JP2003116371A - Paper mulch - Google Patents

Paper mulch

Info

Publication number
JP2003116371A
JP2003116371A JP2001314512A JP2001314512A JP2003116371A JP 2003116371 A JP2003116371 A JP 2003116371A JP 2001314512 A JP2001314512 A JP 2001314512A JP 2001314512 A JP2001314512 A JP 2001314512A JP 2003116371 A JP2003116371 A JP 2003116371A
Authority
JP
Japan
Prior art keywords
paper
biodegradable resin
mulch
paper mulch
water vapor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001314512A
Other languages
Japanese (ja)
Inventor
Noboru Yajima
昇 矢島
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MARUO SEISHI KK
Original Assignee
MARUO SEISHI KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MARUO SEISHI KK filed Critical MARUO SEISHI KK
Priority to JP2001314512A priority Critical patent/JP2003116371A/en
Publication of JP2003116371A publication Critical patent/JP2003116371A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a paper mulch having biodegradability, and further having high wet strength and good water resistance, having high tensile strength, light so that its workability in laying operation is good, and capable of being easily controlled in an acceleration rate of its biodegradation. SOLUTION: This paper mulch is made by adhering a biodegradable resin film to paper composed solely of deinked waste paper pulp or containing the deinked waste paper pulp, or applying a solution obtained by dissolving the biodegradable resin in a solvent, a dispersion of the biodegradable resin or an emulsion thereof to the paper, wherein the paper as a base material is controlled so as to have a basis weight of 20-60 g/m<2> and a water vapor transmission rate of >=400 g/m<2> .24 hr.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、水田、休耕田、畑
作等に用いて好適な紙マルチに関する。TECHNICAL FIELD The present invention relates to a paper mulch suitable for use in paddy fields, fallow fields, upland fields and the like.

【０００２】[0002]

【従来の技術】水田用紙マルチは、水田に敷設されて用
いられ、雑草除去等に供される。従来、紙を基材として
薬剤を無添加とする、特許2762005の如くの農業用紙マ
ルチは、生分解性を有するから、使用後の回収作業及び
焼却処分を必要としない利点がある。2. Description of the Related Art Paddy paper mulch is laid in a paddy field and used for removing weeds. Conventionally, an agricultural paper mulch as described in Japanese Patent No. 2762005, which uses paper as a base material and has no added chemicals, has biodegradability, and therefore has an advantage of not requiring recovery work and incineration disposal after use.

【０００３】[0003]

【発明が解決しようとする課題】しかしながら、従来の
紙マルチでは、生分解性を有するものの、湿潤強度が弱
く耐水性が悪い、引張強度が弱い、重くて敷設作業性が
悪い、生分解促進度を制御しずらい等の問題点がある。However, although the conventional paper mulch has biodegradability, it has weak wet strength and poor water resistance, poor tensile strength, heavy and poor laying workability, and degree of biodegradation promotion. Is difficult to control.

【０００４】本発明の課題は、生分解性を有しながら、
湿潤強度が強くて耐水性が良く、引張強度が強く、軽く
て敷設作業性が良く、生分解促進度の制御が容易な紙マ
ルチを提供することにある。An object of the present invention is to have biodegradability while
(EN) A paper mulch having high wet strength and water resistance, high tensile strength, light weight, good laying workability, and easy control of biodegradation acceleration.

【０００５】[0005]

【課題を解決するための手段】請求項１の発明は、脱墨
古紙パルプ単独或いは脱墨古紙パルプを含む紙に生分解
樹脂フィルムを貼り合わせ、又は生分解樹脂を溶剤に溶
かした溶液もしくは生分解樹脂のディスパージョン或い
はエマルジョンで加工を施し、基材としての紙の坪量を
20ｇ／m２から60ｇ／m２に制御し、水蒸気透過率を400
ｇ／m２・24時間以上に制御した、紙マルチである。According to a first aspect of the present invention, a biodegradable resin film is attached to deinked waste paper pulp alone or a paper containing the deinked waste paper pulp, or a solution or raw solution in which the biodegradable resin is dissolved in a solvent. Treated with a dispersion of a decomposition resin or emulsion to reduce the basis weight of paper as a base material.
Controlled from 20g / m 2 to 60g / m 2 and water vapor permeability of 400
Paper mulch controlled at g / m 2 · 24 hours or more.

【０００６】請求項２の発明は、請求項１の発明におい
て更に、生分解樹脂が澱粉脂肪酸エステル、ポリ乳酸、
ポリブチレンサクシネート、ポリブチレンサクシネート
アジペート、ポリブチレンアジペートテレフタレート、
ポリカプロラクトン、ポリハイドロキシアルカノエート
及びポリエステルカーボネートの１種又は２種以上のコ
ンバウンドから形成されるようにしたものである。According to a second aspect of the invention, in addition to the first aspect, the biodegradable resin is starch fatty acid ester, polylactic acid,
Polybutylene succinate, polybutylene succinate adipate, polybutylene adipate terephthalate,
It is formed from a combination of one or more of polycaprolactone, polyhydroxyalkanoate and polyester carbonate.

【０００７】請求項３の発明は、請求項１又は２の発明
において更に、生分解樹脂フィルムの貼り合わせを行な
って得られる紙マルチにおいて、貼り合わせ処理前のフ
ィルムに予め微細な穴あけ処理を行なっておくこと、或
いは貼り合わせ処理後に微細な穴あけ加工を施すことを
特徴とするものである。According to a third aspect of the present invention, further, in the paper mulch obtained by laminating biodegradable resin films according to the first or second aspect of the present invention, the film before laminating is preliminarily subjected to fine perforating treatment. It is characterized in that it is preliminarily prepared, or a fine drilling process is performed after the bonding process.

