Description

【請求項１】
サンケア用の化粧料であって、微粒子二酸化チタンと微粒子酸化亜鉛とポリエーテル変性メチルポリシロキサンとを含み、前記微粒子二酸化チタンの含有量が２０〜３０重量％であり、且つ、前記微粒子酸化亜鉛の含有量が５〜１５重量％であることを特徴とする、化粧料。
(1)
A cosmetic for sun care, and a particulate titanium dioxide and zinc oxide particles and a polyether-modified methyl polysiloxane, wherein a content of the fine particles of titanium dioxide 20 to 30 wt%, and, of the zinc oxide particles A cosmetic having a content of 5 to 15% by weight.

一方、サンケア用の化粧料であって、微粒子二酸化チタンと微粒子酸化亜鉛とポリエーテル変性メチルポリシロキサンとを含み、前記微粒子二酸化チタンの含有量が２０〜３０重量％であり、且つ、前記微粒子酸化亜鉛の含有量が５〜１５重量％であるものは知られていないし、この様な化粧料が、紫外線Ａ、Ｂに対して良好な防御効果を発揮することも知られていない。
On the other hand, a cosmetic for sun care, and a particulate titanium dioxide and zinc oxide particles and a polyether-modified methyl polysiloxane, the content of the fine particles of titanium dioxide is 20 to 30 wt%, and the particulate oxidation It is not known that the content of zinc is 5 to 15% by weight, and it is not known that such cosmetics exert a good protective effect against ultraviolet rays A and B.

【０００６】
【課題の解決手段】
この様な状況に鑑みて、本発明者らは、使用性に優れ、且つ、紫外線Ａ、Ｂに対して優れた防護作用を有する化粧料を求め、鋭意研究努力を重ねた結果、サンケア用の化粧料であって、微粒子二酸化チタンと微粒子酸化亜鉛とポリエーテル変性メチルポリシロキサンとを含み、前記微粒子二酸化チタンの含有量が２０〜３０重量％であり、且つ、前記微粒子酸化亜鉛の含有量が５〜１５重量％である化粧料がその様な特性を備えていることを見出し、発明を完成させるに至った。即ち、本発明は以下に示す技術に関するものである。
（１）サンケア用の化粧料であって、微粒子二酸化チタンと微粒子酸化亜鉛とポリエーテル変性メチルポリシロキサンとを含み、前記微粒子二酸化チタンの含有量が２０〜３０重
量％であり、且つ、前記微粒子酸化亜鉛の含有量が５〜１５重量％であることを特徴とする、化粧料。
（２）微粒子二酸化チタン及び微粒子酸化亜鉛が親油化表面処理されていることを特徴とする、（１）に記載の化粧料。
（３）前記微粒子二酸化チタンと微粒子酸化亜鉛の重量比が、３：１〜２：１であることを特徴とする、（１）又は（２）に記載の化粧料。
（４）更に、タルクを、微粒子二酸化チタンの重量と微粒子酸化亜鉛の重量の和に対して、５〜１５重量％含有することを特徴とする、（１）〜（３）何れか１項に記載の化粧料。
（５）非水液性製剤であることを特徴とする、（１）〜（４）何れか１項に記載の化粧料。
（６）多価アルコールを含有することを特徴とする、（１）〜（５）何れか１項に記載の化粧料。
（７）紫外線Ａ及びＢに対してサンケア作用を有するものであることを特徴とする、（１）〜（６）何れか１項に記載の化粧料。
（８）有機サンスクリーン剤を実質的に含有しないことを特徴とする、（１）〜（７）何れか１項に記載の化粧料。
[0006]
[Means for solving the problem]
In view of such a situation, the present inventors have sought a cosmetic that has excellent usability and has an excellent protective action against ultraviolet rays A and B. A cosmetic, comprising fine titanium dioxide, fine zinc oxide, and polyether-modified methylpolysiloxane , wherein the content of the fine titanium dioxide is 20 to 30% by weight, and the content of the fine zinc oxide is It has been found that the cosmetics having a content of 5 to 15% by weight have such properties, and the invention has been completed. That is, the present invention relates to the following technology.
(1) A cosmetic for sun care, comprising fine particle titanium dioxide, fine particle zinc oxide and polyether-modified methylpolysiloxane , wherein the content of the fine particle titanium dioxide is 20 to 30% by weight, and the fine particles A cosmetic, wherein the content of zinc oxide is 5 to 15% by weight.
(2) The cosmetic according to (1), wherein the fine particle titanium dioxide and the fine particle zinc oxide have been subjected to lipophilic surface treatment.
(3) The cosmetic according to (1) or (2), wherein the weight ratio between the fine particle titanium dioxide and the fine particle zinc oxide is 3: 1 to 2: 1.
(4) The method according to any one of (1) to (3), wherein talc is contained in an amount of 5 to 15% by weight based on the sum of the weight of the fine particle titanium dioxide and the weight of the fine particle zinc oxide. The cosmetics described.
(5) The cosmetic according to any one of (1) to (4), which is a non-aqueous liquid preparation.
(6) The cosmetic according to any one of (1) to (5), further comprising a polyhydric alcohol.
(7) The cosmetic according to any one of (1) to (6), which has a sun care effect on ultraviolet rays A and B.
(8) The cosmetic according to any one of (1) to (7), which does not substantially contain an organic sunscreen agent.

