JP2002113138A - Golf club head - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a golf club head which can increase a distance while assuring the strength to enable the golf club head to withstand impact in hitting a ball. SOLUTION: This golf club head consists of a head body 1 and a face plate 2 disposed at the front of this head body 1. The face plate 2 consists of a metallic material satisfying the relation y>=0.006x+60 when its Young's modulus is defined as (x) (unit: kgf/mm2) and its tensile strength as (y) (unit: kgf/mm2). The face plate 2 is constituted thickly in its central part and thinly in its peripheral part.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a metal golf club head for hitting a golf ball.

[0002]

2. Description of the Related Art In recent years, wood-type golf club heads mainly made of persimmon mainly use metal materials such as carbon steel, stainless steel, duralumin, and titanium. I have.
Such a golf club head can increase the head volume and face area and stabilize the directionality of a hit ball by increasing the moment of inertia of the head, as compared with a golf club head using persimmon. Furthermore, the sweet area of the head can be increased to reduce the rebound of the ball when the ball is hit with the core removed. In addition, when the golf club head is enlarged, a sense of stability at the time of addressing is improved, and a longer shaft can be attached, thereby increasing the flight distance.

[0003] The applicant of the present application has disclosed a Japanese Patent No. 21305 as a golf club head for maximizing the resilience performance between the head and a golf ball and increasing the flight distance.
No. 19 (Japanese Patent Publication No. 5-33071). In this patent, a frequency indicating a first-order minimum value of the mechanical impedance of a golf club head (hereinafter, may be simply referred to as a “primary frequency of the impedance of the head”) is defined as one of the mechanical impedance of the golf ball.
The frequency showing the next minimum value (hereinafter, sometimes simply referred to as “primary frequency of the impedance of the ball”;
１1600 Hz. ) To maximize the impact speed of the impacted ball (hereinafter sometimes referred to as “impedance matching theory”).

[0004] "Mechanical impedance" is defined as the ratio of the magnitude of a force acting on a certain point to the magnitude of the response speed of another point when this force acts. That is,
Assuming that a force externally applied to a certain object is F and a response speed is V, the mechanical impedance Z is defined as Z = F / V.

In order to reduce the primary frequency of the impedance of the head, it is effective to reduce the rigidity of the face or face of the head. For example, increasing the area of the face portion, reducing the thickness of the face portion, using a material having a low Young's modulus for the face portion, and the like can be mentioned. Especially on the face of the head,
It is also empirically known that the use of a metal material having a low Young's modulus has an advantage that the feel (hit feeling) when hitting a ball is soft and the impact transmitted to the hand is small even at the time of a missed shot. .

However, it is difficult for a metal material having a low Young's modulus but a small tensile strength to have a strength that can withstand an impact at the time of impact. When the thickness of the face portion is increased to obtain the strength of the face portion, the effect of lowering the rigidity of the face portion is small as a result, and there is a limit in reducing the primary frequency of the impedance of the head. Was.

In the case of a metal material having a low Young's modulus but a low surface hardness, the surface of the face portion is worn out early due to friction with the ball at the time of impact or bite of sand between the ball at the time of impact. There is a problem that it is easily worn or damaged.

According to the first to third aspects of the present invention, the impedance matching theory described above is based on reducing the rigidity of the face portion while securing the strength capable of withstanding an impact upon impact. It is an object of the present invention to provide a golf club head that can increase the flight distance based on the golf club head.

In the present invention, it is preferable that the hardness of the face portion is secured while preventing the face portion from being worn or damaged due to friction with the ball at the time of impact or sand biting. It is an object of the present invention to provide a golf club head capable of obtaining a soft feel at impact and further increasing the flight distance based on impedance matching theory, based on a reduction in rigidity.

[0010]

According to a first aspect of the present invention, there is provided a head body, and a face plate disposed on a front surface of the head body.
When the Young's modulus is x (unit: kgf / mm ² ) and the tensile strength is y (unit: kgf / mm ² ), the face plate is made of a metal material satisfying a relationship of y ≧ 0.006x + 60. A golf club head having a thick central portion and a thin peripheral portion.

The invention according to claim 2 is the golf club head according to claim 1, wherein the metal material has a tensile strength y of 105 to 400 (kgf / mm ² ).

