JP2003074161A - Decorative finishing material having wettability - Google Patents
Decorative finishing material having wettabilityInfo
- Publication number
- JP2003074161A JP2003074161A JP2001265562A JP2001265562A JP2003074161A JP 2003074161 A JP2003074161 A JP 2003074161A JP 2001265562 A JP2001265562 A JP 2001265562A JP 2001265562 A JP2001265562 A JP 2001265562A JP 2003074161 A JP2003074161 A JP 2003074161A
- Authority
- JP
- Japan
- Prior art keywords
- finishing material
- humidity control
- makeup
- thin paper
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、建築用途向け等に
用いる、調湿性を有する板状の仕上げ材に対し、その調
湿性を損なわないようにして化粧を付与した、調湿性を
有する化粧仕上げ材に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a humidity-adjusting cosmetic finish, in which makeup is applied to a plate-like finishing material having humidity-controlling properties, which is used for construction purposes, etc. without impairing the humidity-controlling properties. It concerns materials.
【０００２】[0002]
【従来の技術】建築物は、人や家畜等の居住者、家具や
居住のための設備、もしくは紙製品や乾漆製品等を、外
部の環境そのものから遮断して保護するか、もしくは外
部の環境の変化を緩和して、それらに伝える役割を果た
すものである。外部の環境を構成する様々な因子の一つ
に湿度があり、湿度が高いと、皮膚や家具の表面が湿気
を帯びたり、水滴が付着することがあり、甚だしいとき
には黴の原因ともなる。また湿度が低いと、皮膚が乾燥
し、木工製品がひび割れると言った支障を来たす。いず
れにせよ、建築物内の空間の湿度を、ある好ましい範囲
に保つことが望まれる。2. Description of the Related Art Buildings are protected by protecting the occupants, such as people and livestock, furniture, equipment for living, paper products, dry lacquer products, etc., from the outside environment itself. The role of alleviating the changes in and communicating them. Humidity is one of the various factors that make up the external environment. When humidity is high, the skin and the surface of furniture can become moist and water droplets can adhere, which can cause mold in extreme cases. If the humidity is low, the skin will be dried and the woodworking products will be cracked. In any case, it is desirable to keep the humidity of the space within the building within a certain preferred range.
【０００３】従来から建築物の内装仕上げ材としては、
例えば、板状の石膏ボードがよく使用されている。石膏
ボードは、表裏および側面を、厚紙である石膏ボード原
紙で被覆した内部に、水和した石膏を心材として充填し
た構造を有し、鋸引き性等の加工性、難燃性に加えて、
表面が紙であることにより、壁紙等の施工性が優れてい
るものである。石膏ボードは、心材に石膏が使われてい
ることから、調湿性を有するものであると思われがちで
あるが、実際には、石膏ボードの調湿性は、一般的に調
湿性があると言われている木の板に比べて劣っており、
建築物内の湿度が高くなると吸湿し、湿度が低くなると
放湿して、湿度を調節する、いわゆる調湿の機能を充分
に有するとは言えないものであった。Conventionally, as an interior finishing material for buildings,
For example, a plate-shaped gypsum board is often used. Gypsum board has a structure in which the front and back and side surfaces are covered with gypsum board base paper which is cardboard, and hydrated gypsum is filled as a core material, in addition to workability such as sawing property and flame retardancy,
Since the surface is paper, the workability of wallpaper and the like is excellent. Gypsum board is often thought to have humidity control properties, because gypsum is used for the heartwood, but in reality, gypsum board is generally said to have humidity control properties. It is inferior to the wooden board
It cannot be said that the building has a so-called humidity control function of absorbing humidity when the humidity in the building is high and releasing it when the humidity is low to control the humidity.
【０００４】そこで、石膏ボードに調湿性を付与するた
め、心材の石膏に様々な調湿剤を含有させて吸放湿性を
向上させ、調湿の機能を発揮し得る程度の高度な吸放湿
性を石膏ボードに付与する試みがなされ、主として、無
機系の吸放湿性物質を含有させることにより、木製の板
を仕上げ材として用いた場合と同程度の吸放湿性、即ち
調湿性を有する石膏ボードが得られるようになってきて
いる。Therefore, in order to impart humidity controllability to the gypsum board, various moisture control agents are added to the plaster of the heart material to improve the moisture absorption / release property, and the moisture absorption / release property is high enough to exert the humidity control function. Attempts have been made to give to a gypsum board, and by mainly incorporating an inorganic moisture absorptive and desorptive substance, the gypsum board has a moisture absorptive and desorptive property equivalent to that when a wooden board is used as a finishing material, that is, a moisture control Is becoming available.
【０００５】ところで、石膏ボードは、建築物の内装に
おいては、表面の仕上げ材として用いられ、多くの場
合、さらに化粧を伴なうことが普通である。この化粧は
印刷による模様の付与、塗装、もしくは模様等を有する
壁紙の貼付け等によって施される。従って、上記の調湿
性を有する石膏ボードにも、化粧が施されることがあり
得る。しかし、調湿性を有する石膏ボードに化粧を施す
際には、化粧効果を確保する必要がある上、その調湿性
を損なわないようにすることが必要になるので、化粧に
より新たな層が積層されるときには、従来は不要であっ
た、湿気を通すための通気性（もしくは透気度）を、新
たに確保する必要が生じる。By the way, the gypsum board is used as a surface finishing material in the interior of buildings, and in many cases, it is usually accompanied by makeup. This makeup is applied by applying a pattern by printing, painting, or pasting a wallpaper having a pattern or the like. Therefore, makeup may be applied to the gypsum board having the humidity control property. However, when applying makeup to a gypsum board that has humidity control, it is necessary to ensure the makeup effect and it is necessary not to impair the humidity control, so a new layer is laminated by makeup. In this case, it becomes necessary to newly secure air permeability (or air permeability) for passing moisture, which was not necessary in the past.
【０００６】これに関連して、従来の石膏ボードに化粧
を施す際に透気度を考慮した技術として、特公平６−７
４５５９号公報に、石膏ボード原紙に印刷、塗装、およ
びエンボス加工を行ない、透気度を４００秒／１００ｃ
ｃ以下とした石膏ボード用化粧シートを用いることによ
り、養生工程において、心材を形成するための石膏スラ
リー中の水分の蒸発が円滑に行なわれ、厚紙と石膏の間
に気泡が発生し、フクレの原因とならないようにするこ
とが記載されている。[0006] In this regard, Japanese Patent Publication No. 6-7 is a technique which takes air permeability into consideration when applying makeup to a conventional gypsum board.
