JP2002371408A - Protector - Google Patents
ProtectorInfo
- Publication number
- JP2002371408A JP2002371408A JP2002107522A JP2002107522A JP2002371408A JP 2002371408 A JP2002371408 A JP 2002371408A JP 2002107522 A JP2002107522 A JP 2002107522A JP 2002107522 A JP2002107522 A JP 2002107522A JP 2002371408 A JP2002371408 A JP 2002371408A
- Authority
- JP
- Japan
- Prior art keywords
- protector
- protective material
- protector according
- fabric
- chest
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、プロテクターに関
するものであり、さらに詳しくは防刃性、防弾性を有す
るプロテクターに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a protector, and more particularly, to a protector having blade-proof and anti-elastic properties.
【０００２】[0002]
【従来の技術】従来、防護衣としては、アイスピック、
バタフライナイフ、出刃包丁のような鋭利な刃物から身
を護るためには、鉄板、ステンレス板、チタン板などの
金属板、およびポリカーボネート樹脂、ナイロン樹脂な
どの特殊樹脂板を衣服の一部に用いた防護、また、銃器
から発射される弾丸から身を護るためには、高強力繊維
を用いた布帛から構成された防護衣が提案されている。
例えば、特開平１−４６５９７号公報には金属板あるい
は特殊樹脂板を組み合わせた構造のものを制服の一部に
用いた防刃服が提案され、また特開平７−２１８１９１
号公報には破断伸度の異なる高強度高弾性率繊維から構
成される防護衣が提案されいる。しかしながら、前者の
金属板を用いたものは、刃物等に対する防刃性は認めら
れるが、防弾性を付与するには厚さをより厚くする必要
があり、軽量性、気心地の面に問題があり、一方、後者
のものは、防弾性、軽量性の面ではかなりの向上が認め
られるが、防刃性が十分でないのが実状である。2. Description of the Related Art Conventionally, an ice pick,
In order to protect yourself from sharp knives such as butterfly knives and knife blades, metal plates such as iron plates, stainless steel plates and titanium plates, and special resin plates such as polycarbonate resin and nylon resin were used for some of the clothes. In order to provide protection and also protect the body from bullets fired from firearms, protective clothing made of fabric using high-strength fibers has been proposed.
For example, Japanese Patent Application Laid-Open No. 1-46597 proposes a blade-proof garment using a combination of a metal plate or a special resin plate as a part of a uniform, and Japanese Patent Application Laid-Open No. 7-218191.
Japanese Patent Application Publication No. JP-A-2005-64131 proposes a protective garment composed of high-strength high-modulus fibers having different breaking elongations. However, although the former one using a metal plate has a blade-proof property against blades and the like, it needs to be thicker in order to provide ballistic resistance, and there are problems with lightness and comfort. On the other hand, the latter has a considerable improvement in terms of the elasticity and lightness, but does not have a sufficient blade-proof property.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、かかる従来
技術の背景に鑑み、運動性に優れ、着用性を重視した快
適な、しかも、防刃性、防弾性にも優れたプロテクター
を提供せんとするものである。SUMMARY OF THE INVENTION In view of the background of the prior art, the present invention does not provide a protector which is excellent in motility, wearability and comfort, and is also excellent in blade-proof and elastic-proof. It is assumed that.
【０００４】[0004]
【課題を解決するための手段】本発明は、かかる課題を
解決するために、次のような手段を採用するものであ
る。すなわち、本発明のプロテクターは、防護材が少な
くとも胸部に取り付けられたプロテクターであって、該
防護材が、高強力繊維からなる織物積層体、高強力繊維
からなる織物に合成樹脂を含浸させた織物積層成型体、
プラスチック成型体および金属成型体の４種から選ばれ
た少なくとも一種からなり、かつ、下記ａ）〜ｄ）の要
件を同時に満足することを特徴とするものである。The present invention employs the following means in order to solve the above-mentioned problems. That is, the protector of the present invention is a protector in which a protective material is attached to at least the chest, wherein the protective material is a woven fabric made of a high-strength fiber, a woven fabric made of a woven fabric made of a high-strength fiber impregnated with a synthetic resin. Laminated moldings,
It comprises at least one selected from the group consisting of a plastic molded body and a metal molded body, and simultaneously satisfies the following requirements a) to d).
【０００５】 ａ）厚さ(mm) Ｔ １≦Ｔ≦１０ ｂ）面密度(kg/ｍ2) Ｗ １≦Ｗ≦１０ ｃ）エネルギー吸収量(kg・m) Ｅ ５≦Ｅ ｄ）貫通長さ(mm) Ｌ ５≧ＬA) Thickness (mm) T 1 ≦ T ≦ 10 b) Area density (kg / m 2 ) W 1 ≦ W ≦ 10 c) Energy absorption (kg · m) E 5 ≦ E d) Penetration length Length (mm) L 5 ≧ L
【０００６】[0006]
【発明の実施の形態】本発明は、防刃性および防弾性を
有し、さらに運動性、着用性の特性を同時に満足する優
れたプロテクターについて、鋭意検討し、特定の防護材
で、かつ、特定な要件を満たす防護材で構成してみたと
ころ、かかる課題を一挙に解決することを究明したもの
である。BEST MODE FOR CARRYING OUT THE INVENTION The present invention has been studied diligently for an excellent protector having a blade-proof property and an anti-elastic property, and at the same time, satisfying the characteristics of mobility and wearability. When they were constructed with protective materials that met specific requirements, they determined that these problems could be solved at once.
【０００７】本発明の防護剤を構成する高強力繊維とし
ては、芳香族ポリアミド繊維、芳香族ポリエステル繊
維、高分子量ポリエチレン繊維、ポリパラフェニレンベ
ンゾビスオキサゾール繊維、高強度ポリビニールアルコ
ール繊維などを好ましく使用することができる。これら
の中でもパラ系芳香族ポリアミド繊維が、防護性能、成
形性に優れ、より好ましく用いられる。かかるパラ系芳
香族ポリアミド繊維としては、モノマーとしてパラフェ
ニレンジアミンとテレフタル酸ジクロライド、ジアミノ
ジフェニルエーテルなどを用いて重合し、紡糸形成した
繊維であり、例えばポリパラフェニレンテレフタルアミ
ドからなる繊維、コポリパラフェニレン３，４−ジフェ
ニレンエーテルテレフタルアミド繊維が好ましく使用さ
れる。As the high-strength fibers constituting the protective agent of the present invention, aromatic polyamide fibers, aromatic polyester fibers, high-molecular-weight polyethylene fibers, polyparaphenylenebenzobisoxazole fibers, high-strength polyvinyl alcohol fibers and the like are preferably used. can do. Among them, para aromatic polyamide fibers are more preferably used because of their excellent protective performance and moldability. The para-aromatic polyamide fiber is a fiber formed by spinning by polymerization using paraphenylenediamine, terephthalic acid dichloride, diaminodiphenyl ether, or the like as a monomer. For example, a fiber made of polyparaphenylene terephthalamide, copolyparaphenylene 3 , 4-Diphenylene ether terephthalamide fibers are preferably used.
