JP2003213883A - Joint treatment tape and coating method using the same - Google Patents
Joint treatment tape and coating method using the sameInfo
- Publication number
- JP2003213883A JP2003213883A JP2002009317A JP2002009317A JP2003213883A JP 2003213883 A JP2003213883 A JP 2003213883A JP 2002009317 A JP2002009317 A JP 2002009317A JP 2002009317 A JP2002009317 A JP 2002009317A JP 2003213883 A JP2003213883 A JP 2003213883A
- Authority
- JP
- Japan
- Prior art keywords
- joint
- tape
- joint treatment
- treatment tape
- finishing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、建築物の内外壁
に壁板材を用いた場合に、その壁板材の板間の目地に用
いられる目地処理テープ及びそれを用いて処理された目
地部の塗装方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a joint treatment tape used for joints between walls of a wall plate material when the wall board material is used for the inner and outer walls of a building, and a joint portion treated with the joint treatment tape. It relates to the coating method.
【０００２】[0002]
【従来の技術】従来、壁板材の板間の目地に用いられる
目地処理テープには、網状のものやクラフト紙などの紙
を用いたものがある。網状の目地処理テープでは、特開
平１０−３１７６３０号公報に記載された目地処理用掩
蔽テープなどがある。2. Description of the Related Art Heretofore, there have been some joint treatment tapes used for joints between wall boards, such as a mesh-like tape and a paper such as kraft paper. As the mesh-like joint treatment tape, there is a covering tape for joint treatment described in JP-A-10-317630.
【０００３】この発明の目地処理用掩蔽テープは、網状
のテープの下面側の中央にテープ幅より狭い掩蔽フィル
ムなどを接着剤で平行状態で貼着し、その掩蔽フィルム
の下面側には接着剤層を有するものであり、コストが安
価で、使用が容易な目地処理用掩蔽テープが提供されて
いる。The covering tape for joint treatment of the present invention is a mesh tape in which a covering film, which is narrower than the tape width, is adhered in parallel to the center of the lower surface of the mesh tape, and the lower surface of the covering film is covered with the adhesive. A covering tape for joint treatment is provided that has a layer, is inexpensive, and is easy to use.
【０００４】また、クラフト紙を用いたものでは、特開
２０００−３５６０１９号公報に記載されたものなどが
ある。この発明では、建築仕上用壁材に、色違いやひび
割れ等を生じることがなく、壁材を綺麗に仕上げること
ができるものである。Further, examples of those using kraft paper include those described in Japanese Patent Laid-Open No. 2000-356019. According to the present invention, the wall material for architectural finishing can be finished neatly without causing color difference or cracking.
【０００５】[0005]
【発明が解決しようとする課題】ところが、特開平１０
−３１７６３０号公報に記載された目地処理用掩蔽テー
プでは、テープとそのテープの表面に仕上げられる塗材
又は塗料などの仕上げ材との付着性が弱く、目地部の動
きにより、仕上げ材が剥がれる場合がある。また、特開
２０００−３５６０１９号公報に記載されたものでは、
仕上げ材の乾燥過程での短期的な仕上げ材のひび割れを
防止することができるが、長期的な目地部の動きによる
仕上げ材のひび割れを防止できない場合がある。SUMMARY OF THE INVENTION However, Japanese Patent Laid-Open No. Hei 10
In the covering tape for joint treatment described in Japanese Patent No. 317630-A, adhesion between the tape and a finishing material such as a coating material or paint to be finished on the surface of the tape is weak, and the finishing material is peeled off due to movement of the joint portion. There is. Further, in the one disclosed in Japanese Patent Laid-Open No. 2000-356019,
It is possible to prevent short-term cracking of the finishing material during the drying process of the finishing material, but it may not be possible to prevent cracking of the finishing material due to long-term joint movement.
【０００６】この発明は、上記のような従来技術に存在
する問題点に着目してなされたものである。その目的と
するところは、仕上げ材との付着性に優れ、目地部の動
きによる仕上げ材のひび割れの発生を少なくすることが
できる目地処理テープ及びそれを用いた塗装方法を提供
することにある。The present invention has been made by paying attention to the problems existing in the prior art as described above. It is an object of the present invention to provide a joint treatment tape which is excellent in adhesion to a finishing material and can reduce the occurrence of cracks in the finishing material due to movement of joints, and a coating method using the joint treatment tape.
【０００７】[0007]
【課題を解決するための手段】上記の目的を達成するた
めに、請求項１に記載の発明の目地処理テープは、建築
物の壁面を構成する隣接する壁材の端縁部により形成さ
れる目地部を跨がせ覆う目地処理テープであって、その
目地処理テープが不織布であり、その表面と裏面に塗料
が塗布されているものである。In order to achieve the above-mentioned object, the joint treatment tape of the present invention according to claim 1 is formed by the edge portions of adjacent wall materials constituting the wall surface of a building. A joint treatment tape covering and covering a joint portion, wherein the joint treatment tape is a non-woven fabric, and a paint is applied to the front surface and the back surface thereof.
【０００８】請求項２に記載の発明の目地処理テープ
は、請求項１に記載の発明において、裏面の目地方向両
側に粘着部があり、その粘着部がそれぞれ別の離型紙に
覆われているものである。According to a second aspect of the present invention, in the joint treatment tape of the first aspect, there are adhesive portions on both sides of the back surface in the joint direction, and the adhesive portions are covered with different release papers. It is a thing.
