JP2005304999A - Ball for park golf - Google Patents

Ball for park golf Download PDF

Info

Publication number
JP2005304999A
JP2005304999A JP2004129446A JP2004129446A JP2005304999A JP 2005304999 A JP2005304999 A JP 2005304999A JP 2004129446 A JP2004129446 A JP 2004129446A JP 2004129446 A JP2004129446 A JP 2004129446A JP 2005304999 A JP2005304999 A JP 2005304999A
Authority
JP
Japan
Prior art keywords
ball
foamed
resin
park golf
synthetic resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2004129446A
Other languages
Japanese (ja)
Other versions
JP4108639B2 (en
Inventor
Katsuyuki Hori
克行 堀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tabata Co Ltd
Original Assignee
Tabata Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tabata Co Ltd filed Critical Tabata Co Ltd
Priority to JP2004129446A priority Critical patent/JP4108639B2/en
Publication of JP2005304999A publication Critical patent/JP2005304999A/en
Application granted granted Critical
Publication of JP4108639B2 publication Critical patent/JP4108639B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a ball for park golf by which excellent resistance is made when the ball is hit. <P>SOLUTION: The ball 1 for the park golf includes a skin part 6 formed of an ionomer resin with the thickness of 1.3-7.5mm; and a core part 7 arranged at the inner side of the skin part 6 and formed of a synthetic resin which is at least partially foamed. The amount of change of a diameter in the ball 1 under the load of 100kgf is within the range of 3-10%. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

この発明は、パークゴルフに使用するのに好適なボールに関する。   The present invention relates to a ball suitable for use in park golf.

パークゴルフに使用する用具については、国際パークゴルフ協会（北海道中川郡幕別町室町５３−１）によって作成された規定がある。その規定によれば、ボールは８０〜９５グラム、直径６０プラスマイナス０．５ミリメートルの合成樹脂製のもので、反発距離が６５センチメートル以下、ＪＩＳ Ｋ ７１２５のＤ型による表面硬度が４５〜６０°でなければならない。   There is a rule created by the International Park Golf Association (53-1 Muromachi, Makuhetsu-cho, Nakagawa-gun, Hokkaido) for equipment used for park golf. According to the regulations, the ball is made of a synthetic resin having a diameter of 80 to 95 grams, a diameter of 60 plus or minus 0.5 millimeters, a repulsion distance of 65 centimeters or less, and a surface hardness of 45 to 60 according to D type of JIS K 7125. Must be °.

また、特開２００２−７８８２９号公報（特許文献１）には、パークゴルフ等に使用するボールについての発明が開示されている。この発明は、ボールの表面硬度と貯蔵弾性率とを所定の値にすると、ボールの耐摩耗性が向上すると教示している。ここでいう摩耗とは、ボールが地面を転がったときに、砂や土によりボール表面が摩耗することを意味している。このボールの表面層は粘弾性体によって形成され、その粘弾性体の一例はアイオノマー樹脂を主成分とするポリマーである。この発明ではまた、ボールを二層構造にすることができ、表面層内側のコアには種々のゴムを使用することができると教示している。
特開２００２−７８８２９号公報 Japanese Patent Laid-Open No. 2002-78829 (Patent Document 1) discloses an invention relating to a ball used for park golf or the like. The present invention teaches that when the surface hardness and storage elastic modulus of the ball are set to predetermined values, the wear resistance of the ball is improved. The term “wear” as used herein means that the ball surface is worn by sand or earth when the ball rolls on the ground. The surface layer of the ball is formed of a viscoelastic body, and an example of the viscoelastic body is a polymer mainly composed of an ionomer resin. The invention also teaches that the ball can be a two-layer structure and that various rubbers can be used for the core inside the surface layer.
JP 2002-78829 A