【０００８】請求項４の発明は、請求項１〜３のいずれ
かの発明において更に、生分解樹脂フィルムの貼り合わ
せを行なって得られる紙マルチにおいて、紙マルチの伸
縮性と更なる透気度・水蒸気透過率を付与するためのエ
ンボス処理を施すことを特徴とするものである。A fourth aspect of the present invention is the paper mulch obtained by further laminating biodegradable resin films according to any one of the first to third aspects, wherein the paper mulch has elasticity and further air permeability. An embossing treatment for imparting water vapor transmission rate is performed.

【０００９】請求項５の発明は、請求項１〜４のいずれ
かの発明において更に、生分解樹脂の紙への加工方法
が、塗工・サイズプレス・内添・含浸処理の各処理方法
単独或いは組合わせにより行なわれるものである。According to a fifth aspect of the present invention, in addition to the method according to any one of the first to fourth aspects, the method of processing the biodegradable resin into paper includes coating, size press, internal addition and impregnation. Alternatively, the combination is performed.

【００１０】[0010]

【作用】紙マルチは、紙と生分解樹脂からなるもので
あり、紙も生分解樹脂も生分解性を有するものであるか
ら、使用後は自然界の微生物により分解され、最終的に
は水と二酸化炭素等の無機物に分解され、使用後の回収
作業及び焼却処分を必要としない。[Function] Paper mulch is composed of paper and biodegradable resin. Since both paper and biodegradable resin have biodegradability, they are decomposed by microorganisms in the natural world after use, and finally they are treated with water. Decomposed into inorganic substances such as carbon dioxide, so there is no need for recovery work or incineration after use.

【００１１】紙マルチを構成する生分解樹脂が紙マル
チの湿潤強度を強くし、耐水性が向上する。The biodegradable resin constituting the paper mulch strengthens the wet strength of the paper mulch and improves the water resistance.

【００１２】紙マルチを構成する生分解樹脂が紙マル
チの引張強度を強くし、単位強度あたりの重量を軽量化
できるから、紙マルチを薄物化でき、敷設作業性を向上
できる。Since the biodegradable resin constituting the paper mulch can increase the tensile strength of the paper mulch and reduce the weight per unit strength, the paper mulch can be made thin and the laying workability can be improved.

【００１３】紙マルチを構成する生分解樹脂の添加量
比率を調整することにより、又は生分解樹脂の品種（品
種により生分解速度が異なる）の選定により、紙マルチ
の生分解促進度を容易に制御できる。これにより、紙マ
ルチの用途先毎に異なる必要使用期間に応じた寿命を紙
マルチに具備せしめることができる。また、使用後に土
中に鍬込まれてからの紙マルチの分解完了期間も制御で
きる。The degree of biodegradation promotion of the paper mulch can be facilitated by adjusting the addition ratio of the biodegradable resin constituting the paper mulch or by selecting the type of biodegradable resin (the biodegradation rate differs depending on the type). You can control. As a result, it is possible to provide the paper mulch with a life according to the required usage period that differs depending on the intended use of the paper mulch. In addition, it is possible to control the disassembly completion period of the paper mulch after it is ground into the soil after use.

【００１４】基材としての紙の坪量を20ｇ／m２から6
0ｇ／m２に制御した。20ｇ／m２以上とすることにより
紙マルチに十分な強度を確保でき、60ｇ／m２以下とす
ることにより生分解樹脂の水中分解性を確保できる。60
ｇ／m２以上にすると重量的にハンドリングに無理が生
じる。The basis weight of paper as a base material is 20 g / m 2 to 6
It was controlled to 0 g / m 2 . When it is 20 g / m 2 or more, sufficient strength can be secured for the paper mulch, and when it is 60 g / m 2 or less, the biodegradability of the biodegradable resin in water can be secured. 60
If it is set to g / m 2 or more, handling becomes difficult due to weight.

【００１５】水蒸気透過率を400ｇ／m２・24時間以上
に制御した。従って、紙マルチに覆われた水田等で生じ
た微生物の腐敗ガス等を外界に向けて脱気でき、紙マル
チにガスたまりに起因するふくらみを生ずることがな
く、紙マルチの安定した敷設状態を維持できる。The water vapor transmission rate was controlled to 400 g / m 2 · 24 hours or more. Therefore, the spoilage gas of microorganisms generated in paddy fields covered with paper mulch can be degassed to the outside world, and the bulging due to the gas accumulation does not occur in the paper mulch, and the stable laid state of the paper mulch can be maintained. Can be maintained.

【００１６】[0016]

【発明の実施の形態】（第１実施形態）第１実施形態の
水田用紙マルチ１０は、脱墨古紙パルプ単独或いは脱墨
古紙パルプを含む紙１１に生分解樹脂フィルム１２を貼
り合わせたものであり、以下の如くに製造される。BEST MODE FOR CARRYING OUT THE INVENTION (First Embodiment) A paddy paper mulch 10 according to the first embodiment is obtained by laminating a biodegradable resin film 12 on a paper 11 containing deinked waste paper pulp alone or containing deinked waste paper pulp. Yes, it is manufactured as follows.

【００１７】(1)紙１１の作成工程 脱墨古紙パルプ単独或いは脱墨古紙パルプを含む紙１１
を抄紙機で抄造する。紙１１は坪量を20ｇ／m２から60
ｇ／m２に制御される。20ｇ／m２未満では紙マルチ１０
に十分な強度が得られない。60ｇ／m２越えでは生分解
樹脂フィルム１２の水中分解性が悪い。(1) Process of making paper 11 Deinked waste paper pulp alone or paper 11 containing deinked waste paper pulp
Is made with a paper machine. Paper 11 has a basis weight of 20 g / m 2 to 60
It is controlled to g / m 2 . Paper mulch 10 at less than 20 g / m 2
Cannot obtain sufficient strength. If it exceeds 60 g / m 2 , the biodegradable resin film 12 has poor degradability in water.

