JP2002242120A - Filler-filled artificial grass and artificial grass ground - Google Patents
Filler-filled artificial grass and artificial grass groundInfo
- Publication number
- JP2002242120A JP2002242120A JP2001036982A JP2001036982A JP2002242120A JP 2002242120 A JP2002242120 A JP 2002242120A JP 2001036982 A JP2001036982 A JP 2001036982A JP 2001036982 A JP2001036982 A JP 2001036982A JP 2002242120 A JP2002242120 A JP 2002242120A
- Authority
- JP
- Japan
- Prior art keywords
- filler
- pile
- artificial turf
- filled
- piles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ロングパイル人工
芝のパイル間に充填材を充填した充填材入り人工芝に関
し、さらに詳しくいえば、充填材の充填作業性を損なう
ことなく、充填材の飛散を効果的に防止でき、さらに耐
摩耗性などの人工芝性状も向上する技術に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an artificial turf containing a filler, in which a filler is filled between piles of a long-pile artificial turf. The present invention relates to a technology capable of effectively preventing scattering and improving artificial turf properties such as abrasion resistance.
【０００２】[0002]
【従来の技術】サッカー場や野球場などに用いられる人
工芝の多くは、整地された下地上にクッション層を設
け、その上に人工芝を置き敷きしたものに、充填材を充
填するようにした充填材入り人工芝がよく用いられてい
た。2. Description of the Related Art Artificial turf used in soccer fields and baseball stadiums is often provided with a cushion layer on a leveled ground, on which artificial turf is laid and filled with a filler. Filled artificial turf was often used.
【０００３】また、近年では新しいタイプの人工芝とし
て、パイル長さが５０ｍｍ以上であるロングパイルを基
布に植設して、そのパイル間に硅砂などの硬質充填物
と、ゴムチップなどの弾性充填物とからなる充填材を層
状に充填したものが提供されている。In recent years, as a new type of artificial turf, a long pile having a pile length of 50 mm or more is planted in a base cloth, and a hard filler such as silica sand and an elastic filler such as a rubber chip are filled between the piles. There is provided a material in which a filler composed of a material is filled in a layer.
【０００４】このタイプの人工芝は、充填材層が上述し
たクッション層の役割を果たすため、人工芝の安定性や
弾力性がより向上し、また、サッカーや野球のスパイク
が充填材に入り込んで足の動きを拘束しにくいため、良
好なプレー性が得られる。In this type of artificial turf, since the filler layer plays the role of the cushion layer described above, the stability and elasticity of the artificial turf are further improved, and spikes of soccer and baseball enter the filler. Since it is difficult to restrain the movement of the foot, good playability can be obtained.
【０００５】ところで、ロングパイル人工芝に充填され
るゴムチップなどの弾性粒状物は、硅砂などの硬質粒状
物と比較して明らかにその粒径が大きいため、パイル間
に充填材を充填し難い。したがって、このロングパイル
人工芝においては、パイル間に充填材を充填しやすくす
るために、先の従来型の人工芝よりもパイルの植設密度
を低くするようにしている。[0005] By the way, since elastic particles, such as rubber chips, to be filled in long pile artificial turf are clearly larger in particle size than hard particles, such as silica sand, it is difficult to fill the filler between the piles. Therefore, in this long-pile artificial turf, the planting density of the pile is set lower than that of the above-mentioned conventional artificial turf in order to easily fill the filler between the piles.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、パイル
の植設密度が低いと以下のような課題が生じる。すなわ
ち、単位面積当たりのパイル本数が少ないため、必然的
に各パイルに掛かる踏圧などの負荷が大きくなり、耐摩
耗性が低下しやすい。However, when the planting density of the pile is low, the following problems occur. That is, since the number of piles per unit area is small, a load such as a tread pressure applied to each pile is inevitably increased, and the wear resistance is likely to be reduced.
【０００７】また、単位面積当たりのパイル本数が少な
いため、充填材の表面から突出したパイルの先端部分で
の充填材捕捉性が十分発揮されず、充填材が移動した
り、飛散しやすかった。そこで、定期的に人工芝に生じ
た不陸を修正する必要があった。[0007] Further, since the number of piles per unit area is small, the ability of the pile to protrude from the surface of the filler to capture the filler at the tip end is not sufficiently exhibited, and the filler is likely to move or scatter. Therefore, it was necessary to correct irregularities that occurred on the artificial turf periodically.
