JP2005165071A - Toner - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a toner which ensures less unevenness in shape among toner particles, has excellent mechanical stability in toner particles, and is environmentally friendly because crumble (resolvent) of toner particles is hardly produced even in a manufacturing process such as a classification process. <P>SOLUTION: The toner particles 100 consist of a particulate body 4 and an external additive. The particulate body 4 comprises an agglutinate 40 obtained by melt-agglutinating a plurality of fine resin particles, has recesses formed near the surface in portions corresponding to parts where adjacent fine resin particles are agglutinated, and has a compensating phase 42 which reduces the degree of irregularity of the toner particles in at least the recesses. It is preferable that the compensating phase 42 consists mainly of an epoxy resin. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

  The present invention relates to a toner.

  A number of methods are known as electrophotographic methods. In general, a process (exposure process) of forming an electrical latent image on a photoconductor by various means using a photoconductive substance, A developing step of developing the latent image with toner, a transferring step of transferring the toner image onto a transfer material such as paper, and a step of fixing the toner image by heating, pressing, etc. using a fixing roller. doing.

Further, as a toner manufacturing method, a pulverization method or a polymerization method is used.
The pulverization method is a method of kneading a raw material containing a binder resin (binder resin) as a main component and a colorant to obtain a kneaded product, and then cooling and pulverizing the kneaded product (for example, non-patent). Reference 1). Such a pulverization method is excellent in that the range of selection of raw materials is wide and toner can be manufactured relatively easily. However, the toner obtained by the pulverization method is indefinite, has a large variation in shape among particles, and has a drawback that its particle size distribution tends to be wide. As a result, the characteristics of the toner particles differ greatly, and there are problems such as a decrease in transfer efficiency as a whole toner and a decrease in charging characteristics.

  In the polymerization method, toner particles are produced by performing a polymerization reaction in a liquid phase or the like using a monomer that is a constituent component of a binder resin to produce a target binder resin ( For example, see Patent Document 1). Such a polymerization method is excellent in that the shape of the obtained toner particles can be made to have a relatively high sphericity (geometrically close to a perfect sphere). However, in the polymerization method, there may be a case where the variation in the particle size among the particles cannot be sufficiently reduced. In addition, in the polymerization method, the selection range of the type of the binder resin is narrow, and it may be difficult to obtain a toner having desired characteristics.

Supervised by the Society of Electrophotography, “Basics and Applications of Electrophotography” published by Corona, 1988, p482-486 JP-A-6-332257 (page 2, lines 28-35)

  An object of the present invention is to provide a toner having a small variation in shape among toner particles and having excellent mechanical stability of the toner particles.

Such an object is achieved by the present invention described below.
The toner of the present invention is a toner that is an aggregate of toner particles formed by melt-bonding a plurality of resin fine particles mainly composed of a binder resin,
The toner particles have a recess formed in the vicinity of the surface thereof, and have a filling phase that relaxes the degree of unevenness of the toner particle at least in the recess.
As a result, it is possible to provide a toner having a small variation in shape among the toner particles and having excellent mechanical stability of the toner particles.

In the toner of the present invention, it is preferable that the concave portion is formed at a portion corresponding to a joint portion between the adjacent resin fine particles.
Thereby, the mechanical stability of the toner particles can be made particularly excellent.
In the toner of the present invention, it is preferable that the filling phase is mainly composed of a thermosetting resin.
As a result, the mechanical stability of the toner particles can be further improved, and a supplementary phase can be easily formed during the production of the toner.

In the toner of the present invention, it is preferable that the filling phase is mainly composed of an epoxy resin.
As a result, the mechanical stability of the toner particles can be further improved, and a supplementary phase can be more easily formed during the production of the toner.
In the toner of the present invention, the resin fine particles preferably contain a colorant.
Thereby, the dispersibility of the colorant in the toner particles can be made particularly high with relative ease. Further, it is possible to effectively prevent the colorant from exuding to the outside of the toner particles (unintentional colorant exudation). As a result, it is possible to effectively prevent the occurrence of so-called streaks in an image formed using toner, and it is also effective to prevent dirt from adhering to constituent members of an image forming apparatus such as a photoreceptor. Can be prevented.

In the toner of the present invention, the resin fine particles preferably contain a wax.
Thereby, the dispersibility of the wax in the toner particles can be made sufficiently high relatively easily. In addition, it is possible to effectively prevent the wax from exuding to the outside of the toner particles (unintentional exudation of the wax).
In the toner of the present invention, the average particle diameter of the toner particles is preferably 2 to 20 μm.
As a result, the dispersion of characteristics such as charging characteristics and fixing characteristics among the toner particles is particularly small, and the resolution of the image formed by the toner is sufficiently high while the reliability of the entire toner is particularly high. Can be.

The toner of the present invention is preferably provided with an external additive.
As a result, the balance of various properties required for the toner is particularly excellent.
In the toner of the present invention, it is preferable that the standard deviation of the particle diameter between the toner particles is 1.6 μm or less.
As a result, variations in characteristics such as charging characteristics and fixing characteristics among the toner particles are particularly reduced, and the reliability of the toner as a whole is further improved.

In the toner of the present invention, the average circularity R of the toner particles represented by the following formula (I) is preferably 0.91 to 0.99.
R = L ₀ / L ₁ (I)
(Where, L ₁ [μm] is the circumference of the projected image of the toner particles to be measured, and L ₀ [μm] is the circumference of a perfect circle having an area equal to the area of the projected image of the toner particles to be measured) Represents length)
Thereby, the transfer efficiency and mechanical strength of the toner particles can be made particularly excellent while the particle diameter of the toner particles is sufficiently small. Also, the fluidity of the toner is improved.
In the toner of the present invention, the standard deviation of the circularity between the toner particles is preferably 0.05 or less.
As a result, variations in characteristics such as charging characteristics and fixing characteristics among toner particles are particularly reduced, and the reliability of the toner as a whole is further improved.

Hereinafter, preferred embodiments of the toner of the present invention will be described in detail with reference to the accompanying drawings.
[Toner particles]
FIG. 1 is a sectional view schematically showing a preferred embodiment of the toner (toner particles) of the present invention, and FIG. 2 is a flowchart for softening point analysis.
As shown in FIG. 1, the toner particle 100 is composed of a granular body 4 including a joined body (aggregate) 40 formed by melting and joining a plurality of resin fine particles and a filling phase 42, and an external additive (not shown). It is configured. Hereinafter, the joined body 40, the filling phase 42, and the external additive will be described in detail. The constituent materials of the toner (the joined body 40, the filling phase 42, and the constituent materials of the external additive) will be described in detail later.

<Joint>
The joined body (aggregate) 40 is formed by melting and joining at least a plurality of resin fine particles. The resin fine particles (bonded body 40) are mainly composed of a binder resin (binder resin).
Thus, the joined body 40 is formed by melt-joining at least a plurality of resin fine particles. Thereby, the circularity of the toner particles 100 can be set to an appropriate size. As a result, the triboelectric chargeability is improved and the charging characteristics of the toner are particularly excellent. In addition, since the external additive can be reliably supported in the vicinity of the surface of the toner base particles (granular body 4), the function of the external additive can be exhibited more effectively, and the characteristics and reliability of the entire toner can be achieved. Also improves. In addition, since a plurality of resin fine particles are melt-bonded, the mechanical stability as the toner particles 100 is improved, and even if the toner particles 100 have a relatively small particle size, it is easy and reliable. The circularity can be made relatively large. In particular, in this embodiment, the joined body 40 is obtained by melting and integrating a plurality of resin fine particles, and there is substantially no boundary (interface) between the resin fine particles. Thereby, the above effects become more remarkable.

Moreover, the joined body 40 has a recessed part in the site | part corresponding to the joined part of the said resin fine particle which adjoins. That is, the joined body 40 has irregularities reflecting the shape of the resin fine particles (see FIG. 1).
Further, as described above, the resin fine particles (bonded body 40) may be any material as long as it is mainly composed of a binder resin. Agent, wax, charge control agent, etc.). As described above, when the resin fine particles (the bonded body 40) contain constituent components of the toner other than the binder resin, for example, the dispersibility of the constituent components in the toner particles can be made particularly high. In other words, a toner in which constituent components are uniformly mixed can be easily obtained, and the reliability of the obtained toner is particularly excellent.

  In particular, when the resin fine particles contain a colorant, the dispersibility of the colorant in the toner particles 100 can be made particularly easy. Further, when the resin fine particles contain a colorant, it is possible to effectively prevent the colorant from exuding to the outside of the toner particles 100 (unintentional colorant exudation). As a result, it is possible to effectively prevent the occurrence of so-called streaks in an image formed using toner, and it is also effective to prevent dirt from adhering to constituent members of an image forming apparatus such as a photoreceptor. Can be prevented.

  Further, if the resin fine particles contain wax, the dispersibility of the wax in the toner particles 100 can be made particularly high with relative ease. Further, when the resin fine particles contain wax, it is possible to effectively prevent the wax from exuding to the outside of the toner particles 100 (unintentional exudation of wax). As a result, it is possible to effectively prevent dirt from adhering to the constituent members of the image forming apparatus such as the photosensitive member.

  In addition, the constituent components of the toner other than the binder resin such as the colorant, the wax, and the charge control agent may not be included in the resin fine particles. For example, when the toner particle 100 (joined body 40) has fine particles (not shown) other than resin fine particles, components other than the binder resin as described above are included as constituents of the fine particles. May be. When such fine particles other than the resin fine particles are included, it is preferable that the boundary (interface) between the fine particles does not substantially exist as described above.

<Supplementary phase>
By the way, generally, a granular material produced (manufactured) from a plurality of fine particles, such as secondary particles, is inferior in mechanical stability compared to a granular material consisting of a single particle. That is, the granular body produced (manufactured) from a plurality of fine particles has a mechanically unstable portion in the vicinity of the bonding portion (contact portion) between the fine particles. Such a part is generally also present in a granular material in which fine particles are melt-bonded to each other, and particularly in the vicinity of the surface of the granular material so as to form a concave shape reflecting the shape of the fine particles. Yes. And when external force is added to a granular material, collapse (decomposition | disassembly) of a granular material occurs easily from such a site | part. Therefore, when the toner particles are composed only of a plurality of resin fine particles as described above, the width of the particle size distribution between the toner particles can be reduced relatively easily, but as the toner particles. It is difficult to obtain the required sufficient mechanical stability. As described above, when the mechanical stability is inferior, the granular material is likely to be disintegrated (decomposed) in the external addition process, the classification process, etc., so that the yield of toner production is reduced and the toner as a final product is also reduced. , Collapse in the developing machine is likely to occur, and the durability is poor. In addition, by applying a heat treatment under severe conditions to a granular material composed only of resin fine particles, a plurality of resin fine particles are completely integrated, and there are substantially no recesses (unevenness) as described above. In such a case, since the modification and deterioration of the constituent material of the granular material (resin fine particles) also proceed, in the obtained toner, sufficient mechanical stability, durability, and constituent material It is extremely difficult to achieve both of these characteristics.

Therefore, the present inventor has conducted extensive research for the purpose of solving the above-described problems. As a result, a granular material (toner particle) formed by melting and joining a plurality of resin fine particles is formed near the surface. Excellent results can be obtained by having a filling phase that relaxes the degree of unevenness of the granular material (toner particles) in the recessed portion (particularly, the recessed portion formed at the site corresponding to the joint portion of the adjacent resin fine particles). It was found that it can be obtained. That is, by providing a joined body in which a plurality of resin fine particles are melt-bonded, and at least a supplementary phase formed in the recesses, while sufficiently exhibiting the effect of being manufactured from a plurality of resin fine particles, It has been found that the toner particles can be excellent in mechanical stability and durability.
Therefore, also in the present embodiment, the filling phase 42 is provided in a recess formed near the surface of the granular material 4 (toner particles 100) (see FIG. 1). With such a configuration, the toner particles 100 are excellent in mechanical strength and durability.

  Further, by providing the filling phase 42, the circularity of the toner particles 100 can be made relatively large. That is, when the granular material is an aggregate composed of a plurality of fine particles, the surface shape of the granular material reflects the shape of the fine particles, and thus has a large number of irregularities, and the circularity of the granular material. However, it is difficult to make the toner particle 100 relatively large, but the circularity of the toner particles 100 can be made relatively large by having the supplementary phase 42 as shown in the figure. Further, by having the filling phase 42, the transfer efficiency and mechanical strength of the toner particles 100 are particularly excellent, and the toner cleaning property (easy to remove the toner adhered to the photoreceptor) is also excellent. Can be. Also, the fluidity of the toner is improved.

  Further, as described above, since the mechanical stability of the toner particles 100 is improved by having the filling phase 42, in the toner manufacturing process (a process in which a relatively large external force is applied) such as the external addition process and the classification process. In addition, it is possible to effectively prevent the toner particles 100 (the granular body 4 having the joined body 40 and the supplementary phase 42) from collapsing (decomposing). For this reason, the yield of the production of toner as a final product is improved, and the amount of toner raw materials (collapsed toner particles 100) to be discarded can be suppressed. Therefore, the present invention is preferable from the viewpoint of resource saving and environmental protection.

  The filling phase 42 is formed of any material as long as it is formed in at least the recesses as described above and has a function of reducing the degree of unevenness near the surface of the granular material 4 (toner particles 100). Although there may be, it is preferable that it is comprised with the adhesive resin which has adhesiveness. As a result, the above-described effects (particularly, the effect of improving the mechanical stability of the granular material 4 (toner particles 100)) become more prominent. The filling phase (adhesive resin phase) 42 is preferably mainly composed of a thermosetting resin. Thereby, the mechanical stability of the toner particles 100 can be made particularly excellent, and the filling phase 42 can be easily formed at the time of production of the toner. The filling phase 42 may be formed in the final toner (toner particle 100) at least in the recess as described above. For example, the filling phase 42 may be in a substantially completely cured state. It may be in a semi-cured state or in an uncured state. When the material (adhesive resin) constituting the filling phase 42 is in a semi-cured or uncured state, for example, the material can be almost completely cured by heating in the fixing step, The fixing strength of the toner onto the recording medium can be made particularly excellent.

  The filling phase (adhesive resin phase) 42 is preferably mainly composed of an epoxy resin. As a result, the mechanical stability of the toner particles 100 can be further improved, and the filling phase 42 can be formed more easily during the production of the toner. Epoxy resins are particularly excellent in affinity with polyester resins, styrene- (meth) acrylic acid ester copolymers, and the like. Therefore, when the binder resin (binder resin) is made of such a material, the adhesive strength between the bonded body 40 and the filling phase 42 is particularly excellent. As a result, the mechanical properties of the toner particles 100 are increased. Stability can be further improved. The constituent material of the filling phase 42 will be described in detail later.

<Granular material>
The granular body 4 is composed of the joined body 40 and the filling phase 42 as described above.
The average particle diameter D of the granular material 4 is preferably 2 to 20 μm, and more preferably 3 to 8 μm. When the average particle diameter D of the granular material 4 is less than the lower limit value, it becomes difficult to uniformly charge the toner particles 100 and attach to the surface of the electrostatic latent image carrier (for example, a photoreceptor). The adhesion force increases, and as a result, there may be an increase in transfer residual toner and a decrease in transfer efficiency. In addition, it becomes difficult to manufacture the granular material 4 (toner particles 100). On the other hand, if the average particle diameter D of the granular material 4 exceeds the above upper limit value, the average particle diameter of the toner particles 100 also increases. The reproducibility at is reduced. As a result, the resolution is reduced.

Further, the standard deviation of the particle size between the particles of the granular material 4 is preferably 1.6 μm or less, more preferably 1.5 μm or less, and further preferably 1.3 μm or less. When the standard deviation of the particle diameter between the particles of the granular material 4 is 1.6 μm or less, variations in charging characteristics, fixing characteristics and the like are particularly small, and the reliability of the entire toner is further improved.
In addition, the granular material 4 may have a configuration (configuration not shown) other than the bonded body 40 and the supplementary phase 42. The granular material 4 may be provided with fine particles other than resin fine particles, for example. More specifically, the granular material 4 may include, for example, a colorant fine particle mainly composed of a colorant, a wax fine particle mainly composed of a wax, or the like as a structure (not shown).

<External additive>
In the present embodiment, the toner particle 100 has an external additive (not shown) in addition to the granular body 4. That is, the toner particles 100 are obtained by adding an external additive to the vicinity of the surface of the granular body 4 constituted by the joined body 40 and the filling phase 42. As described above, when the external additive is added, the balance of various characteristics (for example, charging characteristics, fluidity, releasability, etc.) required for the toner is particularly excellent.

<Toner particles>
The toner particle 100 has a coating ratio of the external additive (the ratio of the area covered by the external additive in the surface area of the granule 4, and the sphere corresponding to the average particle diameter of the external additive is 6 spheres corresponding to the average particle diameter of the toner. It is preferable that the calculated covering ratio when coated with fine packing is 100 to 300%, and more preferably 120 to 220%. When the coverage of the external additive is less than the lower limit, the function of the external additive may not be sufficiently exhibited. On the other hand, when the coverage of the external additive exceeds the upper limit, the toner fixability tends to decrease.

The toner particles 100 preferably have an average circularity R represented by the following formula (I) of 0.91 to 0.99, and more preferably 0.93 to 0.98. When the average circularity R is less than 0.91, it becomes difficult to sufficiently reduce the difference in charging characteristics between the individual toner particles 100, and the developability on the photoreceptor tends to be lowered. On the other hand, if the average circularity R is too small, toner adhesion (filming) is likely to occur on the photoreceptor, and the toner transfer efficiency may decrease. On the other hand, when the average circularity R exceeds 0.99, the transfer efficiency and mechanical strength are increased, but there is a problem that the average particle diameter is increased by promoting granulation (joining of particles). If the average circularity R exceeds 0.99, for example, it becomes difficult to remove the toner adhering to the photoreceptor or the like by cleaning.
R = L ₀ / L ₁ (I)
(Where, L ₁ [μm] is the circumference of the projected image of the toner particles to be measured, and L ₀ [μm] is a perfect circle having an area equal to the area of the projected image of the toner particles to be measured (completely (Represents the perimeter of a geometric circle)
In addition, the standard deviation of the circularity between the toner particles 100 is preferably 0.05 or less, more preferably 0.03 or less, and further preferably 0.02 or less. When the standard deviation of the circularity between the toner particles 100 is 0.05 or less, variations in charging characteristics, fixing characteristics and the like are particularly small, and the reliability of the toner as a whole is further improved.

Further, the average particle diameter D ″ of the toner particles 100 is preferably 2 to 20 μm, and more preferably 3 to 8 μm. When the average particle diameter D ″ of the toner particles 100 is less than the lower limit, it is difficult to uniformly charge the toner particles 100 and the adhesion force to the surface of the electrostatic latent image carrier (for example, a photoreceptor) is large. As a result, there may be an increase in residual toner and a decrease in transfer efficiency. In addition, it becomes difficult to manufacture the toner particles 100 (granular bodies 4). On the other hand, when the average particle diameter D ″ of the toner particles 100 exceeds the upper limit, the reproducibility of the contour portion of the image formed using the toner, particularly the development of the character image or the light pattern is lowered. As a result, the resolution is reduced.
Further, the standard deviation of the particle diameter between the toner particles 100 is preferably 1.6 μm or less, more preferably 1.5 μm or less, and further preferably 1.3 μm or less. When the standard deviation of the particle diameter between the toner particles 100 is 1.6 μm or less, variations in charging characteristics, fixing characteristics and the like are particularly reduced, and the reliability of the toner as a whole is further improved.

<Constituent materials of toner>
Next, the constituent material of toner (toner particles) (material used for toner production) will be described.
1. Binder resin (binder resin)
The binder resin (binder resin) is a component that greatly contributes to the characteristics required of the toner, such as the fixing characteristics, elastic modulus, and charging characteristics of the toner, and is the main component of the toner.
Further, the binder resin is a main component constituting the resin fine particles (the joined body 40) in the toner particles 100.

Examples of the binder resin include polystyrene, poly-α-methylstyrene, chloropolystyrene, styrene-chlorostyrene copolymer, styrene-propylene copolymer, styrene-butadiene copolymer, styrene-vinyl chloride copolymer, Styrene-vinyl acetate copolymer, styrene-maleic acid copolymer, styrene-acrylic acid ester copolymer, styrene-acrylic copolymer, styrene-methacrylic acid ester copolymer, styrene-acrylic acid ester-methacrylic acid ester Single unit containing styrene or styrene substitution product with styrene resin such as copolymer, styrene-α-chloromethyl acrylate copolymer, styrene-acrylonitrile-acrylic acid ester copolymer, styrene-vinyl methyl ether copolymer Union or copolymer, polyester Resin, epoxy resin, urethane-modified epoxy resin, silicone-modified epoxy resin, vinyl chloride resin, rosin-modified maleic acid resin, phenyl resin, polyethylene, polypropylene, ionomer resin, polyurethane resin, silicone resin, ketone resin, ethylene-ethyl acrylate copolymer A coalescence, a xylene resin, a polyvinyl butyral resin, a terpene resin, a phenol resin, an aliphatic or alicyclic hydrocarbon resin, and the like can be given, and one or more of these can be used in combination. Two or more different components as the binder resin (for example, resin type (classification), molecular weight, constituent monomer type / existence ratio, melting point, softening point, glass transition point, crystallinity (easiness to crystallize), etc. By using a combination of different components, the advantages of each component can be obtained, and various properties required as a toner can be simultaneously improved. More specifically, toner fixing characteristics (width of good fixing temperature range), mechanical strength (mechanical stability), chargeability (ease of chargeability and maintainability), heat resistance (storability), coloring Further improvement of various properties required for toner such as property (color reproducibility) and the balance of the properties can be made particularly excellent.
The “binder resin” used in the production of the toner may be the “binder resin” itself constituting the finally obtained toner, or a precursor of the binder resin (for example, a corresponding monomer, Dimer, trimer, oligomer, prepolymer, etc.).

2. Filling material The filling material is the main component constituting the above-described filling phase.
The filling material may be any material as long as it can constitute the filling phase 42 as described above, but is preferably composed mainly of an adhesive resin having adhesiveness. The mechanical stability of the toner particles 100 can be made particularly excellent. Moreover, it is preferable that such an adhesive resin is mainly composed of a thermosetting resin. Thereby, the mechanical stability of the toner particles 100 can be made particularly excellent, and the supplementary phase 42 can be easily formed at the time of production of the toner. The adhesive resin may be, for example, in an uncured state or in a semi-cured state when the toner is manufactured. Further, the adhesive resin may be liquid (having fluidity) when the toner is manufactured. As described above, when the adhesive resin used for the production of the toner is in a liquid state, it is excellent in handleability without using a solvent material as described later or by using a relatively small amount of solvent material (appropriate Dispersion 3 can be prepared easily and reliably. Further, when the dispersion liquid 3 described later is used in the production of the toner, the adhesive resin is preferably included in the dispersion liquid 3 as a material constituting at least a phase other than the first dispersoid 311. . Thus, the toner particles 100 (granular body 4) having the above-described configuration can be easily and reliably manufactured by a method described later.

Specific examples of the adhesive resin include polystyrene, poly-α-methylstyrene, chloropolystyrene, styrene-chlorostyrene copolymer, styrene-propylene copolymer, styrene-butadiene copolymer, and styrene-vinyl chloride copolymer. Polymer, styrene-vinyl acetate copolymer, styrene-maleic acid copolymer, styrene-acrylic acid ester copolymer, styrene-methacrylic acid ester copolymer, styrene-acrylic acid ester-methacrylic acid ester copolymer, styrene -Styrene resins such as methyl α-chloroacrylate copolymer, styrene-acrylonitrile-acrylate ester copolymer, styrene-vinyl methyl ether copolymer, vinyl resins such as acrylic resin and methacrylic resin, polyester Resin, epoxy resin, urethane Resin, hydrocarbon resin, amine resin, natural rubber, and the like. Among these, one kind or two or more kinds can be used in combination. Among these, it is preferable that the adhesive resin is mainly composed of an epoxy resin. Thereby, the mechanical stability of the toner particles 100 can be further improved, and the filling phase (adhesive resin phase) 42 can be formed more easily during the production of the toner. Epoxy resins are particularly excellent in affinity with polyester resins, styrene- (meth) acrylic acid ester copolymers, and the like. Therefore, when the binder resin (binder resin) is made of such a material, the adhesive strength between the bonded body 40 and the filling phase 42 is particularly excellent. As a result, the mechanical properties of the toner particles 100 are increased. Stability can be further improved.
The “complementary material (adhesive resin)” used for toner production (used as a toner production material) may constitute a dispersoid or constitute a dispersion medium in a dispersion described later. It may be a thing.