【００１８】(2)生分解樹脂フィルム１２の作成工程 生分解樹脂フィルム１２を作成する。生分解樹脂フィル
ム１２は、澱粉脂肪酸エステル、ポリ乳酸、ポリブチレ
ンサクシネート、ポリブチレンサクシネートアジペー
ト、ポリブチレンアジペートテレフタレート、ポリカプ
ロラクトン、ポリハイドロキシアルカノエート及びポリ
エステルカーボネートの１種又は２種以上のコンパウン
ドから形成される。例えば、生分解樹脂フィルム１２は
生分解性脂肪族ポリエステル等を採用でき、液状、粉状
のものを採用できる。例えば、ビオノーレエマルジョン
ＯＬＸ−７５２７（昭和高分子（株）の脂肪族ポリエス
テル（ポリブチレンサクシネート、アジペート）水性エ
マルジョン等を採用できる。また、生分解性澱粉プラス
チックの生分解性ディスパージョン（ランディーｃｐ）
（ミヨシ油脂）等を採用できる。(2) Step of making biodegradable resin film 12 The biodegradable resin film 12 is made. The biodegradable resin film 12 is made of one or more compounds of starch fatty acid ester, polylactic acid, polybutylene succinate, polybutylene succinate adipate, polybutylene adipate terephthalate, polycaprolactone, polyhydroxyalkanoate and polyester carbonate. It is formed. For example, the biodegradable resin film 12 may be biodegradable aliphatic polyester or the like, and may be liquid or powdery. For example, a bionole emulsion OLX-7527 (Showa High Polymer Co., Ltd., aliphatic polyester (polybutylene succinate, adipate) aqueous emulsion, etc.) can be used, or a biodegradable dispersion (landy cp) of biodegradable starch plastic. )
(Miyoshi fats and oils) can be used.

【００１９】(3)生分解樹脂フィルム１２の貼り合わせ 紙１１に生分解樹脂フィルム１２を貼り合わせる。紙１
１と生分解樹脂フィルム１２の貼り合わせは、紙１１と
生分解樹脂フィルム１２の間に接着剤を介して接着す
る、又は紙１１に生分解樹脂フィルム１２を熱融着させ
ることにて行なうことができる。(3) Lamination of biodegradable resin film 12 The biodegradable resin film 12 is attached to the paper 11. Paper 1
1 and the biodegradable resin film 12 are adhered to each other by bonding the paper 11 and the biodegradable resin film 12 with an adhesive or by thermally bonding the biodegradable resin film 12 to the paper 11. You can

【００２０】(4)水蒸気透過率の付与 紙１１に生分解樹脂フィルム１２を貼り合わせたものの
水蒸気透過率を400ｇ／ｍ２・24時間以上に制御し、こ
れを紙マルチ１０とする。これにより、水田に敷設した
紙マルチ１０にガスだまりを生ずることがない。(4) Addition of Water Vapor Transmission Rate The paper 11 having the biodegradable resin film 12 bonded thereto is controlled to have a water vapor transmission rate of 400 g / m 2 · 24 hours or more to obtain a paper mulch 10. As a result, no gas accumulation occurs in the paper mulch 10 laid in the paddy field.

【００２１】具体的には、紙１１に生分解樹脂フィルム
１２を貼り合わせて得られる紙マルチ１０において、貼
り合わせ処理前の生分解樹脂フィルム１２に予め微細な
穴あけ処理を行なっておく、或いは貼り合わせ処理後の
生分解樹脂フィルム１２と紙１１に微細な穴あけ加工を
施すことにより、上述の水蒸気透過率を確保する。微細
な穴は穴径10μm以上、例えば穴径0.1mm、1mmである。Specifically, in the paper mulch 10 obtained by sticking the biodegradable resin film 12 to the paper 11, the biodegradable resin film 12 before the sticking process is preliminarily subjected to a fine perforation process or stuck. By subjecting the biodegradable resin film 12 and the paper 11 after the combination treatment to fine perforation processing, the above-mentioned water vapor transmission rate is secured. The fine holes have a hole diameter of 10 μm or more, for example, hole diameters of 0.1 mm and 1 mm.

【００２２】(5)エンボス処理 紙１１に生分解樹脂フィルム１２を貼り合わせて得られ
る紙マルチ１０の水田等への敷設に際しての展開作業性
を向上するための伸縮性と更なる透気度・水蒸気透過率
を付与するため、紙１１と生分解樹脂フィルム１２の貼
り合わせ体にエンボス処理を施す。この場合にも、貼り
合わせ処理前の生分解樹脂フィルム１２に予め微細な穴
あけ処理を行なっておく、或いは貼り合わせ処理後に生
分解樹脂フィルム１２と紙１１に微細な穴あけ加工を施
すことができ、エンボス処理と同時に微細な穴あけ加工
を施すこともできる。尚、紙マルチ１０において、エン
ボス処理により形成されて相隣る凸面と凹面のそれぞれ
の中心部に微細な穴を設けることができる。(5) Stretchability and further air permeability for improving deployment workability when laying a paper mulch 10 obtained by laminating a biodegradable resin film 12 on embossed paper 11 In order to give water vapor permeability, the bonded body of the paper 11 and the biodegradable resin film 12 is embossed. Also in this case, the biodegradable resin film 12 before the bonding process may be subjected to a fine perforation process in advance, or the biodegradable resin film 12 and the paper 11 may be subjected to a fine perforation process after the bonding process, It is also possible to perform fine drilling at the same time as embossing. In the paper mulch 10, fine holes can be provided at the central portions of the convex surface and the concave surface that are formed by embossing and are adjacent to each other.

