JP2003336179A - Printed natural leather product and method for producing the same - Google Patents
Printed natural leather product and method for producing the sameInfo
- Publication number
- JP2003336179A JP2003336179A JP2002144798A JP2002144798A JP2003336179A JP 2003336179 A JP2003336179 A JP 2003336179A JP 2002144798 A JP2002144798 A JP 2002144798A JP 2002144798 A JP2002144798 A JP 2002144798A JP 2003336179 A JP2003336179 A JP 2003336179A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- natural leather
- coat layer
- printed
- producing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、印刷された天然皮
革製品および印刷された天然皮革製品の製造方法に関す
る。詳細には、印刷層の密着性の良好な天然皮革製品お
よびその製造方法に関する。FIELD OF THE INVENTION The present invention relates to a printed natural leather product and a method for producing a printed natural leather product. More specifically, the present invention relates to a natural leather product having good adhesion of a printed layer and a method for producing the same.
【０００２】[0002]
【従来の技術】従来、天然皮革に様々な色調をもたせる
ために転写法によるプリントが行われている。しかしな
がら、一般に、天然皮革の表面には微小な孔が存在して
おり、そのために従来の転写方法では天然皮革表面に形
成される転写層の接着強度を大きくすることができず、
良好な転写面を得ることができなかった。2. Description of the Related Art Conventionally, printing by a transfer method has been carried out in order to give natural leather various color tones. However, in general, the surface of the natural leather has fine pores, and therefore the conventional transfer method cannot increase the adhesive strength of the transfer layer formed on the surface of the natural leather,
It was not possible to obtain a good transfer surface.
【０００３】そこで、特開平５−２２１１１０号公報に
は、天然皮革の表面に熱可塑性樹脂層を形成し、次い
で、基体シート上に剥離層と絵柄インキ層と熱接着剤層
とが順次積層されてなる熱転写シートにより前記熱可塑
性樹脂層上に転写を行い、さらに転写部分に圧着部材を
重ねて加熱圧着する方法が、開示されている。Therefore, in JP-A-5-221110, a thermoplastic resin layer is formed on the surface of natural leather, and then a release layer, a pattern ink layer and a thermal adhesive layer are sequentially laminated on a base sheet. There is disclosed a method of transferring onto the thermoplastic resin layer by using the thermal transfer sheet formed as described above, and further superimposing a pressure bonding member on the transfer portion and performing thermocompression bonding.
【０００４】しかしながら、転写法を用いているため、
やはり皮革と転写層との接着性が充分ではない。さら
に、転写シートを製造する工程、加熱圧着する工程が必
要であるため、製造工程が煩雑となるという問題もあ
る。However, since the transfer method is used,
After all, the adhesiveness between the leather and the transfer layer is not sufficient. Further, there is also a problem in that the manufacturing process becomes complicated because a process for manufacturing the transfer sheet and a process for thermocompression bonding are required.
【０００５】また、特開２０００−６３９００には、な
めし加工された皮革の表面に水性アクリルペイントの吹
き付けによって所望の図柄をカラー印刷し、さらにその
上にクリア液を吹き付けてオーバーコートする方法が開
示されている。Further, Japanese Unexamined Patent Publication No. 2000-63900 discloses a method in which a desired pattern is color-printed by spraying an aqueous acrylic paint on the surface of tanned leather, and a clear solution is sprayed on the pattern for overcoating. Has been done.
【０００６】しかしながら、皮革の表面に直接水性イン
クを吹き付けているので、インクの滲みや染み込みが生
じてしまい、所望の図柄を得ることが困難であるという
問題がある。However, since the water-based ink is sprayed directly on the surface of the leather, there is a problem that ink bleeding or soaking occurs and it is difficult to obtain a desired pattern.
【０００７】[0007]
【発明が解決しようとする課題】本発明は、前記課題を
解決するものであり、皮革と印刷層との密着性の良好な
印刷された天然皮革製品およびその製造方法を提供する
ものである。SUMMARY OF THE INVENTION The present invention is to solve the above problems and provides a printed natural leather product having good adhesion between the leather and the printing layer and a method for producing the same.
【０００８】[0008]
【課題を解決するための手段】すなわち本発明は、天然
皮革の表面にアンカーコート層を付与する工程と、印刷
層を付与する工程と、バインダー層を付与する工程と、
トップコート層を付与する工程とからなる印刷された天
然皮革製品の製造方法に関する。Means for Solving the Problems That is, the present invention comprises a step of applying an anchor coat layer to the surface of natural leather, a step of applying a printing layer, and a step of applying a binder layer,
And a step of applying a top coat layer, to a method for producing a printed natural leather product.