  As the adhesive resin (complementary material), a water-soluble resin (water-soluble resin) can be used at the time of toner production (adhesive resin used as a raw material for toner production). When the adhesive resin used as a raw material for toner production is a water-soluble resin, the toner can be suitably produced without using an organic solvent in the method described below. In other words, by using a water-soluble adhesive resin, the toner can be suitably manufactured by an environmentally friendly method. Further, when the adhesive resin is a water-soluble resin, the adhesive resin can be unevenly distributed in the dispersion medium in a dispersion liquid (aqueous dispersion liquid) used in a method described later. Thereby, a filling phase can be formed with a more suitable form. That is, it is possible to form a compensation phase that can more effectively exhibit the function of reducing the degree of unevenness as described above.

Further, the adhesive resin (filling material) used as a raw material for toner production is softening point Tf _1/2 (flow 1/2 softening temperature) from the above-described binder resin (binder resin used as a raw material for toner production). However, it is preferable that it is low. As a result, the toner particles 100 having the above-described structure can be easily and reliably manufactured. The softening point Tf _1/2 is, for example, a flow tester, sample amount: 1 g, die hole diameter: 1 mm, die length: 1 mm, load: 20 kgf, preheating time: 300 seconds, measurement start temperature: 50 ° C., The temperature rise rate can be obtained as the temperature of a point on the flow curve corresponding to h / 2 in the flowchart for analysis as shown in FIG. 2 obtained when measured under the condition of 5 ° C./min.
The “adhesive resin (complementary material)” used in the production of the toner may be the “adhesive resin” itself constituting the finally obtained toner, or a precursor (for example, a corresponding monomer) of the adhesive resin. , Dimer, trimer, oligomer, prepolymer, etc.).

3. Colorant The toner (toner particles 100) usually contains a colorant. As the colorant, for example, a pigment, a dye, or the like can be used. Examples of such pigments and dyes include carbon black, spirit black, lamp black (CI No. 77266), magnetite, titanium black, chrome lead, cadmium yellow, mineral fast yellow, navel yellow, and naphthol yellow S. , Hansa Yellow G, Permanent Yellow NCG, Chrome Yellow, Benzidine Yellow, Quinoline Yellow, Tartrazine Lake, Red Mouth Lead, Molybdenum Orange, Permanent Orange GTR, Pyrazolone Orange, Benzidine Orange G, Cadmium Red, Permanent Red 4R, Watching Red Calcium salt, eosin lake, brilliant carmine 3B, manganese purple, fast violet B, methyl violet lake, bitumen, cobalt blue, al Reblue Lake, Victoria Blue Lake, First Sky Blue, Indanthrene Blue BC, Ultramarine Blue, Aniline Blue, Phthalocyanine Blue, Calco Oil Blue, Chrome Green, Chrome Oxide, Pigment Green B, Malachite Green Lake, Phthalocyanine Green, Final Yellow Green G, Rhodamine 6G, quinacridone, rose bengal (C.I. No. 45432), C.I. I. Direct Red 1, C.I. I. Direct Red 4, C.I. I. Acid Red 1, C.I. I. Basic Red 1, C.I. I. Modern Tread 30, C.I. I. Pigment red 48: 1, C.I. I. Pigment red 57: 1, C.I. I. Pigment red 122, C.I. I. Pigment red 184, C.I. I. Direct Blue 1, C.I. I. Direct Blue 2, C.I. I. Acid Blue 9, C.I. I. Acid Blue 15, C.I. I. Basic Blue 3, C.I. I. Basic Blue 5, C.I. I. Modern Blue 7, C.I. I. Pigment blue 15: 1, C.I. I. Pigment blue 15: 3, C.I. I. Pigment blue 5: 1, C.I. I. Direct Green 6, C.I. I. Basic Green 4, C.I. I. Basic Green 6, C.I. I. Pigment yellow 17, C.I. I. Pigment yellow 93, C.I. I. Pigment yellow 97, C.I. I. Pigment yellow 12, C.I. I. Pigment yellow 180, C.I. I. Pigment yellow 162, nigrosine dye (CI No. 50415B), metal complex dye, silica, aluminum oxide, magnetite, maghemite, various ferrites, cupric oxide, nickel oxide, zinc oxide, zirconium oxide, titanium oxide, Examples thereof include metal oxides such as magnesium oxide and magnetic materials containing magnetic metals such as Fe, Co, and Ni, and one or more of these can be used in combination. As the colorant, various color formers, fluorescent substances, phosphorescent substances, and the like may be used.

4). Wax The toner (toner particle 100) may contain a wax as a constituent component.
By including wax in the toner (toner particles 100), for example, the releasability of the toner particles can be improved.

  Examples of the wax include hydrocarbon waxes such as ozokerite, ceresin, paraffin wax, microwax, microcrystalline wax, petrolatum, Fischer-Tropsch wax, carnauba wax, rice wax, methyl laurate, methyl myristate, palmitic acid. Methyl, methyl stearate, butyl stearate, candelilla wax, cotton wax, wood wax, beeswax, lanolin, montan wax, fatty acid ester ester wax, polyethylene wax, polypropylene wax, oxidized polyethylene wax, oxidized polypropylene wax Olefin waxes such as 12-hydroxy stearamide, stearamide, phthalic anhydride amide wax, Lauro , Ketone waxes such as stearone, ether waxes, and the like, can be used singly or in combination of two or more of them.

Melting point _{T m} of a wax is not particularly limited, but is preferably 30 to 160 ° C., and more preferably 50 to 100 ° C.. Note that, for example, by differential scanning calorimetry (DSC), the temperature is increased to 200 ° C. at a temperature increase rate of 10 ° C./min, and further the temperature decrease rate is 10 ° C./min, and then the temperature increase rate is 10 ° C./min. The melting point T _m and the heat of fusion can be determined from the measurement under the condition of increasing the temperature at

5). External Additive The toner (toner particles 100) may contain an external additive as a constituent component.
Examples of the external additive include titanium oxide, silica (positively charged silica, negatively charged silica, etc.), aluminum oxide, strontium titanate, cerium oxide, magnesium oxide, chromium oxide, zinc oxide, alumina, magnetite, and the like. Fine particles composed of inorganic materials such as oxides, nitrides such as silicon nitride, carbides such as silicon carbide, metal salts such as calcium sulfate, calcium carbonate, and aliphatic metal salts, acrylic resins, fluororesins, polystyrene resins, polyesters Examples include resins and organic metal materials such as aliphatic metal salts (for example, magnesium stearate).

Among the external additives, examples of the titanium oxide that can be used as the external additive include rutile type titanium oxide, anatase type titanium oxide, and rutile anatase type titanium oxide.
The rutile anatase type titanium oxide has a rutile type titanium oxide (titanium dioxide) and a crystal structure anatase type titanium oxide (titanium dioxide) in the same particle. That is, the rutile anatase type titanium oxide has a mixed crystal type titanium oxide (titanium dioxide) of a rutile type crystal and an anatase type crystal.

Rutile-type titanium oxide usually has the property of easily forming spindle-shaped crystals. In addition, anatase type titanium oxide has the property of easily depositing fine crystals and being excellent in affinity with a silane coupling agent or the like used for hydrophobizing treatment or the like.
And since rutile anatase type titanium oxide has a mixed crystal type titanium oxide of a rutile type crystal and an anatase type crystal, the advantage of the rutile type titanium oxide and the advantage of the anatase type titanium oxide And have both. That is, in the rutile-anatase type titanium oxide, minute anatase-type crystals are mixed between the rutile-type crystals (inside the rutile-type crystals), and the whole has a substantially spindle shape. The rutile-anatase type titanium oxide powder is difficult to embed in the mother particle (granular material 4) and has excellent affinity with the silane coupling agent as the whole rutile-anatase-type titanium oxide. A uniform and stable hydrophobic film (silane coupling film) is easily formed on the surface of the film. Therefore, the toner obtained by containing the rutile-anatase type titanium oxide has a uniform charge distribution (the charge distribution of the toner particles is sharp), a stable charge characteristic, environmental characteristics (especially moisture resistance), and fluidity. And excellent caking resistance.

  The abundance ratio of the rutile-type titanium oxide and the anatase-type titanium oxide in the rutile-anatase-type titanium oxide is not particularly limited, but is preferably 5:95 to 95: 5 by weight, and 50:50 More preferably, it is -90: 10. By using such a rutile-anatase type titanium oxide, the effect by using the above-mentioned rutile-anatase type titanium oxide becomes more remarkable.

Further, the rutile-anatase type titanium oxide preferably absorbs light in a wavelength region of 300 to 350 nm. Thereby, the toner has excellent light resistance (particularly, light resistance after fixing on a recording medium).
The shape of the rutile-anatase type titanium oxide is not particularly limited, but it is generally a spindle shape.

  When the rutile-anatase type titanium oxide has a substantially spindle shape, the average major axis diameter is preferably 10 to 100 nm, and more preferably 20 to 50 nm. When the average major axis diameter is in such a range, the rutile-anatase type titanium oxide can sufficiently exhibit the above-described functions, and is contained in the toner base particles (granular body 4). It is difficult to be buried and difficult to release. As a result, the stability of the toner against mechanical stress is further improved.

  The content of the rutile-anatase type titanium oxide in the toner is not particularly limited, but is preferably 0.1 to 2.0 wt%, and more preferably 0.5 to 1.0 wt%. If the content of the rutile-anatase type titanium oxide is less than the lower limit, the effect of using the rutile-anatase type titanium oxide as described above may not be sufficiently exhibited. On the other hand, when the content of the rutile-anatase type titanium oxide exceeds the upper limit, the toner fixing property tends to be lowered.

  Such a rutile-anatase type titanium oxide may be prepared by any method, but can be obtained, for example, by firing anatase-type titanium oxide. By using such a method, the abundance ratio of the rutile-type titanium oxide and the anatase-type titanium oxide in the rutile-anatase-type titanium oxide can be controlled relatively easily and reliably. When obtaining a rutile-anatase type titanium oxide by such a method, it is preferable that a calcination temperature is about 700-1000 degreeC. By setting the firing temperature within this range, it is possible to more easily and reliably control the abundance ratio of rutile titanium oxide and anatase titanium oxide in rutile anatase titanium oxide. Become.

  Among the external additives, examples of silica that can be used as the external additive include positively charged silica and negatively charged silica. The positively chargeable silica can be obtained, for example, by subjecting negatively chargeable silica to a surface treatment with a silane coupling agent having a functional group such as an amino group. When negatively chargeable silica is used as the external additive, the charge amount (absolute value) of the toner particles can be increased. As a result, a stable negatively chargeable toner can be obtained, and the toner control of the image forming apparatus can be easily performed.

Further, when negatively chargeable silica is used in combination with the rutile-anatase type titanium oxide described above, a particularly excellent effect is obtained. In other words, by using negatively-charged silica and rutile-anatase type titanium oxide in combination, the fluidity and environmental characteristics (especially moisture resistance) of the toner can be further improved, and more stable tribocharging can be exhibited. Thus, the occurrence of so-called fog can be more effectively prevented. Further, by using negatively-charged silica and rutile-anatase type titanium oxide in combination, the obtained toner can have a large charge amount (absolute value) and a sharper charge distribution.
When the average major axis diameter of the substantially spindle-shaped rutile-anatase type titanium oxide is D ₁ [nm] and the average particle diameter of the negatively chargeable silica is D ₂ [nm], 0.2 ≦ D ₁ / D ₂ ≦ It is preferable that the relationship of 15 is satisfied, and it is more preferable that the relationship of 0.4 ≦ D ₁ / D ₂ ≦ 5 is satisfied. By satisfying such a relationship, the effect of using negatively charged silica and rutile-anatase type titanium oxide in combination becomes even more remarkable. In the present specification, the “average particle diameter” refers to a volume-based average particle diameter.

Further, when positively chargeable silica is used as the external additive, for example, the positively chargeable silica can function as a microcarrier, and the chargeability of the toner particles themselves can be further improved. In particular, by using the positively chargeable silica in combination with the aforementioned rutile-anatase type titanium oxide, the toner obtained can have a large charge amount (absolute value) and a sharper charge distribution. .
When positively charged silica is included, the average particle size is preferably 30 to 100 nm, and more preferably 40 to 50 nm. When the average particle diameter of the positively chargeable silica is in such a range, the above-described effect becomes more remarkable.

  Examples of the external additive include liquid external additives such as straight silicone oil, polyether-modified silicone oil, carboxyl-modified silicone oil, epoxy-modified silicone oil, methacryl-modified silicone oil, amino-modified silicone oil, and aminopolyether silicone oil. An agent may be used.

Further, as the external additive, HMDS, a silane coupling agent (for example, one having a functional group such as an amino group), titanate coupling agent on the surface of the fine particles composed of the above-described materials. In addition, a surface treatment (for example, a hydrophobization treatment or the like) with a fluorine-containing silane coupling agent, silicone oil, or the like may be used.
Further, at least a part of the components used as the external additive may be contained in the toner particles in the finally obtained toner.

6). Other Components The toner (toner particles 100) may contain components other than the binder resin, the filling material, the colorant, the wax, and the external additive as its constituent components. Examples of such components include a charge control agent, a dispersant, and magnetic powder.
Examples of the charge control agent include benzoic acid metal salts, salicylic acid metal salts, alkyl salicylic acid metal salts, catechol metal salts, metal-containing bisazo dyes, nigrosine dyes, tetraphenylborate derivatives, quaternary ammonium salts, Examples thereof include alkyl pyridinium salts, chlorinated polyesters, and nitrohumic acid.

Examples of the dispersant include metal soap, inorganic metal salt, organic metal salt, and polyethylene glycol.
Examples of the metal soap include tristearic acid metal salts (for example, aluminum salts), distearic acid metal salts (for example, aluminum salts, barium salts, etc.), stearic acid metal salts (for example, calcium salts, lead salts, zinc salts, etc.) ), Linolenic acid metal salts (eg, cobalt salts, manganese salts, lead salts, zinc salts, etc.), octanoic acid metal salts (eg, aluminum salts, calcium salts, cobalt salts, etc.), oleic acid metal salts (eg, calcium salts) , Cobalt salts, etc.), palmitic acid metal salts (eg, zinc salts, etc.), naphthenic acid metal salts (eg, calcium salts, cobalt salts, manganese salts, lead salts, zinc salts, etc.), resinic acid metal salts (eg, calcium Salt, cobalt salt, manganese salt, lead salt, zinc salt, etc.).

Examples of the inorganic metal salt and the organic metal salt include a cation of an element selected from the group consisting of metals of Group IA, Group IIA, and Group IIIA of the periodic table as a cationic component, and an anion Examples of the property component include salts containing an anion selected from the group consisting of halogen, carbonate, acetate, sulfate, borate, nitrate, and phosphate.
Examples of the magnetic powder include magnetite, maghemite, various ferrites, cupric oxide, nickel oxide, zinc oxide, zirconium oxide, titanium oxide, magnesium oxide, and other metal oxides such as Fe, Co, and Ni. The thing comprised with the magnetic material containing a magnetic metal etc. are mentioned.

In addition to the above materials, for example, zinc stearate, zinc oxide, cerium oxide, iron oxide, fatty acid, fatty acid metal salt and the like may be used as the additive.
Further, for example, the toner may contain at least a part of components (for example, a solvent, a dispersion medium, a dispersant, a dispersion aid, an emulsifier, etc.) used at the time of preparing a dispersion described later. Good.

[Toner Production Method]
Next, an example of a method for producing the toner (aggregate of toner particles 100) as described above will be described.
FIG. 3 is a longitudinal sectional view schematically showing an example of the configuration of a kneader and a cooler for producing a kneaded product used for preparing the dispersion, and FIG. 4 is a preferred apparatus for preparing the dispersion. FIG. 5 is a longitudinal sectional view schematically showing the embodiment, FIG. 5 is an enlarged sectional view of the vicinity of the chamber of the apparatus shown in FIG. 4, and FIG. 6 is a preferred embodiment of the toner manufacturing apparatus used for manufacturing the toner of the present invention. FIG. 7 is a cross-sectional view schematically showing a preferred embodiment of a nozzle for injecting a dispersion liquid as fine particles, and FIGS. 8, 9 and 10 are other nozzles for injecting a dispersion liquid as fine particles. FIG. 11 is an enlarged cross-sectional view of the main part of the nozzle shown in FIG. 10, FIG. 12 is an enlarged cross-sectional view showing the tip of the inner intermediate ring of the nozzle shown in FIG. 11, and FIG. Sectional drawing which shows other embodiment of the nozzle which injects a liquid as microparticles | fine-particles, 14 is an enlarged cross-sectional view of the main part of the nozzle shown in FIG. 13, FIG. 15 is an enlarged cross-sectional view of the tip of the inner intermediate ring of the nozzle shown in FIG. 13, and FIG. 16 is another nozzle that ejects the dispersion liquid as fine particles. FIG. 17 is a plan view of the gas peeling recess shown in FIG. 16, and FIG. 18 is a cross-sectional view showing another embodiment of a nozzle for injecting a dispersion liquid as fine particles. Hereinafter, in FIG. 3, the left side is assumed to be “base end” and the right side is assumed to be “tip”.

  The toner production method of the present embodiment includes a step of preparing a dispersion (suspension) using a kneaded material obtained by kneading a material containing a binder resin (dispersion preparation step), and finely dispersing the dispersion. By spraying as droplets (fine particles) and solidifying (including semi-solidification) while transporting inside the solidified part, a granular material having a joined body formed by melting and joining a plurality of resin fine particles and a filling phase A step of obtaining a body (granule production step) and a step of applying an external additive to the obtained granule (external additive application step). The dispersion liquid in the present embodiment is sufficient if it contains at least a binder resin, but in the following description, a dispersion mainly containing a binder resin and a filling material (adhesive resin) as constituent components. The case where the liquid is used will be described, and the case where the first liquid (dispersion liquid) containing the binder resin and the second liquid containing the filling material (adhesive resin) are used together will also be described. Examples of the dispersion include an emulsion (emulsion) and a suspension (suspension). Among these, it is preferable to use a suspension. By using the suspension, variation in shape among the toner particles 100 can be easily reduced in the finally obtained toner. Further, it is possible to more effectively prevent the solvent and the like from remaining in the finally obtained toner. In this specification, “suspension” refers to a dispersion (including a suspended colloid) in which a solid (solid) dispersoid (suspended particle) is dispersed in a liquid dispersion medium. The term “emulsified liquid (emulsion, emulsion, milky liquid)” refers to a dispersion in which a liquid dispersoid (dispersed particles) is dispersed in a liquid dispersion medium. In the following description, a case where a suspension is used as a dispersion will be described as a representative.

<Kneaded material>
In the present embodiment, first, a kneaded material K7 is obtained using a raw material K5 containing at least a binder resin among the toner constituent materials described above.
The kneaded material K7 can be manufactured using, for example, an apparatus as shown in FIG.
<Kneading process>
As described above, the raw material K5 subjected to kneading includes at least a binder resin as a constituent material of the toner, but includes components other than the binder resin such as a colorant, a wax, and a charge control agent. Is preferred. Thereby, for example, the dispersibility of the constituent components in the finally obtained toner particles 100 can be made particularly high. In other words, a toner in which constituent components are uniformly mixed can be easily obtained, and the reliability of the obtained toner can be made particularly excellent. Moreover, it is preferable that the raw material K5 used for kneading is obtained by previously mixing these components. Thereby, the effect mentioned above becomes further remarkable.

This embodiment demonstrates the structure which uses a biaxial kneading extruder as a kneading machine.
The kneading machine K1 includes a process part K2 for kneading while conveying the raw material K5, a head part K3 for extruding the kneaded raw material (kneaded material K7) into a predetermined cross-sectional shape, and a raw material K5 in the process part K2. And a feeder K4 to be supplied.
The process part K2 includes a barrel K21, a screw K22 and a screw K23 inserted into the barrel K21, and a fixing member K24 for fixing the head part K3 to the tip of the barrel K21.

In the process part K2, when the screw K22 and the screw K23 rotate, a shearing force is applied to the raw material K5 supplied from the feeder K4, and a uniform kneaded material K7 (especially a binder resin (binder resin as a main component) ) Contains two or more components, a kneaded material K7) in which these resin components are sufficiently finely dispersed or compatibilized is obtained.
The total length of the process part K2 is preferably 50 to 300 cm, and more preferably 100 to 250 cm. If the total length of the process part K2 is less than the lower limit, for example, when the raw material K5 contains two or more components that are difficult to disperse or compatible with each other, these components are sufficiently finely dispersed or compatibilized. May be difficult. On the other hand, when the total length of the process part K2 exceeds the upper limit, depending on the temperature in the process part K2, the number of rotations of the screw K22, the screw K23, and the like, the material K5 is easily denatured by heat, and finally obtained. It may be difficult to sufficiently control the physical properties of the toner.

  Moreover, although the raw material temperature at the time of kneading | mixes changes with compositions etc. of the raw material K5, it is preferable that it is 80-260 degreeC, and it is more preferable that it is 90-230 degreeC. Note that the raw material temperature in the process part K2 may be uniform or may vary depending on the part. For example, the process unit K2 includes a first region having a relatively low set temperature and a second region that is provided on the base end side from the first region and whose set temperature is higher than the first region. You may have.

  In addition, the residence time (time required for passage) of the raw material K5 in the process part K2 is preferably 0.5 to 12 minutes, and more preferably 1 to 7 minutes. When the residence time in the process part K2 is less than the lower limit, for example, when the raw material K5 contains two or more components that are difficult to disperse or compatible with each other, these components are sufficiently finely dispersed or phased. It may be difficult to solubilize. On the other hand, if the residence time in the process part K2 exceeds the upper limit, the production efficiency is reduced. Depending on the temperature in the process part K2, the rotational speed of the screw K22, the screw K23, etc., the heat of the raw material K5 Modification tends to occur, and it may be difficult to sufficiently control the physical properties of the finally obtained toner.

  The number of rotations of the screw K22 and the screw K23 varies depending on the composition of the binder resin and the like, but is preferably 50 to 600 rpm. When the rotational speed of the screw K22 and the screw K23 is less than the lower limit, for example, when the raw material K5 contains two or more components that are difficult to disperse or compatible with each other, these components are sufficiently finely dispersed or Compatibilization may be difficult. On the other hand, when the rotation speed of the screw K22 and the screw K23 exceeds the upper limit, the molecular chain of the binder resin may be cut by shearing, and the properties of the binder resin may be deteriorated.

  Further, in the kneader K1 used in the present embodiment, the inside of the process unit K2 is connected to the pump P via the deaeration port K25. Thereby, the inside of the process part K2 can be degassed, and an increase in the pressure in the process part K2 due to heating or heat generation of the raw material K5 (kneaded material K7) can be prevented. As a result, the kneading process can be performed safely and efficiently. Further, since the inside of the process part K2 is connected to the pump P via the deaeration port K25, it is possible to effectively prevent bubbles (particularly relatively large bubbles) from being contained in the obtained kneaded material K7. And the properties of the finally obtained toner can be made more excellent.

<Extrusion process>
The kneaded material K7 kneaded in the process part K2 is pushed out of the kneader K1 through the head part K3 by the rotation of the screw K22 and the screw K23.
The head part K3 has an internal space K31 into which the kneaded material K7 is fed from the process part K2, and an extrusion port K32 from which the kneaded material K7 is extruded.
The temperature of the kneaded material K7 in the internal space K31 (at least the temperature near the extrusion port K32) is not particularly limited, but is preferably 80 to 150 ° C, more preferably 90 to 140 ° C. When the temperature of the kneaded material K7 in the internal space K31 is a value within the above range, the kneaded material K7 does not solidify in the internal space K31 and is easily extruded from the extrusion port K32.

  In the illustrated configuration, the internal space K31 has a cross-sectional area gradually decreasing portion K33 in which the cross-sectional area gradually decreases in the direction of the extrusion port K32. By having such a cross-sectional area gradually decreasing portion K33, the extrusion amount of the kneaded material K7 extruded from the extrusion port K32 is stabilized, and the cooling rate of the kneaded material K7 in the cooling step described later is stabilized. As a result, the toner produced using the toner has a small variation in characteristics among the toner particles, and has excellent overall characteristics.

《Cooling process》
The softened kneaded material K7 extruded from the extrusion port K32 of the head part K3 is cooled by the cooler K6 and solidified.
The cooler K6 includes rolls K61, K62, K63, and K64, and belts K65 and K66.
The belt K65 is wound around a roll K61 and a roll K62. Similarly, the belt K66 is wound around the roll K63 and the roll K64.

