JP2003135612A - Filter for mask, and mask - Google Patents
Filter for mask, and maskInfo
- Publication number
- JP2003135612A JP2003135612A JP2001335483A JP2001335483A JP2003135612A JP 2003135612 A JP2003135612 A JP 2003135612A JP 2001335483 A JP2001335483 A JP 2001335483A JP 2001335483 A JP2001335483 A JP 2001335483A JP 2003135612 A JP2003135612 A JP 2003135612A
- Authority
- JP
- Japan
- Prior art keywords
- water
- mask
- absorbent
- nonwoven fabric
- sheet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、マスクの内側に重
ねて使用するマスク用フィルタ及びマスクに係り、特に
液体を保持したウエットタイプのマスク用フィルタ及び
マスクに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a mask filter and a mask which are used by being superposed on the inside of a mask, and more particularly to a wet type mask filter and a mask which retain a liquid.
【０００２】[0002]
【従来の技術】従来、マスク本体にまたはマスクに別途
設けたフィルタ部材等に水分を保持させた部材を設ける
ことで、水分を含んだ空気を吸入可能にする方法が知ら
れている。また、前記フィルタ部材等に水分が保持され
ていることで、塵やホコリ、花粉などを効率よく吸着さ
せることも知られている。2. Description of the Related Art Conventionally, there is known a method of allowing air containing water to be sucked by providing a member for holding water in a mask body or a filter member separately provided in the mask. It is also known that dust, dust, pollen and the like can be efficiently adsorbed by retaining water in the filter member and the like.
【０００３】例えば、実開昭６３−１８６４４８号公報
には、通気性の平面状体物にて形成されたマスク本体の
内面側、または内部に、既に水を含んだ高吸水性ポリマ
ーを内装する疎水性繊維シートを装着したことを特徴と
するマスクが記載されている。For example, in Japanese Utility Model Laid-Open No. 186448/1988, a super absorbent polymer containing water is incorporated inside or inside a mask body made of a breathable planar material. A mask is described which is fitted with a hydrophobic fiber sheet.
【０００４】また、実開平３−１２６１５６号公報に
は、少なくとも一部に高吸水性樹脂を有するシートで形
成されたことを特徴とするマスク用濾過シートが記載さ
れており、当該シートは高吸水性樹脂を塗布又は含有さ
せた繊維を使用した不織布を用いてもよいとしている。Further, Japanese Utility Model Laid-Open No. 3-126156 discloses a filter sheet for a mask which is characterized by being formed of a sheet having at least a part of a highly water-absorbent resin. The sheet has a high water-absorption property. It is also possible to use a non-woven fabric using fibers coated with or containing a hydrophilic resin.
【０００５】[0005]
【発明が解決しようとする課題】上述したように従来の
疎水性繊維シートに高吸水性ポリマーを内装したマスク
では、含水させるとポリマーが膨潤してゲル状物とな
り、疎水性繊維シートが隙間なく詰まった状態となるた
め通気性がなくなるか、著しく通気性が低下する。As described above, in the conventional mask in which the superabsorbent polymer is incorporated in the hydrophobic fiber sheet, the polymer swells into a gel when water is contained, and the hydrophobic fiber sheet does not have a gap. It becomes clogged so that the air permeability is lost or the air permeability is significantly reduced.
【０００６】また、高吸水性樹脂を塗布したシート又は
高吸水性樹脂を含有させた繊維のみを使用したシートの
場合にも、前記と同様に含液させた際に高吸水性樹脂が
膨潤してシート材自身の空隙を埋めてしまい、通気性が
著しく損なわれ、高吸水性樹脂の含有量を減らせば、通
気度は上がるが充分な量の水分が保持できず、短時間で
乾燥状態となってしまうという問題点があった。Also in the case of a sheet coated with a super absorbent resin or a sheet using only fibers containing the super absorbent resin, the super absorbent resin swells when impregnated in the same manner as described above. If the content of the super absorbent resin is reduced by filling the voids of the sheet material itself, the air permeability will be significantly reduced, but the air permeability will increase, but a sufficient amount of water will not be retained, and it will be in a dry state in a short time. There was a problem that it would become.
【０００７】すなわち、従来の技術においては、長時間
湿潤状態を保つために充分な量の水分を保持させた際
に、同時に通気度を保つことができないという欠点があ
った。That is, the conventional technique has a drawback in that it is impossible to maintain the air permeability at the same time when a sufficient amount of water is retained for keeping the wet state for a long time.
【０００８】本発明は、これらの事情に鑑みてなされた
ものであり、マスクの外側からの塵やホコリ、花粉など
の異物を効率よく吸着し、かつ、使用者が湿った空気を
長時間吸気できる充分な量の水分が保持され、使用者が
息苦しくない通気度を有するマスク及び通常のマスクに
取り付けて使用するマスク用フィルタを提供することを
目的とする。The present invention has been made in view of these circumstances, and efficiently adsorbs foreign matter such as dust, dust, and pollen from the outside of the mask, and allows the user to inhale moist air for a long time. It is an object of the present invention to provide a mask having a breathability that allows a user to hold a sufficient amount of water so that the user does not breathe, and a mask filter that is used by being attached to a normal mask.
【０００９】[0009]
【課題を解決するための手段】前記目的を達成するため
請求項１に記載のマスク用フィルタは、吸水性繊維を含
有する吸水性不織布と、前記吸水性不織布に液体を保持
させ、該吸水性不織布の含液率を１５ｖ／ｖ％〜９０ｖ
／ｖ％としたときの該吸水性不織布の通気度を１５cc／
cm２／sec〜８０ cc／cm２／sec にするシート材と、を
具備したことを特徴とする。In order to achieve the above-mentioned object, a mask filter according to claim 1 is a water-absorbent nonwoven fabric containing water-absorbent fibers, and the water-absorbent nonwoven fabric holds a liquid, Liquid content of non-woven fabric is 15v / v% ~ 90v
/ V%, the air permeability of the water absorbent nonwoven fabric is 15cc /
and the sheet material to cm 2 / sec~80 cc / cm 2 / sec, characterized by comprising a.
