JP2003220680A - Biodegradable water-resistant printing paper - Google Patents
Biodegradable water-resistant printing paperInfo
- Publication number
- JP2003220680A JP2003220680A JP2002021311A JP2002021311A JP2003220680A JP 2003220680 A JP2003220680 A JP 2003220680A JP 2002021311 A JP2002021311 A JP 2002021311A JP 2002021311 A JP2002021311 A JP 2002021311A JP 2003220680 A JP2003220680 A JP 2003220680A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- biodegradable
- biodegradable resin
- printing paper
- smoothness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は生分解性耐水印刷用
紙に関する。さらに詳しくは、本発明は、合成紙に匹敵
する印刷適性を有すると共に、耐水性も有し、屋外での
長期使用に耐えることができ、しかも良好な生分解性を
有することから、環境汚染をもたらすことのない環境調
和型の印刷用紙に関するものである。TECHNICAL FIELD The present invention relates to a biodegradable waterproof printing paper. More specifically, the present invention has a printability comparable to that of synthetic paper, and also has water resistance, can withstand long-term outdoor use, and has good biodegradability, and thus can reduce environmental pollution. The present invention relates to an environmentally friendly printing paper that never brings.
【０００２】[0002]
【従来の技術】従来、天然繊維を抄造して得られた紙材
料は、印刷適性に優れると共に、リサイクルが可能であ
り、しかも優れた生分解性を有することから、廃棄処分
する場合、焼却による排ガスの問題などが発生せず、環
境調和型材料であることが知られている。しかし、紙材
料は、このような長所を有するが、耐水性に劣るという
欠点を有しており、したがって、屋外用のポスターなど
に関しては、耐水性に優れ、かつ長期耐候性を有すると
共に、印刷適性を付与したプラスチックフィルムや合成
紙からなる印刷用紙が用いられている。2. Description of the Related Art Conventionally, a paper material obtained by making a natural fiber into paper has excellent printability, is recyclable, and has excellent biodegradability. It is known that it is an environmentally friendly material without the problem of exhaust gas. However, the paper material has such an advantage, but has a drawback that it is inferior in water resistance. Therefore, it is excellent in water resistance and has long-term weather resistance as well as printing for outdoor posters. Printing paper made of a plastic film or synthetic paper to which aptitude is given is used.
【０００３】しかしながら、上記プラスチックフィルム
や合成紙からなる印刷用紙においては、使用後、焼却に
よる廃棄処分する場合には、排ガスなどによる周辺環境
への影響や負荷の問題が発生し、また埋立処分する場合
には、非分解性（非減容化）の問題が発生するなど、使
用後の処理が社会問題化しつつある。However, when the printing paper made of the plastic film or the synthetic paper is disposed of by incineration after use, there is a problem of influence and load on the surrounding environment due to exhaust gas and the like, and it is landfilled. In some cases, non-degradability (non-volume reduction) problems occur, and post-use treatment is becoming a social problem.
【０００４】一方、近年、使用後は生ごみなどと一緒に
堆肥などにして利用でき、処理がしやすい素材として、
生分解性樹脂が注目され、一部がすでに実用化されてい
る。この生分解性樹脂は、使用時には、通常のプラスチ
ックと同様の機能を発揮するが、使用後は自然界に存在
する微生物や分解酵素によって分解され、最終的に水と
二酸化炭素になる性質を有している。また、焼却しても
発生熱量が低いので焼却炉を傷付けず、ダイオキシンな
どの有害物質の排出がない上、堆肥を作るコンポスト化
装置の中では、分解がさらに速くなるなどの特性も有し
ている。On the other hand, in recent years, as a material that can be easily processed after being used as compost together with garbage and the like,
Biodegradable resins have attracted attention and some have already been put to practical use. When used, this biodegradable resin has the same function as ordinary plastics, but after use it has the property of being decomposed by microorganisms and degrading enzymes existing in nature to finally become water and carbon dioxide. ing. In addition, since the amount of heat generated is low even when incinerated, it does not damage the incinerator, does not emit harmful substances such as dioxins, and has the property that decomposition is even faster in composting equipment that makes compost. There is.