  The rolls K61, K62, K63, and K64 rotate around the rotation axes K611, K621, K631, and K641 in the directions indicated by e, f, g, and h in the drawing. Thereby, the kneaded material K7 extruded from the extrusion port K32 of the kneading machine K1 is introduced between the belt K65 and the belt K66. The kneaded material K7 introduced between the belt K65 and the belt K66 is cooled while being formed into a plate shape having a substantially uniform thickness. The cooled kneaded material K7 is discharged from the discharge portion K67. The belts K65 and K66 are cooled by a method such as water cooling or air cooling. When such a belt type is used as the cooler, the contact time between the kneaded product extruded from the kneader and the cooling body (belt) can be increased, and the cooling efficiency of the kneaded product is particularly excellent. Can be.

  By the way, in the kneading process, since a shearing force is applied to the raw material K5, even if the raw material K5 contains two or more components that are difficult to disperse or compatible with each other, phase separation (particularly, macrophase separation). However, the kneaded product K7 that has finished the kneading process is not subjected to a shearing force. Therefore, if it is left for a long period of time, it may cause phase separation (macro phase separation) again. is there. Therefore, it is preferable to cool the kneaded material K7 obtained as described above as soon as possible. Specifically, the cooling rate of the kneaded material K7 (for example, the cooling rate when the kneaded material K7 is cooled to about 60 ° C.) is preferably −3 ° C./second or more, and is preferably −5 to −100 ° C. / More preferably it is seconds. Further, the time required from the end of the kneading step (when the shearing force is no longer applied) to the completion of the cooling step (for example, the time required for cooling the temperature of the kneaded product K7 to 60 ° C. or lower) is 20 seconds. Or less, more preferably 3 to 12 seconds.

In the above description, in the embodiment, the configuration using a continuous twin-screw kneading extruder as the kneading machine has been described, but the kneading machine used for kneading the raw materials is not limited to this. For kneading the raw materials, for example, various kneaders such as a kneader, a batch type triaxial roll, a continuous biaxial roll, a wheel mixer, and a blade type mixer can be used.
In the illustrated configuration, the kneader having two screws has been described. However, the number of screws may be one or three or more. Further, the kneading apparatus may have a disc (kneading disc) portion.

Further, in the present embodiment, the configuration using one kneader has been described, but kneading may be performed using two kneaders. In this case, the heating temperature of the raw material, the rotational speed of the screw, and the like may be different between one kneader and the other kneader.
In the above description, the belt-type configuration is used as the cooler. However, for example, a roll-type (cooling roll-type) cooler may be used. Further, the cooling of the kneaded product extruded from the extrusion port K32 of the kneader is not limited to the one using the above-described cooler, and may be performed by, for example, air cooling.

<< Crushing process >>
Next, the kneaded material K7 that has undergone the cooling process as described above is pulverized. Thus, by pulverizing the kneaded material K7, the dispersibility of the dispersoid 31 (first dispersoid 311) in the dispersion 3 (droplets 9) described later can be made particularly excellent. Therefore, even in the finally obtained toner, variations in composition and characteristics among the toner particles are reduced. As a result, the obtained toner has particularly excellent overall characteristics.

The pulverization method is not particularly limited, and for example, it can be performed using various pulverizers such as a ball mill, a vibration mill, a jet mill, and a pin mill, and a crusher.
The pulverization process may be performed in multiple steps (for example, two stages of a coarse pulverization process and a fine pulverization process).
In addition, after such a pulverization step, a classification process or the like may be performed as necessary.

For the classification treatment, for example, a sieve, an airflow classifier or the like can be used.
In this embodiment, a dispersion liquid is prepared using the kneaded material as described above.
By using the kneaded material K7 for the preparation of the dispersion 3, the following effects can be obtained. That is, even when the toner constituent material (the constituent material of the resin fine particles) contains components that are difficult to disperse or compatible with each other, each component is sufficiently contained in the kneaded product obtained by kneading. It can be in a state of being compatible and finely dispersed. As a result, even if the component material of the toner contains a component (hereinafter also referred to as “hardly dispersible component”) inferior in dispersibility with respect to the dispersion medium of the dispersion described later, the dispersion 3 (liquid The dispersibility of the dispersoid 31 (first dispersoid 311) in the droplet 9) can be made particularly excellent. As a result, even in the finally obtained toner, variations in composition and characteristics among the toner particles are reduced. As a result, the obtained toner has particularly excellent overall characteristics.
Next, the dispersion 3 prepared using the kneaded material as described above (cooled and solidified kneaded material) and a method for preparing the dispersion 3 will be described.

<Dispersion>
As described above, the toner particles 100 can be manufactured using the dispersion liquid (suspension) 3. Hereinafter, the configuration of the dispersion liquid 3 and the method for preparing the dispersion liquid 3 will be described.
<Composition of dispersion>
First, the configuration of the dispersion 3 will be described.
The dispersion 3 has a configuration in which a dispersoid (dispersed phase) 31 is finely dispersed in a dispersion medium 32. The dispersion 3 includes at least a first dispersoid 311 mainly composed of a binder resin as the dispersoid 31. In particular, in the present embodiment, the dispersion 3 containing the first dispersoid 311 and the second dispersoid 312 mainly composed of a filling material (adhesive resin) is used as the dispersoid 31.

1. Dispersion Medium The dispersion medium 32 may be any material as long as it can disperse the dispersoid 31 described later, but is mainly a material generally used as a solvent (hereinafter referred to as “solvent material”). It is preferable that it is comprised by these.
Examples of such materials include inorganic solvents such as water, carbon disulfide, and carbon tetrachloride, methyl ethyl ketone (MEK), acetone, diethyl ketone, methyl isobutyl ketone (MIBK), methyl isopropyl ketone (MIPK), cyclohexanone, Ketone solvents such as 3-heptanone and 4-heptanone, methanol, ethanol, n-propanol, isopropanol, n-butanol, i-butanol, t-butanol, 3-methyl-1-butanol, 1-pentanol, 2- Alcohol solvents such as pentanol, n-hexanol, cyclohexanol, 1-heptanol, 1-octanol, 2-octanol, 2-methoxyethanol, allyl alcohol, furfuryl alcohol, phenol, diethyl ether, dipropyl ether Ether solvents such as diisopropyl ether, dibutyl ether, 1,2-dimethoxyethane (DME), 1,4-dioxane, tetrahydrofuran (THF), tetrahydropyran (THP), anisole, diethylene glycol dimethyl ether (diglyme), 2-methoxyethanol Cellosolve solvents such as methyl cellosolve, ethyl cellosolve, phenyl cellosolve, aliphatic hydrocarbon solvents such as hexane, pentane, heptane, cyclohexane, methylcyclohexane, octane, didecane, methylcyclohexene, isoprene, toluene, xylene, benzene, ethylbenzene , Aromatic hydrocarbon solvents such as naphthalene, pyridine, pyrazine, furan, pyrrole, thiophene, 2-methylpyridine, 3-methylpyridine, 4-methyl Aromatic heterocyclic compound solvents such as pyridine and furfuryl alcohol, amide solvents such as N, N-dimethylformamide (DMF) and N, N-dimethylacetamide (DMA), dichloromethane, chloroform, 1,2-dichloroethane, Halogenated solvents such as trichloroethylene and chlorobenzene, acetylacetone, ethyl acetate, methyl acetate, isopropyl acetate, isobutyl acetate, isopentyl acetate, ethyl chloroacetate, butyl chloroacetate, isobutyl chloroacetate, ethyl formate, isobutyl formate, ethyl acrylate, methacrylic acid Ester solvents such as methyl acid and ethyl benzoate, amine solvents such as trimethylamine, hexylamine, triethylamine and aniline, nitrile solvents such as acrylonitrile and acetonitrile, nitromethane, Examples include nitro solvents such as nitroethane, organic solvents such as aldehyde solvents such as acetaldehyde, propionaldehyde, butyraldehyde, pentanal, and acrylic aldehyde. A mixture of one or more selected from these is used. be able to.

  Among the above materials, the dispersion medium 32 is mainly composed of water and / or a water-soluble liquid (a liquid having excellent compatibility with water (for example, a liquid having a solubility in 100 g of water at 25 ° C. of 30 g or more)). It is preferable that Thereby, for example, the dispersibility of the dispersoid 31 (first dispersoid 311) in the dispersion medium 32 can be increased, and the dispersoid 31 in the dispersion 3 can be made relatively small in particle size and large. The variation in thickness can be reduced. As a result, the obtained granular material (toner mother particles) 4 has small variations in size and shape among the particles, and has a relatively large circularity. In particular, when the dispersion medium 32 is composed of water, for example, in the toner manufacturing process, the organic solvent can be substantially prevented from volatilizing. As a result, the toner can be produced by a method that hardly causes adverse effects on the environment, that is, an environmentally friendly method.

  When a mixture of a plurality of components is used as the constituent material of the dispersion medium 32, the constituent material of the dispersion medium 32 is an azeotrope (lowest boiling azeotrope mixture) between at least two components constituting the mixture. ) Is preferably used. As a result, the dispersion medium 32 can be efficiently removed in a solidifying section or the like of a toner manufacturing apparatus described later. In addition, it becomes possible to remove the dispersion medium 32 at a relatively low temperature in a solidification section or the like of a toner manufacturing apparatus to be described later, and it is possible to more effectively prevent deterioration of the characteristics of the obtained granular material (toner mother particles) 4. . For example, liquids that can form an azeotrope with water include carbon disulfide, carbon tetrachloride, methyl ethyl ketone (MEK), acetone, cyclohexanone, 3-heptanone, 4-heptanone, ethanol, n-propanol, Isopropanol, n-butanol, i-butanol, t-butanol, 3-methyl-1-butanol, 1-pentanol, 2-pentanol, n-hexanol, cyclohexanol, 1-heptanol, 1-octanol, 2-octanol 2-methoxyethanol, allyl alcohol, furfuryl alcohol, phenol, dipropyl ether, dibutyl ether, 1,4-dioxane, anisole, 2-methoxyethanol, hexane, heptane, cyclohexane, methylcyclohexane, octane, dideca , Methylcyclohexene, isoprene, toluene, benzene, ethylbenzene, naphthalene, pyridine, 2-methylpyridine, 3-methylpyridine, 4-methylpyridine, furfuryl alcohol, chloroform, 1,2-dichloroethane, trichloroethylene, chlorobenzene, acetylacetone, acetic acid Ethyl acetate, methyl acetate, isopropyl acetate, isobutyl acetate, isopentyl acetate, ethyl chloroacetate, butyl chloroacetate, isobutyl chloroacetate, ethyl formate, isobutyl formate, ethyl acrylate, methyl methacrylate, ethyl benzoate, trimethylamine, hexylamine, triethylamine Aniline, acrylonitrile, acetonitrile, nitromethane, nitroethane, acrylic aldehyde and the like.

Moreover, the boiling point of the dispersion medium 32 (dispersion medium 32 to be removed in the subsequent step) is not particularly limited, but is preferably 180 ° C. or less, more preferably 150 ° C. or less, and 35 to 130 ° C. More preferably. As described above, when the boiling point of the dispersion medium 32 is relatively low, the dispersion medium 32 can be removed relatively easily in a solidifying portion or the like of the toner manufacturing apparatus described later. Moreover, by using such a material as the dispersion medium 32, the residual amount of the dispersion medium 32 in the obtained granular material 4 can be made particularly small. As a result, the reliability as a toner is further increased.
The dispersion medium 32 may contain components other than the materials described above. For example, in the dispersion medium 32, a part of the constituents of the dispersoid 31, organic fine powders such as silica, titanium oxide, and iron oxide, organic fine powders such as fatty acids, fatty acid metal salts, and polymerized fine powders. Various additives such as powder may be included.

2. Dispersoid In the present embodiment, the dispersion 3 includes, as the dispersoid 31, at least a first dispersoid 311 mainly composed of a binder resin and a second dispersion mainly composed of a filling material (adhesive resin). Quality 312 is included.
2-1. First dispersoid The first dispersoid 311 is made of a material containing at least a binder resin (binder resin), and is usually made of a material containing most of the components of the kneaded material K7 described above. ing.

  The content of the binder resin in the first dispersoid 311 is not particularly limited, but is preferably 1 to 99 wt%, and more preferably 15 to 90 wt%. When the content of the binder resin in the first dispersoid 311 is less than the lower limit, the bonding strength (fixing strength) of the finally obtained toner to a recording medium such as paper is reduced and the binding is reduced. Since components (additives such as a colorant) other than the resin are easily detached from the finally obtained toner particles, the photoreceptor and the like are easily contaminated, and durability may be reduced. On the other hand, when the content of the binder resin in the first dispersoid 311 exceeds the upper limit, the content of the colorant in the finally obtained toner is relatively lowered, resulting in insufficient colorability. However, the image density may not be sufficiently obtained.

Moreover, when the raw material K5 containing a colorant is used for the preparation of the kneaded material K7 described above, the colorant is usually contained in the first dispersoid 311 in the dispersion liquid 3 (droplets 9). .
The content of the colorant in the dispersion 3 is not particularly limited, but is preferably 0.1 to 10 wt%, and more preferably 0.3 to 3.0 wt%. When the content of the colorant is less than the lower limit, it may be difficult to form a visible image having a sufficient density depending on the type of the colorant. On the other hand, if the content of the colorant exceeds the upper limit, the fixing characteristics and charging characteristics of the finally obtained toner may be deteriorated.

Further, when the raw material K5 containing wax is used for the preparation of the kneaded material K7 described above, the wax is usually contained in the first dispersoid 311 in the dispersion 3 (droplet 9).
The wax content in the dispersion 3 is not particularly limited, but is preferably 1.0 wt% or less, and more preferably 0.5 wt% or less. When the content of the wax is too large, the wax is liberated and coarsened in the finally obtained toner particles, and the toner seeps into the toner particle surface and the transfer efficiency of the toner tends to decrease. Indicates.

In addition, the first dispersoid 311 dispersed in the dispersion medium 32 may have, for example, substantially the same composition or different composition among the respective particles. .
The average particle diameter d ₁ of the first dispersoid 311 in the dispersion 3 is not particularly limited, but is preferably 0.04 to 1.0 μm, and more preferably 0.10 to 0.80 μm. . When the average particle diameter d ₁ of the first dispersoid 311 is a value in such a range, the finally obtained granular material 4 has an appropriate degree of circularity, and has characteristics and shapes between the particles. Excellent uniformity. On the other hand, if the average particle diameter d ₁ of the first dispersoid 311 in the dispersion liquid 3 is too small, the particle diameter of the resulting granular material (toner base particles) 4 becomes too small, or the flow of the dispersion liquid 3 It may be difficult to eject the droplets 9 having a sufficiently uniform size in the granular material manufacturing process described later. On the other hand, if the average particle diameter d ₁ of the first dispersoid 311 in the dispersion 3 is too large, the particle size (toner base particles) 4 to be obtained becomes too large, or the granular material (toner base particles). It may be difficult to make the circularity of 4 sufficiently large.

Further, when the average particle size of the first dispersoid 311 in the dispersion 3 is d ₁ [μm] and the average particle size of the granular material 4 is D [μm], a relationship of 2 ≦ D / d ₁ ≦ 200 Is more preferable, 3 ≦ D / d ₁ ≦ 150 is more preferable, and 4 ≦ D / d ₁ ≦ 100 is more preferable. By satisfying such a relationship, the finally obtained toner has a particularly small variation in shape, size, composition, etc. among the respective toner particles 100 (granular bodies 4). As a result, the toner The overall characteristics are particularly excellent, and the reliability is improved. On the other hand, when D / d ₁ is less than the lower limit, the surface irregularities are relatively large with respect to the average particle diameter D of the granular material 4, and thus the fluidity tends to deteriorate. Therefore, the thin layer on the developing roller tends to be non-uniform. On the other hand, if D / d ₁ exceeds the upper limit, the irregularities on the surface of the granular material 4 become too small, and the effect of improving the transfer efficiency is lowered and the cleaning property tends to be lowered.

  Although content of the 1st dispersoid 311 in the dispersion liquid 3 is not specifically limited, It is preferable that it is 2-70 wt%, it is more preferable that it is 5-60 wt%, and it is 10-50 wt%. Further preferred. When the content of the first dispersoid 311 is less than the lower limit value, the circularity of the obtained granular material (toner base particles) 4 tends to decrease. Further, when solidifying, a large amount of heat energy may be required. On the other hand, when the content of the first dispersoid 311 exceeds the upper limit, depending on the composition of the dispersion medium 32 and the like, the viscosity of the dispersion 3 increases, and the shape of the resulting granular material (toner base particles) 4, It shows a tendency that the variation in size becomes large. In addition, if the content of the first dispersoid 311 exceeds the upper limit, it may be difficult to sufficiently atomize and eject the droplets of the dispersion 3 in the granule manufacturing process described later. .

2-2. Second Dispersoid The second dispersoid 312 is made of a material containing at least a filling material (adhesive resin). As described above, in this embodiment, the filling material is included as a constituent material of the dispersoid 31. Thus, in the dispersion liquid 3, it is preferable that the filling material is mainly contained in a phase other than the first dispersoid 311 (a phase other than a phase mainly composed of a binder resin). As a result, the toner particles 100 having the above-described configuration can be easily and reliably manufactured. In particular, when the filling material is included as a constituent material of the dispersoid 31 (second dispersoid 312) of the dispersion 3, the filling phase 42 can be efficiently formed in the recess as described above. Can do.

The average particle diameter d2 of the _second dispersoid 312 in the dispersion 3 is not particularly limited, but is preferably 0.04 to 1.0 [mu] m, and more preferably 0.10 to 0.80 [mu] m. . When the average particle diameter d2 of the _second dispersoid 312 is a value in such a range, the recesses as described above exist in the vicinity of the surface of the finally obtained granular body 4 (joined body 40). The filling phase 42 can be formed efficiently. Moreover, the granular material 4 finally obtained can be obtained as having an appropriate circularity, excellent properties and uniformity in shape among the particles, and having particularly excellent mechanical stability. it can. In contrast, when the average particle size d ₂ of the second dispersoids 312 is too small in the dispersion liquid 3, some like the content of the second dispersoids 312 in the dispersion liquid 3, filling phase in the recess It becomes difficult to form 42 efficiently. Further, when the second average particle size d ₂ of the dispersoid 312 too large in the dispersion liquid 3, some like the content of the second dispersoids 312 in the dispersion liquid 3, efficiently melt bonding the resin fine particles And the mechanical stability of the granular material 4 (toner particles 100) tends to decrease.

  The content of the second dispersoid 312 in the dispersion 3 is not particularly limited, but is preferably 2 to 80 wt%, more preferably 10 to 60 wt%, and 20 to 40 wt%. Further preferred. When the content of the second dispersoid 312 is less than the lower limit value, the circularity of the obtained granular material (toner base particles) 4 tends to decrease. Further, when solidifying, a large amount of heat energy may be required. On the other hand, when the content of the second dispersoid 312 exceeds the upper limit, depending on the composition of the dispersion medium 32 and the like, the viscosity of the dispersion 3 increases, and the shape of the obtained granular material (toner base particles) 4, It shows a tendency that the variation in size becomes large. In addition, if the content of the second dispersoid 312 exceeds the upper limit, it may be difficult to sufficiently atomize and eject the droplets of the dispersion 3 in the granular material manufacturing process described later. .

Note that the second dispersoid 312 dispersed in the dispersion medium 32 may have, for example, substantially the same composition or different composition among the particles. .
In addition, the dispersion 3 may contain components other than those described above. Examples of such components include a dispersant and a dispersion aid. Among these, when a dispersant and a dispersion aid are used, for example, the dispersibility of the dispersoid 31 in the dispersion 3 (droplets 9) can be improved.

  Examples of the dispersant include inorganic dispersants such as tricalcium phosphate, nonionic organic dispersants such as polyvinyl alcohol, carboxymethyl cellulose, polyethylene glycol, polyethylene glycol lauric acid diester, and metal tristearate (for example, aluminum salt). Etc.), distearic acid metal salts (eg, aluminum salts, barium salts, etc.), stearic acid metal salts (eg, calcium salts, lead salts, zinc salts, etc.), linolenic acid metal salts (eg, cobalt salts, manganese salts, lead) Salts, zinc salts, etc.), octanoic acid metal salts (eg, aluminum salts, calcium salts, cobalt salts, etc.), oleic acid metal salts (eg, calcium salts, cobalt salts, etc.), palmitic acid metal salts (eg, zinc salts, etc.) ), Naphthenic acid metal salts (eg calcium salts, cobalt salts, man Salts, lead salts, zinc salts, etc.), resinate metal salts (eg, calcium salts, cobalt salts, manganese salts, lead salts, zinc salts, etc.), polyacrylic acid metal salts (eg, sodium salts), polymethacryl Acid metal salt (for example, sodium salt), polymaleic acid metal salt (for example, sodium salt), acrylic acid-maleic acid copolymer metal salt (for example, sodium salt), polystyrene sulfonic acid metal salt (for example, sodium) Anionic organic dispersants such as salts) and cationic organic dispersants such as quaternary ammonium salts. Among these, nonionic organic dispersants or anionic organic dispersants are particularly preferable.

The content of the dispersant in the dispersion 3 is not particularly limited, but is preferably 3.0 wt% or less, and more preferably 0.01 to 1.0 wt%.
Examples of the dispersion aid include anions, cations, and nonionic surfactants.
The dispersing aid may be used alone without being used in combination with the dispersing agent, but is preferably used in combination with the dispersing agent. When the dispersion 3 contains a dispersant, the content of the dispersion aid in the dispersion 3 is not particularly limited, but is preferably 2.0 wt% or less, and is 0.005 to 0.5 wt%. Is more preferable.

The dispersion 3 may contain an emulsifier and the like. In particular, when the dispersion (suspension) 3 is prepared via an emulsion as described later, the emulsifier used in the preparation of the emulsion may be contained in the dispersion 3 ( May remain). For example, when the dispersion (suspension) 3 is prepared via an emulsion as described later, the dispersion 3 (particularly in the dispersoid 31) contains the solvent used for the preparation of the emulsion. May remain.
In the dispersion 3, components other than the dispersoid 31 may be dispersed as an insoluble matter. For example, in the dispersion 3, inorganic fine powders such as silica, titanium oxide, and iron oxide, organic fine powders such as fatty acids and fatty acid metal salts, and the like may be dispersed.

<< Method for Preparing Dispersion (Dispersion Preparation Step) >>
The dispersion 3 as described above can be prepared, for example, as follows (can be prepared through the following dispersion preparation step).
First, a kneaded product K7 pulverized in powder or granular form and a powdery or granular supplementary material are added to water or a water-soluble liquid to obtain a dispersion preparation liquid (pulverized product-containing liquid) 2. The average particle diameter of the kneaded material K7 in the liquid 2 for preparing a dispersion is preferably 0.1 μm to 5 mm, more preferably 1 μm to 2 mm, and further preferably 10 μm to 1 mm. Further, the average particle diameter of the filling material in the dispersion preparing liquid 2 is preferably 0.1 μm to 5 mm, more preferably 1 μm to 2 mm, and further preferably 10 μm to 1 mm.
Thereafter, the dispersion preparation liquid 2 obtained as described above is ejected from a plurality of nozzles, and the dispersion preparation liquid 2 ejected from each nozzle is caused to collide with each other, whereby the dispersion preparation liquid 2 The kneaded material K7 and the filling material contained therein are atomized, and the atomized kneaded material (first dispersoid 311) and the atomized filling material (second dispersoid 312) are mixed with the liquid (dispersion medium 32). ) To obtain dispersion 3 dispersed therein (atomization step).

More specifically, the dispersion liquid 3 can be obtained using an apparatus (atomization apparatus) as shown in FIG.
As shown in FIG. 4, the atomization apparatus B1 includes nozzles B21 and B22 for injecting the dispersion preparation liquid 2 as described above, and a dispersion preparation liquid supply unit B3 for supplying the dispersion preparation liquid 2. , A housing part B5 having a chamber part B4 for colliding the liquid for preparing a dispersion 2 ejected from the nozzle B21 and the nozzle B22, a finely divided kneaded material K7 (first dispersoid 311) and an atomized supplement And a recovery unit B6 for recovering the dispersion 3 (dispersion preparation liquid 2) containing the material (second dispersoid 312). Further, as shown in FIG. 4, the atomization apparatus B1 is supplied from the dispersion preparation liquid supply unit B3 between the dispersion preparation liquid supply unit B3 and each nozzle (nozzle B21, nozzle B22). An ultrahigh pressure generation pump B7 that pressurizes (accelerates) the dispersion preparation liquid 2 and a branching portion B8 that branches the dispersion preparation liquid 2 pressurized (acceleration) by the ultrahigh pressure generation pump B7 to each nozzle. Have.