No. 4559, printing, painting, and embossing on gypsum board base paper, air permeability of 400 seconds / 100c
By using the decorative sheet for gypsum board which is c or less, moisture in the gypsum slurry for forming the core material is smoothly evaporated in the curing step, bubbles are generated between the cardboard and the gypsum, and blister It describes that it should not be the cause.
【０００７】もちろん、上記の技術では、使用した石膏
スラリーが何ら特別のものではないから、調湿性を有す
ることがない、従来の石膏ボードに化粧が施されたもの
が得られるに過ぎず、得られた製品において、石膏ボー
ドの調湿性を損なわないよう化粧を施す思想はまるで無
い。しかも、上記の４００秒／１００ｃｃ以下という透
気度は、石膏ボード製造時の養生に要する時間（数十分
と言われる。）内に、石膏スラリー中の余剰の水分が透
過するのに必要な、かなり高い透気度であり、その実現
のために、エンボス加工を付加して、透気度の確保に努
めている。[0007] Of course, in the above technique, since the gypsum slurry used is not special at all, it is only possible to obtain a conventional gypsum board which has no moisture control property and is made up of makeup, which is advantageous. In the produced product, there is no idea of applying makeup so as not to impair the humidity control of the gypsum board. Moreover, the air permeability of 400 seconds / 100 cc or less is necessary for the excess water in the gypsum slurry to permeate within the time required for curing during the production of gypsum board (which is said to be several tens of minutes). It has a fairly high air permeability, and in order to achieve it, we are adding embossing to try to secure the air permeability.
【０００８】[0008]
【発明が解決しようとする課題】本発明においては、調
湿性を有する石膏ボードのような、調湿性を有する板状
の仕上げ材に化粧を施した化粧仕上げ材の形態で、な
お、調湿性を損なわないものを提供することを課題とす
る。SUMMARY OF THE INVENTION In the present invention, in the form of a makeup finishing material obtained by applying makeup to a plate-like finishing material having humidity control such as a gypsum board having humidity control, The challenge is to provide things that do not damage.
【０００９】[0009]
【課題を解決する手段】上記の課題は、従来の化粧石膏
ボードを製造する際のように、石膏ボード原紙に化粧を
施したものの全体に高い透気度を備えさせることなく、
調湿性を有する板状の仕上げ材上に、薄紙および化粧が
施された不織布からなり、透気度が３０００秒／１００
ｃｃ以下の、透気度がそれほど高くはない化粧シートを
適用することにより、解決することができた。[Means for Solving the Problems] The above-mentioned problems are as described in the case of producing a conventional decorative gypsum board, without providing the entire gypsum board base paper with makeup to have high air permeability,
It consists of thin paper and non-woven fabric with makeup applied on a plate-like finishing material with humidity control and has an air permeability of 3000 seconds / 100.
The problem could be solved by applying a decorative sheet having an air permeability of cc or less and not so high.
【００１０】第１の発明は、調湿性を有する板状の仕上
げ材の表面に、薄紙、および、化粧が施された不織布と
が順に積層された積層構造を有しており、前記積層構造
における、少なくとも、前記調湿性を有する板状の仕上
げ材を除く部分の透気度が、３０００秒／１００ｃｃ以
下であることを特徴とする調湿性を有する化粧仕上げ材
に関するものである。第２の発明は、調湿性を有する板
状の仕上げ材の表面に、化粧が施された不織布が薄紙で
裏打ちされた構造を有し、かつ、透気度が３０００秒／
１００ｃｃ以下である化粧シートが積層されていること
を特徴とする調湿性を有する化粧仕上げ材に関するもの
である。第３の発明は、第１または第２の発明におい
て、前記化粧は、着色組成物からなる模様層の積層によ
り施されていることを特徴とする調湿性を有する化粧仕
上げ材に関するものである。第４の発明は、第１〜第３
いずれかの発明において、前記不織布と前記薄紙、また
は／および前記薄紙と前記調湿性を有する板状の仕上げ
材が、水溶性接着剤層を介して積層されていることを特
徴とする調湿性を有する化粧仕上げ材に関するものであ
る。第５の発明は、第１〜第４いずれかの発明におい
て、前記調湿性を有する板状の仕上げ材が、吸放湿性物
質を含有する石膏ボードであることを特徴とする調湿性
を有する化粧仕上げ材に関するものである。A first aspect of the present invention has a laminated structure in which thin paper and a non-woven fabric with makeup are laminated in this order on the surface of a plate-like finishing material having humidity control properties. The present invention relates to a makeup finishing material having humidity control property, wherein at least the air permeability of a portion excluding the plate-shaped finishing material having humidity control property is 3000 seconds / 100 cc or less. A second invention has a structure in which a makeup-applied non-woven fabric is lined with thin paper on the surface of a plate-like finishing material having humidity control property, and the air permeability is 3000 seconds /
The present invention relates to a decorative finishing material having a humidity control property, in which decorative sheets of 100 cc or less are laminated. A third aspect of the present invention relates to the makeup finishing material having humidity control properties according to the first or second aspect, wherein the makeup is applied by laminating pattern layers made of a coloring composition. 4th invention is 1st-3rd.
In any one of the inventions, the non-woven fabric and the thin paper, or / and the thin paper and the plate-like finishing material having the humidity control property are laminated via a water-soluble adhesive layer to provide the humidity control property. The present invention relates to a cosmetic finishing material. A fifth aspect of the present invention is that in any one of the first to fourth aspects of the present invention, the humidity-controlling plate-like finishing material is a gypsum board containing a moisture absorptive and desorptive substance. It concerns finishing materials.
【００１１】[0011]
【発明の実施の形態】図を引用して説明すると、図１
（ａ）に例示するように、本発明の調湿性を有する化粧
仕上げ材１は、基本的には、調湿性を有する板状の仕上
げ材２を基材とし、その一方の表面に薄紙３、および不
織布４が順に積層されたものであって、図１において
は、不織布４の上面（以降において、上および下、上面
および下面は、図を基準とする。）に相当する面、即ち
薄紙３が積層されているのとは反対側の面に模様層５が
積層されたことにより化粧が施されたものである。化粧
が施された不織布としては、後に述べるように、模様層
５が上面に積層された以外のものもあり得る。また、上
記の本発明の調湿性を有する化粧仕上げ材１において、
薄紙３から上の部分、即ち、薄紙３、不織布４、および
模様層５からなる積層体の透気度が３０００秒／１００
ｃｃ以下であることが好ましい。調湿性を有する板状の
仕上げ材２は、単層もしくは積層体であり得るが、図１
（ｂ）に例示するように、調湿性を有する板状の仕上げ
材２が調湿性を有する石膏ボードである場合、厚紙であ
る石膏ボード原紙２ａで心材である石膏２ｂの周囲が被
覆されたものであり得る。この場合、心材である石膏
は、後に説明するように、吸放湿性物質を含有するもの
である。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Referring to the drawings, FIG.