【０００５】現在、この生分解性樹脂には、大きく分け
て微生物系、化学合成系、天然物利用系の三種があり、
微生物系としては、例えばポリ３−ヒドロキシブチレー
ト、３−ヒドロキシブチレートと３−ヒドロキシバリレ
ートの共重合ポリエステル、ポリアミノ酸などがある。
一方、化学合成系としては、例えばポリカプロラクトン
系、ポリ乳酸系、ポリブチレンサクシネート系、ポリグ
リコール酸系、ポリビニルアルコール系などがあり、天
然物利用系としては、例えば修飾澱粉、酢酸セルロー
ス、キトサン、アルギン酸などの利用が挙げられる。こ
れらの生分解性樹脂の中で、大量生産が可能で、コスト
的に有利なことから、現在、化学合成系の脂肪族ポリエ
ステル系生分解性樹脂であるポリカプロラクトン系、ポ
リ乳酸系、ポリブチレンサクシネート系などを中心に市
場開拓が進められている。At present, there are roughly three types of biodegradable resins: microbial type, chemical synthetic type and natural product utilizing type.
Examples of the microbial system include poly-3-hydroxybutyrate, copolymerized polyester of 3-hydroxybutyrate and 3-hydroxyvalerate, and polyamino acid.
On the other hand, the chemically synthesized system includes, for example, polycaprolactone system, polylactic acid system, polybutylene succinate system, polyglycolic acid system, polyvinyl alcohol system, and the like, and the natural product utilization system includes, for example, modified starch, cellulose acetate, chitosan. , The use of alginic acid and the like. Among these biodegradable resins, mass production is possible and it is advantageous in terms of cost. Therefore, at present, chemically synthesized aliphatic polyester biodegradable resins such as polycaprolactone, polylactic acid and polybutylene are currently available. Market development is being promoted mainly for succinate systems.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、このような
状況下で、合成紙に匹敵する印刷適性を有すると共に、
耐水性も有し、屋外での長期使用に耐えることができ、
しかも良好な生分解性を有することから、環境汚染をも
たらすことのない環境調和型の印刷用紙を提供すること
を目的とするものである。Under the circumstances, the present invention has printability comparable to that of synthetic paper, and
It also has water resistance and can withstand long-term outdoor use.
Moreover, it is an object of the present invention to provide an environmentally friendly printing paper that does not cause environmental pollution because it has good biodegradability.
【０００７】[0007]
【課題を解決するための手段】本発明者らは、前記の優
れた機能を有する印刷用紙を開発すべく鋭意研究を重ね
た結果、所定の平滑度を有する原紙の少なくとも一方の
面に耐水性を有する特定の生分解性樹脂層を設け、かつ
表面平滑度が所定の範囲にある印刷用紙が、その目的に
適合し得ることを見出した。本発明は、かかる知見に基
づいて完成したものである。DISCLOSURE OF THE INVENTION As a result of intensive studies conducted by the present inventors to develop a printing paper having the above-mentioned excellent function, at least one surface of a base paper having a predetermined smoothness has a water resistance. It was found that a printing paper provided with a specific biodegradable resin layer having a surface smoothness within a predetermined range can meet the purpose. The present invention has been completed based on such findings.
