JP2003171651A - Self-adhesive rubber gasket - Google Patents
Self-adhesive rubber gasketInfo
- Publication number
- JP2003171651A JP2003171651A JP2001372240A JP2001372240A JP2003171651A JP 2003171651 A JP2003171651 A JP 2003171651A JP 2001372240 A JP2001372240 A JP 2001372240A JP 2001372240 A JP2001372240 A JP 2001372240A JP 2003171651 A JP2003171651 A JP 2003171651A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- self
- adhesive
- gasket
- rubber gasket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明が属する技術分野】本発明は自己接着性を有する
ゴム組成物に関し、このゴム組成物からなるゴムガスケ
ットに関する。TECHNICAL FIELD The present invention relates to a rubber composition having a self-adhesive property, and a rubber gasket made of this rubber composition.
【０００２】[0002]
【従来技術の内容】部材の繋ぎ部を密封するガスケット
は、ゴム弾性と接着性とを併せ持つ材料とすることによ
り、防音、防振性を確保すると同時にシール性能を飛躍
的に向上させることができる。また、接着性をガスケッ
トに持たしめれば、低荷重の締付けでシール性を確保す
ることができるものとなる。2. Description of the Related Art A gasket for sealing a connecting portion of members is made of a material having both rubber elasticity and adhesiveness, so that it is possible to secure soundproofing and vibrationproofing, and at the same time dramatically improve the sealing performance. . Further, if the gasket has adhesiveness, it becomes possible to secure the sealing property by tightening with a low load.
【０００３】[0003]
【発明が解決しようとする課題】従来の弾性のあるゴム
ガスケットは、接着力によるシール性向上を期待してお
らず、むしろゴム材の材質特性と形状を含むガスケット
装着構造でシール性能を確保してきていた。また、従来
にある接着性液状ガスケットは、圧着により防振効果を
得るにはゴム層が薄くなりすぎることや、多くがシリコ
ーンゴム組成であるため使用環境による大きな制限があ
った。The conventional elastic rubber gasket is not expected to improve the sealing performance due to the adhesive force, but rather, the sealing performance is ensured by the gasket mounting structure including the material characteristics and shape of the rubber material. Was there. Further, in the conventional adhesive liquid gasket, the rubber layer is too thin to obtain the vibration damping effect by pressure bonding, and since most of them are of silicone rubber composition, they are largely limited by the use environment.
【０００４】本発明はこのようなことに鑑みて、ゴム弾
性と接着性とを併せ持つガスケット材料を開発し、防
音、防振性を確保すると同時にシール性能を飛躍的に向
上させることを目的としている。In view of the above, the present invention aims to develop a gasket material having both rubber elasticity and adhesiveness to ensure soundproofing and vibrationproofing and to dramatically improve the sealing performance. .
【０００５】[0005]
【課題を解決するための手段】本発明を詳しく説明する
と、自己接着性ゴムガスケットであって、硬化触媒によ
り接着性とゴム弾性を発揮する付加型シリコーンゴムに
て自己接着性ゴムガスケットを形成し、前記自己接着性
ゴムガスケットと同類のゴム材か、あるいはこれとは異
なるニトリルゴムまたは、水素化ニトリルゴムあるい
は、エチレンプロピレンゴム、アクリルゴム、エチレン
アクリルゴム、シリコーンゴム、フッ素ゴムのいずれか
からなるゴム材の表面に前記自己接着性ゴムガスケット
を付着せしめ、その後、低応力と熱処理若しくは熱履歴
によりアルミニウム材とか鉄材あるいはステンレス材等
の金属材あるいはポリアミド樹脂（ナイロン）あるいは
ポリプロピレン等の合成樹脂材へ接着硬化せしめること
を特徴としている。The present invention will be described in detail. A self-adhesive rubber gasket is formed by an addition type silicone rubber that exhibits adhesiveness and rubber elasticity by a curing catalyst. , A rubber material similar to the self-adhesive rubber gasket, or a nitrile rubber different from this, a hydrogenated nitrile rubber, or ethylene propylene rubber, acrylic rubber, ethylene acrylic rubber, silicone rubber, or fluororubber. The self-adhesive rubber gasket is attached to the surface of a rubber material, and then aluminum material, iron material, metal material such as stainless steel material, or synthetic resin material such as polyamide resin (nylon) or polypropylene by low stress and heat treatment or heat history. It is characterized by adhesive hardening.