As illustrated in (a), the makeup finishing material 1 having a humidity control property of the present invention basically uses a plate-shaped finishing material 2 having a humidity control property as a base material, and a thin paper 3 on one surface thereof, 1 and the non-woven fabric 4 are laminated in this order, and in FIG. 1, a face corresponding to the upper face of the non-woven fabric 4 (hereinafter, the upper and lower faces, the upper face and the lower face are based on the drawing), that is, the thin paper 3. The pattern layer 5 is laminated on the surface opposite to the layer on which the makeup is applied. As the makeup-applied non-woven fabric, there may be a non-woven fabric other than the pattern layer 5 laminated on the upper surface as described later. Further, in the above-mentioned decorative finish 1 having humidity control of the present invention,
The air permeability of the portion above the thin paper 3, that is, the laminated body including the thin paper 3, the nonwoven fabric 4, and the pattern layer 5 is 3000 seconds / 100.
It is preferably cc or less. The plate-like finishing material 2 having a humidity control property may be a single layer or a laminated body.
As illustrated in (b), when the plate-like finishing material 2 having humidity control is a gypsum board having humidity control, a gypsum board base paper 2a which is a cardboard is coated around the gypsum 2b which is a core material. Can be. In this case, the gypsum as the core material contains a moisture absorptive and desorptive substance, as described later.
【００１２】本発明の調湿性を有する化粧仕上げ材１
は、上記の構造以外にも、種々の変形された構造であり
得る。図２に例示するように、本発明の調湿性を有する
化粧仕上げ材１は、図１を引用して説明した上記の構造
における調湿性を有する板状の仕上げ材２と薄紙３との
間に接着剤層６を有していてもよく、あるいは薄紙３と
不織布４との間に接着剤層６’を有していてもよい。本
発明の調湿性を有する化粧仕上げ材１は、接着剤層６お
よび６’のうち、いずれか一方のみを有していてもよい
し、両方を有していてもよい。なお、これら二つの接着
剤層６および６’は、同じ接着剤で構成されていてもよ
いし、異なる接着剤で構成されていてもよい。The decorative finishing material 1 of the present invention having a humidity control property.
Can be various modified structures other than the above structure. As illustrated in FIG. 2, the decorative finish 1 having a humidity control property of the present invention is provided between the plate-like finishing material 2 having a humidity control property and the thin paper 3 in the structure described with reference to FIG. The adhesive layer 6 may be provided, or the adhesive layer 6 ′ may be provided between the thin paper 3 and the nonwoven fabric 4. The moisture-finishing decorative finish 1 of the present invention may have only one of the adhesive layers 6 and 6 ′, or may have both of them. The two adhesive layers 6 and 6'may be made of the same adhesive or different adhesives.
【００１３】図３に例示するように、本発明の調湿性を
有する化粧仕上げ材１は、化粧が施された不織布４を覆
って、種々の目的を果たすトップコート層が積層されて
いてもよく、例えば、不織布４のほつれ止めのためのほ
つれ止め層７が積層されていてもよく、あるいは、ほつ
れ止め層７の上面に撥水層８が積層されていてもよい。
撥水層８は、ほつれ止め層７を伴なわず、直接、化粧が
施された不織布４を覆う層として積層されていてもよ
い。これらのトップコート層は、図１（ａ）を引用して
説明した化粧仕上げ材１にも適用できる。As illustrated in FIG. 3, the decorative finishing material 1 having a humidity control property of the present invention may cover a non-woven fabric 4 to which makeup is applied, and may be laminated with a top coat layer for various purposes. For example, the fray stop layer 7 for preventing the fray of the nonwoven fabric 4 may be laminated, or the water repellent layer 8 may be laminated on the upper surface of the fray stop layer 7.
The water-repellent layer 8 may be directly laminated without covering the anti-raveling layer 7 as a layer covering the non-woven fabric 4 to which makeup is applied. These top coat layers can also be applied to the decorative finishing material 1 described with reference to FIG.
【００１４】図１〜図３を引用して説明したような種々
の積層構造であり得る、本発明の調湿性を有する化粧仕
上げ材１は、化粧が施された不織布４が薄紙３で裏打さ
れた構造の化粧シート１１が、調湿性を有する板状の仕
上げ材２上に積層された構造を有するものであってもよ
い。従って、化粧シート１１は、薄紙３、および化粧が
施された不織布４の積層体（図１（ａ））、薄紙３、接
着剤層６’、および化粧が施された不織布４の積層体
（図２）、もしくは薄紙３、接着剤層６’、化粧が施さ
れた不織布４、ほつれ止め層７、および撥水層８の積層
体等の、図１〜図３を引用して説明した種々の積層体の
うちの薄紙３から上の部分の積層構造を有するものであ
ってよい。従って、調湿性を有する板状の仕上げ材２上
に接着剤層６を介して薄紙３が積層されている場合、化
粧シート１１は、薄紙３の下面に接着剤層６が積層され
たものであり得る。この場合の接着剤層６は、再湿型の
糊を用いて構成されていてもよい。いずれの化粧シート
１１においても、その透気度が３０００秒／１００ｃｃ
以下であることが好ましい。上記の化粧シート１１は、
調湿性を有する板状の仕上げ用基材２とは別体のものち
して製作するものであるが、本発明において言及してい
る透気度は、化粧シート１１を別体として製作するか、
調湿性を有する板状の仕上げ用基材２上に薄紙３、不織
布４等を順次積層して製作するかを問わず、化粧シート
１１に相当する部分について規定するものである。In the decorative finishing material 1 having a humidity control property of the present invention, which may have various laminated structures as described with reference to FIGS. 1 to 3, a non-woven fabric 4 having a makeup applied is lined with a thin paper 3. The decorative sheet 11 having such a structure may have a structure in which it is laminated on the plate-shaped finishing material 2 having a humidity control property. Therefore, the decorative sheet 11 is a laminated body of the thin paper 3 and the non-woven fabric 4 with the makeup (FIG. 1A), a laminated body of the thin paper 3, the adhesive layer 6 ′, and the non-woven fabric 4 with the makeup ( 2) or a laminated body of thin paper 3, adhesive layer 6 ', non-woven fabric 4 with makeup, anti-fray layer 7, and water-repellent layer 8 and the like described with reference to FIGS. It may have a laminated structure of a portion above the thin paper 3 in the laminated body of. Therefore, when the thin paper 3 is laminated on the plate-shaped finishing material 2 having humidity control properties with the adhesive layer 6 interposed therebetween, the decorative sheet 11 is one in which the adhesive layer 6 is laminated on the lower surface of the thin paper 3. possible. In this case, the adhesive layer 6 may be formed by using a rewet type adhesive. The air permeability of any of the decorative sheets 11 is 3000 seconds / 100 cc.
