JP2002339575A - Tape for repairing crack of concrete pole - Google Patents
Tape for repairing crack of concrete poleInfo
- Publication number
- JP2002339575A JP2002339575A JP2001149304A JP2001149304A JP2002339575A JP 2002339575 A JP2002339575 A JP 2002339575A JP 2001149304 A JP2001149304 A JP 2001149304A JP 2001149304 A JP2001149304 A JP 2001149304A JP 2002339575 A JP2002339575 A JP 2002339575A
- Authority
- JP
- Japan
- Prior art keywords
- tape
- crack
- transparent region
- shape
- repair
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】この発明は、コンクリート柱
のひび割れ補修用テープに関する。The present invention relates to a tape for repairing cracks in concrete columns.
【0002】[0002]
【従来の技術】一般にコンクリート柱は型枠により作ら
れるようになっている。2. Description of the Related Art In general, concrete pillars are made of a formwork.
【0003】[0003]
【発明が解決しようとする課題】型枠により作られるコ
ンクリート柱は、その製造過程において、時として型枠
の合せ目に沿って縦のひび割れが発生する。[0003] Concrete pillars made of a formwork sometimes undergo vertical cracks along the seams of the formwork during the manufacturing process.
【0004】ひび割れは、水侵入により内部の鉄筋等の
腐食を促進する等の悪影響が起きるところから発生した
ひび割れは充填剤を注入することで補修を行なってい
る。[0004] Cracks are repaired by injecting a filler, where cracks are caused by adverse effects such as accelerating corrosion of internal reinforcing bars and the like due to water intrusion.
【0005】この場合、ひび割れは、浅いものから深い
ものまであり、充填効率は充填剤の流動性状に左右され
る。特に深い時には充填剤の流動性状が低いと隅々まで
確実にいきわたらなく恐れがあるところから、流動性状
は高いことが望ましい。反面、充填剤の流動性状が高い
と注入時にひび割れ上面にあふれて流れ落ちる等、充填
完了後、見栄えのよい補修仕上面が得られない等の不具
合があった。[0005] In this case, cracks range from shallow to deep, and the filling efficiency depends on the fluidity of the filler. Especially when the filler is deep, if the fluidity of the filler is low, it may not be able to reliably reach all corners, so that the fluidity is preferably high. On the other hand, if the flowability of the filler is high, there are problems such as the overflow of the cracked upper surface at the time of the injection and the flow of the filler, and the appearance of the repaired upper surface after completion of the filling is not obtained.
【0006】そこで、この発明は、確実な充填を可能に
すると共に見栄えのよい補修仕上面が得られるようにし
たコンクリート柱のひび割れ補修用テープを提供するこ
とを目的としている。Accordingly, an object of the present invention is to provide a tape for repairing cracks in a concrete column, which enables reliable filling and obtains a good-looking repaired top surface.
【0007】[0007]
【課題を解決するための手段】前記目的を達成するため
に、この発明の請求項1にあっては、所定の長さに形成
されたテープ本体の中央部位で長手方向に沿って、一方
のテープ端縁から他方のテープ端縁へ向かって連続する
薄肉に形成された長溝状の透明領域を形成する一方、そ
の透明領域の周囲に形成されるU字状の面を、テープ本
体の接着面としたことを特徴とする。In order to achieve the above-mentioned object, according to the first aspect of the present invention, one of the lengths of a tape body formed along a longitudinal direction at a central portion of a tape body formed to have a predetermined length. While forming a thin, long, groove-shaped transparent region that is continuous from the tape edge to the other tape edge, a U-shaped surface formed around the transparent region is bonded to the adhesive surface of the tape body. It is characterized by having.
【0008】これにより、テープ本体の接着面をひび割
れに沿って接着する。この接着時、ひび割れの部分は長
溝状の透明領域内に望むと共に、透明領域に沿って若干
の隙間が作られるから、その上方からチューブ等を介し
て充填剤を注入する。この場合、注入時の状態が外から
監視できると共に流動性状の高いものを用いても外へ流
れ落ちることのない型枠として機能し、ひび割れ内に確
実に充填されるようになる。充填完了後、充填剤の硬化
を待ってテープ本体を取り外せば、見栄えのよい補修仕
上面が得られるようになる。Thus, the bonding surface of the tape body is bonded along the crack. At the time of this bonding, the cracked portion is desired in the long groove-shaped transparent region, and a slight gap is formed along the transparent region. Therefore, the filler is injected from above through a tube or the like. In this case, the state at the time of injection can be monitored from the outside, and even if a material having a high fluidity is used, the mold functions as a mold that does not flow out to the outside, so that the crack can be reliably filled. After the filling is completed, the tape main body is removed after the curing of the filler, and a good-looking repaired upper surface can be obtained.