【００１０】請求項２に記載のマスク用フィルタは、請
求項１に記載のマスク用フィルタであって、前記シート
材は、一方の面に吸水性繊維の層を有し、かつ、他方の
面に疎水性繊維の層を有する吸水性不織布からなること
を特徴とする。The mask filter according to claim 2 is the mask filter according to claim 1, wherein the sheet material has a layer of water-absorbent fibers on one surface and the other surface. It is characterized by comprising a water-absorbent nonwoven fabric having a layer of hydrophobic fibers.
【００１１】請求項３に記載のマスク用フィルタは、請
求項１に記載のマスク用フィルタであって、前記シート
材は、前記吸水性不織布に疎水性不織布を積層してなる
ことを特徴とする。A mask filter according to a third aspect of the present invention is the mask filter according to the first aspect, wherein the sheet material is formed by laminating a hydrophobic nonwoven fabric on the water absorbent nonwoven fabric. .
【００１２】請求項４に記載のマスク用フィルタは、口
や鼻を覆う通気性のあるシート材からなるマスク本体部
と、該マスク本体部に設けられ顔面に装着するための装
着部とを具備したマスクであって、前記マスク本体部が
吸水性繊維を含有する吸水性不織布と疎水性不織布を少
なくとも含むシート材から構成され、該シート材に液体
を保持させ、該シート材の含液率１５ｖ／ｖ％〜９０ｖ
／ｖ％としたときの該シート材の通気度が１５ cc／cm
２／sec〜８０ cc／cm２／sec であることを特徴とす
る。According to a fourth aspect of the present invention, there is provided a mask filter including a mask main body made of a breathable sheet material for covering a mouth and a nose, and a mounting portion provided on the mask main body for mounting on a face. The mask body is composed of a sheet material containing at least a water-absorbent non-woven fabric containing a water-absorbent fiber and a hydrophobic non-woven fabric. The sheet material is made to retain a liquid, and the liquid content of the sheet material is 15v. / V% to 90v
/ V%, the air permeability of the sheet material is 15 cc / cm
2 / sec to 80 cc / cm 2 / sec.
【００１３】請求項５に記載のマスク用フィルタ又はマ
スクは、請求項１乃至３のいずれか１つに記載のマスク
用フィルタであって、前記吸水性不織布は、吸水性繊維
と疎水性繊維との混紡であることを特徴とする。A mask filter or a mask according to claim 5 is the mask filter according to any one of claims 1 to 3, wherein the water-absorbent nonwoven fabric comprises water-absorbent fibers and hydrophobic fibers. It is characterized by being a mixed spinning of.
【００１４】請求項６に記載のマスク用フィルタ又はマ
スクは、請求項１乃至５のいずれか１つに記載のマスク
用フィルタ又はマスクであって、前記吸水性繊維は、芯
がポリオレフィンで鞘が高吸水性樹脂である芯鞘構造の
繊維であることを特徴とする。A mask filter or a mask according to claim 6 is the mask filter or mask according to any one of claims 1 to 5, wherein the water-absorbent fiber has a polyolefin core and a sheath. It is a fiber having a core-sheath structure which is a highly water-absorbent resin.
【００１５】請求項７に記載のマスク用フィルタ又はマ
スクは、請求項１に記載のマスク用フィルタ又は請求項
４に記載のマスクであって、前記吸水性不織布は、前記
吸水性繊維と疎水性繊維との混紡割合が、２０：８０〜
８０：２０の割合であることを特徴とする。A mask filter or a mask according to claim 7 is the mask filter according to claim 1 or the mask according to claim 4, wherein the water absorbent nonwoven fabric is hydrophobic with the water absorbent fibers. The blend ratio with the fiber is 20: 80-
The ratio is 80:20.
【００１６】請求項８に記載のマスク用フィルタ又はマ
スクは、請求項３乃至７のいずれか１つに記載のマスク
用フィルタ又はマスクであって、前記シート材の一方の
面の色と、他方の面の色が、互いに異なることを特徴と
する。A mask filter or a mask according to claim 8 is the mask filter or mask according to any one of claims 3 to 7, wherein the color of one surface of the sheet material and the other The surface colors of the are different from each other.
【００１７】なお、本発明で用いている含液率（ｖ／ｖ
％）とは、吸水性不織布の単位体積当たりの含液量で表
される。この場合、含液率（ｖ／ｖ％）は、以下の式に
示すように、マスク用フィルタに用いられる吸水性不織
布の縦×横×厚みで算出される吸水性不織布の体積から
含液する液体の体積を除して１００を乗じてパーセント
で表記したものが用いられる。The liquid content (v / v) used in the present invention
%) Is represented by the liquid content per unit volume of the water absorbent nonwoven fabric. In this case, the liquid content (v / v%) is calculated from the volume of the water-absorbent nonwoven fabric calculated by the formula: length × width × thickness of the water-absorbent nonwoven fabric used for the mask filter, as shown in the following formula. The volume of the liquid is divided, multiplied by 100, and expressed as a percentage.
【００１８】含液率（ｖ／ｖ％）＝｛含液量（ml）／含
液前吸水性不織布（cm３）｝×１００
ここで、含液させた際には吸水性繊維が膨潤して不織布
自体の体積は増加するが、本発明では含液させる前の不
織布体積と含液量から含液率を算出した。Liquid content (v / v%) = {liquid content (ml) / water-absorbent non-woven fabric before liquid absorption (cm 3 )} × 100 Here, the water-absorbent fibers swell when the liquid is contained. Although the volume of the nonwoven fabric itself increases, in the present invention, the liquid content was calculated from the volume and the liquid content of the nonwoven fabric before containing the liquid.