【０００８】かかる高強力繊維は、単繊維強度が１５ｃ
Ｎ／ｄｔｅｘ以上を有するものが好ましく用いられる。
また、かかる高強力繊維からなる織物を構成する経糸お
よび緯糸の総繊度としては、１５０〜３，５００ｄｔｅ
ｘのものが好ましく使用される。また、かかる織物のカ
バファクターとしては、１，７００〜２，３００のもの
が好ましく使用される。かかるカバファクターが１，７
００より小さいと、防刃性、防弾性が、不十分になり、
また２，３００より大きいと、製織性および品位の面で
好ましくない。ここでいうカバーファクターは、経糸総
繊度(dtex)をＤ１、経糸密度(本/２．５４ｃｍ)をＮ１
とし、緯糸総繊度(dtex)をＤ２、緯糸密度(本/２．５４
ｃｍ)をＮ２としたときに、（Ｄ１）1/2×Ｎ１＋（Ｄ
２）1/2×Ｎ２で表されるものである。The high-strength fiber has a single fiber strength of 15c.
Those having N / dtex or more are preferably used.
The total fineness of the warp and the weft constituting the woven fabric composed of such high-strength fibers is 150 to 3,500 dte.
x are preferably used. Further, as a cover factor of such a woven fabric, one having a coverage of 1,700 to 2,300 is preferably used. Such a cover factor is 1,7
If it is smaller than 00, the blade resistance and the ballistic resistance become insufficient,
If it is larger than 2,300, it is not preferable in terms of weaving and quality. The cover factor referred to here is D1 for the total warp fineness (dtex) and N1 for the warp density (number / 2.54 cm).
And the weft total fineness (dtex) is D2, the weft density (book / 2.54
cm) as N2, (D1) 1/2 × N1 + (D
2) It is represented by 1/2 × N2.
【０００９】また、本発明で言う高強力繊維からなる織
物積層体とは、前記高強力繊維からなる織物を複数枚積
層したものであり、好ましくは５〜３０枚積層したもの
が好ましく用いられる。The woven fabric laminate of high-strength fibers referred to in the present invention is a laminate of a plurality of woven fabrics of the high-strength fibers, and preferably a laminate of 5 to 30 ply fabrics.
【００１０】次に、本発明で言う高強力繊維からなる織
物に含浸させる合成樹脂としては、熱硬化性樹脂では、
フェノール樹脂、エポキシ樹脂、ポリウレタン樹脂、不
飽和ポリエステル樹脂など、熱可塑性樹脂では、ポリエ
チレン、ポリプロピレン、ポリエステル、ポリアミド、
ポリビニルアセタール、ポリビニルブチラール、ポリス
チレン、ポリカーボネートなどが好ましく使用される
が、これらに限定されるものではない。これらの樹脂
は、好ましくは５〜３０重量％含有せしめるが、限定さ
れるものではない。また、必要に応じて、これらの合成
樹脂を混合させてもよい。Next, as the synthetic resin to be impregnated into the woven fabric composed of high-strength fibers referred to in the present invention, thermosetting resins include:
For thermoplastic resins such as phenolic resin, epoxy resin, polyurethane resin and unsaturated polyester resin, polyethylene, polypropylene, polyester, polyamide,
Polyvinyl acetal, polyvinyl butyral, polystyrene, polycarbonate and the like are preferably used, but are not limited thereto. These resins are preferably contained in an amount of 5 to 30% by weight, but are not limited. Moreover, you may mix these synthetic resins as needed.
【００１１】かかる合成樹脂を含浸させた織物の積層成
型体を得るための成型条件としては、加熱温度が１００
〜２００℃、圧力が１０〜１００kg/cｍ2、加熱時間が
３〜６０分間の範囲で適宜調整されて成型されたものが
好ましい。As a molding condition for obtaining a laminated molded article of a woven fabric impregnated with such a synthetic resin, a heating temperature of 100
It is preferably formed by appropriately adjusting the temperature to 200 ° C., the pressure 10 to 100 kg / cm 2 , and the heating time 3 to 60 minutes.
【００１２】また、本発明で言うプラスチック成型体と
は、前記熱硬化性樹脂および熱可塑性樹脂を用いて射出
成型、押出し成型、圧縮成型などにより得られる成型体
を言う。これらの中でも、比較的比重の小さい熱可塑性
樹脂から得られる成型体が適度な弾性があるので、本発
明には好ましく用いられる。なお、防護材の構成によっ
ても異なるが、特に単独使用の場合は、耐叩打性の面か
ら耐衝撃性の優れたプラスチックを使用することが好ま
しい。また、かかるプラスチック成型体は、軽量性、着
用性および運動性の面から比較的屈曲動作が多く、屈曲
角度の大きい部位、例えば、肩部、肘部、膝部などの部
位に使用することが好ましい。The term "plastic molded article" as used in the present invention refers to a molded article obtained by injection molding, extrusion molding, compression molding or the like using the thermosetting resin and the thermoplastic resin. Among these, a molded article obtained from a thermoplastic resin having a relatively small specific gravity has a suitable elasticity, and thus is preferably used in the present invention. It should be noted that although it differs depending on the configuration of the protective material, it is preferable to use a plastic having excellent impact resistance in terms of tapping resistance, especially when used alone. In addition, such a plastic molded body has a relatively large bending operation in terms of lightness, wearability and mobility, and can be used for a portion having a large bending angle, for example, a portion of a shoulder, an elbow, a knee, or the like. preferable.
