0.2 to 10% by mass.

(Method of compound addition)
These wavelength dispersion adjusting agents may be used alone or in combination of two or more compounds at an arbitrary ratio.
Further, the timing of adding these wavelength dispersion adjusting agents may be any time during the dope preparation process, or may be performed at the end of the dope preparation process.

  Specific examples of the wavelength dispersion adjusting agent preferably used in the present invention include, for example, benzotriazole compounds, benzophenone compounds, cyano group-containing compounds, oxybenzophenone compounds, salicylic acid ester compounds, nickel complex compounds, and the like. However, the present invention is not limited to these compounds.

  As the benzotriazole-based compound, those represented by the general formula (101) are preferably used as a wavelength dispersion adjusting agent.

Formula (101) Q ¹ -Q ² -OH

(In the formula, Q ¹ represents a nitrogen-containing aromatic heterocycle Q ² represents an aromatic ring.)

Q ¹ represents a nitrogen-containing aromatic heterocycle, preferably a 5- to 7-membered nitrogen-containing aromatic heterocycle, more preferably a 5- to 6-membered nitrogen-containing aromatic heterocycle, such as imidazole , Pyrazole, triazole, tetrazole, thiazole, oxazole, selenazole, benzotriazole, benzothiazole, benzoxazole, benzoselenazole, thiadiazole, oxadiazole, naphthothiazole, naphthoxazole, azabenzimidazole, purine, pyridine, pyrazine, pyrimidine, And pyridazine, triazine, triazaindene, tetrazaindene and the like, more preferably a 5-membered nitrogen-containing aromatic heterocycle, specifically imidazole, pyrazole, triazole, tetrazole, thiazole, oxazo. Le, benzotriazole, benzothiazole, benzoxazole, thiadiazole, oxadiazole preferably, particularly preferably benzotriazole.
The nitrogen-containing aromatic heterocycle represented by Q ¹ may further have a substituent, and the substituent T described below can be applied as the substituent. In addition, when there are a plurality of substituents, each may be condensed to form a ring.

The aromatic ring represented by Q ² may be an aromatic hydrocarbon ring or an aromatic heterocycle. These may be monocyclic or may form a condensed ring with another ring.
The aromatic hydrocarbon ring is preferably (preferably a monocyclic or bicyclic aromatic hydrocarbon ring having 6 to 30 carbon atoms (for example, benzene ring, naphthalene ring etc.), more preferably 6 carbon atoms. -20 aromatic hydrocarbon ring, more preferably an aromatic hydrocarbon ring having 6 to 12 carbon atoms.) More preferred is a benzene ring.
The aromatic heterocycle is preferably an aromatic heterocycle containing a nitrogen atom or a sulfur atom. Specific examples of the heterocyclic ring include, for example, thiophene, imidazole, pyrazole, pyridine, pyrazine, pyridazine, triazole, triazine, indole, indazole, purine, thiazoline, thiazole, thiadiazole, oxazoline, oxazole, oxadiazole, quinoline, isoquinoline, Examples include phthalazine, naphthyridine, quinoxaline, quinazoline, cinnoline, pteridine, acridine, phenanthroline, phenazine, tetrazole, benzimidazole, benzoxazole, benzthiazole, benzotriazole, and tetrazaindene. Preferred examples of the aromatic heterocycle include pyridine, triazine, and quinoline.
The aromatic ring represented by Q ² is preferably an aromatic hydrocarbon ring, more preferably a naphthalene ring or a benzene ring, and particularly preferably a benzene ring. Q ² may further have a substituent, and the substituent T described later is preferable.
Examples of the substituent T include an alkyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, and particularly preferably 1 to 8 carbon atoms, such as a methyl group, an ethyl group, an isopropyl group, and tert-butyl. Group, n-octyl group, n-decyl group, n-hexadecyl group, cyclopropyl group, cyclopentyl group, cyclohexyl group, etc.), alkenyl group (preferably having 2 to 20 carbon atoms, more preferably 2 carbon atoms). To 12, particularly preferably 2 to 8 carbon atoms, such as vinyl group, allyl group, 2-butenyl group, and 3-pentenyl group), alkynyl group (preferably 2 to 20 carbon atoms, more preferably Has 2 to 12 carbon atoms, particularly preferably 2 to 8 carbon atoms, and examples thereof include a propargyl group and a 3-pentynyl group.), Aryl (Preferably having 6 to 30 carbon atoms, more preferably 6 to 20 carbon atoms, and particularly preferably 6 to 12 carbon atoms, and examples thereof include a phenyl group, a p-methylphenyl group, and a naphthyl group). An unsubstituted amino group (preferably having 0 to 20 carbon atoms, more preferably 0 to 10 carbon atoms, and particularly preferably 0 to 6 carbon atoms; for example, an amino group, a methylamino group, a dimethylamino group, a diethylamino group, a diamino group; Benzylamino group, etc.), alkoxy groups (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, particularly preferably 1 to 8 carbon atoms, such as methoxy group, ethoxy group, butoxy group. An aryloxy group (preferably having 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, and particularly preferably 6 to 12 carbon atoms). , For example, phenyloxy group, 2-naphthyloxy group, etc.), acyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, Acetyl group, benzoyl group, formyl group, pivaloyl group, etc.), alkoxycarbonyl group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, For example, a methoxycarbonyl group, an ethoxycarbonyl group, etc.), an aryloxycarbonyl group (preferably having a carbon number of 7 to 20, more preferably a carbon number of 7 to 16, particularly preferably a carbon number of 7 to 10, such as phenyl An oxycarbonyl group, etc.), an acyloxy group (preferably having 2 to 20 carbon atoms, more preferably carbon It has 2 to 16 primes, particularly preferably 2 to 10 carbons, and examples thereof include acetoxy and benzoyloxy groups. ), An acylamino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 10 carbon atoms, and examples thereof include an acetylamino group and a benzoylamino group), alkoxycarbonyl. An amino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, such as a methoxycarbonylamino group), an aryloxycarbonylamino group (preferably Has 7 to 20 carbon atoms, more preferably 7 to 16 carbon atoms, particularly preferably 7 to 12 carbon atoms, such as a phenyloxycarbonylamino group, and a sulfonylamino group (preferably 1 to 1 carbon atom). 20, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms. Nylamino group, benzenesulfonylamino group, etc.), sulfamoyl group (preferably having 0 to 20 carbon atoms, more preferably 0 to 16 carbon atoms, particularly preferably 0 to 12 carbon atoms, such as sulfamoyl group, methyl A sulfamoyl group, a dimethylsulfamoyl group, a phenylsulfamoyl group, etc.), a carbamoyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably 1 to carbon atoms). For example, carbamoyl group, methylcarbamoyl group, diethylcarbamoyl group, phenylcarbamoyl group, etc.), alkylthio group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably carbon). Examples thereof include methylthio group and ethylthio group. ), An arylthio group (preferably having 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, particularly preferably 6 to 12 carbon atoms, such as a phenylthio group), a sulfonyl group (preferably C1-C20, More preferably, it is C1-C16, Most preferably, it is C1-C12, For example, a mesyl group, a tosyl group, etc. are mentioned), a sulfinyl group (preferably C1-C20, More preferably, it is C1-C16, Most preferably, it is C1-C12, for example, a methanesulfinyl group, a benzenesulfinyl group, etc.), a ureido group (preferably C1-C20, more preferably carbon) The number is 1 to 16, particularly preferably 1 to 12, and examples thereof include a ureido group, a methylureido group, and a phenylureido group. ), A phosphoric acid amide group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably 1 to 12 carbon atoms, such as a diethylphosphoric acid amide group and a phenylphosphoric acid amide group. Hydroxy group, mercapto group, halogen atom (eg fluorine atom, chlorine atom, bromine atom, iodine atom), cyano group, sulfo group, carboxyl group, nitro group, hydroxamic acid group, sulfino group, hydrazino group, imino group Group, heterocyclic group (preferably having 1 to 30 carbon atoms, more preferably 1 to 12 carbon atoms, for example, nitrogen atom, oxygen atom, sulfur atom, specifically imidazolyl group, pyridyl group, quinolyl, etc. Group, furyl group, piperidyl group, morpholino group, benzoxazolyl group, benzimidazolyl group, benzthiazolyl group, etc. ), A silyl group (preferably having 3 to 40 carbon atoms, more preferably 3 to 30 carbon atoms, particularly preferably 3 to 24 carbon atoms, and examples thereof include a trimethylsilyl group and a triphenylsilyl group. For example). These substituents may be further substituted. Moreover, when there are two or more substituents, they may be the same or different. If possible, they may be linked together to form a ring.

As the general formula (101), a compound represented by the following general formula (101-A) is preferable.
General formula (101-A)

(Wherein R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , and R ⁸ each independently represents a hydrogen atom or a substituent)

R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁸ , and R ⁹ each independently represent a hydrogen atom or a substituent, and the above-mentioned substituent T is applied as the substituent. it can. These substituents may be further substituted with another substituent, and the substituents may be condensed to form a ring structure.
R ¹ and R ³ are preferably hydrogen atoms, alkyl groups, alkenyl groups, alkynyl groups, aryl groups, substituted or unsubstituted amino groups, alkoxy groups, aryloxy groups, hydroxy groups, and halogen atoms, more preferably hydrogen atoms. An atom, an alkyl group, an aryl group, an alkyloxy group, an aryloxy group and a halogen atom, more preferably a hydrogen atom and an alkyl group having 1 to 12 carbon atoms, particularly preferably an alkyl group having 1 to 12 carbon atoms (preferably 4 to 12 carbon atoms).

R ² and R ⁴ are preferably a hydrogen atom, an alkyl group, an alkenyl group, an alkynyl group, an aryl group, a substituted or unsubstituted amino group, an alkoxy group, an aryloxy group, a hydroxy group, and a halogen atom, more preferably A hydrogen atom, an alkyl group, an aryl group, an alkyloxy group, an aryloxy group, and a halogen atom, more preferably a hydrogen atom and an alkyl group having 1 to 12 carbon atoms, particularly preferably a hydrogen atom and a methyl group, most preferably Is a hydrogen atom.

R ⁵ and R ⁸ are preferably hydrogen atoms, alkyl groups, alkenyl groups, alkynyl groups, aryl groups, substituted or unsubstituted amino groups, alkoxy groups, aryloxy groups, hydroxy groups, and halogen atoms, more preferably hydrogen atoms. An atom, an alkyl group, an aryl group, an alkyloxy group, an aryloxy group and a halogen atom, more preferably a hydrogen atom and an alkyl group having 1 to 12 carbon atoms, particularly preferably a hydrogen atom and a methyl group, most preferably It is a hydrogen atom.

R ⁶ and R ⁷ are preferably hydrogen atoms, alkyl groups, alkenyl groups, alkynyl groups, aryl groups, substituted or unsubstituted amino groups, alkoxy groups, aryloxy groups, hydroxy groups, and halogen atoms, more preferably hydrogen atoms. An atom, an alkyl group, an aryl group, an alkyloxy group, an aryloxy group, and a halogen atom, more preferably a hydrogen atom and a halogen atom, and particularly preferably a hydrogen atom and a chlorine atom.

More preferable as the general formula (101) is a compound represented by the following general formula (101-B).
General formula (101-B)

(In formula, R < ¹ >, R < ³ >, R < ⁶ > and R < ⁷ > are synonymous with those in general formula (101-A), and their preferred ranges are also the same.)

  Specific examples of the compound represented by formula (101) are listed below, but the present invention is not limited to the following specific examples.

  Among the benzotriazole-based compounds mentioned in the above examples, it is advantageous in terms of retentiveness to produce a cellulose acylate film without containing a molecular weight of 320 or less.

In addition, as the benzophenone compound which is one of the wavelength dispersion adjusting agents used in the present invention, those represented by the general formula (102) are preferably used.
Formula (102)

(In the formula, Q ¹ and Q ² each independently represent an aromatic ring. X represents NR (R represents a hydrogen atom or a substituent), an oxygen atom or a sulfur atom.)

The aromatic ring represented by Q ¹ and Q ² may be an aromatic hydrocarbon ring or an aromatic heterocycle. These may be monocyclic or may form a condensed ring with another ring.
The aromatic hydrocarbon ring represented by Q ¹ and Q ² is preferably (preferably a monocyclic or bicyclic aromatic hydrocarbon ring having 6 to 30 carbon atoms (for example, a benzene ring, a naphthalene ring, etc.). More preferably, it is an aromatic hydrocarbon ring having 6 to 20 carbon atoms, more preferably an aromatic hydrocarbon ring having 6 to 12 carbon atoms.) More preferably, it is a benzene ring.
The aromatic heterocycle represented by Q ¹ and Q ² is preferably an aromatic heterocycle containing at least one of an oxygen atom, a nitrogen atom or a sulfur atom. Specific examples of the heterocyclic ring include, for example, furan, pyrrole, thiophene, imidazole, pyrazole, pyridine, pyrazine, pyridazine, triazole, triazine, indole, indazole, purine, thiazoline, thiazole, thiadiazole, oxazoline, oxazole, oxadiazole, Examples include quinoline, isoquinoline, phthalazine, naphthyridine, quinoxaline, quinazoline, cinnoline, pteridine, acridine, phenanthroline, phenazine, tetrazole, benzimidazole, benzoxazole, benzothiazole, benzotriazole, and tetrazaindene. Preferred examples of the aromatic heterocycle include pyridine, triazine, and quinoline.
The aromatic ring represented by Q ¹ and Q ² is preferably an aromatic hydrocarbon ring, more preferably an aromatic hydrocarbon ring having 6 to 10 carbon atoms, still more preferably a substituted or unsubstituted benzene ring. is there.
Q ¹ and Q ² may further have a substituent, and the substituent T described later is preferable, but the substituent does not contain a carboxylic acid, a sulfonic acid, or a quaternary ammonium salt. Further, if possible, substituents may be linked to form a ring structure.

  X represents NR (R represents a hydrogen atom or a substituent. Substituent T described later can be applied as the substituent), an oxygen atom or a sulfur atom, and X is preferably NR (R is preferably an acyl group) , A sulfonyl group, and these substituents may be further substituted.) Or O, particularly preferably O.

  Examples of the substituent T include an alkyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, and particularly preferably 1 to 8 carbon atoms, such as a methyl group, an ethyl group, an isopropyl group, and tert-butyl. Group, n-octyl group, n-decyl group, n-hexadecyl group, cyclopropyl group, cyclopentyl group, cyclohexyl group, etc.), alkenyl group (preferably having 2 to 20 carbon atoms, more preferably 2 carbon atoms). To 12, particularly preferably 2 to 8 carbon atoms, such as vinyl group, allyl group, 2-butenyl group, and 3-pentenyl group), alkynyl group (preferably 2 to 20 carbon atoms, more preferably Has 2 to 12 carbon atoms, particularly preferably 2 to 8 carbon atoms, and examples thereof include a propargyl group and a 3-pentynyl group.), Aryl (Preferably having 6 to 30 carbon atoms, more preferably 6 to 20 carbon atoms, and particularly preferably 6 to 12 carbon atoms, and examples thereof include a phenyl group, a p-methylphenyl group, and a naphthyl group). An unsubstituted amino group (preferably having 0 to 20 carbon atoms, more preferably 0 to 10 carbon atoms, and particularly preferably 0 to 6 carbon atoms; for example, an amino group, a methylamino group, a dimethylamino group, a diethylamino group, a diamino group; Benzylamino group, etc.), alkoxy groups (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, particularly preferably 1 to 8 carbon atoms, such as methoxy group, ethoxy group, butoxy group. An aryloxy group (preferably having 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, and particularly preferably 6 to 12 carbon atoms). , For example, phenyloxy, 2-naphthyloxy, etc.), acyl groups (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, for example, acetyl group , Benzoyl group, formyl group, pivaloyl group, etc.), alkoxycarbonyl group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, for example, methoxy A carbonyl group, an ethoxycarbonyl group, etc.), an aryloxycarbonyl group (preferably having a carbon number of 7 to 20, more preferably a carbon number of 7 to 16, particularly preferably a carbon number of 7 to 10, for example, phenyloxycarbonyl Group), an acyloxy group (preferably having 2 to 20 carbon atoms, more preferably carbon number). It has 2 to 16, particularly preferably 2 to 10 carbon atoms, and examples thereof include an acetoxy group and a benzoyloxy group. ), An acylamino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 10 carbon atoms, and examples thereof include an acetylamino group and a benzoylamino group), alkoxycarbonyl. An amino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, such as a methoxycarbonylamino group), an aryloxycarbonylamino group (preferably Has 7 to 20 carbon atoms, more preferably 7 to 16 carbon atoms, particularly preferably 7 to 12 carbon atoms, such as a phenyloxycarbonylamino group, and a sulfonylamino group (preferably 1 to 1 carbon atom). 20, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms. Nylamino group, benzenesulfonylamino group, etc.), sulfamoyl group (preferably having 0 to 20 carbon atoms, more preferably 0 to 16 carbon atoms, particularly preferably 0 to 12 carbon atoms, such as sulfamoyl group, methyl A sulfamoyl group, a dimethylsulfamoyl group, a phenylsulfamoyl group, etc.), a carbamoyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably 1 to carbon atoms). 12 and examples thereof include a carbamoyl group, a methylcarbamoyl group, a diethylcarbamoyl group, a phenylcarbamoyl group, etc.), an alkylthio group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably carbon atoms). Examples thereof include methylthio group and ethylthio group. ), An arylthio group (preferably having 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, particularly preferably 6 to 12 carbon atoms, such as a phenylthio group), a sulfonyl group (preferably C1-C20, More preferably, it is C1-C16, Most preferably, it is C1-C12, For example, a mesyl group, a tosyl group, etc. are mentioned), a sulfinyl group (preferably C1-C20, More preferably, it is C1-C16, Most preferably, it is C1-C12, for example, a methanesulfinyl group, a benzenesulfinyl group, etc.), a ureido group (preferably C1-C20, more preferably carbon) The number is 1 to 16, particularly preferably 1 to 12, and examples thereof include a ureido group, a methylureido group, and a phenylureido group. ), A phosphoric acid amide group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably 1 to 12 carbon atoms, such as a diethylphosphoric acid amide group and a phenylphosphoric acid amide group. Hydroxy group, mercapto group, halogen atom (eg fluorine atom, chlorine atom, bromine atom, iodine atom), cyano group, sulfo group, carboxyl group, nitro group, hydroxamic acid group, sulfino group, hydrazino group, imino group Group, heterocyclic group (preferably having 1 to 30 carbon atoms, more preferably 1 to 12 carbon atoms, and examples of the hetero atom include a nitrogen atom, an oxygen atom, and a sulfur atom, specifically, for example, an imidazolyl group, a pyridyl group, and a quinolyl group. Group, furyl group, piperidyl group, morpholino group, benzoxazolyl group, benzimidazolyl group, benzthiazolyl group, etc. ), A silyl group (preferably having 3 to 40 carbon atoms, more preferably 3 to 30 carbon atoms, particularly preferably 3 to 24 carbon atoms, and examples thereof include a trimethylsilyl group and a triphenylsilyl group. For example). These substituents may be further substituted. Moreover, when there are two or more substituents, they may be the same or different. If possible, they may be linked together to form a ring.

As the general formula (102), a compound represented by the following general formula (102-A) is preferable.
Formula (102-A)

(In the formula, R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁸ , and R ⁹ each independently represents a hydrogen atom or a substituent.)

R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁸ , and R ⁹ each independently represent a hydrogen atom or a substituent, and the above-mentioned substituent T is applied as the substituent. it can. These substituents may be further substituted with another substituent, and the substituents may be condensed to form a ring structure.

R ¹ , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁸ and R ⁹ are preferably a hydrogen atom, alkyl group, alkenyl group, alkynyl group, aryl group, substituted or unsubstituted amino group, alkoxy group, aryl An oxy group, a hydroxy group and a halogen atom, more preferably a hydrogen atom, an alkyl group, an aryl group, an alkyloxy group, an aryloxy group and a halogen atom, still more preferably a hydrogen atom and a carbon 1-12 alkyl group. Particularly preferred are a hydrogen atom and a methyl group, and most preferred is a hydrogen atom.

R ² is preferably a hydrogen atom, an alkyl group, an alkenyl group, an alkynyl group, an aryl group, a substituted or unsubstituted amino group, an alkoxy group, an aryloxy group, a hydroxy group, a halogen atom, more preferably a hydrogen atom or one carbon atom. An alkyl group having -20 carbon atoms, an amino group having 0-20 carbon atoms, an alkoxy group having 1-12 carbon atoms, an aryloxy group having 6-12 carbon atoms, and a hydroxy group, more preferably an alkoxy group having 1-20 carbon atoms. And particularly preferably an alkoxy group having 1 to 12 carbon atoms.