【０００８】すなわち、本発明は、（１）天然繊維を抄
造してなる平滑度２０〜２００秒の原紙と、その少なく
とも一方の面にラミネートされた脂肪族ポリエステル系
生分解性樹脂層を有し、かつその表面平滑度が５００〜
２０００秒であることを特徴とする生分解性耐水印刷用
紙、（２）脂肪族ポリエステル系生分解性樹脂層が、ポ
リカプロラクトン系、ポリ乳酸系、ポリアルキレンサク
シネート系及びポリグリコール酸系の中から選ばれる少
なくとも一種の化学合成系生分解性樹脂からなる層であ
る上記（１）の生分解性耐水印刷用紙、（３）脂肪族ポ
リエステル系生分解性樹脂層が、ポリアルキレンサクシ
ネート系生分解性樹脂からなる層である上記（１）の生
分解性耐水印刷用紙原紙
（４）原紙のエッジ吸水度が０〜１．０ｇ／ｍである上
記（１）ないし（３）の生分解性耐水印刷用紙、（５）
原紙の坪量が３０〜３００ｇ／ｍ2 であり、かつその少
なくとも一方の面にラミネートされた脂肪族ポリエステ
ル系生分解性樹脂層の厚さが、５〜５０μｍである上記
（１）ないし（４）の生分解性耐水印刷用紙、及び
（６）脂肪族ポリエステル系生分解性樹脂を押出しラミ
ネート加工して原紙の少なくとも一方の面に該生分解性
樹脂層を設けると同時に、鏡面処理を施す上記（１）〜
（５）の生分解性耐水印刷用紙、を提供するものであ
る。That is, the present invention comprises (1) a base paper having a smoothness of 20 to 200 seconds formed from a natural fiber, and an aliphatic polyester biodegradable resin layer laminated on at least one surface thereof. And its surface smoothness is 500-
2000 seconds of biodegradable water-resistant printing paper, (2) aliphatic polyester biodegradable resin layer is polycaprolactone-based, polylactic acid-based, polyalkylene succinate-based or polyglycolic acid-based The biodegradable waterproof printing paper according to (1), which is a layer composed of at least one chemically synthesized biodegradable resin selected from the above, and (3) the aliphatic polyester biodegradable resin layer is a polyalkylene succinate-based biodegradable resin. Biodegradable water-resistant printing paper base paper of the above (1) which is a layer made of degradable resin (4) Biodegradability of the above (1) to (3), wherein the edge water absorption of the base paper is 0 to 1.0 g / m Water resistant printing paper, (5)
The basis weight of the base paper is 30 to 300 g / m 2 , and the thickness of the aliphatic polyester biodegradable resin layer laminated on at least one surface thereof is 5 to 50 μm (1) to (4). The biodegradable water-resistant printing paper according to 1), and (6) the aliphatic polyester biodegradable resin is extruded and laminated to form the biodegradable resin layer on at least one surface of the base paper, and at the same time, mirror surface treatment is performed. (1) ~
The present invention provides a biodegradable waterproof printing paper according to (5).
【０００９】[0009]
【発明の実施の形態】本発明の生分解性耐水印刷用紙
は、天然繊維を抄造してなる原紙の少なくとも一方の面
に、生分解性樹脂層を設けた複合紙である。この印刷用
紙における原紙に用いられる天然繊維としては、特に制
限はなく、各種木材パルプ、靱皮繊維や雁皮繊維などの
中から選ばれる少なくとも一種が挙げられる。上記木材
パルプとしては、例えば機械パルプ（ＭＰ）、熱機械パ
ルプ（ＴＭＰ）、針葉樹晒クラフトパルプ（ＮＢＫ
Ｐ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹未
晒クラフトパルプ（ＮＵＫＰ）、広葉樹未晒クラフトパ
ルプ（ＬＵＫＰ）などがある。また、古紙再生パルプも
用いることができる。BEST MODE FOR CARRYING OUT THE INVENTION The biodegradable water-resistant printing paper of the present invention is a composite paper in which a biodegradable resin layer is provided on at least one surface of a raw paper made from natural fibers. The natural fiber used as the base paper in this printing paper is not particularly limited and includes at least one selected from various wood pulps, bast fibers, gooseskin fibers and the like. Examples of the wood pulp include mechanical pulp (MP), thermomechanical pulp (TMP), and bleached softwood kraft pulp (NBK).
P), bleached hardwood kraft pulp (LBKP), unbleached softwood kraft pulp (NUKP), unbleached hardwood kraft pulp (LUKP), and the like. Also, recycled pulp of waste paper can be used.
【００１０】原紙の製造は、通常この分野で使用されて
いる抄造技術を用いて行うことができる。まず、前記天
然繊維を水に分散させて紙料を調製する。この試料の調
製に当たっては、所望により、従来抄紙に用いられてい
る各種抄紙用添加剤、例えばクレー、炭酸カルシウム、
二酸化チタンなどの填料、サイズ剤、歩留まり向上剤、
定着剤、湿潤紙力増強剤、乾燥紙力増強剤、顔料、分散
剤、スライムコントロール剤、消泡剤、粘剤、生分解性
バインダー繊維などが挙げられる。次いで、このように
して調製された紙料を、長網抄紙機や円網抄紙機などに
よる湿式抄紙法にてシート化することによって、原紙を
製造することができる。The base paper can be manufactured by using a papermaking technique usually used in this field. First, the natural fiber is dispersed in water to prepare a paper material. In the preparation of this sample, if desired, various papermaking additives conventionally used in papermaking, such as clay, calcium carbonate,
Fillers such as titanium dioxide, sizing agents, yield improvers,
A fixing agent, a wet paper strength enhancer, a dry paper strength enhancer, a pigment, a dispersant, a slime control agent, a defoaming agent, a sticky agent, a biodegradable binder fiber and the like can be mentioned. Next, the base paper can be produced by forming the thus prepared paper material into a sheet by a wet papermaking method using a Fourdrinier paper machine, a cylinder paper machine or the like.