【００１９】本発明で用いられる含液率としてｖ／ｖ％
では、１５〜９０が好ましく、さらに好ましくは１８〜
８５が良い。１５未満では、単位体積当たりの含液量が
不足してマスク用フィルターが塵やホコリ、花粉などを
吸着する効率が悪くなったり、使用者に湿った空気を吸
入させることが困難になったりする。１５〜９０ｖ／ｖ
％の範囲にあると液体が吸水性不織布に対して均一に広
がりやすく、適度な湿潤状態を得ることができる。９０
を超えると不織布の通気性を維持することが困難となる
ため好ましくない。The liquid content used in the present invention is v / v%.
Then, 15 to 90 is preferable, and more preferably 18 to
85 is good. When it is less than 15, the liquid content per unit volume is insufficient, the efficiency of the mask filter for adsorbing dust, dust, pollen, etc. becomes poor, and it becomes difficult for the user to inhale moist air. . 15-90v / v
When it is in the range of%, the liquid easily spreads uniformly on the water-absorbent nonwoven fabric, and an appropriate wet state can be obtained. 90
When it exceeds, it becomes difficult to maintain the air permeability of the nonwoven fabric, which is not preferable.
【００２０】不織布などのシート体では厚さを特定する
ことが困難な場合には、含液率は、以下の式に示すよう
に、吸水性不織布の単位重量当たりの含液重量で算出し
ても良く、吸水性不織布の重量から含液する液体の重量
を除して１００を乗じてパーセントで表記したものが用
いられる。When it is difficult to specify the thickness of a sheet material such as a nonwoven fabric, the liquid content is calculated by the liquid content weight per unit weight of the water absorbent nonwoven fabric as shown in the following formula. Alternatively, the weight of the liquid-containing liquid is subtracted from the weight of the water-absorbent nonwoven fabric, and the product is multiplied by 100 to be expressed as a percentage.
【００２１】含液率（ｗｔ％）＝｛含液重量（g）／含
液前吸水性不織布重量（ｇ）｝×１００
この場合、含液率は、１５０ｗｔ％〜８５０ｗｔ％が好
ましく、さらに好ましくは１７０ｗｔ％〜８００ｗｔ％
がよい。Liquid content (wt%) = {liquid content weight (g) / water-absorbent nonwoven fabric weight before liquid content (g)} × 100 In this case, the liquid content is preferably 150 wt% to 850 wt%, and more preferably Is 170 wt% to 800 wt%
Is good.
【００２２】また、通気度とは、単位時間当たりの通気
量で表される。The air permeability is represented by the air flow rate per unit time.
【００２３】上記のように構成された請求項１乃至３、
５乃至８に記載のマスク用フィルタによれば、通常のマ
スクにセットされ、まず、吸水性繊維を含有する吸水性
不織布に保持された液体により湿潤状態を保っているの
で、塵やホコリ、花粉などを効率よく吸着しつつ、同時
に充分な通気度を保っているので、使用者は湿った空気
を吸入するため、喉に潤いを与えつつ、息苦しさを感じ
ることなく長時間使用することができる。Claims 1 to 3 configured as described above,
According to the mask filter described in 5 to 8, since the mask filter is set in a normal mask and is first kept in a wet state by the liquid held in the water-absorbent nonwoven fabric containing the water-absorbent fibers, dust, dust, and pollen While efficiently adsorbing etc., while maintaining sufficient air permeability, the user inhales moist air, so it can be used for a long time without feeling stuffy, while moisturizing the throat. .
【００２４】請求項４，６乃至８に記載のマスクによれ
ば、吸水性繊維を含有する吸水性不織布に保持された液
体により湿潤状態を保っているので、塵やホコリ、花粉
などを効率よく吸着しつつ、同時に充分な通気度を保っ
ているので、使用者は湿った空気を吸入するため、喉に
潤いを与えつつ、息苦しさを感じることなく長時間使用
することができる。According to the masks of claims 4, 6 to 8, since the wet state is maintained by the liquid held in the water-absorbent nonwoven fabric containing the water-absorbent fibers, dust, dust, pollen, etc. can be efficiently treated. While adsorbing and maintaining a sufficient air permeability at the same time, the user inhales moist air, so that the user can use it for a long time without moisturizing while moisturizing the throat.
【００２５】請求項２，５，６，８に記載のマスク用フ
ィルタによれば、疎水性側を口に当たるようにマスクに
セットして使用することで、さらに、含液した不織布が
直接口にあたらないため、ぺちゃぺちゃした感覚を与え
ることがなく快適に使用することが可能である。According to the mask filter of the second, fifth, sixth, and eighth aspects, the non-woven fabric containing the liquid is directly applied to the mouth by setting the mask so that the hydrophobic side touches the mouth. Since it does not hit, it is possible to use it comfortably without giving a messy feeling.
【００２６】[0026]
【発明の実施の形態】以下、本発明の実施の形態を図面
を参照して説明する。図１は本発明の第１の実施の形態
に係るマスク用フィルタを示す斜視図である。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a perspective view showing a mask filter according to a first embodiment of the present invention.
【００２７】図１において、マスク用フィルタ１は、吸
水性繊維を含有する吸水性不織布２と疎水性不織布３を
少なくとも含むシート材４に水分を保持させたものであ
る。In FIG. 1, the mask filter 1 is a sheet material 4 containing at least a water-absorbent nonwoven fabric 2 containing a water-absorbent fiber and a hydrophobic nonwoven fabric 3 to retain water.
【００２８】吸水性不織布２は、吸水性繊維を含有す
る。シート材４は、前記吸水性不織布２に液体を保持さ
せ、含液率１５ｖ／ｖ％〜９０ｖ／ｖ％としたときの該
吸水性不織布２の通気度が１５cc／cm２／sec〜８０ cc
／cm２／sec としたものである。The water absorbent nonwoven fabric 2 contains water absorbent fibers. The sheet material 4 has a breathability of 15 cc / cm 2 / sec to 80 cc when the water absorbent nonwoven fabric 2 holds a liquid and the liquid content is 15 v / v% to 90 v / v%.
/ Cm 2 / sec.