According to a third aspect of the present invention, the metal material has a Young's modulus x of 3000 to 16000 (kgf / mm
^3. The golf club head according to claim 1, wherein the golf club head is a golf club head.

According to a fourth aspect of the present invention, there is provided a head body.
And the face plate arranged on the front of this head body
And the face plate has a Young's modulus of x (unit: kg)
f / mm ^Two), And its Vickers hardness is z (unit: HV).
And a metal material satisfying the relationship z ≧ (x / 60) +200
The plate is thick at the center and thin at the periphery
A golf club head characterized in that
You.

According to a fifth aspect of the present invention, the metal material has a Young's modulus x of 3000 to 10000 (kgf / mm
The golf club head according to claim 4, which is ² ).

According to a sixth aspect of the present invention, the surface of the face plate has a Vickers hardness of 300 to 1000 (HV).
The golf club head according to claim 4 or 5, wherein

[0016]

Embodiments of the present invention will be described below in detail with reference to the drawings. FIGS. 1 to 3 illustrate a hollow wood type (metal head) golf club head formed of a metal material as a golf club head according to the present invention. In the present embodiment, the head includes a head body 1 and a face plate 2 disposed on the front surface of the head body 1. The golf club head has a head volume of, for example, 80 to 360 cm ³ , preferably 230 to 360 cm ^3.
It is desirable that

The head main body 1 forms a peripheral edge of a face portion 6 for hitting a ball, and has a face mounting portion 1a on which the face plate 2 can be mounted, and a face mounting portion 1a.
, A sole portion 7, a crown portion 8, a side portion 9, and the like. In the present embodiment, the face mounting portion 1a is configured as shown in FIG.
As shown in FIG. 1, a fitting opening 3 having a stepped portion 3a for mounting the face plate 2 and penetrating into the head is formed.

In the present embodiment, the face plate 2 forms a main part of the face portion 6 and is integrated with the fitting opening 3 by a joining method such as welding, caulking, or an adhesive. The face portion 6 can be configured together with 1a. The face mounting portion 1a can also be formed as an opening 3 having no step 3a as shown in FIG. 4A, and a tapered shape expanding toward the inside of the head as shown in FIG. 4B. And a concave portion 4 for fitting that can support the back surface of the face plate 2. In this case, it is desirable that the face plate 2 is also formed in substantially the same tapered shape.

As a result of various experiments by the inventors, the Young's modulus was x (unit: kgf / mm ² ), and the tensile strength was y (unit: kg).
f / mm ² ), it was found that it is desirable that a part of the face portion 6 be formed of a metal material satisfying the relationship y ≧ 0.006x + 60.

In the present embodiment, an example in which the face plate 2 is formed of such a metal material as a part of the face portion 6 is illustrated. For this reason, the face portion 6
(The face plate 2 constituting the main part of the face portion 6 in this example) can keep its Young's modulus low while securing the tensile strength to withstand the impact at the time of impact. Therefore, this golf club head can lower the primary frequency of the impedance of the head, improve the flight distance of the hit ball by the impedance matching theory, and reduce the impact at the time of impact. Provides a soft feel at impact.

Further, since the golf club head can maintain a high tensile strength while reducing the Young's modulus, the thickness of the face portion 6 or the face plate 2 can be reduced to reduce the weight of the head. Becomes possible. Further, for example, the spring constant of the head is reduced by an amount corresponding to the reduction in the thickness of the face plate 2, and the primary frequency of the impedance of the head can be further reduced.

In this embodiment, the thickness of the face plate 2 is substantially uniform. It is desirable that the thickness be, for example, 1 to 4 mm, more preferably 1 to 3 mm. If the thickness of the face plate 2 is less than 1 mm, the strength tends to decrease. Conversely, if it exceeds 4 mm, the effect of reducing the weight of the head and reducing the primary frequency of the impedance of the head decreases. Tend.

Incidentally, the primary frequency of the impedance of a golf ball is in the range of about 600 to 1600 Hz, and about 1000 to 12 Hz for a general two-piece ball.
00 Hz. On the other hand, the primary frequency of the impedance of the conventional stainless steel wood type head is about 1
800 to 2500 Hz, and about 1400 to 2000 Hz for a wood type head made of titanium. In the golf club head according to the present embodiment, the primary frequency of the impedance of the head is made smaller than that of the conventional head, and it is possible to approximate or match the primary frequency of the impedance of the golf ball. It is.