【００１１】本発明においては、このようにして得られ
た原紙の少なくとも一方の面を、生分解性樹脂を含む塗
工液により表面処理し、原紙の耐水性を向上させること
ができる。また、前記塗工液には、所望により、表面サ
イズ剤、顔料などを添加してもよい。この表面処理は、
印刷機、含浸機、各種塗工機などを用いて行うことがで
きる。なお、前述の紙料に所望により添加される生分解
性バインダー繊維及び上記塗工機に用いられる生分解性
樹脂としては、耐水性の良好な脂肪族ポリエステル系の
ものが好適である。In the present invention, at least one surface of the thus obtained base paper can be surface-treated with a coating liquid containing a biodegradable resin to improve the water resistance of the base paper. If desired, a surface sizing agent, a pigment, etc. may be added to the coating liquid. This surface treatment is
It can be performed using a printing machine, an impregnation machine, various coating machines, and the like. In addition, as the biodegradable binder fiber optionally added to the above-mentioned stock and the biodegradable resin used in the coating machine, an aliphatic polyester-based resin having good water resistance is suitable.
【００１２】本発明の印刷用紙に用いられる原紙の平滑
度は、２０〜２００秒の範囲である。この平滑度が２０
秒未満では、表面平滑度が十分に高い印刷用紙が得られ
にくく、一方２００秒を超える場合、原紙と、それにラ
ミネートされる生分解性樹脂層との接着強度が低下す
る。この原紙の好ましい平滑度は４０〜１５０秒の範囲
である。なお、前記平滑度は、以下に示す方法により、
測定した値である。The smoothness of the base paper used for the printing paper of the present invention is in the range of 20 to 200 seconds. This smoothness is 20
If it is less than seconds, it is difficult to obtain a printing paper having a sufficiently high surface smoothness, while if it exceeds 200 seconds, the adhesive strength between the base paper and the biodegradable resin layer laminated on it is lowered. The preferred smoothness of this base paper is in the range of 40 to 150 seconds. The smoothness is calculated by the following method.
It is the measured value.
【００１３】＜平滑度の測定方法＞ＪＡＰＡＮ ＴＡＰ
ＰＩ 紙パルプ試験方法ＮＯ．５−２：２０００王研法
また、該原紙は、エッジ吸水度が０〜１．０ｇ／ｍ程度
の耐水性を有するものが好ましい。このエッジ吸水度が
１．０ｇ／ｍを超えると所望の耐水性を有する印刷用紙
が得られにくい。なお、上記エッジ吸水度は、以下に示
す方法により、測定した値である。<Smoothness Measuring Method> JAPAN TAP
PI paper pulp test method NO. 5-2: 2000 Oken method Further, the base paper preferably has water resistance with an edge water absorption of about 0 to 1.0 g / m. If the edge water absorption exceeds 1.0 g / m, it is difficult to obtain a printing paper having desired water resistance. The edge water absorption is a value measured by the method described below.
【００１４】＜エッジ吸水度の測定方法＞既知の重量の
原紙の表面を透明ポリエステルテープで覆ったサンプル
（５０×２００ｍｍ）を２３℃の水中に２４時間浸漬
後、重量を測定し、その重量増加（ｇ）を０．５で除し
た値（ｇ／ｍ）をエッジ吸水度とする。<Measurement Method of Edge Water Absorption> A sample (50 × 200 mm) in which a surface of a base paper having a known weight is covered with a transparent polyester tape is immersed in water at 23 ° C. for 24 hours, and then the weight is measured to increase the weight. The value (g / m) obtained by dividing (g) by 0.5 is taken as the edge water absorption.