【０００９】前記アンカーコート層が、酢酸ビニルおよ
びアクリル酸エステルからなることが好ましい。It is preferable that the anchor coat layer is made of vinyl acetate and acrylic ester.
【００１０】前記アンカーコート層、バインダー層およ
びトップコート層がスプレーコート法により付与されて
なることが好ましい。It is preferable that the anchor coat layer, the binder layer and the top coat layer are applied by a spray coating method.
【００１１】前記印刷層が、インクジェット法により付
与されてなることが好ましい。The printing layer is preferably applied by an ink jet method.
【００１２】また、天然皮革の表面にアンカーコート
層、印刷層、バインダー層およびトップコート層が順次
積層されてなる印刷された天然皮革製品に関する。Further, the present invention relates to a printed natural leather product in which an anchor coat layer, a printing layer, a binder layer and a top coat layer are sequentially laminated on the surface of natural leather.
【００１３】前記アンカーコート層が、酢酸ビニルおよ
びアクリル酸エステルからなることが好ましい。It is preferable that the anchor coat layer is composed of vinyl acetate and acrylic ester.
【００１４】[0014]
【発明の実施の形態】本発明で使用される天然皮革は、
牛皮、馬皮、羊皮、やぎ皮、豚皮などのほかに、へび、
トカゲ、ワニなどのは虫類や両生類の皮革などがあげら
れ、とくに限定されない。なかでも、成牛、中牛、子牛
などの牛皮が好ましい。また、本発明には、牛皮を２枚
に分割して生じる吟付皮（銀面）だけでなく、凹凸の多
い床皮、編皮および毛皮などの多種の皮革を用いること
ができる。BEST MODE FOR CARRYING OUT THE INVENTION The natural leather used in the present invention is
In addition to cow skin, horse skin, sheep skin, goat skin, pig skin, snake,
Examples include reptile and amphibian leathers such as lizards and crocodiles, and are not particularly limited. Of these, cowhides such as adult cows, middle cows and calves are preferable. Further, in the present invention, various kinds of leather such as floor leather, knitted leather, and fur, which have many irregularities, can be used, in addition to the grated leather (silver surface) produced by dividing cowhide into two pieces.
【００１５】前記天然皮革の表面に、アンカーコート
層、印刷層、バインダー層、およびトップコート層が付
与される。前記アンカーコート層、バインダー層、およ
びトップコート層の付与方法としては、とくに限定され
ないが、リバースロールコーティング法、スプレーコー
ト法、ロールコーティング法、グラビアコーティング
法、キスロールコーティング法、ナイフコート法などが
あげられる。なかでも、使用されるアンカーコート剤、
バインダーおよびトップコート剤の浸透性の点で、スプ
レーコート法が好ましい。また、印刷層の付与方法もと
くに限定されないが、スクリーン法、グラビア法、イン
クジェット法などがあげられる。なかでも、浸透性、選
定模様の多彩性、復元性および少量多品種が可能である
点で、インクジェット法が好ましい。An anchor coat layer, a printing layer, a binder layer, and a top coat layer are provided on the surface of the natural leather. The method for applying the anchor coat layer, the binder layer, and the top coat layer is not particularly limited, but includes reverse roll coating method, spray coating method, roll coating method, gravure coating method, kiss roll coating method, knife coating method, and the like. can give. Among them, the anchor coating agent used,
The spray coating method is preferable in terms of the permeability of the binder and the top coating agent. The method of applying the printing layer is not particularly limited, and examples thereof include a screen method, a gravure method, and an inkjet method. Among them, the inkjet method is preferable in terms of penetrability, versatility of selected patterns, restoration property, and small quantity and large variety.
【００１６】また、前記アンカーコート層は、天然皮革
の表面を滑らかにし、インクの染み込み、滲み、はがれ
などを防止するために付与される。前記層を形成するア
ンカーコート剤は、とくに限定されないが、アクリル酸
エステル系樹脂、ポリ塩化ビニル系樹脂、ポリエステル
系樹脂、ポリアミド系樹脂、ウレタン系樹脂などがあげ
られる。なかでも、印刷層に使用されるインクの染み込
みを防止する効果の点で、アクリル酸エステルと酢酸ビ
ニルとの混合物からなるエマルジョンが好ましい。アク
リル酸エステルが少ないと、鮮明な画像が得られない傾
向にあり、アクリル酸エステルが多いと、剥離が生じる
傾向にある。また、アンカーコート層の厚みは、１０〜
１２μｍであることが好ましい。１０μｍより少ない
と、印刷層に使用されるインクの染み込みの原因となる
傾向にあり、１２μｍをこえると、印刷層に使用される
インクが滲む原因となる傾向にある。The anchor coat layer is provided in order to smooth the surface of the natural leather and prevent ink penetration, bleeding, peeling and the like. The anchor coating agent forming the layer is not particularly limited, and examples thereof include acrylic acid ester-based resin, polyvinyl chloride-based resin, polyester-based resin, polyamide-based resin, urethane-based resin and the like. Among them, an emulsion composed of a mixture of an acrylic ester and vinyl acetate is preferable from the viewpoint of preventing the ink used in the printing layer from seeping through. When the amount of acrylic acid ester is small, a clear image tends not to be obtained, and when the amount of acrylic acid ester is large, peeling tends to occur. The thickness of the anchor coat layer is 10 to 10.
