JP2002165902A - Golf club head - Google Patents

Golf club head

Info

Publication number
JP2002165902A
JP2002165902A JP2000370379A JP2000370379A JP2002165902A JP 2002165902 A JP2002165902 A JP 2002165902A JP 2000370379 A JP2000370379 A JP 2000370379A JP 2000370379 A JP2000370379 A JP 2000370379A JP 2002165902 A JP2002165902 A JP 2002165902A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
head
portion
crown plate
crown
specific gravity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2000370379A
Other languages
Japanese (ja)
Other versions
JP4451982B2 (en )
Inventor
Masanori Yabu
眞徳 藪
Original Assignee
Sumitomo Rubber Ind Ltd
住友ゴム工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To increase the moment of inertia while lowering the center of gravity. SOLUTION: This golf club head 1 is hollow in it and comprises a crown plate 7 defining a main part of a crown part 3 of the upper surface of the head and a head body 3 having the crown plate 7. The crown plate 7 is made of low specific gravity metal material Ml with 5.0 or lower of specific gravity, and the head body 9 is made of high specific gravity metal material M2 with 7.0 or higher of specific gravity. The crown plate 7 is brazed with the head body 9.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、低重心化を図りつつ慣性モーメントを増大しうるゴルフクラブヘッドに関する。 The present invention relates to relates to a golf club head which may increase the moment of inertia while achieving a low center of gravity.

【0002】 [0002]

【従来の技術及び発明が解決しようとする課題】例えば内部に中空部を形成した金属製のウッド型ゴルフクラブヘッドにあっては、近年ではチタンないしチタン合金などの高強度かつ低比重の材料が好適に用いられている。 In the BACKGROUND OF THE INVENTION Invention is to Solve] For example a metal wood type golf club head to form a hollow portion therein, a high strength and a low specific gravity material such as In recent years, titanium or titanium alloys It is suitably used.
このようなゴルフクラブヘッドは、柿の木材を用いた従来のヘッドに比べ、ヘッド体積を大型化できる。 Such golf club heads, compared with the conventional head using a persimmon tree material, can increase the size of the head volume. ヘッド体積の大型化は、慣性モーメント(本明細書で「慣性モーメント」というときは、特に明記しない場合にはヘッドの重心を通る垂直軸回りの左右の慣性モーメントを指すものとする。)の増大をもたらし、スイートエリアの増大やミスショット時のヘッドのぶれを抑制するなど打球の方向安定性を向上しうる。 Enlargement of the volume of the head, the moment of inertia (when referred to herein as "inertia" is, when otherwise indicated shall refer to the left and right moment of inertia about a vertical axis passing through the center of gravity of the head.) Increased the lead can improve the directional stability of the hit ball, such as to suppress the vibration of the head during an increase or missed shot of sweet area.

【0003】また近年では、図7に示すように、ヘッドaのソール部bに銅合金ないしタングステンといった比重の大きな金属材料からなる錘部材cを固着し、ヘッドaの重心gを低く設計することが行われている(特開2 [0003] In recent years, as shown in FIG. 7, the fixed weight member c comprising a large metal material having a specific gravity of such a copper alloy or tungsten sole portion b of the head a, designing low center of gravity g of the head a is being carried out (JP 2
000−116825号参照)。 See No. 000-116825). このように、ヘッドを低重心化すると、打球の打ち出し角度を大としかつバックスピン量を適度に減少させることにより、飛距離を増大させ得る。 Thus, when a low center of gravity of the head, by reducing the launch angle of the ball large Toshikatsu backspin moderately, may increase the flight distance.

【0004】他方、ヘッドの慣性モーメントを増大させるためには、重心gから離れたヘッドの周囲、より具体的にはサイド部dやソール部bの周囲により多くの重量を配分することが効果的となる。 [0004] On the other hand, in order to increase the moment of inertia of the head, around the head away from the center of gravity g, and more specifically effectively be to allocate more weight on the surrounding side portion d and the sole portion b to become. しかしながら、ソール部bに錘部材cを固着した上記ヘッドaでは、低重心化を達成しうるものの、ソール部bを局部的に重くしているため、ヘッドaの周囲の重量配分効果が相対的に薄れてしまい前記慣性モーメントが小さくなるという欠点がある。 However, in the head a was fixed to the weight member c to the sole portion b, but can achieve lower center of gravity, because of the locally heavier sole portion b, the relative weight distribution effect around the head a is there is a drawback that it is the moment of inertia would fading to become smaller.

【0005】本発明は、以上のような問題点に鑑み案出なされたもので、ヘッド上面のクラウン部の主要部をなすクラウン板と、このクラウン板が配されるヘッド本体部とからなり、かつ前記クラウン板を、比重が5.0以下の低比重金属材料から形成するとともに、ヘッド本体部を比重が7.0以上の高比重金属材料を用いて形成しこれらをロウ付けにより接合することを基本として低重心化を図りつつも慣性モーメントの低下を防止して打球の方向安定性を向上できしかも耐久性にも優れるゴルフクラブヘッドを提供することを目的としている。 [0005] The present invention has been made devised in view of the above problems, consists of a crown plate which forms the main portion of the crown portion of the head top surface, a head main body portion which the crown plate is disposed, and the crown plate, with a specific gravity to form a 5.0 or lower specific gravity metal material, the specific gravity of the head body portion are joined by brazing them formed using 7.0 or more high density metal material and its object is to provide a low while achieving center of gravity can also improve the directional stability of the ball and prevent a reduction in moment of inertia Moreover golf club head which is excellent in durability as basic.