【００１５】本発明の印刷用紙に用いられる原紙の坪量
としては、通常３０〜３００ｇ／ｍ 2 の範囲である。本
発明の印刷用紙においては、前記原紙の少なくとも一方
の面にラミネートされる生分解性樹脂層を構成する生分
解性樹脂として、耐水性、シート形成性、印刷適性、機
械特性などの点から、脂肪族ポリエステル系生分解性樹
脂が用いられる。この脂肪族ポリエステル系生分解性樹
脂には、微生物系及び化学合成系があるが、大量生産が
可能で、コスト的に有利であり、かつ上記の特性に優れ
る点から、特にポリカプロラクトン系、ポリ乳酸系、ポ
リアルキレンサクシネート系及びポリグリコール酸系な
どの化学合成系生分解性樹脂が好適である。これらの中
では、ポリブチレンレンサクシネート等のポリアルキレ
ンサクシネート系の化学合成系生分解性樹脂が、印刷特
性、生分解性及びラミネート加工適性をバランス良く有
している点から、特に好ましい。これらの生分解性樹脂
は、一種を単独で用いてもよく、二種以上を組み合わせ
て用いてもよい。The basis weight of the base paper used for the printing paper of the present invention
As usually 30-300 g / m 2Is the range. Book
In the printing paper of the invention, at least one of the base papers
Of biodegradable resin layer laminated on the surface of
As degradable resin, water resistance, sheet formability, printability, machine
From the viewpoint of mechanical properties, etc., an aliphatic polyester biodegradable tree
Fat is used. This aliphatic polyester biodegradable tree
There are microbial and chemically synthesized fats, but mass production
Possible, cost effective, and excellent in the above characteristics
From the point of view, especially polycaprolactone type, polylactic acid type,
Lialkylene succinate type and polyglycolic acid type
Any chemically synthesized biodegradable resin is suitable. Among these
Then, polyalkylene such as polybutylene succinate
The chemically synthesized biodegradable resin based on succinate
With good balance of biodegradability, biodegradability and suitability for laminating
Therefore, it is particularly preferable. These biodegradable resins
May be used alone or in combination of two or more
You may use it.
【００１６】本発明においては、前記脂肪族ポリエステ
ル系生分解性樹脂に、本発明の目的が損なわれない範囲
で、所望により通常のプラスチックに使用される各種添
加剤、例えば酸化防止剤、紫外線吸収剤、光安定剤、可
塑剤、フィラー、帯電防止剤、滑剤、着色剤などを配合
して、成形材料を調製し、この成形材料を押出しラミネ
ート加工して、前記原紙の少なくとも一方の面に、生分
解性樹脂層を設けることが好ましい。そして、この押出
しラミネート加工時に鏡面処理を施し、ラミネートされ
た生分解性樹脂層に、所望の平滑度を付与するのが有利
である。また、前記成形材料を用いて、公知の成形方法
により、予めフィルムを作製し、このフィルムを、原紙
の少なくとも一方の面にドライラミネート加工により、
ラミネートする方法を用いることもできる。In the present invention, the aliphatic polyester biodegradable resin is added to the above-mentioned aliphatic polyester biodegradable resin, if desired, in the range where the object of the present invention is not impaired, if desired, for example, various additives such as an antioxidant and an ultraviolet absorber. Agent, a light stabilizer, a plasticizer, a filler, an antistatic agent, a lubricant, a colorant and the like are mixed to prepare a molding material, and the molding material is extruded and laminated, and at least one surface of the base paper, It is preferable to provide a biodegradable resin layer. Then, it is advantageous to give a desired smoothness to the laminated biodegradable resin layer by applying a mirror surface treatment during the extrusion laminating process. Further, using the above-mentioned molding material, a film is prepared in advance by a known molding method, and this film is dry-laminated on at least one surface of the base paper,
A laminating method can also be used.