【０００７】
【発明の実施の形態】
（１）本発明の化粧料の必須成分である微粒子二酸化チタンと微粒子酸化亜鉛
本発明の化粧料は、サンケア用であって、微粒子二酸化チタンと微粒子酸化亜鉛を含有する。ここで微粒子とは平均粒径が０．１μｍ以下のものを意味し、かかる微粒子の二酸化チタン或いは酸化亜鉛は既に市販されているものが存在する。又、かかる微粒子二酸化チタン或いは微粒子酸化亜鉛は、その表面が処理されていても良いし、されていなくても良い。表面処理としては、通常化粧料原料に於いて知られているものであれば特段の限定を受けずに適用することが出来、例えば、ハイドロジェンメチルポリシロキサン焼き付け処理、ジメチルポリシロキサン焼き付け処理、アミノ変性シリコーン被覆処理、シランカップリング剤処理、脂肪酸金属石けん被覆処理、アシル化アミノ酸塩被覆処理、リン脂質被覆処理などが例示できる。処理は、処理剤を粉体に対して１〜１０重量％作用させることによって行われる。適宜、１００〜７００℃で１〜７２時間の加熱工程を経ても良い。特に好ましいものは、表面処理されたものであり、中でも特に好ましいものは、ハイドロジェンメチルポリシロキサン焼き付け処理をしたものであり、かかる処理粉体は既に市販されているものを利用できる。市販品としては、親油化表面処理（ハイドロジェンメチルシロキサン焼き付け処理）微粒子二酸化チタンとしては、Ｅ０９７−２（テイカ株式会社製）が、親油化表面処理（ハイドロジェンメチルシロキサン焼き付け処理）微粒子酸化亜鉛としては、Ｅ０９６−２（テイカ株式会社製）が好ましく例示できる。本発明の化粧料に於ける、かかる微粒子二酸化チタン及び微粒子酸化亜鉛の好ましい含有量は、微粒子二酸化チタンが２０〜３０重量％であり、更に好ましくは、２３〜２８重量％が好ましく、且つ、微粒子酸化亜鉛が５〜１５重量％であり、更に好ましくは７〜１３重量％である。前記微粒子二酸化チタンと微粒子酸化亜鉛の重量比が、３：１〜２：１であることが好ましい。これは、この割合に於いて、紫外線Ａ、Ｂに対してともに有効な防護作用を発揮するからである。
[0007]
BEST MODE FOR CARRYING OUT THE INVENTION
(1) Fine titanium dioxide and fine zinc oxide which are essential components of the cosmetic of the present invention The cosmetic of the present invention is for sun care and contains fine titanium dioxide and fine zinc oxide. Here, the fine particles mean those having an average particle diameter of 0.1 μm or less, and titanium dioxide or zinc oxide of such fine particles are already commercially available. The surface of the fine particle titanium dioxide or the fine particle zinc oxide may or may not be treated. The surface treatment can be applied without any particular limitation as long as it is generally known in cosmetic raw materials, for example, hydrogen methyl polysiloxane baking treatment, dimethyl polysiloxane baking treatment, amino acid Examples thereof include a modified silicone coating treatment, a silane coupling agent treatment, a fatty acid metal soap coating treatment, an acylated amino acid salt coating treatment, and a phospholipid coating treatment. The treatment is performed by causing the treating agent to act on the powder at 1 to 10% by weight. Optionally, a heating step at 100 to 700 ° C. for 1 to 72 hours may be performed. Particularly preferred are those subjected to surface treatment, and particularly preferred are those subjected to hydrogen methylpolysiloxane baking treatment, and as such treated powder, commercially available powders can be used. As a commercially available product, E097-2 (manufactured by Teica Co., Ltd.) is used as a lipophilic surface treatment (hydrogen methyl siloxane baking treatment) and fine particle oxidation is used as titanium dioxide. Preferred examples of zinc include E096-2 (manufactured by Teica Corporation). The preferred content of the cosmetic in the fee, such particulate titanium dioxide and zinc oxide particles of the present invention is a fine particulate titanium dioxide 20 to 30 wt%, more preferably, is preferably 23 to 28 wt%, and particulate The content of zinc oxide is 5 to 15% by weight, and more preferably 7 to 13% by weight. It is preferable that the weight ratio between the fine particle titanium dioxide and the fine particle zinc oxide is 3: 1 to 2: 1. This is because, at this ratio, both of the ultraviolet rays A and B exert an effective protective action.