【０００６】また、自己接着性ゴムガスケットであっ
て、アミノ系あるいはビニル系シランカップリング剤を
導入した、シリコーンゴム、アクリルゴム、エチレンア
クリルゴムあるいはフッ素ゴムのいずれかにて自己接着
性ゴムガスケットを形成し、前記自己接着性ゴムガスケ
ットを低応力と熱処理若しくは熱履歴によりアルミニウ
ム材とか鉄材あるいはステンレス材等の金属材あるいは
ポリアミド樹脂（ナイロン）あるいはポリプロピレン等
の合成樹脂材へ接着硬化せしめることと、または前記自
己接着性ゴムガスケットと同類のゴム材か、あるいはこ
れとは異なるニトリルゴムまたは、水素化ニトリルゴム
あるいは、エチレンプロピレンゴム、アクリルゴム、エ
チレンアクリルゴム、シリコーンゴム、フッ素ゴムのい
ずれかからなるゴム材の表面に前記自己接着性ゴムガス
ケットを付着せしめ、その後、低応力と熱処理若しくは
熱履歴によりアルミニウム材とか鉄材あるいはステンレ
ス材等の金属材あるいはポリアミド樹脂（ナイロン）あ
るいはポリプロピレン等の合成樹脂材へ接着硬化せしめ
ることを特徴としている。A self-adhesive rubber gasket made of any one of silicone rubber, acrylic rubber, ethylene acrylic rubber or fluororubber into which an amino-based or vinyl-based silane coupling agent is introduced is used. Forming and adhering the self-adhesive rubber gasket to a metal material such as an aluminum material, an iron material or a stainless material, or a synthetic resin material such as polyamide resin (nylon) or polypropylene by low stress and heat treatment or heat history, or A rubber material similar to the self-adhesive rubber gasket, or a nitrile rubber different from this, a hydrogenated nitrile rubber, or a rubber made of ethylene propylene rubber, acrylic rubber, ethylene acrylic rubber, silicone rubber, or fluororubber. The self-adhesive rubber gasket is attached to the surface of, and then adhesively cured to a metal material such as aluminum material, iron material or stainless steel material, or synthetic resin material such as polyamide resin (nylon) or polypropylene by low stress and heat treatment or heat history. It is characterized by being busy.
【０００７】また、自己接着性ゴムガスケットであっ
て、カルボキシル基を有する化合物を添加した、ニトリ
ルゴムまたは、水素化ニトリルゴムあるいは、エチレン
プロピレンゴムなどの組成物のいずれかにて接着性ゴム
組成物を形成し、金属材あるいは合成樹脂材へ接着硬化
せしめるとか、または前記自己接着性ゴムガスケットと
同類のゴム材か、あるいはこれとは異なるニトリルゴム
または、水素化ニトリルゴムあるいは、エチレンプロピ
レンゴム、アクリルゴム、エチレンアクリルゴム、シリ
コーンゴム、フッ素ゴムのいずれかからなるゴム材の表
面に前記自己接着性ゴムガスケットを付着せしめ、その
後、金属材あるいは合成樹脂材へ接着硬化せしめること
を特徴としている。Further, a self-adhesive rubber gasket, which is an adhesive rubber composition made of any of nitrile rubber, hydrogenated nitrile rubber, ethylene propylene rubber and the like, to which a compound having a carboxyl group is added. Of the above-mentioned self-adhesive rubber gasket, or a nitrile rubber different from this, a hydrogenated nitrile rubber, an ethylene propylene rubber, or an acrylic resin. The self-adhesive rubber gasket is attached to the surface of a rubber material made of rubber, ethylene acrylic rubber, silicone rubber, or fluororubber, and then adhered and cured to a metal material or a synthetic resin material.