【０００８】上述した課題は、パイルの植設密度を高く
設定することである程度は回避されるが、逆に高すぎる
と、充填材（主に、弾性粒状物）をパイル間に充填しに
くくなるばかりでなく、スパイクが引っ掛かりやすくな
るため、プレー性も損なわれやすかった。[0008] The above-mentioned problem can be avoided to some extent by setting the planting density of the pile high. On the contrary, if the planting density is too high, it becomes difficult to fill the filler (mainly, elastic granular material) between the piles. Not only that, spikes were easily caught and playability was easily impaired.
【０００９】[0009]
【課題を解決するための手段】そこで、本発明の発明者
は、ロングパイル人工芝において、充填材の充填作業性
を損なうことなく、充填材の飛散を効果的に防止でき、
耐摩耗性などの各種人工芝性状を向上させることができ
るパイルの好適な植設条件を見出した。SUMMARY OF THE INVENTION Accordingly, the inventor of the present invention has been able to effectively prevent the scattering of the filler in the long pile artificial turf without impairing the workability of filling the filler.
The present inventors have found suitable pile planting conditions that can improve various artificial turf properties such as abrasion resistance.
【００１０】すなわち、本発明は、基布にパイルを植設
した人工芝のパイル間に弾性粒状物を含む充填材を充填
し、その充填材の表面からパイル先端を１０ｍｍ以上突
出させてなる充填材入り人工芝において、上記パイルの
上記基布に対する単位面積当たりの植設密度が０．７〜
１．７本／ｃｍ２であることを特徴としている。That is, the present invention relates to a filling method comprising filling a filler containing elastic particles between piles of artificial turf in which a pile is planted in a base cloth, and projecting a tip of the pile from the surface of the filler by 10 mm or more. In the artificial turf containing timber, the planting density per unit area of the pile with respect to the base fabric is 0.7 to 0.7%.
It is 1.7 lines / cm 2 .
【００１１】これによれば、上記植設密度を満足させる
ことにより、充填材の充填性や飛散防止性（捕捉性）を
損なうことなく、人工芝の耐摩耗性やプレー性を向上さ
せることができる。ここで、本発明の植設密度とは、単
位面積当たりの基布に対するパイルの植設箇所の個数を
いう。According to this, by satisfying the planting density, it is possible to improve the wear resistance and playability of the artificial turf without impairing the filling property of the filler and the scattering prevention property (capturing property). it can. Here, the planting density of the present invention refers to the number of places where the pile is planted with respect to the base fabric per unit area.
【００１２】すなわち、植設密度が０．７本／ｃｍ２よ
りも小さいと、充填材が飛散しやすく、パイルの耐摩耗
性が低くなる。逆に、植設密度が１．７本／ｃｍ２より
も高いと、充填材が充填しにくく、スパイク効果が効き
すぎるためプレー性を損なうおそれがでてくる。That is, when the planting density is smaller than 0.7 fibers / cm 2 , the filler is liable to be scattered, and the wear resistance of the pile is lowered. Conversely, if the planting density is higher than 1.7 fibers / cm 2 , the filler is difficult to fill and the spike effect is too effective, which may impair playability.
【００１３】本発明の人工芝をタフティングマシンを用
いて製造する場合、タフト方向の植設間隔（ステッチ）
は、基布の送り速度を変えるなどして自由に変えること
ができるが、ステッチ方向に対して直交する方向の植設
間隔（ゲージ）は、針の間隔を制御するため変化させに
くい。When the artificial turf of the present invention is manufactured by using a tufting machine, the planting interval (stitch) in the tuft direction is used.
Can be freely changed by changing the feed speed of the base cloth, but the planting interval (gauge) in the direction orthogonal to the stitch direction is difficult to change because the interval between the needles is controlled.
【００１４】そこで、上記基布に対する上記パイルのゲ
ージを１２ｍｍ以上として、上記植設密度０．７〜１．
７本／ｃｍ２を基本的に満足させ、細かな調整はステッ
チ間隔で対応することが好ましい。すなわち、ゲージを
あらかじめ上記設定値に設定しておき、上述した植設密
度の範囲内でステッチを自由に変えることにより、充填
材の充填性および捕捉性を維持しつつ、各種用途に応じ
て要求される人工芝性状に対応することができる。Therefore, the gauge of the pile with respect to the base cloth is set to 12 mm or more, and the planting density is 0.7 to 1.
It is preferable that 7 lines / cm 2 be basically satisfied, and that fine adjustments be made at stitch intervals. That is, the gauge is set to the above set value in advance, and stitches are freely changed within the above-described range of the planting density. It can correspond to the artificial turf properties to be performed.