For example, in this embodiment, the primary frequency of the impedance of the head can be set to less than 1300 Hz. This is a value that approximately matches that of a two-piece ball. Thereby, in the golf club head of the present embodiment, the launch speed of the ball at the time of impact is maximized, and the flight distance is increased. Also, preferably,
When the Young's modulus is x (unit: kgf / mm ² ) and the tensile strength is y (unit: kgf / mm ² ), at least a part of the face portion 6 is made of a metal satisfying a relationship of y ≧ 0.006x + 63. It is also desirable to use a material, or more preferably, a metal material that satisfies the relationship y ≧ 0.006x + 100.

If the metal material of the face plate 2 satisfies y <0.006x + 60, for example, the balance between the tensile strength and the Young's modulus deteriorates,
While securing the strength to withstand the impact impact,
It is difficult to reduce the rigidity of the metal part. In the present embodiment, the tensile strength of the face plate 2 metal material, it is desirable to maintain a degree that does not significantly increase the thickness of the face plate 2, for example, 80 kgf / mm ² or more, preferably 105kgf / mm ² or more , More preferably 13
Desirably, it is 0 kgf / mm ² or more. Note that the upper limit of the tensile strength can be set to 400 kgf / mm ² or less even in combination with any of the above-mentioned lower limits due to manufacturing problems and the like.

In this embodiment, the face plate
The Young's modulus of metallic material 2 is an example to obtain the required rigidity.
For example, 3000kgf / mm^TwoAbove, preferably 5000kgf
/ Mm ^TwoIt is desirable to make the above. However, the Young's modulus is large.
If too large, the rigidity of the face 6 tends to increase.
Therefore, its upper limit is combined with any of the above lower limits.
25000kgf / mm in total^TwoBelow, preferably
20000kgf / mm^TwoHereinafter, more preferably 1600
0kgf / mm^TwoOr less, more preferably 12000 kgf / mm
^TwoHereinafter, more preferably 10,000 kgf / mm^TwoAnd
It is desirable to do.

In these embodiments, the rigidity of the face portion is reduced while ensuring the strength to withstand the impact at the time of impact. Next, the friction with the ball at the time of impact, An embodiment capable of preventing wear and damage of the surface of the face portion due to biting of sand will be described.

This embodiment can also be applied to golf club heads having the shapes shown in FIGS. 1 to 3 or FIGS. 4A and 4B.
(Unit: kgf / mm ² ), Vickers hardness is z (unit: H
When V), it was found that it is desirable that at least a part of the surface of the face portion be made of a metal material satisfying the relationship z ≧ (x / 60) +200. For example, by forming the face plate 2 with such a metal material, a part of the surface of the face portion 6 can be formed with a metal material satisfying z ≧ (x / 60) +200. In the present embodiment, the surface of the face plate 2 is not provided with a surface layer of another metal, resin, wood, or the like, and is exposed.

The Vickers hardness of the metal material is a hardness obtained by using a diamond square quadrangular pyramid indenter having a face-to-face angle of 136 degrees, a test load when a test surface is recessed, and a surface area of the recess. The details are specified in JIS and the like, and the test load is 30 kgf in the present invention. In this embodiment, the face plate 2 secures a large Vickers hardness and can prevent abrasion and damage of the face portion 6 due to friction with a ball at the time of impact or sand biting. In addition, since the metal material of the face plate has the above-described relationship between the Young's modulus x and the Vickers hardness z, it is possible to maintain a low Young's modulus while securing a large Vickers hardness.

Therefore, also in the golf club head of this embodiment, the primary frequency of the impedance of the head can be reduced, and the flight distance of the hit ball can be improved by the impedance matching theory. In addition, since a part of the surface of the face portion has a low Young's modulus, impact at the time of impact is reduced, and a soft feel at impact is provided.

In this embodiment, if the face plate 2 is made of a metal material satisfying z <(x / 60) +200, a soft feel at impact, an increase in flight distance,
It becomes impossible to simultaneously satisfy the three performances, that is, the durability of the face portion 6. In addition, the face plate 2 can maintain a large Vickers hardness while lowering the Young's modulus, so that the thickness of the face portion 6 (face plate 2) can be reduced. Therefore, the weight of the head can be reduced, and the spring constant of the head decreases as much as the thickness of the face plate 2 is reduced. Therefore, a synergistic action of these factors further reduces the primary frequency of the impedance of the head. Can be lowered.