【０００９】請求項３に記載の発明の目地処理テープ
は、請求項１又は請求項２に記載の発明において、前記
両端の粘着部の間隔が目地幅以上であるものである。The joint treatment tape according to a third aspect of the present invention is the tape according to the first or second aspect of the present invention, in which the gap between the adhesive portions at both ends is not less than the joint width.
【００１０】請求項４に記載の発明の目地処理テープ
は、請求項１ないし請求項３のいずれかに記載の発明に
おいて、さらに、テープ両端にテープ幅の１／２より小
さい直径の複数個の穴が設けられたものである。A joint treatment tape according to a fourth aspect of the present invention is the joint treatment tape according to any one of the first to third aspects, further comprising a plurality of tapes having a diameter smaller than ½ of the tape width at both ends of the tape. It has holes.
【００１１】請求項５に記載の発明の塗装方法は、前記
請求項１ないし請求項４のいずれかの目地処理テープを
壁面の目地部に貼り付けた後、そのテープ厚みの１．５
倍以上の塗膜を壁面に形成させることである。According to a fifth aspect of the coating method of the present invention, after the joint treatment tape according to any one of the first to fourth aspects is attached to the joint portion of the wall surface, the tape thickness is 1.5.
It is to form a coating film more than double the amount on the wall surface.
【００１２】[0012]
【発明の実施の形態】以下、この発明の実施形態を詳細
に説明する。この発明の目地処理テープは、建築物の壁
面を構成する隣接する壁材の端縁部により形成される目
地部を跨がせ覆う目地処理テープであって、その目地処
理テープが不織布であり、その表面と裏面に塗料が塗布
されているものである。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described in detail below. The joint treatment tape of the present invention is a joint treatment tape which straddles and covers the joint portion formed by the edge portions of the adjacent wall materials constituting the wall surface of the building, and the joint treatment tape is a non-woven fabric, The paint is applied to the front surface and the back surface.
【００１３】まず、壁材には、建築物の内外壁に用いら
れる石膏ボード、ＧＲＣ板、木板、スレート板、窯業系
サイディング、ＡＬＣ版、押出し成形セメント板などが
あげられる。これらの壁板は、建築物の柱、梁、胴縁な
どに釘、ネジ、ボルトや固定用の金物などの固定具によ
り固定され壁面を構成する。固定する場合には、隣接す
る壁板同士の間隔を無くした状態で固定、又は、一定の
間隔の目地を設けて固定する場合があり、壁板材の種類
などにより異なる。上記のように固定された隣接する壁
板の端縁部同士により目地部が形成される。この発明で
の目地部とは、壁板の端縁部又は壁板の端縁部と壁板を
一定の間隔を設けて固定した場合の目地とを含めた目地
処理テープを接着する部分のことである。First, examples of the wall material include gypsum board, GRC board, wood board, slate board, ceramic siding, ALC plate, and extruded cement board used for the inner and outer walls of buildings. These wall plates are fixed to a pillar, a beam, a furring strip, etc. of a building by a fixture such as a nail, a screw, a bolt or a metal for fixing to form a wall surface. When fixing, it may be fixed in a state where the space between adjacent wall plates is eliminated, or may be fixed by providing joints with a constant space, and it depends on the type of wall plate material and the like. The joint portion is formed by the edge portions of the adjacent wall plates fixed as described above. The joint portion in the present invention is a portion to which a joint treatment tape including the end edge portion of the wall plate or the joint portion when the end edge portion of the wall plate and the wall plate are fixed with a certain interval is fixed. Is.
【００１４】この形成された目地部を跨がせ覆う目地処
理テープは、不織布であり、その表面と裏面に塗料が塗
布されているものである。不織布は、織布に比べ、方向
による強度の違いが少ないため、目地処理テープの強度
が方向により異なることが少なく、安定した強度を持つ
目地処理テープを得ることができる。また、型くずれが
少なく、糸のほつれが無く、寸法安定性が良いため、目
地部の処理が行い易いものである。The joint treatment tape which covers the joint portion thus formed is a non-woven fabric, and the front surface and the back surface of the joint treatment tape are coated with a coating material. Since the non-woven fabric has less difference in strength depending on the direction than the woven fabric, the strength of the joint treatment tape is unlikely to differ depending on the direction, and a joint treatment tape having stable strength can be obtained. Further, since the shape of the joint is small, the yarn is not frayed, and the dimensional stability is good, the joint portion can be easily treated.
【００１５】さらに、厚みに斑が少ないものであるた
め、目地処理テープの表面に仕上げを行った場合には、
より薄く仕上げを行うことができる。また、紙などを用
いた場合より、強度が優れ、後述する塗料により寸法、
形状などの変化を起こすことが少ないものであるFurthermore, since the thickness is less uneven, when the surface of the joint treatment tape is finished,
A thinner finish can be achieved. In addition, the strength is superior to the case of using paper etc.
It rarely causes changes in shape, etc.
【００１６】この不織布には、ポリエステル、レーヨ
ン、ビニロン、アクリル繊維など一般的な繊維により形
成された不織布を用いることができる。これらのうち、
ポリエステル繊維により形成された不織布を用いること
が好ましい。ポリエステル繊維の不織布は、他の繊維の
不織布に比べ、水分に対する影響が少なく、寸法安定性
に優れたものであるため、目地処理が行い易く、処理さ
れた目地の耐水性を向上させることができる。As the non-woven fabric, a non-woven fabric formed of general fibers such as polyester, rayon, vinylon, acrylic fiber can be used. Of these,
It is preferable to use a non-woven fabric formed of polyester fibers. The non-woven fabric of polyester fiber is less affected by moisture than other non-woven fabrics and has excellent dimensional stability, so that the joint treatment is easy to perform and the water resistance of the treated joint can be improved. .