【００１７】本発明の印刷用紙においては、このように
してラミネートされた生分解性樹脂層の表面平滑度は、
５００〜２０００秒の範囲にあることが必要である。こ
の平滑度が５００秒未満では印刷後の仕上がり性に劣
り、一方、２０００秒を超えると印刷適性が不充分とな
る場合がある。印刷仕上がり性及び印刷適性などを考慮
すると、この表面平滑度は７００〜１６００秒の範囲が
好ましい。In the printing paper of the present invention, the surface smoothness of the biodegradable resin layer thus laminated is
It should be in the range of 500-2000 seconds. If the smoothness is less than 500 seconds, the finish after printing is poor, and if it exceeds 2000 seconds, printability may be insufficient. Considering the print finish and printability, the surface smoothness is preferably in the range of 700 to 1600 seconds.
【００１８】このような性状を有する本発明の印刷用紙
は、以下に示す効果を奏する。
（１）既存の合成紙に匹敵する印刷仕上がり性が可能で
ある。
（２）良好な耐水性及び耐候性を有することから、合成
紙と同様に屋外での長期使用に耐えることができる。
（３）生分解性を有する（土壤中で微生物により分解可
能）ので、使用後のゴミの軽減を図ることができる。
（４）焼却が不要で、有害大気汚染物質などを排出する
ことがないので、環境汚染をもたらさない。The printing paper of the present invention having such properties has the following effects. (1) A print finish comparable to existing synthetic paper is possible. (2) Since it has good water resistance and weather resistance, it can withstand long-term outdoor use like synthetic paper. (3) Since it has biodegradability (it can be decomposed by microorganisms in the soil), it is possible to reduce dust after use. (4) Since it does not require incineration and does not emit harmful air pollutants, it does not cause environmental pollution.
【００１９】[0019]
【実施例】次に、本発明を実施例により、さらに詳細に
説明するが、本発明は、これらの例によってなんら限定
されるものではない。なお、各例で得られた印刷用紙の
諸特性は、以下に示す要領に従って評価した。また、平
滑度及びエッジ吸水度は、明細書本文に記載の方法によ
り、測定した。EXAMPLES The present invention will now be described in more detail with reference to examples, but the present invention is not limited to these examples. The various properties of the printing paper obtained in each example were evaluated according to the following points. Further, the smoothness and the edge water absorption were measured by the methods described in the text of the specification.
【００２０】（１）印刷仕上がり性
目視観察により、下記の判定基準にて、印刷仕上がり性
を評価した。
○：全体にむらなく精細にインクが乗っている。
△：一部に印刷むらが見られる。
×：全体に印刷むらが見られる。(1) Print finish The print finish was evaluated by visual observation according to the following criteria. ◯: Ink is finely distributed on the entire surface. Δ: Print unevenness is partially observed. X: Uneven printing is seen on the whole.
【００２１】（２）生分解性 下記の判定基準にて、生分解性を評価した。 ○：土中にて、１ケ月以内に分解を開始する。 △：土中にて、１ケ月以上経過後に分解を開始する。 ×：分解せず。(2) Biodegradability The biodegradability was evaluated according to the following criteria. ◯: Decomposition starts in the soil within one month. Δ: Decomposition starts in soil after one month or more. X: Not decomposed.
【００２２】（３）耐水性
ウエザーメーターにて、１０分／６０分の頻度での降雨
条件で４８時間処理後、下記の判定基準にて耐水性を評
価した。
○：変化なし（エッジ部からのしみ込みなし）。
△：部分的に水の浸透が見られる。
×：全体に水の浸透が見られる。(3) Water resistance With a weather meter, after 48 hours of treatment under a rainfall condition of a frequency of 10 minutes / 60 minutes, the water resistance was evaluated according to the following criteria. ○: No change (no penetration from the edge) Δ: Permeation of water is partially observed. X: Water permeation is seen throughout.
【００２３】実施例１
原紙として、湿潤紙力を付与した坪量１２７．９ｇ／ｍ
2 のケント紙（平滑度５０秒、エッジ吸水度０．０５ｇ
／ｍ）を、生分解性樹脂として、ポリブチレンサクシネ
ート系生分解性樹脂〔昭和高分子（株）製「ビオノーレ
＃１９０３」〕を使用した。上記生分解性樹脂を、押出
しラミネーターにて、上記原紙の両面に、それぞれ２０
μｍの厚さに鏡面ラミネート加工し、平滑度１４８０秒
の印刷用紙を作製した。この印刷用紙の諸特性を第１表
に示す。Example 1 As a base paper, a basis weight of 127.9 g / m 2 with wet paper strength applied
2 Kent paper (smoothness 50 seconds, edge water absorption 0.05g
/ M) as a biodegradable resin, a polybutylene succinate-based biodegradable resin [“Bionore # 1903” manufactured by Showa Highpolymer Co., Ltd.] was used. The biodegradable resin is extruded on the both sides of the base paper by an extrusion laminator to form 20
Mirror-like lamination was performed to a thickness of μm to produce a printing paper with a smoothness of 1480 seconds. Table 1 shows various characteristics of this printing paper.