The preferred range of the Vickers hardness of the face plate 2 is 250 HV or more, preferably 300 HV or more. If it is more preferably 370 HV or more, and still more preferably 400 HV or more, very excellent scratch resistance is obtained, which is ideal. The upper limit can be set to 1000 HV or less even in combination with any of the above lower limits due to manufacturing problems and the like.
Thereby, it is possible to more suitably prevent the surface of the face portion 6 from being damaged.

Preferably, the Young's modulus is x (unit:
kgf / mm^Two), Vickers hardness is z (unit: HV)
In this case, it is desirable that at least a part of the surface of the face portion 6 is made of a metal material satisfying z ≧ (x / 60) +250. Again
Also in the embodiment, the Young's modulus of the face plate 2
Is, for example, 3000 kgf / mm to obtain the required rigidity.^Two
Above, preferably 5000 kgf / mm^TwoHope to do more
Good. However, if the Young's modulus is too large, the face
6 tends to have a high rigidity, so the upper limit is
250 in combination with any of the above lower limits
00kgf / mm ^TwoBelow, preferably 20,000 kgf / mm^Two
And more preferably 16,000 kgf / mm^TwoBelow
More preferably 12000 kgf / mm^TwoBelow, even more preferred
Ha 10,000 kgf / mm^TwoIt is desirable to make the following.

Although the two embodiments have been described,
The metal material forming such a face plate 2 is preferably an amorphous metal. Amorphous metal refers to a material whose atomic arrangement is not regular over a wide range. At present, a molten alloy obtained by melting various alloy materials at a high temperature is rapidly cooled so that crystal nuclei do not form and grow. It is manufactured by cooling to a solid. In the present embodiment, the degree of amorphousness, that is, the amorphous ratio, which is the ratio (v1 / v) of the volume v1 of the amorphous phase to the total volume v, is 50.
% Or more of the amorphous metal is preferably used.

The amorphous metal is represented by the general formula: MaXb (where a and b are 65% a ≦ 10
0, 0 ≦ b ≦ 35). Here, M is Zr, V, Cr, Mn, Fe, Co, Ni, C
u, Ti, Mo, W, Ca, Li, Mg, Si, Al,
One or more metal elements selected from Pd and Be;
X is made of one or more metal elements selected from Y, La, Ce, Sm, Md, Hf, Nb, and Ta. Preferably, a and b satisfy 99 ≦ a ≦ 1000 ≦ b ≦ 1.

Such an amorphous metal has a high tensile strength,
Since it has both high Vickers hardness and low Young's modulus, it is a metal material suitable for the golf club head of the present invention. As this amorphous metal, a zirconium-based amorphous alloy can be particularly preferably employed. This zirconium-based amorphous alloy has higher tensile strength and lower Young's modulus. In addition, the cooling rate during manufacturing can be made relatively small,
It is practical and preferable in that a molten metal is poured into a mold and cooled, and a lump or a plate can be formed relatively easily.

The zirconium-based amorphous alloy is represented by the general formula: ZrcMdXe (c, d, and e are atomic%, 20 ≦ c ≦ 80, 20 ≦ d ≦ 8
0, 0 ≦ e ≦ 35). However, Zr is zirconium, M is V, Cr, Mn, Fe,
Co, Ni, Cu, Ti, Mo, W, Ca, Li, M
g, one or more metal elements selected from Si, Al, Pd, Be, and X is Y, La, Ce, Sm, Md, H
It is made of one or more metal elements selected from f, Nb, and Ta.

The above-mentioned c, d, and e preferably satisfy 35 ≦ c ≦ 75 25 ≦ d ≦ 650 ≦ e ≦ 30, and more preferably 35 ≦ c ≦ 75 25 ≦ d ≦ 650 ≦ e. ≦ 1 More preferably 50 ≦ c ≦ 75 25 ≦ d ≦ 500 ≦ e ≦ 1 M is particularly preferably Al, Cu or Ni, and X is preferably Hf. In particular, as such a zirconium-based amorphous alloy, ZrcAld1Cud2Nid3Hfe is preferable (where d1 + d2 + d3 = d. C
+ D + e = 100).