【００１３】次に、本発明で言う金属成型体とは、ステ
ンレス、純チタン、チタン合金、アルミニウム合金いわ
ゆるジュラルミンなどからなる金属成型体を言う。これ
らの中でも軽くて、安価なアルミニウム合金が好ましく
用いられる。アルミニウム合金の中でも、特に銅成分を
３〜５％含有するアルミニウム・銅系からなるアルミニ
ウム合金、すなわちＪＩＳ Ｈ４０００規格で表される
Ａ２０１４Ｐ、Ａ２０１７Ｐ、Ａ２０２４Ｐなどのアル
ミニウム合金が好ましい。また、厚さとしては、０．３
〜３ｍｍが好ましく、アルミニウム合金単独使用または
前記防護材との組み合わせ使用により、適宜厚さを調整
することができる。なお、単独使用の場合は、２．２〜
３ｍｍが好ましく用いられる。Next, the metal molded body referred to in the present invention means a metal molded body made of stainless steel, pure titanium, a titanium alloy, an aluminum alloy, so-called duralumin, or the like. Of these, light and inexpensive aluminum alloys are preferably used. Among aluminum alloys, an aluminum alloy containing an aluminum-copper system containing a copper component in an amount of 3 to 5%, that is, an aluminum alloy such as A2014P, A2017P, or A2024P represented by JIS H4000 standard is particularly preferable. The thickness is 0.3
The thickness is preferably adjusted to 3 mm by using the aluminum alloy alone or in combination with the protective material. In the case of single use, 2.2 to 2.2
3 mm is preferably used.
【００１４】かかる防護材は、単独または適宜組み合わ
せ、身体の部位を防護するために適宜積層して用いるこ
とができるが、その中でも、少なくとも胸部を防護する
ために用いられるものである。かかる防護材は、身体の
部位によって適宜使い分けることができるが、特に胸部
に使用される防護材の重量は、軽くて性能に優れたもの
が要求され、好ましくは１．２ｋｇ以下、より好ましく
は１ｋｇ以下の軽量のものが使用される。Such protective materials can be used alone or in appropriate combination, and can be appropriately laminated and used to protect a body part. Among them, the protective material is used to protect at least the chest. Such a protective material can be properly used depending on the body part, but the weight of the protective material used particularly for the chest is required to be light and excellent in performance, preferably 1.2 kg or less, more preferably 1 kg or less. The following lightweight ones are used.
【００１５】さらに、かかる防護材の性能としては、下
記ａ）〜ｄ）の要件を同時に満足することが必須であ
る。Further, it is essential for the performance of such a protective material to simultaneously satisfy the following requirements a) to d).
【００１６】 ａ）厚さ(mm) Ｔ １≦Ｔ≦１０ ｂ）面密度(kg/ｍ2) Ｗ １≦Ｗ≦１０ ｃ）エネルギー吸収(kg・m) Ｅ ５≦Ｅ ｄ）貫通長さ(mm) Ｌ ５≧Ｌ すなわち、厚さ(mm)Ｔは、１≦Ｔ≦１０であり、１＞Ｔ
であると、防刃性、防弾性が不十分であり、１０＜Ｔで
あると、厚過ぎて、着用性すなわち運動性が劣る。面密
度(kg/ｍ2)Ｗは、１≦Ｗ≦１０であり、１＞Ｗである
と、防刃性、防弾性が不十分であり、１０＜Ｗである
と、重過ぎて、着用性すなわち運動性が劣る。防弾性の
パラメーターになるエネルギー吸収(kg・m) Ｅは、５≦
Ｅであり、好ましくは１０≦Ｅである。５＞Ｅである
と、防弾性が不十分である。防刃性を示す貫通長さ(mm)
Ｌは５≧Ｌであり、５＜Ｌであると、防刃性が不十分に
なる。なお、本発明の貫通長さ(mm)Ｌは１６ジュールの
仕事量に相当する力を加えた時の刃物の貫通長さを言う
が、より好ましくは２０ジュール、特に好ましくは２５
ジュールの仕事量に相当する力を加えた時の刃物の貫通
長さが、５≧Ｌであるのがよい。A) Thickness (mm) T 1 ≦ T ≦ 10 b) Area density (kg / m 2 ) W 1 ≦ W ≦ 10 c) Energy absorption (kg · m) E 5 ≦ E d) Penetration length (mm) L 5 ≧ L That is, the thickness (mm) T is 1 ≦ T ≦ 10, and 1> T
If it is, the blade-proof property and the anti-elasticity are insufficient, and if 10 <T, it is too thick and the wearability, that is, the mobility is inferior. The surface density (kg / m 2 ) W is 1 ≦ W ≦ 10, and when 1> W, the blade-proof property and the elasticity-proof are insufficient, and when 10 <W, it is too heavy and worn. Poor motility, that is, mobility. Energy absorption (kg · m) that is a parameter of the ballistic resistance E is 5 ≦
E, and preferably 10 ≦ E. When 5> E, the ballistic resistance is insufficient. Penetration length (mm) showing blade-proof properties
L is 5 ≧ L, and when 5 <L, the blade-proof property becomes insufficient. The penetration length (mm) L of the present invention refers to the penetration length of the blade when a force equivalent to a work amount of 16 joules is applied, more preferably 20 joules, and particularly preferably 25 joules.
The penetration length of the blade when a force corresponding to the work of the joule is applied is preferably 5 ≧ L.
【００１７】また、かかる防護材は、発泡構造体、スポ
ンジ、ゴムなどの緩衝材と貼り合わせた構造で使用する
と、着用性および耐叩打性の面でさらに好ましい。な
お、胸部以外の部位は、必ずしも上記特性を満足する防
護材を使用しなくてもよい。Further, it is more preferable to use such a protective material in a structure in which the protective material is bonded to a cushioning material such as a foamed structure, a sponge, or rubber in terms of wearability and tapping resistance. It is not always necessary to use a protective material that satisfies the above-mentioned characteristics in the part other than the chest.
【００１８】本発明のプロテクターは、かかる防護材
を、織物、編物、不織布などの布帛に取り付けた形でプ
ロテクターを構成するのが好ましい。かかる取り付け構
造としては、防護材を布帛に縫合、ファスナー、面ファ
スナー等で結合させるか、ストラップまたは金具類など
で結合させるなどの手段で取り付ける構造を採用するこ
とができる。また、２枚の布帛間に狭持する構造、また
は、脱着自在の構造などの適宜の手段も好ましく採用す
ることもできる。In the protector of the present invention, it is preferable that the protector is constituted by attaching the protective material to a fabric such as a woven fabric, a knitted fabric, or a non-woven fabric. As such an attachment structure, a structure in which the protective material is attached to the cloth by means of sewing, fasteners, hook-and-loop fasteners, or the like, or by means of a strap, metal fittings, or the like can be adopted. Appropriate means such as a structure of holding between two cloths or a detachable structure can also be preferably adopted.