It is preferably 12 μm. When it is less than 10 μm, it tends to cause penetration of the ink used in the printing layer, and when it exceeds 12 μm, it tends to cause the ink used in the printing layer to bleed.
【００１７】また、前記印刷層を形成するインクは、と
くに限定されないが、摩擦堅牢度向上の目的で使用され
るトップコート剤との相溶性、天然皮革への染み込みが
少ない点、均等な発色が得られる点、および環境への配
慮という点で、水性インクが好ましい。The ink for forming the printing layer is not particularly limited, but it has compatibility with a top coat agent used for the purpose of improving the fastness to friction, less penetration into natural leather, and uniform coloring. A water-based ink is preferable from the viewpoints of obtaining it and considering the environment.
【００１８】また、前記バインダー層は、印刷層とトッ
プコート層の接着性を向上させるために付与される。前
記層を形成するバインダーは、とくに限定されないが、
アクリル系樹脂、ポリ塩化ビニル系樹脂、ポリエステル
系樹脂、ポリアミド系樹脂、ウレタン系樹脂、ゴム系樹
脂などがあげられる。なかでも、印刷層に使用されるイ
ンクとの密着性、および面張り性能向上の点でウレタン
系樹脂、浸透性の点で水性のアクリル系樹脂が好まし
い。また、天然皮革に対するタテ、ヨコの均等な塗膜形
成の目的で、前記ウレタン系樹脂および水性のアクリル
系樹脂を併用することが好ましい。なお、ウレタン系樹
脂を使用する場合は、架橋剤を添加してもよい。また、
前記層の厚みは、１０〜１５μｍであることが好まし
い。１０μｍより少ないと、トップコート層に使用され
る溶剤（とくにメチルエチルケトン）が印刷層に使用さ
れるインクを溶解する傾向にあり、１５μｍをこえる
と、印刷層に使用されるインクの透過性が低下する傾向
にある。The binder layer is provided to improve the adhesiveness between the print layer and the top coat layer. The binder forming the layer is not particularly limited,
Examples thereof include acrylic resins, polyvinyl chloride resins, polyester resins, polyamide resins, urethane resins, rubber resins and the like. Among them, urethane resin is preferable from the viewpoint of adhesion to the ink used in the printing layer, and improvement of surface tension performance, and water-based acrylic resin is preferable from the viewpoint of permeability. Further, it is preferable to use the urethane resin and the water-based acrylic resin in combination for the purpose of forming a uniform coating film on the natural leather in the vertical and horizontal directions. If a urethane resin is used, a crosslinking agent may be added. Also,
The thickness of the layer is preferably 10 to 15 μm. If it is less than 10 μm, the solvent (especially methyl ethyl ketone) used in the topcoat layer tends to dissolve the ink used in the printing layer, and if it exceeds 15 μm, the permeability of the ink used in the printing layer decreases. There is a tendency.
【００１９】また、前記トップコート層は、光、摩擦な
どに対する印刷層の堅牢度を向上させるために付与され
る。前記層を形成するトップコート剤は、とくに限定さ
れないが、アクリル系樹脂、ポリ塩化ビニル系樹脂、ポ
リエステル系樹脂、ポリアミド系樹脂、ウレタン系樹
脂、ゴム系樹脂などがあげられる。なかでも、得られる
製品の堅牢度性能および耐溶剤性能の点で、ウレタン系
樹脂が好ましい。また、前記層の厚みは、１０〜１２μ
ｍであることが好ましい。１０μｍより少ないと、堅牢
度性能および得られる製品の耐溶剤性能が低下する傾向
にあり、１２μｍをこえると、得られる製品の屈曲性能
が低下する傾向にある。Further, the top coat layer is provided in order to improve the fastness of the printed layer against light, friction and the like. The top coat agent that forms the layer is not particularly limited, and examples thereof include acrylic resin, polyvinyl chloride resin, polyester resin, polyamide resin, urethane resin, and rubber resin. Among them, urethane resins are preferable from the viewpoints of fastness performance and solvent resistance performance of the obtained product. The thickness of the layer is 10 to 12 μm.