【００２４】実施例２
原紙として、湿潤紙力を付与した坪量１２７．９ｇ／ｍ
2 のケント紙（平滑度３０秒、エッジ吸水度０．０５ｇ
／ｍ）を用い、生分解性樹脂フィルムとして、厚さ２０
μｍのポリ乳酸系生分解性樹脂フィルム〔三井化学
（株）製「レイシア２０μｍフィルム」〕を使用した。
上記生分解性樹脂フィルムを、ドライラミネーターに
て、上記原紙の両面にラミネート加工し、平滑度７９０
秒の印刷用紙を作製した。この印刷用紙の諸特性を第１
表に示す。Example 2 As a base paper, a basis weight of 127.9 g / m 2 with wet paper strength applied
2 Kent paper (smoothness 30 seconds, edge water absorption 0.05g
/ M) as a biodegradable resin film with a thickness of 20
A polylactic acid-based biodegradable resin film having a thickness of [μm] [“Lysia 20 μm film” manufactured by Mitsui Chemicals, Inc.] was used.
The biodegradable resin film was laminated on both sides of the base paper with a dry laminator to obtain a smoothness of 790.
Second printing paper was prepared. The characteristics of this printing paper are
Shown in the table.
【００２５】比較例１
原紙として、湿潤紙力を付与した坪量１２７．９ｇ／ｍ
2 のケント紙（平滑度１５秒、エッジ吸水度０．０６ｇ
／ｍ）を、生分解性樹脂として、ポリブチレンサクシネ
ート系生分解性樹脂〔昭和高分子（株）製「ビオノーレ
＃１９０３」〕を使用した。上記生分解性樹脂を、押出
しラミネーターにて、上記原紙の両面に、それぞれ２０
μｍの厚さにラミネート加工し、平滑度１１０秒の印刷
用紙を作製した。この印刷用紙の諸特性を第１表に示
す。Comparative Example 1 As a base paper, a basis weight of 127.9 g / m 2 with wet paper strength applied
2 Kent paper (smoothness 15 seconds, edge water absorption 0.06g
/ M) as a biodegradable resin, a polybutylene succinate-based biodegradable resin [“Bionore # 1903” manufactured by Showa Highpolymer Co., Ltd.] was used. The biodegradable resin is extruded on the both sides of the base paper by an extrusion laminator to form 20
A printing paper having a smoothness of 110 seconds was produced by laminating to a thickness of μm. Table 1 shows various characteristics of this printing paper.
【００２６】比較例２
印刷用紙として、坪量１３０ｇ／ｍ2 のポリプロピレン
ラミネート紙を用いた。この印刷用紙の諸特性を第１表
に示す。Comparative Example 2 A polypropylene laminated paper having a basis weight of 130 g / m 2 was used as the printing paper. Table 1 shows various characteristics of this printing paper.
【００２７】比較例３
印刷用紙として、坪量１３０ｇ／ｍ2 のポリプロピレン
系合成紙を用いた。この印刷用紙の諸特性を第１表に示
す。Comparative Example 3 A polypropylene synthetic paper having a basis weight of 130 g / m 2 was used as the printing paper. Table 1 shows various characteristics of this printing paper.