【0009】また、この発明の請求項2によれば、中央
部位が帯状に開口し、正面からみてU字状に形成される
と共に、U字状に形成された一方の面が接着面となるよ
うブチルゴム系粘着剤が塗布された長手方向に連続する
ベーステープと、そのベーステープと幅及び長さが同一
で接着面となる反対側の面に重ね合せ結合された透明な
軟質塩化ビニールテープとから成ることを特徴とする。According to the second aspect of the present invention, the central portion is opened in a band shape, is formed in a U shape when viewed from the front, and one surface formed in the U shape is an adhesive surface. A base tape continuous in the longitudinal direction to which a butyl rubber-based adhesive is applied, and a transparent soft PVC tape that is the same in width and length as the base tape and that is overlapped and bonded to the opposite surface serving as an adhesive surface. Characterized by comprising:
【0010】これにより、ベーステープと透明な軟質塩
化ビニールテープとの重ね合せ結合により、注入状態が
監視できる透明窓となる透明領域を備えた補修用テープ
が簡単に作れるようになる。また、ブチルゴム系粘着剤
によってコンクリート柱のように表面が荒く、しかも、
曲面形状となる等の悪条件下にあっても確実に接着させ
ることが可能となる。[0010] This makes it possible to easily produce a repair tape having a transparent region which becomes a transparent window in which the state of injection can be monitored by superimposing and bonding the base tape and the transparent soft vinyl chloride tape. In addition, the surface is rough like a concrete pillar by butyl rubber adhesive, and moreover,
Even under bad conditions such as a curved surface shape, it is possible to securely adhere.
【0011】[0011]
【発明の実施の形態】以下、図1乃至図5の図面を参照
しながらこの発明の実施の形態について具体的に説明す
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be specifically described below with reference to FIGS.
【0012】図1は補修用テープ1の正面図を示したも
ので、補修用テープ1のテープ本体3は、図2、図3に
示すように接着面5を有するベーステープ7と透明な軟
質塩化ビニールテープ9とから成っている。FIG. 1 is a front view of the repair tape 1. The tape body 3 of the repair tape 1 is composed of a base tape 7 having an adhesive surface 5 and a transparent soft material as shown in FIGS. And a vinyl chloride tape 9.
【0013】ベーステープ7は、テープ上端縁からテー
プ下端縁に向かって帯状に開口することで正面からみて
上下に長いU字状に形成されている。U字状に形成され
た一方の面は、前記したように接着面5となっていて、
この接着面5は、ブチルゴム系粘着剤を塗布することで
形成されている。The base tape 7 is formed in a U-shape that is vertically long when viewed from the front by opening in a belt shape from the upper edge of the tape toward the lower edge of the tape. One surface formed in a U-shape is the bonding surface 5 as described above,
The bonding surface 5 is formed by applying a butyl rubber-based adhesive.
【0014】透明な軟質塩化ビニールテープ9は、前記
ベーステープ7と幅及び長さが同一に形成され、接着面
5となる反対側の面に接着手段によって重ね合せ結合さ
れている。この場合、軟質塩化ビニールテープ9とベー
ステープ7の結合は接着手段に特定されず、他の結合手
段を用いてもよい。The transparent soft vinyl chloride tape 9 is formed to have the same width and length as the base tape 7 and is overlapped and bonded to the surface opposite to the bonding surface 5 by bonding means. In this case, the bonding between the soft vinyl chloride tape 9 and the base tape 7 is not limited to the bonding means, and other bonding means may be used.
【0015】これにより、透明な軟質塩化ビニールテー
プ9によって図1で示すようにテープ本体3の中央部位
で長手方向に沿って薄肉に形成された長溝状の透明領域
11が作られる一方、図2に示すように透明領域11と
なる長溝13内は、コンクリート柱15に接着した時に
充填剤が充填される上方が開放された型枠スペースとし
て機能するようになっている。Thus, as shown in FIG. 1, the transparent soft vinyl chloride tape 9 forms a long groove-shaped transparent region 11 formed in the center portion of the tape main body 3 along the longitudinal direction. As shown in the figure, the inside of the long groove 13 which becomes the transparent area 11 functions as a form space in which the upper portion is opened when the filler is filled when it is bonded to the concrete column 15.
【0016】このように構成された補修用テープ1は、
所定の長さに形成されると共に接着面5は剥離紙16に
よって接着面5が汚れることがないよう管理されてい
る。The repair tape 1 constructed as described above is
The adhesive surface 5 is formed to have a predetermined length and is managed so that the adhesive surface 5 is not stained by the release paper 16.
【0017】したがって、使用する時には、図4に示す
ようにコンクリート柱15のひび割れ17に対応して上
端側を必要な長さに切断すると共に剥離紙16を剥して
ひび割れ17に沿って接着する。この接着時、コンクリ
ート柱15のように表面が荒く、しかも、曲面形状にあ
っても確実に接着し合う。と同時にひび割れ17の部分
は、長溝状の透明領域11内に望むと共に透明領域11
に沿って若干の隙間が作られるから、充填容器19から
延長された供給チューブ21の先端を一杯に挿入し、充
填剤23を注入する。この時の充填剤23はセメント
系、樹脂系いずれであってもよい。Therefore, at the time of use, as shown in FIG. 4, the upper end side is cut to a required length corresponding to the crack 17 of the concrete column 15, and the release paper 16 is peeled off and adhered along the crack 17. At the time of this bonding, the surfaces are rough like the concrete pillars 15 and even if they have a curved surface shape, they are securely bonded to each other. At the same time, the portion of the crack 17 is desired in the long groove-shaped transparent region 11 and the transparent region 11
Since a slight gap is formed along the line, the tip of the supply tube 21 extended from the filling container 19 is fully inserted, and the filler 23 is injected. At this time, the filler 23 may be a cement type or a resin type.