【００１５】ただし、ゲージが２８ｍｍ以上になると充
填材の捕捉性が低下するため、好ましくは２８ｍｍ以
下、より好ましくは２５ｍｍ以下に設定されることが好
ましい。However, if the gauge is 28 mm or more, the trapping property of the filler decreases, so that it is preferably set to 28 mm or less, more preferably 25 mm or less.
【００１６】なお、本発明において、ゲージとは、タフ
ト方向の植設間隔（ステッチ）に対して直交する方向の
植設間隔をいい、言い換えれば、１列に沿ってタフトさ
れたパイルを行方向に配列する配列間隔をいう。In the present invention, the gauge refers to a planting interval in a direction orthogonal to the planting interval (stitch) in the tuft direction. In other words, a pile that has been tufted along one row is placed in the row direction. Means the arrangement interval.
【００１７】本発明には、この充填材入り人工芝によっ
て構築された人工芝グラウンドも含まれる。すなわち、
野球競技場、サッカー場、テニスコートなど各種の人工
芝競技施設に適用することができる。The present invention also includes an artificial turf ground constructed with the artificial turf containing the filler. That is,
The present invention can be applied to various artificial turf sports facilities such as a baseball stadium, a soccer field, and a tennis court.
【００１８】[0018]
【発明の実施の形態】次に、本発明の具体的な実施形態
について図面を参照しながら説明する。図１を参照し
て、この充填材入り人工芝１は、基布２に所定間隔でパ
イル３がタフティングされた人工芝であって、そのパイ
ル３間には充填材４が充填されている。Next, specific embodiments of the present invention will be described with reference to the drawings. Referring to FIG. 1, this artificial turf 1 containing a filler is an artificial turf in which piles 3 are tufted on a base cloth 2 at predetermined intervals, and a filler 4 is filled between the piles 3. .
【００１９】基布２には、ポリプロピレン（ＰＰ）、ポ
リエチレン（ＰＥ）、ナイロン（ＮＹ）、ポリエチレン
テレフタレート（ＰＥＴ）などの合成樹脂製からなる織
布または不織布などが用いられ、この基布２の裏面側に
は、タフティングされたパイル３の抜け落ちを防止する
ため、ＳＢＲラテックスゴム、ウレタンなどからなるバ
ッキング材２１が所定の塗布量（好ましくは、乾燥状態
の重量で５００〜８００ｇ／ｍ２）で塗布されている。As the base fabric 2, a woven or non-woven fabric made of a synthetic resin such as polypropylene (PP), polyethylene (PE), nylon (NY), or polyethylene terephthalate (PET) is used. On the back side, a backing material 21 made of SBR latex rubber, urethane, or the like is applied in a predetermined amount (preferably 500 to 800 g / m 2 in a dry state) in order to prevent the tufted pile 3 from falling off. It is applied with.
【００２０】パイル３には、ポリプロピレン（ＰＰ）、
ポリエチレン（ＰＥ）、ナイロン（ＮＹ）などの合成樹
脂製のモノフィラメントヤーンやスプリットヤーン（総
デニール５５００〜１１０００ｄｔｅｘ）が用いられ、
基布表面から先端までのパイル長さＨが５０〜６０ｍｍ
以上とされた、いわゆるロングパイルである。The pile 3 includes polypropylene (PP),
Monofilament yarn or split yarn (total denier 5500 to 11000 dtex) made of synthetic resin such as polyethylene (PE) and nylon (NY) is used,
The pile length H from the base cloth surface to the tip is 50-60 mm
This is the so-called long pile described above.
【００２１】パイル３がモノフィラメントヤーンの場合
は、単糸デニールで４００〜８００ｄｔｅｘを数十本撚
り合わせ、合計太さが５５００〜１１０００ｄｔｅｘと
して基布にタフトすることが好ましい。この人工芝はカ
ットパイルなので、単糸それぞれがバラバラに拡がり高
いカバーリング性（粒状物捕捉性）が得られる。When the pile 3 is a monofilament yarn, it is preferable to twist several tens of 400 to 800 dtex with single yarn denier and to tuft the base fabric with a total thickness of 5500 to 11000 dtex. Since this artificial turf is a cut pile, each of the single yarns spreads separately, and high covering properties (granular substance capturing properties) can be obtained.