【００１７】目地処理テープに用いられる不織布の重量
は、単位面積あたり２０ｇ／ｍ２〜１００ｇ／ｍ２の範
囲のものが好ましく用いられる。２０ｇ／ｍ２より軽い
ものでは、強度が小さく、目地の動きにより亀裂を起こ
し、仕上げ材にひび割れを起こすことがある。１００ｇ
／ｍ２より重いものは、繊維の量が多くなり、目地部に
負荷をかけることがある。また、目地処理テープの厚み
を増し、そのテープを覆う仕上げ材を多く使うことにな
る。The weight of the nonwoven fabric used for the joint processing tape, the range of per unit area 20g / m 2 ~100g / m 2 is preferably used. If the weight is less than 20 g / m 2 , the strength is low and cracks may occur due to the movement of joints, which may cause cracks in the finishing material. 100g
If it is heavier than / m 2 , the amount of fibers is large and the joint part may be loaded. Also, the thickness of the joint treatment tape is increased, and a lot of finishing material is used to cover the tape.
【００１８】さらに、上記不織布の両面を同一の塗料に
より塗装する。不織布に塗料を塗装することにより、目
地処理テープの強度が増し、寸法安定性が向上する。さ
らに、目地処理テープの表面及び裏面が滑らかになるた
め、目地処理作業の際に用いられるテープを貼りつける
ための接着剤、粘着剤又は両面テープなどとの接着に優
れ、また、目地処理終了後に用いられる仕上げ材との付
着性が向上する。Furthermore, both surfaces of the above-mentioned non-woven fabric are coated with the same paint. By coating the non-woven fabric with paint, the strength of the joint treatment tape is increased and the dimensional stability is improved. Furthermore, since the front and back surfaces of the joint treatment tape become smooth, it is excellent in adhesion with adhesives, adhesives or double-sided tape for attaching the tape used during joint treatment, and after the joint treatment is completed. Adhesion with the finish used is improved.
【００１９】目地処理テープに用いられる塗料は、仕上
げ材との付着性が良く、接着剤などとの接着性が良いも
のであれば良い。そのため、仕上げ材と同質の塗料が好
ましい。逆に言えば、この目地処理テープを用いた場合
には、目地処理テープに塗装された塗料と同成分の塗材
又は塗料により仕上げることが好ましいことである。ま
た、壁紙などの表装材である場合には、その表装材を貼
るための接着剤と同成分の塗料を用いたものである。The paint used for the joint treatment tape may be one having good adhesion to the finishing material and good adhesion to the adhesive or the like. Therefore, a paint of the same quality as the finishing material is preferable. Conversely, when this joint treatment tape is used, it is preferable to finish with a coating material or paint having the same components as the paint applied to the joint treatment tape. Further, in the case of a cover material such as wallpaper, a paint having the same components as the adhesive for sticking the cover material is used.
【００２０】一般的に、目地処理テープを必要とする部
分がある壁面に用いられる仕上げ材、特に、塗料、塗材
においては、アクリル樹脂を主成分とするものが多いた
め、目地処理テープに用いられる塗料は、アクリル樹脂
を含有するものが好ましい。さらに、仕上げ材と目地処
理テープを壁板に貼りつける接着剤などと性質の違う樹
脂を用いる場合には、そのテープ表面には仕上げ材と同
成分の塗料により塗装を行い、裏面には、接着剤などと
同成分の塗料により塗装することも可能である。Generally, a finishing material used for a wall surface having a portion requiring a joint treatment tape, especially a paint or a coating material, which mainly contains an acrylic resin, is used for the joint treatment tape. The paint to be obtained preferably contains an acrylic resin. Furthermore, when using a resin that has different properties from the adhesive that attaches the finishing material and joint treatment tape to the wallboard, paint the surface of the tape with a paint that has the same components as the finishing material, and bond it to the back surface. It is also possible to paint with a paint of the same composition as the agent.
【００２１】また、目地処理テープに用いられる塗料の
色調は、仕上げ材と同系色のもの又は仕上げ材の色調よ
り薄い色調のものが好ましく、同色のものがより好まし
い。このような色調にすることにより、仕上げを行った
目地処理テープが透けることが少なくなる。目地処理テ
ープへの塗料の塗布方法としては、スプレーを用いた塗
装、ナイフコーター、ロールコーターなどを用いた塗装
方法など一般的な塗布方法により行うことができる。Further, the color tone of the paint used for the joint treatment tape is preferably the same color as that of the finishing material or a color tone lighter than that of the finishing material, more preferably the same color. With such a color tone, the finished joint treatment tape is less likely to be transparent. As a method of applying the coating material to the joint treatment tape, a general application method such as a coating method using a spray, a coating method using a knife coater, a roll coater or the like can be used.
【００２２】さらに、この発明の実施形態を図面に基づ
いて、より詳細に説明する。まず、図１には、目地処理
テープ１１の形態の一例を示したものである。図１のよ
うに目地処理テープ１１を一定の長さにし、巻状したも
のが目地処理の作業性及びテープの輸送に適しているた
め好ましく用いられる。また、前もって目地処理部分の
長さがわかっている場合には、目地処理テープ１１をそ
の長さに切断した短冊状のものを用いることによりより
作業性が向上するためより好ましい。Further, embodiments of the present invention will be described in more detail with reference to the drawings. First, FIG. 1 shows an example of the form of the joint treatment tape 11. As shown in FIG. 1, a joint treatment tape 11 having a constant length and wound is preferably used because it is suitable for workability of joint treatment and transportation of the tape. Further, when the length of the joint treatment portion is known in advance, it is more preferable to use a strip-shaped joint treatment tape 11 cut to the length because the workability is further improved.