【0018】一方、注入時の状態は外から監視できると
共に流動性状の高い充填剤23を用いても長溝状の透明
領域11は型枠として機能し外へ流れ落ちることはな
く、ひび割れ17内に確実に充填されるようになる。充
填完了後、硬化を待って補修用テープ1を取り外せば、
図5に示すようにコンクリート柱15の表面に若干盛り
上がった状態の見栄えのよい補修仕上面25が得られる
ようになる。On the other hand, the state at the time of injection can be monitored from the outside, and even if a filler 23 having a high fluidity is used, the long groove-shaped transparent region 11 functions as a mold and does not flow down to the outside. Will be filled. After filling is completed, wait for curing and remove the repair tape 1
As shown in FIG. 5, a good-looking repaired upper surface 25 slightly raised on the surface of the concrete pillar 15 can be obtained.
【0019】[0019]
【発明の効果】以上、説明したようにこの発明の請求項
1によれば、補修用テープによって充填剤をひび割れ内
に確実に充填を行なうことができると共に、見栄えのよ
い補修仕上面が得られるようになる。As described above, according to the first aspect of the present invention, the filler can be reliably filled into the cracks by the repair tape, and the repaired top surface with good appearance can be obtained. Become like
【0020】また、この発明の請求項2によれば、注入
状態が監視できる透明領域を備えた補修用テープが簡単
に作れるようになる。しかも、ブチルゴム系粘着剤によ
ってコンクリート柱のように表面が荒く、曲面形状にあ
る条件の悪い所でも確実に接着させることが可能とな
る。Further, according to the second aspect of the present invention, a repair tape having a transparent region in which an injection state can be monitored can be easily manufactured. Moreover, the butyl rubber-based pressure-sensitive adhesive makes it possible to reliably adhere even to a place having a rough surface such as a concrete column and a curved surface with poor conditions.
【図1】この発明にかかる補修用テープの概要正面図。FIG. 1 is a schematic front view of a repair tape according to the present invention.
【図2】図1のA−A断面図。FIG. 2 is a sectional view taken along line AA of FIG.
【図3】補修用テープを分解した概要説明図。FIG. 3 is a schematic explanatory view in which a repair tape is disassembled.
【図4】ひび割れの補修作業を示した説明図。FIG. 4 is an explanatory view showing a repair work for cracks.
【図5】補修完了後の補修仕上面を示した説明図。FIG. 5 is an explanatory view showing a repaired upper surface after completion of the repair.
3…テープ本体 5…接着面 11…透明領域 15…コンクリート柱 17…ひび割れ 23…充填剤 3 Tape main body 5 Adhesive surface 11 Transparent area 15 Concrete pillar 17 Crack 23 Filler
───────────────────────────────────────────────────── フロントページの続き (72)発明者 半田 隆夫 東京都新宿区西新宿三丁目19番2号 東日 本電信電話株式会社内 Fターム(参考) 2E176 AA04 BB12 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Takao Handa 3-19-2 Nishi-Shinjuku, Shinjuku-ku, Tokyo F-term in Nippon Telegraph and Telephone Corporation 2E176 AA04 BB12
Claims (2)
央部位で長手方向に沿って、一方のテープ端縁から他方
のテープ端縁へ向かって連続する薄肉に形成された長溝
状の透明領域を形成する一方、その透明領域の周囲に形
成されるU字状の面を、テープ本体の接着面としたこと
を特徴とするコンクリート柱のひび割れ補修用テープ。1. A thin, long, groove-shaped transparent part that is continuous from one tape edge to the other tape edge along a longitudinal direction at a central portion of a tape body formed to a predetermined length. A tape for repairing cracks in a concrete column, wherein a U-shaped surface formed around the transparent region is formed as an adhesive surface of the tape body while forming the region.
字状に形成されると共に、U字状に形成された一方の面
が接着面となるようブチルゴム系粘着剤が塗布された長
手方向に連続するベーステープと、そのベーステープと
幅及び長さが同一で接着面となる反対側の面に重ね合せ
結合された透明な軟質塩化ビニールテープとから成るこ
とを特徴とするコンクリート柱のひび割れ補修用テー
プ。2. A central portion is opened in a strip shape and viewed from the front,
A base tape formed in a U-shape and having a butyl rubber-based pressure-sensitive adhesive applied so that one surface formed in a U-shape is an adhesive surface, and a base tape having a width and a length that are continuous with the base tape. A tape for repairing cracks in concrete columns, comprising a transparent soft vinyl chloride tape superimposed and bonded to the same surface opposite to the adhesive surface.