スキン部分とその内側のコア部分とからなり、スキン部分がアイオノマー樹脂で形成されているゴルフボールは周知である。そのような周知のゴルフボールにおいてはまた、アイオノマー樹脂からなるボール表面が強靭で耐摩耗性に優れていることや平滑性、光の透過性に優れていることもよく知られている。しかし、ゴルフボールを打つためのクラブとは全く異なり、ヘッドの材質が木質のもに限られると規定されているパークゴルフ用クラブで打たれるパークゴルフ用のボールは、スキン部分とコア部分とをアイオノマー樹脂のみで作ってみても、またスキン部分をアイオノマー樹脂で作りコア部分をゴムで作ってみても、クラブで打ったときの手応えは硬すぎるものになったり、柔らかすぎるものになったりする。   A golf ball having a skin portion and an inner core portion, and the skin portion is formed of an ionomer resin is well known. In such well-known golf balls, it is also well known that the surface of the ball made of ionomer resin is tough and excellent in wear resistance, smoothness and light transmission. However, unlike a club for hitting a golf ball, a park golf ball hit by a park golf club, which is prescribed that the head material is limited to wood, has a skin portion and a core portion. Even if it is made only with ionomer resin, or even if the skin part is made with ionomer resin and the core part is made of rubber, the response when hit with a club becomes too hard or too soft. .

この発明が課題とするところは、規定のクラブでボールを打ったときにほどよい手応えの得られるパークゴルフ用ボールの提供にある。   An object of the present invention is to provide a golf ball for a park golf that can obtain a good response when the ball is hit with a specified club.

課題を解決するための手段及び発明の効果Means for Solving the Problems and Effects of the Invention

前記課題解決のために、この発明が対象とするのは、直径６０ｍｍ、重さ８０〜９５グラムを有するパークゴルフ用ボールである。かかるボールにおいて、この発明が特徴とするところは、前記ボールの断面が１．３〜７．５ｍｍの厚さを有しアイオノマー樹脂で形成されたスキン部分と、前記スキン部分の内側にあって少なくとも一部分が発泡した状態にある合成樹脂を含むコア部分とからなり、１００ｋｇｆの圧縮荷重下での前記ボールの直径の変化量が３〜１０％の範囲にあること、にある。   In order to solve the above problems, the present invention is intended for a park golf ball having a diameter of 60 mm and a weight of 80 to 95 grams. In such a ball, the present invention is characterized in that the cross section of the ball has a thickness of 1.3 to 7.5 mm and is formed of an ionomer resin, and is provided at least inside the skin portion. It consists of a core part containing a synthetic resin partly in a foamed state, and the amount of change in the diameter of the ball under a compression load of 100 kgf is in the range of 3 to 10%.

かかる発明において、直径の変化量Ａは、圧縮前のボールの直径をＤ０とし、１００ｋｇｆの荷重を５秒間かけた後の直径をＤ１としたときに、Ａ（％）＝（Ｄ０−Ｄ１）／Ｄ０×１００と定義される。変化量Ａが３〜１０％であるときに、クラブでボールを打ったときの手応えがほどよいものになることが実験的に確かめられている。 In this invention, the change amount A of the diameter is A (%) = (D 0 − when the diameter of the ball before compression is D 0 and the diameter after applying a load of 100 kgf for 5 seconds is D 1. D 1 ) / D 0 × 100. It has been experimentally confirmed that when the amount of change A is 3 to 10%, the response when a ball is hit with a club becomes moderate.

請求項２に係るこの発明の実施態様において、前記コア部分が、前記スキン部分に接していて０．５〜５ｍｍの厚さを有する前記合成樹脂の非発泡層と、前記非発泡層の内側を充たす前記合成樹脂の発泡層とからなる。   In an embodiment of the present invention according to claim 2, the core portion is in contact with the skin portion and has a non-foamed layer of the synthetic resin having a thickness of 0.5 to 5 mm, and an inner side of the non-foamed layer. It consists of a foamed layer of the synthetic resin to be filled.