It is preferably m. If it is less than 10 μm, the fastness performance and the solvent resistance of the obtained product tend to be lowered, and if it exceeds 12 μm, the bending performance of the obtained product tends to be lowered.
【００２０】本発明の印刷された天然皮革製品は、前記
天然皮革の表面に、前記アンカーコート層、印刷層、バ
インダー層およびトップコート層が順次積層されてな
る。アンカーコート層の上に印刷層が形成されることに
より、印刷層におけるインクの滲みや染み込みが生じな
い。さらに、その上にバインダー層を設けることによっ
て、目止め剤としてはたらくため、得られる製品の性能
向上の目的でトップコート剤を使用することができるよ
うになるという効果が得られる。The printed natural leather product of the present invention has the anchor coat layer, the printing layer, the binder layer and the top coat layer sequentially laminated on the surface of the natural leather. By forming the printing layer on the anchor coat layer, ink bleeding or soaking into the printing layer does not occur. Furthermore, by providing a binder layer on it, it acts as a filling agent, so that the top coat agent can be used for the purpose of improving the performance of the obtained product.
【００２１】[0021]
【実施例】実施例１ 天然皮革として、クロム革（牛皮）を使用した。[Example] Example 1 Chrome leather (cowhide) was used as the natural leather.
【００２２】前記クロム革に、アンカーコート剤として
酢酸ビニルおよびアクリル酸エステルからなるエマルジ
ョン（株式会社トウペ製、トアビンデルＧＫ、樹脂分４
０％）を使用して、エアースプレーガンによりスプレー
コートし、厚み１０〜１２μｍのアンカーコート層を付
与した。ついで、前記クロム革をインクジェット装置に
導入して、水性インクを使用し、インクジェットプリン
トを行った。そののち、バインダーとしてアニオン系ウ
レタンディスパージョン（株式会社トウペ製、トアタン
Ｓ、固形分３０％）、トップコート剤としてウレタン系
樹脂（株式会社トウペ製、トアウレタン＃３５００）を
使用して、それぞれエアースプレーガンによりスプレー
コートし、厚み１０〜１２μｍのバインダー層および厚
み１０〜１２μｍのトップコート層を付与した。An emulsion of vinyl acetate and an acrylic ester as an anchor coating agent on the above-mentioned chrome leather (Toabindel GK, manufactured by Toupe Co., resin content 4
0%) was used for spray coating with an air spray gun to provide an anchor coat layer having a thickness of 10 to 12 μm. Then, the chrome leather was introduced into an inkjet device, and inkjet printing was performed using a water-based ink. After that, anion-based urethane dispersion (manufactured by Toupe Co., Toatan S, solid content 30%) is used as a binder, and urethane-based resin (manufactured by Toupe Co., Toaurethane # 3500) is used as a top coat agent. Spray coating was performed with a gun to provide a binder layer having a thickness of 10 to 12 μm and a top coat layer having a thickness of 10 to 12 μm.
【００２３】比較例１
アンカーコート層を付与しなかったこと以外は、実施例
１と同様に処理を行った。得られた天然皮革の画像は不
鮮明であった。Comparative Example 1 The same treatment as in Example 1 was carried out except that the anchor coat layer was not applied. The image of the obtained natural leather was unclear.
【００２４】評価法
密着試験：ＪＩＳ Ｋ ５４００−８．５．２の碁盤目
テープ法に準じた。
屈曲試験：ＪＩＳ Ｋ ６５４５（フレキソメーター使
用）に準じた。
耐光性：ＪＩＳ Ｌ ０８４２（変退色用グレースケー
ル）に準じ、変退色用グレースケール標準光源下で評価
を行った。
摩擦堅牢度：ＪＩＳ Ｋ ６５４７に準じた。Evaluation method Adhesion test: According to the cross-cut tape method of JIS K 5400-8.5.2. Bending test: According to JIS K 6545 (using a flexometer). Light resistance: In accordance with JIS L 0842 (gray scale for discoloration / fading), evaluation was performed under a gray scale standard light source for discoloration / fading. Friction fastness: according to JIS K 6547.
【００２５】前記評価法に従い、実施例１および比較例
１で得た天然皮革を評価した。結果を表１に示す。The natural leathers obtained in Example 1 and Comparative Example 1 were evaluated according to the above evaluation method. The results are shown in Table 1.
