JP2005350348A - Quick hardening cement concrete and quick setting cement concrete - Google Patents
Quick hardening cement concrete and quick setting cement concrete Download PDFInfo
- Publication number
- JP2005350348A JP2005350348A JP2005167694A JP2005167694A JP2005350348A JP 2005350348 A JP2005350348 A JP 2005350348A JP 2005167694 A JP2005167694 A JP 2005167694A JP 2005167694 A JP2005167694 A JP 2005167694A JP 2005350348 A JP2005350348 A JP 2005350348A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- weight
- cement
- alkali metal
- cement concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、急硬性セメントコンクリート及び急結性セメントコンクリートに関するものである。
なお、本発明でいうセメントコンクリートとは、セメントペースト、モルタル、及びコンクリートを総称する。
The present invention relates to rapid hardening cement concrete and rapid setting cement concrete.
The cement concrete as used in the present invention is a generic term for cement paste, mortar, and concrete.
従来、急硬セメントコンクリートは短時間強度の発現性に優れているので、一般工事、緊急工事、及び止水工事等に使用されている。
一方、山岳トンネル等においては、覆工体を形成すべくセメントコンクリートの打設工事や吹付け工事を行う場合には、当該セメントコンクリートの凝結や硬化を促進させ、強度を早期に発現させる点で、粉体又は液体の急結剤を添加する方法がとられている。
さらに、切羽の外周に沿って形成した掘削溝にセメントコンクリートを充填打設して切羽の前方に覆工体を構築する工法においては、切羽の手前で急硬セメントコンクリートに急結剤を供給することにより、充填打設後に速やかに硬化し、短時間で優れた強度発現性を得ている。
Conventionally, rapid-hardening cement concrete is excellent in short-term strength and has been used for general construction, emergency construction, and water stop construction.
On the other hand, in mountain tunnels, when performing concrete concrete placement work or spray work to form a lining body, it accelerates the setting and hardening of the cement concrete, in order to express the strength early. A method of adding a powder or liquid quick-setting agent is used.
Furthermore, in the construction method in which cement concrete is filled in the excavation groove formed along the outer periphery of the face and a lining body is constructed in front of the face, a rapid setting agent is supplied to the hardened cement concrete before the face. By this, it hardens | cures rapidly after filling casting and has acquired the outstanding strength development property in a short time.
そして、例えば、前記の工法を使用する場合、急硬セメントコンクリートの練混ぜから運搬にかかる時間や現場での段取りや打設にかかる作業時間等を考慮すると、少なくとも90分程度の可使時間が必要となってくる。 And, for example, when using the above-mentioned construction method, taking into consideration the time required for mixing and transporting rapid cement concrete, the work time required for setup and setting on site, etc., the pot life is at least about 90 minutes. It becomes necessary.
しかしながら、生コンプラントやコンクリート工場等で製造された急硬セメントコンクリートは、作業時間（可使時間）をコントロールすることが難しく、現場に到着したときには流動性が著しく損なわれてしまうという課題があった。 However, hard cement concrete produced in ready-mixed concrete plants and concrete factories has a problem that it is difficult to control the working time (usable time) and the fluidity is significantly impaired when it arrives at the site. .
本発明者は種々検討を重ねた結果、特定のスランプ保持材を使用することにより、前記課題が解決できるという知見を得て本発明を完成するに至った。 As a result of various studies, the present inventor has obtained the knowledge that the above problem can be solved by using a specific slump holding material, and has completed the present invention.