【００１９】かかる布帛は、通気性の面からメッシュ組
織の布帛が好ましく使用され、さらに好ましくは、難燃
性が、ＪＩＳ Ｌ１０９６Ａ−１法で合格許容範囲内の
ものが使用される。As such a cloth, a cloth having a mesh structure is preferably used from the viewpoint of air permeability, and more preferably, a cloth having a flame retardancy within an acceptable range according to the JIS L1096A-1 method.
【００２０】かかるプロテクターは、該防護材が身体の
部位に沿って曲面した形状の構造を有するものが、着用
性の面で好ましく使用される。また、かかる防護材は、
身体の少なくとも胸部に取り付けられていることが必須
であるが、さらに肩部、上腕部、前腕部、肘部、腹部、
骨盤部、大腿部、局部、膝部、臑部、甲部、背中部など
に取り付けられていることも好ましく、推奨される構成
としては、少なくとも胸部を含む２部位以上に取り付け
られていることが好ましい。なお、軽量性、着用性、運
動性の面から比較的屈曲動作が多く、屈曲角度の大きい
部位、例えば、肩部、肘部、膝部などの部位にプラスチ
ック成型体を含む防護材が好ましく用いられる。As such a protector, one in which the protective material has a curved shape along the body part is preferably used in terms of wearability. In addition, such protective materials,
It is essential that it is attached to at least the chest of the body, but also the shoulders, upper arms, forearms, elbows, abdomen,
It is also preferable to be attached to the pelvis, thigh, local area, knee, shin, instep, back, etc. As a recommended configuration, it should be attached to at least two sites including the chest. Is preferred. In addition, a protective material including a plastic molded body is preferably used in a portion having a relatively large bending operation and a large bending angle in terms of lightness, wearability, and mobility, for example, a portion of a shoulder, an elbow, and a knee. Can be
【００２１】また、かかるプロテクターにおいて、プロ
テクターの総重量は、軽い方が好ましく、好ましくは５
ｋｇ以下、より好ましくは、４ｋｇ以下であるのがよ
い。In such a protector, the total weight of the protector is preferably light, and
The weight is preferably not more than 4 kg, more preferably not more than 4 kg.
【００２２】本発明のプロテクターを図面により、説明
する。まず、図１は、本発明のプロテクターを構成する
防護材の構成の一例を示す概略図であり、この防護材の
例は、布帛１に、スポンジ２、高強力繊維からなる織物
積層体３、高強力繊維からなる織物に樹脂を含浸させた
織物積層成型体４、プラスチック成型体５を順に積層し
て構成されたものである。The protector of the present invention will be described with reference to the drawings. First, FIG. 1 is a schematic diagram showing an example of the configuration of a protective material constituting the protector of the present invention. The protective material is formed by adding a sponge 2 to a cloth 1, a woven laminate 3 composed of high-strength fibers, It is constituted by sequentially laminating a woven fabric laminate 4 and a plastic molded body 5 in which a woven fabric of high-strength fiber is impregnated with a resin.
【００２３】また、図２は、本発明のプロテクターの正
面の構成の一例を示す概略図であり、胸部８は、高強力
繊維からなる織物積層体と高強力繊維からなる織物に樹
脂を含浸させた織物積層成型体とプラスチック成型体と
スポンジからなる防護材で構成されたものであり、他の
部位６〜１７は耐衝撃型プラスチック成型体とスポンジ
からなる防護材で構成されたものである。また、各部位
の防護材は、身体の部位に沿う形状に曲面した構造を有
するものである。一方、布帛への取り付けは、金具１９
およびストラップ２０で取り付けられる。なお、必要に
応じて、各部位の隣り合わせの防護材は、うろこ状に重
ねることもできる。FIG. 2 is a schematic view showing an example of the front configuration of the protector of the present invention. The chest 8 is obtained by impregnating a woven fabric made of a high-strength fiber and a woven fabric made of a high-strength fiber with a resin. The other parts 6 to 17 are made of a protective material made of an impact-resistant plastic molded article and a sponge, and the other parts 6 to 17 are made of a protective material made of a sponge. Further, the protective material of each part has a structure curved in a shape along the body part. On the other hand, the attachment to the cloth
And a strap 20. In addition, if necessary, the protective materials adjacent to each part may be stacked in a scale shape.
【００２４】また、図３は、本発明のプロテクターの背
面の上半身の構成の一例を示す概略図であり、背面１８
は、プラスチック成型体からなる防護材で、同防護材を
うろこ状に複数枚を重ね合わせた構造を有し、金具１９
により補強布帛に取り付け、さらに、そのものを縫合に
より布帛１に取り付けたものである。FIG. 3 is a schematic view showing an example of the structure of the upper body of the back of the protector of the present invention.
Is a protective material made of a plastic molded body, and has a structure in which a plurality of the protective materials are stacked in a scaly shape.
And attached to the fabric 1 by stitching.
【００２５】[0025]
【実施例】次に実施例により、本発明をさらに詳しく説
明する。Next, the present invention will be described in more detail by way of examples.
【００２６】なお、実施例中における特性は、下記の方
法により求めた。 １）厚さ マイクロメータ（三豊製作所製）で測定した。 ２）面密度 防護材（４００ｃｍ2）の質量を量り、１ｍ2当たりの質
量を求めた。 ３）エネルギー吸収量 鋼片発射試験機を用い、２．９グラムの鋼片を４００ｍ
／ｓｅｃで発射させた時のエネルギー吸収を次式により
求めた。The characteristics in the examples were determined by the following methods. 1) Thickness The thickness was measured with a micrometer (manufactured by Mitoyo Seisakusho). 2) Area density The mass of the protective material (400 cm 2 ) was measured, and the mass per 1 m 2 was determined. 3) Energy absorption Using a slab launching tester, a 2.9-gram slab was 400 m long.
The energy absorption when firing at / sec was determined by the following equation.
【００２７】エネルギー吸収Ｅ(Kg・m)＝１／２ｍ（Ｖ1 2
−Ｖ2 2）／Ｇ ［式中、ｍ：鋼片の重量(Kg)、Ｖ1：着弾前の速度(m/se
c)、Ｖ2：着弾後の速度(m/sec)、Ｇ：9.8m/sec2］ ４）貫通長さ 落下衝撃試験機（吉田精機製）を用い、これに刃物とし
てアイスピック、出刃包丁、バタフライナイフを取り付
け、下方には人体疑似物質として油粘土を敷き、その上
に試料を置く。仕事量が１６ジュールなるように荷重と
高さを調整し、自然落下させた時の刃物の貫通長さを測
定した。[0027] The energy absorption E (Kg · m) = 1 / 2m (V 1 2
−V 2 2 ) / G [where, m: weight of billet (kg), V 1 : velocity before landing (m / se
c), V 2 : velocity after landing (m / sec), G: 9.8 m / sec 2 ] 4) Penetration length Using a drop impact tester (manufactured by Yoshida Seiki), using an ice pick as a blade, a knife knife Attach a butterfly knife, spread oil clay as a simulated human body below, and place the sample on it. The load and height were adjusted so that the work amount became 16 joules, and the penetration length of the blade when dropped naturally was measured.