R ⁷ is preferably a hydrogen atom, an alkyl group, an alkenyl group, an alkynyl group, an aryl group, a substituted or unsubstituted amino group, an alkoxy group, an aryloxy group, a hydroxy group, a halogen atom, more preferably a hydrogen atom or a carbon number of 1 An alkyl group having -20 carbon atoms, an amino group having 0-20 carbon atoms, an alkoxy group having 1-12 carbon atoms, an aryloxy group having 6-12 carbon atoms, and a hydroxy group, more preferably a hydrogen atom, having 1-20 carbon atoms. An alkyl group (preferably having 1 to 12 carbon atoms, more preferably 1 to 8 carbon atoms, still more preferably a methyl group), particularly preferably a methyl group or a hydrogen atom.

More preferable as the general formula (102) is a compound represented by the following general formula (102-B).
General formula (102-B)

(Wherein R ¹⁰ represents a hydrogen atom, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted alkynyl group, or a substituted or unsubstituted aryl group.)

R ¹⁰ represents a hydrogen atom, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted alkynyl group, or a substituted or unsubstituted aryl group. Applicable.
R ¹⁰ is preferably a substituted or unsubstituted alkyl group, more preferably a substituted or unsubstituted alkyl group having 5 to 20 carbon atoms, and further preferably a substituted or unsubstituted alkyl group having 5 to 12 carbon atoms. (Including n-hexyl group, 2-ethylhexyl group, n-octyl group, n-decyl group, n-dodecyl group, benzyl group, etc.), particularly preferably a substitution of 6 to 12 carbon atoms or An unsubstituted alkyl group (2-ethylhexyl group, n-octyl group, n-decyl group, n-dodecyl group, benzyl group).

The compound represented by the general formula (102) can be synthesized by a known method described in JP-A-11-12219.
Specific examples of the compound represented by the general formula (102) are given below, but the present invention is not limited to the following specific examples.

As the compound containing a cyano group, which is one of the wavelength dispersion adjusting agents used in the present invention, those represented by the general formula (103) are preferably used.
General formula (103)

(In the formula, Q ¹ and Q ² each independently represent an aromatic ring. X ¹ and X ² represent a hydrogen atom or a substituent, and at least one of them represents a cyano group, a carbonyl group, a sulfonyl group, an aromatic group. Represents an aromatic ring.) The aromatic ring represented by Q ¹ and Q ² may be an aromatic hydrocarbon ring or an aromatic heterocyclic ring. These may be monocyclic or may form a condensed ring with another ring.

  The aromatic hydrocarbon ring is preferably (preferably a monocyclic or bicyclic aromatic hydrocarbon ring having 6 to 30 carbon atoms (for example, benzene ring, naphthalene ring etc.), more preferably 6 carbon atoms. -20 aromatic hydrocarbon ring, more preferably an aromatic hydrocarbon ring having 6 to 12 carbon atoms.) More preferred is a benzene ring.

  The aromatic heterocycle is preferably an aromatic heterocycle containing a nitrogen atom or a sulfur atom. Specific examples of the heterocyclic ring include, for example, thiophene, imidazole, pyrazole, pyridine, pyrazine, pyridazine, triazole, triazine, indole, indazole, purine, thiazoline, thiazole, thiadiazole, oxazoline, oxazole, oxadiazole, quinoline, isoquinoline, Examples include phthalazine, naphthyridine, quinoxaline, quinazoline, cinnoline, pteridine, acridine, phenanthroline, phenazine, tetrazole, benzimidazole, benzoxazole, benzthiazole, benzotriazole, and tetrazaindene. Preferred examples of the aromatic heterocycle include pyridine, triazine, and quinoline.

The aromatic ring represented by Q ¹ and Q ² is preferably an aromatic hydrocarbon ring, and more preferably a benzene ring.
Q ¹ and Q ² may further have a substituent, and a substituent T described later is preferable. Examples of the substituent T include an alkyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, and particularly preferably 1 to 8 carbon atoms, such as a methyl group, an ethyl group, an isopropyl group, and tert-butyl. Group, n-octyl group, n-decyl group, n-hexadecyl group, cyclopropyl group, cyclopentyl group, cyclohexyl group, etc.), alkenyl group (preferably having 2 to 20 carbon atoms, more preferably 2 carbon atoms). To 12, particularly preferably 2 to 8 carbon atoms, such as vinyl group, allyl group, 2-butenyl group, and 3-pentenyl group), alkynyl group (preferably 2 to 20 carbon atoms, more preferably Has 2 to 12 carbon atoms, particularly preferably 2 to 8 carbon atoms, and examples thereof include a propargyl group and a 3-pentynyl group.), Aryl (Preferably having 6 to 30 carbon atoms, more preferably 6 to 20 carbon atoms, and particularly preferably 6 to 12 carbon atoms, and examples thereof include a phenyl group, a p-methylphenyl group, and a naphthyl group). An unsubstituted amino group (preferably having 0 to 20 carbon atoms, more preferably 0 to 10 carbon atoms, and particularly preferably 0 to 6 carbon atoms; for example, an amino group, a methylamino group, a dimethylamino group, a diethylamino group, a diamino group; Benzylamino group, etc.), alkoxy groups (preferably having 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms, particularly preferably 1 to 8 carbon atoms, such as methoxy group, ethoxy group, butoxy group. An aryloxy group (preferably having 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, and particularly preferably 6 to 12 carbon atoms). , For example, phenyloxy group, 2-naphthyloxy group, etc.), acyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms, Acetyl group, benzoyl group, formyl group, pivaloyl group, etc.), alkoxycarbonyl group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, For example, a methoxycarbonyl group, an ethoxycarbonyl group, etc.), an aryloxycarbonyl group (preferably having a carbon number of 7 to 20, more preferably a carbon number of 7 to 16, particularly preferably a carbon number of 7 to 10, such as phenyl An oxycarbonyl group, etc.), an acyloxy group (preferably having 2 to 20 carbon atoms, more preferably carbon It has 2 to 16 primes, particularly preferably 2 to 10 carbons, and examples thereof include an acetoxy group and a benzoyloxy group. ), An acylamino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 10 carbon atoms, and examples thereof include an acetylamino group and a benzoylamino group), alkoxycarbonyl. An amino group (preferably having 2 to 20 carbon atoms, more preferably 2 to 16 carbon atoms, particularly preferably 2 to 12 carbon atoms, such as a methoxycarbonylamino group), an aryloxycarbonylamino group (preferably Has 7 to 20 carbon atoms, more preferably 7 to 16 carbon atoms, particularly preferably 7 to 12 carbon atoms, such as a phenyloxycarbonylamino group, and a sulfonylamino group (preferably 1 to 1 carbon atom). 20, more preferably 1 to 16 carbon atoms, particularly preferably 1 to 12 carbon atoms. Nylamino group, benzenesulfonylamino group, etc.), sulfamoyl group (preferably having 0 to 20 carbon atoms, more preferably 0 to 16 carbon atoms, particularly preferably 0 to 12 carbon atoms, such as sulfamoyl group, methyl A sulfamoyl group, a dimethylsulfamoyl group, a phenylsulfamoyl group, etc.), a carbamoyl group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably 1 to carbon atoms). For example, carbamoyl group, methylcarbamoyl group, diethylcarbamoyl group, phenylcarbamoyl group, etc.), alkylthio group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, particularly preferably carbon). Examples thereof include methylthio group and ethylthio group. ), An arylthio group (preferably having 6 to 20 carbon atoms, more preferably 6 to 16 carbon atoms, particularly preferably 6 to 12 carbon atoms, such as a phenylthio group), a sulfonyl group (preferably C1-C20, More preferably, it is C1-C16, Most preferably, it is C1-C12, For example, a mesyl group, a tosyl group, etc. are mentioned), a sulfinyl group (preferably C1-C20, More preferably, it is C1-C16, Most preferably, it is C1-C12, for example, a methanesulfinyl group, a benzenesulfinyl group, etc.), a ureido group (preferably C1-C20, more preferably carbon) The number is 1 to 16, particularly preferably 1 to 12, and examples thereof include a ureido group, a methylureido group, and a phenylureido group. ), A phosphoric acid amide group (preferably having 1 to 20 carbon atoms, more preferably 1 to 16 carbon atoms, and particularly preferably 1 to 12 carbon atoms, such as a diethylphosphoric acid amide group and a phenylphosphoric acid amide group. Hydroxy group, mercapto group, halogen atom (eg fluorine atom, chlorine atom, bromine atom, iodine atom), cyano group, sulfo group, carboxyl group, nitro group, hydroxamic acid group, sulfino group, hydrazino group, imino group Group, heterocyclic group (preferably having 1 to 30 carbon atoms, more preferably 1 to 12 carbon atoms, for example, nitrogen atom, oxygen atom, sulfur atom, specifically imidazolyl group, pyridyl group, quinolyl, etc. Group, furyl group, piperidyl group, morpholino group, benzoxazolyl group, benzimidazolyl group, benzthiazolyl group, etc. ), A silyl group (preferably having 3 to 40 carbon atoms, more preferably 3 to 30 carbon atoms, particularly preferably 3 to 24 carbon atoms, and examples thereof include a trimethylsilyl group and a triphenylsilyl group. For example). These substituents may be further substituted. Moreover, when there are two or more substituents, they may be the same or different. If possible, they may be linked together to form a ring.

X ¹ and X ² each represent a hydrogen atom or a substituent, and at least one of them represents a cyano group, a carbonyl group, a sulfonyl group, or an aromatic heterocycle. The substituent T described above can be applied to the substituents represented by X ¹ and X ² . In addition, the substituent represented by X ¹ and X ² may be further substituted with another substituent, and X ¹ and X ² may be condensed to form a ring structure.

X ¹ and X ² are preferably a hydrogen atom, an alkyl group, an aryl group, a cyano group, a nitro group, a carbonyl group, a sulfonyl group, or an aromatic heterocycle, and more preferably a cyano group, a carbonyl group, a sulfonyl group, An aromatic heterocycle, more preferably a cyano group or a carbonyl group, and particularly preferably a cyano group or an alkoxycarbonyl group (—C (═O) OR (R is an alkyl group having 1 to 20 carbon atoms, 6 carbon atoms). ˜12 aryl groups and combinations thereof.

As the general formula (103), a compound represented by the following general formula (103-A) is preferable.
General formula (103-A)

(Wherein R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁸ , R ⁹ and R ¹⁰ each independently represents a hydrogen atom or a substituent. X ¹ and X ² Are the same as those in formula (103), and the preferred range is also the same.)

R ¹ , R ² , R ³ , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁸ , R ⁹ and R ¹⁰ each independently represents a hydrogen atom or a substituent. Is applicable. These substituents may be further substituted with another substituent, and the substituents may be condensed to form a ring structure.

R ¹ , R ² , R ⁴ , R ⁵ , R ⁶ , R ⁷ , R ⁹ , and R ¹⁰ are preferably a hydrogen atom, an alkyl group, an alkenyl group, an alkynyl group, an aryl group, a substituted or unsubstituted amino group, An alkoxy group, an aryloxy group, a hydroxy group, and a halogen atom, more preferably a hydrogen atom, an alkyl group, an aryl group, an alkyloxy group, an aryloxy group, and a halogen atom, still more preferably a hydrogen atom and carbon 1-12. An alkyl group, particularly preferably a hydrogen atom or a methyl group, and most preferably a hydrogen atom.

R ³ and R ⁸ are preferably hydrogen atoms, alkyl groups, alkenyl groups, alkynyl groups, aryl groups, substituted or unsubstituted amino groups, alkoxy groups, aryloxy groups, hydroxy groups, halogen atoms, more preferably hydrogen atoms. , An alkyl group having 1 to 20 carbon atoms, an amino group having 0 to 20 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 6 to 12 carbon atoms, and a hydroxy group, and more preferably a hydrogen atom and a carbon number An alkyl group having 1 to 12 carbon atoms and an alkoxy group having 1 to 12 carbon atoms, particularly preferably a hydrogen atom.

More preferable as the general formula (103) is a compound represented by the following general formula (103-B).
General formula (103-B)

(Wherein R ³ and R ⁸ have the same meanings as those in formula (103-A), and preferred ranges are also the same. X ³ represents a hydrogen atom or a substituent.)

X ³ represents a hydrogen atom or a substituent. As the substituent, the above-described substituent T can be applied, and if possible, the substituent may be further substituted with another substituent. X ³ is preferably a hydrogen atom, an alkyl group, an aryl group, a cyano group, a nitro group, a carbonyl group, a sulfonyl group or an aromatic heterocyclic ring, more preferably a cyano group, a carbonyl group, a sulfonyl group or an aromatic heterocyclic ring. More preferably a cyano group or a carbonyl group, and particularly preferably a cyano group or an alkoxycarbonyl group (—C (═O) OR (R is an alkyl group having 1 to 20 carbon atoms, an aryl having 6 to 12 carbon atoms). Group and a combination thereof).

More preferred as the general formula (103) is a compound represented by the general formula (103-C).
General formula (103-C)

(Wherein R ³ and R ⁸ have the same meanings as those in formula (103-A), and the preferred ranges are also the same. R ²¹ represents an alkyl group having 1 to 20 carbon atoms.)

R ²¹ is preferably an alkyl group having 2 to 12 carbon atoms, more preferably an alkyl group having 4 to 12 carbon atoms, even more preferably 6 carbon atoms when both R ³ and R ⁸ are hydrogen. To 12 alkyl groups, particularly preferably an n-octyl group, a tert-octyl group, a 2-ethylhexyl group, an n-decyl group, and an n-dodecyl group, most preferably a 2-ethylhexyl group. It is.

When R ³ and R ⁸ are preferably other than hydrogen as R ²¹ , the compound represented by the general formula (103-C) has a molecular weight of 300 or more and an alkyl group having 20 or less carbon atoms. preferable.

  The compound represented by the general formula (103) can be synthesized by the method described in Journal of American Chemical Society 63, 3452 (1941).

  Specific examples of the compound represented by the general formula (103) are given below, but the present invention is not limited to the following specific examples.

Next, the cellulose acylate used in the present invention will be described in detail. In the present invention, two or more different cellulose acylates may be mixed and used. The specific cellulose acylate is a fatty acid ester of cellulose obtained by substituting a hydroxyl group of cellulose with an acetyl group and an acyl group having 3 or more carbon atoms, and preferably the degree of substitution of the cellulose with a hydroxyl group is represented by the following formula: Satisfies (I).
Formula (I): 2.0 ≦ A + B ≦ 3.0
Here, in the formula, A and B represent the substitution degree of the acyl group substituted with the hydroxyl group of cellulose, A is the substitution degree of the acetyl group, and B is the substitution degree of the acyl group having 3 or more carbon atoms.

Glucose units having β-1,4 bonds constituting cellulose have free hydroxyl groups at the 2nd, 3rd and 6th positions. Cellulose acylate is a polymer obtained by esterifying some or all of these hydroxyl groups with acyl groups. The degree of acyl substitution means the proportion of cellulose esterified at each of the 2-position, 3-position and 6-position (100% esterification has a substitution degree of 1).
When the substitution degree of the 2-position hydroxyl group of the cellulose acylate film with an acyl group is DS2, the substitution degree of the 3-position hydroxyl group with an acyl group is DS3, and the substitution degree of the 6-position hydroxyl group with an acyl group is DS6. The following mathematical formulas (VI-a) and (VI-b) are preferably satisfied together with the mathematical formula (VI) relating to the thermal expansion coefficient described later.
Formula (VI-a): 2.0 ≦ DS2 + DS3 + DS6 ≦ 3.0
Formula (VI-b): DS6 / (DS2 + DS3 + DS6) ≧ 0.315

In the present invention, the total substitution degree (A + B) of hydroxyl groups A and B is preferably 2.0 to 3.0, more preferably 2.2 to 2, as shown in the above formula (I). 0.9, and particularly preferably 2.40 to 2.85. Further, the substitution degree of B may be zero. When it is not 0, it is preferably 0.9 or more, particularly preferably 1.3 or more.
When A + B is 2.0 or more, hydrophilicity is weak and it is difficult to be affected by environmental humidity.
Cellulose acetate with B of 0 is easily affected by environmental humidity, but the influence of environmental temperature is smaller than that when the linear thermal expansion coefficient described later is not 0, and is displayed on a liquid crystal display device. Occurrence of unevenness at the time can be suppressed.
Further, B is preferably 28% or more of the substitution degree of the 6-position hydroxyl group, more preferably 30% or more is the substitution degree of the 6-position hydroxyl group, more preferably 31% or more, and particularly preferably 32% or more. The substitution degree of the 6-position hydroxyl group is preferred.
Furthermore, the total substitution degree of A and B at the 6-position hydroxyl group of cellulose acylate is preferably 0.75 or more, more preferably 0.80 or more, and particularly preferably 0.85 or more. With these cellulose acylate films, a solution for preparing a film having preferable solubility and filterability can be produced, and a good solution can be produced even in a non-chlorine organic solvent. Furthermore, it becomes possible to produce a solution having a low viscosity and good filterability.

  The acyl group having 3 or more carbon atoms may be an aliphatic group or an aromatic hydrocarbon group, and is not particularly limited. They are, for example, alkyl carbonyl esters, alkenyl carbonyl esters or aromatic carbonyl esters of cellulose, aromatic alkyl carbonyl esters and the like, each of which may further have a substituted group. As these preferable B, propionyl group, butanoyl group, keptanoyl group, hexanoyl group, octanoyl group, decanoyl group, dodecanoyl group, tridecanoyl group, tetradecanoyl group, hexadecanoyl group, octadecanoyl group, iso-butanoyl group , T-butanoyl group, cyclohexanecarbonyl group, oleoyl group, benzoyl group, naphthylcarbonyl group, cinnamoyl group and the like. Among these, a propionyl group, a butanoyl group, a dodecanoyl group, an octadecanoyl group, a t-butanoyl group, an oleoyl group, a benzoyl group, a naphthylcarbonyl group, a cinnamoyl group and the like are preferable. Particularly preferred are a propionyl group and a butanoyl group. In the case of a propionyl group, the substitution degree B is preferably 0.6 or more.

  Specific examples of cellulose acylate include cellulose acetate, cellulose acetate propionate, and cellulose acetate butyrate.

[Method of synthesizing cellulose acylate]
The basic principle of the cellulose acylate synthesis method is described in Mita et al., Wood chemistry, 180-190 (Kyoritsu Shuppan, 1968). A typical synthesis method is a liquid phase acetylation method using a carboxylic acid anhydride-acetic acid-sulfuric acid catalyst.
Specifically, cellulose raw materials such as cotton linter and wood pulp are pretreated with an appropriate amount of acetic acid, and then put into a pre-cooled carboxylic acid mixture to be esterified to complete cellulose acylate (2nd, 3rd and 6th). The total degree of acyl substitution at the position is approximately 3.00). The carboxylated mixed solution generally contains acetic acid as a solvent, carboxylic anhydride as an esterifying agent, and sulfuric acid as a catalyst. The carboxylic anhydride is usually used in a stoichiometric excess over the sum of the cellulose that reacts with it and the water present in the system. After completion of the esterification reaction, a neutralizing agent (for example, calcium, magnesium, iron, aluminum or zinc) is used for hydrolysis of excess carboxylic anhydride remaining in the system and neutralization of a part of the esterification catalyst. Of carbonate, acetate or oxide). Next, the obtained complete cellulose acylate is saponified and aged by maintaining it at 50 to 90 ° C. in the presence of a small amount of an acetylation reaction catalyst (generally, remaining sulfuric acid) to obtain the desired degree of acyl substitution and polymerization. The cellulose acylate having a degree is changed. When the desired cellulose acylate is obtained, the catalyst remaining in the system is completely neutralized with the neutralizing agent as described above, or in water or dilute sulfuric acid without neutralization. The cellulose acylate solution is added (or water or dilute sulfuric acid is added to the cellulose acylate solution), the cellulose acylate is separated, washed and stabilized, and the like. Can be obtained.

In the cellulose acylate film, the polymer component constituting the film is preferably substantially composed of the specific cellulose acylate. “Substantially” means 55% by mass or more (preferably 70% by mass or more, more preferably 80% by mass or more) of the polymer component.
Cellulose acylate is preferably used in the form of particles. 90% by mass or more of the particles to be used preferably have a particle diameter of 0.5 to 5 mm. Moreover, it is preferable that 50 mass% or more of the particle | grains to be used have a particle diameter of 1-4 mm. The cellulose acylate particles preferably have a shape as close to a sphere as possible.
The degree of polymerization of cellulose acylate preferably used in the present invention is a viscosity average degree of polymerization, preferably 200 to 700, more preferably 250 to 550, still more preferably 250 to 400, and particularly preferably 250 to 350. . The average degree of polymerization can be measured by Uda et al.'S intrinsic viscosity method (Kazuo Uda, Hideo Saito, Journal of Textile Society, Vol. Further details are described in JP-A-9-95538.