本発明は、セメント、カルシウムアルミネート、無機硫酸塩、並びに、アルカリ金属炭酸塩と有機酸類の混合物スラリーであるスランプ保持材を含有してなる急硬性セメントコンクリートであって、カルシウムアルミネートと無機硫酸塩の混合物がセメント100重量部に対して５〜25重量部であり、無機硫酸塩がカルシウムアルミネート100重量部に対して70〜150重量部であり、アルカリ金属炭酸塩と有機酸類の混合物がセメント、カルシウムアルミネート、及び無機硫酸塩の合計100重量部に対して0.1〜1.8重量部であり、アルカリ金属炭酸塩がアルカリ金属炭酸塩と有機酸類の合計100重量部中50〜85重量部であり、アルカリ金属炭酸塩と有機酸類の混合物が水100重量部に対して１〜95重量部である急硬性セメントコンクリートであり、該急硬性セメントコンクリートと急結剤を含有してなる急結性セメントコンクリートであり、急結剤が、セメント100部に対して１〜20重量部である該急結性セメントコンクリートである。 The present invention relates to a cement, calcium aluminate, inorganic sulfate, and a rapid hardening cement concrete containing a slump holding material which is a mixture slurry of an alkali metal carbonate and an organic acid, the calcium aluminate and the inorganic sulfate. The salt mixture is 5 to 25 parts by weight with respect to 100 parts by weight of cement, the inorganic sulfate is 70 to 150 parts by weight with respect to 100 parts by weight of calcium aluminate, and the mixture of alkali metal carbonate and organic acid is 0.1 to 1.8 parts by weight based on 100 parts by weight of cement, calcium aluminate, and inorganic sulfate, and 50 to 85 parts by weight of alkali metal carbonate in 100 parts by weight of alkali metal carbonate and organic acids. There is a rapid hardening cement concrete in which the mixture of alkali metal carbonate and organic acid is 1 to 95 parts by weight with respect to 100 parts by weight of water, and the rapid hardening cement This is a quick setting cement concrete containing a concrete and a quick setting agent, and the quick setting agent is 1 to 20 parts by weight with respect to 100 parts of cement.
本発明の急硬性セメントコンクリートは期待される可使時間が確保できる。又、本発明の急結性セメントコンクリートは初期強度発現性等の機能を効率よく発揮できる。 The rapid-hardening cement concrete of the present invention can ensure the expected pot life. Moreover, the quick setting cement concrete of this invention can exhibit functions, such as initial stage strength development efficiency, efficiently.
以下、本発明をさらに詳しく説明する。
本発明で使用するカルシウムアルミネートとは、カルシアを含む原料と、アルミナを含む原料とを混合して、キルンでの焼成や、電気炉での溶融等の熱処理をして得られる、CaOとAl2O3とを主たる成分とし、水和活性を有する物質の総称であり、CaO及び／又はAl2O3の一部が、アルカリ金属酸化物、アルカリ土類金属酸化物、酸化ケイ素、酸化チタン、酸化鉄、アルカリ金属ハロゲン化物、アルカリ土類金属ハロゲン化物、アルカリ金属硫酸塩、及びアルカリ土類金属硫酸塩等と置換した化合物、あるいは、CaOとAl2O3とを主成分とするものに、これらが少量固溶した物質である。鉱物形態としては、結晶質、非晶質いずれであってもよい。
Hereinafter, the present invention will be described in more detail.
The calcium aluminate used in the present invention is obtained by mixing a raw material containing calcia and a raw material containing alumina, and obtained by heat treatment such as firing in a kiln or melting in an electric furnace. 2 O 3 is a general term for substances that have hydration activity, and a part of CaO and / or Al 2 O 3 is an alkali metal oxide, alkaline earth metal oxide, silicon oxide, titanium oxide , Iron oxide, alkali metal halides, alkaline earth metal halides, alkali metal sulfates, compounds substituted with alkaline earth metal sulfates, etc., or those containing CaO and Al 2 O 3 as main components These are substances in which a small amount is dissolved. The mineral form may be either crystalline or amorphous.
これらの中では、反応活性の点で、12CaO・７Al2O3（以下、C12A7という）組成に対応する熱処理物を急冷した非晶質カルシウムアルミネートが好ましい。 Among these, in view of reaction activity, amorphous calcium aluminate obtained by quenching a heat-treated product corresponding to a composition of 12CaO · 7Al 2 O 3 (hereinafter referred to as C 12 A 7 ) is preferable.
カルシウムアルミネートの粒度は、急結性や初期強度発現性の点で、ブレーン値で4,000cm2/g以上が好ましく、5,000cm2/g以上がより好ましい。4,000cm2/g未満だと急結性や初期強度発現性が低下するおそれがある。 The particle size of the calcium aluminate, in terms of quick-setting property and the initial strength development, preferably 4,000 cm 2 / g or more in Blaine value, 5,000 cm 2 / g or more is more preferable. If it is less than 4,000 cm 2 / g, the quick setting property and the initial strength may be lowered.