【００２９】吸水性不織布２としては、吸水性繊維を少
なくとも含有していれば良く、親水性繊維、疎水性繊維
を混紡していても良い。この吸水性繊維は、特に制限は
なく、吸水性繊維が芯鞘構造であると、吸水性繊維が繊
維状の吸水性樹脂からなるものに比べて繊維自体に腰が
あるため空隙を確保することが容易になり、通気度１５
cc／cm２／sec〜８０ cc／cm２／sec の範囲に調整す
ることが容易で好ましい。The water absorbent nonwoven fabric 2 may contain at least water absorbent fibers, and may be a mixture of hydrophilic fibers and hydrophobic fibers. This water-absorbent fiber is not particularly limited, and when the water-absorbent fiber has a core-sheath structure, the fiber itself is more flexible than that made of a fibrous water-absorbent resin, so that a space should be secured. Easy to use, breathability 15
It is preferable easy to adjust the range of cc / cm 2 / sec~80 cc / cm 2 / sec.
【００３０】吸水性繊維として直接ポリアクリル酸系ポ
リマーを紡糸して製造したものも用いられる。As the water absorbent fiber, a fiber produced by directly spinning a polyacrylic acid type polymer is also used.
【００３１】芯鞘構造繊維として、例えば、芯物質とし
ては、低密度ポリエチレン、高密護ポリエチレン、ポリ
プロピレンで代表される結晶性ポリオレフィンが用いら
れ、鞘物質としては、熱可塑性エラストマーおよび、又
は高吸水性樹脂を主成分とするもので、熱可塑性エラス
トマーとしては、例えばオレフィン系、スチレン系、ポ
リエステル系、ジエン系、アミド系熱可塑性エラストマ
ーを用いることができ、高吸水性樹脂としては、例えば
デンプン・アクリロニトリルグラフト重合体の加水分解
物、カルボキシメチルセルロース架橋物の他、ポリアク
リル酸塩系、ポリオキシエチレン系、ポリビニルアルコ
ール・無水マレイン酸系、酢ピ・アクリル酸塩系等多く
の市販の吸水性樹脂の中から適宜選択して使用すること
ができる。なお、無機充填剤の添加は繊維表面を粗面化
し、乾燥状態のみならず吸水状態においても繊維のブロ
ッキングや粘着を防止する効果を有するため適宜添加す
るのが好ましい。As the core-sheath structure fiber, for example, a crystalline polyolefin represented by low density polyethylene, highly protected polyethylene or polypropylene is used as the core substance, and a thermoplastic elastomer and / or a highly water-absorbent substance is used as the sheath substance. Resins as a main component, examples of thermoplastic elastomers that can be used include olefin-based, styrene-based, polyester-based, diene-based, and amide-based thermoplastic elastomers, and examples of superabsorbent resins include starch-acrylonitrile. In addition to graft polymer hydrolysates and carboxymethyl cellulose cross-linked products, many commercially available water-absorbent resins such as polyacrylate-based, polyoxyethylene-based, polyvinyl alcohol / maleic anhydride-based, vinyl acetate / acrylate-based, etc. It can be appropriately selected and used from among them. The inorganic filler is preferably added as it has the effect of roughening the fiber surface and preventing the blocking and sticking of the fiber not only in the dry state but also in the water absorbing state.
【００３２】疎水性不織布３は、疎水性繊維を主に含む
不織布からなる。この疎水性繊維は、ポリオレフィン系
樹脂が少なくとも繊維表面とした繊維が用いられる。こ
のポリオレフィン系樹脂としては、ポリエステル、ポリ
プロピレン（ＰＰ）、高密度ポリエチレン（ＨＤＰ
Ｅ）、ＰＰ／ポリ４ メチルペンテン １（ＰＭＰ）、
ＰＭＰ／ＨＤＰＥおよびこれらのＨＤＰＥの代わりにポ
リメチル水素シロキサンのアルケンおよびプロピレン付
加物（ＮＲ Ｂ）などのオルガノポリシロキサン（Ｏ
Ｓ）をＨＤＰＥに数重量％練り込んだ樹脂等が用いられ
る。The hydrophobic nonwoven fabric 3 is composed of a nonwoven fabric mainly containing hydrophobic fibers. As the hydrophobic fiber, a fiber having at least a fiber surface of a polyolefin resin is used. This polyolefin resin includes polyester, polypropylene (PP), high density polyethylene (HDP).
E), PP / poly 4 methylpentene 1 (PMP),
PMP / HDPE and organopolysiloxanes such as alkenes and propylene adducts of polymethylhydrogen siloxanes (NR B) in place of these HDPE (O
A resin obtained by kneading S) into HDPE by several wt% is used.
【００３３】吸水性不織布２に含有させる繊維として
は、吸水性繊維や疎水性繊維の他に親水性繊維を含有さ
せることができ、例えば親水性繊維としては、レイヨ
ン、コットンなどが用いられる。As the fibers contained in the water absorbent nonwoven fabric 2, hydrophilic fibers can be contained in addition to the water absorbent fibers and the hydrophobic fibers. For example, rayon, cotton, etc. are used as the hydrophilic fibers.
【００３４】吸水性不織布２に保持される液体として
は、水であっても良く、より好ましくは喉に潤いを付与
する薬効成分を水に混合して用いてもよい。また、喉に
潤いを付与する薬効成分に代えて、鼻腔の通りを良くす
る薬効成分など使用者が吸入して効能を得られる薬剤、
例えばメンソールを混合することができる。その他、防
腐剤、香料、着色剤など適宜添加しうる。The liquid retained in the water-absorbent nonwoven fabric 2 may be water, and more preferably, a medicinal component that moisturizes the throat may be mixed with water. Further, in place of the medicinal component that imparts moisturization to the throat, a medicinal component that improves the passage of the nasal cavity such as a medicinal substance that the user can inhale to obtain an effect,
For example, menthol can be mixed. In addition, preservatives, fragrances, coloring agents and the like may be added as appropriate.