  The dispersion preparation liquid supply unit B3 may have any function as long as it has a function of supplying the dispersion preparation liquid 2 to the ultrahigh pressure generation pump B7, but as illustrated, stirring for stirring the dispersion preparation liquid 2 It may have means B31. Thereby, for example, even if the kneaded material K7 and the filling material are difficult to disperse in the dispersion medium 32, the liquid for preparing a dispersion in a state where the powdered or granular kneaded material K7 and the filling material are sufficiently uniformly dispersed. 2 can be supplied to the ultrahigh pressure generation pump B7.

  Further, as shown in FIG. 5, the nozzle B21 and the nozzle B22 are arranged so that the dispersion liquid preparation liquid 2 ejected from each nozzle collides at a predetermined angle θ on the central axis of the chamber B4. Yes. Although this collision angle (theta) is not specifically limited, It is preferable that it is 90-180 degrees, and it is more preferable that it is 120-180 degrees. By making the collision angle θ within such a range, when two jets collide, the kinetic energy possessed by the jets is reduced with as little loss as possible, and the energy for atomizing the kneaded material K7 and the filling material ( Collision energy), the kneaded material K7 and the filling material can be efficiently atomized. On the other hand, if the collision angle θ is less than the lower limit, the loss of kinetic energy of the jet flow becomes large, and the kneaded material K7 and the filling material may not be sufficiently atomized. Note that the collision angle indicates an angle formed by two straight lines as shown in FIG. 5 and is 180 ° or less.

The kneaded material K7 and the supplementary material in the dispersion liquid 2 are atomized by the atomizer B1 as follows.
The dispersion preparation liquid 2 supplied from the dispersion preparation liquid supply section B3 into the atomization apparatus B1 is pressurized (accelerated) by the ultrahigh pressure generation pump B7 and branched by the branch section B8. Each of the branched liquid preparation liquids 2 is transported to the nozzle B21 and the nozzle B22, sprayed from the tip of each nozzle, and collides. The kneaded material K7 and the filling material in the dispersion liquid 2 are atomized by collision to obtain the dispersion 3. The dispersion 3 descends in the housing part B5 and is recovered by the recovery part B6.

  The pressure (injection pressure) for injecting the dispersion preparation liquid 2 from the nozzle B21 and the nozzle B22 is preferably 50 to 300 MPa, and more preferably 70 to 250 MPa. By setting the injection pressure within such a range, the dispersion 3 containing the dispersoid 31 (the first dispersoid 311 and the second dispersoid 312) having an appropriate particle diameter can be efficiently obtained. On the other hand, if the injection pressure is too low, the kneaded material K7 and the filling material are not sufficiently atomized, and it becomes difficult to sufficiently reduce the size of the dispersoid 31 in the obtained dispersion liquid 3. In some cases, the dispersion 3 may not be obtained (the kneaded material K7 and the filling material cannot be dispersed in the liquid). On the other hand, if the injection pressure is too high, the kneaded material K7 and the constituent materials of the filling material may be altered and deteriorated. In addition, the injection pressure in the nozzle B21 and the nozzle B22 may be the same or different.

  Further, in such a atomization step, for example, the dispersion liquid 2 may be heated (heated). Thereby, the circularity of the dispersoid 31 in the obtained dispersion liquid 3 can be made moderate, and as a result, the circularity of the finally obtained toner particles can be made relatively high. That is, by heating in this way, the kneaded material K7 in the dispersion-preparing liquid 2 and the atomized kneaded material K7 (first dispersoid 311) and the filling material while performing the atomization treatment of the filling material A thermal spheronization process can be performed on the material (second dispersoid 312).

Moreover, it is preferable that it is 20-200 degreeC, and, as for the temperature of the liquid 2 for dispersion preparation injected from each nozzle, it is more preferable that it is 40-160 degreeC. Thereby, the above-mentioned effect becomes more remarkable.
In addition, the atomizer B1 prepares a dispersion liquid in which at least a part of the dispersion liquid 3 (or the kneaded material K7 and the supplementary material is pulverized) from the recovery part B6 to the liquid supply part for dispersion preparation (dispersion liquid supply part) B3. Means for conveying the working liquid 2). That is, as shown in FIG. 4, the dispersion liquid 3 (or the kneaded product K7, the dispersion preparation liquid 2 in which at least a part of the supplementary material is crushed) To the dispersion preparation liquid supply unit B3.

  Thus, it is preferable that the atomization process is repeatedly performed. As a result, it is possible to efficiently form the dispersoid 31 having a small variation in shape among the particles and a small width of the particle size distribution. This repetition is preferably carried out until the average particle size of the obtained dispersoid 31 (first dispersoid 311 and second dispersoid 312) becomes a value within the above range. Thereby, the above-mentioned effect becomes more remarkable.

  When the dispersion 3 is prepared by the method as described above, the dispersion 3 can be prepared without substantially using an organic solvent or using an extremely small amount of an organic solvent. For this reason, it is possible to substantially prevent the organic solvent from being volatilized in a solidifying section or the like of a toner manufacturing apparatus as will be described later. As a result, the toner can be manufactured by a method that hardly causes adverse effects on the environment.

Although the preferred embodiment of the kneaded material K7 in the dispersion preparation liquid 2 and the device for atomizing the filling material (atomization device B1) has been described above, the configuration of the atomization device is not limited thereto. For example, each part constituting the atomization apparatus can be replaced with an arbitrary one that exhibits the same function, or another structure can be added.
For example, in the above-described embodiment, an apparatus using two nozzles has been described. However, the present invention is not limited to this, and three or more nozzles may be used. When three or more nozzles are used in this way, the collision angle θ of the dispersion-preparing liquid 2 ejected from the two nozzles whose tip ends are the farthest is in the above-described range. Is preferred.

  As described above, the method as described above causes the dispersion preparation liquid 2 obtained as described above to be ejected from two or more nozzles, and the dispersion preparation liquids 2 ejected from the respective nozzles are combined. It has the atomization process of making the kneaded material K7 and the supplementary material atomize by colliding. As a result, the finally obtained toner has a small variation in shape among the toner particles and a particularly small width of the particle size distribution. In addition, by performing atomization in this way, the kneaded product K7 can be atomized while more suitably maintaining the dispersion state of the additives such as wax in the kneaded product K7. As a result, the obtained toner has excellent properties such as durability, storage stability, and charging characteristics.

  Further, in the above description, the dispersion preparation liquid 2 has been described as including a supplement material, but the dispersion preparation liquid 2 may not include a supplement material. More specifically, the liquid preparation liquid 2 containing no supplement material is subjected to the same treatment as described above, and then a powdery (fine powder) supplement material is added to the treated liquid. The dispersion 3 may be prepared by adding. In addition, for example, the dispersion preparation liquid 2 containing the kneaded material K7 and not containing the supplementary material is subjected to the same treatment as described above to obtain the first liquid (binder resin suspension) and supplementing. The dispersion preparation liquid 2 containing the material and not containing the kneaded material K7 is subjected to the same treatment as above to obtain a second liquid (supplementary material suspension), and then the first liquid (condensation). The target dispersion 3 can also be obtained by mixing the (resin suspension) and the second liquid (filling material suspension). As a result, each of the kneaded material K7 and the filling material can be atomized under optimum conditions. As a result, both the first dispersoid 311 and the second dispersoid 312 have an optimum particle size distribution. In addition, it is possible to easily and reliably obtain the dispersion liquid 3 with little modification and deterioration of the constituent materials. In the above description, the filling material has been described as constituting a dispersoid (second dispersoid), but the filling material may constitute a dispersion medium. Further, when the filling material is a constituent material of the dispersion medium in this way, for example, the same treatment as described above is performed on the dispersion liquid 2 that does not include the filling material, and then the above treatment is performed. The dispersion liquid 3 can be prepared by adding a filling material to the liquid. As a result, a relatively large particle diameter filling material can be used for the preparation of the dispersion liquid 3, and the handling of the filling material is facilitated. Can be prevented.

The dispersion 3 can also be prepared by the following method. In this method, as described below, a kneaded material suspension (binder resin suspension) in which a kneaded material is dispersed as a dispersoid and a filling material suspension in which a filling material is dispersed as a dispersoid are mixed. By doing so, the target dispersion 3 is obtained.
First, preparation of a kneaded product suspension (binder resin suspension) will be described.

First, an aqueous liquid in which a dispersant and / or a dispersion aid is added to water or a water-soluble (excellent water compatibility) liquid as necessary is prepared.
On the other hand, a binder resin liquid containing the kneaded material K7 is prepared. The binder resin liquid can be prepared, for example, by using a solvent capable of dissolving at least a part of the constituent material of the kneaded material K7 (particularly, the binder resin).
Next, the dispersoid (dispersed particles) containing the binder resin is dispersed in the aqueous dispersion medium by gradually adding the binder resin liquid to the stirred aqueous liquid while dropping. An emulsified liquid (emulsion) is obtained.

  Thereafter, the solvent is removed from the obtained emulsion to obtain a kneaded product suspension (binder resin suspension) in which the kneaded product is dispersed as a dispersoid. The removal of the solvent can be performed, for example, by heating the emulsion or placing it in a reduced pressure atmosphere (solvent removal step). By using such a method, the circularity of the first dispersoid 311 in the dispersion 3 (droplet 9) can be further increased. As a result, the granular material (toner base particles) 4 can be obtained with a sufficiently high circularity and a particularly small variation in shape among the particles. In addition, when dripping the binder resin liquid, the aqueous liquid and / or the binder resin liquid may be heated. Moreover, when such a method is used, the particle size of the dispersoid (first dispersoid 311 in the dispersion 3) in the kneaded product suspension can be controlled to an appropriate size.

The solvent may be any solvent as long as it can dissolve at least a part of the constituent material (particularly the binder resin) of the kneaded product K7, but can be easily removed in the solvent removal step. It is preferred that
The solvent is preferably a solvent having low compatibility with the dispersion medium 32 described above (for example, a solvent having a solubility in 100 g of the dispersion medium at 25 ° C. of 30 g or less). Thereby, even if the removal of the solvent in the solvent removal step is insufficient, the first dispersoid 311 can be finely dispersed in a stable state in the dispersion 3 (droplet 9).

  The composition of the solvent can be appropriately selected according to, for example, the composition of the binder resin described above, the composition of the colorant, the composition of the dispersion medium 32, and the like. Examples of the solvent include inorganic solvents such as water, carbon disulfide, and carbon tetrachloride, methyl ethyl ketone (MEK), acetone, diethyl ketone, methyl isobutyl ketone (MIBK), methyl isopropyl ketone (MIPK), cyclohexanone, and 3-heptanone. , Ketone solvents such as 4-heptanone, methanol, ethanol, n-propanol, isopropanol, n-butanol, i-butanol, t-butanol, 3-methyl-1-butanol, 1-pentanol, 2-pentanol, Alcohol solvents such as n-hexanol, cyclohexanol, 1-heptanol, 1-octanol, 2-octanol, 2-methoxyethanol, allyl alcohol, furfuryl alcohol, phenol, diethyl ether, dipropyl ether, diisopropyl Ether solvents such as pyr ether, dibutyl ether, 1,2-dimethoxyethane (DME), 1,4-dioxane, tetrahydrofuran (THF), tetrahydropyran (THP), anisole, diethylene glycol dimethyl ether (diglyme), 2-methoxyethanol Cellosolve solvents such as methyl cellosolve, ethyl cellosolve, phenyl cellosolve, aliphatic hydrocarbon solvents such as hexane, pentane, heptane, cyclohexane, methylcyclohexane, octane, didecane, methylcyclohexene, isoprene, toluene, xylene, benzene, ethylbenzene , Aromatic hydrocarbon solvents such as naphthalene, pyridine, pyrazine, furan, pyrrole, thiophene, 2-methylpyridine, 3-methylpyridine, 4-methylpyridine Aromatic heterocyclic compound solvents such as furfuryl alcohol, amide solvents such as N, N-dimethylformamide (DMF), N, N-dimethylacetamide (DMA), dichloromethane, chloroform, 1,2-dichloroethane, trichlorethylene, Halogenated solvents such as chlorobenzene and carbon tetrachloride, acetylacetone, ethyl acetate, methyl acetate, propyl acetate, isopropyl acetate, butyl acetate, isobutyl acetate, isopentyl acetate, ethyl chloroacetate, butyl chloroacetate, isobutyl chloroacetate, ethyl formate, Ester solvents such as isobutyl formate, ethyl acrylate, methyl methacrylate and ethyl benzoate; amine solvents such as trimethylamine, hexylamine, triethylamine and aniline; and nitric acids such as acrylonitrile and acetonitrile. Organic solvents such as tolyl solvents, nitro solvents such as nitromethane and nitroethane, and aldehyde solvents such as acetaldehyde, propionaldehyde, butyraldehyde, pentanal, and acrylic aldehyde, and the like, one or more selected from these Can be used. Among these, those containing an organic solvent are preferable, ketone solvents (more preferably, methyl ethyl ketone (MEK), methyl isobutyl ketone (MIBK), methyl isopropyl ketone (MIPK), etc.), ether solvents, cellosolve solvents are preferable. , Aliphatic hydrocarbon solvents (more preferably cyclohexane etc.), aromatic hydrocarbon solvents (more preferably toluene, ethylbenzene etc.), aromatic heterocyclic compounds solvents, amide solvents, halogen compound solvents ( More preferably, from chloroform, trichloroethylene, carbon tetrachloride, etc.), ester solvents (more preferably, ethyl acetate, propyl acetate, butyl acetate, etc.), amine solvents, nitrile solvents, nitro solvents, aldehyde solvents, etc. Contains one or more selected Than it is. By using such a solvent, the removal of the solvent in the solvent removal step can be performed relatively easily, and even if the removal of the solvent in the solvent removal step is insufficient, the dispersion 3 In the (droplet 9), the first dispersoid 311 can be finely dispersed in a stable state.

Next, preparation of the supplement material suspension will be described.
First, in the same manner as described above, an aqueous liquid is prepared by adding a dispersant and / or a dispersion aid as necessary to water or a water-soluble (excellent compatibility with water) liquid.
On the other hand, a filling material solution containing the filling material is prepared. The filling material liquid can be prepared, for example, by using a solvent capable of dissolving at least a part of the filling material.
Next, the emulsification in which the dispersoid (dispersed particles) containing the supplementary material is dispersed in the aqueous dispersion medium by adding the above supplementary material solution to the stirred aqueous solution while gradually dropping. A liquid (emulsion) is obtained.

  Thereafter, the solvent is removed from the obtained emulsion to obtain a filling material suspension in which the filling material is dispersed as a dispersoid. The removal of the solvent can be performed, for example, by heating the emulsion or placing it in a reduced pressure atmosphere (solvent removal step). By using such a method, the circularity of the second dispersoid 312 in the dispersion 3 (droplet 9) can be further increased. In addition, when dripping the filling material liquid, the aqueous liquid and / or the filling material liquid may be heated. Further, when such a method is used, the particle size of the dispersoid in the filling material suspension (second dispersoid 312 in the dispersion 3) can be controlled to an appropriate size.

Any solvent can be used as long as it can dissolve at least a part of the filling material. However, it is preferable that the solvent is easily removed in the solvent removal step.
The solvent is preferably a solvent having low compatibility with the dispersion medium 32 described above (for example, a solvent having a solubility in 100 g of the dispersion medium at 25 ° C. of 30 g or less). Thereby, even if the solvent removal in the solvent removal step is insufficient, the second dispersoid 312 can be finely dispersed in a stable state in the dispersion 3 (droplets 9).

  The composition of the solvent can be appropriately selected according to, for example, the composition of the above-described filling material, the composition of the dispersion medium 32, and the like. Specifically, for example, the above-described kneaded material suspension (binding) What was illustrated as a solvent used at the time of preparation of resin suspension) etc. can be used. By using such a solvent, the removal of the solvent in the solvent removal step can be performed relatively easily, and even if the removal of the solvent in the solvent removal step is insufficient, the dispersion 3 In (droplet 9), the second dispersoid 312 can be finely dispersed in a stable state.

Then, the dispersion liquid 3 is obtained by mixing the kneaded material suspension (binder resin suspension) obtained as described above and the filling material suspension.
Moreover, when preparing the suspension as the dispersion liquid 3 by the above methods, it is preferable to satisfy the following conditions. That is, the boiling point of the solvent (solvent capable of dissolving at least a part of the constituent material of the kneaded material K7) used for the preparation of the kneaded material suspension (binder resin suspension) under atmospheric pressure is T _bp ( sol) [° C.], where T _bp (dm) [° C.] is the boiling point under atmospheric pressure of the liquid used as the dispersion medium of the dispersion (emulsion) containing the kneaded product, | T _bp (dm) −T _It is preferable to satisfy the relationship of _bp (sol) | ≦ 40. By satisfying such a relationship, the solvent removal step of preparing the kneaded product suspension from the emulsified liquid can be performed smoothly, and the solvent remains more reliably in the obtained kneaded product suspension. Can be prevented. Further, it is more preferable that the relationship of −30 <T _bp (dm) −T _bp (sol) <40 is satisfied between T _bp (sol) and T _bp (dm), and −20 <T _bp ( dm) −T _bp (sol) <40 is more preferable, and it is most preferable that the relationship 0 ≦ T _bp (dm) −T _bp (sol) <40 is satisfied. By satisfying such a relationship, from the inside of the dispersoid in the solvent removal step, etc., while performing the solvent removal step sufficiently smoothly so that the solvent does not substantially remain in the kneaded product suspension obtained. It is possible to reliably prevent the solvent from being rapidly vaporized (boiled), and to effectively prevent the formation of an irregularly shaped dispersoid in the kneaded product suspension obtained.

When the method as described above is employed, the dispersion 3 having a very small variation in the size of the dispersoid 31 (the first dispersoid 311 and the second dispersoid 312) can be easily and reliably prepared.
The dispersion 3 can also be prepared by the following method. Also in this method, a kneaded material suspension (binder resin suspension) in which the kneaded material is dispersed as a dispersoid, and a filling material suspension in which the filling material is dispersed as a dispersoid, as in the method described above. By mixing, the target dispersion 3 is obtained.

First, preparation of a kneaded product suspension (binder resin suspension) will be described.
First, an aqueous liquid in which a dispersant and / or a dispersion aid is added to water or a water-soluble liquid as necessary is prepared.
On the other hand, a kneaded material K7 pulverized into a powder or granule is prepared.
Next, the kneaded product is gradually added into an agitated aqueous liquid, whereby a kneaded material suspension in which the dispersoid containing the binder resin is dispersed in the aqueous dispersion medium (condensation). (Resin suspension) is obtained.

In addition, when the kneaded material is added, for example, an aqueous liquid may be heated. Thereby, the particle size of the first dispersoid 311 in the dispersion 3 can be controlled to an appropriate size. The average particle size of the kneaded material put into the aqueous liquid is preferably 0.1 μm to 5 mm, more preferably 0.15 to 10 μm, and still more preferably 0.2 to 2 μm.
Next, preparation of the supplement material suspension will be described.

First, an aqueous liquid in which a dispersant and / or a dispersion aid is added to water or a water-soluble liquid as necessary is prepared.
On the other hand, a powdery or granular filling material is prepared.
Next, the filling material is gradually added to the stirred aqueous liquid to obtain a filling material suspension in which the dispersoid containing the filling material is dispersed in the aqueous dispersion medium. .

In addition, when introducing the filling material, for example, an aqueous liquid may be heated. Thereby, the particle size of the second dispersoid 312 in the dispersion 3 can be controlled to an appropriate size. The average particle diameter of the filling material introduced into the aqueous liquid is preferably 0.1 μm to 5 mm, more preferably 0.15 to 10 μm, and still more preferably 0.2 to 2 μm.
Then, the dispersion 3 is obtained by mixing the kneaded material suspension (binder resin suspension) obtained as described above and the filling material suspension (adhesive resin suspension). When the dispersion liquid 3 is prepared by such a method, the dispersion liquid 3 can be prepared without substantially using an organic solvent or using an extremely small amount of an organic solvent. For this reason, it is possible to substantially prevent the organic solvent from being volatilized in a solidifying section or the like of a toner manufacturing apparatus as will be described later. As a result, the toner can be manufactured by a method that hardly causes adverse effects on the environment.

The dispersion 3 can also be prepared by the following method.
First, a binder resin dispersion (binder resin suspension) obtained by dispersing a kneaded product K7 containing at least a binder resin, and a colorant dispersion (colorant suspension) obtained by dispersing at least a colorant. And a filling material dispersion liquid (filling material suspension) obtained by dispersing the filling material. The binder resin dispersion, the colorant dispersion, and the filling material dispersion can be suitably prepared by applying the method described above.

  Next, the binder resin dispersion, the colorant dispersion, and the filling material dispersion are mixed and stirred. As a result, the first dispersoid 311 made of a material containing a binder resin, the second dispersoid 312 made of a material containing a filling material, and the third dispersoid made of a material containing a colorant. A dispersion 3 containing the dispersoid is obtained. Thus, the dispersion 3 may include a dispersoid other than the first dispersoid 311 and the second dispersoid 312. In addition, when such a method is used, the particle size of the dispersoid 31 (the first dispersoid 311, the second dispersoid 312 and the third dispersoid) in the dispersion 3 is controlled to an appropriate size. be able to.

  In such a method, for example, first, the binder resin dispersion and the colorant dispersion may be mixed and stirred without adding the filler material dispersion to obtain a new binder resin suspension. At this time, if necessary, an aggregating agent such as an inorganic metal salt may be added while stirring. Thereby, the aggregate which the kneaded material and the colorant aggregated to an appropriate size can be formed. Thereafter, the dispersion liquid 3 can be obtained by adding the filler dispersion liquid to the new binder resin suspension and further mixing and stirring. When such a method is used, the particle size of the dispersoid 31 (particularly, the first dispersoid 311) in the dispersion 3 can be controlled to an appropriate size by the aggregation.

<Granule production process and granule (toner base particle)>
Next, the dispersion liquid 3 as described above is subjected to a granular body manufacturing process as described in detail below, whereby a joined body 40 in which a plurality of resin fine particles derived from the first dispersoid 311 are melt-bonded and Thus, the granular material 4 having the filling phase 42 as described above is obtained.
In this way, by obtaining the granular body 4 as having a bonded body 40 in which a plurality of resin fine particles derived from the first dispersoid 311 are melt-bonded, the obtained granular body 4 has a space between each particle. Variations in shape, size, composition, etc. are particularly small. In other words, as described above, when the granular material 4 is obtained as an aggregate (joined body) of a plurality of first dispersoids 311, the first dispersoid 311 constituting the dispersion 3 is: Even when there is a relatively large variation in shape, size, composition, etc. among the individual particles (between individual dispersoid particles), the obtained granular material 4 has a shape, size between the particles. , Variations in composition and the like are small. As a result, the finally obtained toner has particularly small variations in shape, size, composition, and the like among the respective toner particles, has excellent properties as a whole toner, and improves reliability. In addition, even when a classification process, a thermal spheronization process, a mechanical surface modification process, or the like is performed after the granule manufacturing process, such a process can be simplified or performed under mild conditions. . In addition, since the granule 4 obtained in this step has a filling phase 42 formed in the recesses existing in the vicinity of the surface thereof, it is excellent in mechanical strength and even when a relatively large external force is applied, Unintentional collapse (especially, collapse from the vicinity of the recess as described above) is unlikely to occur.

  On the other hand, when the granular material cannot be obtained as an aggregate (junction) of the dispersoid (first dispersoid) as described above, that is, each dispersoid particle is an independent granular material (toner). When the mother particles are formed, the finally obtained toner has a large variation in shape, size, composition, etc. among the toner particles. As a result, the characteristics of the toner as a whole are lowered and the reliability is low. In such a case, even if a classification process is performed after the granular material manufacturing process described later, it is difficult to sufficiently reduce the size variation among the particles, and the toner manufacturing yield also increases. , It will be significantly lower. In order to suppress the variation in shape as described above, it is conceivable to perform a heat spheronization treatment at the time of forming the granular material or after the formation of the granular material. In such a case (particularly, formation of the granular material). If the conditions of the thermal spheronization treatment are not relatively severe, it is difficult to sufficiently reduce the variation in the shape of the obtained granular material. Deterioration and destruction of the compatibilized state and finely dispersed state of each component in the granular material are likely to occur, and it is difficult to exert sufficient characteristics in the finally obtained toner.