【0006】 [0006]

【課題を解決するための手段】本発明のうち請求項1記載の発明は、内部を中空としたゴルフクラブヘッドであって、ヘッド上面のクラウン部の主要部をなすクラウン板と、このクラウン板が配されるヘッド本体部とからなり、前記クラウン板は、比重が5.0以下の低比重金属材料から形成され、かつ前記ヘッド本体部は比重が7. According to one aspect of the SUMMARY OF THE INVENTION The present invention is a golf club head having an interior hollow, and a crown plate which forms the main portion of the crown portion of the head top surface, the crown plate made from the head main body portion and which is disposed, said crown plate has a specific gravity 5.0 is formed from the following low specific gravity metal material, and the head main body specific gravity 7.
0以上の高比重金属材料を用いて形成されるとともに、 Together are formed by using zero or more of a metal with a high specific gravity material,
前記クラウン板とヘッド本体部とをロウ付けにより接合したことを特徴としている。 It is characterized in that joined by brazing with said crown plate and the head body portion.

【0007】また請求項2記載の発明は、前記クラウン板の重量が、前記ヘッド本体部の重量の10〜30%であることを特徴とする請求項1記載のゴルフクラブヘッドである。 [0007] According to a second aspect of the invention, the weight of the crown plate, a golf club head of claim 1, wherein 10 to 30% of the weight of the head body portion.

【0008】また請求項3記載の発明は、前記ヘッド本体部は、ボールを打撃するフェース部と、該フェース部の下縁に連なりヘッド底部をなすソール部と、前記ソール部の周囲から立ち上がりかつ前記フェース部のトウ側からバックフェースを通り該フェース部のヒール側にのびるサイド部と、シャフトを装着しうるシャフト差込部とを含んでなる請求項1又は2記載のゴルフクラブヘッドである。 [0008] According to a third aspect of the invention, the head main body portion, a face portion for hitting a ball, and a sole portion that forms a head bottom continuous to the lower edge of the face portion, the rising and from the periphery of the sole portion a side portion extending to the heel side of the street the face portion back face from the toe side of the face portion, a claim 1 or 2 golf club head according comprising a shaft insertion portion capable of mounting the shaft.

【0009】また請求項4記載の発明は、前記クラウン板は、チタン又はチタン合金からなり、かつ前記ヘッド本体部はステンレス鋼を含むことを特徴とする請求項1 [0009] The invention of claim 4, wherein, the crown plate, according to claim 1 made of titanium or a titanium alloy, and the head main body portion, characterized in that it comprises a stainless steel
〜3のいずれかに記載のゴルフクラブヘッドである。 Is a golf club head according to any one to 3 of.

【0010】 [0010]

【発明の実施の形態】以下本発明の実施の一形態を図面に基づき説明する。 DETAILED DESCRIPTION OF THE INVENTION One embodiment of the following invention will be described with reference to the drawings. 図1は本発明の実施形態に係るゴルフクラブヘッドの斜視図、図2は、その分解斜視図を例示している。 Figure 1 is a perspective view of a golf club head according to an embodiment of the present invention, FIG. 2 illustrates a exploded perspective view thereof. 図1において、ゴルフクラブヘッド(以下、単に「ヘッド」ということがある。)1は、ボールを打撃するフェース面Fを表面に具えたフェース部2 In Figure 1, a golf club head (hereinafter, simply referred to as "head".) 1, face portion 2 which includes a face surface F for striking a ball on the surface
と、該フェース部2の上縁2aに連なりヘッド上面をなすクラウン部3と、前記フェース部2の下縁2bに連なりヘッド底面をなすソール部4と、このソール部4の周囲から立ち上がりかつ前記フェース部2のトウt側からバックフェースを通り該フェース部2のヒールe側にのびるサイド部5と、シャフトを装着しうるシャフト差込部6とを具えたものが例示される。 When, a crown portion 3 forming a head top surface contiguous with the upper edge 2a of the face portion 2, the a sole portion 4 forming a head bottom surface continuous with the lower edge 2b of the face portion 2, the rising and the from the periphery of the sole portion 4 a side portion 5 extending back face to the heel e side of the street the face portion 2 from the toe t side of the face portion 2, that comprises a shaft insertion portion 6 which can attach the shaft is illustrated. また本例のヘッド1 The head 1 of the present example
は、金属材料からなりかつ内部に中空部iを設けたウッド型のものが例示される。 It is of a wood type provided with a hollow portion i in the interior and a metal material is exemplified.

【0011】図2に示すように、ヘッド1は、前記クラウン部3の主要部をなすクラウン板7と、このクラウン板7が配されるヘッド本体部9とから構成される。 [0011] As shown in FIG. 2, the head 1 includes a crown plate 7 forming a main portion of the crown portion 3 and a head main body portion 9 for this crown plate 7 is disposed. 前記クラウン部3は、本例では前記フェース部2の上縁2a The crown portion 3, the upper edge 2a of the face portion 2 in this embodiment
と、前記サイド部5の上縁5aとがなす輪郭線で囲まれるヘッドの上面の領域をなしかつ前記シャフト差込部6 If, without the area of ​​the upper surface of the head surrounded by the contour line formed between the upper edge 5a of the side portion 5 and the shaft insertion portion 6
を実質的に除いた部分で構成されている。 It is composed of a substantially excluding the portion on which the. なおシャフト差込部6と前記クラウン部3との間には、図4に示すように、ヘッド内方に向かって凹む凹み面で形成される滑らかな継ぎ面11が形成されている。 Note Between the crown portion 3 and the shaft inserting portion 6, as shown in FIG. 4, a smooth joint surface 11 formed by the recessed surface recessed toward the head side is formed.

【0012】前記クラウン板7は、本例では前記クラウン部3の前記輪郭線から小距離Lを内方に隔てた形状で形成された1枚の板状をなすものが例示される。 [0012] The crown plate 7 is in this example intended to form a single plate-shaped formed in a shape at a small distance L inward from the contour of the crown portion 3 is exemplified. 前記小距離Lは特に限定はされないが、例えば2〜10mm程度、好ましくは2〜5mm程度とするのが望ましく、これにより、クラウン板7は、本例では実質的に前記クラウン部3の全域を構成しうる。 Wherein at small distance L is not particularly limited, for example 2~10mm, preferably about desirably set to about 2 to 5 mm, thereby, the crown plate 7, in this example the entire area of ​​substantially the crown portion 3 It may be configured.