【０００８】なお、前記カルボキシル基を有する化合物
は、アクリル酸、メタクリル酸、マレイン酸及びそれら
の変性体を添加してなることを特徴としている。The compound having a carboxyl group is characterized by adding acrylic acid, methacrylic acid, maleic acid and modified products thereof.
【０００９】[0009]
【発明の実施の形態】以下、本発明でなる自己接着性ゴ
ムガスケットの好ましい実施形態を図面を基に説明す
る。BEST MODE FOR CARRYING OUT THE INVENTION Preferred embodiments of the self-adhesive rubber gasket according to the present invention will be described below with reference to the drawings.
【００１０】本発明の自己接着性ゴムガスケット１は、
アミノ系あるいはビニル系シランカップリング剤を導入
したシリコーンゴムとか、アクリルゴム、エチレンアク
リルゴムあるいはフッ素ゴムのいずれかにて形成するこ
とができ、さらには、カルボキシル基を有する化合物を
添加した、ニトリルゴムまたは、水素化ニトリルゴムあ
るいは、エチレンプロピレンゴムなどの組成物のいずれ
かにて形成され、このようにして形成された自己接着性
ゴムガスケット１を単体（図示していない）にて金属材
あるいは合成樹脂材へ接着硬化せしめる。The self-adhesive rubber gasket 1 of the present invention comprises:
Nitrile rubber that can be formed of silicone rubber introduced with an amino- or vinyl-based silane coupling agent, acrylic rubber, ethylene acrylic rubber, or fluororubber, and is further added with a compound having a carboxyl group. Alternatively, the self-adhesive rubber gasket 1 formed of either a hydrogenated nitrile rubber or a composition such as ethylene propylene rubber, and the self-adhesive rubber gasket 1 formed in this manner can be used alone (not shown) as a metal material or a synthetic material. Adhesive to resin material and cured.
【００１１】このような単体で自己接着性ゴムガスケッ
ト１を用いることから、図１では前記自己接着性ゴムガ
スケット１をゴム基材２の表面へ配置しており、ここで
は片面密着させるべく片方の表面に設けているが、両面
接着を望めば（多くの場合がこれに当たる）図２に示す
ように両側面に該自己接着性ゴムガスケット１を設ける
ことも可能であり、フィルム状あるいはシート状に形成
した自己接着性ゴムガスケットＡを１を貼りつけとか溶
融した液状物を塗布あるいはスクリーン印刷または転写
などすることによって形成される。Since the self-adhesive rubber gasket 1 is used alone as described above, the self-adhesive rubber gasket 1 is arranged on the surface of the rubber substrate 2 in FIG. Although it is provided on the surface, if it is desired to adhere to both sides (this is the case in most cases), it is possible to provide the self-adhesive rubber gaskets 1 on both sides as shown in FIG. The formed self-adhesive rubber gasket A is formed by pasting 1 or by applying a molten liquid material, screen printing or transfer.
【００１２】この自己接着性ゴムガスケット１を接着硬
化せしめるには、アルミニウム材、ステンレス材あるい
は鉄材などの金属材か、あるいはポリアミド樹脂（ナイ
ロン）、ポリプロピレンなどの合成樹脂材へ、低応力と
熱処理もしくは熱履歴により接着し、自らはゴム弾性体
となって硬化形成される。In order to bond and cure the self-adhesive rubber gasket 1, a metal material such as an aluminum material, a stainless material or an iron material, or a synthetic resin material such as polyamide resin (nylon) or polypropylene is treated with low stress and heat treatment. It adheres due to heat history and becomes a rubber elastic body and is hardened and formed.
【００１３】一方、前記のように自己接着性ゴムガスケ
ット１をゴム基材２の表面へ付着せしめることなく、図
３に示すように前記ゴム基材２へ自己接着性ゴムガスケ
ット１を混合せしめて形成することも自在であり、この
混合にあっては内部での粘着効果により強い一体化が果
たされ、自己接着性ゴムガスケット１′の物性の低下を
一切きたすものでなく、勿論接着性能において些かも低
下するものでない。On the other hand, as shown in FIG. 3, the self-adhesive rubber gasket 1 is mixed with the rubber base material 2 without adhering the self-adhesive rubber gasket 1 to the surface of the rubber base material 2 as described above. It can be formed freely, and in this mixing, strong adhesion is achieved due to the adhesive effect inside, and it does not cause any deterioration of the physical properties of the self-adhesive rubber gasket 1 '. It doesn't decrease a little.