【００２８】実施例１ 単繊維強度２０．５ｃＮ／ｄｔｅｘ、のパラ系芳香族ポ
リアミド(ポリパラフェニレンテレフタルアミド)[東レ
デュポン製]繊維を用い、総繊度３，３３３ｄｔｅｘ、
経密度および緯密度が共に１７本／２．５４ｃｍの平織
物を得た。次いで、この平織物表面にポリビニルブチラ
ール樹脂とフェノール樹脂が１：１からなる混合樹脂液
を塗布し、乾燥し、樹脂含有量１２．５％のプリプレグ
を得た。このプリプレグを５枚積層し、胸部形状の金型
を用い、１６０℃、３０ｋｇ／ｃｍ2で加熱加圧して織
物積層成型体を得た。Example 1 Using a para-aromatic polyamide (polyparaphenylene terephthalamide) [manufactured by Toray DuPont] fibers having a single fiber strength of 20.5 cN / dtex, a total fineness of 3,333 dtex,
A plain fabric having both a warp density and a weft density of 17 / 2.54 cm was obtained. Next, a mixed resin solution consisting of a 1: 1 mixture of polyvinyl butyral resin and phenol resin was applied to the surface of the plain fabric, and dried to obtain a prepreg having a resin content of 12.5%. Five prepregs were stacked and heated and pressed at 160 ° C. and 30 kg / cm 2 using a chest-shaped mold to obtain a woven fabric laminate.
【００２９】一方、単繊維強度２０．５ｃＮ／ｄｔｅ
ｘ、のパラ系芳香族ポリアミド(ポリパラフェニレンテ
レフタルアミド)[東レデュポン製]繊維を用い、総繊度
２２２ｄｔｅｘ、経密度および緯密度が共に７０本／
２．５４ｃｍの平織物を得た。この織物を胸部形状に裁
断し、１５枚が一体になるように縫製して織物積層体を
得た。On the other hand, the single fiber strength is 20.5 cN / dte
x, using a para-aromatic polyamide (polyparaphenylene terephthalamide) [manufactured by Toray Dupont] fiber, with a total fineness of 222 dtex, a density of 70 and a density of weft of 70 /
A 2.54 cm plain weave was obtained. This woven fabric was cut into a chest shape, and sewed so that 15 sheets were integrated to obtain a woven fabric laminate.
【００３０】さらに、黒顔料添加ポリアミド樹脂(耐衝
撃型ナイロン６６樹脂）[東レ製]を用い、胸部形状の金
型を用い射出成型機にて、厚さ３ｍｍのプラスチック成
型体を得た。Further, a plastic molded body having a thickness of 3 mm was obtained by an injection molding machine using a black pigment-added polyamide resin (impact-resistant nylon 66 resin) [manufactured by Toray Industries Co., Ltd.] and a chest-shaped mold.
【００３１】次いで、身体側から織物積層体、織物積層
成型体、プラスチック成型体になるように両面接着テー
プで一体化し、胸部の防護材を作製した。次いで、防護
材の織物積層体側に緩衝材として厚さ２ｍｍの発泡ポリ
エチレンシートを貼り付けた。次いで、防護衣を構成す
るベース布帛に難燃性を有するポリエステル布帛を使用
し、同布帛の胸部に１，３５０ｃｍ2の前記防護材を用
い、胸部以外の部位は射出成形で得られた前記ナイロン
６６樹脂からなる厚さ３ｍｍの各部位のプラスチック成
形体に前記発泡ポリエチレンシートを貼り付けたものを
用い、各部位をリベットと面ファスナーで取り付けプロ
テクターを作製した。Then, the fabric laminate, the fabric laminate molded product, and the plastic molded product were integrated with a double-sided adhesive tape from the body side to prepare a chest protective material. Next, a foamed polyethylene sheet having a thickness of 2 mm was stuck as a cushioning material to the side of the protective material on the fabric laminate side. Next, a polyester fabric having flame retardancy was used for the base fabric constituting the protective clothing, the protective material of 1,350 cm 2 was used for the chest of the same fabric, and the nylon except for the portion obtained by injection molding was used for parts other than the chest. Using a foamed polyethylene sheet adhered to a plastic molded body of each part having a thickness of 3 mm and made of 66 resin, each part was attached with a rivet and a hook-and-loop fastener to produce a protector.
【００３２】このようにして得られたプロテクターの特
性を表１に示した。本発明のプロテクターの胸部は防刃
性、防弾性に優れ、またプロテクターそのものは運動
性、着用性に優れていた。Table 1 shows the characteristics of the protector thus obtained. The chest of the protector of the present invention was excellent in blade-proof property and elasticity-proof, and the protector itself was excellent in mobility and wearability.
【００３３】比較例１ 単繊維強度２０．５ｃＮ／ｄｔｅｘ、のパラ系芳香族ポ
リアミド(ポリパラフェニレンテレフタルアミド)[東レ
デュポン製]繊維を用い、総繊度３，３３３ｄｔｅｘ、
経密度および緯密度が共に１７本／２．５４ｃｍの平織
物を得た。次いで、この平織物表面にポリビニルブチラ
ール樹脂とフェノール樹脂が１：１からなる混合樹脂液
を塗布し、乾燥し、樹脂含有量１２．５％のプリプレグ
を得た。このプリプレグを１０枚積層し、胸部形状の金
型を用い、１６０℃、３０ｋｇ／ｃｍ2で加熱加圧して
織物積層成型体を得た。Comparative Example 1 Using a para-aromatic polyamide (polyparaphenylene terephthalamide) (manufactured by Toray DuPont) fibers having a single fiber strength of 20.5 cN / dtex, a total fineness of 3,333 dtex,
A plain fabric having both a warp density and a weft density of 17 / 2.54 cm was obtained. Next, a mixed resin solution consisting of a 1: 1 mixture of polyvinyl butyral resin and phenol resin was applied to the surface of the plain fabric, and dried to obtain a prepreg having a resin content of 12.5%. Ten prepregs were laminated and heated and pressed at 160 ° C. and 30 kg / cm 2 using a chest-shaped mold to obtain a woven laminated molded product.