【００２８】[0028]
【表１】 [Table 1]
【００２９】[0029]
【発明の効果】本発明によれば、合成紙に匹敵する印刷
適性を有すると共に、耐水性も有し、屋外での長期使用
に耐えることができ、しかも良好な生分解性を有するこ
とから、環境汚染をもたらすことのない環境調和型の印
刷用紙を提供することができる。本発明の印刷用紙は、
例えば屋内外用ポスターや、紙トレーなどの紙器等に好
適に用いられる。According to the present invention, since it has printability comparable to that of synthetic paper, has water resistance, can withstand long-term outdoor use, and has good biodegradability, It is possible to provide an environmentally friendly printing paper that does not cause environmental pollution. The printing paper of the present invention is
For example, it is suitably used for indoor and outdoor posters, paper containers such as paper trays, and the like.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 小林 香子 静岡県島田市幸町９−３ (72)発明者 袴田 芳則 静岡県掛川市日坂34−２ (72)発明者 田中 秀紀 静岡県藤枝市平島1333−３ Ｆターム(参考） 4F100 AK41A AK41C BA03 BA06 BA10A BA10C DG10B GB90 JA20A JA20B JA20C JB07 JD15B JK15A JK15B JK15C JL00 JL01 JL09 YY00A YY00B YY00C 4L055 AJ01 AJ02 BE13 BE20 EA07 EA10 EA12 FA15 FA19 FA20 GA15 GA47 GA50 ─────────────────────────────────────────────────── ─── Continued front page (72) Inventor Kako Kobayashi 9-3 Saiwaicho, Shimada City, Shizuoka Prefecture (72) Inventor Yoshinori Hakada 34-2 Hisaka, Kakegawa City, Shizuoka Prefecture (72) Inventor Hidenori Tanaka 1333-3 Hirashima, Fujieda City, Shizuoka Prefecture F-term (reference) 4F100 AK41A AK41C BA03 BA06 BA10A BA10C DG10B GB90 JA20A JA20B JA20C JB07 JD15B JK15A JK15B JK15C JL00 JL01 JL09 YY00A YY00B YY00C 4L055 AJ01 AJ02 BE13 BE20 EA07 EA10 EA12 FA15 FA19 FA20 GA15 GA47 GA50
Claims (6)
００秒の原紙と、その少なくとも一方の面にラミネート
された脂肪族ポリエステル系生分解性樹脂層を有し、か
つその表面平滑度が５００〜２０００秒であることを特
徴とする生分解性耐水印刷用紙。1. A smoothness of 20 to 2 obtained by forming a natural fiber into paper.
A biodegradable water-resistant printing having a 00 second base paper and an aliphatic polyester biodegradable resin layer laminated on at least one surface thereof, and having a surface smoothness of 500 to 2000 seconds. Paper.
が、ポリカプロラクトン系、ポリ乳酸系、ポリアルキレ
ンサクシネート系及びポリグリコール酸系の中から選ば
れる少なくとも一種の化学合成系生分解性樹脂からなる
層である請求項１記載の生分解性耐水印刷用紙。2. The aliphatic polyester biodegradable resin layer comprises at least one chemically synthesized biodegradable resin selected from polycaprolactone type, polylactic acid type, polyalkylene succinate type and polyglycolic acid type. The biodegradable waterproof printing paper according to claim 1, which is a layer consisting of
が、ポリアルキレンサクシネート系生分解性樹脂からな
る層である請求項１記載の生分解性耐水印刷用紙。3. The biodegradable waterproof printing paper according to claim 1, wherein the aliphatic polyester biodegradable resin layer is a layer made of a polyalkylene succinate biodegradable resin.
である請求項１ないし３のいずれかに記載の生分解性耐
水印刷用紙。4. The edge water absorption of the base paper is 0 to 1.0 g / m.
The biodegradable waterproof printing paper according to any one of claims 1 to 3.
り、かつその少なくとも一方の面にラミネートされた脂
肪族ポリエステル系生分解性樹脂層の厚さが、５〜５０
μｍである請求項１ないし４のいずれかに記載の生分解
性耐水印刷用紙。5. The basis weight of the base paper is 30 to 300 g / m 2 , and the thickness of the aliphatic polyester biodegradable resin layer laminated on at least one surface thereof is 5 to 50.
The biodegradable water-resistant printing paper according to any one of claims 1 to 4, which has a thickness of μm.
出しラミネート加工して原紙の少なくとも一方の面に該
生分解性樹脂層を設けると同時に、鏡面処理を施す請求
項１ないし５のいずれかに記載の生分解性耐水印刷用
紙。6. An aliphatic polyester-based biodegradable resin is extruded and laminated to provide the biodegradable resin layer on at least one surface of the base paper, and at the same time, mirror surface treatment is performed. Biodegradable waterproof printing paper as described.