この態様の発明によれば、スキン部分が透明であっても、非発泡層によって発泡層を隠蔽することができるので、スキン部分とコア部分との間に設けられたマーク、装飾模様等の表示手段の視認性が発泡層の存在によって低下するということがない。   According to the invention of this aspect, even if the skin portion is transparent, the foamed layer can be concealed by the non-foamed layer, so that the mark, the decorative pattern, etc. provided between the skin portion and the core portion are displayed. The visibility of the means is not reduced by the presence of the foam layer.

請求項３に係るこの発明の実施態様において、前記合成樹脂がエチレン酢酸ビニル樹脂である。   In an embodiment of the present invention according to claim 3, the synthetic resin is an ethylene vinyl acetate resin.

コア部分が発泡したエチレン酢酸ビニル樹脂を含むパークゴルフ用ボールは、それを打ったときの手応えが特に良好である。   A park golf ball including an ethylene vinyl acetate resin having a foamed core portion has particularly good response when hit.

添付の図面を参照して、この発明に係るゴルフ用ボールの詳細を説明すると、以下のとおりである。   The details of the golf ball according to the present invention will be described with reference to the accompanying drawings.

図１，２は、パークゴルフ用ボール１の正面図と、その正面図のＩＩ−ＩＩ線断面図である。ボール１は、国際パークゴルフ協会が規定する寸法と性能とを有するもので、図１では、フィルム２に表示手段として印刷されたマークや装飾模様の一例であるＡ，Ｂ，Ｃの三文字からなるマーク３をボール１の表面から透視できるが、そのフィルム２には無色透明なものが使用されているからフィルム２の存在が目立つことはない。ボール１の直径は６０ｍｍであり、その断面には、厚さ１．３〜７．５ｍｍのスキン部分６と、スキン部分６の内側を充たすコア部分７とが現われている。スキン部分６は、アイオノマー樹脂、より好ましくは透明ないし半透明のアイオノマー樹脂で形成されている。コア部分７は、少なくとも一部分が発泡した状態にある合成樹脂を含むもので、好ましくはスキン部分６と接する部位に厚さ０．５〜５ｍｍの第１コア層８を有し、第１コア層８の内側に第２コア層９を有する。コア部分７はエチレン酢酸ビニル樹脂からなるものであるが、第１コア層８ではエチレン酢酸ビニル樹脂が非発泡状態にあり、第２コア層９ではエチレン酢酸ビニル樹脂が発泡状態にある。ここでエチレン酢酸ビニル樹脂が非発泡状態にあるとは、図２の断面においてこの樹脂が発泡した状態にあることを目視によっては確認できないことを意味し、発泡状態にあるとは、目視によってその発泡状態を確認できることを意味している。マーク３が印刷されている透明なフィルム２は、スキン部分６とコア部分７との間にあり、マーク３はコア部分７における第１コア層８の色を背景にして、透明ないし半透明のスキン部分６を透して見ることができる。第１コア層８は非発泡状態にあるから、発泡しているエチレン酢酸ビニル樹脂が透けて見えてマーク３の視認性が低下するということはない。   1 and 2 are a front view of the park golf ball 1 and a cross-sectional view taken along the line II-II of the front view. The ball 1 has the dimensions and performance prescribed by the International Park Golf Association. In FIG. 1, the three characters A, B, and C, which are examples of marks and decorative patterns printed on the film 2 as display means, are used. The mark 3 can be seen through from the surface of the ball 1, but since the film 2 is colorless and transparent, the presence of the film 2 is not noticeable. The diameter of the ball 1 is 60 mm, and a skin portion 6 having a thickness of 1.3 to 7.5 mm and a core portion 7 filling the inside of the skin portion 6 appear in the cross section. The skin portion 6 is formed of an ionomer resin, more preferably a transparent or translucent ionomer resin. The core portion 7 includes a synthetic resin in which at least a part is foamed. The core portion 7 preferably includes a first core layer 8 having a thickness of 0.5 to 5 mm at a portion in contact with the skin portion 6. 8 has a second core layer 9 inside. The core portion 7 is made of an ethylene vinyl acetate resin. In the first core layer 8, the ethylene vinyl acetate resin is in a non-foamed state, and in the second core layer 9, the ethylene vinyl acetate resin is in a foamed state. Here, the ethylene vinyl acetate resin is in a non-foamed state means that it cannot be visually confirmed that the resin is in a foamed state in the cross section of FIG. This means that the foaming state can be confirmed. The transparent film 2 on which the mark 3 is printed is between the skin portion 6 and the core portion 7, and the mark 3 is transparent or translucent against the background of the color of the first core layer 8 in the core portion 7. The skin portion 6 can be seen through. Since the first core layer 8 is in a non-foamed state, the foamed ethylene vinyl acetate resin is not seen through and the visibility of the mark 3 is not lowered.