本発明で使用する無機硫酸塩としては、硫酸マグネシウム、硫酸カルシウム、硫酸アルミニウム、及び亜硫酸アルミニウム等が挙げられ、これらの１種又は２種以上が使用できる。これらの中では、効果が大きい点で、硫酸カルシウムが好ましい。
硫酸カルシウムとしては、石膏が使用できる。これらの中では、II型無水石膏や天然石膏が好ましい。
Examples of the inorganic sulfate used in the present invention include magnesium sulfate, calcium sulfate, aluminum sulfate, and aluminum sulfite. One or more of these can be used. Among these, calcium sulfate is preferable because of its great effect.
Gypsum can be used as calcium sulfate. Of these, type II anhydrous gypsum and natural gypsum are preferable.
無機硫酸塩の粒度は、ブレーン値で3,000cm2/g以上が好ましく、4,000〜7,000cm2/gがより好ましい。3,000cm2/g未満だと初期強度発現性が低下するおそれがある。 The particle size of the inorganic sulfate is preferably 3,000 cm 2 / g or more in Blaine value, 4,000~7,000cm 2 / g is more preferable. If it is less than 3,000 cm 2 / g, the initial strength development may be reduced.
無機硫酸塩の使用量は、カルシウムアルミネート100重量部に対して、70〜150重量部が好ましく、90〜110重量部がより好ましい。70重量部未満だと、セメントコンクリートのスランプ保持が困難となり、初期強度の発現性が低下するおそれがあり、150重量部を越えると長期強度の発現性が低下するおそれがある。 The amount of inorganic sulfate used is preferably 70 to 150 parts by weight and more preferably 90 to 110 parts by weight with respect to 100 parts by weight of calcium aluminate. If it is less than 70 parts by weight, it will be difficult to maintain the slump of cement concrete, and there is a risk that the initial strength will be lowered, and if it exceeds 150 parts by weight, the long-term strength may be lowered.
カルシウムアルミネートと無機硫酸塩の混合物の使用量は、セメント100重量部に対して、５〜25重量部が好ましく、10〜20重量部がより好ましい。５重量部未満だと凝結が遅れ、初期強度が低下するおそれがあり、25重量部を越えると凝結時間が短く、可使時間コントロールが困難となり、初期強度発現性が低下するおそれがある。 The amount of the mixture of calcium aluminate and inorganic sulfate used is preferably 5 to 25 parts by weight and more preferably 10 to 20 parts by weight with respect to 100 parts by weight of cement. If the amount is less than 5 parts by weight, the setting may be delayed and the initial strength may be lowered. If the amount exceeds 25 parts by weight, the setting time may be short, making it difficult to control the pot life and the initial strength may be deteriorated.
本発明で使用するスランプ保持材は、アルカリ金属炭酸塩と有機酸類の混合物スラリーであり、セメントコンクリートのハンドリングを調整するためのものである。ここでスラリーは、懸濁液でもよく、溶液でもよい。 The slump holding material used in the present invention is a mixture slurry of an alkali metal carbonate and an organic acid for adjusting the handling of cement concrete. Here, the slurry may be a suspension or a solution.
本発明で使用するアルカリ金属炭酸塩としては、炭酸ナトリウム、炭酸カリウム、及び重炭酸ナトリウム等が挙げられ、これらの１種又は２種以上が使用できる。これらの中では、効果が大きい点で、炭酸カリウムが好ましい。 Examples of the alkali metal carbonate used in the present invention include sodium carbonate, potassium carbonate, and sodium bicarbonate, and one or more of these can be used. Among these, potassium carbonate is preferable because of its great effect.
アルカリ金属炭酸塩の使用量は、アルカリ金属炭酸塩と有機酸類の合計100重量部中、50〜85重量部が好ましく、60〜80重量部がより好ましい。50重量部未満だとセメントコンクリートの可使時間は長くなるが、初期強度発現性が低下し、セメントコンクリートが硬化しにくいおそれがあり、85重量部を越えるとセメントコンクリートのスランプ保持が困難となり、初期強度発現性が低下するおそれがある。 The amount of the alkali metal carbonate used is preferably 50 to 85 parts by weight, more preferably 60 to 80 parts by weight, in a total of 100 parts by weight of the alkali metal carbonate and the organic acids. If it is less than 50 parts by weight, the pot life of cement concrete will be longer, but the initial strength development will be reduced, and cement concrete may be hard to harden. There is a risk that the initial strength developability is lowered.