The amorphous metal has an amorphous ratio of 75%.
Or more, more preferably 80% or more, and still more preferably 9% or more.
It is desirable to set it to 0%. Such an amorphous ratio can be specified by observing the cut cross section of the sample of the metal material by mirror polishing and etching treatment with an optical microscope and measuring the area of the amorphous portion. The amorphous ratio is determined by the alloy composition of the amorphous metal, the cooling temperature at which the molten alloy is cooled when producing the amorphous metal, and the oxygen in the surrounding gas when producing the amorphous metal. It can be adjusted by changing the concentration and the like. In particular, the amorphous rate can be increased as the cooling rate is increased and the oxygen concentration in the surrounding gas is decreased.

In the present invention, the thickness of the face plate is made thicker at the center and gradually thinner at the periphery toward the outside (not shown in the figure). This allows
It is possible to further reduce the primary frequency of the impedance of the head without reducing the strength of the face plate 2.

The head body 1 can be made of a conventional metal material such as titanium, a titanium alloy, and stainless steel. Further, as shown in FIG. 5, all the heads forming the face portion 6, the sole portion 7, the crown portion 8 and the side portion 9 have a Young's modulus of x (unit: kgf).
/ Mm ² ), and when the tensile strength is y (unit: kgf / mm ² ), the metal material satisfying the relationship y ≧ 0.006x + 60 or the Vickers hardness is z
When (unit: HV), a metal material satisfying the relationship z ≧ (x / 60) +200 can be used. In this case, impact durability and shot feeling are further improved, and the primary frequency of the impedance of the head can be further reduced.

FIGS. 6 and 7 show a metal iron type club head as another embodiment of the present invention.
In this example, the head is shown to be composed of a head main body 101 and a face surface insert plate 102 fitted on the face portion 104 side of the head main body 101. The face surface insert plate 102 forms a main part of the face portion 104 and mainly hits the ball with its surface. Further, the face surface insert plate 102 is provided with a fitting recess 10 formed on the face portion 104 side of the head main body 1.
No. 3 shows the one fitted and fixed by an adhesive, welding, caulking, press-fitting or the like. For this reason, since the entire back surface of the face surface insert plate 102 is in close contact with or in contact with the head main body 1, the durability of the face portion 104 is increased.

For example, the Young's modulus of the face insert plate 102 is x (unit: kgf / m).
m ² ) and when the tensile strength is y (unit: kgf / mm ² ), the metal material satisfying the relationship y ≧ 0.006x + 60 or the Young's modulus is x (unit:
kgf / mm ² ) and a Vickers hardness of z (unit: HV), the same effect as described above can be obtained by using a metal material satisfying the relationship z ≧ (x / 60) +200.

Although several embodiments have been described above, the present invention relates to a type of head, particularly a wood type head.
An iron type is preferred, but a putter type can also be used. Further, in each of the above embodiments, the face plate 2 or the face surface insert plate 102 is formed such that Young's modulus is x (unit: kgf / mm ² ) and tensile strength is y (unit: kgf).
/ Mm ² ) and a metal material that satisfies y ≧ 0.006x + 60 and z ≧ (x / 60) +200 when Vickers hardness is z (unit: HV). In this case, based on the impedance matching theory, it is possible to improve the flight distance of the ball, and at the same time, to have a strength that can withstand the impact at impact and a highly durable golf club having a very durable face that does not easily damage the surface. The head is obtained.

[0045]

EXAMPLES <First Specific Example> A zirconium-based amorphous alloy (Zr-A) in which the alloy composition was variously changed was used in a part of the face portion.
1-Cu-Ni-Hf or Zr-Al-Cu-Ni)
Is used to produce a wood-type golf club head (Examples, Reference Examples 1 to 5), and using the golf club head, a head speed, a ball speed, a coefficient of restitution, a carry,
The total flight distance, the frequency of the first-order minimum value of the mechanical impedance of the head, the feel at impact, and the like were examined. The results are shown in Table 1. As Comparative Examples 1 and 2, a wood-type hollow head made of titanium and a wood-type hollow head made of stainless steel were manufactured, and the performance was compared. The head speed, ball speed, coefficient of restitution, carry and total flight distance were measured by a hitting test using a swing robot. In order to measure the frequency of the first-order minimum value of the mechanical impedance of the head, the vibration using a vibrator, an acceleration pickup, a power unit, a dynamic signal analyzer, or the like similar to that described in the Japanese patent is used. A measurement method was used. The shot feeling was evaluated by 20 golfers who actually hit the ball, and based on the low impact (whether a soft feel is obtained), a five-point sensory evaluation of 1 to 5 points was performed. The average was taken.

