JP2004313415A

JP2004313415A - Antibacterial mask

Info

Publication number: JP2004313415A
Application number: JP2003110832A
Authority: JP
Inventors: Yoichi Kobayashi; 洋一小林; Minoru Morita; 稔森田
Original assignee: TOOKOO EIZAI KK
Current assignee: TOOKOO EIZAI KK
Priority date: 2003-04-15
Filing date: 2003-04-15
Publication date: 2004-11-11
Anticipated expiration: 2023-04-15
Also published as: JP4004987B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide an antibacterial mask which inactivates a virus or the like and has bells and whistles such as a skin care function or the like. <P>SOLUTION: A mask 20 is composed of a main body of the mask 21 made of a fiber sheet 23 and hook members 25 disposed at both the sides of the main body of the mask, wherein the main body of the mask is laminated with an antibacterial fiber sheet 22 stuck with an ascorbic acid derivative so that the mask is antiviral. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、ウイルス等の不活化が可能な抗ウイルスマスクに関するものである。
【０００２】
【従来の技術】
空気中の粉塵、花粉、細菌やウイルス等が呼吸を介して体内への侵入を防ぐ目的で衛生用もしくは医療用等のマスクは以前から広く知られている。
【０００３】
従来、このようなマスクとしては、例えば特許文献１〜５などがある。特許文献１には、ゼオライトを繊維類に接着することにより、ウイルス等の有害成分を吸着捕捉するマスクが、また特許文献２には、ハイドロキシアパタイト等のリン酸カルシウム系化合物を不織布などのシートに担持させ、かつ多数の微小通気孔により、各種細菌、ウイルス等の有害成分を捕捉するマスクが開示されている。しかしながら、ウイルス等を物理的に吸着させたこれらの方法では、活性状態のウイルスがマスク本体に存在しうる。また、吸着能力が限界に達すると、活性状態のウイルスがマスク本体を通して人体内に侵入することも考えられ、あまり有効なものとはいえない。
【０００４】
一方、薬剤を用いてウイルス等を化学的に不活化させるようなマスクとして、例えば特許文献３や４には茶の抽出成分である茶ポリフェノールを不織布に添着した抗ウイルスマスクが、また、特許文献５には、銀付繊維を用いた抗菌マスクが開示されている。それら薬剤は通常、皮膚に対して安全であるとは言われているものの、人によってはアレルギーを起こしてしまうなどの問題があり、必ずしも全く安全なものとは言いきれない。
【０００５】
また、一般的に、マスクは口元周辺に着用され、皮膚に直接ないしは間接的に触れるが、それら従来のマスクにおいては粉塵、花粉、細菌やウイルス等の異物を何らかの方法で防ぐという単独機能を有するのみであり、口元周辺のスキンケア等の観点にまでは考慮されてはいない。
【０００６】
【特許文献１】
特開昭５３−５６８９４号公報
【特許文献２】
特開平５−１１５５７２号公報
【特許文献３】
特開平８−３３３２７１号公報
【特許文献４】
特開２００２−１３６６１５号公報
【特許文献５】
特開平１１−１９２３８号公報
【０００７】
【発明が解決しようとする課題】
本発明の課題は、上述の事情に鑑みなされたもので、ウイルス等の不活化ができると同時にスキンケア等の付加機能を有する抗ウイルスマスクを提供することにある。
【０００８】
【課題を解決するための手段】
本発明者らは、上記課題を解決すべく、鋭意研究を重ねた結果、アスコルビン酸誘導体が固着した繊維シートであれば、ウイルス等を化学的に不活化させ、各種感染を防ぐことができると共に、アスコルビン酸誘導体を皮膚表面から体内へ徐放出させることが可能な、スキンケア等の付加機能を有する抗ウイルスマスクが得られることを見出し、本発明を完成するに至った。
【０００９】
本発明の第１は、繊維シートよりなるマスク本体と、該マスク本体の両端部に設けた耳掛け部とからなるマスクにおいて、アスコルビン酸誘導体が固着した抗ウィルス用繊維シートを該マスク本体に積層してなることを特徴とする抗ウイルスマスクに関する。
本発明の第２は、前記アスコルビン酸誘導体が安定型の油溶性アスコルビン酸類である請求項１に記載の抗ウイルスマスクに関する。
本発明の第３は、前記アスコルビン酸誘導体が固着した抗ウイルス用繊維シートを、前記マスク本体の皮膚に直接触れる側に積層した請求項１または２に記載の抗ウイルスマスクに関する。