【００１４】また、前記ゴム基材２へ発泡剤を含む自己
接着性ゴムガスケット１を混合せしめて形成した自己接
着性ゴムガスケット１´を、図４に示すように熱処理を
なさしめて発泡形成せしめることも可能であり、この発
泡と自己接着によりさらなる強力なゴム弾性と密封性を
得ることができる。Further, as shown in FIG. 4, the self-adhesive rubber gasket 1'formed by mixing the self-adhesive rubber gasket 1 containing a foaming agent with the rubber base material 2 is heat-treated to form foam. It is also possible, and this foaming and self-adhesion can provide stronger rubber elasticity and sealing property.
【００１５】[0015]
【実施例】本発明の実施では、アクリルゴム（ＡＣ
Ｍ）、フッ素ゴム（ＦＫＭ）、シリコーンゴム（ＶＭ
Ｑ）のいずれかのコンパウンドにアミノシランカップリ
ング剤またはビニルシランカップリング剤を０．１〜３
ｐｈｒ添加して自己接着性ゴムガスケット１を形成し
た。このゴム材料の比較表を以下の表１に示す。EXAMPLES In the practice of the present invention, acrylic rubber (AC
M), fluororubber (FKM), silicone rubber (VM
Aminosilane coupling agent or vinylsilane coupling agent is added to any of the compounds of Q) in an amount of 0.1 to 3
phr was added to form a self-adhesive rubber gasket 1. A comparison table of this rubber material is shown in Table 1 below.
【００１６】[0016]
【表１】
上記試料作製条件は図５に示す。また、ここでの接着強
度測定方法は図６に示す。[Table 1] The sample preparation conditions are shown in FIG. The method for measuring the adhesive strength here is shown in FIG.
【００１７】本発明では、接着性が付与された自己接着
性ゴムガスケット１あるいは１´の片面を、遠赤外線な
どの熱処理や油あるいは離型剤等の表面処理を施すこと
によってその接着性を抑制し、片面だけを接着すること
でシール性を確保しつつメンテナンス性をも得ることが
出来るものとなる。（例えば、エンジンのヘッドカバー
ガスケットあるいはオイルフィラーガスケットなどに適
するものとなる。）In the present invention, one side of the self-adhesive rubber gasket 1 or 1'provided with adhesiveness is subjected to heat treatment with far infrared rays or surface treatment with oil or a release agent to suppress the adhesiveness. However, by adhering only one side, it is possible to obtain maintainability while ensuring sealing performance. (For example, it is suitable for an engine head cover gasket or an oil filler gasket.)
【００１８】[0018]
【発明の効果】本発明による自己接着性ゴムガスケット
１は、金属材あるいは合成樹脂材のフランジへ直接接着
されるものとなり、その接着面のシール性を確実に確保
することが出来る。また、この自己接着性ゴムガスケッ
ト１は、密封する部材であるカバーとも自己接着するも
ので、有効なガスケットの脱落防止効果を発揮する。こ
のように本発明の自己接着性ゴムガスケット１は十分な
ゴム弾性と密封部材に対して強力な接着性を持つことに
より、防音、防振性を確保すると同時にシール性能を飛
躍的に向上させることができる。また、低荷重の締付け
でシール性を確保することができる利点も有する。The self-adhesive rubber gasket 1 according to the present invention is directly bonded to a flange made of a metal material or a synthetic resin material, and the sealing property of the bonded surface can be reliably ensured. The self-adhesive rubber gasket 1 also self-adheres to the cover, which is a sealing member, and exhibits an effective effect of preventing the gasket from coming off. As described above, the self-adhesive rubber gasket 1 of the present invention has sufficient rubber elasticity and strong adhesiveness to the sealing member, thereby ensuring soundproofing and vibration-proofing properties and at the same time dramatically improving the sealing performance. You can Further, there is an advantage that the sealing property can be secured by tightening with a low load.