When the low molecular component is removed, the average molecular weight (polymerization degree) is increased, but the viscosity is lower than that of ordinary cellulose acylate. Therefore, the cellulose acylate from which the low molecular component is removed is useful. . Cellulose acylate having a small amount of low molecular components can be obtained by removing low molecular components from cellulose acylate synthesized by a usual method. The removal of the low molecular component can be carried out by washing the cellulose acylate with an appropriate organic solvent. In addition, when manufacturing a cellulose acylate with few low molecular components, it is preferable to adjust the sulfuric acid catalyst amount in an acetylation reaction to 0.5-25 mass parts with respect to 100 mass parts of cellulose acylates. When the amount of the sulfuric acid catalyst is in the above range, cellulose acylate that is preferable in terms of molecular weight distribution (uniform molecular weight distribution) can be synthesized. When used in the production of cellulose acylate, the water content is preferably 2% by mass or less, more preferably 1% by mass or less, and particularly 0.7% by mass or less. In general, cellulose acylate contains water and generally has a water content of 2.5 to 5% by mass. In order to obtain this moisture content, drying is preferable, and the method is not particularly limited as long as the desired moisture content is achieved.
The raw material cotton of cellulose acylate and the synthesis method thereof are disclosed in JIII Journal of Technical Disclosure No. 2001-1745 (issued March 15, 2001, Invention Association) p. Raw material cotton and synthesis methods described in detail in 7-12 can be employed.

  In the present invention, a cellulose acylate film can be obtained by forming a film using a solution obtained by dissolving the cellulose acylate and, if necessary, an additive in an organic solvent.

[Additive]
In the present invention, examples of the additive that can be used for the cellulose acylate include a plasticizer, an ultraviolet absorber, a deterioration inhibitor, a retardation (optical anisotropy) developing agent, fine particles, a peeling accelerator, and an infrared ray. An absorbent etc. can be mentioned. In this invention, it is preferable to use 1 or more types of a plasticizer, a ultraviolet absorber, and a peeling accelerator. They may be solid or oily. That is, the melting point and boiling point are not particularly limited. For example, a UV absorber having a melting point of 20 ° C. or lower and a temperature of 20 ° C. or higher can be used as a mixture, or a plasticizer can be used in the same manner. For example, those described in JP-A-2001-151901 Can be used.

  As the ultraviolet absorber, any type can be selected according to the purpose, and a salicylic acid ester type, benzophenone type, benzotriazole type, benzoate type, cyanoacrylate type, nickel complex type ultraviolet absorber or the like should be used. Preferred are benzophenone, benzotriazole, and salicylic acid ester UV absorbers. Examples of benzophenone ultraviolet absorbers include 2,4-dihydroxybenzophenone, 2-hydroxy-4-acetoxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2,2′-di-hydroxy-4-methoxybenzophenone, 2, 2′-di-hydroxy-4,4′-methoxybenzophenone, 2-hydroxy-4-n-octoxybenzophenone, 2-hydroxy-4-dodecyloxybenzophenone, 2-hydroxy-4- (2-hydroxy-3- And methacryloxy) propoxybenzophenone. As a benzotriazole ultraviolet absorber, 2 (2′-hydroxy-3′-tert-butyl-5′-methylphenyl) -5-chlorobenzotriazole, 2 (2′-hydroxy-5′-tert-butylphenyl) ) Benzotriazole, 2 (2′-hydroxy-3 ′, 5′-di-tert-amylphenyl) benzotriazole, 2 (2′-hydroxy-3 ′, 5′-di-tert-butylphenyl) -5 Examples include chlorobenzotriazole, 2 (2′-hydroxy-5′-tert-octylphenyl) benzotriazole, and the like. Examples of the salicylic acid ester ultraviolet absorber include phenyl salicylate, p-octylphenyl salicylate, p-tert-butylphenyl salicylate, and the like. Among these exemplified UV absorbers, 2-hydroxy-4-methoxybenzophenone, 2,2′-di-hydroxy-4,4′-methoxybenzophenone, 2 (2′-hydroxy-3′-tert-butyl-5) '-Methylphenyl) -5-chlorobenzotriazole, 2 (2'-hydroxy-5'-tert-butylphenyl) benzotriazole, 2 (2'-hydroxy-3', 5'-di-tert-amylphenyl) Benzotriazole, 2 (2′-hydroxy-3 ′, 5′-di-tert-butylphenyl) -5-chlorobenzotriazole is particularly preferred.

  As the ultraviolet absorber, it is preferable to use a combination of a plurality of absorbers having different absorption wavelengths because a high blocking effect can be obtained in a wide wavelength range. From the viewpoint of preventing deterioration of the liquid crystal, the ultraviolet absorbent for liquid crystal is preferably excellent in the ability to absorb ultraviolet light having a wavelength of 370 nm or less, and has little absorption of visible light having a wavelength of 400 nm or more from the viewpoint of liquid crystal display. Particularly preferred ultraviolet absorbers are the benzotriazole compounds, benzophenone compounds, and salicylic acid ester compounds mentioned above. Among these, a benzotriazole-based compound is preferable because unnecessary coloring with respect to the cellulose ester is small.

  As for the UV absorber, JP-A-60-235852, JP-A-3-199201, JP-A-51907073, JP-A-5-194789, JP-A-5-271471, JP-A-6-107854, JP-A-6-107854. 118233, 6-148430, 7-11056, 7-11055, 7-11056, 8-29619, 8-239509, JP-A-2000-204173 These compounds can also be used.

  The addition amount of the ultraviolet absorber is preferably 0.001 to 5% by mass, preferably 0.01 to 1% by mass with respect to the cellulose acylate from the viewpoint of the addition effect and suppression of bleeding out of the ultraviolet absorber to the film surface. Is more preferable.

  Further, the ultraviolet absorber may be added simultaneously with the dissolution of cellulose acylate, or may be added to the dope after dissolution. In particular, a mode in which an ultraviolet absorbent solution is added to the dope immediately before casting using a static mixer or the like is preferable because the spectral absorption characteristics can be easily adjusted.

  The deterioration inhibitor can prevent deterioration and decomposition of cellulose triacetate and the like. Examples of the deterioration preventing agent include butylamine, hindered amine compounds (JP-A-8-325537), guanidine compounds (JP-A-5-271471), benzotriazole-based UV absorbers (JP-A-6-235819), and benzophenone-based compounds. A compound such as a UV absorber (JP-A-6-118233) can be used.

  As a plasticizer, it is preferable to use phosphate ester and carboxylic acid ester. Specific examples of the plasticizer include triphenyl phosphate (TPP), tricresyl phosphate (TCP), cresyl diphenyl phosphate, octyl diphenyl phosphate, diphenyl biphenyl phosphate, trioctyl phosphate, tributyl phosphate, dimethyl phthalate (DMP), Diethyl phthalate (DEP), dibutyl phthalate (DBP), dioctyl phthalate (DOP), diphenyl phthalate (DPP), diethyl hexyl phthalate (DEHP), triethyl O-acetylcitrate (OACTE), tributyl O-acetylcitrate (OACTB) , Acetyl triethyl citrate, acetyl tributyl citrate, butyl oleate, methyl acetyl ricinoleate, dibutyl sebacate, triacetin Tributyrin, butyl phthalyl butyl glycolate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, butyl phthalyl butyl glycolate may be preferably mentioned. Further, preferred plasticizers include (di) pentaerythritol esters, glycerol esters, and diglycerol esters.

  Examples of the peeling accelerator include citric acid ethyl esters. Moreover, as an infrared absorber, the infrared absorber described in Unexamined-Japanese-Patent No. 2001-194522 can be used, for example.

  The timing for adding these additives may be added at any stage in the dope preparation process, but may be performed by adding a process for adding additives as the final preparation process in the dope preparation process. Furthermore, the amount of each material added is not particularly limited as long as the function is manifested. Moreover, when a cellulose acylate film is a multilayer, the kind and addition amount of the additive of each layer may differ. For example, it is described in Japanese Patent Application Laid-Open No. 2001-151902, and these are conventionally known techniques.

The linear thermal expansion coefficient of the cellulose acylate film obtained by the production method of the present invention is the linear thermal expansion coefficient D (MD) in the casting (conveying) direction and the linear thermal expansion in the casting width direction (casting vertical direction). It is preferable that the rate D (TD) satisfies the following formulas (II), (III), and (IV), and further satisfies the formulas (V) and (VI).
Formula (II): 30 ppm ≦ D (MD) ≦ 90 ppm
Formula (III): 25 ppm ≦ D (TD) ≦ 90 ppm
Formula (IV): 1.0 ≦ D (MD) / D (TD) ≦ 5.0
Formula (V): 50 ppm ≦ D (MD) ≦ 75 ppm, 30 ppm ≦ D (TD) ≦ 75p
pm
Formula (VI): 1.0 ≦ D (MD) / D (TD) ≦ 3.0
The linear thermal expansion coefficient of the cellulose acylate film can satisfy the above mathematical formula depending on the draw ratio, the type and amount of the plasticizer, and the selection of cotton.
The linear thermal expansion coefficient D (MD) in the casting (conveying) direction and the linear thermal expansion coefficient D (TD) in the casting width direction (vertical casting direction) satisfy the above formulas (II) to (VI). The technical significance of is as follows. When there is a change in the environment (temperature), the polarizing plate constituent parts composed of an adhesive layer, a retardation film, a polarizing film, a protective film, etc. cause contraction and expansion, and stress is generated between the respective parts. By satisfying the above formula, this stress is well balanced in the constituent parts of the polarizing plate, and even if there is a change in environmental temperature, the polarizing plate becomes a liquid crystal display device with little change in viewing angle characteristics, and preferable results are obtained.

  The glass transition point Tg of the cellulose acylate film is preferably 70 to 180 ° C, more preferably 100 to 170 ° C, and more preferably 120 ° C to 160 ° C. The glass transition point Tg can be measured with a dynamic viscoelasticity measuring device (Vibron: DVA-225 (ITG Measurement Control Co., Ltd.)). The glass transition point can also be adjusted to the above range by appropriately selecting the type and amount of plasticizer. The cellulose acylate film used in the present invention preferably has a glass transition point Tg in the above range from the viewpoint of process suitability for polarizing plate processing and liquid crystal display device assembly.

  Furthermore, regarding the additive, the Japan Society of Invention and Innovation Technical Bulletin No. 2001-1745 (issued March 15, 2001, Japan Society of Invention) p. Those described in detail after 16 can be used as appropriate.

[Matting agent fine particles]
It is preferable to add fine particles as a matting agent to the cellulose acylate film obtained by the production method of the present invention. The fine particles used in the present invention include silicon dioxide, titanium dioxide, aluminum oxide, zirconium oxide, calcium carbonate, calcium carbonate, talc, clay, calcined kaolin, calcined calcium silicate, hydrated calcium silicate, aluminum silicate, silica Mention may be made of magnesium and calcium phosphates. Fine particles containing silicon are preferable from the viewpoint of low turbidity, and silicon dioxide is particularly preferable. The fine particles of silicon dioxide preferably have a primary average particle diameter of 20 nm or less and an apparent specific gravity of 70 g / liter or more. Those having an average primary particle size as small as 5 to 16 nm are more preferred because they can reduce the haze of the film. The apparent specific gravity is preferably 90 to 200 g / liter or more, and more preferably 100 to 200 g / liter or more. A larger apparent specific gravity is preferable because a high-concentration dispersion can be produced, and haze and aggregates are improved.
The amount of silicon dioxide fine particles used is preferably 0.01 to 0.3 parts by mass with respect to 100 parts by mass of the polymer component containing cellulose acylate.

These fine particles usually form secondary particles having an average particle diameter of 0.1 to 3.0 μm, and are present as aggregates of primary particles in the film, and 0.1 to 3.0 μm on the film surface. Unevenness can be formed. The secondary average particle size is preferably from 0.2 μm to 1.5 μm, more preferably from 0.4 μm to 1.2 μm, and most preferably from 0.6 μm to 1.1 μm. If the secondary average particle diameter is in the above range, the effect of preventing squeaking is sufficiently exhibited and the haze is small and preferable.
The primary and secondary particle diameters are determined by observing the particles in the film with a scanning electron microscope and using the diameter of a circle circumscribing the particles as the particle diameter. Also, 200 particles are observed at different locations, and the average value is taken as the average particle diameter.

  As fine particles of silicon dioxide, for example, commercially available products such as Aerosil R972, R972V, R974, R812, 200, 200V, 300, R202, OX50, TT600 (above Nippon Aerosil Co., Ltd.) can be used. Zirconium oxide fine particles are commercially available, for example, under the trade names Aerosil R976 and R811 (manufactured by Nippon Aerosil Co., Ltd.), and can be used.

  Among these, Aerosil 200V and Aerosil R972V are fine particles of silicon dioxide having a primary average particle diameter of 20 nm or less and an apparent specific gravity of 70 g / liter or more, and the coefficient of friction is maintained while keeping the turbidity of the optical film low. It is particularly preferable because it has a great effect of reducing the effect.

In order to obtain a cellulose acylate film having particles having a small secondary average particle size in the present invention, several methods are conceivable when preparing a fine particle dispersion. For example, a method of preparing a fine particle dispersion in which a solvent and fine particles are mixed with stirring in advance, adding this fine particle dispersion to a small amount of cellulose acylate solution separately prepared, stirring and dissolving, and further mixing with the main cellulose acylate dope solution There is. This method is a preferable preparation method in that the dispersibility of the silicon dioxide fine particles is good and the silicon dioxide fine particles are more difficult to reaggregate. In addition, after adding a small amount of cellulose ester to the solvent and dissolving with stirring, add the fine particles to this and disperse with a disperser to make this fine particle additive solution, and mix this fine particle additive solution with the dope solution using an inline mixer There is also a way to do it. The present invention is not limited to these methods, but the concentration of silicon dioxide when the silicon dioxide fine particles are mixed and dispersed with a solvent or the like is preferably 5 to 30% by mass, more preferably 10 to 25% by mass, and 15 to 20%. Mass% is most preferred. A higher dispersion concentration is preferable because the liquid turbidity with respect to the added amount is lowered, and haze and aggregates are improved. The addition amount of the matting agent in the final cellulose acylate dope solution is preferably 0.01 to 1.0 g, more preferably 0.03 to 0.3 g, and 0.08 to 0.16 g per 1 m ^2. Most preferred.

  The solvent used is preferably lower alcohols such as methyl alcohol, ethyl alcohol, propyl alcohol, isopropyl alcohol, butyl alcohol and the like. Although it does not specifically limit as solvents other than a lower alcohol, It is preferable to use the solvent used at the time of film forming of a cellulose ester.

Next, the organic solvent used for dissolving cellulose acylate in the present invention will be described.
In the present invention, any of a chlorinated solvent containing a chlorinated organic solvent as a main solvent and a non-chlorinated solvent not containing a chlorinated organic solvent can be used as the organic solvent.
[Chlorine solvent]
In preparing the cellulose acylate solution in the present invention, a chlorinated organic solvent is preferably used as the main solvent. In the present invention, the type of the chlorinated organic solvent is not particularly limited as long as the object can be achieved within a range where the cellulose acylate can be dissolved, cast and formed. These chlorinated organic solvents are preferably dichloromethane and chloroform. Particularly preferred is dichloromethane. In addition, there is no particular problem in mixing an organic solvent other than the chlorinated organic solvent. In that case, it is necessary to use at least 50% by mass of dichloromethane in the total amount of the organic solvent. Other organic solvents used in combination with the chlorinated organic solvent in the present invention will be described below. That is, as another preferable organic solvent, a solvent selected from esters, ketones, ethers, alcohols, hydrocarbons and the like having 3 to 12 carbon atoms is preferable. Esters, ketones, ethers and alcohols may have a cyclic structure. A compound having two or more functional groups of esters, ketones and ethers (that is, —O—, —CO— and —COO—) can also be used as a solvent. For example, other functional groups such as alcoholic hydroxyl groups can be used. You may have group simultaneously. In the case of a solvent having two or more types of functional groups, the number of carbon atoms may be within the specified range of the compound having any functional group. Examples of esters having 3 to 12 carbon atoms include ethyl formate, propyl formate, pentyl formate, methyl acetate, ethyl acetate and pentyl acetate. Examples of ketones having 3 to 12 carbon atoms include acetone, methyl ethyl ketone, diethyl ketone, diisobutyl ketone, cyclopentanone, cyclohexanone and methylcyclohexanone. Examples of ethers having 3 to 12 carbon atoms include diisopropyl ether, dimethoxymethane, dimethoxyethane, 1,4-dioxane, 1,3-dioxolane, tetrahydrofuran, anisole and phenetole. Examples of the organic solvent having two or more kinds of functional groups include 2-ethoxyethyl acetate, 2-methoxyethanol and 2-butoxyethanol.

The alcohol used in combination with the chlorinated organic solvent may be linear, branched or cyclic, and among them, saturated aliphatic hydrocarbon is preferable. The hydroxyl group of the alcohol may be any of primary to tertiary. Examples of the alcohol include methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, t-butanol, 1-pentanol, 2-methyl-2-butanol and cyclohexanol. As the alcohol, fluorine-based alcohol is also used. Examples thereof include 2-fluoroethanol, 2,2,2-trifluoroethanol, 2,2,3,3-tetrafluoro-1-propanol and the like. Furthermore, the hydrocarbon may be linear, branched or cyclic. Either aromatic hydrocarbons or aliphatic hydrocarbons can be used. The aliphatic hydrocarbon may be saturated or unsaturated. Examples of hydrocarbons include cyclohexane, hexane, benzene, toluene and xylene.
Examples of combinations of chlorinated organic solvents and other organic solvents include the following compositions, but are not limited thereto.

Dichloromethane / methanol / ethanol / butanol (80/10/5/5, parts by mass),
Dichloromethane / acetone / methanol / propanol (80/10/5/5, parts by mass),
Dichloromethane / methanol / butanol / cyclohexane (80/10/5/5, parts by mass),
Dichloromethane / methyl ethyl ketone / methanol / butanol (80/10/5/5, parts by mass),
・ Dichloromethane / acetone / methyl ethyl ketone / ethanol / isopropanol (75/8/5/5/7, parts by mass)
・ Dichloromethane / cyclopentanone / methanol / isopropanol (80/7/5/8, part by mass)
Dichloromethane / methyl acetate / butanol (80/10/10, parts by mass),
Dichloromethane / cyclohexanone / methanol / hexane (70/20/5/5, parts by mass)
Dichloromethane / methyl ethyl ketone / acetone / methanol / ethanol (50/20/20/5/5, parts by mass),
・ Dichloromethane / 1, 3 dioxolane / methanol / ethanol (70/20/5/5, part by mass),
Dichloromethane / dioxane / acetone / methanol / ethanol (60/20/10/5/5, parts by mass),
Dichloromethane / acetone / cyclopentanone / ethanol / isobutanol / cyclohexane (65/10/10/5/5/5, parts by mass),
・ Dichloromethane / methyl ethyl ketone / acetone / methanol / ethanol (70/10/10/5/5, parts by mass),
Dichloromethane / acetone / ethyl acetate / ethanol / butanol / hexane (65/10/10/5/5/5, parts by mass),
Dichloromethane / methyl acetoacetate / methanol / ethanol (65/20/10/5, parts by mass),
Dichloromethane / cyclopentanone / ethanol / butanol (65/20/10/5, parts by mass),
And so on.

[Non-chlorine solvents]
Next, in the present invention, a non-chlorine organic solvent that is preferably used in preparing a cellulose acylate solution will be described. In the present invention, the non-chlorine organic solvent is not particularly limited as long as the object can be achieved as long as the cellulose acylate can be dissolved and cast and formed into a film. The non-chlorine organic solvent used in the present invention is preferably a solvent selected from esters, ketones and ethers having 3 to 12 carbon atoms. Esters, ketones and ethers may have a cyclic structure. A compound having two or more functional groups of esters, ketones and ethers (that is, —O—, —CO—, and —COO—) can also be used as a main solvent, such as an alcoholic hydroxyl group. It may have a functional group of In the case of the main solvent having two or more kinds of functional groups, the number of carbon atoms may be within the specified range of the compound having any functional group. Examples of esters having 3 to 12 carbon atoms include ethyl formate, propyl formate, pentyl formate, methyl acetate, ethyl acetate and pentyl acetate. Examples of ketones having 3 to 12 carbon atoms include acetone, methyl ethyl ketone, diethyl ketone, diisobutyl ketone, cyclopentanone, cyclohexanone and methylcyclohexanone. Examples of ethers having 3 to 12 carbon atoms include diisopropyl ether, dimethoxymethane, dimethoxyethane, 1,4-dioxane, 1,3-dioxolane, tetrahydrofuran, anisole and phenetole. Examples of the organic solvent having two or more kinds of functional groups include 2-ethoxyethyl acetate, 2-methoxyethanol and 2-butoxyethanol.