本発明の第４は、抗菌機能および／またはエレクトレットフィルター（いいかえれば静電フィルター）機能をも有する請求項１〜３のいずれか記載の抗ウイルスマスクに関する。
【００１０】
本発明においては、アスコルビン酸誘導体が固着した繊維シートを用いることによって、空気中の飛沫ウイルス、及び呼吸によって排泄されるウイルスは、該抗ウイルス用繊維シートに接触することにより不活化される。
【００１１】
本発明におけるアスコルビン酸誘導体とは、安定型のアスコルビン酸類を意味する。すなわち、一般的に不安定とされているアスコルビン酸、及びアスコルビン酸塩以外の油溶性アスコルビン酸エステル類、すなわちアスコルビン酸モノエステル、アスコルビン酸ジエステル、アスコルビン酸トリエステル、アスコルビン酸テトラエステルを意味する。アスコルビン酸エステルのなかでもＬ−アスコルビン酸エステル、とくにＬ−アスコルビン酸アルキルエステル、とりわけＬ−アスコルビン酸ポリアルキルエステルが好ましい。具体的化合物としては、アスコルビン酸パルミテート（パルミチン酸アスコルビル）、アスコルビン酸ステアレート（ステアリン酸アスコルビル）、ジパルミチン酸アスコルビル、テトラヘキシルデカン酸アスコルビル、テトラ２−ヘキシルデカン酸アスコルビル、アスコルビン酸リン酸アミノプロピルなどを挙げることができる。
【００１２】
アスコルビン酸誘導体を繊維シートに固着させる方法としてはとくに制限はないが、たとえば繊維シートの表面層ないしは繊維間に固着させる方法、いわゆる後処理加工法やシートにする前の繊維に固着させる前処理方法などを採用することができる。一例としては、特開２００２−６１０７３号公報の記載による、アスコルビン酸誘導体と界面活性剤と水を混合した乳化液に繊維シートを浸漬し、乾燥処理する方法が挙げられる。それらの方法により、アスコルビン酸誘導体を繊維シート１ｇに対して０．１〜４５ｍｇ程度の範囲で固着させることができる。
【００１３】
前記界面活性剤としては、ポリオキシエチレンアルキルエーテル硫酸ナトリウムのようなポリオキシエチレン系のアニオン系界面活性剤や、ポリオキシエチレン誘導体、ソルビタンアルキレートなどの非イオン系界面活性剤が好ましい。
【００１４】
本発明における繊維シートは、いわゆる布帛状のものであればとくに制限はなく、織物、編物、不織布などを挙げることができる。使用される繊維素材としては綿、羊毛、絹等の天然繊維、ポリエステル、ポリオレフィン、ナイロン、アクリル等の合成繊維、レーヨン、ポリノジック、アセテート等の再生繊維が挙げられる。
【００１５】
繊維シートを複数枚用いたマスク本体は、古くから用いられているガーゼの積層体（通常ガーゼ２０枚程度積層）であってもよいし、最近よくみられる不織布の積層体（通常５枚程度を積層）であってもよく、マスク本体には全く制限はない。
【００１６】
なお、本発明の抗ウイルス用繊維シートには、あらかじめアスコルビン酸誘導体が固着された加工品を使用できる。このような加工品の一例としては、富士紡績株式会社製のＶ−ＵＰ（商品名）が挙げられる。これらの抗ウイルス用繊維シートは本発明ではマスク用に選択的に使用するものであるが、サポーター、バンソー膏のパッド、ガーゼ、包帯などに選択的に使用することもできる。
【００１７】
本発明の抗ウイルスマスクは、前述のアスコルビン酸誘導体を固着した抗ウイルス用繊維シートをマスク本体に積層し、その両端部に耳掛け部を設けることにより得ることができるが、必要に応じて耳掛け部も抗ウイルス用繊維を使用してもよく、抗ウイルス用繊維シートをマスク本体に積層したもので、耳掛け部を含め、マスク全体を構成してもよい。
【００１８】
本発明におけるマスク本体は、アスコルビン酸誘導体が固着された抗ウイルス用繊維シートの他に普通のマスク用の繊維シートを１層以上積層してもよい。積層の順序としては、アスコルビン酸誘導体が固着された抗ウイルス用繊維シートが皮膚に直接触れる側とすることが最も好ましい。
【００１９】
一般的に、アスコルビン酸誘導体は、アスコルビン酸の前駆体もしくはプロビタミン剤とも呼ばれており、化粧品等でよく使用されている。アスコルビン酸誘導体が生体内に吸収されると、生体内酵素によって、アスコルビン酸に分解するため、アスコルビン酸の本来持っているメラニン生成の抑制、美白作用、色素沈着抑制、抗酸化作用、コラーゲンの生成促進等の効果を発揮するとされている。したがって、アスコルビン酸誘導体が固着された抗ウイルス用繊維シートに皮膚が直接触れることで、ウイルス等が不活化されると共に、アスコルビン酸誘導体が、皮膚表面の皮脂成分を介して、体内に徐放出させることが可能になる。
【００２０】
また、本発明においては前記抗ウイルス機能に加えて、抗菌機能および／またはエレクトレットフィルター機能をさらに付与することもできる。このためには抗ウイルス用繊維シートにさらに抗菌機能やエレクトレットフィルター機能をもたせてもよいが、マスク本体に、抗菌シートやエレクトレットフィルターを単独あるいは併用し積層することもできる。勿論この場合もアスコルビン酸誘導体を固着した抗ウイルス用繊維シートが皮膚と直接接触するように積層することが好ましい。このような積層によって、空気中の各種有害成分が、呼吸を介して体内へ侵入するのを更に防ぐこと、及び体内から空気中に各種有害成分が排泄されるのを防ぐことが可能になる。
【００２１】