Further, even when the granular material is obtained as an aggregate of a plurality of dispersoids (resin fine particles), the granular material obtained is inferior in mechanical strength if there is no supplementary phase as described above. That is, when there is no supplementary phase, it is difficult to sufficiently increase the mechanical stability of the granular material, and even when a relatively small external force is applied, Collapse (decomposition) is likely to occur. Further, when there is no supplementary phase, the finally obtained toner particles are inferior in mechanical stability and environmental characteristics. Therefore, the toner composed of such granular materials has a large variation in shape, size, characteristics and the like among the toner particles, and the reliability of the toner as a whole is low.
The granule manufacturing process can be performed using, for example, a toner manufacturing apparatus M1 as shown in FIG.

<Toner production equipment>
As shown in FIG. 6, the toner manufacturing apparatus M1 includes a nozzle M2 that ejects the dispersion 3 (droplet 9) as described above, a dispersion supply unit M4 that supplies the dispersion 3 to the nozzle M2, and a nozzle M2. A solidified part M3 to which a liquid dispersion 3 (droplet 9) in the form of droplets (particulates) ejected from is transported, and a recovery part M5 to recover the produced granular material (toner mother particles) 4. ing.

The dispersion liquid supply unit M4 may have any function as long as it has a function of supplying the dispersion liquid 3 to the nozzle M2, but may include a stirring means M41 for stirring the dispersion liquid 3 as illustrated. Thereby, for example, even when the dispersoid 31 is difficult to disperse in the dispersion medium 32, the dispersion 3 in which the dispersoid 31 is sufficiently uniformly dispersed can be supplied to the nozzle M2.
The nozzle M2 has a function of ejecting the dispersion liquid 3 as fine droplets (fine particles) 9. The nozzle M2 will be described in detail later.

As shown in FIG. 6, the toner manufacturing apparatus M1 has a gas flow supply means M10. The gas supplied from the gas flow supply means M10 is sent to the nozzle M2 through the duct M101. This is used for ejecting the dispersion liquid 3 (droplet 9) from the nozzle M2, which will be described in detail later.
A valve M11 is attached to the gas flow supply means M10. Thereby, the pressure of the gas used for the ejection of the dispersion liquid 3 (droplets 9) can be adjusted.

The toner manufacturing apparatus M1 having the illustrated configuration has a plurality of nozzles M2. Then, fine droplets 9 are respectively ejected from these nozzles M2 to the solidified portion M3.
Each nozzle M2 may eject the droplet 9 almost simultaneously, but it is preferable that at least two adjacent nozzles are controlled so that the ejection timing of the droplet 9 is different. Accordingly, it is possible to more effectively prevent the droplets 9 from colliding and aggregating before the droplets 9 ejected from the adjacent nozzle M2 are solidified.

The droplets (fine particles) 9 ejected from the nozzle M2 are solidified while being transported through the solidified portion M3, whereby a granular body having a joined body 40 in which a plurality of resin fine particles are melt-joined and a supplementary phase 42. (Toner mother particles) 4
When the dispersion medium 32 includes the solvent material as described above, the solvent material is removed when the droplet (fine particle) 9 is conveyed through the solidified portion M3. In such a case, as the dispersion medium 32 in the ejected droplet 9 is removed, the plurality of first dispersoids 311 (resin fine particles) contained in the droplet 9 aggregate. As a result, the granular material (toner mother particles) 4 is a molten joined body of a plurality of resin fine particles (resin fine particles derived from the first dispersoid 311), and is formed at least in the concave portion existing near the surface thereof. It is obtained as having a supplementary phase 42.

  Further, when the dispersion medium 32 is substantially composed of a liquid filling material (adhesive resin) without substantially containing a solvent material, the filling is performed when the droplets (fine particles) 9 are conveyed through the solidified portion M3. The material is cured or semi-cured. As a result, the granular material (toner base particle) 4 is obtained as having a joined body 40 formed by melting and joining a plurality of resin fine particles (resin fine particles derived from the first dispersoid 311) and a filling phase 42. .

As described above, the granular material (toner base particle) 4 is obtained as an aggregate (joint) of resin fine particles derived from the first dispersoid 311, but the resin fine particles are the first dispersion. Any material may be used as long as it includes at least a part of the components constituting the material 311. For example, it may be composed of a material from which some of the components contained in the first dispersoid 311 are removed. .
The solidification part M3 is comprised by the cylindrical housing M31.

During the production of the granular material 4 (from the discharge of the dispersion 3 to the formation of the granular material 4), the inside of the housing M31 is preferably maintained at a temperature within a predetermined range. As a result, variations in characteristics among the granular bodies 4 due to differences in manufacturing conditions can be reduced, and the reliability of the entire toner is improved.
Thus, for the purpose of keeping the temperature in the housing M31 within a predetermined range, for example, a heat source or a cooling source is installed inside or outside the housing M31, or a flow path for the heat medium or the cooling medium is formed in the housing M31. It is good also as a made jacket.

  The temperature in the housing M31 is not particularly limited, but is preferably 40 to 160 ° C, more preferably 50 to 150 ° C, and further preferably 60 to 140 ° C. When the temperature in the housing M31 is a value within the above range, for example, a solvent material that forms the dispersion medium 32 from the droplets 9 while sufficiently preventing modification of the constituent material of the toner (particularly the binder resin). Can be removed more smoothly. Further, when the temperature in the housing M31 is a value within the above range, the supplementary phase 42 can be efficiently formed.

  In the illustrated configuration, the pressure in the housing M31 is adjusted by the pressure adjusting means M12. As described above, by adjusting the pressure in the housing M31, for example, it is possible to efficiently remove the solvent material constituting the dispersion medium 32 from the ejected droplets 9, and the toner productivity is improved. . In the configuration shown in the figure, the pressure adjusting means M12 is connected to the housing M31 by a connecting pipe M121. Further, an enlarged diameter portion M122 having an enlarged inner diameter is formed in the vicinity of the end portion of the connection pipe M121 connected to the housing M31, and a filter M123 for preventing suction of the granular material 4 and the like is further provided. ing.

The pressure in the housing M31 is not particularly limited, but is preferably 150 kPa or less, more preferably 100 kPa or less, and further preferably 0.1 to 50 kPa. When the pressure in the housing M31 is a value within the above range, for example, the solvent material constituting the dispersion medium 32 from the droplets 9 can be more smoothly prevented while sufficiently preventing the generation of irregularly shaped particles 4 or the like. Can be removed.
The particle size of the dispersoid 31 (particularly the first dispersoid 311) contained in the dispersion 3 (droplet 9) is usually sufficiently smaller than that of the obtained granular material 4 (droplet 9). It is. Therefore, the granular material (toner base particle) 4 obtained as an aggregate of the dispersoid 31 (first dispersoid 311) has a sufficiently large circularity.

  In addition, when the dispersion medium 32 includes the solvent material as described above, the obtained granular material 4 is usually smaller than the droplet 9 ejected from the nozzle M2. For this reason, even when the droplet 9 of the dispersion 3 ejected from the nozzle (ejection unit) M2 is relatively large, the size of the obtained granular material 4 can be relatively small. Therefore, in this embodiment, the granular material 4 with a particularly small average particle diameter can be easily obtained.

In the present embodiment, as will be described in detail later, the droplets 9 ejected from each nozzle M2 can be made sufficiently small and the particle size distribution can be made sufficiently sharp. As a result, the granular material 4 also has a small variation in particle size, that is, a sharp particle size distribution.
As described above, by using a dispersion liquid (particularly a suspension) as the jetting liquid (discharge liquid), even when the particle size (toner base particles) to be produced is sufficiently small, The circularity can be made sufficiently high and the particle size distribution can be sharp. As a result, the obtained toner has a uniform charge between the toner particles, and a thin layer of toner formed on the developing roller when the toner is used for printing, which is leveled and densified. It becomes. As a result, defects such as fog are hardly generated and a sharper image can be formed. Further, since the shape and particle size of the granular material 4 are uniform, the bulk density of the entire toner (aggregate of granular material 4) can be increased. As a result, it is advantageous for increasing the amount of toner filled in the cartridge of the same volume and for reducing the size of the cartridge.

The housing M31 is connected to voltage application means M8 for applying a voltage. By applying a voltage having the same polarity as that of the droplet 9 (granular body 4) to the inner surface side of the housing M31 by the voltage applying means M8, the following effects can be obtained.
Usually, the toner base particles are positively or negatively charged. For this reason, if there is a charged substance charged with a polarity different from that of the toner base particles, a phenomenon occurs in which the toner base particles are electrostatically attracted and adhered to the charged substance. On the other hand, if there is a charged substance charged with the same polarity as the toner mother particles, the charged substance and the toner mother particles repel each other, effectively preventing the phenomenon that the toner adheres to the surface of the charged object. it can. Therefore, by applying a voltage having the same polarity as the droplet 9 (granular body (toner mother particle) 4) to the inner surface side of the housing M31, the droplet 9 (granular body (toner mother particle) 4) is applied to the inner surface of the housing M31. ) Can be effectively prevented. Thereby, generation | occurrence | production of the toner powder of irregular shape can be prevented more effectively, and the collection | recovery efficiency of the granular material 4 also improves.

The housing M31 has a reduced diameter portion M311 in which the inner diameter decreases in the downward direction in FIG. 6 in the vicinity of the recovery portion M5. By forming such a reduced diameter portion M311, it is possible to efficiently recover the granular material 4. As described above, the droplet 9 ejected from the nozzle M2 is solidified in the solidification part M3, but such solidification is almost completely completed in the vicinity of the recovery part M5, and the reduced diameter part M311. In the vicinity, problems such as agglomeration hardly occur even if each particle contacts.
The granular material 4 obtained by solidifying the droplet 9 is collected by the collection unit M5.
Next, the nozzle M2 that ejects the granular dispersion liquid 3 (droplets 9) will be described in detail.

  In the present embodiment, the dispersion 3 is ejected as fine particles (droplets 9) in a unique state. That is, in the present embodiment, as shown in FIG. 7, the dispersion 3 sent to the inclined surface 7 is thinly stretched into a thin laminar flow 8 by the gas flow flowing along the inclined surface 7. The thin laminar flow 8 flowing along the inclined surface 7 is too thin when leaving the inclined surface 7 and cannot be put into a layered state (film state), and is broken into pieces by the surface tension to form a droplet 9 of fine particles. . In particular, since the laminar flow 8 is composed of the dispersion liquid (suspension containing a solid dispersoid) 3, a uniform liquid (for example, a liquid or a solution substantially consisting of a pure substance) was used. Compared to the case, the droplets 9 are easily subdivided from the thin laminar flow 8. Therefore, in this embodiment, the fine particle dispersion 3 (droplet 9) can be ejected particularly efficiently. Further, it is possible to prevent the droplets from forming a projection by pulling the tail. In the present embodiment, the dispersion 3 is ejected as a thin laminar flow 8 as fine particles (droplets 9) with a gas flow. For this reason, there is a feature that the droplet 9 of the dispersion liquid 3 can be formed into circular ultrafine particles. Thereby, the clogging of the supply port 5 of the dispersion liquid 3 can be prevented more reliably, and the processing of the supply port 5 can be easily performed.

Furthermore, as shown in FIG. 7, when a sharp edge 7A is provided at the tip of the inclined surface 7, and the atomizing gas and the spreading gas are caused to collide with the edge 7A, air (gas) can be vibrated vigorously. The air vibration has the effect of making the dispersion 3 further fine.
Further, the nozzle M2 used in the present embodiment has a ring-shaped edge 7A at the tip of the inclined surface 7, and the dispersion liquid 3 (droplet 9) can be ejected from the edge 7A in the form of fine particles in a holographic state. Thereby, for example, the solvent material constituting the dispersion medium 32 can be efficiently removed from the droplets 9 ejected by the hollow cone.

The nozzle M2 that ejects the liquid shown in FIG. 7 in the form of fine particles includes a supply port 5 that discharges the dispersion 3 (droplet 9) in a ring shape, and an inclined surface that allows the dispersion 3 discharged from the supply port 5 to flow. 7 and a gas port 10 for injecting pressurized gas onto the inclined surface 7.
The nozzle M <b> 2 shown in this figure includes an inner ring (cylinder) 11, an intermediate ring (cylinder) 12, and an outer ring (cylinder) 13. A supply port 5 is provided between the inner ring 11 and the intermediate ring 12, an atomizing gas flow path 14 is provided at the center of the inner ring 11, and a spreading gas supply path is provided between the intermediate ring 12 and the outer ring 13. 15.

  The inner ring 11 has a cylindrical outer shape, and the intermediate ring 12 has a cylindrical inner shape. A slit-shaped supply port 5 having a predetermined width is provided between the inner ring 11 and the intermediate ring 12. ing. The supply port 5 is formed in a ring shape, and the slit width is designed such that the dispersion liquid 3 is not clogged. In the nozzle of the present embodiment, there is no need to send the dispersion 3 from the supply port 5 as a thin film (thin layer). This is because the dispersion 3 is thinly stretched on the inclined surface 7 and ejected as fine particles (droplets 9). Accordingly, the slit width of the supply port 5 is set to an optimum value in consideration of the flow rate of the dispersion 3 to be sent out, the length of the inclined surface 7, the flow rate of the atomized gas injected onto the inclined surface 7, the inner diameter of the supply port 5, and the like. Designed. For example, the slit width of the supply port 5 is designed to be 0.2 to 1.5 mm, preferably 0.4 to 1 mm, and optimally about 0.8 mm.

The diameter of the supply port 5 is designed to an optimum value in consideration of the flow rate of the dispersion liquid to be discharged (injected), the dimension of the slit width, and the like. The diameter of the supply port 5 is designed to be about 50 mmφ, for example, in a nozzle that ejects the dispersion 3 (droplet 9) of 1000 g / min. The diameter of the supply port 5 is designed to be large when the flow rate is large and small when the flow rate is small.
The outer peripheral portion of the inner ring 11 and the tip surface of the intermediate ring 12 are cut into a tapered shape to form an inclined surface 7. The inclined surfaces 7 of the inner ring 11 and the intermediate ring 12 are flush with each other so that the gas flowing along and flowing along the inclined surface 7 of the inner ring 11 is not turbulent at the boundary between the inner ring 11 and the intermediate ring 12. Is formed. When the inclined surface 7 of the inner ring 11 and the intermediate ring 12 is the same plane, there is no step between the inclined surface 7 of the inner ring 11 and the intermediate ring 12 and the inclined surface 7 of the intermediate ring 12 from the inclined surface 7 of the inner ring 11. It means a state in which gas flows linearly. Thus, in order to process the inclined surface 7 of the inner ring 11 and the intermediate ring 12 into a tapered shape on the same plane, for example, the inner ring 11 and the intermediate ring 12 may be connected and tapered. Furthermore, the inclined surface 7 is a smooth surface along the flow direction of the dispersion liquid 3 so that the dispersion liquid 3 flowing along the surface does not become a turbulent flow. The inclined surface 7 of the nozzle shown in the figure is conical and has a smooth surface as a whole.

  By providing the inclined surface 7 on the inner ring 11 and the intermediate ring 12, the supply port 5 is opened in the middle of the inclined surface 7. The inclination angle α of the inclined surface 7 provided in the inner ring 11 and the intermediate ring 12 is not particularly limited, but is, for example, 100 to 170 degrees, preferably 120 so that the angle of the supply port 5 with respect to the inclined surface 7 becomes an obtuse angle. It is designed to be -160 degrees, more preferably 130-160 degrees, and most preferably about 150 degrees. The larger the inclination angle α, the more stable the liquid outflow. However, the optimum value of the inclination angle α varies depending on the slit width. The inclination angle α is preferably designed so that the opening width of the supply port 5 on the inclined surface 7 does not exceed 2 mm.

  A center ring 16 is disposed at the tip of the inner ring 11, and a gas port 10 is opened between the center ring 16 and the inner ring 11. Although not shown, the center ring 16 is fixed to the inner ring 11 and disposed at a predetermined position. The center ring 16 is processed into a tapered shape along the inclined surface 7 of the inner ring 11 on the outer peripheral surface. A gas port 10 formed between the center ring 16 and the inner ring 11 has a slit shape, from which a pressurized gas is injected into a laminar flow state and flows along the inclined surface 7.

The atomizing gas flow path 14 of the inner ring 11 is connected to a pressurized gas source F. The gas port 10 injects atomized gas that flows along the inclined surface 7. The pressurized gas source F is, for example, 3 to 20 kg / cm ² , preferably 4 to 15 kg / cm ² , more preferably 4 to 10 kg / cm ² , and most preferably about 6.5 kg / cm ^2. To supply. When the atomizing gas injection pressure is increased, the flow velocity of the gas flowing along the inclined surface 7 is increased, and the dispersion 3 can be more effectively thinned to make the dispersion 3 fine droplets (fine particles) 9. . However, when the injection pressure is increased, a special compressor is required and the energy consumption increases. Therefore, the optimum value is designed in consideration of the required particle diameter of the fine particles and the energy consumption.

  Furthermore, the nozzle shown in FIG. 7 injects spreading gas to the outer periphery of the inclined surface 7 in addition to the atomizing gas. However, the spreading gas is not necessarily injected. This is because the dispersion liquid 3 can be ejected as fine particles (droplets 9) with the atomizing gas without spraying the spreading gas. The nozzle that ejects the atomizing gas and the spreading gas has the advantage that the atomizing gas and the spreading gas collide with each other at the edge 7A of the inclined surface 7 so that the droplet 9 can be made into smaller particles. Furthermore, the angle of the holocon can be adjusted with the spreading gas. Further, depending on the properties of the dispersion 3, the separation at the edge 7A may become worse, and a liquid backflow may occur on the spreading gas side. However, by injecting the spreading gas, the occurrence of such a problem is further increased. It can be surely prevented.

The spreading gas is injected from a spreading gas injection port 17 provided between the intermediate ring 12 and the outer ring 13. The spreading gas can be a low pressure gas compared to the atomizing gas. For example, when the atomizing gas is about 6.5 kg / cm ² , the spreading gas can be about 1 kg / cm ² . The spreading gas need not be forced to stretch the dispersion 3 thinly unlike the atomizing gas, and can be set, for example, in the range of 0.5 to ³ kg / cm ² .

  In the nozzle for injecting both atomizing gas and spreading gas, the tip of the inclined surface 7 has a sharp edge 7A. The intermediate ring 12 forms an inclined surface 7 on the tip surface, and an outer periphery of the tip is processed into a cylindrical shape, thereby forming an edge 7A at the tip of the inclined surface 7. The intermediate ring 12 having this shape can form a sharp edge 7A having an angle of (180 degrees−inclination angle α) at the tip of the inclined surface 7. However, although the nozzle is not shown, the outer periphery of the intermediate ring 12 can be processed into a taper shape to adjust the angle of the edge 7A.

The nozzle shown in FIG. 7 can eject the dispersion 3 as fine particles (droplets 9) in the following state, for example.
(1) A pressurized atomizing gas is supplied to the atomizing gas flow path 14 provided at the center of the inner ring 11, and the spreading gas is supplied to the spreading gas injection port 17 between the intermediate ring 12 and the outer ring 13. Then, the dispersion 3 is fed from the supply port 5 to the inclined surface 7.
(2) The dispersion 3 supplied to the inclined surface 7 is thinly stretched by the atomizing gas flowing along the inclined surface 7 to become a thin laminar flow 8. For example, the atomized gas is caused to flow along the inclined surface 7 at a flow rate of about Mach 1.5, the dispersion 3 is sent to the supply port 5, and the flow rate at the tip of the laminar flow 8 is 1/20 of the atomized gas. Then, it becomes 25.5 m / s. If the diameter of the edge 7A provided at the tip of the inclined surface 7 is about 50 mm, the dispersion 3 is supplied at about 1 liter / minute, and the membrane pressure of the thin laminar flow 8 is about 4 μm.
(3) The thin laminar flow 8 having a small film thickness as described above is too thin to pass through the edge 7A of the inclined surface 7 and cannot be in a film state, and is broken into pieces by the surface tension, and the fine droplet 9 Become.
(4) The fine particle droplet 9 collides with the atomizing gas and the spreading gas at the edge 7A, rubs and vibrates to make the droplet 9 smaller (fine droplet 9).
(5) The droplets 9 of fine particles are carried radially by the atomizing gas and the spreading gas. This state is called a holocorn. The cone angle of the hollow cone is determined by the angle of the inclined surface 7, but can also be adjusted by the injection pressure of the atomizing gas and the spreading gas.

The droplets 9 ejected in the state of a hollow cone are solidified as described above, and become granular bodies (toner base particles) 4 including a joined body 40 and a supplementary phase 42.
FIG. 8 shows a nozzle in which liquid A and liquid B are mixed to form dispersion fine particles (droplets 9). In the nozzle shown in this figure, the intermediate ring 12 of the nozzle shown in FIG. 7 has a double tube structure of an inner intermediate ring (cylinder) 12A and an outer intermediate ring (cylinder) 12B. A B liquid supply port 5 is provided between the inner intermediate ring 12A and the outer intermediate ring 12B. The ring-shaped inner intermediate ring 12A has tapered inclined surfaces 7 on the inner surface and the outer surface, and the tip thereof is a sharp edge 7A. The front end surface of the outer intermediate ring 12B is also tapered to form an inclined surface 7. The inclined surface 7 of the outer intermediate ring 12B is connected to the same plane as the inclined surface 7 of the inner intermediate ring 12A.

  The nozzle shown in FIG. 8 has inclined surfaces 7 on the inner side surface and the outer side surface of the inner intermediate ring 12A, the A liquid supply port 5 is provided on the inclined surface 7 provided on the inner side, and B is provided on the outer inclined surface 7 side. A liquid supply port 5 is provided. Both the gas port 10 of the inner ring 11 and the spreading gas injection port 17 between the outer intermediate ring 12B and the outer ring 13 so that both the A liquid and the B liquid can be thinly extended to the inclined surface 7 by atomizing gas. High-pressure atomized gas is injected from

  By using the nozzle M2 having such a structure, a toner with high uniformity (dispersibility) can be obtained even when components having poor dispersibility and compatibility are used. Further, by using the nozzle M2 having such a structure, the toner particles 100 having a multiphase structure (a structure including a phase of a bonded body 40 in which a plurality of resin fine particles are melt-bonded and a supplementary phase 42). Can be obtained easily and reliably. In the present embodiment, the liquid A and the liquid B may have substantially the same composition or may have different compositions. In the following description, it is assumed that the liquid B has substantially the same composition, that is, both the liquid A and the liquid B are the dispersion liquid 3 as described above. The case where the liquid A and the liquid B have different compositions will be described in detail later.

When the A liquid and the B liquid have substantially the same composition, it is possible to more reliably reduce variations in the composition and characteristics of the obtained granular material. Further, by supplying the liquid (dispersion liquid 3) having the same composition from the plurality of supply ports 5, it is possible to more reliably control the ejection conditions (conditions for ejecting the liquid droplets 9) of the dispersion liquid 3.
The nozzle shown in FIG. 8 has inclined surfaces 7 on both the inner and outer sides of the inner intermediate ring 12A, and can supply liquid A and liquid B to the inner and outer inclined surfaces 7, respectively. It is configured. The nozzle shown in FIG. 9 has four supply ports 5 in the middle of the inclined surface 7. In the nozzle having such a structure, the liquid (dispersion 3) can be supplied from the four supply ports 5 and discharged simultaneously. In the nozzle shown in FIG. 9 as well, a liquid (dispersion 3) having substantially the same composition may be supplied from all the supply ports 5 as described above. Thereby, the same effect as described above can be obtained.

  Further, FIGS. 10 and 11 show a nozzle that can eject the dispersion liquid as finer fine particles. In the nozzles shown in these drawings, the intermediate ring 12 has a double tube structure of an inner intermediate ring (cylindrical body) 12A and an outer intermediate ring (cylindrical body) 12B, as in the nozzle shown in FIG. A B liquid supply port 5 is provided between the inner intermediate ring 12A and the outer intermediate ring 12B. The ring-shaped inner intermediate ring 12A has tapered inclined surfaces 7 on both the inner side surface and the outer side surface, and the tip thereof is a sharp edge 7A. The front end surface of the outer intermediate ring 12B is also tapered to form an inclined surface 7. Further, a liquid A supply port 5 is provided between the inner intermediate ring 12 </ b> A and the inner ring 11.