  The non-chlorine organic solvent used in the above cellulose acylate is selected from the various viewpoints described above, and is preferably as follows. That is, the non-chlorine solvent is preferably a mixed solvent containing the non-chlorine organic solvent as a main solvent, and is a mixed solvent of three or more different solvents, wherein the first solvent is methyl acetate, ethyl acetate, At least one selected from methyl formate, ethyl formate, acetone, dioxolane, and dioxane, or a mixture thereof; the second solvent is selected from ketones having 4 to 7 carbon atoms or acetoacetate; The solvent is a mixed solvent selected from alcohols or hydrocarbons having 1 to 10 carbon atoms, more preferably alcohols having 1 to 8 carbon atoms. Note that when the first solvent is a mixed liquid of two or more kinds of solvents, the second solvent may be omitted. The first solvent is more preferably methyl acetate, acetone, methyl formate, ethyl formate, or a mixture thereof, and the second solvent is preferably methyl ethyl ketone, cyclopentanone, cyclohexanone, methyl acetyl acetate, or a mixed solvent thereof. It may be.

  The alcohol as the third solvent may be linear, branched or cyclic, and is preferably a saturated aliphatic hydrocarbon. The hydroxyl group of the alcohol may be any of primary to tertiary. Examples of the alcohol include methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, t-butanol, 1-pentanol, 2-methyl-2-butanol and cyclohexanol. As the alcohol, fluorine-based alcohol is also used. Examples thereof include 2-fluoroethanol, 2,2,2-trifluoroethanol, 2,2,3,3-tetrafluoro-1-propanol and the like. Furthermore, the hydrocarbon may be linear, branched or cyclic. Either aromatic hydrocarbons or aliphatic hydrocarbons can be used. The aliphatic hydrocarbon may be saturated or unsaturated. Examples of hydrocarbons include cyclohexane, hexane, benzene, toluene and xylene. These alcohols and hydrocarbons as the third solvent may be used alone or in combination of two or more, and are not particularly limited. As the third solvent, preferred specific compounds include alcohol, methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, and cyclohexanol, cyclohexane, hexane, Are methanol, ethanol, 1-propanol, 2-propanol, 1-butanol.

  The mixing ratio of the above three types of mixed solvents is 20 to 95% by mass for the first solvent, 2 to 60% by mass for the second solvent, and 2 to 30% by mass for the third solvent in the total amount of the mixed solvent. The first solvent is preferably 30 to 90% by mass, the second solvent is 3 to 50% by mass, and the third alcohol is preferably 3 to 25% by mass. . In particular, it is preferable that the first solvent is 30 to 90% by mass, the second solvent is 3 to 30% by mass, and the third solvent is alcohol and 3 to 15% by mass. The non-chlorine-based organic solvent used in the present invention described above is more specifically described in JIII Journal of Technical Disclosure No. 2001-1745 (issued March 15, 2001, Invention Association) p. 12-16. Preferred combinations of non-chlorine organic solvents of the present invention can include the following, but are not limited thereto.

-Methyl acetate / acetone / methanol / ethanol / butanol (75/10/5/5/5, parts by mass),
-Methyl acetate / acetone / methanol / ethanol / propanol (75/10/5/5/5, parts by mass),
Methyl acetate / acetone / methanol / butanol / cyclohexane (75/10/5/5/5, parts by mass),
・ Methyl acetate / acetone / ethanol / butanol (81/8/7/4, parts by mass)
・ Methyl acetate / acetone / ethanol / butanol (82/10/4/4, parts by mass)
・ Methyl acetate / acetone / ethanol / butanol (80/10/4/6, part by mass)
Methyl acetate / methyl ethyl ketone / methanol / butanol (80/10/5/5, parts by mass),
-Methyl acetate / acetone / methyl ethyl ketone / ethanol / isopropanol (75/8/5/5/7, parts by mass)
Methyl acetate / cyclopentanone / methanol / isopropanol (80/7/5/8, parts by mass),
Methyl acetate / acetone / butanol (85/10/5, parts by mass),
Methyl acetate / cyclopentanone / acetone / methanol / butanol (60/15/14/5/6, parts by mass),
-Methyl acetate / cyclohexanone / methanol / hexane (70/20/5/5, parts by mass)
・ Methyl acetate / methyl ethyl ketone / acetone / methanol / ethanol (50/20/20/5/5, part by mass),
・ Methyl acetate / 1,3-dioxolane / methanol / ethanol (70/20/5/5, parts by mass),
-Methyl acetate / dioxane / acetone / methanol / ethanol (60/20/10/5/5, parts by mass),
Methyl acetate / acetone / cyclopentanone / ethanol / isobutanol / cyclohexane (65/10/10/5/5/5, parts by mass),

・ Methyl formate / methyl ethyl ketone / acetone / methanol / ethanol (50/20/20/5/5, part by mass),
-Methyl formate / acetone / ethyl acetate / ethanol / butanol / hexane (65/10/10/5/5/5, parts by mass)
Acetone / methyl acetoacetate / methanol / ethanol (65/20/10/5, parts by mass),
Acetone / cyclopentanone / ethanol / butanol (65/20/10/5, parts by mass),
Acetone / 1,3-dioxolane / ethanol / butanol (65/20/10/5, parts by mass),
1,3-dioxolane / cyclohexanone / methyl ethyl ketone / methanol / butanol (55/20/10/5/5/5, parts by mass)
And so on.

Further, a cellulose acylate solution prepared by the following method can also be used.
A method of preparing a cellulose acylate solution with methyl acetate / acetone / ethanol / butanol (81/8/7/4, parts by mass), adding 2 parts by weight of butanol after filtration and concentration, and methyl acetate / acetone / ethanol / Butanol (84/10/4/2, parts by mass) A method for adding a cellulose acylate solution after filtration and concentration, and adding 4 parts by mass of butanol after addition. Methyl acetate / acetone / ethanol (84/10/6, A method for preparing a cellulose acylate solution by mass parts) and adding 5 parts by mass of butanol after filtration and concentration. In addition to the non-chlorine organic solvent of the present invention, dichloromethane is used as the total organic solvent for the dope used in the present invention. You may make it contain 10 mass% or less of quantity.

[Cellulose acylate solution properties]
The cellulose acylate solution is preferably a solution obtained by dissolving cellulose acylate in the organic solvent at a concentration of 10 to 30% by mass from the viewpoint of suitability for film formation, and more preferably 13 to 27% by mass. It is particularly preferably 15 to 25% by mass. The method for carrying out the cellulose acylate at these concentrations may be carried out so as to obtain a predetermined concentration at the stage of dissolution, or it is prepared as a low-concentration solution (for example, 9 to 14% by mass) and then concentrated as described later You may adjust to a predetermined high concentration solution by a process. Furthermore, after making a cellulose acylate solution with a high concentration in advance, various additives may be added to obtain a predetermined low concentration cellulose acylate solution. If implemented, there is no particular problem.

  In the present invention, the retardation developing agent having the predetermined powder properties can be added to the cellulose acylate solution in the form of powder, and the cellulose acylate solution can be added to the cellulose acylate solution in the state of an additive solution dissolved in an organic solvent. It can also be added. In order to obtain a better surface shape, it is preferable to add to the cellulose acylate film in the state of an additive solution. Since the retardation enhancer used in the present invention has the predetermined physical properties described above, it can be well dispersed in the additive solution. As an organic solvent used for the additive solution, a solvent that can be used for the cellulose acylate solution described above can be used. The concentration of the additive solution can be appropriately set within a range in which the retardation developing agent can be satisfactorily dispersed. There is no particular limitation on the timing of adding the additive solution to the cellulose acylate solution.

In this invention, it is preferable that the aggregate molecular weight of the cellulose acylate in the diluted solution which made the cellulose acylate solution 0.1-5 mass% with the organic solvent of the same composition is 150,000-15 million. More preferably, the associated molecular weight is 180,000 to 9 million. This associated molecular weight can be determined by a static light scattering method. In that case, it is preferable to dissolve so that the inertial square radius required at the same time is 10 to 200 nm. A more preferable inertial square radius is 20 to 200 nm. Furthermore, it is preferable to dissolve so that the second virial coefficient is −2 × 10 ⁻⁴ to + 4 × 10 ^−4, and more preferably, the second virial coefficient is −2 × 10 ⁻⁴ to + 2 × 10 ^−4. It is.

Here, the definition of the association molecular weight, the inertial square radius, and the second virial coefficient in the present invention will be described. These are measured using the static light scattering method according to the following method. Although the measurement is performed in a dilute region for the convenience of the apparatus, these measured values reflect the behavior of the dope in the high concentration region of the present invention.
First, cellulose acylate is dissolved in a solvent used for the dope to prepare 0.1 mass%, 0.2 mass%, 0.3 mass%, and 0.4 mass% solutions. In order to prevent moisture absorption, the cellulose acylate is dried at 120 ° C. for 2 hours and is measured at 25 ° C. and 10% RH. The dissolution method is carried out according to the method employed at the time of dope dissolution (room temperature dissolution method, cooling dissolution method, high temperature dissolution method). Subsequently, these solutions and the solvent are filtered through a 0.2 μm Teflon filter. Then, the static light scattering of the filtered solution is measured at an interval of 10 ° from 30 ° to 140 ° at 25 ° C. using a light scattering measuring device (DLS-700 manufactured by Otsuka Electronics Co., Ltd.). The obtained data is analyzed by the BERRY plot method. In addition, the refractive index required for this analysis uses the value of the solvent calculated | required with the Abbe refractive system, and the refractive index concentration gradient (dn / dc) uses the differential refractometer (Otsuka Electronics Co., Ltd. DRM-1021). Measure using the solvent and solution used for light scattering measurement.

[Dope preparation]
Next, preparation of a cellulose acylate solution (dope) will be described. The method for dissolving cellulose acylate is not particularly limited, and may be room temperature, and further, a cooling dissolution method or a high temperature dissolution method, and further a combination thereof. With respect to these, for example, JP-A-5-163301, JP-A-61-106628, JP-A-58-127737, JP-A-9-95544, JP-A-10-95854, JP-A-10-45950, JP 2000-53784, JP 11-322946, JP 11-322947, JP 2-276830, JP 2000-273239, JP 11-71463, JP 04-259511, Special JP-A 2000-273184, JP-A-11-323017, JP-A-11-302388, etc. describe methods for preparing a cellulose acylate solution.
The above-described method for dissolving cellulose acylate in an organic solvent is applicable to the present invention as long as it is within the scope of the present invention. For details of these, particularly for non-chlorine-based solvent systems, the Japan Society for Invention and Innovation Publication No. 2001-1745 (issued March 15, 2001, Japan Society for Invention) p. It is carried out in the manner described in detail in 22-25. Furthermore, the cellulose acylate dope solution of the present invention is usually subjected to solution concentration and filtration, and similarly, the Japan Institute of Invention and Technology Publication No. 2001-1745 (issued March 15, 2001, Invention Association) p. 25 in detail. In addition, when it melt | dissolves at high temperature, it is the case where it is more than the boiling point of the organic solvent to be used, and in that case, it uses in a pressurized state.

  It is preferable that the cellulose acylate solution has a viscosity and a dynamic storage elastic modulus within the ranges described below because it is easy to cast. 1 mL of the sample solution is measured with a rheometer (CLS 500) using a Steel Cone having a diameter of 4 cm / 2 ° (both manufactured by TA Instruments). Measurement conditions were measured at Oscillation Step / Temperature Ramp, varying from 40 ° C to -10 ° C at 2 ° C / min, and static non-Newtonian viscosity n * (Pa · s) at 40 ° C and storage at -5 ° C Obtain the elastic modulus G '(Pa). The sample solution is preliminarily kept at the measurement start temperature until the liquid temperature becomes constant, and then the measurement is started. In the present invention, the viscosity at 40 ° C. is 1 to 400 Pa · s, the dynamic storage elastic modulus at 15 ° C. is preferably 500 Pa or more, and more preferably the viscosity at 40 ° C. is 10 to 200 Pa · s. And the dynamic storage elastic modulus in 15 degreeC is 100-1 million. Furthermore, it is preferable that the dynamic storage elastic modulus at a low temperature is large. For example, when the casting support is −5 ° C., the dynamic storage elastic modulus is preferably 10,000 to 1,000,000 Pa at −5 ° C. When the body is at −50 ° C., the dynamic storage elastic modulus at −50 ° C. is preferably 10,000 to 5 million Pa.

  In the present invention, by using the above-mentioned specific cellulose acylate, a high concentration dope can be obtained, and a cellulose acylate solution having a high concentration and excellent stability can be obtained without depending on the means of concentration. . Furthermore, in order to make it easy to melt | dissolve, after making it melt | dissolve at a low density | concentration, you may concentrate using a concentration means. The concentration method is not particularly limited. For example, the low-concentration solution is guided between the cylindrical body and the rotation trajectory of the outer periphery of the rotating blade rotating in the circumferential direction, and the temperature between the solution and the solution. A method of obtaining a high-concentration solution while evaporating the solvent by giving a difference (for example, JP-A-4-259511), a heated low-concentration solution is blown into the container from the nozzle, and the solution is applied from the nozzle to the inner wall of the container In which the solvent is flash evaporated and the solvent vapor is withdrawn from the container and the concentrated solution is withdrawn from the bottom of the container (eg, US Pat. No. 2,541,012, US Pat. No. 2,858,229, US Pat. No. 4,414,341, US Pat. No. 4,504,355, etc.).

Prior to casting, it is preferable to filter off foreign matters such as undissolved matter, dust, and impurities using a suitable filter medium such as a wire mesh or flannel. For the filtration of the cellulose acylate solution, it is preferable to use a filter having an absolute filtration accuracy of 0.1 to 100 μm, and it is more preferable to use a filter having an absolute filtration accuracy of 0.5 to 25 μm. The thickness of the filter is preferably 0.1 to 10 mm, and more preferably 0.2 to 2 mm. In that case, the filtration pressure is 1.6 MPa. The following is preferable, more preferably 1.2 MPa or less, further 1.0 MPa or less, and particularly preferably 0.2 MPa or less. As the filter medium, conventionally known materials such as glass fibers, cellulose fibers, filter paper, and fluororesins such as tetrafluoroethylene resin can be preferably used, and ceramics, metals and the like are particularly preferably used. The viscosity of the cellulose acylate solution immediately before film formation may be in a range that can be cast during film formation, and is usually preferably adjusted in the range of 10 Pa · s to 2000 Pa · s, and preferably 30 Pa · s to 1000 Pa. · S is more preferable, and 40 Pa · s to 500 Pa · s is more preferable. The temperature at this time is not particularly limited as long as it is the temperature at the time of casting, but is preferably −5 to + 70 ° C., more preferably −5 to + 55 ° C.

[Film formation]
The cellulose acylate film used in the present invention can be obtained by forming a film using the cellulose acylate solution. As a film forming method and equipment, a solution casting film forming method and a solution casting film forming apparatus conventionally used for producing a cellulose triacetate film are used. The dope (cellulose acylate solution) prepared from the dissolving machine (kettle) is temporarily stored in a storage kettle, and the foam contained in the dope is defoamed for final preparation. The dope is fed from the dope discharge port to the pressure die through a pressure metering gear pump capable of delivering a constant amount of liquid with high accuracy, for example, by the number of rotations. The dry-dried dope film (also referred to as a web) is peeled off from the metal support at the peeling point which is uniformly cast on the metal support and the metal support has almost gone around. Both ends of the obtained web are sandwiched between clips, transported by a tenter while keeping the width, dried, then transported by a roll group of a drying device, dried, and wound up to a predetermined length by a winder. The combination of the tenter and the roll group dryer varies depending on the purpose. In the solution casting film forming method used for the functional protective film for electronic displays, in addition to the solution casting film forming apparatus, surface processing on films such as an undercoat layer, an antistatic layer, an antihalation layer, a protective layer, etc. Therefore, a coating device is often added. Although each manufacturing process is described briefly below, it is not limited to these.

  First, when a cellulose acylate film is prepared by a solvent cast method, the prepared cellulose acylate solution (dope) is cast on a drum or band, and the solvent is evaporated to form a film. It is preferable to adjust the concentration of the dope before casting so that the solid content is 5 to 40% by mass. The surface of the drum or band is preferably finished in a mirror state. The dope is preferably cast on a drum or band having a surface temperature of 30 ° C. or lower, and particularly preferably a metal support temperature of −10 to 20 ° C. Further, JP 2000-301555, JP 2000-301558, JP 07-032391, JP 03-193316, JP 05-086212, JP 62-037113, JP 02-276607. The methods described in JP-A Nos. 55-014201, 02-111511, and 02-208650 can be used in the present invention.

[Multilayer casting]
The cellulose acylate solution may be cast as a single layer liquid on a smooth band or drum as a metal support, or a plurality of cellulose acylate liquids of two or more layers may be cast. When casting a plurality of cellulose acylate solutions, produce a film while casting and laminating a solution containing cellulose acylate from a plurality of casting openings provided at intervals in the traveling direction of the metal support. For example, the methods described in JP-A-61-158414, JP-A-1-122419, and JP-A-11-198285 can be applied. Alternatively, a film may be formed by casting a cellulose acylate solution from two casting ports. For example, JP-B-60-27562, JP-A-61-94724, JP-A-61-947245, It can be carried out by the methods described in JP-A Nos. 61-104813, 61-158413, and 6-134933. Further, a cellulose acylate film in which a flow of a high-viscosity cellulose acylate solution described in JP-A-56-162617 is wrapped with a low-viscosity cellulose acylate solution, and the high- and low-viscosity cellulose acylate solutions are simultaneously extruded. A casting method may be used. Furthermore, it is also a preferred embodiment that the outer solution described in JP-A-61-94724 and JP-A-61-94725 contains a larger amount of an alcohol component which is a poor solvent than the inner solution. Alternatively, by using two casting ports, peeling the film formed on the metal support by the first casting port, and performing the second casting on the side that was in contact with the metal support surface, A film may be produced, for example, a method described in Japanese Patent Publication No. 44-20235. The cellulose acylate solution to be cast may be the same solution or different cellulose acylate solutions, and is not particularly limited. In order to give a function to a plurality of cellulose acylate layers, a cellulose acylate solution corresponding to the function may be extruded from each casting port. Furthermore, the cellulose acylate solution can be cast by simultaneously casting other functional layers (for example, an adhesive layer, a dye layer, an antistatic layer, an antihalation layer, a UV absorbing layer, a polarizing layer).

  In the conventional single-layer liquid, it is necessary to extrude a high-concentration and high-viscosity cellulose acylate solution in order to obtain the required film thickness. In many cases, this causes a problem such as a fault or flatness. As a solution to this, by casting a plurality of cellulose acylate solutions from a casting port, a highly viscous solution can be extruded onto a metal support at the same time. Not only can it be produced, but also a concentrated cellulose acylate solution can be used to reduce the drying load and increase the film production speed. In the case of co-casting, the inner and outer thicknesses are not particularly limited, but preferably the outer side is preferably 1 to 50% of the total film thickness, and more preferably 2 to 30%. Here, in the case of co-casting with three or more layers, the total thickness of the layer in contact with the metal support and the layer in contact with the air side is defined as the outer thickness. In the case of co-casting, a cellulose acylate film having a laminated structure can be produced by co-casting cellulose acylate solutions having different additive concentrations such as the above-mentioned plasticizer, ultraviolet absorber and matting agent. For example, a cellulose acylate film having a structure of skin layer / core layer / skin layer can be produced. For example, the matting agent can be contained in the skin layer in a large amount or only in the skin layer. The plasticizer and the ultraviolet absorber can be contained in the core layer more than the skin layer, and may be contained only in the core layer. It is also possible to change the type of plasticizer and ultraviolet absorber between the core layer and the skin layer. For example, the skin layer contains at least one of a low-volatile plasticizer and an ultraviolet absorber, and the core layer is plastic. It is also possible to add an excellent plasticizer or an ultraviolet absorber excellent in ultraviolet absorption. Moreover, it is also a preferable aspect to contain a peeling accelerator only in the skin layer on the metal support side. It is also preferable to add more alcohol, which is a poor solvent, to the skin layer than the core layer in order to cool the metal support by the cooling drum method to gel the solution. The Tg of the skin layer and the core layer may be different, and the Tg of the core layer is preferably lower than the Tg of the skin layer. Further, the viscosity of the solution containing cellulose acylate during casting may be different between the skin layer and the core layer, and the viscosity of the skin layer is preferably smaller than the viscosity of the core layer. It may be smaller than the viscosity.