本発明に使用できる前記抗菌シートは、抗菌作用を有する成分が繊維シートに含まれているものである。このような抗菌作用を有する成分としては、キトサン、ヒノキチオール等の天然系抗菌剤、シリコン第四級アンモニウム塩、ビグアナイド系化合物、イミダゾール系化合物等の有機系抗菌剤、銀ゼオライト、銀シリカゲル、酸化チタン、活性炭等の無機系抗菌剤が挙げられる。該抗菌シートを加工する方法としては、公知の方法、例えば後処理加工法、あるいは原糸改良加工法のいずれかで行えばよい。また、あらかじめ抗菌剤が含まれた加工品を使用してもよい。該他の抗菌シートの選択によって、各種細菌類をも不活化することが可能になる。
【００２２】
本発明に使用できるエレクトレットフィルターは、誘電体である樹脂繊維などに静電気を帯電させたものである。繊維素材としては、静電気が帯電しやすいもの、例えば、ポリオレフィン、ポリエステル、又はそれらの共重合体が好ましく、繊維の形状としてはとくに不織布状のものが好ましい。エレクトレット化の方法としては、公知の方法、例えば、熱エレクトレット法、エレクトロエレクトレット法などいずれの方法で行ってもよい。また、あらかじめ帯電された加工品を使用してもよい。このような加工品の一例としては、東レ株式会社製のトレミクロン（商品名）、東洋紡績株式会社製のエリトロン（商品名）、日本バイリーン株式会社製のＶＥ−２Ｎ（商品名）などが挙げられる。該エレクトレットフィルターを用いることによって、粉塵、花粉、ウイルス、タバコの煙等の有害成分を電気的に吸着することが可能になる。
【００２３】
また、マスク本体への付加機能として、２段、または３段などのヒダ折り成形を施してもよい。それによって、鼻から顎まで広く覆うことや、口元周辺にフィットする等のことが可能になる。更に、ノーズワイヤーや口元ワイヤーを設けても良い。とくに口元ワイヤーは、それによって、口元周辺へのフィット性が更に向上するうえ、息苦しさが軽減し、口紅もつきにくいなどのメリットがある。またノーズワイヤーは鼻部分によくフィットし、空気もれが少なく、眼鏡着用者にとっては、眼鏡の曇りを防止することもできる。
【００２４】
【実施例】
以下、本発明を実験例および実施例により具体的に説明するが、これらにより本発明はなんら限定されるものではない。
【００２５】
（試験例）
アスコルビン酸誘導体が固着された抗ウイルス用繊維シートのウイルス不活化効果確認試験を行った。
（１）使用材料
・供試物質：下記式で示されるアスコルビン酸誘導体（アスコルビン酸テトラ−２−ヘキシルデシルエステル、別名テトラ２−ヘキシルデカン酸アスコルビル）固着ポリエステル不織布（Ｖ−ＵＰ加工品：富士紡績株式会社製）｛（Ａ）０．２２２ｍｇ／ｇ、（Ｂ）１．７１５ｍｇ／ｇ（Ｃ）５．１５１ｍｇ／ｇ｝よりなる抗ウイルス用繊維シート、及びブランクのポリエステル不織布｛（Ｄ）０ｍｇ／ｇ｝
【化１】

・ウイルス：Ｉｎｆｌｕｅｎｚａｖｉｒｕｓ（Ｈ１Ｎ１）
Ａ／ＰＲ８／３４（ＡＴＣＣＶＲ−９５）
・細胞：ＭＤＣＫ細胞（イヌ腎細胞）〔入手先：大日本製薬（株）〕
・細胞増殖培地：１０％牛胎児血清含有イーグルＭＥＮ培地（ＧＩＢＣＯ製）
・ウイルス維持培地：１％牛アルブミン含有イーグルＭＥＮ培地（ＧＩＢＣＯ製）
（２）試験方法
ａ）供試物質とウイルスの接触方法
供試物質は、２×２ｃｍ程度の大きさに細切りし、１２１℃２０分間高圧蒸気滅菌を行った。この供試物質をシャーレに４枚入れ、ウイルス液５００μｌを添加し、室温で３０分間作用させた。
ｂ）細胞への接種方法
予め、マイクロプレートにて培養した細胞増殖培地を除去し、ＰＢＳ（−）で細胞を洗浄した後、供試物質接触（作用）後のウイルス液（１０倍段階希釈）５０μｌを６０分間感染させた。感染後、ウイルス液を除去してウイルス維持培地を加え、３７℃、５（ｖ／ｖ）％ＣＯ_２条件下のふらん器内で培養を行った。
ｃ）判定方法
ＣＰＥ（細胞変性効果）出現の有無により、Ｒｅｅｄ−Ｍｕｅｎｃｈ法によって、５０％感染価（ＴＣＩＤ_５０）を求めた。
（３）試験結果
各供試物質のＴＣＩＤ_５０を表１に示した。以上のことから、アスコルビン酸誘導体固着抗ウイルス用繊維シートのウイルス不活化効果が確認された。
【００２６】
【表１】

【００２７】
実施例１
ポリエステル不織布３枚（マスク本体）、アスコルビン酸誘導体固着ポリエステル不織布〔Ｖ−ＵＰ加工品：テトラ−２−ヘキシルデカン酸アスコルビル（アスコルビルテトライソパルミテート）１．７１５ｍｇ／ｇ含有：富士紡績株式会社製よりなる抗ウイルス用繊維シート〕１枚の順に重ね、図１に示すようなヒダ折り成形を施した積層体を得た。ついでこの内部にノーズワイヤーを設け、該積層体の周縁部を縫製し、さらに耳掛けウーリーゴムを設けて図１に示すような抗ウイルスマスクを作成した。このマスクは図１にみられるように、口元周辺にもプラスチック等のバー（口元ワイヤー）２７を用いているが、これは必須ではない。口元ワイヤーを用いない場合であっても、該周辺にミシン目を設けることが好ましい。プラチック等のバー（口元ワイヤー）を用いる時とほぼ同様の効果が期待できるからである。なお、実施例１の変形として、マスク本体とアスコルビン酸誘導体固着ポリエステル不織布との間に静電フィルター、抗菌シートをそれぞれ挿入したもの、および両者を挿入したマスクも作成した。いずれも所期の効果をもつマスクであった。
【００２８】
実施例２
ポリエステル不織布３枚（マスク本体）、アスコルビン酸誘導体固着ポリエステル不織布（Ｖ−ＵＰ加工品：富士紡績株式会社製よりなる抗ウイルス用繊維シート）１枚の順に重ね、３段ヒダ折り成形を施した積層体を得た。次に、該積層体内部に、ノーズワイヤー（塩化ビニル被覆鉄芯）を設け、該積層体周縁部を縫製した。更に、耳掛けウーリーゴムを設け、図２に示すような抗ウイルスマスクを作成した。このマスクは期待どうりの効果を示した。