[0046]

[Table 1]

As is apparent from Table 1, the frequencies of the first-order minimum values of the mechanical impedance of the golf club heads of Comparative Examples 1 and 2 are 1450 Hz and 1980 Hz, while the Examples and Reference Examples 1 to 5 , Are all suppressed to 1290 Hz or less. Thereby, Examples and Reference Examples 1 to 5
Can reduce the frequency of the primary minimum value of the mechanical impedance of the head to a value smaller than that of the conventional head, and can approximate the frequency of the primary minimum value of the mechanical impedance of the two-piece ball (about 1000 to 1200 Hz). Was confirmed. Note that the tensile strength of the metal material used for the face plate is 200 kgf / mm ² or less. Further, the restitution coefficient, carry, and total flight distance of Comparative Examples 1 to 5 and Examples of Comparative Examples 1 and 2 were all the same.
It turns out that it is larger than. Further, with regard to the feel at impact, the examples are better (softer) than the comparative examples 1 and 2.

In the reference example, the thickness of the face plate (amorphous metal portion) is set smaller as the tensile strength becomes higher. It is considered that the decrease in the thickness further reduced the spring constant of the face portion, and increased the coefficient of restitution, carry, the total flight distance, and the shot feeling. FIG. 8 shows the Young's modulus x and the tensile strength y of the metal material.
The relationship is shown. The metal materials used for the face plates of the above Examples, Reference Examples 1 to 5 and Comparative Examples 1 and 2 are plotted in FIG. The data for duralumin, magnesium alloy and Super Hyten were also plotted.

In FIG. 8, the line 10 is y = 0.006.
The graph line indicating x + 60, the straight line 11 is y = 0.006x
The graph line indicating +63 and the straight line 12 are y = 0.006x +
It is a graph line which shows 100. Note that y ≧ 0.006x +
The region satisfying 60 is indicated by oblique lines. The metal material used in Examples and Reference Examples 1 to 5 is y ≧ 0.006x
It satisfies +60, but it can be seen that y <0.006x + 60 for the metal materials used in Comparative Examples 1 and 2, duralumin, magnesium alloy, super high tensile steel, and the like.

<Second Specific Example> Next, as another example, the relationship between Young's modulus and Vickers hardness was examined. Manufacture iron-type heads similar to those shown in FIGS. 6 and 7 (Reference Examples 7 to 9) and wood-type heads similar to those shown in FIGS. 1 to 3 (Reference Examples 10 to 12). did. Further, iron type heads (Comparative Examples 4 to 6) and wood type heads (Comparative Examples 7 to 9) were manufactured by using stainless steel, titanium, and duralumin as the material of the face surface insert plate and the face plate. For these heads, tests were conducted mainly on the scratch resistance of the surface of the face portion and the softness of the shot feeling. The scratch resistance of the surface of the face portion was determined by examining the amount of scratches on the surface of the face portion by using a swing robot to hit a golf ball placed on the ground with slight sand. The softness of the shot feeling was obtained by evaluating the feeling with 20 golfers and taking the average. The measured load of Vickers hardness is 30 kgf. Tables 2 and 3 show the test results.

[0051]

[Table 2]

[0052]

[Table 3]

As is clear from Tables 2 and 3, the golf club heads of Reference Examples 7 to 9 and Reference Examples 10 to 12
The surface of the face portion is hardly damaged (less or very little damage), and the shot feeling is soft (good or extremely good). At least one of the face surface damage and the soft feeling performance is "very good". Further, for example, Reference Example 7 has the same Vickers hardness (same scratch resistance) as Comparative Examples 3 and 4, but has a very low Young's modulus. Therefore, the golf club head of this embodiment has an increased flight distance and a soft feeling when hitting a ball,
It can be seen that there is little damage due to sand, stones, etc., and the wear resistance is excellent.