【００２２】一方、スプリットヤーンによれば、ヤーン
に所定間隔でスリットが設けられていることから、適度
なボリューム感が得られる。しかし、１枚のテープから
なるため、モノフィラメントヤーンに比べるとカバーリ
ング性が劣る。そこで、充填材の充填後に、その充填材
表面から突出した部分を開繊処理（引き裂く処理）を施
して、カバーリング性を向上させることが好ましい。On the other hand, according to the split yarn, since the yarn is provided with slits at predetermined intervals, a moderate volume feeling can be obtained. However, since it is composed of one tape, the covering property is inferior to monofilament yarn. Therefore, it is preferable that after the filler is filled, a portion protruding from the surface of the filler is subjected to a fiber opening treatment (tearing treatment) to improve the covering property.
【００２３】この実施形態において、パイル３は、フラ
ットテープヤーンに所定間隔でスリット３１が設けられ
たスプリットヤーンが用いられており、基布２に対する
植設密度（単位面積当たりの基布に対するパイルの植設
箇所の個数）が０．７〜１．７本／ｃｍ２（好ましくは
１．０〜１．７本／ｃｍ２、より好ましくは１．２〜
１．５本／ｃｍ２）の範囲を満足するように基布２に植
設されている。In this embodiment, as the pile 3, a split yarn in which slits 31 are provided at predetermined intervals in a flat tape yarn is used, and the planting density for the base cloth 2 (the pile density relative to the base cloth per unit area) is used. 0.7-1.7 pieces / cm 2 (preferably 1.0-1.7 pieces / cm 2 , more preferably 1.2-piece)
It is planted on the base cloth 2 so as to satisfy the range of 1.5 fibers / cm 2 ).
【００２４】すなわち、植設密度が０．７本／ｃｍ２よ
りも小さいと、充填材が飛散しやすく、またパイルの耐
摩耗性が低くなる。逆に、植設密度が１．７本／ｃｍ２
よりも高いと、充填材が充填しにくく、またスパイクが
引っ掛かりやすくなるためプレー性が損なわれてしま
う。That is, if the planting density is smaller than 0.7 fibers / cm 2 , the filler is liable to be scattered, and the wear resistance of the pile is lowered. Conversely, planted bristle density is 1.7 present / cm 2
If it is higher than this, the filler is difficult to fill, and the spikes are easily caught, so that the playability is impaired.
【００２５】パイル３をタフティングマシンを用いて基
布２に植設する場合、タフト方向の植設間隔（ステッ
チ）は、基布の送り速度を変えるなどして自由に変える
ことができるが、ステッチに対して直交する方向の植設
間隔（ゲージ）は、針の間隔を制御するため変化させに
くい。When the pile 3 is planted on the base fabric 2 using a tufting machine, the planting interval (stitch) in the tuft direction can be freely changed by changing the feed speed of the base fabric. The implantation interval (gauge) in the direction perpendicular to the stitch is difficult to change because the interval between the needles is controlled.
【００２６】そこで、この実施形態では、上記植設密度
０．７〜１．７本／ｃｍ２を基本的に満足させるため、
パイル３のゲージＧを１２ｍｍ以上の間隔として基布２
にタフトし、細かな調整はステッチを変えて行うように
している。これによれば、充填材の充填性および捕捉性
を維持しつつ、各種用途に応じて要求される人工芝性状
に対応することができる。Therefore, in this embodiment, in order to basically satisfy the planting density of 0.7 to 1.7 plants / cm 2 ,
The base fabric 2 with the gauge G of the pile 3 set to an interval of 12 mm or more
Tufting, and fine adjustments are made by changing the stitch. According to this, it is possible to cope with the artificial turf properties required for various applications while maintaining the filling property and the trapping property of the filler.
【００２７】ただし、ゲージが２８ｍｍ以上になると充
填材の捕捉性が低下するため、好ましくは２８ｍｍ以
下、より好ましくは２５ｍｍ以下に設定されていること
が好ましい。However, when the gauge is 28 mm or more, the trapping property of the filler decreases, so that it is preferably set to 28 mm or less, more preferably 25 mm or less.
【００２８】次に、上記の条件を満たして作製された人
工芝１を整地された下地上に敷設した後、パイル３間に
は充填材４が充填される。充填材４は、硬質粒状物４１
（下層）と弾性粒状物４２（上層）の２層構造（合計層
厚さ：３０〜５０ｍｍ）で充填されている。なお、この
２層構造の充填材４を１つの単位層として、この単位層
を複数層設けてもよい。Next, after the artificial turf 1 produced under the above conditions is laid on the ground, the filler 3 is filled between the piles 3. Filler 4 is hard granular material 41
(Lower layer) and a two-layer structure (total layer thickness: 30 to 50 mm) of the elastic granular material 42 (upper layer). Note that a plurality of unit layers may be provided with the filler 4 having the two-layer structure as one unit layer.