【００２９】
実施例３
ポリエステル不織布、エレクトレットフィルター〔帯電加工ポリオレフィン不織布：（ＶＥ−２Ｎ）日本バイリーン株式会社製〕、抗菌シート〔銀ゼオライト（商品名：ゼオミック：株式会社シナネンゼオミック製）固着ポリオレフィン不織布〕、アスコルビン酸誘導体固着ポリエステル不織布（Ｖ−ＵＰ加工品：富士紡績株式会社製）よりなる抗ウイルス用繊維シートをそれぞれ１枚ずつ記載の順に重ねた以外は、実施例２と同様にして、図３に示すような抗ウイルスマスクを作成した。このマスクも期待どうりの効果を示した。
【００３０】
実施例４
ガーゼ３枚（マスク本体）、実施例１で用いたと同じアスコルビン酸誘導体固着ポリエステル不織布１枚の順に重ねて積層体を得、この端部に耳掛けウーリーゴムを通して縫製し、抗ウイルスガーゼマスクを作成した。このマスクも期待どうりの効果を発揮した。
【００３１】
【発明の効果】
本発明の抗ウイルスマスクは、アスコルビン酸誘導体が固着した繊維シートが積層されているので、ウイルスを不活化させ、風邪、インフルエンザ等の各種感染予防に有効である。それと同時に、アスコルビン酸誘導体を皮膚より摂取することが可能になるため、スキンケア等にも有効である。更に、抗菌シートおよび／またはエレクトレットフィルターをさらに積層することで、ウイルス・細菌等が体内へ侵入することを更に防げると共に、空気中のその他あらゆる有害成分をも防ぐことが可能になる。
【図面の簡単な説明】
【図１】（ａ）は、本発明に係る実施例１の抗ウイルスマスクの口に接触する側の一部切欠斜視図である。
（ｂ）は、本発明に係る実施例１の抗ウイルスマスクの正面図〔（ａ）の裏側からみた正面図〕である。
【図２】本発明に係る実施例２の抗ウイルスマスクの一部切欠斜視図である。
【図３】本発明に係る実施例３の抗ウイルスマスクの一部切欠斜視図である。
【符号の説明】
２０マスク
２１マスク本体
２２アスコルビン酸誘導体が固着した繊維シート
２３繊維シート
２４ノーズワイヤー
２５耳掛け部
２６折り目部
２７プラスチック等のバー
２８ミシン目
２３１抗菌シート
２３２エレクトレットフィルター
２３３不織布[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to an antiviral mask capable of inactivating viruses and the like.
[0002]
[Prior art]
Masks for hygiene or medical use have been widely known for the purpose of preventing dust, pollen, bacteria, viruses and the like in the air from entering the body through respiration.
[0003]
Conventionally, as such a mask, there are Patent Documents 1 to 5, for example. Patent Document 1 discloses a mask for adsorbing and capturing harmful components such as viruses by bonding zeolite to fibers. Patent Document 2 discloses a method in which a calcium phosphate compound such as hydroxyapatite is supported on a sheet such as a nonwoven fabric. In addition, a mask that captures harmful components such as various bacteria and viruses by using a large number of minute air holes is disclosed. However, in these methods in which a virus or the like is physically adsorbed, an active virus may be present in the mask body. Further, when the adsorption capacity reaches the limit, the virus in an active state may enter the human body through the mask main body, which is not very effective.
[0004]