  An enlarged view of the inclined surface is shown in FIG. As shown in this figure, the inclined surface 7 of the inner intermediate ring 12A is slightly stepped in the vicinity of the supply port 5 with respect to the extended line of the outer intermediate ring 12B and the inclined surface 7 of the inner ring 11 located on both sides thereof. It is provided and formed low (so that the angle formed by the inclined surface 7 of the inner intermediate ring 12A is smaller than the angle formed by the inclined surface 7 of the outer intermediate ring 12B). In the nozzle having the inclined surface having such a shape, the gas flow flowing along the inclined surface 7 as shown by the arrow can smoothly discharge (discharge) the liquid (dispersion liquid 3) from the supply port 5. It has the feature. This is because the inclined surface 7 of the inner intermediate ring 12A does not protrude with respect to the inclined surface 7 on the outer peripheral side (outer intermediate ring 12B). Although not shown, when the inclined surface 7 of the inner intermediate ring 12A protrudes from the extended line of the inclined surface 7 (outside intermediate ring 12B) located on the outer peripheral side thereof, the gas collides with the protruding portion to smoothly liquid (disperse) It becomes difficult to discharge the liquid 3).

  Furthermore, in the nozzle shown in the enlarged view of FIG. 12, the inclined surface 7 of the inner intermediate ring 12A is curved so that the tip portion protrudes from an extension line of the adjacent inclined surface 7. In the inclined surface 7 of the inner intermediate ring 12 </ b> A having such a shape, the gas flow that flows in the direction of the arrow along the inclined surface 7 is strongly pressed against the inclined surface 7 at the tip portion and flows through the inclined surface 7. The thin laminar flow 8 of the liquid (dispersion 3) can be stretched thinner. For this reason, the nozzle having such a structure has an advantage that the dispersion liquid 3 can be ejected as finer fine particles (droplets 9).

In such a nozzle, when the angles of the outer intermediate ring 12B, the inner intermediate ring 12A, and the tip of the inner ring 11 are designed as shown in the figure, the dispersion liquid 3 can be injected with a holocone.
In the nozzle shown in FIGS. 7, 8, and 10, the spreading gas injection port 17, and the distal end portions of the center ring 16 and the outer ring 13 constituting the gas port 10 are configured by a gas permeable member 18. The breathable member 18 has a breathability that allows the gas press-fitted into the gas port 10 to penetrate from the surface. The air permeable member 18 is made of, for example, a sintered metal made of stainless steel having an average particle diameter of about 1 μm. The air-permeable member 18 has an effect of preventing a mist from adhering to the surfaces of the center ring 16 and the tip of the outer ring 13 by injecting part of the gas injected from the gas port 10 from the surface.

  Furthermore, FIG. 13 shows a nozzle that can spray fine particles on both the holocone and the full cone. FIG. 14 shows an enlarged view of the main part of the tip of the nozzle in this figure. Also in this nozzle, as in the nozzle shown in FIG. 8, the intermediate ring 12 has a double tube structure of an inner intermediate ring 12A and an outer intermediate ring 12B. A B liquid supply port 5 is provided between the inner intermediate ring 12A and the outer intermediate ring 12B. The ring-shaped inner intermediate ring 12A has tapered inclined surfaces 7 on both the inner surface and the outer surface, and the tip thereof is a sharp edge 7A. The front end surface of the outer intermediate ring 12B is a straight inclined surface 7. Further, a liquid A supply port 5 is provided between the inner intermediate ring 12 </ b> A and the inner ring 11.

  FIG. 15 shows an enlarged view of the inclined surface 7 provided on the inner intermediate ring 12A. Also in the nozzle shown in this figure, the inclined surface 7 of the inner intermediate ring 12A is inclined between the outer intermediate ring 12B and the inner ring 11 located on both sides in the vicinity of the supply port 5, as in the nozzle shown in FIG. A level difference is provided with respect to the extended line of the surface 7 and is formed low (so that the angle formed by the inclined surface 7 of the inner intermediate ring 12A is smaller than the angle formed by the inclined surface 7 of the outer intermediate ring 12B). Yes. Even in the nozzle having the inclined surface 7 having such a shape, the gas flow flowing along the inclined surface 7 as shown by the arrow can smoothly discharge the liquid (dispersed liquid 3) from the supply port 5.

  Further, the nozzle shown in FIG. 15 is formed so that the inclination angle of the inclined surface 7 of the inner intermediate ring 12A changes toward the tip direction, and the tip portion protrudes from the extension line of the adjacent inclined surface 7. Has been. In the inclined surface 7 of the inner intermediate ring 12A having such a shape, the gas flow flowing in the direction of the arrow along the inclined surface 7 is strongly pressed against the inclined surface 7 at the tip portion, and flows on the inclined surface 7. A thin laminar flow 8 of liquid (dispersion 3) can be stretched thinly. For this reason, the nozzle of this structure has the feature that the dispersion liquid 3 can be ejected as finer fine particles (droplets 9).

  Further, in such a nozzle, the angles of the outer ring 13, the outer intermediate ring 12B, the inner intermediate ring 12A, and the tip of the inner ring 11 are designed as shown in the figure, and the dispersion liquid 3 is made into a holocone and a full cone. Both can be injected. For example, the atomizing gas injection pressure injected from the gas port 10 between the outer intermediate ring 12B and the outer ring 13 is used as the atomizing gas injection pressure injected from the gas port 10 between the center ring 16 and the inner ring 11. If it is larger than this, the dispersion 3 can be jetted in the state of a holocone. On the contrary, the atomizing gas injection pressure injected from the gas port 10 between the outer intermediate ring 12 </ b> B and the outer ring 13 is the atomizing gas injection pressure injected from the gas port 10 between the center ring 16 and the inner ring 11. If it is stronger, the dispersion 3 can be sprayed in a full cone state.

Similarly to the nozzle shown in FIG. 10, the nozzle shown in FIG. 13 has mist on the surfaces of the center ring 16 and the outer ring 13, with the tip portions of the center ring 16 and the outer ring 13 constituting the gas port 10 as the breathable members 18. Is prevented from adhering.
In addition, the nozzle shown in FIG. 16 has a unique structure that prevents mist adhesion without using a breathable member. The nozzle of this figure has a gas peeling recess 19 on the tip surface of the center ring 16 and has a gas peeling recess 19 inside the supply port 5 and on the tip surface of the nozzle. The gas peeling recess 19 is connected to the flow path 1 between the inner ring 11 and the center ring 16 through a through hole 20 provided in the center ring 16. As shown in FIG. 17, the through hole 20 opens in a direction in which the gas to be injected is rotated by the gas separation recess 19, that is, inclined from the radial direction to the tangential direction. The surface of the gas peeling recess 19 is a smooth surface that can flow in a laminar flow state without disturbing the gas flow. Further, the outer peripheral portion of the gas separation recess 19 is streamlined like an airplane wing and is smoothly curved toward the gas port 10.

  In the nozzle having such a structure, when pressurized gas is injected from the through hole 20 to the gas peeling recess 19 in the tangential direction, the gas collides with the inner surface of the taper gas peeling recess 19 and spreads thinly. It becomes a swirl flow. At this time, the ratio of the air flow toward the outlet direction (upward in the figure) of the gas peeling recess 19 can be changed by the taper angle (θ) of the gas peeling recess 19. When the taper angle (θ) is 15 degrees as shown in the figure, the swirling airflow toward the exit direction is about 70%, and the remaining about 30% becomes the swirling airflow toward the bottom of the gas separation recess 19, After reaching the bottom, decrease the wind speed and head toward the exit. And it is caught in the above-mentioned about 70% whirling airflow, and is discharged | emitted from the gas peeling recessed part 19.

  The swirling airflow of the gas flowing along the inner surface of the gas separation recess 19 moves along the inclined surface of the taper surface and the aerodynamic part of the airfoil, and flows along the airfoil surface when reaching the tip. The gas is drawn into the atomizing gas injected from the flow path 1 provided between the inner ring 11 and the center ring 16. Since the streamlined airfoil portion is smoothly curved toward the gas port 10, the gas flows along the surface, creating a gas layer that flows to the front of the central ring 16.

  Since almost the entire front surface of the center ring 16 is covered with the flowing gas layer, the mist (droplet 9) of the dispersion 3 is prevented from adhering. The number of through-holes 20 is preferably about six so that gas can be uniformly injected from the gas peeling recess 19. However, the number of through holes can be further increased. Further, when the through hole is formed in a slit shape and the lateral width is widened, the gas can be blown out uniformly from the gas peeling recess even when the number of the through holes is small.

  In the nozzle having such a structure, since the front surface of the nozzle is covered with the gas layer, the flying mist is prevented from adhering to the surface, and is blown off by the streamline air stream which is a flowing gas layer. Further, when the nozzle having such a structure is used, the same effect can be obtained with a smaller amount of gas than the method of preventing powder adhesion by the air permeable member 18 described above.

  Furthermore, the nozzle shown in FIG. 18 can supply gas and liquid (dispersed liquid) uniformly from the gas port 10 and the supply port 5. The nozzle shown in this figure has helical ribs 22 in the flow path 1 and the liquid flow path 21. In the flow path 1 and the liquid flow path 21, ribs are provided between the rings for centering when assembling the rings, that is, for precisely matching the centers of all the rings. By bringing the tips of the ribs into contact, each ring is centered and assembled accurately.

  The nozzle of FIG. 18 has a helical rib 22 that spins a gas flowing in the axial direction to rotate in a spiral manner in the flow path 1 that communicates with the gas ports 10 opened on both sides of the edge 7A. The gas injected from the gas ports 10 on both sides of the edge 7A is injected toward the edge 7A while rotating in opposite directions. In the nozzle having such a structure, the atomized gases flowing on both sides of the edge 7A are reversed to each other, and when the mist is formed at the tip of the edge 7A, the twisting action of both gases is added to increase the mist crushing effect. You can make mist.

  However, the nozzle for injecting the dispersion 3 is not necessarily limited to the atomizing gas that flows on both sides of the edge as a reverse spin. For example, the atomizing gas on both sides of the edge is spun in the same direction. Also good. Further, in a nozzle having a plurality of gas ports, the gas ejected from all the gas ports may not be spun. Therefore, you may have a helical rib only in a specific flow path.

  Further, in the nozzle shown in FIG. 18, helical ribs 22 are also provided in the liquid flow path 21. Normally, the liquid (dispersion 3) has a slower flow rate than gas, so in the illustrated nozzle, the inclination angle α of the helical rib 22 is increased to about 60 degrees. Inclination angle (alpha) can be made into the range of 30-70 degree, for example, Preferably it is 45-65 degree. Similarly to the helical rib 22 of the flow channel 1, the helical rib 22 of the liquid flow channel 21 has a strong spin when the inclination angle α is large, but on the other hand, the flow resistance of the liquid tends to increase. Indicates. For this reason, the inclination angle α of the helical rib 22 is appropriately selected in consideration of the flow resistance and spin of the liquid.

By using the nozzle M2 as described above, the following effects can be obtained.
-The dispersion can be ejected as extremely small fine particles, and can be continuously ejected for a long time while sufficiently effectively preventing clogging. Further, since the dispersion liquid is stretched into a thin laminar flow to form droplets of fine particles, the droplets can be ejected as extremely small fine particles at a flow rate of gas flowing along a smooth surface.
-It can be ejected as fine droplets by increasing the ejection amount per unit time.

  In addition, the initial velocity of the dispersion 3 (droplet 9) ejected from the nozzle M2 to the solidifying part M3 is preferably, for example, 0.1 to 10 m / second, and more preferably 2 to 8 m / second. preferable. When the initial velocity of the dispersion 3 (droplet 9) is less than the lower limit, the toner productivity is lowered. On the other hand, when the initial velocity of the dispersion 3 (droplet 9) exceeds the upper limit, the sphericity (circularity) of the obtained granular material 4 tends to decrease.

  Further, the viscosity of the dispersion 3 ejected from the nozzle M2 is not particularly limited, but is preferably 5 to 3000 cps, and more preferably 10 to 1000 cps at 25 ° C., for example. If the viscosity of the dispersion 3 is less than the lower limit, it may be difficult to sufficiently control the size of the ejected particles (droplets 9), and dispersion of the obtained granular material 4 may increase. On the other hand, when the viscosity of the dispersion 3 exceeds the upper limit, the diameter of the formed droplets increases. In addition, when the viscosity of the dispersion liquid 3 is particularly large, adhesion to the nozzle tip becomes intense and continuous operation becomes difficult, and the dispersion liquid 3 is difficult to be supplied to the nozzle.

  Further, the dispersion 3 ejected from the nozzle M2 may be preheated (heated). By heating the dispersion liquid 3 in this manner, for example, the viscosity of the dispersion liquid 3 is reduced, and the clogging at the nozzle M2 can be more effectively prevented, and the ejected liquid droplets (mist). 9 can be made sufficiently small, and the variation in size among the droplets 9 can be made particularly small. In addition, by heating the dispersion 3, the solidification part M 3 can smoothly agglomerate (fuse) the resin fine particles derived from the first dispersoid 311 and efficiently form the supplementary phase 42. . As a result, the finally obtained toner particles 1 have more excellent shape stability.

Further, the ejection amount of one droplet of the dispersion liquid 3 (the volume of one droplet 9) slightly varies depending on the content of the first dispersoid 311 in the dispersion liquid 3, but is 0.05 to 500 pl. It is preferable that it is 0.5-5 pl. By setting the spray amount for one drop of the dispersion 3 to a value in such a range, the granular material 4 can have an appropriate particle size.
Further, the average particle diameter D ′ of the droplets 9 obtained by atomizing the dispersion liquid 3 is preferably 2.5 to 20 μm, and more preferably 4 to 15 μm. By setting the average particle diameter D ′ of the droplets 9 within such a range, the same effect as described above can be obtained.

Incidentally, the droplets 9 ejected from the nozzle M2 are generally sufficiently larger than the dispersoid 31 in the dispersion 3. That is, a large number of dispersoids 31 are dispersed in the droplet 9. For this reason, even if the particle size variation of the dispersoid 31 (particularly, the first dispersoid 311) is relatively large, the proportion of the dispersoid 31 in the ejected droplets 9 is the same as each droplet. It is almost uniform. Therefore, even when the dispersion of the particle size of the dispersoid 31 is relatively large, the granular material 4 is formed into particles by making the spray amount of the dispersion 3 (volume per droplet 9) substantially uniform. The variation in diameter is small. Such a tendency becomes more remarkable as the ratio of the average particle diameter of the dispersoid 31 (particularly, the first dispersoid 311) to the average particle diameter of the jetted dispersion 3 (droplet 9) is smaller. Become. For example, when the average particle size of the sprayed dispersion 3 (droplet 9) is D ′ [μm] and the average particle size of the first dispersoid 311 in the dispersion 3 is d ₁ [μm], d _{1 /} D ′ <0.5 is preferably satisfied, d ₁ /D′<0.2 is more preferable, and d ₁ /D′<0.1 is satisfied. Is more preferable.

  Further, when the average particle diameter of the dispersion 3 (droplet 9) to be ejected is D ′ [μm] and the average particle diameter of the finally obtained toner particles 100 is D ″ [μm], 0.05 is obtained. It is preferable that the relationship of ≦ D ″ /D′≦1.0 is satisfied, and it is more preferable that the relationship of 0.1 ≦ D ″ /D′≦0.8 is satisfied. By satisfying such a relationship, it is possible to relatively easily obtain toner particles 100 that are sufficiently fine, have a high degree of circularity, and have a sharp particle size distribution.

  In the above description, it has been described that one type of liquid (dispersion 3) is discharged from the supply port 5 of the nozzle M2. However, in the nozzle M2 having a plurality of supply ports 5, for example, from each supply port 5 , Liquids having different compositions can be discharged. More specifically, in the nozzle M2 as shown in FIGS. 8 to 18, liquids having different compositions are discharged from the respective supply ports 5, and these are joined together to disperse the binder resin and the filling material. After the liquid 3 is formed, the dispersion 3 can be sprayed toward the solidified portion M3. For example, in the description of the method for preparing the dispersion 3 described above, the binder resin is obtained by mixing the dispersion (suspension) containing the binder resin and the dispersion (suspension) containing the filling material. A plurality of methods for preparing the dispersion liquid 3 containing the filler material and the filling material have been described, but the dispersion liquid containing the binder resin (binder resin suspension) and the dispersion liquid containing the filling material prepared by these methods. (Supplementary material suspension) can be discharged from the plurality of supply ports 5 of the nozzle M2 as a first liquid and a second liquid, respectively. In the nozzle M2 having three or more supply ports 5 as shown in FIG. 9, for example, three or more kinds of liquids can be used in combination. More specifically, in the nozzle M2 configured as shown in FIG. 9, a dispersion liquid (binding resin suspension) containing a binding resin and a liquid containing a filling material (filling) are supplied from four supply ports 5, respectively. Material suspension), a dispersion containing a colorant (colorant suspension), a dispersion containing a wax (wax suspension), and joining them in the vicinity of the inclined surface 7 and the edge 7A, The dispersion liquid 3 may be ejected. Further, in the nozzle M2 configured as shown in FIG. 9, three types of liquids may be used. That is, liquids having different compositions are discharged from three of the four supply ports 5, and liquids having the same composition as any of these three liquids are discharged from the remaining one supply port 5. It may be discharged. Further, as described above, when a plurality of types of liquids are used, two or more of these include a dispersoid (first dispersoid) mainly composed of a binder resin and a filling material. The content of the binder resin and the filling material may be different from each other. Thus, the adhesive resin phase 42 can be selectively formed near the surface of the granular material 4 by using a combination of two or more kinds of liquids. That is, the granular material 4 can be obtained as a material substantially composed only of the constituent material of the resin fine particles in the vicinity of the central portion and having the adhesive resin phase 42 in the concave portion near the surface. As a result, the properties of the binder resin can be more effectively exhibited in the finally obtained toner.

  In the above description, a nozzle (liquid (dispersion)) as shown in FIGS. 7 to 18 is pressed against a smooth surface by a gas flow to be thinned to form a thin laminar flow, and the thin laminar flow is separated from the smooth surface. The method of making the dispersion into droplets (fine particles) using a nozzle that sprays as dispersion fine particles has been described, but any method can be used as long as a droplet-like dispersion can be obtained. For example, a spray drying method, a so-called ink jet method, a bubble jet (“bubble jet” is a registered trademark) method, or the like may be used.

The spray drying method is a method of obtaining droplets by ejecting (spraying) a liquid (dispersion) using a high-pressure gas.
Moreover, as a method to which a so-called ink jet method is applied, a method described in Japanese Patent Application No. 2002-169349 can be cited. That is, in the present invention, as a method of forming a droplet-like dispersion, “a method in which a dispersion is intermittently ejected from a head portion by piezoelectric pulses and conveyed in a solidified portion by an air current and granulated” is applied. can do.

  Moreover, as a method to which a so-called bubble jet (“bubble jet” is a registered trademark) method is applied, a method described in the specification of Japanese Patent Application No. 2002-169348 can be cited. That is, in the present invention, as a method of forming a droplet-like dispersion, “a method of intermittently discharging the dispersion from the head portion by changing the volume of the gas and making it granular while being conveyed in the solidified portion by an air current” Can be applied.

In particular, in the present invention, when the nozzle as described above is used, the following advantages are obtained as compared with the case where a general spray drying method is applied.
That is, in the method using the nozzle as described above, it is possible to easily and accurately control the ejection condition (amount of ejected droplets) of the dispersion compared to a general spray drying method. For this reason, for example, a granular material (toner base particle) having a desired size and shape can be efficiently produced. In particular, in the method described above, the formed fine particles can have very small size variation (small particle size distribution width), and therefore, variation in the moving speed of each particle can also be reduced. . Therefore, collision and aggregation between the ejected particles can be effectively prevented before the ejected dispersion liquid (droplet) is solidified, and as a result, an irregularly shaped powder is hardly formed. Accordingly, variation in the shape and size of the obtained granular material (toner mother particles) is particularly small, and even in the final toner, variations in charging characteristics, fixing characteristics, etc. among the particles are small, and the entire toner As a result, the reliability is particularly high. In the above-described method, even when the size of the granular material (toner base particle) to be manufactured is relatively small, the particle size distribution of the granular material (toner base particle) can be sharpened.

Further, the toner manufacturing apparatus M1 may be provided with a gas jetting unit (not shown) between the nozzle (jetting unit) M2 and the nozzle (jetting unit) M2. Thereby, the dispersion liquid 3 can be conveyed and solidified, maintaining the space | interval of the droplet 9 ejected intermittently from the nozzle M2. As a result, collision and aggregation of the ejected droplets 9 are more effectively prevented.
Further, by providing the gas injection means, it is possible to form a gas flow that flows in substantially one direction (downward in the figure) in the solidified portion M3. If such a gas flow is formed, the droplet 9 (granular body 4) in the solidification part M3 can be conveyed more efficiently.

Further, by providing the gas injection means, an airflow curtain is formed between the particles (droplets) ejected from each nozzle M2, and for example, collision and aggregation between the particles ejected from the adjacent nozzles. It becomes possible to prevent more effectively.
When such a gas injection means is provided, it is preferable that a heat exchanger (not shown) having a function of setting the temperature of the injected gas to a preferable value is attached. Thereby, the droplet 9 injected to the solidification part M3 can be solidified efficiently.
Further, when such a gas injection means is provided, it is possible to easily control the solidification speed and the like of the droplet 9 injected from the nozzle M2 by adjusting the supply amount of the gas flow.

<External addition process (external addition process)>
The granular material 4 obtained as described above is subjected to an external addition treatment for applying an external additive. Thereby, a toner (toner particle 100) is obtained.
As described above, since the granular body 4 has the filling phase 42, the degree of unevenness on the surface of the granular body 4 is relaxed, but usually the surface of the granular body 4 has minute unevenness. Exists. As a result, the external additive can be reliably supported, and the function as the external additive can be exhibited more effectively.

The external addition process can be performed, for example, by mixing the granular material (toner base particles) 4 and the external additive using a Henschel mixer or the like. The external additive may be jetted and / or convected into the solidified portion M3, and the external additive may be attached to the droplets 9 or the granular material (toner base particles) 4.
As the external additive, for example, those described above can be used.

  Further, substantially all of the external additive may be attached to the granular material 4 in the toner, or a part of the external additive may be released from the surface of the granular material 4. That is, the toner may contain an external additive released from the granular material 4. As described above, when the external additive released from the granular material 4 is contained in the toner in a predetermined ratio (relatively small amount), such a free external additive is, for example, opposite to the granular material 4. It can function as a microcarrier that is charged to polarity.

The toner obtained as described above may be subjected to classification treatment as necessary. The classification process may be performed before the external addition process.
For the classification treatment, for example, a sieve, an airflow classifier or the like can be used.
As mentioned above, although this invention was demonstrated based on suitable embodiment, this invention is not limited to this.

  For example, in the above-described embodiment, the kneaded product is used for preparing the dispersion, but the method for preparing the dispersion is not limited to this. For example, it may be prepared through a process in which components such as a binder resin, a filling material, and a colorant are put into a liquid medium (liquid). Moreover, the first dispersoid constituting the dispersion may be formed by a method such as an emulsion polymerization method.

Further, in the above-described embodiment, it has been described that a dispersion is prepared using a kneaded material made of a material containing at least a binder resin and a filling material, but instead of the filling material, a filling material and Mixtures with other components may be used.
Moreover, although embodiment mentioned above demonstrated the structure which uses a suspension liquid as a dispersion liquid, you may use an emulsion as a dispersion liquid, for example.

Further, in the above-described embodiment, the toner particles are described as being composed of a granular body including a joined body and a supplementary phase, and an external additive. However, the toner particles (toner) may include an external additive. It may not have. In other words, the granular material as described above may be used as toner particles as it is.
In addition, each part of the toner manufacturing apparatus used for manufacturing the toner of the present invention can be replaced with an arbitrary one that exhibits the same function, or another configuration can be added. For example, in the above-described embodiment, the configuration in which the granular dispersion liquid 3 (droplet 9) is ejected downward has been described. However, the ejection direction of the dispersion liquid may be any direction such as vertically upward or horizontal. Also good.

Further, in the above-described embodiment, it has been described that the binder resin is included in the resin fine particles (bonded body) and the filling material is included in the filling phase, but a part of the filling material is resin fine particles (bonded body). It may be included. Similarly, a part of the binder resin may be included in the filling phase.
In the embodiment described above, the rutile-anatase type titanium oxide has been described as being added as an external additive. For example, by using the rutile-anatase-type titanium oxide as one component of the raw material provided for the kneading step. The toner may be contained in the toner.