【００３４】一方、黒顔料添加ポリアミド樹脂(耐衝撃
型ナイロン６６樹脂）[東レ製]を用い、胸部形状の金型
を用い射出成型機にて、厚さ３ｍｍのプラスチック成型
体を得た。On the other hand, using a black pigment-added polyamide resin (impact-resistant nylon 66 resin) [manufactured by Toray Industries, Ltd.], a 3 mm-thick plastic molded body was obtained by an injection molding machine using a chest-shaped mold.
【００３５】次いで、身体側が織物積層成型体になるよ
うに、プラスチック成型体と両面接着テープで一体化
し、胸部の防護材を作製した。次いで、防護材の織物積
層体側に緩衝材として厚さ２ｍｍの発泡ポリエチレンシ
ートを貼り付けた。次いで、防護衣を構成するベース布
帛に難燃性を有するポリエステル布帛を使用し、同布帛
の胸部に１，３５０ｃｍ2の前記防護材を用い、胸部以
外の部位は、射出成形で得られた前記ナイロン６６樹脂
からなる厚さ３ｍｍの各部位のプラスチック成形体に前
記発泡ポリエチレンシートを貼り付けたものを用い、各
部位をリベットと面ファスナーで取り付けプロテクター
を作製した。Next, the plastic molded body was integrated with a double-sided adhesive tape so that the body side became a woven laminated molded body, thereby producing a chest protective material. Next, a foamed polyethylene sheet having a thickness of 2 mm was stuck as a cushioning material to the side of the protective material on the fabric laminate side. Next, a polyester fabric having flame retardancy was used for the base fabric constituting the protective garment, and the protective material of 1,350 cm 2 was used for the chest of the fabric, and portions other than the chest were obtained by injection molding. Using a foamed polyethylene sheet adhered to a plastic molded body of each part having a thickness of 3 mm and made of nylon 66 resin, each part was attached with a rivet and a hook-and-loop fastener to prepare a protector.
【００３６】このようにして得られたプロテクターの特
性を表１に示した。比較例１のプロテクターの胸部は防
弾性に優れていたが、防刃性が不十分であった。The properties of the protector thus obtained are shown in Table 1. The chest of the protector of Comparative Example 1 was excellent in elasticity, but insufficient in blade-proofing.
【００３７】実施例２ 単繊維強度２１．５ｃＮ／ｄｔｅｘ、のパラ系芳香族ポ
リアミド(ポリパラフェニレンテレフタルアミド)[東レ
デュポン製]繊維を用い、総繊度３，３３３ｄｔｅｘ、
経密度および緯密度が共に１７本／２．５４ｃｍの平織
物を得た。次いで、この平織物表面にポリビニルブチラ
ール樹脂とフェノール樹脂が１：１からなる混合樹脂液
を塗布し、乾燥し、樹脂含有量１０．５％のプリプレグ
を得た。このプリプレグを５枚積層し、胸部形状の金型
を用い、１６０℃、３０ｋｇ／ｃｍ2で加熱加圧して織
物積層成型体を得た。Example 2 Using a para-aromatic polyamide (polyparaphenylene terephthalamide) [manufactured by Toray DuPont] fibers having a single fiber strength of 21.5 cN / dtex, a total fineness of 3,333 dtex,
A plain fabric having both a warp density and a weft density of 17 / 2.54 cm was obtained. Next, a mixed resin solution of polyvinyl butyral resin and phenol resin in a ratio of 1: 1 was applied to the surface of the plain fabric and dried to obtain a prepreg having a resin content of 10.5%. Five prepregs were stacked and heated and pressed at 160 ° C. and 30 kg / cm 2 using a chest-shaped mold to obtain a woven fabric laminate.
【００３８】一方、アルミニウム合金板を用い、厚さ
１．５ｍｍを有する胸部形状の成型体を作製した。次い
で、身体側が織物成型体になるように、アルミニウム合
金成型体と両面接着テープにて一体化し、胸部の防護材
を作製した。次いで、防護材の織物積層体側に緩衝材と
して厚さ３ｍｍのスポンジシートを貼り付けた。次い
で、防護衣を構成するベース布帛に難燃性を有するポリ
エステル布帛を使用し、同布帛の胸部に１，２００ｃｍ
2の前記防護材を用い、胸部以外の部位はにホリエチレ
ンカーボネートからなるプラスチック成型体に同スポン
ジを貼り付けたものを用い、各部位をリベットと面ファ
スナーで取り付けプロテクターを作製した。On the other hand, a chest-shaped molded body having a thickness of 1.5 mm was prepared using an aluminum alloy plate. Next, the aluminum alloy molded body was integrated with a double-sided adhesive tape so that the body side became a woven fabric molded body, thereby producing a chest protective material. Next, a sponge sheet having a thickness of 3 mm was attached as a cushioning material to the side of the protective material on the fabric laminate side. Next, a polyester fabric having flame retardancy was used for the base fabric constituting the protective clothing, and 1,200 cm was applied to the chest of the fabric.
Using the protective material described in 2 , the sponge was adhered to a plastic molded body made of polyethylene carbonate on the part other than the chest, and each part was attached with a rivet and a hook-and-loop fastener to produce a protector.
【００３９】このようにして得られたプロテクターの特
性を表１に示した。本発明のプロテクターの胸部は防刃
性、防弾性に優れ、またプロテクターそのものは運動
性、着用性に優れていた。The characteristics of the protector thus obtained are shown in Table 1. The chest of the protector of the present invention was excellent in blade-proof property and elasticity-proof, and the protector itself was excellent in mobility and wearability.