【００２３】（第２実施形態）第２実施形態の水田用紙
マルチ１０は、脱墨古紙パルプ単独或いは脱墨古紙パル
プを含む紙１１に生分解樹脂を溶剤に溶かした溶液（も
しくは生分解樹脂のディスパージョン或いはエマルジョ
ン）で塗工したものであり、以下の如くに製造される。(Second Embodiment) The paddy paper mulch 10 of the second embodiment is a solution (or a biodegradable resin solution) obtained by dissolving a biodegradable resin in a solvent in a paper 11 containing deinked waste paper pulp alone or a paper 11 containing the deinked waste paper pulp. It is coated with a dispersion or emulsion and is manufactured as follows.

【００２４】(1)紙１１の作成工程 脱墨古紙パルプ単独或いは脱墨古紙パルプを含む紙１１
を抄紙機で抄造する。紙１１は坪量を20ｇ／m２から60
ｇ／m２に制御される。20ｇ／m２未満では紙マルチ１０
に十分な強度が得られない。60ｇ／m２越えでは生分解
樹脂１２の水中分解性が悪い。(1) Process for producing paper 11 Deinked waste paper pulp alone or paper 11 containing deinked waste paper pulp
Is made with a paper machine. Paper 11 has a basis weight of 20 g / m 2 to 60
It is controlled to g / m 2 . Paper mulch 10 at less than 20 g / m 2
Cannot obtain sufficient strength. If it exceeds 60 g / m 2 , the biodegradability of biodegradable resin 12 in water is poor.

【００２５】(2)生分解樹脂の塗工 紙１１に、ロールコータ等を用いて生分解樹脂１２を塗
工する。紙１１に対する生分解樹脂１２の塗工厚みをコ
ントロールし、紙１１の全面において均等塗工厚みもし
くは不均等塗工厚みとすることができる。また、生分解
樹脂１２は紙１１の全面に塗工するものに限らず、模様
付けするように紙１１の各部に分散塗工しても良い。こ
れにより、紙１１に対する生分解樹脂１２の付加量を容
易にコントロールできるし、紙１１に付与する後述の水
蒸気透過率を容易にコントロールできる。(2) The biodegradable resin 12 is coated on the biodegradable resin coated paper 11 using a roll coater or the like. The coating thickness of the biodegradable resin 12 on the paper 11 can be controlled so that the entire surface of the paper 11 has a uniform coating thickness or a non-uniform coating thickness. Further, the biodegradable resin 12 is not limited to the one coated on the entire surface of the paper 11, but may be dispersed and coated on each part of the paper 11 so as to be patterned. This makes it possible to easily control the amount of biodegradable resin 12 added to the paper 11 and easily control the water vapor permeability of the paper 11 which will be described later.

【００２６】生分解樹脂１２は、澱粉脂肪酸エステル、
ポリ乳酸、ポリブチレンサクシネート、ポリブチレンサ
クシネートアジペート、ポリブチレンアジペートテレフ
タレート、ポリカプロラクトン、ポリハイドロキシアル
カノエート及びポリエステルカーボネートの１種又は２
種以上のコンパウンドから形成される。例えば、生分解
樹脂１２は生分解性脂肪族ポリエステル等を採用でき、
液状、粉状のものを採用できる。例えば、ビオノーレエ
マルジョンＯＬＸ−７５２７（昭和高分子（株）の脂肪
族ポリエステル（ポリブチレンサクシネート、アジペー
ト）水性エマルジョン等を採用できる。また、生分解性
澱粉プラスチックの生分解性ディスパージョン（ランデ
ィーｃｐ）（ミヨシ油脂）等を採用できる。The biodegradable resin 12 is a starch fatty acid ester,
One or two of polylactic acid, polybutylene succinate, polybutylene succinate adipate, polybutylene adipate terephthalate, polycaprolactone, polyhydroxyalkanoate and polyester carbonate
Formed from more than one compound. For example, the biodegradable resin 12 may be biodegradable aliphatic polyester,
Liquid or powder can be used. For example, a bionole emulsion OLX-7527 (Showa High Polymer Co., Ltd., aliphatic polyester (polybutylene succinate, adipate) aqueous emulsion, etc.) can be used, or a biodegradable dispersion (landy cp) of biodegradable starch plastic. ) (Miyoshi fats and oils) can be used.

【００２７】(3)水蒸気透過率の付与 紙１１に生分解樹脂１２を塗工したものの水蒸気透過率
を400ｇ／ｍ２・24時間以上に制御し、これを紙マルチ
１０とする。これにより、水田に敷設した紙マルチ１０
にガスだまりを生ずることがない。(3) Water vapor transmission rate The paper 11 coated with the biodegradable resin 12 is controlled to have a water vapor transmission rate of 400 g / m 2 · 24 hours or more to obtain a paper mulch 10. As a result, the paper mulch 10 laid in the paddy field
There is no gas accumulation in.

【００２８】具体的には、紙１１に生分解樹脂１２を塗
工して得られる紙マルチ１０において、生分解樹脂１２
の塗膜量の調整、紙１１に対する生分解樹脂１２の塗工
領域の調整により、上述の水蒸気透過率を確保する。紙
１１において生分解樹脂１２が付加されない領域の水蒸
気透過率は、紙１１そのものの水蒸気透過率を呈するこ
とになる。Specifically, in the paper mulch 10 obtained by coating the paper 11 with the biodegradable resin 12, the biodegradable resin 12 is used.
The above-mentioned water vapor transmission rate is secured by adjusting the amount of coating film and adjusting the coating area of the biodegradable resin 12 on the paper 11. The water vapor transmission rate of the area where the biodegradable resin 12 is not added on the paper 11 is the water vapor transmission rate of the paper 11 itself.

