JP2003027371A - Functional nonwoven fabric, sanitary material, and cleaning cloth - Google Patents
Functional nonwoven fabric, sanitary material, and cleaning clothInfo
- Publication number
- JP2003027371A JP2003027371A JP2001214874A JP2001214874A JP2003027371A JP 2003027371 A JP2003027371 A JP 2003027371A JP 2001214874 A JP2001214874 A JP 2001214874A JP 2001214874 A JP2001214874 A JP 2001214874A JP 2003027371 A JP2003027371 A JP 2003027371A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- antibacterial
- antibacterial agent
- woven fabric
- pyridine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、優れた抗菌性を有
し、軽量、かつ、安価な機能性不織布および衛生材料な
らびに清掃用布帛に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a functional non-woven fabric, a sanitary material, and a cleaning cloth which have excellent antibacterial properties, are lightweight, and are inexpensive.
【０００２】[0002]
【従来の技術】環境、衛生に感心が高まる中、従来から
抗菌性を有する不織布は数多く提案されている。無機系
抗菌剤を使用するものとしては、不織布を構成する合成
繊維の製造工程で、抗菌剤を練り込み、溶融紡糸する方
法や抗菌剤をバインダーを介して繊維表面に固着させる
方法などがある。しかし抗菌剤を練り込んだものは抗菌
剤が繊維内部に入り込み、またバインダーを介して抗菌
剤を固着させたものはバインダー内部に抗菌剤が入り込
み、いずれの場合も抗菌剤が各種菌と接触する機会が少
ないため抗菌効果としては低く、高い抗菌効果を得るた
めには多量の抗菌剤を使用することが必要でありコスト
が高くなるという問題があった。2. Description of the Related Art With increasing interest in the environment and hygiene, many nonwoven fabrics having antibacterial properties have been proposed. As a method of using an inorganic antibacterial agent, there are a method of kneading an antibacterial agent and melt-spinning it in a process of manufacturing a synthetic fiber constituting a nonwoven fabric, a method of fixing the antibacterial agent to a fiber surface through a binder, and the like. However, in the case where the antibacterial agent is kneaded, the antibacterial agent enters the inside of the fiber, and in the case where the antibacterial agent is fixed via the binder, the antibacterial agent enters the binder, and in any case, the antibacterial agent comes into contact with various bacteria. Since there are few opportunities, the antibacterial effect is low, and in order to obtain a high antibacterial effect, it is necessary to use a large amount of antibacterial agent, which causes a problem of high cost.
【０００３】また、有機系抗菌剤を使用するものとして
は、第４級アンモニウム塩を繊維表面に固着させる方法
などがある。しかしこれらは黄色ブドウ状球菌等の弱い
菌に対しては有効であるが、メシチリン耐性ブドウ状球
菌（以下ＭＲＳＡ）や緑膿菌などの菌に対しては効果が
薄いものであった。As a method of using an organic antibacterial agent, there is a method of fixing a quaternary ammonium salt on the fiber surface. However, although they are effective against weak bacteria such as Staphylococcus aureus, they are less effective against bacteria such as mesitillin-resistant Staphylococcus aureus (hereinafter MRSA) and Pseudomonas aeruginosa.
【０００４】不織布を構成する繊維としては、各種合成
繊維が多く提案されているが、ポリエステル系繊維、ポ
リアミド系繊維はコストが高く、また比重も高いため不
織布のメリットである低コスト、軽量という目的からは
好ましくない。Although various synthetic fibers have been proposed as fibers constituting a nonwoven fabric, polyester fibers and polyamide fibers are high in cost and have a high specific gravity. Is not preferable.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、かかる従来
技術の背景に鑑み、優れた抗菌性を有し、軽量且つ安価
な不織布および衛生材料ならびに清掃用布帛を提供せん
とするものである。SUMMARY OF THE INVENTION In view of such background of the prior art, the present invention provides a lightweight and inexpensive non-woven fabric, sanitary material, and cleaning cloth having excellent antibacterial properties.