【００３５】上記のような吸水性不織布２と疎水性不織
布３とを積層することで得られるマスク用フィルタ１
は、含液率が１５ｖ／ｖ％〜９０ｖ／ｖ％のとき、通気
度が１５cc／cm２／sec〜８０cc／cm２／secとなり、充
分な含液量と通気性を有する。A mask filter 1 obtained by laminating the water-absorbent nonwoven fabric 2 and the hydrophobic nonwoven fabric 3 as described above.
When liquid content of 15v / v% ~90v / v% , air permeability has 15cc / cm 2 / sec~80cc / cm 2 / sec , and the sufficient solution content and breathability.
【００３６】前記吸水性不織布２の色と疎水性不織布３
の色は、互いに異なるようにすることが好ましい。具体
的には、吸水性不織布２の色を青とし、疎水性不織布３
の色を白にする。このような異なる色を用いることで、
マスク用フィルタ１を後述の使用者に装着する場合にお
いて、マスク用フィルタ１を向きを確認しやすくするこ
とができる。Color of the water-absorbent nonwoven fabric 2 and hydrophobic nonwoven fabric 3
The colors are preferably different from each other. Specifically, the color of the water-absorbent nonwoven fabric 2 is blue, and the hydrophobic nonwoven fabric 3
Make the color of white. By using different colors like this,
When the mask filter 1 is attached to the user, which will be described later, the orientation of the mask filter 1 can be easily confirmed.
【００３７】また、シート材４は、吸水性繊維に疎水性
繊維を積繊して、一方の面を吸水性繊維の層とし、他方
の面を疎水性繊維の層とする吸水性不織布２としてもよ
い。つまり、シート材４に疎水性の面を設ける方法とし
ては、吸水性不織布２に疎水性不織布３を積層する手段
の他に、一枚の不織布が吸水性繊維に偏った面と疎水性
繊維に偏った面を有する構造としても良く、この場合、
この一枚の不織布の断面中央付近では吸水性繊維と疎水
性繊維が混合されたもので、厳密に層状に分離している
必要はない。このように疎水性の面を設けることで使用
者の口には含水したマスク用フィルタが不快感無く装着
される。The sheet material 4 is a water-absorbent nonwoven fabric 2 in which hydrophobic fibers are stacked on water-absorbent fibers to form a layer of water-absorbent fibers on one side and a layer of hydrophobic fibers on the other side. Good. That is, as a method for providing the hydrophobic surface on the sheet material 4, in addition to the means for laminating the hydrophobic non-woven fabric 3 on the water absorbent non-woven fabric 2, one non-woven fabric has a surface deviated to the water absorbent fiber and a hydrophobic fiber. A structure having an uneven surface may be used. In this case,
In the vicinity of the center of the cross section of this one nonwoven fabric, the water absorbing fibers and the hydrophobic fibers are mixed, and it is not necessary to strictly separate them into layers. By providing the hydrophobic surface in this way, the hydrated mask filter can be attached to the user's mouth without discomfort.
【００３８】また、シート材４は、吸水性面と疎水性面
で色を変えるのが好ましい。また、シート材４は、吸水
性不織布２の表面と裏面の両方に疎水性不織布３を取り
付ける三層構造を用いてもよい。このような構造を用い
ることで、マスク用フィルタは表面と裏面の両方の向き
で使用者に装着することができる。Further, it is preferable that the sheet material 4 has different colors on the water absorbing surface and the hydrophobic surface. The sheet material 4 may have a three-layer structure in which the hydrophobic nonwoven fabric 3 is attached to both the front surface and the back surface of the water absorbent nonwoven fabric 2. By using such a structure, the mask filter can be attached to the user in both front and back directions.
【００３９】図２及び図３は本発明のマスク用フィルタ
の使用方法を示す図であり、図２はマスク用フィルタを
マスクに重ねた状態を示す斜視図、図３は本発明のマス
ク用フィルタの使用状態を示す説明図である。2 and 3 are views showing a method of using the mask filter of the present invention. FIG. 2 is a perspective view showing a state in which the mask filter is superposed on the mask, and FIG. 3 is a mask filter of the present invention. It is explanatory drawing which shows the use condition.
【００４０】図２において、マスク１０としては、従来
から一般に市販されているものを使用しており、 ガー
ゼ等の布で形成されたマスク本体部１１の両側に装着具
１２を設けたものである。装着具１３は、ゴム紐等を耳
に掛けられるような形状にしたものである。マスク本体
部１１の裏側には、吸水性不織布２側をマスク本体部１
１側に向けて、マスク用フィルタ１を重ねて配置する。In FIG. 2, as the mask 10, a mask which has been conventionally sold on the market is used, and the wearing tools 12 are provided on both sides of the mask body 11 formed of cloth such as gauze. . The mounting tool 13 has a shape such that a rubber cord can be worn around the ear. On the back side of the mask body 11, the water absorbent nonwoven fabric 2 side is provided on the mask body 1 side.
The masking filter 1 is arranged so as to overlap with the first side.
【００４１】この後、図３のように、使用者１４はマス
ク用フィルタ１を重ねたマスク１０を装着する。この場
合、マスク用フィルタ１は、疎水性不織布３側を使用者
１４の口１５に、吸水性不織布２側をマスク１０のマス
ク本体部１１に当てて使用することで、含水した吸水性
不織布２が直後口にあたらない構成となっているため、
使用者１４にとって快適な装着感を有する。After this, as shown in FIG. 3, the user 14 wears the mask 10 on which the mask filter 1 is overlaid. In this case, the mask filter 1 is used by using the hydrophobic non-woven fabric 3 side against the mouth 15 of the user 14 and the water-absorbent non-woven fabric 2 side against the mask body 11 of the mask 10 to use the water-absorbent non-woven fabric 2 Since it is a structure that does not hit the mouth immediately after,
The user 14 feels comfortable to wear.