本発明で使用する有機酸類としては、グルコン酸、酒石酸、クエン酸、リンゴ酸、及び乳酸又はこれらの塩等が挙げられ、これらの１種又は２種以上が使用できる。これらの中では、効果が大きい点で、クエン酸やグルコン酸又はこれらの塩が好ましい。 Examples of the organic acids used in the present invention include gluconic acid, tartaric acid, citric acid, malic acid, lactic acid, and salts thereof, and one or more of these can be used. Among these, citric acid, gluconic acid, or salts thereof are preferable because they are highly effective.
有機酸類の使用量は、アルカリ金属炭酸塩と有機酸類の合計100重量部中、15〜50重量部が好ましく、20〜40重量部がより好ましい。15重量部未満だとセメントコンクリートのスランプ保持が困難となり、初期強度発現性が低下するおそれがあり、50重量部を越えるとセメントコンクリートの可使時間は長くなるが、初期強度発現性が低下し、セメントコンクリートが硬化しにくいおそれがある。 The amount of the organic acid used is preferably 15 to 50 parts by weight, and more preferably 20 to 40 parts by weight, in a total of 100 parts by weight of the alkali metal carbonate and the organic acid. If it is less than 15 parts by weight, it will be difficult to maintain the slump of cement concrete, and the initial strength development may be reduced. If it exceeds 50 parts by weight, the pot life of cement concrete will be longer, but the initial strength development will be reduced. Cement concrete may be hard to harden.
スランプ保持材において、アルカリ金属炭酸塩と有機酸類の混合物の使用量は、水100重量部に対して、１〜95重量部であり、２〜10重量部が好ましい。１重量部未満だと、セメントコンクリートのスランプを保持するために必要とするスラリーの使用量が著しく多くなるために、結果的に水セメント比が高くなり強度発現性が低下するおそれがあり、95重量部を越えると濃度は高くなるが、使用量が少なくなるために、セメントコンクリート中での分散性が悪くなりスランプ保持ができなくなるおそれがある。 In the slump holding material, the amount of the mixture of alkali metal carbonate and organic acid used is 1 to 95 parts by weight, preferably 2 to 10 parts by weight, based on 100 parts by weight of water. If the amount is less than 1 part by weight, the amount of slurry used to hold the slump of cement concrete is remarkably increased. As a result, the water-cement ratio may increase and the strength development may decrease. If the amount exceeds part by weight, the concentration increases, but the amount used decreases, so that the dispersibility in cement concrete is deteriorated, and there is a possibility that the slump cannot be retained.
スランプ保持材中の有効成分であるアルカリ金属炭酸塩と有機酸類の混合物の使用量は、施工温度（環境温度）により変わるので一義的には決まらないが、セメント、カルシウムアルミネート、及び無機硫酸塩の合計（以下結合材という）100重量部に対して、0.1〜1.8重量部が好ましく、1.0〜1.7重量部がより好ましい。0.1重量部未満だとスランプ保持ができないおそれがあり、1.8重量部を越えると可使時間が著しく長くなり、セメントコンクリートが硬化しにくく、初期強度発現性が低下するおそれがある。 The amount of the mixture of alkali metal carbonates and organic acids, which are the active ingredients in the slump retention material, varies depending on the construction temperature (environmental temperature), so it is not uniquely determined, but cement, calcium aluminate, and inorganic sulfates Is preferably 0.1 to 1.8 parts by weight, more preferably 1.0 to 1.7 parts by weight, based on 100 parts by weight of the total (hereinafter referred to as binder). If it is less than 0.1 part by weight, it may not be possible to hold the slump. If it exceeds 1.8 parts by weight, the pot life will be significantly long, and the cement concrete will be hard to harden and the initial strength may be reduced.