パークゴルフ用ボールの規定重量は８０〜９５ｇであり、図１，２に示されたボール１で厚さ１．３〜７．５ｍｍを有するスキン部分６のアイオノマー樹脂が占める重量はその比重に基づく計算から規定重量の約３０％になるので、残り約７０％の重量はコア部分７のエチレン酢酸ビニル樹脂の重量となる。そのエチレン酢酸ビニル樹脂は、第１コア層８の内側を発泡した状態の第２コア層９で充たすことができるように、発泡剤の量と発泡条件とが調整される。   The specified weight of the park golf ball is 80 to 95 g, and the weight occupied by the ionomer resin of the skin portion 6 having a thickness of 1.3 to 7.5 mm in the ball 1 shown in FIGS. 1 and 2 is based on its specific gravity. Since the calculated weight is about 30%, the remaining weight of about 70% is the weight of the ethylene vinyl acetate resin of the core portion 7. The amount of the foaming agent and the foaming conditions are adjusted so that the ethylene vinyl acetate resin can be filled with the second core layer 9 in the foamed state inside the first core layer 8.

この発明の発明者が知見したところによれば、規定重量のボールであっても、圧縮試験機によって１００ｋｇｆの荷重を５秒間かけたときの直径の変化量Ａによって、ボールをクラブで打ったときの手応え、換言すると手に伝わる衝撃の度合いが変化する。その変化量Ａは、荷重をかける前の直径をＤ０とし、１００ｋｇｆの荷重を５秒間かけた後の直径をＤ１とすると、Ａ（％）＝（Ｄ０−Ｄ１）／Ｄ０×１００と定義される値である。発明者の実験によれば、図１，２の構造を有するアイオノマー樹脂とエチレン酢酸ビニル樹脂とからなるボール１では、変化量Ａが１０％を超えるときに、５人のプレーヤー全員が柔らかすぎて反発力に欠ける手応えのものと判断し、変化量Ａが３％未満であるときのボール１では、全員が硬すぎて、手に加わる衝撃が大きい手応えのものと判断した。変化量Ａが３〜１０％の間にあるときには、５人中の少なくとも３人のプレーヤーがボールの硬さが適度でほどよい手応えのものと判断した。 According to the knowledge of the inventors of the present invention, even when the ball has a specified weight, when the ball is hit with a club by the amount A of change in diameter when a load of 100 kgf is applied for 5 seconds by a compression tester. In other words, the degree of impact transmitted to the hand changes. The amount of change A is A (%) = (D 0 −D 1 ) / D 0 ×, where D 0 is the diameter before the load is applied and D 1 is the diameter after the 100 kgf load is applied for 5 seconds. A value defined as 100. According to the inventor's experiment, in the ball 1 made of the ionomer resin having the structure shown in FIGS. 1 and 2 and the ethylene vinyl acetate resin, when the change amount A exceeds 10%, all the five players are too soft. It was judged that the response was lacking in repulsive force, and in the ball 1 when the change amount A was less than 3%, all the members were too hard and judged to be a response with a large impact on the hand. When the amount of change A was between 3% and 10%, at least 3 out of 5 players judged that the ball hardness was moderate and moderately responsive.