【００４０】比較例２ 単繊維強度２１．５ｃＮ／ｄｔｅｘ、のパラ系芳香族ポ
リアミド(ポリパラフェニレンテレフタルアミド)[東レ
デュポン製]繊維を用い、総繊度３，３３３ｄｔｅｘ、
経密度および緯密度が共に１７本／２．５４ｃｍの平織
物を得た。次いで、この平織物表面にポリビニルブチラ
ール樹脂とフェノール樹脂が１：１からなる混合樹脂液
を塗布し、乾燥し、樹脂含有量１０．５％のプリプレグ
を得た。このプリプレグを５枚積層し、胸部形状の金型
を用い、１６０℃、３０ｋｇ／ｃｍ2で加熱加圧して織
物積層成型体を得た。Comparative Example 2 Using a para-aromatic polyamide (polyparaphenylene terephthalamide) [manufactured by Toray DuPont] fibers having a single fiber strength of 21.5 cN / dtex, a total fineness of 3,333 dtex,
A plain fabric having both a warp density and a weft density of 17 / 2.54 cm was obtained. Next, a mixed resin solution of polyvinyl butyral resin and phenol resin in a ratio of 1: 1 was applied to the surface of the plain fabric and dried to obtain a prepreg having a resin content of 10.5%. Five prepregs were stacked and heated and pressed at 160 ° C. and 30 kg / cm 2 using a chest-shaped mold to obtain a woven fabric laminate.
【００４１】一方、チタン合金からなる厚さ１．５ｍｍ
を有する胸部形状の成型体を作製した。次いで、身体側
が織物成型体になるように、チタン合金成型体と両面接
着テープにて一体化し、胸部の防護材を作製した。次い
で、防護材の織物積層体側に緩衝材として厚さ３ｍｍの
スポンジシートを貼り付けた。次いで、防護衣を構成す
るベース布帛に難燃性を有するポリエステル布帛を使用
し、同布帛の胸部に１，２００ｃｍ2の前記防護材を用
い、胸部以外の部位にはポリエチレンカーボネートから
なるプラスチック成型体に同スポンジを貼り付けたもの
を用い、各部位をリベットと面ファスナーで取り付けプ
ロテクターを作製した。On the other hand, a 1.5 mm thick titanium alloy
A chest-shaped molded body having the following formula was prepared. Then, the titanium alloy molded body was integrated with a double-sided adhesive tape so that the body side became a woven molded body, thereby producing a chest protective material. Next, a sponge sheet having a thickness of 3 mm was attached as a cushioning material to the side of the protective material on the fabric laminate side. Next, a polyester fabric having flame retardancy is used for the base fabric constituting the protective clothing, and the protective material of 1,200 cm 2 is used for the chest of the fabric, and a plastic molded body made of polyethylene carbonate is used for parts other than the chest. Each part was attached with a rivet and a hook-and-loop fastener to prepare a protector.
【００４２】このようにして得られたプロテクターの特
性を表１に示した。比較例２のプロテクターの胸部は防
刃性、防弾性に優れていたが、重く運動性、着用性に欠
けていた。The characteristics of the protector thus obtained are shown in Table 1. The chest of the protector of Comparative Example 2 was excellent in blade resistance and elasticity resistance, but was heavy and lacked in mobility and wearability.
【００４３】[0043]
【表１】 [Table 1]
【００４４】実施例３ 厚さ３．０ｍｍのアルミニウム・銅系からなるアルミニ
ウム合金板（ＪＩＳＨ４０００規格のＡ２０２４Ｐ）を
用い、プレス成形にて胸部形状(１２００ｃｍ2)のアル
ミニウム合金成形体を作製し、胸部用防護材を得た。次
いで、防護衣を構成するベース布帛に８００ｄｔｅｘの
黒系ナイロン布帛を使用し、前記防護材が脱着可能なポ
ケット状構造を有するベストを縫製し、前記防護材を挿
入した胸部用プロテクターを作製した。一方、胸部以外
の防護材として、黒顔料添加ポリアミド樹脂(耐衝撃型
ナイロン６６樹脂)[東レ製] を用い、各部位形状の金型
にて射出成形し、厚さ３．０ｍｍのプラスチック成形体
を作製した。このプラスチック成形体をナイロン６６の
ニット地で覆った厚さ２．０ｍｍの発泡ポリエチレンシ
ートと面ファスナー付きパワーゴムテープに縫着し、各
部位のプロテクターを作製した。Example 3 An aluminum alloy sheet of a chest shape (1200 cm 2 ) was manufactured by press molding using an aluminum alloy plate (A2024P of JIS H4000 standard) having a thickness of 3.0 mm and made of aluminum and copper. Protective material was obtained. Next, using a black nylon fabric of 800 dtex as a base fabric constituting the protective clothing, a vest having a pocket-like structure to which the protective material can be attached and detached was sewn, and a chest protector into which the protective material was inserted was produced. On the other hand, a black pigment-added polyamide resin (impact-resistant nylon 66 resin) [manufactured by Toray Industries Co., Ltd.] (produced by Toray Co., Ltd.) was used as a protective material other than the chest, and injection-molded with a mold having a shape of each part to obtain a plastic molded product having a thickness of 3.0 mm. Was prepared. The plastic molded body was sewn to a 2.0-mm-thick foamed polyethylene sheet covered with a nylon 66 knitted fabric and a power rubber tape with a hook-and-loop fastener to produce protectors at each site.
【００４５】このようにした得られたプロテクターの特
性を表２に示した。本発明のプロテクターの胸部は、防
刃性、防弾性に優れ、また全部位のプロテクターを装着
した時も運動性、着用性に優れていた。The characteristics of the protector thus obtained are shown in Table 2. The chest of the protector of the present invention was excellent in blade-proofing property and elasticity-proof, and was excellent in mobility and wearability even when the protectors of all parts were mounted.
【００４６】[0046]
【表２】 [Table 2]
【００４７】[0047]
【発明の効果】本発明によれば、高い防刃性能および高
い防弾性能を有すると共に、身体に沿った形状を有する
ため、運動性、着用性に優れたプロテクターを提供する
ことができる。According to the present invention, it is possible to provide a protector which is excellent in motility and wearability because it has high blade-proof performance and high bullet-proof performance and has a shape along the body.
【図１】この図は、本発明のプロテクターを構成する防
護材の構成の一例を示す概略図である。FIG. 1 is a schematic view showing an example of a configuration of a protective material constituting a protector of the present invention.
【図２】この図は、本発明のプロテクターの正面の構成
の一例を示す概略図である。FIG. 2 is a schematic diagram showing an example of a front configuration of the protector of the present invention.
【図３】この図は、本発明のプロテクターの背面の構成
の一例を示す概略図である。FIG. 3 is a schematic view showing an example of the configuration of the back surface of the protector of the present invention.