（３）本発明の化粧料
本発明の化粧料は、サンケア用の化粧料であって、前記必須成分を含有し、好ましい形態に於いて、好ましい成分を含有することを特徴とする。本発明の化粧料に於いて特徴的な性質は、紫外線Ａ、Ｂの両方に対して優れた防護作用を発揮することである。かかる作用を更に高めるためには、本発明の化粧料は非水性の製剤であることが好ましい。この様な形態を取ることにより、被膜の厚さを適度なものに調整し、紫外線防護作用を損なわずに自然な仕上がりを具現化できるためである。又、好ましい形態に於いては、表面処理をされていない板状粉体を含むため、液層との親和性の維持の観点から、液層になじみ、且つ、非表面処理粉体にもなじむ、１，３−ブタンジオールなどの多価アルコールを０．５〜３重量％程度含有することが好ましい。本発明の化粧料に於いては、かかる構成によって紫外線Ａ及びＢに対して防護作用を発揮するため、従来のように有機の紫外線吸収剤を含有させる必要が無く、かかる成分は含有させないことが出来る。この様な形態は、安全性の面からも好ましい。本発明の化粧料に於いては、本発明の効果を損なわない範囲に於いて、通常化粧料で使用されている任意成分を含有することが出来る。かかる任意成分としては、例えば、スクワラン、流動パラフィン、軽質流動イソパラフィン、重質流動イソパラフィン、マイクロクリスタリンワックス、固形パラフィンなどの炭化水素類、ジメチコン、フェメチコン、シクロメチコン、アモジメチコン、ポリエーテル変性シリコーンなどのシリコーン類、ホホバ油、カルナウバワックス、モクロウ、ミツロウ、ゲイロウ、オレイン酸オクチルドデシル、イソプロピルミリステート、ネオペンチルグリコールジイソステアレート、リンゴ酸ジイソステアレートなどのエステル類、ステアリン酸、ラウリン酸、ミリスチン酸、パルミチン酸、イソステアリン酸、イソパルミチン酸、ベヘン酸、オレイン酸などの脂肪酸類、ベヘニルアルコール、セタノール、オレイルアルコール、オクタデシルアルコールなどの高級アルコール類、ヒマシ油、椰子油、水添椰子油、椿油、小麦胚芽油、イソステアリン酸トリグリセライド、イソオクタン酸トリグリセライド、オリーブオイル等のトリグリセライド類、ソルビタンセスキオレート、ソルビタンモノオレート、ソルビタントリオレート、ソルビタンセスキステアレート、ソルビタンモノステアレート、ポリオキシエチレンソルビタンモノオレート、ポリオキシエチレンソルビタンモノステアレート、ポリオキシエチレンステアレート、ポリオキシエチレンオレート、ポリオキシエチレングリセリル脂肪酸エステル、ポリオキシエチレンアルキルエーテル、ポリオキシエチレン硬化ヒマシ油等の非イオン界面活性剤、ソジウムラウリルステアレート、ポリオキシエチレンアルキル硫酸塩、スルホコハク酸エステル塩などのアニオン界面活性剤、４級アルキルアンモニウム塩等のカチオン界面活性剤類、アルキルベタイン等の両性界面活性剤類、結晶セルロースや架橋型メチルポリシロキサン、ポリエチレン粉末、アクリル樹脂粉体等の有機粉体類、炭酸マグネシウム、炭酸カルシウム、酸化鉄、紺青、群青、チタンマイカ、チタンセリサイト、シリカ等の表面処理されていても良い粉体類、アクリル酸・メタクリル酸アルキルコポリマー及び／又はその塩、カルボキシビニルポリマー及び／又はその塩、キサンタンガムやヒドロキシプロピルセルロースなどの増粘剤、レチノール、レチノイン酸、トコフェロール、リボフラビン、ピリドキシン、アスコルビン酸、アスコルビン酸リン酸エステル塩などのビタミンやグリチルリチン酸塩、グリチルレチン、ウルソール酸、オレアノール酸などのテルペン類、エストラジオール、エチニルエストラジオール、エストリオールなどのステロイド類などの有効成分、フェノキシエタノール、パラベン類、ヒビテングルコネート、塩化ベンザルコニウム等の防腐剤、ジメチルアミノ安息香酸エステル類、桂皮酸エステル類、ベンゾフェノン類などの紫外線吸収剤などが好ましく例示できる。かかる必須成分、好ましい成分及び任意成分を常法に従って処理することにより、本発明の化粧料は製造することが出来る。
(3) Cosmetic of the Present Invention The cosmetic of the present invention is a cosmetic for sun care, which contains the essential components described above, and in a preferable embodiment, contains a preferable component. A characteristic feature of the cosmetic of the present invention is that it exhibits an excellent protective action against both ultraviolet rays A and B. In order to further enhance such action, the cosmetic of the present invention is preferably a non-aqueous preparation. By adopting such a form, the thickness of the coating can be adjusted to an appropriate thickness, and a natural finish can be realized without impairing the ultraviolet protection effect. Further, in a preferred embodiment, since it contains a plate-like powder that has not been subjected to a surface treatment, it is compatible with the liquid layer and also with non-surface-treated powder from the viewpoint of maintaining affinity with the liquid layer. It is preferable to contain about 0.5 to 3% by weight of a polyhydric alcohol such as 1,3-butanediol. In the cosmetic of the present invention, the protective action against the ultraviolet rays A and B is exerted by such a configuration, so that it is not necessary to