Description

Ｌｎ源化合物としてＹ₂Ｏ₃；１．４４モル、Ｍ源化合物としてγ−Ａｌ₂Ｏ₃；２．５モル、Ｃｅ源化合物としてＣｅＯ₂；０．０９モル、Ｔｂ源化合物としてＴｂ₄Ｏ₇：０．０
０７５モル、並びに融剤としてＢａＦ₂；０．２５モルを用い、１４００℃で焼成したこ
と以外は実施例１と同様の方法にて、黄色発光蛍光体（Ｙ_0.96Ｃｅ_0.03Ｔｂ_0.01）₃Ａｌ₅Ｏ₁₂を作製した。得られた蛍光体につき、実施例１と同様に物体色と全光束を測定したところ、物体色はＬ^*＝１０２．７、ａ^*＝−１４．９、ｂ^*＝５８．８、全光束は１１６％
であった。結果を表−１に示す。
（実施例６）
Y ₂ O ₃ as the Ln source compound; 1.44 mol, γ-Al ₂ O ₃ as the M source compound; 2.5 mol, CeO ₂ as the Ce source compound; 0.09 mol, Tb ₄ O ₇ as the Tb source compound : 0.0
075 mol, and BaF ₂ as a flux; with 0.25 mole, in the same manner as in Example 1 except that calcined at 1 400 ° C., the yellow-emitting phosphor _{_{_{(Y 0.96 Ce 0.03 Tb 0.01)}}} 3 Al ₅ O ₁₂ was produced. When the object color and the total luminous flux were measured for the obtained phosphor as in Example 1, the object color was L ^* = 102.7, a ^* = − 14.9, b ^* = 58.8, the total luminous flux. 116%
Met. The results are shown in Table-1.
(Example 6)

Ｌｎ源化合物としてＹ₂Ｏ₃；１．４４モル、Ｍ源化合物としてγ−Ａｌ₂Ｏ₃；２．５モル、Ｃｅ源化合物としてＣｅＯ₂；０．１２モル、並びに融剤としてＢａＦ₂；０．２５モルを用い、１４００℃で焼成したこと以外は実施例１と同様の方法にて、黄色発光蛍光
体（Ｙ_0.96Ｃｅ_0.04）₃Ａｌ₅Ｏ₁₂を作製した。実施例１と同様の評価を行ったところ、物体色はＬ^*＝１０１．２、ａ^*＝−１４．７、ｂ^*＝５７．８、全光束は１１０％、温度特
性は９８％であった。また、ｔ１は１５１ｎｓ、ｔ２／ｔ１は２．０３であった。結果を表−１に示す。
（実施例７） Y ₂ O ₃ as the Ln source compound; 1.44 mol, γ-Al ₂ O ₃ as the M source compound; 2.5 mol, CeO ₂ as the Ce source compound; 0.12 mol, and BaF ₂ as the flux: 0 with .25 mole, in the same manner except that calcined at 1 400 ° C. as in example 1 to prepare a yellow-emitting phosphor _{_{_{(Y 0.96 Ce 0.04) 3 Al}}} 5 O 12. When the same evaluation as in Example 1 was performed, the object color was L ^* = 101.2, a ^* = − 14.7, b ^* = 57.8, the total luminous flux was 110%, and the temperature characteristic was 98%. It was. Moreover, t1 was 151 ns and t2 / t1 was 2.03. The results are shown in Table-1.
(Example 7)