本発明ではさらに、セメントコンクリートの凝結や硬化を促進する点で、急結剤を使用することが好ましい。急結剤としては、粉体及び／又は液体のものが挙げられる。これらの中では、均一に分散しやすい点で、液体の急結剤が好ましい。 In the present invention, it is further preferable to use a quick setting agent in terms of accelerating the setting and hardening of cement concrete. Examples of the quick setting agent include powders and / or liquids. Among these, a liquid quick-setting agent is preferable because it can be uniformly dispersed.
急結剤としては、アルミン酸ナトリウムやアルミン酸カリウム等のアルミン酸塩、硫酸アルミニウム等のアルミニウム塩、及びケイ酸ナトリウム（水ガラス）等が挙げられる。これらの１種又は２種以上が使用できる。 Examples of the quick setting agent include aluminates such as sodium aluminate and potassium aluminate, aluminum salts such as aluminum sulfate, and sodium silicate (water glass). These 1 type (s) or 2 or more types can be used.
急結剤の使用量は、セメント100重量部に対して、１〜20重量部が好ましく、３〜10重量部がより好ましい。１重量部未満だと急結性に欠け、初期強度発現性が低下するおそれがあり、20重量部を越えると長期強度発現性が低下するおそれがある。 The amount of the rapid setting agent is preferably 1 to 20 parts by weight, and more preferably 3 to 10 parts by weight with respect to 100 parts by weight of cement. If the amount is less than 1 part by weight, the quick setting property may be lacking, and the initial strength development may be reduced. If the amount exceeds 20 parts by weight, the long-term strength development may be reduced.
本発明では、さらに、繊維、超微粉、及び減水剤を併用できる。 In the present invention, fibers, ultrafine powder, and a water reducing agent can be used in combination.
水の使用量は、水／セメント比（以下Ｗ／Ｃという）で、35〜60％が好ましく、40〜50％がより好ましい。35％未満だとミキサーで混練りできないおそれがあり、60％を越えると強度発現性が小さく、強度発現性を出すために各材料の使用量が多くなりコスト高になるおそれがある。 The amount of water used is preferably a water / cement ratio (hereinafter referred to as W / C) of 35 to 60%, more preferably 40 to 50%. If it is less than 35%, kneading with a mixer may not be possible, and if it exceeds 60%, strength development is small, and in order to achieve strength development, the amount of each material used may be increased, resulting in high costs.
本発明で使用する粗骨材や細骨材等の骨材はセメントコンクリートに添加するものであり、吸水率が低くて、骨材強度が高いものが好ましいが、特に制限されるものではない。粗骨材としては最大直径５〜20mmが好ましく、圧送性の点で、最大寸法５〜15mmがより好ましく、川砂利、山砂利、及び石灰砂利等が使用できる。
細骨材としては最大直径５mm以下が好ましく、川砂、山砂、石灰砂、及び珪砂等が挙げられる。
Aggregates such as coarse aggregate and fine aggregate used in the present invention are added to cement concrete, and those having low water absorption and high aggregate strength are preferred, but are not particularly limited. The coarse aggregate preferably has a maximum diameter of 5 to 20 mm, more preferably a maximum size of 5 to 15 mm in terms of pumpability, and river gravel, mountain gravel, lime gravel and the like can be used.
The fine aggregate preferably has a maximum diameter of 5 mm or less, and examples include river sand, mountain sand, lime sand, and quartz sand.
本発明において、急硬性セメントコンクリートの混合方法は特に限定されるものではなく、生コンプラントやコンクリート工場等で使用される各種混合機が使用可能である。
本発明において、急硬性セメントコンクリートに急結剤を添加して急結性セメントコンクリートとする方法としては、急結剤が急硬性セメントコンクリート中で均一に分散すれば特に限定されるものではなく、セメントコンクリート圧送管の途中に注入ノズルを設けて、添加する方法等が挙げられる。急結剤添加後、急結性セメントコンクリートは極短時間で凝結、硬化するために、急結剤は打設直前に添加することが好ましい。
In the present invention, the method for mixing the rapid-hardening cement concrete is not particularly limited, and various mixers used in raw concrete plants, concrete factories and the like can be used.