include an organic ultraviolet absorber as in the related art, and such a component may not be contained. I can do it. Such a form is preferable also from the viewpoint of safety. The cosmetic of the present invention may contain optional components commonly used in cosmetics as long as the effects of the present invention are not impaired. Such optional components include, for example, squalane, liquid paraffin, light liquid isoparaffin, heavy liquid isoparaffin, microcrystalline wax, hydrocarbons such as solid paraffin, dimethicone, femethicone, cyclomethicone, amodimethicone, and polyether-modified silicone. Silicones, jojoba oil, carnauba wax, mokuro, beeswax, gay wax, octyldodecyl oleate, isopropyl myristate, neopentyl glycol diisostearate, esters such as malic acid diisostearate, stearic acid, lauric acid, Fatty acids such as myristic acid, palmitic acid, isostearic acid, isopalmitic acid, behenic acid, oleic acid, behenyl alcohol, cetanol, oleyl alcohol, octadecyl alcohol Higher alcohols such as coal, castor oil, coconut oil, hydrogenated coconut oil, camellia oil, wheat germ oil, triglycerides such as isostearic acid triglyceride, isooctanoic acid triglyceride, olive oil, sorbitan sesquiolate, sorbitan monooleate, and sorbitan triolate , sorbitan sesquistearate, sorbitan monostearate, polyoxyethylene sorbitan monooleate, polyoxyethylene sorbitan monostearate, polyoxyethylene stearate, polyoxyethylene oleate, polyoxyethylene glyceryl fatty acid esters, polio alkoxy polyoxyethylene alkyl ether , Nonionic surfactants such as polyoxyethylene hydrogenated castor oil, sodium lauryl stearate, polyoxyethylene alkyl sulfate, sulfonate Anionic surfactants such as succinic acid ester salts, cationic surfactants such as quaternary alkylammonium salts, amphoteric surfactants such as alkyl betaine, crystalline cellulose, cross-linked methylpolysiloxane, polyethylene powder, acrylic resin powder Powders which may be surface-treated such as organic powders such as magnesium carbonate, calcium carbonate, iron oxide, navy blue, ultramarine blue, titanium mica, titanium sericite, silica, etc., acrylic acid / alkyl methacrylate copolymer and / or Or a salt thereof, a carboxyvinyl polymer and / or a salt thereof, a thickener such as xanthan gum or hydroxypropylcellulose, vitamins such as retinol, retinoic acid, tocopherol, riboflavin, pyridoxine, ascorbic acid, and ascorbic acid phosphate, and glycyrrhizic acid. salt Active ingredients such as terpenes such as glycyrrhetin, ursolic acid and oleanolic acid; steroids such as estradiol, ethinyl estradiol and estriol; preservatives such as phenoxyethanol, parabens, hibitene gluconate and benzalkonium chloride; dimethylaminobenzoate Preferred examples include ultraviolet absorbers such as acid esters, cinnamic esters and benzophenones. The cosmetic of the present invention can be produced by treating such essential components, preferred components and optional components according to a conventional method.