[Casting]
As a solution casting method, a method in which the prepared dope is uniformly extruded from a pressure die onto a metal support, and a method using a doctor blade in which the dope once cast on the metal support is adjusted with a blade is used. Alternatively, there is a method using a reverse roll coater that adjusts with a reverse rotating roll, and a method using a pressure die is preferable. The pressure die includes a coat hanger type and a T die type, and any of them can be preferably used. In addition to the methods listed here, it can be carried out by various methods of casting a cellulose triacetate solution known in the art, and by setting each condition in consideration of differences in the boiling point of the solvent used, etc. The same effects as those described in the above publication can be obtained. In the present invention, the endlessly running metal support used for producing the cellulose acylate film includes a drum whose surface is mirror-finished by chrome plating and a stainless steel belt which is mirror-finished by surface polishing (referred to as a band). May be used). In the present invention, one or two or more pressure dies used for producing the cellulose acylate film may be installed above the metal support. Preferably 1 or 2 groups. When two or more units are installed, the amount of dope to be cast may be divided into various ratios for each die, or the dope may be fed to the dies from each of a plurality of precision quantitative gear pumps. The temperature of the cellulose acylate solution used for casting is preferably −10 to 55 ° C., more preferably 25 to 50 ° C. In that case, all of the steps may be the same or may be different at different points in the step. If they are different, it may be a desired temperature just before casting.

[Dry]
The drying of the dope on the metal support involved in the production of the cellulose acylate film is generally performed by applying hot air from the surface side of the metal support (drum or belt), that is, the surface of the web on the metal support, A method of applying hot air from the back of the drum or belt, contacting the temperature-controlled liquid from the back of the belt or drum opposite the dope casting surface, and heating the drum or belt by heat transfer to control the surface temperature Although there is a heat transfer method, the back surface liquid heat transfer method is preferable. The surface temperature of the metal support before casting may be any number as long as it is not higher than the boiling point of the solvent used for the dope. However, in order to promote drying and to lose fluidity on the metal support, the temperature should be set to 1 to 10 ° C. lower than the boiling point of the lowest boiling solvent used. Is preferred. This is not the case when the cast dope is cooled and peeled off without drying.

[Stretching treatment]
In the present invention, it is preferable to stretch the cellulose acylate film by 10% or more in the film casting direction or the casting width direction. In the present invention, the retardation can be adjusted by a stretching treatment. Furthermore, there is also a method of positively stretching in the width direction. -48271, and the like. In the methods described in these publications, the produced film is stretched to increase the front retardation value of the cellulose acylate film. The stretching of the film can be performed at room temperature or under heating conditions. The heating temperature is preferably ± 20 ° C. sandwiching the glass transition temperature of the film. If the film is stretched at a temperature extremely lower than the glass transition temperature, it tends to break and cannot exhibit desired optical properties. In addition, if the film is stretched at a temperature extremely higher than the glass transition temperature, it cannot be fixed by the heat at the time of stretching, and the orientation of the optical properties is developed before the molecularly oriented film is stretched by heat. Becomes worse.
The stretching of the film may be uniaxial stretching (fixed width, free width) only in the longitudinal or lateral direction, or simultaneous or sequential biaxial stretching. The stretching is preferably performed at 10 to 200%, more preferably 12 to 100%, particularly preferably 15 to 80%. The birefringence of the optical film is preferably such that the refractive index in the width direction is larger than the refractive index in the length direction. Therefore, it is preferable to stretch more in the width direction. In addition, the stretching process may be performed in the middle of the film forming process, or the raw film that has been formed and wound may be stretched. In the former case, stretching may be performed in a state including the residual solvent amount, and the residual solvent amount (residual solvent amount / (residual solvent amount + solid content amount)) may be preferably 2 to 50%.

  The film thickness of the cellulose acylate film obtained by the production method of the present invention is preferably 20 to 300 μm, more preferably 30 to 180 μm. The thickness of the film may be adjusted by adjusting the solid content concentration contained in the dope, the slit gap of the die base, the extrusion pressure from the die, the metal support speed, and the like. The width of the cellulose acylate film obtained as described above is preferably 0.5 to 3 m, more preferably 0.6 to 2.5 m, and still more preferably 0.8 to 2.2 m. The length is preferably 100 to 10,000 m per roll, more preferably 500 to 7000 m, and still more preferably 1000 to 6000 m. When winding, it is preferable to give a knurling to at least one end, the width is preferably 3 mm to 50 mm, more preferably 5 mm to 30 mm, and the height is preferably 0.5 to 500 μm, more preferably 1 to 200 μm. This may be a single push or a double push.

In the cellulose acylate film obtained by the production method of the present invention, Re ₍₆₃₀₎ and Rth _{(630) at} 25 ° C. and 60% RH preferably satisfy the following formulas (A) to (C).
Formula (A) 46 ≦ Re ₍₆₃₀₎ ≦ 150
Formula (B) Rth ₍₆₃₀₎ = a-5.9 Re ₍₆₃₀₎
Formula (C) 580 ≦ a ≦ 670
[In the formula, Re ₍₆₃₀₎ is the front retardation value at a wavelength of 630 nm (unit: nm),
Rth ₍₆₃₀₎ is a retardation value (unit: nm) in the film thickness direction at a wavelength of 630 nm. Further, a is an adjustment factor (unit: nm) of optical characteristics. ]
a is an adjustment coefficient of Re and Rth, more preferably 590 ≦ a ≦ 660, and further preferably 600 ≦ a ≦ 650. The presence of a in the above range is preferable in terms of widening the viewing angle characteristics of the vertical alignment type liquid crystal display device.

  The cellulose acylate film has a difference ΔRe between Re value at 25 ° C. and 10% RH and Re value at 25 ° C. and 80% RH (= Re 10% RH−Re 80% RH) of 0 to 10 nm, and 25 ° C. The difference ΔRth (= Rth10% RH−Rth80% RH) between the Rth value at 10% RH and the Rth value at 25 ° C. and 80% RH is 0 to 30 nm, so that the color change with time of the liquid crystal display device is reduced. This is preferable.

The film thickness distribution in the width direction of Re was sequentially sampled from the position of 2 cm (width direction) × 3 cm (width direction perpendicular) of the film in the width direction from the position of the film edge 5 cm, Ten points were collected at equal intervals. The film thickness of each test piece (2 cm × 3 cm) was measured at a total of nine points in the longitudinal and horizontal directions in the plane of the film, and the film thickness of the sample was measured.
When the film thickness distribution R is defined as R (%) = (Rmax−Rmin) / Rave × 100 when the maximum value, minimum value, and average value of the film thickness in the width direction are Rmax, Rmin, and Rave, respectively. These are preferably adjusted to 0 to 8%, more preferably adjusted to 0 to 7.8%, and further preferably adjusted to 0 to 7.6%. Since Re and Rth are values proportional to the film thickness, the smaller the film thickness distribution in the width direction of the film thickness, the smaller the variation in Re (590) and Rth (590).
The distribution of Re (590) and Rth (590) is caused by the above-described film thickness variation, or due to stretching unevenness, drying unevenness, etc., but this Re distribution (variation) is 5% or less. The Rth distribution is preferably adjusted to 10% or less. More preferably, the Re distribution is 4.8% or less, the Rth distribution is 9.8% or less, more preferably the Re distribution is 4.6% or less, and the Rth distribution is 9.6% or less. It is preferable.
The film thickness distribution R, Re distribution, and Rth distribution described above are preferable because display unevenness is reduced when the film is used in a liquid crystal display device (particularly a VA liquid crystal display device).

In addition, the cellulose acylate film has a color difference ΔE ^* ab before and after aging at 90 ° C. for 500 hours, preferably 0.8 or less, preferably 0.7 or less, and 0.5 or less. More preferably. The color difference between before and after aging at 140 ° C. for 24 hours is preferably 1.5 or less, more preferably 1.0 or less, and further preferably 0.5 or less. If the film is colored under environmentally forced conditions such as 90 ° C. for 500 hours or 140 ° C. for 24 hours, the optical compensation ability as a retardation film is lowered, which is not preferable in terms of appearance. The color difference was measured using UV3100 (manufactured by Shimadzu Corporation). The measurement was carried out by adjusting the film to 25 ° C. and 60% RH for 2 hours or more, and then measuring the color of the film before aging the thermo to obtain initial values (L0 ^* , a0 ^* , b0 ^* ). Thereafter, the film alone was left in an air thermostat for a predetermined time. After the elapse of a predetermined time, the film was taken out from the thermostatic bath, adjusted to 25 ° C. and 60% RH for 2 hours, then subjected to color measurement, and values after thermo-aging (L1 ^* , a1 ^* , b1 ^* ) were obtained. From these, the color difference ΔE ^* ab = ((L0 ^* −L1 ^* ) ² + (a0 ^* −a1 ^* ) ² + (b0 ^* −b1 ^* ) ² ) ^1/2 was obtained.

The cellulose acylate film has an equilibrium water content at 25 ° C. and 80% RH of preferably 5.0% or less, more preferably 4.0% or less, and 3.2% or less. Is more preferable, and it is preferable in order to reduce the color change with time of the liquid crystal display device.
The moisture content is measured by measuring a cellulose acylate film sample 7 mm × 35 mm by a Karl Fischer method using a moisture meter and a sample drying apparatus (CA-03, VA-05, both Mitsubishi Chemical Corporation). Calculated by dividing the amount of water (g) by the sample weight (g).
The cellulose acylate film has a moisture permeability of 60 ° C., 95% RH, 24 hr (film thickness 80 μm conversion) of 400 g / m ² · 24 hr to 1800 g / m ² · 24 hr. This is preferable in order to reduce the color change with time.
If the film thickness of the cellulose acylate film is thick, the moisture permeability becomes small, and if the film thickness is thin, the moisture permeability becomes large. The measured moisture permeability is converted with a reference film thickness of 80 μm. The converted value of moisture permeability is calculated by “80 μm converted moisture permeability = actually measured moisture permeability × actually measured film thickness μm / 80 μm”.
The measurement method of moisture permeability is “Polymer Properties II” (Polymer Experiment Course 4, Kyoritsu Shuppan), pages 285-294: Measurement of vapor permeation (mass method, thermometer method, vapor pressure method, adsorption amount method) The method described in can be applied.

  The glass transition temperature was measured after adjusting the humidity of a cellulose acylate film sample (unstretched) 5 mm × 30 mm at 25 ° C. and 60% RH for 2 hours or more (Vibron: DVA-225 (IT measurement) Measured at a distance between grips of 20 mm, a temperature increase rate of 2 ° C./minute, a measurement temperature range of 30 ° C. to 200 ° C. and a frequency of 1 Hz, the logarithmic axis is the storage elastic modulus, and the horizontal axis is linear When the temperature (° C.) is taken at the axis, the sharp decrease in the storage elastic modulus observed when the storage elastic modulus shifts from the solid region to the glass transition region is drawn with a straight line 1 in the solid region, and a straight line 2 in the glass transition region. Is the temperature at which the storage elastic modulus suddenly decreases and the film begins to soften when the temperature rises, and the temperature at which the film begins to transition to the glass transition region. Therefore, the glass transition temperature Tg (Dynamic visco ) To.

  The elastic modulus is measured by adjusting a dry film cellulose acylate film sample 10 mm × 150 mm at 25 ° C. and 60% RH for 2 hours or more and then using a tensile tester (Strograph-R2 (manufactured by Toyo Seiki)) The distance was 100 mm, the temperature was 25 ° C., and the stretching speed was 10 mm / min.

The cellulose acylate film preferably has a haze of 0.01 to 2%. Here, haze is measured as follows.
A cellulose acylate film sample of 40 mm × 80 mm is measured at 25 ° C. and 60% RH with a haze meter (HGM-2DP, Suga Test Machine) in accordance with JIS K-6714.
Moreover, it is preferable that the mass change when the said cellulose acylate film is left to stand for 48 hours on 80 degreeC and 90% RH conditions is 0 to 5%.
The cellulose acylate film has a dimensional change when left for 24 hours under conditions of 60 ° C. and 95% RH, and a dimensional change when left for 24 hours under conditions of 90 ° C. and 5% RH. However, it is preferable that all are 0 to 5%.

The cellulose acylate film preferably has a photoelastic coefficient of 50 × 10 ⁻¹³ cm ² / dyne or less in order to reduce color change with time of the liquid crystal display device.
As a specific measuring method, a tensile stress is applied to the major axis direction of a 10 mm × 100 mm cellulose acylate film sample, and the retardation at that time is measured with an ellipsometer (M150, JASCO Corporation). The photoelastic coefficient is calculated from the amount of change in retardation with respect to.

[Polarizer]
Next, the polarizing plate of the present invention will be described.
A polarizing plate usually comprises a polarizing film and two protective films disposed on both sides thereof. And in this invention, the cellulose acylate film obtained by the manufacturing method of the above-mentioned this invention is used as at least one protective film. The other protective film may be the above-described cellulose acylate film or a normal cellulose acetate film. Examples of the polarizing film include an iodine polarizing film, a dye polarizing film using a dichroic dye, and a polyene polarizing film. The iodine polarizing film and the dye polarizing film are generally produced using a polyvinyl alcohol film. The manufacturing method of the polarizing plate of this invention is not specifically limited, It can manufacture by a general method. For example, there is a method in which the obtained cellulose acylate film is treated with an alkali and bonded to both surfaces of a polarizing film prepared by immersing and stretching a polyvinyl alcohol film in an iodine solution using a completely saponified polyvinyl alcohol aqueous solution. Instead of alkali treatment, easy adhesion processing as described in JP-A-6-94915 and JP-A-6-118232 may be performed. Examples of the adhesive used to bond the protective film-treated surface and the polarizing film include polyvinyl alcohol adhesives such as polyvinyl alcohol and polyvinyl butyral, vinyl latexes such as butyl acrylate, and the like. The polarizing plate is composed of a polarizing film and protective films for protecting both surfaces of the polarizing film. Further, a protective film may be bonded to one surface of the polarizing plate and a separate film may be bonded to the opposite surface. The protective film and the separate film are used for the purpose of protecting the polarizing plate at the time of shipping the polarizing plate and at the time of product inspection. In this case, the protect film is bonded for the purpose of protecting the surface of the polarizing plate, and is used on the side opposite to the surface where the polarizing plate is bonded to the liquid crystal plate. Moreover, a separate film is used in order to cover the contact bonding layer bonded to a liquid crystal plate, and is used for the surface side which bonds a polarizing plate to a liquid crystal plate.

As shown in FIG. 1, the cellulose acylate film is bonded to the polarizing film so that the transmission axis of the polarizing film and the slow axis of the cellulose acylate film (TAC1 in the figure) coincide with each other. Is preferred.
Note that a polarizing plate produced under polarizing cross Nicol has a polarizing plate cross when the orthogonal accuracy between the slow axis of the cellulose acylate film and the absorption axis of the polarizing film (axis orthogonal to the transmission axis) is greater than 1 °. The direction of the main refractive index nx of the cellulose acylate film and the polarizing plate because when the combination with a liquid crystal cell cannot obtain sufficient black level and contrast when the polarization degree performance under Nicol is lowered and light leakage occurs The direction of the transmission axis is preferably within 1 °, more preferably within 0.5 °.
In the present invention, the single plate transmittance, parallel transmittance, and orthogonal transmittance of the polarizing plate were measured using UV3100PC (manufactured by Shimadzu Corporation). In the measurement, the measurement was performed in the range of 380 nm to 780 nm under the condition of 25 ° C. and 60% RH, and the average value of 10 measurements was used for each of the single plate, parallel and orthogonal transmittances. The measurement was performed as follows in two types of forms in which (1) only the polarizing plate and (2) the polarizing plate were bonded to glass via an adhesive. For the measurement of only the polarizing plate, two orthogonal and the same ones were prepared and measured so that the optical compensation film was sandwiched between the two polarizing films. Two samples (approx. 5 cm × 5 cm) are prepared by attaching a polarizing plate on glass so that the optical compensation film is on the glass side. In the single plate transmittance measurement, the film side of this sample was set facing the light source. Two samples were measured respectively, and the average value was defined as the transmittance of the single plate. The preferable range of polarization performance is 40.0 ≦ TT ≦ 45.0, 30.0 ≦ PT ≦ 40.0, and CT ≦ 2.0 in the order of single plate transmittance, parallel transmittance, and orthogonal transmittance, respectively. More preferable range is 40.2 ≦ TT ≦ 44.8, 32.2 ≦ PT ≦ 39.5, CT ≦ 1.6, and further preferable range is 41.0 ≦ TT ≦ 44.6. 34 ≦ PT ≦ 39.1 and CT ≦ 1.3.
The degree of polarization P is calculated from these transmittances, and the greater the degree of polarization P is, the less light leaks when arranged in a cross, indicating that the performance of the polarizing plate is higher. The degree of polarization P is preferably 95.0% or more, more preferably 96.0% or more, and further preferably 97.0% or more.

In the polarizing plate of the present invention, T ₍₃₈₀₎ , T ₍₄₁₀₎ , and T ₍₇₀₀₎ are at least one of the following formulas (e) to (g), where T ₍ λ ₎ is the orthogonal transmittance at wavelength λ. It is preferable to satisfy one or more.
(E) T ₍₃₈₀₎ ≦ 2.0
(F) T ₍₄₁₀₎ ≦ 1.0
(G) T ₍₇₀₀₎ ≦ 0.5
More preferably, T (380) ≦ 1.95, T (410) ≦ 0.9, T (700) ≦ 0.49, and even more preferably T (380) ≦ 1.90, T (410) ≦ 0. .8, T (700) ≦ 0.48.
The polarizing plate of the present invention has an orthogonal single plate transmittance change ΔCT and a polarization degree change ΔP of at least the following formulas (j) and (k) when left at 60 ° C. and 95% RH for 500 hours. It is preferable to satisfy one or more.
(J) −6.0 ≦ ΔCT ≦ 6.0
(K) -10.0 ≦ ΔP ≦ 0.0
(However, the amount of change is the value obtained by subtracting the pre-test measurement value from the post-test measurement value)
More preferably, −5.8 ≦ ΔCT ≦ 5.8, −9.5 ≦ ΔP ≦ 0.0, and still more preferably, −5.6 ≦ ΔCT ≦ 5.6, −9.0 ≦ ΔP ≦ 0.0. It is.
The polarizing plate of the present invention has an orthogonal single plate transmittance change ΔCT and a polarization degree change ΔP of at least the following formulas (h) and (i) when left at 60 ° C. and 90% RH for 500 hours. It is preferable to satisfy one or more.
(H) −3.0 ≦ ΔCT ≦ 3.0
(I) −5.0 ≦ ΔP ≦ 0.0
In the polarizing plate of the present invention, at least one or more of the following formulas (l) and (m) has a change amount ΔCT and a change degree of polarization degree ΔP of the orthogonal single plate when left at 80 ° C. for 500 hours. It is preferable to satisfy.
(L) −3.0 ≦ ΔCT ≦ 3.0
(M) −2.0 ≦ ΔP ≦ 0.0
In the polarizing plate durability test, the amount of change is preferably smaller.

  On the surface of the cellulose acylate film, an optically anisotropic layer having in-plane optical anisotropy may be provided. You may have the orientation film which controls the orientation of the liquid crystalline compound in an optically anisotropic layer between the said cellulose acylate film and an optically anisotropic layer.

[Optically anisotropic layer]
The optically anisotropic layer can be formed from a liquid crystalline compound. For example, the optically anisotropic layer may be directly formed on the surface of a support composed of a cellulose acylate film, or an alignment film is formed on the support and the alignment is performed. You may form on a film | membrane. Moreover, it is also possible to produce an optical compensation film by transferring a liquid crystalline compound layer formed on another substrate onto a cellulose acylate film using an adhesive, an adhesive, or the like.
Examples of the liquid crystalline compound used for forming the optically anisotropic layer include a rod-like liquid crystalline compound and a discotic liquid crystalline compound (hereinafter, the discotic liquid crystalline compound may be referred to as a “discotic liquid crystalline compound”). The rod-like liquid crystal compound and the discotic liquid crystal compound may be a high-molecular liquid crystal or a low-molecular liquid crystal. Further, the compound finally contained in the optically anisotropic layer no longer needs to exhibit liquid crystallinity. For example, when a low-molecular liquid crystalline compound is used for the production of the optically anisotropic layer, the optically anisotropic layer In the process of forming, the compound may be cross-linked and no longer exhibits liquid crystallinity.

(Bar-shaped liquid crystalline compound)
Examples of the rod-like liquid crystalline compound that can be used in the present invention include azomethines, azoxys, cyanobiphenyls, cyanophenyl esters, benzoic acid esters, cyclohexanecarboxylic acid phenyl esters, cyanophenylcyclohexanes, and cyano-substituted phenylpyrimidines. Alkoxy-substituted phenylpyrimidines, phenyldioxanes, tolanes and alkenylcyclohexylbenzonitriles are preferably used. The rod-like liquid crystalline compound includes a metal complex. A liquid crystal polymer containing a rod-like liquid crystal compound in a repeating unit can also be used. In other words, the rod-like liquid crystalline compound may be bonded to a (liquid crystal) polymer.
For rod-like liquid crystalline compounds, see Chapter 4, Chapter 7 and Chapter 11 of the Chemistry of the Quarterly Chemical Review Vol. 22 Liquid Crystal Chemistry (1994) edited by the Chemical Society of Japan, and the 142nd Committee of the Japan Society for the Promotion of Science. Described in Chapter 3.