Further, intermediates such as placing the granule (toner base particles) obtained by removing the dispersion medium from the dispersion and the toner particles to which the external additive has been added to the granule under reduced pressure or heating. Processing and post-processing may be performed. Thereby, it is possible to more effectively prevent the dispersion medium and the like from remaining in the finally obtained toner particles.
Moreover, you may perform the thermal spheronization process which heats and spheroidizes the powder obtained by removing a dispersion medium from a dispersion liquid. Thereby, the circularity of the obtained granular material (toner base particles) can be further improved. The thermal spheronization treatment can be performed by spraying the powder obtained by removing the dispersion medium from the dispersion liquid (droplets) into a heated atmosphere using, for example, compressed air. Further, the thermal spheronization treatment may be performed in a liquid.

Moreover, although embodiment mentioned above demonstrated the structure which uses a continuous twin-screw extruder as a kneading machine, the kneading machine used for kneading | mixing a raw material is not limited to this. For kneading the raw materials, for example, various kneaders such as a kneader, a batch type triaxial roll, a continuous biaxial roll, a wheel mixer, and a blade type mixer can be used.
In the illustrated configuration, the kneader having two screws has been described. However, the number of screws may be one or three or more.

In the above-described embodiment, the configuration using the belt type as the cooler has been described. However, for example, a roll type (cooling roll type) cooler may be used. Moreover, the cooling of the kneaded material extruded from the extrusion port of the kneader is not limited to the one using the above-described cooling machine, and may be performed by air cooling or the like, for example.
Further, in the above-described embodiment, the colorant, the wax, and the like are described as the constituents of the dispersoid in the dispersion, but these components are included in the dispersion as the constituents of the dispersion medium. There may be.

Further, in the above-described embodiment, the bonded body 40 is described as one in which a plurality of resin fine particles are fused and integrated, and the boundary (interface) between the resin fine particles does not substantially exist. It may have a clear interface (boundary surface) between the fine particles.
Moreover, the filling phase 42 should just be formed in the recessed part near the surface of the granular material 4 (joined body 40) at least, and may be formed in parts other than such a recessed part. As a result, the mechanical stability and environmental characteristics of the toner particles can be further improved.

  In the above-described embodiment, the toner particles (granular bodies) including the joined body and the supplementary phase are obtained by discharging the dispersion liquid. However, the method for manufacturing the toner particles is not limited thereto. . For example, after forming resin fine particles by a method such as an emulsion polymerization method, a plurality of formed resin fine particles are melt-bonded to form a bonded body, and at least in a recess existing near the surface of the bonded body, a filling material is provided. Granules may be produced by applying and forming a fill phase. In addition, by discharging a dispersion liquid that does not contain a filling material, after forming a joined body in which a plurality of resin fine particles are melt-bonded, the joined body is immersed in a liquid containing a filling material, etc. A filling phase may be formed.

[1] Production of Toner A toner was produced as follows.
(Example 1)
<Preparation of binder resin suspension>
First, polyester resin as a binder resin (glass transition point Tg: 62 ° C., softening point Tf _1/2 : 108 ° C., weight average molecular weight Mw: 9800): 100 parts by weight, phthalocyanine pigment as a colorant (manufactured by Dainichi Seika Co., Ltd.) Phthalocyanine blue): 5 parts by weight, Cr-salicylic acid complex as a charge control agent (Bontron E-81, manufactured by Orient Chemical Industries): 1 part by weight, carnauba wax as a wax: 3 parts by weight, tetrahydrofuran as a solvent (Wako Pure Chemicals) 300 parts by weight were prepared.

These components were mixed and dispersed in a ball mill for 10 hours to prepare a binder resin solution.
On the other hand, an aqueous solution prepared by dissolving 10 parts by weight of sodium polyacrylate as a dispersant (manufactured by Wako Pure Chemical Industries, average polymerization degree n = 2700 to 7500) in 590 parts by weight of ion-exchanged water was prepared.
Next, 600 parts by weight of this aqueous solution is placed in a 3 liter round bottom stainless steel container, and a binder resin solution: 409 weights while stirring at a rotation speed of 4000 rpm using a TK homomixer (manufactured by Tokki Kako). The portion was gradually added dropwise over 10 minutes. At this time, the liquid temperature was kept at 70 ° C. The emulsion was further stirred for 10 minutes while maintaining the liquid temperature at 70 ° C. after the completion of the dropwise addition of the binder resin solution.

Next, under conditions of temperature: 45 ° C. and atmospheric pressure: 150 to 80 mmHg, tetrahydrofuran in the emulsion (dispersoid) is removed, then cooled to room temperature, and further ion-exchanged water is added to form a solid. A binder resin suspension in which fine particles were dispersed was obtained. The solid content (dispersoid) concentration in the binder resin suspension was 30 wt%. The average particle size d ₁ of the dispersoid constituting the binder resin suspension was 0.24 .mu.m. The average particle size of the dispersoid was measured using a laser diffraction / scattering particle size distribution analyzer (LA-920, manufactured by Horiba, Ltd.).

<Preparation of filling material suspension (adhesive resin suspension)>
First, an epoxy resin (glass transition point Tg: 58 ° C., softening point Tf _1/2 : 92 ° C., weight average molecular weight Mw: 8200): 100 parts by weight of tetrahydrofuran (Wako Pure Chemical Industries, Ltd.) as a filling material (adhesive resin) Manufactured): Dissolved in 100 parts by weight to obtain a filling material solution.
On the other hand, an aqueous solution prepared by dissolving 2 parts by weight of an anionic emulsifying dispersant (Sanyo Kasei Kogyo Co., Ltd., Ionette D-2) in 198 parts by weight of ion-exchanged water was prepared.

Next, 200 parts by weight of this aqueous solution is placed in a 3 liter round bottom stainless steel container, and using a TK homomixer (manufactured by Special Machine Chemical Co., Ltd.) while stirring at a rotational speed of 4000 rpm, the supplementary material solution: 200 parts by weight Was gradually added dropwise over 10 minutes. At this time, the liquid temperature was kept at 85 ° C. The emulsion was further stirred for 10 minutes while maintaining the liquid temperature at 85 ° C. after the completion of the dropwise addition of the binder resin solution.
Next, under the conditions of temperature: 50 ° C. and atmospheric pressure: 150-80 mmHg, the tetrahydrofuran in the emulsion (dispersoid) was removed, and then cooled to room temperature, whereby the solid fine particles (epoxy resin) were dispersed. A filling material suspension (adhesive resin suspension) was obtained. Thereafter, ion-exchanged water was further added so that the solid content (dispersoid) concentration was 40 wt% to obtain a final supplementary material suspension. The average particle size of the dispersoid constituting the filling material suspension was 0.21 μm.

<Preparation of suspension for granule production>
A first dispersoid mainly composed of a polyester resin and mainly composed of an epoxy resin by adding a supplementary material suspension to the binder resin suspension while stirring the binder resin suspension. A suspension (suspension) for producing a granule containing the second dispersoid was obtained. In the mixing of the binder resin suspension and the filling material suspension, the ratio of the polyester resin (binding resin) and the epoxy resin (filling material) in the suspension for producing the granular material is 5 by weight. : 1. Further, the viscosity at 25 ° C. of the obtained suspension for producing a granular material (suspension) was 15 cps.

<Manufacture of granular material>
The dispersion (suspension for granule production) obtained as described above was charged into the dispersion supply section of the toner production apparatus having the configuration shown in FIGS. While the dispersion liquid in the dispersion liquid supply part was stirred by the stirring means, it was supplied to the nozzle by a metering pump and was sprayed from the nozzle to the solidification part. Note that the temperature of the dispersion in the dispersion supply unit was adjusted to 25 ° C.
The dispersion was injected by injecting 20 mL / min of the dispersion together with compressed air having a pressure of 0.55 MPa.

The initial velocity of the dispersion liquid ejected from the nozzle was 4.2 m / second, and the average ejection amount for one drop of the dispersion liquid ejected from the nozzle was 1.5 pl (particle diameter D ′: 9.2 μm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.
Further, at the time of injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 85 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

  In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).

  The granular material formed in the solidified part was recovered with a cyclone. The recovered granular material had an average circularity R of 0.982, a circularity standard deviation of 0.010, a volume-based average particle diameter D of 7.5 μm, and a volume-based particle diameter standard deviation of 1.0 μm. The circularity was measured in a water dispersion system using a flow particle image analyzer (manufactured by Toa Medical Electronics Co., Ltd., FPIA-2000). However, the circularity R is represented by the following formula (I).

R = L ₀ / L ₁ (I)
(Wherein, L ₁ [μm] is the circumference of the projected image of the particle to be measured, and L ₀ [μm] is the circumference of a perfect circle having an area equal to the area of the projected image of the particle to be measured. Represents.)
<External treatment (manufacture of toner)>
An external additive: 2.5 parts by weight was added to 100 parts by weight of the obtained granular material to obtain a final toner (toner particles). The external additive was applied using a vertical high-speed mixer. As external additives, negatively chargeable small particle size silica (average particle size: 12 nm): 1 part by weight, negatively chargeable large particle size silica (average particle size: 40 nm): 0.5 part by weight, rutile anatase A type of titanium oxide (substantially spindle shape, average major axis diameter: 30 nm): 1 part by weight was used. In addition, as the negatively chargeable silica (negatively chargeable small particle size silica, negatively chargeable large particle size silica), those subjected to surface treatment (hydrophobization treatment) with hexamethyldisilazane were used. In addition, as the rutile-anatase type titanium oxide, the ratio of the rutile-type titanium oxide crystal structure to the anatase-type titanium oxide is 90:10 and absorbs light in the wavelength region of 300 to 350 nm. A thing was used. The finally obtained toner (toner particles) has an average circularity R of 0.980, a circularity standard deviation of 0.010, a volume-based average particle diameter D ″ of 7.6 μm, and a volume-based particle diameter standard. The deviation was 0.9 μm.
Further, the coverage of the external additive in the obtained toner (toner particles) was 150%.

(Example 2)
<Preparation of binder resin suspension>
First, nonionic surfactant (Sanyo Chemical Industries, Nonipol 85): 15 parts by weight, anionic surfactant (Daiichi Kogyo Seiyaku, Neogen SC): 5 parts by weight, and ion-exchanged water: An aqueous solution prepared by mixing 600 parts by weight was prepared.

Next, while stirring this aqueous solution in a flask, 300 parts by weight of styrene (manufactured by Wako Pure Chemical Industries, Ltd.) as a binder resin binder and butyl acrylate (Wako Pure Chemical Industries, Ltd.) are added to the aqueous solution. Product): An emulsion was obtained by gradually adding a mixture of 100 parts by weight and acrylic acid (manufactured by Wako Pure Chemical Industries, Ltd.): 10 parts by weight.
Next, an aqueous solution obtained by mixing 2 parts by weight of ammonium persulfate (manufactured by Tokai Denka Co., Ltd.) and 50 parts by weight of ion-exchanged water was added to the emulsion.

Next, the inside of the flask was purged with nitrogen, and then the solution in the flask was heated under the conditions of 70 ° C. × 5 hours while stirring to carry out an emulsion polymerization reaction.
Thereafter, the reaction solution is cooled to room temperature, and then moisture is removed by heating in an oven at 80 ° C., which is composed of a styrene resin (glass transition point Tg: 55 ° C., softening point Tf _1/2 : 134 ° C.). Thus, a binder resin suspension in which a dispersoid having an average particle diameter d _{1 of} 0.37 μm was dispersed was obtained.

<Preparation of colorant suspension>
Phthalocyanine pigment as a colorant (manufactured by Dainichi Seika Co., Ltd., phthalocyanine blue): 60 parts by weight, anionic surfactant (manufactured by Sanyo Chemical Industries, Ionette D-2): 2 parts by weight, and ion-exchanged water: 300 By mixing the weight part with a homogenizer, a colorant suspension in which colorant particles are dispersed as a dispersoid having an average particle diameter of 0.18 μm was obtained.

<Preparation of wax suspension>
Carnauba wax as wax: 100 parts by weight, anionic surfactant (Daiichi Kogyo Seiyaku Co., Ltd., Neogen SC): 5 parts by weight, ion-exchanged water: 1000 parts by weight, using a homogenizer, 100 parts The mixture was heated to 0 ° C. and then cooled to obtain a wax suspension in which wax particles were dispersed as a dispersoid having an average particle size of 0.45 μm.

<Preparation of filling material suspension (adhesive resin suspension)>
First, an epoxy resin (glass transition point Tg: 58 ° C., softening point Tf _1/2 : 92 ° C., weight average molecular weight Mw: 8200): 100 parts by weight of tetrahydrofuran (Wako Pure Chemical Industries, Ltd.) as a filling material (adhesive resin) Manufactured): Dissolved in 100 parts by weight to obtain a filling material solution.
On the other hand, an aqueous solution prepared by dissolving 2 parts by weight of an anionic emulsifying dispersant (Sanyo Kasei Kogyo Co., Ltd., Ionette D-2) in 198 parts by weight of ion-exchanged water was prepared.

  Next, 200 parts by weight of this aqueous solution is placed in a 3 liter round bottom stainless steel container, and a supplementary material solution: 200 parts by weight while stirring at a rotation speed of 4000 rpm using a TK homomixer (manufactured by Koki Kako). Was gradually added dropwise over 10 minutes. At this time, the liquid temperature was kept at 25 ° C. The emulsion was further stirred for 10 minutes while maintaining the liquid temperature at 25 ° C. after the completion of the dropwise addition of the binder resin solution.

  Next, under the conditions of temperature: 50 ° C. and atmospheric pressure: 150-80 mmHg, the tetrahydrofuran in the emulsion (dispersoid) was removed, and then cooled to room temperature to disperse the solid fine particles (epoxy resin). A filling material suspension was obtained. Thereafter, ion-exchanged water was further added so that the solid content (dispersoid) concentration was 30 wt% to obtain a final adhesive resin suspension. The average particle size of the dispersoid constituting the filling material suspension was 0.21 μm.

<Preparation of suspension for granule production>
By stirring the binder resin suspension, the colorant suspension, the wax suspension, and the filler suspension are added to the binder resin suspension in this order, thereby mainly producing styrene. A first dispersoid composed of a resin, a second dispersoid composed mainly of an epoxy resin, a dispersoid composed mainly of a phthalocyanine pigment (third dispersoid), and mainly carnauba wax. A suspension for producing a granular material (suspension) containing the constituted dispersoid (third dispersoid) was obtained. The mixing ratio of the binder resin suspension, the colorant suspension, the wax suspension, and the filling material suspension was 65: 5: 5: 25 by weight. Further, the viscosity at 25 ° C. of the obtained suspension for producing a granular material (suspension) was 18 cps.

<Manufacture of granular material>
The dispersion (suspension for granule production) obtained as described above was charged into the dispersion supply section of the toner production apparatus having the configuration shown in FIGS. While the dispersion liquid in the dispersion liquid supply part was stirred by the stirring means, it was supplied to the nozzle by a metering pump and was sprayed from the nozzle to the solidification part. Note that the temperature of the dispersion in the dispersion supply unit was adjusted to 25 ° C. Moreover, the same suspension, ie, the suspension for granule manufacture prepared as mentioned above, was supplied from two supply ports.

The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa.
The initial velocity of the dispersion liquid ejected from the nozzle was 4.2 m / second, and the average ejection amount for one drop of the dispersion liquid ejected from the nozzle was 0.68 pl (particle diameter D ′: 7.0 μm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.

In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.
(Example 3)
<Manufacture of kneaded material>
First, polyester resin as a binder resin (glass transition point Tg: 62 ° C., softening point Tf _1/2 : 108 ° C., weight average molecular weight Mw: 9800): 100 parts by weight, phthalocyanine pigment (manufactured by Dainichi Seika Co., Ltd.) as a colorant Phthalocyanine blue): 5 parts by weight, as a charge control agent, a salicylic acid Cr complex (Bontron E-81, manufactured by Orient Chemical Industries): 1 part by weight, and as a wax, 3 parts by weight of carnauba wax.

These components were mixed using a 20 L type Henschel mixer to obtain a raw material for preparing a kneaded product.
Next, this raw material (mixture) was kneaded using a biaxial kneading extruder as shown in FIG.
The total length of the process part of the biaxial kneading extruder was 160 cm.
Moreover, it set so that the temperature of the raw material in a process part might be 105-115 degreeC.

The screw rotation speed was 120 rpm, and the raw material charging speed was 20 kg / hour.
The time required for the raw material to pass through the process part, determined from such conditions, is about 4 minutes.
The kneading as described above was performed while degassing the inside of the process unit by operating a vacuum pump connected to the process unit via a degassing port.

The raw material (kneaded material) kneaded in the process part was extruded outside the biaxial kneading extruder through the head part. The temperature of the kneaded material in the head part was adjusted to 110 ° C.
Thus, the kneaded material extruded from the extrusion port of the biaxial kneader-extruder was cooled using a cooler as shown in FIG. The temperature of the kneaded material immediately after the cooling step was about 46 ° C.
The cooling rate of the kneaded product was −7 ° C./second. In addition, the time required from the end of the kneading process to the end of the cooling process was 10 seconds.

<Preparation of binder resin suspension>
The kneaded material cooled as described above was coarsely pulverized to obtain a powder having an average particle size of 1.5 mm. A hammer mill was used for coarse pulverization of the kneaded product.
Next, 300 parts by weight of the above coarsely pulverized product was put into 1000 parts by weight of toluene and heated to 80 ° C. with stirring to obtain a binder resin solution.

On the other hand, an aqueous solution prepared by dissolving 50 parts by weight of sodium polyacrylate as a dispersant (manufactured by Wako Pure Chemical Industries, average polymerization degree n = 2700-7500) in 2000 parts by weight of ion-exchanged water was prepared.
Next, 2050 parts by weight of this aqueous solution is placed in a 3 liter round bottom stainless steel container, and a binder resin solution: 1300 weights while stirring at a rotation speed of 4000 rpm using a TK homomixer (manufactured by Special Machine Chemical Co., Ltd.). The portion was gradually dropped. At this time, the liquid temperature was kept at 70 ° C. The emulsion was further stirred for 10 minutes while maintaining the liquid temperature at 70 ° C. after the completion of the dropwise addition of the binder resin solution.

Next, under conditions of temperature: 45 ° C. and atmospheric pressure: 150 to 80 mmHg, tetrahydrofuran in the emulsion (dispersoid) is removed, then cooled to room temperature, and further ion-exchanged water is added to form a solid. A binder resin suspension in which fine particles were dispersed was obtained. The solid content (dispersoid) concentration in the binder resin suspension was 30 wt%. The average particle size d ₁ of the dispersoid constituting the binder resin suspension was 0.36 .mu.m.

<Preparation of filling material suspension (adhesive resin suspension)>
First, urethane resin (glass transition point Tg: 56 ° C., softening point Tf _1/2 : 95 ° C., weight average molecular weight Mw: 7700): 100 parts by weight of tetrahydrofuran (Wako Pure Chemical Industries, Ltd.) as a filling material (adhesive resin) Product): Dissolved in 100 parts by weight to obtain a filling material solution.
On the other hand, an aqueous solution prepared by dissolving 2 parts by weight of an anionic emulsifying dispersant (Sanyo Kasei Kogyo Co., Ltd., Ionette D-2) in 198 parts by weight of ion-exchanged water was prepared.

  Next, 200 parts by weight of this aqueous solution is placed in a 3 liter round bottom stainless steel container, and a supplementary material solution: 200 parts by weight while stirring at a rotation speed of 4000 rpm using a TK homomixer (manufactured by Koki Kako). Was gradually added dropwise over 10 minutes. At this time, the liquid temperature was kept at 85 ° C. The emulsion was further stirred for 10 minutes while maintaining the liquid temperature at 85 ° C. after the completion of the dropwise addition of the binder resin solution.

  Next, under the conditions of temperature: 50 ° C. and atmospheric pressure: 150 to 80 mmHg, the tetrahydrofuran in the emulsion (dispersoid) was removed, and then cooled to room temperature, whereby solid fine particles (urethane resin) were dispersed. A filling material suspension was obtained. The solid content (dispersoid) concentration in the filling material suspension was 30 wt%. The average particle size of the dispersoid constituting the filling material suspension was 0.23 μm.

<Preparation of suspension for granule production>
While stirring the binder resin suspension, by adding the filler material suspension to the binder resin suspension, the first dispersoid mainly composed of polyester resin and mainly composed of urethane resin A suspension for producing a granule containing the second dispersoid was obtained. In the mixing of the binder resin suspension and the filler material suspension, the ratio of the polyester resin (binder resin) and the urethane resin (filler material) in the suspension for granule production is 5 by weight. : 1. Further, the viscosity at 25 ° C. of the obtained suspension for producing a granular material (suspension) was 25 cps.

<Manufacture of granular material>
The dispersion (suspension for granule production) obtained as described above was charged into the dispersion supply section of the toner production apparatus having the configuration shown in FIGS. While the dispersion liquid in the dispersion liquid supply part was stirred by the stirring means, it was supplied to the nozzle by a metering pump and was sprayed from the nozzle to the solidification part. Note that the temperature of the dispersion in the dispersion supply unit was adjusted to 25 ° C. Further, the same suspension, that is, the granule-producing suspension prepared as described above was supplied from the four supply ports.

The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa.
The initial velocity of the dispersion liquid ejected from the nozzle was 4.2 m / second, and the average ejection amount of one drop of the dispersion liquid ejected from the nozzle was 1.1 pl (particle diameter D ′: 8.1 μm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.

In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.
Example 4
<Manufacture of kneaded material>
First, a kneaded material was produced in the same manner as in Example 3.

<Preparation of liquid for preparing dispersion (liquid for preparing binder resin suspension)>
The kneaded material cooled as described above was coarsely pulverized to obtain a powder having an average particle size of 1.5 mm. A hammer mill was used for coarse pulverization of the kneaded product.
On the other hand, polyethylene glycol (Wako Pure Chemical Industries, # 5000): 60 g as a dispersant was dissolved in 12 liters of water to prepare an aqueous liquid.
Next, while stirring this aqueous liquid, 3 kg of the above coarsely pulverized product was added to the aqueous liquid to obtain a liquid for preparing a dispersion (liquid for preparing a binder resin suspension).

<Preparation of binder resin suspension>
Next, using the atomization apparatus as shown in FIG. 4 and FIG. 5, the dispersion preparation liquid (binding resin suspension preparation liquid) was subjected to the following treatment to be atomized. A dispersion (binder resin suspension) containing the kneaded product as a dispersoid was obtained.
First, the liquid for preparing a dispersion (liquid for preparing a binder resin suspension) was charged into the liquid supply part for preparing a dispersion of the atomizer. While the dispersion preparation liquid in the dispersion preparation liquid supply unit was stirred by the stirring means, it was supplied to two nozzles by an ultrahigh pressure generation pump, and the dispersion preparation liquid was ejected from each nozzle and collided. The collision angle θ of the dispersion preparation liquid ejected from each nozzle was adjusted to about 165 ° C. Further, the dispersion preparation liquid was allowed to collide while being heated so that the temperature of the dispersion preparation liquid (jetting temperature) when jetting from each nozzle was about 80 ° C. In addition, the dispersion preparation liquid (dispersion liquid) ejected and collided from each nozzle is transported from the recovery section to the dispersion preparation liquid supply section, and repeatedly used for injection and collision (atomization treatment) from the nozzles. It was done.

The dispersion preparation liquid was jetted from each nozzle at a jetting speed of 500 mL / min and a jetting pressure of 245 MPa for 10 minutes. The obtained dispersion had a viscosity at 25 ° C. of 140 cps and a solid content (dispersoid) concentration of 29.8 wt%. The average particle size d ₁ of the dispersoid dispersed in the dispersion liquid (solid particles) was 0.75 .mu.m.

<Preparation of liquid for preparing dispersion (liquid for preparing supplementary material suspension)>
First, a powder of epoxy resin having an average particle size of 1.0 mm (glass transition point Tg: 58 ° C., softening point Tf _1/2 : 92 ° C., weight average molecular weight Mw: 8200) was prepared as a filling material (adhesive resin). .
On the other hand, polyethylene glycol (Wako Pure Chemical Industries, # 5000): 60 g as a dispersant was dissolved in 12 liters of water to prepare an aqueous liquid.
Next, while stirring this aqueous liquid, 3 kg of the above-mentioned epoxy resin (complementary material) was added to the aqueous liquid to obtain a liquid for preparing a dispersion (liquid for preparing a supplementary material suspension).