【０００６】[0006]
【課題を解決するための手段】本発明は、かかる課題を
解決するために、次のような手段を採用するものであ
る。すなわち、本発明の機能性不織布は、ポリオレフィ
ン系繊維を含む繊維で構成され不織布であって、該不織
布に、分子量が２００〜７００で、平均粒径が２μｍ以
下で、かつ、無機性／有機性値が０．３〜１．４である
ピリジン系抗菌剤が固着されていることを特徴とするも
のである。また、本発明の衛生材料および清掃用布帛
は、かかる機能性不織布を少なくとも１部に用いて構成
されていることを特徴とするものである。The present invention employs the following means in order to solve the above problems. That is, the functional non-woven fabric of the present invention is a non-woven fabric composed of fibers including a polyolefin fiber, wherein the non-woven fabric has a molecular weight of 200 to 700, an average particle size of 2 μm or less, and an inorganic / organic property. A pyridine antibacterial agent having a value of 0.3 to 1.4 is fixed. Further, the sanitary material and the cleaning cloth of the present invention are characterized in that the functional nonwoven fabric is used at least in part.
【０００７】[0007]
【発明の実施の形態】本発明は、前記課題、つまり優れ
た抗菌性を有し、軽量且つ安価な不織布について、鋭意
検討し、ポリオレフィン系繊維を含む繊維で構成され不
織布という特定な不織布に、無機性／有機性値が０．３
〜１．４であるという特定なピリジン系抗菌剤で、か
つ、分子量、粒子径が特定なものを選択して使用してみ
たところ、かかる課題を一挙に解決することを究明した
ものである。BEST MODE FOR CARRYING OUT THE INVENTION The present invention has made a serious study on the above-mentioned problems, that is, a lightweight and inexpensive nonwoven fabric having excellent antibacterial properties, and a specific nonwoven fabric composed of fibers containing polyolefin fibers, Inorganic / organic value is 0.3
When a specific pyridine antibacterial agent having a specific molecular weight and particle size of 1.4 is selected and used, it is clarified that these problems can be solved at once.
【０００８】本発明でいうポリオレフィン系繊維とは、
ポリプロピレン繊維およびポリエチレン繊維から選ばれ
た少なくとも１種で構成されていることが好ましい。繊
維の形態は特に限定されるものではなく、１種のポリマ
ーから構成されてもよく、２種以上のポリマーから構成
されていても差し支えないが、軽量性、低コスト性を考
慮すると、ポリプロピレン繊維またはポリエチレン繊維
単独によって構成されていることが好ましい。本発明
は、これら繊維によって構成されたスパンボンド、スパ
ンレース等の不織布が好ましく使用される。The polyolefin fiber referred to in the present invention is
It is preferably composed of at least one selected from polypropylene fibers and polyethylene fibers. The form of the fiber is not particularly limited, and may be composed of one kind of polymer or two or more kinds of polymers, but in view of lightness and low cost, polypropylene fiber is used. Alternatively, it is preferably composed of polyethylene fibers alone. In the present invention, a spunbond, spunlace, or other non-woven fabric composed of these fibers is preferably used.
【０００９】本発明でいうピリジン系抗菌剤とは、分子
量が２００〜７００で、平均粒径が２μｍ以下であり、
かつ、無機性／有機性値が０．３〜１．４であることが
重要である。The pyridine type antibacterial agent referred to in the present invention has a molecular weight of 200 to 700 and an average particle size of 2 μm or less,
Moreover, it is important that the inorganic / organic value is 0.3 to 1.4.
【００１０】かかるピリジン系抗菌剤は、少量でも、ポ
リオレフィン系繊維に対し非常に抗菌効果を発揮するこ
とを究明したものである。かかる抗菌剤として２−クロ
ロ−６−トリクロロメチルピリジン、２−クロロ−４−
トリクロロメチル−６−メトキシピリジン、２−クロロ
−４−トリクロロメチル−６−（２−フリメトキシ）ピ
リジン、ジ（４−クロロフェニル）ピリジンメタノー
ル、２，３，５−トリクロロ−４−（ｎ−プロピルスル
フォニル）ピリジン、２−ピリジルチオール−１−オキ
シド亜鉛、ジ（２−ピリジルチオール−１−オキシド）
等のピリジン系化合物を用いることができる。その中で
も特に、２−ピリジルチオール−１−オキシド亜鉛が、
抗菌効果が高く、ＭＲＳＡをはじめ、効果を示す対象菌
種の広さの点で好ましく使用される。It has been clarified that such a pyridine type antibacterial agent exerts an extremely antibacterial effect on polyolefin type fibers even in a small amount. As such an antibacterial agent, 2-chloro-6-trichloromethylpyridine, 2-chloro-4-
Trichloromethyl-6-methoxypyridine, 2-chloro-4-trichloromethyl-6- (2-furimethoxy) pyridine, di (4-chlorophenyl) pyridinemethanol, 2,3,5-trichloro-4- (n-propylsulfonyl) ) Pyridine, 2-pyridylthiol-1-oxide zinc, di (2-pyridylthiol-1-oxide)
And other pyridine compounds can be used. Among them, especially 2-pyridylthiol-1-oxide zinc is
It has a high antibacterial effect, and it is preferably used in terms of the breadth of target bacterial strains that exhibit the effect including MRSA.