【0013】また前記ヘッド本体部9は、本例では前記フェース部2、ソール部4、サイド部5及びシャフト差込部6と、小巾をなすクラウン周縁部3eを含んで構成されている。 [0013] The head main body portion 9, the face portion 2 in the present example, the sole portion 4, a side portion 5 and the shaft insertion portion 6 is configured to include a crown periphery 3e forming a small width. このようなヘッド本体部9は、好ましくは例えばロストワックス精密鋳造などにより、各部を一体的に形成するのが望ましい他、予め2以上に分割して形成した各パーツを溶接により一体化して形成することもできる。 Such head body portion 9, preferably by, for example, Precision Casting, other desirable to integrally form the respective parts, is integrally formed by welding the parts formed by dividing beforehand 2 or more it is also possible. このようにヘッド本体部9は、種々の方法を用いて製造することができ、その方法は特に限定されるものではない。 The head body portion 9 as may be produced using a variety of methods, the method is not limited in particular. また本実施形態においては、前記フェース部2、ソール部4、サイド部5及びシャフト差込部6 In this embodiment also, the face portion 2, a sole portion 4, the side portions 5 and the shaft insertion portion 6
は、同じ金属材料で形成されたものを例示している。 Illustrates those formed with the same metal material.

【0014】前記クラウン周縁部3eは、図2、図4〜 [0014] The crown periphery. 3e, 2, 4 to
6に示すように、前記フェース板7をこのクラウン部周縁部と略面一に保持して下方から支える受け部12が形成されている。 As shown in 6, the receiving portion 12 for supporting from below to hold the face plate 7 in the crown portion periphery substantially flush is formed. 本実施形態の受け部12は、前記クラウン板7の全周縁に亘って形成されたものが示されている。 Receiving portion of the embodiment 12, that is formed along the entire periphery of the crown plate 7 is shown. またこの受け部12の巾A(図5に示す。)は、特に限定はされないが、例えば2〜7mm、より好ましくは3〜5mmとすることが望ましい。 The (shown in Figure 5.) Width A of the receiving portion 12 is not particularly limited, for example 2 to 7 mm, more preferably it is desirable that the 3 to 5 mm. このような受け部12 Such a receiving portion 12
は、クラウン板7のヘッド本体部9への取り付けに際して、クラウン板7の位置決めを容易として精度良く取り付けし得るほか、後述するロウ付けの接合強度を高めるのに役立つ。 , Upon attachment to the head main body portion 9 of the crown plate 7, in addition to be attached accurately positioning the crown plate 7 as easy, it helps to increase the bonding strength of the brazing, which will be described later.

【0015】また本発明では、前記クラウン板7は、比重が5.0以下の低比重金属材料M1から形成される一方、前記ヘッド本体部9は比重が7.0以上の高比重金属材料M2を用いて形成される。 [0015] In the present invention, the crown plate 7, while the specific gravity is formed from a 5.0 or lower specific gravity metal material M1, the head main body portion 9 is high density metal material specific gravity of 7.0 or more M2 It is formed using. このように、クラウン部3の主要部をなすクラウン板7に低比重金属材料M1 Thus, low specific gravity metal crown plate 7 forming the main portion of the crown portion 3 material M1
を用いることによって、ヘッド1の上部側の重量を軽減することができ、その結果、ヘッド1の重心Gをより低く設定することが可能となる。 By using, it is possible to reduce the weight of the upper side of the head 1, as a result, it is possible to set lower the center of gravity G of the head 1. また、クラウン板7が配される前記ヘッド本体部9に高比重金属材料M2を用いることにより、ヘッド1のさらなる低重心化が可能となるほか、ソール部4だけでなくサイド部5といったヘッド1の周囲部分にもより多くの重量を配分しうる結果、 Further, by using a high density metal material M2 to the head main body portion 9 of the crown plate 7 is arranged, in addition to further lower the center of gravity of the head 1 can be, head such side portion 5 not only the sole portion 4 1 the results of the can allocate more weight to the peripheral portion,
ヘッド1の慣性モーメントも増大しうる。 The moment of inertia of the head 1 may also be increased. このように、 in this way,
本発明のヘッド1では、ソール部4だけを相対的に重くするのではなく、クラウン部3以外をバランス良く重くしているため、低重心化と慣性モーメントの増大をより効果的に両立しうる。 In the head 1 of the present invention, rather than heavier relative only sole portion 4, since the heavy good balance other than the crown portion 3, may both increase in low center of gravity and moment of inertia more effectively .

【0016】なお本実施形態では、ソール部4に塊状の錘部材などを複合化してはいないが、ヘッド1の慣性モーメントの悪化を招かない範囲でこのような錘部材を取り付けることは可能である。 [0016] In the present embodiment, although not complexed and weight member of the bulk in the sole portion 4, it is possible to mount such a weight member to the extent that does not cause the deterioration of the moment of inertia of the head 1 .

【0017】ここで前記クラウン板7を構成する金属材料の比重が5.0を超えると、ヘッド1の上部側をなすクラウン部3の重量が相対的に増す傾向があり、ヘッド本体部9の重量だけでは低重心化を達成し難くなる。 [0017] Here, the specific gravity of the metal material constituting the crown plate 7 is more than 5.0, there is a tendency for the weight of the crown portion 3 constituting the upper side of the head 1 increases relatively, the head main body portion 9 only the weight is difficult to achieve a low center of gravity. このような観点より、前記クラウン板7の低比重金属材料M1の比重は、小さいほど望ましく、より好ましくは4.5以下とすることが望ましい。 From this point of view, the specific gravity of the low specific gravity metal material M1 of the crown plate 7 is smaller preferably, and more preferably it is desirable to be 4.5 or less.