FIG. 9 shows the relationship between the Young's modulus x and the Vickers hardness z of the metal material. The metal materials of the face plates of Reference Examples 7 to 9 and Comparative Examples 3 to 8, magnesium, and super high tensile strength were used. Are plotted. In the figure, the straight line 16 is z = (x / 60)
+200, and line 17 is z = (x / 60) +250
Is shown. A region satisfying the relationship z ≧ (x / 60) +200 is indicated by oblique lines. As is clear from the figure, Reference Examples 7 to 12 satisfy the relationship z ≧ (x / 60) +200.

[0055]

As described above, according to the golf club head of the first aspect, it is possible to easily achieve both high tensile strength and low Young's modulus, and a part of the face portion can be easily removed at the time of impact. Rigidity can be reduced while maintaining tensile strength to withstand impact. Therefore, the frequency of the first-order minimum value of the mechanical impedance of the head can be made smaller than that of the conventional golf club head. For example, the frequency of the primary minimum value of the mechanical impedance of the golf club head can be set to a value closer to the frequency of the primary minimum value of the mechanical impedance of the golf ball.
Therefore, the flight distance increases. Also, the hitting feel at the time of hitting the ball can be made soft. Further, the golf club head can reduce the thickness of the face portion,
Further weight reduction can be achieved. When the thickness of the face portion is reduced, the spring constant of the face portion is reduced by that amount, and the frequency of the first-order minimum value of the mechanical impedance can be reduced.

In the golf club head according to the fourth aspect, both high tensile strength and low Young's modulus can be easily achieved, and a part of the face portion is subjected to friction at impact or sand biting at impact. The rigidity can be reduced while maintaining the surface hardness that can withstand the pressure. Therefore,
The frequency of the primary minimum value of the mechanical impedance can be made smaller than that of a conventional golf club head while maintaining the durability and scratch resistance of the head. For example, the frequency of the primary minimum value of the mechanical impedance of the golf club head can be set to a value closer to the frequency of the primary minimum value of the mechanical impedance of the golf ball.
Therefore, the flight distance increases. Also, the hitting feel at the time of hitting the ball can be made soft. Further, the golf club head can reduce the thickness of the face portion,
Further weight reduction can be achieved. When the thickness of the face portion is reduced, the spring constant of the face portion is reduced by that amount, and the frequency of the first-order minimum value of the mechanical impedance can be reduced.

[Brief description of the drawings]

FIG. 1 is a front view showing one embodiment of a wood type golf club head.

FIG. 2 is a side view thereof.

FIG. 3 is a sectional view of FIG. 2;

FIGS. 4A and 4B are cross-sectional views of another embodiment of a head having a different mounting structure of a face plate.

FIG. 5 is a sectional view of a head showing still another embodiment.

FIG. 6 is a front view showing an embodiment of an iron type golf club head.

FIG. 7 is a sectional view of the same.

FIG. 8 is a graph showing the relationship between Young's modulus and tensile strength.

FIG. 9 is a graph showing the relationship between Young's modulus and Vickers hardness.

[Explanation of symbols]

 1 golf club head 2 face plate 3 opening

Claims (6)

[Claims] 1. A head body comprising: a head body; and a face plate disposed on a front surface of the head body.
When the Young's modulus is x (unit: kgf / mm ² ) and the tensile strength is y (unit: kgf / mm ² ), the face plate is made of a metal material satisfying the relationship y ≧ 0.006x + 60. A golf club head comprising a thick central portion and a thin peripheral portion. 2. The metal material has a tensile strength y of 105.
^2. The golf club head according to claim 1, wherein the weight of the golf club head is in the range of 400 to 400 (kgf / mm ² ). 3. The metal material has a Young's modulus x of 300.
0~16000 (kgf / mm ²⁾ in a claim 1 or 2 golf club head according. 4. A head body comprising: a head body; and a face plate disposed on a front surface of the head body.
When the Young's modulus is x (unit: kgf / mm ² ) and its Vickers hardness is z (unit: HV), the face plate is made of a metal material satisfying a relationship of z ≧ (x / 60) +200. Is a golf club head having a thick central portion and a thin peripheral portion. 5. The metal material has a Young's modulus x of 300.
0~10000 (kgf / mm ²⁾ The golf club head according to claim 4, wherein. 6. The golf club head according to claim 4, wherein the Vickers hardness of the surface of the face plate is 300 to 1000 (HV).