【００２３】図２には、請求項２に記載された目地処理
テープ１１の形態の一例を示したものであり、図３に
は、図２に示した目地処理テープ１１の断面図を示した
ものである。この目地処理テープ１１では、壁材に接着
する目地処理テープの裏面側に粘着加工が施されている
ものであり、その粘着部１３を離型紙１２に覆ているも
のである。この離型紙１２は、目地処理テープの中心付
近で図２及び図３のように左右に分離されている。FIG. 2 shows an example of the form of the joint treatment tape 11 described in claim 2, and FIG. 3 shows a sectional view of the joint treatment tape 11 shown in FIG. It is a thing. In this joint treatment tape 11, the back surface side of the joint treatment tape adhered to the wall material is subjected to an adhesive treatment, and the adhesive portion 13 is covered with the release paper 12. The release paper 12 is separated right and left near the center of the joint treatment tape as shown in FIGS.
【００２４】このような形態の目地処理テープ１１を用
いた場合では、まず、左右どちらかの離型紙１２を剥が
しながら目地部の位置を確認しながら目地部に貼り、そ
の後、もう一方の離型紙１２を剥がしながら目地処理テ
ープを完全に接着し、目地処理作業が終了となり、目地
処理作業が容易となる。In the case of using the joint treatment tape 11 having such a form, first, the release paper 12 on either side is peeled off and the position of the joint is confirmed while the joint is applied to the joint, and then the other release paper is used. The joint treatment tape is completely adhered while peeling off 12, and the joint treatment work is completed, and the joint treatment work is facilitated.
【００２５】図４には、請求項３に記載された目地処理
テープ１１の形態の一例を示したものであり、図５に
は、図４に示した目地処理テープ１１の断面図を示した
ものである。この目地処理テープ１１は、壁材に接着す
る目地処理テープの裏面側の中央部に絶縁部ａとなる部
分を設け、その両端部に粘着加工が施されているもので
あり、それぞれの粘着部１３を別々の離型紙１２に覆て
いるものである。つまり、図２及び図３に示した目地処
理テープの粘着部１３の中央付近に一定間隔の隙間を設
け、その部分を絶縁部ａとしたものである。FIG. 4 shows an example of the form of the joint treatment tape 11 described in claim 3, and FIG. 5 shows a sectional view of the joint treatment tape 11 shown in FIG. It is a thing. The joint treatment tape 11 is such that a portion to be an insulating portion a is provided in the central portion on the back surface side of the joint treatment tape that is adhered to a wall material, and both ends thereof are subjected to adhesive processing. 13 is covered with a separate release paper 12. That is, a gap having a constant interval is provided near the center of the adhesive portion 13 of the joint treatment tape shown in FIGS. 2 and 3, and that portion is used as the insulating portion a.
【００２６】絶縁部ａを設け、この部分を壁板端縁部か
ら形成される目地に対応させ目地部に目地処理テープ１
１を貼る。この場合、上記と同様に左右どちらかの離型
紙１２を剥がしながら目地部にある目地の位置を確認し
ながら貼り、その後、もう一方の離型紙１２を剥がしな
がら目地処理テープを完全に接着する。The insulating portion a is provided, and this portion is made to correspond to the joint formed from the edge portion of the wall plate, and the joint treatment tape 1 is attached to the joint portion.
Paste 1. In this case, similarly to the above, the left or right release paper 12 is peeled off while adhering while confirming the position of the joint in the joint portion, and then the other release paper 12 is peeled off and the joint treatment tape is completely adhered.
【００２７】このように目地処理された部分では、目地
と目地処理テープの中央付近で接着されていない状態と
なる。つまり、目地と目地処理テープとが絶縁状態とな
る。この目地に目地処理テープの絶縁部ａを対応させる
ことにより、壁板が動いた場合に、その動きが絶縁部ａ
内で起こるため、目地処理テープの表面側にある仕上げ
材のひび割れをより起こりにくくすることができる。In the joint-treated portion as described above, the joint and the joint treatment tape are not bonded to each other near the center. That is, the joint and the joint treatment tape are in an insulating state. By associating the joint portion with the insulating portion a of the joint treatment tape, when the wall board moves, the movement of the insulating portion a
Since it occurs inside, it is possible to make cracking of the finishing material on the surface side of the joint treatment tape less likely to occur.
【００２８】両端の粘着部の間隔、つまり、絶縁部ａの
幅は、目地幅以上であることが好ましい。目地幅以上の
間隔が確保させることにより、目地部の目地を絶縁する
ことができ、目地での動きに十分対応することができ、
仕上げ材のひび割れをより一層起こりにくくすることが
できる。また、粘着部１３の幅は、壁材への接着が十分
であり、作業効率に影響を及ぼさない範囲であれば良
い。具体的には、５ｍｍ〜５０ｍｍの範囲内であれば壁
材への接着が十分であり、作業効率に影響が無いもので
ある。The distance between the adhesive portions at both ends, that is, the width of the insulating portion a is preferably equal to or larger than the joint width. By securing a space equal to or larger than the joint width, it is possible to insulate the joints in the joints, and it is possible to respond sufficiently to movements in the joints.