【００２９】生分解樹脂１２を塗工した後の紙１１に微
細な穴あけ加工を施すことにより、上述の水蒸気透過率
を確保しても良い。微細な穴は穴径10μm以上、例えば
穴径0.1mm、1mmである。The above-mentioned water vapor transmission rate may be secured by finely perforating the paper 11 after coating the biodegradable resin 12. The fine holes have a hole diameter of 10 μm or more, for example, hole diameters of 0.1 mm and 1 mm.

【００３０】(4)エンボス処理 紙１１に生分解樹脂１２を塗工して得られる紙マルチ１
０の水田等への敷設に際しての展開作業性を向上するた
めの伸縮性と更なる透気度・水蒸気透過率を付与するた
め、塗工処理後の紙１１にエンボス処理を施す。尚、紙
マルチ１０において、エンボス処理により形成されて相
隣る凸面と凹面のそれぞれの中心部に微細な穴を設ける
ことができる。(4) Paper mulch 1 obtained by coating biodegradable resin 12 on embossed paper 11
The paper 11 after the coating treatment is embossed in order to impart stretchability and further air permeability and water vapor permeability for improving the workability of deployment when laying 0 in a paddy field. In the paper mulch 10, fine holes can be provided at the central portions of the convex surface and the concave surface that are formed by embossing and are adjacent to each other.

【００３１】（第３実施形態）第３実施形態の紙マルチ
１０は、脱墨古紙パルプ単独或いは脱墨古紙パルプを含
む紙１１に生分解樹脂のディスパージョン或いはエマル
ジョン（もしくは生分解樹脂を溶剤に溶かした溶液）を
内添したものであり、抄紙機で、以下の如くに製造され
る。(Third Embodiment) A paper mulch 10 according to the third embodiment is a dispersion of a biodegradable resin or an emulsion (or a biodegradable resin as a solvent) in a paper 11 containing deinked waste paper pulp alone or a paper 11 containing the deinked waste paper pulp. (Melted solution) is added internally, and it is produced by a paper machine as follows.

【００３２】(1)原料作成工程 脱墨古紙パルプ単独或いは脱墨古紙パルプを含む紙１１
を、生分解樹脂１２と定着剤１３を溶剤に溶かした溶液
又は生分解樹脂１２のディスパージョン或いはエマルジ
ョンに混合して原料を作成する。(1) Raw material preparation process Paper 11 containing deinked waste paper pulp alone or containing deinked waste paper pulp 11
Is mixed with a solution obtained by dissolving the biodegradable resin 12 and the fixing agent 13 in a solvent or a dispersion or emulsion of the biodegradable resin 12 to prepare a raw material.

【００３３】生分解樹脂１２は、澱粉脂肪酸エステル・
ポリ乳酸・ポリブチレンサクシネート・ポリブチレンサ
クシネートアジペート・ポリブチレンアジペートテレフ
タレート・ポリカプロラクトン・ポリハイドロキシアル
カノエート及びポリエステルカーボネートの１種又は２
種以上のコンパウンドから形成される。例えば、生分解
樹脂１２は生分解性脂肪族ポリエステル等を採用でき、
液状、粉状のものを採用できる。例えば、ビオノーレエ
マルジョンＯＬＸ−７５２７（昭和高分子（株）の脂肪
族ポリエステル（ポリブチレンサクシネート、アジペー
ト）水性エマルジョン等を採用できる。The biodegradable resin 12 is a starch fatty acid ester.
One or two of polylactic acid / polybutylene succinate / polybutylene succinate adipate / polybutylene adipate terephthalate / polycaprolactone / polyhydroxyalkanoate and polyester carbonate
Formed from more than one compound. For example, the biodegradable resin 12 may be biodegradable aliphatic polyester,
Liquid or powder can be used. For example, a bionole emulsion OLX-7527 (Showa High Polymer Co., Ltd. aliphatic polyester (polybutylene succinate, adipate) aqueous emulsion or the like can be used.

【００３４】定着剤１３はスチレン系定着剤（例えば、
セラフィックスＳＴ（明成化学（株））、ポリアクリル
アミド系定着剤（例えば、マイネックＭ（明成化学
（株））、ファイレックスＭ（明成化学（株））を採用
できる。The fixing agent 13 is a styrene type fixing agent (for example,
Cerafix ST (Meisei Chemical Co., Ltd.), polyacrylamide-based fixing agent (for example, Myneck M (Meisei Chemical Co., Ltd.), and Pyrex M (Meisei Chemical Co., Ltd.) can be used.

【００３５】原料において、基材としての紙１１は坪量
20ｇ／ｍ２から80ｇ／ｍ２であることが好ましい。20ｇ
／ｍ２未満では生分解樹脂加工紙マルチ１０に十分な強
度が得られない。80ｇ／ｍ２越えでは生分解樹脂加工紙
マルチ１０の単位強度当たりの重量が重くなってハンド
リング性を損なう。In the raw material, the paper 11 as the base material has a basis weight.
It is preferably 20 g / m 2 to 80 g / m 2 . 20 g
If it is less than / m 2 , the biodegradable resin-processed paper mulch 10 cannot have sufficient strength. If it exceeds 80 g / m 2 , the weight per unit strength of the biodegradable resin-coated paper mulch 10 becomes heavy and the handling property is impaired.