【0018】このようなクラウン板7を形成する低比重金属材料M1としては、特に限定されるものではないが、例えば純チタン(比重約4.5)、チタン合金(比重約4.4〜4.7)、マグネシウム合金(比重約1. Examples of the low specific gravity metal material M1 forming such crown plate 7, is not particularly limited, for example, pure titanium (specific gravity of about 4.5), titanium alloy (specific gravity of about 4.4 to 4 .7), magnesium alloy (specific gravity of about 1.
8〜2.3)、ジュラルミン(比重約2.8)又はアルミニウム−リチウム(Al−Li)合金(比重約2. 8 to 2.3), duralumin (specific gravity about 2.8) or aluminum - lithium (Al-Li) alloys (specific gravity of about 2.
6)、等を挙ることができる。 6), or the like can be raised to. 中でもクラウン板7には、比強度の確保と低比重の観点よりチタン合金あるいはアルミニウム合金(ジュラルミン)などの材料を用いることが望ましく、本実施形態ではチタン合金(Ti− The inter alia crown plate 7, it is desirable to use a material, such as specific strength of securing the low density aspect of titanium alloy or aluminum alloy (duralumin), the present embodiment the titanium alloy (Ti-
6Al−4V)を用いたものを例示している。 It illustrates 6Al-4V) that was used.

【0019】またクラウン板7の厚さは特に限定はされないが、好ましくは軽量化と強度との兼ね合いより、例えば0.7〜1.2mm、より好ましくは0.9〜1.1 [0019] The thickness of the crown plate 7 is not particularly limited, preferably from balance with weight reduction and strength, for example 0.7 to 1.2 mm, more preferably 0.9 to 1.1
mmとすることが望ましい。 It is desirable that the mm. このようなクラウン板7は、 Such a crown plate 7,
鍛造、鋳造、圧延など種々の加工法にて形成することができるのは言うまでもない。 Forging, casting, is of course possible to form in various processing methods such as rolling.

【0020】またクラウン板7に、繊維強化樹脂といった低比重の複合材を用いることも考えられる。 Further to the crown plate 7, it is considered to use a composite material of low specific gravity such as fiber-reinforced resin. しかしながら、このような材料をクラウン板7に用いると、一般的なヘッドとは打球音が極端に異なったり、またクラウン部3の剛性が不足するためにその厚さを増すなどの工夫が必要となりヘッドの反発性能が著しく低下する不具合があるため採用し難い。 However, the use of such materials to the crown plate 7, a typical head and requires a contrivance such as or different extremes hitting sound, also increase its thickness to the rigidity of the crown portion 3 is insufficient difficult to employ because the resilience performance of the head there is a problem to be significantly reduced.

【0021】逆に前記ヘッド本体部9を構成する金属材料の比重が7.0未満であると、ヘッド1の周囲(サイド部5)ないしヘッドの底部(ソール部4)により多くの重量を配分することが困難となり、ヘッド1の低重心化と慣性モーメントの増大を実現することが困難になる。 [0021] If the specific gravity of the metal material constituting the head body portion 9 on the contrary is less than 7.0, allocating more weight by the surrounding of the head 1 (the side part 5) to the bottom of the head (the sole portion 4) it becomes difficult to, it becomes difficult to achieve an increase in the low center of gravity and moment of inertia of the head 1.

【0022】このようなヘッド本体部9を形成する高比重金属材料M2としては、例えばSUS630(比重7.8)、CUSTOM450(米国カーペンター社製、比重7.8)などのステンレス鋼(比重約7.8〜 Examples of the high specific gravity metal material M2 for forming such head body portion 9, for example, SUS630 (specific gravity 7.8), CUSTOM450 (US Carpenter Co., specific gravity 7.8) Stainless steel such as (specific gravity of about 7 .8~
8.0)、ニッケル−銅合金(比重約8.9)、タングステン合金(比重約12〜15)又はタングステン(比重約18)、白金(比重約21.3)、銅合金(比重約8〜13)、マレージング系合金(比重7.0〜8. 8.0), a nickel - copper alloys (specific gravity of about 8.9), a tungsten alloy (specific gravity of about 12 to 15) or tungsten (specific gravity about 18), platinum (specific gravity of about 21.3), a copper alloy (specific gravity of about 8 13), maraging alloy (specific gravity from 7.0 to 8.
2)等を挙ることができる。 2) and the like can be raised to. 中でもヘッド本体部9には、強度、加工容易性、経済性などの観点より、SUS Above all in the head main body portion 9, the strength, ease of processing, from the viewpoint of economic efficiency, SUS
630、CUSTOM450などの材料を用いることが望ましく、本例ではSUS630を用いたものを例示している。 630, it is desirable to use a material such as CUSTOM450, in this example illustrates that using a SUS630. また実用上の観点から、前記高比重金属材料M And from a practical point of view, the high-density metal material M
2の比重は7.0〜10程度、より好ましくは7〜8. 2 having a specific gravity of about 7.0 to 10, more preferably 7-8.
5程度とするのが良い。 It is good to be about 5. またヘッド本体部9は、高比重金属材料M2から形成されるものであれば、2種以上の金属材料を用いて形成することもできる。 The head body portion 9, as long as it is formed from a high density metal material M2, may also be formed using two or more metal materials.

【0023】またヘッド本体部9において、各部の厚さは、特に限定されるものではないが、例えばソール部4 [0023] In the head main body portion 9, the thickness of each part, but are not particularly limited, for example, the sole portion 4
では、1.0mm以上、より好ましくは1.5mm以上とし、サイド部5では、例えば0.7mm以上、より好ましくは0.7〜1.0mmとするのが望ましい。 In, 1.0 mm or more, more preferably not less than 1.5 mm, the side portions 5, for example 0.7mm or more, and more preferably it is desirable to 0.7 to 1.0 mm. またフェース部2の厚さは、例えば2.2〜3.0mm、より好ましくは2.4〜2.6mmとすることが望ましい。 The thickness of the face portion 2, for example 2.2~3.0Mm, more preferably it is desirable that the 2.4~2.6Mm.