It is possible to make cracks in the finishing material less likely to occur. Further, the width of the adhesive portion 13 may be within a range in which adhesion to the wall material is sufficient and work efficiency is not affected. Specifically, if the thickness is in the range of 5 mm to 50 mm, the adhesion to the wall material is sufficient and the work efficiency is not affected.
【００２９】さらに、図６には、請求項４に記載された
目地処理テープの形態の一例を示したものであり、図７
には、図６に示した目地処理テープの断面図を示したも
のである。この目地処理テープ１１は、壁材に接着する
目地処理テープの裏面側の中央部に絶縁部ａを設け、そ
の両端部に粘着加工が施されているものであり、それぞ
れの粘着部１３を別々の離型紙１２に覆ているもので、
その粘着部１３及び離型紙１２に複数個の穴１４が空い
ている。つまり、図４及び図５に示した目地処理テープ
の両端の粘着部１３及び離型紙１２に穴１４が空いてい
るものである。Further, FIG. 6 shows an example of the form of the joint treatment tape according to claim 4, and FIG.
7 shows a cross-sectional view of the joint treatment tape shown in FIG. This joint treatment tape 11 is one in which an insulating portion a is provided in the central portion on the back surface side of the joint treatment tape to be adhered to a wall material, and both ends thereof are subjected to adhesive processing, and each adhesive portion 13 is separately provided. Which is covered with the release paper 12 of
A plurality of holes 14 are formed in the adhesive portion 13 and the release paper 12. That is, the holes 14 are formed in the adhesive portions 13 and the release paper 12 at both ends of the joint treatment tape shown in FIGS. 4 and 5.
【００３０】この穴14は、目地処理テープを貼った後に
行う仕上げ材がその穴１４を通じて壁板に付着し、仕上
げを行った後の目地部の強度を向上させ、仕上げ材のひ
び割れの発生をより少なくすることができる。さらに
は、仕上げ材の剥落を防止することができる。前記穴１
４の直径は、目地処理テープの幅の１／２より小さいも
のである。１／２以上である場合には、目地処理テープ
の強度が低下することがある。また、穴１４を空ける加
工作業においてもその作業性が低下する。In this hole 14, the finishing material to be applied after the joint treatment tape is attached adheres to the wall board through the hole 14 to improve the strength of the joint portion after finishing, and to prevent the occurrence of cracks in the finishing material. Can be less. Furthermore, the finishing material can be prevented from peeling off. The hole 1
The diameter of 4 is smaller than 1/2 of the width of the joint treatment tape. If it is ½ or more, the strength of the joint treatment tape may decrease. In addition, the workability is also reduced in the processing work for making the holes 14.
【００３１】また、目地処理テープに粘着部１３が施さ
れている場合には、その粘着部１３の幅より小さく、さ
らに好ましくは、その粘着部１３の幅の１／４より小さ
い半径の穴１４が良い。このことにより、粘着剤と仕上
げ材とによる接着効果により、より目地部の強度を向上
させることができる。前記穴１４の形状は、円形である
必要は無く、楕円及び四角、三角などの多角形などであ
っても良いが、穴１４を空ける加工作業の容易性より円
形のものが好ましい。When the joint treatment tape is provided with the adhesive portion 13, the hole 14 having a radius smaller than the width of the adhesive portion 13, and more preferably smaller than 1/4 of the width of the adhesive portion 13. Is good. As a result, the strength of the joint can be further improved by the adhesive effect of the adhesive and the finishing material. The shape of the hole 14 does not have to be circular, and may be an ellipse, a polygon such as a quadrangle, a triangle, or the like, but a circular shape is preferable in view of the ease of the working operation for making the hole 14.
【００３２】次に、前記のように構成された目地処理テ
ープを用いた塗装方法を説明する。図８では、目地処理
テープを用いた目地部の構造の一例を示したものであ
る。この目地部の構造は、胴縁１６に壁板１５を固定
し、その壁板１５の端縁部により目地１７を形成したも
のである。目地には、パテ、シーリング材などの目地材
が挿入されている。Next, a coating method using the joint treatment tape having the above structure will be described. FIG. 8 shows an example of the structure of the joint portion using the joint treatment tape. In the structure of the joint portion, the wall plate 15 is fixed to the furring strip 16, and the joint 17 is formed by the end edge portion of the wall plate 15. A joint material such as putty or a sealing material is inserted in the joint.
【００３３】この目地部に図６に示された目地処理テー
プを接着する。接着した後、目地処理テープに用いられ
た塗料と同質の仕上げ材１８により仕上げを行った。こ
の仕上げ材は、好ましく用いられる塗材である。この目
地処理テープの絶縁部ａの幅は、目地１７の幅ｂより大
きいものである。The joint treatment tape shown in FIG. 6 is adhered to the joint portion. After the bonding, the finishing material 18 of the same quality as the paint used for the joint treatment tape was used for finishing. This finishing material is a coating material that is preferably used. The width of the insulating portion a of the joint treatment tape is larger than the width b of the joint 17.