【００３６】また、原料において、脱墨古紙パルプ単独
或いは脱墨古紙パルプを含む紙１１の加工に使用される
生分解樹脂１２は、紙マルチ１０の用途に応じて、ベー
スの紙１ｍ２当たり5ｇから40ｇであることが好まし
い。紙マルチ１０がとうもろこしの如くの床畝に2ヶ月
半程度使用される場合には、紙１ｍ２当たり5ｇの生分
解樹脂１２を添加する。紙マルチ１０が落花生、玉ねぎ
の如くの床畝に6ヶ月程度使用される場合には、紙１ｍ
２当たり40ｇの生分解樹脂１２を添加する。In the raw material, the biodegradable resin 12 used for processing the deinked waste paper pulp alone or the paper 11 containing the deinked waste paper pulp is 5 g per 1 m 2 of the base paper depending on the use of the paper mulch 10. To 40 g is preferred. When the paper mulch 10 is used for floor ridges such as corn for about two and a half months, 5 g of biodegradable resin 12 is added per 1 m 2 of paper. When the paper mulch 10 is used for floor ridges such as peanuts and onions for about 6 months, 1 m of paper
40 g of biodegradable resin 12 per 2 are added.

【００３７】従って、紙１１と生分解樹脂１２と定着剤
１３の好適な混合比率（重量％）は、紙１１が70％〜95
％、生分解樹脂１２が30％〜5％、定着剤１３が2％〜7
％である。Therefore, the preferable mixing ratio (weight%) of the paper 11, the biodegradable resin 12, and the fixing agent 13 is 70% to 95 for the paper 11.
%, Biodegradable resin 12 is 30% to 5%, fixing agent 13 is 2% to 7%
%.

【００３８】(2)シート成形工程 上述(1)の原料をヘッドボックスからワイヤパートに供
給し、更にプレスパートへと移送し、シートに成形す
る。このワイヤパートとプレスパートにおけるシート成
形の過程で、生分解樹脂１２を定着剤１３により紙１１
に定着する。(2) Sheet Forming Step The raw material of the above (1) is supplied from the head box to the wire part, further transferred to the press part, and formed into a sheet. During the sheet forming process in the wire part and the press part, the biodegradable resin 12 is fixed to the paper 11 by the fixing agent 13.
Settles in.

【００３９】(3)シート乾燥工程 上述(2)のシートをドライヤパートに移送し、ドライヤ
を用いて乾燥する。このドライヤパートにおけるシート
乾燥の過程で、ドライヤによりシートの表面温度を100
℃以上（生分解樹脂１２の溶融温度以上）に加熱し、紙
１１に上述(2)で定着した生分解樹脂１２を熱溶融する
ことにより、生分解樹脂１２を膜状にして紙１１に広く
接着して内添せしめ、生分解樹脂加工紙マルチ１０とす
る。尚、生分解樹脂１２が上述のビオノーレである場合
の溶融温度は95℃である。(3) Sheet Drying Step The above-mentioned sheet (2) is transferred to a dryer part and dried using a dryer. In the process of drying the sheet in this dryer part, the surface temperature of the sheet is controlled to 100 by the dryer.
The biodegradable resin 12 is heated to a temperature of ℃ or more (above the melting temperature of the biodegradable resin 12) and the biodegradable resin 12 fixed on the paper 11 in the above (2) is heat-melted to form a film of the biodegradable resin 12 and widely It is adhered and internally added to obtain a biodegradable resin processed paper mulch 10. The melting temperature when the biodegradable resin 12 is the above-mentioned bionole is 95 ° C.

【００４０】(4)巻取り工程 上述(3)の生分解樹脂加工紙マルチ１０をリールに巻取
る。(4) Winding Step The biodegradable resin processed paper mulch 10 in (3) above is wound on a reel.

【００４１】(5)水蒸気透過率の付与 紙１１に生分解樹脂１２を内添したものの水蒸気透過率
を400ｇ／ｍ２・24時間以上に制御し、これを紙マルチ
１０とする。これにより、水田に敷設した紙マルチ１０
にガスだまりを生ずることがない。(5) Provision of water vapor transmission rate The water vapor transmission rate of the paper 11 in which the biodegradable resin 12 is internally added is controlled to 400 g / m 2 · 24 hours or more, and this is used as the paper mulch 10. As a result, the paper mulch 10 laid in the paddy field
There is no gas accumulation in.

【００４２】具体的には、紙１１に生分解樹脂１２を内
添した紙マルチ１０において、生分解樹脂１２の内添量
の調整、紙１１における生分解樹脂１２の内添領域の調
整により、上述の水蒸気透過率を確保する。紙１１にお
いて生分解樹脂１２が内添されない領域の水蒸気透過率
は、紙１１そのものの水蒸気透過率を呈することにな
る。Specifically, in the paper mulch 10 in which the biodegradable resin 12 is internally added to the paper 11, the internal addition amount of the biodegradable resin 12 is adjusted and the internal addition area of the biodegradable resin 12 in the paper 11 is adjusted. Ensure the above water vapor transmission rate. The water vapor transmission rate of the area where the biodegradable resin 12 is not internally added in the paper 11 indicates the water vapor transmission rate of the paper 11 itself.

【００４３】生分解樹脂１２を内添した後の紙１１に微
細な穴あけ加工を施すことにより、上述の水蒸気透過率
を確保しても良い。微細な穴は穴径10μm以上、例えば
穴径0.1mm、1mmである。The above-mentioned water vapor transmission rate may be secured by finely perforating the paper 11 after the biodegradable resin 12 is internally added. The fine holes have a hole diameter of 10 μm or more, for example, hole diameters of 0.1 mm and 1 mm.

【００４４】(6)エンボス処理 紙１１に生分解樹脂１２を内添して得られる紙マルチ１
０の水田等への敷設に際しての展開作業性を向上するた
めの伸縮性と更なる透気度・水蒸気透過率を付与するた
め、内添処理後の紙１１にエンボス処理を施す。尚、紙
マルチ１０において、エンボス処理により形成されて相
隣る凸面と凹面のそれぞれの中心部に微細な穴を設ける
ことができる。(6) Paper mulch 1 obtained by internally adding biodegradable resin 12 to embossed paper 11
The paper 11 after the internal addition treatment is embossed in order to impart stretchability for improving the workability of deployment when laying 0 in a paddy field and the like and further air permeability and water vapor permeability. In the paper mulch 10, fine holes can be provided at the central portions of the convex surface and the concave surface that are formed by embossing and are adjacent to each other.