【００４２】上記第１の実施の形態に係るマスク用フィ
ルタ１について、具体的に、親水性繊維としてレイヨン
１０％、アクリル系繊維２０％と、吸水性繊維としてポ
リアクリル酸系繊維１０％と、疎水性繊維としてポリエ
ステル６０％からなる吸水性不織布２（目付１００ｇ／
ｍ２）を用いて表１に示す条件で第１乃至第５の実施例
を作成し、含液率と通気度について検証してみた。含液
させた液体は水を用いた。なお、通気度の試験方法は、
フラジール通気度試験（ＪＩＳ Ｌ−１０９６）で行っ
た。Regarding the mask filter 1 according to the first embodiment, specifically, 10% rayon as hydrophilic fiber and 20% acrylic fiber, and 10% polyacrylic acid fiber as water absorbing fiber, Water-absorbent non-woven fabric 2 made of 60% polyester as hydrophobic fiber (Basis weight 100 g /
m 2 ), the first to fifth examples were prepared under the conditions shown in Table 1, and the liquid content and air permeability were examined. Water was used as the impregnated liquid. The air permeability test method is
The Frazier air permeability test (JIS L-1096) was performed.
【００４３】[0043]
【表１】
表１において、ブランクは、水分を含水しない綿製布帛
を示し、マスクの通気度は、図１のシート材４をフィル
タ材として市販の綿製マスクに重層させて測定してい
る。（この市販のマスクのみの通気度は７５cc／cm２／
secであった）
表１に示すように、シート材４（フィルタ材）の含液率
１５ｖ／ｖ％〜９０ｖ／ｖ％としたときに、該吸水性不
織布の通気度が１５cc／cm２／sec〜８０ cc／cm２／se
c の範囲に調整可能であり、マスクの通気度は１５cc／
cm２／sec〜３２ cc／cm２／sec の範囲に調整すること
が解る。[Table 1] In Table 1, the blank represents a cotton cloth that does not contain water, and the air permeability of the mask is measured by overlaying a commercially available cotton mask with the sheet material 4 of FIG. 1 as a filter material. (The air permeability of this commercially available mask is 75cc / cm 2 /
As shown in Table 1, when the liquid content of the sheet material 4 (filter material) is 15 v / v% to 90 v / v%, the air permeability of the water-absorbent nonwoven fabric is 15 cc / cm 2 / sec ~ 80 cc / cm 2 / se
The air permeability of the mask can be adjusted to 15cc /
It can be seen that to adjust the range of the cm 2 / sec~32 cc / cm 2 / sec.
【００４４】さらに、本発明のマスク用フィルターの効
果を明確にするため比較試験を行った。Further, a comparative test was conducted to clarify the effect of the mask filter of the present invention.
【００４５】第１の比較例では、第１の実施の形態のシ
ート材４に代えて、粉粒体状の吸水性樹脂２．０ｇを収
容した疎水性不織布からなる袋体を用いた以外は第１の
実施の形態と同様の構成でマスク用フィルターを作成し
た。In the first comparative example, instead of the sheet material 4 of the first embodiment, a bag made of a hydrophobic non-woven fabric containing 2.0 g of a granular water absorbent resin was used. A mask filter was created with the same configuration as that of the first embodiment.
【００４６】このときの含液率および通気度については
表２に記載した。第２の比較例では、第１の実施の形態
のシート材４に代えて、レーヨンからなる親水性不織布
にポリエチレンからなる疎水性不織布を積層してなる不
織布に親水性不織布側に吸水性樹脂の粉体を０．４ｇを
均一に散布含有させたシート材４を用いた以外は第１の
実施の形態と同様の構成でマスク用フィルターを作成し
た。The liquid content and air permeability at this time are shown in Table 2. In the second comparative example, instead of the sheet material 4 of the first embodiment, a hydrophilic nonwoven fabric made of rayon and a hydrophobic nonwoven fabric made of polyethylene are laminated on the hydrophilic nonwoven fabric side of the water absorbent resin. A mask filter was prepared with the same configuration as that of the first embodiment except that the sheet material 4 in which 0.4 g of the powder was uniformly dispersed and contained was used.
【００４７】このときの含液率および通気度については
表２に記載した。第３の比較例では、第１の実施の形態
のシート材４に代えて、吸水性繊維であるポリアクリル
酸系繊維と、親水性繊維であるレーヨンと疎水性繊維ポ
リエステルの混紡割合が１：５４：４５の不織布を用い
た以外は第１の実施の形態と同様の構成でマスク用フィ
ルタを作成した。The liquid content and air permeability at this time are shown in Table 2. In the third comparative example, instead of the sheet material 4 of the first embodiment, a mixed spinning ratio of polyacrylic acid type fibers which are water absorbing fibers, rayon which is hydrophilic fibers and hydrophobic fiber polyester is 1 :. A mask filter was prepared with the same configuration as that of the first embodiment except that a 54:45 non-woven fabric was used.
【００４８】このときの含液率および通気度については
表２に記載した。The liquid content and air permeability at this time are shown in Table 2.
【表２】
第１及び第３の比較例では、通気度が１５ cc／cm２／s
ec〜８０ cc／cm２／sec の範囲から外れており、適切
な通気度が得られないことが解る。[Table 2] In the first and third comparative examples, the air permeability is 15 cc / cm 2 / s.
It is out of the range of ec to 80 cc / cm 2 / sec, and it can be seen that an appropriate air permeability cannot be obtained.
【００４９】本発明の実施の形態に記載のマスク用フィ
ルタは、含液率１５ｖ／ｖ％〜９０ｖ／ｖ％であって通
気度が１５ cc／cm２／sec〜８０ cc／cm２／sec に保
たれているため、充分な通気性があり、使用していても
息苦しくなく、また、適度な含液量であるから水分が滴
り落ちることもなく保持され、逆にすぐに乾燥してしま
わず使用者の吸気の際に適度な湿り気を与えることがで
きた。The mask filter according to the embodiment of the present invention, air permeability a liquid content 15v / v% ~90v / v% is 15 cc / cm 2 / sec~80 cc / cm 2 / sec Since it is kept in a good condition, it has sufficient breathability, it does not breathe even when used, and since it has an appropriate liquid content, it retains without dripping water, and conversely it dries immediately. Instead, the user was able to give a proper amount of damp air when inhaling.