On the other hand, as masks for chemically inactivating viruses and the like using chemicals, for example, Patent Literatures 3 and 4 disclose an antiviral mask in which tea polyphenol, a tea extraction component, is attached to a nonwoven fabric. No. 5 discloses an antibacterial mask using silver-coated fibers. Although these drugs are usually said to be safe for the skin, they are not always safe at all because of problems such as causing allergy to some people.
[0005]
In addition, masks are generally worn around the mouth and directly or indirectly touch the skin, but these conventional masks have the sole function of preventing foreign substances such as dust, pollen, bacteria and viruses in some way. No consideration is given to skin care around the mouth.
[0006]
[Patent Document 1]
JP-A-53-56894 [Patent Document 2]
Japanese Patent Application Laid-Open No. 5-115572 [Patent Document 3]
JP-A-8-333271 [Patent Document 4]
JP 2002-136615 A [Patent Document 5]
JP-A-11-19238
[Problems to be solved by the invention]
SUMMARY OF THE INVENTION An object of the present invention is to provide an anti-virus mask capable of inactivating viruses and the like and having an additional function such as skin care at the same time in view of the above circumstances.
[0008]
[Means for Solving the Problems]
The present inventors have conducted intensive studies in order to solve the above problems, and as a result, as long as the fiber sheet has an ascorbic acid derivative fixed thereto, it can chemically inactivate viruses and the like, and can prevent various infections. The present inventors have found that an antiviral mask having an additional function such as skin care, which can gradually release an ascorbic acid derivative from the skin surface into the body, can be obtained, thereby completing the present invention.
[0009]
According to a first aspect of the present invention, in a mask including a mask body made of a fiber sheet and ear hooks provided at both ends of the mask body, an antiviral fiber sheet to which an ascorbic acid derivative is fixed is laminated on the mask body. The present invention relates to an antiviral mask characterized by comprising:
A second aspect of the present invention relates to the antiviral mask according to claim 1, wherein the ascorbic acid derivative is a stable oil-soluble ascorbic acid.
A third aspect of the present invention relates to the antiviral mask according to claim 1 or 2, wherein the antiviral fiber sheet to which the ascorbic acid derivative is fixed is laminated on a side of the mask body that directly contacts the skin.