In the present invention, as a method of adding a quick setting agent to the quick setting cement concrete to make the quick setting cement concrete, it is not particularly limited as long as the quick setting agent is uniformly dispersed in the quick setting cement concrete, A method of adding an injection nozzle in the middle of a cement concrete pressure feeding pipe and adding it may be mentioned. Since the quick setting cement concrete sets and hardens in a very short time after the quick setting agent is added, it is preferable to add the quick setting agent immediately before placing.
以下、実験例により本発明を詳細に説明するが、本発明はこれら実験例に限定されるものではない。 Hereinafter, the present invention will be described in detail by experimental examples, but the present invention is not limited to these experimental examples.
実験例１
各材料の単位量を、セメント200kg/m3、水344kg/m3、細骨材762kg/m3、及び粗骨材942kg/m3とした。
これに、カルシウムアルミネート100重量部と表１に示す量の無機硫酸塩からなる混合物を、セメント100重量部に対して15重量部使用し、さらに、アルカリ金属炭酸塩70重量部と有機酸類30重量部からなる混合物を、セメント、カルシウムアルミネート、及び無機硫酸塩の合計（結合材）100重量部に対して1.5重量部で、かつ、水100重量部に対して３重量部となるように調製したスランプ保持材を添加して、急硬性コンクリートを調製した。
この急硬性コンクリートに、急結剤をセメント100重量部に対して５重量部添加して、急結性コンクリートを調製し、物性を評価した。結果を表１に示す。
Experimental example 1
The unit amount of each material was cement 200 kg / m 3 , water 344 kg / m 3 , fine aggregate 762 kg / m 3 , and coarse aggregate 942 kg / m 3 .
To this, 15 parts by weight of a mixture of 100 parts by weight of calcium aluminate and inorganic sulfate in the amount shown in Table 1 is used with respect to 100 parts by weight of cement, and further 70 parts by weight of alkali metal carbonate and 30 parts of organic acids. The mixture consisting of parts by weight is 1.5 parts by weight with respect to 100 parts by weight of the total of cement, calcium aluminate, and inorganic sulfate (binding material), and 3 parts by weight with respect to 100 parts by weight of water. The prepared slump holding material was added to prepare quick-hardening concrete.
A rapid setting concrete was prepared by adding 5 parts by weight of the quick setting agent to 100 parts by weight of cement to the rapid hardening concrete, and the physical properties were evaluated. The results are shown in Table 1.
（使用材料）
セメント ：普通ポルトランドセメント、市販品、ブレーン値3,200cm2/g、比重3.16
細骨材 ：千葉県君津産山砂、表乾状態、比重2.56、最大直径５mm以下
粗骨材 ：千葉県君津産砕石、表乾状態、比重2.59、最大寸法10mm
カルシウムアルミネート：主成分C12A7、非晶質、ブレーン値6,000cm2/g
無機硫酸塩：II型無水石膏、ブレーン値6,050cm2/g
アルカリ金属炭酸塩：市販炭酸カリウム、粉末状
有機酸類 ：市販品、グルコン酸
急結剤 ：市販品、アルミン酸カリウム溶液
(Materials used)
Cement: Ordinary Portland cement, commercially available, 3,200 cm 2 / g brain value, 3.16 specific gravity
Fine aggregate: Kimitsu sand, Chiba prefecture, surface dry state, specific gravity 2.56, maximum diameter 5mm or less Coarse aggregate: Crushed stone from Kimitsu, surface dry state, specific gravity 2.59, maximum dimension 10mm
Calcium aluminate: main component C 12 A 7 , amorphous, brain value 6,000cm 2 / g
Inorganic sulfate: type II anhydrous gypsum, brain value 6,050cm 2 / g
Alkali metal carbonates: Commercially available potassium carbonate, powdered organic acids: Commercially available products, Gluconic acid quick setting agents: Commercially available products, potassium aluminate
（測定方法）
圧縮強度 ：所定材齢の急結性コンクリートを、JIS A 1108に従い、測定した。
スランプ ：混練後、所定時間の急硬性コンクリートを、JIS A 1101に従い、測定した。
(Measuring method)
Compressive strength: Quick setting concrete of a predetermined age was measured according to JIS A 1108.
Slump: Rapidly hardened concrete for a predetermined time after kneading was measured according to JIS A 1101.