The birefringence of the rod-like liquid crystalline compound used in the present invention is preferably in the range of 0.001 to 0.7.
The rod-like liquid crystalline compound preferably has a polymerizable group in order to fix its alignment state. The polymerizable group is preferably an unsaturated polymerizable group or an epoxy group, more preferably an unsaturated polymerizable group, and most preferably an ethylenically unsaturated polymerizable group.

(Discotic liquid crystalline compounds)
Examples of discotic liquid crystalline compounds include C.I. Destrade et al., Mol. Cryst. 71, 111 (1981), benzene derivatives described in C.I. Destrade et al., Mol. Cryst. 122, 141 (1985), Physics lett, A, 78, 82 (1990); Kohne et al., Angew. Chem. 96, page 70 (1984) and the cyclohexane derivatives described in J. Am. M.M. Lehn et al. Chem. Commun. , 1794 (1985), J. Am. Zhang et al., J. Am. Chem. Soc. 116, 2655 (1994), azacrown type and phenylacetylene type macrocycles are included.

  The discotic liquid crystalline compound exhibits liquid crystallinity with a structure in which a linear alkyl group, an alkoxy group or a substituted benzoyloxy group is radially substituted as a side chain of the mother nucleus with respect to the mother nucleus at the center of the molecule. Also included are compounds. The molecule or the assembly of molecules is preferably a compound having rotational symmetry and imparting a certain orientation.

  As described above, when an optically anisotropic layer is formed from a liquid crystalline compound, the compound finally contained in the optically anisotropic layer no longer needs to exhibit liquid crystallinity. For example, a low-molecular discotic liquid crystalline compound has a group that reacts with heat or light, and the group reacts with heat or light to polymerize or crosslink to increase the molecular weight. When a layer is formed, the compound contained in the optically anisotropic layer may no longer have liquid crystallinity. Preferred examples of the discotic liquid crystalline compound are described in JP-A-8-50206. Moreover, about superposition | polymerization of a discotic liquid crystalline compound, Unexamined-Japanese-Patent No. 8-27284 has description.

  In order to fix the discotic liquid crystalline compound by polymerization, it is necessary to bond a polymerizable group as a substituent to the discotic core of the discotic liquid crystalline compound. However, when the polymerizable group is directly connected to the disc-shaped core, it becomes difficult to maintain the orientation state in the polymerization reaction. Therefore, a linking group is introduced between the discotic core and the polymerizable group. Accordingly, the discotic liquid crystalline compound having a polymerizable group is preferably a compound represented by the following formula (III).

Formula (III)
D (-LQ) _n
In the formula, D is a discotic core, L is a divalent linking group, Q is a polymerizable group, and n is an integer of 4 to 12.

  An example of the disk-shaped core (D) is shown below. In each of the following examples, LQ (or QL) means a combination of a divalent linking group (L) and a polymerizable group (Q).

  In the formula (III), the divalent linking group (L) is selected from the group consisting of an alkylene group, an alkenylene group, an arylene group, —CO—, —NH—, —O—, —S—, and combinations thereof. A divalent linking group selected is preferable. The divalent linking group (L) is a divalent combination of at least two divalent groups selected from the group consisting of an alkylene group, an arylene group, -CO-, -NH-, -O-, and S-. The linking group is more preferable. The divalent linking group (L) is most preferably a divalent linking group in which at least two divalent groups selected from the group consisting of an alkylene group, an arylene group, -CO- and O- are combined. preferable. The alkylene group preferably has 1 to 12 carbon atoms. The alkenylene group preferably has 2 to 12 carbon atoms. The arylene group preferably has 6 to 10 carbon atoms.

  Examples of the divalent linking group (L) are shown below. The left side is bonded to the discotic core (D), and the right side is bonded to the polymerizable group (Q). AL represents an alkylene group or alkenylene group, and AR represents an arylene group. The alkylene group, alkenylene group and arylene group may have a substituent (eg, an alkyl group).

L1: -AL-CO-O-AL-
L2: -AL-CO-O-AL-O-
L3: -AL-CO-O-AL-O-AL-
L4: -AL-CO-O-AL-O-CO-
L5: -CO-AR-O-AL-
L6: -CO-AR-O-AL-O-
L7: -CO-AR-O-AL-O-CO-
L8: -CO-NH-AL-
L9: -NH-AL-O-
L10: -NH-AL-O-CO-

L11: -O-AL-
L12: -O-AL-O-
L13: -O-AL-O-CO-
L14: -O-AL-O-CO-NH-AL-
L15: -O-AL-S-AL-
L16: -O-CO-AR-O-AL-CO-
L17: -O-CO-AR-O-AL-O-CO-
L18: -O-CO-AR-O-AL-O-AL-O-CO-
L19: -O-CO-AR-O-AL-O-AL-O-AL-O-CO-
L20: -S-AL-
L21: -S-AL-O-
L22: -S-AL-O-CO-
L23: -S-AL-S-AL-
L24: -S-AR-AL-

The polymerizable group (Q) of the formula (III) is determined according to the type of polymerization reaction. The polymerizable group (Q) is preferably an unsaturated polymerizable group or an epoxy group, more preferably an unsaturated polymerizable group, and most preferably an ethylenically unsaturated polymerizable group.
In formula (III), n is an integer of 4-12. A specific number is determined according to the type of the disk-shaped core (D). In addition, although the combination of several L and Q may differ, it is preferable that it is the same.

  In the present invention, in the optically anisotropic layer, the molecules of the rod-like compound or the discotic compound are fixed in an oriented state. The orientation average direction at the interface on the cellulose acylate film side of the molecular symmetry axis of the liquid crystal compound has an intersecting angle of about 45 degrees with the slow axis in the plane of the cellulose acylate film. In this specification, “approximately 45 °” refers to an angle in the range of 45 ° ± 5 °, preferably 42 to 48 °, and more preferably 43 to 47 °. The average direction of the molecular symmetry axis of the liquid crystalline compound in the optically anisotropic layer is preferably 43 ° to 47 ° with respect to the longitudinal direction of the support (that is, the fast axis direction of the support).

  The orientation average direction of the molecular symmetry axis of the liquid crystal compound can be generally adjusted by selecting a material of the liquid crystal compound or the alignment film or by selecting a rubbing treatment method. In the present invention, for example, when an alignment film for forming an optically anisotropic layer is produced by rubbing, the molecular symmetry of the liquid crystalline compound is obtained by rubbing in the direction of 45 ° with respect to the slow axis of the support. An optically anisotropic layer in which the orientation average direction of the axis at least at the support interface is 45 ° with respect to the slow axis of the cellulose acylate film can be formed. For example, the optical compensation film used in the present invention can be continuously produced by using a long cellulose acylate film whose slow axis is parallel to the longitudinal direction. Specifically, a coating liquid for forming an alignment film is continuously applied to the surface of a long cellulose acylate film to prepare a film, and then the surface of the film is continuously 45 ° in the longitudinal direction. An alignment film is produced by rubbing in the direction, and then a coating liquid for forming an optically anisotropic layer containing a liquid crystalline compound is continuously applied onto the prepared alignment film to align the molecules of the liquid crystalline compound. Then, the optically anisotropic layer can be produced by fixing in that state, and a long optical compensation film can be produced continuously. The optical compensation film produced in a long shape is cut into a desired shape before being incorporated into the liquid crystal display device.

  In addition, with respect to the orientation average direction of the molecular symmetry axis on the surface side (air side) of the liquid crystalline compound, the orientation average direction of the molecular symmetry axis of the liquid crystalline compound on the air interface side is relative to the slow axis of the cellulose acylate film. It is preferably approximately 45 °, more preferably 42 to 48 °, and even more preferably 43 to 47 °. In general, the orientation average direction of the molecular symmetry axis of the liquid crystal compound on the air interface side can be adjusted by selecting the type of the liquid crystal compound or the additive used together with the liquid crystal compound. Examples of the additive used together with the liquid crystal compound include a plasticizer, a surfactant, a polymerizable monomer and a polymer. Similarly to the above, the degree of change in the orientation direction of the molecular symmetry axis can be adjusted by selecting the liquid crystal compound and the additive. In particular, regarding the surfactant, it is preferable that the surface tension control of the coating solution is compatible.

  The plasticizer, surfactant and polymerizable monomer used together with the liquid crystal compound are compatible with the discotic liquid crystal compound and may change the tilt angle of the liquid crystal compound or do not inhibit the alignment. preferable. A polymerizable monomer (eg, a compound having a vinyl group, a vinyloxy group, an acryloyl group and a methacryloyl group) is preferred. The amount of the compound added is generally in the range of 1 to 50% by mass and preferably in the range of 5 to 30% by mass with respect to the liquid crystal compound. In addition, when a monomer having 4 or more polymerizable reactive functional groups is mixed and used, adhesion between the alignment film and the optically anisotropic layer can be improved.

When a discotic liquid crystalline compound is used as the liquid crystalline compound, it is preferable to use a polymer that has a certain degree of compatibility with the discotic liquid crystalline compound and can change the tilt angle of the discotic liquid crystalline compound.
A cellulose ester can be mentioned as an example of a polymer. Preferred examples of the cellulose ester include cellulose acetate, cellulose acetate propionate, hydroxypropyl cellulose, and cellulose acetate butyrate. In order not to inhibit the orientation of the discotic liquid crystalline compound, the amount of the polymer added is preferably in the range of 0.1 to 10% by mass, preferably 0.1 to 8% by mass with respect to the discotic liquid crystalline compound. More preferably, it is in the range of 0.1 to 5% by mass.
The discotic nematic liquid crystal phase-solid phase transition temperature of the discotic liquid crystalline compound is preferably 70 to 300 ° C, more preferably 70 to 170 ° C.

  In the present invention, the optically anisotropic layer has at least in-plane optical anisotropy. The front retardation Re of the optically anisotropic layer is preferably 3 to 300 nm, more preferably 5 to 200 nm, and still more preferably 10 to 100 nm. The retardation Rth in the film thickness direction of the optically anisotropic layer is preferably 20 to 400 nm, and more preferably 50 to 200 nm. The thickness of the optically anisotropic layer is preferably 0.1 to 20 μm, more preferably 0.5 to 15 μm, and most preferably 1 to 10 μm.

[Alignment film]
The optical compensation film used in the present invention may have an alignment film between the support and the optically anisotropic layer. In addition, an alignment film is used only when preparing an optically anisotropic layer, and after preparing an optically anisotropic layer on the alignment film, only the optically anisotropic layer is transferred onto a cellulose acylate film. Also good.
In the present invention, the alignment film is preferably a layer made of a crosslinked polymer. The polymer used for the alignment film may be either a polymer that can be crosslinked by itself or a polymer that is crosslinked by a crosslinking agent. The alignment film is formed by reacting a polymer having a functional group or a polymer having a functional group introduced therein with light, heat, pH change, or the like; or a cross-linking agent that is a highly reactive compound Can be formed by introducing a linking group derived from a cross-linking agent between polymers to cross-link between the polymers.

The alignment film composed of a crosslinked polymer can be usually formed by applying a coating solution containing the polymer or a mixture of a polymer and a crosslinking agent on a support, followed by heating or the like.
In the rubbing process described later, it is preferable to increase the degree of crosslinking in order to suppress the dust generation of the alignment film. A value (1- (Ma / Mb)) obtained by subtracting 1 from the ratio (Ma / Mb) of the amount (Ma) of the crosslinking agent remaining after crosslinking to the amount (Mb) of the crosslinking agent added to the coating solution. When Mb)) is defined as the degree of crosslinking, the degree of crosslinking is preferably 50% to 100%, more preferably 65% to 100%, and most preferably 75% to 100%.

In the present invention, the polymer used for the alignment film may be either a polymer that can be crosslinked by itself or a polymer that is crosslinked by a crosslinking agent. Of course, a polymer having both functions can also be used. Examples of the polymer include polymethyl methacrylate, acrylic acid / methacrylic acid copolymer, styrene / maleimide copolymer, polyvinyl alcohol and modified polyvinyl alcohol, poly (N-methylolacrylamide), Styrene / vinyl toluene copolymer, chlorosulfonated polyethylene, nitrocellulose, polyvinyl chloride, chlorinated polyolefin, polyester, polyimide, vinyl acetate / vinyl chloride copolymer, ethylene / vinyl acetate copolymer, carboxymethyl cellulose And polymers such as gelatin, polyethylene, polypropylene and polycarbonate, and compounds such as silane coupling agents. Examples of preferred polymers are water-soluble polymers such as poly (N-methylacrylamide), carboxymethyl cellulose, gelatin, polyvir alcohol and modified polyvinyl alcohol, and further gelatin, polyvir alcohol and modified polyvinyl alcohol. In particular, mention may be made of polyvinyl alcohol and modified polyvinyl alcohol.
When polyville alcohol and modified polyvinyl alcohol are directly coated on the support, a method of providing a hydrophilic undercoat layer or performing a saponification treatment described in Japanese Patent Application No. 2000-369004 is preferably used.

Among the above polymers, polyvinyl alcohol or modified polyvinyl alcohol is preferable.
Examples of the polyvinyl alcohol include those having a saponification degree of 70 to 100%, generally those having a saponification degree of 80 to 100%, and more preferably those having a saponification degree of 82 to 98%. The degree of polymerization is preferably in the range of 100 to 3000.
Examples of the modified polyvinyl alcohol include those modified by copolymerization (for example, COONa, Si (OX) ₃ , N (CH ₃ ) ₃ .Cl, C ₉ H ₁₉ COO, SO ₃ Na, C ₁₂ H ₂₅ etc. Modified by chain transfer (for example, COONa, SH, SC ₁₂ H ₂₅ etc. are introduced as modifying groups), modified by block polymerization (modified groups such as COOH, for example) , CONH ₂ , COOR, C ₆ H _5, etc. are introduced). As a polymerization degree, the range of 100-3000 is preferable. Among these, unmodified or modified polyvinyl alcohol having a saponification degree of 80 to 100% is preferable, and unmodified or alkylthio-modified polyvinyl alcohol having a saponification degree of 85 to 95% is more preferable.

As the modified polyvinyl alcohol used for the alignment film, a reaction product of a compound represented by the following general formula (6) and polyvinyl alcohol is preferable.
General formula (6):

In the formula, R ^1d represents an unsubstituted alkyl group or an alkyl group substituted with an acrylolyl group, a methacryloyl group or an epoxy group, W represents a halogen atom, an alkyl group or an alkoxy group, X ^1d represents an active ester, an acid A group of atoms necessary for forming an anhydride or an acid halide is represented, l represents 0 or 1, and n represents an integer of 0 to 4.

Moreover, as the modified polyvinyl alcohol used for the alignment film, a reaction product of a compound represented by the following general formula (7) and polyvinyl alcohol is also preferable.
General formula (7 '):

In the formula, X ^2d represents an atomic group necessary for forming an active ester, an acid anhydride or an acid halide, and m represents an integer of 2 to 24.

Examples of the polyvinyl alcohol used for reacting with the compounds represented by the general formula (6) and the general formula (7) include the unmodified polyvinyl alcohol and the copolymer-modified one, that is, chain transfer. Examples include modified products of polyvinyl alcohol such as modified products and modified products by block polymerization. Preferred examples of the specific modified polyvinyl alcohol are described in detail in JP-A-8-338913.
When using a hydrophilic polymer such as polyvinyl alcohol for the alignment film, it is preferable to control the moisture content from the viewpoint of the degree of hardening, preferably 0.4% to 2.5%, 0.6% More preferably, it is -1.6%. The water content can be measured with a commercially available Karl Fischer moisture content measuring device.
The alignment film preferably has a thickness of 10 μm or less.

[surface treatment]
In the present invention, the obtained cellulose acylate film is optionally subjected to a surface treatment to achieve improved adhesion between the cellulose acylate film and each functional layer (for example, an undercoat layer and a back layer). Can do. As the surface treatment, for example, glow discharge treatment, ultraviolet irradiation treatment, corona treatment, flame treatment, acid or alkali treatment can be used. The glow discharge treatment here may be low-temperature plasma that occurs in a low-pressure gas of 10 ^{−3 to} 20 Torr, and plasma treatment under atmospheric pressure is also preferable. A plasma-excitable gas is a gas that is plasma-excited under the above-mentioned conditions, and examples thereof include chlorofluorocarbons such as argon, helium, neon, krypton, xenon, nitrogen, carbon dioxide, tetrafluoromethane, and mixtures thereof. It is done. Regarding these, the details are disclosed in the Invention Association Public Technical Bulletin No. 2001-1745 (issued March 15, 2001, Invention Association) p. 30-32. Note that, in the plasma treatment at atmospheric pressure which has been attracting attention in recent years, for example, irradiation energy of 20 to 500 Kgy is used under 10 to 1000 Kev, and more preferably irradiation energy of 20 to 300 Kgy is used under 30 to 500 Kev. Among these, an alkali saponification treatment is particularly preferable, and it is extremely effective as a surface treatment of a cellulose acylate film.

  The alkali saponification treatment is preferably carried out by a method in which the cellulose acylate film is directly immersed in a saponification solution tank or a method in which the saponification solution is applied to the cellulose acylate film. Examples of the coating method include a dip coating method, a curtain coating method, an extrusion coating method, a bar coating method, and an E-type coating method. The solvent of the alkali saponification coating solution has good wettability in order to apply the saponification solution to the cellulose acylate film, and the surface of the cellulose acylate film surface is not formed by the saponification solution solvent. It is preferred to select a solvent that remains good. Specifically, an alcohol solvent is preferable, and isopropyl alcohol is particularly preferable. An aqueous solution of a surfactant can also be used as a solvent. The alkali of the alkali saponification coating solution is preferably an alkali that dissolves in the above solvent, and more preferably KOH or NaOH. The pH of the saponification coating solution is preferably 10 or more, more preferably 12 or more. The reaction conditions during alkali saponification are preferably 1 second to 5 minutes at room temperature, more preferably 5 seconds to 5 minutes, and particularly preferably 20 seconds to 3 minutes. After the alkali saponification reaction, it is preferable to wash the surface on which the saponification solution is applied with water or with an acid and then with water.

  In addition, the polarizing plate of the present invention is preferably one in which at least one layer of a hard coat layer, an antiglare layer and an antireflection layer is provided on the surface of the protective film on the other side of the polarizing plate. That is, as shown in FIG. 2, it is preferable to provide a functional film such as an antireflection layer on the protective film disposed on the side opposite to the liquid crystal cell when the polarizing plate is used in a liquid crystal display device. It is preferable to provide at least one layer of a hard coat layer, an antiglare layer, and an antireflection layer. Each layer does not need to be provided as a separate layer. For example, the antireflection layer may function as an antireflection layer and an antiglare layer by providing the antireflection layer with a function as an antiglare layer.

[Antireflection layer]
In the present invention, an antireflective layer in which at least a light scattering layer and a low refractive index layer are laminated in this order on a protective film, or a medium refractive index layer, a high refractive index layer, and a low refractive index layer on the protective film. An antireflection layer laminated in order is preferably used. Preferred examples thereof are described below.

A preferred example of an antireflection layer in which a light scattering layer and a low refractive index layer are provided on a protective film will be described.
It is preferable that mat particles are dispersed in the light scattering layer, and the refractive index of the material other than the mat particles in the light scattering layer is preferably in the range of 1.50 to 2.00. The refractive index of the low refractive index layer is preferably in the range of 1.20 to 1.49. In the present invention, the light scattering layer has both antiglare properties and hard coat properties, and may be a single layer or a plurality of layers, for example, 2 to 4 layers.

The antireflection layer has an uneven surface shape with a center line average roughness Ra of 0.08 to 0.40 μm, a 10-point average roughness Rz of 10 times or less of Ra, an average mountain valley distance Sm of 1 to 100 μm, and an uneven depth. Designed so that the standard deviation of the height of the convex part from the part is 0.5 μm or less, the standard deviation of the average mountain valley distance Sm with respect to the center line is 20 μm or less, and the surface with the inclination angle of 0 to 5 degrees is 10% or more. By doing so, sufficient anti-glare properties and a visually uniform matte feeling are achieved, which is preferable. In addition, the ratio of the minimum value and the maximum value of the reflectance in the range of a ^* value −2 to 2, b ^* value −3 to 3, and 380 nm to 780 nm is 0. By being 5-0.99, the color of reflected light becomes neutral, which is preferable. Moreover, by setting the b ^* value of the transmitted light under the C light source to 0 to 3, the yellow color of white display when applied to a display device is reduced, which is preferable. In addition, when a 120 μm × 40 μm grid is inserted between the surface light source and the antireflection film of the present invention and the luminance distribution is measured on the film, the standard deviation of the luminance distribution is 20 or less. The glare when applying the film of the present invention is reduced, which is preferable.