【００２６】[0026]
【表１】 [Table 1]
【００２７】[0027]
【発明の効果】本発明によれば、天然皮革に対して優れ
た密着性を有する印刷層を付与することができる。ま
た、接着性の点で、転写法では印刷することのできなか
った吟付皮、床皮、編皮および毛皮などの多種の皮革に
対しても、優れた密着性で印刷層を付与することができ
る。EFFECTS OF THE INVENTION According to the present invention, a printing layer having excellent adhesion to natural leather can be provided. Also, in terms of adhesiveness, it is possible to apply a printing layer with excellent adhesion to various types of leather such as Ginza, floor leather, knit leather and fur that could not be printed by the transfer method. You can
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｂ０５Ｄ 7/24 Ｂ０５Ｄ 7/24 ３０２Ｐ ４Ｈ０５７ Ｂ３２Ｂ 9/02 Ｂ３２Ｂ 9/02 Ｂ４１Ｊ 2/01 Ｂ４１Ｍ 5/00 Ａ Ｂ４１Ｍ 5/00 Ｃ１４Ｃ 11/00 Ｃ１４Ｃ 11/00 Ｄ０６Ｐ 5/00 １１１Ａ Ｄ０６Ｐ 5/00 １１１ １１２ １１２ １１３ １１３ Ｂ４１Ｊ 3/04 １０１Ｚ Ｆターム(参考） 2C056 EA13 FB01 2H086 BA05 BA17 BA34 4D075 AC06 AE03 AE07 CA13 CA47 DA04 DB16 DC38 EA07 EA41 EB12 EB15 EB22 EB35 EB38 EB39 4F056 AA01 CC06 CC07 CC08 CC66 DD04 DD44 FF17 4F100 AJ10A AK22B AK25B AK51 AS00D BA05 BA07 BA10A BA10E CC00B CC00E EH46B EH46D EH46E EJ65B EJ65E HB31C JK06 JL11 JM01 4H057 AA01 AA02 CA13 CA18 CB08 CB16 CC01 CC03 DA02 DA21 GA06 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) B05D 7/24 B05D 7/24 302P 4H057 B32B 9/02 B32B 9/02 B41J 2/01 B41M 5/00 A B41M 5/00 C14C 11/00 C14C 11/00 D06P 5/00 111A D06P 5/00 111 112 112 112 113 113 B41J 3/04 101Z F term (reference) 2C056 EA13 FB01 2H086 BA05 BA17 BA34 4D075 AC06 AE03 DA04 CA04 DB16 DC38 EA07 EA41 EB12 EB15 EB22 EB35 EB38 EB39 4F056 AA01 CC06 CC07 CC08 CC66 DD04 DD44 FF17 4F100 AJ10A AK22B AK25B AK51 AS00D BA05 BA07 BA01 A06 J65A01 J65A06J65A01 J65E0646A06J65JE0546JE0646H6BJE0546B16JE0146HB DA21 GA06
Claims (6)
与する工程と、印刷層を付与する工程と、バインダー層
を付与する工程と、トップコート層を付与する工程とか
らなる印刷された天然皮革製品の製造方法。1. A printed natural leather comprising the steps of applying an anchor coat layer to the surface of natural leather, applying a printing layer, applying a binder layer, and applying a top coat layer. Product manufacturing method.
よびアクリル酸エステルからなる請求項１記載の印刷さ
れた天然皮革製品の製造方法。2. The method for producing a printed natural leather product according to claim 1, wherein the anchor coat layer is made of vinyl acetate and acrylic acid ester.
よびトップコート層がスプレーコート法により付与され
てなる請求項１または２記載の印刷された天然皮革製品
の製造方法。3. The method for producing a printed natural leather product according to claim 1, wherein the anchor coat layer, the binder layer and the top coat layer are applied by a spray coat method.
付与されてなる請求項１、２または３記載の印刷された
天然皮革製品の製造方法。4. The method for producing a printed natural leather product according to claim 1, 2 or 3, wherein the printing layer is applied by an inkjet method.
刷層、バインダー層およびトップコート層が順次積層さ
れてなる印刷された天然皮革製品。5. A printed natural leather product in which an anchor coat layer, a printing layer, a binder layer and a top coat layer are sequentially laminated on the surface of natural leather.
よびアクリル酸エステルからなる請求項５記載の印刷さ
れた天然皮革製品。6. The printed natural leather product of claim 5, wherein the anchor coat layer comprises vinyl acetate and an acrylic ester.