実験例２
カルシウムアルミネート100重量部と無機硫酸塩100重量部からなる混合物を、セメント100重量部に対して15重量部使用し、さらに、表２に示す量のアルカリ金属炭酸塩と有機酸類からなる混合物を、結合材100重量部に対して1.5重量部で、かつ、水100重量部に対して３重量部となるように調製したこと以外は、実験例１と同様に行った。結果を表２に示す。
Experimental example 2
A mixture consisting of 100 parts by weight of calcium aluminate and 100 parts by weight of inorganic sulfate is used in an amount of 15 parts by weight with respect to 100 parts by weight of cement. Further, a mixture of alkali metal carbonate and organic acids in the amounts shown in Table 2 is used. The experiment was conducted in the same manner as in Experimental Example 1 except that the amount was 1.5 parts by weight with respect to 100 parts by weight of the binder and 3 parts by weight with respect to 100 parts by weight of water. The results are shown in Table 2.
（測定方法）
凝結時間Ｉ：急結性コンクリートを、ASTM C 403に従い、測定した。
(Measuring method)
Setting time I: Rapid setting concrete was measured according to ASTM C403.
実験例３
カルシウムアルミネート100重量部と無機硫酸塩100重量部からなる混合物を、セメント100重量部に対して15重量部使用し、さらに、アルカリ金属炭酸塩70重量部と有機酸類30重量部からなる混合物を、結合材100重量部に対して1.5重量部で、かつ、水100重量部に対して表３に示す量となるように調製したこと以外は、実験例１と同様に行った。結果を表３に示す。
Experimental example 3
15 parts by weight of a mixture consisting of 100 parts by weight of calcium aluminate and 100 parts by weight of inorganic sulfate is used with respect to 100 parts by weight of cement, and further a mixture of 70 parts by weight of alkali metal carbonate and 30 parts by weight of organic acids. The test was performed in the same manner as in Experimental Example 1 except that the amount was 1.5 parts by weight with respect to 100 parts by weight of the binder and the amount shown in Table 3 with respect to 100 parts by weight of water. The results are shown in Table 3.
実験例４
カルシウムアルミネート100重量部と無機硫酸塩100重量部からなる混合物を、セメント100重量部に対して15重量部使用し、さらに、アルカリ金属炭酸塩70重量部と有機酸類30重量部からなる混合物を、結合材100重量部に対して表４に示す量で、かつ、水100重量部に対して３重量部となるように調製したこと以外は、実験例１と同様に行った。結果を表４に示す。
Experimental Example 4
15 parts by weight of a mixture consisting of 100 parts by weight of calcium aluminate and 100 parts by weight of inorganic sulfate is used with respect to 100 parts by weight of cement, and further a mixture of 70 parts by weight of alkali metal carbonate and 30 parts by weight of organic acids. The same procedure as in Experimental Example 1 was conducted except that the amount was as shown in Table 4 with respect to 100 parts by weight of the binder and 3 parts by weight with respect to 100 parts by weight of water. The results are shown in Table 4.
実験例５
カルシウムアルミネート100重量部と無機硫酸塩100重量部からなる混合物を、セメント100重量部に対して表５に示す量使用したこと以外は、実験例１と同様に行った。結果を表５に示す。
Experimental Example 5
The experiment was conducted in the same manner as in Experimental Example 1 except that a mixture of 100 parts by weight of calcium aluminate and 100 parts by weight of inorganic sulfate was used in an amount shown in Table 5 with respect to 100 parts by weight of cement. The results are shown in Table 5.
（測定方法）
凝結時間II：急硬性コンクリートを、ASTM M 403に従い、測定した。
(Measuring method)
Setting time II: Rapidly hardened concrete was measured according to ASTM M403.
実験例６
カルシウムアルミネート100重量部と無機硫酸塩100重量部からなる混合物を、セメント100重量部に対して15重量部使用し、又、急結剤をセメント100重量部に対して表６に示す量使用したこと以外は、実験例１と同様に行った。結果を表６に示す。
Experimental Example 6
15 parts by weight of a mixture consisting of 100 parts by weight of calcium aluminate and 100 parts by weight of inorganic sulfate is used with respect to 100 parts by weight of cement. Except for this, the same procedure as in Experimental Example 1 was performed. The results are shown in Table 6.
Claims (6)