【００１１】かかるピリジン系抗菌剤は、コロイド状態
で粒状化していることが好ましい。コロイド化されてい
ると、抗菌剤が繊維に強固に付着することができ、ま
た、不織布の組織内部にまで、均一に付着しやすくする
上から、その平均粒径を２μｍ以下であるものを使用す
ることが好ましく、かくすることにより、さらに抗菌効
果が出やすくすることができるものである。なかでも水
とホルマリン縮合物によりコロイド状態とすることが、
抗菌剤の分散性が高まり、良好な分散状態を保つことが
できるという効果を発揮する上から、好ましく採用され
る。The pyridine antibacterial agent is preferably granulated in a colloidal state. When colloidal, the antibacterial agent can firmly adhere to the fiber, and the average particle size is 2 μm or less to facilitate uniform adhesion even inside the tissue of the nonwoven fabric. The antibacterial effect can be more easily obtained by doing so. Among them, it is possible to make a colloidal state with water and formalin condensate,
It is preferably used because the dispersibility of the antibacterial agent is enhanced and the effect of maintaining a good dispersed state can be exhibited.
【００１２】また、かかるピリジン系抗菌剤は、その分
子量が２００〜７００であることが抗菌効果の上から重
要である。すなわち、２００未満または７００を超える
と、ポリオレフィン系繊維に対して抗菌剤が付着しにく
くなり抗菌性が出にくいものとなる。In addition, it is important for the antibacterial effect that the molecular weight of the pyridine antibacterial agent is 200 to 700. That is, when it is less than 200 or more than 700, the antibacterial agent is less likely to adhere to the polyolefin fibers, and antibacterial properties are less likely to be obtained.
【００１３】本発明の抗菌剤は、無機性／有機性値が
０．３〜１．４の範囲にあるものを使用することが重要
である。It is important to use the antibacterial agent of the present invention having an inorganic / organic value in the range of 0.3 to 1.4.
【００１４】本発明にいう無機性／有機性値とは、藤田
稔氏が考案した〔改編 化学実験学−有機化学編−河出
書房（１９７１）参照〕各種有機化合物の極性を有機概
念的に取り扱った値であり、炭素（Ｃ）１個を有機性２
０とし、それに対し各種極性基の無機性、有機性の値を
表１のごとく定め、無機性値の和と有機性値の和を求め
両者の比をとった値をいう。The term "inorganic / organic value" used in the present invention is devised by Minoru Fujita [Revised Chemical Experiments-Organic Chemistry-Kawade Shobo (1971)]. It is the value of 1 carbon (C) and organic 2
It is defined as 0, and the inorganic and organic values of various polar groups are determined as shown in Table 1, and the sum of the inorganic value and the organic value is calculated to obtain the ratio of the two.
【００１５】[0015]
【表１】 [Table 1]
【００１６】無機性／有機性値が０．３未満の場合は、
有機性が強くなりすぎて、逆に１．４を超える場合は無
機性が強くなりすぎて、どちらの場合も合成繊維に付着
しにくくなるものである。ポリオレフィン系繊維は無機
性／有機性値はこの範囲には入るものではないが、かか
る範囲の抗菌剤が、ポリオレフィン系繊維に対して少量
で非常に効果を発揮することを究明したものである。If the inorganic / organic value is less than 0.3,
If the organicity becomes too strong, and conversely exceeds 1.4, the inorganicity becomes too strong, and in either case, it becomes difficult to adhere to the synthetic fiber. Although the inorganic / organic value of the polyolefin fiber does not fall within this range, it has been clarified that an antibacterial agent in such a range exerts a great effect on the polyolefin fiber in a small amount.