【００５０】一方で、上記第１の比較例に記載のマスク
用フィルタは、吸水性樹脂粉末が含水してゲル化し板状
となり通気性がないものとなってしまった。また、第２
の比較例に記載のマスク用フィルターでも、吸水性樹脂
粉末が含水して膨潤し不織布上でゲル化し空隙を塞いで
しまい通気度は特に低いものとなってしまった。また、
第３の比較例に記載のマスク用フィルターは、十分な通
気度を有するものの含液率が低いためすぐに乾燥してし
まった。On the other hand, in the mask filter described in the first comparative example, the water-absorbent resin powder was hydrated and gelled into a plate, which was impermeable to air. Also, the second
Also in the mask filter described in the comparative example, the water-absorbent resin powder hydrated and swelled, gelled on the non-woven fabric, and closed the voids, resulting in a particularly low air permeability. Also,
Although the mask filter described in the third comparative example has a sufficient air permeability, it has a low liquid content and is immediately dried.
【００５１】以上、説明したように、本実施の形態のマ
スク用フィルタによれば、吸水性繊維を含有する不織布
に保持された水分により湿潤状態を保つと同時に充分な
通気度を保っており、マスクの外側からの塵やホコリ、
花粉などの異物を効率よく吸着し、かつ、使用者が湿っ
た空気を長時間吸気できる充分な量の水分が保持され、
使用者が息苦しくない通気度を確保することができ、使
用者に好印象を与えることができる。また、疎水性不織
布側を口に当てて使用すれば含水した不織布が直接口に
あたりぺちゃぺちゃした感覚を与えることがないので、
水分により喉に潤いを与えつつ、快適に長時間使用する
ことができる。As described above, according to the mask filter of the present embodiment, the wet state is maintained by the water retained in the nonwoven fabric containing the water-absorbent fibers and at the same time the sufficient air permeability is maintained. Dust and dust from the outside of the mask,
Efficiently absorbs foreign substances such as pollen and retains a sufficient amount of water that allows the user to inhale moist air for a long time.
The air permeability can be secured so that the user does not breathe, and a good impression can be given to the user. Also, if the hydrophobic non-woven fabric side is applied to the mouth, the water-containing non-woven fabric will not directly touch the mouth and give a stuffy feeling,
You can use it comfortably for a long time while moisturizing your throat with water.
【００５２】図４は本発明の第２の実施の形態に係るマ
スクを示す斜視図である。図４に示すように、マスク２
１は、口や鼻を覆う通気性のあるシート材からなるマス
ク本体部２２と、該マスク本体部２２に顔面に装着する
ための装着部の装着具２３とから構成されている。FIG. 4 is a perspective view showing a mask according to the second embodiment of the present invention. As shown in FIG. 4, the mask 2
Reference numeral 1 includes a mask main body 22 made of a breathable sheet material that covers the mouth and nose, and a mounting tool 23 for mounting the mask main body 22 on the face.
【００５３】前記マスク本体部２２は、吸水性繊維を含
有する吸水性不織布２４の裏面と表面にそれぞれ疎水性
不織布２５，２６を少なくとも含むシート材からなり、
該シート材に液体を保持させ、含液率１５ｖ／ｖ％〜９
０ｖ／ｖ％としたときの該シート材の通気度が１５ cc
／cm２／sec〜８０ cc／cm２／sec になっている。The mask body 22 is made of a sheet material containing at least hydrophobic non-woven fabrics 25 and 26 on the back and front surfaces of the water-absorbent non-woven fabric 24 containing the water-absorbent fiber, respectively.
The sheet material is made to hold a liquid, and the liquid content is 15 v / v% to 9
The air permeability of the sheet material when it is 0 v / v% is 15 cc
/ Cm 2 / sec to 80 cc / cm 2 / sec.
【００５４】また、装着具２３はマスク本体部２２の両
端に設けられ、耳に掛けられるような形状となってお
り、材質はマスク本体部２２と同素材、綿、ゴム紐等特
に限定されないが、伸縮性を有するものが好ましい。The fittings 23 are provided at both ends of the mask main body 22 and are shaped so that they can be worn on the ears, and the material thereof is not particularly limited to the same material as the mask main body 22, such as cotton and rubber cord. Those having elasticity are preferable.
【００５５】図５は第２の実施の形態のマスク２１の使
用状態を示す図である。図５に示すように、使用者１４
はマスク２１を装着する。この場合、マスク２１のマス
ク本体部２２は、疎水性不織布２５側（または疎水性不
織布２６側）を使用者１４の口１５に当てて使用するこ
とで、含水した吸水性不織布２４が直接口に当たらない
構成となっている。これにより、マスク２１は使用者１
４に快適な装着感を与えている。FIG. 5 is a view showing a usage state of the mask 21 of the second embodiment. As shown in FIG.
Wears the mask 21. In this case, the mask main body 22 of the mask 21 is used by applying the hydrophobic non-woven fabric 25 side (or the hydrophobic non-woven fabric 26 side) to the mouth 15 of the user 14, so that the water-absorbent non-woven fabric 24 is directly applied to the mouth. It does not hit. As a result, the mask 21 is used by the user 1
4 gives a comfortable fit.
【００５６】このような第２の実施の形態によれば、吸
水性不織布２４と疎水性不織布２５，２６を少なくとも
含むシート材に使用者への装着部２３を設けたマスク２
１についても、図１の実施の形態と同様の効果が得られ
る。According to the second embodiment as described above, the mask 2 in which the user wearing portion 23 is provided on the sheet material including at least the water absorbent nonwoven fabric 24 and the hydrophobic nonwoven fabrics 25 and 26.
With respect to No. 1, the same effect as that of the embodiment of FIG. 1 can be obtained.