A fourth aspect of the present invention relates to the antiviral mask according to any one of claims 1 to 3, which also has an antibacterial function and / or an electret filter (in other words, an electrostatic filter) function.
[0010]
In the present invention, by using the fiber sheet to which the ascorbic acid derivative is fixed, the droplet virus in the air and the virus excreted by respiration are inactivated by contact with the antiviral fiber sheet.
[0011]
The ascorbic acid derivative in the present invention means stable ascorbic acids. That is, it means oil-soluble ascorbic acid esters other than ascorbic acid and ascorbate, which are generally considered to be unstable, that is, ascorbic acid monoester, ascorbic acid diester, ascorbic acid triester, and ascorbic acid tetraester. Among the ascorbic acid esters, L-ascorbic acid esters, particularly alkyl L-ascorbic acid esters, particularly polyalkyl L-ascorbic acid esters are preferred. Specific compounds include ascorbic acid palmitate (ascorbyl palmitate), ascorbic acid stearate (ascorbyl stearate), ascorbyl dipalmitate, ascorbyl tetrahexyldecanoate, ascorbyl tetra-2-hexyldecanoate, aminopropyl ascorbate and the like. Can be mentioned.
[0012]
The method of fixing the ascorbic acid derivative to the fiber sheet is not particularly limited. For example, a method of fixing the surface layer of the fiber sheet or between the fibers, a so-called post-processing method, or a pre-treatment method of fixing the fiber to a sheet before forming the sheet. Etc. can be adopted. As an example, there is a method described in JP-A-2002-61073, in which a fiber sheet is immersed in an emulsion obtained by mixing an ascorbic acid derivative, a surfactant and water, and then dried. By these methods, the ascorbic acid derivative can be fixed in the range of about 0.1 to 45 mg per 1 g of the fiber sheet.
[0013]
The surfactant is preferably a polyoxyethylene-based anionic surfactant such as sodium polyoxyethylene alkyl ether sulfate, or a nonionic surfactant such as a polyoxyethylene derivative or sorbitan alkylate.
[0014]
The fiber sheet in the present invention is not particularly limited as long as it is a so-called fabric-like sheet, and examples thereof include a woven fabric, a knitted fabric, and a nonwoven fabric. Examples of the fiber material used include natural fibers such as cotton, wool, and silk; synthetic fibers such as polyester, polyolefin, nylon, and acrylic; and regenerated fibers such as rayon, polynosic, and acetate.
[0015]
The mask body using a plurality of fiber sheets may be a laminated body of gauze that has been used for a long time (usually about 20 laminated gauze layers) or a laminated body of a nonwoven fabric that is frequently seen recently (usually, about 5 laminated layers). And the mask body is not limited at all.
[0016]
In addition, as the antiviral fiber sheet of the present invention, a processed product to which an ascorbic acid derivative is fixed in advance can be used. An example of such a processed product is V-UP (trade name) manufactured by Fuji Boseki Co., Ltd. In the present invention, these antiviral fiber sheets are selectively used for a mask, but can also be selectively used for a supporter, a bansaw plaster pad, a gauze, a bandage, and the like.
[0017]
The antiviral mask of the present invention can be obtained by laminating an antiviral fiber sheet to which the above-described ascorbic acid derivative is fixed on the mask body and providing ear hooks at both ends thereof. The hanging portion may also use an anti-virus fiber, and the anti-virus fiber sheet may be laminated on the mask body to form the entire mask including the ear hanging portion.
[0018]
The mask body in the present invention may be formed by laminating one or more ordinary fiber sheets for masks in addition to the antiviral fiber sheets to which the ascorbic acid derivative is fixed. The order of lamination is most preferably on the side where the antiviral fiber sheet to which the ascorbic acid derivative is fixed is in direct contact with the skin.
[0019]
Generally, ascorbic acid derivatives are also called ascorbic acid precursors or provitamin agents and are often used in cosmetics and the like. When the ascorbic acid derivative is absorbed into the living body, it is decomposed into ascorbic acid by the in vivo enzyme, which suppresses the melanin production inherent in ascorbic acid, whitening action, pigmentation suppression, antioxidant action, collagen production. It is said to exhibit effects such as promotion. Therefore, when the skin directly touches the antiviral fiber sheet to which the ascorbic acid derivative is fixed, the virus and the like are inactivated, and the ascorbic acid derivative is gradually released into the body via the sebum component on the skin surface. It becomes possible.