【００１７】かかる抗菌剤は、ポリエステル系繊維やポ
リアミド系繊維に対しては繊維内部に吸尽されるが、ポ
リオレフィン系繊維に対してはほとんど吸尽されること
がなく、抗菌剤は繊維表面に多く存在する。抗菌剤は、
菌が抗菌剤に接触することにより、初めて抗菌効果を発
揮するものであるため、繊維表面により多く抗菌剤を存
在せしめることができるポリオレフィン系繊維に、かか
る抗菌剤が固着されていることは、抗菌効果を発揮させ
る上で非常に好ましいものである。The antibacterial agent is exhausted inside the fibers for the polyester fibers and the polyamide fibers, but is hardly exhausted for the polyolefin fibers, and the antibacterial agent is deposited on the fiber surface. There are many. Antibacterial agents
Since the bacteria exhibit an antibacterial effect for the first time when they come into contact with the antibacterial agent, the fact that such an antibacterial agent is adhered to the polyolefin fiber that allows more antibacterial agents to exist on the fiber surface means that the antibacterial agent is fixed. It is very preferable for exerting the effect.
【００１８】かかる抗菌剤の不織布に対する付着量は、
０．０２〜１．５重量％が好ましく、特に好ましくは
０．１〜１．０重量％である。０．０２重量％未満で
は、十分な抗菌効果が得られず、また１．５重量％を超
えても抗菌効果としては既に十分であり、過剰に付着し
ているだけで必要性がない。The amount of the antibacterial agent attached to the nonwoven fabric is
0.02 to 1.5% by weight is preferable, and 0.1 to 1.0% by weight is particularly preferable. If it is less than 0.02% by weight, a sufficient antibacterial effect cannot be obtained, and if it exceeds 1.5% by weight, the antibacterial effect is already sufficient, and excessive adhesion is not necessary.
【００１９】また、かかる抗菌剤は、バインダーで繊維
に固着させる必要がないため、柔軟な風合いを要求され
る用途においては非常に好ましく、またバインダーの内
部に抗菌剤が埋もれてしまうことがない。Further, since such an antibacterial agent does not need to be fixed to the fiber with a binder, it is very preferable in applications requiring a soft texture, and the antibacterial agent is not buried inside the binder.
【００２０】本発明でいう衛生材料および清掃用布帛
は、上述した機能性不織布を少なくとも１部に用いて構
成されているものであり、衛生材料および清掃用布帛
は、その少なくとも１層に前記不織布を有するものであ
り、好ましくは積層物で構成されたものである。The sanitary material and the cleaning cloth referred to in the present invention are constructed by using the above-mentioned functional nonwoven fabric in at least a part thereof, and the sanitary material and the cleaning cloth have at least one layer of the nonwoven fabric. And is preferably composed of a laminate.
【００２１】ここでいう積層構造とは、２層以上の層で
構成されているものが好ましく、液体を吸収する機能を
有するものであり、たとえば、衛生材料ならば、おむ
つ、生理用ナプキン、パンティーライナー、ペット用尿
パッドが含まれ、該材料を構成する層内に高吸水ポリマ
ーを含有していてもよい。The laminated structure referred to herein is preferably composed of two or more layers and has a function of absorbing liquid. For example, sanitary materials include diapers, sanitary napkins and panties. A liner and a urine pad for pets are included, and the super absorbent polymer may be contained in the layer constituting the material.
【００２２】また、清掃用布帛は、上述した機能性不織
布を少なくとも１部に用いて構成されているものであ
り、１層から構成されていてもよく２層以上の積層構造
であっても差し支えない。かかる清掃用布帛としては、
たとえば、おしぼり、濡れティッシュなどとして好まし
く採用される。Further, the cleaning cloth is composed of the above-mentioned functional non-woven fabric as at least a part thereof, and may be composed of one layer or a laminated structure of two or more layers. Absent. As such a cleaning cloth,
For example, it is preferably used as a hand towel and a wet tissue.
【００２３】いずれの場合も、肌に直接ふれる機会が多
いため、柔軟性を有することが必須である。これらの観
点からかかる不織布にはポリオレフィン系繊維が好まし
く、またかかる不織布が抗菌性を有することは、衛生
上、非常に好ましい。In any case, it is essential to have flexibility because there are many opportunities to directly touch the skin. From these viewpoints, polyolefin fibers are preferable for the non-woven fabric, and it is highly preferable that the non-woven fabric has antibacterial properties in view of hygiene.