【００３４】前記塗材は、壁紙、塗料などの仕上げ材に
比べ、厚膜の仕上げを行うことができる。厚膜の塗膜を
容易に得ることができるため、目地処理に用いられた目
地処理テープの厚みの１．５倍以上の塗膜を壁面に形成
させることが容易に行うことができる。壁面に塗膜を形
成させる塗装方法としては、スプレー、塗装用ローラ
ー、鏝などの一般的な塗装器具を用いて行うことがで
き、また、これらの塗装器具を複数用いて行うことがで
きる。The coating material is capable of finishing a thick film as compared with a finishing material such as wallpaper or paint. Since a thick coating film can be easily obtained, it is possible to easily form a coating film on the wall surface that is 1.5 times or more the thickness of the joint treatment tape used for joint treatment. As a coating method for forming a coating film on a wall surface, a general coating tool such as a sprayer, a coating roller, and a trowel can be used, and a plurality of these coating tools can be used.
【００３５】この目地処理テープの厚みの１．５倍以上
の塗膜を壁面に形成させることにより、壁板により構成
される壁面を均一に仕上げることができ、仕上げられた
壁面に存在する目地を隠すことができる。壁板の目地を
隠すことにより、壁面を一枚の壁面のように見せること
ができる。また、この発明の目地処理テープを用いて、
目地部の処理を行い、そのテープ厚みの１．５倍以上の
塗膜により仕上げを行うことで、壁板の動きが発生した
場合であっても仕上げ材にひび割れが生じることが無
く、壁面を一枚の壁面のように見せることができる。By forming a coating film having a thickness of 1.5 times or more the thickness of the joint treatment tape on the wall surface, the wall surface constituted by the wall plate can be finished uniformly, and the joints existing on the finished wall surface can be formed. Can be hidden. By hiding the joints of the wallboard, the wall can be made to look like a single wall. Further, using the joint treatment tape of the present invention,
By treating the joints and finishing with a coating film that is 1.5 times the tape thickness or more, even if the wall plate moves, the finish material will not crack and the wall surface You can make it look like a wall.
【００３６】以上のように、この実施形態によれば次の
ような効果が発揮される。
・ 建築物の壁面を構成する隣接する壁材の端縁部によ
り形成される目地部を跨がせ覆う目地処理テープであっ
て、その目地処理テープが不織布であり、その表面と裏
面に塗料が塗布されているものであることにより、仕上
げ材との付着性に優れ、目地部の動きによる仕上げ材の
ひび割れの発生を少なくすることができるものである。As described above, according to this embodiment, the following effects are exhibited. -A joint treatment tape that covers the joint portion formed by the edge portions of the adjacent wall materials that form the wall surface of the building, the joint treatment tape being a non-woven fabric, and the coating on the front surface and the back surface of the joint treatment tape. By being applied, the adhesiveness to the finishing material is excellent, and the occurrence of cracks in the finishing material due to the movement of the joints can be reduced.
【００３７】・ 裏面の目地方向両側に粘着部があり、
その粘着部がそれぞれ別の離型紙に覆われているもので
あることにより、左右どちらかの離型紙を剥がしながら
目地部の位置を確認しながら目地部に貼り、その後、も
う一方の離型紙を剥がしながら目地処理テープを完全に
接着し、目地処理作業が終了となり、目地処理作業が容
易となる。-There are adhesive parts on both sides of the back surface in the joint direction,
Since the adhesive parts are covered with different release papers, peel off either the left or right release paper and check the position of the joint part while sticking it on the joint part, and then the other release paper. The joint treatment tape is completely adhered while peeling off, and the joint treatment work is completed, and the joint treatment work becomes easy.
【００３８】・ 前記両端の粘着部の間隔が目地幅以上
であることにより、目地と目地処理テープとが絶縁部を
形成し、壁板が動いた場合に、その動きが絶縁部内で起
こるため、目地処理テープの表面側にある仕上げ材のひ
び割れをより起こりにくくすることができる。Since the space between the adhesive parts at both ends is equal to or larger than the joint width, the joint and the joint treatment tape form an insulating part, and when the wall plate moves, the movement occurs in the insulating part. It is possible to make cracking of the finishing material on the surface side of the joint treatment tape less likely to occur.
【００３９】・ テープ両端にテープ幅の１／２より小
さい直径の複数個の穴が設けられたものであることによ
り、仕上げ材がその穴を通じて壁板に付着し、仕上げを
行った後の目地部の強度を向上させ、仕上げ材のひび割
れの発生をより少なくすることができる。さらには、仕
上げ材の剥落を防止することができる。Since the plurality of holes having a diameter smaller than ½ of the tape width are provided at both ends of the tape, the finishing material adheres to the wall plate through the holes and the joint after finishing is performed. It is possible to improve the strength of the portion and reduce the occurrence of cracks in the finishing material. Furthermore, the finishing material can be prevented from peeling off.
【００４０】・ 前記請求項１ないし請求項４のいずれ
かの目地処理テープを壁面の目地部に貼り付けた後、そ
のテープ厚みの１．５倍以上の塗膜を壁面に形成させる
ことであることにより、壁板により構成される壁面を均
一に仕上げることができ、仕上げられた壁面に存在する
目地を隠すことができ、さらに、壁板の動きが発生した
場合であっても仕上げ材にひび割れが生じることが無
く、壁面を一枚の壁面のように見せることができる。After applying the joint treatment tape according to any one of claims 1 to 4 to the joint portion of the wall surface, a coating film having a thickness of 1.5 times or more of the tape thickness is formed on the wall surface. This makes it possible to evenly finish the wall surface composed of wallboards, hide the joints existing on the finished wallboard, and even when the wallboard moves, the finish material is cracked. The wall surface can be made to look like a single wall surface without causing a crack.