＜実施例１＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ５０、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア４、被膜閉塞感の無さがスコア４であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。同時に、親油化微粒子二酸化チタンを親油化した通常の二酸化チタン（平均粒径１．２μｍ）に置換した比較例１、親油化微粒子酸化亜鉛を親油化した通常の酸化亜鉛（平均粒径１．５μｍ）に置換した比較例２、親油化微粒子二酸化チタンを親油化した通常の二酸化チタン（平均粒径１．２μｍ）に、且つ、親油化微粒子酸化亜鉛を親油化した通常の酸化亜鉛（平均粒径１．５μｍ）に置換した比較例３を作成したところ、比較例１は、ＳＰＦ４０、ＰＡ＋＋＋、白さの目だたなさスコア３、被膜閉塞感の無さスコア３であり、比較例２は、ＳＰＦ４４、ＰＡ＋＋、白さの目だたなさスコア３、被膜閉塞感の無さスコア３であり、比較例３は、ＳＰＦ４０、ＰＡ＋＋、白さの目だたなさスコア３、被膜閉塞感の無さスコア３であった。これより、本発明の化粧料が優れた紫外線防護効果と脂溶性を備えていることがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１３重量部
１，３−ブタンジオール１重量部
<Example 1>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was an SPF50 and PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, according to the evaluation of the usability by a specialized panelist, the score was 4 for the lack of whiteness and the score 4 for the absence of a feeling of film occlusion. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. At the same time, Comparative Example 1 in which lipophilic fine particle titanium dioxide was replaced by lipophilic normal titanium dioxide (average particle diameter 1.2 μm), normal lipophilic fine particle zinc oxide lipophilic normal zinc oxide (average particle Comparative Example 2, in which lipophilic fine particle titanium dioxide was replaced by lipophilic fine particle titanium dioxide (average particle diameter: 1.2 μm), and lipophilic fine particle zinc oxide was replaced by lipophilic fine particles. Comparative Example 3 in which ordinary zinc oxide (average particle size: 1.5 μm) was substituted was prepared. In Comparative Example 1, SPF40, PA ++, inconspicuousness score of whiteness 3, score of non-occlusive feeling of film 3 Comparative Example 2 had an SPF of 44, PA ++, whiteness inconsistency score of 3, and no film obstruction sensation score of 3. Comparative Example 3 had an SPF of 40, PA ++, and whiteness inconspicuous score. 3. The score of the absence of a feeling of film occlusion was 3. This indicates that the cosmetic of the present invention has an excellent ultraviolet protection effect and fat solubility.
Lipophilic fine particle titanium dioxide (E097-2) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 13 parts by weight 1 , 3-butanediol 1 part by weight