【0024】なおヘッド体積が小さすぎると、ヘッドの慣性モーメントを増大させる効果が低下し、逆に大きすぎると、ヘッド重量が過大となったり、またヘッドの重心が高くなるおそれもある。 It should be noted the head volume is too small, decrease the effect of increasing the moment of inertia of the head is and an excessively large or became head weight is excessive, also save on it the center of gravity of the head is increased. このような観点より、ヘッド1のヘッド体積は、例えば100〜200cm 3 、より好ましくは120〜170cm 3とすることが望ましい。 From this point of view, the head volume of the head 1, for example 100~200Cm 3, more preferably it is desirable that the 120~170cm 3.

【0025】また前記クラウン板7の重量は、前記ヘッド本体部9の重量の10〜30%、より好ましくは10 [0025] weight of the crown plate 7, 10-30% of the weight of the head body portion 9, and more preferably 10
〜25%、さらに好ましくは10〜17%とするのが望ましい。 25%, more preferably not to a 10 to 17%. 前記クラウン板7の重量がヘッド本体部9の重量の30%を超えると、ヘッド1の上部側の重量が増大化してヘッド1の重心高さが大となる傾向があり、逆に10%を下回ると、実質的にクラウン板7の厚さを小とすることとなる傾向があり、実用上必要な耐久性が得られ難い場合がある。 When the weight of the crown plate 7 is more than 30% of the weight of the head body portion 9, there is a tendency that the height of the center of gravity of the head 1 by weight of the upper side of the head 1 is increased reduction becomes large, 10% in the reverse below the tend to be be substantially small thickness of the crown plate 7, practically necessary durability it may be difficult to obtain.

【0026】また本発明では、クラウン板7とヘッド本体部9とは異種金属からなるため、クラウン板7とヘッド本体部9とをロウ付けにより接合されている。 [0026] In the present invention, since made of different metals and crown plate 7 and the head body portion 9 are joined by brazing a crown plate 7 and the head body portion 9. ロウ付けは、異種金属同士を接合するために母材よりも融点の低い金属ないし合金、すなわちロウを溶融させ、母材間の隙間に例えば毛細管現象を利用してロウを満たし固化させることで異種金属同士を接合する方法である。 Brazing heterogeneous by metal or alloy having a melting point lower than Hahazai for joining dissimilar metals to each other, i.e. to melt the wax, using a gap, for example a capillary phenomenon between the base material is solidified satisfies the wax a method of joining metal together. このような、ロウ付けは接着剤を用いて接合した場合に比して接合強度をより大にでき、これによりヘッドの耐久性が維持されうる。 Such brazing joint strength as compared with the case of bonding using an adhesive can turn on a larger, thereby the durability of the head can be maintained.

【0027】このようなロウ付けを行う場合、特に限定されるわけではないが、図5に拡大して示したように、 [0027] As the case of performing such brazing, is not particularly limited, shown enlarged in FIG. 5,
クラウン周縁部3eの周囲に受け部12を設けることにより、クラウン板7の周縁7eと内外で重なる重ね継手Jを形成することが望ましい。 By providing the receiving portions 12 on the periphery of the crown periphery 3e, it is desirable to form a lap joint J that overlaps the peripheral 7e and the inner and outer crown plate 7. このような重ね継手Jとすることにより、例えば強度の低いロウを用いた場合や多少の欠陥が生じても重ね代を十分に確保することにより、継手部分の強度を向上しクラウン板7とヘッド本体部9との外れを防止できる。 With such a lap joint J, for example, by the case and some defects with low wax strength is sufficiently secured even if the overlapping margin occurs, a crown plate 7 to increase the strength of the joint portion Head It can be prevented from coming off the body portion 9.

【0028】また、クラウン板7とクラウン周縁部3e Further, the crown plate 7 and the crown periphery 3e
とをロウ付けする場合、上述のように重ね継手Jを形成することが望ましが、とりわけクラウン板7とヘッド本体部3との接合面積を例えば200mm 2以上、好ましくは300mm 2以上、より好ましくは400mm 2以上、さらに好ましくは400〜800mm 2とすることが望ましい。 When brazing the bets, but Shi desirable to form the joint J overlapped as described above, especially the bonding area between the crown plate 7 and the head body portion 3, for example 200 mm 2 or more, preferably 300 mm 2 or more, more preferably the 400 mm 2 or more, more preferably it is desirable that the 400~800mm 2. なお該接合面積は、受け部12とクラウン板7との重なり面積とクラウン板7の端面7aの面積との総和として求められる。 Note the junction area is determined as the sum of the area of ​​the receiving portion 12 and the end surface 7a of the overlapping area of ​​the crown plate 7 of a crown plate 7.

【0029】前記接合面積が200mm 2未満であると、 [0029] When the junction area is less than 200 mm 2,
クラウン板7とヘッド本体部9との接合部における強度が十分に得られず、ヘッド1の耐久性が低下する傾向があり、逆に前記受け部12の巾を増すなどにより接合面積を800mm 2よりも大とすると、クラウン部3の剛性が著しく高められる結果、ヘッド1の打球感や打球音が悪化する傾向がある。 Strength is not sufficiently obtained at the junction of the crown plate 7 and the head body portion 9, there is a tendency that the durability of the head 1 is lowered, 800 mm bonding area due increasing the width of the receiving portion 12 in the reverse 2 When larger than, the results rigidity of the crown portion 3 is enhanced remarkably, there is a tendency that the shot feel and the hitting sound of the head 1 is deteriorated. 特にクラウン部の剛性が高くなると、打球音の中でも残響音が短くなってフィーリングが悪くなる。 In particular, the rigidity of the crown portion is higher, feeling the reverberation is shortened even in the hitting sound is poor.