ボール１の変化量Ａをこのように３〜１０％の範囲に納めるには、８０〜９５ｇのボール１で、スキン部分６の厚さを１．３〜７．５ｍｍの範囲で調整し、そのときのスキン部分６の重量とボール１の規定重量との差をコア部分７の重量とし、かつ第１コア層８の厚さを０．５〜５ｍｍの範囲で調整することが好ましい。ボール１は、スキン部分６がアイオノマー樹脂で形成され、コア部分７が発泡したエチレン酢酸ビニル樹脂を含むことが好ましいものであるが、そのエチレン酢酸ビニル樹脂に代えて発泡したウレタン樹脂や塩化ビニル樹脂を含むことも可能である。また、マーク３の視認性が特に問題にならないときには、コア部分７の全体を発泡した合成樹脂で形成することができる。   In order to keep the change amount A of the ball 1 in the range of 3 to 10% in this way, the thickness of the skin portion 6 is adjusted in the range of 1.3 to 7.5 mm with the ball 1 of 80 to 95 g, It is preferable that the difference between the weight of the skin portion 6 and the specified weight of the ball 1 is the weight of the core portion 7 and the thickness of the first core layer 8 is adjusted in the range of 0.5 to 5 mm. The ball 1 preferably includes an ethylene vinyl acetate resin in which the skin portion 6 is formed of an ionomer resin and the core portion 7 is foamed. Can also be included. Further, when the visibility of the mark 3 is not particularly problematic, the entire core portion 7 can be formed of a foamed synthetic resin.

この発明によれば、クラブでボールを打ったときにほどよい衝撃が手に伝わるパークゴルフ用ボールの製造が可能になる。   According to the present invention, it is possible to manufacture a park golf ball in which a moderate impact is transmitted to the hand when the ball is hit with a club.

ボールの正面図。Front view of the ball. 図１のＩＩ−ＩＩ線断面図。II-II sectional view taken on the line of FIG.

符号の説明Explanation of symbols

１ ボール
６ スキン部分
７ コア部分
８ 非発泡層
９ 発泡層 1 Ball 6 Skin part 7 Core part 8 Non-foamed layer 9 Foamed layer

Claims (3)

直径６０ｍｍ、重さ８０〜９５グラムを有するパークゴルフ用ボールであって、
前記ボールの断面が１．３〜７．５ｍｍの厚さを有しアイオノマー樹脂で形成されたスキン部分と、前記スキン部分の内側にあって少なくとも一部分が発泡した状態にある合成樹脂を含むコア部分とからなり、１００ｋｇｆの圧縮荷重下での前記ボールの直径の変化量が３〜１０％の範囲にあることを特徴とする前記ボール。 A park golf ball having a diameter of 60 mm and a weight of 80 to 95 grams,
A skin portion having a cross section of the ball having a thickness of 1.3 to 7.5 mm and formed of an ionomer resin, and a core portion including a synthetic resin inside the skin portion and at least a part of which is foamed The ball is characterized in that the change in the diameter of the ball under a compressive load of 100 kgf is in the range of 3 to 10%. 前記コア部分は、前記スキン部分に接していて０．５〜５ｍｍの厚さを有する前記合成樹脂の非発泡層と、前記非発泡層の内側を充たす前記合成樹脂の発泡層とからなる請求項１記載のボール。   The core portion includes a non-foamed layer of the synthetic resin that is in contact with the skin portion and has a thickness of 0.5 to 5 mm, and a foamed layer of the synthetic resin that fills the inside of the non-foamed layer. 1. The ball according to 1. 前記合成樹脂がエチレン酢酸ビニル樹脂である請求項１または２記載のボール。   The ball according to claim 1, wherein the synthetic resin is an ethylene vinyl acetate resin.
JP2004129446A 2004-04-26 2004-04-26 Park Golf Ball Expired - Fee Related JP4108639B2 (en)