【００２４】[0024]
【実施例】以下、本発明を実施例により更に具体的に説
明する。なお、実施例中での品質評価は次の方法を用い
た。
［抗菌性］評価方法は、統一試験法を採用し、試験菌体
は黄色ブドウ状球菌臨床分離株を用いた。試験方法は、
滅菌試験布に上記試験菌を注加し、１８時間培養後の生
菌数を計測し、殖菌数に対する菌数を求め、次の基準に
従った。EXAMPLES The present invention will be described in more detail below with reference to examples. The following method was used for quality evaluation in the examples. [Antibacterial property] The unified test method was adopted as the evaluation method, and Staphylococcus aureus clinical isolates were used as test cells. The test method is
The above-mentioned test bacteria were added to a sterilization test cloth, the number of viable bacteria after 18 hours of culture was counted, and the number of bacteria was calculated based on the number of bacteria inoculated.
【００２５】ｌｏｇ（Ｂ／Ａ）＞１．５の条件下、ｌｏ
ｇ（Ｂ／Ｃ）を静菌活性値とし、２．２以上を合格とし
た。ただし、Ａは無加工品の接種直後分散回収した菌
数、Ｂは無加工品の１８時間培養後分散回収した菌数、
Ｃは加工品の１８時間培養後分散回収した菌数を表す。Under the condition of log (B / A)> 1.5, lo
g (B / C) was defined as the bacteriostatic activity value, and 2.2 or more was accepted. However, A is the number of bacteria that were dispersed and recovered immediately after inoculation of the unprocessed product, B is the number of bacteria that were dispersed and recovered after 18-hour culture of the unprocessed product,
C represents the number of bacteria that were dispersed and recovered after culturing the processed product for 18 hours.
【００２６】（実施例１）０．１１ｄｔｅｘのポリプロ
ピレン繊維をメルトブロー・スパンボンド・メルトブロ
ー方式で積層した目付１５ｇ／ｍ2の不織布に対し、抗
菌剤として２−ピリジルチオール−１−オキシド亜鉛分
散液を用い、ピックアップ３０％で、スパンボンドに対
して付着量０．１重量％になるようパッディングし、次
いで１３０℃で２分乾燥した。得られたスパンボンドの
抗菌性評価結果を表２に示す。Example 1 A non-woven fabric having a basis weight of 15 g / m 2 obtained by laminating polypropylene fibers of 0.11 dtex by a melt blow / spun bond / melt blow method was treated with 2-pyridylthiol-1-oxide zinc dispersion as an antibacterial agent. It was padded with a pickup of 30% so that the adhesion amount to the spunbond was 0.1% by weight, and then dried at 130 ° C. for 2 minutes. Table 2 shows the antibacterial evaluation results of the obtained spunbond.
【００２７】このスパンボンドは、高い抗菌効果を示す
と共に風合いも柔らかいものであった。The spunbond exhibited a high antibacterial effect and had a soft texture.
【００２８】（比較例１）０．１１ｄｔｅｘのポリエチ
レンテレフタレート繊維をメルトブロー・スパンボンド
・メルトブロー方式で積層した目付１５ｇ／ｍ2の不織
布に対し、実施例１と同様の処理を行った。得られたス
パンボンドの抗菌性評価結果を表２に示す。Comparative Example 1 A nonwoven fabric having a basis weight of 15 g / m 2 obtained by laminating polyethylene terephthalate fibers of 0.11 dtex by the melt blow / spun bond / melt blow method was treated in the same manner as in Example 1. Table 2 shows the antibacterial evaluation results of the obtained spunbond.
【００２９】このスパンボンドは、高い抗菌効果を示す
ものの、風合いは硬いものであり、抗菌性を必要とする
肌に触れる部分に対しては非常に使いづらいものであっ
た。Although this spunbond exhibits a high antibacterial effect, it has a hard texture and is very difficult to use for a part that comes into contact with the skin which requires antibacterial properties.
【００３０】（比較例２）実施例１で使用したのと同様
の不織布に対し、抗菌剤として１，４−（１−ジョード
メチルスルフォニル）ベンゼンを使用する以外は実施例
１と同様の処理を行った。得られたスパンボンドの抗菌
性評価結果を表２に示す。Comparative Example 2 A nonwoven fabric similar to that used in Example 1 was treated as in Example 1 except that 1,4- (1-jodomethylsulfonyl) benzene was used as the antibacterial agent. went. Table 2 shows the antibacterial evaluation results of the obtained spunbond.