【0030】またロウ付けに用いるロウは、接合する金属材料、その融点などに応じて種々選択されるが、強度とロウ付け条件の適正化という理由により、好ましくは銀ロウ(Ag−Al、Ag−Cu(BAg−19)、A Further waxes used in the brazing, the metallic material to be joined, but is variously selected depending on its melting point, for reasons that optimizing the strength and brazing conditions, preferably silver solder (Ag-Al, Ag -Cu (BAg-19), A
g−Al−Mn、Ti−Zr−Ni、Ti−Cu−N g-Al-Mn, Ti-Zr-Ni, Ti-Cu-N
i、Ti−Cu−Ni−Zr、Ag−Pb−Ga、Pb i, Ti-Cu-Ni-Zr, Ag-Pb-Ga, Pb
−Ag−Si)を用いるのが望ましい。 -ag-Si) is desirably used.

【0031】銀ロウは、銀−銅合金を主成分とするもので、鉄鋼材料、同、ニッケル及びそれらの合金など、マグネシウムとアルミニウム以外の広範囲の金属材料のロウ付けに好適に用いることができる。 The silver solder is a silver - as a main component of copper alloy, steel material, the, nickel and alloys thereof, it can be suitably used for brazing magnesium and aluminum non-extensive metallic material . 添加成分として、 As an additive component,
Cd、Ni、Sn、Liの元素が挙げられ、例えばJI Cd, Ni, Sn, include elements of Li, for example, JI
S Z3261に種々のものが記載されている。 It is described various ones in S Z3261. 融点は概ね620〜800℃であって、本実施形態で用いるチタン合金、SUS630よりも低融点となるなど好適に使用できる。 Melting point be generally 620-800 ° C., a titanium alloy used in the present embodiment can be used suitably such as a low melting point than SUS630.

【0032】本実施形態では、図2に示したようなクラウン板7とヘッド本体部9とを準備し、クラウン板7を前記クラウン周縁部3eの受け部12上に位置決め載置する。 [0032] In the present embodiment prepares a crown plate 7 and the head body portion 9 as shown in FIG. 2, to position placing the crown plate 7 on the receiving portion 12 of the crown periphery 3e. この際、必要であれば、クラウン板7とヘッド本体部9とを治具等により加圧し仮固定する。 At this time, if necessary, pressurized temporarily fixed by such jig and crown plate 7 and the head body portion 9. このときの加圧力が低すぎると、ロウ材料の充填が充分でなく隙間等の外観不良が生じ易く、逆に高すぎると、ヘッド本体そのものを傷付けたり、変形させてしまうおそれがある。 When pressure at this time is too low, tends poor appearance occur such gap insufficient filling of the braze material, and an excessively high, damaging the head main body itself, there is a possibility that deformed. このような観点より、前記加圧力は好ましくは0. From this point of view, the pressure is preferably 0.
1〜1.0MPa、より好ましくは0.3〜0.7MP 1~1.0MPa, more preferably 0.3~0.7MP
aとするのが望ましい。 It is desirable that as a.

【0033】そして、図3及び図5に一点鎖線で示すように、該クラウン板7とヘッド本体部9のクラウン周縁部3eとの境界部の隙間を中心として本例ではペースト状のロウ13を塗布する。 [0033] Then, as shown by a chain line in FIGS. 3 and 5, the crown plate 7 and pasty wax 13 in this example about the clearance of the boundary portion between the crown periphery 3e of the head main body portion 9 applied. そして、このヘッド1を例えば真空中の雰囲気の炉内で加熱することにより、溶けたロウ13が前記接合部の隙間に毛細管現象で浸入する。 Then, by heating the head 1, for example in a furnace atmosphere in a vacuum, wax 13 melts from entering by capillary action into the gap of the joint portion.
しかる後、ヘッド1を炉から取り出して接合部の研磨、 Thereafter, the polishing of the joint is taken out of the head 1 from the furnace,
塗装等を行ってヘッド1が製造される。 Head 1 is manufactured by performing a coating or the like.

【0034】なおヘッド1をロウ付けする際に加熱する温度は、クラウン板7、ヘッド本体部9の融点よりも低い温度かつロウ13の融点以上であるが、本実施形態の材料の組み合わせの場合、好ましくは620〜900 The temperature for heating the head 1 during brazing Incidentally, the crown plate 7, although lower temperatures and melting point of the wax 13 or more than the melting point of the head main body portion 9, the combination of the material of this embodiment , preferably 620-900
℃、より好ましくは650〜850℃とすることが望ましい。 ° C., more preferably it is desirable that the 650 to 850 ° C.. 620℃未満になると、ロウが融解せず、ロウ付けが困難となり、逆に900℃を超えると、クラウン板にβ変態するTi合金を用いたときなど該ロウ付け時にβ変態を生じてしまうためである。 If less than 620 ° C., the wax is not melted, the brazing is difficult, if conversely exceeds 900 ° C., since occurs the β transformation during the brazing, such as when using a Ti alloy β transformation on the crown plate it is.

【0035】またロウ付けの方法としては、前記炉中ロウ付け法以外にも、ガスロウ付法、高周波ロウ付け法、 [0035] Also as a method of brazing, in addition to the furnace brazing method, method with Gasurou, high-frequency brazing method,
アークロウ付け法、光ビームロウ付け法など種々の方法があり、いずれの方法で行っても良いが、好ましくは大量生産に適した前記炉中ロウ付け法が特に望ましい。 Arklow with method, there are various methods such as light Bimurou with method may be performed by any method, but preferably is particularly desirable the furnace brazing process suitable for mass production. また真空雰囲気中以外でロウ付けを行うときには、フラックスなどを先に塗布し接合表面の酸化を抑制する。 Also when performing brazing outside the vacuum atmosphere inhibits oxidation of the bonding surface by applying flux and first. またクラウン板7とヘッド本体部9とは重ね継手以外にも、 Further in addition overlap the crown plate 7 and the head body portion 9 fitting,
例えば突き合わせ継手としても良い。 For example, butt may be the joint.