The following is preferable. The above decorative sheet 11 is
Although it is manufactured separately from the plate-like finishing substrate 2 having a humidity control property, the air permeability referred to in the present invention depends on whether the decorative sheet 11 is manufactured separately. ,
It defines the portion corresponding to the decorative sheet 11 regardless of whether the thin paper 3, the nonwoven fabric 4 and the like are sequentially laminated on the plate-shaped finishing substrate 2 having the humidity control property.
【００１５】本発明における、調湿性を有する板状の仕
上げ材として、実用的価値が高いものは、吸放湿性物資
を含有する石膏ボードである。吸放湿性物質を含有する
石膏ボードは、特開２００１−８０９４８、もしくは特
開２００１−１２３５４７に記載されているように、通
常の石膏ボードに準じて作られたもので、石膏中に、無
機系吸放湿性物質であるゼオライト群、珪藻土（例え
ば、稚内層珪藻頁岩等）、珪質頁岩、ハロサイト、もし
くはモンモリロナイト（酸性白土）等の粘土鉱物、また
はこれらの粘土鉱物を酸処理したもの（例；活性白
土）、もしくは、か焼処理したもの、を含有するもので
ある。これらの粘土鉱物は、化学的には、シリカまたは
／およびアルミナを主成分とするものである。石膏に対
するこれら吸放湿性物質の配合割合は、質量基準で、石
膏１００部に対し、３〜３０部、より好ましくは、５〜
２０部程度である。石膏中に含有させる吸放湿性物質と
しては、上記の無機系吸放湿性物質以外にも、有機系吸
放湿性物質である、通常の炭や活性炭、食品、パルプ、
紙などの廃棄物を炭化処理した、いわゆる炭類を用いる
こともでき、無機系吸放湿性物質および有機系吸放湿性
物質の両方を併用してあってもよい。吸放湿性物質を含
有する石膏ボードとしては、市販品である、吉野石膏
（株）製の「タイガースカットボード」（商品名）、も
しくは、チヨダウーテ（株）製の「さわやかせっこうボ
ード」（商品名）等を用いることができる。前者は、天
然の活性白土（具体的にはシリカとアルミナが主成分）
を配合したものとされている。吸放湿性物資を含有する
石膏ボードは、調湿性を有する以外は、普通の石膏ボー
ドと同等な性能を有するものである。The gypsum board containing a moisture absorbing / releasing material has a high practical value as a plate-like finishing material having a humidity control property in the present invention. A gypsum board containing a moisture absorptive and desorptive substance is made according to a normal gypsum board as described in JP 2001-80948 A or JP 2001-123547 A, and an inorganic type gypsum board is used. Clay minerals such as zeolites, which are moisture absorbing / releasing substances, diatomaceous earth (for example, Wakkanai diatom shale, etc.), siliceous shale, halosite, montmorillonite (acid clay), etc., or acid treatment of these clay minerals (example Activated clay) or calcinated. These clay minerals are chemically composed mainly of silica and / or alumina. The mixing ratio of these moisture absorbing / releasing substances to gypsum is 3 to 30 parts, and more preferably 5 to 100 parts by weight of gypsum.
It is about 20 copies. As the moisture absorptive and desorptive substance to be contained in the gypsum, in addition to the above-described inorganic moisture absorptive and desorptive substance, an organic moisture absorptive and desorptive substance, ordinary charcoal and activated carbon, food, pulp,
So-called charcoal obtained by carbonizing waste such as paper may be used, and both an inorganic moisture absorbing / releasing substance and an organic moisture absorbing / releasing substance may be used in combination. As a gypsum board containing a moisture absorbing / releasing substance, a commercially available product, "Tigers Cut Board" (trade name) manufactured by Yoshino Gypsum Co., Ltd., or "Sawaya Kakekko Board" (product manufactured by Chiyoda Ute Co., Ltd.) Name) etc. can be used. The former is natural activated clay (specifically, silica and alumina are the main components).
It is said to be a mixture. The gypsum board containing the moisture absorbing / releasing material has the same performance as that of a normal gypsum board except that it has a humidity control property.
【００１６】調湿性を有する板状の仕上げ材としては、
吸放湿性物資を含有する石膏ボード以外にも、通常の石
膏ボード、木製の板や合板、木を素材の一部とする木質
繊維板、多孔性セラミックタイルもしくはボード、ケイ
カル板（珪酸カルシウム板）も使用可能である。As a plate-like finishing material having a humidity control property,
In addition to gypsum board containing moisture absorbing / releasing materials, ordinary gypsum board, wooden board or plywood, wood fiber board made of wood as a part of material, porous ceramic tile or board, silica sheet (calcium silicate board) Can also be used.
【００１７】不織布４は、繊維、通常は合成繊維を、紡
糸せずに直接、機械的、熱的、または化学的な手段によ
り交絡させてシート化したものであり、その構造上、透
気度が高い。また、不織布４に対して印刷法により模様
層５を積層しても、不織布４が言わば孔だらけのもので
あるために、不織布４が均一な層で被覆されにくく、不
織布４が持つ透気度を確保することが容易であり、ま
た、布に類似した柔らかい落ち着いた外観を有するた
め、化粧を施す対象として好ましい。The non-woven fabric 4 is made of fibers, usually synthetic fibers, which are directly entangled by a mechanical, thermal or chemical means without being spun into a sheet and have a structure having an air permeability. Is high. Further, even if the pattern layer 5 is laminated on the non-woven fabric 4 by a printing method, the non-woven fabric 4 is difficult to be covered with a uniform layer because the non-woven fabric 4 is so full of holes that the non-woven fabric 4 has an air permeability. Is easy to secure, and has a soft and calm appearance similar to cloth, which is preferable as an object to be applied with makeup.