  The antireflection layer that can be used in the present invention preferably has, as its optical characteristics, a specular reflectance of 2.5% or less, a transmittance of 90% or more, and a 60 ° gloss of 70% or less. By doing in this way, reflection of external light can be suppressed and visibility improves. In particular, the specular reflectance is more preferably 1% or less, and most preferably 0.5% or less. Haze 20% to 50%, internal haze / total haze value 0.3 to 1, haze value after formation of low refractive index layer from haze value to light scattering layer within 15%, comb width at 0.5 mm Transmission image clarity 20% to 50%, vertical transmission light / transmittance ratio of 2 degrees from vertical to 1.5 to 5.0 prevents glare on high-definition LCD panels, characters, etc. Reduction of blur is achieved, which is preferable.

[Low refractive index layer]
The low refractive index layer in the antireflection layer in which at least a light scattering layer and a low refractive index layer are laminated in this order on the protective film is described below.
The refractive index of the low refractive index layer is preferably 1.20 to 1.49, more preferably 1.30 to 1.44. Furthermore, the low refractive index layer preferably satisfies the following formula (XV) from the viewpoint of reducing the reflectance.
Formula (XV): (m / 4) × 0.7 <n1d1 <(m / 4) × 1.3
In the formula, m is a positive odd number, n1 is the refractive index of the low refractive index layer, and d1 is the film thickness (nm) of the low refractive index layer. Further, λ is a wavelength, which is a value in the range of 500 to 550 nm.

The material for forming the low refractive index layer will be described below.
The low refractive index layer preferably contains a fluorine-containing polymer as a low refractive index binder. The fluorine polymer is preferably a fluorine-containing polymer that is crosslinked by heat or ionizing radiation having a coefficient of dynamic friction of 0.03 to 0.20, a contact angle with water of 90 to 120 °, and a sliding angle of pure water of 70 ° or less. When the polarizing plate of the present invention is mounted on an image display device, the lower the peel strength from a commercially available adhesive tape, the easier it is to peel off after sticking a sticker or memo, preferably 500 gf or less when measured with a tensile tester. 300 gf or less is more preferable, and 100 gf or less is most preferable. Further, the higher the surface hardness measured with a microhardness meter, the harder it is to scratch, preferably 0.3 GPa or more, more preferably 0.5 GPa or more.

  Examples of the fluorine-containing polymer used in the low refractive index layer include hydrolysis and dehydration condensate of perfluoroalkyl group-containing silane compounds (for example, (heptadecafluoro-1,1,2,2-tetrahydrodecyl) triethoxysilane). And a fluorine-containing copolymer having a fluorine-containing monomer unit and a structural unit for imparting crosslinking reactivity as structural components.

  Specific examples of the monomer that forms the fluorinated monomer unit that is a constituent of the fluorinated copolymer include, for example, fluoroolefins (for example, fluoroethylene, vinylidene fluoride, tetrafluoroethylene, perfluorooctylethylene, hexafluoropropylene, Perfluoro-2,2-dimethyl-1,3-dioxole, etc.), a part of (meth) acrylic acid or a fully fluorinated alkyl ester derivative (for example, Biscoat 6FM (manufactured by Osaka Organic Chemicals) or M-2020 (manufactured by Daikin) Etc.), fully or partially fluorinated vinyl ethers, and the like, preferably perfluoroolefins, and particularly preferably hexafluoropropylene from the viewpoints of refractive index, solubility, transparency, availability, and the like.

  As structural units for imparting crosslinking reactivity, structural units obtained by polymerization of monomers having a self-crosslinkable functional group in the molecule in advance such as glycidyl (meth) acrylate and glycidyl vinyl ether, carboxyl groups, hydroxy groups, amino acids Polymerization of monomers having a group, a sulfo group, etc. (eg (meth) acrylic acid, methylol (meth) acrylate, hydroxyalkyl (meth) acrylate, allyl acrylate, hydroxyethyl vinyl ether, hydroxybutyl vinyl ether, maleic acid, crotonic acid, etc.) The resulting structural unit, a structural unit in which a crosslinking reactive group such as a (meth) acryloyl group is introduced into these structural units by a polymer reaction (for example, an acrylic acid chloride is allowed to act on a hydroxy group). And the like.

  In addition to the above-mentioned fluorine-containing monomer units and structural units for imparting crosslinking reactivity, monomers not containing fluorine atoms can be copolymerized as appropriate from the viewpoints of solubility in solvents and film transparency. The monomer that can be used in combination is not particularly limited. For example, olefins (ethylene, propylene, isoprene, vinyl chloride, vinylidene chloride, etc.), acrylic esters (methyl acrylate, methyl acrylate, ethyl acrylate, 2-acrylic acid 2- Ethyl hexyl), methacrylates (methyl methacrylate, ethyl methacrylate, butyl methacrylate, ethylene glycol dimethacrylate, etc.), styrene derivatives (styrene, divinylbenzene, vinyl toluene, α-methylstyrene, etc.), vinyl ethers (methyl vinyl ether) , Ethyl vinyl ether, cyclohexyl vinyl ether, etc.), vinyl esters (vinyl acetate, vinyl propionate, vinyl cinnamate etc.), acrylamides (N-tert-butylacrylamide, N-cycl) Hexyl acrylamide), methacrylamides, and acrylonitrile derivatives.

  As described in JP-A-10-25388 and JP-A-10-147739, a curing agent may be appropriately used in combination with the above polymer.

[Light scattering layer]
The light scattering layer is formed for the purpose of contributing to the film light diffusibility due to at least one of surface scattering and internal scattering and hard coat properties for improving the scratch resistance of the film. Therefore, it is formed to contain a binder for imparting hard coat properties, matte particles for imparting light diffusibility, and inorganic fillers for increasing the refractive index, preventing cross-linking shrinkage, and increasing the strength as necessary. The Further, by providing such a light scattering layer, the light scattering layer also functions as an antiglare layer, and the polarizing plate has an antiglare layer.

  The thickness of the light scattering layer is preferably 1 to 10 μm and more preferably 1.2 to 6 μm for the purpose of imparting hard coat properties. If it is too thin, the hard property will be insufficient, and if it is too thick, curling and brittleness will deteriorate and the workability will be insufficient.

  The binder of the light scattering layer is preferably a polymer having a saturated hydrocarbon chain or a polyether chain as the main chain, and more preferably a polymer having a saturated hydrocarbon chain as the main chain. The binder polymer preferably has a crosslinked structure. As the binder polymer having a saturated hydrocarbon chain as a main chain, a polymer of an ethylenically unsaturated monomer is preferable. As the binder polymer having a saturated hydrocarbon chain as the main chain and having a crosslinked structure, a (co) polymer of monomers having two or more ethylenically unsaturated groups is preferable. In order to make the binder polymer have a high refractive index, the monomer structure contains an aromatic ring or at least one atom selected from halogen atoms other than fluorine, sulfur atoms, phosphorus atoms, and nitrogen atoms. You can also choose.

  Examples of the monomer having two or more ethylenically unsaturated groups include esters of polyhydric alcohol and (meth) acrylic acid (eg, ethylene glycol di (meth) acrylate, butanediol di (meth) acrylate, hexanediol di ( (Meth) acrylate, 1,4-cyclohexanediacrylate, pentaerythritol tetra (meth) acrylate), pentaerythritol tri (meth) acrylate, trimethylolpropane tri (meth) acrylate, trimethylolethane tri (meth) acrylate, dipentaerythritol Tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, pentaerythritol hexa (meth) acrylate, 1,2,3-si Rhohexanetetramethacrylate, polyurethane polyacrylate, polyester polyacrylate), modified ethylene oxide, vinylbenzene and derivatives thereof (eg, 1,4-divinylbenzene, 4-vinylbenzoic acid-2-acryloylethyl ester, 1, 4-divinylcyclohexanone), vinyl sulfone (eg, divinyl sulfone), acrylamide (eg, methylenebisacrylamide) and methacrylamide. Two or more of these monomers may be used in combination.

Specific examples of the high refractive index monomer include bis (4-methacryloylthiophenyl) sulfide, vinyl naphthalene, vinyl phenyl sulfide, 4-methacryloxyphenyl-4′-methoxyphenyl thioether, and the like. Two or more of these monomers may be used in combination.

Polymerization of the monomer having an ethylenically unsaturated group can be performed by irradiation with ionizing radiation or heating in the presence of a photo radical initiator or a thermal radical initiator.
Therefore, a coating liquid containing a monomer having an ethylenically unsaturated group, a photo radical initiator or a thermal radical initiator, mat particles, and an inorganic filler is prepared, and the coating liquid is applied onto a protective film and then ionizing radiation or heat. It can be cured by a polymerization reaction to form an antireflection film. As these photo radical initiators, known ones can be used.

The polymer having a polyether as the main chain is preferably a ring-opening polymer of a polyfunctional epoxy compound. The ring-opening polymerization of the polyfunctional epoxy compound can be performed by irradiation with ionizing radiation or heating in the presence of a photoacid generator or a thermal acid generator.
Therefore, a coating solution containing a polyfunctional epoxy compound, a photoacid generator or a thermal acid generator, matte particles and an inorganic filler is prepared, and the coating solution is applied on a protective film and then cured by ionizing radiation or heat polymerization reaction. Thus, an antireflection film can be formed.

Instead of or in addition to a monomer having two or more ethylenically unsaturated groups, a monomer having a crosslinkable functional group is used to introduce a crosslinkable functional group into the polymer, and by reaction of this crosslinkable functional group, A crosslinked structure may be introduced into the binder polymer.
Examples of the crosslinkable functional group include isocyanate group, epoxy group, aziridine group, oxazoline group, aldehyde group, carbonyl group, hydrazine group, carboxyl group, methylol group and active methylene group. Vinylsulfonic acid, acid anhydride, cyanoacrylate derivative, melamine, etherified methylol, ester and urethane, and metal alkoxide such as tetramethoxysilane can also be used as a monomer for introducing a crosslinked structure. A functional group that exhibits crosslinkability as a result of the decomposition reaction, such as a block isocyanate group, may be used. That is, in the present invention, the crosslinkable functional group may not react immediately but may exhibit reactivity as a result of decomposition.
These binder polymers having a crosslinkable functional group can form a crosslinked structure by heating after coating.

For the purpose of imparting antiglare properties, the light scattering layer contains matte particles having an average particle size of 1 to 10 μm, preferably 1.5 to 7.0 μm, such as inorganic compound particles or resin particles, for the purpose of imparting antiglare properties. Is done.
As specific examples of the mat particles, inorganic particles such as silica particles and TiO ₂ particles; resin particles such as acrylic particles, cross-linked acrylic particles, polystyrene particles, cross-linked styrene particles, melamine resin particles, and benzoguanamine resin particles are preferable. Can be mentioned. Of these, crosslinked styrene particles, crosslinked acrylic particles, crosslinked acrylic styrene particles, and silica particles are preferable. The shape of the mat particles can be either spherical or irregular.

  Two or more kinds of mat particles having different particle diameters may be used in combination. It is possible to impart anti-glare properties with mat particles having a larger particle size and to impart other optical characteristics with mat particles having a smaller particle size.

  Furthermore, the particle size distribution of the mat particles is most preferably monodisperse, and the particle sizes of the particles are preferably closer to each other. For example, when particles having a particle size of 20% or more than the average particle size are defined as coarse particles, the proportion of coarse particles is preferably 1% or less of the total number of particles, more preferably 0.1%. Or less, more preferably 0.01% or less. Matt particles having such a particle size distribution are obtained by classification after a normal synthesis reaction, and a matting agent having a more preferable distribution can be obtained by increasing the number of classifications or increasing the degree of classification.

The mat particles are contained in the light scattering layer so that the amount of mat particles in the formed light scattering layer is preferably 10 to 1000 mg / m ² , more preferably 100 to 700 mg / m ² .
The particle size distribution of the mat particles is measured by a Coulter counter method, and the measured distribution is converted into a particle number distribution.

The light scattering layer is made of an oxide of at least one metal selected from titanium, zirconium, aluminum, indium, zinc, tin, and antimony, in addition to the above mat particles, in order to increase the refractive index of the layer. Thus, it is preferable that an inorganic filler having an average particle size of 0.2 μm or less, preferably 0.1 μm or less, more preferably 0.06 μm or less is contained.
Conversely, in order to increase the refractive index difference from the mat particles, it is also preferable to use a silicon oxide in order to keep the refractive index of the layer low in the light scattering layer using the high refractive index mat particles. The preferred particle size is the same as that of the aforementioned inorganic filler.
Specific examples of the inorganic filler to be used in the light scattering _{layer, TiO 2, ZrO 2, Al} 2 O 3, In 2 O 3, ZnO, SnO 2, Sb 2 O 3, ITO and SiO ₂ and the like. TiO ₂ and ZrO ₂ are particularly preferable from the viewpoint of increasing the refractive index. The surface of the inorganic filler is preferably subjected to silane coupling treatment or titanium coupling treatment, and a surface treatment agent having a functional group capable of reacting with a binder species on the filler surface is preferably used.
The amount of these inorganic fillers added is preferably 10 to 90% of the total mass of the light scattering layer, more preferably 20 to 80%, and particularly preferably 30 to 75%.
In addition, since such a filler has a particle size sufficiently smaller than the wavelength of light, scattering does not occur, and a dispersion in which the filler is dispersed in a binder polymer behaves as an optically uniform substance.

  The bulk refractive index of the mixture of binder and inorganic filler in the light scattering layer is preferably 1.50 to 2.00, more preferably 1.51 to 1.80. In order to make the refractive index within the above range, the type and amount ratio of the binder and the inorganic filler may be appropriately selected. How to select can be easily known experimentally in advance.

  In order to ensure surface uniformity such as uneven coating, uneven drying, point defects, etc., the light scattering layer should be coated with either a fluorine-based surfactant or a silicone-based surfactant, or both for forming the light scattering layer. Contained in the composition. In particular, a fluorine-based surfactant is preferably used because an effect of improving surface defects such as coating unevenness, drying unevenness, and point defects of the antireflection film appears with a smaller addition amount. The purpose is to increase productivity by giving high-speed coating suitability while improving surface uniformity.

Next, an antireflection layer in which a middle refractive index layer, a high refractive index layer, and a low refractive index layer are laminated in this order on the protective film will be described.
The antireflection layer comprising at least a middle refractive index layer, a high refractive index layer, and a low refractive index layer (outermost layer) in order on the protective film is designed to have a refractive index satisfying the following relationship. .
High refractive index layer refractive index> Medium refractive index layer refractive index> Protective film refractive index> Low refractive index layer refractive index A hard coat layer may be provided between the protective film and the medium refractive index layer. . Furthermore, it may consist of a medium refractive index hard coat layer, a high refractive index layer and a low refractive index layer.
Examples thereof include antireflection layers described in JP-A-8-122504, JP-A-8-110401, JP-A-10-300902, JP-A-2002-243906, JP-A-2000-11706, and the like.
Other functions may be imparted to each layer, for example, an antifouling low refractive index layer or an antistatic high refractive index layer (eg, JP-A-10-206603, JP-A-2002). -243906 publication etc.) etc. are mentioned.
The haze of the antireflection layer is preferably 5% or less, more preferably 3% or less. The strength of the film is preferably H or higher, more preferably 2H or higher, and most preferably 3H or higher in a pencil hardness test according to JIS K5400.

[High refractive index layer and medium refractive index layer]
The layer having a high refractive index of the antireflection layer is composed of a cured film containing at least an inorganic compound fine particle having a high refractive index having an average particle diameter of 100 nm or less and a matrix binder.
Examples of the high refractive index inorganic compound fine particles include inorganic compound fine particles having a refractive index of 1.65 or more, preferably those having a refractive index of 1.9 or more. Examples thereof include fine particles such as oxides such as Ti, Zn, Sb, Sn, Zr, Ce, Ta, La, and In, and composite oxides containing these metal atoms.
In order to obtain fine particles having an average particle size of 100 nm or less, the surface of the particles is treated with a surface treatment agent (for example, silane coupling agents, etc .: JP-A Nos. 1-295503, 11-153703, and 2000). No.-9908, an anionic compound or an organometallic coupling agent: Japanese Patent Laid-Open No. 2001-310432, etc., and a core-shell structure with high refractive index particles as a core (eg, Japanese Patent Laid-Open No. 2001-166104) ), Specific dispersants (for example, JP-A No. 11-153703, US Pat. No. 6,210,858B1, JP-A No. 2002-276069) and the like.
Examples of the material forming the matrix include conventionally known thermoplastic resins and curable resin films.
Furthermore, from a polyfunctional compound-containing composition containing two or more polymerizable groups of at least one of radically polymerizable and cationically polymerizable, an organometallic compound containing a hydrolyzable group, and a partial condensate-containing composition thereof At least one composition selected is preferred. For example, the composition as described in Unexamined-Japanese-Patent No. 2000-47004, 2001-315242, 2001-31871, 2001-296401 etc. is mentioned.
A curable film obtained from a colloidal metal oxide obtained from a hydrolyzed condensate of metal alkoxide and a metal alkoxide composition is also preferred. For example, it describes in Unexamined-Japanese-Patent No. 2001-293818.
The refractive index of the high refractive index layer is preferably 1.70 to 2.20. The thickness of the high refractive index layer is preferably 5 nm to 10 μm, and more preferably 10 nm to 1 μm.
The refractive index of the middle refractive index layer is adjusted to be a value between the refractive index of the low refractive index layer and the refractive index of the high refractive index layer. The refractive index of the middle refractive index layer is preferably 1.50 to 1.70. The thickness is preferably 5 nm to 10 μm, and more preferably 10 nm to 1 μm.

[Low refractive index layer]
Next, the low refractive index layer in the antireflection layer in which the middle refractive index layer, the high refractive index layer, and the low refractive index layer are laminated in this order on the protective film will be described.
The low refractive index layer is formed by sequentially laminating on the high refractive index layer. The refractive index of the low refractive index layer is preferably 1.20 to 1.55. More preferably, it is 1.30-1.50.
It is preferable to construct as the outermost layer having scratch resistance and antifouling property. As means for greatly improving the scratch resistance, it is effective to impart slipperiness to the surface, and conventionally known thin film layer means such as introduction of silicone or introduction of fluorine can be applied.
The fluorine-containing compound is preferably a compound containing a crosslinkable or polymerizable functional group containing fluorine atoms in the range of 35 to 80% by mass.
For example, paragraph numbers [0018] to [0026] of Japanese Patent Application Laid-Open No. 9-222503, paragraph numbers [0019] to [0030] of Japanese Patent Application Laid-Open No. 11-38202, and paragraph numbers of Japanese Patent Application Laid-Open No. 2001-40284. [0027] to [0028], compounds described in JP-A No. 2000-284102, and the like.
The refractive index of the fluorine-containing compound is preferably 1.35 to 1.50. More preferably, it is 1.36-1.47.
The silicone compound is a compound having a polysiloxane structure, preferably containing a curable functional group or a polymerizable functional group in the polymer chain and having a crosslinked structure in the film. For example, reactive silicone (eg, Silaplane (manufactured by Chisso Corporation), silanol group-containing polysiloxane (Japanese Patent Laid-Open No. 11-258403, etc.) and the like can be mentioned.
The crosslinking or polymerization reaction of at least one of a fluorine-containing polymer having a crosslinking or polymerizable group and a siloxane polymer is performed by applying a coating composition for forming an outermost layer containing a polymerization initiator, a sensitizer and the like. It is preferable to form the low refractive index layer by light irradiation or heating simultaneously or after coating.

Also preferred is a sol-gel cured film in which an organometallic compound such as a silane coupling agent and a specific fluorine-containing hydrocarbon group-containing silane coupling agent are cured by a condensation reaction in the presence of a catalyst.
For example, a polyfluoroalkyl group-containing silane compound or a partially hydrolyzed condensate thereof (Japanese Patent Laid-Open Nos. 58-142958, 58-147483, 58-147484, Japanese Patent Laid-Open Nos. 9-157582, 11) -106704), silyl compounds containing a poly "perfluoroalkyl ether" group which is a fluorine-containing long chain group (Japanese Patent Application Laid-Open Nos. 2000-117902, 2001-48590, 2002) 53804), and the like.

The low refractive index layer has an average primary particle diameter of 1 to 150 nm such as a filler (for example, silicon dioxide (silica), fluorine-containing particles (magnesium fluoride, calcium fluoride, barium fluoride)) as an additive other than the above. A low refractive index inorganic compound, organic fine particles described in paragraphs [0020] to [0038] of JP-A-11-3820), silane coupling agents, slip agents, surfactants, and the like.
When the low refractive index layer is located below the outermost layer, the low refractive index layer may be formed by a vapor phase method (vacuum deposition method, sputtering method, ion plating method, plasma CVD method, etc.). The coating method is preferable because it can be manufactured at a low cost.
The film thickness of the low refractive index layer is preferably 30 to 200 nm, more preferably 50 to 150 nm, and most preferably 60 to 120 nm.