【００４１】・ 前記不織布がポリエステル繊維により
形成された不織布であることにより、水分に対する影響
が少なく、寸法安定性に優れたものであり、さらに、目
地処理が行い易く、処理された目地の耐水性を向上させ
ることができる。Since the non-woven fabric is a non-woven fabric formed of polyester fiber, it has little influence on moisture and is excellent in dimensional stability. Furthermore, joint treatment is easy to perform, and the water resistance of the treated joint is high. Can be improved.
【００４２】・ 前記不織布の重量はが単位面積あたり
２０ｇ／ｍ２〜１００ｇ／ｍ２の範囲のものであること
により、目地処理テープの強度があり、目地の動きによ
り亀裂を起こし、仕上げ材にひび割れを起こすことが少
ないものである。また、目地部に負荷をかけることがな
く、そのテープを覆う仕上げ材を少なくすることができ
る。[0042] By Weight of the nonwoven fabric is one of the range of per unit area 20g / m 2 ~100g / m 2 , there is the strength of the joint processing tape, causing a crack by the movement of joints, in the finish It rarely cracks. Further, it is possible to reduce the amount of finishing material that covers the tape without applying a load to the joint portion.
【００４３】・ 粘着部の幅が５ｍｍ〜５０ｍｍの範囲
内であることにより、壁材への接着が十分であり、作業
効率に影響が無いものである。When the width of the adhesive portion is in the range of 5 mm to 50 mm, the adhesion to the wall material is sufficient and the work efficiency is not affected.
【００４４】・ 目地処理テープに粘着部が施されてい
る場合であって、その粘着部１３の幅より小さく、さら
に好ましくは、その粘着部１３の幅の１／４より小さい
半径の穴１４であることにより、粘着剤と仕上げ材によ
る接着効果により、より目地部の強度を向上させること
ができる。In the case where the joint treatment tape is provided with an adhesive portion, the width of the adhesive portion 13 is smaller than the width of the adhesive portion 13, and more preferably, a hole 14 having a radius smaller than ¼ of the width of the adhesive portion 13. As a result, the strength of the joint can be further improved by the adhesive effect of the adhesive and the finishing material.
【００４５】次に、前記実施形態から把握できる技術的
思想について以下に記載する。
・ 前記不織布がポリエステル繊維により形成されたも
のであることを特徴とする請求項１ないし請求項４のい
ずれかに記載の目地処理テープ。このことにより、水分
に対する影響が少なく、寸法安定性に優れたものであ
り、さらに、目地処理が行い易く、処理された目地の耐
水性を向上させることができる。Next, the technical idea which can be understood from the above-mentioned embodiment will be described below. The joint treatment tape according to any one of claims 1 to 4, wherein the non-woven fabric is formed of polyester fiber. As a result, it has little influence on water content, is excellent in dimensional stability, is easy to perform joint treatment, and can improve the water resistance of the treated joint.
【００４６】・ 前記不織布の重量はが単位面積あたり
２０ｇ／ｍ２〜１００ｇ／ｍ２の範囲であることことを
特徴とする請求項１ないし請求項４のいずれかに記載の
目地処理テープ。このことにより、目地処理テープの強
度があり、目地の動きにより亀裂を起こし、仕上げ材に
ひび割れを起こすことが少ないものである。また、目地
部に負荷をかけることがなく、そのテープを覆う仕上げ
材を少なくすることができる。[0046] - the joint processing tape according to any one of claims 1 to 4 weight of the nonwoven fabric is characterized in that it is in the range of 20g / m 2 ~100g / m 2 per unit area. As a result, the joint treatment tape is strong, and the movement of the joint causes a crack, and the finish material is less likely to crack. Further, it is possible to reduce the amount of finishing material that covers the tape without applying a load to the joint portion.
【００４７】・ 前記粘着部の幅が５ｍｍ〜５０ｍｍの
範囲内であることを特徴とする請求項２ないし請求項４
のいずれかに記載の目地処理テープ。このことにより、
壁材への接着が十分であり、作業効率に影響が無いもの
である。The width of the adhesive portion is in the range of 5 mm to 50 mm, wherein the adhesive portion has a width of 5 mm to 50 mm.
The joint treatment tape described in any one of 1. By this,
Adhesion to the wall material is sufficient and work efficiency is not affected.
【００４８】・ 前記穴が前記粘着部の幅より小さく、
さらには、粘着部の幅の１／４より小さいことを特徴と
す請求項４に記載の目地処理テープ。このことにより、
粘着剤と仕上げ材とによる接着効果により、より目地部
の強度を向上させることができる。The hole is smaller than the width of the adhesive portion,
Furthermore, the joint treatment tape according to claim 4, wherein the joint treatment tape is smaller than 1/4 of the width of the adhesive portion. By this,
The adhesive effect of the adhesive and the finishing material can further improve the strength of the joint portion.
【００４９】[0049]
【発明の効果】この発明は、以上のように構成されてい
るため、次のような効果を奏する。請求項１に記載の発
明の目地処理テープによれば、仕上げ材との付着性に優
れ、目地部の動きによる仕上げ材のひび割れの発生を少
なくすることができるものである。Since the present invention is constructed as described above, it has the following effects. According to the joint treatment tape of the invention described in claim 1, the adhesiveness to the finishing material is excellent, and the occurrence of cracks in the finishing material due to the movement of the joint portion can be reduced.