【００１８】不織布４を構成する繊維としては、特に限
定することはないが、ポリアミド（ナイロン）、ポリエ
ステル、レーヨン、ポリプロピレン、もしくはアクリル
の化学繊維、木綿等の天然繊維であり得る。使用する不
織布４としては、目付け量が過大でない、３０〜１５０
ｇ／ｍ2程度のものを使用することが、透気度の上から
も、また、防火性能上も好ましい。The fibers constituting the non-woven fabric 4 are not particularly limited, but may be natural fibers such as polyamide (nylon), polyester, rayon, polypropylene, or acrylic chemical fiber or cotton. As the non-woven fabric 4 used, the basis weight is not excessive, 30 to 150
It is preferable to use g / m 2 in terms of air permeability and fire prevention performance.
【００１９】不織布４の化粧は、代表的には、印刷法に
よる模様層５の積層による。この場合、模様層５はイン
キが固化したことにより生じる、顔料もしくは染料とバ
インダ樹脂を主成分とする着色組成物からなる。具体的
な印刷法の方式としては、いずれの方式でもよいが、不
織布４の表面は粗面であるため、印刷を鮮明に行ないた
いときは、シルクスクリーン印刷が適しており、グラビ
ア印刷も好ましい。ただし、剥離性シートに一旦印刷す
る等した後、不織布４に転写する転写法によれば、シル
クスクリーン印刷やグラビア印刷によらなくても、鮮明
な印刷が可能である。このほか、染色の手法を用いた
り、電子写真やインキジェット法の利用、パソコンの出
力用プリンターの利用等により、化粧を施してもよい。
電子写真、インキジェット法、パソコンの出力用プリン
ターの利用の場合、模様層は、顔料もしくは染料とバイ
ンダ樹脂を主成分とする着色組成物からなる。The makeup of the nonwoven fabric 4 is typically made by laminating the pattern layer 5 by a printing method. In this case, the pattern layer 5 is composed of a coloring composition containing a pigment or dye and a binder resin as main components, which is generated by solidification of the ink. Although any method may be used as a concrete printing method, since the surface of the nonwoven fabric 4 is a rough surface, silk screen printing is suitable for clear printing, and gravure printing is also preferable. However, according to the transfer method in which the non-woven fabric 4 is once printed on the peelable sheet and then transferred, clear printing is possible without using silk screen printing or gravure printing. In addition, the makeup may be applied by using a dyeing method, an electrophotography or an ink jet method, an output printer of a personal computer, or the like.
In the case of electrophotography, the ink jet method, and the use of a personal computer output printer, the pattern layer is composed of a coloring composition containing a pigment or dye and a binder resin as main components.
【００２０】不織布４に模様層４を積層して化粧を施す
場合のように、化粧を不織布４の片面に行なうときは、
不織布４の上面に行なうことが好ましいが、不織布４の
透明性が高い場合には、化粧を不織布４の下面に行なっ
てもよい。また、化粧が不織布４の厚みの全体に渡って
行なわれてもよい。When the makeup is applied to one side of the nonwoven fabric 4, as in the case of applying the makeup by laminating the pattern layer 4 on the nonwoven fabric 4,
It is preferable that the upper surface of the non-woven fabric 4 be applied, but if the non-woven fabric 4 has high transparency, the makeup may be applied to the lower surface of the non-woven fabric 4. Further, makeup may be applied to the entire thickness of the nonwoven fabric 4.
【００２１】不織布４は、薄紙３を観察側とは反対側に
伴なっていることが好ましい。と言うのは、不織布４が
薄紙３を伴なった方が、調湿性を有する板状の仕上げ材
２上に接着剤層６を介して積層する際に、強い接着力を
得やすいからであり、また、不織布４は一般に密度が低
く、下地隠蔽性が乏しいので、薄紙３を伴なうことによ
り、下地の調湿性を有する板状の仕上げ材２が着色して
いても、下地の色の影響を回避しやすいからである。薄
紙としては、薄葉紙、上質紙、クラフト紙、和紙、もし
くはリンター紙等のほか、壁紙の裏打ち紙も利用でき、
３０〜１２０ｇ／ｍ2程度のものを使用することが好ま
しい。The non-woven fabric 4 is preferably accompanied by the thin paper 3 on the side opposite to the observation side. The reason for this is that the non-woven fabric 4 accompanied by the thin paper 3 can easily obtain a strong adhesive force when it is laminated on the plate-like finishing material 2 having humidity control properties via the adhesive layer 6. Also, since the nonwoven fabric 4 generally has a low density and poor base-mask hiding property, even if the thin paper 3 accompanies the plate-like finishing material 2 having the humidity control property of the base, the color of the base is This is because it is easy to avoid the effect. As the thin paper, thin paper, high-quality paper, kraft paper, Japanese paper, linter paper, etc., as well as wallpaper lining paper,
It is preferable to use one having a weight of about 30 to 120 g / m 2 .
【００２２】薄紙３と不織布４とを積層するには、接着
剤層６’を介する場合と、介さない場合とがあり得る。
接着剤層６’を介する場合、接着剤としては、透気度を
確保する目的で、水溶性接着剤を用いることが好まし
く、水溶性接着剤としては、デンプン糊、ポリビニルア
ルコール系接着剤、もしくはアラビアゴム糊等を挙げる
ことができる。ただし、接着剤層６’を、点状、もしく
は網目状に設ける等して、薄紙３と不織布４との間を全
面で接着せず、各部分毎に接着するようにすれば、水溶
性接着剤以外の接着剤を用いてもよい。The thin paper 3 and the nonwoven fabric 4 may be laminated with or without the adhesive layer 6 '.
In the case of interposing the adhesive layer 6 ′, it is preferable to use a water-soluble adhesive as the adhesive for the purpose of ensuring air permeability, and as the water-soluble adhesive, a starch paste, a polyvinyl alcohol-based adhesive, or Examples thereof include gum arabic glue. However, if the adhesive layer 6 ′ is provided in a dot shape or a mesh shape so that the thin paper 3 and the non-woven fabric 4 are not adhered over the entire surface but are adhered at each part, water-soluble adhesion is achieved. An adhesive other than the agent may be used.
【００２３】薄紙３と不織布４とは、接着剤層６’を介
さないで積層することもできる。不織布３または／およ
び不織布４中に含まれるバインダを利用して熱接着させ
るか、薄紙３の製造過程で、薄紙３を形成するためのバ
インダを利用して不織布４を積層する、もしくは不織布
４の製造過程で、不織布４を形成するためのバインダを
薄紙３を積層する等である。The thin paper 3 and the non-woven fabric 4 may be laminated without the adhesive layer 6 '. The binder contained in the non-woven fabric 3 and / or the non-woven fabric 4 is used for thermal bonding, or in the manufacturing process of the thin paper 3, the non-woven fabric 4 is laminated using the binder for forming the thin paper 3, or In the manufacturing process, the binder for forming the nonwoven fabric 4 is laminated on the thin paper 3.