[Hard coat layer]
The hard coat layer is provided on the surface of the protective film in order to impart physical strength to the protective film provided with the antireflection layer. In particular, it is preferably provided between the transparent support and the high refractive index layer. The hard coat layer is preferably formed by a crosslinking reaction or a polymerization reaction of the curable compound by at least one of light and heat. The curable functional group in the curable compound is preferably a photopolymerizable functional group. Also preferred are hydrolyzable functional group-containing organometallic compounds and organoalkoxysilyl compounds.
Specific examples of these compounds are the same as those exemplified for the high refractive index layer. Specific examples of the constituent composition of the hard coat layer include those described in JP-A Nos. 2002-144913, 2000-9908, and WO00 / 46617.
The high refractive index layer can also serve as a hard coat layer. In such a case, it is preferable to form fine particles dispersed in the hard coat layer using the method described for the high refractive index layer.

The hard coat layer can also serve as an antiglare layer containing particles having an average particle size of 0.2 to 10 μm and imparted with an antiglare function (antiglare function).
The film thickness of the hard coat layer can be appropriately designed depending on the application. The film thickness of the hard coat layer is preferably 0.2 to 10 μm, more preferably 0.5 to 7 μm.
The strength of the hard coat layer is preferably H or higher, more preferably 2H or higher, and most preferably 3H or higher in a pencil hardness test according to JIS K5400. Further, in the Taber test according to JIS K5400, the smaller the wear amount of the test piece before and after the test, the better.

[Other layers of antireflection layer]
Further, a forward scattering layer, a primer layer, an antistatic layer, an undercoat layer, a protective layer, and the like may be provided.

[Antistatic layer]
In the case of providing an antistatic layer, it is preferable to impart conductivity with a volume resistivity of 10 ⁻⁸ (Ωcm ⁻³ ) or less. The use of hygroscopic substances, water-soluble inorganic salts, certain surfactants, cationic polymers, anionic polymers, colloidal silica, etc. can give a volume resistivity of 10 ⁻⁸ (Ωcm ⁻³ ). There is a problem that dependency is large, and sufficient conductivity cannot be secured at low humidity. Therefore, a metal oxide is preferable as the conductive layer material. Some metal oxides are colored, but using such metal oxides as the conductive layer material is not preferable because the entire film is colored. Zn, Ti, Al, In, Si, Mg, Ba, Mo, W, or V can be given as the metal that forms the metal oxide without coloration, and a metal oxide mainly composed of this can be used. preferable. As specific examples, ZnO, TiO ₂ , SnO ₂ , Al ₂ O ₃ , In ₂ O ₃ , SiO ₂ , MgO, BaO, MoO ₃ , V ₂ O _5, or a composite oxide thereof is particularly preferable. ZnO, TiO ₂ and SnO ₂ are preferred. Examples of containing different atoms include, for example, additives such as Al and In for ZnO, addition of Sb, Nb and halogen elements for SnO ₂ , and addition of Nb and TA for TiO ₂ . Addition is effective. Furthermore, as described in Japanese Examined Patent Publication No. 59-6235, a material in which the above metal oxide is attached to other crystalline metal particles or fibrous materials (for example, titanium oxide) may be used. The volume resistivity and surface resistivity can not be compared simply a different physical property values, in order to ensure a 10 ^-8 (Ωcm ^-3) or less of the conductive volume resistivity value, the charging The prevention layer should just have a surface resistance value of 10 ⁻¹⁰ (Ω / □) or less, more preferably 10 ⁻⁸ (Ω / □) or less. The surface resistance value of the antistatic layer is a value obtained when the antistatic layer is the outermost layer, and can be measured in the middle of forming the antistatic layer.

[Liquid Crystal Display]
The liquid crystal display device of the present invention is a cellulose acylate film obtained by the production method of the present invention or a liquid crystal display device having the polarizing plate of the present invention (first embodiment), a liquid crystal cell and both sides of the liquid crystal cell. A liquid crystal display device having a pair of polarizing plates, wherein the polarizing plate is the polarizing plate of the present invention, and an OCB or VA mode liquid crystal display device (second embodiment), and the polarizing plate of the present invention as a back It is a VA mode liquid crystal display device (third embodiment) used on the light side.
The polarizing plate of the present invention can be used for liquid crystal cells in various display modes. TN (Twisted Nematic), IPS (In-Plane Switching), FLC (Ferroelectric Liquid Crystal), AFLC (Anti-ferroelectric Liquid Crystal), OCB (Optically Compensatory Bend), STN (Supper Twisted Nematic), VA (Vertically Aligned) and HAN Various display modes such as (Hybrid Aligned Nematic) have been proposed. Among these, it can use preferably for VA mode or OCB mode.

In a VA mode liquid crystal cell, rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied.
The VA mode liquid crystal cell includes (1) a narrowly defined VA mode liquid crystal cell in which rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied, and substantially horizontally when a voltage is applied (Japanese Patent Laid-Open No. Hei 2-). 176625) (2) Liquid crystal cell (SID97, Digest of tech. Papers (Preliminary Proceed) 28 (1997) 845 in which the VA mode is made into a multi-domain (MVA mode) for widening the viewing angle ), (3) Liquid crystal cell in a mode (n-ASM mode) in which rod-like liquid crystalline molecules are substantially vertically aligned when no voltage is applied and twisted multi-domain alignment is applied when a voltage is applied (Preliminary collections 58-59 of the Japanese Liquid Crystal Society) (1998)) and (4) SURVAVAL mode liquid crystal cells (announced at LCD International 98).
As a VA mode liquid crystal display device, as shown in FIG. 3, a liquid crystal cell (VA mode cell) and one comprising two polarizing plates arranged on both sides thereof can be mentioned. The liquid crystal cell carries liquid crystal between two electrode substrates, although not particularly shown.

  In the liquid crystal display device of the present invention, the cellulose acylate film obtained by the production method of the present invention can be used as a protective film for the polarizing plate disposed between the liquid crystal cell and the polarizing film. The cellulose acylate film obtained by the production method of the present invention may be used only for the protective film (between the liquid crystal cell and the polarizing film) of one polarizing plate, or (the liquid crystal cell and the liquid crystal cell of both polarizing plates). The cellulose acylate film obtained by the production method of the present invention may be used for the two protective films (between the polarizing films). When the cellulose acylate film obtained by the production method of the present invention is used only for the protective film (between the liquid crystal cell and the polarizing film) of one polarizing plate, this is the upper polarizing plate (observation side), the lower side Either side of the polarizing plate (backlight side) may be used and there is no functional problem. However, when used as an upper polarizing plate, it is necessary to provide a functional film on the observation side (upper side), and the production yield may be lowered. It is considered an embodiment.

And what formed both the light source side and observer side of FIG. 3 with the polarizing plate of this invention is the liquid crystal display device of a 2nd form, and what formed only the light source side with the polarizing plate of this invention is 3rd. It is a liquid crystal display device of a form.
The protective film other than the protective film made of the cellulose acylate film obtained by the production method of the present invention may be a normal cellyl acylate film. The film thickness is preferably 40 to 80 μm. Examples of commercially available products include, but are not limited to, KC4UX2M (40 μm manufactured by Konica Caputo), KC5UX (60 μm manufactured by Konica Caputo), TD80 (80 μm manufactured by Fuji Photo Film), and the like.

  The features of the present invention will be described more specifically with reference to examples and comparative examples. The materials, amounts used, ratios, processing details, processing procedures, and the like shown in the following examples can be changed as appropriate without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be construed as being limited by the specific examples shown below.

[Example 1]
Formation of cellulose acylate film (1) Cellulose acylate Cellulose triacetate (cellulose ester derivative having an acyl group consisting only of an acetate group) and an acetyl group substitution degree of 2.82, DS6 / (DS2 + DS3 + DS6) = 0.321 Cellulose acylate was prepared. In this, sulfuric acid (7.8 parts by mass with respect to 100 parts by mass of cellulose) was added as a catalyst, and a carboxylic acid serving as a raw material for the acetyl substituent was added to carry out an acylation reaction at 40 ° C. At this time, the substitution degree of the acyl group was adjusted by adjusting the amount of carboxylic acid. Moreover, it age | cure | ripened at 40 degreeC after acylation. Further, the low molecular weight component of the cellulose acylate was removed by washing with acetone.

(2) Dope Preparation <1-1> Cellulose Acylate Solution The following composition is put into a mixing tank, stirred to dissolve each component, further heated to 90 ° C. for about 10 minutes, and then a filter paper having an average pore size of 34 μm and It filtered with the sintered metal filter with an average hole diameter of 10 micrometers.
―――――――――――――――――――――――――――――――――
Cellulose acylate solution ――――――――――――――――――――――――――――――――――
Cellulose acylate 100.0 parts by mass Triphenyl phosphate 8.0 parts by mass Biphenyl diphenyl phosphate 4.0 parts by mass Methylene chloride 403.0 parts by mass Methanol 60.2 parts by mass ――――――――――― ――――――――――――――――――――――

<1-2> Matting Agent Dispersion Solution Next, the following composition containing the cellulose acylate solution prepared by the above method was charged into a dispersing machine to prepare a matting agent dispersion.
―――――――――――――――――――――――――――――――――
Matting agent dispersion ―――――――――――――――――――――――――――――――――
Silica particles having an average particle size of 16 nm (Aerosil R972, manufactured by Nippon Aerosil Co., Ltd. 2.0 parts by mass methylene chloride 72.4 parts by mass methanol 10.8 parts by mass cellulose acylate solution 10.3 parts by mass ――――――――――――――――――――――――――
<1-3> Retardation developer solution Next, the following composition containing the cellulose acylate solution prepared by the above method is charged into a mixing tank and dissolved by stirring while heating to prepare retardation developer solution A. did.
―――――――――――――――――――――――――――――――――
Retardation developer solution ―――――――――――――――――――――――――――――――――
Retardation developer A 20.0 parts by mass Methylene chloride 58.3 parts by mass Methanol 8.7 parts by mass Cellulose acylate solution 12.8 parts by mass ――――――――――――――――― ―――――――――――――――
100 parts by mass of the cellulose acylate solution, 1.35 parts by mass of the matting agent dispersion, and a retardation developer solution in an amount such that the amount of retardation developer A in the cellulose acylate film is 5.1 parts by mass. The dope for film formation was prepared by mixing. The addition ratio of the retardation enhancer is shown in parts by mass when the cellulose acylate amount is 100 parts by mass.

(Casting)
The above dope was cast using a band casting machine. The film peeled off from the band with a residual solvent amount of 25 to 35% by mass is supplied in the tenter zone at an air supply temperature of 140 ° C. (exhaust temperature is in the range of 90 ° C. to 125 ° C.) at a draw ratio of 25%. And a cellulose acylate film having a thickness of 92 μm was produced. The cast film thickness was adjusted so that the film thickness after stretching was 92 μm. Re and Rth of the produced cellulose acylate film were measured and are shown in Table 1.

[Examples 2 to 4, Comparative Examples 1 to 3]
A cellulose acylate film was produced in the same manner as in Example 1 except that the type and amount of the retardation developer were changed as shown in Table 1. The powder physical properties of the retardation developer were controlled by a combination of pulverization, classification, sieving, and mixing.

[Measurement method of front retardation Re and retardation Rth in film thickness direction]
A sample 30 mm x 40 mm was conditioned at 25 ° C and 60% RH for 2 hours. Re (λ) is an automatic birefringence meter KOBRA 21ADH (manufactured by Oji Scientific Instruments). Measured by incidence. Rth (λ) is Re (λ), a retardation value measured by making light of wavelength λnm incident from a direction inclined + 40 ° with respect to the film normal direction with the in-plane slow axis as the tilt axis, And the retardation value measured in three directions, that is, the retardation value measured by making light of wavelength λ nm incident from the direction inclined −40 ° with respect to the film normal direction with the in-plane slow axis as the tilt axis. On the basis of the cellulose acylate film, an assumed average refractive index of 1.48 and a film thickness were input and calculated.

[Measurement of powder properties]
(1) Angle of repose At 25 ° C and 50% RH, set the angle of repose unit on the multi tester MT-1001 manufactured by Seishin Co., Ltd., set the sample on the upper sieve and start the feeder. I read the angle. Next, the angle of repose table was rotated to read three angles, and the arithmetic average was defined as the angle of repose.
(2) Compressibility At 25 ° C. and 50% RH, a cell for compressibility measurement was set in the multi tester MT-1001 manufactured by Seishin Co., Ltd., the sample was set in the upper sieve, the feeder was started, and the sample was filled in the cell. . After filling the sample, an excess sample was scraped off with a scraping plate, the mass was measured with a balance, and the mass of the cell measured in advance was subtracted to obtain the sample volume. The loose bulk density (ρa) was determined from the sample mass and volume.
After measuring the loose bulk density, a cell cap was attached, and a sample was further introduced from the upper sieve. Tapping was performed by setting the tapping counter to 180 times. After completion of tapping, an excess sample was scraped off with a scraping plate and the mass was measured with a balance. The bulk density (ρp) was determined from the mass and volume of the sample obtained by subtracting the mass of the cell from this mass.
The degree of compression (Cp) was calculated from the following formula.
Cp = (ρp−ρa) / ρa × 100
(3) Spatula Angle At 25 ° C. and 50% RH, a spatula angle measurement unit was set on a multi-tester MT-1001 manufactured by Seishin Co., Ltd., the spatula was lowered, and a sample was poured from above. Subsequently, the spatula was lifted upward and the angle θ ₁ of the spatula peak was measured at three locations. The weight attached to the spatula angle measurement unit was dropped once to measure the three angles θ ₂ of the spatula peaks, and the average value of θ ₁ and θ ₂ was defined as the spatula angle.
(4) Aggregation degree At 25 ° C. and 50% RH, a 2 g sample was placed on the standard sieve of Multitester MT-1001 manufactured by Seishin Co., Ltd., vibrated for a certain period of time, and the aggregation degree was determined from the passing amount of the sample. The vibration time, selection of sieves, and calculation of the degree of aggregation were in accordance with the description on pages 66 to 67 of “Introduction to Revision Supplementary Powder Trouble Optics” (published by Kogyo Kenkyukai).

[Surface evaluation]
The surface of the cellulose acylate film was visually observed to evaluate the film surface shape.
○: good surface shape by visual inspection (no streaks or irregularities on the surface)
○ △: Slight streak-like failure is observed by visual inspection (acceptable)
×: Remarkable streak-like failure is observed by visual inspection (unacceptable)

The results are shown in Table 1.

  As shown in Table 1, a cellulose acylate film having a good surface shape and high retardation can be obtained by using a retardation enhancer having predetermined powder properties.

<Preparation of polarizing plate>
A polarizing film was prepared by adsorbing iodine to a stretched polyvinyl alcohol film.
The cellulose acylate films prepared in Examples 1 to 4 were attached to one side of the polarizing film using a polyvinyl alcohol adhesive. The saponification treatment was performed under the following conditions.
A 1.5 mol / liter aqueous sodium hydroxide solution was prepared and kept at 55 ° C. A 0.01 mol / liter dilute sulfuric acid aqueous solution was prepared and kept at 35 ° C. The produced cellulose acylate film was immersed in the aqueous sodium hydroxide solution for 2 minutes, and then immersed in water to sufficiently wash away the aqueous sodium hydroxide solution. Subsequently, after being immersed in the above-mentioned dilute sulfuric acid aqueous solution for 1 minute, it was immersed in water to sufficiently wash away the dilute sulfuric acid aqueous solution. Finally, the sample was thoroughly dried at 120 ° C.
A commercially available cellulose triacylate film (Fujitac TD80UF, manufactured by Fuji Photo Film Co., Ltd.) is saponified, and is attached to the opposite side of the polarizer using a polyvinyl alcohol adhesive, and at 70 ° C. for 10 minutes or more. Dried.
It arrange | positioned so that the transmission axis of a polarizing film and the slow axis of the cellulose acylate film produced as mentioned above might become parallel (FIG. 1). The transmission axis of the polarizing film and the slow axis of a commercially available cellulose triacylate film were arranged so as to be orthogonal.

<Production of liquid crystal cell>
The liquid crystal cell has a cell gap between substrates of 3.6 μm, and a liquid crystal material having negative dielectric anisotropy (“MLC6608”, manufactured by Merck & Co., Inc.) is dropped and sealed between the substrates. Prepared by forming a layer. The retardation of the liquid crystal layer (that is, the product Δn · d of the thickness d (μm) of the liquid crystal layer and the refractive index anisotropy Δn) was set to 300 nm. The liquid crystal material was aligned so as to be vertically aligned.

<Mounting on VA panel>
A commercially available super high contrast product (HLC2-5618 manufactured by Sanlitz Co., Ltd.) was used as the upper polarizing plate (observer side) of the liquid crystal display device (FIG. 3) using the vertical alignment type liquid crystal cell. A polarizing plate provided with the cellulose acylate film prepared in Examples 1 to 4 on the lower polarizing plate (backlight side) so that the cellulose acylate film prepared in Examples 1 to 4 is on the liquid crystal cell side. installed. The upper polarizing plate and the lower polarizing plate were attached to the liquid crystal cell via an adhesive. The crossed Nicols were arranged so that the transmission axis of the upper polarizing plate was in the vertical direction and the transmission axis of the lower polarizing plate was in the left-right direction. As a result of observing the produced liquid crystal display device, a neutral black display was realized in both the front direction and the viewing angle direction.

  According to the present invention, a VA liquid crystal display device having excellent display characteristics and viewing angle characteristics can be provided.

It is a schematic diagram which shows the bonding method of the cellulose acylate film at the time of manufacture of the polarizing plate of this invention. It is sectional drawing which shows typically the cross-section of the polarizing plate of this invention. It is sectional drawing which shows typically the cross-section of the polarizing plate of this invention.

Claims (11)

A method for producing a cellulose acylate film containing a retardation developer,
As the retardation developer, the following powder physical properties:
(1) Angle of repose 55 degrees or less (2) Compressibility 30% or less (3) Spatula angle 75 degrees or less (4) Using a powder satisfying an aggregation degree of 30% or less, the front retardation Re is in the range of 50 to 100 nm. And a cellulose acylate film having a retardation Rth in the film thickness direction of 160 to 300 nm is obtained. The method for producing a cellulose acylate film according to claim 1, further comprising a stretching step of stretching the cellulose acylate film by 10% or more in the film casting direction or the casting width direction. The method for producing a cellulose acylate film according to claim 2, wherein the stretching step is performed by a uniaxial stretching method, a simultaneous biaxial stretching method, or a sequential biaxial stretching method. The manufacturing method of the cellulose acylate film of any one of Claims 1-3 used in the state of the addition liquid which melt | dissolved the said retardation expression agent in the organic solvent. The method for producing a cellulose acylate film according to any one of claims 1 to 4, wherein the retardation enhancer is a rod-like or discotic compound. In the cellulose acylate film, the substitution degree of the hydroxyl group at the 2-position of the glucose unit of the cellulose acylate film by DS2 is DS2, the substitution degree by the acyl group of the hydroxyl group at the 3-position is DS3, and the substitution degree of the hydroxyl group at the 6-position is substituted by the acyl group When the degree is DS6, the following mathematical formulas (VI-a) and (VI-b) are satisfied, and the thermal expansion coefficients D (MD) and D (TD) of the cellulose acylate film satisfy the following mathematical formula (VI). The manufacturing method of the cellulose acylate film of any one of Claims 1-5 satisfy | filled.
Formula (VI-a): 2.0 ≦ DS2 + DS3 + DS6 ≦ 3.0
Formula (VI-b): DS6 / (DS2 + DS3 + DS6) ≧ 0.315
Formula (VI): 1.0 ≦ D (MD) / D (TD) ≦ 3.0 The said cellulose acylate film is a manufacturing method of the cellulose acylate film of any one of Claims 1-6 containing at least 1 sort (s) among a plasticizer, a ultraviolet absorber, and a peeling accelerator. A polarizing plate having a polarizing film and a pair of protective films sandwiching the polarizing film,
A polarizing plate, wherein at least one of the protective films is a cellulose acylate film obtained by the production method according to claim 1. A liquid crystal display device comprising the cellulose acylate film obtained by the production method according to claim 1 or the polarizing plate according to claim 8. A liquid crystal display device having a liquid crystal cell and a pair of polarizing plates disposed on both sides of the liquid crystal cell,
An OCB or VA mode liquid crystal display device, wherein the polarizing plate is the polarizing plate according to claim 8. A VA mode liquid crystal display device using the polarizing plate according to claim 8 on the backlight side.