１ 布帛 ２ スポンジ ３ 織物積層体 ４ 織物積層成型体 ５ プラスチック成型体 ６ 肩部防護材 ７ 上腕部防護材 ８ 胸部防護材 ９ 肘部防護材 １０ 前腕部防護材 １１ 腰部防護材 １２ 腹部防護材 １３ 局部防護材 １４ 大腿部防護材 １５ 膝部防護材 １６ 臑部防護材 １７ 足甲部防護材 １８ 背中部防護材 １９ 取付け金具 ２０ ストラップ ２１ 縫糸 DESCRIPTION OF SYMBOLS 1 Cloth 2 Sponge 3 Woven laminated body 4 Woven laminated molded body 5 Plastic molded body 6 Shoulder protective material 7 Upper arm protective material 8 Chest protective material 9 Elbow protective material 10 Forearm protective material 11 Waist protective material 12 Abdominal protective material 13 Local protective material 14 Thigh protective material 15 Knee protective material 16 Shine protective material 17 Instep protective material 18 Back protective material 19 Mounting bracket 20 Strap 21 Sewing thread
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ａ４１Ｄ 31/00 Ａ４１Ｄ 31/00 ５０２Ｈ ５０３ ５０３Ｆ ５０４ ５０４Ａ 31/02 31/02 Ａ Ｂ Ｃ Ｄ０３Ｄ 1/00 Ｄ０３Ｄ 1/00 Ａ 15/12 15/12 Ｚ 23/00 23/00 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) A41D 31/00 A41D 31/00 502H 503 503F 504 504A 31/02 31/02 ABC D03D 1/00 D03D 1/00 A 15/12 15/12 Z 23/00 23/00
Claims (21)
プロテクターであって、該防護材が、高強力繊維からな
る織物積層体、高強力繊維からなる織物に合成樹脂を含
浸させた織物積層成型体、プラスチック成型体および金
属成型体の４種から選ばれた少なくとも一種からなり、
かつ、下記ａ）〜ｄ）の要件を同時に満足することを特
徴とするプロテクター。 ａ）厚さ(mm) Ｔ １≦Ｔ≦１０ ｂ）面密度(kg/ｍ2) Ｗ １≦Ｗ≦１０ ｃ）エネルギー吸収量(kg・m) Ｅ ５≦Ｅ ｄ）貫通長さ(mm) Ｌ ５≧Ｌ1. A protector in which a protective material is attached to at least the chest, wherein the protective material is a woven laminate made of high-strength fibers, and a woven laminate formed by impregnating a woven fabric made of high-strength fibers with a synthetic resin. , Consisting of at least one selected from the four types of molded plastic and molded metal,
And a protector that simultaneously satisfies the following requirements a) to d). a) Thickness (mm) T 1 ≦ T ≦ 10 b) Area density (kg / m 2 ) W 1 ≦ W ≦ 10 c) Energy absorption (kg · m) E 5 ≦ E d) Penetration length (mm) ) L5 ≧ L
の単繊維強度を有するものである請求項１に記載のプロ
テクター。2. The protector according to claim 1, wherein the high-strength fiber has a single fiber strength of 15 cN / dtex or more.
繊維である請求項１または２に記載のプロテクター。3. The protector according to claim 1, wherein the high-strength fiber is a para-aromatic polyamide fiber.
３，５００ｄｔｅｘの総繊度を有する経糸および緯糸で
構成されているものである請求項１〜３のいずれかに記
載のプロテクター。4. A woven fabric comprising said high-strength fiber,
The protector according to any one of claims 1 to 3, wherein the protector is constituted by a warp and a weft having a total fineness of 3,500 dtex.
〜２，３００のカバーファクターを有するものである請
求項１〜４のいずれかに記載のプロテクター。5. A fabric comprising said high-strength fiber,
The protector according to any one of claims 1 to 4, which has a cover factor of ~ 2,300.
ら構成されている請求項１に記載のプロテクター。6. The protector according to claim 1, wherein said plastic molded body is made of a thermoplastic resin.
されたものである請求項１に記載のプロテクター。7. The protector according to claim 1, wherein the metal molded body is made of an aluminum alloy.
厚さを有するものである請求項７に記載のプロテクタ
ー。8. The protector according to claim 7, wherein said aluminum alloy has a thickness of 0.3 to 3 mm.
ゴムの中から選ばれた少なくとも一種の緩衝材を貼り合
わせて構成されたものである請求項１に記載のプロテク
ター。9. The protector according to claim 1, wherein said protective material is formed by bonding at least one kind of cushioning material selected from a foamed structure, sponge and rubber.
テクターを構成しているものである請求項１または９に
記載のプロテクター。10. The protector according to claim 1, wherein said protective material is attached to a fabric to form a protector.
ラップおよび金具から選ばれた少なくとも１種の結合手
段により布帛に取り付けられている請求項１０に記載の
プロテクター。11. The protector according to claim 10, wherein the protective material is attached to the fabric by at least one kind of joining means selected from a sewn, a hook-and-loop fastener, a strap and a metal fitting.
る構造で取り付けられている請求項１０または１１に記
載のプロテクター。12. The protector according to claim 10, wherein said protective material is attached by a structure sandwiched between two cloths.
り付けられている請求項１０〜１２のいずれかに記載の
プロテクター。13. The protector according to claim 10, wherein said protective material is attached to the fabric in a detachable structure.
選ばれた少なくとも一種である請求項１０〜１２のいず
れかに記載のプロテクター。14. The protector according to claim 10, wherein said fabric is at least one selected from a woven fabric, a knitted fabric and a nonwoven fabric.
求項１４に記載のプロテクター。15. The protector according to claim 14, wherein the cloth is a cloth having a mesh structure.
に基づいて測定される難燃性に合格するものである請求
項１０〜１５のいずれかに記載のプロテクター。16. The protector according to claim 10, wherein the fabric passes the flame retardancy measured based on JIS L1091 A-1 method.
面した構造を有するものである請求項１〜１６のいずれ
かに記載のプロテクター。17. The protector according to claim 1, wherein said protective material has a structure curved in a shape along a body part.
型体を含む構造である請求項１〜１６のいずれかに記載
のプロテクター。18. The protector according to claim 1, wherein said protective material has a structure including at least a plastic molded body.
下の重量を有する防護材で構成されているものである請
求項１〜１８のいずれかに記載のプロテクター。19. The protector according to claim 1, wherein the chest of the protector is made of a protective material having a weight of 1.2 kg or less.
５００cｍ2の面積を有する防護材で構成されているもの
である請求項１９に記載のプロテクター。20. The protector according to claim 20, wherein the chest is 500 to 1,
20. The protector according to claim 19, comprising a protective material having an area of 500 cm < 2 >.
を有するものである請求項１〜２０のいずれかに記載の
プロテクター。21. The protector according to claim 1, wherein said protector has a total weight of 5 kg or less.