【００５０】請求項２に記載の発明の目地処理テープに
よれば、請求項１に記載の発明の効果に加え、左右どち
らかの離型紙を剥がしながら目地部の位置を確認しなが
ら目地部に貼り、その後、もう一方の離型紙を剥がしな
がら目地処理テープを完全に接着し、目地処理作業が終
了となり、目地処理作業が容易となる。According to the joint treatment tape of the invention described in claim 2, in addition to the effect of the invention described in claim 1, the joint paper is applied to the joint portion while peeling off either the right or left release paper and confirming the position of the joint portion. After the sticking, the joint release tape is completely adhered while the other release paper is peeled off, and the joint treatment work is completed and the joint treatment work becomes easy.
【００５１】請求項３に記載の発明の目地処理テープに
よれば、請求項１又は請求項２に記載の発明の効果に加
え、目地と目地処理テープとが絶縁部を形成し、壁板が
動いた場合に、その動きが絶縁部内で起こるため、目地
処理テープの表面側にある仕上げ材のひび割れをより起
こりにくくすることができる。According to the joint treatment tape of the invention described in claim 3, in addition to the effect of the invention described in claim 1 or 2, the joint and the joint treatment tape form an insulating portion, and the wall plate is When it moves, the movement occurs in the insulating portion, so that cracking of the finishing material on the surface side of the joint treatment tape can be made less likely to occur.
【００５２】請求項４に記載の発明の目地処理テープに
よれば、請求項ないしは請求項３のいずれかに記載の発
明の効果に加え、仕上げ材がその穴を通じて壁板に付着
し、仕上げを行った後の目地部の強度を向上させ、仕上
げ材のひび割れの発生をより少なくすることができる。
さらには、仕上げ材の剥落を防止することができる。According to the joint treatment tape of the invention described in claim 4, in addition to the effect of the invention described in any one of claims or 3, the finishing material adheres to the wall board through the hole to finish the surface. It is possible to improve the strength of the joint after the treatment and reduce the occurrence of cracks in the finishing material.
Furthermore, the finishing material can be prevented from peeling off.
【００５３】請求項５に記載の発明の塗装方法によれ
ば、壁板により構成される壁面を均一に仕上げることが
でき、仕上げられた壁面に存在する目地を隠すことがで
き、さらに、壁板の動きが発生した場合であっても仕上
げ材にひび割れが生じることが無く、壁面を一枚の壁面
のように見せることができる。According to the coating method of the fifth aspect of the present invention, the wall surface constituted by the wall board can be finished uniformly, and the joints existing on the finished wall surface can be hidden. Even if such a movement occurs, the finishing material does not crack and the wall surface can be made to look like a single wall surface.
【図１】 目地処理テープの形態の一例を示したものFIG. 1 shows an example of the form of a joint treatment tape.
【図２】 目地処理テープの形態の一例を示したものFIG. 2 shows an example of the form of a joint treatment tape.
【図３】 図２に示した目地処理テープの断面図を示し
たものFIG. 3 shows a cross-sectional view of the joint treatment tape shown in FIG.
【図４】 目地処理テープの形態の一例を示したものFIG. 4 shows an example of the form of a joint treatment tape.
【図５】 図４に示した目地処理テープの断面図を示し
たもの5 is a cross-sectional view of the joint treatment tape shown in FIG.
【図６】 目地処理テープの形態の一例を示したものFIG. 6 shows an example of the form of a joint treatment tape.
【図７】 図６に示した目地処理テープの断面図を示し
たものFIG. 7 shows a cross-sectional view of the joint treatment tape shown in FIG.
【図８】 目地処理テープを用いた目地部の構造の一例
を示したものFIG. 8 shows an example of a structure of a joint portion using a joint treatment tape.
１１…目地処理テープ。１２…離型紙。１３…粘着部。
１４…穴。１５…壁板。１６…胴縁。１７…目地。１８
…仕上げ材。ａ…絶縁部。ｂ…目地幅。11 ... Joint treatment tape. 12 ... Release paper. 13 ... Adhesive part.
14 ... hole. 15 ... Wall plate. 16 ... Furry edge. 17 ... Joint. 18
… Finishing materials. a ... Insulating part. b ... Joint width.
Claims (5)
端縁部により形成される目地部を跨がせ覆う目地処理テ
ープであって、その目地処理テープが不織布であり、そ
の表面と裏面に塗料が塗布されていることを特徴とする
目地処理テープ。1. A joint treatment tape which straddles and covers a joint portion formed by edges of adjacent wall materials constituting a wall surface of a building, the joint treatment tape being a non-woven fabric, and a surface thereof. A joint treatment tape having a back surface coated with paint.
の粘着部がそれぞれ別の離型紙に覆われていることを特
徴とする請求項１に記載の目地処理テープ。2. The joint treatment tape according to claim 1, wherein there are adhesive portions on both sides of the back surface in the joint direction, and the adhesive portions are covered with different release papers.
あることを特徴とする請求項１又は請求項２に記載の目
地処理テープ。3. The joint treatment tape according to claim 1, wherein the gap between the adhesive portions on both ends is equal to or larger than the joint width.
より小さい直径の複数個の穴が設けられたことを特徴と
する請求項１ないし請求項３のいずれかに記載の目地処
理テープ。4. The tape width is ½ of both ends of the tape.
The joint treatment tape according to any one of claims 1 to 3, wherein a plurality of holes having a smaller diameter are provided.
の目地処理テープを壁面の目地部に貼り付けた後、その
テープ厚みの１．５倍以上の塗膜を壁面に形成させるこ
とを特徴とする塗装方法。5. After applying the joint treatment tape according to any one of claims 1 to 4 to a joint portion of a wall surface, a coating film having a thickness 1.5 times or more of the tape thickness is formed on the wall surface. Characteristic coating method.