【0036】以上詳述したが、本発明は、例示のウッド型ゴルフクラブヘッドに限定されるものではなく、内部に中空部を有するものであれば、アイアン型や、ウッド型とアイアン型との中間的なヘッド形状を有するユーティリティ型、さらにはパター型など種々のヘッドに適用しうるのは言うまでもない。 [0036] Although described in detail above, the present invention is not intended to be limited to the illustrated wood type golf club head, as long as it has a hollow portion therein, and an iron type, of the wood type and iron type utility type having an intermediate head shape, more of can be applied to various head such putter type of course.

【0037】 [0037]

【実施例】以下、本発明のより具体的な実施例について説明する。 BRIEF DESCRIPTION more specific embodiment of the present invention. 表1に示す仕様にてウッド型のゴルフクラブヘッドを試作し、ヘッドの慣性モーメント、重心高さ、 At the specifications shown in Table 1 were prototyped a wood type golf club head, the moment of inertia of the head, the center of gravity height,
耐久性、打球時のフィーリングなどをテストした。 Durability, tested and feeling of the time of hitting the ball. なおヘッド形状はいずれも、ヘッド体積を170cm 3 、ヘッド質量を225gに統一した。 Note any head shape, 170cm 3 of head volume was unified head mass 225 g. なお、比較例1、2、4 In Comparative Example 1, 2, 4
は、クラウン板とヘッド本体とを一体に形成した。 Formed a crown plate and the head body integrally. テスト内容は次の通りである。 Test contents are as follows.

【0038】<ヘッドの慣性モーメント>各供試ヘッドを規定のライ角、ロフト角で水平面に載置するとともに、その重心を通る垂直軸回りの慣性モーメントを、IN The lie angle of defining each of the trial heads <inertia moment of the head>, as well as placed on a horizontal plane in the loft angle, the moment of inertia about the vertical axis passing through the center of gravity, IN
ERTIA DYNAMICS Inc社製のMOMENT OF INERTIA MEASURIN ERTIA DYNAMICS Inc Co. MOMENT OF INERTIA MEASURIN
G INSTRUMENTの MODEL NO.005-002を用いて測定した。 It was measured by using the MODEL NO.005-002 of G INSTRUMENT.

【0039】<耐久性>各ヘッドにそれぞれ同一のシャフトを装着してウッド型ゴルフクラブを試作するとともに、各クラブをスイングロボットに取り付け、ヘッドスピード50m/sにてフェース部の中央で1000発の試打テストを行い、クラウン板とヘッド本体部との接合はずれ等を確認した。 [0039] <Durability> to each head wearing the same shaft with the prototype of the wood type golf club, mounting each club to swing robot, at a head speed of 50m / s of 1000 shots at the center of the face portion perform test hitting test was confirmed joining out like the crown plate and the head body portion. 接合部に外れ、亀裂等が生じていなかったものを○、その他を×として評価した。 Off the joint, what crack or the like did not occur ○, and evaluate other as ×.

【0040】<打球時のフィーリング>前記各ウッド型ゴルフクラブについて、10名のゴルファによる試打テストを行い、打球感、打球音を5点法で評価し10名の平均点を求めた。 [0040] For each of the wood-type golf club <feeling of hitting>, performs a test hitting test by 10 people golfer, shot feeling, to determine the average point of to evaluate the hitting sound in the 5-point method 10 people. 数値が大きいほど良好である。 The value, the better the larger. テストの結果などを表1に示す。 The results such as test shown in Table 1.

【0041】 [0041]

【表1】 [Table 1]

【0042】テストの結果、実施例のものは、比較例に比べてヘッドの重心を下げつつ慣性モーメントを増大していることが確認できる。 The test results, those embodiments, it can be confirmed that by increasing the moment of inertia while lowering the center of gravity of the head as compared with the comparative example. 概ね実施例のヘッドでは、慣性モーメントをX(g・mm 2 )、重心高さをY(mm)としたときに、比(X/Y)が130以上、好ましくは1 In generally the head of the embodiment, the moment of inertia X (g · mm 2), when the center of gravity height and Y (mm), the ratio (X / Y) is 130 or more, preferably 1
40以上、さらに好ましくは150以上に設定でき、単位重心高さ当たりの慣性モーメントをより大きく得ることができる。 40 or more, more preferably be set to 150 or higher, it is possible to obtain greater moment of inertia per unit height of the center of gravity.

【0043】これに対して比較例1では、ヘッド本体部が低比重材料により形成されるとともにソール部に錘部材を配して重量を集中的に配分しているため、ソール部に重量が偏り慣性モーメントが悪化していることが確認できる。 [0043] In Comparative Example 1 with respect to this, since the head main body portion is intensively distributed weight by arranging the weight member to the sole portion together is formed by a low density material, the weight is a bias in the sole portion it can be confirmed that the moment of inertia is getting worse. また比較例2又は4では、クラウン板を高比重材料により形成しているため、低重心化が図れていない。 In Comparative Example 2 or 4, for forming the crown plate by a high density material, not Hakare low center of gravity. さらに比較例3では、クラウン板が繊維強化樹脂からなり、またヘッド本体部との接合方法も接着としているため、耐久性が低くかつ打球フィーリングが悪化している。 In addition Comparative Example 3, crown plate from fiber reinforced resin, and because you are joining method also bonding the head main body, and the hitting feeling low durability is deteriorated. また比較例5は、クラウン板に低比重金属材料を、ヘッド本体部に高比重金属材料を用いてはいるが、 The Comparative Example 5, a low specific gravity metal material to the crown plate, but by using the high specific gravity metal material to the head body portion,
両者を接着剤により接合しているため、十分な耐久性が得られていない。 Due to the adhesively bonded to each other, so sufficient durability can not be obtained. また実施例において、接合面積を増大した実施例5は、打球フィーリングがやや劣るものとなった。 In addition examples, Examples 5 to increase the bonding area, hitting feeling was assumed that slightly inferior. これは、クラウン部の剛性が過度に高められた結果と考えられる。 This is believed to result the rigidity of the crown portion is increased excessively.