＜実施例２＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ４２、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア４、被膜閉塞感の無さがスコア４であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、微粒子二酸化チタンの量は少なくとも２０重量％必要であることがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２０重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１７重量部
１，３−ブタンジオール１重量部
<Example 2>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was SPF42, PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, according to the evaluation of the usability by a specialized panelist, the score was 4 for the lack of whiteness and the score 4 for the absence of a feeling of film occlusion. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it is understood that the amount of the fine particle titanium dioxide needs to be at least 20% by weight.
Lipophilic fine particle titanium dioxide (E097-1) 20 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 17 parts by weight 1 , 3-butanediol 1 part by weight

＜実施例３＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ５０、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア３、被膜閉塞感の無さがスコア３であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、微粒子二酸化チタンの量は多くとも３０重量％であることがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）３０重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン７重量部
１，３−ブタンジオール１重量部
<Example 3>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was an SPF50 and PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, in the evaluation of the usability by a specialized panelist, a score of 3 was given for the inconspicuousness of the whiteness, and a score of 3 was given for the absence of the sense of blocking the coat. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it is understood that the amount of the fine particle titanium dioxide is at most 30% by weight.
Lipophilic fine particle titanium dioxide (E097-1) 30 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 7 parts by weight 1 , 3-butanediol 1 part by weight

＜実施例４＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ４７、ＰＡ＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア４、被膜閉塞感の無さがスコア４であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、微粒子酸化亜鉛の量は少なくとも５重量％必要であることがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）５重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１７重量部
１，３−ブタンジオール１重量部
<Example 4>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was SPF47, PA ++ in an ultraviolet ray protection test using volunteers, and showed excellent protection against ultraviolet rays A and B. In addition, according to the evaluation of the usability by a specialized panelist, the score was 4 for the lack of whiteness and the score 4 for the absence of a feeling of film occlusion. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it can be seen that the amount of the particulate zinc oxide needs to be at least 5% by weight.
Lipophilic fine particle titanium dioxide (E097-2) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 5 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 17 parts by weight 1 , 3-butanediol 1 part by weight

＜実施例５＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ５０、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア３、被膜閉塞感の無さがスコア３であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、微粒子酸化亜鉛の量は多くとも１５重量％であることがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）１５重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン７重量部
１，３−ブタンジオール１重量部
<Example 5>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was an SPF50 and PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, in the evaluation of the usability by a specialized panelist, a score of 3 was given for the inconspicuousness of the whiteness, and a score of 3 was given for the absence of the sense of blocking the coat. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it can be seen that the amount of the particulate zinc oxide is at most 15% by weight.
Lipophilic fine particle titanium dioxide (E097-1) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 15 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 7 parts by weight 1 , 3-butanediol 1 part by weight

＜実施例６＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ５０、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア５、被膜閉塞感の無さがスコア５であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、本発明の化粧料に於いてはタルクの様な板状粉体を含有することが好ましいことがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１０重量部
タルク３重量部
１，３−ブタンジオール１重量部
<Example 6>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was an SPF50 and PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, according to the evaluation of usability by a specialized panelist, a score of 5 was given for the inconspicuousness of whiteness, and a score of 5 was given for the absence of a feeling of film occlusion. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it is understood that the cosmetic of the present invention preferably contains a plate-like powder such as talc.
Lipophilic fine particle titanium dioxide (E097-1) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 10 parts by weight talc 3 parts by weight 1,3-butanediol 1 part by weight