【００２４】調湿性を有する板状の仕上げ材２と薄紙３
とを積層するにも、接着剤層６を介する場合と、介さな
い場合とがあり得る。接着剤層６を介する場合、接着剤
層６を構成する接着剤としては、接着剤層６’を構成す
る接着剤として挙げたものと同様なものを使用すること
ができる。A plate-like finishing material 2 and thin paper 3 having humidity control properties
Even when the and are laminated, there may be a case where the adhesive layer 6 is interposed and a case where the adhesive layer 6 is not interposed. When the adhesive layer 6 is interposed, as the adhesive forming the adhesive layer 6, the same adhesive as the adhesive forming the adhesive layer 6 ′ can be used.
【００２５】調湿性を有する板状の仕上げ材２と薄紙３
との積層の場合も薄紙３に含まれるバインダを利用し
て、あるいは、調湿性を有する板状の仕上げ材２が吸放
湿性物質を含有する石膏ボードであるときは、石膏ボー
ド原紙または／および薄紙３中に含まれるバインダを利
用して熱接着させるか、薄紙３の製造過程で、薄紙３を
形成するためのバインダを利用して石膏ボード原紙を積
層する、もしくは石膏ボード原紙の製造過程で、石膏ボ
ード原紙を形成するためのバインダを利用して薄紙３を
積層する等である。Plate-like finishing material 2 and thin paper 3 having humidity control
Also in the case of stacking with the above, using the binder contained in the thin paper 3, or when the plate-like finishing material 2 having humidity control properties is a gypsum board containing a moisture absorbing / releasing substance, the gypsum board base paper or / and In the manufacturing process of the thin paper 3, the binder contained in the thin paper 3 is used for heat bonding, or the gypsum board base paper is laminated using the binder for forming the thin paper 3, or in the manufacturing process of the gypsum board base paper. The thin paper 3 is laminated using a binder for forming the gypsum board base paper.
【００２６】ほつれ止め層７は、本発明の調湿性を有す
る化粧仕上げ材の表面側にある不織布４の繊維の一部が
不織布４内に充分固定されず、繊維の一端が不織布４か
ら突出する「ほつれ」を防止するもので、不織布４を構
成する繊維との密着のよい適宜なバインダ樹脂を含む透
明塗料を薄く塗付することにより、形成することができ
る。In the anti-fray layer 7, a part of the fibers of the non-woven fabric 4 on the surface side of the moisture-conditioned decorative finish of the present invention is not sufficiently fixed in the non-woven fabric 4 and one end of the fiber projects from the non-woven fabric 4. It prevents "raveling" and can be formed by thinly applying a transparent coating material containing an appropriate binder resin that has good adhesion to the fibers forming the nonwoven fabric 4.
【００２７】撥水層８は、本発明の調湿性を有する化粧
仕上げ材の最表面の汚染やテープ剥離の際の表面層の剥
離に対する耐性を向上させるためのものであり、シリコ
ーン樹脂やフッ素系樹脂等の撥水性樹脂をバインダ樹脂
とする、もしくはこれらの樹脂を適宜なバインダ樹脂中
に含む透明塗料を薄く塗付することにより、形成するこ
とができる。The water-repellent layer 8 is for improving the resistance to contamination of the outermost surface of the humidity-controlling decorative finishing material of the present invention and peeling of the surface layer at the time of tape peeling. It can be formed by using a water-repellent resin such as a resin as a binder resin, or by thinly applying a transparent paint containing these resins in an appropriate binder resin.
【００２８】本発明において、調湿性を有する板状の仕
上げ材の表面に積層するものの透気度の値は、王研式透
気度・平滑度試験器で測定した値が、３０００秒／１０
０ｃｃ以下であることが好ましく、３０００秒／１００
ｃｃを超えると、調湿性を有する化粧仕上げ材の吸放湿
性能が低下する。透気度の値が小さいほど、透気度が高
くなるので、仕上げ材の調湿性を損なわないためには透
気度が高ければ高いほど好ましいように見えるが、実
際、調湿の機能を発揮する際には、高い透気度を必要と
しない。従来技術として挙げた、透気度を４００秒／１
００ｃｃ以下とした石膏ボード用化粧シートを用いて、
石膏ボード製造時の養生工程において、厚紙と石膏の間
に気泡が発生し、フクレの原因となることを防止する必
要も又ない。むしろ、過度に透気度を高くしようとする
と、不織布４を薄くして強度の低下を招いたり、薄紙を
薄くして下地隠蔽性の低下を招く、もしくは模様層５を
まばらに形成して美観の低下を招く等、化粧仕上げ材と
しての機能を損ねる結果となる。従って、これらの観点
から、透気度を５００秒／１００ｃｃ以上とすることが
好ましく、より好ましくは１０００秒／１００ｃｃ以上
である。In the present invention, the value of the air permeability of the laminate laminated on the surface of the plate-like finishing material having humidity control property is 3000 seconds / 10 for the value measured by the Oken type air permeability / smoothness tester.
It is preferably 0 cc or less and 3000 seconds / 100
When it exceeds cc, the moisture absorbing / releasing performance of the decorative finishing material having a humidity control property deteriorates. The smaller the value of air permeability, the higher the air permeability, so in order not to impair the humidity control of the finishing material, the higher the air permeability, the more preferable it seems. It does not require high air permeability. Permeability of 400 seconds / 1 mentioned in the prior art
Using a decorative sheet for gypsum board that is less than 00cc,
In the curing process during the production of gypsum board, it is not necessary to prevent bubbles from being generated between the cardboard and the gypsum and causing blister. On the contrary, if the air permeability is excessively increased, the non-woven fabric 4 is thinned to lower the strength, or the thin paper is thinned to lower the underlayer concealing property, or the pattern layer 5 is sparsely formed to give an aesthetic appearance. As a result, the function as a cosmetic finishing material is impaired. Therefore, from these viewpoints, the air permeability is preferably 500 seconds / 100 cc or more, more preferably 1000 seconds / 100 cc or more.