【００４５】第１実施形態〜第３実施形態の紙マルチ１
０によれば以下の作用がある。 紙マルチ１０は、紙１１と生分解樹脂１２からなるも
のであり、紙１１も生分解樹脂１２も生分解性を有する
ものであるから、使用後は自然界の微生物により分解さ
れ、最終的には水と二酸化炭素等の無機物に分解され、
使用後の回収作業及び焼却処分を必要としない。Paper mulch 1 according to the first to third embodiments
According to 0, there is the following effect. The paper mulch 10 is composed of the paper 11 and the biodegradable resin 12, and since both the paper 11 and the biodegradable resin 12 have biodegradability, they are decomposed by microorganisms in the natural world after use and finally Decomposed into water and inorganic substances such as carbon dioxide,
No recovery work or incineration after use is required.

【００４６】紙マルチ１０を構成する生分解樹脂１２
が紙マルチ１０の湿潤強度を強くし、耐水性が向上す
る。Biodegradable resin 12 constituting the paper mulch 10
Enhances the wet strength of the paper mulch 10 and improves the water resistance.

【００４７】尚、紙１１の湿潤強度0.3kgf／cm２に対
し、生分解樹脂１２の湿潤強度は前述のビオノーレにお
いて190〜330kgf／cm２である。The wet strength of the paper 11 is 0.3 kgf / cm 2, whereas the wet strength of the biodegradable resin 12 is 190 to 330 kgf / cm 2 in the bionole.

【００４８】紙マルチ１０を構成する生分解樹脂１２
が紙マルチ１０の引張強度を強くし、単位強度あたりの
重量を軽量化できるから、紙マルチ１０を薄物化でき、
敷設作業性を向上できる。Biodegradable resin 12 constituting the paper mulch 10
Since the tensile strength of the paper mulch 10 can be increased and the weight per unit strength can be reduced, the paper mulch 10 can be thinned,
Laying workability can be improved.

【００４９】尚、紙１１の引張強度4.2kgf／cm２に対
し、生分解樹脂１２の引張強度は前述のビオノーレにお
いて5.85kgf／cm２である。[0049] Incidentally, with respect to tensile strength 4.2kgf / cm 2 of paper 11, the tensile strength of the biodegradable resin 12 is 5.85kgf / cm 2 in the aforementioned Bionolle.

【００５０】紙マルチ１０を構成する生分解樹脂１２
の添加量比率を調整することにより、又は生分解樹脂１
２の品種（品種により生分解速度が異なる）の選定によ
り、紙マルチ１０の生分解促進度を容易に制御できる。
これにより、紙マルチ１０の用途先毎に異なる必要使用
期間に応じた寿命を紙マルチ１０に具備せしめることが
できる。また、使用後に土中に鍬込まれてからの紙マル
チ１０の分解完了期間も制御できる。Biodegradable resin 12 constituting the paper mulch 10
Biodegradable resin 1
The biodegradation promotion degree of the paper mulch 10 can be easily controlled by selecting two types (the biodegradation rate differs depending on the type).
As a result, the paper mulch 10 can be provided with a life according to the required usage period that differs depending on the intended use of the paper mulch 10. Further, it is possible to control the disassembly completion period of the paper mulch 10 after it is ground into the soil after use.

【００５１】例えば、生分解樹脂１２として前述のビオ
ノーレを採用した場合、紙１１に対する生分解樹脂１２
の添加量比率（紙１１の100重量部に対し生分解樹脂１
２の添加重量部がなす比率）を、10とするときの紙マル
チ１０の寿命（生分解開始までの使用可能期間）は0.5
〜1カ月、30とするときの紙マルチ１０の寿命は1〜3カ
月になる。For example, when the aforementioned bionole is used as the biodegradable resin 12, the biodegradable resin 12 for the paper 11 is used.
Addition ratio (1 biodegradable resin to 100 parts by weight of paper 11)
The life of the paper mulch 10 (usable period until the start of biodegradation) is 0.5 when the ratio of 2 parts by weight added) is 10.
The life of the paper mulch 10 at 1 to 30 months is 1 to 3 months.

【００５２】基材としての紙１１の坪量を20ｇ／m２
から60ｇ／m２に制御した。20ｇ／m ２以上とすることに
より紙マルチ１０に十分な強度を確保でき、60ｇ／m２
以下とすることにより生分解樹脂１２の水中分解性を確
保できる。The basis weight of the paper 11 as the base material is 20 g / m.Two
To 60 g / mTwoControlled to. 20 g / m TwoTo do more
More secure enough for paper mulch 10, 60g / mTwo
Ensure the biodegradability of biodegradable resin 12 in water by
Can be kept.

【００５３】水蒸気透過率を400ｇ／m２・24時間以上
に制御した。従って、紙マルチ１０に覆われた水田等で
生じた微生物の腐敗ガス等を外界に向けて脱気でき、紙
マルチ１０にガスたまりに起因するふくらみを生ずるこ
とがなく、紙マルチ１０の安定した敷設状態を維持でき
る。The water vapor transmission rate was controlled to 400 g / m 2 · 24 hours or more. Therefore, the spoilage gas of microorganisms generated in the paddy field covered with the paper mulch 10 can be degassed to the outside, and the bulge due to the gas accumulation does not occur in the paper mulch 10 and the paper mulch 10 is stable. The laid condition can be maintained.