[0020]
In the present invention, an antibacterial function and / or an electret filter function can be further provided in addition to the antiviral function. For this purpose, the antiviral fiber sheet may be further provided with an antibacterial function and an electret filter function. However, the antibacterial sheet and the electret filter may be laminated on the mask body alone or in combination. Of course, also in this case, it is preferable that the antiviral fiber sheet to which the ascorbic acid derivative is fixed is laminated so as to be in direct contact with the skin. Such lamination can further prevent various harmful components in the air from entering the body via respiration, and prevent excretion of various harmful components from the body into the air.
[0021]
The antibacterial sheet that can be used in the present invention is one in which a component having an antibacterial action is contained in a fiber sheet. Components having such an antibacterial action include natural antibacterial agents such as chitosan and hinokitiol, silicon quaternary ammonium salts, biguanide compounds, organic antibacterial agents such as imidazole compounds, silver zeolites, silver silica gel, and titanium oxide. And inorganic antibacterial agents such as activated carbon. The antibacterial sheet may be processed by a known method, for example, any one of a post-processing method and an original yarn improving processing method. Further, a processed product containing an antibacterial agent in advance may be used. By selecting the other antibacterial sheet, it becomes possible to inactivate various bacteria.
[0022]
The electret filter that can be used in the present invention is obtained by charging a resin fiber, which is a dielectric, with static electricity. The fiber material is preferably a material easily charged with static electricity, for example, a polyolefin, a polyester, or a copolymer thereof. The fiber shape is particularly preferably a nonwoven fabric. The electretization may be performed by any known method, for example, a thermal electret method, an electroelectret method, or the like. Alternatively, a pre-charged processed product may be used. Examples of such processed products include Tremicron (trade name) manufactured by Toray Industries, Inc., Eritron (trade name) manufactured by Toyobo Co., Ltd., and VE-2N (trade name) manufactured by Japan Vilene Co., Ltd. Can be By using the electret filter, harmful components such as dust, pollen, virus, and cigarette smoke can be electrically adsorbed.
[0023]
In addition, as an additional function to the mask body, folds may be formed in two or three steps. This makes it possible to cover the nose to the chin widely, to fit around the mouth, and the like. Further, a nose wire and a mouth wire may be provided. In particular, the lip wire has the advantages of further improving the fit around the lip, reducing breathlessness, and preventing lipstick from sticking. In addition, the nose wire fits well into the nose, has less air leakage, and can prevent the spectacle wearer from fogging the spectacles.
[0024]
【Example】
Hereinafter, the present invention will be described specifically with reference to Experimental Examples and Examples, but the present invention is not limited thereto.
[0025]
(Test example)
A virus inactivation effect confirmation test of the antiviral fiber sheet to which the ascorbic acid derivative was fixed was performed.
(1) Materials and test substances: Ascorbic acid derivative (tetra-2-hexyldecyl ascorbate, also known as ascorbyl tetra-2-hexyldecanoate) fixed polyester nonwoven fabric (V-UP processed product: Fuji Boseki Co., Ltd.) represented by the following formula (A company) {(A) 0.222 mg / g, (B) 1.715 mg / g (C) 5.151 mg / g}, anti-virus fiber sheet and blank polyester nonwoven fabric {(D) 0 mg / g ｝
Embedded image

・ Virus: Influenza virus (H1N1)
A / PR8 / 34 (ATCC VR-95)
-Cells: MDCK cells (canine kidney cells) [Obtained by Dainippon Pharmaceutical Co., Ltd.]
-Cell growth medium: Eagle MEN medium containing 10% fetal bovine serum (GIBCO)
-Virus maintenance medium: Eagle MEN medium containing 1% bovine albumin (GIBCO)
(2) Test method a) Contact method between test substance and virus The test substance was cut into small pieces of about 2 x 2 cm and subjected to high-pressure steam sterilization at 121 ° C for 20 minutes. Four test substances were placed in a petri dish, 500 μl of a virus solution was added, and the mixture was allowed to act at room temperature for 30 minutes.
b) Inoculation method to cells The cell growth medium previously cultured in a microplate was removed, the cells were washed with PBS (-), and the virus solution after contact with the test substance (action) (10-fold serial dilution) 50 μl were infected for 60 minutes. After the infection, the virus solution was removed, a virus maintenance medium was added, and the cells were cultured in a spatula under the conditions of 37 ° C. and 5 (v / v)% CO ₂ .
c) Determination method A 50% infectious titer (TCID ₅₀ ) was determined by the Reed-Muench method based on the presence or absence of CPE (cytopathic effect).
(3) Test Results Table 1 shows the TCID ₅₀ of each test substance. From the above, the virus inactivating effect of the ascorbic acid derivative-fixed antiviral fiber sheet was confirmed.