【００３１】このスパンボンドは、風合いは柔らかいも
のの、抗菌効果は低いものであった。This spunbond had a soft texture but a low antibacterial effect.
【００３２】（比較例３）実施例１で使用したのと同様
の不織布に対し、特殊アニオン活性剤からなる一時帯電
防止剤をパッディングし、次いで１３０℃で２分乾燥し
た。得られたスパンボンドの抗菌性評価結果を表２に示
す。Comparative Example 3 The same non-woven fabric as used in Example 1 was padded with a temporary antistatic agent consisting of a special anion activator and then dried at 130 ° C. for 2 minutes. Table 2 shows the antibacterial evaluation results of the obtained spunbond.
【００３３】このスパンボンドは、風合いは柔らかいも
のの、抗菌効果はないものであった。The spunbond had a soft texture but had no antibacterial effect.
【００３４】（実施例２）実施例１で得られた不織布お
よび未加工不織布、コーティングした撥水性不織布によ
り高吸水ポリマーを包含した衛生材料により、使い捨て
おむつを作成した。得られたおむつの抗菌性評価結果を
表２に示す。(Example 2) A disposable diaper was prepared from a sanitary material containing a highly water-absorbing polymer by the nonwoven fabric obtained in Example 1, unprocessed nonwoven fabric and coated water-repellent nonwoven fabric. Table 2 shows the antibacterial evaluation results of the obtained diapers.
【００３５】このおむつは、高い抗菌効果を示すと共に
風合いも柔らかく、着用感も良好であった。This diaper exhibited a high antibacterial effect, a soft texture, and a good wearing feeling.
【００３６】（比較例４）実施例１の不織布を用いない
以外は、実施例２と同様に使い捨ておむつを作成した。
得られたおむつの抗菌性評価結果を表２に示す。(Comparative Example 4) A disposable diaper was prepared in the same manner as in Example 2 except that the nonwoven fabric of Example 1 was not used.
Table 2 shows the antibacterial evaluation results of the obtained diapers.
【００３７】このおむつは、風合いは柔らかく着用感に
は優れるものの、抗菌効果はないものであった。This diaper had a soft texture and an excellent wearing feeling, but had no antibacterial effect.
【００３８】（実施例３）グリセリンおよび精製水を含
有した液に実施例１で得られた不織布に含浸させ濡れテ
ィッシュを作成した。得られた濡れティッシュの抗菌性
評価結果を表２に示す。(Example 3) A wet tissue was prepared by impregnating the non-woven fabric obtained in Example 1 with a liquid containing glycerin and purified water. Table 2 shows the results of evaluating the antibacterial properties of the obtained wet tissues.
【００３９】このティッシュは、高い抗菌効果を示すと
共に風合いも柔らかく、細かい部分のふき取り性も良好
であった。This tissue exhibited a high antibacterial effect, had a soft texture, and had a good wiping property for fine parts.
【００４０】（比較例５）未加工の不織布を用い、実施
例３と同様に濡れティッシュを作成した。得られた濡れ
ティッシュの抗菌性評価結果を表２に示す。(Comparative Example 5) A wet tissue was prepared in the same manner as in Example 3 using an unprocessed nonwoven fabric. Table 2 shows the results of evaluating the antibacterial properties of the obtained wet tissues.
【００４１】このティッシュは、風合いは柔らかく着用
感には優れるものの、抗菌効果はないものであった。This tissue had a soft texture and an excellent wearing feeling, but had no antibacterial effect.