【0044】 [0044]

【発明の効果】上述したように、請求項1記載の発明では、ゴルフクラブヘッドが、ヘッド上面のクラウン部の主要部をなすクラウン板と、このクラウン板が配されるヘッド本体部とからなり、クラウン板は、比重が5.0 [Effect of the Invention] As described above, in the first aspect of the present invention, the golf club head is made up of a crown plate which forms the main portion of the crown portion of the head top surface, a head main body portion which the crown plate is disposed , crown plate, a specific gravity of 5.0
以下の低比重金属材料から形成され、かつ前記ヘッド本体部は比重が7.0以上の高比重金属材料を用いて形成されるとともに、前記クラウン板とヘッド本体部とをロウ付けにより接合したことにより、ヘッドの重心を下げつつ慣性モーメントを増大でい、しかもヘッドに必要な耐久性を確保することが可能になる。 Is formed from the following low specific gravity metal material, and the head main body portion with a specific gravity is formed by using a 7.0 or a high specific gravity metal material, that the said crown plate and the head body portion joined by brazing Accordingly, we have a moment of inertia increases while lowering the center of gravity of the head, moreover it is possible to ensure durability required for the head.

【0045】また、請求項2記載の発明では、クラウン板7の重量を、ヘッド本体部の重量に対して一定範囲に限定したことにより、より効果的に低重心化と慣性モーメントの増大を図りうる。 [0045] In the second aspect of the present invention, the weight of the crown plate 7, by which is limited to a certain range relative to the weight of the head body portion, it aims to more effectively increased low center of gravity and moment of inertia sell.

【0046】また、請求項4記載の発明では、クラウン板に高強度かつ低比重のチタン等を、またヘッド本体部には高強度かつ高比重のステンレス鋼を用いることにより、今までのヘッド素材を用いて容易に低重心かつ慣性モーメントの大きなゴルフクラブヘッドを製造できる。 [0046] In the invention of claim 4, wherein, the crown plate of high strength and low specific gravity such as titanium, also in the head main body portion by using a high-strength and high density stainless steel, the head material to date It can produce large golf club head easily low center of gravity and moment of inertia with.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本実施形態のゴルフクラブヘッドを例示する斜視図である。 1 is a perspective view illustrating a golf club head of this embodiment.

【図2】その分解斜視図である。 2 is an exploded perspective view thereof.

【図3】クラウン板とヘッド本体部との境界部にロウを塗布した状態っっを示す斜視図である。 3 is a perspective view showing the applied condition Tsutsu wax at the boundary between the crown plate and the head body portion.

【図4】ヘッドの断面図である。 4 is a cross-sectional view of the head.

【図5】そのA部の拡大図である。 FIG. 5 is an enlarged view of the A part.

【図6】ヘッドの断面図である。 6 is a cross-sectional view of the head.

【図7】従来のヘッドを例示する断面図である。 7 is a cross-sectional view illustrating a conventional head.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 ゴルフクラブヘッド 2 フェース部 3 クラウン部 3e クラウン周縁部 4 ソール部 5 サイド部 6 シャフト差込部 7 クラウン板 9 ヘッド本体部 12 受け部 13 ロウ M1 低比重金属材料 M2 高比重金属材料 1 golf club head 2 face portion 3 crown portion 3e crown periphery 4 sole portion 5 side portions 6 shaft insertion portion 7 crown plate 9 head body portion 12 receiving portion 13 row M1 low specific gravity metal material M2 high specific gravity metal material

Claims (4)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】内部を中空としたゴルフクラブヘッドであって、 ヘッド上面のクラウン部の主要部をなすクラウン板と、 And 1. A golf club head having an internal hollow, the crown plate constituting the main portion of the crown portion of the head top surface,
    このクラウン板が配されるヘッド本体部とからなり、 前記クラウン板は、比重が5.0以下の低比重金属材料から形成され、かつ前記ヘッド本体部は比重が7.0以上の高比重金属材料を用いて形成されるとともに、 前記クラウン板とヘッド本体部とをロウ付けにより接合したことを特徴とするゴルフクラブヘッド。 Consists of a head main body portion which the crown plate is disposed, said crown plate has a specific gravity 5.0 is formed from the following low specific gravity metal material, and the head main body highly dense metal density is 7.0 or more together are formed of a material, golf club heads, characterized in that the said crown plate and the head body portion joined by brazing.
  2. 【請求項2】前記クラウン板の重量が、前記ヘッド本体部の重量の10〜30%であることを特徴とする請求項1記載のゴルフクラブヘッド。 Wherein the weight of the crown plate, the golf club head of claim 1, wherein 10 to 30% of the weight of the head body portion.
  3. 【請求項3】前記ヘッド本体部は、ボールを打撃するフェース部と、該フェース部の下縁に連なりヘッド底部をなすソール部と、前記ソール部の周囲から立ち上がりかつ前記フェース部のトウ側からバックフェースを通り該フェース部のヒール側にのびるサイド部と、シャフトを装着しうるシャフト差込部とを含んでなる請求項1又は2記載のゴルフクラブヘッド。 Wherein the head body portion, a face portion for hitting a ball, and a sole portion that forms a head bottom continuous to the lower edge of the face portion, the toe side rising and the face portion from the periphery of the sole portion a side portion extending back face to the heel side of the street the face portion, claim 1 or 2 golf club head according comprising a shaft insertion portion capable of mounting the shaft.
  4. 【請求項4】前記クラウン板は、チタン又はチタン合金からなり、かつ前記ヘッド本体部はステンレス鋼を含むことを特徴とする請求項1〜3のいずれかに記載のゴルフクラブヘッド。 Wherein said crown plate is made of titanium or a titanium alloy, and a golf club head according to claim 1 wherein the head main body portion, characterized in that it comprises a stainless steel.
JP2000370379A 2000-12-05 2000-12-05 Golf club head Active JP4451982B2 (en)