【００５７】[0057]
【発明の効果】以上述べたように本発明によれば、吸水
性繊維を含有する不織布に保持された水分により湿潤状
態を保つと同時に充分な通気度を保っており、マスクの
外側からの塵やホコリ、花粉などの異物を効率よく吸着
し、かつ、使用者が湿った空気を長時間吸気できる充分
な量の水分が保持され、使用者が息苦しくない通気度を
確保することができ、使用者に好印象を与えることがで
きる。また、疎水性不織布側を口に当てて使用すれば含
水した不織布が直接口にあたりぺちゃぺちゃした感覚を
与えることがないので、水分により喉に潤いを与えつ
つ、快適に長時間使用することができる。As described above, according to the present invention, the moisture retained by the nonwoven fabric containing the water-absorbent fibers keeps the wet state and at the same time the sufficient air permeability is maintained. Dust, pollen, and other foreign matter can be adsorbed efficiently, and a sufficient amount of water that allows the user to inhale moist air for a long time is retained, ensuring a breathability that does not cause the user to breathe. The person can be impressed. Further, when the hydrophobic non-woven fabric side is applied to the mouth, the water-containing non-woven fabric does not directly touch the mouth to give a sensation of fluffiness, so that it is possible to comfortably use the product for a long time while moisturizing the throat with water.
【図１】図１は本発明の第１の実施の形態に係るマスク
用フィルタを示す斜視図。FIG. 1 is a perspective view showing a mask filter according to a first embodiment of the present invention.
【図２】図１のマスク用フィルタをマスクに重ねた状態
を示す斜視図。FIG. 2 is a perspective view showing a state in which the mask filter of FIG. 1 is superimposed on a mask.
【図３】図３は本発明のマスク用フィルタの使用状態を
示す説明図。FIG. 3 is an explanatory view showing a usage state of the mask filter of the present invention.
【図４】図４は本発明の第２の実施の形態に係るマスク
を示す斜視図。FIG. 4 is a perspective view showing a mask according to a second embodiment of the present invention.
【図５】第２の実施の形態のマスクの使用状態を示す
図。FIG. 5 is a view showing a usage state of the mask according to the second embodiment.
１ マスク用フィルタ ２，２４ 吸水性不織布 ３，２５，２６ 疎水性不織布 ４ シート材 ２１ マスク ２２ マスク本体部 ２３ 装着具 1 Mask filter 2,24 Water absorbent non-woven fabric 3,25,26 Hydrophobic non-woven fabric 4 sheet materials 21 mask 22 Mask body 23 Wearing equipment
Claims (8)
含液率を１５ｖ／ｖ％〜９０ｖ／ｖ％としたときの該吸
水性不織布の通気度を１５cc／cm２／sec〜８０ cc／cm
２／sec にするシート材と、 を具備したことを特徴とするマスク用フィルタ。1. A water-absorbent non-woven fabric containing water-absorbent fibers, and the water-absorbent non-woven fabric which retains a liquid and has a liquid content of 15 v / v% to 90 v / v%. Of non-woven fabric with a permeability of 15 cc / cm 2 / sec to 80 cc / cm
A mask filter comprising: a sheet material of 2 / sec.
の層を有し、かつ、他方の面に疎水性繊維の層を有する
吸水性不織布からなることを特徴とする請求項１に記載
のマスク用フィルタ。2. The sheet material is made of a water absorbent nonwoven fabric having a layer of water absorbing fibers on one surface and a layer of hydrophobic fibers on the other surface. The mask filter described.
水性不織布を積層してなることを特徴とする請求項１記
載のマスク用フィルタ。3. The mask filter according to claim 1, wherein the sheet material is formed by laminating a hydrophobic nonwoven fabric on the water absorbent nonwoven fabric.
なるマスク本体部と、該マスク本体部に設けられ顔面に
装着するための装着部とを具備したマスクであって、 前記マスク本体部が吸水性繊維を含有する吸水性不織布
と疎水性不織布を少なくとも含むシート材から構成さ
れ、該シート材に液体を保持させ、該シート材の含液率
１５ｖ／ｖ％〜９０ｖ／ｖ％としたときの該シート材の
通気度が１５ cc／cm２／sec〜８０ cc／cm２／sec で
あることを特徴とするマスク。4. A mask comprising: a mask main body made of a breathable sheet material for covering a mouth and a nose; and a mounting portion provided on the mask main body for mounting on the face. Part is made of a sheet material containing at least a water-absorbent nonwoven fabric containing a water-absorbent fiber and a hydrophobic nonwoven fabric, the sheet material is made to retain a liquid, and the liquid content of the sheet material is 15 v / v% to 90 v / v%. mask, wherein the air permeability of the sheet material when it is 15 cc / cm 2 / sec~80 cc / cm 2 / sec.
性繊維との混紡であることを特徴とする請求項１乃至３
のいずれか１つに記載のマスク用フィルタ。5. The water-absorbent non-woven fabric is a mixed spinning of water-absorbent fibers and hydrophobic fibers.
The mask filter according to any one of 1.
で鞘が高吸水性樹脂である芯鞘構造の繊維であることを
特徴とする請求項１乃至５のいずれか１つに記載のマス
ク用フィルタ又はマスク。6. The mask according to any one of claims 1 to 5, wherein the water-absorbent fiber is a fiber having a core-sheath structure in which a core is a polyolefin and a sheath is a highly water-absorbent resin. Filter or mask.
疎水性繊維との混紡割合が、２０：８０〜８０：２０の
割合であることを特徴とする請求項１記載のマスク用フ
ィルタ又は請求項４記載のマスク。7. The mask filter according to claim 1, wherein the water-absorbent nonwoven fabric has a mixed spinning ratio of the water-absorbent fibers and the hydrophobic fibers of 20:80 to 80:20. The mask according to claim 4.
面の色が、互いに異なることを特徴とする請求項３乃至
７のいずれか１つに記載のマスク用フィルタ又はマス
ク。8. The mask filter or mask according to claim 3, wherein the color of one surface of the sheet material and the color of the other surface are different from each other.