【００２９】[0029]
【実施例】（実施例１）６０ｇ／ｍ2のレーヨン不織布
の片面に印刷して化粧を施し、印刷面にさらにフッ素系
樹脂塗料を塗布して撥水層とし、印刷面とは反対側の面
にウレタン接着剤を塗付して、１２０ｇ／ｍ2の裏打ち
紙を貼り合わせ、透気度が１５００秒／１００ｃｃの化
粧シートを得た。なお、透気度は、以降の測定も含め、
王研式透気度・平滑度試験器を用いて測定した。調湿性
を有する板状の仕上げ材として、厚み１２ｍｍの調湿性
を有する石膏ボード（吉野石膏（株）製、商品名；タイ
ガースカットボード）を準備し、その上に、上記で得ら
れた化粧シートをデンプン糊を１２０ｇ／ｍ2使用して
ラミネートし、化粧石膏ボードの形態の調湿性を有する
化粧仕上げ材とし、そこから、２０ｃｍ×２０ｃｍのサ
イズに裁断した試料片を準備した。Example 1 A surface of 60 g / m 2 rayon non-woven fabric was printed on one side to give a makeup, and a fluororesin paint was further applied to the printed side to form a water repellent layer on the side opposite to the printed side. A urethane adhesive was applied to the surface and a backing paper of 120 g / m 2 was adhered to obtain a decorative sheet having an air permeability of 1500 seconds / 100 cc. The air permeability, including the subsequent measurements,
It measured using the Oken type air permeability / smoothness tester. A 12 mm thick gypsum board (manufactured by Yoshino Gypsum Co., Ltd., trade name; Tiger's Cut Board) having a thickness of 12 mm is prepared as a moisture-controlling plate-like finishing material, and the decorative sheet obtained above is prepared thereon. Was laminated with 120 g / m 2 of starch paste to form a decorative finishing material having a humidity control property in the form of a decorative gypsum board, from which a sample piece cut into a size of 20 cm × 20 cm was prepared.
【００３０】（実施例２）１２０ｇ／ｍ2のレーヨン不
織布を用いた以外は実施例１と同様にした。化粧シート
の透気度は３０００秒／１００ｃｃであった。(Example 2) The same procedure as in Example 1 was carried out except that 120 g / m 2 of rayon nonwoven fabric was used. The air permeability of the decorative sheet was 3000 seconds / 100 cc.
【００３１】（比較例１）アクリル樹脂のエマルジョン
を壁紙裏打紙に塗付し作成した透気度が５５００秒／１
００ｃｃの壁紙を化粧シートの代わりに用い、その他は
実施例１にならった。(Comparative Example 1) An air-permeable material prepared by applying an emulsion of an acrylic resin to wallpaper backing paper and having an air permeability of 5500 seconds / 1.
A wallpaper of 00 cc was used instead of the decorative sheet, and the others were the same as in Example 1.
【００３２】（参照例）実施例１で用いたのと同じ調湿
性を有する石膏ボード単独から試料片を得た。Reference Example A sample piece was obtained from gypsum board alone having the same humidity control property as that used in Example 1.
【００３３】得られた各試料を評価するため、内部が縦
２５ｃｍ×横２５cm×高さ２５ｃｍのアルミニウム製の
密封可能な容器を５個（容器Ａ、容器Ｂ、容器Ｃ、容器
Ｄ、および容器Ｅ）準備し、容器Ａ中には実施例１で得
た試料片、容器Ｂ中には実施例２で得た試料片、容器Ｃ
中には比較例１で得た試料片、および容器Ｄ中には参照
例としての調湿性を有する石膏ボード単独の試料片を、
それぞれ収納し、また、容器Ｅには何も収納せずに空の
状態のままとし、各容器Ａ〜Ｅを恒温恒湿槽内で、温
度；２０℃、相対湿度；５５％に保ち、恒量化させた。
上記の容器および試料片の大きさは、通常の住居の３．
３ｍ2（容積で約８ｍ3）の部屋の４面の壁に化粧仕上げ
材を用いた場合にほぼ相当する。恒量化させた後、各容
器内に試料を収納したまま密封し、２０℃の恒温槽内で
２時間経過させ、その後、直ちに３０℃の恒温槽内に移
して２時間経過させ、以降、２０℃、１０℃、および２
０℃の各温度の恒温槽内に移して、各々２時間ずつ経過
させることにより、容器の外の温度を変化させ、各容器
の内部の湿度の変化を測定した。また、試料片を収納し
ない容器単独についても、同様な試験を行なった。In order to evaluate each of the obtained samples, five aluminum-sealable containers each having a length of 25 cm × width 25 cm × height 25 cm (container A, container B, container C, container D, and container) E) Prepared, the sample piece obtained in Example 1 in container A, the sample piece obtained in Example 2 in container B, and container C
The sample piece obtained in Comparative Example 1 and the sample piece of gypsum board alone having humidity control as a reference example in the container D,
Each container is stored, and nothing is stored in the container E, and the container E is left empty, and each container A to E is kept at a temperature of 20 ° C. and a relative humidity of 55% in a thermo-hygrostat. Quantified.
The size of the above-mentioned container and sample piece is 3.
This is almost equivalent to the case where a decorative finishing material is used on the four walls of a room of 3 m 2 (about 8 m 3 in volume). After constant weighting, each container was sealed while containing the sample, and allowed to stand in a constant temperature bath at 20 ° C for 2 hours, and then immediately moved to a constant temperature bath at 30 ° C for 2 hours, and thereafter 20 ℃, 10 ℃, and 2
The temperature outside the container was changed by moving the container into a constant temperature bath at 0 ° C. for 2 hours, and the change in humidity inside each container was measured. Further, the same test was conducted on the container alone which does not contain the sample piece.
【００３４】測定結果は、図４のグラフの通りであり、
実施例１および実施例２で得られた化粧石膏ボードは、
石膏ボード単独に匹敵する調湿性が確保されているが、
比較例の化粧石膏ボードは、貼った壁紙の透気度が低い
ために、調湿性が低下し、下地の石膏ボードの調湿性を
充分に発揮することができなかった。The measurement results are shown in the graph of FIG.
The decorative gypsum boards obtained in Examples 1 and 2 were:
The humidity control that is comparable to that of gypsum board alone is secured,
The decorative gypsum board of the comparative example had low moisture permeability because of the low air permeability of the pasted wallpaper, and the moisture control of the underlying gypsum board could not be sufficiently exhibited.