【００２９】また、硬質粒状物４１と弾性粒状物４２と
の界面は、実質的に硬質粒状物４１と弾性粒状物４２と
が混在した状態となっており、充填材４にはこのような
混在物も含まれる。さらに、用途によっては、硬質粒状
物４１ないしは弾性粒状物４２のいずれか１つからなる
単層構造であってもよい。The interface between the hard granular material 41 and the elastic granular material 42 is substantially in a state in which the hard granular material 41 and the elastic granular material 42 are mixed. Things are also included. Further, depending on the application, a single-layer structure composed of any one of the hard granular material 41 or the elastic granular material 42 may be used.
【００３０】硬質粒状物４１は、硅砂やガラス粉砕品な
どの無機系物質からなる粒状物（平均粒径０．２〜１．
５ｍｍ）が好ましく用いられ、弾性粒状物４２は、ゴム
チップ、ウレタンチップ、コルクチップなどの粒状物
（平均粒径０．２〜３．０ｍｍ）が好ましく用いられる
が、その角部分が面取りされている方がより好ましい。The hard granular material 41 is a granular material (average particle size of 0.2 to 1.g) made of an inorganic substance such as silica sand or glass pulverized product.
5 mm) is preferably used, and the elastic granular material 42 is preferably a granular material (average particle diameter: 0.2 to 3.0 mm) such as a rubber chip, urethane chip, or cork chip, and its corner is chamfered. Is more preferred.
【００３１】充填材４は、パイル先端までのパイル突出
長さｈが少なくとも１０ｍｍ以上、この実施形態では１
０〜２０ｍｍとなるようにパイル３間に充填されてい
る。すなわち、パイル突出長さｈが１０ｍｍ未満である
場合、後述する開繊作業後も充填材の飛散防止効果が小
さいため、充填材が飛散するおそれがある。The filler 4 has a pile protrusion length h up to the tip of the pile of at least 10 mm or more.
The space between the piles 3 is filled so as to be 0 to 20 mm. That is, when the pile projection length h is less than 10 mm, the filler may be scattered because the effect of preventing the filler from scattering is small even after the opening operation described later.
【００３２】この実施形態のようにパイル３にスプリッ
トヤーンを用いた場合、パイル３の先端部（突出部）
は、充填材４の飛散をより効果的に防止するために、細
かく引き裂かれた状態、いわゆる、開繊状態とされてい
ることが好ましい。When a split yarn is used for the pile 3 as in this embodiment, the tip (projection) of the pile 3
In order to more effectively prevent the filler 4 from scattering, it is preferable that the filler 4 is in a finely torn state, that is, a so-called open state.
【００３３】すなわち、パイル３の突出部は、図１の部
分拡大図に示すように開繊後のパイル１本当たりの単位
幅ｂが、パイルの全幅ａ（未開繊部分の幅）の７％以
上、かつ、３ｍｍ以下になるように開繊されていること
が好ましい。That is, as shown in the partially enlarged view of FIG. 1, the projecting portion of the pile 3 is such that the unit width b per pile after opening is 7% of the total width a of the pile (the width of the unspread portion). It is preferable that the fiber is opened so as to be 3 mm or less.
【００３４】これによれば、突出部を開繊することで、
パイル３の表面積が増え、より一層の飛散防止効果が得
られる。なお、開繊の度合いが全幅の７％未満である場
合は、先端のマイクロフィブリル化が促進され、人工芝
の耐久性が著しく悪くなる。また、３ｍｍよりも大きい
場合は、粒状物の飛散防止効果が小さい。According to this, by opening the protruding portion,
The surface area of the pile 3 is increased, and a further scattering prevention effect can be obtained. If the degree of fiber opening is less than 7% of the entire width, microfibrillation at the tip is promoted, and the durability of the artificial turf is significantly deteriorated. On the other hand, if it is larger than 3 mm, the effect of preventing the particulate matter from scattering is small.
【００３５】上述した開繊作業は、充填材４の捕捉性を
より高くするのに効果的である。なお、パイル３の開繊
には、所定の植設密度にてブラシが植設された金ブラシ
などが用いられるが、それ以外のものも使用条件に応じ
て適宜選択可能である。The above-described fiber opening operation is effective for further enhancing the ability to capture the filler 4. In order to open the pile 3, a gold brush or the like in which a brush is planted at a predetermined planting density is used, but other brushes can be appropriately selected according to use conditions.