[0026]
[Table 1]

[0027]
Example 1
Three polyester non-woven fabrics (mask body), ascorbic acid derivative-fixed polyester non-woven fabric [V-UP processed product: ascorbyl tetra-2-hexyldecanoate (ascorbyl tetraisopalmitate) 1.715 mg / g content: made by Fuji Boseki Co., Ltd. Anti-Vibration Fiber Sheet] One sheet was stacked in this order to obtain a fold-folded laminate as shown in FIG. Next, a nose wire was provided therein, the periphery of the laminate was sewn, and an ear hanging woolly rubber was further provided to prepare an antiviral mask as shown in FIG. As shown in FIG. 1, this mask uses a bar (mouth wire) 27 made of plastic or the like also around the mouth, but this is not essential. Even when the mouth wire is not used, it is preferable to provide perforations around the periphery. This is because substantially the same effect as when a bar (mouth wire) such as plastic is used can be expected. In addition, as a modification of Example 1, one in which an electrostatic filter and an antibacterial sheet were inserted between the mask body and the ascorbic acid derivative-fixed polyester nonwoven fabric, and a mask in which both were inserted were also prepared. All were masks with the expected effect.
[0028]
Example 2
Three layers of polyester non-woven fabric (mask body) and one layer of ascorbic acid derivative-fixed polyester non-woven fabric (V-UP processed product: anti-virus fiber sheet made by Fuji Boseki Co., Ltd.) stacked in this order, and subjected to three-stage fold folding Got a body. Next, a nose wire (iron core coated with vinyl chloride) was provided inside the laminate, and the periphery of the laminate was sewn. Further, an ear hanging woolly rubber was provided, and an antiviral mask as shown in FIG. 2 was prepared. This mask showed the expected effect.
[0029]
Example 3
Polyester nonwoven fabric, electret filter [charge-treated polyolefin nonwoven fabric: (VE-2N) manufactured by Japan Vilene Co., Ltd.], antibacterial sheet [silver zeolite (trade name: Zeomic: manufactured by Sinanen Zeomic Co., Ltd.) fixed polyolefin nonwoven fabric], ascorbic acid derivative fixed polyester An antivirus as shown in FIG. 3 was prepared in the same manner as in Example 2 except that one antiviral fiber sheet made of a nonwoven fabric (V-UP processed product: manufactured by Fuji Boseki Co., Ltd.) was stacked one by one in the order described. Created a mask. This mask also showed the expected effect.
[0030]
Example 4
Three gauze (mask body) and one same ascorbic acid derivative-fixed polyester nonwoven fabric used in Example 1 were stacked in this order to obtain a laminate, and the end was sewn through woolly rubber to create an antiviral gauze mask. did. This mask also had the expected effect.
[0031]
【The invention's effect】
Since the antiviral mask of the present invention has a laminated fiber sheet to which an ascorbic acid derivative is fixed, it is effective for inactivating viruses and preventing various infections such as colds and influenza. At the same time, the ascorbic acid derivative can be taken from the skin, which is effective for skin care and the like. Further, by further laminating an antibacterial sheet and / or an electret filter, it is possible to further prevent viruses and bacteria from entering the body and also to prevent any other harmful components in the air.
[Brief description of the drawings]
FIG. 1 (a) is a partially cutaway perspective view of a side of an antiviral mask according to the first embodiment of the present invention, which is in contact with a mouth.
(B) is a front view of the anti-virus mask of Example 1 according to the present invention [front view as seen from the back side of (a)].
FIG. 2 is a partially cutaway perspective view of an antiviral mask according to a second embodiment of the present invention.
FIG. 3 is a partially cutaway perspective view of an antiviral mask according to a third embodiment of the present invention.
[Explanation of symbols]
Reference Signs List 20 mask 21 mask body 22 fiber sheet 23 to which ascorbic acid derivative is adhered fiber sheet 24 nose wire 25 ear hook part 26 fold part 27 bar of plastic 28 perforation 231 antibacterial sheet 232 electret filter 233 non-woven fabric

Claims

In a mask comprising a mask body made of a fiber sheet and ear hooks provided at both ends of the mask body, an antiviral fiber sheet to which an ascorbic acid derivative is fixed is laminated on the mask body. Anti-virus mask.

The antiviral mask according to claim 1, wherein the ascorbic acid derivative is a stable oil-soluble ascorbic acid.

The antiviral mask according to claim 1 or 2, wherein the antiviral fiber sheet to which the ascorbic acid derivative is adhered is laminated on a side of the mask body that directly contacts the skin.

The antiviral mask according to any one of claims 1 to 3, which also has an antibacterial function and / or an electret filter function.