＜実施例７＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良
く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ５０、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア５、被膜閉塞感の無さがスコア４であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、本発明の化粧料に於いては、板状粉体としてセリサイトを含有しても効果があり、好ましいことがわかる。親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１０重量部
セリサイト３重量部
１，３−ブタンジオール１重量部
<Example 7>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. This was an SPF50 and PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, according to the evaluation of usability by a specialized panelist, a score of 5 for unremarkable whiteness and a score of 4 for no sensation of film occlusion. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it can be seen that the cosmetic of the present invention is effective even if it contains sericite as a plate-like powder, and is preferable. Lipophilic fine particle titanium dioxide (E097-2) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 10 parts by weight Site 3 parts by weight 1,3-butanediol 1 part by weight

＜実施例８＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ４８、ＰＡ＋＋＋であり、優れた紫外線Ａ、Ｂに対する防護効果を示した。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア４、被膜閉塞感の無さがスコア５であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、本発明の化粧料に於いてはタルクとしては、表面処理しないものの方が好ましいことがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１０重量部
親油化タルク３重量部
１，３−ブタンジオール１重量部
Example 8
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. These were SPF48 and PA ++ in a UV protection test using volunteers, and showed excellent protection against UVA and UVB. In addition, according to the evaluation of the usability by a specialized panelist, the whiteness was unsatisfactory, and the score was 4; The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these results, it can be seen that in the cosmetics of the present invention, talc preferably has no surface treatment.
Lipophilic fine particle titanium dioxide (E097-2) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 10 parts by weight Oiled talc 3 parts by weight 1,3-butanediol 1 part by weight

＜実施例９＞
以下に示す処方に従って、本発明のサンケア用の化粧料を作成した。即ち、処方成分を良く混合し、しかる後、３本ロールにかけ、本発明のサンケア用の化粧料（非水分散タイプ）を得た。このものはボランティアを用いた紫外線保護試験に於いて、ＳＰＦ４５、ＰＡ＋＋であり、紫外線Ａ、Ｂに対する防護効果を示したものの実施例１程ではないことがわかる。又、専門パネラーによる使用性の評価では、白さの目だたなさがスコア５、被膜閉
塞感の無さがスコア５であった。尚、これらのスコアの基準は、スコア５：非常によい、スコア４：良い、スコア３：やや良い、スコア２：やや悪い、スコア１：悪いを用いた。これらより、本発明の化粧料に於いてはナイロンパウダーのような球状粉体は好ましくないことがわかる。
親油化微粒子二酸化チタン（Ｅ０９７−２）２４重量部
親油化微粒子酸化亜鉛（Ｅ０９６−２）９重量部
ポリエーテル変性メチルポリシロキサン８重量部
デカメチルシクロペンタシロキサン４５重量部
ジメチコン１０重量部
ナイロンパウダー３重量部
１，３−ブタンジオール１重量部 <Example 9>
According to the following formulation, a cosmetic for sun care of the present invention was prepared. That is, the prescription components were mixed well and then rolled on three rolls to obtain the sun care cosmetic (non-aqueous dispersion type) of the present invention. These were SPF45 and PA ++ in the ultraviolet ray protection test using volunteers, and showed a protective effect against ultraviolet rays A and B, but not as much as in Example 1. In addition, according to the evaluation of usability by a specialized panelist, a score of 5 was given for the inconspicuousness of whiteness, and a score of 5 was given for the absence of a feeling of film occlusion. The criteria for these scores were score 5: very good, score 4: good, score 3: somewhat good, score 2: slightly bad, and score 1: bad. From these, it is understood that spherical powders such as nylon powder are not preferable in the cosmetics of the present invention.
Lipophilic fine particle titanium dioxide (E097-2) 24 parts by weight Lipophilic fine particle zinc oxide (E096-2) 9 parts by weight Polyether-modified methylpolysiloxane 8 parts by weight Decamethylcyclopentasiloxane 45 parts by weight Dimethicone 10 parts by weight Nylon Powder 3 parts by weight 1,3-butanediol 1 part by weight