【００４２】[0042]
【表２】 [Table 2]
【００４３】[0043]
【発明の効果】本発明によれば、優れた抗菌性と柔軟な
風合い、且つ低コストの不織布、またかかる性能を有し
た衛生材料および清掃用布帛を提供することができる。Industrial Applicability According to the present invention, it is possible to provide a non-woven fabric having excellent antibacterial properties, a soft texture, and low cost, and a sanitary material and a cleaning cloth having such performance.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ａ４７Ｌ 13/16 Ａ４７Ｌ 13/16 Ａ ４Ｈ０１１ 13/17 13/17 Ａ ４Ｌ０３３ Ａ６１Ｆ 13/00 ３５１ Ａ６１Ｆ 13/00 ３５１Ｆ ４Ｌ０４７ 13/15 Ａ６１Ｌ 2/16 Ｚ 13/472 Ｄ０４Ｈ 1/42 Ｋ 13/53 Ａ６１Ｆ 5/44 Ｈ Ａ６１Ｌ 2/16 Ｄ０６Ｍ 101:20 Ｄ０４Ｈ 1/42 Ａ６１Ｆ 13/18 Ｂ // Ａ６１Ｆ 5/44 ３０３ Ｄ０６Ｍ 101:20 Ｆターム(参考） 3B029 HA00 HB05 3B074 AA02 AA08 AB01 CC01 4C003 AA07 AA16 HA02 4C058 AA04 AA05 AA28 BB07 JJ04 JJ30 4C098 AA09 CC08 CC14 DD10 DD14 DD20 DD25 4H011 AA02 BA01 BB09 BB16 BC19 DA10 DH02 4L033 AA05 AB07 AC10 BA57 4L047 AA14 BA23 CA05 CB10 CC03 CC16 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) A47L 13/16 A47L 13/16 A 4H011 13/17 13/17 A 4L033 A61F 13/00 351 A61F 13/00 351F 4L047 13/15 A61L 2/16 Z 13/472 D04H 1/42 K 13/53 A61F 5/44 H A61L 2/16 D06M 101: 20 D04H 1/42 A61F 13/18 B // A61F 5/44 303 D06M 101: 20 F-term (reference) 3B029 HA00 HB05 3B074 AA02 AA08 AB01 CC01 4C003 AA07 AA16 HA02 4C058 AA04 AA05 AA28 BB07 JJ04 JJ30 4C098 AA09 CC08 CC14 DD10 DD14 DD20 DD25 41607A10 CC08 CC14 DD10 DD14 DD20 DD25 4H0119A09 CC08 4 AA14 BA23 CA05 CB10 CC03 CC16
Claims (5)
れ不織布であって、該不織布に、分子量が２００〜７０
０で、平均粒径が２μｍ以下で、かつ、無機性／有機性
値が０．３〜１．４であるピリジン系抗菌剤が固着され
ていることを特徴とする不織布。1. A non-woven fabric composed of fibers containing a polyolefin fiber, wherein the non-woven fabric has a molecular weight of 200 to 70.
A non-woven fabric characterized in that a pyridine-based antibacterial agent having an average particle size of 0, an average particle size of 2 μm or less, and an inorganic / organic value of 0.3 to 1.4 is adhered.
ンおよびポリエチレンから選ばれた少なくとも１種であ
ることを特徴とする請求項１記載の不織布。2. The non-woven fabric according to claim 1, wherein the polyolefin fiber is at least one selected from polypropylene and polyethylene.
トリクロロメチルピリジン、２−クロロ−４−トリクロ
ロメチル−６−メトキシピリジン、２−クロロ−４−ト
リクロロメチル−６−（２−フリメトキシ）ピリジン、
ジ（４−クロロフェニル）ピリジンメタノール、２，
３，５−トリクロロ−４−（ｎ−プロピルスルフォニ
ル）ピリジン、および、２−ピリジルチオール−１−オ
キシド亜鉛、ジ（２−ピリジルチオール−１−オキシ
ド）から選ばれた少なくとも１種であることを特徴とす
る請求項１または２に記載の不織布。3. The pyridine antibacterial agent is 2-chloro-6-
Trichloromethylpyridine, 2-chloro-4-trichloromethyl-6-methoxypyridine, 2-chloro-4-trichloromethyl-6- (2-furimethoxy) pyridine,
Di (4-chlorophenyl) pyridine methanol, 2,
3,5-trichloro-4- (n-propylsulfonyl) pyridine, and at least one selected from 2-pyridylthiol-1-oxide zinc and di (2-pyridylthiol-1-oxide). The non-woven fabric according to claim 1 or 2, which is characterized.
少なくとも１部に用いて構成されていることを特徴とす
る衛生材料。4. A sanitary material comprising at least a part of the nonwoven fabric according to any one of claims 1 to 3.
少なくとも１部に用いて構成されていることを特徴とす
る清掃用布帛。5. A cleaning cloth comprising the non-woven fabric according to any one of claims 1 to 3 as at least a part thereof.