【００３６】また、上述した開繊作業に加えて、振動ロ
ーラなどによってパイル先端を充填材４の表面に沿って
強制的に折り曲げて、癖付け加工してもよい。これによ
れば、パイル先端が充填材４の表面を覆うようになり、
より一層充填材４の飛散防止効果が生まれる。なお、開
繊作業を行わずに、癖付け加工のみを行ってもよい。Further, in addition to the above-described opening operation, the tip of the pile may be forcibly bent along the surface of the filler 4 by a vibrating roller or the like, and may be processed. According to this, the pile tip comes to cover the surface of the filler 4,
The effect of preventing the filler 4 from scattering is further enhanced. In addition, only the knitting process may be performed without performing the fiber opening operation.
【００３７】本発明の充填材入り人工芝１は、野球競技
場、サッカー場、テニスコートなどの各種人工芝グラウ
ンドに適用することができる。また、他の人工芝施設で
あっても、本発明によって得られる人工芝性状が適用可
能なものであれば任意に選択して施工してもよい。The artificial turf 1 containing a filler of the present invention can be applied to various artificial turf grounds such as a baseball stadium, a soccer field, and a tennis court. Further, other artificial turf facilities may be arbitrarily selected and constructed as long as the artificial turf properties obtained by the present invention can be applied.
【００３８】[0038]
【実施例】次に、本発明のより具体的な実施例につい
て、比較例とともに比較検討する。まず、下記の方法に
て充填材入り人工芝を作製した。Next, more specific examples of the present invention will be compared with comparative examples. First, an artificial turf containing a filler was produced by the following method.
【００３９】（充填材入り人工芝の作製） ：人工芝の作製 ポリプロピレン製スプリットヤーン７８００ｄｔｅｘ
（幅１２ｍｍ）をポリプロピレン製平織り布からなる基
布にパイル長５０ｍｍでタフト後、裏面からＳＢＲラテ
ックスゴムを一様に塗布して抜け止め防止加工を施し
て、人工芝を製造した。なお、各例とも植設密度または
ゲージ間隔は異なるが、用いる材料およびパイル長は同
じとした。 ：硬質粒状物の充填 で作製された人工芝の３ｍ角をあらかじめ整地された
下地上に敷設して、砂（硬質粒状物）を１５ｍｍ厚にな
るように充填した。砂は粒径が０．２〜０．６ｍｍのも
のが全体の８０％以上を占める天然珪砂を使用した。 ：弾性粒状物の充填 の人工芝の上にゴムチップ（弾性粒状物）を１５ｍｍ
厚になるように充填した。ゴムチップは粒径が０．４〜
１．５ｍｍのものが全体の８０％以上を占めるタイヤ粉
砕品を使用した。上記〜の方法にて作製された人工
芝を、以下の各種評価試験に供した。(Preparation of artificial turf containing filler): Preparation of artificial turf Polypropylene split yarn 7800 dtex
(12 mm in width) was tufted onto a base cloth made of a plain woven cloth made of polypropylene with a pile length of 50 mm, and then SBR latex rubber was uniformly applied from the back surface to prevent slippage, thereby producing an artificial turf. Although the planting density or the gauge interval differs in each example, the materials used and the pile length were the same. : Filling of Hard Granular Material A 3 m square of the artificial turf produced in the above was laid on a pre-grounded ground, and sand (hard granular material) was filled to a thickness of 15 mm. As the sand, natural silica sand having a particle size of 0.2 to 0.6 mm occupying 80% or more of the whole was used. : Filling of elastic granules 15mm rubber chip (elastic granules) on artificial grass
It was filled to be thick. Rubber chips have a particle size of 0.4 ~
A tire crushed product having a size of 1.5 mm occupying 80% or more of the whole was used. The artificial turf produced by the above-mentioned methods was subjected to the following various evaluation tests.
【００４０】（充填材の充填性を確認）まず、充填材の
充填性を確認した。確認方法は、各人工芝について充填
材がほぼ平坦に充填されるまでの所要時間を計測し、そ
の計測時間を充填材の充填性の評価基準とした。(Confirmation of Fillability of Filler) First, the fillability of the filler was confirmed. As a confirmation method, the time required until the filler was filled almost flatly for each artificial turf was measured, and the measured time was used as an evaluation criterion for the filling property of the filler.