【００５４】尚、本発明の紙マルチは、脱墨古紙パルプ
単独或いは脱墨古紙パルプを含む紙に、生分解樹脂を溶
剤に溶かした溶液もしくは生分解樹脂のディスパージョ
ン或いはエマルジョンでサイズプレス、含浸処理等の加
工を施して作成されるものでも良い。そして、その際の
生分解樹脂の紙への加工方法は、塗工・サイズプレス・
内添・含浸処理の各処理方法の組合わせにより行なうこ
とができる。The paper mulch of the present invention is a size press or impregnated with a solution obtained by dissolving biodegradable resin in a solvent, or a dispersion or emulsion of biodegradable resin, on a paper containing deinked waste paper pulp alone or containing deinked waste paper pulp. It may be created by processing such as processing. And the method of processing biodegradable resin into paper at that time is coating, size press,
It can be carried out by a combination of internal addition and impregnation treatment methods.

【００５５】また、本発明の紙マルチは、脱墨古紙パル
プ単独或いは脱墨古紙パルプを含む紙に、生分解樹脂を
溶剤に溶かした溶液もしくは生分解樹脂のディスパージ
ョン或いはエマルジョンで塗工・サイズプレス・内添・
含浸処理等の加工を施し、その加工後の紙に生分解樹脂
フィルムを貼り合わせて作成されるものでもよい。Further, the paper mulch of the present invention is applied to a deinked waste paper pulp alone or a paper containing the deinked waste paper pulp with a solution in which a biodegradable resin is dissolved in a solvent or a dispersion or emulsion of the biodegradable resin. Press, internal attachment,
It may be produced by subjecting a paper after the treatment such as impregnation treatment to a biodegradable resin film.

【００５６】以上、本発明の実施の形態を詳述したが、
本発明の具体的な構成はこの実施の形態に限られるもの
ではなく、本発明の要旨を逸脱しない範囲の変更等があ
っても本発明に含まれる。The embodiment of the present invention has been described in detail above.
The specific configuration of the present invention is not limited to this embodiment, and modifications and the like within the scope of the present invention are included in the present invention.

【００５７】[0057]

【発明の効果】以上のように本発明によれば、生分解性
を有しながら、湿潤強度が強くて耐水性が良く、引張強
度が強く、軽くて敷設作業性が良く、生分解促進度の制
御が容易な紙マルチを得ることができる。As described above, according to the present invention, while having biodegradability, the wet strength is strong and the water resistance is good, the tensile strength is strong, the weight is light and the laying workability is good, and the degree of biodegradation acceleration is high. It is possible to obtain a paper mulch that is easy to control.

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 脱墨古紙パルプ単独或いは脱墨古紙パル
プを含む紙に生分解樹脂フィルムを貼り合わせ、又は生
分解樹脂を溶剤に溶かした溶液もしくは生分解樹脂のデ
ィスパージョン或いはエマルジョンで加工を施し、基材
としての紙の坪量を20ｇ／m２から60ｇ／m２に制御し、
水蒸気透過率を400ｇ／m２・24時間以上に制御した、紙
マルチ。1. A biodegradable resin film is attached to deinked waste paper pulp alone or paper containing deinked waste paper pulp, or processed with a solution of biodegradable resin in a solvent or a dispersion or emulsion of biodegradable resin. , Controlling the basis weight of the paper as a base material from 20 g / m 2 to 60 g / m 2 ,
The water vapor permeability was controlled to 400g / m 2 · 24 hours or more, paper multi. 【請求項２】 生分解樹脂が澱粉脂肪酸エステル、ポリ
乳酸、ポリブチレンサクシネート、ポリブチレンサクシ
ネートアジペート、ポリブチレンアジペートテレフタレ
ート、ポリカプロラクトン、ポリハイドロキシアルカノ
エート及びポリエステルカーボネートの１種又は２種以
上のコンバウンドから形成される、請求項１に記載の紙
マルチ。2. The biodegradable resin is one or more of starch fatty acid ester, polylactic acid, polybutylene succinate, polybutylene succinate adipate, polybutylene adipate terephthalate, polycaprolactone, polyhydroxyalkanoate and polyester carbonate. The paper mulch according to claim 1, which is formed from a conbound. 【請求項３】 生分解樹脂フィルムの貼り合わせを行な
って得られる紙マルチにおいて、貼り合わせ処理前のフ
ィルムに予め微細な穴あけ処理を行なっておくこと、或
いは貼り合わせ処理後に微細な穴あけ加工を施すことを
特徴とする、請求項１又は２に記載の紙マルチ。3. A paper mulch obtained by laminating biodegradable resin films, wherein the film before laminating is preliminarily subjected to fine perforating treatment, or fine lapping is performed after laminating. The paper mulch according to claim 1 or 2, characterized in that. 【請求項４】 生分解樹脂フィルムの貼り合わせを行な
って得られる紙マルチにおいて、紙マルチの伸縮性と更
なる透気度・水蒸気透過率を付与するためのエンボス処
理を施すことを特徴とする、請求項１〜３のいずれかに
記載の紙マルチ。4. A paper mulch obtained by laminating biodegradable resin films, characterized by being subjected to an embossing treatment for imparting elasticity and further air permeability and water vapor permeability to the paper mulch. The paper mulch according to claim 1. 【請求項５】 生分解樹脂の紙への加工方法が、塗工・
サイズプレス・内添・含浸処理の各処理方法単独或いは
組合わせにより行なわれる、請求項１〜４のいずれかに
記載の紙マルチ。5. The method of processing biodegradable resin into paper is
The paper mulch according to any one of claims 1 to 4, wherein the size mulling, internal addition, and impregnation treatments are performed individually or in combination.
JP2001314512A 2001-10-11 2001-10-11 Paper mulch Pending JP2003116371A (en)