【００３５】[0035]
【発明の効果】請求項１の発明によれば、調湿性を有す
る板状の仕上げ材の表面に、薄紙を介して、化粧が施さ
れた布類似の外観を有する不織布が積層されており、し
かも、調湿性を有する板状の仕上げ材を除く部分の透気
度が、３０００秒／１００ｃｃ以下であるので、十分な
化粧効果を有する上、調湿性が加味された化粧仕上げ材
を提供することができる。請求項２の発明によれば、請
求項１の発明と同様な効果に加え、予め、別に作成した
化粧シートを調湿性を有する板状の仕上げ材の表面に貼
り合せる製造方式に適した化粧仕上げ材を提供すること
ができる。請求項３の発明によれば、請求項１または請
求項２の発明の効果に加え、印刷、電子写真、インキジ
ェット法、もしくはパソコンの出力用プリンターの利用
等による化粧方式に適した化粧仕上げ材を提供すること
ができる。請求項４の発明によれば、請求項１〜請求項
３いずれかの発明の効果に加え、不織布〜薄紙間、およ
び／または、薄紙〜調湿性を有する板状の仕上げ材間が
水溶性接着剤層により接着されているので、積層が確実
で、しかも透気度の確保が容易な化粧仕上げ材を提供す
ることができる。請求項５の発明によれば、請求項１〜
請求項４いずれかの発明の効果に加え、吸放湿性物質を
含有する石膏ボードを用いて構成されているので、普通
の石膏ボードの持つ種々の特徴をも兼ね備えた化粧仕上
げ材を提供することができる。According to the first aspect of the present invention, a nonwoven fabric having an appearance similar to that of a cloth to which makeup is applied is laminated on the surface of a plate-like finishing material having a humidity control property via a thin paper. Moreover, since the air permeability of the portion excluding the plate-like finishing material having humidity control is 3000 seconds / 100 cc or less, it is possible to provide a makeup finishing material which has a sufficient cosmetic effect and in which humidity control is added. You can According to the invention of claim 2, in addition to the same effect as that of the invention of claim 1, a makeup finish suitable for a manufacturing method in which a separately prepared makeup sheet is attached to the surface of a plate-like finishing material having humidity control properties. Material can be provided. According to the invention of claim 3, in addition to the effect of the invention of claim 1 or claim 2, a makeup finishing material suitable for a makeup method by printing, electrophotography, an ink jet method, or the use of a printer for output of a personal computer. Can be provided. According to the invention of claim 4, in addition to the effect of the invention of any one of claims 1 to 3, water-soluble adhesion is provided between the non-woven fabric and the thin paper, and / or between the thin paper and the plate-like finishing material having humidity control property. Since they are adhered by the agent layer, it is possible to provide a decorative finishing material which is surely laminated and whose air permeability is easily secured. According to the invention of claim 5, claims 1 to
In addition to the effect of any one of the inventions, since it is constituted by using a gypsum board containing a moisture absorptive and desorptive substance, it is possible to provide a decorative finishing material which has various characteristics of an ordinary gypsum board. You can
【図１】本発明の化粧仕上げ材の断面図である。1 is a cross-sectional view of a decorative finish of the present invention.
【図２】接着剤層を有する化粧仕上げ材の断面図であ
る。FIG. 2 is a cross-sectional view of a decorative finish having an adhesive layer.
【図３】ほつれ止め層および撥水層を有する化粧仕上げ
材の断面図である。FIG. 3 is a cross-sectional view of a decorative finish having an anti-fray layer and a water repellent layer.
【図４】実施例、比較例等の試料の調湿性の試験結果を
示すグラフである。FIG. 4 is a graph showing test results of humidity control of samples of Examples and Comparative Examples.
１ 化粧仕上げ材 ２ 仕上げ材 ３ 薄紙 ４ 不織布 ５ 模様層 ６ 接着剤層 ７ ほつれ止め層 ８ 撥水層 1 makeup finish 2 Finishing material 3 thin paper 4 non-woven fabric 5 pattern layers 6 Adhesive layer 7 Anti-fray layer 8 Water repellent layer
フロントページの続き Ｆターム(参考） 2E001 DB03 GA24 GA25 GA28 HA03 HA14 HA21 HC02 HC07 HC08 HC11 HD00 2E110 AA16 AB04 AB23 BA03 BA12 BB02 GA42W GB16X GB62W GB63W 4F100 AK51 AT00A BA03 BA04 BA07 BA10A BA10C CB00D DG10B DG15C GB07 HB00C JB05D JD02B JD02C Continued front page F-term (reference) 2E001 DB03 GA24 GA25 GA28 HA03 HA14 HA21 HC02 HC07 HC08 HC11 HD00 2E110 AA16 AB04 AB23 BA03 BA12 BB02 GA42W GB16X GB62W GB63W 4F100 AK51 AT00A BA03 BA04 BA07 BA10A BA10C CB00D DG10B DG15C GB07 HB00C JB05D JD02B JD02C
Claims (5)
に、薄紙、および、化粧が施された不織布とが順に積層
された積層構造を有しており、前記積層構造における、
少なくとも、前記調湿性を有する板状の仕上げ材を除く
部分の透気度が、３０００秒／１００ｃｃ以下であるこ
とを特徴とする調湿性を有する化粧仕上げ材。1. A laminated structure, in which thin paper and a non-woven fabric with a makeup are laminated in this order on the surface of a plate-shaped finishing material having humidity control properties, and in the laminated structure,
At least the air permeability of the portion excluding the plate-like finishing material having the humidity control property is 3000 seconds / 100 cc or less, and the makeup finishing material having the humidity control property.
に、化粧が施された不織布が薄紙で裏打ちされた構造を
有し、かつ、透気度が３０００秒／１００ｃｃ以下であ
る化粧シートが積層されていることを特徴とする調湿性
を有する化粧仕上げ材。2. A decorative sheet having a structure in which a non-woven fabric provided with makeup is lined with a thin paper on the surface of a plate-like finishing material having humidity control properties, and having an air permeability of 3000 seconds / 100 cc or less. A laminated decorative finishing material having humidity control properties.
の積層により施されていることを特徴とする請求項１ま
たは請求項２記載の調湿性を有する化粧仕上げ材。3. The makeup finishing material having humidity control properties according to claim 1 or 2, wherein the makeup is applied by laminating pattern layers made of a coloring composition.
前記薄紙と前記調湿性を有する板状の仕上げ材が、水溶
性接着剤層を介して積層されていることを特徴とする請
求項１〜請求項３いずれか記載の調湿性を有する化粧仕
上げ材。4. The non-woven fabric and the thin paper, or / and the thin paper and the humidity-controlling plate-like finishing material are laminated via a water-soluble adhesive layer. A cosmetic finishing material having a humidity control property according to claim 3.
吸放湿性物質を含有する石膏ボードであることを特徴と
する請求項１〜請求項４いずれか記載の調湿性を有する
化粧仕上げ材。5. The plate-shaped finishing material having humidity control,
It is a gypsum board containing a moisture absorptive and desorptive substance, and the cosmetic finishing material having a humidity control property according to any one of claims 1 to 4.