【図１】本発明の一実施例を示した断面図である。FIG. 1 is a sectional view showing an embodiment of the present invention.
【図２】本発明の他の実施例を示す断面図である。FIG. 2 is a sectional view showing another embodiment of the present invention.
【図３】本発明のその他の実施例を示す断面図である。FIG. 3 is a cross-sectional view showing another embodiment of the present invention.
【図４】本発明のその他の実施例を示す断面図である。FIG. 4 is a sectional view showing another embodiment of the present invention.
【図５】実施例の試料作製条件を示す。FIG. 5 shows the sample preparation conditions of the example.
【図６】実施例の接着強度測定方法を示す。FIG. 6 shows a method for measuring the adhesive strength of an example.
１ 自己接着性ゴムガスケット １´ ゴム基材２を混合した自己接着性ゴムガスケット ２ ゴム基材 1 Self-adhesive rubber gasket 1'Self-adhesive rubber gasket with rubber base 2 mixed 2 rubber base material
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０８Ｌ 83/04 Ｃ０８Ｌ 83/04 Ｆ１６Ｊ 15/14 Ｆ１６Ｊ 15/14 Ｃ Ｆターム(参考） 4F100 AK04B AK17B AK27B AK52A AK52B AK64B AL01B AL06B AL09A AN02B BA02 GB32 GB51 JB12A JB12B JD05 JH01 JH02 JK07 JL11 4H017 AA03 AA04 AA23 AB01 AB07 AB12 AB15 AB17 AC09 AD01 AE02 4J002 BB081 BD121 BG041 CP031 EX016 EX076 FD206 GJ00 GM00 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) C08L 83/04 C08L 83/04 F16J 15/14 F16J 15/14 C F term (reference) 4F100 AK04B AK17B AK27B AK52A AK52B AK64B AL01B AL06B AL09A AN02B BA02 GB32 GB51 JB12A JB12B JD05 JH01 JH02 JK07 JL11 4H017 AA03 AA04 AA23 AB01 AB07 AB12 AB15 AB17 AC09 AD01 AE02 4J002 BB081 BD121 BG041 CP761 EX016 EX016 EX016
Claims (7)
する付加型シリコーンゴムにて自己接着性ゴムガスケッ
トを形成し、前記自己接着性ゴムガスケットと同類のゴ
ム材か、あるいはこれとは異なるニトリルゴムまたは、
水素化ニトリルゴムあるいは、エチレンプロピレンゴ
ム、アクリルゴム、エチレンアクリルゴム、シリコーン
ゴム、フッ素ゴムのいずれかからなるゴム材の表面に前
記自己接着性ゴムガスケットを付着せしめ、金属材ある
いは合成樹脂材へ接着硬化せしめることを特徴とする自
己接着性ゴムガスケット。1. A self-adhesive rubber gasket is formed from an addition type silicone rubber that exhibits adhesiveness and rubber elasticity by a curing catalyst, and a rubber material similar to the self-adhesive rubber gasket or a nitrile different from this is used. Rubber or
The self-adhesive rubber gasket is attached to the surface of a rubber material made of hydrogenated nitrile rubber, ethylene propylene rubber, acrylic rubber, ethylene acrylic rubber, silicone rubber, or fluororubber and bonded to a metal material or synthetic resin material. A self-adhesive rubber gasket characterized by being hardened.
リング剤を導入した、シリコーンゴム、アクリルゴム、
エチレンアクリルゴムあるいはフッ素ゴムのいずれかに
て自己接着性ゴムガスケットを形成し、金属材あるいは
合成樹脂材へ接着硬化せしめることを特徴とする自己接
着性ゴムガスケット。2. A silicone rubber, an acrylic rubber, in which an amino-type or vinyl-type silane coupling agent is introduced,
A self-adhesive rubber gasket, characterized in that a self-adhesive rubber gasket is formed of either ethylene acrylic rubber or fluororubber, and is adhered and cured to a metal material or a synthetic resin material.