<Preparation of supplementary material suspension>
Next, by using the atomization apparatus as shown in FIGS. 4 and 5, the dispersion preparation liquid (replenishment material suspension preparation liquid) is subjected to the following treatment, and thus atomized epoxy. A dispersion (resin material suspension) containing the resin as a dispersoid was obtained.
First, the liquid for preparing a dispersion (liquid for preparing a supplementary material suspension) was charged into the liquid supply for preparing a dispersion of the atomizer. While the dispersion preparation liquid in the dispersion preparation liquid supply unit was stirred by the stirring means, it was supplied to two nozzles by an ultrahigh pressure generation pump, and the dispersion preparation liquid was ejected from each nozzle and collided. The collision angle θ of the dispersion preparation liquid ejected from each nozzle was adjusted to about 165 ° C. Further, the dispersion preparation liquid was allowed to collide while being heated so that the temperature (injection temperature) of the dispersion preparation liquid when jetting from each nozzle was about 100 ° C. In addition, the dispersion preparation liquid (dispersion liquid) ejected and collided from each nozzle is transported from the recovery section to the dispersion preparation liquid supply section, and repeatedly used for injection and collision (atomization treatment) from the nozzles. It was done.
The dispersion preparation liquid was jetted from each nozzle at a jetting speed of 500 mL / min and a jetting pressure of 245 MPa for 10 minutes. The resulting dispersion had a viscosity at 25 ° C. of 122 cps and a solid content (dispersoid) concentration of 30 wt%. The average particle size of the dispersoid (solid fine particles) dispersed in the dispersion was 0.64 μm.

<Preparation of suspension for granule production>
A first dispersoid composed mainly of a polyester resin and mainly composed of an epoxy resin by adding a supplementary material suspension to the binder resin suspension while stirring the binder resin suspension. A granule-producing suspension containing the second dispersoid was obtained. In the mixing of the binder resin suspension and the filling material suspension, the ratio of the polyester resin (binding resin) and the epoxy resin (filling material) in the suspension for producing the granular material is 5 by weight. : 1.

<Manufacture of granular material>
The dispersion (suspension for granule production) obtained as described above was charged into the dispersion supply section of the toner production apparatus having the configuration shown in FIGS. 6 and 10 to 12. While the dispersion liquid in the dispersion liquid supply part was stirred by the stirring means, it was supplied to the nozzle by a metering pump and was sprayed from the nozzle to the solidification part. Note that the temperature of the dispersion in the dispersion supply unit was adjusted to 25 ° C. Moreover, the same suspension, ie, the suspension for granule manufacture prepared as mentioned above, was supplied from two supply ports.

The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa.
The initial velocity of the dispersion liquid ejected from the nozzle was 4.2 m / second, and the average ejection amount for one drop of the dispersion liquid ejected from the nozzle was 0.43 pl (particle diameter D ′: 6.1 μm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.

In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.
(Example 5)
Instead of the filling material suspension, a filling material solution in which the filling material (adhesive resin) is dissolved is used. At the time of external addition treatment, positively charged silica (average particle size: 40 nm): 1 part by weight is added as an external additive. Granules and toner (toner particles) were produced in the same manner as in Example 2 except that they were used. In addition, as a supplement material solution, what was dissolved in ion-exchange water so that the density | concentration of water-soluble epoxy resin might be 30 wt% was used. Moreover, the viscosity at 25 ° C. of the suspension for producing a granular material (suspension) used in this example was 120 cps.

(Example 6)
First, in the same manner as in Example 1, a binder resin suspension and a filling material suspension were prepared.
Thereafter, the binder resin suspension and the supplementary material suspension were put into the two dispersion supply parts of the toner manufacturing apparatus having the configuration shown in FIGS. 6 and 8, respectively. While the dispersion liquid (binder resin suspension and supplementary material suspension) in each dispersion supply part was stirred by a stirring means, it was supplied to the nozzle by a metering pump, and the two suspensions were combined. Then, it sprayed to the solidification part from this nozzle. The temperature of each dispersion in each dispersion supply unit was adjusted to 25 ° C. In the toner manufacturing apparatus having such a configuration, the binder resin suspension is supplied from the supply port on the inner peripheral side of the nozzle, and the supplementary material suspension is supplied from the supply port on the outer peripheral side.

  The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa. In addition, the discharge amount of the binder resin suspension and the filling material suspension from each supply port is determined by the dispersion liquid (first dispersoid mainly composed of the binder resin and mainly composed of the filler material). The ratio of the polyester resin (binder resin) and the epoxy resin (complementary material) in the suspension containing the second dispersoid was adjusted to 5: 1 by weight.

The initial velocity of the dispersion liquid ejected from the nozzle (mixed liquid of the above two dispersion liquids) is 4.2 m / second, and the average ejection amount of one droplet of the dispersion liquid ejected from the nozzle is 1.5 pl (particle diameter D ': 9.2 µm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.
In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. At this time, the pressure in the housing was adjusted to 0.109 to 0.110 MPa, and the exhaust air temperature at the lower part of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.

(Example 7)
First, in the same manner as in Example 7, a binder resin suspension, a colorant suspension, a wax suspension and a filling material suspension were prepared.
Thereafter, the binder resin suspension, the colorant suspension, the wax suspension, and the supplementary material suspension are respectively charged into the four dispersion supply units of the toner manufacturing apparatus configured as shown in FIGS. did. While the dispersion liquid (binder resin suspension, colorant suspension, wax suspension and supplementary material suspension) in each dispersion supply section is stirred by a stirring means, it is supplied to the nozzle by a metering pump, After the four types of suspensions were merged, they were sprayed from the nozzles to the solidified portion. The temperature of each dispersion in each dispersion supply unit was adjusted to 25 ° C. Further, in the toner manufacturing apparatus having such a configuration, from the four supply ports of the nozzle, the binder resin suspension, the colorant suspension, the wax suspension, A filling material suspension was fed.

The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa. The discharge amount of the binder resin suspension, the colorant suspension, the wax suspension and the filling material suspension from each supply port is such that the mixing ratio is 65: 5: 5 by weight. : Adjusted to be 25.
The initial velocity of the dispersion liquid ejected from the nozzle (mixture of the above four dispersion liquids) is 4.2 m / second, and the average ejection amount of one droplet of the dispersion liquid ejected from the nozzle is 0.68 pl (particle diameter D ': 7.0 μm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.

In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.

(Example 8)
First, in the same manner as in Example 3, a binder resin suspension and a supplement material suspension were prepared.
Thereafter, the binder resin suspension and the supplementary material suspension were put into the two dispersion supply parts of the toner manufacturing apparatus having the configuration shown in FIGS. 6 and 8, respectively. While the dispersion liquid (binder resin suspension and supplementary material suspension) in each dispersion supply part was stirred by a stirring means, it was supplied to the nozzle by a metering pump, and the two suspensions were combined. Then, it sprayed to the solidification part from this nozzle. The temperature of each dispersion in each dispersion supply unit was adjusted to 25 ° C. In the toner manufacturing apparatus having such a configuration, the binder resin suspension is supplied from the supply port on the inner peripheral side of the nozzle, and the supplementary material suspension is supplied from the supply port on the outer peripheral side.

  The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa. In addition, the discharge amount of the binder resin suspension and the filling material suspension from each supply port is determined by the dispersion liquid (first dispersoid mainly composed of the binder resin and mainly composed of the filler material). The ratio of the polyester resin (binder resin) and the urethane resin (complementary material) in the suspension containing the second dispersoid was adjusted to 5: 1 by weight.

The initial velocity of the dispersion liquid ejected from the nozzle (mixed liquid of the above two dispersion liquids) is 4.2 m / second, and the average ejection amount of one droplet of the dispersion liquid ejected from the nozzle is 1.1 pl (particle diameter D ': 8.1 µm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.
In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.

Example 9
First, in the same manner as in Example 4, a binder resin suspension and a supplement material suspension were prepared.
Thereafter, the binder resin suspension and the supplementary material suspension were put into the two dispersion supply parts of the toner manufacturing apparatus having the configuration shown in FIGS. 6 and 8, respectively. While the dispersion liquid (binder resin suspension and supplementary material suspension) in each dispersion supply part was stirred by a stirring means, it was supplied to the nozzle by a metering pump, and the two suspensions were combined. Then, it sprayed to the solidification part from this nozzle. The temperature of each dispersion in each dispersion supply unit was adjusted to 25 ° C. In the toner manufacturing apparatus having such a configuration, the binder resin suspension is supplied from the supply port on the inner peripheral side of the nozzle, and the supplementary material suspension is supplied from the supply port on the outer peripheral side.

  The dispersion was injected by injecting 20 mL of dispersion per minute together with compressed air having a pressure of 0.64 MPa. In addition, the discharge amount of the binder resin suspension and the filling material suspension from each supply port is determined by the dispersion liquid (first dispersoid mainly composed of the binder resin and mainly composed of the filler material). The ratio of the polyester resin (binder resin) and the epoxy resin (complementary material) in the suspension containing the second dispersoid was adjusted to 5: 1 by weight.

The initial velocity of the dispersion liquid ejected from the nozzle (mixed liquid of the above two dispersion liquids) is 4.2 m / second, and the average ejection amount of one droplet of the dispersion liquid ejected from the nozzle is 0.43 pl (particle diameter D ': 6.1 µm). Further, the dispersion liquid was ejected so that the ejection timing of the dispersion liquid was shifted by at least adjacent nozzles among the plurality of nozzles.
In addition, when injecting the dispersion liquid, air of temperature: 135 ° C., humidity: 30% RH, flow rate: 0.9 m ³ / min is injected vertically downward from a gas injection port (not shown) provided between the nozzles. In this case, the pressure in the housing was adjusted to 1 to 5 kPa, and the exhaust air temperature at the bottom of the housing was adjusted to 90 ° C. In addition, a voltage was applied to the housing of the solidified portion so that the potential on the inner surface side became −200 V, thereby preventing the dispersion liquid (granular material (toner mother particles)) from adhering to the inner wall. .

In the solidification part, the dispersion medium is removed from the sprayed dispersion, and a plurality of resin fine particles (resin fine particles derived from the first dispersoid) are melt-bonded, and a supplement material derived from the second dispersoid Granules (toner mother particles) having (complementary phase) were formed. The obtained granular material had at least a filling phase in a concave portion (a concave portion formed at a portion corresponding to the bonded portion of the adjacent resin fine particles) near the surface of the granular material (bonded body).
The granular material formed in the solidified part was recovered with a cyclone.

<External treatment (manufacture of toner)>
An external additive was applied to the obtained granular material in the same manner as in Example 1 to obtain a final toner (toner particle). The coverage of the external additive in the obtained toner (toner particles) was 150%.
(Example 10)
Instead of the supplementary material suspension, a supplementary material solution in which the supplementary material was dissolved was used, and at the time of external addition treatment, positively charged silica (average particle size: 40 nm): 1 part by weight was used as an external additive. In the same manner as in Example 7, granules and toner (toner particles) were produced. In addition, as a supplement material solution, what was dissolved in ion-exchange water so that the density | concentration of water-soluble epoxy resin might be 30 wt% was used. Moreover, the viscosity at 25 ° C. of the suspension for producing a granular material (suspension) used in this example was 120 cps.

(Comparative Example 1)
First, a coarsely pulverized kneaded material was obtained in the same manner as in Example 3.
Next, the coarsely pulverized kneaded product was finely pulverized. A jet mill (200 AFG, manufactured by Hosokawa Micron Corporation) was used for finely pulverizing the kneaded product. The fine pulverization was performed at a pulverization air pressure: 500 [kPa] and a rotor rotational speed: 7000 [rpm].

The pulverized material thus obtained was classified with an airflow diverter (manufactured by Hosokawa Micron Corporation, 100 ATP).
Thereafter, the classified pulverized product (powder for toner production) was subjected to a thermal spheronization treatment. The thermal spheronization treatment was performed using a thermal spheronization apparatus (Nippon Pneumatic Co., Ltd., SFS3 type). The temperature of the atmosphere during the heat spheronization treatment was 270 ° C.
Thereafter, an external additive was applied to the powder subjected to the thermal spheronization treatment under the same conditions as in Example 3 to obtain a toner.

(Comparative Example 2)
First, a coarsely pulverized kneaded product was obtained in the same manner as in Comparative Example 1.
Next, the coarsely pulverized kneaded product was finely pulverized to obtain a finely pulverized product. A jet mill (200 AFG, manufactured by Hosokawa Micron Corporation) was used for finely pulverizing the kneaded product. The fine pulverization was performed at a pulverization air pressure: 500 [kPa] and a rotor rotational speed: 7000 [rpm].

  The above finely pulverized product: 100 parts by weight, together with zinc stearate (dispersing agent): 5 parts by weight, negatively charged small particle size silica (average particle diameter: 12 nm): 10 parts by weight, added to 1000 parts by weight of water By sufficiently stirring with a mixer, a dispersion (including a precipitate) was obtained. In addition, as the negatively chargeable small particle size silica, those subjected to surface treatment (hydrophobization treatment) with hexamethyldisilazane were used.

  The dispersion was spray-dried using a centrifugal spray dryer using an atomizer under the conditions of hot air temperature: 280 ° C. and rotation speed: 10,000 rpm to obtain a toner. By spraying the dispersion under such conditions, the finely pulverized product contained in the dispersion was turned into a hot sphere. Further, the obtained toner particles are obtained by attaching negatively chargeable small particle size silica to the surface of each finely pulverized product contained in the dispersion, and a plurality of finely pulverized products (dispersoids). The presence of aggregates was not confirmed.

(Comparative Example 3)
In the same manner as in Example 1 except that the binder resin suspension was used as it was as a suspension for producing granules without mixing with the filler suspension, the granules, toner (toner particles) ) Was manufactured. The viscosity at 25 ° C. of the suspension for producing a granular material (suspension) used in Comparative Example 3 was 14 cps.

(Comparative Example 4)
In the production of the granular material, the temperature of the air injected from the gas injection port is 170 ° C., and the temperature in the housing at this time is 170 ° C. Toner (toner particles) was produced.
The surface shapes of the granular materials and toner particles obtained in Examples 1 to 10 were observed using a scanning electron microscope (SEM). In the granular materials and toner particles of Examples 1 to 10, a plurality of binder resin fine particles are melt-bonded, and correspond to the concave portions near the surface of the granular materials (joined bodies) (joining portions of the adjacent resin fine particles). It was confirmed that a filling phase was present in the recesses formed in the part, and that the filling phase relaxed the irregularities of the granular material (toner particles). On the other hand, the granule and toner particles of the comparative example did not have such a configuration.

For each of the examples and comparative examples, the average circularity R, the circularity standard deviation, the volume-based average particle diameter D, the particle diameter standard deviation, and the average circularity R of the toner particles for the granular material (toner base particles). , Circularity standard deviation, volume-based average particle diameter D ″, and particle diameter standard deviation are the conditions of the dispersion used in the production of the toner (the average particle diameter D ′ of the droplet, the average particle of the first dispersoid The results are shown in Table 1 together with the diameter d ₁ ).

  As apparent from Table 1, in the toner of the present invention, the granularity (toner base particles), the circularity of the toner particles is relatively large, and the standard deviation of the circularity and the standard deviation of the particle diameter are small, The variation in size was small. On the other hand, in the comparative examples (particularly Comparative Examples 1 and 2), the degree of circularity was small and the variation in shape and size was large.

[2] Evaluation Each toner obtained as described above was evaluated for durability, transfer efficiency, cleaning properties, image density, and good fixing range.
[2.1] Durability The toner obtained in each of the above examples and comparative examples is packed in a cartridge of a laser printer (manufactured by Seiko Epson Corporation, LP-3000C), set in the printer, and developed without printing. The device was driven continuously. After 12 hours, the developing device was taken out from the printer, and the formation state of the toner thin layer on the developing roller was visually observed and evaluated according to the following four criteria.
A: No disturbance is observed in the thin layer.
○: Disturbance is hardly observed in the thin layer.
Δ: Some disturbance is observed in the thin layer.
X: Many streaky disturbances are clearly recognized in the thin layer.

[2.2] Transfer efficiency Evaluation was performed as follows using a laser printer (manufactured by Seiko Epson Corporation, LP-3000C).
The toner on the photoconductor immediately after the development process (before transfer) to the photoconductor (image carrier) and the toner on the photoconductor after transfer (after printing) are collected using separate tapes. The weight was measured. When the toner weight on the photoconductor before transfer is W _b [g] and the toner weight on the photoconductor after transfer is W _a [g], it is obtained as (W _b −W _a ) × 100 / W _b. The value was determined as transfer efficiency. It can be said that the larger the numerical value, the better the transfer efficiency.

[2.3] Cleaning property The toner obtained in each of the above examples and comparative examples is packed in a cartridge of a laser printer (manufactured by Seiko Epson Corporation, LP-3000C), set in the printer, and continuously printed 6000 sheets. The cleaning property was evaluated according to the following three criteria.
○: No wiping residue on the surface of the photoreceptor is observed.
Δ: At the initial stage of printing, almost no wiping residue on the surface of the photoreceptor is observed, but the cleaning defect gradually increases, and when 5000 sheets are printed, an obvious cleaning defect is observed.
X: A clear cleaning defect is recognized from the initial stage of printing.

[2.4] Image Density of the solid image portion of a print sample obtained using a laser printer (manufactured by Seiko Epson Corporation, LP-3000C) using the toner obtained in each of the above Examples and Comparative Examples. The print density and uniformity were visually observed and evaluated according to the following two-stage criteria.
○: Image density is sufficient and uniform.
X: Insufficient image density or streaky unevenness.

[2.5] Good Fixing Region First, a laser printer (manufactured by Seiko Epson Corporation, LP-3000C) equipped with a fixing device was prepared. In this fixing device, the time Δt required for the toner to pass through the nip portion was set to 0.05 seconds.
Next, an unfixed image sample was collected using the above laser printer, and the following test was performed with the fixing device of the laser printer. The solid amount of the sample to be collected was adjusted to an adhesion amount of 0.40 to 0.50 mg / cm ² .

In the state where the surface temperature of the fixing roller of the fixing device constituting the laser printer is set to a predetermined temperature, the paper on which the unfixed toner image is transferred (Seiko Epson, high-quality plain paper) is introduced into the fixing device. As a result, the toner image was fixed on the paper, and the presence or absence of offset after fixing was visually confirmed.
Similarly, the set temperature of the surface of the fixing roller is sequentially changed within a range of 100 to 250 ° C., and the presence or absence of occurrence of an offset at each temperature is confirmed. It was determined as “range” and evaluated according to the following four-stage criteria.
(Double-circle): The width | variety of a favorable fixing area is 60 degreeC or more.
◯: The width of the fixing good region is 45 ° C. or more and less than 60 ° C.
(Triangle | delta): The width | variety of a favorable fixing area is 30 degreeC or more and less than 45 degreeC.
X: The width of the good fixing region is less than 30 ° C.
These results are summarized in Table 2.

As can be seen from Table 2, the toner of the present invention gave excellent results in all of durability, transfer efficiency, cleaning properties, image density, and good fixing area.
On the other hand, with the toner of the comparative example, sufficient characteristics could not be obtained.
In particular, the toners of Comparative Examples 3 and 4 in which the toner particles are composed of a plurality of fine particles (resin fine particles) and have no supplementary phase have particularly low durability. Further, in the toners of Comparative Examples 2 and 4, characteristics such as a good fixing area were remarkably low. This is considered to be because the constituent material of the toner was deteriorated because the conditions for ejecting the liquid for producing the toner were severe. Further, in the toner of Comparative Example 2, the external additive added in the dispersion liquid is buried in the toner base particles at the time of spray drying, and the function as the external additive is not sufficiently exhibited. It was.

  In addition, as a colorant, C.I. I. Pigment blue, carbon black, quinacridone (PR 122), pigment red 57: 1, C.I. I. Except that Pigment Yellow 93 was used, toners were prepared in the same manner as in the above Examples and Comparative Examples, and these toners were evaluated in the same manner as described above. As a result, the same results as those of the respective Examples and Comparative Examples were obtained.

FIG. 2 is a cross-sectional view schematically showing a preferred embodiment of the toner (toner particles) of the present invention. It is a flowchart for a softening point analysis. It is a longitudinal cross-sectional view which shows typically an example of a structure of the kneading machine for manufacturing the kneaded material used for preparation of a dispersion liquid, and a cooler. It is a longitudinal cross-sectional view which shows typically suitable embodiment of the apparatus for preparing a dispersion liquid. It is an expanded sectional view of the chamber vicinity of the apparatus shown in FIG. FIG. 3 is a longitudinal sectional view schematically showing a preferred embodiment of a toner production apparatus used for producing the toner of the present invention. It is sectional drawing which shows suitable embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles. It is sectional drawing which shows other embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles. It is sectional drawing which shows other embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles. It is sectional drawing which shows other embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles. It is a principal part expanded sectional view of the nozzle shown in FIG. It is an expanded sectional view which shows the inner side intermediate ring front-end | tip part of the nozzle shown in FIG. It is sectional drawing which shows other embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles. It is a principal part expanded sectional view of the nozzle shown in FIG. It is an expanded sectional view which shows the inner side intermediate ring front-end | tip part of the nozzle shown in FIG. It is sectional drawing which shows other embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles. It is a top view of the gas peeling recessed part shown in FIG. It is sectional drawing which shows other embodiment of the nozzle which injects a dispersion liquid as microparticles | fine-particles.

Explanation of symbols

  K1 …… Kneading machine K2 …… Process part K21 …… Barrel K22, K23 …… Screw K24 …… Fixing member K25 …… Deaeration port K3 …… Head K31 …… Internal space K32 …… Extrusion port K33 …… Transverse Area gradually decreasing part K4 ... Feeder K5 ... Raw material K6 ... Cooler K61, K62, K63, K64 ... Roll K611, K621, K631, K641 ... Rotating shaft K65, K66 ... Belt K67 ... Discharge part K7 ... ... Kneaded material B1 ... Atomizer B21, B22 ... Nozzle B3 ... Liquid supply part for dispersion preparation (dispersion supply part) B31 ... Agitating means B4 ... Chamber B5 ... Housing part B6 ... Recovery part B7 …… Ultra-high pressure generating pump B8 …… Branching part B9 …… Conveying pump B10 …… Conveying pipe M1 …… Toner manufacturing device M …… Nozzle M3 …… Solidifying part M31 …… Housing M311 …… Reduced diameter part M4 …… Dispersed liquid supply part M41 …… Agitating means M5 …… Recovery part M8 …… Voltage applying means M10 …… Gas flow supplying means M101… … Duct M11 …… Valve M12 …… Pressure adjusting means M121 …… Connecting pipe M122 …… Diameter enlarged part M123 …… Filter 1 …… Flow path 2 …… Liquid for preparing dispersion (crushed material-containing liquid) 3 …… Dispersion Liquid 31 ... Dispersoid 311 ... First dispersoid 312 ... Second dispersoid 32 ... Dispersion medium 4 ... Granules (toner mother particles) 40 ... Conjugate 42 ... Supplementary phase 5 ... Supply port 7: Inclined surface 7A: Edge 8: Thin laminar flow 9 ... Droplet 10 ... Gas port 11 ... Inner ring 12 ... Intermediate ring 12A ... Inner intermediate ring 12B: Outer intermediate ring 3 ... Outer ring 14 ... Atomized gas flow path 15 ... Spreading gas supply path 16 ... Center ring 17 ... Spreading gas injection port 18 ... Breathable member 19 ... Gas separation recess 20 ... Through hole 21 ... Liquid flow path 22 ... Helical rib F ... Pressurized gas source P ... Pump 100 ... Toner particles

Claims (11)

A toner that is an aggregate of toner particles obtained by melt-bonding a plurality of resin fine particles mainly composed of a binder resin,
The toner particle has a recess formed near the surface thereof, and has a filling phase that relaxes the degree of unevenness of the toner particle at least in the recess.   The toner according to claim 1, wherein the concave portion is formed in a portion corresponding to a joint portion of the resin fine particles adjacent to each other.   The toner according to claim 1, wherein the filling phase is mainly composed of a thermosetting resin.   The toner according to claim 1, wherein the filling phase is mainly composed of an epoxy resin.   The toner according to claim 1, wherein the resin fine particles contain a colorant.   The toner according to claim 1, wherein the resin fine particles contain a wax.   The toner according to claim 1, wherein an average particle diameter of the toner particles is 2 to 20 μm.   The toner according to claim 1, further comprising an external additive.   The toner according to claim 1, wherein the standard deviation of the particle diameter between the toner particles is 1.6 μm or less. The toner according to claim 1, wherein the toner particles represented by the following formula (I) have an average circularity R of 0.91 to 0.99.
R = L ₀ / L ₁ (I)
(Where, L ₁ [μm] is the circumference of the projected image of the toner particles to be measured, and L ₀ [μm] is the circumference of a perfect circle having an area equal to the area of the projected image of the toner particles to be measured) Represents length)   The toner according to claim 1, wherein a standard deviation of circularity between the toner particles is 0.05 or less.

Images