【００４１】（スパイクの非拘束性の評価）次に、各充
填材入り人工芝上でのスパイクの非拘束性について評価
した。評価方法は、図２に示すトルク試験機５を用い
た。このトルク試験機５は、おもり５２によって所定の
負荷荷重が掛けられた円盤状のベースプレート５１の下
面側（対人工芝面側）に市販のスパイクピン５１１を取
り付けたものからなり、このベースプレート５１を人工
芝面上に載置して、一端がベースプレート５１に連結さ
れたシャフト５３の他端にトルクメーター５４を取り付
けて、このトルクメーター５４を介してベースプレート
５１を回転したときにシャフト５３に掛かる軸トルクを
測定した。(Evaluation of Non-Restriction of Spikes) Next, the non-restriction of spikes on artificial turf containing each filler was evaluated. The evaluation method used the torque tester 5 shown in FIG. This torque tester 5 is formed by attaching a commercially available spike pin 511 to the lower surface side (toward the artificial grass surface side) of a disc-shaped base plate 51 on which a predetermined load is applied by a weight 52. A torque meter 54 is attached to the other end of a shaft 53 having one end connected to the base plate 51 and placed on the artificial turf surface, and an axis applied to the shaft 53 when the base plate 51 is rotated via the torque meter 54. The torque was measured.
【００４２】（粒状物の飛散防止性およびパイルの耐摩
耗性の確認）さらに、敷設した状態で３ヶ月間自由に歩
行して貰い、粒状物の飛散防止性およびパイルの摩耗状
態（耐摩耗性）を目視で確認した。以下に各評価結果を
示す。(Confirmation of the scattering prevention of the particulate matter and the wear resistance of the pile) Furthermore, the user was allowed to walk freely for three months in the laid state, and the scattering prevention of the particulate matter and the wear state of the pile (wear resistance) ) Was visually confirmed. The evaluation results are shown below.
【００４３】《実施例１》 （パイル仕様）植設密度：０．７本／ｃｍ２、ゲージ：
１３ｍｍ （評価結果） ・充填材の充填時間：２５分 ・トルク試験：２０Ｎ・ｍ ・飛散防止性：良好（○） ・耐摩耗性：少し摩耗（○〜△）<< Example 1 >> (Pile specification) Planting density: 0.7 lines / cm 2 , gauge:
13mm (Evaluation result) ・ Filling time of filler: 25 minutes ・ Torque test: 20N ・ m ・ Shatterproofing property: good (○) ・ Abrasion resistance: slight wear (○ ～ △)
【００４４】《実施例２》 （パイル仕様）植設密度：１．７本／ｃｍ２、ゲージ：
１３ｍｍ （評価結果） ・充填材の充填時間：３０分 ・トルク試験：２５Ｎ・ｍ ・飛散防止性：良好（○） ・耐摩耗性：著しい摩耗見られず（○）Example 2 (Pile specification) Planting density: 1.7 lines / cm 2 , gauge:
13mm (Evaluation result) ・ Filling time of filler: 30 minutes ・ Torque test: 25N ・ m ・ Shatterproofing property: good (○) ・ Abrasion resistance: no remarkable wear was observed (○)
【００４５】《実施例３》 （パイル仕様）植設密度：１．７本／ｃｍ２、ゲージ：
１０ｍｍ （評価結果） ・充填材の充填時間：３３分 ・トルク試験：２５Ｎ・ｍ ・飛散防止性：良好（○）・耐摩耗性：著しい摩耗見ら
れず（○）Example 3 (Pile specification) Planting density: 1.7 lines / cm 2 , gauge:
10 mm (Evaluation result)-Filling time of filler: 33 minutes-Torque test: 25 Nm-Anti-scattering property: good (O)-Abrasion resistance: No noticeable abrasion (O)
【００４６】〈比較例１〉 （パイル仕様）植設密度：０．５本／ｃｍ２、ゲージ：
１３ｍｍ （評価結果） ・充填材の充填時間：１７分 ・トルク試験：２０Ｎ・ｍ ・飛散防止性：飛散が激しい（×） ・耐摩耗性：激しく摩耗（×）<Comparative Example 1> (Pile specification) Planting density: 0.5 pieces / cm 2 , gauge:
13mm (Evaluation result) ・ Filling time of filler: 17 minutes ・ Torque test: 20N ・ m ・ Splash prevention: Severe scattering (×) ・ Abrasion resistance: Severe wear (×)
【００４７】〈比較例２〉 （パイル仕様）植設密度：２．１本／ｃｍ２、ゲージ：
１３ｍｍ （評価結果） ・充填材の充填時間：３９分 ・トルク試験：３５Ｎ・ｍ ・飛散防止性：良好（○） ・耐摩耗性：著しい摩耗見られず（○）Comparative Example 2 (Pile specification) Planting density: 2.1 / cm 2 , Gauge:
13 mm (Evaluation result)-Filling time of filler: 39 minutes-Torque test: 35 Nm-Anti-scattering property: good (o)-Abrasion resistance: no remarkable wear was observed (o)
【００４８】参考までに、上記実施例１〜３と比較例１
〜２の結果のまとめを表１に示す。For reference, the above Examples 1 to 3 and Comparative Example 1
Table 1 shows a summary of the results of Nos. 1 to 2.