リング剤を導入した、シリコーンゴム、アクリルゴム、
エチレンアクリルゴムあるいはフッ素ゴムのいずれかに
て自己接着性ゴムガスケットを形成し、前記自己接着性
ゴムガスケットと同類のゴム材か、あるいはこれとは異
なるニトリルゴムまたは、水素化ニトリルゴムあるい
は、エチレンプロピレンゴム、アクリルゴム、エチレン
アクリルゴム、シリコーンゴム、フッ素ゴムのいずれか
からなるゴム材の表面に前記自己接着性ゴムガスケット
を付着せしめ、金属材あるいは合成樹脂材へ接着硬化せ
しめることを特徴とする自己接着性ゴムガスケット。3. A silicone rubber, an acrylic rubber, in which an amino-type or vinyl-type silane coupling agent is introduced,
A self-adhesive rubber gasket is formed from either ethylene acrylic rubber or fluororubber, and a rubber material similar to the self-adhesive rubber gasket or a different nitrile rubber, hydrogenated nitrile rubber, or ethylene propylene rubber is used. The self-adhesive rubber gasket is attached to the surface of a rubber material made of rubber, acrylic rubber, ethylene acrylic rubber, silicone rubber, or fluororubber, and the self-adhesive rubber gasket is adhered and cured to a metal material or a synthetic resin material. Adhesive rubber gasket.
た、ニトリルゴムまたは、水素化ニトリルゴムあるい
は、エチレンプロピレンゴムなどの組成物のいずれかに
て自己接着性ゴムガスケットを形成し、金属材あるいは
合成樹脂材へ接着硬化せしめることを特徴とする自己接
着性ゴムガスケット。4. A self-adhesive rubber gasket is formed from a composition such as nitrile rubber, hydrogenated nitrile rubber, or ethylene propylene rubber to which a compound having a carboxyl group is added to form a metal material or a synthetic resin. A self-adhesive rubber gasket characterized by being adhesively cured to a material.
た、ニトリルゴムまたは、水素化ニトリルゴムあるい
は、エチレンプロピレンゴムなどの組成物のいずれかに
て自己接着性ゴムガスケットを形成し、前記自己接着性
ゴムガスケットと同類のゴム材か、あるいはこれとは異
なるニトリルゴムまたは、水素化ニトリルゴムあるい
は、エチレンプロピレンゴム、アクリルゴム、エチレン
アクリルゴム、シリコーンゴム、フッ素ゴムのいずれか
からなるゴム材の表面に前記自己接着性ゴムガスケット
を付着せしめ、金属材あるいは合成樹脂材へ接着硬化せ
しめることを特徴とする自己接着性ゴムガスケット。5. A self-adhesive rubber gasket is formed by forming a self-adhesive rubber gasket from a composition such as nitrile rubber, hydrogenated nitrile rubber, or ethylene propylene rubber, to which a compound having a carboxyl group is added. A rubber material similar to the gasket, or a nitrile rubber different from this, a hydrogenated nitrile rubber, or a rubber material made of ethylene propylene rubber, acrylic rubber, ethylene acrylic rubber, silicone rubber, or fluorine rubber A self-adhesive rubber gasket, characterized in that a self-adhesive rubber gasket is adhered to it and then adhered and cured to a metal material or synthetic resin material.
アクリル酸、メタクリル酸、マレイン酸及びそれらの変
性体を添加してなることを特徴とする請求項４ないし５
の自己接着性ゴムガスケット。6. The compound having a carboxyl group is
6. Acrylic acid, methacrylic acid, maleic acid and modified products thereof are added.
Self-adhesive rubber gasket.
ルゴムあるいは、エチレンプロピレンゴム、アクリルゴ
ム、エチレンアクリルゴム、シリコーンゴム、フッ素ゴ
ムのいずれかからなるゴム基材と、前記自己接着性ゴム
ガスケットとを混合せしめて形成したことを特徴とする
請求項１ないし３ないし５の自己接着性ゴムガスケッ
ト。7. A rubber base material made of any one of nitrile rubber, hydrogenated nitrile rubber, ethylene propylene rubber, acrylic rubber, ethylene acrylic rubber, silicone rubber, and fluororubber, and the self-adhesive rubber gasket. The self-adhesive rubber gasket according to claim 1, wherein the self-adhesive rubber gasket is formed by mixing.