【００４９】[0049]
【表１】 [Table 1]
【００５０】実施例の結果から、以下のような知見を得
た。 ・実施例３は、実施例２と比較すると、ゲージ間隔が狭
いため充填材の充填に若干時間を要する。 ・比較例１は、植設密度が低すぎるため、充填材の飛散
が激しく、パイルの耐摩耗性も低い。 ・比較例２は、植設密度が高すぎるため、充填材の充填
材に時間を要し、またスパイクが刺さったときの抵抗も
大きい。From the results of the examples, the following findings were obtained. -Example 3 requires a little time to fill the filler because the gauge interval is narrower than Example 2. In Comparative Example 1, since the planting density was too low, the filler was scattered sharply and the abrasion resistance of the pile was low. In Comparative Example 2, since the planting density is too high, it takes time for the filler to be filled, and the resistance when the spike is stabbed is large.
【００５１】[0051]
【発明の効果】以上説明したように、本発明によれば、
基布にパイルを植設した人工芝のパイル間に弾性粒状物
を含む充填材を充填し、その充填材の表面からパイル先
端を１０ｍｍ以上突出させてなる充填材入り人工芝にお
いて、このパイルの基布に対する単位面積当たりの植設
密度が０．７〜１．７本／ｃｍ２としたことことによ
り、充填材の充填作業性を損なうことなく、充填材の飛
散を効果的に防止でき、耐摩耗性などの人工芝性状を向
上させることができる。As described above, according to the present invention,
An artificial turf with a filler, in which a filler containing elastic particles is filled between the piles of the artificial turf in which the pile is planted on the base cloth and the tip of the pile protrudes 10 mm or more from the surface of the filler, By setting the planting density per unit area with respect to the base cloth to 0.7 to 1.7 lines / cm 2 , the scattering of the filler can be effectively prevented without impairing the workability of filling the filler, The artificial turf properties such as abrasion resistance can be improved.
【００５２】さらに、基布に対するパイルのゲージを１
２ｍｍ以上としたことにより、タフティングマシンを用
いて製造された人工芝であっても、パイル間に充填材を
充填しやすくなる。Further, the gauge of the pile with respect to the base cloth is set to 1
When the thickness is 2 mm or more, even if the artificial turf is manufactured using a tufting machine, the filler is easily filled between the piles.
【図１】本発明の実施形態に係る充填材入り人工芝の斜
視図。FIG. 1 is a perspective view of an artificial turf containing a filler according to an embodiment of the present invention.
【図２】トルク試験機の構造を説明するための説明図。FIG. 2 is an explanatory diagram for explaining the structure of a torque tester.
１ 充填材入り人工芝 ２ 基布 ２１ バッキング材 ３ パイル ３１ スリット ４ 充填材 ４１ 硬質粒状物 ４２ 弾性粒状物 ５ トルク試験機 Ｇ ゲージ REFERENCE SIGNS LIST 1 artificial turf containing filler 2 base cloth 21 backing material 3 pile 31 slit 4 filler 41 hard granular material 42 elastic granular material 5 torque tester G gauge
Claims (3)
間に弾性粒状物を含む充填材を充填し、その充填材の表
面からパイル先端を１０ｍｍ以上突出させてなる充填材
入り人工芝において、 上記パイルの上記基布に対する単位面積当たりの植設密
度が０．７〜１．７本／ｃｍ２であることを特徴とする
充填材入り人工芝。1. An artificial turf containing a filler, wherein a filler containing elastic particles is filled between the piles of the artificial turf in which the pile is planted on a base cloth, and a tip of the pile projects from the surface of the filler by 10 mm or more. in, a filled artificial turf planted bristle density per unit area with respect to the base fabric of the pile is characterized in that it is a 0.7 to 1.7 present / cm 2.
が、１２ｍｍ以上である請求項１に記載の充填材入り人
工芝。2. The artificial turf containing a filler according to claim 1, wherein a gauge of the pile with respect to the base cloth is 12 mm or more.
芝によって構築された人工芝グラウンド。3. An artificial turf ground constructed by the artificial turf containing a filler according to claim 1 or 2.